KR102286459B1 - Easy openable cpp film and food package containing the same - Google Patents

Easy openable cpp film and food package containing the same Download PDF

Info

Publication number
KR102286459B1
KR102286459B1 KR1020200160739A KR20200160739A KR102286459B1 KR 102286459 B1 KR102286459 B1 KR 102286459B1 KR 1020200160739 A KR1020200160739 A KR 1020200160739A KR 20200160739 A KR20200160739 A KR 20200160739A KR 102286459 B1 KR102286459 B1 KR 102286459B1
Authority
KR
South Korea
Prior art keywords
film
layer
present
polypropylene
elastomer
Prior art date
Application number
KR1020200160739A
Other languages
Korean (ko)
Inventor
신동욱
도상록
이진호
Original Assignee
주식회사 유상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 유상 filed Critical 주식회사 유상
Priority to KR1020200160739A priority Critical patent/KR102286459B1/en
Application granted granted Critical
Publication of KR102286459B1 publication Critical patent/KR102286459B1/en

Abstract

The present invention relates to an easily-openable multi-layered film and a food package material including the same, and more specifically, to an easily-openable multi-layered film which is produced to be non-oriented by using polypropylene and produced by a 3-layer coextrusion process, and to a food package material including the same. The easily-openable film (UCF-EOF) according to the present invention is a non-oriented multi-layered functional film produced by a 3-layer coextrusion process, wherein package paper, to which the UCF-EOF is applied, has excellent transparency, excellent tensile strength, high surface energy, and excellent lamination process workability, and can be opened with little force, thereby being useful for a product with a risk of causing contents therein to be broken torn during an opening process. In addition, during opening of the package paper, the package paper is opened with a clean opening surface so as to minimize occurrence of film residues, thereby preventing the incorporation of foreign substances. Therefore, the functional film according to the present invention can be widely used for package products for snacks, noodles, bread, and seaweed laver, which can be damaged upon opening or which are required to be easily opened.

Description

용이한 개봉성을 갖는 무연신 필름 및 이를 포함하는 식품 포장재{Easy openable cpp film and food package containing the same}A non-stretched film having easy openability and a food packaging material comprising the same {Easy openable cpp film and food package containing the same}

본 발명은 용이한 개봉성을 갖는 다층 필름 및 이를 포함하는 식품 포장재에 관한 것으로서, 좀 더 상세하게는 폴리프로필렌을 이용하여 무연신, 3-layer 공압출 공정으로 만들어짐으로써 용이한 개봉성을 갖는 다층 필름 및 이를 포함하는 식품 포장재에 관한 것이다.The present invention relates to a multilayer film having easy openability and a food packaging material including the same, and more particularly, to a multilayer film having easy openability and, more particularly, to a polypropylene having easy openability by being made in a non-stretching, 3-layer coextrusion process. It relates to a multilayer film and a food packaging material comprising the same.

식품포장용 필름의 경우에는 우수한 가스차단성, 수분차단성, 투명성 및 인장강도가 요구되고 있다.In the case of food packaging films, excellent gas barrier properties, moisture barrier properties, transparency and tensile strength are required.

종래 식품포장용 필름으로는 대한민국 등록특허 제10-1805047호에서는 (ⅰ) 선형 저밀도 폴리에틸렌 수지로 이루어진 내층, (ⅱ) 폴리아미드 수지, 저밀도 폴리에틸렌 수지 및 고밀도 폴리에틸렌 수지 중에서 선택된 1종의 수지와 접착제 성분을 함유하는 중간층 및 (ⅲ) 폴리아미드 수지로 이루어진 외층들로 구성되는 식품포장용 공압출 다층필름을 게재하고 있으나, 상기 종래의 식품포장용 공압출 다층필름은 생분해성이 부족하여 사용 후 폐기시 환경을 심하게 오염시키는 문제가 있었고, 중간층이 폴리아미드 수지로 구성되면 같은 수지로 이루어진 외층과의 접착성은 우수하나 다른 수지로 이루어진 내층과의 접착성이 나빠지고, 중간층이 폴리에틸렌 수지로 구성되면 반대로 내층과의 접착성은 우수하나 외층과의 접착성이 나빠져 공압출 복합필름의 제조공정이 나빠지는 문제가 있었다.As a conventional food packaging film, in Korean Patent Registration No. 10-1805047, (i) an inner layer made of a linear low-density polyethylene resin, (ii) a polyamide resin, a low-density polyethylene resin, and a high-density polyethylene resin. Although a coextrusion multilayer film for food packaging is disclosed, which consists of an intermediate layer containing and (iii) an outer layer made of polyamide resin, the conventional coextrusion multilayer film for food packaging lacks biodegradability, which severely degrades the environment when discarded after use. There was a problem of contamination, and when the intermediate layer is made of polyamide resin, the adhesion to the outer layer made of the same resin is excellent, but the adhesion to the inner layer made of another resin is poor. Although the property is excellent, there was a problem that the manufacturing process of the coextrusion composite film was deteriorated due to poor adhesion with the outer layer.

또 다른 종래기술로서 대한민국 공개특허 제10-2014-0095925호에 게재된 바와 같이 개질 셀룰로오스외 폴리락틱산의 혼합수지로 구성된 필름을 게재하고 있으나, 상기 종래의 필름은 생분해성 수지들로 이루어져 생분해성은 우수하지만 2층 이상 구조인 복합 필름이 아니고 1층 구조이기 때문에 인장강도 등의 기계적 물성이 부족한 문제가 있었다.As another prior art, as disclosed in Korean Patent Application Laid-Open No. 10-2014-0095925, a film composed of a mixed resin of polylactic acid other than modified cellulose is disclosed. Although excellent, there was a problem in that mechanical properties such as tensile strength were insufficient because it was a one-layer structure rather than a two-layer or more composite film.

또한, 종래의 식품 포장재는 통상 스킨층, 코어층 및 실링층으로 이루어진 CPP 필름 또는 이 CPP 필름 위에 PET 또는 OPP(oriented polypropylene) 필름을 합지하여 파우치를 만들어 사용하여 왔다. 이러한 종래의 무연신 폴리프로필렌 필름은 연신 폴리프로필렌(Oriented Polypropylene, OPP) 필름에 비해 광택이나 투명성은 떨어지지만, 가격이 저렴하고 저온 충격강도 및 열접착이 필요한 포장재에 많이 사용되고 있다.In addition, conventional food packaging materials have been used to make a pouch by laminating a CPP film or a PET or OPP (oriented polypropylene) film on the CPP film or the CPP film comprising a skin layer, a core layer, and a sealing layer. This conventional non-stretched polypropylene film is inferior in gloss or transparency compared to an oriented polypropylene (OPP) film, but is inexpensive and is widely used in packaging materials requiring low-temperature impact strength and thermal bonding.

이때, 실링층은 포장재의 최 내면에 위치하여 내용물을 저장한 후, 실링층을 서로 마주보도록 대면시키고 부위에 열과 압력을 가함으로써 포장재를 밀봉하였다. 상기 실링층은 다른 실링층과 대면시킨 후 소정의 온도로 가열된 실 바(seal bar)로 눌렀을 때 서로 대면하는 실링층의 수지가 녹아 상호 융착하여 밀봉된다. At this time, the sealing layer was located on the innermost surface of the packaging material to store the contents, the sealing layers were faced to face each other, and heat and pressure were applied to the area to seal the packaging material. When the sealing layer is pressed with a seal bar heated to a predetermined temperature after facing the other sealing layer, the resin of the sealing layers facing each other is melted and fused to each other to be sealed.

그러나, 이러한 종래 기술에 의한 식품 포장용 필름은 가스차단성, 수분차단성, 투명성 및 인장강도 등은 어느 정도 확보될 수 있었으나, 과도한 힘을 가하여 개봉하는 과정에서 내용물이 부서지거나 찢어질 위험성이 있고 필름 잔여물(angel hair)을 발생할 우려가 있어서 이러한 점들은 개선할 필요가 있다.However, in the food packaging film according to the prior art, gas barrier properties, moisture barrier properties, transparency, and tensile strength could be secured to some extent, but there is a risk of the contents breaking or tearing in the process of opening by applying excessive force, and the film residue There is a risk of generating angel hair, so these points need to be improved.

한국 등록번호 제10-0270480호(2000년08월02일)Korea Registration No. 10-0270480 (August 02, 2000) 한국 등록번호 제10-1772485호(2017년08월23일)Korea Registration No. 10-1772485 (August 23, 2017) 한국 등록번호 제10-1220670호(2013년01월03일)Korea Registration No. 10-1220670 (January 03, 2013)

본 발명자는 포장 필름에 수반되는 종래 기술의 문제점들을 해소하고, 기능성 등이 우수한 포장 필름을 제공하기 위하여 예의 연구한 결과, 후술하는 바와 같이 제조되는 무연신 다층 필름이 이러한 요건을 만족시킬 수 있음은 물론 우수한 투명도, 우수한 인장강도, 높은 표면에너지, 우수한 라미네이션 공정 작업성을 가질 뿐만 아니라, 적은 힘으로 개봉이 가능하며 개봉과정에서 내용물이 부서지거나 찢어질 위험성이 적고, 또한 개봉시에는 개봉면이 깨끗하여 필름 잔여물(angel hair)을 발생을 최소화하여 이물질 혼입을 방지할 수 있음을 발견하고 본 발명을 완성하기에 이르렀다.As a result of intensive research to solve the problems of the prior art accompanying the packaging film and to provide a packaging film having excellent functionality, the present inventors have found that a non-stretched multilayer film manufactured as described below can satisfy these requirements. Of course, it has excellent transparency, excellent tensile strength, high surface energy, and excellent lamination process workability. It was found that it was possible to prevent the mixing of foreign substances by minimizing the generation of film residue (angel hair), and led to the completion of the present invention.

따라서, 본 발명의 목적은, 물론 우수한 투명도, 우수한 인장강도, 높은 표면에너지, 우수한 라미네이션 공정 작업성을 가질 뿐만 아니라, 적은 힘으로 개봉이 가능하며 개봉과정에서 내용물이 부서지거나 찢어질 위험성이 적고, 또한 개봉시에는 개봉면이 깨끗하여 필름 잔여물(angel hair)을 발생을 최소화하여 이물질 혼입을 방지할 수 있는 무연신 필름을 제공하는 것에 있다.Therefore, an object of the present invention is, of course, excellent transparency, excellent tensile strength, high surface energy, and excellent lamination process workability, as well as being able to open with little force, and the risk of breaking or tearing the contents during the opening process is small, Another object of the present invention is to provide a non-stretched film capable of preventing the mixing of foreign substances by minimizing the occurrence of film residues (angel hair) because the opening surface is clean upon opening.

위와 같은 본 발명의 목적은, 일면에 있어서The object of the present invention as described above, in one aspect

폴리프로필렌 또는 폴리프로필렌과 엘라스토머로 이루어진 스킨층;a skin layer made of polypropylene or polypropylene and an elastomer;

폴리프로필렌으로 이루어진 코어층; 및a core layer made of polypropylene; and

폴리프로필렌, 엘라스토머 및 첨가제 또는 폴리프로필렌, 폴리에틸렌, 엘라스토머 및 첨가제로 이루어진 실링층으로 이루어진 것을 특징으로 하는 무연신 필름에 의해 달성될 수 있다.It can be achieved by a non-stretched film characterized in that it consists of polypropylene, an elastomer and an additive or a sealing layer made of polypropylene, polyethylene, an elastomer and an additive.

본 발명에 따른 용이한 개봉성을 갖는 필름(UCF-EOF)은 무연신, 3-lay 공압출 공정으로 만들어진 다층 기능성 필름으로, UCF-EOF가 적용된 포장지는 우수한 투명도, 우수한 인장강도, 높은 표면에너지, 우수한 라미네이션 공정 작업성을 가지며, 적은 힘으로 개봉이 가능하며 개봉과정에서 내용물이 부서지거나 찢어질 위험성이 있는 제품에 특히 유용하다. 또한, 개봉시에는 개봉면이 깨끗하여 필름 잔여물(angel hair)을 발생을 최소화하여 이물질 혼입을 방지할 수 있다. The film with easy opening (UCF-EOF) according to the present invention is a multilayer functional film made by a non-stretching, 3-lay co-extrusion process, and the wrapping paper to which UCF-EOF is applied has excellent transparency, excellent tensile strength, and high surface energy. , It has excellent lamination process workability, can be opened with little force, and is particularly useful for products with a risk of breaking or tearing the contents during the opening process. In addition, when opening, the opening surface is clean to minimize the generation of film residues (angel hair), thereby preventing the mixing of foreign substances.

따라서, 본 발명에 따른 기능성 필름은 스낵, 라면, 빵, 김 포장 제품 등의 개봉시 제품이 손상될 우려가 있거나 손쉬운 개봉을 요하는 제품에 널리 사용될 수 있다.Therefore, the functional film according to the present invention can be widely used in products that may be damaged or require easy opening upon opening of snacks, ramen, bread, seaweed packaging products, and the like.

도 1은 본 발명에 따른 기능성 다층 필름의 층 구조를 나타내는 단면 설명도이다.
도 2는 본 발명의 용이 개봉성을 설명하는 도면이다.
도 3은 본 발명의 기능성 다층 필름의 제조 공정을 나타내는 공정 설명도이다.
도 4는 본 발명에 따른 포장지의 내면의 개봉 상태를 설명하는 사진이다. 1 is a cross-sectional explanatory view showing a layer structure of a functional multilayer film according to the present invention.
It is a figure explaining the easily openability of this invention.
3 is a process explanatory diagram showing the manufacturing process of the functional multilayer film of the present invention.
4 is a photograph illustrating the opened state of the inner surface of the wrapping paper according to the present invention.

본 발명은, 일면에 있어서,The present invention, in one aspect,

폴리프로필렌 또는 폴리프로필렌과 엘라스토머로 이루어진 스킨층;a skin layer made of polypropylene or polypropylene and an elastomer;

폴리프로필렌으로 이루어진 코어층; 및a core layer made of polypropylene; and

폴리프로필렌, 엘라스토머 및 첨가제 또는 폴리프로필렌, 폴리에틸렌, 엘라스토머 및 첨가제로 이루어진 실링층으로 이루어진 것을 특징으로 하는 무연신 필름을 제공한다.Provided is a non-stretched film comprising a sealing layer made of polypropylene, elastomer and additives or polypropylene, polyethylene, elastomer and additives.

본 발명은, 다른 일면에 있어서, The present invention, in another aspect,

상기 필름은 용이한 개봉성을 가지며, 식품용으로 사용되는 것을 특징으로 하는 무연신 필름을 제공한다.The film has an easy opening property, and provides a non-stretched film, characterized in that it is used for food.

본 발명은, 추가의 다른 일면에 있어서, The present invention, in a further further aspect,

상기 필름의 두께는 20 ~ 80㎛이고, 두께를 기준으로 상기 스킨층은 10~40%, 상기 코어층은 20~80%, 상기 실링층은 10~40%로 이루어진 것을 특징으로 하는 무연신 필름을 제공한다.The thickness of the film is 20 ~ 80㎛, based on the thickness of the skin layer is 10 ~ 40%, the core layer is 20 ~ 80%, the sealing layer is a non-stretched film, characterized in that consisting of 10 ~ 40% provides

본 발명은, 추가의 다른 일면에 있어서, The present invention, in a further further aspect,

상기 엘라스토머는 폴리올레핀 엘라스토머, 프로필렌-에틸렌 코폴리머 또는 이들의 혼합물이고, 상기 첨가제는 AB제, 슬립제 또는 이들의 혼합물인 것을 특징으로 하는 무연신 필름을 제공한다.The elastomer is a polyolefin elastomer, a propylene-ethylene copolymer, or a mixture thereof, and the additive is an AB agent, a slip agent, or a mixture thereof.

본 발명은, 추가의 다른 일면에 있어서, The present invention, in a further further aspect,

열접착 강도가 100℃~160℃에서, 50~560 gf/15mm인 것을 특징으로 하는 무연신 필름을 제공한다.It provides a non-stretched film, characterized in that the thermal adhesive strength is 100 ℃ ~ 160 ℃, 50 ~ 560 gf / 15mm.

본 발명은, 다른 추가의 일면에 있어서 상기 무연신 필름; 및The present invention, the unstretched film in another further aspect; and

A1 증착층으로 된 최외층(40)이 적층되어 이루어진 것을 특징으로 하는 식품 포장용 포장재 및 상기 무연신 필름; 및 상기 무연신 필름의 최외층에 PET 필름 또는 연신 폴리프로필렌 필름이 적층되어 있는 것을 특징으로 하는 식품 포장용 포장재를 제공한다.A packaging material for food packaging and the non-stretched film, characterized in that the outermost layer 40 of the A1 deposition layer is laminated; And it provides a packaging material for food packaging, characterized in that the PET film or the stretched polypropylene film is laminated on the outermost layer of the unstretched film.

이하, 본 발명에 따른 무연신 필름 및 이를 포함하는 포장재에 관하여 첨부 도면을 참조하여 더욱 구체적으로 설명한다.Hereinafter, the unstretched film according to the present invention and a packaging material including the same will be described in more detail with reference to the accompanying drawings.

본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이므로, 본 출원 시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.The terms or words used in the present specification and claims are not to be construed as limited in their ordinary or dictionary meanings, and on the principle that the inventor can appropriately define the concept of the term in order to best describe his invention. It should be interpreted as meaning and concept consistent with the technical idea of the present invention. Therefore, since the embodiments described in this specification and the configurations shown in the drawings are only the most preferred embodiment of the present invention, it is understood that there may be various equivalents and modifications that can be substituted for them at the time of the present application. shall.

본 발명에 따른 무연신 다층 필름은 우수한 투명도, 우수한 인장강도, 높은 표면에너지, 우수한 라미네이션 공정 작업성을 가질 뿐만 아니라, 적은 힘으로 개봉이 가능하며 개봉과정에서 내용물이 부서지거나 찢어질 위험성이 적고, 또한 개봉시에는 개봉면이 깨끗하여 필름 잔여물(angel hair)을 발생을 최소화하여 이물질 혼입을 방지할 수 있다.The non-stretched multilayer film according to the present invention not only has excellent transparency, excellent tensile strength, high surface energy, and excellent lamination process workability, but also can be opened with little force, and the risk of breaking or tearing the contents during the opening process is small, In addition, when opening, the opening surface is clean to minimize the generation of film residues (angel hair), thereby preventing the mixing of foreign substances.

도 1은 본 발명에 따른 기능성 다층 필름의 층 구조를 나타내는 단면 설명도이고, 도 2는 본 발명의 용이 개봉성을 설명하는 도면이며, 도 3은 본 발명의 기능성 다층 필름의 제조 공정을 나타내는 공정 설명도이며, 도 4는 본 발명에 따른 포장지의 내면의 개봉 상태를 설명하는 사진이다. 1 is a cross-sectional explanatory view showing the layer structure of the functional multilayer film according to the present invention, FIG. 2 is a view for explaining the easy opening of the present invention, and FIG. 3 is a process showing the manufacturing process of the functional multilayer film of the present invention It is an explanatory view, and FIG. 4 is a photograph explaining the opening state of the inner surface of the wrapping paper according to the present invention.

도 1에 나타낸 바와 같이, 본 발명에 따른 무연신 다층 필름(이하, "UCF-EOF"라고 도 함)은 크게 스킨층(10, 코어층(20) 및 실링층(30)으로 이루어진다.As shown in FIG. 1 , the unstretched multilayer film (hereinafter, also referred to as “UCF-EOF”) according to the present invention is largely composed of a skin layer 10 , a core layer 20 , and a sealing layer 30 .

상기 스킨층(10)은 본 발명에 따른 CPP 필름의 외부 표면에 해당하며, 상기 스킨층(10)은 필요에 따라 진공 증착되는 알루미늄과 이종의 필름과 라미네이션시 우수한 접착력을 갖는 것이 더욱 바람직하다.The skin layer 10 corresponds to the outer surface of the CPP film according to the present invention, and it is more preferable that the skin layer 10 has excellent adhesion during lamination with a film of a different type and aluminum that is vacuum-deposited if necessary.

상기 스킨층(10)은 폴리프로필렌 단독 또는 폴리프로필렌과 엘라스토머로 이루어지는 것이 바람직할 수 있다.The skin layer 10 may be made of polypropylene alone or polypropylene and an elastomer.

상기 엘라스토머는 폴리올레핀 엘라스토머, 프로필렌-에틸렌 코폴리머 또는 이들의 혼합물을 사용함으로써 실링시 비카트 연화점을 낮출 수 있다. 따라서, 스킨층의 조성물로 엘라스토머를 첨가하여 접착력을 증대시킬 수 있다.The elastomer may lower the Vicat softening point during sealing by using a polyolefin elastomer, a propylene-ethylene copolymer, or a mixture thereof. Accordingly, the adhesive force may be increased by adding an elastomer to the composition of the skin layer.

상기 폴리올레핀 엘라스토머는 올레핀 블록 코폴리머(Infuse DOW 케미칼사 제품, GARDE 명: INFUSE 9507, MI 5.0, 밀도 0.866g/㎤), 에틸렌 알파 올레핀 코폴리머(Tafmer Mitsui 케미칼사 제품, GRADE 명 A-4085S, MI6.7g/10min, 밀도 0.8885g/㎤) 등을 사용할 수 있다.The polyolefin elastomer is an olefin block copolymer (manufactured by Infuse DOW Chemical, GARDE name: INFUSE 9507, MI 5.0, density 0.866 g/cm3), ethylene alpha olefin copolymer (manufactured by Tafmer Mitsui Chemicals, GRADE name A-4085S, MI6) .7 g/10 min, density 0.8885 g/cm 3 ) and the like can be used.

상기 프로필렌-에틸렌 코폴리머의 엘라스토머는 비카트 연화점(Vicat softening point)이 60℃인 수지로서 프로필렌-부텐-에틸렌 터폴리머에 비하여 비카트 연화점이 약 55℃ 정도 낮다.The elastomer of the propylene-ethylene copolymer is a resin having a Vicat softening point of 60°C, and has a Vicat softening point of about 55°C lower than that of the propylene-butene-ethylene terpolymer.

상기 엘라스토머가 사용되는 경우 스킨층의 조성물의 전체량을 기준으로 5~40 중량%로 포함되는 것이 바람직하고, 40중량% 이상에서는 필름에 Tacky로 인한 블로킹 발생의 우려가 있다.When the elastomer is used, it is preferably included in an amount of 5 to 40% by weight based on the total amount of the composition of the skin layer, and at 40% by weight or more, there is a risk of blocking due to tacky in the film.

상기 코어층(20)은 필름의 기재로서 역할하고 인장 및 신장율, 필름의 스티프니스에 영향을 주며 고객이 원하는 스티프니스에 따라 호모 폴리프로필렌, 랜덤 폴리프로필렌, 블록 코폴리머 폴리프로필렌을 포함할 수 있고, 호모 폴리프로필렌을 포함하는 것이 특히 바람직할 수 있다.The core layer 20 serves as a base material for the film and affects the tensile and elongation rates, and the stiffness of the film. It may be particularly preferred to include polypropylene.

상기 실링층(30)은 실 바(seal bar)로 눌렀을 때 수지가 열에 의해 녹아 수지간의 융착이 이루어져하기 때문에 특히 저온 열접착성이 우수해야 한다.Since the sealing layer 30 is melted by heat when pressed with a seal bar, and fusion between the resins is formed, it should have excellent low-temperature thermal adhesiveness.

이러한 요건을 만족시키는 성분으로서는 폴리프로필렌, 엘라스토머 및 첨가제 또는 폴리프로필렌, 폴리에틸렌, 엘라스토머 및 첨가제로 이루어진 수지 조성물을 사용할 수 있다.As a component satisfying these requirements, polypropylene, an elastomer and an additive or a resin composition composed of polypropylene, polyethylene, an elastomer and an additive may be used.

더욱 바람직하게는 실링층(30)은 폴리프로필렌 25~60 중량%, 폴리에틸렌 0~20 중량%, 엘라스토머 35~65 중량%, 및 첨가제 3~7 중량%를 포함하는 것이 바람직할 수 있다.More preferably, the sealing layer 30 may include 25 to 60% by weight of polypropylene, 0 to 20% by weight of polyethylene, 35 to 65% by weight of elastomer, and 3 to 7% by weight of additives.

상기 엘라스토머는 상기 스킨층(10)에서 설명한 바와 같다.The elastomer is the same as described for the skin layer 10 .

상기 폴리올레핀 엘라스토머는 실링 과정에서 접착 성능을 증대시키는 것으로서, 올레핀 블록 코폴리머(Infuse DOW 케미칼사 제품, GARDE 명: INFUSE 9507, MI 5.0, 밀도 0.866g/㎤), 에틸렌 알파 올레핀 코폴리머(Tafmer Mitsui 케미칼사 제품, GRADE 명 A-4085S, MI6.7g/10min, 밀도 0.8885g/㎤) 등을 사용할 수 있다.The polyolefin elastomer increases adhesive performance during the sealing process, and an olefin block copolymer (manufactured by Infuse DOW Chemical, GARDE name: INFUSE 9507, MI 5.0, density 0.866 g/cm 3 ), ethylene alpha olefin copolymer (Tafmer Mitsui Chemical) Company product, grade name A-4085S, MI6.7g/10min, density 0.8885g/cm3), etc. can be used.

상기 프로필렌-에틸렌 코폴리머의 엘라스토머는 비카트 연화점(Vicat softening point)이 60℃인 수지로서 프로필렌-부텐-에틸렌 터폴리머에 비하여 비카트 연화점이 약 55℃ 정도 낮다.The elastomer of the propylene-ethylene copolymer is a resin having a Vicat softening point of 60°C, and has a Vicat softening point of about 55°C lower than that of the propylene-butene-ethylene terpolymer.

상기 엘라스토머는 실링층의 조성물의 전체량을 기준으로 35~65 중량%로 포함되는 것이 바람직하고, 65중량% 이상에서는 포장지 특성을 열화시킬 우려가 있다.The elastomer is preferably included in an amount of 35 to 65% by weight based on the total amount of the composition of the sealing layer, and in an amount of 65% by weight or more, there is a risk of deteriorating the properties of the wrapping paper.

따라서, 이러한 실링층의 적정한 조성물을 사용하여 실링 속도를 높일 수 있어 포장 생산성을 현저히 향상시킬 수 있다.Therefore, it is possible to increase the sealing speed by using an appropriate composition of the sealing layer, thereby remarkably improving the packaging productivity.

상기 첨가제는 블로킹 방지제, 슬립제 또는 이들의 혼합물을 상기 실링층의 전체 중량을 기준으로 3~7 중량%로 사용하는 것이 바람직할 수 있다.As the additive, it may be preferable to use an anti-blocking agent, a slip agent, or a mixture thereof in an amount of 3 to 7 wt % based on the total weight of the sealing layer.

상기 블로킹 방지제는 블로킹 방지 및 슬립성 부여를 위해 첨가되는 것으로서, 포장재의 보관 및 이송 중에 롤 상태로 권취 후 사용시 풀 때 내층과 외층의 블로킹을 방지함은 물론, 식품 포장용으로 사용시 필름의 수지 상호간이 대면한 상태에서 실링한 후 포장재 내에 내용물을 투입하기 위해 입구 개봉을 용이하게 한다.The anti-blocking agent is added to prevent blocking and impart slip properties, and prevents blocking of the inner and outer layers when unwinding after winding in a roll state during storage and transportation of packaging materials After sealing in a face-to-face state, it facilitates opening of the entrance to put the contents into the packaging material.

상기 블로킹 방지제는 통상적으로 사용되는 것이라면 본 발명에서도 적합하게 적용할 수 있다. 예를 들면, 이들에 한정되지 않으나, 정일프라콤사의 AB1305PM3, 탄산칼슘 CaCO3, 탈크(Talc), 실리카(SiO2), 알루미늄실리케이트, 및 실리콘 비드 등을 들 수 있다. 이들 블로킹 방지제는 단독으로 사용할 수 있음은 물론, 2 이상을 혼합하여 사용할 수도 있다.The antiblocking agent can be suitably applied in the present invention as long as it is commonly used. For example, although not limited to these, AB1305PM3 manufactured by Jeongil Pracom, calcium carbonate CaCO 3 , talc (Talc), silica (SiO 2 ), aluminum silicate, and silicon beads may be mentioned. These antiblocking agents can be used independently, of course, two or more can also be mixed and used for it.

상기 슬립제는 통상적으로 사용되는 것이라면 본 발명에서도 적합하게 적용할 수 있다. 예를 들면, 이들에 한정되지 않으나, 에루카아마이드, 올레아마이드, 스테아마이드 등을 들 수 있다.The slip agent can be suitably applied in the present invention as long as it is commonly used. For example, although not limited to these, erucamide, oleamide, stearamide, etc. are mentioned.

상기 첨가제의 함량이 3중량% 미만으로 포함하는 경우, 블로킹 방지성 및 슬립성이 충분하지 못하고, 포장재 내로의 식품 봉입을 위한 포장재의 개봉이 용이하지 않아 작업성을 저하시킬 수 있다. 한편，블로킹 방지제의 함량이 10중량%를 초과하는 경우에는 필름의 내층 상에 열접착 온도가 높아져 저온 열접착을 방해하고 필름의 투명도 저하 및 증착 후 광택도를 떨어뜨릴 수 있다When the content of the additive is less than 3% by weight, blocking prevention and slip properties are not sufficient, and it is not easy to open the packaging material for encapsulating food in the packaging material, thereby reducing workability. On the other hand, when the content of the anti-blocking agent exceeds 10% by weight, the thermal bonding temperature on the inner layer of the film is increased to prevent low-temperature thermal bonding, and the transparency of the film may be lowered and the glossiness after deposition may be lowered.

상기 무연신 폴리프로필렌 필름은 두께가 20 내지 80㎛이고, 두께를 기준으로 상기 스킨층은 10~40%, 상기 코어층은 20~80%, 상기 실링층은 10~40%로 이루어진 것이 바람직할 수 있다.The unstretched polypropylene film has a thickness of 20 to 80 μm, and based on the thickness, the skin layer is preferably composed of 10 to 40%, the core layer is composed of 20 to 80%, and the sealing layer is composed of 10 to 40%. can

한편，본 발명에서 얻어지는 포장재용 무연신 필름의 두께는 반드시 이에 한정하는 것은 아니지만, 20 ㎛ 이상의 두께를 갖는 것이 바람직하다. 20 ㎛ 미만의 두께를 갖는 필름은 그 제조에 비용 증가를 야기하여 경제적인 생산이 용이하지 않다. 한편, 상기 무연신 필름의 두께는 그 상한을 특별히 한정하지 않으며, 본 발명의 내층을 적용함에는 특별한 제한이 없다. 다만, 상기 필름의 두께가 80㎛를 초과하는 두께를 갖는 경우에는 이를 사용하여 실링함에 있어서 고속 포장에 적합하지 않을 수 있다. 상기 무연신 필름은 20 내지 30㎛의 두께를 갖는 것이 제조 용이성 및 고속 포장성의 관점에서 더욱 바람직할 수 있다.On the other hand, the thickness of the unstretched film for packaging material obtained in the present invention is not necessarily limited thereto, but preferably has a thickness of 20 μm or more. A film having a thickness of less than 20 mu m causes an increase in cost in its manufacture, so that economical production is not easy. On the other hand, the thickness of the unstretched film does not specifically limit the upper limit, and there is no particular limitation in applying the inner layer of the present invention. However, when the film has a thickness exceeding 80 μm, it may not be suitable for high-speed packaging in sealing using the film. It may be more preferable that the unstretched film has a thickness of 20 to 30 μm in terms of ease of manufacture and high-speed packaging.

상기 스킨층(10)의 경우, 너무 얇게 구비되면 PET 등 라미네이션 강도가 저하되거나 AL 증착 Bonding Strength 문제가 생기는 단점이 있다. 또한, 설정한 범위를 초과하는 경우 너무 두껍게 구비되어 필름의 스티프니스와 가공 적성이 저하되는 단점이 있다.In the case of the skin layer 10, if it is provided too thinly, lamination strength such as PET is lowered or AL deposition bonding strength problem occurs. In addition, if it exceeds the set range, there is a disadvantage in that the film stiffness and processing aptitude are deteriorated because it is provided too thickly.

상기 코어층(20)의 경우, 20중량% 이하로 구비될 경우, 스티프니스가 낮아져 필름 형성이 어려울 수 있고, 두께비가 9%를 초과하는 경우, 다른 층들의 비율이 낮아져 원하는 물성을 제공하기 어렵다.In the case of the core layer 20, when it is provided at 20% by weight or less, it may be difficult to form a film due to low stiffness.

상기 실링층(30)은 10%이하에서는 접착성이 낮아 접착이 용이하게 이루어지지 않는 단점이 있다. The sealing layer 30 has a disadvantage in that adhesion is not easily achieved due to low adhesion at 10% or less.

한편, 본 발명의 무연신 필름은 상기 스킨층(10)의 표면에 알루미늄 증착층을 더 포함시켜 식품 포장재를 제공할 수 있다.On the other hand, the non-stretched film of the present invention can provide a food packaging material by further including an aluminum deposition layer on the surface of the skin layer (10).

증착필름이란, 고진공상태에서 임의의 금속을 융점 이상으로 가열하면 금속은 증기로 되어 산소 및 질소 분자와 충돌 없이 수십 cm정도 직진 비산하여 냉각된 피증착판에 분자상태로 응결하여 얇은 금속피막을 형성하는 것을 이용한 것을 말한다.When a metal is heated above its melting point in a high vacuum, the metal becomes vapor and scatters straight for several tens of centimeters without colliding with oxygen and nitrogen molecules. It says using what

이러한 식품 포장재는 상기 무연신 폴리프로필렌 필름; 및 Al 증착층으로 된 최외층(40); 및 이 적층되어 이루어지는 것이 바람직하다.These food packaging materials include the unstretched polypropylene film; and an outermost layer 40 made of an Al deposited layer; and it is preferably laminated.

상기 Al 증착층은 산소, 수증기 배리어성이 우수하여 배리어 층으로서의 기능을 제공한다. 상기 증착층은 일반적으로 약 380Å의 두께로 증착될 수 있다. 이때, 광학밀도(optical density, 0D)는 2.2 내지 2.3의 값을 갖는 것이 바람직하다.The Al deposition layer has excellent oxygen and water vapor barrier properties, and thus provides a function as a barrier layer. The deposition layer may be generally deposited to a thickness of about 380 Å. At this time, the optical density (optical density, 0D) preferably has a value of 2.2 to 2.3.

상기 A1 증착층(40)은 스킨층(10)의 폴리프로필렌의 분자 구조로 인하여 A1 증착층과의 결합력이 높아지게 된다. The A1 deposition layer 40 has a higher bonding strength with the A1 deposition layer due to the molecular structure of the polypropylene of the skin layer 10 .

A1 증착층은 무연신 필름상에 코로나 처리를 수행한 후에 증착하게 되는데, 이때, 코로나 처리에 의한 표면 산화에 의해 극성기를 도입함으로써 A1 증착층 형성을 보다 용이하게 할 수 있다.The A1 deposition layer is deposited after corona treatment is performed on the unstretched film. At this time, the A1 deposition layer can be more easily formed by introducing a polar group by surface oxidation by corona treatment.

한편, 본 발명의 추가의 실시형태에 따른 포장용 포장재는 상기 무연신 폴리프로필렌 필름; 및 상기 무연신 폴리프로필렌 필름의 최외층에 PET 필름 또는 연신 폴리프로필렌(oriented polypropylene, OPP) 필름이 적층된 것을 포함한다.On the other hand, the packaging material according to a further embodiment of the present invention is the unstretched polypropylene film; and a PET film or an oriented polypropylene (OPP) film laminated on the outermost layer of the non-oriented polypropylene film.

포장되는 내용물에 따라 요구되는 추가적 기능을 부여하기 위해, 이와 다른 층 구조를 가질 수도 있음은 본 발명이 속하는 기술 분야의 당업자에게는 자명할 것이다. It will be apparent to those skilled in the art that the present invention may have a layer structure different from this in order to provide additional functions required according to the contents to be packaged.

상기 본 발명에 따른 무연신 스킨층(10) 상에 PET 필름 또는 OPP 필름, BOPP 필름 등의 1차 제품을 적층함으로써, 식품 포장용 포장재를 얻을 수 있다. 이때, 상기 외층 상의 1차 제품은 접착제에 의해 적층될 수도 있다.By laminating a primary product such as a PET film, an OPP film, or a BOPP film on the non-stretched skin layer 10 according to the present invention, a packaging material for food packaging can be obtained. At this time, the primary product on the outer layer may be laminated by an adhesive.

위와 같은 포장재 필름은 상기 외층 상에 접착제에 의한 CPP 필름의 적층이나 A1 증착층의 증착 등의 공정을 수행하기 전에 필요에 따라 코로나 처리를 수행할 수 있다. 상기 코로나 처리는 무극성인 폴리프로필렌이나 폴리에틸렌 등으로 된 본 발명의 포장재 필름의 표면을 물리적으로 개질하여 극성을 부여함으로써 접착력을 향상시켜 주는 역할을 제공한다. 이에 의해 본 발명의 포장재 필름에 대하여 후가공시, 접착제 접착력 향상, 잉크 접착력 향상 및 알루미늄 증착시접착력 향상 등의 효과를 얻을 수 있다.The above packaging film may be subjected to corona treatment if necessary before performing a process such as lamination of a CPP film by an adhesive on the outer layer or deposition of an A1 deposition layer. The corona treatment provides a role of improving adhesion by physically modifying the surface of the packaging material film of the present invention made of non-polar polypropylene or polyethylene, etc. to give polarity. Thereby, it is possible to obtain effects such as an improvement in adhesive strength, an improvement in ink adhesion, and an improvement in adhesion during aluminum deposition during post-processing of the packaging film of the present invention.

이하, 본 발명에 따른 무연신 필름의 제조 방법에 관련하여 구체적으로 설명한다.Hereinafter, a method for manufacturing a non-stretched film according to the present invention will be described in detail.

본 발명에 따른 무연신 필름은 압출 라미네이션(=T-Die) 공법에 의한 제조하는 것이 바람직할 수 있다.The unstretched film according to the present invention may be preferably manufactured by extrusion lamination (=T-Die) method.

도 3의 무연신 필름 제조공정도에 나타낸 바와 같이, 상기와 같은 원료 조성물을 각각의 사일로(1)에 넣고, 압출기(2)로 압출하게 되는데, 이때, 용융되지 않은 수지가 통과하지 못하도톡 필터링(3)하면서 압출기(2)를 통해 T-다이(4)로 공압출하여 외층/중간층/내층의 3층 구조의 CPP 필름을 형성한다.As shown in the non-stretched film manufacturing process diagram of FIG. 3, the raw material composition as described above is put into each silo 1 and extruded with an extruder 2, at this time, the unmelted resin does not pass through filtering ( 3) while co-extruding with a T-die (4) through an extruder (2) to form a CPP film having a three-layer structure of outer layer/middle layer/inner layer.

이어서, 상기 T-다이로 압출된 용융된 수지를 35℃로 급속히 냉각시켜 결정을 형성하여 캐스팅함으로써(5) 필름으로 형성한다.Then, the molten resin extruded with the T-die is rapidly cooled to 35° C. to form crystals and cast (5) to form a film.

B-ray(6)를 통해 목표로 하는 두께로 형성된 필름의 두께를 측정하고 균일하게 조절한 후, 얻어진 필름의 표면을 코로나 처리기(7)로 처리하고, 필름 표면에 존재하는 이물질을 검출기(8)를 통해 검출 제거하고, 얻어진 필름을 와인더(winder)(9)로 권취하여 필름을 제조한다.After measuring and uniformly adjusting the thickness of the film formed to a target thickness through B-ray (6), the surface of the obtained film is treated with a corona treatment machine (7), and foreign substances present on the surface of the film are detected by a detector (8) ) through detection and removal, and winding the obtained film with a winder (9) to prepare a film.

이와 같이 본 발명의 CPP 필름은 종래의 포장재에서 얻을 수 있는 기본적인 물성(투명성, 인장강도, 열접착강도)를 유지하면서 열접착 온도를 현저히 낮출 수 있어서 생산성이 우수하다.As described above, the CPP film of the present invention has excellent productivity because it can significantly lower the thermal bonding temperature while maintaining the basic physical properties (transparency, tensile strength, thermal bonding strength) obtained from conventional packaging materials.

실시예Example

이하, 본 발명을 실시예를 들어 보다 구체적으로 설명한다. 그러나, 이러한 실시예는 본 발명을 구체적인 예를 들어 설명하고자 하는 것으로서, 이에 의해 본 발명을 한정하고자 하는 것이 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples. However, these examples are intended to illustrate the present invention with specific examples, and are not intended to limit the present invention thereby.

실시예 1 내지 6 및 비교예: 무연신 필름의 제조Examples 1 to 6 and Comparative Examples: Preparation of unstretched films

다음과 같이 표 1에 나타낸 바의 조성 및 함량의 원료를 준비하여 무연신 필름을 3-레이 공압출 방식으로 제조하였다.Raw materials having the composition and content shown in Table 1 were prepared as follows, and a non-stretched film was prepared by a 3-ray co-extrusion method.

스킨층(10): 폴리프로필렌 단독 또는 폴리프로필렌 + 엘라스토머Skin layer 10: polypropylene alone or polypropylene + elastomer

코어층(20): 폴리프로필렌 단독Core layer 20: polypropylene alone

실링층(30): 폴리프로필렌 + (폴리에틸렌) + 엘라스토머 + 첨가제Sealing layer 30: polypropylene + (polyethylene) + elastomer + additives

　 　 실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 실시예5Example 5 실시예6Example 6 비교예comparative example 　
스킨층
(10~40%)
skin layer
(10-40%) 폴리프로필렌polypropylene 100100 9595 9090 9090 7575 100100 100100 엘라스토머elastomer -- 55 1010 1010 3535 -- -- 코어층
(20~80%)core layer
(20-80%) 폴리프로필렌polypropylene 100100 100100 100100 100100 100100 100100 100100 실링층
(10~40%)sealing layer
(10-40%) 폴리프로필렌polypropylene 6060 4545 4545 3030 3030 2525 100100 폴리에틸렌polyethylene -- -- -- -- -- 2020 -- 엘라스토머elastomer 3535 5050 5050 6565 6565 5050 -- 첨가제　additive 5　5 5　5 5　5 5　5 5　5 55 --

시험예 1: 열접착 강도 시험Test Example 1: Thermal bonding strength test

상기 실시예 1 내지 6 및 비교예에 의해 얻어진 필름에 대하여 열접착 강도를 측정하고, 그 결과를 표 2에 나타내었다. The thermal bonding strength was measured for the films obtained in Examples 1 to 6 and Comparative Examples, and the results are shown in Table 2.

　 　 실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 실시예5Example 5 실시예6Example 6 비교예comparative example 열접착강도
(gf/15mm)heat bonding strength
(gf/15mm) 100℃100℃ 부착안됨not attached 5050 5555 100100 130130 150150 부착안됨not attached 110℃110℃ 부착안됨not attached 150150 160160 150150 190190 200200 부착안됨not attached 120℃120℃ 100100 290290 315315 200200 210210 350350 부착안됨not attached 130℃130℃ 405405 530530 550550 400400 450450 580580 500500 140℃140℃ 550550 540540 555555 410410 480480 590590 600600 150℃150℃ 580580 560560 560560 420420 475475 585585 660660 160℃160℃ 600600 545545 555555 430430 485485 590590 660660 용이개봉성easy opening 있음has exist 있음has exist 있음has exist 있음has exist 있음has exist 있음has exist 있음has exist 없음does not exist

상기 시험 결과로 부터 확인되는 바와 같이, 본 발명의 필름은 비교예의 것에 비하여 열접착 온도의 범위가 넓고 열접착 강도가 우수하였으며, 열접착부의 개봉이 용이하였다.As can be seen from the above test results, the film of the present invention has a wider range of thermal bonding temperature and excellent thermal bonding strength compared to that of Comparative Example, and opening of the thermal bonding portion is easy.

시험예 2: 필름간 층간 접착 시험Test Example 2: Interlayer adhesion test between films

상기 실시예 1 내지 6 및 비교예에 의해 얻어진 필름을 PE 압출코팅 라미네이션으로 PET 필름과 접착 후 PE접착층과 실험 대상 필름의 층간 접착력 시험을 진행하였다. 그 결과를 표 3에 나타내었다.After bonding the films obtained in Examples 1 to 6 and Comparative Examples to the PET film by PE extrusion coating lamination, an interlayer adhesion test between the PE adhesive layer and the test subject film was performed. The results are shown in Table 3.

실시예1Example 1 실시예2Example 2 실시예3Example 3 실시예4Example 4 실시예5Example 5 실시예6Example 6 비교예comparative example 필름간 접착강도(gf/15mm))Adhesive strength between films (gf/15mm)) 140140 180180 220220 235235 260260 155155 120120

상기 시험결과로부터 확인되는 바와 같이, 본 발명의 필름은 비교예의 것에 비하여 필름간 접착강도가 우수했으며 특히 스킨층에 엘라스토머가 증가할수록 필름간 접착강도가 우수하였다As can be seen from the above test results, the film of the present invention was superior in adhesive strength between films compared to that of Comparative Example, and in particular, as the amount of elastomer in the skin layer increased, the adhesive strength between films was excellent.

이와 같이 본 발명은 도면 및 명세서를 통하여 발명의 바람직한 실시형태를 예를 들어 설명하였으나, 본 발명의 기술 분야에서 통상의 지식을 가진 자라면 다양한 변형 및 균등한 실시가 가능함은 자명하다.As described above, the present invention has been described with reference to the drawings and the specification for preferred embodiments of the invention, but it is apparent that various modifications and equivalent implementations are possible by those skilled in the art of the present invention.

10: 스킨층
20: 코어층
30: 실링층
40: 증착층10: skin layer
20: core layer
30: sealing layer
40: deposition layer

Claims (7)

폴리프로필렌과 엘라스토머로 이루어진 스킨층;
폴리프로필렌으로 이루어진 코어층; 및
폴리프로필렌, 엘라스토머 및 첨가제로 이루어진 실링층;으로 이루어지고,
상기 스킨층에서 엘라스토머의 함량은 스킨층의 조성물의 전체량을 기준으로 5~40 중량%로 포함되고,
상기 실링층은 폴리프로필렌 25~60 중량%, 엘라스토머 35~65 중량%, 및 첨가제 3~7 중량%를 포함하며,
상기 엘라스토머는 폴리올레핀 엘라스토머, 프로필렌-에틸렌 코폴리머 또는 이들의 혼합물이고, 상기 첨가제는 AB제, 슬립제 또는 이들의 혼합물이며,
필름의 두께는 20 ~ 80㎛이고, 두께를 기준으로 상기 스킨층은 10~40%, 상기 코어층은 20~80%, 상기 실링층은 10~40%로 이루어지고, 열접착 강도가 100℃~160℃에서 50~560 gf/15mm인 것을 특징으로 하는 식품용 무연신 필름.a skin layer made of polypropylene and elastomer;
a core layer made of polypropylene; and
A sealing layer made of polypropylene, an elastomer, and an additive; consists of,
The content of the elastomer in the skin layer is included in an amount of 5 to 40% by weight based on the total amount of the composition of the skin layer,
The sealing layer comprises 25 to 60% by weight of polypropylene, 35 to 65% by weight of elastomer, and 3 to 7% by weight of additives,
wherein the elastomer is a polyolefin elastomer, a propylene-ethylene copolymer, or a mixture thereof, and the additive is an AB agent, a slip agent, or a mixture thereof;
The thickness of the film is 20 ~ 80㎛, the skin layer is 10 ~ 40% based on the thickness, the core layer is 20 ~ 80%, the sealing layer is made of 10 ~ 40%, the thermal adhesive strength is 100 ℃ Unstretched film for food, characterized in that 50 to 560 gf / 15mm at ~160 ℃. 삭제delete 삭제delete 삭제delete 삭제delete 청구항 1에 따른 무연신 필름; 및
A1 증착층으로 된 최외층이 적층되어 이루어진 것을 특징으로 하는 식품 포장용 포장재.The unstretched film according to claim 1; and
A packaging material for food packaging, characterized in that the outermost layer of the A1 deposition layer is laminated. 청구항 1에 따른 무연신 필름; 및
상기 무연신 필름의 최외층에 PET 필름 또는 연신 폴리프로필렌 필름이 적층되어 있는 것을 특징으로 하는 식품 포장용 포장재.The unstretched film according to claim 1; and
A packaging material for food packaging, characterized in that a PET film or a stretched polypropylene film is laminated on the outermost layer of the unstretched film.
KR1020200160739A 2020-11-26 2020-11-26 Easy openable cpp film and food package containing the same KR102286459B1 (en)