KR102326197B1 - Functional hydroponic growing media containing carbon fiber and manufacturing method of the same - Google Patents
Functional hydroponic growing media containing carbon fiber and manufacturing method of the same Download PDFInfo
- Publication number
- KR102326197B1 KR102326197B1 KR1020200023643A KR20200023643A KR102326197B1 KR 102326197 B1 KR102326197 B1 KR 102326197B1 KR 1020200023643 A KR1020200023643 A KR 1020200023643A KR 20200023643 A KR20200023643 A KR 20200023643A KR 102326197 B1 KR102326197 B1 KR 102326197B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- carbon fiber
- artificial medium
- functional artificial
- extract
- Prior art date
Abstract
본 발명은 탄소섬유를 함유하는 기능성 인공배지 및 이의 제조 방법에 관한 것으로, 침지처리 된 직포 또는 부직포를 포함하는 베이스 재료, 볏짚, 밀짚 및 보리짚 중 적어도 하나를 포함하는 짚 재료와 쌀겨의 혼합물을 포함하는 바이오매스 재료, 탄소섬유, 고흡수성 수지 및 바인더를 포함하는 것을 특징으로 하는 탄소섬유를 함유하는 기능성 인공배지를 제공한다.The present invention relates to a functional artificial medium containing carbon fiber and a method for producing the same, comprising a base material including a woven or non-woven fabric that has been soaked, and a straw material including at least one of rice straw, wheat straw and barley straw and a mixture of rice bran It provides a functional artificial medium containing carbon fibers, characterized in that it includes a biomass material, carbon fiber, superabsorbent resin, and a binder comprising
Description
본 발명은 탄소섬유를 함유하는 기능성 인공배지 및 이의 제조 방법에 관한 것으로서, 더욱 상세하게는 탄소섬유를 함유하여 원적외선 방사 및 항균성이 더욱 강화된 기능성 인공배지 및 이의 제조 방법에 관한 것이다.The present invention relates to a functional artificial medium containing carbon fibers and a method for manufacturing the same, and more particularly, to a functional artificial medium containing carbon fibers with enhanced far-infrared radiation and antibacterial properties and a method for manufacturing the same.
일반적으로 식물을 이용한 액자나 벽면녹화, 입체적인 꽃조형물, 플라워볼과 같은 형상물은, 주변의 환경개선, 미관, 인테리어 등 경관 조성 등의 목적으로 활성화되고 있다.In general, frame using plants, wall greening, three-dimensional flower sculptures, and shapes such as flower balls are being activated for the purpose of improving the surrounding environment, aesthetics, and landscape creation such as interiors.
이러한 형상물에 식물을 식재하기 위해서는 토양이 필요한데, 일반토양은 토양의 흘러내림으로 인해 형상을 유지하지 못하므로, 부직포를 이용하여 주머니 형태로 만들어서 식물을 식재하거나 그물망을 설치한 다음 식물을 식재하는 방식을 사용하고 있다.In order to plant plants in these shapes, soil is required, and since ordinary soil cannot maintain its shape due to soil runoff, it is a method of planting plants or installing a mesh after making a bag shape using a nonwoven fabric. is using
그러나, 이러한 방식은 입체적인 형상을 만들기 어렵고, 식물을 이용하여 정밀한 형상을 표현하기 어렵다는 단점이 있다. 또한, 그 작업에 많은 인원과 시간이 투입되어야 하며, 작업 완료 후 토양의 유실 및 오염, 먼지 발생 등으로 식물을 원활하게 재배하기 어려우며, 그물망을 설치하여 토양 충진 후 식물을 식재한 후에도 관수시 토양의 유실이 계속적으로 발생하고 토양의 영양분이 소실되어 균일한 물성 및 영양분이 고르게 함유된 토양성분을 제공할 수 없으므로 식물을 최적으로 재배하기 어렵다는 문제점이 있다.However, this method has disadvantages in that it is difficult to make a three-dimensional shape and it is difficult to express a precise shape using plants. In addition, a large number of people and time must be invested in the work, and it is difficult to grow plants smoothly due to soil loss, contamination, and dust generation after work is completed. There is a problem in that it is difficult to optimally cultivate plants because the loss of soil continues to occur and nutrients in the soil are lost, so that it is impossible to provide a soil component containing uniform physical properties and nutrients.
본원의 배경이 되는 기술은 대한민국 등록특허 제10-1090949호에 개시되어 있다.The technology that is the background of the present application is disclosed in Korean Patent Registration No. 10-1090949.
본 발명이 해결하고자 하는 과제는 토양 유실에 따른 문제를 해결함과 더불어 흡수성, 항균성, 살균성, 탈취성 및 원적외선 방사 효과가 개선된, 탄소섬유를 함유한 기능성 인공배지 및 이의 제조 방법을 제공하는데 있다. The problem to be solved by the present invention is to provide a functional artificial medium containing carbon fiber and a method for producing the same, in which absorption, antibacterial, sterilizing, deodorizing and far-infrared radiation effects are improved, as well as solving problems caused by soil loss. .
본 발명이 해결하고자 하는 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems to be solved by the present invention are not limited to the problems mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.
상기 과제를 달성하기 위한 본 발명의 실시예들에 따른 탄소섬유를 함유하는 기능성 인공배지는 침지처리 된 직포 또는 부직포를 포함하는 베이스 재료, 볏짚, 밀짚 및 보리짚 중 적어도 하나를 포함하는 짚 재료와 쌀겨의 혼합물을 포함하는 바이오매스 재료, 탄소섬유, 고흡수성 수지 및 바인더를 포함하는 것을 특징으로 한다.A functional artificial medium containing carbon fiber according to embodiments of the present invention for achieving the above object is a base material including an immersed woven or non-woven fabric, a straw material including at least one of rice straw, wheat straw and barley straw; It is characterized in that it contains a biomass material containing a mixture of rice bran, carbon fiber, super absorbent polymer and a binder.
일 실시예에 따르면, 상기 베이스 재료 40 내지 60 중량%, 상기 바이오매스 재료 10 내지 25 중량%, 상기 탄소섬유 5 내지 10 중량%, 상기 고흡수성 수지 5 내지 10 중량% 및 상기 바인더 5 내지 15 중량%를 포함하는 것을 특징으로 할 수 있다.According to an embodiment, 40 to 60% by weight of the base material, 10 to 25% by weight of the biomass material, 5 to 10% by weight of the carbon fiber, 5 to 10% by weight of the superabsorbent polymer, and 5 to 15% by weight of the binder % may be included.
일 실시예에 따르면, 상기 베이스 재료, 상기 바이오매스 재료 및 상기 고흡수성 수지는 분쇄되어 1 내지 10mm의 입자크기를 갖는 분말 형태로 사용되고, 상기 탄소섬유는 분쇄되어 1 내지 5mm의 길이를 갖도록 사용되는 것을 특징으로 할 수 있다.According to one embodiment, the base material, the biomass material, and the superabsorbent resin are pulverized and used in the form of a powder having a particle size of 1 to 10 mm, and the carbon fiber is pulverized and used to have a length of 1 to 5 mm. can be characterized as
일 실시예에 따르면, 상기 침지처리 된 직포 또는 부직포는 복합 천연추출물을 포함하는 천연 침지액을 이용하여 침지처리 된 것이되, 상기 복합 천연추출물은 모링가 추출물, 향나무 추출물, 붉나무 추출물 및 감잎 추출물을 포함하는 것을 특징으로 할 수 있다.According to one embodiment, the immersion-treated woven or nonwoven fabric is immersed using a natural immersion solution containing a complex natural extract, and the complex natural extract is a moringa extract, juniper extract, redwood extract and persimmon leaf extract. It may be characterized by including.
일 실시예에 따르면, 폴리페놀 함유 건조식물 및 광물혼합물 중 적어도 하나를 포함하는 보조 첨가제를 더 포함하고, 상기 폴리페놀 함유 건조식물은 녹차, 도토리 및 선인장 중 적어도 하나의 건조식물을 포함하고, 상기 광물혼합물은 석영, 견운모, 토루말린, 알루미나, 할로이사이트, 카올리나이트, 딕카이트, 산화철, 산화칼슘 및 산화마그네슘 중 적어도 2종 이상의 혼합광물이 소성 및 분쇄되어 제조된 것을 특징으로 할 수 있다.According to one embodiment, it further comprises an auxiliary additive comprising at least one of a polyphenol-containing dried plant and a mineral mixture, wherein the polyphenol-containing dried plant includes at least one dried plant of green tea, acorn, and cactus; The mineral mixture may be characterized in that it is produced by calcining and pulverizing at least two or more mixed minerals of quartz, sericite, tourumaline, alumina, halloysite, kaolinite, dickite, iron oxide, calcium oxide and magnesium oxide.
일 실시예에 따르면, 상기 베이스 재료 40 내지 60 중량%, 상기 바이오매스 재료 10 내지 25 중량%, 상기 탄소섬유 5 내지 10 중량%, 상기 고흡수성 수지 5 내지 10 중량%, 상기 바인더 5 내지 15 중량%, 상기 폴리페놀 함유 건조식물 5 내지 10 중량%, 및 상기 광물혼합물 5 내지 10 중량%를 포함하는 것을 특징으로 할 수 있다.According to an embodiment, 40 to 60% by weight of the base material, 10 to 25% by weight of the biomass material, 5 to 10% by weight of the carbon fiber, 5 to 10% by weight of the superabsorbent polymer, 5 to 15% by weight of the binder %, 5 to 10% by weight of the polyphenol-containing dry plant, and 5 to 10% by weight of the mineral mixture.
상기 과제를 달성하기 위한 본 발명의 실시예들에 따른 탄소섬유를 함유하는 기능성 인공배지의 제조 방법은 베이스 재료, 바이오매스 재료, 탄소섬유 및 고흡수성 수지를 각각 분쇄한 후 혼합하여 분쇄 혼합물을 제조하는 단계; 정제수에 상기 분쇄 혼합물 및 바인더를 첨가하고 교반하여 기능성 인공배지용 조성물을 제조하는 단계; 및 성형 틀을 이용한 프레스 성형 공정을 통해 상기 기능성 인공배지용 조성물을 압축 성형하는 단계를 포함하고, 상기 베이스 재료는 침지처리 된 직포 또는 부직포를 포함하고, 상기 바이오매스 재료는 볏짚, 밀짚 및 보리짚 중 적어도 하나를 포함하는 짚 재료와 쌀겨의 혼합물을 포함하는 것을 특징으로 한다.In the method for producing a functional artificial medium containing carbon fibers according to embodiments of the present invention for achieving the above object, a base material, a biomass material, a carbon fiber and a superabsorbent resin are respectively pulverized and then mixed to prepare a pulverized mixture to do; preparing a composition for a functional artificial medium by adding the grinding mixture and a binder to purified water and stirring; and compression molding the composition for functional artificial medium through a press molding process using a molding die, wherein the base material includes an immersed woven or nonwoven fabric, and the biomass material is rice straw, wheat straw and barley straw. It is characterized in that it comprises a mixture of straw material and rice bran containing at least one of.
본 발명의 실시예들에 따르면, 기능성 인공배지가 소일리스 폼(soiless form)의 형태로 구현되어 토양의 유실이 발생하지 않기 때문에, 식물로 이루어진 다양한 조형물에 적용할 수 있으며, 박테리아와 해충에 대한 우려가 없고, 우수한 흡수성과 다공질 공간의 충분한 확보를 통해 물과 공기의 최상의 균형비율의 유지가 가능하여 식재 식물의 장기간 생육이 가능하고, 쉽게 교체 가능하며 위생적이기 때문에 유지관리가 용이할 수 있다. According to the embodiments of the present invention, since the functional artificial medium is implemented in the form of a soilless form and soil loss does not occur, it can be applied to various sculptures made of plants, and can be applied to bacteria and pests. There is no concern, and it is possible to maintain the best balance ratio of water and air through excellent absorption and sufficient securing of porous space, so that long-term growth of planted plants is possible.
또한, 본 발명의 실시예들에 따른 기능성 인공배지는 흡수성, 항균성, 살균성 및 탈취성이 우수하여 수분의 공급이 지속적으로 이루어지지 않더라도 효과적으로 식물을 재배할 수 있으며, 특히 탄소섬유를 함유함에 따라 항균성이 향상되어 식물의 생장에 더욱 효과적일 수 있고, 원적외선 방사를 통해 바이오 필터로서의 기능이 강화되어 쾌적한 환경의 제공이 가능한 벽면녹화용 식생포트로서 이용 가능할 수 있다.In addition, the functional artificial medium according to the embodiments of the present invention has excellent absorbency, antibacterial properties, sterilization and deodorization properties, so that plants can be effectively grown even if the supply of moisture is not made continuously. This can be improved to be more effective for plant growth, and the function as a bio-filter is strengthened through far-infrared radiation, so that it can be used as a vegetation port for wall greening that can provide a comfortable environment.
도 1은 본 발명의 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지의 제조 방법을 설명하기 위한 순서도이다.
도 2는 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지를 이용한 식생포트를 설명하기 위한 도면이다.
도 3 및 도 4는 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지를 이용한 벽면녹화 구조물의 예를 도시하는 도면들이다.1 is a flowchart for explaining a method for manufacturing a functional artificial medium containing carbon fibers according to embodiments of the present invention.
2 is a view for explaining a vegetation pot using a functional artificial medium containing carbon fiber according to embodiments of the present invention.
3 and 4 are views showing an example of a green wall structure using a functional artificial medium containing carbon fiber according to embodiments of the present invention.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 이하에서 개시되는 실시예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 수 있으며, 단지 본 실시예는 본 발명의 개시가 완전하도록 하고, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 명세서 전문에 걸쳐 동일 참조 부호는 동일 구성 요소를 지칭한다.Advantages and features of the present invention, and methods for achieving them, will become apparent with reference to the embodiments described below in detail in conjunction with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but may be implemented in various different forms, only this embodiment allows the disclosure of the present invention to be complete, and common knowledge in the technical field to which the present invention belongs It is provided to fully inform the possessor of the scope of the invention, and the present invention is only defined by the scope of the claims. Like reference numerals refer to like elements throughout the specification.
본원 명세서에서, 어떤 부재가 다른 부재 “상에” 위치하고 있다고 할 때, 이는 어떤 부재가 다른 부재에 접해 있는 경우뿐 아니라 두 부재 사이에 또 다른 부재가 존재하는 경우도 포함한다. 또한, 본원 명세서에서, 어떤 부분이 어떤 구성요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는한 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. In the present specification, when a member is said to be located “on” another member, this includes not only a case in which a member is in contact with another member but also a case in which another member is present between the two members. In addition, in the present specification, when a part "includes" a certain component, it means that other components may be further included rather than excluding other components unless otherwise stated.
본원 명세서 전체에서 사용되는 정도의 용어 "약", "실질적으로" 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때, 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본원의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다. As used throughout this specification, the terms "about," "substantially," and the like are used in a sense at or close to the numerical value when the manufacturing and material tolerances inherent in the stated meaning are presented, and are used in the understanding of this application. It is used to prevent unfair use by unconscionable infringers of the disclosure in which exact or absolute figures are mentioned to help
이하 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지 및 이의 제조 방법에 대해 상세히 설명한다.Hereinafter, a functional artificial medium containing carbon fibers and a manufacturing method thereof according to embodiments of the present invention will be described in detail.
도 1은 본 발명의 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지의 제조 방법을 설명하기 위한 순서도이다. 도 2는 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지의 이용예를 설명하기 위한 도면이다. 도 3 및 도 4는 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지를 이용한 벽면녹화 구조물의 예를 도시하는 도면들이다.1 is a flowchart for explaining a method for manufacturing a functional artificial medium containing carbon fibers according to embodiments of the present invention. 2 is a view for explaining an example of use of a functional artificial medium containing carbon fibers according to embodiments of the present invention. 3 and 4 are views showing an example of a green wall structure using a functional artificial medium containing carbon fiber according to embodiments of the present invention.
도 1을 참조하면, 본 발명의 실시예들에 따른 탄소섬유를 함유한 기능성 인공배지는 베이스 재료, 바이오매스 재료, 탄소섬유, 고흡수성 수지 및 바인더를 포함할 수 있으며, 이의 제조 방법은 베이스 재료, 바이오매스 재료, 탄소섬유 및 고흡수성 수지를 각각 분쇄한 후 혼합하여 분쇄 혼합물을 제조하는 단계(S10), 정제수에 분쇄 혼합물 및 바인더를 첨가하고 교반하여 기능성 인공배지용 조성물을 제조하는 단계(S20) 및 성형 틀을 이용한 프레스 성형 공정을 통해 기능성 인공배지용 조성물을 압축 성형하는 단계(S30)를 포함할 수 있다. Referring to Figure 1, the functional artificial medium containing carbon fibers according to embodiments of the present invention may include a base material, a biomass material, carbon fibers, a superabsorbent resin and a binder, and a method of manufacturing the same is a base material , biomass material, carbon fiber and superabsorbent resin are respectively pulverized and mixed to prepare a pulverized mixture (S10), and a pulverized mixture and a binder are added to purified water and stirred to prepare a composition for a functional artificial medium (S20) ) and compression molding the composition for a functional artificial medium through a press molding process using a molding mold (S30).
상세하게, 베이스 재료는 본 발명의 기능성 인공배지에서 식물을 지지함과 동시에 빈 공간을 형성하여 식물의 뿌리가 쉽게 자리 잡을 수 있도록 하는 역할을 수행하기 위해 사용될 수 있다. 베이스 재료는 침지처리 된 직포 또는 부직포를 이용할 수 있다. 예컨대, 직포 또는 부직포는 폴리에스터, 폴리에틸렌, 폴리프로필렌, 아크릴로니트릴부타디엔스티렌, 폴리스티렌, 폴리카보네이트 및 폴리아미드 중에서 선택된 적어도 하나의 합성수지를 이용하여 제조된 것을 포함할 수 있으나, 이에 제한되는 것은 아니다. In detail, the base material can be used to support the plant in the functional artificial medium of the present invention and at the same time form an empty space to perform a role of allowing the root of the plant to be easily located. The base material may be an impregnated woven or non-woven fabric. For example, the woven or nonwoven fabric may include one manufactured using at least one synthetic resin selected from polyester, polyethylene, polypropylene, acrylonitrile butadiene styrene, polystyrene, polycarbonate, and polyamide, but is not limited thereto.
직포 또는 부직포의 침지처리는 복합 천연추출물을 포함하는 천연 침지액을 이용하여 수행될 수 있다. 복합 천연추출물은 예컨대, 모링가 추출물, 향나무 추출물, 붉나무 추출물 및 감잎 추출물을 포함할 수 있다. The immersion treatment of the woven or nonwoven fabric may be performed using a natural immersion solution containing a complex natural extract. The complex natural extract may include, for example, moringa extract, juniper extract, red tree extract and persimmon leaf extract.
모링가(Moringa oleifera)는 열대 및 아열대 기후에 널리 분포하는 십자화목과의 속씨식물 속의 하나이다. 모링가는 올레산이 풍부하여 열매(씨)를 압착하거나 헥산 추출에 의해 얻은 오일을 식용으로 사용하기도 한다. 열매는 녹색일 때 콩처럼 식용하며 성숙된 씨는 약 40% 오일을 함유한다. 모링가에서 획득한 오일은 양질의 조리용 이외에도, 향수, 비누, 화장품 등의 화장료 제조시에도 널리 사용되어 왔다. 이러한 모링가는 문헌에 따르면 90가지 영양소, 46가지 항산화제, 36가지 항 염증제를 포함하는 539가지의 다양하고 유익한 생화학적 활성물질을 함유하고 있다고 알려져 있다. 특히 시드는 스테롤들, 지방산, 단백질, 섬유질, 오메가 6, 9, 10, 토코페롤로 구성된다고 알려져 있으며, 또한 시드는 4-(α-L-람노 피라노 실록시)-벤질 글루코 시놀 레이트를 포함한 글루코시놀레이트를 함유한다. 또한, 모링가 종의 잎 및 시드는 시토키닌, 예를 들면 제아틴, 디히드로 제아틴, 및 이소펜틸 아데닌을 함유하는 것으로 알려져 있다.Moringa (Moringa oleifera) is a genus of angiosperms of the Cruciferae family widely distributed in tropical and subtropical climates. Moringa is rich in oleic acid, so the oil obtained by pressing the fruit (seed) or hexane extraction is sometimes used for food. The fruits are edible like beans when green, and the mature seeds contain about 40% oil. The oil obtained from moringa has been widely used in the manufacture of cosmetics, such as perfume, soap, and cosmetics, in addition to high-quality cooking. According to the literature, moringa is known to contain 539 diverse and beneficial biochemically active substances, including 90 nutrients, 46 antioxidants, and 36 anti-inflammatory agents. In particular, the seed is known to consist of sterols, fatty acids, protein, fiber, omega 6, 9, 10, and tocopherols, and the seed is also known to be glucosinol including 4-(α-L-rhamnopyranosiloxy)-benzyl glucosinolate contains rate. The leaves and seeds of Moringa species are also known to contain cytokinins, such as zeatin, dihydrozeatin, and isopentyl adenine.
향나무는 측백나무과에 속하는 늘푸른 바늘잎나무로, 키는 15 내지 25m에 이르고 온 몸에서 향이 나는 나무이다. 어린 향나무는 원추형으로 자라며, 줄기가 곧지만 나이가 들면서 주변의 조건에 맞게 비틀어지고 구부러지는 특징이 있다. 향나무의 성분에는 아멘토플라본(amentoflavone), 히노키플라본(hinokiflavone), 및 아피게닌(apigenin) 등이 존재하며, 세드롤(cedrol), 피넨(pinene)등과 같은 정유성분이 존재한다. 예로부터 향나무는 혈액순환촉진작용, 살균작용, 해독작용, 해열작용, 감기, 변비 및 다양한 질병에 대한 약재로도 사용이 되었으며, 현재까지도 향나무를 이용하여 여러가지 질병의 치료를 위한 연구가 계속되고 있다.The juniper is an evergreen needle-leaved tree belonging to the arboraceae family, reaching 15 to 25 m in height, and is a tree that smells all over the body. Young juniper trees grow in a cone shape and have straight stems, but as they age, they twist and bend according to the surrounding conditions. The components of juniper include amentoflavone, hinokiflavone, and apigenin, and essential oil components such as cedrol and pinene exist. Since ancient times, juniper has been used as a medicine for blood circulation promotion, sterilization, detoxification, antipyretic activity, colds, constipation, and various diseases. .
붉나무(Rhys javanica L.)는 옻나무과에 속하는 낙엽관목으로, 전국 각지의 야산에서 자생한다. 옻나무에 속하지만 독성은 없으며, 한방에서는 수렴, 지혈, 해독, 향균의 효력이 있어, 설사, 탈항, 위궤양, 십이지장궤양, 도한, 유정, 혈변, 혈뇨, 구내염 등에 처방한다. 또한 붉나무의 뿌리와 잎을 염부목(鹽膚木)이라 부르며 해열 및 제독, 타박상, 지혈 등의 용도로 사용하여 왔다. 붉나무의 열매는 둥글고 납작하며 시고 짠맛이 나는 흰 가루로 덮여있어 붉나무 열매를 물에 넣고 주물러서 그 물을 소금 대신 쓰거나 간수 대신 두부를 만드는데 쓰인다. 잎에는 굵은 벌레집이 달리는데 이것을 오배자(五倍子) 또는 염부자(鹽膚子)라고 한다.Red tree (Rhys javanica L.) is a deciduous shrub belonging to the Sumacaceae family, and grows wild in the wilds of various parts of the country. Although it belongs to the sumac tree, it is non-toxic. In oriental medicine, it has astringent, hemostasis, detoxification, and antibacterial effects, and is prescribed for diarrhea, prolapse, gastric ulcer, duodenal ulcer, sweating, oily stool, bloody stool, hematuria, and stomatitis. In addition, the roots and leaves of the red tree are called yeombumok (鹽膚木) and have been used for antipyretic, detoxification, bruises, and hemostasis. The red fruit is round, flat, and covered with white powder with a sour and salty taste. The red fruit is kneaded in water, and the water is used instead of salt or used to make tofu instead of bittern. A thick worm nest runs on the leaves, and this is called five-fold or yeombu-ja (鹽膚子).
감나무(Diospyros kaki Thunb)는 우리나라 중부 이남 지방에 주로 분포되어 있으며 생식하는 시자 이외에도 시엽, 시화, 시체 등은 예로부터 민간요법으로 사용되어 왔다. 그 중에서도 특히 감잎은 주로 차로 이용되어 동의보감에 혈관질환의 예방, 치료와 함께 자반증(혈관염증)에도 효과가 있다고 기록되어 있다. 감잎에는 비타민 C, 아미노산, 핵산, 페놀성 화합물, 유리당 등 여러 물질들이 다양하게 함유되어 있다. 감잎의 플라보노이드(flavonoid)는 kaempferol의 배당체인 astragalin, myricetin의 배당체인 myricetin의 배당체인 myricitrin, isoquercitrin 등의 배당체 형태가 존재한다. 감잎은 총 페놀성 화합물 함량이 0.1 ~ 5.8%로 다른 식물에 비하여 높으며, 우수한 항산화능과 항균성이 확인되었고, Superoxide dismutase(SOD)활성에도 관여하는 것으로 알려져 있다.The persimmon tree (Diospyros kaki Thunb) is mainly distributed in the central and southern regions of Korea. In addition to the reproductive Shija, the leaves, Shihwa, and corpses have been used as folk remedies since ancient times. Among them, persimmon leaves are mainly used as tea, and it is recorded in Donguibogam that it is effective in preventing and treating vascular diseases as well as in purpura (vascular inflammation). Persimmon leaves contain various substances such as vitamin C, amino acids, nucleic acids, phenolic compounds, and free sugar. The flavonoids of persimmon leaves exist in the form of glycosides such as astragalin, a glycoside of kaempferol, myricitrin, a glycoside of myricetin, a glycoside of myricetin, and isoquercitrin. Persimmon leaves have a high total phenolic compound content of 0.1 to 5.8% compared to other plants, and have excellent antioxidant and antibacterial properties, and are known to be involved in superoxide dismutase (SOD) activity.
모링가 추출물, 향나무 추출물, 붉나무 추출물, 및 감잎 추출물은 각각의 기관(예컨대, 뿌리, 가지, 줄기, 잎 또는 꽃)으로부터 당해 기술 분야의 전문가에 의해 추출할 수 있는 일반적인 추출 방법으로 추출된 추출물을 의미하며, 추출 부위가 특정의 부분으로 제한되지 않는다. 각각의 추출물은 액상 형태로 이용될 수 있다. Moringa extract, juniper extract, redwood extract, and persimmon leaf extract are extracts extracted by a general extraction method that can be extracted from each organ (eg, root, branch, stem, leaf or flower) by a person skilled in the art. Meaning, the extraction site is not limited to a specific portion. Each extract is available in liquid form.
천연 침지액은 정제수에 모링가 추출물, 향나무 추출물, 붉나무 추출물 및 감잎 추출물을 포함하는 복합 천연추출물을 혼합하고 교반하여 제조될 수 있다. 일 실시예에 있어서, 천연 침지액은 정제수 100 중량부당 복합 천연무출물 5 내지 10 중량부가 혼합되어 제조될 수 있으며, 이 때 모링가 추출물, 향나무 추출물, 붉나무 추출물 및 감잎 추출물은 1:0.5~1:0.5~1:1~2의 중량비로 혼합되는 것이 바람직할 수 있다. 본 발명에서, 복합 천연추출물은 베이스 재료의 항균성, 살균성 및 탈취성의 개선을 위해 사용될 수 있다. The natural immersion solution may be prepared by mixing and stirring a complex natural extract including a moringa extract, juniper extract, red tree extract and persimmon leaf extract in purified water. In one embodiment, the natural immersion solution may be prepared by mixing 5 to 10 parts by weight of complex natural extracts per 100 parts by weight of purified water, wherein the moringa extract, juniper extract, red tree extract and persimmon leaf extract are 1:0.5 to 1 It may be preferable to mix in a weight ratio of :0.5 to 1:1 to 2. In the present invention, the complex natural extract can be used to improve the antibacterial, bactericidal and deodorizing properties of the base material.
한편, 침지처리는 천연 침지액에 직포 또는 부직포를 침지시킨 후 60 내지 80℃의 온도에서 20 내지 30분 동안 가열한 후 건져내고, 탈수 및 송풍 건조를 수행하는 것을 포함할 수 있다. 상기 송풍 건조는 30 내지 40℃의 온도에서 30 내지 60분 동안 진행될 수 있다. 상기와 같은 천연 침지액을 이용한 침지 처리는 복수 회 수행될 수 있다. 예컨대, 천연 침지액을 이용한 직포 또는 부직포의 침지 처리는 적어도 3회 이상 수행되는 것이 바람직할 수 있다. 이를 통해, 천연 침지액에 포함된 유용 성분이 베이스 재료 내로 흡수되는 흡수율은 증대되고, 흡수된 유용 성분의 탈리율은 감소될 수 있다. On the other hand, the immersion treatment may include immersing the woven or nonwoven fabric in a natural immersion solution, heating it at a temperature of 60 to 80° C. for 20 to 30 minutes, and then removing it, and performing dehydration and air drying. The blow drying may be performed for 30 to 60 minutes at a temperature of 30 to 40 °C. The immersion treatment using the natural immersion solution as described above may be performed multiple times. For example, it may be preferable that the immersion treatment of the woven or nonwoven fabric using a natural immersion solution is performed at least three times. Through this, the absorption rate at which the useful component contained in the natural immersion liquid is absorbed into the base material may be increased, and the desorption rate of the absorbed useful component may be reduced.
베이스 재료는 기능성 인공배지의 총 중량대비 40 내지 60 중량%로 함유될 수 있다. 베이스 재료가 40 중량% 미만이면 수분 보유 및 전달력이 떨어지고, 60 중량%를 초과하면 기능성 및 성형성이 저하될 수 있다. The base material may be contained in an amount of 40 to 60% by weight based on the total weight of the functional artificial medium. When the amount of the base material is less than 40% by weight, moisture retention and transmission ability is deteriorated, and when it exceeds 60% by weight, functionality and moldability may be deteriorated.
바이오매스 재료는 식물의 성장에 필요한 수분공급을 위한 습도조절기능 및 식물의 성장에 필요한 산소의 함유 기능을 위해 사용될 수 있다. 예컨대, 바이오매스 재료는 볏짚, 밀짚 및 보리짚 중 적어도 하나를 포함하는 짚 재료와 쌀겨의 혼합물을 이용할 수 있다. 바이오매스 재료는 기능성 인공배지 총 중량대비 15 내지 25 중량%로 함유될 수 있다. 바이오매스 재료가 15 중량% 미만이면 상술한 바이오매스 재료의 효과가 미미할 수 있고, 50 중량%를 초과하면 성형성이 저하될 수 있다. 또한, 바이오매스 재료의 효과의 극대화를 위해, 바이오매스 재료를 구성하는 짚 재료와 쌀겨는 1:1 내지 4:1의 중량비로 혼합될 수 있다. 더욱 바람직하게, 바이오매스 재료는 볏짚, 밀짚, 보리짚 및 쌀겨가 1:1:1:1의 중량비로 혼합되어 사용될 수 있다.The biomass material may be used for a function of regulating humidity for supply of moisture required for plant growth and a function of containing oxygen required for plant growth. For example, the biomass material may use a mixture of rice bran and a straw material including at least one of rice straw, wheat straw, and barley straw. The biomass material may be contained in an amount of 15 to 25% by weight based on the total weight of the functional artificial medium. If the biomass material is less than 15% by weight, the effect of the above-described biomass material may be insignificant, and if it exceeds 50% by weight, the moldability may be deteriorated. In addition, in order to maximize the effect of the biomass material, the straw material and the rice bran constituting the biomass material may be mixed in a weight ratio of 1:1 to 4:1. More preferably, the biomass material may be used by mixing rice straw, wheat straw, barley straw and rice bran in a weight ratio of 1:1:1:1.
탄소섬유는 원적외선 방출 및 항균작용으로 식물의 뿌리를 건강하게 보호해주는 기능을 수행함과 더불어, 본 발명의 기능성 인공배지를 이용한 구조물(예컨대, 벽면녹화(green wall))이 바이오 필터로서 기능하는 것을 보강해주는 역할을 수행할 수 있다. 이를 통해, 본 발명의 기능성 인공배지를 이용한 구조물이 설치된 공간의 사용자에게 원적외선 방사에 따른 쾌적한 환경의 제공이 가능할 수 있다. Carbon fiber serves to protect the roots of plants in a healthy way by emitting far-infrared rays and antibacterial action, and reinforces the function of the structure (eg, green wall) using the functional artificial medium of the present invention as a bio-filter. can play a role. Through this, it may be possible to provide a comfortable environment according to far-infrared radiation to the user of the space where the structure using the functional artificial medium of the present invention is installed.
일 예로, 탄소섬유는 열경화성수지 분말에 미량의 첨가물(항균제, 광물 분말 등)을 혼합하여 원료혼합물을 준비하고, 준비된 원료 혼합물을 공지된 방법을 통해 섬유상으로 형성하여 제조될 수 있다. 열경화성수지 분말은 탄소섬유의 탄소원으로서 탄화공정에 의하여 탄화되어 활성탄소섬유로 변하는 원료물질이다. 이는 통상의 탄소화합물들은 모두 사용될 수 있기는 하나, 특히 공정의 안정성과 수득된 탄소섬유에서의 불순물 함량을 최소화시킬 수 있는 것이 사용되는 것이 바람직할 수 있다. 소결 또는 탄화 동안에도 변형되지 않으며, 불순물 함량이 적게 나타나는 것으로서, 예를 들면 노볼락형 페놀수지 등이 사용될 수 있다. 그리나, 본 발명이 이에 한정되지 않으며 노볼락형 페놀수지 이외에도 다양한 종류의 열경화성수지가 사용될 수 있다. For example, carbon fiber may be prepared by mixing a small amount of additives (antibacterial agent, mineral powder, etc.) with thermosetting resin powder to prepare a raw material mixture, and forming the prepared raw material mixture into a fibrous form through a known method. The thermosetting resin powder is a raw material that is carbonized by a carbonization process as a carbon source for carbon fibers and turns into activated carbon fibers. Although all common carbon compounds may be used, it may be preferable to use one capable of minimizing the stability of the process and the content of impurities in the obtained carbon fiber. It is not deformed even during sintering or carbonization, and the impurity content is low. For example, a novolak-type phenolic resin may be used. However, the present invention is not limited thereto, and various types of thermosetting resins may be used in addition to the novolak-type phenolic resin.
탄소섬유는 기능성 인공배지 총 중량대비 5 내지 10 중량%로 함유될 수 있다. 탄소섬유가 5 중량% 미만이여 탄소섬유의 효능이 미미할 수 있고, 10 중량%를 초과하면 첨가량에 비해 성능 개선의 효과가 미비하고 성형성이 저하될 수 있다.Carbon fiber may be contained in an amount of 5 to 10% by weight based on the total weight of the functional artificial medium. If the amount of carbon fiber is less than 5% by weight, the effect of carbon fiber may be insignificant, and if it exceeds 10% by weight, the effect of improving the performance may be insignificant compared to the amount added and the moldability may be reduced.
고흡수성 수지는 기능성 인공배지에 수분이 공급되었을 때, 수분을 흡수하여 기능성 인공배지 내에 습도를 일정하게 유지시켜 주는 기능을 수행하기 위해 사용될 수 있다. 고흡수성 수지는 수분을 함유하여 습도를 일정하게 유지시켜 주는 역할을 하는 것이면, 특별히 한정하지 않고 어떠한 것이든 사용가능하나, 폴리아크릴산, 폴리비닐알코올 및 폴리에틸렌 옥시드 등의 수용성 고분자를 가교에 의해 물에 불용화하여 얻어지는 것을 사용하는 것이 바람직할 수 있다. When moisture is supplied to the functional artificial medium, the superabsorbent polymer can be used to absorb moisture and perform a function of maintaining constant humidity in the functional artificial medium. The super absorbent polymer is not particularly limited as long as it contains moisture and plays a role of maintaining a constant humidity, but any superabsorbent polymer can be used. It may be preferable to use what is obtained by insolubilization.
고흡수성 수지는 기능성 인공배지의 총 중량대비 5 내지 10 중량%로 함유될 수 있다. 고흡수성 수지의 함량이 5 중량부 미만이면, 기능성 인공배지의 내부가 식물이 생장할 수 있을 정도의 습도를 나타낼 수 없으며, 고흡수성 수지의 함량이 10 중량부를 초과하게 되면, 기능성 인공배지의 내부 습도가 지나치게 증가하여 식물의 생장을 저해할 수 있다. The superabsorbent polymer may be contained in an amount of 5 to 10% by weight based on the total weight of the functional artificial medium. If the content of the superabsorbent polymer is less than 5 parts by weight, the inside of the functional artificial medium cannot show humidity enough for plants to grow, and when the content of the superabsorbent polymer exceeds 10 parts by weight, the inside of the functional artificial medium Excessive humidity can inhibit plant growth.
분쇄 혼합물은 상술한 베이스 재료, 바이오매스 재료, 탄소섬유 및 고흡수성 수지가 각각 분쇄 후 혼합되어 제조될 수 있다(S10). 예컨대, 베이스 재료, 바이오매스 재료 및 고흡수성 수지는 각각 분쇄되어 1 내지 10mm의 입자크기를 갖는 분말 형태로 포함 또는 사용될 수 있다. 그리고, 탄소섬유는 분쇄되어 1 내지 5mm의 길이를 갖도록 포함 또는 사용될 수 있다. The pulverized mixture may be prepared by pulverizing and mixing the above-described base material, biomass material, carbon fiber, and superabsorbent resin, respectively (S10). For example, the base material, the biomass material, and the superabsorbent resin may each be pulverized and included or used in the form of a powder having a particle size of 1 to 10 mm. And, the carbon fiber may be included or used to have a length of 1 to 5 mm by being pulverized.
상기와 같이 제조된 분쇄 혼합물을 정제수 및 바인더와 혼합한 후 교반하여 기능성 인공배지용 조성물이 제조될 수 있다(S20).After mixing the pulverized mixture prepared as described above with purified water and a binder, a composition for a functional artificial medium can be prepared by stirring (S20).
정제수는 분말 형태의 분쇄혼합물이 고루 섞이도록 하기 위해, 분쇄혼합물 100 중량부당 400 내지 600 중량부의 정제수가 사용되는 것이 바람직할 수 있다.Purified water may preferably be used in an amount of 400 to 600 parts by weight of purified water per 100 parts by weight of the pulverized mixture in order to evenly mix the pulverized mixture in powder form.
바인더는 베이스 재료, 탄소섬유, 바이오매스 재료 및 고흡습성 수지 간의 부착력을 증대시킴으로써, 기능성 인공배지용 조성물를 이용한 성형 공정시의 접착력은 물론, 성형 후의 강도도 증가시키는 기능을 수행할 수 있다. 또한, 베이스 재료, 탄소섬유, 바이오매스 재료 및 고흡습성 수지가 분쇄된 형태로 바인더에 의해 결합됨에 따라, 후속에서 압축 성형을 통해 형성되는 기능성 인공배지에는 식물 성장에 필수적인 공기 공급원으로서 기능하는 다공질 공간이 형성될 수 있다. 예컨대, 바인더는 아크릴계 수지, 에폭시계 수지, 우레탄계 수지 또는 실리콘계 수지를 사용할 수 있다. 바인더는 기능성 인공배지 총 중량 대비 10 내지 20 중량%로 함유될 수 있다. 바인더가 10 중량% 미만이며 접착력이 떨어지고, 20 중량%를 초과하면 성형성이 저하될 수 있다.The binder increases the adhesion between the base material, carbon fiber, biomass material, and the highly hygroscopic resin, thereby increasing the adhesion strength during the molding process using the composition for functional artificial medium, as well as the strength after molding. In addition, as the base material, carbon fiber, biomass material and high hygroscopic resin are combined by a binder in a pulverized form, a porous space that functions as an essential air source for plant growth in a functional artificial medium formed through compression molding subsequently can be formed. For example, the binder may be an acrylic resin, an epoxy resin, a urethane resin, or a silicone resin. The binder may be contained in an amount of 10 to 20% by weight based on the total weight of the functional artificial medium. If the binder is less than 10% by weight and the adhesive strength is poor, if it exceeds 20% by weight, the moldability may be deteriorated.
선택적으로, 기능성 인공배지용 조성물은 보조 첨가제를 더 포함할 수 있다. 보조 첨가제는 탄소섬유의 기능을 더욱 강화하기 위한 것으로서, 폴리페놀 함유 건조식물 및 광물혼합물 중 적어도 하나를 포함할 수 있다. 바람직하게, 보조 첨가제로서 폴리페놀 함유 건조식물 및 광물혼합물 모두가 사용될 수 있다.Optionally, the composition for a functional artificial medium may further include an auxiliary additive. The auxiliary additive is intended to further strengthen the function of carbon fiber, and may include at least one of polyphenol-containing dry plants and mineral mixtures. Preferably, both polyphenol-containing dry plants and mineral mixtures can be used as auxiliary additives.
폴리페놀 함유 건조 식물은 항산화 및 항균 기능의 강화를 위한 것으로서, 예컨대, 녹차, 도토리 및 선인장 중 적어도 하나를 포함할 수 있다. 도토리에 함유된 탄닌, 모링가에 함유된 클로로겐산, 녹차에 함유된 카테킨, 및 선인장에 함유된 플라보노이드 등은 모두 폴리페놀 화합물에 해당한다. 본 명세서에서 예시되는 건조 식물은 그 식물의 전초 또는 그의 다양한 기관을 의미할 수 있다. 폴리페놀 함유 건조 식물은 1 내지 3mm의 입자크기를 갖도록 분쇄되어 분말 형태로 사용될 수 있으며, 기능성 인공배지 총 중량대비 1 내지 5 중량%로 함유될 수 있다. 폴리페놀 함유 건조 식물이 1 중량% 미만이면 그 효과가 미미하고, 5 중량%를 초과하면 효과 상승 비율이 크지 않고, 비용이 상승되는 문제가 발생할 수 있다.Dried plants containing polyphenols are for enhancing antioxidant and antibacterial functions, and may include, for example, at least one of green tea, acorns and cactus. Tannins contained in acorns, chlorogenic acid contained in moringa, catechins contained in green tea, and flavonoids contained in cactus are all polyphenolic compounds. A dry plant exemplified herein may refer to an outpost of the plant or various organs thereof. The polyphenol-containing dried plant may be pulverized to have a particle size of 1 to 3 mm and used in the form of a powder, and may be contained in an amount of 1 to 5% by weight based on the total weight of the functional artificial medium. If the polyphenol-containing dry plant is less than 1% by weight, the effect is insignificant, and if it exceeds 5% by weight, the effect increase rate is not large and the cost may be increased.
광물혼합물은 원적외선 방사 및 항균작용을 위해 사용되는 것으로서, 석영, 견운모, 토루말린, 알루미나, 할로이사이트, 카올리나이트, 딕카이트, 산화철, 산화칼슘 및 산화마그네슘 중 적어도 2종 이상의 혼합광물을 포함할 수 있다. 광물혼합물은 상기 혼합광물이 소성 및 분쇄되어 제조될 수 있다. 혼합광물의 소성은 800 내지 900℃의 온도에서 1차 수행되고, 1000 내지 1300℃의 온도에서 2차로 수행될 수 있다. 혼합광물의 분쇄는 1차 소성과 2차 소성 사이에 진행될 수 있다. 예컨대, 1차 소성된 혼합광물은 500 내지 800mesh의 입도를 갖도록 분쇄될 수 있다. 바람직하게, 광물혼합물은 석영, 견운모, 토루말린, 알루미나, 할로이사이트, 카올리나이트, 딕카이트, 산화철, 산화칼슘 및 산화마그네슘이 1:1~1.5:1~1.5:1~1.5:0.5~1:0.5~1:0.5~1:2~2.5:2~2.5:2~2.5의 중량비로 혼합되어 제조될 수 있다. 광물혼합물은 기능성 인공배지 총 중량대비 1 내지 5 중량%로 함유될 수 있다. 광물혼합물이 1 중량% 미만이면 그 효과가 미미하고, 5 중량%를 초과하면 효과 상승 비율이 크지 않고, 비용이 상승되는 문제가 발생할 수 있다. The mineral mixture is used for far-infrared radiation and antibacterial action, and may include at least two or more mixed minerals of quartz, sericite, tourmaline, alumina, halloysite, kaolinite, dickite, iron oxide, calcium oxide and magnesium oxide. . The mineral mixture may be prepared by calcining and pulverizing the mixed mineral. The calcination of the mixed mineral may be performed first at a temperature of 800 to 900°C, and secondarily at a temperature of 1000 to 1300°C. Grinding of the mixed mineral may be performed between the primary and secondary firing. For example, the primary calcined mixed mineral may be pulverized to have a particle size of 500 to 800 mesh. Preferably, the mineral mixture contains quartz, sericite, tourumaline, alumina, halloysite, kaolinite, dickite, iron oxide, calcium oxide and magnesium oxide 1:1 to 1.5:1 to 1.5:1 to 1.5:0.5 to 1:0.5 ~1:0.5 ~ 1:2 ~ 2.5:2 ~ 2.5: can be prepared by mixing in a weight ratio of 2 to 2.5. The mineral mixture may be contained in an amount of 1 to 5% by weight based on the total weight of the functional artificial medium. If the mineral mixture is less than 1% by weight, the effect is insignificant, and if it exceeds 5% by weight, the effect increase rate is not large, and there may be a problem in that the cost is increased.
이어서, 성형 틀을 이용한 프레스 성형 공정을 통해 기능성 인공배지용 조성물을 압축 성형할 수 있다(S30). 예컨대, 기능성 인공배지용 조성물의 압축 성형은 80 내지 120℃의 온도에서 수행될 수 있으며, 압축 성형 동안 기능성 인공배지용 조성물에 함유된 바인더가 용융되어 각 성분이 결속됨에 따라 기능성 인공배지용 조성물로부터 기능성 인공배지의 제조가 완성될 수 있다.Subsequently, the composition for functional artificial medium may be compression molded through a press molding process using a molding die (S30). For example, compression molding of the composition for functional artificial medium may be performed at a temperature of 80 to 120 ° C. During compression molding, the binder contained in the composition for functional artificial medium is melted and as each component is bound, from the composition for functional artificial medium The production of the functional artificial medium can be completed.
상술한 바와 같이 제조된 기능성 인공배지는 소일리스 폼(soilless form)의 인공토양으로서, 도 2에 도시된 바와 같이 별도의 수용부재(예컨대, 식물 용기) 없이 식물(110)의 재배가 가능한 식생포트(100)로 이용될 수 있다. 또한, 본 발명의 기능성 인공배지가 소일리스 폼(soilless form)의 형태로 구현됨에 따라, 도 3 또는 도 4에 도시된 바와 같이, 별도의 수용부재 없이 벽면녹화용 지지 프레임에 직접 수용되어 벽면녹화에 이용될 수 있다.The functional artificial medium prepared as described above is an artificial soil of a soilless form, and as shown in FIG. 2, a vegetation port capable of cultivating the
본 발명의 실시예들에 따르면, 기능성 인공배지가 소일리스 폼(soiless form)의 형태로 구현되어 토양의 유실이 발생하지 않기 때문에, 식물로 이루어진 다양한 조형물에 적용할 수 있으며, 박테리아와 해충에 대한 우려가 없고, 우수한 흡수성과 다공질 공간의 충분한 확보를 통해 물과 공기의 최상의 균형비율의 유지가 가능하여 식재 식물의 장기간 생육이 가능하고, 쉽게 교체 가능하며 위생적이기 때문에 유지관리가 용이할 수 있다. According to the embodiments of the present invention, since the functional artificial medium is implemented in the form of a soilless form and soil loss does not occur, it can be applied to various sculptures made of plants, and can be applied to bacteria and pests. There is no concern, and it is possible to maintain the best balance ratio of water and air through excellent absorption and sufficient securing of porous space, so that long-term growth of planted plants is possible.
또한, 본 발명의 실시예들에 따른 기능성 인공배지는 흡수성, 항균성, 살균성 및 탈취성이 우수하여 수분의 공급이 지속적으로 이루어지지 않더라도 효과적으로 식물을 재배할 수 있으며, 특히 탄소섬유를 함유함에 따라 항균성이 향상되어 식물의 생장에 더욱 효과적일 수 있고, 원적외선 방사를 통해 바이오 필터로서의 기능이 강화되어 쾌적한 환경의 제공이 가능한 벽면녹화용 식생포트로서 이용 가능할 수 있다. In addition, the functional artificial medium according to the embodiments of the present invention has excellent absorbency, antibacterial properties, sterilization and deodorization properties, so that plants can be effectively grown even if the supply of moisture is not made continuously. This can be improved to be more effective for plant growth, and the function as a bio-filter is strengthened through far-infrared radiation, so that it can be used as a vegetation port for wall greening that can provide a comfortable environment.
이상, 첨부된 도면들을 참조하여 본 발명의 실시 예들을 예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들 및 응용 예에는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.In the above, embodiments of the present invention have been described with reference to the accompanying drawings, but those of ordinary skill in the art to which the present invention pertains will implement the present invention in other specific forms without changing the technical spirit or essential features. You will understand that it can be Therefore, it should be understood that the embodiments and application examples described above are illustrative in all respects and not restrictive.
Claims (7)
상기 침지처리 된 직포 또는 부직포는 복합 천연추출물을 포함하는 천연 침지액을 이용하여 침지처리 된 것이되,
상기 복합 천연추출물은 모링가 추출물, 향나무 추출물, 붉나무 추출물 및 감잎 추출물을 포함하는 것을 특징으로 하는, 탄소섬유를 함유하는 기능성 인공배지.A biomass material including a mixture of rice bran and a base material including a woven or nonwoven fabric that has been soaked, rice straw, straw material including at least one of wheat straw and barley straw, carbon fiber, a superabsorbent polymer and a binder,
The immersion-treated woven or non-woven fabric is immersed using a natural immersion solution containing a complex natural extract,
The complex natural extract is a functional artificial medium containing carbon fiber, characterized in that it comprises a moringa extract, juniper extract, red tree extract and persimmon leaf extract.
상기 베이스 재료 40 내지 60 중량%, 상기 바이오매스 재료 10 내지 25 중량%, 상기 탄소섬유 5 내지 10 중량%, 상기 고흡수성 수지 5 내지 10 중량% 및 상기 바인더 5 내지 15 중량%를 포함하는 것을 특징으로 하는, 탄소섬유를 함유하는 기능성 인공배지.The method of claim 1,
40 to 60% by weight of the base material, 10 to 25% by weight of the biomass material, 5 to 10% by weight of the carbon fiber, 5 to 10% by weight of the superabsorbent polymer, and 5 to 15% by weight of the binder A functional artificial medium containing carbon fibers.
상기 베이스 재료, 상기 바이오매스 재료 및 상기 고흡수성 수지는 분쇄되어 1 내지 10mm의 입자크기를 갖는 분말 형태로 사용되고,
상기 탄소섬유는 분쇄되어 1 내지 5mm의 길이를 갖도록 사용되는 것을 특징으로 하는, 탄소섬유를 함유하는 기능성 인공배지.3. The method of claim 2,
The base material, the biomass material, and the superabsorbent resin are pulverized and used in the form of a powder having a particle size of 1 to 10 mm,
The carbon fiber is pulverized, characterized in that used to have a length of 1 to 5 mm, a functional artificial medium containing carbon fibers.
폴리페놀 함유 건조식물 및 광물혼합물 중 적어도 하나를 포함하는 보조 첨가제를 더 포함하고,
상기 폴리페놀 함유 건조식물은 녹차, 도토리 및 선인장 중 적어도 하나의 건조식물을 포함하고,
상기 광물혼합물은 석영, 견운모, 토루말린, 알루미나, 할로이사이트, 카올리나이트, 딕카이트, 산화철, 산화칼슘 및 산화마그네슘 중 적어도 2종 이상의 혼합광물이 소성 및 분쇄되어 제조된 것을 특징으로 하는, 탄소섬유를 함유하는 기능성 인공배지.The method of claim 1,
Further comprising an auxiliary additive comprising at least one of polyphenol-containing dry plants and mineral mixtures,
The polyphenol-containing dried plant includes at least one dried plant of green tea, acorn, and cactus,
The mineral mixture is quartz, sericite, tourumaline, alumina, halloysite, kaolinite, dickite, iron oxide, calcium oxide and magnesium oxide at least two kinds of mixed minerals are calcined and pulverized carbon fiber, characterized in that produced Functional artificial medium containing
상기 베이스 재료 40 내지 60 중량%, 상기 바이오매스 재료 10 내지 25 중량%, 상기 탄소섬유 5 내지 10 중량%, 상기 고흡수성 수지 5 내지 10 중량%, 상기 바인더 5 내지 15 중량%, 상기 폴리페놀 함유 건조식물 5 내지 10 중량%, 및 상기 광물혼합물 5 내지 10 중량%를 포함하는 것을 특징으로 하는, 탄소섬유를 함유하는 기능성 인공배지.6. The method of claim 5,
40 to 60% by weight of the base material, 10 to 25% by weight of the biomass material, 5 to 10% by weight of the carbon fiber, 5 to 10% by weight of the superabsorbent polymer, 5 to 15% by weight of the binder, the polyphenol containing 5 to 10% by weight of dried plants, and 5 to 10% by weight of the mineral mixture, a functional artificial medium containing carbon fibers.