KR102207013B1 - Water-Impermeable Waterproof Asphalt Concrete Compositions Comprising Crum Rubber Modifier and Constructing Methods Using Thereof - Google Patents

Water-Impermeable Waterproof Asphalt Concrete Compositions Comprising Crum Rubber Modifier and Constructing Methods Using Thereof Download PDF

Info

Publication number
KR102207013B1
KR102207013B1 KR1020200138379A KR20200138379A KR102207013B1 KR 102207013 B1 KR102207013 B1 KR 102207013B1 KR 1020200138379 A KR1020200138379 A KR 1020200138379A KR 20200138379 A KR20200138379 A KR 20200138379A KR 102207013 B1 KR102207013 B1 KR 102207013B1
Authority
KR
South Korea
Prior art keywords
parts
weight
asphalt
waste tire
concrete composition
Prior art date
Application number
KR1020200138379A
Other languages
Korean (ko)
Inventor
이동현
Original Assignee
(주)이도엔지니어링
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)이도엔지니어링 filed Critical (주)이도엔지니어링
Priority to KR1020200138379A priority Critical patent/KR102207013B1/en
Application granted granted Critical
Publication of KR102207013B1 publication Critical patent/KR102207013B1/en

Abstract

The present invention provides a water-impermeable waterproof asphalt concrete composition comprising waste tire powder. The water-impermeable waterproof asphalt concrete composition comprises, based on 100 parts by weight of asphalt: 1 to 25 parts by weight of waste tire powder; 1 to 25 parts by weight of styrene butadiene styrene; 1 to 25 parts by weight of a petroleum resin; 500 to 2,000 parts by weight of aggregates; 30 to 150 parts by weight of fine powder aggregates; 0.1 to 2 parts by weight of cellulose fiber; 0.1 to 2 parts by weight of wax; and 0.1 to 2 parts by weight of a rubber anti-aging agent. The water-impermeable waterproof asphalt concrete composition according to the present invention, specifically, the water-impermeable waterproof asphalt concrete composition comprising waste tire powder has good waterproof performance and durability through water-impermeable properties, can prevent plastic deformation, aging, and/or peeling from occurring easily, can enable a placing process to be easily carried out at low costs, can prevent pavement subsidence, and can secure support force.

Description

폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 및 이의 시공방법{Water-Impermeable Waterproof Asphalt Concrete Compositions Comprising Crum Rubber Modifier and Constructing Methods Using Thereof}Water-Impermeable Waterproof Asphalt Concrete Compositions Comprising Crum Rubber Modifier and Constructing Methods Using Thereof}

본 발명은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것으로서, 보다 상세하게는 아스팔트 콘크리트 조성물의 물성을 향상시키기 위한 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 및 이의 시공방법에 관한 것이다.The present invention relates to an impermeable waterproof asphalt concrete composition including waste tire powder and a construction method thereof, and more particularly, to an impermeable waterproof asphalt concrete composition including waste tire powder for improving the physical properties of the asphalt concrete composition, and a construction method thereof It is about.

일반적으로 아스팔트는 유기화합물과 미량의 무기화합물 등이 포함된 수천 종 이상의 고분자 탄화수소(C-H)가 매우 복잡하게 구성된 흑색 또는 흑갈색 고체 또는 반고체의 열가소성 물질로서 가열하게 되면 서서히 액상으로 변화되는 특성을 갖는다.In general, asphalt is a black or dark brown solid or semi-solid thermoplastic material composed of a very complex composition of thousands or more of high molecular hydrocarbons (C-H) containing organic compounds and trace amounts of inorganic compounds, and has the property of gradually changing to a liquid state when heated.

상기 아스팔트는 천연 아스팔트, 석유계 아스팔트 및 포장용 타르와 같은 종류로 나눠지며 스트레이트 아스팔트, 유화 아스팔트가 널리 알려져 있다.The asphalt is divided into natural asphalt, petroleum-based asphalt and paving tar, and straight asphalt and emulsified asphalt are widely known.

또한 상기 아스팔트는 점착성이 뛰어나고 광물질 재료와의 부착성이 우수하기 때문에 결합재료나 접착재료로 이용되며, 물에 용해되지 않고 불투수성이므로 방수재료로도 이용되며, 사용목적에 따라 점도를 변화시킬 수 있어 그 활용범위가 다양하고 도로 포장용, 방수용, 일반 공업용, 농업용 등의 다양한 용도로 사용되고 있다.In addition, the asphalt is used as a bonding material or an adhesive material because it has excellent adhesion and excellent adhesion to mineral materials, and is also used as a waterproof material because it is not soluble in water and is impermeable, and the viscosity can be changed according to the purpose of use. Its application range is diverse, and it is used for various purposes such as road pavement, waterproofing, general industrial use, and agricultural use.

도로 포장용으로 사용되는 아스팔트는 석유계 아스팔트로 접착성, 신장성(伸張性), 흡투수(吸透水)가 우수한 스트레이트 아스팔트가 일반적으로 사용된다.Asphalt used for road pavement is petroleum-based asphalt, straight asphalt having excellent adhesion, extensibility, and water absorption is generally used.

그러나, 스트레이트 아스팔트는 연화점이 낮고, 온도감온성이 크고, 내후성이 약하고, 응집력이 약한 단점을 가지고 있으므로 이를 보완하고, 사용하는 곳의 특성에 맞도록 다양한 개질재를 첨가하여 사용되고 있다.However, since straight asphalt has a low softening point, high temperature sensitivity, low weather resistance, and low cohesive strength, it is supplemented and used by adding various modifiers to suit the characteristics of the place where it is used.

일반적으로 아스팔트 개질재의 종류로는 고무계열, 열가소성수지계열, 열경화성수지계열, 탄화수소계열, 필러계열, 섬유계열, 산화방지제, 환원제 등이 있으며 고무계열에는 천연고무, Styrene Butadiene Rubber(SBR), 폐타이어(Crumb Rubber) 등을 사용하며, 열가소성수지계열에는 Styrene Butadiene Styrene(SBS), Ethylenevinylacetate(EVA), Polyethylene(PE), Polypropylene(PP), Polyvinyl Chloride(PVC), Polyethylene Terephthalate(PET) 등이 사용되며, 열경화성수지계열에는 에폭시수지, 우레탄수지, 아크릴수지, 페놀수지, 석유수지 등이 이용되며 탄화수소계열에는 천연아스팔트, 길소나이트 등이 있다.In general, the types of asphalt modifiers include rubber, thermoplastic resin, thermosetting resin, hydrocarbon, filler, fiber, antioxidant, reducing agent, and natural rubber, styrene butadiene rubber (SBR), and waste tires. (Crumb Rubber), etc. are used, and Styrene Butadiene Styrene (SBS), Ethylenevinylacetate (EVA), Polyethylene (PE), Polypropylene (PP), Polyvinyl Chloride (PVC), Polyethylene Terephthalate (PET), etc. are used for the thermoplastic resin series. , Epoxy resin, urethane resin, acrylic resin, phenol resin, petroleum resin, etc. are used in the thermosetting resin series, and natural asphalt and gilsonite are used in the hydrocarbon series.

하지만, 지금까지 개발된 아스팔트 개질재는 사계절의 큰 기온차이에 의하여 시공 후 시간이 지나면 아스팔트가 저온균열과 피로균열에 대한 저항성이 감소되어 나타나는 포장의 균열 및 소성변형에 대한 문제점을 가지고 있으며, 공기와 햇빛에 노출됨으로써 발생되는 아스팔트 산화, 부착력 약화에 의한 골재탈리 등의 문제점이 나타나며 또한, 현장투입식 개질재(Plant-mix type)는 균일한 품질의 확보가 용이하지 않고, 사전혼합식(Premixtype) 개질 아스팔트는 구성물을 균일한 혼합이 쉽지 않고 개질재와 아스팔트 등의 각각의 구성물이 물리적인 결합에 의존하기에 저장성이 떨어져 보존에 어려움이 있다.However, the asphalt modifiers developed so far have problems with cracks and plastic deformation of the pavement, which appears as asphalt decreases resistance to low-temperature cracks and fatigue cracks after construction due to the large temperature difference of the four seasons. There are problems such as oxidation of asphalt caused by exposure to sunlight and aggregate desorption due to weakening of adhesion. In addition, the plant-mix type is not easy to secure uniform quality, and premix type In the modified asphalt, it is difficult to uniformly mix the constituents, and because each constituent such as the modifying material and asphalt relies on physical bonding, it is difficult to preserve due to poor storage properties.

특히, 2000년 이후 속경성 시멘트와 폴리머로 콘크리트의 성능을 개선한 개질콘크리트가 개발되었으며, 짧은 경화시간과 높은 투수저항성, 동결융해저항성 등으로 인하여 콘크리트 도로구조물의 보수재료로 널리 사용되고 있다.In particular, since 2000, modified concrete, which has improved the performance of concrete with fast-setting cement and polymer, has been developed, and has been widely used as a repair material for concrete road structures due to its short curing time, high water permeability and freezing and thawing resistance.

그러나 상기 개질콘크리트는 다량의 라텍스를 포함하므로 비용이 고가이고, 열반사율이 높아 동절기 초기결빙에 대한 예방효과가 종래 아스팔트 콘크리트보다 미비하며, 열흡수율이 낮아 우리나라와 같이 외기온도변화(일교차, 4계절)가 심한 환경에서는 온도응력으로 인하여 균열, 표면박리, 탈락(포트홀) 등이 발생한다는 문제점이 있다.However, since the modified concrete contains a large amount of latex, the cost is high, and the heat reflectance is high, so the prevention effect of early freezing in winter is inferior to that of conventional asphalt concrete, and the heat absorption rate is low, as in Korea, as in Korea In an environment where) is severe, there is a problem that cracks, surface peeling, and falling out (portholes) occur due to temperature stress.

더욱이, 일부 교량이나 특수지역 중 지/정체가 심하고 중 차량 비율이 높은 교통조건에서는 일반 개질아스팔트(Polymer-modified asphalt: PMA) 포장도 견디기 어려운 곳이 있다.Moreover, in some bridges and special areas where the ground/congestion is severe and the heavy vehicle ratio is high, it is difficult to withstand general modified asphalt (PMA) pavement.

따라서 매우 강한 아스팔트 포장을 두껍게 시공해야하나 일반 아스팔트 포장의 경우 두꺼운 것뿐만 아니라 자체적으로 탄성(Elasticity), 인성(Toughness) 및 인장강도(Tensile strength) 등이 강해야 한다.Therefore, a very strong asphalt pavement should be constructed thick, but in the case of general asphalt pavement, not only should it be thick, but also have strong elasticity, toughness, and tensile strength.

일반적으로 강상판(Steel box girder) 교량은 물론 콘크리트 교량 등에도 하부 층의 열화(Deterioration) 방지를 위하여 방수공정이 수반된다.In general, a waterproofing process is involved in preventing deterioration of the lower layer in concrete bridges as well as steel box girder bridges.

하지만 방수 층(도막이나 코팅 등)은 구조적 성능은 없으면서도 비용이 높다는 문제점이 있다.However, the waterproof layer (such as a coating or coating) has a problem in that it has no structural performance and is expensive.

또한, 시공 측면에서도 아스팔트 콘크리트를 일일이 운반하여 포설하거나, 현장에서 장비를 투입하여 시공하게 되더라도 프라임 코팅층과 아스팔트 콘크리트층을 일체형으로 작업하기 어려운 현실이다.In addition, in terms of construction, even if asphalt concrete is transported and installed one by one, or equipment is input and installed on site, it is difficult to work with the prime coating layer and the asphalt concrete layer in one piece.

따라서 상기에 언급한대로 탄성이 우수한 혼합물과 인성과 인장강도가 크면서도 고 부착기능이 수반된 혼합물을 적용한다면 구조적 성능과 내구성을 동시에 발휘하는 아스팔트 포장이 될 수 있고, 이에 따라 과다한 교통하중을 견딜 수 있으면서 내구성이 우수한 기능도 함께 수반한 아스팔트 포장이 되므로 시공 상 용이함은 물론 빠른 교통개방이 가능하게 된다.Therefore, as mentioned above, if a mixture having excellent elasticity and a mixture having high toughness and tensile strength but accompanied by a high adhesion function is applied, an asphalt pavement that exhibits structural performance and durability at the same time can be achieved, and thus it can withstand excessive traffic loads. It is an asphalt pavement with excellent durability and functions, so it is easy to construct and to open traffic quickly.

한편, 전술한 기술과 관련된 종래기술로서 등록특허 1491105호에 도로포장 및 보수를 위한 방수성 고강도 상온아스팔트가 개시되어 있다.On the other hand, as a prior art related to the above-described technology, a waterproof high-strength room temperature asphalt for road pavement and repair is disclosed in Korean Patent No. 1491105.

본 발명은 전술한 문제점을 극복하기 위해 창출된 것으로서, 내구성, 방수성 및 불투수성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도 포장침하를 방지하고, 지지력을 확보할 수 있는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 제공한다.The present invention was created in order to overcome the above-described problems, and has good durability, water resistance and impermeability, and plastic deformation, aging and/or peeling do not easily occur, but a waste tire that can prevent pavement settlement and secure support It provides an impermeable waterproof asphalt concrete composition containing powder.

본 발명은The present invention

아스팔트 100중량부 기준으로,Based on 100 parts by weight of asphalt,

폐타이어 분말 1 내지 25중량부;1 to 25 parts by weight of waste tire powder;

스티렌부타디엔스티렌 1 내지 25중량부;1 to 25 parts by weight of styrene butadiene styrene;

석유수지 1 내지 25중량부;1 to 25 parts by weight of petroleum resin;

골재 500 내지 2,000중량부;500 to 2,000 parts by weight of aggregate;

미분말 골재 30 내지 150중량부;30 to 150 parts by weight of fine powder aggregate;

셀룰로오스 섬유 0.1 내지 2중량부;0.1 to 2 parts by weight of cellulose fibers;

왁스 0.1 내지 2중량부; 및0.1 to 2 parts by weight of wax; And

고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 제공한다.It provides an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 0.1 to 2 parts by weight of a rubber aging inhibitor.

또한, 본 발명은In addition, the present invention

시공하고자 하는 대상면을 정리하는 정리단계;An arrangement step of arranging the target surface to be constructed;

상기 정리단계가 종료된 대상면에 아스팔트 100중량부 기준으로, 폐타이어 분말 1 내지 25중량부, 스티렌부타디엔스티렌 1 내지 25중량부, 석유수지 1 내지 25중량부, 골재 500 내지 2,000중량부, 미분말 골재 30 내지 150중량부, 셀룰로오스 섬유 0.1 내지 2중량부, 왁스 0.1 내지 2중량부, 및 고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 타설하는 타설단계;1 to 25 parts by weight of waste tire powder, 1 to 25 parts by weight of styrene butadiene styrene, 1 to 25 parts by weight of petroleum resin, 500 to 2,000 parts by weight of aggregate, fine powder A pouring step of pouring an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 30 to 150 parts by weight of aggregate, 0.1 to 2 parts by weight of cellulose fibers, 0.1 to 2 parts by weight of wax, and 0.1 to 2 parts by weight of a rubber aging inhibitor;

상기 타설단계가 종료된 뒤 타설된 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 다지는 다짐단계; 및A compaction step of compacting the impermeable asphalt concrete composition including the poured waste tire powder after the pouring step is completed; And

상기 다짐단계가 종료된 후 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 양생하는 양생단계를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 시공방법을 제공한다.It provides a method of constructing an impermeable waterproof asphalt concrete composition including waste tire powder comprising a curing step of curing an impermeable asphalt concrete composition including waste tire powder after the compaction step is completed.

본 발명에 따른 불투수성 아스팔트 콘크리트 조성물, 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 불투수성을 통한 방수성 및 내구성이 좋고, 소성변형, 노화 및/또는 박리가 쉽게 발생하지 않으면서도, 저비용으로 타설공정을 용이하게 수행할 수 있을 뿐만 아니라, 포장침하를 방지하고, 지지력을 확보할 수 있도록 하는 등의 효과가 있다.The impermeable asphalt concrete composition according to the present invention, specifically the impermeable waterproof asphalt concrete composition including waste tire powder, has good waterproofness and durability through impermeability, and plastic deformation, aging and/or peeling do not easily occur, and at low cost. In addition to being able to easily perform the pouring process, there are effects such as preventing pavement subsidence and securing support.

이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.

한 가지 관점에서, 본 발명은 아스팔트 100중량부 기준으로, 폐타이어 분말 1 내지 25중량부; 스티렌부타디엔스티렌 1 내지 25중량부; 석유수지 1 내지 25중량부; 골재 500 내지 2,000중량부; 미분말 골재 30 내지 150중량부; 셀룰로오스 섬유 0.1 내지 2중량부; 왁스 0.1 내지 2중량부; 및 고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 제공한다.In one aspect, the present invention based on 100 parts by weight of asphalt, 1 to 25 parts by weight of waste tire powder; 1 to 25 parts by weight of styrene butadiene styrene; 1 to 25 parts by weight of petroleum resin; 500 to 2,000 parts by weight of aggregate; 30 to 150 parts by weight of fine powder aggregate; 0.1 to 2 parts by weight of cellulose fibers; 0.1 to 2 parts by weight of wax; And it provides an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 0.1 to 2 parts by weight of a rubber anti-aging agent.

다른 관점에서, 본 발명은 시공하고자 하는 대상면을 정리하는 정리단계; 상기 정리단계가 종료된 대상면에 아스팔트 100중량부 기준으로, 폐타이어 분말 1 내지 25중량부, 스티렌부타디엔스티렌 1 내지 25중량부, 석유수지 1 내지 25중량부, 골재 500 내지 2,000중량부, 미분말 골재 30 내지 150중량부, 셀룰로오스 섬유 0.1 내지 2중량부, 왁스 0.1 내지 2중량부, 및 고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 타설하는 타설단계; 상기 타설단계가 종료된 뒤 타설된 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 다지는 다짐단계; 및 상기 다짐단계가 종료된 후 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 양생하는 양생단계를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 시공방법을 제공한다.In another aspect, the present invention is a cleanup step of arranging the target surface to be constructed; 1 to 25 parts by weight of waste tire powder, 1 to 25 parts by weight of styrene butadiene styrene, 1 to 25 parts by weight of petroleum resin, 500 to 2,000 parts by weight of aggregate, fine powder A pouring step of pouring an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 30 to 150 parts by weight of aggregate, 0.1 to 2 parts by weight of cellulose fibers, 0.1 to 2 parts by weight of wax, and 0.1 to 2 parts by weight of a rubber aging inhibitor; A compaction step of compacting the impermeable asphalt concrete composition including the poured waste tire powder after the pouring step is completed; And it provides a method of constructing an impermeable waterproof asphalt concrete composition comprising waste tire powder comprising a curing step of curing an impermeable asphalt concrete composition comprising waste tire powder after the compaction step is completed.

본 발명에 따른 아스팔트는 당업계에서 통상적으로 사용되는 아스팔트라면 특별히 한정되지 않지만, 추천하기로는 스트레이트 아스팔트 등의 석유계 아스팔트 또는 아스팔트 혼합물을 사용할 수 있다.The asphalt according to the present invention is not particularly limited as long as it is an asphalt commonly used in the art, but petroleum-based asphalt such as straight asphalt or an asphalt mixture may be used.

여기서, 상기 아스팔트 혼합물은 천연 아스팔트 혼합물을 사용하는 것을 추천한다.Here, it is recommended to use a natural asphalt mixture as the asphalt mixture.

상기 아스팔트 혼합물, 특정적으로 천연 아스팔트 혼합물은 당업계에서 통상적으로 사용되는 천연 아스팔트 혼합물이라면 특별히 한정되지 않지만, 바람직하게는 스트레이트(straight) 아스팔트, 트리니다드레이크(Trinidad lake) 아스팔트, 트리니다드에퓨레(Trinidad epure) 아스팔트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 보다 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트와 천연 아스팔트, 예를 들면 트리니다드레이크 아스팔트 및/또는 트리니다드에퓨레 아스팔트 혼합물을 사용하는 것이 좋고, 더욱 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트 70 내지 80중량% 및 트리니다드레이크 아스팔트 또는 트리니다드에퓨레 아스팔트로 이루어진 천연 아스팔트 20 내지 30중량%를 혼합한 것을 사용하는 것을 추천한다.The asphalt mixture, in particular, the natural asphalt mixture is not particularly limited as long as it is a natural asphalt mixture commonly used in the art, but preferably straight asphalt, Trinidad lake asphalt, Trinidad epure (Trinidad epure) ) It is preferable to use asphalt or a mixture of at least one or more selected from these, more preferably a mixture of straight asphalt and natural asphalt with a penetration degree of 20 to 40, for example Trinidadrake asphalt and/or Trinidad ePure asphalt. It is recommended to use a mixture of 70 to 80% by weight of straight asphalt having a penetration degree of 20 to 40 and 20 to 30% by weight of natural asphalt consisting of Trinidad Epure asphalt or Trinidad ePure asphalt.

여기서, 상기 스트레이트 아스팔트(straight asphalt)는 석유 아스팔트로 원료를 건류 또는 증류한 잔류물을 정제한 통상의 아스팔트로, 특히 침입도가 20 내지 40인 것이 도로에 시공 시 용이성이 있어 더욱 좋으며, 단독 또는 아스팔트 혼합물에 혼합하여 사용하는 것이 좋다.Here, the straight asphalt is a conventional asphalt obtained by distilling or distilling the raw material with petroleum asphalt and purifying the residue, especially those having an intrusion degree of 20 to 40 are better because they are easy to install on roads, alone or It is better to mix it with the asphalt mixture.

상기 스트레이트 아스팔트는 아스팔트 혼합물에 70 내지 80중량%로 포함되는 것이 바람직하다. 그 함량이 70중량% 미만일 경우에는 아스팔트 포장 후 굳는데 오랜 시간이 소요될 수 있고, 연화점이 낮아질 수 있으며, 80중량%를 초과할 경우에는 유동성이 저하될 수 있다.The straight asphalt is preferably contained in the asphalt mixture in an amount of 70 to 80% by weight. If the content is less than 70% by weight, it may take a long time to harden after paving the asphalt, the softening point may be lowered, and if it exceeds 80% by weight, the fluidity may be lowered.

또한, 상기 천연 아스팔트는 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 유동성 개선과 더불어 변형저항, 미끄럼저항 및 마찰저항 등을 증가시키는 작용을 한다.In addition, the natural asphalt functions to improve the fluidity of the impermeable waterproof asphalt concrete composition including the waste tire powder according to the present invention, and to increase deformation resistance, sliding resistance, and friction resistance.

상기 천연 아스팔트는 트리니다드레이크(trinidad lake) 아스팔트 및/또는 트리니다드에퓨레(Trinidad epure) 아스팔트 등을 사용할 수 있다.As the natural asphalt, Trinidad lake asphalt and/or Trinidad epure asphalt may be used.

상기 천연 아스팔트는 아스팔트 혼합물에 20 내지 30중량%로 포함되는 것이 바람직하며, 그 함량이 20중량% 미만일 경우에는 유동성, 변형저항, 미끄럼저항 및 마찰저항의 개선효과가 미미하며, 30중량%를 초과할 경우에는 본 발명의 아스팔트가 연질화되고 연화점이 낮아질 수 있다.The natural asphalt is preferably included in the asphalt mixture in an amount of 20 to 30% by weight, and when the content is less than 20% by weight, the effect of improving fluidity, deformation resistance, sliding resistance and friction resistance is insignificant, and exceeds 30% by weight. If so, the asphalt of the present invention may be softened and the softening point may be lowered.

본 발명에 따른 불투수성 아스팔트 콘크리트 조성물, 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 구성하는 아스팔트 외 나머지 성분들의 함량은 아스팔트 100중량부 기준으로 한다.The content of the remaining components other than asphalt constituting the impermeable asphalt concrete composition according to the present invention, specifically the impermeable waterproof asphalt concrete composition including waste tire powder, is based on 100 parts by weight of asphalt.

본 발명에 따른 폐타이어 분말(CRM, Crum Rubber Modifier)은 불투수성 아스팔트 콘크리트 조성물, 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 결속력 및 내구성을 향상시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 폐타이어 분말이라면 특별히 한정되지 않는다.The waste tire powder (CRM, Crum Rubber Modifier) according to the present invention is to improve the binding strength and durability of the impermeable asphalt concrete composition, specifically the impermeable waterproof asphalt concrete composition including the waste tire powder. It is not particularly limited as long as it is a conventional waste tire powder.

바람직한 폐타이어 분말의 사용량은 아스팔트 100중량부 기준으로 1 내지 25중량부인 것이 좋다.The preferred amount of waste tire powder is 1 to 25 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 스티렌부타디엔스티렌(stylene butadien stylene; SBS)은 균열 발생을 억제하고, 포트홀을 방지할 뿐 아니라, 아스팔트에 점결력을 제공하는 동시에 강도를 향상시킨다.Styrene butadien styrene (SBS) according to the present invention suppresses the occurrence of cracks, prevents potholes, and improves strength while providing a caking force to asphalt.

바람직한 스티렌부타디엔스티렌은 신율이 320 내지 1,400%인 스티렌부타디엔스티렌을 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 25중량부인 것을 추천한다.Preferred styrene butadiene styrene is preferably styrene butadiene styrene having an elongation of 320 to 1,400%, and the amount is recommended to be 1 to 25 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 석유수지는 불투수성 아스팔트 콘크리트 조성물, 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에 고접착성을 제공하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용하는 석유수지, 바람직하게는 방향족 석유수지, 지방족 석유수지 또는 이들의 혼합물을 사용할 수 있고, 특히 바람직하게는 용융온도가 100℃ 이상이고 침입도가 3dmm이하, 140℃에서 점도(이하 140℃ 점도)가 50 내지 500cps인 석유수지가 적합하지만, 추천하기로는 용융온도가 110℃ 내지 140℃이고 침입도가 0.5 내지 2dmm, 140℃ 점도가 50 내지 300cps인 석유수지가 좋지만, 더욱 추천하기로는 점도가 100 내지 150cps인 지방족 C-5석유수지를 사용하는 것이 좋다.The petroleum resin according to the present invention is intended to provide high adhesion to an impermeable asphalt concrete composition, specifically an impermeable waterproof asphalt concrete composition including waste tire powder, and a petroleum resin commonly used in the art for this purpose, Preferably, an aromatic petroleum resin, an aliphatic petroleum resin, or a mixture thereof may be used, and particularly preferably the melting temperature is 100°C or higher, the penetration degree is 3dmm or less, and the viscosity (hereinafter 140°C viscosity) at 140°C is 50 to 500 cps. Phosphorus petroleum resin is suitable, but recommended is a petroleum resin with a melting temperature of 110°C to 140°C, penetration of 0.5 to 2dmm, and a viscosity of 140°C of 50 to 300 cps, but more recommended is an aliphatic viscosity of 100 to 150 cps. It is better to use C-5 petroleum resin.

바람직한 석유수지의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 아스팔트 100중량부 기준으로 1 내지 25중량부인 것이 좋다.A preferred amount of petroleum resin used is not particularly limited, but it is recommended that it is 1 to 25 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 골재는 아스팔트, 스티렌부타디엔스티렌, 폐타이어 분말 및/또는 석유수지 등과 같은 결합재에 의하여 뭉쳐져서 한 덩어리를 이룰 수 있는 건설용 광물질 재료이며, 화학적으로 안정하다.The aggregate according to the present invention is a mineral material for construction that can form a lump by lumping together by a binder such as asphalt, styrene butadiene styrene, waste tire powder and/or petroleum resin, and is chemically stable.

상기 골재는 모래, 자갈, 현무암, 오석, 바잘트, 기타 이와 비슷한 재료를 지칭한다.The aggregate refers to sand, gravel, basalt, pitted stone, basalt, and other similar materials.

특정적으로, 상기 골재로서 약 0.7%의 흡수율을 갖는 염기성 맥암을 더 포함할 수 있다.Specifically, it may further include a basic malt having an absorption rate of about 0.7% as the aggregate.

여기서, 상기 골재의 평균입도는 0.08 내지 13mm인 것을 사용하는 것이 좋고, 특정적으로 0.08mm 이상 4.76mm 미만의 것은 잔골재라 하고, 4.76mm 이상의 것은 굵은 골재라 한다.Here, it is preferable to use the aggregate having an average particle size of 0.08 to 13 mm, specifically, those having an average particle size of 0.08 mm or more and less than 4.76 mm are referred to as fine aggregates, and those of 4.76 mm or more are referred to as coarse aggregates.

바람직한 골재의 사용량은 아스팔트 100중량부 기준으로 500 내지 2,000중량부인 것이 좋고, 상기 골재에 포함되는 잔골재 및 굵은 골재의 혼합량은 특별히 제한되지 않으므로 필요에 따라 적절하게 조절할 수 있다.The preferred amount of aggregate is preferably 500 to 2,000 parts by weight based on 100 parts by weight of asphalt, and the amount of fine aggregate and coarse aggregate contained in the aggregate is not particularly limited, and thus can be appropriately adjusted as needed.

본 발명에 따른 미분말 골재는 상기 골재, 특정적으로 잔골재와 굵은 골재들 사이의 공극에 충진되어 방수성 등을 향상시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 사용하는 미분말 골재라면 어떠한 것을 사용하여도 무방하다.The fine powder aggregate according to the present invention is to be filled in the pores between the aggregate, specifically fine aggregate and coarse aggregate, to improve waterproofness, etc., and any fine powder aggregate commonly used in the art for this purpose is used. It is also okay.

바람직한 미분말 골재의 크기는 적어도 0.08mm미만, 보다 바람직하게는 0.001 내지 0.079mm의 평균입도를 갖는 것을 추천하고, 그 사용량은 아스팔트 100중량부 기준으로 30 내지 150중량부인 것이 좋다.It is recommended that the size of the fine powder aggregate has an average particle size of at least 0.08 mm, more preferably 0.001 to 0.079 mm, and the amount used is preferably 30 to 150 parts by weight based on 100 parts by weight of asphalt.

또한, 상기 미분말 골재는 석분 미분말, 석회석 미분말, 모래 미분말, 자갈 미분말, 현무암 미분말, 오석 미분말, 바잘트 미분말, 기타 이와 비슷한 재료를 지칭한다.In addition, the fine powder aggregate refers to a fine stone powder, a limestone fine powder, a sand fine powder, a gravel fine powder, a basalt fine powder, a crushed stone fine powder, a basalt fine powder, and other similar materials.

본 발명에 따른 셀룰로오스 섬유는 불투수성 아스팔트 콘크리트 조성물로 형성된 타설면의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 셀룰로오스 섬유라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 천연 셀룰로오스 섬유를 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.The cellulose fiber according to the present invention is to provide tensile strength and/or light weight due to stress applied in the longitudinal-transverse direction of the pouring surface formed of the impermeable asphalt concrete composition, and any cellulose fiber having this purpose is used. It is also okay, but it is preferable to use natural cellulose fibers, and the amount is preferably 0.1 to 2 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 왁스는 아스팔트 콘크리트 조성물, 특정적으로 불투수성 아스팔트 콘크리트 조성물, 보다 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 제조 및/또는 시공시 필요한 온도를 종래공법에 비하여 낮추는, 바람직하게는 20 내지 40℃ 정도 낮출 수 있도록 하여 이산화탄소 및 유해물질 배출을 최소화하기 위한 것으로서, 이러한 목적으로 사용되는 당업계의 통상적인 왁스라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리에틸렌 왁스를 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.Wax according to the present invention is an asphalt concrete composition, specifically an impermeable asphalt concrete composition, more specifically, lowering the temperature required for the production and / or construction of the impermeable waterproof asphalt concrete composition including waste tire powder compared to the conventional method. It is intended to minimize the emission of carbon dioxide and harmful substances by allowing it to be lowered by about 20 to 40°C, and any conventional wax used for this purpose may be used, but preferably polyethylene wax is used. It is good, and the amount is preferably 0.1 to 2 parts by weight based on 100 parts by weight of asphalt.

특정 양태로서, 본 발명에 따른 왁스는 개질 지방산과 혼합된 혼합물을 사용할 수도 있는바, 이러한 경우, 상기 왁스, 특정적으로 폴리에틸렌 왁스는 개질 지방산과 1:0.1 내지 0.6의 중량비율로 혼합되는 것이 좋다.As a specific embodiment, the wax according to the present invention may be a mixture mixed with a modified fatty acid. In this case, the wax, specifically polyethylene wax, is preferably mixed with a modified fatty acid in a weight ratio of 1:0.1 to 0.6. .

여기서, 상기 폴리에틸렌 왁스는 융점이 95 내지 125℃이고, 약 140℃에서의 용융점도가 80 내지 400cPs인 것이 바람직하다.Here, it is preferable that the polyethylene wax has a melting point of 95 to 125°C and a melt viscosity of 80 to 400 cPs at about 140°C.

이때, 상기 폴리에틸렌 왁스의 융점이 95℃ 미만인 경우에는 아스팔트와 혼합시에 아스팔트의 강성이 약해질 수 있고, 융점이 125℃를 초과하는 경우에는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에 충분히 분산되지 않아 물성 저하의 우려가 있다.At this time, if the melting point of the polyethylene wax is less than 95°C, the stiffness of the asphalt may be weakened when mixed with asphalt, and if the melting point exceeds 125°C, it is sufficiently dispersed in the impermeable waterproof asphalt concrete composition including waste tire powder. And there is a risk of deterioration of properties.

또한, 폴리에틸렌 왁스의 140℃에서 용융점도가 80cPs 미만인 경우에는 고온 물성이 약화되어 도로 포장용 아스팔트로서 부적합하며, 140℃에서 용융점도가 400cPs을 초과하는 경우에는 아스팔트의 점도가 지나치게 높아져 아스팔트 콘크리트 조성물 제조 및 타설 시에 공정이 제대로 이루어지지 않는 문제가 발생할 수 있다.In addition, when the melt viscosity of polyethylene wax at 140°C is less than 80 cPs, the high-temperature properties are weakened, making it unsuitable as asphalt for road pavement.When the melt viscosity at 140°C exceeds 400 cPs, the viscosity of the asphalt becomes too high to produce asphalt concrete composition and There may be a problem that the process is not performed properly during pouring.

한편, 상기 왁스와 함께 혼합되어 사용되는 개질 지방산은 아스팔트 콘크리트 조성물의 수분 민감성을 향상시키는 역할을 한다.Meanwhile, the modified fatty acid used by mixing with the wax serves to improve the moisture sensitivity of the asphalt concrete composition.

특정적으로, 상기 개질 지방산은 탄소수 12 내지 24개의 지방산을 수산화칼슘, 수산화마그네슘, 수산화아연 및 산화아연으로 이루어진 군으로부터 선택되는 1종 이상과 용융 반응시켜 얻어지는 것이 아스팔트 콘크리트 조성물의 수분 민감성 개선 효과 측면에서 바람직하다.Specifically, the modified fatty acid is obtained by melt-reacting a fatty acid having 12 to 24 carbon atoms with at least one selected from the group consisting of calcium hydroxide, magnesium hydroxide, zinc hydroxide and zinc oxide in terms of the effect of improving the moisture sensitivity of the asphalt concrete composition. desirable.

또한, 상기 개질 지방산은 융점이 110 내지 140℃의 범위인 것이 바람직하다. 개질 지방산의 융점이 상기 범위를 벗어나서 아스팔트 콘크리트 조성물의 제조온도보다 높은 경우에는 수분 민감성 개선 효과를 얻을 수 없다.In addition, it is preferable that the modified fatty acid has a melting point in the range of 110 to 140°C. When the melting point of the modified fatty acid is out of the above range and is higher than the manufacturing temperature of the asphalt concrete composition, the moisture sensitivity improvement effect cannot be obtained.

본 발명에 따른 고무노화방지제는 조성물에 포함된 폐타이어 분말 등의 노화를 방지하는 효과를 나타내는 바, 이는 주로 광산화를 일으키는 자외선을 흡수하는 기능이 있으며 구체적으로는 광산화물을 분해하여 버티칼상의 안정된 물질로 하거나 과산화물 라디칼과 작용하여 불활성 물질로 변화시키거나 라디칼 정지반응에 의해 생성한 물질과 반응하여 원래의 노화방지제 또는 다른 노화방지제서 작용하는 물질로 바뀐다. The rubber anti-aging agent according to the present invention exhibits an effect of preventing aging of waste tire powder contained in the composition, and it has a function of mainly absorbing ultraviolet rays that cause photooxidation, and specifically, a stable material in vertical form by decomposing photooxide. Or reacts with peroxide radicals to change into inert substances, or reacts with substances produced by radical stop reactions to change into substances that act as original anti-aging agents or other anti-aging agents

바람직한 고무노화방지제로는 2-멜캅토 벤조이미다졸을 사용하는 것이 좋고, 그 사용량은 특별히 한정되지 않지만, 추천하기로는 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것이 좋다.It is preferable to use 2-melcapto benzoimidazole as a preferable rubber anti-aging agent, and the amount of it is not particularly limited, but it is recommended that it is 0.1 to 2 parts by weight based on 100 parts by weight of asphalt.

본 발명에 따른 아스팔트 콘크리트 조성물, 특정적으로 불투수성 아스팔트 콘크리트 조성물, 보다 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 하기의 특정 양태로 실시되는 부가물을 1종 또는 1종 이상 더 포함할 수 있다.The asphalt concrete composition according to the present invention, specifically the impermeable asphalt concrete composition, and more specifically the impermeable waterproof asphalt concrete composition comprising waste tire powder further includes one or more additives implemented in the following specific embodiments. can do.

특정 양태로서, 본 발명에 따른 아스팔트 콘크리트 조성물, 특정적으로 불투수성 방수아스팔트 콘크리트 조성물, 보다 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 타설후 신속한 경화를 진행하여도 크랙 및 탈락현상을 개선하고, 조성물의 가공성, 밀착력 및 안정성 등을 제공하기 위하여 폴리비닐리덴플로라이드수지를 아스팔트 100중량부 기준으로 0.1 내지 4량부로 더 포함할 수 있다.In a specific embodiment, the asphalt concrete composition according to the present invention, specifically the impermeable waterproof asphalt concrete composition, more specifically the impermeable waterproof asphalt concrete composition comprising waste tire powder, cracks and falls out even after rapid curing after the composition is placed. In order to improve the phenomenon and provide processability, adhesion and stability of the composition, the polyvinylidene fluoride resin may be further included in an amount of 0.1 to 4 parts by weight based on 100 parts by weight of asphalt.

다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 흡착성 및 접착성을 향상시키고, 조성물의 혼합시 반응속도를 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 2-브로모피리딘(2-Bromopyridine)을 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 3 parts by weight based on 100 parts by weight of asphalt in order to improve the adsorption and adhesion of the composition and to improve the reaction rate when the composition is mixed. It may further include a weight part of 2-bromopyridine (2-Bromopyridine).

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 성분들간의 비중차에 따른 재료의 분리현상을 방지하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 웰란 검(welan gum)을 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 3 parts by weight based on 100 parts by weight of asphalt in order to prevent separation of the material due to the difference in specific gravity between the components of the composition. Welan gum (welan gum) may be further included.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 양생시 수축을 방지하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 4중량부의 네오펜틸글리콜(Neopentylglycol, NPG)을 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 4 parts by weight based on 100 parts by weight of asphalt in order to prevent shrinkage during curing of the composition, Neopentylglycol (NPG) It may further include.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물에 포함된 성분이 물과 용이하게 혼합되도록 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 플라스터(plaster)를 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention comprises 0.1 to 5 parts by weight of a plaster based on 100 parts by weight of asphalt so that the components contained in the composition are easily mixed with water. It may contain more.

여기서, 상기 플라스터의 사용량이 아스팔트 100중량부 기준으로 0.5 중량부 미만인 경우는 조성물에 포함된 다양한 성분이 물과 용이하게 혼합되기 어렵고, 5중량부를 초과하는 경우는 강도 및 내화학성 등이 저하되는 문제가 있다.Here, when the amount of the plaster used is less than 0.5 parts by weight based on 100 parts by weight of asphalt, it is difficult for various components included in the composition to be easily mixed with water, and when it exceeds 5 parts by weight, strength and chemical resistance are deteriorated. There is.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 가소성 및 보수성을 증진시키고, 균열방지와 강도증진을 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 코코베타인을 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention improves plasticity and water retention of the composition, prevents cracking and increases strength, in order to prevent cracking and increase strength, 0.1 to 5 parts by weight of coco It may further contain betaine.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 강도, 내마모성 및 내화성을 개선하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 깁사이트를 더 포함할 수 있다. As another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further include 0.1 to 5 parts by weight of gibbsite based on 100 parts by weight of asphalt in order to improve strength, abrasion resistance, and fire resistance. .

여기서, 상기 깁사이트의 사용량은 0.1중량부 미만일 경우 성능 개선 효과가 미약할 수 있고, 상기 깁사이트의 사용량이 5중량부를 초과할 경우에는 작업성이 저하되고 제조 원가가 높아져 경제적이지 못하다.Here, when the amount of gibsite is less than 0.1 parts by weight, the performance improvement effect may be weak, and when the amount of gibsite is more than 5 parts by weight, workability decreases and manufacturing cost increases, which is not economical.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 강도, 내화성 및 내식성을 개선하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 세륨을 더 포함할 수 있다. As another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further contain 0.1 to 5 parts by weight of cerium based on 100 parts by weight of asphalt in order to improve strength, fire resistance and corrosion resistance.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 장기강도, 내식성 및 내화성을 향상시키기 위하여 페라이트(ferrite)를 아스팔트 100중량부 기준으로 1 내지 3중량부 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 3중량부를 초과하면 빠른 경화특성을 보이기는 하나 경제성이 떨어지며, 1중량부 미만이면 상기와 같은 개선효과가 미미하여 좋지 않다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention comprises 1 to 3 parts by weight of ferrite based on 100 parts by weight of asphalt in order to improve the long-term strength, corrosion resistance and fire resistance of the composition. It may further include, and if the content exceeds 3 parts by weight based on 100 parts by weight of asphalt, it exhibits rapid hardening properties, but the economy is poor, and if it is less than 1 part by weight, the above-described improvement effect is insignificant and is not good.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 강도, 내화성, 내마모성, 및 내부식성 등을 개선하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 4중량부의 할로이사이트(halloysite)를 더 포함할 수 있는데, 상기 할로이사이트는 알루미늄과 실리콘이 약 1:1의 비율로 포함되어 있는 점토질 광물질로서 이를 조성물에 포함시키면 상기와 같은 효과를 발현하게 된다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 4 parts by weight of halo based on 100 parts by weight of asphalt in order to improve the strength, fire resistance, abrasion resistance, and corrosion resistance of the composition. It may further include a halloysite, and the halloysite is a clay mineral containing aluminum and silicon in a ratio of about 1:1, and when it is included in the composition, the above effect is expressed.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 습윤강도 및 마모저항성을 강화하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 4중량부의 진크암모늄클로라이드를 더 포함할 수 있다.As another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further include 0.1 to 4 parts by weight of zinc ammonium chloride based on 100 parts by weight of asphalt in order to enhance wet strength and abrasion resistance. have.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 통기성 및 흡유성 향상을 위하여 천매암 분말을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함할 수 있는데, 상기 천매암은 점토질의 퇴적층이 열수변질에 의한 가수분해 작용 및 변성, 풍화 부식 등의 과정을 거쳐 생성된 변성암의 일종으로 주 성분이 실리카, 알루미나 및 금속산화물을 포함하고 있으며, 내부에 여러 크기의 공극을 포함하고 비석(zeolite)과 거의 유사한 공극률을 갖으면서도 거포의 분율이 큰 특징을 갖고 있어 이를 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에 포함시키면, 상기와 같은 효과를 갖게 되며, 바람직한 천매암 분말의 평균입도는 3 내지 30㎛ 이다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further include 0.1 to 5 parts by weight of phylum rock powder based on 100 parts by weight of asphalt in order to improve the breathability and oil absorption of the composition. , The phyllite is a type of metamorphic rock that is formed through processes such as hydrolysis and metamorphism, weathering and corrosion in the clay sediment layer, and its main components include silica, alumina, and metal oxides. It contains voids and has a porosity that is almost similar to that of zeolite, but has a large fraction of foam.If this is included in an impermeable waterproof asphalt concrete composition containing waste tire powder, it will have the same effect as described above, and desirable The average particle size of the powder is 3 to 30 μm.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물이 시공되는 시공면의 공극으로 침투하여 조직을 치밀하게 유지함으로써 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 들뜸방지와 내구성 및 부착 강도를 향상시키기 위하여 보크사이트 분말을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함할 수 있는데, 바람직한 보크사이트 분말의 평균입도는 1 내지 10㎛ 이다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention penetrates into the pores of the construction surface where the impermeable waterproof asphalt concrete composition containing the waste tire powder is installed, thereby maintaining the structure densely. Bauxite powder may be further included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of asphalt in order to prevent lift and improve durability and adhesion strength of the impermeable waterproof asphalt concrete composition containing tire powder.The average particle size of the preferred bauxite powder Is 1 to 10 μm.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 크랙발생 및 박리방지를 위하여 디부틸프탈레이트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.As another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further contain dibutylphthalate in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt to prevent cracking and peeling of the composition. have.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 강도, 침투력, 및 발수성 등을 향상시키기 위하여 3-메르캅토프로필트리메톡시실란을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention comprises 3-mercaptopropyltrimethoxysilane based on 100 parts by weight of asphalt in order to improve the strength, penetration, and water repellency of the composition. It may further include 1 to 3 parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 장기강도 발현 및 내구성 증진을 위하여 겔라이트 미분말을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있는데, 상기 겔라이트는 황토의 187배 이상의 효과를 가진 광물질로서 상기 효과 이외에 양질의 원적외선 방출 효과도 있는 것으로서, 바람직한 평균입도는 1 내지 5㎛ 이다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention further comprises 1 to 3 parts by weight of gelite fine powder based on 100 parts by weight of asphalt in order to develop long-term strength and durability of the composition. The gelite is a mineral that has an effect of 187 times or more of loess, and has a high-quality far-infrared emission effect in addition to the above effect, and the preferred average particle size is 1 to 5 μm.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물을 구성하는 재료의 응결을 방지하고 일정시간 작업시간을 확보하기 위하여 구연산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention contains citric acid based on 100 parts by weight of asphalt in order to prevent condensation of the material constituting the composition and to secure a certain working time. It may further include 5 parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 표면에 수분침투를 방지하면서 통기성을 확보하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 소디윰스테아레이트를 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 1중량부 미만이면 목적한 수분침투 방지기능을 얻을 수 없고, 5중량부를 초과하면 조성물의 강도 저하현상이 나타나 좋지 않다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 1 to 5 parts by weight of sodium stea based on 100 parts by weight of asphalt in order to secure breathability while preventing moisture penetration on the surface of the composition. The rate may be further included, and if the content is less than 1 part by weight based on 100 parts by weight of asphalt, the desired moisture penetration prevention function cannot be obtained, and if it exceeds 5 parts by weight, the strength of the composition decreases, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 내수성 및 내스크래치성을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 붕산 화합물을 더 포함할 수 있는데, 상기 붕산 화합물로는 오르토붕산, 메타붕산, 사붕산, 붕산 메틸, 붕산 에틸 등을 들 수 있으며, 바람직하게는 오르토붕산을 사용하는 것이 좋다.As another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention further comprises 0.1 to 5 parts by weight of a boric acid compound based on 100 parts by weight of asphalt in order to improve the water resistance and scratch resistance of the composition. Examples of the boric acid compound may include orthoboric acid, metaboric acid, tetraboric acid, methyl borate, ethyl borate, and the like, and orthoboric acid is preferably used.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 건조 수축을 방지하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 알루민산 칼슘을 더 포함할 수 있는데, 알루민산 칼슘이 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에 포함되면 팽창성을 띄게 되어 조성물의 건조수축을 방지하게 되는 것으로, 그 사용량이 아스팔트 100중량부 기준으로 0.1중량부 미만이면 그 효과가 미미하며, 5중량부를 초과할 경우 과다하여 작업성을 저하 시킬 수 있어 좋지 않다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further contain 0.1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of asphalt in order to prevent the drying shrinkage of the composition. , When calcium aluminate is included in the impermeable waterproof asphalt concrete composition containing waste tire powder, it becomes expandable and prevents drying shrinkage of the composition.If the amount is less than 0.1 parts by weight based on 100 parts by weight of asphalt, the effect is It is insignificant, and if it exceeds 5 parts by weight, it is not good because it is excessive and can reduce workability.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 압축강도 및 휨강도를 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 메타규산나트륨을 더 포함할 수 있는데, 그 함량이 1중량부 미만이면 유동성이 낮아지고 불규칙한 기포가 형성되며, 5중량부를 초과하면 경화시간을 확보하기 어려워 좋지 않다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention further comprises 1 to 5 parts by weight of sodium metasilicate based on 100 parts by weight of asphalt in order to improve the compressive strength and flexural strength of the composition. If the content is less than 1 part by weight, fluidity is lowered and irregular air bubbles are formed, and if it exceeds 5 parts by weight, it is difficult to secure a curing time, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 강도, 내마모성, 및 내구성을 향상시키기 위하여 질화마그네슘을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention further includes magnesium nitride in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt in order to improve the strength, abrasion resistance, and durability of the composition. can do.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 반응성을 개선하여 강도를 발현하고, 내오염성 및 재료분리 저항성을 향상시키기 위하여 메타인산 나트륨(sodium metaphosphate)를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific aspect, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is sodium metaphosphate to improve the reactivity of the composition to express strength, and to improve fouling resistance and material separation resistance. It may further include 0.1 to 3 parts by weight based on 100 parts by weight of asphalt.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 동절기 응결 지연 현상을 차단하고, 강도 증진 및 점성을 증가시켜 아스팔트의 흐름성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 황산알루미늄을 더 포함할 수 있다.As another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is based on 100 parts by weight of asphalt in order to block the delay of setting in winter, increase strength and increase viscosity to improve the flowability of asphalt. As 1 to 5 parts by weight of aluminum sulfate may be further included.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물 반응성을 높여 조기강도를 발현하기 위하여 알루민산스트론튬(strontium aluminate)를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 3 parts by weight based on 100 parts by weight of asphalt in order to increase the composition reactivity and express early strength. It may contain more as wealth.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 항균성 및 방오성을 향상시키기 위하여 일라이트를 아스팔트 100중량부 기준으로 0.1 내지 1중량부로 더 포함할 수 있다As another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention may further include ilite in an amount of 0.1 to 1 part by weight based on 100 parts by weight of asphalt in order to improve the antibacterial and antifouling properties of the composition.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 발수성을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 칼륨메틸실리코네이트를 더 포함할 수 있으며, 상기 칼륨메틸실리코네이트의 사용량이 0.1중량부 미만이면 발수성의 효과가 미미하며, 5중량부를 초과하면 상용성이 저하된다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 5 parts by weight based on 100 parts by weight of asphalt in order to improve the water repellency of the water impermeable waterproof asphalt concrete composition comprising the waste tire powder. Potassium methylsiliconate may be further included, and if the amount of potassium methylsiliconate is less than 0.1 parts by weight, the effect of water repellency is insignificant, and if it exceeds 5 parts by weight, compatibility is lowered.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물이 도포되는 대상물이 염해 또는 중성화 등의 성능저하 요인에 의해 부식 및 피복 탈락 등이 발생하는 것을 방지하기 위해 메틸트리메톡시실란(MTMS(methyltrimethoxysilane))을 더 포함할 수 있는데, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 5중량부가 좋다.As another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is to prevent corrosion and coating dropout due to deterioration factors such as salt damage or neutralization of the object to which the composition is applied. It may further include methyltrimethoxysilane (MTMS), the amount of which is preferably 1 to 5 parts by weight based on 100 parts by weight of asphalt.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 재료분리 저항성, 작업성 및 동결융해 내구성 등을 향상시키기 위하여 이미다졸린베타인을 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is imidazoline betaine based on 100 parts by weight of asphalt in order to improve the material separation resistance, workability and freeze-thaw durability of the composition. It may further contain 0.1 to 2 parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 부착성능을 향상시키기 위하여 노말부틸아크릴레이트(n-butyl acrylate)를 아스팔트 100중량부 기준으로 0.1 내지 4중량부로 더 포함할 수 있는데, 아스팔트 100중량부 기준으로 1중량부 미만이면 부착력이 저하되며, 4중량부를 초과하면 경제적이지 못하여 좋지 않다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising waste tire powder according to the present invention is a normal butyl acrylate (n-butyl acrylate) to improve the adhesion performance of the impermeable waterproof asphalt concrete composition comprising waste tire powder. It may further include 0.1 to 4 parts by weight based on 100 parts by weight of asphalt. If it is less than 1 part by weight based on 100 parts by weight of asphalt, the adhesion is lowered, and if it exceeds 4 parts by weight, it is not good because it is not economical.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 강도, 내크리프성, 내마모성, 내화성 등을 개선하기 위하여 멀라이트(mullite)를 아스팔트 100중량부 기준으로 1 내지 5량부로 더 포함할 수 있는데, 상기 멀라이트는 사방정계에 속하는 광물질로서 무색 또는 담홍색을 띄며, 산화알루미늄과 이산화규소를 많이 함유하고 있는데, 아스팔트 100중량부 기준으로 1중량부 미만이면 강도, 내마모성 및 내화성 등의 개선효과가 미미하며, 5중량부를 초과하면 작업성이 저하되어 좋지 않다.In another specific aspect, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is Mullite to improve the strength, creep resistance, abrasion resistance, fire resistance, etc. of the impermeable waterproof asphalt concrete composition including the waste tire powder. (mullite) may be further included in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt.The mullite is a mineral belonging to an orthorhombic system and has a colorless or pink color, and contains a lot of aluminum oxide and silicon dioxide. Asphalt 100 If it is less than 1 part by weight, the improvement effect such as strength, abrasion resistance, and fire resistance is insignificant, and if it exceeds 5 parts by weight, the workability is deteriorated, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 경화속도를 조절하고, 방수성 및 내식성을 개선하기 위하여 규불화마그네슘을 아스팔트 100중량부 기준으로 0.5 내지 3중량부로 더 포함할 수 있다. In another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is magnesium silicate in order to control the curing rate of the impermeable waterproof asphalt concrete composition including the waste tire powder, and improve waterproofness and corrosion resistance. It may further include 0.5 to 3 parts by weight based on 100 parts by weight of asphalt.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물의 내구성, 내마모성 및 분산성을 향상시키기 위하여 스테아린산칼슘을 아스팔트 100중량부 기준으로 0.1 내지 2량부로 더 포함할 수 있다.In another specific embodiment, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 100 weight of calcium stearate as asphalt in order to improve the durability, abrasion resistance and dispersibility of the impermeable waterproof asphalt concrete composition comprising the waste tire powder. It may further include 0.1 to 2 parts by weight on a part basis.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 내수성, 내화학성 및/또는 내부착성 등을 향상시키기 위하여 테트라메틸렌 디이소시아네이트를 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention comprises tetramethylene diisocyanate based on 100 parts by weight of asphalt in order to improve water resistance, chemical resistance and/or internal adhesion of the composition. It may further contain 0.1 to 5 parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 방수성, 내화학성 등을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 울소나이트(Ursolite)로 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is made of 0.1 to 3 parts by weight of ulsonite based on 100 parts by weight of asphalt in order to improve the waterproofness and chemical resistance of the composition. It may contain more.

여기서, 상기 울소나이트는 침상의 흡수성이 우수한 분체로 유기 증점제를 대체하여 분체 입자표면에 입자, 예를 들면 수지 등의 입자를 흡착시켜 아스팔트 콘크리트의 슬럼프가 높거나 시공시 교행하는 진동원에 의해 입자가 아스팔트 콘크리트의 표층으로 마이그레이션(migration)하는 것을 억제하기 위해 첨가되며, 최대의 효과를 얻기 위해서는 경도 4.5 내지 5.0, 비중 약 2.9, 입자크기 30㎛±5, 어스팩트비(aspect ratio) 15:1의 조건을 만족시키는 것을 사용하는 것이 바람직하다.Here, the ulsonite is a powder having excellent acicular absorption, replacing the organic thickener and adsorbing particles, such as resin, on the surface of the powder particles, so that the slump of asphalt concrete is high or the particles are caused by the vibration source intersecting during construction. Is added to suppress migration to the surface layer of asphalt concrete, and to obtain maximum effect, hardness 4.5 to 5.0, specific gravity of about 2.9, particle size 30㎛±5, aspect ratio 15:1 It is preferable to use one that satisfies the conditions of.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 산패 발생 및 노화방지와 안정성 향상을 위하여 디부틸하이드록시톨루엔을 아스팔트 100중량부 기준으로 1 내지 4중량부로 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention contains 1 to 4 parts by weight of dibutylhydroxytoluene based on 100 parts by weight of asphalt in order to prevent rancidity and aging of the composition and improve stability. It may contain more as wealth.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물을 구성하는 성분들간의 배합을 용이하게 하고 조성물의 안정성을 향상하기 위하여 술폭시폴리에틸렌글리콜알릴에테르를 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 0.1중량부 미만이면 조성물의 배합이 용이하지 못하며, 5중량부를 초과하면 과량으로 안정성이 저하되어 좋지 않다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is prepared by using sulfoxy polyethylene glycol allyl ether as asphalt 100 to facilitate mixing between the components constituting the composition and to improve the stability of the composition. It may further include 0.1 to 5 parts by weight based on parts by weight, but if the content is less than 0.1 parts by weight based on 100 parts by weight of asphalt, the composition is not easily blended, and if it exceeds 5 parts by weight, stability is degraded excessively, which is not good. .

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물의 방수성, 내화학성 등을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 4중량부의 부틸-2-프로페노에이트를 더 포함할 수 있다.In another specific aspect, the impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.1 to 4 parts by weight of butyl-2-propeno based on 100 parts by weight of asphalt in order to improve the waterproofness and chemical resistance of the composition. It may further include eight.

또 다른 특정 양태로서, 본 발명에 따른 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물은 조성물을 구성하는 구성성분간의 결합력을 향상시키 위하여 아스팔트 100중량부 기준으로 0.01 내지 1중량부의 모노-터트-부틸-하이드로퀴논를 더 포함할 수 있다.In another specific embodiment, the water impermeable waterproof asphalt concrete composition comprising the waste tire powder according to the present invention is 0.01 to 1 part by weight of mono-tert-butyl based on 100 parts by weight of asphalt in order to improve the bonding strength between the components constituting the composition. -It may further contain hydroquinone.

이와 같은 구성을 갖는 본 발명에 따른 불투수성 아스팔트 콘크리트 조성물, 특정적으로 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 시공방법을 설명하면 다음과 같다.A method of constructing an impermeable asphalt concrete composition according to the present invention having such a configuration, specifically an impermeable waterproof asphalt concrete composition including waste tire powder will be described as follows.

여기서, 상기 폐타이어 분말을 포함하는 불투성 아스팔트 콘크리트 조성물 시공방법은 특별히 한정되지 않지만, 바람직하게는 시공하고자 하는 대상면을 정리하는 정리단계;Here, the method of constructing the impermeable asphalt concrete composition including the waste tire powder is not particularly limited, but preferably, an arrangement step of arranging the target surface to be constructed;

상기 정리단계가 종료된 대상면에 아스팔트 100중량부 기준으로, 폐타이어 분말 1 내지 25중량부, 스티렌부타디엔스티렌 1 내지 25중량부, 석유수지 1 내지 25중량부, 골재 500 내지 2,000중량부, 미분말 골재 30 내지 150중량부, 셀룰로오스 섬유 0.1 내지 2중량부, 왁스 0.1 내지 2중량부, 및 고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 타설하는 타설단계;1 to 25 parts by weight of waste tire powder, 1 to 25 parts by weight of styrene butadiene styrene, 1 to 25 parts by weight of petroleum resin, 500 to 2,000 parts by weight of aggregate, fine powder A pouring step of pouring an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 30 to 150 parts by weight of aggregate, 0.1 to 2 parts by weight of cellulose fibers, 0.1 to 2 parts by weight of wax, and 0.1 to 2 parts by weight of a rubber aging inhibitor;

상기 타설단계가 종료된 뒤 타설된 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 다지는 다짐단계; 및A compaction step of compacting the impermeable asphalt concrete composition including the poured waste tire powder after the pouring step is completed; And

상기 다짐단계가 종료된 후 폐타이어 분말을 포함하는 불투수성 아스팔트 콘크리트 조성물을 양생하는 양생단계를 포함한다.It includes a curing step of curing the impermeable asphalt concrete composition including waste tire powder after the compaction step is completed.

이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail through examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention by these examples.

[실시예 1][Example 1]

침입도 30의 스트레이트 아스팔트 100g, 폐타이어 분말 13g, 신율이 약 850%인 스티렌부타디엔스티렌 14g, 140℃ 점도가 130cps인 지방족 C-5석유수지 13g, 평균입도가 약 3mm인 자갈과 평균입도가 약 5mm인 자갈이 5:5의 중량비율로 혼합된 골재 1,200g, 평균입도가 약 0.03mm인 석회석으로 이루어진 미분말 골재 80g, 천연 셀룰로오스 섬유 1g, 폴리에틸렌 왁스 1g 및 2-멜캅토 벤조이미다졸 1g을 혼합하여 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 제조하였다.100g of straight asphalt with a penetration of 30, 13g of waste tire powder, 14g of styrene butadiene styrene with an elongation of about 850%, 13g of aliphatic C-5 petroleum resin with a viscosity of 130 cps at 140℃, gravel with an average particle size of about 3mm, and an average particle size of about 1,200 g of aggregate mixed with 5 mm gravel in a weight ratio of 5:5, 80 g of fine powder aggregate consisting of limestone with an average particle size of about 0.03 mm, 1 g of natural cellulose fiber, 1 g of polyethylene wax and 1 g of 2-mercapto benzoimidazole Thus, an impermeable waterproof asphalt concrete composition containing waste tire powder was prepared.

[실시예 2][Example 2]

실시예 1과 동일한 방법으로 실시하되, 폴리에틸렌 왁스 1g 대신 폴리에틸렌 왁스와 탄소수 12~24개의 지방산을 수산화칼슘과 용융 반응시켜 얻어진 개질 지방산이 1:0.5의 중량비율로 혼합된 혼합물 1g을 사용하여 실시하였다.It was carried out in the same manner as in Example 1, but instead of 1 g of polyethylene wax, 1 g of a mixture in which a modified fatty acid obtained by melt-reacting a polyethylene wax and a fatty acid having 12 to 24 carbon atoms with calcium hydroxide was mixed in a weight ratio of 1: 0.5 was used.

[실시예 3][Example 3]

실시예 1과 동일한 방법으로 실시하되, 폴리비닐리덴플로라이드수지 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of a polyvinylidene fluoride resin.

[실시예 4][Example 4]

실시예 1과 동일한 방법으로 실시하되, 2-브로모피리딘 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of 2-bromopyridine.

[실시예 5][Example 5]

실시예 1과 동일한 방법으로 실시하되, 웰란 검 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of Wellan gum.

[실시예 6][Example 6]

실시예 1과 동일한 방법으로 실시하되, 네오펜틸글리콜 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of neopentyl glycol.

[실시예 7][Example 7]

실시예 1과 동일한 방법으로 실시하되, 플라스터 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of plaster.

[실시예 8][Example 8]

실시예 1과 동일한 방법으로 실시하되, 코코베타인 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of coco betaine.

[실시예 9][Example 9]

실시예 1과 동일한 방법으로 실시하되, 깁사이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of gibbsite.

[실시예 10][Example 10]

실시예 1과 동일한 방법으로 실시하되, 세륨 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of cerium.

[실시예 11][Example 11]

실시예 1과 동일한 방법으로 실시하되, 페라이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of ferrite.

[실시예 12][Example 12]

실시예 1과 동일한 방법으로 실시하되, 할로이사이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of haloysite.

[실시예 13][Example 13]

실시예 1과 동일한 방법으로 실시하되, 진크암모늄클로라이드 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 2 g of zinc ammonium chloride.

[실시예 14][Example 14]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 5㎛인 천매암 분말 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but with an average particle size of 5 μm, 3 g of cheonmaeam powder was further added.

[실시예 15][Example 15]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 보크사이트 분말 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 3 g of bauxite powder having an average particle size of 3 μm.

[실시예 16][Example 16]

실시예 1과 동일한 방법으로 실시하되, 디부틸프탈레이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of dibutylphthalate.

[실시예 17][Example 17]

실시예 1과 동일한 방법으로 실시하되, 3-메르캅토프로필트리메톡시실란 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 2 g of 3-mercaptopropyltrimethoxysilane.

[실시예 18][Example 18]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 겔라이트 미분말 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 2 g of a fine gelite powder having an average particle size of 3 μm.

[실시예 19][Example 19]

실시예 1과 동일한 방법으로 실시하되, 구연산 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of citric acid.

[실시예 20][Example 20]

실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of sodium stearate.

[실시예 21][Example 21]

실시예 1과 동일한 방법으로 실시하되, 오르토붕산 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of orthoboric acid.

[실시예 22][Example 22]

실시예 1과 동일한 방법으로 실시하되, 알루민산 칼슘 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of calcium aluminate.

[실시예 23][Example 23]

실시예 1과 동일한 방법으로 실시하되, 메타규산나트륨 4g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 4 g of sodium metasilicate.

[실시예 24][Example 24]

실시예 1과 동일한 방법으로 실시하되, 질화마그네슘 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of magnesium nitride.

[실시예 25][Example 25]

실시예 1과 동일한 방법으로 실시하되, 메타인산 나트륨 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of sodium metaphosphate.

[실시예 26][Example 26]

실시예 1과 동일한 방법으로 실시하되, 황산알루미늄 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of aluminum sulfate.

[실시예 27][Example 27]

실시예 1과 동일한 방법으로 실시하되, 알루민산스트론튬 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, except that 2 g of strontium aluminate was further added.

[실시예 28][Example 28]

실시예 1과 동일한 방법으로 실시하되, 일라이트 0.5g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 0.5 g of illite.

[실시예 29][Example 29]

실시예 1과 동일한 방법으로 실시하되, 칼륨메틸실리코네이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of potassium methylsiliconate.

[실시예 30][Example 30]

실시예 1과 동일한 방법으로 실시하되, 메틸트리메톡시실란 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of methyltrimethoxysilane.

[실시예 31][Example 31]

실시예 1과 동일한 방법으로 실시하되, 이미다졸린베타인 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of imidazoline betaine.

[실시예 32][Example 32]

실시예 1과 동일한 방법으로 실시하되, 노말부틸아크릴레이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of normal butyl acrylate.

[실시예 33][Example 33]

실시예 1과 동일한 방법으로 실시하되, 멀라이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of mullite.

[실시예 34][Example 34]

실시예 1과 동일한 방법으로 실시하되, 규불화마그네슘 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of magnesium silicide.

[실시예 35][Example 35]

실시예 1과 동일한 방법으로 실시하되, 스테아린산칼슘 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of calcium stearate.

[실시예 36][Example 36]

실시예 1과 동일한 방법으로 실시하되, 테트라메틸렌 디이소시아네이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 3 g of tetramethylene diisocyanate.

[실시예 37][Example 37]

실시예 1과 동일한 방법으로 실시하되, 울소나이트 0.5g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 0.5 g of ulsonite.

[실시예 38][Example 38]

실시예 1과 동일한 방법으로 실시하되, 디부틸하이드록시톨루엔 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 3 g of dibutylhydroxytoluene.

[실시예 39][Example 39]

실시예 1과 동일한 방법으로 실시하되, 술폭시폴리에틸렌글리콜알릴에테르 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of sulfoxy polyethylene glycol allyl ether.

[실시예 40][Example 40]

실시예 1과 동일한 방법으로 실시하되, 부틸-2-프로페노에이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of butyl-2-propenoate.

[실시예 41][Example 41]

실시예 1과 동일한 방법으로 실시하되, 모노-터트-부틸-하이드로퀴논 0.5g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but 0.5 g of mono-tert-butyl-hydroquinone was further added.

[실시예 42][Example 42]

실시예 1과 동일한 방법으로 실시하되, 실시예 3 내지 실시예 41에 따라 부가된 부가물을 모두 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but all of the additives added according to Examples 3 to 41 were added.

[실 험][Experiment]

실시예들에 따라 제조된 조성물을 이용하여 약 60mm 두께의 아스팔트 콘크리트층을 제조한 후 공극률, 방수성, 균열성, 간접인장강도, 변형강도, 압축강도 등을 측정하였고, 약 50mm 두께의 아스팔트 콘크리트층을 제조하여 동적안정도를 측정하여 표 1로 나타냈다. After preparing an asphalt concrete layer of about 60 mm thickness using the composition prepared according to the examples, porosity, waterproofness, cracking property, indirect tensile strength, deformation strength, compressive strength, etc. were measured, and an asphalt concrete layer of about 50 mm thickness Was prepared to measure the dynamic stability and shown in Table 1.

여기서, 동적안정도는 소성변형 저항성 평가로 Kim Test에 의한 변형강도 시험과 시험을 통해 측정하고, 간접인강도는 균열 저항성을 평가하기 위해 진행되었고, 압축강도는 아스팔트 압축강도시험기를 이용하여 측정하였다.Here, the dynamic stability was measured through the deformation strength test and test by the Kim Test as plastic deformation resistance evaluation, the indirect tensile strength was conducted to evaluate the crack resistance, and the compressive strength was measured using an asphalt compressive strength tester.

공극률Porosity 방수성Waterproof 균열정도Degree of cracking 동적안정도
(pass/mm)Dynamic stability
(pass/mm) 간접인장강도
(ITS)Indirect tensile strength
(ITS) 변형강도
(Mpa)Deformation strength
(Mpa) 압축강도(MPa)Compressive strength (MPa) 7일간7 days 28일간28 days 실시예 1Example 1 2.3%2.3% 98%98% 없음none 18521852 0.840.84 5.915.91 29.729.7 8181 실시예 2Example 2 2.2%2.2% 98%98% 없음none 16501650 0.850.85 5.915.91 30.430.4 8282 실시예 3Example 3 2,4%2,4% 98%98% 없음none 18411841 0.830.83 5.935.93 31.431.4 8585 실시예 4Example 4 2.1%2.1% 98%98% 없음none 18531853 0.840.84 5.935.93 29.829.8 8585 실시예 5Example 5 1.7%1.7% 99%99% 없음none 18541854 0.850.85 5.955.95 29.829.8 8484 실시예 6Example 6 1.8%1.8% 99%99% 없음none 18431843 0.860.86 5.925.92 29.629.6 8383 실시예 7Example 7 1.5%1.5% 99%99% 없음none 18551855 0.840.84 5.945.94 29.329.3 8484 실시예 8Example 8 1.6%1.6% 99%99% 없음none 18541854 0.880.88 5.905.90 29.829.8 8383 실시예 9Example 9 1.7%1.7% 99%99% 없음none 18561856 0.850.85 5.885.88 30.530.5 8585 실시예 10Example 10 1.5%1.5% 99%99% 없음none 18621862 0.860.86 5.955.95 31.331.3 8484 실시예 11Example 11 1.6%1.6% 99%99% 없음none 18541854 0.850.85 5.875.87 28.528.5 8585 실시예 12Example 12 1.7%1.7% 99%99% 없음none 18431843 0.860.86 5.925.92 31.631.6 8787 실시예 13Example 13 1.5%1.5% 99%99% 없음none 18451845 0.850.85 5.925.92 31.731.7 8686 실시예 14Example 14 1.6%1.6% 99%99% 없음none 18671867 0.840.84 5.875.87 30.830.8 8585 실시예 15Example 15 1.7%1.7% 99%99% 없음none 18521852 0.860.86 5.885.88 29.529.5 8686 실시예 16Example 16 1.8%1.8% 99%99% 없음none 18341834 0.860.86 5.945.94 31.331.3 8484 실시예 17Example 17 1.9%1.9% 98%98% 없음none 18611861 0.880.88 5.875.87 32.632.6 8686 실시예 18Example 18 1.3%1.3% 99%99% 없음none 18541854 0.870.87 5.865.86 32.732.7 8787 실시예 19Example 19 1.4%1.4% 99%99% 없음none 18391839 0.860.86 5.875.87 31.431.4 8585 실시예 20Example 20 1.6%1.6% 99%99% 없음none 18681868 0.860.86 5.845.84 31.631.6 8686 실시예 21Example 21 1.5%1.5% 99%99% 없음none 18521852 0.850.85 5.565.56 29.129.1 8383 실시예 22Example 22 1.4%1.4% 99%99% 없음none 18481848 0.840.84 5.875.87 31.931.9 8686 실시예 23Example 23 1.4%1.4% 99%99% 없음none 18521852 0.850.85 5.845.84 31.131.1 8787 실시예 24Example 24 1.5%1.5% 99%99% 없음none 18541854 0.860.86 5.835.83 31.231.2 8585 실시예 25Example 25 1.6%1.6% 99%99% 없음none 18571857 0.870.87 5.745.74 32.732.7 8888 실시예 26Example 26 1.3%1.3% 99%99% 없음none 18551855 0.840.84 5.755.75 31.531.5 8686 실시예 27Example 27 1.6%1.6% 99%99% 없음none 18651865 0.840.84 5.765.76 33.133.1 8989 실시예 28Example 28 1.7%1.7% 99%99% 없음none 18571857 0.850.85 5.855.85 31.631.6 8585 실시예 29Example 29 1.4%1.4% 99%99% 없음none 18751875 0.860.86 5.825.82 29.829.8 8484 실시예 30Example 30 2.2%2.2% 98%98% 없음none 18771877 0.870.87 5.815.81 31.131.1 8585 실시예 31Example 31 2.3%2.3% 98%98% 없음none 18451845 0.850.85 5.825.82 32.432.4 8686 실시예 32Example 32 2.2%2.2% 98%98% 없음none 18581858 0.840.84 5.855.85 31.231.2 8585 실시예 33Example 33 1.6%1.6% 99%99% 없음none 18521852 0.850.85 5.855.85 29.829.8 8383 실시예 34Example 34 1.4%1.4% 99%99% 없음none 18631863 0.830.83 5.835.83 30.330.3 8484 실시예 35Example 35 1.6%1.6% 99%99% 없음none 18511851 0.850.85 5.865.86 31.131.1 8686 실시예 36Example 36 1.7%1.7% 99%99% 없음none 18861886 0.860.86 5.835.83 30.330.3 8585 실시예 37Example 37 1.5%1.5% 99%99% 없음none 18631863 0.860.86 5.805.80 29.429.4 8383 실시예 38Example 38 1.7%1.7% 99%99% 없음none 18871887 0.860.86 5.825.82 32.732.7 8787 실시예 39Example 39 1.5%1.5% 98%98% 없음none 18651865 0.870.87 5.845.84 29.729.7 8282 실시예 40Example 40 1.6%1.6% 99%99% 없음none 18541854 0.840.84 5.735.73 31.831.8 8585 실시예 41Example 41 1.7%1.7% 99%99% 없음none 18511851 0.870.87 5.755.75 29.929.9 8383 실시예 42Example 42 1.5%1.5% 99%99% 없음none 18631863 0.890.89 5.815.81 28.828.8 8282

표 1에 나타낸 바와 같이, 불투수성 개질아스팔트 콘크리트 조성물을 사용한 실시예들의 공극률이 1~3% 범위 내로 좋고, 방수성, 동적안정도, 간접인장강도 및 변형강도가 좋으며, 균열이 없고, 압축강도는 28일이 경과한 시점에서 75메가파스칼 이상으로서, 상기 실시예의 모든 조성물이 고강도인 것을 확인할 수 있었다.As shown in Table 1, the porosity of the examples using the impermeable modified asphalt concrete composition is good within the range of 1 to 3%, waterproofness, dynamic stability, indirect tensile strength and deformation strength are good, there is no crack, and the compressive strength is 28 days. When this elapsed, it was confirmed that all the compositions of the above examples had high strength as 75 megapascals or more.

이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art to which the present invention pertains will understand that the present invention can be implemented in other specific forms without changing the technical spirit or essential features. Therefore, all the embodiments described above are illustrative and should be understood as non-limiting. The scope of the present invention should be construed as including all altered or modified forms derived from the meaning and scope of the claims to be described later rather than the above detailed description, and equivalent concepts thereof.

Claims (5)

아스팔트 100중량부 기준으로,
폐타이어 분말 1 내지 25중량부;
스티렌부타디엔스티렌 1 내지 25중량부;
140℃ 점도가 130cps인 지방족 C-5석유수지 1 내지 25중량부;
골재 500 내지 2,000중량부;
미분말 골재 30 내지 150중량부;
셀룰로오스 섬유 0.1 내지 2중량부;
왁스 0.1 내지 2중량부; 및
고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에,
2-브로모피리딘을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고,
웰란 검을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며,
네오펜틸글리콜을 아스팔트 100중량부 기준으로 0.1 내지 4중량부로 더 포함하고,
코코베타인을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하며,
세륨을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고,
진크암모늄클로라이드를 아스팔트 100중량부 기준으로 0.1 내지 4중량부로 더 포함하며,
천매암 분말을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고,
3-메르캅토프로필트리메톡시실란을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
구연산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
메타규산나트륨을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
질화마그네슘을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고,
황산알루미늄을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
이미다졸린베타인을 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함하고,
규불화마그네슘을 아스팔트 100중량부 기준으로 0.5 내지 3중량부로 더 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물.
Based on 100 parts by weight of asphalt,
1 to 25 parts by weight of waste tire powder;
1 to 25 parts by weight of styrene butadiene styrene;
140° C. 1 to 25 parts by weight of an aliphatic C-5 petroleum resin having a viscosity of 130 cps;
500 to 2,000 parts by weight of aggregate;
30 to 150 parts by weight of fine powder aggregate;
0.1 to 2 parts by weight of cellulose fibers;
0.1 to 2 parts by weight of wax; And
In an impermeable waterproof asphalt concrete composition comprising waste tire powder containing 0.1 to 2 parts by weight of a rubber aging inhibitor,
2-bromopyridine is further included in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt,
Welan gum further comprises 0.1 to 3 parts by weight based on 100 parts by weight of asphalt,
Neopentyl glycol is further included in an amount of 0.1 to 4 parts by weight based on 100 parts by weight of asphalt,
It further contains 0.1 to 5 parts by weight of coco betaine based on 100 parts by weight of asphalt,
Cerium further comprises 0.1 to 5 parts by weight based on 100 parts by weight of asphalt,
Further comprising 0.1 to 4 parts by weight of zinc ammonium chloride based on 100 parts by weight of asphalt,
Further comprising 0.1 to 5 parts by weight of cheonmaelite powder based on 100 parts by weight of asphalt,
3-mercaptopropyltrimethoxysilane further comprises 1 to 3 parts by weight based on 100 parts by weight of asphalt,
Citric acid is further included in 1 to 5 parts by weight based on 100 parts by weight of asphalt,
Sodium metasilicate is further included in an amount of 1 to 5 parts by weight based on 100 parts by weight of asphalt,
Further containing magnesium nitride in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt,
Further comprising 1 to 5 parts by weight of aluminum sulfate based on 100 parts by weight of asphalt,
Imidazoline betaine further comprises 0.1 to 2 parts by weight based on 100 parts by weight of asphalt,
An impermeable waterproof asphalt concrete composition comprising waste tire powder further comprising 0.5 to 3 parts by weight of magnesium silicate based on 100 parts by weight of asphalt.
 삭제delete 삭제delete 삭제delete 시공하고자 하는 대상면을 정리하는 정리단계;
상기 정리단계가 종료된 대상면에 아스팔트 100중량부 기준으로, 폐타이어 분말 1 내지 25중량부, 스티렌부타디엔스티렌 1 내지 25중량부, 140℃ 점도가 130cps인 지방족 C-5석유수지 1 내지 25중량부, 골재 500 내지 2,000중량부, 미분말 골재 30 내지 150중량부, 셀룰로오스 섬유 0.1 내지 2중량부, 왁스 0.1 내지 2중량부, 및 고무노화방지제 0.1 내지 2중량부를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물에, 2-브로모피리딘을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 웰란 검을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며, 네오펜틸글리콜을 아스팔트 100중량부 기준으로 0.1 내지 4중량부로 더 포함하고, 코코베타인을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하며, 세륨을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고, 진크암모늄클로라이드를 아스팔트 100중량부 기준으로 0.1 내지 4중량부로 더 포함하며, 천매암 분말을 아스팔트 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고, 3-메르캅토프로필트리메톡시실란을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 구연산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 메타규산나트륨을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 질화마그네슘을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 황산알루미늄을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 이미다졸린베타인을 아스팔트 100중량부 기준으로 0.1 내지 2중량부로 더 포함하고, 규불화마그네슘을 아스팔트 100중량부 기준으로 0.5 내지 3중량부로 더 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 타설하는 타설단계;
상기 타설단계가 종료된 뒤 타설된 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 다지는 다짐단계; 및
상기 다짐단계가 종료된 후 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물을 양생하는 양생단계를 포함하는 폐타이어 분말을 포함하는 불투수성 방수아스팔트 콘크리트 조성물 시공방법.An arrangement step of arranging the target surface to be constructed;
1 to 25 parts by weight of waste tire powder, 1 to 25 parts by weight of styrene butadiene styrene, 1 to 25 parts by weight of aliphatic C-5 petroleum resin having a viscosity of 130 cps at 140°C, based on 100 parts by weight of asphalt on the surface where the cleaning step is completed Impermeability including waste tire powder including parts, 500 to 2,000 parts by weight of aggregate, 30 to 150 parts by weight of fine powder aggregate, 0.1 to 2 parts by weight of cellulose fiber, 0.1 to 2 parts by weight of wax, and 0.1 to 2 parts by weight of rubber aging inhibitor In the waterproof asphalt concrete composition, 2-bromopyridine is further included in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt, and a wellan gum is further included in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of asphalt, and neopentyl glycol is used in an amount of asphalt 100 It further comprises 0.1 to 4 parts by weight based on parts by weight, and further comprises 0.1 to 5 parts by weight based on 100 parts by weight of asphalt, further comprising 0.1 to 5 parts by weight of cerium based on 100 parts by weight of asphalt, and zinc ammonium Chloride is further included in an amount of 0.1 to 4 parts by weight based on 100 parts by weight of asphalt, and a phyllite powder is further included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of asphalt, and 3-mercaptopropyltrimethoxysilane is based on 100 parts by weight of asphalt. It further comprises 1 to 3 parts by weight, citric acid is further included in 1 to 5 parts by weight based on 100 parts by weight of asphalt, and sodium metasilicate is further included in 1 to 5 parts by weight based on 100 parts by weight of asphalt, and magnesium nitride is used as asphalt. Including 0.1 to 3 parts by weight based on 100 parts by weight, aluminum sulfate is further included in 1 to 5 parts by weight based on 100 parts by weight of asphalt, and further containing imidazoline betaine in 0.1 to 2 parts by weight based on 100 parts by weight of asphalt And, a pouring step of pouring an impermeable waterproof asphalt concrete composition comprising waste tire powder further comprising 0.5 to 3 parts by weight of magnesium silicate based on 100 parts by weight of asphalt;
A compaction step of compacting the impermeable waterproof asphalt concrete composition including the poured waste tire powder after the pouring step is completed; And
A method of constructing an impermeable waterproof asphalt concrete composition comprising waste tire powder comprising a curing step of curing an impermeable waterproof asphalt concrete composition comprising waste tire powder after the compaction step is completed.
KR1020200138379A 2020-10-23 2020-10-23 Water-Impermeable Waterproof Asphalt Concrete Compositions Comprising Crum Rubber Modifier and Constructing Methods Using Thereof KR102207013B1 (en)