KR102394814B1 - Room temperature cure two-part sealer - Google Patents
Room temperature cure two-part sealer Download PDFInfo
- Publication number
- KR102394814B1 KR102394814B1 KR1020170183871A KR20170183871A KR102394814B1 KR 102394814 B1 KR102394814 B1 KR 102394814B1 KR 1020170183871 A KR1020170183871 A KR 1020170183871A KR 20170183871 A KR20170183871 A KR 20170183871A KR 102394814 B1 KR102394814 B1 KR 102394814B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- room temperature
- epoxy resin
- temperature curing
- amine
- Prior art date
Abstract
본 발명은 지방산 변성 에폭시 수지 50~75중량%, 비스 페놀 A형 에폭시 수지 5~10중량%, 제1 충진제 15~25중량% 및 첨가제 0.5~3중량%를 포함하는 주제 및 지방족 변성 아민 수지 65~80중량%, 아민-터미네이티드 반응성 액상 고무 10~20중량% 및 제2 충진제 10~20중량%를 포함하는 경화제를 포함하는 구성을 마련한다.
상기와 같은 상온 경화 이액형 실러는 신율 특성 및 기계적 물성이 우수하다.The present invention is a main and aliphatic-modified amine resin 65 comprising 50 to 75% by weight of a fatty acid-modified epoxy resin, 5 to 10% by weight of a bisphenol A-type epoxy resin, 15 to 25% by weight of a first filler, and 0.5 to 3% by weight of an additive -80 wt%, an amine-terminated reactive liquid rubber 10 to 20% by weight, and a second filler comprising a curing agent comprising 10 to 20% by weight is prepared.
The room temperature curing two-component sealer as described above has excellent elongation properties and mechanical properties.
Description
본 발명은 상온 경화 이액형 실러에 관한 것으로, 신율 특성 및 기계적 물성이 우수한 상온 경화 이액형 실러에 관한 것이다.The present invention relates to a room temperature curing two-component sealer, and to a room temperature curing two-component sealer having excellent elongation properties and mechanical properties.
일반적으로 도장실러는 PVC를 주성분으로 사용하고, 이 외에 접착부여제, 충전제 및 가소제 등을 혼합시켜 제조되는 열경화 일액형 접착제이다. In general, a paint sealer is a thermosetting one-component adhesive manufactured by using PVC as a main component and mixing an adhesive imparting agent, a filler, and a plasticizer.
이러한 도장실러는 차체조립 완료 및 전착 공정 통과한 후 도포되므로 조립부에 가려지는 부분에 대해서 도장실러가 도포되지 못하는 상황이 발생된다. 이에 미처 마감처리가 이루어지지 못한 틈 사이로 물이 새어 들어가 불량이 발생되는 문제점이 있다.Since the paint sealer is applied after the body assembly is completed and the electrodeposition process is completed, there is a situation in which the paint sealer cannot be applied to the part covered by the assembly part. Accordingly, there is a problem in that water leaks through gaps that have not yet been finished and causes defects.
상술한 바와 같은 문제점을 해결하기 위해서 차체조립 이전에 도장실러를 도포하여 마감 처리를 실시하는 방법이 요구된다. 이때 도장실러로 상온 경화 이액형 실러가 적용된다. In order to solve the above-described problems, a method of performing finishing treatment by applying a paint sealer before assembling a vehicle body is required. At this time, a room temperature curing two-component sealer is applied as a paint sealer.
이러한 상온 경화 이액형 실러의 주성분으로 에폭시 수지를 사용하는데, 이를 이용하여 마감 처리를 실시할 경우, 유연성이 부족하여 신율이 저하되거나 기존 도포되는 도장실러와 접촉하는 부분에 크랙이 형성될 수 있다. 따라서 반복되는 충격 또는 온도 변화에도 유연성을 갖는 실러에 관한 연구가 진행되고 있다. Epoxy resin is used as the main component of this room temperature curing two-component sealer, and when a finishing treatment is performed using this, the elongation may be lowered due to lack of flexibility, or cracks may be formed in the portion in contact with the previously applied paint sealer. Therefore, research on a sealer having flexibility despite repeated impact or temperature change is being conducted.
이러한 기술의 일 예가 하기 특허문헌 1에 개시되어 있다.An example of such a technique is disclosed in Patent Document 1 below.
즉, 하기 특허문헌 1은 에폭시 수지 조성물에 관한 것으로, (1) 적어도 하나의 에폭시 수지, (2) 적어도 하나의 폴리에테르디아민 또는 폴리에테르트리아민, 특히 폴리에테르트리아민, (3) 적어도 하나의 카르복실-말단의 부타디엔-아크릴로니트릴 공중합체 및 (4) 코어/쉘 구조를 갖는 고무입자를 반응시킴으로써 수득될 수 있는 예비중합체를 포함하는 접착제 조성물에 대해 개시한다.That is, the following Patent Document 1 relates to an epoxy resin composition, (1) at least one epoxy resin, (2) at least one polyetherdiamine or polyethertriamine, particularly polyethertriamine, (3) at least one Disclosed is an adhesive composition comprising a prepolymer obtainable by reacting a carboxyl-terminated butadiene-acrylonitrile copolymer and (4) rubber particles having a core/shell structure.
그러나, 상술한 바와 같은 특허문헌 1은 에폭시 수지 조성물이 적용된 접착제에 대해 개시하고 있으나, 상온에서의 경화 여부는 알기 어려우며, 제조공정이 복잡한 문제점이 있다.However, although Patent Document 1 as described above discloses an adhesive to which an epoxy resin composition is applied, it is difficult to know whether curing at room temperature is achieved, and the manufacturing process is complicated.
본 발명은 신율 특성 및 기계적 물성이 우수한 상온 경화 이액형 실러를 제공하는 것을 목적으로 한다. An object of the present invention is to provide a room temperature curing two-component sealer having excellent elongation properties and mechanical properties.
발명의 목적은 이상에서 언급한 목적으로 제한되지 않는다. 본 발명의 목적은 이하의 설명으로 보다 분명해 질 것이며, 특허청구범위에 기재된 수단 및 그 조합으로 실현될 것이다.The object of the invention is not limited to the object mentioned above. The object of the present invention will become clearer from the following description, and will be realized by means and combinations thereof described in the claims.
본 발명의 일 실시예에 따른 상온 경화 이액형 실러는 지방산 변성 에폭시 수지 50~75중량%, 비스 페놀 A형 에폭시 수지 5~10중량%, 제1 충진제 15~25중량% 및 첨가제 0.5~3중량%를 포함하는 주제 및 지방족 변성 아민 수지 65~80중량%, 아민-터미네이티드 반응성 액상 고무 10~20중량% 및 제2 충진제 10~20중량%를 포함하는 경화제를 포함한다.A room temperature curing two-component sealer according to an embodiment of the present invention is 50 to 75 wt% of a fatty acid-modified epoxy resin, 5 to 10 wt% of a bisphenol A-type epoxy resin, 15 to 25 wt% of a first filler, and 0.5 to 3 wt% of an additive % of the main agent and aliphatic-modified amine resin, 65 to 80% by weight, amine-terminated reactive
본 발명의 일 실시예에 있어서, 상기 주제 및 경화제는 8~12:1 의 중량비로 배합될 수 있다.In one embodiment of the present invention, the main agent and the curing agent may be mixed in a weight ratio of 8 to 12:1.
본 발명의 일 실시예에 있어서, 상기 제1 충진제 및 제2 충진제는 무기질 충진제, 인편형상 무기질 충진제, 섬유 형상 무기질 충진제 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있다.In one embodiment of the present invention, the first filler and the second filler may be selected from the group consisting of inorganic fillers, scale-shaped inorganic fillers, fibrous inorganic fillers, and combinations thereof.
본 발명의 일 실시예에 있어서, 상기 무기질 충진제는 탄산칼슘, 카올린, 실리카, 탈크, 황산바륨, 알루미나, 산화철, 산화티탄, 탄산마그네슘, 수산화알루미늄, 규조토, 규회석, 클레이 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종이고, 상기 인편형상 무기질 충진제는 유리플레이크, 운모 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종이며, 상기 섬유 형상 무기질 충진제는 금속산화물 위스커, 유리 섬유 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종일 수 있다.In one embodiment of the present invention, the inorganic filler is calcium carbonate, kaolin, silica, talc, barium sulfate, alumina, iron oxide, titanium oxide, magnesium carbonate, aluminum hydroxide, diatomaceous earth, wollastonite, clay, and mixtures thereof. at least one selected from, the flaky inorganic filler is at least one selected from the group consisting of glass flakes, mica, and mixtures thereof, and the fibrous inorganic filler is a metal oxide whisker, glass fiber, and mixtures thereof. It may be at least one selected from the group consisting of.
본 발명의 일 실시예에 있어서, 상기 첨가제는 잠재성 경화제, 촉진제, 흐름방지제, 점도조절제, 소포제, 분사제 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있다.In one embodiment of the present invention, the additive may be selected from the group consisting of a latent curing agent, an accelerator, a flow inhibitor, a viscosity modifier, an antifoaming agent, a propellant, and combinations thereof.
본 발명의 일 실시예에 있어서, 상기 지방산 변성 에폭시 수지는 제1 에폭시 수지, 상기 제1 에폭시 수지와는 중첩되지 않는 에폭시 당량 범위를 갖는 제2 에폭시 수지 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있다.In one embodiment of the present invention, the fatty acid-modified epoxy resin may be selected from the group consisting of a first epoxy resin, a second epoxy resin having an epoxy equivalent range that does not overlap with the first epoxy resin, and combinations thereof. there is.
본 발명의 일 실시예에 있어서, 상기 제1 에폭시 수지의 에폭시 당량은 600~700g/eqiv이고, 상기 제2 에폭시 수지의 에폭시 당량은 400~500g/eqiv일 수 있다.In an embodiment of the present invention, the epoxy equivalent of the first epoxy resin may be 600 to 700 g/eqiv, and the epoxy equivalent of the second epoxy resin may be 400 to 500 g/eqiv.
본 발명의 일 실시예에 있어서, 상기 비스 페놀 A형 에폭시 수지의 에폭시 당량은 180~190g/eqiv일 수 있다.In one embodiment of the present invention, the epoxy equivalent of the bisphenol A type epoxy resin may be 180 ~ 190 g / eqiv.
본 발명의 일 실시예에 있어서, 상기 주제의 점도는 100,000~200,000cps일 수 있다.In one embodiment of the present invention, the viscosity of the subject may be 100,000 ~ 200,000 cps.
본 발명의 일 실시예에 있어서, 상기 지방족 변성 아민 수지의 아민 당량은 60~80g/eqiv일 수 있다.In one embodiment of the present invention, the amine equivalent weight of the aliphatic-modified amine resin may be 60 ~ 80 g / eqiv.
본 발명의 일 실시예에 있어서, 상기 아민-터미네이티드 반응성 액상 고무의 아민 당량은 800~1000g/eqiv일 수 있다.In an embodiment of the present invention, the amine equivalent of the amine-terminated reactive liquid rubber may be 800 to 1000 g/eqiv.
본 발명의 일 실시예에 있어서, 경화제의 점도는 50,000~100,000cps일 수 있다.In one embodiment of the present invention, the viscosity of the curing agent may be 50,000 ~ 100,000cps.
본 발명의 실시예에 따르면, 지방산 변성 에폭시를 활용한 주제 및 아민-터미네이티드 반응성 액상 고무를 포함하는 경화제를 혼합함으로써 신율 특성 및 기계적 물성이 우수한 상온 경화 이액형 실러를 제공할 수 있다. According to an embodiment of the present invention, a room temperature curing two-component sealer having excellent elongation properties and mechanical properties can be provided by mixing a curing agent including a main agent using a fatty acid-modified epoxy and an amine-terminated reactive liquid rubber.
도 1은 본 발명의 실험예1의 전단강도를 측정하기 위한 장치를 나타낸 도면이다.1 is a view showing an apparatus for measuring the shear strength of Experimental Example 1 of the present invention.
이상의 본 발명의 목적들, 다른 목적들, 특징들 및 이점들은 첨부된 도면과 관련된 이하의 바람직한 실시예들을 통해서 쉽게 이해될 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 통상의 기술자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다.The above objects, other objects, features and advantages of the present invention will be easily understood through the following preferred embodiments in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided so that the disclosed subject matter may be thorough and complete, and that the spirit of the present invention may be sufficiently conveyed to those skilled in the art.
각 도면을 설명하면서 유사한 참조부호를 유사한 구성요소에 대해 사용하였다. 첨부된 도면에 있어서, 구조물들의 치수는 본 발명의 명확성을 위하여 실제보다 확대하여 도시한 것이다. 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리 범위를 벗어나지 않으면서 제1 구성요소는 제2 구성요소로 명명될 수 있고, 유사하게 제2 구성요소도 제1 구성요소로 명명될 수 있다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다.In describing each figure, like reference numerals have been used for like elements. In the accompanying drawings, the dimensions of the structures are enlarged than the actual size for clarity of the present invention. Terms such as first, second, etc. may be used to describe various elements, but the elements should not be limited by the terms. The above terms are used only for the purpose of distinguishing one component from another. For example, without departing from the scope of the present invention, a first component may be referred to as a second component, and similarly, a second component may also be referred to as a first component. The singular expression includes the plural expression unless the context clearly dictates otherwise.
본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 또한, 층, 막, 영역, 판 등의 부분이 다른 부분 "상에" 있다고 할 경우, 이는 다른 부분 "바로 위에" 있는 경우뿐만 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다. 반대로 층, 막, 영역, 판 등의 부분이 다른 부분 "하부에" 있다고 할 경우, 이는 다른 부분 "바로 아래에" 있는 경우뿐만 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다.In this specification, terms such as "comprise" or "have" are intended to designate that a feature, number, step, operation, component, part, or a combination thereof described in the specification exists, but one or more other features It is to be understood that it does not preclude the possibility of the presence or addition of numbers, steps, operations, components, parts, or combinations thereof. Also, when a part of a layer, film, region, plate, etc. is said to be “on” another part, it includes not only the case where the other part is “directly on” but also the case where there is another part in between. Conversely, when a part, such as a layer, film, region, plate, etc., is "under" another part, this includes not only cases where it is "directly under" another part, but also a case where another part is in the middle.
달리 명시되지 않는 한, 본 명세서에서 사용된 성분, 반응 조건, 폴리머 조성물 및 배합물의 양을 표현하는 모든 숫자, 값 및/또는 표현은, 이러한 숫자들이 본질적으로 다른 것들 중에서 이러한 값을 얻는 데 발생하는 측정의 다양한 불확실성이 반영된 근사치들이므로, 모든 경우 "약"이라는 용어에 의해 수식되는 것으로 이해되어야 한다. 또한, 본 기재에서 수치범위가 개시되는 경우, 이러한 범위는 연속적이며, 달리 지적되지 않는 한 이러한 범 위의 최소값으로부터 최대값이 포함된 상기 최대값까지의 모든 값을 포함한다. 더 나아가, 이러한 범위가 정수를 지칭하는 경우, 달리 지적되지 않는 한 최소값으로부터 최대값이 포함된 상기 최대값까지를 포함하는 모든 정수가 포함된다.Unless otherwise specified, all numbers, values, and/or expressions expressing quantities of ingredients, reaction conditions, polymer compositions and formulations used herein, contain all numbers, values and/or expressions in which such numbers essentially occur in obtaining such values, among others. Since they are approximations reflecting various uncertainties in the measurement, it should be understood as being modified by the term "about" in all cases. Also, where the disclosure discloses numerical ranges, such ranges are continuous and inclusive of all values from the minimum to the maximum inclusive of the range, unless otherwise indicated. Furthermore, when such ranges refer to integers, all integers inclusive from the minimum to the maximum inclusive are included, unless otherwise indicated.
본 명세서에 있어서, 범위가 변수에 대해 기재되는 경우, 상기 변수는 상기 범위의 기재된 종료점들을 포함하는 기재된 범위 내의 모든 값들을 포함하는 것으로 이해될 것이다. 예를 들면, "5 내지 10"의 범위는 5, 6, 7, 8, 9, 및 10의 값들뿐만 아니라 6 내지 10, 7 내지 10, 6 내지 9, 7 내지 9 등의 임의의 하위 범위를 포함하고, 5.5, 6.5, 7.5, 5.5 내지 8.5 및 6.5 내지 9 등과 같은 기재된 범위의 범주에 타당한 정수들 사이의 임의의 값도 포함하는 것으로 이해될 것이다. 또한 예를 들면, "10% 내지 30%"의 범위는 10%, 11%, 12%, 13% 등의 값들과 30%까지를 포함하는 모든 정수들뿐만 아니라 10% 내지 15%, 12% 내지 18%, 20% 내지 30% 등의 임의의 하위 범위를 포함하고, 10.5%, 15.5%, 25.5% 등과 같이 기재된 범위의 범주 내의 타당한 정수들 사이의 임의의 값도 포함하는 것으로 이해될 것이다. In this specification, when a range is described for a variable, the variable will be understood to include all values within the stated range including the stated endpoints of the range. For example, a range of “5 to 10” includes the values of 5, 6, 7, 8, 9, and 10, as well as any subranges such as 6 to 10, 7 to 10, 6 to 9, 7 to 9, etc. It will be understood to include any value between integers that are appropriate for the scope of the recited range, such as 5.5, 6.5, 7.5, 5.5 to 8.5 and 6.5 to 9, and the like. Also for example, ranges from "10% to 30%" include values of 10%, 11%, 12%, 13%, etc. and all integers up to and including 30%, as well as 10% to 15%, 12% to It will be understood to include any subranges such as 18%, 20% to 30%, etc., as well as any value between reasonable integers within the scope of the recited ranges, such as 10.5%, 15.5%, 25.5%, and the like.
이하에서는, 본 발명의 상온 경화 이액형 실러에 대해서 상세하게 설명한다. Hereinafter, the room temperature curing two-component sealer of the present invention will be described in detail.
본 발명의 상온 경화 이액형 실러는 주제 및 경화제를 포함한다. 구체적으로, 상기 상온 경화 이액형 실러는 주제 및 경화제를 배합한 것이다.The room temperature curing two-component sealer of the present invention includes a main agent and a curing agent. Specifically, the room temperature curing two-component sealer is a mixture of a main agent and a curing agent.
우선, 상온 경화 이액형 실러의 주제의 성분 및 각 성분의 제한 사유를 설명한다. First, the main components of the room temperature curing two-component sealer and the reasons for limiting each component will be described.
주제는 지방산 변성 에폭시 수지 50~75중량%, 비스 페놀 A형 에폭시 수지 5~10중량%, 제1 충진제 15~25중량% 및 첨가제 0.5~3중량%를 포함하고, 이때, 점도는 100,000~200,000cps, 바람직하게는 130,000~170,000cps의 범위일 수 있다. 이는 100,000cps미만이면, 주제의 저점도로 인해 흐름성문제가 발생할 수 있으며, 주제보다 낮은 점도를 형성해야 하는 경화제의 조제가 어려울 수 있고, 200,000cps를 초과하면, 경화제와의 혼합성에 있어서 불량이 발생될 수 있다. 그러므로 점도는 경화제와의 혼합이 용이하도록 100,000~200,000cps으로 조절하는 것이 바람직하다. The main agent contains 50 to 75% by weight of a fatty acid-modified epoxy resin, 5 to 10% by weight of a bisphenol A type epoxy resin, 15 to 25% by weight of a first filler, and 0.5 to 3% by weight of an additive, wherein the viscosity is 100,000 to 200,000 cps, preferably in the range of 130,000 to 170,000 cps. If it is less than 100,000 cps, flow problems may occur due to the low viscosity of the main material, it may be difficult to prepare a curing agent that has to form a viscosity lower than the main material, and if it exceeds 200,000 cps, a failure may occur in miscibility with the curing agent. can Therefore, the viscosity is preferably adjusted to 100,000 ~ 200,000cps to facilitate mixing with the curing agent.
여기서, 중량%는 주제의 총 중량을 기준으로 한다.Here, weight percent is based on the total weight of the subject.
지방산 변성 에폭시 수지는 지방산과 에폭시 수지를 반응시켜 제조된다. 상세하게는 다이머 산(Dimer Acid) 및 범용 에폭시 수지의 합성 반응에 의해 제조된다. A fatty acid-modified epoxy resin is prepared by reacting a fatty acid with an epoxy resin. In detail, it is prepared by the synthesis reaction of a dimer acid and a general-purpose epoxy resin.
상기 지방산 변성 에폭시 수지는 에폭시 당량이 상이한 2이상의 지방산 변성에폭시 수지를 혼합할 수 있다. 상세하게는 제1 에폭시 수지, 제1 에폭시 수지와는 중첩되지 않는 에폭시 당량 범위를 갖는 제2 에폭시 수지 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있다. 이때, 제1 에폭시 수지의 에폭시 당량은 600~700g/eqiv이고, 제2 에폭시 수지의 에폭시 당량은 400~500g/eqiv일 수 있다. 이는 400g/eqiv미만이면, 작업하기는 수월하지만 경화 속도가 너무 빨라 부착 형태의 불량 발생률이 커질 수 있고, 700g/eqiv를 초과하면, 고형 에폭시로 작업하기가 매우 어려우므로 생산성이 저하될 수 있다. The fatty acid-modified epoxy resin may be mixed with two or more fatty acid-modified epoxy resins having different epoxy equivalents. Specifically, it may be selected from the group consisting of a first epoxy resin, a second epoxy resin having an epoxy equivalent range that does not overlap with the first epoxy resin, and combinations thereof. In this case, the epoxy equivalent of the first epoxy resin may be 600 to 700 g/eqiv, and the epoxy equivalent of the second epoxy resin may be 400 to 500 g/eqiv. If it is less than 400 g/eqiv, it is easy to work, but the curing rate is too fast and the incidence of defects in the adhesion form may increase. If it exceeds 700 g/eqiv, it is very difficult to work with solid epoxy, so productivity may be reduced.
또한, 당량이 큰 한 종류의 에폭시 수지만을 사용하게 되면, 경화속도가 너무 느리고, 당량이 낮은 한 종류의 에폭시 수지만을 사용하게 되면, 경화 속도가 너무 빠르며 부착 형태에 있어서 불량이 발생될 수 있다. 따라서, 양호하게 부착될 수 있도록 에폭시 당량이 상이한 2이상의 지방산 변성에폭시 수지를 혼합하여 사용하는 것이 바람직하다.In addition, if only one type of epoxy resin with a large equivalent is used, the curing rate is too slow, and if only one type of epoxy resin with a low equivalent is used, the curing rate is too fast and defects may occur in the attachment form. there is. Therefore, it is preferable to use a mixture of two or more fatty acid-modified epoxy resins having different epoxy equivalents so that they can be adhered well.
상기 에폭시 당량(epoxy equivalent weight)은 1당량의 에폭시기를 포함하는 수지의 g수를 의미한다.The epoxy equivalent weight means the number of g of a resin including one equivalent of an epoxy group.
지방산 변성 에폭시 수지는 주제 100중량%에 대하여, 50~75중량%, 바람직하게는 50~70중량%로 포함될 수 있다. 이는 50중량% 미만이면, 신율 특성을 확보하기가 어렵고 점도가 높아져 작업성이 불량한 문제가 발생할 수 있고, 75중량%를 초과하면, 점도가 낮아져 작업성이 불량해 질 수 있으며, 접착력이 떨어질 수 있다. 따라서, 본 발명에서 요구되는 신율을 확보하면서 작업이 용이하게 실시될 수 있도록 50~75중량%로 포함되는 것이 바람직하다.The fatty acid-modified epoxy resin may be included in an amount of 50 to 75% by weight, preferably 50 to 70% by weight, based on 100% by weight of the main agent. If it is less than 50% by weight, it is difficult to secure the elongation properties and the viscosity may be high, which may cause a problem of poor workability. there is. Therefore, it is preferably included in an amount of 50 to 75% by weight so that the operation can be easily carried out while ensuring the elongation required in the present invention.
비스 페놀 A형 에폭시 수지는 에폭시 당량(epoxy equivalent weight)이 185~190g/eqiv인 범용 에폭시로, 주제 100중량%에 대하여, 5~10중량%로 포함될 수 있다. 이는 5중량% 미만이면, 접착 불량이 발생될 수 있고, 10중량%를 초과하면, 딱딱한 성질이 살아나며, 이에 신율 특성에 악영향을 미칠 수 있다. Bisphenol A type epoxy resin is a general-purpose epoxy having an epoxy equivalent weight of 185 to 190 g/eqiv, and may be included in an amount of 5 to 10% by weight based on 100% by weight of the main ingredient. If it is less than 5% by weight, adhesion failure may occur, and if it exceeds 10% by weight, hard properties will be revived, which may adversely affect elongation properties.
상기 에폭시 당량(epoxy equivalent weight)은 1당량의 에폭시기를 포함하는 수지의 g수를 의미한다.The epoxy equivalent weight means the number of g of a resin including one equivalent of an epoxy group.
제1 충진제는 무기질 충진제, 인편형상 무기질 충진제, 섬유 형상 무기질 충진제 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있으며, 바람직하게는 무기질 충진제일 수 있다. 예를 들어, 무기질 충진제는 탄산칼슘, 카올린, 실리카, 탈크, 황산바륨, 알루미나, 산화철, 산화티탄, 탄산마그네슘, 수산화알루미늄, 규조토, 규회석, 클레이 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있고, 인편형상 무기질 충진제는 유리플레이크, 운모 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있으며, 섬유 형상 무기질 충진제는 금속산화물 위스커, 유리 섬유 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있다.The first filler may be selected from the group consisting of inorganic fillers, scale-like inorganic fillers, fibrous inorganic fillers, and combinations thereof, and may preferably be inorganic fillers. For example, the inorganic filler may be one selected from the group consisting of calcium carbonate, kaolin, silica, talc, barium sulfate, alumina, iron oxide, titanium oxide, magnesium carbonate, aluminum hydroxide, diatomaceous earth, wollastonite, clay, and mixtures thereof. And, the scale-shaped inorganic filler may be one selected from the group consisting of glass flakes, mica, and mixtures thereof, and the fibrous inorganic filler may be one selected from the group consisting of metal oxide whiskers, glass fibers, and mixtures thereof. there is.
상기 제1 충진제는 주제100중량%에 대하여, 15~25중량%로 포함될 수 있다. 이는 15중량% 미만이면, 점도가 낮아 작업성이 불량할 수 있고, 25중량%를 초과하면, 점도와 비중이 높아지는 현상이 발생되어 작업성이 불량해질 수 있다.The first filler may be included in an amount of 15 to 25% by weight based on 100% by weight of the main material. If it is less than 15% by weight, the viscosity may be low and workability may be poor.
첨가제는 잠재성 경화제, 촉진제, 흐름방지제, 점도조절제, 소포제, 분사제 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있다. 첨가제는 주제 100중량%에 대하여, 0.5~3중량%로 포함될 수 있다. 이는 0.5중량% 미만이면, 에폭시 경화가 제대로 이루어지기 어렵고, 3중량%를 초과하면, 에폭시가 과경화될 수 있으며, 이에 신율 특성 및 부착성에 악영향을 미칠 수 있다.The additive may be selected from the group consisting of latent curing agents, accelerators, flow inhibitors, viscosity modifiers, defoamers, propellants, and combinations thereof. The additive may be included in an amount of 0.5 to 3% by weight based on 100% by weight of the main agent. If it is less than 0.5% by weight, it is difficult to properly cure the epoxy, and if it exceeds 3% by weight, the epoxy may be overcured, which may adversely affect elongation properties and adhesion.
다음으로, 상온 경화 이액형 실러의 경화제의 성분 및 각 성분의 제한사유를 설명한다.Next, the components of the curing agent of the room temperature curing two-component sealer and reasons for limitation of each component will be described.
경화제는 지방족 변성 아민 수지 65~80중량%, 아민-터미네이티드 반응성 액상 고무 10~20중량% 및 제2 충진제 10~20중량%를 포함하고, 이때, 점도는 50,000~100,000cps, 바람직하게는 60,000~80,000cps의 범위일 수 있다. 이는 50,000cps미만이면, 칙소성에 문제가 발생하여 정확한 양의 투입이 어려울 뿐만 아니라 흐름성 및 경화제의 조제가 어려울 수 있고, 100,000cps를 초과하면, 주제보다 적은 양 사용되는 경화제가 주제보다 점도가 커져 주제와의 혼합이 어려울 수 있다. 여기서, 중량%는 경화제의 총 중량을 기준으로 한다.The curing agent includes 65 to 80% by weight of an aliphatic modified amine resin, 10 to 20% by weight of an amine-terminated reactive liquid rubber, and 10 to 20% by weight of a second filler, wherein the viscosity is 50,000 to 100,000cps, preferably It can range from 60,000 to 80,000 cps. If it is less than 50,000cps, there may be a problem in thixotropy, making it difficult to inject an accurate amount, as well as difficult to prepare flowability and curing agent, If it exceeds 100,000cps, the curing agent used in a smaller amount than the main agent may have a greater viscosity than the main agent, and mixing with the main agent may be difficult. Here, the weight percent is based on the total weight of the curing agent.
지방산 변성 아민 수지에서 아민 당량은 신율과 상온 경화 속도에 영향을 미치는 요소로, 60~80g/eqiv의 범위일 수 있다. 당량이 60g/eqiv 미만이면, 상온 경화 속도는 빨라지나 신율 특성이 나빠질 수 있고, 80g/eqiv를 초과하면, 신율 특성은 좋아지나 상온 경화 속도가 느려질 수 있다. 따라서 본 발명에서 요구되는 신율 특성 및 상온 경화 속도를 만족할 수 있도록 아민 당량은 60~80g/eqiv의 범위로 포함됨이 바람직하다. 상기 아민 당량(amine equivalent weight)은 1당량의 아민기를 포함하는 수지의 g수를 의미한다.In the fatty acid-modified amine resin, the amine equivalent weight is a factor affecting elongation and curing rate at room temperature, and may be in the range of 60 to 80 g/eqiv. If the equivalent weight is less than 60 g/eqiv, the curing rate at room temperature may be increased but the elongation property may be deteriorated, and if it exceeds 80 g/eqiv, the elongation property may be improved but the room temperature curing speed may be slow. Therefore, it is preferable that the amine equivalent is included in the range of 60 to 80 g/eqiv so as to satisfy the elongation properties and the curing rate at room temperature required in the present invention. The amine equivalent weight means the number of g of a resin including 1 equivalent of an amine group.
상기 지방산 변성 아민 수지는 경화제 100중량%에 대하여, 65~80중량%로 포함될 수 있다. 이는 65중량% 미만이면, 상온 경화가 이루어지는데 시간이 길어질 뿐만 아니라 작업환경이 나빠질 수 있고, 80중량%를 초과하면, 경화 시간이 짧아지므로 인해 부착성이 불량해질 수 있다.The fatty acid-modified amine resin may be included in an amount of 65 to 80% by weight based on 100% by weight of the curing agent. If it is less than 65% by weight, it may take a long time to cure at room temperature, as well as deteriorate the working environment, and if it exceeds 80% by weight, the curing time may be shortened, so adhesion may be poor.
아민-터미네이티드 반응성 액상 고무는 ATBN(amine-terminated butadiene acrylonitrile rubber), ATB(amine-terminated butadiene) 및 이들의 조합으로 이루어진 군으로부터 선택될 수 있으며, 바람직하게는 ATBN(amine-terminated butadiene acrylonitrile rubber)일 수 있다. The amine-terminated reactive liquid rubber may be selected from the group consisting of amine-terminated butadiene acrylonitrile rubber (ATBN), amine-terminated butadiene (ATB), and combinations thereof, preferably amine-terminated butadiene acrylonitrile rubber (ATBN). ) can be
아민-터미네이티드 반응성 액상 고무의 아민 당량은 800~1,000g/eqiv의 범위일 수 있다. 다만, 본 발명에서 아민-터미네이티드 반응성 액상 고무의 아민 당량은 높을수록 좋다. 그러나, 고 아민 당량의 아민-터미네이티드 반응성 액상 고무를 사용할 경우, 경화 시간이 길어지는 문제점이 발생될 수 있으므로 그 함량을 조절하는 것이 바람직하다. 상기 아민 당량(amine equivalent weight)은 1당량의 아민기를 포함하는 수지의 g수를 의미한다.The amine equivalent weight of the amine-terminated reactive liquid rubber may be in the range of 800 to 1,000 g/eqiv. However, in the present invention, the higher the amine equivalent of the amine-terminated reactive liquid rubber, the better. However, when an amine-terminated reactive liquid rubber having a high amine equivalent weight is used, the curing time may be prolonged, so it is preferable to control the content thereof. The amine equivalent weight means the number of g of a resin including 1 equivalent of an amine group.
상기 아민-터미네이티드 반응성 액상 고무는 경화제 100중량%에 대하여, 10~20중량%로 포함될 수 있다. 이는 10중량% 미만이면, 신율 특성을 확보하기 어렵고, 20중량%를 초과하면, 상온경화 속도가 너무 길어져 작업환경이 나빠질 수 있다.The amine-terminated reactive liquid rubber may be included in an amount of 10 to 20% by weight based on 100% by weight of the curing agent. If it is less than 10% by weight, it is difficult to secure the elongation characteristics, and if it exceeds 20% by weight, the room temperature curing rate becomes too long and the working environment may deteriorate.
제2 충진제는 무기질 충진제, 인편형상 무기질 충진제 또는 섬유 형상 무기질 충진제를 포함하며, 바람직하게는 무기질 충진제를 포함할 수 있다. 예를 들어, 무기질 충진제는 탄산칼슘, 카올린, 실리카, 탈크, 황산바륨, 알루미나, 산화철, 산화티탄, 탄산마그네슘, 수산화알루미늄, 규조토, 규회석, 클레이 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있고, 인편형상 무기질 충진제는 유리플레이크, 운모 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있으며, 섬유 형상 무기질 충진제는 금속산화물 위스커, 유리 섬유 및 이들의 혼합물로 이루어진 군으로부터 선택되는 1종일 수 있다.The second filler includes an inorganic filler, a scale-like inorganic filler, or a fibrous inorganic filler, and may preferably include an inorganic filler. For example, the inorganic filler may be one selected from the group consisting of calcium carbonate, kaolin, silica, talc, barium sulfate, alumina, iron oxide, titanium oxide, magnesium carbonate, aluminum hydroxide, diatomaceous earth, wollastonite, clay, and mixtures thereof. And, the scale-shaped inorganic filler may be one selected from the group consisting of glass flakes, mica, and mixtures thereof, and the fibrous inorganic filler may be one selected from the group consisting of metal oxide whiskers, glass fibers, and mixtures thereof. there is.
상기 제2 충진제는 경화제 100중량%에 대하여, 10~20중량%로 포함될 수 있다. 이는 10중량% 미만이면, 점도가 낮아 작업성이 불량 또는 저하될 수 있고, 20중량%를 초과하면, 점도가 높아져 주제와의 혼합이 어려울 수 있다. 따라서, 제2 충진제는 주제와의 혼합이 용이하면서 작업성이 향상될 수 있도록 10~20중량%로 포함되는 것이 바람직하다.The second filler may be included in an amount of 10 to 20% by weight based on 100% by weight of the curing agent. If it is less than 10% by weight, the viscosity may be low and workability may be poor or deteriorated, and if it exceeds 20% by weight, the viscosity may increase and mixing with the main agent may be difficult. Therefore, it is preferable that the second filler be included in an amount of 10 to 20% by weight so that it can be easily mixed with the main agent and workability can be improved.
상술한 바와 같은 상온 경화 이액형 실러는 주제 및 경화제가 8~12:1, 바람직하게는 10:1 의 중량비로 배합될 수 있다. 이는 주제가 8미만이면, 경도가 너무 강해 신율에 문제가 발생될 수 있고, 주제가 12를 초과하면, 경화되는 속도가 느려져 흐름성 및 부착성이 나빠질 수 있다. In the room temperature curing two-component sealer as described above, the main agent and the curing agent may be mixed in a weight ratio of 8 to 12:1, preferably 10:1. If the main material is less than 8, the hardness is too strong and a problem may occur in elongation.
또한, 본 발명의 상온 경화 이액형 실러는 지방산 변성 에폭시를 활용한 주제 및 아민-터미네이티드 반응성 액상 고무를 포함하는 경화제를 혼합함으로써 높은 신율 및 우수한 접착 강도의 확보가 가능하여 도장실러가 도포되지 못하고 벌어져 있는 틈새를 긴밀한 밀폐할 수 있는 우수한 효과가 유도될 수 있다.In addition, the room temperature curing two-component sealer of the present invention can secure high elongation and excellent adhesive strength by mixing a curing agent containing a main agent using fatty acid-modified epoxy and an amine-terminated reactive liquid rubber, so that the paint sealer is not applied. An excellent effect of tightly sealing the gaps and gaps can be induced.
제조예 1-1. 주제(1)의 제조Preparation Example 1-1. Preparation of subject (1)
하기 표 1에 개시된 성분 및 함량으로 각각 혼합하여 주제(1)을 제조하였다.Subject (1) was prepared by mixing each of the ingredients and contents shown in Table 1 below.
표 1은 주제(1)의 성분 및 함량(중량%)을 나타낸 표이다.Table 1 is a table showing the components and content (% by weight) of the subject (1).
제조예 1-2. 주제(2)의 제조Preparation 1-2. Preparation of subject (2)
하기 표 2에 개시된 성분 및 함량으로 각각 혼합하여 주제(2)를 제조하였다.Subject (2) was prepared by mixing each of the ingredients and contents disclosed in Table 2 below.
표 2는 주제(2)의 성분 및 함량(중량%)을 나타낸 표이다.Table 2 is a table showing the components and content (% by weight) of the subject (2).
제조예 1-3. 주제(3)의 제조Preparation Example 1-3. Preparation of subject (3)
하기 표 3에 개시된 성분 및 함량으로 각각 혼합하여 주제(3)을 제조하였다.Subject (3) was prepared by mixing each of the ingredients and contents disclosed in Table 3 below.
표 3은 주제(3)의 성분 및 함량(중량%)을 나타낸 표이다.Table 3 is a table showing the components and content (% by weight) of the subject (3).
제조예 1-4. 주제(4)의 제조Preparation Example 1-4. Preparation of subject (4)
하기 표 4에 개시된 성분 및 함량으로 각각 혼합하여 주제(4)를 제조하였다.Subject (4) was prepared by mixing each of the ingredients and contents disclosed in Table 4 below.
표 4는 주제(4)의 성분 및 함량(중량%)을 나타낸 표이다.Table 4 is a table showing the components and content (% by weight) of the subject (4).
제조예 1-5. 주제(5)의 제조Preparation Example 1-5. Preparation of subject (5)
하기 표 5에 개시된 성분 및 함량으로 각각 혼합하여 주제(5)을 제조하였다.Subject (5) was prepared by mixing each of the ingredients and contents shown in Table 5 below.
표 5은 주제(1)의 성분 및 함량(중량%)을 나타낸 표이다.Table 5 is a table showing the components and content (% by weight) of the subject (1).
제조예 2. 경화제의 제조Preparation Example 2. Preparation of curing agent
하기 표 6에 개시된 성분 및 함량으로 각각 혼합하여 경화제를 제조하였다.A curing agent was prepared by mixing each of the components and contents disclosed in Table 6 below.
표 6은 경화제의 성분 및 함량(중량%)을 나타낸 표이다.Table 6 is a table showing the components and content (% by weight) of the curing agent.
실시예 1. 상온 경화 이액형 실러의 제조Example 1. Preparation of room temperature curing two-component sealer
제조예 1-1에서 제조된 주제(1)과 제조예 2에서 제조된 경화제를 10:1의 중량비로 혼합 및 교반하여 실시예 1의 상온 경화 이액형 실러를 제조하였다.The room temperature curing two-component sealer of Example 1 was prepared by mixing and stirring the main agent (1) prepared in Preparation Example 1-1 and the curing agent prepared in Preparation Example 2 in a weight ratio of 10:1.
비교예 1~9. 상온 경화 이액형 실러의 제조Comparative Examples 1 to 9. Manufacture of room temperature curing two-component sealer
하기 표 2에 개시된 배합비로 각각 혼합하여 비교예 1~9의 상온 경화 이액형 실러를 제조하였다.The room temperature curing two-component sealers of Comparative Examples 1 to 9 were prepared by mixing them at the mixing ratios shown in Table 2 below.
표 7은 비교예 1~9의 상온 경화 이액형 실러에서 각각의 주제 및 경화제의 배합 중량비를 나타낸 표이다.Table 7 is a table showing the mixing weight ratio of each main agent and curing agent in the room temperature curing two-component sealer of Comparative Examples 1 to 9.
실험예 1. 상온 경화 이액형 실러의 물성 특성Experimental Example 1. Physical properties of room temperature curing two-component sealer
본원발명에 따른 실시예 1 및 비교예 1 내지 비교예 9에서 수득한 상온 경화 이액형 실러의 물성 특성을 평가하기 위하여 하기와 같이 실험을 실시하였다. In order to evaluate the physical properties of the room temperature curing two-component sealer obtained in Example 1 and Comparative Examples 1 to 9 according to the present invention, an experiment was conducted as follows.
지촉건조는 막대 온도계를 이용하여 막대 온도계에 상온 경화 이액형 실러가 묻어나지 않을 때까지 걸리는 시간을 측정하였다. For dry to touch, the time it takes until the room temperature curing two-component sealer does not stick to the bar thermometer was measured using a bar thermometer.
도 1은 전단강도를 측정하기 위한 장치를 나타낸 도면이다.1 is a view showing an apparatus for measuring shear strength.
도 1에 도시된 (a), (b)에 각각 실시예 1 및 비교예 1 내지 비교예 9를 도포하고, 이를 160℃에서 20분 동안 경화한 다음 상온에서 1시간 동안 방지한 후, 테스트 장비(UTM)를 이용하여 접착면의 파단 시 강도를 측정하였다.After applying Example 1 and Comparative Examples 1 to 9, respectively, to (a) and (b) shown in FIG. 1 , and curing it at 160° C. for 20 minutes, and preventing it at room temperature for 1 hour, test equipment (UTM) was used to measure the strength at break of the adhesive surface.
또한, 아령 2호형으로 양각 ?돛슉? 테프론판을 이형지 또는 접착이 되지 않는 판 위에 고정시킨 후, 실시예 1 및 비교예 1 내지 비교예 9를 각각 양각 뚫린 곳에 기포가 들어가지 않도록 채워 지촉건조 시간 동안 방치하였다. 그 다음 160℃에서 20분 동안 경화하여 실러가 식은 후에 양각판을 분리하여 테스트 장비(UTM)로 신율을 측정하였다.Also, embossed with dumbbell No. 2 ?Sailshun? After fixing the Teflon plate on the release paper or the non-adhesive plate, Example 1 and Comparative Examples 1 to 9 were filled in each embossed hole to prevent air bubbles from entering and left to dry to the touch. Then, it was cured at 160° C. for 20 minutes, and after the sealer cooled, the embossed plate was removed and the elongation was measured with a test equipment (UTM).
표 8은 본 발명의 목표 범위를 나타낸 표이다. Table 8 is a table showing the target range of the present invention.
표 9는 본 발명에 따른 실시예 1 및 비교예 1 내지 비교예 9의 신율, 지촉건조 및 전단강도의 측정 결과를 나타낸 표이다. Table 9 is a table showing the measurement results of the elongation, dry to touch, and shear strength of Example 1 and Comparative Examples 1 to 9 according to the present invention.
그 결과, 표 9를 참고하면, 실시예 1의 물성이 전반적으로 우수하나 특히, 신율이 비교예 1 내지 비교예 9에 비해 매우 높다는 것을 확인할 수 있었다. As a result, referring to Table 9, it was confirmed that the physical properties of Example 1 were generally excellent, but in particular, the elongation was very high compared to Comparative Examples 1 to 9.
실시예 1의 신율 및 접착 강도가 우수한 것으로 미루어 도장실러가 도포되지 못하고 벌어져 있는 틈새의 긴밀한 밀폐가 가능하여 유수를 방지할 수 있는 효과가 유도될 수 있음을 짐작할 수 있었다.Considering that the elongation and adhesive strength of Example 1 were excellent, it could be inferred that the paint sealer could not be applied and the gap could be tightly sealed, which could lead to the effect of preventing running water.
이상 본 발명자에 의해서 이루어진 발명을 상기 실시 예에 따라 구체적으로 설명하였지만, 본 발명은 상기 실시 예에 한정되는 것은 아니고 그 요지를 이탈하지 않는 범위에서 여러 가지로 변경 가능한 것은 물론이다. Although the invention made by the present inventors has been described in detail according to the above embodiments, the present invention is not limited to the above embodiments and various modifications can be made without departing from the gist of the present invention.
Claims (12)
지방족 변성 아민 수지 65~80중량%, 아민-터미네이티드 반응성 액상 고무 10~20중량% 및 제2 충진제 10~20중량%를 포함하는 경화제;를 포함하는 상온 경화 이액형 실러.
A main agent comprising 50 to 75% by weight of a fatty acid-modified epoxy resin, 5 to 10% by weight of a bisphenol A type epoxy resin, 15 to 25% by weight of a first filler, and 0.5 to 3% by weight of an additive; and
A curing agent comprising 65 to 80% by weight of an aliphatic-modified amine resin, 10 to 20% by weight of an amine-terminated reactive liquid rubber, and 10 to 20% by weight of a second filler; A room temperature curing two-component sealer comprising.
상기 주제 및 경화제는 8~12:1의 중량비로 배합되는 상온 경화 이액형 실러.
According to claim 1,
A room temperature curing two-component sealer in which the main agent and the curing agent are mixed in a weight ratio of 8 to 12:1.
상기 제1 충진제 및 제2 충진제는 무기질 충진제, 인편형상 무기질 충진제, 섬유 형상 무기질 충진제 및 이들의 조합으로 이루어진 군으로부터 선택되는 상온 경화 이액형 실러.
According to claim 1,
The first and second fillers are room temperature curing two-component sealer selected from the group consisting of inorganic fillers, scale-shaped inorganic fillers, fibrous inorganic fillers, and combinations thereof.
상기 무기질 충진제는 탄산칼슘, 카올린, 실리카, 탈크, 황산바륨, 알루미나, 산화철, 산화티탄, 탄산마그네슘, 수산화알루미늄, 규조토, 규회석, 클레이 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종이고,
상기 인편형상 무기질 충진제는 유리플레이크, 운모 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종이며,
상기 섬유 형상 무기질 충진제는 금속산화물 위스커, 유리 섬유 및 이들의 혼합물로 이루어진 군으로부터 선택되는 적어도 1종인 상온 경화 이액형 실러.
4. The method of claim 3,
The inorganic filler is at least one selected from the group consisting of calcium carbonate, kaolin, silica, talc, barium sulfate, alumina, iron oxide, titanium oxide, magnesium carbonate, aluminum hydroxide, diatomaceous earth, wollastonite, clay, and mixtures thereof,
The scale-like inorganic filler is at least one selected from the group consisting of glass flakes, mica, and mixtures thereof,
The fibrous inorganic filler is at least one selected from the group consisting of metal oxide whiskers, glass fibers, and mixtures thereof.
상기 첨가제는 잠재성 경화제, 촉진제, 흐름방지제, 점도조절제, 소포제, 분사제 및 이들의 조합으로 이루어진 군으로부터 선택되는 상온 경화 이액형 실러.
According to claim 1,
The additive is a room temperature curing two-component sealer selected from the group consisting of a latent curing agent, an accelerator, a flow inhibitor, a viscosity modifier, an antifoaming agent, a propellant, and combinations thereof.
상기 지방산 변성 에폭시 수지는 제1 에폭시 수지,
상기 제1 에폭시 수지와는 중첩되지 않는 에폭시 당량 범위를 갖는 제2 에폭시 수지 및 이들의 조합으로 이루어진 군으로부터 선택되는 상온 경화 이액형 실러.
According to claim 1,
The fatty acid-modified epoxy resin is a first epoxy resin,
A room temperature curing two-component sealer selected from the group consisting of a second epoxy resin having an epoxy equivalent range that does not overlap with the first epoxy resin, and combinations thereof.
상기 제1 에폭시 수지의 에폭시 당량은 600~700g/eqiv이고, 상기 제2 에폭시 수지의 에폭시 당량은 400~500g/eqiv인 상온 경화 이액형 실러.
7. The method of claim 6,
The epoxy equivalent of the first epoxy resin is 600 ~ 700 g / eqiv, and the epoxy equivalent of the second epoxy resin is 400 ~ 500 g / eqiv room temperature curing two-component sealer.
상기 비스 페놀 A형 에폭시 수지의 에폭시 당량은 180~190g/eqiv인 상온 경화 이액형 실러.
According to claim 1,
The epoxy equivalent of the bisphenol A type epoxy resin is 180 ~ 190 g / eqiv room temperature curing two-component sealer.
상기 주제의 점도는 100,000~200,000cps인 상온 경화 이액형 실러.
According to claim 1,
The viscosity of the subject is 100,000 to 200,000 cps room temperature curing two-component sealer.
상기 지방족 변성 아민 수지의 아민 당량은 60~80g/eqiv인 상온 경화 이액형 실러.
According to claim 1,
An amine equivalent of the aliphatic-modified amine resin is 60 to 80 g/eqiv of room temperature curing two-component sealer.
상기 아민-터미네이티드 반응성 액상 고무의 아민 당량은 800~1000g/eqiv인 상온 경화 이액형 실러.
According to claim 1,
The amine-terminated reactive liquid rubber has an amine equivalent weight of 800 to 1000 g/eqiv.
상기 경화제의 점도는 50,000~100,000cps인 상온 경화 이액형 실러.
According to claim 1,
The viscosity of the curing agent is room temperature curing two-component sealer of 50,000 ~ 100,000cps.