KR102127439B1 - Conjugated microporous polymers film and manufacturing method the same - Google Patents
Conjugated microporous polymers film and manufacturing method the same Download PDFInfo
- Publication number
- KR102127439B1 KR102127439B1 KR1020180064861A KR20180064861A KR102127439B1 KR 102127439 B1 KR102127439 B1 KR 102127439B1 KR 1020180064861 A KR1020180064861 A KR 1020180064861A KR 20180064861 A KR20180064861 A KR 20180064861A KR 102127439 B1 KR102127439 B1 KR 102127439B1
- Authority
- KR
- South Korea
- Prior art keywords
- microporous polymer
- conjugated microporous
- polymer film
- nozzle
- monomer
- Prior art date
Abstract
본 발명은 공액 미소공성 고분자 필름 및 이의 제조방법 관한 것으로, 더욱 자세하게는, 공액 미소공성 고분자(conjugated microporous polymers)의 단량체를 포함하는 단량체 용액을 준비하는 단계; 촉매 용액을 준비하는 단계; 상기 단량체 용액을 제1 노즐에 도입하는 단계; 상기 촉매 용액을 제2 노즐에 도입하는 단계; 및 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하는 단계;를 포함하는, 공액 미소공성 고분자 필름의 제조방법 및 이를 통해 제조된 공액 미소공성 고분자 필름에 관한 것이다.The present invention relates to a conjugated microporous polymer film and a method for manufacturing the same, and more specifically, preparing a monomer solution containing a monomer of conjugated microporous polymers; Preparing a catalyst solution; Introducing the monomer solution into a first nozzle; Introducing the catalyst solution into a second nozzle; And ultrasonically spraying the monomer solution and the catalyst solution simultaneously using the first nozzle and the second nozzle on a substrate; including a method for manufacturing a conjugated microporous polymer film and a conjugated microporous polymer prepared therefrom It's about the film.
Description
본 발명은 공액 미소공성 고분자 필름 및 이의 제조방법 관한 것이다.The present invention relates to a conjugated microporous polymer film and a method for manufacturing the same.
COF(covalent organic frameworks)는 큰 표면적을 갖는 다공성 고분자로써 공유결합을 이용하여 pore의 크기를 정밀하게 조작함으로써 2D 및 3D의 구조체를 형성 할 수 있는 새로운 물질이며, 2005년 Yaghi 교수가 science에 최초로 보고한 이후에 최근 10여 년간 매우 활발한 연구가 진행되고 있다. COF는 다양한 building block들을 이용하여 여러 가지 가스들(CO2, CH4, H2, NH3)의 저장, 반도체 및 광전도 분야, 촉매반응 등에 응용될 수 있다.COF (covalent organic frameworks) is a porous polymer with a large surface area, and is a new material capable of forming 2D and 3D structures by precisely manipulating pore sizes using covalent bonds. Since then, very active research has been in progress for the past 10 years. COF can be applied to storage of various gases (CO 2 , CH 4 , H 2 , NH 3 ), semiconductor and photoconductive fields, and catalytic reactions using various building blocks.
building block을 형성하기 위한 대표적인 힘은 π- π 결합과 같은 약한 것부터 공유결합과 같은 상대적으로 강한 것에 이르기까지 다양하다. 무기물 구조체로는 나노파티클, 나노와이어, 2차원 층 물질, zeolite 등이 있고, 유-무기 복합체들은 1D & 2D coordination polymer, MOF(metal organic frameworks) 등이 보고되었다. 또한, 유기물 구조체는 자연에 존재하는 tropinone, polyethylene, nylon, polystyrene, 다공성 유기 고분자들(HCP(hypercrosslinked polymers), PIM(polymers of intrinsic microporosity), CMPs(conjugated microporous polymers, 2D & 3D COF(covalent organic frameworks))이 있다.Typical forces for building blocks range from weak, such as π-π bonds, to relatively strong, such as covalent bonds. Inorganic structures include nanoparticles, nanowires, two-dimensional layer materials, zeolites, etc., and organic-inorganic composites have been reported as 1D & 2D coordination polymers, MOFs (metal organic frameworks), and the like. In addition, organic structures include tropinone, polyethylene, nylon, polystyrene, porous organic polymers (HCPs), polymers of intrinsic microporosity (PIM), conjugated microporous polymers (CMPs), 2D & 3D covalent organic frameworks )).
CMPs(conjugated microporous polymers)는 공액 파이 전자계 (Conjugated π electron system)가 3D 네트워크로 이루어진 공액 고분자로, 미소공성 (microporous)을 가지며 공액 분자로 이뤄져 반도체 (semiconductor) 특성을 가지고 있다. 이런 특성을 바탕으로, 현재 CMPs는 에너지 저장 및 변환 소재, 광촉매 또는 흡착 및 분리막 (adsorption and separation membrane)에서 뛰어난 특성을 보여주며 새로운 신소재로 각광을 받고 있다. 그러나, CMPs를 새로운 소재로 적용하기 위해서는 얇은 박막 형태로 제조하는 것이 필수적이나, CMPs의 낮은 분산성 및 녹지 않는 특성으로 가공성(processability)에 문제점을 가지고 있다. 현재까지 연구되어온 CMP-film 제조법은 복잡한 공정과정, 한정된 합성법 및 생산성의 한계를 보여왔다.Conjugated microporous polymers (CMPs) are conjugated polymers composed of a conjugated π electron system (3D network) and are microporous and consist of conjugated molecules to have semiconductor properties. Based on these characteristics, CMPs are now emerging as new materials with excellent properties in energy storage and conversion materials, photocatalysts or adsorption and separation membranes. However, in order to apply CMPs as a new material, it is essential to manufacture a thin film, but it has a problem in processability due to low dispersibility and insoluble properties of CMPs. The CMP-film manufacturing method that has been studied to date has shown a complicated process, limited synthesis, and limitations in productivity.
본 발명은 상술한 문제점을 해결하기 위한 것으로, 본 발명의 목적은, 간단한 프로세스를 통해 단량체 (monomer)에서 한번에(one-step) 공액 미소공성 고분자 필름을 제조할 수 있는 제조방법을 제공하는 것이다. The present invention is to solve the above-mentioned problems, and an object of the present invention is to provide a manufacturing method capable of producing a one-step conjugated microporous polymer film in a monomer through a simple process.
또한, 본 발명의 공액 미소공성 고분자 필름의 제조방법에 따라 제조된 얇은 박막 형태의 공액 미소공성 고분자 필름을 제공하는 것이다.In addition, to provide a conjugated microporous polymer film in the form of a thin thin film prepared according to the method for producing a conjugated microporous polymer film of the present invention.
그러나, 본 발명이 해결하고자 하는 과제는 이상에서 언급한 것들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 해당 분야 통상의 기술자에게 명확하게 이해될 수 있을 것이다.However, the problems to be solved by the present invention are not limited to those mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.
본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 공액 미소공성 고분자(conjugated microporous polymers)의 단량체를 포함하는 단량체 용액을 준비하는 단계; 촉매 용액을 준비하는 단계; 상기 단량체 용액을 제1 노즐에 도입하는 단계; 상기 촉매 용액을 제2 노즐에 도입하는 단계; 및 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하는 단계;를 포함한다.Method for producing a conjugated microporous polymer film according to an embodiment of the present invention, preparing a monomer solution containing a monomer of the conjugated microporous polymers (conjugated microporous polymers); Preparing a catalyst solution; Introducing the monomer solution into a first nozzle; Introducing the catalyst solution into a second nozzle; And ultrasonically spraying the monomer solution and the catalyst solution simultaneously on the substrate using the first nozzle and the second nozzle.
일 측면에 따르면, 상기 공액 미소공성 고분자의 단량체는, 하기 화학식 1 내지 3, 브로모벤젠 (bromobenzene), 디브로모벤젠 (dibromobenzene), 트리브로모벤젠 (tribromobenzene), 테트라 브로모벤젠 (tetrabromobenzene), 헥사브로모벤젠 (hexabromobenzene), 요오드벤젠 (iodobenzene), 디요오드벤젠 (diiodobenzene), 트리요오드벤젠 (triiodobenzene), 테트라요오드벤젠 (tetraiodobenzene), 헥사요오드벤젠 (hexaiodobenzene), 페닐보론산 (phenylboronic acid), 페닐디보론산 (phenyldiboronic acid), 페닐트리보론산 (phenyltriboronic acid), 페닐테트라보론산 (phenyltetraboronic acid), 페닐헥사보론산 (phenylhexaboronic acid), 벤젠카르복시알데히드 (Benzenecarboxaldehyde), 벤젠디카르복시알데히드 (Benzenedicarboxaldehyde), 벤젠트리카르복시알데히드 (Benzenetricarboxaldehyde), 벤젠테트라카르복시알데히드 (Benzenetetracarboxaldehyde), 벤젠헥사카르복시알데히드 (Benzenehexacarboxaldehyde), 에티닐벤젠 (ethynylbenzene), 디에티닐벤젠 (diethynylbenzene), 트리에티닐벤젠 (triethynylbenzene), 테트라에티닐벤젠 (tetraethynylbenzene), 헥사에티닐벤젠 (hexaethynylbenzene), 벤젠아민 (Benzeneamine), 벤젠다이아민 (Benzenediamine), 벤젠트리아민 (Benzenetriamine), 벤젠테트라아민 (Benzenetetraamine), 벤젠헥사아민 (Benzenehexaamine), 벤젠카르보니트릴 (benzenecarbonitrile), 벤젠디카르보니트릴 (benzenedicarbonitrile), 벤젠트리카르보니트릴(benzenetricarbonitrile), 벤젠테트라카르보니트릴 (benzenetetracarbonitrile), 벤젠헥사카르보니트릴 (benzenehexacarbonitrile), 트라이페닐아민 (triphenylamine), 카바졸 (9H-carbazole) 및 이들의 유도체로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다.According to one aspect, the monomers of the conjugated microporous polymer are the following
[화학식 1][Formula 1]
[화학식 2][Formula 2]
[화학식 3][Formula 3]
일 측면에 따르면, 상기 촉매는, FeCl3, Fe(TsO)3 및 Na2S2O8으로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다.According to an aspect, the catalyst may include at least one selected from the group consisting of FeCl 3 , Fe(TsO) 3 and Na 2 S 2 O 8 .
일 측면에 따르면, 상기 단량체 용액의 농도는, 0.4 mg/ml 내지 1.0 mg/ml 인 것일 수 있다.According to one aspect, the concentration of the monomer solution may be 0.4 mg/ml to 1.0 mg/ml.
일 측면에 따르면, 상기 촉매 용액의 농도는, 2.0 mg/ml 내지 3.0 mg/ml인 것일 수 있다.According to one aspect, the concentration of the catalyst solution may be 2.0 mg/ml to 3.0 mg/ml.
일 측면에 따르면, 상기 초음파 분사하는 단계에서 기판의 온도는, 100 ℃ 내지 200 ℃인 것일 수 있다.According to one aspect, the temperature of the substrate in the ultrasonic injection step may be 100 ℃ to 200 ℃.
일 측면에 따르면, 상기 기판은, 투명전극, 유리, 금속, 섬유 및 종이로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다.According to an aspect, the substrate may include at least one selected from the group consisting of a transparent electrode, glass, metal, fiber, and paper.
일 측면에 따르면, 상기 초음파 분사하는 단계는, 100 kHz 내지 200 kHz의 주파수를 가지는 초음파를 이용하는 것일 수 있다.According to one aspect, the ultrasonic injection step may be to use ultrasonic waves having a frequency of 100 kHz to 200 kHz.
일 측면에 따르면, 상기 초음파 분사하는 단계는, 200 W 이상의 전력을 가지는 초음파를 이용하는 것일 수 있다.According to one aspect, the ultrasonic injection step may be to use ultrasonic waves having a power of 200 W or more.
일 측면에 따르면, 상기 초음파 분사하는 단계에서 분사되는 상기 단량체 및 상기 촉매는, 분사 후 서로 반응하여 공액 미소공성 고분자 필름으로 합성되는 것일 수 있다.According to one aspect, the monomer and the catalyst injected in the ultrasonic injection step may be synthesized into a conjugated microporous polymer film by reacting with each other after injection.
본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름은, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법에 의해 제조되고, 1.5 ㎛ 이하의 두께를 가지는 것이다.The conjugated microporous polymer film according to an embodiment of the present invention is manufactured by a method for producing a conjugated microporous polymer film according to an embodiment of the present invention, and has a thickness of 1.5 μm or less.
본 발명에 따른 초음파 스프레이 화학(Ultrasonic Spray Chemistry, USC) 기술을 이용하여 공액 미소공성 고분자 필름을 제조함으로써, 간단한 프로세스를 통해 단량체(monomer)에서 단일 공정(one-step)으로 얇은 박막 형태의 공액 미소공성 고분자 필름을 제조할 수 있다. 즉, 단 시간에 공액 미소공성 고분자 필름 제조가 가능 할 뿐만 아니라 연속공정이 (Continuous) 가능하여 양산화가 가능하다.By producing a conjugated microporous polymer film using the ultrasonic spray chemistry (U.S.C.) technology according to the present invention, a simple thin film-conjugated microstructure in a single step from a monomer through a simple process A porous polymer film can be prepared. In other words, it is possible not only to produce a conjugated microporous polymer film in a short time, but also to perform continuous process (Continuous), so that mass production is possible.
또한, 더블 노즐 시스템으로 단량체와 촉매를 분리 할 수 있어 산화 커플링 반응(oxidative coupling reaction) 뿐만 아니라 축합 반응(condensation), 스즈키 커플링(suzuki coupling) 등 다양한 화학반응을 적용하여 미소공성 고분자 필름을 제조할 수 있다.In addition, it is possible to separate monomers and catalysts with a double nozzle system to apply various chemical reactions such as condensation and suzuki coupling as well as oxidative coupling reaction to produce microporous polymer films. Can be produced.
또한, 기판 (substrate)에 제한이 없어 투명전극, 유리, 금속은 물론 섬유나 종이에 공액 미소공성 고분자 필름을 제작할 수 있어 기존 연구에서 다루지 못했던 다양한 분야에 응용할 수 있다.In addition, since there is no restriction on the substrate, it is possible to manufacture a conjugated microporous polymer film on a transparent electrode, glass, metal, as well as fiber or paper, and thus it can be applied to various fields not covered in the previous research.
도 1은, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법의 공정 흐름도이다.
도 2a 내지 도 2c는, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름에 포함되는 단량체의 종류를 도시한 도면이다.
도 3은 본 발명의 일 실시예에 따른 초음파 분사 시스템의 구성을 나타낸 도면이다.
도 4는 본 발명의 초음파 분사 화학반응에 의한 공액 미소공성 고분자 필름의 중합 메커니즘을 나타낸 도면이다.
도 5a 내지 도 5c는 본 발명의 실시예 1 내지 실시예 4를 통해 제조된 공액 미소공성 고분자 필름 및 비교예의 FT-IR 그래프이다.
도 6은 본 발명의 실시예 4를 통해 제조된 공액 미소공성 고분자 필름의 SEM 이미지 및 TEM 이미지이다.1 is a process flow diagram of a method for producing a conjugated microporous polymer film according to an embodiment of the present invention.
2A to 2C are diagrams showing types of monomers included in the conjugated microporous polymer film according to an embodiment of the present invention.
3 is a view showing the configuration of an ultrasonic injection system according to an embodiment of the present invention.
4 is a view showing the polymerization mechanism of the conjugated microporous polymer film by the ultrasonic injection chemical reaction of the present invention.
5A to 5C are FT-IR graphs of conjugated microporous polymer films and comparative examples prepared through Examples 1 to 4 of the present invention.
6 is a SEM image and a TEM image of the conjugated microporous polymer film prepared through Example 4 of the present invention.
이하 첨부된 도면을 참조하여 본 발명의 실시예들을 상세히 설명한다. 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 또한, 본 명세서에서 사용되는 용어들은 본 발명의 바람직한 실시예를 적절히 표현하기 위해 사용된 용어들로서, 이는 사용자, 운용자의 의도 또는 본 발명이 속하는 분야의 관례 등에 따라 달라질 수 있다. 따라서, 본 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다. 각 도면에 제시된 동일한 참조 부호는 동일한 부재를 나타낸다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. In describing the present invention, when it is determined that a detailed description of related known functions or configurations may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted. In addition, terms used in the present specification are terms used to appropriately represent a preferred embodiment of the present invention, which may vary according to a user's, operator's intention, or customs in the field to which the present invention pertains. Accordingly, definitions of these terms should be made based on the contents throughout the specification. The same reference numerals in each drawing denote the same members.
명세서 전체에서, 어떤 부재가 다른 부재 "상에" 위치하고 있다고 할 때, 이는 어떤 부재가 다른 부재에 접해 있는 경우뿐 아니라 두 부재 사이에 또 다른 부재가 존재하는 경우도 포함한다.Throughout the specification, when one member is positioned “on” another member, this includes not only the case where one member abuts another member, but also the case where another member exists between the two members.
명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 다른 구성요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다.Throughout the specification, when a part “includes” a certain component, it means that the other component may be further included instead of excluding the other component.
이하, 본 발명의 공액 미소공성 고분자 필름 및 이의 제조방법에 대하여 실시예 및 도면을 참조하여 구체적으로 설명하도록 한다. 그러나, 본 발명이 이러한 실시예 및 도면에 제한되는 것은 아니다.Hereinafter, the conjugated microporous polymer film of the present invention and a method for manufacturing the same will be described in detail with reference to examples and drawings. However, the present invention is not limited to these examples and drawings.
본 발명은, 공액 미소공성 고분자 필름의 제조방법에 관한 것으로, 본 발명의 일 실시예에 따라, 상기 제조방법은, 초음파 분사 화학 기술(Ultrasonic spray chemistry)에 의한 용액 공정을 적용하여, 간단한 프로세스를 통해 단량체(monomer)에서 단일 공정(one-step)으로 얇은 박막 형태의 공액 미소공성 고분자 필름을 제조할 수 있다.The present invention relates to a method for manufacturing a conjugated microporous polymer film, and according to an embodiment of the present invention, the manufacturing method applies a solution process by ultrasonic spray chemistry technology (Ultrasonic spray chemistry) to perform a simple process. Through it, it is possible to manufacture a conjugated microporous polymer film in the form of a thin thin film in a single step from a monomer.
도 1은, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법의 공정 흐름도이다. 본 발명의 일 실시예에 따라, 도 1을 참조하며, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 공액 미소공성 고분자의 단량체를 포함하는 단량체 용액을 준비하는 단계(100a); 촉매 용액을 준비하는 단계(100b); 및 공액 미소공성 고분자 필름이 중합되는 단계(200); 를 포함할 수 있다.1 is a process flow diagram of a method for producing a conjugated microporous polymer film according to an embodiment of the present invention. According to an embodiment of the present invention, referring to FIG. 1, a method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention includes preparing a monomer solution containing a monomer of a conjugated microporous polymer (100a ); Preparing a catalyst solution (100b); And a
구체적으로, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 공액 미소공성 고분자(conjugated microporous polymers)의 단량체를 포함하는 단량체 용액을 준비하는 단계(100a); 촉매 용액을 준비하는 단계(100b); 상기 단량체 용액을 제1 노즐에 도입하는 단계(210); 상기 촉매 용액을 제2 노즐에 도입하는 단계(210); 및 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하는 단계(220);를 포함한다.Specifically, a method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention comprises the steps of preparing a monomer solution containing a monomer of a conjugated microporous polymer (100a); Preparing a catalyst solution (100b); Introducing the monomer solution into a first nozzle (210); Introducing the catalyst solution into a second nozzle (210); And a step (220) of ultrasonically spraying the monomer solution and the catalyst solution simultaneously using the first nozzle and the second nozzle on a substrate.
도 2a 내지 도 2c는, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름에 포함되는 단량체의 종류를 도시한 도면이다.2A to 2C are diagrams showing types of monomers included in a conjugated microporous polymer film according to an embodiment of the present invention.
도 2a 내지 도 2c를 참조하면, 상기 공액 미소공성 고분자의 단량체는 쉽게 산화할 수 있는 전자 공여 유닛(electron donating unit)을 포함하는 것을 알 수 있다. 다만, 이에 한정되지 않고, 공액 미소공성 고분자(conjugated microporous polymers)를 구성할 수 있는 모노머(monomer)라면 제한 없이 사용할 수 있다.Referring to Figures 2a to 2c, it can be seen that the monomer of the conjugated microporous polymer includes an electron donating unit that can be easily oxidized. However, the present invention is not limited thereto, and any monomer capable of forming conjugated microporous polymers may be used without limitation.
일 측면에 따르면, 상기 공액 미소공성 고분자의 단량체는, 하기 화학식 1 내지 3, 브로모벤젠 (bromobenzene), 디브로모벤젠 (dibromobenzene), 트리브로모벤젠 (tribromobenzene), 테트라 브로모벤젠 (tetrabromobenzene), 헥사브로모벤젠 (hexabromobenzene), 요오드벤젠 (iodobenzene), 디요오드벤젠 (diiodobenzene), 트리요오드벤젠 (triiodobenzene), 테트라요오드벤젠 (tetraiodobenzene), 헥사요오드벤젠 (hexaiodobenzene), 페닐보론산 (phenylboronic acid), 페닐디보론산 (phenyldiboronic acid), 페닐트리보론산 (phenyltriboronic acid), 페닐테트라보론산 (phenyltetraboronic acid), 페닐헥사보론산 (phenylhexaboronic acid), 벤젠카르복시알데히드 (Benzenecarboxaldehyde), 벤젠디카르복시알데히드 (Benzenedicarboxaldehyde), 벤젠트리카르복시알데히드 (Benzenetricarboxaldehyde), 벤젠테트라카르복시알데히드 (Benzenetetracarboxaldehyde), 벤젠헥사카르복시알데히드 (Benzenehexacarboxaldehyde), 에티닐벤젠 (ethynylbenzene), 디에티닐벤젠 (diethynylbenzene), 트리에티닐벤젠 (triethynylbenzene), 테트라에티닐벤젠 (tetraethynylbenzene), 헥사에티닐벤젠 (hexaethynylbenzene), 벤젠아민 (Benzeneamine), 벤젠다이아민 (Benzenediamine), 벤젠트리아민 (Benzenetriamine), 벤젠테트라아민 (Benzenetetraamine), 벤젠헥사아민 (Benzenehexaamine), 벤젠카르보니트릴 (benzenecarbonitrile), 벤젠디카르보니트릴 (benzenedicarbonitrile), 벤젠트리카르보니트릴(benzenetricarbonitrile), 벤젠테트라카르보니트릴 (benzenetetracarbonitrile), 벤젠헥사카르보니트릴 (benzenehexacarbonitrile), 트라이페닐아민 (triphenylamine), 카바졸 (9H-carbazole) 및 이들의 유도체로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다.According to one aspect, the monomers of the conjugated microporous polymer are the following
[화학식 1][Formula 1]
[화학식 2][Formula 2]
[화학식 3][Formula 3]
본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 더블 노즐 시스템으로 단량체와 촉매를 분리 할 수 있어 산화 커플링 반응(oxidative coupling reaction) 뿐만 아니라 축합 반응(condensation), 스즈키 커플링(suzuki coupling) 등 다양한 화학반응을 적용할 수 있다. 즉, 원하는 화학반응에 따라 다양한 단량체를 사용할 수 있다.The method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention can separate a monomer and a catalyst using a double nozzle system, as well as an oxidative coupling reaction, condensation, and Suzuki coupling. Various chemical reactions such as (suzuki coupling) can be applied. That is, various monomers can be used according to a desired chemical reaction.
일 측면에 따르면, 상기 단량체 용액의 농도는, 0.4 mg/ml 내지 1.0 mg/ml 인 것일 수 있다. 바람직하게는 0.5 mg/ml인 것일 수 있다. 상기 단량체 용액의 농도가 0.4 mg/ml 미만일 경우 공액 미소공성 고분자의 합성이 충분히 되지 않아, 고분자 필름이 기판 위에서 찢어지고 떨어져 나가는 문제점이 발생할 수 있고, 상기 단량체 용액의 농도가 1.0 mg/ml을 초과할 경우 공액 미소공성 고분자 합성의 수득률이 낮고, 필름의 표면이 고르지 못하는 문제점이 발생할 수 있다.According to one aspect, the concentration of the monomer solution may be 0.4 mg/ml to 1.0 mg/ml. It may be preferably 0.5 mg/ml. When the concentration of the monomer solution is less than 0.4 mg/ml, the synthesis of the conjugated microporous polymer is not sufficiently performed, which may cause the polymer film to tear on the substrate and fall off, and the concentration of the monomer solution exceeds 1.0 mg/ml. If it does, the yield of the conjugated microporous polymer synthesis is low, and the surface of the film may be uneven.
일 측면에 따르면, 상기 촉매는, FeCl3, Fe(TsO)3 및 Na2S2O8으로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다. 다만, 이에 한정되지 않으며, 단량체를 산화 시킬 수 있는 산화제라면 제한 없이 사용할 수 있다. 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 더블 노즐 시스템으로 단량체와 촉매를 분리 할 수 있어 산화 커플링 반응(oxidative coupling reaction) 뿐만 아니라 축합 반응(condensation), 스즈키 커플링(suzuki coupling) 등 다양한 화학반응을 적용할 수 있다. 즉, 원하는 화학반응에 따라 다양한 촉매를 사용할 수 있다.According to an aspect, the catalyst may include at least one selected from the group consisting of FeCl 3 , Fe(TsO) 3 and Na 2 S 2 O 8 . However, the present invention is not limited thereto, and any oxidizing agent capable of oxidizing the monomer may be used without limitation. The method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention can separate a monomer and a catalyst using a double nozzle system, so as to not only oxidative coupling reaction, but also condensation, Suzuki coupling Various chemical reactions such as (suzuki coupling) can be applied. That is, various catalysts can be used depending on the desired chemical reaction.
일 측면에 따르면, 상기 촉매 용액의 농도는, 2.0 mg/ml 내지 3.0 mg/ml인 것일 수 있다. 바람직하게는 2.6 mg/ml인 것일 수 있다. 상기 촉매 용액의 농도가 2.0 mg/ml 미만일 경우 반응성이 낮아져 공액 미소공성 고분자 필름이 합성되지 않는 문제점이 발생할 수 있고, 상기 촉매 용액의 농도가 3.0 mg/ml을 초과할 경우 공액 미소공성 고분자 필름의 표면도가 고르지 못하며, 남은 촉매를 필름에서 제거 할 때 필름에 핀홀이 생기는 문제점이 발생할 수 있다.According to one aspect, the concentration of the catalyst solution may be 2.0 mg/ml to 3.0 mg/ml. Preferably it may be 2.6 mg / ml. When the concentration of the catalyst solution is less than 2.0 mg/ml, reactivity becomes low, and thus a problem that a conjugated microporous polymer film is not synthesized may occur, and when the concentration of the catalyst solution exceeds 3.0 mg/ml, the conjugated microporous polymer film The surface is uneven, and pinholes may occur in the film when the remaining catalyst is removed from the film.
본 발명의 일 예로, 공액 미소공성 고분자 필름이 중합되는 단계(200)는, 단량체 용액 및 촉매 용액을 노즐에 도입하는 단계(210); 및 기판 상에 초음파 분사하는 단계(220);를 포함할 수 있다.As an example of the present invention, the
일 측면에 따르면, 공액 미소공성 고분자 필름이 중합되는 단계(200)는, 복수개의 노즐을 갖는 초음파 분사 시스템을 이용할 수 있으며, 도 3은 본 발명의 일 실시예에 따른 초음파 분사 시스템의 구성을 예시적으로 나타낸 것으로, 도 3에서 공액 미소공성 고분자 필름이 중합되는 단계(200)는, 제1 노즐 및 제2 노즐을 포함하는 더블 노즐(Double-nozzle)을 구비한 초음파 분사 시스템을 이용할 수 있다.According to one aspect, the
일 측면에 따르면, 단량체 용액 및 촉매 용액을 노즐에 도입하는 단계(210)는, 단량체 용액을 제1 노즐에 도입하고, 촉매 용액을 제2 노즐에 도입하는 단계이다. 예를 들어, 단량체 용액 및 촉매 용액을 노즐에 도입하는 단계(210)는 연속적으로 수행되는 것일 수 있다. 즉, 본 발명의 일 실시예에 따르면, 단 시간에 공액 미소공성 고분자 필름 제조가 가능 할 뿐만 아니라 연속공정이 (Continuous) 가능하여 양산화가 가능하다.According to one aspect, the
일 측면에 따르면, 노즐에 도입하는 단계(210)는, 각 용액을 0.2 ml/min 이상; 0.3 ml/min 내지 10 ml/min; 0.3 ml/min 내지 6 ml/min; 0.3 ml/min 내지 2 ml/min; 또는 0.1 ml/min 내지 1 ml/min의 유량으로 도입하는 것일 수 있다. According to one aspect, the step of introducing 210 to the nozzle, each solution 0.2 ml / min or more; 0.3 ml/min to 10 ml/min; 0.3 ml/min to 6 ml/min; 0.3 ml/min to 2 ml/min; Or it may be introduced at a flow rate of 0.1 ml/min to 1 ml/min.
상술한 바와 같이 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 더블 노즐 시스템으로 단량체와 촉매를 분리 할 수 있어 다양한 화학반응을 적용할 수 있다. 또한, 유량을 자유롭게 조절하여, 화학반응의 정도를 손쉽게 제어할 수 있다. As described above, the method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention can separate monomers and catalysts using a double nozzle system to apply various chemical reactions. In addition, the degree of chemical reaction can be easily controlled by freely adjusting the flow rate.
일 측면에 따르면, 기판 상에 초음파 분사하는 단계(220)는, 노즐 시스템으로 분리된 단량체 용액 및 촉매 용액이 초음파 노즐내에서 초음파에 의해 균일하게 (homogeneous) 혼합되는 단계 및 기판 상에 상기 혼합된 용액을 분사하는 단계를 포함하는 것일 수 있다. 이 때, 초음파 에너지원에 의해, 액상 매질에서 진공 기포의 폭발이(초음파 공동 현상, Cavitation) 일어나게 되며, 공동현상이 일어나는 순간 일시적으로 온도와 압력이 기하급수적으로 증가(약 5000 ℃ 및 1000 atm 수준으로 증가)하게 된다. 기하급수적으로 증가된 온도와 압력에 의해 단량체와 촉매가 활성화 상태가 되며, 이후 분무(Nebulization)되어 기판 상에서 공액 미소공성 고분자 필름이 중합된다.According to one aspect, the
보다 구체적으로, 도 4를 참조하면, 도 4는, 본 발명의 일 실시예에 따른, 본 발명에 의한 초음파 분사 화학반응에 의한 공액 미소공성 고분자 필름의 중합 메커니즘을 예시적으로 나타낸 것으로, 도 4 (a)는 초음파 분사 화학반응(Ultrasonic chemical reaction)의 초음파 에너지 공동 현상을 나타낸 것이고, 도 4 (b)는 기존의 열수 합성(Hydrothermal synthesis) 방법 및 본 발명의 일 실시예에 따른 초음파 분사 화학반응(Ultrasonic chemical reaction)을 통해 제조된 공액 미소공성 고분자의 차이를 나타낸 것이다.More specifically, referring to Figure 4, Figure 4, according to an embodiment of the present invention, illustratively shows the polymerization mechanism of the conjugated microporous polymer film by the ultrasonic injection chemical reaction according to the present invention, Figure 4 (a) shows the ultrasonic energy cavitation of the ultrasonic spraying chemical reaction (Ultrasonic chemical reaction), Figure 4 (b) is a conventional hydrothermal synthesis (Hydrothermal synthesis) method and ultrasonic spraying chemical reaction according to an embodiment of the present invention (Ultrasonic chemical reaction) shows the difference between the conjugated microporous polymer prepared.
도 4 (a)를 참조하면, 등방성 초음파의 고진동 정상파(Isostatic ultrasound)의 초음파 에너지원에 의해, 액상 매질에서 진공 기포의 폭발(초음파 공동 현상, Cavitation)이 일어나게 되며, 폭발(Cavitation)이 일어나는 순간 일시적으로 온도와 압력이 기하급수적으로 증가(예를 들어, 약 5000 °C, 1000 atm)하게 되어 양자역학적으로 높은 활성화 에너지를 생성하고, 이러한 순간적인 고온 고압에 의해 단량체 및 촉매는, 화학적으로 불안정한 활성화 상태가 된다. 활성화된 단량체는 기판 상에서 산화 커플링 반응(oxidative coupling reaction)을 일으켜 필름 형태로 제조된다. Referring to FIG. 4 (a), by the ultrasonic energy source of isostatic ultrasonic wave, the explosion of vacuum bubbles (ultrasonic cavitation, cavitation) occurs in the liquid medium, and the moment of explosion (cavitation) Temporarily, temperature and pressure increase exponentially (e.g., about 5000 °C, 1000 atm) to generate quantum mechanically high activation energy, and by this instantaneous high temperature and pressure, monomers and catalysts are chemically unstable. It becomes active. The activated monomer undergoes an oxidative coupling reaction on the substrate and is produced in the form of a film.
도 4 (b)를 참조하면, 초음파 분사 화학반응(Ultrasonic chemical reaction)을 통해 제조된 공액 미소공성 고분자 필름 형태로 제조되는 반면 기존의 열수 합성(Hydrothermal synthesis) 방법으로 제조된 공액 미소공성 고분자는 파우더 형태로 제조되는 것을 알 수 있다. 즉, 본 발명에 따른 초음파 스프레이 화학(Ultrasonic Spray Chemistry, USC) 기술을 이용하여 공액 미소공성 고분자 필름을 제조함으로써, 간단한 프로세스를 통해 단량체(monomer)에서 단일 공정(one-step)으로 얇은 박막 형태의 공액 미소공성 고분자 필름을 제조할 수 있다.Referring to FIG. 4(b), the conjugated microporous polymer prepared by a conventional hydrothermal synthesis method is powdered while being prepared in the form of a conjugated microporous polymer film produced through an ultrasonic injection chemical reaction. It can be seen that it is produced in the form. That is, by producing a conjugated microporous polymer film using the ultrasonic spray chemistry (Ultrasonic Spray Chemistry, USC) technology according to the present invention, a simple process in a thin film form in a single step (monomer) through a simple process A conjugated microporous polymer film can be prepared.
일 측면에 따르면, 상기 초음파 분사하는 단계에서 기판의 온도는, 100 ℃ 내지 200 ℃인 것일 수 있다. 바람직하게는, 145 ℃인 것일 수 있다. 상기 초음파 분사하는 단계에서 기판의 온도가 100 ℃ 미만일 경우, 반응성이 낮아 공액 미소공성 고분자 필름이 합성되지 않는 문제점이 발생할 수 있고, 상기 초음파 분사하는 단계에서 기판의 온도가 200 ℃를 초과할 경우 공액 미소공성 고분자 필름이 변질되는 문제점이 발생할 수 있다.According to one aspect, the temperature of the substrate in the ultrasonic injection step may be 100 ℃ to 200 ℃. Preferably, it may be 145 ℃. When the temperature of the substrate in the ultrasonic spraying step is less than 100°C, a problem may arise that the conjugated microporous polymer film is not synthesized due to low reactivity, and when the temperature of the substrate exceeds 200°C in the ultrasonic spraying step A problem that the microporous polymer film is deteriorated may occur.
일 측면에 따르면, 상기 기판은, 투명전극, 유리, 금속, 섬유 및 종이로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것일 수 있다. 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법에 따르면, 기판 (substrate)에 제한이 없어 투명전극, 유리, 금속은 물론 섬유나 종이 상에 공액 미소공성 고분자 필름을 제작할 수 있어 기존 연구에서 다루지 못했던 다양한 응용을 기대할 수 있다.According to an aspect, the substrate may include at least one selected from the group consisting of a transparent electrode, glass, metal, fiber, and paper. According to the method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention, there is no restriction on the substrate, and thus it is possible to manufacture a conjugated microporous polymer film on transparent electrodes, glass, metal, as well as fibers or paper. You can expect a variety of applications not covered in the study.
일 측면에 따르면, 상기 초음파 분사하는 단계는, 100 kHz 내지 200 kHz의 주파수를 가지는 초음파를 이용하는 것일 수 있다. 바람직하게는, 120 kHz 내지 180 kHz의 주파수를 가지는 초음파를 이용하는 것일 수 있다. 다만, 이에 한정되지 않으며, 사용하는 단량체 및 촉매의 종류에 따라 조절할 수 있다.According to one aspect, the ultrasonic injection step may be to use ultrasonic waves having a frequency of 100 kHz to 200 kHz. Preferably, it may be to use ultrasonic waves having a frequency of 120 kHz to 180 kHz. However, it is not limited thereto, and may be adjusted according to the type of monomer and catalyst used.
일 측면에 따르면, 상기 초음파 분사하는 단계는, 200 W 이상의 전력을 가지는 초음파를 이용하는 것일 수 있다. 다만, 이에 한정되지 않으며, 사용하는 단량체 및 촉매의 종류에 따라 조절할 수 있다.According to one aspect, the ultrasonic injection step may be to use ultrasonic waves having a power of 200 W or more. However, it is not limited thereto, and may be adjusted according to the type of monomer and catalyst used.
상기 초음파 주파수 범위 및 전력 범위 내에 포함되면, 과도한 초음파 에너지에 의한 용매 등의 변형을 방지할 수 있다.When included in the ultrasonic frequency range and power range, it is possible to prevent deformation of the solvent and the like due to excessive ultrasonic energy.
일 측면에 따르면, 상기 초음파 분사하는 단계에서 분사되는 상기 단량체 및 상기 촉매는, 분사 후 서로 반응하여 공액 미소공성 고분자 필름으로 합성되는 것일 수 있다. 초음파 에너지를 통해 활성화 상태가 된 촉매와 단량체는 수초, 예를 들어 10초 이내, 8초 이내 또는 5초 이내에 서로 반응하여 공액 미소공성 고분자 필름으로 합성된다. 즉, 본 발명에 따른 초음파 스프레이 화학(Ultrasonic Spray Chemistry, USC) 기술을 이용하여 공액 미소공성 고분자 필름을 제조함으로써, 단 시간에 공액 미소공성 고분자 필름 제조가 가능 할 뿐만 아니라 연속공정이 (Continuous) 가능하여 양산화가 가능하다.According to one aspect, the monomer and the catalyst injected in the ultrasonic injection step may be synthesized into a conjugated microporous polymer film by reacting with each other after injection. The catalyst and the monomer which have been activated through ultrasonic energy are synthesized into a conjugated microporous polymer film by reacting with each other within a few seconds, for example, within 10 seconds, within 8 seconds, or within 5 seconds. That is, by producing a conjugated microporous polymer film using the ultrasonic spray chemistry (Ultrasonic Spray Chemistry, USC) technology according to the present invention, it is possible to produce a conjugated microporous polymer film in a short time as well as a continuous process (Continuous) So mass production is possible.
본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름은, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법에 의해 제조되고, 1.5 ㎛이하의 두께를 가지는 것이다. 즉, 본 발명의 일 실시예에 따른 공액 미소공성 고분자 필름의 제조방법은, 초음파 분사 화학 기술(Ultrasonic spray chemistry)에 의한 용액 공정을 적용하여, 간단한 프로세스를 통해 단량체(monomer)에서 단일 공정(one-step)으로 얇은 박막 형태의 공액 미소공성 고분자 필름을 제조할 수 있다.The conjugated microporous polymer film according to an embodiment of the present invention is produced by a method for producing a conjugated microporous polymer film according to an embodiment of the present invention, and has a thickness of 1.5 μm or less. That is, the method of manufacturing a conjugated microporous polymer film according to an embodiment of the present invention, by applying a solution process by ultrasonic spray chemistry technology (Ultrasonic spray chemistry), a single process from a monomer (monomer) through a simple process (one -step) can produce a conjugated microporous polymer film in the form of a thin film.
이하, 실시예 및 비교예에 의하여 본 발명을 더욱 상세히 설명하고자 한다.Hereinafter, the present invention will be described in more detail by examples and comparative examples.
단, 하기 실시예는 본 발명을 예시하기 위한 것일 뿐, 본 발명의 내용이 하기 실시예에 한정되는 것은 아니다.However, the following examples are only for illustrating the present invention, and the contents of the present invention are not limited to the following examples.
실시예 1Example 1
하기 화학식 1로 표기되는 단량체를 포함하는 단량체 용액(0.5 mg/mL in Chloroform)을 준비하였다. FeCl3 촉매 용액(2.6 mg/mL in Ethanol)을 준비하였다. 상기 단량체 용액을 제1 노즐에 도입하고, 상기 촉매 용액을 제2 노즐에 도입하였다. 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하여 기판 상에서 공액 미소공성 고분자 필름을 합성하였다. 이 때, 초음파 주파수 (Frequency)는 180 kHz로 설정하였고, 초음파 파워(Power)는 240 W로 설정하였으며, 액상 유량 (Flow rate)은 0.2 mL/min로 설정하였고, 분사 이동속도 (Spray speed)는 20 mm/min로 설정하였으며, 분사 영역(Spacing area)은 10 mm2 로 설정하였고, 기판의 온도 (Substrate temperature)는 145 ℃로 설정하였다. (이하에서는 실시예 1을 통해 제조된 공액 미소공성 고분자 필름을 "CMP(화학식 1-180kHz)" 로 표기한다.)A monomer solution (0.5 mg/mL in Chloroform) containing a monomer represented by the following
[화학식 1][Formula 1]
실시예 2Example 2
하기 화학식 2로 표기되는 단량체를 포함하는 단량체 용액(0.5 mg/mL in Chloroform)을 준비하였다. FeCl3 촉매 용액(2.6 mg/mL in Ethanol)을 준비하였다. 상기 단량체 용액을 제1 노즐에 도입하고, 상기 촉매 용액을 제2 노즐에 도입하였다. 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하여 기판 상에서 공액 미소공성 고분자 필름을 합성하였다. 이 때, 초음파 주파수 (Frequency)는 120 kHz로 설정하였고, 초음파 파워(Power)는 240 W로 설정하였으며, 액상 유량 (Flow rate)은 0.2 mL/min로 설정하였고, 분사 이동속도 (Spray speed)는 20 mm/min로 설정하였으며, 분사 영역(Spacing area)은 10 mm2 로 설정하였고, 기판의 온도 (Substrate temperature)는 145 ℃로 설정하였다. (이하에서는 실시예 2를 통해 제조된 공액 미소공성 고분자 필름을 "CMP(화학식 2-120kHz)" 로 표기한다.)A monomer solution (0.5 mg/mL in Chloroform) containing a monomer represented by the following
[화학식 2] [Formula 2]
실시예 3Example 3
하기 화학식 3으로 표기되는 단량체를 포함하는 단량체 용액(0.5 mg/mL in Chloroform)을 준비하였다. FeCl3 촉매 용액(2.6 mg/mL in Ethanol)을 준비하였다. 상기 단량체 용액을 제1 노즐에 도입하고, 상기 촉매 용액을 제2 노즐에 도입하였다. 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하여 기판 상에서 공액 미소공성 고분자 필름을 합성하였다. 이 때, 초음파 주파수 (Frequency)는 120 kHz로 설정하였고, 초음파 파워(Power)는 240 W로 설정하였으며, 액상 유량 (Flow rate)은 0.2 mL/min로 설정하였고, 분사 이동속도 (Spray speed)는 20 mm/min로 설정하였으며, 분사 영역(Spacing area)은 10 mm2 로 설정하였고, 기판의 온도 (Substrate temperature)는 145 ℃로 설정하였다. (이하에서는 실시예 3을 통해 제조된 공액 미소공성 고분자 필름을 "CMP(화학식 3-120kHz)" 로 표기한다.)A monomer solution (0.5 mg/mL in Chloroform) containing a monomer represented by the following Chemical Formula 3 was prepared. FeCl 3 catalyst solution (2.6 mg/mL in Ethanol) was prepared. The monomer solution was introduced into the first nozzle, and the catalyst solution was introduced into the second nozzle. Conjugated microporous polymer films were synthesized on the substrate by ultrasonically spraying the monomer solution and the catalyst solution using the first nozzle and the second nozzle on the substrate. At this time, the ultrasonic frequency (Frequency) was set to 120 kHz, the ultrasonic power (Power) was set to 240 W, the liquid flow rate (Flow rate) was set to 0.2 mL / min, the spray moving speed (Spray speed) is It was set to 20 mm/min, the spraying area was set to 10 mm 2 , and the substrate temperature was set to 145°C. (Hereinafter, the conjugated microporous polymer film prepared through Example 3 is referred to as "CMP (Chemical Formula 3-120 kHz)".)
[화학식 3][Formula 3]
실시예 4Example 4
하기 화학식 3으로 표기되는 단량체를 포함하는 단량체 용액(0.5 mg/mL in Chloroform)을 준비하였다. FeCl3 촉매 용액(2.6 mg/mL in Ethanol)을 준비하였다. 상기 단량체 용액을 제1 노즐에 도입하고, 상기 촉매 용액을 제2 노즐에 도입하였다. 기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하여 기판 상에서 공액 미소공성 고분자 필름을 합성하였다. 이 때, 초음파 주파수 (Frequency)는 180 kHz로 설정하였고, 초음파 파워(Power)는 240 W로 설정하였으며, 액상 유량 (Flow rate)은 0.2 mL/min로 설정하였고, 분사 이동속도 (Spray speed)는 20 mm/min로 설정하였으며, 분사 영역(Spacing area)은 10 mm2 로 설정하였고, 기판의 온도 (Substrate temperature)는 145 ℃로 설정하였다. (이하에서는 실시예 4를 통해 제조된 공액 미소공성 고분자 필름을 "CMP(화학식 3-180kHz)" 로 표기한다.)A monomer solution (0.5 mg/mL in Chloroform) containing a monomer represented by the following Chemical Formula 3 was prepared. FeCl 3 catalyst solution (2.6 mg/mL in Ethanol) was prepared. The monomer solution was introduced into the first nozzle, and the catalyst solution was introduced into the second nozzle. Conjugated microporous polymer films were synthesized on the substrate by ultrasonically spraying the monomer solution and the catalyst solution using the first nozzle and the second nozzle on the substrate. At this time, the ultrasonic frequency (Frequency) was set to 180 kHz, the ultrasonic power (Power) was set to 240 W, the liquid flow rate (Flow rate) was set to 0.2 mL / min, the spray moving speed (Spray speed) is It was set to 20 mm/min, the spraying area was set to 10 mm 2 , and the substrate temperature was set to 145°C. (Hereinafter, the conjugated microporous polymer film prepared through Example 4 is referred to as "CMP (Chemical Formula 3-180 kHz)".)
[화학식 3][Formula 3]
비교예Comparative example
일반적으로 판매되는 공액 미소공성 고분자 필름을 준비하였다. (CMP-비교예)A conjugated microporous polymer film, which is generally sold, was prepared. (CMP-comparative example)
상기 실시예 1 내지 실시예 4를 통해 제조된 공액 미소공성 고분자 필름을 용매에 용해했을 때, 어떠한 용매에도 용해되지 않는 것을 확인할 수 있었다. 이는, 본 발명의 제조방법에 따라 제조된 공액 미소공성 고분자 필름이 고도로 가교된 결합 구조를 가지는 것을 의미한다.When the conjugated microporous polymer films prepared through Examples 1 to 4 were dissolved in a solvent, it was confirmed that they were not dissolved in any solvent. This means that the conjugated microporous polymer film prepared according to the production method of the present invention has a highly crosslinked bonding structure.
도 5a 내지 도 5c는 본 발명의 실시예 1 내지 실시예 4를 통해 제조된 공액 미소공성 고분자 필름 및 비교예의 FT-IR 그래프이다.5A to 5C are FT-IR graphs of conjugated microporous polymer films and comparative examples prepared through Examples 1 to 4 of the present invention.
더욱 자세하게 도 5a는 실시예 1을 통해 제조된 공액 미소공성 고분자 필름 및 비교예의 FT-IR 그래프이고, 도 5b는 실시예 2를 통해 제조된 공액 미소공성 고분자 필름 및 비교예의 FT-IR 그래프이며, 도 5c는 실시예 3 및 실시예 4를 통해 제조된 공액 미소공성 고분자 필름 및 비교예의 FT-IR 그래프이다.5A is a FT-IR graph of the conjugated microporous polymer film prepared through Example 1 and a comparative example, and FIG. 5B is a FT-IR graph of the conjugated microporous polymer film prepared through Example 2 and a comparative example, Figure 5c is a FT-IR graph of the conjugated microporous polymer film and Comparative Examples prepared through Examples 3 and 4.
도 5a 내지 도 5c를 참조하면, 본 발명의 실시예 1 내지 실시예 4를 통해 제조된 공액 미소공성 고분자 필름의 FT-IR 피크와 비교예의 FT-IR 피크를 비교하였을 때, 동일한 피크를 가지는 것을 알 수 있다.5A to 5C, when the FT-IR peaks of the conjugated microporous polymer films prepared through Examples 1 to 4 of the present invention were compared with the FT-IR peaks of the Comparative Example, those having the same peaks Able to know.
이는, 본 발명에 따른 초음파 스프레이 화학(Ultrasonic Spray Chemistry, USC) 기술을 이용하여 공액 미소공성 고분자 필름을 제조함으로써, 단 시간에 공액 미소공성 고분자 필름 제조가 가능 할 뿐만 아니라 연속공정이 (Continuous) 가능하여 양산화가 가능하다는 것을 의미한다.This, by producing a conjugated microporous polymer film using the ultrasonic spray chemistry (Ultrasonic Spray Chemistry, USC) technology according to the present invention, it is possible to produce a conjugated microporous polymer film in a short time as well as a continuous process (Continuous) possible This means that mass production is possible.
도 6은 본 발명의 실시예 4를 통해 제조된 공액 미소공성 고분자 필름의 SEM 이미지 및 TEM 이미지이다.6 is a SEM image and a TEM image of the conjugated microporous polymer film prepared through Example 4 of the present invention.
더욱 자세하게 도 6 (a)는 CMP(화학식 3-180kHz)의 단면을 촬영한 SEM 이미지이고, 도 6 (b)는 CMP(화학식 3-180kHz)의 표면을 촬영한 SEM 이미지이며, 도 6 (c)는 CMP(화학식 3-180kHz)의 TEM 이미지이다.More specifically, FIG. 6 (a) is a SEM image of a cross section of CMP (chemical formula 3-180 kHz), and FIG. 6 (b) is a SEM image of a surface of CMP (chemical formula 3-180 kHz), and FIG. 6 (c) ) Is a TEM image of CMP (Formula 3-180 kHz).
도 6 (a)를 참조하면, 기판 표면에 674 nm 두께의 CMP 박막이 형성된 것을 알 수 있다. Referring to Figure 6 (a), it can be seen that a CMP thin film having a thickness of 674 nm is formed on the substrate surface.
도 6 (b)를 참조하면, 본 발명의 실시예에 따라 제조된 공액 미소공성 고분자 필름은 필름 표면에 약간의 균열이 있으면서도 부드러운 필름 형태를 보여 주는 것을 알 수 있다. 이는 단량체의 용매가 기판 상에서 빠르게 증발되기 때문이며, CMP 막이 나노 스케일 구형 CMPs (~ 10 nm)로 구성되었음을 보여 주는 것이다. 이 결과는 초음파 에너지에 의해 활성화된 단량체가 기판 상에서 중합되는 것을 보여주는 것이다. 또한, 나노 크기의 CMPs로 구성된 프리 스탠딩 (free-standing) 막임을 의미한다.Referring to Figure 6 (b), it can be seen that the conjugated microporous polymer film prepared according to the embodiment of the present invention shows a smooth film shape even with slight cracks on the film surface. This is because the solvent of the monomer evaporates rapidly on the substrate, showing that the CMP film is composed of nanoscale spherical CMPs (~ 10 nm). This result shows that the monomer activated by ultrasonic energy is polymerized on the substrate. It also means that it is a free-standing film composed of nano-sized CMPs.
도 6 (c)를 참조하면, 본 발명의 실시예에 따라 제조된 공액 미소공성 고분자 필름은 1 nm 미만의 직경을 갖는 균일한 미소공성을 가지는 다공성 구조인 것을 알 수 있다.Referring to Figure 6 (c), it can be seen that the conjugated microporous polymer film prepared according to the embodiment of the present invention is a porous structure having a uniform micropore having a diameter of less than 1 nm.
상술한 바와 같이 본 발명의 공액 미소공성 고분자 필름의 제조방법은, 1) 초음파 스프레이 화학(Ultrasonic Spray Chemistry, USC) 기술을 이용하여 공액 미소공성 고분자 필름을 제조함으로써, 단 시간에 공액 미소공성 고분자 필름 제조가 가능 할 뿐만 아니라 연속공정이 (Continuous) 가능하여 양산화가 가능하며, 2) 더블 노즐 시스템으로 단량체와 촉매를 분리 할 수 있어 산화 커플링 반응(oxidative coupling reaction) 뿐만 아니라 축합 반응(condensation), 스즈키 커플링(suzuki coupling) 등 다양한 화학반응을 적용하여 미소공성 고분자 필름을 제조할 수 있고, 3) 기판 (substrate)에 제한이 없어 투명전극, 유리, 금속은 물론 섬유나 종이에 공액 미소공성 고분자 필름을 제작할 수 있어 기존 연구에서 다루지 못했던 다양한 분야에 응용할 수 있다.As described above, the method for producing a conjugated microporous polymer film of the present invention is: 1) by preparing a conjugated microporous polymer film using ultrasonic spray chemistry (Ultrasonic Spray Chemistry, USC) technology, the conjugated microporous polymer film in a short time Not only is it possible to manufacture, but also can be mass-produced by continuous process (2), and it is possible to separate monomers and catalysts with a double nozzle system, so it is possible to separate not only oxidative coupling reactions, but also condensation reactions. Microporous polymer films can be manufactured by applying various chemical reactions such as Suzuki coupling, and 3) There are no restrictions on the substrate, so it is not only transparent electrodes, glass, metal, but also conjugated microporous polymer on fibers or paper. The film can be produced, and can be applied to various fields not covered in the previous research.
이상과 같이 실시예들이 비록 한정된 실시예와 도면에 의해 설명되었으나, 해당 기술분야에서 통상의 지식을 가진 자라면 상기의 기재로부터 다양한 수정 및 변형이 가능하다. 예를 들어, 설명된 기술들이 설명된 방법과 다른 순서로 수행되거나, 및/또는 설명된 구성요소들이 설명된 방법과 다른 형태로 결합 또는 조합되거나, 다른 구성요소 또는 균등물에 의하여 대치되거나 치환되더라도 적절한 결과가 달성될 수 있다. 그러므로, 다른 구현들, 다른 실시예들 및 특허청구범위와 균등한 것들도 후술하는 특허청구범위의 범위에 속한다.As described above, although the embodiments have been described by a limited embodiment and drawings, those skilled in the art can make various modifications and variations from the above description. For example, even if the described techniques are performed in a different order than the described method, and/or the described components are combined or combined in a different form from the described method, or replaced or replaced by another component or equivalent Appropriate results can be achieved. Therefore, other implementations, other embodiments, and equivalents to the claims are also within the scope of the following claims.
Claims (11)
촉매 용액을 준비하는 단계;
상기 단량체 용액을 제1 노즐에 도입하는 단계;
상기 촉매 용액을 제2 노즐에 도입하는 단계; 및
기판 상에 상기 제1 노즐 및 제2 노즐을 이용하여 상기 단량체 용액 및 상기 촉매 용액을 동시에 초음파 분사하는 단계;
를 포함하는,
공액 미소공성 고분자 필름의 제조방법.
Preparing a monomer solution containing monomers of conjugated microporous polymers;
Preparing a catalyst solution;
Introducing the monomer solution into a first nozzle;
Introducing the catalyst solution into a second nozzle; And
Ultrasonically spraying the monomer solution and the catalyst solution simultaneously on the substrate using the first nozzle and the second nozzle;
Containing,
Method for producing conjugated microporous polymer film.
상기 공액 미소공성 고분자의 단량체는, 하기 화학식 1 내지 3, 트라이페닐아민 (triphenylamine), 카바졸 (9H-carbazole) 및 이들의 유도체로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것인,
공액 미소공성 고분자 필름의 제조방법:
[화학식 1]
[화학식 2]
[화학식 3]
According to claim 1,
The conjugated microporous polymer monomer includes at least one selected from the group consisting of the following Chemical Formulas 1 to 3, triphenylamine, carbazole (9 H- carbazole), and derivatives thereof.
Manufacturing method of conjugated microporous polymer film:
[Formula 1]
[Formula 2]
[Formula 3]
상기 촉매는, FeCl3을 포함하는 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The catalyst is to include FeCl 3 ,
Method for producing conjugated microporous polymer film.
상기 단량체 용액의 농도는, 0.4 mg/ml 내지 1.0 mg/ml인 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The concentration of the monomer solution is 0.4 mg/ml to 1.0 mg/ml,
Method for producing conjugated microporous polymer film.
상기 촉매 용액의 농도는, 2.0 mg/ml 내지 3.0 mg/ml인 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The concentration of the catalyst solution is 2.0 mg/ml to 3.0 mg/ml,
Method for producing conjugated microporous polymer film.
상기 초음파 분사하는 단계에서 기판의 온도는, 100 ℃ 내지 200 ℃인 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
In the ultrasonic injection step, the temperature of the substrate is 100 °C to 200 °C,
Method for producing conjugated microporous polymer film.
상기 기판은, 투명전극, 유리, 금속, 섬유 및 종이로 이루어진 군으로부터 선택된 적어도 하나를 포함하는 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The substrate is to include at least one selected from the group consisting of transparent electrodes, glass, metal, fiber and paper,
Method for producing conjugated microporous polymer film.
상기 초음파 분사하는 단계는, 100 kHz 내지 200 kHz의 주파수를 가지는 초음파를 이용하는 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The ultrasonic injection step is to use ultrasonic waves having a frequency of 100 kHz to 200 kHz,
Method for producing conjugated microporous polymer film.
상기 초음파 분사하는 단계는, 200 W 이상의 전력을 가지는 초음파를 이용하는 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The ultrasonic injection step is to use ultrasonic waves having a power of 200 W or more,
Method for producing conjugated microporous polymer film.
상기 초음파 분사하는 단계에서 분사되는 상기 단량체 및 상기 촉매는, 분사 후 서로 반응하여 공액 미소공성 고분자 필름으로 합성되는 것인,
공액 미소공성 고분자 필름의 제조방법.
According to claim 1,
The monomer and the catalyst sprayed in the ultrasonic spraying step are reacted with each other after spraying to be synthesized into a conjugated microporous polymer film,
Method for producing conjugated microporous polymer film.
1.5 ㎛ 이하의 두께를 가지는 것인,
공액 미소공성 고분자 필름
It is produced by a method for producing a conjugated microporous polymer film according to any one of claims 1 to 10,
It has a thickness of 1.5 μm or less,
Conjugated microporous polymer film