KR102063827B1 - Preparing Method for Multi-functional Fabric Material Coated with Silicon Without Use of Volatile Solvent - Google Patents
Preparing Method for Multi-functional Fabric Material Coated with Silicon Without Use of Volatile Solvent Download PDFInfo
- Publication number
- KR102063827B1 KR102063827B1 KR1020190084123A KR20190084123A KR102063827B1 KR 102063827 B1 KR102063827 B1 KR 102063827B1 KR 1020190084123 A KR1020190084123 A KR 1020190084123A KR 20190084123 A KR20190084123 A KR 20190084123A KR 102063827 B1 KR102063827 B1 KR 102063827B1
- Authority
- KR
- South Korea
- Prior art keywords
- silicone
- weight
- coating
- liquid
- fabric
- Prior art date
Abstract
Description
본 발명은 무용제형 다기능성 실리콘 코팅 원단의 제조방법에 관한 것이다. 보다 구체적으로는 휘발성 유기용제를 사용하지 않고 슬립성, 난연성, 내열성, 내한성, 발수성, 방수성, 내오성, 내약품성, 내후성 특성이 우수한 실리콘 코팅된 원단을 제조하는 방법, 상기 제조방법에 사용되는 원단 코팅용 실리콘 코팅액 조성물, 및 상기 제조방법에 의해 제조된 실리콘 코팅된 원단에 관한 것이다. The present invention relates to a method for producing a solvent-free multifunctional silicone coated fabric. More specifically, a method for producing a silicone coated fabric having excellent slip resistance, flame retardancy, heat resistance, cold resistance, water repellency, water resistance, dirt resistance, chemical resistance, and weather resistance properties without using a volatile organic solvent, and the fabric used in the manufacturing method It relates to a silicone coating liquid composition for coating, and a silicone coated fabric prepared by the above method.
실리콘은 천연소재인 석영모래에서 추출한다. 석영모래를 약 4000℃의 고열로 가열하여 금속규소를 추출한 다음 산소와 결합시킨 것이 실리콘이다. 실리콘은 난연성, 뛰어난 전기절연성, 내약품성, 내열성, 내한성, 무독성, 친환경성 등 다양한 특성으로 인해 현대 산업에 있어서 꼭 필요하며 가장 널리 쓰이고 있는 소재이다. 예를 들어, 인체에 삽입하는 보형물이나 성형물과 아기 젖꼭지 등 고도의 무독성을 요구하는 제품에 널리 사용되고 있다. 또한, 뛰어난 전기절연성, 내열성(320℃), 내한성(-52℃) 등의 특성으로 반도체 및 자동차, 우주선 등 첨단산업에 널리 쓰이고 있다. Silicon is extracted from quartz sand, a natural material. Silicon sand was extracted by heating quartz sand at a high temperature of about 4000 ° C. and then combined with oxygen. Silicone is a necessary and most widely used material in the modern industry because of various characteristics such as flame retardancy, excellent electrical insulation, chemical resistance, heat resistance, cold resistance, non-toxicity and eco-friendliness. For example, it is widely used in products requiring high nontoxicity, such as implants or moldings and baby nipples inserted into the human body. In addition, it is widely used in high-tech industries such as semiconductors, automobiles and spacecrafts due to its excellent electrical insulation, heat resistance (320 ° C.) and cold resistance (−52 ° C.).
실리콘 코팅원단은 무독성 친환경 소재인 실리콘 중 고순도인 액상형 실리콘을 원단에 코팅하여 제조한 기능성 원단이다. 실리콘 코팅 원단은 공해물질과 유해물질을 배출하는 천연가죽과, PVC나 PU를 라미네이팅하여 제조한 합성피혁을 대체하여 환경오염을 감소시키는 친환경 천연소재 원단으로 각광 받고 있다. 또한, 화재 발생에도 화염이나 유독가스가 발생하지 않는 난연성, 방염성 특성도 갖고 있어 가구재, 내장재, 마감재의 안전성 측면에서도 우위성을 갖고 있다. Silicone coating fabric is a functional fabric manufactured by coating high-purity liquid-type silicone among the non-toxic eco-friendly silicone. Silicone coated fabrics are spotlighted as eco-friendly natural materials that reduce environmental pollution by replacing natural leather that emits pollutants and harmful substances and synthetic leather manufactured by laminating PVC or PU. In addition, it has a flame retardant and flame retardant property that does not generate flame or toxic gas even in the event of fire, and thus has an advantage in terms of safety of furniture, interior materials and finishes.
그러나, 실리콘 코팅된 원단은 실리콘의 본래 특성상 표면의 슬립성이 개선되어야 하는 문제점이 있다. 또한, 현재 실리콘 코팅원단을 생산하는 경우 대개 휘발성 유기용제를 사용한다. 그러나, 휘발성 유기용제 화합물은 탄화수소화합물로써 피부접촉 또는 호흡기로 흡입되는 경우 신경계 등에 장애를 일으키는 발암물질로 알려져 있으며, 증기압이 높아 대기 중으로 쉽게 휘발하여 악취 및 오존의 원인물질이 된다. However, the silicone coated fabric has a problem that the slip property of the surface should be improved due to the inherent properties of the silicone. In addition, volatile organic solvents are usually used when producing silicon coated fabrics. However, volatile organic solvent compounds are known as carcinogens that cause disorders in the nervous system and the like when they are inhaled by skin contact or respiratory tract as a hydrocarbon compound.
따라서, 실리콘 원단의 표면의 슬립성이 개선된 제품의 개발 및 제조 공정시 휘발성 유기용제를 사용하지 않는 제조방법의 개발이 요구되고 있다. Therefore, there is a demand for the development of a product which does not use a volatile organic solvent in the development and manufacturing process of a product having improved slip property of a silicon fabric.
본 발명자들은 실리콘 코팅된 원단의 제조시에 최종 제품의 실리콘 표면의 슬립성이 개선되며, 제조 공정 동안 휘발성 유기용제를 사용하지 않는 친환경 제조 공법을 개발하기 위해 연구 노력하였다. 그 결과, 본 발명자들은 제1차, 제2차 및 제3차의 실리콘 코팅액을 순차적으로 코팅하면 실리콘 코팅 원단의 슬립성 개선 뿐만 아니라 난연성, 내열성, 내한성, 발수성, 방수성, 내오성, 내약품성, 내후성 특성이 우수한 실리콘 원단을 제조할 수 있음을 확인하여 본 발명을 완성하였다.The present inventors have made efforts to develop an eco-friendly manufacturing method which improves the slip property of the silicon surface of the final product during the manufacture of the silicone coated fabric and does not use volatile organic solvents during the manufacturing process. As a result, the present inventors sequentially coating the first, second and third silicone coating liquids not only improve the slip resistance of the silicone coating fabric but also flame retardancy, heat resistance, cold resistance, water repellency, waterproof, fouling resistance, chemical resistance, The present invention was completed by confirming that a silicone fabric having excellent weatherability characteristics can be manufactured.
따라서, 본 발명의 목적은 휘발성 유기용제를 사용하지 않고, 실리콘 원단의 표면의 슬립성이 개선된 실리콘 코팅 원단의 제조방법을 제공하는 것에 있다. Accordingly, it is an object of the present invention to provide a method for producing a silicone coated fabric having improved slip property of the surface of the silicone fabric without using a volatile organic solvent.
본 발명의 다른 목적은 실리콘 코팅 원단의 제조에 사용되는 원단 코팅용 실리콘 코팅액 조성물을 제공하는 것에 있다. Another object of the present invention is to provide a silicone coating liquid composition for fabric coating used in the production of silicone coating fabric.
본 발명의 또 다른 목적은 상기 제조 방법에 의해 제조된, 원단 및 실리콘 코팅층을 갖는 실리콘 코팅 원단을 제공하는 것에 있다. Still another object of the present invention is to provide a silicone coated fabric having a fabric and a silicone coating layer produced by the above production method.
본 발명의 다른 목적 및 기술적 특징은 이하의 발명의 상세한 설명, 청구의 범위 및 도면에 의해 보다 구체적으로 제시된다. Other objects and technical features of the present invention are more specifically shown by the following detailed description, claims and drawings.
상기 과제를 해결하기 위해, In order to solve the above problems,
본 발명은 The present invention
(a) 제1차 실리콘 코팅액을 이형지에 코팅하고 경화시키는 단계; (a) coating the first silicone coating solution on a release paper and curing the release paper;
(b) 제2차 실리콘 코팅액을 상기 이형지의 제1차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고 경화시키는 단계; 및 (b) coating the second silicone coating solution on the cured surface by coating the first silicone coating solution of the release paper and curing the second silicone coating solution; And
(c) 상기 제3차 실리콘 코팅액을 상기 이형지의 제2차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고, 이를 원단과 접착시킨 후 경화시키는 단계를 포함하는 실리콘 코팅 원단의 제조방법을 제공한다. (c) coating the third silicone coating solution on the cured surface of the second silicone coating solution of the release paper, and attaching the third silicone coating solution to the fabric and curing the same.
또한, 본 발명은 제1차 실리콘 코팅액, 제2차 실리콘 코팅액, 및 제3차 실리콘 코팅액을 포함하는 원단 코팅용 실리콘 코팅액 조성물을 제공한다. In addition, the present invention provides a silicone coating liquid composition for fabric coating comprising a first silicone coating liquid, a second silicone coating liquid, and a third silicone coating liquid.
또한, 본 발명은 상기 제조방법에 의해 제조된 실리콘 코팅 원단을 제공한다. In addition, the present invention provides a silicone coated fabric prepared by the above manufacturing method.
이하에서, 본 발명을 각 양태에 따라 상세하게 설명한다. Below, this invention is demonstrated in detail according to each aspect.
본 발명의 일 양태에 따르면, 본 발명은 According to one aspect of the present invention,
(a) 제1차 실리콘 코팅액을 이형지에 코팅하고 경화시키는 단계; (a) coating the first silicone coating solution on a release paper and curing the release paper;
(b) 제2차 실리콘 코팅액을 상기 이형지의 제1차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고 경화시키는 단계; 및 (b) coating the second silicone coating solution on the cured surface by coating the first silicone coating solution of the release paper and curing the second silicone coating solution; And
(c) 상기 제3차 실리콘 코팅액을 상기 이형지의 제2차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고, 이를 원단과 접착시킨 후 경화시키는 단계를 포함하는 실리콘 코팅 원단의 제조방법으로서; (c) a method of manufacturing a silicone coated fabric comprising the step of coating the third silicone coating solution on the surface of the second silicone coating solution of the release paper coated and cured, and adhering it with the fabric;
상기 제1차 실리콘 코팅액은 The first silicon coating liquid
(i) 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, vinyl group-terminated); 및 40-50 중량％의 실리콘 다이옥사이드(Silicon dioxide)를 포함하는 액상형 실리콘 수지 A; 및 (i) 50-60% by weight of [siloxane and silicones, di-Me, vinyl group-terminated]; And liquid silicone resin A comprising 40-50% by weight of silicon dioxide; And
(ii) 40-50 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소](Siloxanes and Silicones, di-Me, Me hydrogen); 및 30-40 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 B가 1 : 0.5 ~ 2의 중량비율로 혼합된 실리콘 코팅액이고; (ii) 40-50% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 20-30% by weight [siloxane and silicones, di-Me, Me hydrogen); And liquid silicone resin B containing 30-40% by weight of silicon dioxide is a silicone coating liquid mixed in a weight ratio of 1: 0.5 to 2;
상기 제2차 실리콘 코팅액은 The second silicon coating liquid
(i) 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 10-20 중량％의 실리콘 다이옥사이드; 및 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)를 포함하는 액상형 실리콘 수지 C; 및 (i) 70-80% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; 10-20% by weight of silicon dioxide; And 1-10% by weight of liquid silicone resin C comprising [siloxane and silicones, di-methyl, methyl vinyl, vinyl group-terminated] (Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated) ; And
(ii) 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]를 포함하는 액상형 실리콘 수지 D가 8 ~ 12 : 1의 중량 비율로 혼합된 실리콘 코팅액이고; (ii) 70-80% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; And 20-30% by weight of liquid silicone resin D comprising [siloxane and silicon, di-methyl, methyl hydrogen] in a weight ratio of 8 to 12: 1;
상기 제3차 실리콘 코팅액은 The third silicone coating liquid
(i) 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-테미네이티드]; 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]; 및 40-50 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 E; 및 (i) 50-60% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 1-10% by weight [siloxane and silicon, di-methyl, methyl hydrogen]; And liquid silicone resin E comprising 40-50% by weight of silicon dioxide; And
(ii) 80-90 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 10-20 중량％의 실리콘 다이옥사이드를 포함하는 실리콘 촉매제 F가 100 : 0.1 ~ 1.0의 중량 비율로 혼합된 실리콘 코팅액인 것을 특징으로 하는, 실리콘 코팅 원단의 제조방법. (ii) 80-90% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; And a silicon catalyst F comprising 10-20% by weight of silicon dioxide is a silicon coating liquid mixed in a weight ratio of 100: 0.1 to 1.0.
이하에서, 본 발명의 제조방법을 각 단계에 따라 상세히 설명한다. Hereinafter, the manufacturing method of the present invention will be described in detail for each step.
단계 (a): 제1차 실리콘 코팅액을 이형지에 코팅하고 경화시키는 단계 Step (a): coating the first silicone coating solution on the release paper and curing
제1차 실리콘 코팅액은 액상형 실리콘 수지 A 및 액상형 실리콘 수지 B를 혼합하여 제조한다. The first silicone coating liquid is prepared by mixing the liquid silicone resin A and the liquid silicone resin B.
액상형 실리콘 수지 A는 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, vinyl group-terminated); 및 40-50 중량％의 실리콘 다이옥사이드(Silicon dioxide)을 포함하여 구성된다. Liquid silicone resin A is 50-60% by weight of [siloxane and silicones, di-Me, vinyl group-terminated]; And 40-50% by weight of silicon dioxide.
상기 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, vinyl group-terminated)는 오르가노실록산 화합물의 일종으로서, 비닐터미네이티드 폴리다이메틸실록산(vinyl terminated polydimethylsiloxane) 화합물이라고도 지칭되는 화합물이다. [Siloxanes and Silicones, di-Me, vinyl group-terminated] is a kind of organosiloxane compound, and vinyl-terminated polydimethylsiloxane (vinyl) terminated polydimethylsiloxane) compounds.
액상형 실리콘 수지 B는 40-50 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소](Siloxanes and Silicones, di-Me, Me hydrogen); 및 30-40 중량％의 실리콘 다이옥사이드를 포함하여 구성된다. Liquid silicone resin B is 40-50% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 20-30% by weight [siloxane and silicones, di-Me, Me hydrogen); And 30-40% by weight of silicon dioxide.
상기 [실록산과 실리콘, 다이-메틸, 메틸 수소](Siloxanes and Silicones, di-Me, Me hydrogen) 화합물은 오르가노실록산 화합물의 일종으로서, 다이메틸 메틸하이드로젠 실록산(dimethly methylhydrogen siloxane)으로도 지칭되는 화합물이다. [Siloxanes and Silicones, di-Me, Me hydrogen) compound is a kind of organosiloxane compound, also referred to as dimethly methylhydrogen siloxane. Compound.
상기 액상형 실리콘 수지 A와 액상형 실리콘 수지 B를 1 : 0.5 ~ 2의 중량비율로, 더 바람직하게는 1 : 0.7 ~ 1.8 중량비율, 더욱 바람직하게는 1 : 0.8 ~ 1.5의 중량비율, 가장 바람직하게는 1 : 1 중량비율로 혼합하여 제1차 실리콘 코팅액을 제조한다. The liquid silicone resin A and the liquid silicone resin B in a weight ratio of 1: 0.5 to 2, more preferably 1: 0.7 to 1.8 weight ratio, more preferably 1: 0.8 to 1.5 weight ratio, most preferably The primary silicone coating solution was prepared by mixing at a weight ratio of 1: 1.
제1차 실리콘 코팅액은 실리콘 코팅된 원단에서 실리콘 코팅 표면 슬립성 개선 특성을 부여한다. The primary silicone coating liquid imparts a silicone coating surface slip improvement characteristic in the silicone coated fabric.
상기 제조한 제1차 실리콘 코팅액을 이형지(Release paper)에 코팅하고 경화시킨다. 제1차 실리콘 코팅액은 나이프를 이용하여 일정한 두께로 코팅한다. The prepared first silicone coating solution is coated on a release paper and cured. The first silicone coating liquid is coated to a constant thickness using a knife.
코팅의 두께는 특정 범위로 한정되지 않으며, 필요에 따라 적절한 두께로 코팅할 수 있다. The thickness of the coating is not limited to a specific range, and may be coated to an appropriate thickness as needed.
코팅된 제1차 실리콘 코팅액의 경화는 고온에서 행한다. 예를 들어, 100 ~ 150℃의 온도범위를 갖는 챔버를 일정시간 통과시켜 경화시킬 수 있으나, 이에 한정되지 않는다. 제1차 실리콘 코팅액의 경화시간은 필요에 따라 적절한 시간을 선택할 수 있으며, 예를 들어 상기 온도 범위에서의 경화시간은 10초 ~ 10분의 범위에서 선택할 수 있으나, 이에 한정되지 않는다. Curing of the coated primary silicone coating liquid is performed at high temperature. For example, the chamber having a temperature range of 100 to 150 ° C. may be cured by passing through it for a predetermined time, but is not limited thereto. The curing time of the first silicone coating liquid may be selected as appropriate time, for example, the curing time in the temperature range may be selected from the range of 10 seconds to 10 minutes, but is not limited thereto.
단계 (b): 제2차 실리콘 코팅액을 상기 이형지의 제1차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고 경화시키는 단계 Step (b): coating and curing the second silicone coating liquid on the cured surface coated with the first silicone coating liquid of the release paper.
제2차 실리콘 코팅액은 액상형 실리콘 수지 C 및 액상형 실리콘 수지 D를 혼합하여 제조한다. The secondary silicone coating liquid is prepared by mixing the liquid silicone resin C and the liquid silicone resin D.
액상형 실리콘 수지 C는 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 10-20 중량％의 실리콘 다이옥사이드; 및 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)를 포함하여 구성한다. Liquid silicone resin C is 70-80% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 10-20% by weight of silicon dioxide; And 1-10% by weight of [siloxane and silicone, di-methyl, methyl vinyl, vinyl group-terminated] (Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated).
상기 [실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)는 (비닐메틸실록산)-다이메틸실록산 비닐 터미네이티드 코폴리머로도 지칭되는 화합물이다. [Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated] is (vinylmethylsiloxane) -dimethylsiloxane vinyl terminator Also referred to as tide copolymers.
액상형 실리콘 수지 D는 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]를 포함하여 구성한다. Liquid silicone resin D is 70-80% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; And 20-30% by weight of [siloxane and silicon, di-methyl, methyl hydrogen].
상기 액상형 실리콘 수지 C와 액상형 실리콘 수지 D를 8 ~ 12 : 1의 중량 비율로, 더 바람직하게는 9 ~ 11 : 1의 중량비율로, 가장 바람직하게는 10 : 1의 중량비율로 혼합하여 제2차 실리콘 코팅액을 제조한다. The liquid silicone resin C and the liquid silicone resin D are mixed in a weight ratio of 8 to 12: 1, more preferably in a weight ratio of 9 to 11: 1, most preferably in a weight ratio of 10: 1, and the second A primary silicone coating solution is prepared.
본 발명에서 제2차 실리콘 코팅액은 제1차 실리콘 코팅액의 경화층과 제3차 실리콘 코팅액 경화층을 결합시키는 바인더로서 역할을 한다. In the present invention, the second silicone coating solution serves as a binder for bonding the cured layer of the first silicone coating solution and the third silicone coating solution cured layer.
상기 제조한 제2차 실리콘 코팅액을 상기 이형지의 제1차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고 경화시킨다. The prepared secondary silicone coating solution is coated with the primary silicone coating solution of the release paper and then cured on the cured surface.
제2차 실리콘 코팅액은 나이프를 이용하여 일정한 두께로 코팅한다. 코팅의 두께는 특정 범위로 한정되지 않으며, 필요에 따라 적절한 두께로 코팅할 수 있다. The secondary silicone coating solution is coated to a constant thickness using a knife. The thickness of the coating is not limited to a specific range, and may be coated to an appropriate thickness as needed.
코팅된 제2차 실리콘 코팅액의 경화는 고온에서 행한다. 예를 들어, 100 ~ 160℃의 온도범위를 갖는 챔버를 일정시간 통과시켜 경화시킬 수 있으나, 이에 한정되지 않는다. 제2차 실리콘 코팅액의 경화시간은 필요에 따라 적절한 시간을 선택할 수 있으며, 예를 들어 상기 온도 범위에서의 경화시간은 10초 ~ 10분의 범위에서 선택할 수 있으나, 이에 한정되지 않는다. Curing of the coated secondary silicone coating liquid is performed at high temperature. For example, the chamber having a temperature range of 100 to 160 ° C. may be cured by passing through it for a predetermined time, but is not limited thereto. The curing time of the secondary silicone coating liquid may be selected as appropriate time, for example, the curing time in the temperature range may be selected from the range of 10 seconds to 10 minutes, but is not limited thereto.
단계 (c): 제3차 실리콘 코팅액을 상기 이형지의 제2차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅하고, 이를 원단과 접착시킨 후 경화시키는 단계 Step (c): coating the third silicone coating liquid on the cured surface of the second silicone coating liquid of the release paper, attaching the third silicone coating liquid to the fabric, and then curing the third silicone coating liquid.
제3차 실리콘 코팅액은 액상형 실리콘 수지 E 및 실리콘 촉매제 F를 혼합하여 제조한다. The third silicone coating liquid is prepared by mixing the liquid silicone resin E and the silicone catalyst F.
액상형 실리콘 수지 E는 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-테미네이티드]; 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]; 및 40-50 중량％의 실리콘 다이옥사이드를 포함하여 구성한다. Liquid silicone resin E is 50-60% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 1-10% by weight [siloxane and silicon, di-methyl, methyl hydrogen]; And 40-50% by weight of silicon dioxide.
실리콘 촉매제 F는 80-90 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 10-20 중량％의 실리콘 다이옥사이드를 포함하여 구성한다. Silicone catalyst F comprises 80-90% by weight of [siloxane and silicon, di-methyl, vinyl group-terminated]; And 10-20% by weight of silicon dioxide.
상기 액상형 실리콘 수지 E와 실리콘 촉매제 F를 100 : 0.1 ~ 1.0의 중량 비율로, 바람직하게는 100 : 0.2 ~ 0.9의 비율로, 더욱 바람직하게는 100 : 0.2 ~ 0.5의 비율로, 가장 바람직하게는 100 : 0.3의 비율로 혼합하여 제3차 실리콘 코팅액을 제조한다. The liquid silicone resin E and the silicon catalyst F in a weight ratio of 100: 0.1 to 1.0, preferably in a ratio of 100: 0.2 to 0.9, more preferably in a ratio of 100: 0.2 to 0.5, most preferably 100 A third silicon coating solution is prepared by mixing at a ratio of 0.3.
상기 제조한 제3차 실리콘 코팅액을 상기 이형지의 제2차 실리콘 코팅액이 코팅되어 경화된 표면에 코팅한다. 제3차 실리콘 코팅액은 나이프를 이용하여 일정한 두께로 코팅한다. 코팅의 두께는 특정 범위로 한정되지 않으며, 필요에 따라 적절한 두께로 코팅할 수 있다. The prepared third silicone coating liquid is coated on the cured surface by coating the second silicone coating liquid of the release paper. The third silicone coating liquid is coated to a constant thickness using a knife. The thickness of the coating is not limited to a specific range, and may be coated to an appropriate thickness as needed.
상기 제3차 실리콘 코팅액이 코팅된 이형지를 롤프레스를 이용하여 원단과 접착시킨 후 고온에서 경화시켜 원단과 최종적으로 접착시킨다. The third silicone coating solution is coated with a release paper coated with a fabric using a roll press, and then cured at high temperature to finally adhere to the fabric.
상기 코팅된 제3차 코팅액의 경화는 고온에서 행한다. 예를 들어, 100 ~ 180℃의 온도범위를 갖는 챔버를 일정시간 통과시켜 경화시킬 수 있으나, 이에 한정되지 않는다. 제3차 실리콘 코팅액의 경화시간은 필요에 따라 적절한 시간을 선택할 수 있으며, 예를 들어 상기 온도 범위에서의 경화시간은 10초 ~ 15분의 범위에서 선택할 수 있으나, 이에 한정되지 않는다. Curing of the coated third coating liquid is performed at a high temperature. For example, the chamber having a temperature range of 100 to 180 ° C. may be cured by passing a predetermined time, but is not limited thereto. The curing time of the third silicone coating liquid may be selected as appropriate time, for example, the curing time in the temperature range may be selected from the range of 10 seconds to 15 minutes, but is not limited thereto.
상기 경화가 완료되어 실리콘 코팅이 원단에 완전히 접착되면 이형지를 제거한다. When the curing is completed and the silicone coating is completely adhered to the fabric to remove the release paper.
본 발명에서 실리콘 코팅에 사용될 수 있는 원단은 실리콘 코팅이 적용될 수 있다면 제한 없이 사용될 수 있다. Fabrics that can be used for the silicone coating in the present invention can be used without limitation as long as the silicone coating can be applied.
본 발명의 일 구현예에 따르면, 상기 원단은 면(cotton), 아마(Linen), 저마(Ramie), 견(silk), 레이온, 모(wool), 또는 합성섬유일 수 있으나, 이에 한정되지 않는다. According to one embodiment of the invention, the fabric may be cotton, linen, Ramie, silk, rayon, wool, or synthetic fibers, but is not limited thereto. .
본 발명의 다른 구현예에 따르면, 상기 합성섬유는 나일론, 폴리에스테르, 또는 아크릴일 수 있다. According to another embodiment of the present invention, the synthetic fiber may be nylon, polyester, or acrylic.
본 발명의 구체예에 따르면, 상기 원단은 가구용 원단, 카시트, 가방용 원단, 요트용 원단, 벽지, 유아용품용 원단(예들 들어, 턱받이, 방수매트, 기저귀 갈이대 등) 스포츠 의류용 원단(예를 들어, 수영복, 수상용 슈트, 요가용 매트, 구명쪼끼 원단 등), 매트리스원단(예를 들어, 환자용매트, 온열매트, 전기담요 등), 앞치마(예를 들어, 요리사용 앞치마, 어부용 방수 앞치마, 용접용 앞치마 등), 특수복(예를 들어 소방복, 수술복, 화학약품제조공장용 특수복, 용접복 등) 등이 있으나, 이에 한정되지 않는다. According to an embodiment of the present invention, the fabric is a fabric for furniture, car seat, bag fabric, yacht fabric, wallpaper, fabrics for baby products (for example, bib, waterproof mat, diaper change, etc.) sports clothing fabric (for example For example, swimwear, water suits, yoga mats, lifejackets, etc., mattress fabrics (e.g., patient mats, thermal mats, electric blankets, etc.), aprons (e.g., chef aprons, fisherman aprons, etc.) , Welding aprons, etc., special clothing (for example, fire fighting clothing, surgical clothing, chemical manufacturing factory special clothing, welding clothes, etc.), but is not limited thereto.
본 발명의 다른 양태에 따르면, 다음의 제1차, 제2차, 및 제3차 실리콘 코팅액을 포함하는 원단 코팅용 실리콘 코팅액 조성물을 제공한다: According to another aspect of the present invention, there is provided a silicone coating liquid composition for fabric coating comprising the following primary, secondary, and tertiary silicone coating liquids:
(a) 제1차 실리콘 코팅액으로서, (a) a primary silicone coating liquid,
(i) 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, vinyl group-terminated); 및 40-50 중량％의 실리콘 다이옥사이드(Silicon dioxide)를 포함하는 액상형 실리콘 수지 A; 및 (i) 50-60% by weight of [siloxane and silicones, di-Me, vinyl group-terminated]; And liquid silicone resin A comprising 40-50% by weight of silicon dioxide; And
(ii) 40-50 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소](Siloxanes and Silicones, di-Me, Me hydrogen); 및 30-40 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 B가 1 : 0.5 ~ 2 의 중량비율로 혼합된, 제1차 실리콘 코팅액; (ii) 40-50% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 20-30% by weight [siloxane and silicones, di-Me, Me hydrogen); And a liquid silicone resin B including 30-40 wt% of silicon dioxide in a weight ratio of 1: 0.5 to 2;
(b) 제2차 실리콘 코팅액으로서, (b) a secondary silicone coating liquid,
(i) 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 10-20 중량％의 실리콘 다이옥사이드; 및 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)를 포함하는 액상형 실리콘 수지 C; 및 (i) 70-80% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; 10-20% by weight of silicon dioxide; And 1-10% by weight of liquid silicone resin C comprising [siloxane and silicones, di-methyl, methyl vinyl, vinyl group-terminated] (Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated) ; And
(ii) 70-80 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 20-30 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]를 포함하는 액상형 실리콘 수지 D이 8 ~ 12 : 1의 중량 비율로 혼합된, 제2차 실리콘 코팅액; 및 (ii) 70-80% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; And a second silicone coating liquid in which a liquid silicone resin D including 20-30% by weight of [siloxane and silicon, di-methyl, methyl hydrogen] is mixed in a weight ratio of 8 to 12: 1; And
(c) 제3차 실리콘 코팅액으로서, (c) a third silicone coating liquid,
(i) 50-60 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-테미네이티드]; 1-10 중량％의 [실록산과 실리콘, 다이-메틸, 메틸 수소]; 및 40-50 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 E; 및 (i) 50-60% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 1-10% by weight [siloxane and silicon, di-methyl, methyl hydrogen]; And liquid silicone resin E comprising 40-50% by weight of silicon dioxide; And
(ii) 80-90 중량％의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 10-20 중량％의 실리콘 다이옥사이드를 포함하는 실리콘 촉매제 F가 100 : 0.1 ~ 1.0의 중량 비율로 혼합된, 제3차 실리콘 코팅액. (ii) 80-90% by weight [siloxane and silicone, di-methyl, vinyl group-terminated]; And a silicon catalyst F including 10-20% by weight of silicon dioxide in a weight ratio of 100: 0.1 to 1.0.
본 발명의 또 다른 양태에 따르면, 상기 제조 방법에 의해 제조된 실리콘 코팅 원단으로서, (i) 원단; 및 (ii) 상기 원단의 표면에 상기 제1차 실리콘 코팅액, 제2차 실리콘 코팅액 및 제3차 실리콘 코팅액이 순차적으로 코팅되어 경화된 실리콘 코팅층을 갖는 것을 특징으로 하는 실리콘 코팅 원단을 제공한다. According to another aspect of the invention, the silicone coated fabric produced by the manufacturing method, (i) the fabric; And (ii) the first silicone coating liquid, the second silicone coating liquid, and the third silicone coating liquid are sequentially coated on the surface of the fabric to have a cured silicone coating layer.
본 발명에서 실리콘 코팅에 사용될 수 있는 원단은 실리콘 코팅이 적용될 수 있다면 제한없이 사용될 수 있다. Fabrics that can be used for the silicone coating in the present invention can be used without limitation as long as the silicone coating can be applied.
본 발명의 일 구현예에 따르면, 상기 원단은 면(cotton), 아마(Linen), 저마(Ramie), 견(silk), 레이온, 모(wool), 또는 합성섬유일 수 있으나, 이에 한정되지 않는다. According to one embodiment of the invention, the fabric may be cotton, linen, Ramie, silk, rayon, wool, or synthetic fibers, but is not limited thereto. .
본 발명의 다른 구현예에 따르면, 상기 합성섬유는 나일론, 폴리에스테르, 또는 아크릴일 수 있다. According to another embodiment of the present invention, the synthetic fiber may be nylon, polyester, or acrylic.
본 발명의 구체예에 따르면, 상기 원단은 가구용 원단, 카시트, 가방용 원단, 요트용 원단, 벽지, 유아용품용 원단(예들 들어, 턱받이, 방수매트, 기저귀 갈이대 등) 스포츠 의류용 원단(예를 들어, 수영복, 수상용 슈트, 요가용 매트, 구명쪼끼 원단 등), 매트리스원단(예를 들어, 환자용매트, 온열매트, 전기담요 등), 앞치마(예를 들어, 요리사용 앞치마, 어부용 방수 앞치마, 용접용 앞치마 등), 특수복(예를 들어 소방복, 수술복, 화학약품제조공장용 특수복, 용접복 등) 등이 있으나, 이에 한정되지 않는다. According to an embodiment of the present invention, the fabric is a fabric for furniture, car seat, bag fabric, yacht fabric, wallpaper, fabrics for baby products (for example, bib, waterproof mat, diaper change, etc.) sports clothing fabric (for example For example, swimwear, water suits, yoga mats, lifejackets, etc., mattress fabrics (e.g., patient mats, thermal mats, electric blankets, etc.), aprons (e.g., chef aprons, fisherman aprons, etc.) , Welding aprons, etc., special clothing (for example, fire fighting clothing, surgical clothing, chemical manufacturing factory special clothing, welding clothes, etc.), but is not limited thereto.
본 발명은 무용제형 다기능성 실리콘 코팅 원단의 제조방법, 상기 제조방법에 사용되는 실리콘 원단 코팅용 코팅액 조성물, 및 상기 제조방법에 의해 제조된 실리콘 코팅 원단에 관한 것이다. 본 발명의 제조방법은 휘발성 유기용제를 사용하지 않으므로, 제조 공정시 작업 환경이 개선되며, 대기중으로 오염물질의 방출이 발생하지 않는다. 또한, 본 발명에 의해 제조된 실리콘 코팅된 원단은 표면 슬립성, 난연성, 내열성, 내한성, 발수성, 방수성, 내오성, 내약품성, 내후성 특성이 현저히 향상된다. The present invention relates to a manufacturing method of a solvent-free multifunctional silicone coating fabric, a coating liquid composition for coating the silicone fabric used in the manufacturing method, and a silicone coating fabric produced by the manufacturing method. Since the manufacturing method of the present invention does not use a volatile organic solvent, the working environment is improved during the manufacturing process, and no emission of pollutants into the atmosphere occurs. In addition, the silicone-coated fabric produced by the present invention is significantly improved surface slip resistance, flame retardancy, heat resistance, cold resistance, water repellency, waterproof, dirt resistance, chemical resistance, weather resistance properties.
도 1은 본 발명의 방법에 따라 제조한 실리콘 코팅된 자동차 시트커버용 원단의 유해물질 검출 여부를 시험방법 MS 300-55:2018에 따라 측정한 결과이다.
도 2는 본 발명의 방법에 따라 제조한 실리콘 코팅된 자동차 시트커버용 원단의 유해물질 검출 여부를 시험한 측정 조건이다.
도 3은 실리콘 코팅된 자동차 시트커버용 원단에 대해 현대기아자동차 기술표준 MS 300-08에 따라 난연성 특성을 측정한 결과이다. 1 is a result of measuring the detection of harmful substances in the silicon coated car seat cover fabric prepared according to the method of the present invention according to the test method MS 300-55: 2018.
Figure 2 is a measurement condition that tested whether the detection of harmful substances in the silicone-coated car seat cover fabric prepared according to the method of the present invention.
Figure 3 is the result of measuring the flame retardant properties according to the Hyundai-Kia Motors technical standard MS 300-08 for the silicone-coated car seat cover fabric.
본 명세서에서 설명된 구체적인 실시예는 본 발명의 바람직한 구현예 또는 예시를 대표하는 의미이며, 이에 의해 본 발명의 범위가 한정되지는 않는다. 본 발명의 변형과 다른 용도가 본 명세서 특허청구범위에 기재된 발명의 범위로부터 벗어나지 않는다는 것은 당업자에게 명백하다. Specific embodiments described herein are meant to represent preferred embodiments or examples of the present invention, whereby the scope of the present invention is not limited. It will be apparent to those skilled in the art that modifications and other uses of the invention do not depart from the scope of the invention described in the claims.
실시예 Example
실시예 1: 액상형 실리콘 수지의 제조 Example 1 Preparation of Liquid Silicone Resin
(1) 액상형 실리콘 수지 A의 제조 (1) Preparation of Liquid Silicone Resin A
전체 액상형 실리콘 수지 조성물에 대해, 50 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드(Siloxanes and Silicones, di-Me, vinyl group-terminated) 및 40 중량％의 실리콘 다이옥사이드(Silicon dioxide)를 포함하는 액상형 실리콘 수지 A를 제조하였다. 50% by weight of siloxane and silicon, di-methyl, vinyl group-terminated (Siloxanes and Silicones, di-Me, vinyl group-terminated) and 40% by weight of silicon dioxide relative to the total liquid silicone resin composition Liquid silicone resin A including) was prepared.
(2) 액상형 실리콘 수지 B의 제조 (2) Preparation of Liquid Silicone Resin B
전체 액상형 실리콘 수지 조성물에 대해, 40 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드, 20 중량％의 실록산과 실리콘, 다이-메틸, 메틸 수소(Siloxanes and Silicones, di-Me, Me hydrogen), 및 30 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 B를 제조하였다. 40% by weight of siloxane with silicone, di-methyl, vinyl group-terminated, 20% by weight of siloxane with silicone, di-methyl, methyl hydrogen (Siloxanes and Silicones, di-Me, Me hydrogen), and liquid silicone resin B including 30 wt% of silicon dioxide was prepared.
(3) 액상형 실리콘 수지 C의 제조 (3) Preparation of Liquid Silicone Resin C
전체 액상형 실리콘 수지 조성물에 대해, 70 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드, 10 중량％의 실리콘 다이옥사이드, 및 3 중량％의 실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드(Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)를 포함하는 액상형 실리콘 수지 C를 제조하였다. 70% by weight of siloxane and silicone, di-methyl, vinyl group-terminated, 10% by weight of silicon dioxide, and 3% by weight of siloxane with silicone, dimethyl, methyl vinyl, Liquid silicone resin C was prepared including vinyl group-terminated (Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated).
(4) 액상형 실리콘 수지 D의 제조 (4) Preparation of Liquid Silicone Resin D
전체 액상형 실리콘 수지 조성물에 대해, 70 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드 및 20 중량％의 실록산과 실리콘, 다이-메틸, 메틸 수소를 포함하는 액상형 실리콘 수지 D를 제조하였다. Liquid silicone resin D comprising 70 wt% siloxane and silicone, di-methyl, vinyl group-terminated and 20 wt% siloxane and silicone, di-methyl, methyl hydrogen, based on the total liquid silicone resin composition It was.
(5) 액상형 실리콘 수지 E의 제조 (5) Preparation of Liquid Silicone Resin E
전체 액상형 실리콘 수지 조성물에 대해, 50 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-테미네이티드, 5 중량％의 실록산과 실리콘, 다이-메틸, 메틸 수소, 및 40 중량％의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 E를 제조하였다. 50% by weight of siloxane and silicon, di-methyl, vinyl group-terminated, 5% by weight of siloxane and silicon, di-methyl, methyl hydrogen, and 40% by weight of silicon dioxide, based on the total liquid silicone resin composition. A liquid silicone resin E was prepared.
(6) 실리콘 촉매제 F의 제조 (6) Preparation of Silicon Catalyst F
촉매제 전체에 대해, 80 중량％의 실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드, 및 10 중량％의 실리콘 다이옥사이드를 포함하는 실리콘 촉매제 F를 제조하였다. Based on the total catalyst, a silicon catalyst F comprising 80 wt% siloxane and silicon, di-methyl, vinyl group-terminated, and 10 wt% silicon dioxide was prepared.
실시예 2: 실리콘 코팅액의 제조 Example 2: Preparation of Silicone Coating Liquid
상기 제조한 액상형 실리콘 수지 A와 B를 1 : 1의 중량비율로 혼합하여 제1차 코팅액을 제조하였다. 또한, 상기 제조한 액상형 실리콘 수지 C와 D를 10 : 1의 중량비율로 혼합하여 제2차 코팅액을 제조하였다. 또한, 상기 제조한 액상형 실리콘 수지 E와 실리콘 촉매제 F를 100 : 0.3의 중량 비율로 혼합하여 교반하여 제3차 코팅액을 제조하였다. The liquid silicone resins A and B prepared above were mixed at a weight ratio of 1: 1 to prepare a first coating solution. In addition, a secondary coating solution was prepared by mixing the prepared liquid silicone resins C and D in a weight ratio of 10: 1. In addition, the liquid silicone resin E prepared above and the silicone catalyst F were mixed and stirred at a weight ratio of 100: 0.3 to prepare a third coating solution.
실시예 3: 실리콘 코팅 원단의 제조 Example 3: Preparation of Silicone Coated Fabrics
(1) 실리콘 코팅된 폴더 매트용 원단의 제작 (1) Fabrication of silicone coated folder mat fabric
상기 제조한 제1차 코팅액을 이형지(Release Paper, RP)에 나이프를 이용하여 0.03 mm의 두께로 코팅한 후 120℃의 챔버에 약 2분 간 통과시켜 경화를 유도하였다. 제1차 코팅액을 코팅하고 경화시킨 이형지에 상기 제조한 제2차 코팅액을 나이프를 이용하여 0.05 mm의 두께로 코팅한 후 130℃의 챔버에 약 3분 간 통과시켜 경화시켰다. 제2차 코팅액이 코팅되어 경화된 이형지에 상기 제조한 제3차 코팅액을 나이프를 이용하여 0.07 mm의 두께로 코팅한 후 롤프레스를 이용하여 폴더 매트용 원단에 접착시키고, 140℃의 챔버에 약 3분 30초간 경화시켜 원단에 실리콘 코팅의 접착을 완성하였다. The prepared primary coating solution was coated on a release paper (RP) to a thickness of 0.03 mm using a knife and then passed through a chamber at 120 ° C. for about 2 minutes to induce curing. The secondary coating solution prepared above was coated on the first release paper coated and cured to a thickness of 0.05 mm using a knife, and then cured by passing it through a chamber at 130 ° C. for about 3 minutes. After coating the third coating solution prepared on the release paper cured with the second coating solution to a thickness of 0.07 mm using a knife, and then adhered to the fabric for the folder mat using a roll press, and about 140 ℃ chamber Curing for 3
(2) 실리콘 코팅된 자동차 시트커버용 원단의 제작 (2) Fabrication of silicone coated car seat fabric
실시예 3의 (1)항목에 기재된 방법과 동일한 방법에 따라 자동차 시트 커버용 원단에 실리콘을 코팅하여, 실리콘 코팅된 자동차 시트커버용 원단을 제작하였다. According to the same method as described in the item (1) of Example 3, the silicone car seat cover fabric was coated with silicon to fabricate the silicone car seat cover fabric.
실시예 4: 실리콘 코팅 원단의 특성 측정 Example 4 Measurement of Properties of Silicone Coated Fabrics
(1) 폴더 매트용 원단의 유해물질 방출량 측정 (1) Measurement of the amount of harmful substances released on fabric for folder mat
실시예 3의 (1)항목의 방법에 따라 제조한 실리콘 코팅된 폴더 매트용 원단의 유해물질 방출량을 측정하여 그 결과를 아래 표 1에 나타내었다. The amount of harmful substances emitted from the fabric for silicone coated folder mat prepared according to the method of item (1) of Example 3 was measured and the results are shown in Table 1 below.
* 시험방법 및 안전요건: 안전확인 안전기준 부속서 2(합성수지제 어린이용품) * Test Methods and Safety Requirements: Annex 2 (Safety Goods for Children)
(2) 자동차 시트커버용 원단의 특성 측정 (2) Measurement of characteristics of fabric for automobile seat cover
① 유해물질 방출량 측정 ① Measurement of emission amount of hazardous substances
실시예 3의 (2)항목의 방법에 따라 제조한 실리콘 코팅된 자동차 시트커버용 원단의 유해물질 검출 여부를 시험방법 MS 300-55:2018에 따라 측정하였다(시험소: 한국건설생활환경시험연구원). 측정 결과는 하기 표 2와 도 1에 나타내었고, 측정 조건은 도 2에 나타내었다. The detection of harmful substances in the silicone-coated car seat cover fabric prepared according to the method of item (2) of Example 3 was measured according to test method MS 300-55: 2018 (Laboratory: Korea Institute of Construction and Environmental Testing) . The measurement results are shown in Table 2 and FIG. 1, and the measurement conditions are shown in FIG. 2.
② 난연성 특성 ② flame retardant properties
실시예 3의 (2)항목의 방법에 따라 제조한 실리콘 코팅된 자동차 시트커버용 원단에 대해 현대기아자동차 기술표준 MS 300-08에 따라 난연성 특성을 측정하였다. 그 실험결과는 아래 표 3과 도 3에 각각 나타내었다. Flame-retardant properties were measured according to Hyundai-Kia Motors Technical Standard MS 300-08 for the silicone-coated car seat cover fabric prepared according to the method of item (2) of Example 3. The experimental results are shown in Table 3 and FIG. 3, respectively.
실시예 5: 실리콘 코팅 원단의 슬립성 특성 측정 Example 5: Measurement of slip property of silicone coated fabric
(1) 시험편의 제작 (1) Preparation of test piece
상기 실시예 2에 따라 제조한 제1차 코팅액을 이형지(Release Paper, RP)에 나이프를 이용하여 0.03 mm의 두께로 코팅한 후 120℃의 챔버에 약 2분 간 통과시켜 경화를 유도하였다. 제1차 코팅액을 코팅하고 경화시킨 이형지에 상기 실시예 2에 따라 제조한 제2차 코팅액을 나이프를 이용하여 0.05 mm의 두께로 코팅한 후 130℃의 챔버에 약 3분 간 통과시켜 경화시켰다. 제2차 코팅액이 코팅되어 경화된 이형지에 상기 실시예 2에 따라 제조한 제3차 코팅액을 나이프를 이용하여 0.07 mm의 두께로 코팅한 후 롤프레스를 이용하여 원단에 접착시키고, 140℃의 챔버에 약 3분 30초간 경화시켜 원단에 실리콘 코팅의 접착을 완성하여, 시험편 A을 제작하였다. 한편, 비교 시험편 B는 종래의 실리콘 코팅 방법에 따라 제작한 타사 실리콘 코팅 원단을 구입하여 시험에 사용하였다. The first coating solution prepared according to Example 2 was coated on a release paper (RP) to a thickness of 0.03 mm using a knife, and then passed through a chamber at 120 ° C. for about 2 minutes to induce curing. The second coating solution prepared according to Example 2 was coated on the release paper cured and coated with the first coating solution to a thickness of 0.05 mm using a knife, and then cured by passing it through a chamber at 130 ° C. for about 3 minutes. After coating the third coating solution prepared according to Example 2 on the release paper cured by coating the second coating solution to a thickness of 0.07 mm using a knife, and then bonded to the fabric using a roll press, the chamber of 140 ℃ Was cured for about 3 minutes and 30 seconds to complete adhesion of the silicone coating to the fabric, thereby preparing Test Piece A. On the other hand, Comparative Test Piece B was used for the test by purchasing a third-party silicone coating fabric produced in accordance with the conventional silicone coating method.
(2) 마찰계수의 측정 및 결과 (2) Measurement and result of friction coefficient
마찰력은 KS G 5749 체조 경기용 착지매트에 준한 방법으로 측정하였고, 마찰계수는 측정된 힘과 추의 하중(3kg)을 이용하여 산출하였다(한국건설생활환경시험연구원). 마찰계수를 측정한 결과, 본 발명의 시험편 A는 가로 0.71, 세로 0.68의 값이 측정되었고, 비교 시험편 B는 가로 1.82, 세로 1.66의 값이 측정되었다. 상기 실험결과, 본 발명의 방법에 의해 제조한 실리콘 코팅 원단은 종래의 방법으로 제조한 실리콘 코팅 원단 보다 슬립성이 월등히 개선된 것을 확인할 수 있었다. Friction force was measured by the method according to KS G 5749 gymnastics landing mat, and friction coefficient was calculated by using the measured force and weight of the weight (3kg) (Korea Institute of Construction and Environmental Testing). As a result of measuring the friction coefficient, the test piece A of the present invention measured the values of the width 0.71 and the length 0.68, and the comparative test piece B the value of the width 1.82 and the length 1.66. As a result of the experiment, the silicone coating fabric produced by the method of the present invention was confirmed that the slip properties are significantly improved than the silicone coating fabric prepared by the conventional method.
이상으로 본 발명의 특정한 부분을 상세히 기술하였는 바, 당업계의 통상의 지식을 가진 자에게 있어서 이러한 구체적인 기술은 단지 바람직한 구현 예일 뿐이며, 이에 본 발명의 범위가 제한되는 것이 아닌 점은 명백하다. 따라서, 본 발명의 실질적인 범위는 첨부된 청구항과 그의 등가물에 의하여 정의된다고 할 것이다.Having described the specific part of the present invention in detail, it is apparent to those skilled in the art that such a specific technology is only a preferred embodiment, and the scope of the present invention is not limited thereto. Therefore, the substantial scope of the present invention will be defined by the appended claims and equivalents thereof.
Claims (9)
(b) 제2차 실리콘 코팅액을 상기 이형지의 제1차 실리콘 코팅액이 코팅되어 경화된 표면에 0.05mm 두께로 코팅하고 경화시키는 단계; 및
(c) 제3차 실리콘 코팅액을 상기 이형지의 제2차 실리콘 코팅액이 코팅되어 경화된 표면에 0.07mm 두께로 코팅하고, 이를 원단과 접착시킨 후 경화시키는 단계를 포함하는 실리콘 코팅 원단의 제조방법으로서;
상기 제1차 실리콘 코팅액은
(i) 50-60 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, vinyl group-terminated); 및 40-50 중량%의 실리콘 다이옥사이드(Silicon dioxide)를 포함하는 액상형 실리콘 수지 A; 및
(ii) 40-50 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 20-30 중량%의 [실록산과 실리콘, 다이-메틸, 메틸 수소](Siloxanes and Silicones, di-Me, Me hydrogen); 및 30-40 중량%의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 B가 1 : 0.5 ~ 2의 중량비율로 혼합된 실리콘 코팅액이고;
상기 제2차 실리콘 코팅액은
(i) 70-80 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 10-20 중량%의 실리콘 다이옥사이드; 및 1-10 중량%의 [실록산과 실리콘, 다이-메틸, 메틸 비닐, 비닐기-터미네이티드](Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated)를 포함하는 액상형 실리콘 수지 C; 및
(ii) 70-80 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 20-30 중량%의 [실록산과 실리콘, 다이-메틸, 메틸 수소]를 포함하는 액상형 실리콘 수지 D가 8 ~ 12 : 1의 중량 비율로 혼합된 실리콘 코팅액이고;
상기 제3차 실리콘 코팅액은
(i) 50-59 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-테미네이티드]; 1-5 중량%의 [실록산과 실리콘, 다이-메틸, 메틸 수소]; 및 40-45 중량%의 실리콘 다이옥사이드를 포함하는 액상형 실리콘 수지 E; 및
(ii) 80-90 중량%의 [실록산과 실리콘, 다이-메틸, 비닐기-터미네이티드]; 및 10-20 중량%의 실리콘 다이옥사이드를 포함하는 실리콘 촉매제 F가 100 : 0.1 ~ 1.0의 중량 비율로 혼합된 실리콘 코팅액이고,
상기 제1차 실리콘 코팅액은 액상형 실리콘 수지 A 및 B가 1 : 1의 중량비율로 혼합되고,
상기 제2차 실리콘 코팅액은 액상형 실리콘 수지 C 및 D가 10 : 1의 중량 비율로 혼합되고,
상기 제3차 실리콘 코팅액은 액상형 실리콘 수지 E와 실리콘 촉매제 F가 100 : 0.3의 중량 비율로 혼합된 것임을 특징으로 하는, 실리콘 코팅 원단의 제조방법.
(a) coating the first silicone coating solution on a release paper with a thickness of 0.03 mm and curing the first silicone coating solution;
(b) coating the second silicone coating solution on the cured surface by coating the first silicone coating solution of the release paper to a thickness of 0.05 mm and curing the second silicone coating solution; And
(c) coating a third silicone coating solution on the cured surface by coating the second silicone coating solution of the release paper with a thickness of 0.07 mm; ;
The first silicon coating liquid
(i) 50-60% by weight [siloxane and silicones, di-Me, vinyl group-terminated]; And liquid silicone resin A comprising 40-50% by weight of silicon dioxide; And
(ii) 40-50% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 20-30% by weight of [siloxane and silicones, di-Me, Me hydrogen]; And liquid silicone resin B containing 30-40% by weight of silicon dioxide is a silicone coating liquid mixed in a weight ratio of 1: 0.5 to 2;
The second silicon coating liquid
(i) 70-80% by weight [siloxane with silicone, di-methyl, vinyl group-terminated]; 10-20% by weight of silicon dioxide; And 1-10% by weight of liquid silicone resin C comprising [siloxane and silicones, di-Me, Me vinyl, vinyl group-terminated] [Siloxanes and Silicones, di-Me, Me vinyl, vinyl group-terminated] ; And
(ii) 70-80% by weight [siloxane with silicone, di-methyl, vinyl group-terminated]; And 20-30% by weight of liquid silicone resin D comprising [siloxane and silicon, di-methyl, methyl hydrogen] in a weight ratio of 8 to 12: 1;
The third silicone coating liquid
(i) 50-59% by weight of [siloxane and silicone, di-methyl, vinyl group-terminated]; 1-5% by weight of [siloxane and silicon, di-methyl, methyl hydrogen]; And 40-45% by weight of liquid silicone resin E; And
(ii) 80-90 wt.% [siloxane with silicone, di-methyl, vinyl group-terminated]; And silicon catalyst F containing 10-20% by weight of silicon dioxide is a silicon coating liquid mixed in a weight ratio of 100: 0.1 ~ 1.0,
The first silicone coating liquid is a liquid silicone resin A and B are mixed in a weight ratio of 1: 1,
The second silicone coating liquid is a liquid silicone resin C and D are mixed in a weight ratio of 10: 1,
The third silicone coating solution is characterized in that the liquid silicone resin E and the silicon catalyst F is mixed in a weight ratio of 100: 0.3, the method of manufacturing a silicone coating fabric.
The method of claim 1, wherein the fabric is cotton, linen, Ramie, silk, rayon, wool, or synthetic fibers, the production of silicone coated fabric Way.
The method of claim 5, wherein the synthetic fiber is nylon, polyester, or acrylic.
A silicone coated fabric produced by the process of claim 1, comprising: (i) a fabric; And (ii) a first silicone coating layer on which the first silicone coating solution is cured to a thickness of 0.03 mm on the surface of the fabric, and a second silicone on which a second silicone coating solution is cured to a thickness of 0.05 mm on the surface of the first silicone coating layer. Silicone coating fabric, characterized in that the coating layer and the surface of the second silicon coating layer has a silicon coating layer sequentially coated with a third silicon coating layer cured to a thickness of 0.07mm third silicone coating liquid.
10. The silicone coated fabric of claim 8 wherein the fabric is cotton, linen, ramie, silk, rayon, wool, or synthetic fibers.