KR102372851B1 - Reflection screen and method for manufacturing the same - Google Patents

Reflection screen and method for manufacturing the same Download PDF

Info

Publication number
KR102372851B1
KR102372851B1 KR1020140191044A KR20140191044A KR102372851B1 KR 102372851 B1 KR102372851 B1 KR 102372851B1 KR 1020140191044 A KR1020140191044 A KR 1020140191044A KR 20140191044 A KR20140191044 A KR 20140191044A KR 102372851 B1 KR102372851 B1 KR 102372851B1
Authority
KR
South Korea
Prior art keywords
reflective layer
layer
colored
lens
black
Prior art date
Application number
KR1020140191044A
Other languages
Korean (ko)
Other versions
KR20160079536A (en
Inventor
강보경
김영성
김성태
김진범
조훈
Original Assignee
엘지전자 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지전자 주식회사 filed Critical 엘지전자 주식회사
Priority to KR1020140191044A priority Critical patent/KR102372851B1/en
Publication of KR20160079536A publication Critical patent/KR20160079536A/en
Application granted granted Critical
Publication of KR102372851B1 publication Critical patent/KR102372851B1/en

Abstract

상기와 같은 기술적 과제를 해결하기 위해, 본 발명의 일 실시 예에 따른 반사형 스크린은 보호층에 형성되는 확산층, 상기 확산층에 형성되는 렌즈, 상기 렌즈에 형성되고, 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층, 상기 착색반사층에 형성되고, 상기 영상 중 상기 착색반사층을 투과하여도달한 영상을 반사시키는 반사층, 및 상기 반사층에 형성되는 코팅층을 포함할 수 있다.In order to solve the above technical problems, the reflective screen according to an embodiment of the present invention includes a diffusion layer formed on a protective layer, a lens formed on the diffusion layer, a lens formed on the lens, and absorbs external light incident from the surroundings. , a colored reflective layer that reflects an image incident from the projector, a reflective layer that is formed on the colored reflective layer and reflects an image that has passed through the colored reflective layer among the images, and a coating layer formed on the reflective layer.

Description

반사형 스크린 및 그 제조방법{REFLECTION SCREEN AND METHOD FOR MANUFACTURING THE SAME}Reflective screen and manufacturing method thereof

본 발명은 반사형 스크린 및 그 제조방법에 관한 것이다.
The present invention relates to a reflective screen and a method for manufacturing the same.

프로젝터는 스크린에 영상을 출력하고 사용자는 스크린에 반사된 빛을 통하여, 해당 영상을 시각적으로 제공받는다. 입사각과 반사각은 대칭적으로 나타나므로, 종래와 같이 먼 거리에서 영상을 출력하는 방식의 프로젝터를 이용할 때에는 프로젝터에서 출력된 영상이 스크린에 반사되어 적절히 사용자에게 전달될 수 있었다.The projector outputs an image to the screen, and the user is visually provided with the image through the light reflected on the screen. Since the angle of incidence and the angle of reflection appear symmetrically, when using a projector that outputs an image from a long distance as in the prior art, the image output from the projector is reflected on the screen and can be appropriately transmitted to the user.

그러나, 최근에는 프로젝터가 출력하는 영상의 투사거리가 짧으면서도, 큰 화면을 구성할 수 있는 단초점 프로젝터가 점점 늘어나는 추세에 있다. 이러한 단초점 프로젝터의 경우, 스크린과 상대적으로 가까운 거리에서 영상을 출력하기 때문에, 입사각이 종래의 프로젝터 방식에 비해 크다. 그리고 입사각이 크기 때문에, 스크린에서 반사되는 반사각도 커지게 된다. 그 결과, 반사된 대부분의 빛이 사용자의 눈으로 제공되는 것이 아니라, 천장 쪽으로 반사되어 사용자는 매우 어두운 영상을 시청하게 되는 문제가 발생하고 있다. However, in recent years, the number of short-throw projectors capable of configuring a large screen while having a short projection distance of an image output by the projector has been increasing. In the case of such a short throw projector, since an image is output at a relatively close distance to the screen, the angle of incidence is larger than that of the conventional projector. And since the angle of incidence is large, the angle of reflection reflected from the screen is also increased. As a result, most of the reflected light is not provided to the user's eyes, but is reflected toward the ceiling, resulting in a problem that the user views a very dark image.

이를 해결하기 위한 방안으로, 스크린 표면에 착색층 렌즈 및 반사층을 구비한 스크린이 제작되었다. 구체적으로, 착색층, 렌즈 및 반사층을 구비한 스크린은 프로젝터에서 출력된 영상이 시청자에게 올바르게 제공되도록 하고, 주변의 외광은 흡수하거나 경로를 바꾸어 반사되는 영상의 명암비(특히, 명실명암비)를 향상시킨다. As a solution to this problem, a screen having a colored lens and a reflective layer on the surface of the screen was manufactured. Specifically, a screen having a coloring layer, a lens, and a reflective layer ensures that the image output from the projector is correctly provided to the viewer, and the external light is absorbed or changes the path to improve the contrast ratio (especially the contrast ratio) of the reflected image. .

그러나, 위와 같은 구성에 따른 스크린에 포함된 착색층은 주변의 외광 뿐만 아니라 프로젝터에서 출력된 영상까지 흡수하는 문제점이 있고, 착색층을 형성함에 있어서, 다른 공정과 구분되는 공정의 단계 및 제조 비용이 증가하는 문제점이 있다. 이와 더불어, 여러 층에 따른 일정 수준 이상의 두께로 인해서, 롤링으로 스크린을 형성하기에 한계가 있다.
However, the colored layer included in the screen according to the above configuration has a problem in that it absorbs not only the ambient external light but also the image output from the projector, There is a growing problem. In addition, due to the thickness of a certain level or more according to the various layers, there is a limit to forming the screen by rolling.

본 발명의 목적은 외광은 흡수하고, 프로젝터의 영상은 반사시키는 착색반사층을 구비하는 반사형 스크린 및 그 제조방법을 제공하는 데 있다.An object of the present invention is to provide a reflective screen having a colored reflective layer that absorbs external light and reflects an image of a projector, and a method for manufacturing the same.

본 발명의 다른 목적은 반사층을 형성하는 공정과 동일한 공정으로 형성되는 착색반사층을 구비하는 반사형 스크린 및 그 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a reflective screen including a colored reflective layer formed by the same process as the process for forming the reflective layer, and a method for manufacturing the same.

본 발명의 또 다른 목적은 구조의 단순화로 두께를 감소시켜 롤링으로 형성이 가능한 반사형 스크린 및 그 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a reflective screen that can be formed by rolling by reducing the thickness by simplifying the structure and a method for manufacturing the same.

본 발명의 또 다른 목적은 외광의 흡수에 따른 블랙휘도를 감소시키고, 명실명암비를 증가시키는 반사형 스크린 및 그 제조방법을 제공하는 데 있다.
Another object of the present invention is to provide a reflective screen that reduces black luminance due to absorption of external light and increases the bright-to-brightness ratio, and a method for manufacturing the same.

상기와 같은 기술적 과제를 해결하기 위해, 본 발명의 일 실시 예에 따른 반사형 스크린은 보호층에 형성되는 확산층, 상기 확산층에 형성되는 렌즈, 상기 렌즈에 형성되고, 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층, 상기 착색반사층에 형성되고, 상기 영상 중 상기 착색반사층을 투과하여 도달한 영상을 반사시키는 반사층, 및 상기 반사층에 형성되는 코팅층을 포함할 수 있다.In order to solve the above technical problems, the reflective screen according to an embodiment of the present invention includes a diffusion layer formed on a protective layer, a lens formed on the diffusion layer, a lens formed on the lens, and absorbs external light incident from the surroundings. , a colored reflective layer that reflects an image incident from the projector, a reflective layer that is formed on the colored reflective layer and reflects an image that has passed through the colored reflective layer among the images, and a coating layer formed on the reflective layer.

실시 예에 있어서, 상기 착색반사층은 블랙이면서 반사율이 일정 수준 이상인 블랙실버로 형성될 수 있다.In an embodiment, the colored reflective layer may be formed of black silver having a reflectance of a certain level or higher while being black.

실시 예에 있어서, 상기 착색반사층은 크롬 산화물 기반의 블랙실버로 형성될 수 있다.In an embodiment, the colored reflective layer may be formed of chromium oxide-based black silver.

실시 예에 있어서, 상기 렌즈는 프레넬 렌즈(fresnel lens)를 포함할 수 있다.In an embodiment, the lens may include a Fresnel lens.

실시 예에 있어서, 상기 코팅층은 블랙안료 또는 카본블랙을 용매 또는 분산제에 혼합하여 형성될 수 있다.In an embodiment, the coating layer may be formed by mixing a black pigment or carbon black with a solvent or a dispersant.

상기와 같은 기술적 과제를 해결하기 위해, 본 발명의 다른 일 실시 예에 따른 반사형 스크린 제조방법은 보호층에 확산층을 형성하는 단계, 상기 확산층에 렌즈를 형성하는 단계, 상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계, 상기 착색반사층에 상기 영상 중 상기 착색반사층을 투과하여 도달한 영상을 반사시키는 반사층을 형성하는 단계, 및 상기 반사층에 코팅층을 형성하는 단계를 포함할 수 있다.In order to solve the above technical problems, the method for manufacturing a reflective screen according to another embodiment of the present invention includes the steps of forming a diffusion layer on a protective layer, forming a lens on the diffusion layer, forming a colored reflective layer that absorbs external light and reflects an image incident from the projector; It may include the step of forming

실시 예에 있어서, 상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계는 바코팅, 스크린 프린팅 및 스프레이 코팅 중 적어도 하나를 통해서, 블랙이면서 반사율이 일정 수준 이상인 블랙실버로 상기 착색반사층을 형성하는 단계를 포함할 수 있다.In an embodiment, the step of absorbing external light incident from the periphery on the lens and forming a colored reflective layer that reflects the image incident from the projector is black and has a reflectance through at least one of bar coating, screen printing, and spray coating. The method may include forming the colored reflective layer with black silver above a certain level.

실시 예에 있어서, 상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계는 상기 반사층을 형성하는 공정과 동일한 공정을 통하여, 상기 착색반사층을 형성하는 단계를 포함할 수 있다.In an embodiment, the step of forming the colored reflective layer that absorbs external light incident from the periphery on the lens and reflects the image incident from the projector is the same as the process of forming the reflective layer, forming the colored reflective layer may include steps.

실시 예에 있어서, 상기 착색반사층 및 상기 반사층은 스프레이 코팅을 통해서 형성되고, 상기 착색반사층의 두께는 0 μm 초과 10 μm 미만일 수 있다.In an embodiment, the colored reflective layer and the reflective layer are formed through spray coating, and the thickness of the colored reflective layer may be greater than 0 μm and less than 10 μm.

실시 예에 있어서, 상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계는 상기 블랙실버를 용제에 혼합하여 상기 착색반사층을 형성하는 단계를 포함하고, 상기 블랙실버의 고형분(solid content)의 비율은 전체의 5% 내지 15%이고, 상기 블랙실버의 입자 크기(particle size distribution)는 입도 분석기(particle size analyzer)의 D50에서 10 μm 내지 20 μm 이고, 상기 블랙실버의 용제(solvent)의 비율은 전체의 70% 내지 95%일 수 있다.In an embodiment, the step of forming the colored reflective layer that absorbs external light incident from the periphery on the lens and reflects the image incident from the projector comprises mixing the black silver with a solvent to form the colored reflective layer, , The ratio of the solid content of the black silver is 5% to 15% of the total, and the particle size distribution of the black silver is 10 μm to 20 μm in D50 of the particle size analyzer, and , the ratio of the solvent of the black silver may be 70% to 95% of the total.

실시 예에 있어서, 상기 용제는 메톡시 에탄올, 부록시 에탄올, 이소펜틸옥시 에탄올, 디에틸렌글리콜, 메톡시 프로판올, 에톡시 프로판올 및 폴리프로필렌글리콜 중 적어도 하나일 수 있다.
In an embodiment, the solvent may be at least one of methoxy ethanol, appendix ethanol, isopentyloxy ethanol, diethylene glycol, methoxy propanol, ethoxy propanol, and polypropylene glycol.

본 발명에 따른 반사형 스크린 및 그 제조방법의 효과에 대해 설명하면 다음과 같다.The effects of the reflective screen and its manufacturing method according to the present invention will be described as follows.

본 발명의 실시 예들 중 적어도 하나에 의하면, 외광은 흡수하고, 프로젝터의 영상은 반사시키는 착색반사층을 구비할 수 있다.According to at least one of the embodiments of the present invention, a colored reflective layer that absorbs external light and reflects the image of the projector may be provided.

또한, 본 발명의 실시 예들 중 적어도 하나에 의하면, 반사층을 형성하는 공정과 동일한 공정으로 형성되는 착색반사층을 구비할 수 있다.In addition, according to at least one of the embodiments of the present invention, the colored reflective layer formed by the same process as the process of forming the reflective layer may be provided.

또한, 본 발명의 실시 예들 중 적어도 하나에 의하면, 구조의 단순화로 두께를 감소시켜 롤링으로 형성이 가능할 수 있다.In addition, according to at least one of the embodiments of the present invention, it may be possible to form by rolling by reducing the thickness through the simplification of the structure.

또한, 본 발명의 실시 예들 중 적어도 하나에 의하면, 외광의 흡수에 따른 블랙휘도를 감소시키고, 명실명암비를 증가시킬 수 있다.
In addition, according to at least one of the embodiments of the present invention, it is possible to reduce black luminance according to absorption of external light and increase the bright-brightness ratio.

도 1는 본 발명의 일 실시 예에 따른 반사형 스크린을 나타내는 도면이다.
도 2 내지 도 6는 본 발명의 다른 일 실시 예에 따른 반사형 스크린 제조방법을 나타내는 도면이다.
도 7은 본 발명의 일 실시 예에 따른 반사형 스크린과 기존 스크린을 비교한 결과를 나타내는 도면이다.1 is a view showing a reflective screen according to an embodiment of the present invention.
2 to 6 are views showing a method of manufacturing a reflective screen according to another embodiment of the present invention.
7 is a view showing a result of comparing a reflective screen according to an embodiment of the present invention and a conventional screen.

이하, 첨부된 도면을 참조하여 본 명세서에 개시된 실시 예를 상세히 설명하되, 도면 부호에 관계없이 동일하거나 유사한 구성요소는 동일한 참조 번호를 부여하고 이에 대한 중복되는 설명은 생략하기로 한다. 이하의 설명에서 사용되는 구성요소에 대한 접미사 "모듈" 및 "부"는 명세서 작성의 용이함만이 고려되어 부여되거나 혼용되는 것으로서, 그 자체로 서로 구별되는 의미 또는 역할을 갖는 것은 아니다. 또한, 본 명세서에 개시된 실시 예를 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 명세서에 개시된 실시 예의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다. 또한, 첨부된 도면은 본 명세서에 개시된 실시 예를 쉽게 이해할 수 있도록 하기 위한 것일 뿐, 첨부된 도면에 의해 본 명세서에 개시된 기술적 사상이 제한되지 않으며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. Hereinafter, the embodiments disclosed in the present specification will be described in detail with reference to the accompanying drawings, but the same or similar components are assigned the same reference numbers regardless of reference numerals, and redundant description thereof will be omitted. The suffixes "module" and "part" for components used in the following description are given or mixed in consideration of only the ease of writing the specification, and do not have distinct meanings or roles by themselves. In addition, in describing the embodiments disclosed in the present specification, if it is determined that detailed descriptions of related known technologies may obscure the gist of the embodiments disclosed in this specification, the detailed description thereof will be omitted. In addition, the accompanying drawings are only for easy understanding of the embodiments disclosed in the present specification, and the technical idea disclosed herein is not limited by the accompanying drawings, and all changes included in the spirit and scope of the present invention , should be understood to include equivalents or substitutes.

제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되지는 않는다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.Terms including an ordinal number such as 1st, 2nd, etc. may be used to describe various elements, but the elements are not limited by the terms. The above terms are used only for the purpose of distinguishing one component from another.

어떤 구성요소가 다른 구성요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.When an element is referred to as being “connected” or “connected” to another element, it is understood that it may be directly connected or connected to the other element, but other elements may exist in between. it should be On the other hand, when it is mentioned that a certain element is "directly connected" or "directly connected" to another element, it should be understood that no other element is present in the middle.

단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. The singular expression includes the plural expression unless the context clearly dictates otherwise.

본 출원에서, "포함한다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.In the present application, terms such as “comprises” or “have” are intended to designate that a feature, number, step, operation, component, part, or combination thereof described in the specification exists, but one or more other features It should be understood that this does not preclude the existence or addition of numbers, steps, operations, components, parts, or combinations thereof.

이하, 도면들을 참조하여 본 발명의 실시 예에 대해 상세히 설명하기로 한다. 본 발명은 본 발명의 정신 및 필수적 특징을 벗어나지 않는 범위에서 다른 특정한 형태로 구체화될 수 있음은 당업자에게 자명하다.Hereinafter, an embodiment of the present invention will be described in detail with reference to the drawings. It is apparent to those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit and essential characteristics of the present invention.

기존의 프로젝터용 반사형 스크린은 스크린 표면 전체에 형성된 착색층을 구비한다. 착색층은 주변의 외광을 흡수하지만, 프로젝터로부터 나오는 영상까지 흡수하여 명실명암비는 감소시키고, 블랙휘도는 증가하는 문제점이 있고, 여러 층을 구비하는 스크린의 구조는 제조 비용 및 스크린 전체의 두께를 증가시켜 롤링으로 스크린을 형성하는데 있어 단점이 있다.A conventional reflective screen for a projector has a colored layer formed over the entire surface of the screen. Although the colored layer absorbs ambient light, it also absorbs the image from the projector, thereby reducing the contrast ratio and increasing black luminance. There is a disadvantage in forming a screen by rolling.

도 1는 본 발명의 일 실시 예에 따른 반사형 스크린을 나타내는 도면이다. 도 1을 참조하면, 반사형 스크린은 확산층(120), 렌즈(lens; 140), 착색반사층(170), 반사층(150) 및 코팅층(160)을 포함할 수 있다.1 is a view showing a reflective screen according to an embodiment of the present invention. Referring to FIG. 1 , the reflective screen may include a diffusion layer 120 , a lens 140 , a colored reflection layer 170 , a reflection layer 150 , and a coating layer 160 .

확산층(120)은 보호층(110)의 일면에 형성될 수 있다. 여기서, 보호층(110)은 확산층(120) 및 확산층(120)에 형성된 다른 구성들이 외부의 자극으로부터 훼손되는 것을 방지한다. 구체적으로, 보호층은 하드코팅층으로 형성될 수 있다. 그리고, 확산층(120)은 시야각을 확보하기 위한 것으로, 사용자가 정면에서 바라보지 않고 비스듬한 위치에서 스크린을 바라보는 경우에도 스크린에 반사된 영상을 볼 수 있도록 프로젝터로부터 출력되는 영상을 확산시켜 시야각을 넓혀줄 수 있다.The diffusion layer 120 may be formed on one surface of the protective layer 110 . Here, the protective layer 110 prevents the diffusion layer 120 and other components formed in the diffusion layer 120 from being damaged by external stimuli. Specifically, the protective layer may be formed of a hard coating layer. In addition, the diffusion layer 120 is to secure the viewing angle, and spreads the image output from the projector so that the user can see the image reflected on the screen even when the user looks at the screen from an oblique position without looking from the front to widen the viewing angle. can give

여기서, 확산층(120)은 입사되는 광의 입사각에 따라 리타데이션(retardation) 값의 차가 적은 물질로 형성될 수 있고, 구체적인 예로 폴리메틸메타아크릴레이트(PMMA; poly methyl methaacrylate)로 형성될 수 있다.Here, the diffusion layer 120 may be formed of a material having a small difference in retardation value according to the incident angle of the incident light, and as a specific example, it may be formed of poly methyl methacrylate (PMMA).

렌즈(140)는 확산층(120)의 일면에 형성될 수 있다. 여기서, 렌즈(140)는 자외선 경화수지 또는 열경화 수지 등의 수지로 형성될 수 있다. 그리고, 렌즈(140)는 확산층(120)과 제1경사각을 이루는 복수의 렌즈면 및 확산층(120)과 제2경사각을 이루는 복수의 라이즈(raise)면을 구비할 수 있다. 여기서, 렌즈면이 확산층(120)과 이루는 제1경사각은 0도 및 90도가 아닌 각도이며, 라이즈면이 확산층(120)과 이루는 제2경사각은 수직일 수 있다. 그러나, 제1경사각 및 제2경사각은 이에 한정되지 않고, 구현하고자 하는 반사형 스크린의 사양에 따라 다양하게 결정될 수 있다. 그리고, 렌즈(140)는 프레넬 렌즈로 형성될 수 있다. 프레넬 렌즈는 굴곡진 렌즈의 두께를 줄일 수 있는 렌즈로서, 굴곡진 렌즈 면을 분할하여 평면으로 구성된 렌즈를 말한다.The lens 140 may be formed on one surface of the diffusion layer 120 . Here, the lens 140 may be formed of a resin such as an ultraviolet curable resin or a thermosetting resin. In addition, the lens 140 may include a plurality of lens surfaces forming a first inclination angle with the diffusion layer 120 and a plurality of raise surfaces forming a second inclination angle with the diffusion layer 120 . Here, the first inclination angle between the lens surface and the diffusion layer 120 may be an angle other than 0 degrees and 90 degrees, and the second inclination angle between the rise surface and the diffusion layer 120 may be vertical. However, the first inclination angle and the second inclination angle are not limited thereto, and may be variously determined according to the specifications of the reflective screen to be implemented. In addition, the lens 140 may be formed of a Fresnel lens. A Fresnel lens is a lens that can reduce the thickness of a curved lens, and refers to a lens composed of a plane by dividing the curved lens surface.

착색반사층(170)은 렌즈(140)의 일면에 형성될 수 있다. 여기서, 렌즈(140)가 렌즈면 및 라이즈면을 구비하는 경우, 착색반사층(170)은 렌즈면에 형성될 수 있다. 그리고, 착색반사층(170)은 프로젝터가 아닌 프로젝터의 주변으로부터 출력되어 반사형 스크린에 도달하는 외광을 흡수할 수 있다. 이와 더불어, 착색반사층(170)은 외광이 아닌 프로젝터로부터 출력되어 반사형 스크린에 도달하는 영상을 반사시킨다. 즉, 착색반사층(170)은 프로젝터로부터 출력되어 반사형 스크린에 도달하는 영상만을 선택적으로 반사시켜 사용자에게 제공할 수 있다.The colored reflective layer 170 may be formed on one surface of the lens 140 . Here, when the lens 140 has a lens surface and a rise surface, the colored reflective layer 170 may be formed on the lens surface. In addition, the colored reflective layer 170 may absorb external light that is output from the periphery of the projector rather than the projector and reaches the reflective screen. In addition, the colored reflective layer 170 reflects the image that is output from the projector rather than external light and reaches the reflective screen. That is, the colored reflective layer 170 may selectively reflect only the image output from the projector and reaching the reflective screen and provide it to the user.

특히, 본 발명에 따른 반사형 스크린에 포함되는 착색반사층(170)은 블랙이면서 반사율이 일정 수준 이상으로 높은 재료인 블랙실버로 형성될 수 있으며, 구체적으로, 크롬 산화물 기반의 블랙실버로 형성될 수 있다.In particular, the colored reflective layer 170 included in the reflective screen according to the present invention may be formed of black silver, which is black and has a high reflectance at a certain level or higher, and specifically, may be formed of black silver based on chromium oxide. there is.

반사층(150)은 착색반사층(170)의 일면에 형성될 수 있다. 마찬가지로, 렌즈(140)가 렌즈면 및 라이즈면을 구비하는 경우, 반사층(150)은 렌즈면에 형성된 착색반사층(170)의 일면에 형성될 수 있다. 여기서, 반사층(150)은 프로젝터로부터 출력되는 영상 중 착색반사층(170)에서 반사되지 않고, 착색반사층(170)을 투과하여 반사층(150)에 도달한 영상을 반사시켜 사용자에게 전달한다. 그리고, 반사층(150)은 알루미늄 분말을 용매 및 분산제에 혼합하여 형성될 수 있다.The reflective layer 150 may be formed on one surface of the colored reflective layer 170 . Similarly, when the lens 140 has a lens surface and a rise surface, the reflective layer 150 may be formed on one surface of the colored reflective layer 170 formed on the lens surface. Here, the reflective layer 150 reflects the image that is not reflected by the colored reflective layer 170 among the images output from the projector, but passes through the colored reflective layer 170 and reaches the reflective layer 150 , and transmits it to the user. In addition, the reflective layer 150 may be formed by mixing aluminum powder with a solvent and a dispersant.

코팅층(160)은 반사층(150)에 형성될 수 있다. 여기서, 코팅층(160)은 후면 코팅층이 될 수 있고, 반사층(150)의 훼손을 방지할 수 있다. 여기서, 코팅층(160)은 블랙안료 또는 카본블랙을 용매 또는 분산제에 혼합하여 형성될 수 있다.The coating layer 160 may be formed on the reflective layer 150 . Here, the coating layer 160 may be a rear coating layer and may prevent damage to the reflective layer 150 . Here, the coating layer 160 may be formed by mixing black pigment or carbon black with a solvent or dispersant.

위와 같은 구성들을 통하여, 본 발명에 따른 반사형 스크린은 주변의 외광은 흡수하고, 프로젝터에서 출력되는 영상은 사용자에게 반사시키는 착색반사층을 렌즈(140) 및 반사층(150) 사이에 구비할 수 있다. 그 결과, 본 발명에 따른 반사형 스크린은 외광의 흡수에 따른 블랙휘도를 감소시키고, 명실명암비를 증가시킬 수 있으며, 두께가 감소되어 롤링으로 형성될 수 있다.Through the above configurations, the reflective screen according to the present invention may include a colored reflective layer between the lens 140 and the reflective layer 150 that absorbs ambient external light and reflects the image output from the projector to the user. As a result, the reflective screen according to the present invention can reduce black luminance due to absorption of external light, increase the bright-to-brightness ratio, and can be formed by rolling with a reduced thickness.

도 2 내지 도 6는 본 발명의 다른 일 실시 예에 따른 반사형 스크린 제조방법을 나타내는 도면이다.2 to 6 are views showing a method of manufacturing a reflective screen according to another embodiment of the present invention.

도 2 및 도3을 참조하면, 본 발명에 따른 반사형 스크린 제조방법에서 먼저, 보호층(210)의 일면에 확산층(220)이 형성될 수 있다. 그리고, 확상층(220)의 일면에 렌즈(240)가 형성될 수 있다. 여기서, 렌즈(240)는 확산층(220)과 제1경사각을 이루는 복수의 렌즈면 및 확산층(220)과 제2경사각을 이루는 복수의 라이즈면을 구비할 수 있다.2 and 3 , in the method for manufacturing a reflective screen according to the present invention, first, a diffusion layer 220 may be formed on one surface of the protective layer 210 . In addition, the lens 240 may be formed on one surface of the expansion layer 220 . Here, the lens 240 may include a plurality of lens surfaces forming a first inclination angle with the diffusion layer 220 and a plurality of rise surfaces forming a second inclination angle with the diffusion layer 220 .

도 4를 참조하면, 렌즈(240)에 착색반사층(270)이 형성될 수 있다. 구체적으로, 렌즈(240)가 렌즈면 및 라이즈면을 구비하는 경우, 착색반사층(270)은 렌즈면에 형성될 수 있다. 도 4에서 형성된 착색반사층(270)은 프로젝터의 주변으로부터 출력되어 반사형 스크린에 도달하는 외광을 흡수할 수 있다. 이와 함께, 착색반사층(270)은 외광이 아닌 프로젝터로부터 출력되어 반사형 스크린에 도달하는 영상을 반사시킨다. 즉, 착색반사층(270)은 프로젝터로부터 출력되어 반사형 스크린에 도달하는 영상만을 선택적으로 반사시켜 사용자에게 제공할 수 있다.Referring to FIG. 4 , a colored reflective layer 270 may be formed on the lens 240 . Specifically, when the lens 240 includes a lens surface and a rise surface, the colored reflective layer 270 may be formed on the lens surface. The colored reflective layer 270 formed in FIG. 4 may absorb external light output from the periphery of the projector and reaching the reflective screen. In addition, the colored reflective layer 270 reflects the image output from the projector and reaching the reflective screen instead of external light. That is, the colored reflective layer 270 may selectively reflect only the image output from the projector and reaching the reflective screen and provide it to the user.

특히, 본 발명에 따른 반사형 스크린 제조방법은 착색반사층(270)을 바코팅, 스크린 프린팅 및 스프레이 코팅 중 적어도 하나를 통해서 형성할 수 있다. 그리고, 블랙이면서 반사율이 일정 수준 이상으로 높은 재료인 블랙실버를 사용하여 착색반사층(270)을 형성할 수 있다. In particular, in the reflective screen manufacturing method according to the present invention, the colored reflective layer 270 may be formed through at least one of bar coating, screen printing, and spray coating. In addition, the colored reflective layer 270 may be formed using black silver, which is black and has a high reflectance at a certain level or higher.

또한, 후술하겠지만, 본 발명에 따른 반사형 스크린 제조방법은 반사층(250)을 형성하는 공정과 동일한 공정을 통하여 형성될 수 있다. 구체적으로, 반사층(250)이 스프레이 코팅으로 형성되는 경우, 착색반사층(270) 역시 스프레이 코팅으로 형성될 수 있다.In addition, as will be described later, the method for manufacturing a reflective screen according to the present invention may be formed through the same process as that of forming the reflective layer 250 . Specifically, when the reflective layer 250 is formed by spray coating, the colored reflective layer 270 may also be formed by spray coating.

그 결과, 본 발명에 따른 반사형 스크린 제조방법은 반사형 스크린을 제조하는 공정을 단순화시킬 수 있고, 제조 비용이 감소되며, 스프레이 공정의 경우, 착색반사층(270)의 두께가 0 μm 초과 10 μm 미만으로 형성될 수 있으므로, 반사형 스크린의 전체 두께가 감소되어 롤링으로 반사형 스크린을 형성할 수 있다.As a result, the method for manufacturing the reflective screen according to the present invention can simplify the process of manufacturing the reflective screen, reduce the manufacturing cost, and in the case of the spray process, the thickness of the colored reflective layer 270 is more than 0 μm and 10 μm Since it can be formed less than, the overall thickness of the reflective screen can be reduced to form the reflective screen by rolling.

그리고, 본 발명에 따른 반사형 스크린 제조방법은 블랙실버를 용제에 혼합하여 착색반사층(270)을 형성할 수 있다. 이러한 경우, 블랙실버의 고형분(solid content)의 비율은 전체 도료 함량의 5% 내지 15%이 될 수 있다. 더욱 바람직하게는 블랙실버의 고형은의 비율은 7% 내지 11%가 될 수 있다. 그리고, 블랙실버의 입자 크기(particle size distribution)는 입도 분석기(particle size analyzer)에서 측정된 입자 크기의 누적분포 중 최고 큰 값에 대하여 50%에 해당하는 크기의 값인 D50이 10 μm 내지 20 μm에 해당될 수 있다. 또한, 블랙실버의 용제(solvent)의 비율은 전체 도료함량의 70% 내지 95%가 될 수 있다.Also, in the method for manufacturing a reflective screen according to the present invention, the colored reflective layer 270 may be formed by mixing black silver with a solvent. In this case, the proportion of the solid content of the black silver may be 5% to 15% of the total paint content. More preferably, the proportion of solid silver in black silver may be 7% to 11%. And, for the particle size distribution of black silver, D50, a value of size corresponding to 50% of the largest value among the cumulative distribution of particle sizes measured by a particle size analyzer, is 10 μm to 20 μm. may be applicable. In addition, the ratio of the solvent (solvent) of the black silver may be 70% to 95% of the total paint content.

그리고, 블랙실버를 혼합하는 용제는 메톡시 에탄올, 부록시 에탄올, 이소펜틸옥시 에탄올, 디에틸렌글리콜, 메톡시 프로판올, 에톡시 프로판올 및 폴리프로필렌글리콜 중 적어도 하나일 수 있다.And, the solvent for mixing the black silver may be at least one of methoxy ethanol, appendix ethanol, isopentyloxy ethanol, diethylene glycol, methoxy propanol, ethoxy propanol, and polypropylene glycol.

그 결과, 본 발명에 따른 반사형 스크린 제조방법을 통하여 제조되는 반사형 스크린은 주변의 외광을 흡수하면, 프로젝터로부터 출력되는 영상을 반사시킬 수 있고, 그에 따라, 블랙휘도가 감소되고, 명실명암비가 증가할 수 있다.As a result, when the reflective screen manufactured by the reflective screen manufacturing method according to the present invention absorbs ambient light, it can reflect the image output from the projector, and accordingly, the black luminance is reduced, and the bright-room contrast ratio is reduced. can increase

도 5를 참조하면, 반사층(250)은 착색반사층(270)에 형성될 수 있다. 구체적으로, 렌즈(240)가 렌즈면 및 라이즈면을 구비하는 경우, 반사층(250)은 렌즈면에 형성된 착색반사층(270)의 일면에 형성될 수 있다. 그리고, 반사층(250)은 프로젝터로부터 출력되는 영상 중 착색반사층(270)에서 반사되지 않고, 착색반사층(270)을 투과하여 반사층(250)에 도달한 영상을 반사시켜 사용자에게 전달한다. 그리고, 반사층(250)은 바코팅, 스크린 프린팅 또는 스프레이 코팅 등과 같은 공정으로 형성될 수 있으며, 앞서 설명한 바와 같이 반사층(250) 및 착색반사층(270)은 동일한 공정을 통해서 형성되어 반사형 스크린을 제조하는 비용이 감소될 수 있다.Referring to FIG. 5 , the reflective layer 250 may be formed on the colored reflective layer 270 . Specifically, when the lens 240 includes a lens surface and a rise surface, the reflective layer 250 may be formed on one surface of the colored reflective layer 270 formed on the lens surface. In addition, the reflective layer 250 reflects the image that is not reflected by the colored reflective layer 270 among the images output from the projector, but passes through the colored reflective layer 270 and reaches the reflective layer 250 , and transmits it to the user. In addition, the reflective layer 250 may be formed by a process such as bar coating, screen printing, or spray coating, and as described above, the reflective layer 250 and the colored reflective layer 270 are formed through the same process to manufacture a reflective screen. cost can be reduced.

도 6을 참조하면, 코팅층(260)은 반사층(250)에 형성될 수 있다. 코팅층(260)은 블랙안료 또는 카본블랙을 용매 또는 분산제에 혼합하여 형성될 수 있으며, 반사층(250)의 훼손을 방지할 수 있다.Referring to FIG. 6 , the coating layer 260 may be formed on the reflective layer 250 . The coating layer 260 may be formed by mixing black pigment or carbon black with a solvent or a dispersant, and may prevent damage to the reflective layer 250 .

도 7은 본 발명의 일 실시 예에 따른 반사형 스크린과 기존 스크린을 비교한 결과를 나타내는 도면이다.7 is a view showing a result of comparing a reflective screen and a conventional screen according to an embodiment of the present invention.

도 7의 착색반사층을 구비한 반사형 스크린은 본 발명에 따른 반사형 스크린 제조방법으로 제작되었다. 구체적으로, 도 7의 착색반사층을 구비한 반사형 스크린은 전체 도료 함량의 약10%를 차지하는 블랙실버의 고형분의 비율, D50의 값이 약13 μm 내지 15 μm에 해당하는 블랙실버의 입자 크기 및 전체 도료함량의 약90%를 차지하는 용제의 비율을 통해서 형성되었다.The reflective screen having the colored reflective layer of FIG. 7 was manufactured by the reflective screen manufacturing method according to the present invention. Specifically, the reflective screen having the colored reflective layer of FIG. 7 has a black silver solid content ratio of about 10% of the total paint content, a black silver particle size corresponding to a D50 value of about 13 μm to 15 μm, and It was formed through the proportion of solvent that accounts for about 90% of the total paint content.

도7을 통해서 알 수 있듯이, 기존의 스크린의 블랙휘도는 3.17이고, 착색반사층을 구비한 본 발명에 따른 반사형 스크린의 블랙휘도는 2.67이다. 또한, 기존의 스크린의 명실명암비는 43:1이고, 착색반사층을 구비한 본 발명에 따른 반사형 스크린의 명실명암비는 74:1이다.As can be seen from FIG. 7, the black luminance of the conventional screen is 3.17, and the black luminance of the reflective screen according to the present invention having the colored reflective layer is 2.67. In addition, the bright and dark ratio of the conventional screen is 43:1, and the bright and dark ratio of the reflective screen according to the present invention having the colored reflective layer is 74:1.

즉, 본 발명에 따른 반사형 스크린은 블랙휘도가 2.67로 기존 스크린과 대비하여 약 16% 정도 감소된 블랙휘도를 나타내는 것을 알 수 있다. 그리고, 명실명암비 역시 기존의 스크린에서는 43:1이지만, 본 발명에 따른 반사형 스크린의 명실명암비는 74:1로, 기존 스크린과 대비하여 약 72% 정도 증가된 명실명암비를 나타내는 것을 알 수 있다.That is, it can be seen that the reflective screen according to the present invention has a black luminance of 2.67, which is about 16% reduced compared to the conventional screen. In addition, the bright-to-real-contrast ratio is also 43:1 in the conventional screen, but the bright-to-real-contrast ratio of the reflective screen according to the present invention is 74:1, indicating that the contrast ratio is increased by about 72% compared to the conventional screen.

결국, 본 발명에 따른 반사형 스크린은 주변의 외광은 흡수하고, 프로젝터에서 출력되는 영상은 사용자에게 반사시키는 착색반사층을 렌즈 및 반사층 사이에 구비할 수 있다. 그 결과, 본 발명에 따른 반사형 스크린은 외광의 흡수에 따른 블랙휘도를 감소시키고, 명실명암비를 증가시킬 수 있으며, 두께가 감소되어 롤링으로 형성될 수 있다. 그리고, 본 발명에 따른 반사형 스크린 제조방법은 스프레이 공정을 통해서, 착색반사층 및 반사층을 동일한 공정으로 형성하여 제조 비용을 감소시킬 수 있다.As a result, the reflective screen according to the present invention may include a colored reflective layer between the lens and the reflective layer that absorbs ambient external light and reflects the image output from the projector to the user. As a result, the reflective screen according to the present invention can reduce black luminance due to absorption of external light, increase the bright-to-brightness ratio, and can be formed by rolling with a reduced thickness. In addition, the method for manufacturing a reflective screen according to the present invention can reduce the manufacturing cost by forming the colored reflective layer and the reflective layer in the same process through the spray process.

따라서, 이상의 상세한 설명은 모든 면에서 제한적으로 해석되어서는 아니되고 예시적인 것으로 고려되어야 한다. 본 발명의 범위는 첨부된 청구항의 합리적 해석에 의해 결정되어야 하고, 본 발명의 등가적 범위 내에서의 모든 변경은 본 발명의 범위에 포함된다.Accordingly, the above detailed description should not be construed as restrictive in all respects, but should be considered as exemplary. The scope of the present invention should be determined by a reasonable interpretation of the appended claims, and all modifications within the equivalent scope of the present invention are included in the scope of the present invention.

Claims (11)

보호층에 형성되는 확산층;
상기 확산층에 형성되는 렌즈;
상기 렌즈에 형성되고, 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층;
상기 착색반사층에 형성되고, 상기 영상 중 상기 착색반사층에서 반사되지 않고 상기 착색반사층을 투과하여 도달한 영상을 반사시키는 반사층; 및
상기 반사층에 형성되는 코팅층을 포함하고,
상기 착색 반사층은 크롬 산화물 기반의 블랙실버로 형성되고,
상기 블랙실버의 고형분(solid content)의 비율은 전체의 5% 내지 15%이고, 상기 블랙실버의 입자 크기(particle size distribution)는 입도 분석기(particle size analyzer)의 D50에서 10 μm 내지 20 μm 이고, 상기 블랙실버의 용제(solvent)의 비율은 전체의 70% 내지 95%이고,
상기 용제는 메톡시 에탄올, 부록시 에탄올, 이소펜틸옥시 에탄올, 디에틸렌글리콜, 메톡시 프로판올, 에톡시 프로판올 및 폴리프로필렌글리콜 중 적어도 하나인 반사형 스크린.a diffusion layer formed on the protective layer;
a lens formed on the diffusion layer;
a colored reflective layer formed on the lens, absorbing external light incident from the periphery, and reflecting an image incident from the projector;
a reflective layer formed on the colored reflective layer and configured to reflect an image that is transmitted through the colored reflective layer without being reflected by the colored reflective layer among the images; and
A coating layer formed on the reflective layer,
The colored reflective layer is formed of chromium oxide-based black silver,
The proportion of the solid content of the black silver is 5% to 15% of the total, and the particle size distribution of the black silver is 10 μm to 20 μm at D50 of a particle size analyzer, The ratio of the solvent of the black silver is 70% to 95% of the total,
The solvent is at least one of methoxy ethanol, appendix ethanol, isopentyloxy ethanol, diethylene glycol, methoxy propanol, ethoxy propanol and polypropylene glycol. 제 1 항에 있어서,
상기 착색반사층은,
블랙이면서 반사율이 일정 수준 이상인 블랙실버로 형성되는 반사형 스크린.
The method of claim 1,
The colored reflective layer,
A reflective screen made of black silver that is black and has a reflectance above a certain level.
 삭제delete 제 1 항에 있어서,
상기 렌즈는 프레넬 렌즈(fresnel lens)를 포함하는 반사형 스크린.
The method of claim 1,
The lens is a reflective screen comprising a Fresnel lens.
 제 1 항에 있어서,
상기 코팅층은,
블랙안료 또는 카본블랙을 용매 또는 분산제에 혼합하여 형성되는 블랙 코팅층인 반사형 스크린.
The method of claim 1,
The coating layer is
A reflective screen that is a black coating layer formed by mixing black pigment or carbon black with a solvent or dispersant.
 보호층에 확산층을 형성하는 단계;
상기 확산층에 렌즈를 형성하는 단계;
상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계;
상기 착색반사층에 상기 영상 중 상기 착색반사층에서 반사되지 않고 상기 착색반사층을 투과하여 도달한 영상을 반사시키는 반사층을 형성하는 단계; 및
상기 반사층에 코팅층을 형성하는 단계를 포함하고,
상기 착색 반사층은 크롬 산화물 기반의 블랙실버로 형성되고,
상기 블랙실버의 고형분(solid content)의 비율은 전체의 5% 내지 15%이고, 상기 블랙실버의 입자 크기(particle size distribution)는 입도 분석기(particle size analyzer)의 D50에서 10 μm 내지 20 μm 이고, 상기 블랙실버의 용제(solvent)의 비율은 전체의 70% 내지 95%이고,
상기 용제는 메톡시 에탄올, 부록시 에탄올, 이소펜틸옥시 에탄올, 디에틸렌글리콜, 메톡시 프로판올, 에톡시 프로판올 및 폴리프로필렌글리콜 중 적어도 하나인 반사형 스크린 제조방법.forming a diffusion layer on the protective layer;
forming a lens on the diffusion layer;
forming a colored reflective layer on the lens to absorb external light incident from the periphery and reflect the image incident from the projector;
forming a reflective layer on the colored reflective layer to reflect an image that has passed through the colored reflective layer without being reflected from the colored reflective layer among the images; and
Comprising the step of forming a coating layer on the reflective layer,
The colored reflective layer is formed of chromium oxide-based black silver,
The proportion of the solid content of the black silver is 5% to 15% of the total, and the particle size distribution of the black silver is 10 μm to 20 μm at D50 of a particle size analyzer, The ratio of the solvent of the black silver is 70% to 95% of the total,
The solvent is at least one of methoxy ethanol, appendix ethanol, isopentyloxy ethanol, diethylene glycol, methoxy propanol, ethoxy propanol and polypropylene glycol. 제 6 항에 있어서,
상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계는,
바코팅, 스크린 프린팅 및 스프레이 코팅 중 적어도 하나를 통해서, 블랙이면서 반사율이 일정 수준 이상인 블랙실버로 상기 착색반사층을 형성하는 단계를 포함하는 반사형 스크린 제조방법.
7. The method of claim 6,
The step of forming a colored reflective layer that absorbs external light incident from the periphery on the lens and reflects the image incident from the projector comprises:
A method for manufacturing a reflective screen, comprising the step of forming the colored reflective layer with black silver having a reflectance of a certain level or higher while being black through at least one of bar coating, screen printing, and spray coating.
 제 6 항에 있어서,
상기 렌즈에 주변으로부터 입사되는 외광을 흡수하고, 프로젝터로부터 입사되는 영상을 반사시키는 착색반사층을 형성하는 단계는,
상기 반사층을 형성하는 공정과 동일한 공정을 통하여, 상기 착색반사층을 형성하는 단계를 포함하는 반사형 스크린 제조방법.
7. The method of claim 6,
The step of forming a colored reflective layer that absorbs external light incident from the periphery on the lens and reflects the image incident from the projector comprises:
and forming the colored reflective layer through the same process as the process for forming the reflective layer.
 제 8 항에 있어서,
상기 착색반사층 및 상기 반사층은 스프레이 코팅을 통해서 형성되고,
상기 착색반사층의 두께는 0 μm 초과 10 μm 미만인 반사형 스크린 제조방법.
9. The method of claim 8,
The colored reflective layer and the reflective layer are formed through spray coating,
The thickness of the colored reflective layer is more than 0 μm and less than 10 μm of a reflective screen manufacturing method.
 삭제delete 삭제delete
KR1020140191044A 2014-12-26 2014-12-26 Reflection screen and method for manufacturing the same KR102372851B1 (en)