KR102098506B1 - Method for setting roll-gap of roll leveler - Google Patents
Method for setting roll-gap of roll leveler Download PDFInfo
- Publication number
- KR102098506B1 KR102098506B1 KR1020180153091A KR20180153091A KR102098506B1 KR 102098506 B1 KR102098506 B1 KR 102098506B1 KR 1020180153091 A KR1020180153091 A KR 1020180153091A KR 20180153091 A KR20180153091 A KR 20180153091A KR 102098506 B1 KR102098506 B1 KR 102098506B1
- Authority
- KR
- South Korea
- Prior art keywords
- roll
- test plate
- roll gap
- target
- gap
- Prior art date
Abstract
Description
본 발명은 롤 교정기의 롤갭 이상 여부를 확인하고 설정하는 롤 교정기의 롤갭 설정방법에 관한 것이다. The present invention relates to a roll gap setting method of a roll straightener to check and set whether the roll straightener is abnormal.
판의 교정 공정에서 주로 사용되는 롤 교정기는 복수의 롤이 상하 지그재그로 배치되고, 상하 롤들 사이의 간격을 판의 두께보다 작게 설정하여 그 사이로 판을 이송시키면서 판에 상하 굽힘이 차례로 일어나게 한다. 이로써, 판의 형상을 평탄화하고 내부의 잔류응력을 줄일 수 있게 된다.The roll straightener mainly used in the straightening process of the plate is a plurality of rolls are arranged in a zigzag up and down, and the gap between the top and bottom rolls is set to be smaller than the thickness of the plate to cause the plate to be vertically bent while transferring the plate therebetween. This makes it possible to flatten the shape of the plate and reduce the residual stress inside.
이때, 정확한 형상 교정을 위해서는 교정 모델의 원하는 목표값이 롤 교정기의 롤갭에 동일하게 설정되는 것이 필요하다. 롤갭 설정이 목표값과 대비해서 상이한 경우에는 교정 후 형상이 다르게 되어 판의 형상 품질에 불량이 초래된다. At this time, for correct shape correction, it is necessary that the desired target value of the calibration model is set equal to the roll gap of the roll calibrator. If the roll gap setting is different from the target value, the shape is different after calibration, resulting in defects in the shape quality of the plate.
종래의 롤갭을 설정하는 방법으로는, 시험용 판의 표면에 미세하게 홈을 가공하고 스트레인 게이지를 부착한 후, 롤 교정기를 통과시켜 스트레인 게이지로 측정된 값으로 균일하게 눌러졌는지 확인하는 방법이 있다. 하지만, 이러한 방법은 시험용 판에 홈을 정밀하게 가공해야 하고 다양한 조건으로 교정이 이루어지면 스트레인 게이지가 판에서 탈락되어 측정이 불가능한 경우가 많기 때문에 시간이 과도하게 소요되는 단점이 있다. As a method of setting a conventional roll gap, there is a method of confirming that the groove is finely processed on the surface of the test plate and attached to the strain gauge, and then passed through the roll calibrator to uniformly press the measured value with the strain gauge. However, this method has a disadvantage in that the grooves must be precisely machined on the test plate, and if the calibration is performed under various conditions, the strain gauge may fall off the plate and measurement is often impossible.
다른 방법으로는, 레이저 센서를 이용하여 거리를 측정하는 방법이 있으나, 롤에 하중이 걸리지 않은 상태에서 롤갭을 측정하는 것이어서, 하중이 걸렸을 때의 롤갭을 반영할 수 없는 단점이 있다. As another method, there is a method of measuring a distance using a laser sensor, but it is a measure of the roll gap in a state in which no load is applied to the roll, and thus there is a disadvantage that the roll gap when a load is applied cannot be reflected.
또 다른 방법으로는, 두께가 약 100mm 이상인 1개 내지 2개의 게이지 플레이트를 롤 교정기로 균일하게 가압한 후, 롤 교정기의 유압장치에 설치된 로드셀에 일정한 하중이 균일하게 걸리도록 조정하여 롤갭을 설정하고 있다. 이 방법은 각 롤에 걸리는 하중을 고려하는 것이 아니어서, 개별 롤갭의 상태를 확인하는 것은 불가능하다. As another method, after uniformly pressing one or two gauge plates having a thickness of about 100 mm or more with a roll calibrator, the roll gap is set by adjusting a load uniformly on the load cell installed in the hydraulic device of the roll calibrator to set the roll gap. have. This method does not take into account the load applied to each roll, so it is impossible to check the state of the individual roll gaps.
(특허문헌 1) KR 1127125 B (Patent Document 1) KR 1127125 B
(특허문헌 2) JP 2005-262233 A (Patent Document 2) JP 2005-262233 A
이에 본 발명은 롤 교정기에서 판의 균일 압하가 가능하도록, 롤 교정기의 롤갭 이상 여부를 확인하고 목표값으로 설정할 수 있는 롤 교정기의 롤갭 설정방법을 제공하는 데에 그 목적이 있다. Accordingly, an object of the present invention is to provide a method for setting a roll gap of a roll calibrator capable of checking whether or not the roll gap of the roll calibrator is abnormal and setting a target value so that the plate can be uniformly pressed in the roll calibrator.
본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법은, 소정 길이의 시험용 판을 준비하는 단계; 롤 교정기로 상기 시험용 판을 압하하여, 상기 시험용 판에 압흔을 형성하는 단계; 및 상기 압흔의 파고로부터 산출된 실제 롤갭과 미리 결정된 목표 롤갭을 비교하여, 롤갭의 이상 여부를 판단하는 단계; 및 상기 시험용 판에 형성된 압흔의 폭방향 평탄도를 측정하는 단계를 포함하는 것을 특징으로 한다. Method for setting a roll gap of a roll straightener according to an embodiment of the present invention includes: preparing a test plate having a predetermined length; Pressing the test plate with a roll straightener to form indentations in the test plate; And comparing the actual roll gap calculated from the wave height of the indentation with a predetermined target roll gap, and determining whether the roll gap is abnormal; And measuring a flatness in the width direction of the indentation formed on the test plate.
이상과 같이 본 발명에 의하면, 시험용 판에 실제 하중을 가하여 변형시킨 후 그 변형된 압흔을 이용하기 때문에, 빠른 시간에 적은 비용으로 롤 교정기의 롤갭 이상 여부를 정확히 확인할 수 있게 됨으로써 롤 교정기의 성능을 향상시킬 수 있음과 더불어, 교정 효과를 극대화시키고 판의 형상 품질을 높일 수 효과를 얻게 된다. According to the present invention as described above, since the deformed indentation is used after deforming by applying an actual load to the test plate, it is possible to accurately check whether or not the roll gap of the roll calibrator is correct at a low cost in a short time. In addition to being improved, it is possible to maximize the correction effect and increase the shape quality of the plate.
도 1은 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법 중 롤 교정기로 시험용 판을 압하하여 압흔을 형성하는 단계를 도시한 도면들이다.
도 2는 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법을 설명하기 위해 롤갭과 피치 및 직경을 나타낸 개략도이다.1 is a view showing a step of forming an indentation by pressing the test plate with a roll straightener in the roll gap setting method of the roll straightener according to an embodiment of the present invention.
Figure 2 is a schematic diagram showing the roll gap and pitch and diameter to explain the roll gap setting method of the roll corrector according to an embodiment of the present invention.
이하, 본 발명이 예시적인 도면을 통해 상세하게 설명된다. 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다.Hereinafter, the present invention will be described in detail through exemplary drawings. It should be noted that in adding reference numerals to the components of each drawing, the same components have the same reference numerals as possible even though they are displayed on different drawings. In addition, in describing the present invention, when it is determined that detailed descriptions of related well-known configurations or functions may obscure the subject matter of the present invention, detailed descriptions thereof will be omitted.
도 1은 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법 중 롤 교정기로 시험용 판을 압하하여 압흔을 형성하는 단계를 도시한 도면들이다.1 is a view showing a step of forming an indentation by pressing the test plate with a roll straightener in the roll gap setting method of the roll straightener according to an embodiment of the present invention.
이에 도시된 바와 같이, 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법은, 소정 길이의 시험용 판(1)을 준비하는 단계; 롤 교정기로 시험용 판을 압하하여, 시험용 판에 압흔을 형성하는 단계; 및 압흔의 파고로부터 산출된 실제 롤갭과 미리 결정된 목표 롤갭을 비교하여, 롤갭의 이상 여부를 판단하는 단계를 포함하고 있다. As shown in this, the roll gap setting method of the roll calibrator according to an embodiment of the present invention comprises: preparing a test plate 1 of a predetermined length; Pressing the test plate with a roll straightener to form indentations in the test plate; And comparing the actual roll gap calculated from the wave height of the indentation with a predetermined target roll gap, and determining whether the roll gap is abnormal.
본 발명에서는 빠른 시간에 적은 비용으로 롤 교정기의 롤갭 이상 여부를 정확히 확인하기 위해, 복수의 롤(2)을 포함한 롤 교정기로 시험용 판(1)을 그 두께방향으로 일정한 힘을 가하여 압하한다. In the present invention, in order to accurately check whether the roll calibrator has an abnormality at a low cost at a short time, the test plate 1 is pressed by applying a constant force in its thickness direction with a roll calibrator including a plurality of
롤 교정기에 의해 시험용 판(1)의 길이방향 및 폭방향으로 균일 압하가 이루어지고 있는지를 평가하기 위해, 시험용 판을 압하한 후 롤 교정기의 상부측 롤(2a)을 들어올려, 압하로 인해 시험용 판에 생성된 압흔의 형상을 측정하고, 이로부터 롤 교정기의 롤갭 상태를 파악할 수 있다. In order to evaluate whether uniform reduction is performed in the longitudinal direction and the width direction of the test plate 1 by the roll calibrator, after the test plate is pressed, the
먼저, 시험용 판(1)에 형성된 압흔의 균일한 폭방향 변형량은 평탄도계 등을 사용하여 측정되는 평탄도에 의해 확인될 수 있다. First, the uniform width direction deformation amount of the indentation formed in the test plate 1 can be confirmed by the flatness measured using a flatness meter or the like.
시험용 판(1)의 폭방향으로 형성된 파형상의 변형이 측정되고, 파형상 중 산의 높이가 일정한 값을 가지면 정상상태인 것으로 판단한다. 만일 파형상의 산의 높이가 허용범위를 벗어난 분포를 가지면 이상상태인 것으로 판단하고, 이후에 해당 롤(2)의 휨 또는 크라운을 조정할 수 있다. It is determined that the deformation of the wave shape formed in the width direction of the test plate 1 is measured, and if the height of the acid in the wave shape has a constant value, it is determined to be normal. If the height of the mountain in the wave shape has a distribution outside the allowable range, it is determined that it is in an abnormal state, and then the warpage or crown of the
이와 같이 해서, 롤 교정기로 교정될 판의 폭방향 형상 교정 조건이 실제와 일치되게 설정될 수 있게 된다. In this way, the condition for correcting the width shape of the plate to be corrected by the roll straightener can be set to match the actual condition.
한편, 이러한 시험에서는 시험용 판(1)의 치수에 따라 압하의 영향이 상이하게 나타날 수 있으며, 이러한 경우에는 마치 롤갭 설정이 잘못된 것으로 오인될 우려가 있다. On the other hand, in such a test, the influence of the reduction may appear differently depending on the dimensions of the test plate 1, and in such a case, there is a possibility that the roll gap setting is wrong.
예를 들어, 시험용 판(1)의 길이가 길어지면 그 자중에 의한 눌림이 발생하고, 이에 따라 시험용 판이 롤(2)에 밀착되는 쪽으로 변형이 더 가해지게 되어 압하의 잔류 변형이 크게 남게 된다. 또한, 압하량이 적게 됨으로써 소성 변형량이 적게 되면, 평탄도계 등이 그 변형량을 측정하지 못하는 경우가 발생한다.For example, when the length of the test plate 1 becomes longer, pressing due to its own weight occurs, and accordingly, deformation is further applied toward the test plate in close contact with the
이에 따라, 롤 교정기의 사양에 따라 적절한 치수를 가진 시험용 판을 준비하는 것이 중요하다. Accordingly, it is important to prepare a test plate with appropriate dimensions according to the specifications of the roll straightener.
도 2는 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법을 설명하기 위해 롤갭과 피치 및 직경을 나타낸 개략도이다.Figure 2 is a schematic diagram showing the roll gap and pitch and diameter to explain the roll gap setting method of the roll corrector according to an embodiment of the present invention.
본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법에서는, 시험용 판(1)을 준비할 때, 이 시험용 판이 아래의 수학식 1로 정의된 범위의 길이를 갖는 것이 바람직하다. In the roll gap setting method of the roll calibrator according to an embodiment of the present invention, when preparing the test plate 1, it is preferable that the test plate has a length defined in the following equation (1).
[수학식 1][Equation 1]
N × P 〈 L 〈 (N × P) + 100(mm)N × P 〈L 〈(N × P) + 100 (mm)
여기서, N은 롤의 개수로서, 롤 교정기의 상부측 롤(2a)과 하부측 롤(2b) 중 보다 많은 쪽 롤의 개수이다. P는 피치로서, 많은 쪽의 인접한 롤(2)들에서 어느 한쪽 롤의 중심과 다른 한쪽 롤의 중심 간 거리(mm)이다. L은 시험용 판(1)의 길이(mm)이다. Here, N is the number of rolls, which is the number of more rolls among the
이와 같이 정의된 적정한 길이를 가진 시험용 판(1)을 롤 교정기로 압하하고, 압하로 인해 생성된 시험용 판의 압흔에서 길이방향으로 형성된 파형상의 변형을 측정하여, 알맞은 롤갭 또는 압하량을 산출할 수 있다. The test plate (1) having an appropriate length defined as described above is pressed with a roll calibrator, and the deformation of the wave shape formed in the longitudinal direction from the indentation of the test plate generated by the pressing can be measured to calculate an appropriate roll gap or amount of reduction. have.
이를 위해, 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법에서는, 시험용 판(1)의 길이방향으로 형성된 압흔의 파형상 중 높이가 가장 낮은 산과 깊이가 가장 얕은 골 사이의 높이차를 파고라 정의한다. To this end, in the roll gap setting method of the roll corrector according to an embodiment of the present invention, the height difference between the lowest height and the shallowest bone among the waveforms of indentations formed in the longitudinal direction of the test plate 1 define.
또한, 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법에서는 이러한 파고로부터 시험용 판(1)의 소성율을 산출할 수 있다. In addition, in the roll gap setting method of the roll calibrator according to an embodiment of the present invention, the firing rate of the test plate 1 can be calculated from such a wave height.
롤 교정기의 롤(1)의 압하로 인해 생성된 시험용 판(1)의 압흔에서 소성 변형으로 발생한 파형상의 파고와, 롤의 직경, 롤 간 피치, 시험용 판의 항복강도, 시험용 판의 두께, 및 소성율의 관계는 아래의 수학식 2와 같다. Waveform wave height caused by plastic deformation in the indentation of the test plate 1 generated by the reduction of the roll 1 of the roll calibrator, diameter of the roll, pitch between rolls, yield strength of the test plate, thickness of the test plate, and The relationship between the firing rates is as shown in
[수학식 2][Equation 2]
H = - 18.8 - 0.0022D + 0.026P + 0.00518Y - 0.195t + 0.215SH =-18.8-0.0022D + 0.026P + 0.00518Y-0.195t + 0.215S
여기서, H는 시험용 판(1)의 압흔에 형성된 파형상 중 전술한 정의의 파고(mm)이고, D는 롤 교정기의 롤의 직경(mm)이며, P는 전술한 정의의 피치(mm)이고, Y는 시험용 판이 갖는 항복강도(MPa)이며, t는 시험용 판의 두께(mm)이고, S는 시험용 판의 소성율(%)이다. Here, H is the wave height (mm) of the above definition among the waveforms formed on the indentation of the test plate (1), D is the diameter (mm) of the roll of the roll straightener, P is the pitch (mm) of the above definition , Y is the yield strength (MPa) of the test plate, t is the thickness of the test plate (mm), and S is the plasticity rate (%) of the test plate.
이러한 회귀식으로부터 소성율이 산출되면, 소성율과 압하량 사이의 관계식을 이용하여 압하량을 구한다. 압하량을 산출하는 관계식은 아래의 수학식 3과 같다.When the plasticity ratio is calculated from the regression equation, the amount of rolling reduction is determined using the relationship between the plasticity ratio and the rolling reduction amount. The relational expression for calculating the rolling reduction is as shown in Equation 3 below.
[수학식 3][Equation 3]
여기서, δ는 시험용 판(1)의 압하량(mm)이며, P는 전술한 정의의 피치(mm)이고, Y는 시험용 판이 갖는 항복강도(MPa)이며, E는 영의 계수(Young's modulus) 또는 탄성계수(MPa)이고, t는 시험용 판의 두께(mm)이며, S는 시험용 판의 소성율(%)이다. Here, δ is the rolling amount (mm) of the test plate (1), P is the pitch (mm) of the above-described definition, Y is the yield strength (MPa) of the test plate, E is Young's modulus (Young's modulus) Or, it is the modulus of elasticity (MPa), t is the thickness of the test plate (mm), and S is the plasticity rate (%) of the test plate.
압하량이 산출되면, 압하량과 롤갭 사이의 관계식을 이용하여 롤갭을 구할 수 있다. 롤갭을 산출하는 관계식은 아래의 수학식 4와 같다.When the rolling reduction amount is calculated, the roll gap can be obtained by using the relationship between the rolling reduction amount and the roll gap. The relational expression for calculating the roll gap is as shown in Equation 4 below.
[수학식 4][Equation 4]
G = t - δG = t-δ
여기서, G는 롤 교정기의 상부측 롤(2a)과 하부측 롤(2b) 사이의 롤갭이고, t는 시험용 판(1)의 두께(mm)이며, δ는 시험용 판의 압하량(mm)이다. Here, G is a roll gap between the
예컨대 압하량이 0(zero)이면, 롤갭은 시험용 판(1)의 두께와 같거나 두께 이상으로 될 수 있다.For example, if the reduction amount is 0 (zero), the roll gap may be equal to or greater than the thickness of the test plate 1.
이와 같이, 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법에서는, 시험용 판(1)을 롤 교정기에 의해 실제로 압하하고, 압하로 인해 생성된 시험용 판의 압흔이 갖는 파형상의 파고로부터 회귀식인 수학식 2를 이용하여 시험용 판의 실제 소성율을 얻을 수 있다. As described above, in the roll gap setting method of the roll calibrator according to an embodiment of the present invention, the test plate 1 is actually pressed by the roll calibrator, and the regression equation is obtained from the wave height of the indentation of the test plate generated by the pressing.
또한, 실제 소성율로부터, 소성율과 압하량 사이의 관계식인 수학식 3을 이용하여 압하량을 구하고 나서, 압하량과 롤갭 사이의 관계식인 수학식 4를 이용하여 롤 교정기의 실제 롤갭을 구할 수 있다. In addition, the actual rolling gap of the roll corrector can be obtained from the actual firing rate using the equation 3 which is the relationship between the firing rate and the rolling amount, and then using the equation 4 which is the relationship between the rolling amount and the roll gap. have.
롤갭의 이상 여부를 판단하기 위해서는, 실제 롤갭에 대한 비교 대상이 필요한데, 이를 위해 목표 롤갭을 미리 결정할 수 있으며, 본 발명의 일 실시예에 따른 롤 교정기의 롤갭 설정방법에서는 목표 롤갭을 결정하기 위해 목표 파고가 주어질 수 있다. In order to determine whether the roll gap is abnormal, a comparison target with respect to the actual roll gap is required. To this end, the target roll gap can be determined in advance, and in the roll gap setting method of the roll calibrator according to an embodiment of the present invention, the target roll gap Digging can be given.
목표 파고는, 시험용 판(1)의 재질이 갖는 기계적 물성(예컨대 항복강도나 탄성계수 등)이나 치수(예컨대 두께나 길이 등), 혹은 롤 교정기의 사양(예컨대 롤의 직경이나 롤 간 피치 등)에 따라 변경될 수 있지만, 예를 들어 대략 3mm 이상의 값으로 결정되는 것이 좋다. The target wave height is the mechanical properties (e.g., yield strength and elastic modulus, etc.) or dimensions (e.g., thickness or length, etc.) of the material of the test plate (1), or specifications of the roll calibrator (e.g., roll diameter or pitch between rolls) It can be changed according to, but it is preferable to determine the value, for example, approximately 3 mm or more.
이 값은 일종의 경험치로서, 목표 파고가 대략 3mm 이상의 값을 가질 때에 통상적으로 압흔에서의 변형이 뚜렷하게 나타나면서 적어도 임의의 노이즈와 혼동되지 않아 그 변형량을 측정할 수 있는 수준의 압흔이 형성된다. This value is a kind of empirical value, and when the target wave height has a value of approximately 3 mm or more, the deformation in the indentation is usually apparent, and at least not confused with any noise, the indentation is formed at a level capable of measuring the amount of deformation.
목표 파고가 주어지면, 파고와, 롤(2)의 직경, 롤 간 피치, 시험용 판(1)의 항복강도, 시험용 판의 두께, 및 소성율의 관계를 나타내는 수학식 2를 이용하여 시험용 판이 이론적으로 가져야 하는 목표 소성율을 얻을 수 있다. Given the target crest, the test plate is theoretical using
또한, 목표 소성율로부터, 소성율과 압하량 사이의 관계식인 수학식 3을 이용하여 압하량을 구하고 나서, 압하량과 롤갭 사이의 관계식인 수학식 4를 이용하여 롤 교정기의 이상적인 목표 롤갭을 구할 수 있다. In addition, from the target firing rate, the rolling reduction amount is obtained using Equation 3, which is a relationship between the firing rate and the rolling amount, and then, using Equation 4, which is a relationship between the rolling reduction amount and the roll gap, an ideal target roll gap of the roll corrector is obtained. You can.
다음으로, 압흔의 파고로부터 산출된 실제 소성율과 이에 따른 압하량을 통해 얻은 실제 롤갭과, 주어진 목표 파고로부터 산출된 목표 소성율과 이에 따른 압하량을 통해 결정된 목표 롤갭을 비교하여, 롤갭의 이상 여부를 판단한다.Next, the actual roll rate calculated from the wave height of the indentation and the actual roll gap obtained through the reduction amount, and the target roll rate calculated from the given target wave height and the target roll gap determined through the amount of rolling reduction, are compared to determine the abnormality of the roll gap. Judge whether or not.
실제 롤갭이 목표 롤갭의 허용범위, 예를 들면 목표 롤갭의 ±10% 내에 있으면, 정상상태인 것으로 판단한다. 만일, 실제 롤갭이 목표 롤갭의 허용범위를 벗어나면 이상상태인 것으로 판단하고, 이후에 롤 교정기의 롤갭을 목표 롤갭 또는 그 허용범위 내로 조정할 수 있다.If the actual roll gap is within the allowable range of the target roll gap, for example, ± 10% of the target roll gap, it is determined as normal. If the actual roll gap is outside the allowable range of the target roll gap, it is determined that it is in an abnormal state, and then the roll gap of the roll calibrator can be adjusted within the target roll gap or its allowable range.
이와 같이 해서, 롤 교정기로 교정될 판의 길이방향 형상 교정 조건이 실제와 일치되게 설정될 수 있게 되는 것이다. In this way, the condition for correcting the longitudinal shape of the plate to be corrected by the roll straightener can be set to match the actual condition.
본 발명의 다른 실시예에 따른 롤 교정기의 롤갭 설정방법에서는 목표 롤갭을 결정하기 위해 목표 소성율이 주어질 수 있다. In the roll gap setting method of the roll straightener according to another embodiment of the present invention, a target sintering rate may be given to determine a target roll gap.
소성율은 아래의 수학식 5와 같이 정의될 수 있다. The firing rate may be defined as in Equation 5 below.
[수학식 5][Equation 5]
S = (ts / t) × 100S = (t s / t) × 100
여기서, S는 시험용 판(1)의 소성율(%)이고, ts는 시험용 판에서 소성 변형이 발생한 두께(mm)이며, t는 시험용 판의 두께(mm)이다.Here, S is the plasticity rate (%) of the test plate 1, t s is the thickness (mm) of plastic deformation in the test plate, and t is the thickness of the test plate (mm).
이러한 소성율은 예를 들어 75% 이상의 값으로 결정되는 것이 좋다. It is preferable that the sintering rate is determined to be at least 75%, for example.
목표 소성율이 주어지면, 소성율과 압하량 사이의 관계식인 수학식 3을 이용하여 압하량을 구하고 나서, 압하량과 롤갭 사이의 관계식인 수학식 4를 이용하여 롤 교정기의 목표 롤갭을 구할 수 있다. When the target sintering rate is given, the rolling reduction amount is obtained by using Equation 3, which is a relationship between the sintering rate and the rolling amount, and then the target roll gap of the roll corrector can be obtained by using Equation 4, which is a relationship between the rolling reduction amount and the roll gap. have.
전술한 일 실시예와 마찬가지로, 압흔의 파고로부터 산출된 실제 소성율과 이에 따른 압하량을 통해 얻은 실제 롤갭과, 주어진 목표 파고로부터 산출된 목표 소성율과 이에 따른 압하량을 통해 결정된 목표 롤갭을 비교하여, 롤갭의 이상 여부를 판단한다.Similar to the above-described embodiment, the actual plasticity ratio calculated from the crest of the indentation and the actual roll gap obtained through the reduction amount, and the target plasticity ratio calculated from the given target crest and the target roll gap determined through the reduction amount accordingly Then, it is determined whether the roll gap is abnormal.
실제 롤갭이 목표 롤갭의 허용범위, 예를 들면 목표 롤갭의 ±10% 내에 있으면, 정상상태인 것으로 판단한다. 만일, 실제 롤갭이 목표 롤갭의 허용범위를 벗어나면 이상상태인 것으로 판단하고, 이후에 롤 교정기의 롤갭을 목표 롤갭 또는 그 허용범위 내로 조정할 수 있다.If the actual roll gap is within the allowable range of the target roll gap, for example, ± 10% of the target roll gap, it is determined as normal. If the actual roll gap is outside the allowable range of the target roll gap, it is determined that it is in an abnormal state, and then the roll gap of the roll calibrator can be adjusted within the target roll gap or its allowable range.
이와 같이 해서, 롤 교정기로 교정될 판의 길이방향 형상 교정 조건이 실제와 일치되게 설정될 수 있게 되는 것이다. In this way, the condition for correcting the longitudinal shape of the plate to be corrected by the roll straightener can be set to match the actual condition.
이상과 같이 본 발명에 의하면, 시험용 판에 실제 하중을 가하여 변형시킨 후 그 변형된 압흔을 이용하기 때문에, 빠른 시간에 적은 비용으로 롤 교정기의 롤갭 이상 여부를 정확히 확인할 수 있게 됨으로써 롤 교정기의 성능을 향상시킬 수 있음과 더불어, 교정 효과를 극대화시키고 판의 형상 품질을 높일 수 효과를 얻게 된다. According to the present invention as described above, since the deformed indentation is used after deforming by applying an actual load to the test plate, it is possible to accurately check whether or not the roll gap of the roll calibrator is correct at a low cost in a short time. In addition to being improved, it is possible to maximize the correction effect and increase the shape quality of the plate.
이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 명세서 및 도면에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may make various modifications and variations without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present specification and drawings are not intended to limit the technical spirit of the present invention, but to describe the present invention, and the scope of the technical spirit of the present invention is not limited by these embodiments. The scope of protection of the present invention should be interpreted by the claims below, and all technical spirits within the scope equivalent thereto should be interpreted as being included in the scope of the present invention.
1: 시험용 판
2: 롤1: Test plate
2: Roll
Claims (12)
롤 교정기로 상기 시험용 판을 압하하여, 상기 시험용 판에 압흔을 형성하는 단계; 및
상기 압흔의 파고로부터 산출된 실제 롤갭과 미리 결정된 목표 롤갭을 비교하여, 롤갭의 이상 여부를 판단하는 단계; 및
상기 시험용 판에 형성된 압흔의 폭방향 평탄도를 측정하는 단계
를 포함하는 롤 교정기의 롤갭 설정방법.
Preparing a test plate of a predetermined length;
Pressing the test plate with a roll straightener to form indentations in the test plate; And
Comparing the actual roll gap calculated from the wave height of the indentation with a predetermined target roll gap, and determining whether the roll gap is abnormal; And
Measuring the flatness in the width direction of the indentation formed on the test plate
Roll gap setting method of the roll straightener comprising a.
상기 시험용 판은 아래의 수학식으로 정의된 범위의 길이를 갖고,
[수학식]
N × P 〈 L 〈 (N × P) + 100(mm)
여기서, N은 롤의 개수로서, 상기 롤 교정기의 상부측 롤과 하부측 롤 중 보다 많은 쪽 롤의 개수이고, P는 피치로서, 인접한 롤들에서 어느 한쪽 롤의 중심과 다른 한쪽 롤의 중심 간 거리(mm)이며, L은 상기 시험용 판의 길이(mm)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
According to claim 1,
The test plate has a length defined in the following equation,
[Mathematics]
N × P 〈L 〈(N × P) + 100 (mm)
Here, N is the number of rolls, which is the number of the upper rolls and the lower rolls of the roll straightener, and P is the pitch, the distance between the center of one roll and the center of the other roll in adjacent rolls (mm), L is the length of the test plate (mm), characterized in that the roll gap setting method of the roll calibrator.
상기 파고는, 상기 시험용 판의 길이방향으로 형성된 압흔의 파형상 중 높이가 가장 낮은 산과 깊이가 가장 얕은 골 사이의 높이차로 정의되는 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
According to claim 2,
The wave height, the roll gap setting method of the roll calibrator, characterized in that defined as the height difference between the valley of the lowest height and the shallowest depth of the wave shape of the indentation formed in the longitudinal direction of the test plate.
상기 롤갭의 이상 여부를 판단하는 단계는, 상기 파고로부터 상기 시험용 판의 소성율을 산출하는 단계를 포함하고,
상기 소성율은 아래의 수학식에 의해 산출되며,
[수학식]
H = - 18.8 - 0.0022D + 0.026P + 0.00518Y - 0.195t + 0.215S
여기서, H는 파고(mm)이고, D는 상기 롤 교정기의 롤의 직경(mm)이며, P는 피치(mm)이고, Y는 상기 시험용 판이 갖는 항복강도(MPa)이며, t는 상기 시험용 판의 두께(mm)이고, S는 상기 시험용 판의 소성율(%)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
According to claim 3,
The step of determining whether the roll gap is abnormal includes calculating a plasticity rate of the test plate from the wave height,
The firing rate is calculated by the following equation,
[Mathematics]
H =-18.8-0.0022D + 0.026P + 0.00518Y-0.195t + 0.215S
Here, H is the wave height (mm), D is the diameter of the roll of the roll calibrator (mm), P is the pitch (mm), Y is the yield strength (MPa) of the test plate, and t is the test plate The thickness of (mm), S is the method of setting the roll gap of the roll calibrator, characterized in that the plasticity rate (%) of the test plate.
상기 롤갭의 이상 여부를 판단하는 단계는, 상기 소성율로부터 압하량을 산출하고, 상기 압하량으로부터 상기 실제 롤갭을 산출하는 단계를 포함하고,
상기 압하량은 아래의 수학식에 의해 산출되며,
[수학식]
여기서, δ는 상기 시험용 판의 압하량(mm)이며, P는 피치(mm)이고, Y는 상기 시험용 판이 갖는 항복강도(MPa)이며, E는 영의 계수(Young's modulus) 또는 탄성계수(MPa)이고, t는 상기 시험용 판의 두께(mm)이며, S는 상기 시험용 판의 소성율(%)이고,
상기 실제 롤갭은 아래의 수학식에 의해 산출되며,
[수학식]
G = t - δ
여기서, G는 상기 롤 교정기의 실제 롤갭이고, t는 상기 시험용 판의 두께(mm)이며, δ는 시험용 판의 압하량(mm)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
According to claim 4,
The step of determining whether the roll gap is abnormal includes calculating a rolling reduction amount from the firing rate and calculating the actual roll gap from the rolling reduction amount,
The reduction amount is calculated by the following equation,
[Mathematics]
Here, δ is the rolling amount of the test plate (mm), P is the pitch (mm), Y is the yield strength (MPa) of the test plate, E is Young's modulus (Young's modulus) or modulus of elasticity (MPa) ), T is the thickness (mm) of the test plate, S is the plasticity (%) of the test plate,
The actual roll gap is calculated by the following equation,
[Mathematics]
G = t-δ
Here, G is the actual roll gap of the roll straightener, t is the thickness of the test plate (mm), and δ is the roll gap setting method of the roll straightener, characterized in that the rolling amount of the test plate (mm).
상기 목표 롤갭을 결정하기 위해 목표 파고가 주어지는 단계; 및
상기 목표 파고로부터 상기 시험용 판의 목표 소성율을 산출하는 단계
를 더 포함하고,
상기 목표 소성율은 아래의 수학식에 의해 산출되며,
[수학식]
H = - 18.8 - 0.0022D + 0.026P + 0.00518Y - 0.195t + 0.215S
여기서, H는 목표 파고(mm)이고, D는 상기 롤 교정기의 롤의 직경(mm)이며, P는 피치(mm)이고, Y는 상기 시험용 판이 갖는 항복강도(MPa)이며, t는 상기 시험용 판의 두께(mm)이고, S는 상기 시험용 판의 목표 소성율(%)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
The method of claim 5,
A target wave height is given to determine the target roll gap; And
Calculating a target firing rate of the test plate from the target wave height
Further comprising,
The target firing rate is calculated by the following equation,
[Mathematics]
H =-18.8-0.0022D + 0.026P + 0.00518Y-0.195t + 0.215S
Here, H is the target wave height (mm), D is the diameter of the roll of the roll straightener (mm), P is the pitch (mm), Y is the yield strength (MPa) of the test plate, and t is for the test The thickness of the plate (mm), S is the method of setting the roll gap of the roll calibrator, characterized in that the target plasticity of the test plate (%).
상기 목표 롤갭을 결정하기 위해 목표 소성율이 주어지는 단계를 더 포함하는 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
The method of claim 5,
A method of setting a roll gap of a roll corrector, further comprising the step of giving a target sintering rate to determine the target roll gap.
상기 목표 소성율은 아래의 수학식과 같이 정의되며,
[수학식 5]
S = (ts / t) × 100
여기서, S는 상기 시험용 판의 목표 소성율(%)이고, ts는 상기 시험용 판에서 소성 변형이 발생한 두께(mm)이며, t는 상기 시험용 판의 두께(mm)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
The method of claim 7,
The target firing rate is defined as the following equation,
[Equation 5]
S = (t s / t) × 100
Here, S is the target sintering rate (%) of the test plate, t s is the thickness of the plastic deformation occurred in the test plate (mm), t is a roll calibrator, characterized in that the thickness of the test plate (mm) How to set the roll gap.
상기 목표 소성율로부터 압하량을 산출하고, 상기 압하량으로부터 상기 목표 롤갭을 산출하는 단계를 더 포함하고,
상기 압하량은 아래의 수학식에 의해 산출되며,
[수학식]
여기서, δ는 상기 시험용 판의 압하량(mm)이며, P는 피치(mm)이고, Y는 상기 시험용 판이 갖는 항복강도(MPa)이며, E는 영의 계수(Young's modulus) 또는 탄성계수(MPa)이고, t는 상기 시험용 판의 두께(mm)이며, S는 상기 시험용 판의 목표 소성율(%)이고,
상기 목표 롤갭은 아래의 수학식에 의해 산출되며,
[수학식]
G = t - δ
여기서, G는 상기 롤 교정기의 목표 롤갭이고, t는 상기 시험용 판의 두께(mm)이며, δ는 시험용 판의 압하량(mm)인 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
The method of claim 6 or 7,
Comprising the step of calculating the reduction amount from the target firing rate, and calculating the target roll gap from the reduction amount,
The reduction amount is calculated by the following equation,
[Mathematics]
Here, δ is the rolling amount of the test plate (mm), P is the pitch (mm), Y is the yield strength (MPa) of the test plate, E is Young's modulus (Young's modulus) or modulus of elasticity (MPa) ), T is the thickness (mm) of the test plate, S is the target plasticity (%) of the test plate,
The target roll gap is calculated by the following equation,
[Mathematics]
G = t-δ
Here, G is the target roll gap of the roll calibrator, t is the thickness of the test plate (mm), and δ is the roll gap setting method of the roll calibrator, characterized in that the rolling amount of the test plate (mm).
상기 실제 롤갭이 상기 목표 롤갭의 허용범위 내에 있으면, 정상상태인 것으로 판단하고, 허용범위를 벗어나면 이상상태인 것으로 판단하는 것을 특징으로 하는 롤 교정기의 롤갭 설정방법.
The method of claim 9,
If the actual roll gap is within the allowable range of the target roll gap, it is determined that it is in a normal state, and if it is outside the allowable range, it is determined that it is in an abnormal state.
상기 시험용 판의 폭방향으로 형성된 파형상의 변형이 측정되고, 상기 파형상 중 산의 높이가 일정한 값을 가지면 정상상태인 것으로 판단하고, 상기 파형상의 산의 높이가 허용범위를 벗어난 분포를 가지면 이상상태인 것으로 판단하는 것을 특징으로 하는 롤 교정기의 롤갭 설정방법. According to claim 1,
Deformation of the wave shape formed in the width direction of the test plate is measured, and if the height of the mountain among the wave shapes has a constant value, it is determined that it is normal, and if the height of the mountain on the wave shape has a distribution outside the allowable range, the abnormal condition The roll gap setting method of the roll straightener, characterized in that it is determined to be.