KR102239754B1 - Composition for making miniature - Google Patents
Composition for making miniature Download PDFInfo
- Publication number
- KR102239754B1 KR102239754B1 KR1020200153286A KR20200153286A KR102239754B1 KR 102239754 B1 KR102239754 B1 KR 102239754B1 KR 1020200153286 A KR1020200153286 A KR 1020200153286A KR 20200153286 A KR20200153286 A KR 20200153286A KR 102239754 B1 KR102239754 B1 KR 102239754B1
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- present
- weight
- miniature
- starch
- Prior art date
Abstract
Description
본 발명은 직접 손으로 원하는 형상을 만든 후 일정 시간이 지나면 자연 경화되어 다양한 모형, 예를 들어, 미니어처를 제작할 수 있는 조성물에 관한 기술이다.The present invention relates to a composition capable of producing various models, for example, miniatures, which are naturally cured after a certain period of time after making a desired shape by hand.
더욱 구체적으로는 수지 성분을 포함하여 이루어지되, 사용자가 형상을 만드는 동안에는 손 또는 기계를 이용하여 작업해도 되며, 형상의 완성 후 대기 중에서 일정 시간이 지나면 굳어져 물에 용해되지도 않으며, 플라스틱 제품처럼 굳어진 상태를 유지하는 자연경화형 미니어처 제작용 조성물에 관한 기술이다.More specifically, it contains a resin component, but while the user makes a shape, it can be worked by hand or machine. After the shape is completed, it hardens after a certain period of time in the atmosphere and does not dissolve in water, like a plastic product. It is a technology related to a composition for producing a naturally curable miniature that maintains a hardened state.
본 발명은 각종 모형, 캐릭터, 토핑(topping) 등을 제작할 수 있는 조소 조성물에 관한 기술이다. 본 발명은 실제로 점토를 포함하지 않으면서 점토와 같이 모형 제작이 가능하고, 일정 시간이 지난 후 굳어지는 성질을 갖는 수지 성분을 포함하는 조소 조성물에 관한 기술로서, 안료 및 염료의 혼합이 용이하여 자신이 원하는 모든 색상을 구현할 수 있다. 본 발명의 조성물은 각종 캐릭터, 건축 모형 등의 다양한 축소 모형을 제조할 수 있으나, 본 발명에서는 설명의 편의상 "미니어처"로 통칭하기로 한다. The present invention relates to a sculptural composition capable of producing various models, characters, toppings, and the like. The present invention is a technology related to a sculpting composition containing a resin component having a property that can be modeled like clay without actually including clay, and has a hardening property after a certain period of time, and it is easy to mix pigments and dyes. You can implement any color you want. The composition of the present invention can produce various reduced models such as various characters and architectural models, but in the present invention, it will be collectively referred to as "miniature" for convenience of description.
어린이의 미술 교육에 사용되거나, 각종 모형 제작을 위한 용도로 사용되는 점토는 일반적으로 사용자가 손으로 원하는 형태로 변형시켜 조형물을 제조하고, 일정 시간이 지나 건조가 완료되면 굳어져서 형상을 유지하는 것을 특징으로 한다. 점토의 예로, 찰흙이 있는데, 높은 비중의 무기계 물질인 찰흙은 운반 및 조형성이 용이하지 못하다는 단점을 가지며, 또한 건조과정에서 찰흙 내의 물이 빠르게 증발하여 작업을 할 수 있는 시간이 촉박하고, 조형물의 표면이 갈라지거나 쉽게 부스러지는 등의 문제점이 있다. Clay used for children's art education or for making various models is generally used to make sculptures by transforming it into a shape desired by the user by hand, and to harden and maintain the shape when drying is completed after a certain period of time. It is characterized. As an example of clay, there is clay. Clay, which is an inorganic material with a high specific gravity, has the disadvantage that it is not easy to transport and form. Also, water in the clay evaporates rapidly during the drying process, so the time to work is short, and the sculpture There are problems such as cracking or easily crushing of the surface.
상술한 전통적인 점토의 문제점을 개선하기 위하여 중공미세구, 폴리비닐알콜, 겔화제 및 물 등으로 구성된 경량 점토가 제안된 바 있다. 경량 점토는 저비중의 중공 미세구를 충전제로 사용하여 점토의 무게를 많이 감소시켜 점토의 운반성과 조형성을 크게 개선했다. 또한, 수용성 고분자인 폴리비닐알콜을 사용하여 점토의 유연성이 탁월하고, 수분의 증발에 의한 조형물의 수축되는 정도가 아주 작아 표면 갈라짐이 적다는 특징을 가지고 있다. 하지만, 상기 경량 점토는 사용시 손에 부착되고, 쉽게 굳어 변형이 용이하지 않으며, 탄력성이 지나쳐 원하는 형태로 늘어나는 것이 힘들며, 늘어난 표면에 평활성이 없으며, 외력에 의해 쉽게 부러뜨려지는 등의 변형 내구성이 없어 제작된 작품이 안정적으로 유지하는 것이 불가능하다는 단점이 있었다.In order to improve the problems of the above-described traditional clay, a lightweight clay composed of hollow microspheres, polyvinyl alcohol, a gelling agent, and water has been proposed. Lightweight clay uses low specific gravity hollow microspheres as a filler, greatly reducing the weight of the clay, greatly improving the transportability and formability of the clay. In addition, the use of polyvinyl alcohol, which is a water-soluble polymer, has excellent flexibility, and the degree of shrinkage of the sculpture due to evaporation of moisture is very small, and surface cracking is small. However, the lightweight clay adheres to the hand when in use, hardens easily and is not easy to deform, it is difficult to stretch into a desired shape due to excessive elasticity, there is no smoothness on the stretched surface, and there is no deformation durability such as easily broken by external force. There was a disadvantage that it was impossible to keep the produced work stable.
상기 경량 점토의 문제점을 해결하고자 특허등록 제0978692호는 폴리비닐알콜계 수지, 점도 조정제, 물 및 경량화재를 함유하는 경량 조형재료를 개시하였으나, 수분의 양 및 건조 속도의 조절이 어려워 조형물의 변형 내구성이 떨어지는 문제점이 있었다.In order to solve the problem of the lightweight clay, Patent Registration No. 0978692 discloses a lightweight molding material containing a polyvinyl alcohol resin, a viscosity modifier, water and a lightweight fire, but it is difficult to control the amount of moisture and the drying speed. There was a problem of poor durability.
또한, 산업용에서 사용하는 미니어처 재료로서 아파트, 건축 등의 설계 이전에 축소 모형을 만들기 위한 조소 조성물로서, PVA에 붕사(sodium tetraborate)를 혼합하여 만들어지는 미니어처 조성물은 붕사로 인해 피부에 자극을 줄 수 있으며, 어린이가 실수로 섭취하는 경우 인체에 해를 끼칠 수 있다. 또한, 장시간 작업을 하는 경우 피부 자극으로 인한 피부 갈라짐이 일어나기 때문에 전문적으로 장시간 동안 미니어처를 제작하는 사람들에게는 피부 트러블을 해결할 수 있는 미니어처 제작용 조성물의 개발이 필요했다.In addition, as a miniature material used in industry, it is a sculptural composition for making a scaled-down model before designing apartments and buildings. A miniature composition made by mixing sodium tetraborate with PVA can irritate the skin due to borax. And, if children accidentally consume it, it can harm the human body. In addition, since skin cracking due to skin irritation occurs when working for a long time, it is necessary to develop a composition for producing miniatures capable of solving skin problems for those who professionally manufacture miniatures for a long time.
본 발명은 모형 제작 후 자연경화되는 미니어처 제작용 조성물로서, 친환경적이며 피부에 자극이 없는 조성물을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a composition for producing a miniature that is naturally cured after making a model, which is environmentally friendly and does not irritate the skin.
또한, 본 발명에서는 종래 기술에서는 미니어처 제작용 조성물의 빠른 경화 시간으로 인해 작업 시간에 제약이 많았으며, 조형물이 경화 이후 쉽게 갈라지고 파손되는 문제점이 있었으나, 본 발명은 상기의 문제점을 해결한 신규한 미니어처 제작용 조성물를 제공하는 것을 목적으로 한다.In addition, in the present invention, in the prior art, there were many restrictions on working time due to the fast curing time of the composition for producing miniatures, and there was a problem that the sculpture was easily cracked and damaged after curing, but the present invention solves the above problems. It is an object of the present invention to provide a composition for producing miniatures.
특히, 본 발명은 프탈레이트 가소제, 보레이트, 납 등의 인체 및 환경에 유해한 물질을 포함하지 않으며, 종래 기술에 비해 친환경적인 재료가 많이 포함된 미니어처 제작용 조성물을 제공하는 것을 목적으로 한다.In particular, an object of the present invention is to provide a composition for manufacturing a miniature that does not contain substances harmful to the human body and environment such as phthalate plasticizer, borate, lead, etc., and contains a lot of environmentally friendly materials compared to the prior art.
특히, 종래 기술에서는 장기간 보관하면 곰팡이가 피거나, 오래되면 본드 냄새 등 악취가 나는 문제점이 있었으나, 본 발명은 상기한 문제점을 해결한 미니어처 제작용 조성물을 제공하는 것을 목적으로 한다.In particular, in the prior art, there is a problem that mold occurs when stored for a long period of time, or a bad smell such as a bond odor occurs when it is old, but an object of the present invention is to provide a composition for manufacturing a miniature that solves the above problems.
본 발명은 물 15 ~ 35 중량%; 폴리비닐아세테이트 15 ~ 40 중량%; 전분 30 ~ 60 중량%; 바인더 1 ~ 15% 및 트레할로스 1 ~ 10 중량%를 포함하는 자연경화형 미니어처 제작용 조성물을 제공한다.The present invention is water 15 to 35% by weight; 15 to 40% by weight of polyvinyl acetate; 30-60% by weight of starch; It provides a composition for producing a naturally curable miniature containing 1 to 15% of a binder and 1 to 10% by weight of trehalose.
특히, 본 발명에서 상기 바인더는 아크릴계 바인더 또는 우레탄계 바인더일 수 있다.In particular, in the present invention, the binder may be an acrylic binder or a urethane binder.
특히, 본 발명에서는 왁스 5 ~ 15 중량% 더 첨가할 수 있다.Particularly, in the present invention, 5 to 15% by weight of wax may be further added.
특히, 본 발명에서는 프로판디올 1 ~ 5 중량% 더 첨가할 수 있다.Particularly, in the present invention, 1 to 5% by weight of propanediol may be further added.
특히, 본 발명에서는 아연 1 ~ 10%를 더 첨가할 수 있다.In particular, 1 to 10% of zinc may be further added in the present invention.
특히, 본 발명에서는 물과 수지성분의 유화제로서, 중성지방산 트리글리세라이드, 유기산 모노글리세라이드, 글리세린지방산에스테르, 폴리옥시에틸렌지방산에스테르, 프로필렌글리콜지방산 에스테르, 의약품용 유화제 및 화장품용 유화제 중 어느 하나 이상을 1 ~ 5 중량% 더 포함할 수 있다.In particular, in the present invention, as an emulsifier of water and resin components, any one or more of triglycerides of neutral fatty acids, monoglycerides of organic acids, glycerin fatty acid esters, polyoxyethylene fatty acid esters, propylene glycol fatty acid esters, emulsifiers for pharmaceuticals and emulsifiers for cosmetics It may further contain 1 to 5% by weight.
본 발명의 조성물은 종래 문제가 되었던 성분인 붕사를 사용하지 않고 아크릴 바인더 또는 우레탄계 바인더로 대체하며, 여기에 트레할로스를 혼합하여 종래 제품에 비해 피부 자극이 덜하며 보습 효과까지 갖는다.The composition of the present invention does not use borax, which has been a conventional problem, but is replaced with an acrylic binder or a urethane-based binder, and trehalose is added thereto to reduce skin irritation and even have a moisturizing effect compared to conventional products.
또한, 본 발명에서는 전분을 주성분의 하나로 사용함으로써, 수지 성분인 폴리비닐아세테이트를 종래 기술보다 상대적으로 적게 사용할 수 있는 장점이 있다. 특히, 전분은 수지 성분과는 달리 인체에 해를 미칠 가능성이 없는 친환경적인 재료라는 장점이 있다. In addition, in the present invention, by using starch as one of the main components, there is an advantage in that polyvinyl acetate, which is a resin component, can be used relatively less than in the prior art. In particular, unlike resin components, starch has the advantage of being an eco-friendly material that does not have the potential to harm the human body.
도 1은 본 발명의 조성물을 이용한 다양한 케이크 형상의 미니어처의 사진이다.
도 2a 내지 2e는 본 발명의 조성물을 손으로 만져서 곰 형상의 미니어처를 만드는 과정을 촬영한 사진이다.1 is a photograph of miniatures of various cake shapes using the composition of the present invention.
2A to 2E are photographs of a process of making a bear-shaped miniature by touching the composition of the present invention by hand.
본 발명은 물 15 ~ 35 중량%; 폴리비닐아세테이트 15 ~ 40 중량%; 전분 30 ~ 60 중량%; 바인더 1 ~ 15% 및 트레할로스 1 ~ 10 중량%를 포함하는 자연경화형 미니어처 제작용 조성물을 제공한다.The present invention is water 15 to 35% by weight; 15 to 40% by weight of polyvinyl acetate; 30-60% by weight of starch; It provides a composition for producing a naturally curable miniature containing 1 to 15% of a binder and 1 to 10% by weight of trehalose.
본 발명에서는 폴리비닐아세테이트를 수지 성분으로 사용한다. 폴리비닐아세테이트는 전체 조성물 총량 중 15~40 중량% 범위로 사용될 수 있다. In the present invention, polyvinyl acetate is used as a resin component. Polyvinyl acetate may be used in the range of 15 to 40% by weight of the total amount of the composition.
본 발명에서는 종래 사용되던 붕사 대신에 바인더로서 아크릴계 바인더 또는 우레탄계 바인더를 1 ~ 15% 사용할 수 있다. In the present invention, 1 to 15% of an acrylic binder or a urethane binder may be used as a binder instead of borax that has been conventionally used.
물은 상기 복합 수지와 먼저 혼합한 후 다른 성분들과 혼합되는 것이 바람직한데, 물과 상기 수지의 혼합 상태는 일종의 에멀젼 상태로 볼 수 있으며, 물은 전체 조성물 총량 중 15 ~ 35 중량% 내에서 상기 복합 수지보다 같거나 적은 양으로 사용되는 것이 바람직하다.It is preferable that water is first mixed with the composite resin and then mixed with other components.The mixed state of water and the resin can be seen as a kind of emulsion, and water is within 15 to 35% by weight of the total composition. It is preferably used in an amount equal to or less than that of the composite resin.
또한, 물과 수지의 혼합을 위한 유화제로서 중성지방산 트리글리세라이드, 유기산 모노글리세라이드, 글리세린지방산에스테르, 폴리옥시에틸렌지방산에스테르, 프로필렌글리콜지방산 에스테르, 의약품용 유화제 및 화장품용 유화제 중 어느 하나 이상을 1 ~ 5 중량% 더 포함할 수 있다.In addition, as an emulsifier for mixing water and resin, one or more of neutral fatty acid triglyceride, organic acid monoglyceride, glycerin fatty acid ester, polyoxyethylene fatty acid ester, propylene glycol fatty acid ester, pharmaceutical emulsifier and cosmetic emulsifier 1 ~ It may further contain 5% by weight.
한편, 본 발명에서는 조소 조형물의 충전제(몸체) 역할을 하는 물질로서, 전분을 사용하는 것을 특징으로 한다. 전분은 인체에 무해할 뿐만 아니라, 수성 및 유성 잉크와 모두 혼합이 가능하여 색채 표현이 자유롭다. 본 발명에서 전분은 감자 전분, 옥수수 전분, 고구마 전분, 밀 전분 등 다양한 전분이 모두 사용 가능하며, 혼합 사용도 가능하다. 전분은 전체 총 조성물 중 30 ~ 60 중량%가 바람직하며, 전술한 바와 같이 수지 성분보다는 소량 많게 사용하는 것이 바람직하다.On the other hand, in the present invention, as a material that serves as a filler (body) for the sculptured sculpture, it is characterized in that starch is used. Starch is not only harmless to the human body, and can be mixed with both water-based and oil-based inks, so color expression is free. In the present invention, the starch in the present invention can be used in any of a variety of starches, such as potato starch, corn starch, sweet potato starch, wheat starch, etc., it is also possible to use a mixture. Starch is preferably 30 to 60% by weight of the total composition, and as described above, it is preferable to use a small amount more than the resin component.
본 발명에서는 트레할로스를 1 ~ 10 중량% 포함한다. 트레할로스( trehalose)는 포도당 2분자로 구성된 이당류로서 녹말로부터 트레할로스를 저렴하게 추출하는 기술을 개발되어 근래 사용이 증가하는 성분이다. 트레할로스는 높은 보습 능력을 갖추고 있으며, 식품, 화장품, 의약품에 사용된다. 본 발명에서는 트레할로스의 보습성을 이용함으로써 작업자의 피부에 보습 효과를 부여하는 것을 특징으로 한다. 종래 화장품 분야에서는 트레할로스의 사용이 알려졌지만, 본 발명과 같은 모형을 제작하기 위한 미니어처 제작용 조성물 분야에서는 트레할로스의 사용은 전혀 알려진 바가 없는 신규한 기술임이 명백하다.In the present invention, 1 to 10% by weight of trehalose is included. Trehalose (trehalose) is a disaccharide composed of two molecules of glucose, and it is a component that has been increasingly used in recent years due to the development of a technology to extract trehalose from starch inexpensively. Trehalose has a high moisturizing ability and is used in foods, cosmetics, and pharmaceuticals. In the present invention, by using the moisturizing properties of trehalose, it is characterized in that a moisturizing effect is given to the skin of a worker. Although the use of trehalose has been known in the conventional cosmetic field, it is clear that the use of trehalose is a novel technology that is not known at all in the field of a composition for producing miniatures for producing a model like the present invention.
특히, 본 발명에서는 왁스를 5 ~ 15 중량% 더 첨가할 수 있다. 왁스는 석유계왁스, 광물계왁스, 식물성왁스, 동물성왁스 등 다양한 왁스가 모두 사용 가능하다. 왁스는 조성물의 혼합성을 높여줄 뿐만 아니라, 전분과 마찬가지로 조성물의 충전제 역할을 한다. 예를 들어, 밀랍, 카나우바 왁스 등의 천연 왁스를 사용하는 것이 사용자의 피부 트러블을 방지할 수 있어 바람직한 왁스의 예로 사용될 수 있다.In particular, in the present invention, 5 to 15% by weight of wax may be further added. As for the wax, various waxes such as petroleum wax, mineral wax, vegetable wax, and animal wax can be used. Wax not only enhances the blendability of the composition, but, like starch, acts as a filler for the composition. For example, using a natural wax such as beeswax or carnauba wax can prevent skin troubles of a user, and thus may be used as an example of a preferred wax.
본 발명에서는 아연 1 ~ 10%를 더 첨가할 수 있다. 아연은 본 조성물이 혼합될 때 활성이 우수하고 첨가율에 따라 굳는 시간을 조절할 수 있고 다른 물질과 혼합이 잘 되도록 하는 분산제의 역할이 우수하다. 또한, 아연을 포함하는 경우 각종 염료와의 혼합성이 높아져 조성물의 다양한 색상 구현에 유리하다. 아연은 산화아연 또는 스테아린산아연 형태로 사용될 수 있다. In the present invention, 1 to 10% of zinc may be further added. Zinc is excellent in activity when the composition is mixed, and the hardening time can be adjusted according to the addition rate, and it has an excellent role as a dispersant to make it well mixed with other substances. In addition, when zinc is included, mixing with various dyes increases, which is advantageous for realizing various colors of the composition. Zinc can be used in the form of zinc oxide or zinc stearate.
본 발명에서는 프로판디올을 1 ~ 5 중량% 더 첨가할 수 있다. 프로판디올은 점도 조절, 보습제 역할, 제품의 발림성을 높여주는 역할을 할 뿐만 아니라, 특히, 미니어처 조소들은 곰팡이가 피는 것을 방지하기 위해 방부제를 첨가하는데 프로판디올은 아주 강력한 방부제 역할을 한다.In the present invention, 1 to 5% by weight of propanediol may be further added. Propanediol not only plays a role in controlling viscosity, acting as a moisturizing agent, and enhancing the spreadability of the product. In particular, miniature sculptures add preservatives to prevent mold growth. Propanediol acts as a very strong preservative.
도 1은 본 발명의 조성물을 이용하여 다양한 케이크 모형의 미니어처의 사진이며, 도 2a 내지 도 2e는 곰 모형의 미니어처를 제작하는 단계를 촬영한 사진이다. 본 발명의 조성물은 손으로 직접 모형을 만든 후, 채색을 하여 미니어처를 완성할 수 있다. 본 발명의 조성물은 손으로 모형을 만든 후 일정 시간이 경과하면 자연 경화하여 단단하게 굳기 때문에 미니어처로서 소장할 수 있다.1 is a photograph of a miniature of various cake models using the composition of the present invention, and FIGS. 2A to 2E are photographs taken in steps of manufacturing a miniature of a bear model. The composition of the present invention can be made by hand and then painted to complete a miniature. The composition of the present invention can be stored as a miniature because it naturally hardens and hardens after a certain period of time after making a model by hand.
이하에서는 실험예를 통하여 본 발명에 대하여 더욱 자세히 설명하기로 한다.Hereinafter, the present invention will be described in more detail through experimental examples.
실험예 : 경도 실험Experimental example: hardness test
본 발명의 조성물의 경화도를 측정하기 실시예 샘플들을 평판 형태로 만든 후 대기 중에서 충분히 자연경화시킨 후 경도를 측정하였다.Measuring the degree of curing of the composition of the present invention Example samples were made into a flat plate shape and then sufficiently naturally cured in the atmosphere, and then the hardness was measured.
아세테이트Polyvinyl
acetate
비닐알콜Poly
Vinyl alcohol
(kg/mm2)Hardness
(kg/mm 2 )
** 상기 각 수치는 중량%임** Each value above is a weight percent
위 표의 결과를 보면, 트레할로스의 함량이 줄어듦에 따라 경도가 미세하게 낮아지기는 하나, 약 4 kg/mm2으로 경도가 낮아 자연경화 후에도 탄성을 유지하는 것을 알 수 있었다. 한편, 종래 시판되는 PVA와 붕사를 포함하는 조소 조성물(구입제품의 특성상 비교예의 경우 성분들의 구체적인 함량비는 확인할 수 없었음)을 구입하여 본 발명의 실시예와 비교하기 위하여 전체 중량 중 40%가 되도록 전분을 더 추가한 후 경도를 테스트한 결과 23(kg/mm2)로 매우 경도가 높아 자연경화 후 미니어처의 탄성(휨성)이 부족한 것을 알 수 있었다.Looking at the results in the table above, it was found that the hardness slightly decreased as the content of trehalose decreased, but the hardness was low at about 4 kg/mm 2 , and it was found that the elasticity was maintained even after natural curing. Meanwhile, 40% of the total weight was purchased by purchasing a sculpting composition containing PVA and borax that are commercially available in the past (in the case of the comparative example due to the characteristics of the purchased product, the specific content ratio of the ingredients could not be confirmed). As a result of testing the hardness after adding more starch as possible, it was found that the hardness was very high at 23 (kg/mm 2 ), and the elasticity (bendability) of the miniature after natural hardening was insufficient.
또한, 본 발명의 실시예의 경우 자연경화 후에도 육안 관찰 결과 갈라짐이 발생하지 않고 미니어처 제작 직후의 형상을 그대로 유지하고 있었다.In addition, in the case of the embodiment of the present invention, even after natural curing, no cracking occurred as a result of visual observation, and the shape of the miniature was maintained as it was.
또한, 약 5시간의 미니어처 제작 작업 후에 작업자의 손을 씻은 후 손을 육안 검사한 결과, 손에 본 발명의 조성물이 묻지 않았을 뿐만 아니라, 피부 갈라짐도 관찰되지 않아 본 발명의 조성물의 보습 효과를 확인할 수 있었다.In addition, as a result of visual inspection of the hands after washing the hands of the worker after about 5 hours of miniaturization work, not only did not the composition of the present invention come into contact with the hands, but also no cracking of the skin was observed, confirming the moisturizing effect of the composition of the present invention. Could.
Claims (5)
폴리비닐아세테이트 15 ~ 40 중량%;
전분 30 ~ 60 중량%;
바인더 1 ~ 15%; 및
트레할로스 1 ~ 10 중량%을 포함하며,
상기 바인더는 아크릴계 바인더 또는 우레탄계 바인더이며,
프로판디올을 1 ~ 5 중량% 및 아연 1 ~ 10%를 더 포함하는,
자연경화형 미니어처 제작용 조성물.
15 to 35% by weight of water;
15 to 40% by weight of polyvinyl acetate;
30-60% by weight of starch;
Binder 1-15%; And
Contains 1 to 10% by weight of trehalose,
The binder is an acrylic binder or a urethane binder,
Further comprising 1 to 5% by weight of propanediol and 1 to 10% of zinc,
Composition for producing naturally curable miniatures.
In claim 1, 5 to 15% by weight of the wax is further added, the composition for producing a naturally curable miniature.