KR102061572B1 - Structure for Repairing and Reinforcing Concrete Structure1s and Its Application Method - Google Patents

Structure for Repairing and Reinforcing Concrete Structure1s and Its Application Method Download PDF

Info

Publication number
KR102061572B1
KR102061572B1 KR1020190052865A KR20190052865A KR102061572B1 KR 102061572 B1 KR102061572 B1 KR 102061572B1 KR 1020190052865 A KR1020190052865 A KR 1020190052865A KR 20190052865 A KR20190052865 A KR 20190052865A KR 102061572 B1 KR102061572 B1 KR 102061572B1
Authority
KR
South Korea
Prior art keywords
concrete structure
coupling
flame retardant
panel
epoxy resin
Prior art date
Application number
KR1020190052865A
Other languages
Korean (ko)
Inventor
윤풍식
유철주
손세현
Original Assignee
윤풍식
유철주
손세현
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤풍식, 유철주, 손세현 filed Critical 윤풍식
Priority to KR1020190052865A priority Critical patent/KR102061572B1/en
Application granted granted Critical
Publication of KR102061572B1 publication Critical patent/KR102061572B1/en

Abstract

The present invention relates to a flame retardant panel for repairing and reinforcing a concrete structure, and a construction method thereof, and more specifically, to a flame retardant panel for repairing and reinforcing a concrete structure, wherein glass fibers, aramid fibers, or carbon fibers having excellent tensile strength are immersed in a flame retardant resin to be plasticized and formed into a panel, an adhering agent is attached to a rear surface, and release paper is attached and thus, the flame retardant panel can be conveniently constructed on an old concrete structure, and to a construction method thereof. According to the present invention, materials of the flame retardant panel are similar to each other so that local deformation caused by a difference in thermal expansion coefficients is not generated, and the present invention is light weight so that an additional load is not applied to a concrete structure (1) and thus, deformation caused by the load can be prevented. The present invention has excellent weather resistance and fire resistance, thereby protecting the concrete structure (1) against a poor external environment, shows excellent durability, thereby reducing costs required to perform a repairing operation, and behaves in a completely integral manner with the concrete structure (1) by means of an anchor bolt (7) and an epoxy filling material (2b), thereby maximizing repairing and reinforcing effects on the concrete structure (1).

Description

콘크리트 구조물의 보수보강 구조물 및 그 시공방법{Structure for Repairing and Reinforcing Concrete Structure1s and Its Application Method}Structure for Repairing and Reinforcing Concrete Structures1 and Its Application Method}

본 발명은 콘크리트 구조물 보수보강용 난연패널 및 이의 시공방법에 관한 것으로, 특히 인장강도가 뛰어난 유리섬유, 아라미드 섬유, 또는 탄소섬유 등이 난연성 수지에 함침되어 패널로 소성 성형되고, 배면에 접착제가 부착되고, 이형지가 부착되어 노후 콘크리트 구조물에 시공이 편리한 콘크리트 구조물 보수보강용 난연패널 및 이의 시공방법에 관한 것이다.The present invention relates to a flame retardant panel for repair and reinforcement of a concrete structure, and a construction method thereof. In particular, glass fiber, aramid fiber, or carbon fiber having excellent tensile strength is impregnated with a flame retardant resin and plastically molded into a panel, and an adhesive is attached to the back surface. The present invention relates to a flame retardant panel for repairing and reinforcing concrete structures, which is easily installed on old concrete structures with release paper attached thereto.

일반적으로, 콘크리트 구조물은 시간 경과로 인한 노화, 재해, 설계 및 시공상의 하자, 사용변경 등 다양한 이유로 내구성, 내하력 및 콘크리트 구조물의 수명에 영향을 받으며, 구조적으로 손상된 경우에는 전면 또는 부분적인 보강조치가 요구된다.In general, concrete structures are affected by durability, load capacity and lifespan of concrete structures due to various reasons such as aging, disasters, defects in design and construction, change of use over time, and in case of structural damage, front or partial reinforcement measures Required.

따라서 상기한 콘크리트 구조물의 보수와 보강은 콘크리트 구조물의 수명을 증가시키고 안전성의 확보를 위한 필수적인 과정이 된다.Therefore, repair and reinforcement of the concrete structure is an essential process for increasing the life of the concrete structure and ensuring safety.

특히 철근 콘크리트 구조물의 경우에는 콘크리트의 중성화 또는 재료분리에 의한 박리현상, 못 또는 앵커에 의한 핀홀 및 공극, 콘크리트의 균열 등에 의하여 구조적으로 치명적인 문제가 종종 발생한다.Particularly in the case of reinforced concrete structures, structurally fatal problems are often caused by neutralization of concrete or peeling due to material separation, pinholes and voids caused by nails or anchors, and cracking of concrete.

이러한 구조적인 문제의 진행을 억제하고, 콘크리트 구조물을 보강하고자 여러 가지 보수·보강공법이 개발되고 있으며, 중요한 보강공법으로는 강판접착보강공법, 탄소섬유시트보강공법 등이 주로 사용되고 있다.In order to suppress the progress of these structural problems and to reinforce concrete structures, various repair and reinforcement methods have been developed. The important reinforcement methods are steel sheet bonding reinforcement methods and carbon fiber sheet reinforcement methods.

그러나, 강판접착보강공법은 강판의 무게가 많이 나가서 작업이 어렵고, 강판의 무게에 의한 구조물의 손상이 발생될 수 있는 문제점이 있었다.However, the steel sheet adhesion reinforcement method is difficult to work because the weight of the steel sheet is a lot, there was a problem that can damage the structure by the weight of the steel sheet.

반대로, 탄소섬유스트보강공법의 경우, 화제에 취약한 문제점이 발생되었다.On the contrary, in the case of the carbon fiber reinforcement method, a problem that is vulnerable to the topic has occurred.

따라서, 이러한 문제점을 해결할 수 있는 새로운 방법이 필요하게 되었다.Therefore, there is a need for a new method to solve this problem.

등록특허 10-0557280호,10-0557280,

본 발명은 상기의 문제점을 해결하기 위한 것으로, 기본적으로 뛰어난 인성을 가지는 경량 난연패널을 이용하여 시공함으로써, 콘크리트 구조물(1)의 지속적인 유지보수의 횟수를 감소시키며, 환경오염물질의 침투에 의한 콘크리트 구조물(1)의 손상을 방지하며, 콘크리트 구조물(1)의 미관을 손상시키지 않는 범위에서 시공할 수 있을 뿐만 아니라 시공이 편리하여 공사비용의 절감 및 공기단축이 가능하도록 한 콘크리트 구조물 보수보강용 난연패널 및 이의 시공방법을 제공함에 그 목적이 있다.The present invention is to solve the above problems, basically by using a lightweight flame retardant panel having excellent toughness, reducing the number of continuous maintenance of the concrete structure (1), concrete by the penetration of environmental pollutants Prevents damage to the structure (1), and can be installed in a range that does not damage the aesthetics of the concrete structure (1), as well as convenient construction, to reduce the construction cost and to shorten the air reinforcement for flame reinforcement for the concrete structure The purpose is to provide a panel and its construction method.

상기한 목적을 달성하기 위한 본 발명은, 유리섬유, 아라미드섬유, 또는 탄소섬유 등의 고인장 섬유 가운데 적어도 한 종류 이상이 일방향으로 고르게 분포된 섬유심(2a) 70∼80 중량%에 150℃ 이상의 고온에서 경화되는 난연성 수지가 주를 이루는 충전재(2b)가 20∼30중량% 함침되어 두께 20mm 이하, 폭 2,000mm 이하로 이루어지는 패널본체(2)와, 상기 패널본체(2)의 상면에 적층된 로빙크로스 섬유매쉬(3)와, 상기 로빙크로스 섬유매쉬(3)의 상면에 적층된 에폭시수지접착제(4)와, 상기 에폭시수지접착제(4)의 상면에 적층된 이형지(5)를 포함하는 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널이 제공된다.The present invention for achieving the above object is 150 ℃ or more to 70 to 80% by weight of the fiber core (2a) in which at least one or more kinds of high tensile fibers such as glass fibers, aramid fibers, or carbon fibers are evenly distributed in one direction A filler 2b mainly composed of a flame-retardant resin cured at a high temperature is impregnated with 20 to 30% by weight and laminated on a panel body 2 having a thickness of 20 mm or less and a width of 2,000 mm or less, and the upper surface of the panel body 2. It includes a roving cross fiber mesh (3), an epoxy resin adhesive (4) laminated on the upper surface of the roving cross fiber mesh (3), and a release paper (5) laminated on the upper surface of the epoxy resin adhesive (4). A flame retardant panel for reinforcing and reinforcing concrete structures is provided.

본 발명의 다른 특징에 따르면, 상기 충전재(2b)는 폴리에스테르수지와 비닐에스테르수지, 에폭시 수지 또는 이들의 혼합물로 이루어진 원료에 인계 난연재를 3~5중량%를 혼합하여 구성된 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널이 제공된다.According to another feature of the invention, the filler (2b) is a concrete structure, characterized in that consisting of 3 to 5% by weight of the phosphorus-based flame retardant to the raw material consisting of polyester resin, vinyl ester resin, epoxy resin or a mixture thereof Maintenance-retardant fire retardant panels are provided.

본 발명의 또 다른 특징에 따르면, 상기 패널본체(2)의 하측면에는 상호 측방향으로 이격되도록 복수개의 돌출리브(2c)가 구비된 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널이 제공된다.According to another feature of the present invention, the lower surface of the panel body 2 is provided with a flame retardant panel for reinforcing concrete structures, characterized in that a plurality of protruding ribs (2c) are provided so as to be spaced laterally apart from each other.

본 발명의 또 다른 특징에 따르면, 상기 콘크리트 구조물 보수보강용 난연패널은 다수개의 릴(61)에서 풀려나온 섬유심(2a)을 배스(62)에 저장된 충전재(2b)에 함침시키는 함침단계와, 상기 함침단계를 통과한 섬유심(2a)의 상면에 로빙크로스 섬유매쉬(3)를 적층하는 적층단계와, 로빙크로스 섬유매쉬(3)가 적층된 섬유심(2a)를 압출성형금형(64)의 성형공(64a)을 통과시켜 패널형태로 성형하는 성형단계와, 상기 성형단계를 통과한 패널을 가열하여 건조시키는 건조단계와, 상기 건조단계를 통과하여 건조된 패널을 권취롤(67a)에 권취하는 권취단계를 통해 제작되는 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널이 제공된다.According to another feature of the present invention, the concrete structure maintenance reinforcement flame retardant panel is impregnating step of impregnating the fiber core (2a) released from the plurality of reels (61) in the filler (2b) stored in the bath 62, The stacking step of laminating the roving cross fiber mesh (3) on the upper surface of the fiber core (2a) passed through the impregnation step, and the extrusion of the fiber core (2a) on which the roving cross fiber mesh (3) is laminated The molding step of passing through the molding hole (64a) of the molding to form a panel, the drying step of heating and drying the panel passed through the molding step, and the panel dried through the drying step to the take-up roll (67a) Provided is a flame retardant panel for reinforcing concrete structures, which is produced through a winding step of winding up.

본 발명의 또 다른 특징에 따르면, 시공 대상 콘크리트 구조물(1)을 치핑하는 치핑단계와, 치핑된 콘크리트 구조물(1)에 에폭시수지(D)를 충전하도록 주입관(A)과 차단판(B) 및 배출관(C)을 설치하는 설치단계와, 상기 주입관(A)을 통해 콘크리트 구조물(1)의 내부에 에폭시수지(D)를 충전하면서 배출관(C)을 에폭시수지(D)가 누출되는지를 확인하면서 에폭시수지(D)를 충전하는 충전단계와, 상기 에폭시수지(D)가 충전된 콘크리트 구조물(1)의 표면에 프라이머(E)를 도포하는 도포단계와, 상기 프라이머(E)의 표면에 4관능성 에폭시 수지인 테트라글리시딜에테르 디아미노디페닐 메탄 100중량부, 에폭시기의 경화를 위한 방향족 아민 경화제인 디아미노디페닐 메탄 20 내지 50중량부 및 에폭시 수지의 개질을 위한 열가소성 수지인 폴리에테르술폰 10 내지 30중량부로 구성된 에폭시 수지 접착제를 도포하여 접착층(F)을 형성하는 접착층형성단계와, 권취롤(67a)에 권취된 콘크리트 구조물 보수보강용 난연패널을 적절한 길이로 절단하고 상기 에폭시 수지 접착층(F)에 콘크리트 구조물 보수보강용 난연패널을 부착한 후 상기 콘크리트 구조물 보수보강용 난연패널을 앵커볼트(7)로 고정하는 고정단계와, 상기 콘크리트 구조물 보수보강용 난연패널에 형성된 돌출리브(2c)에 고정부재(69)를 결합하여 콘크리트 구조물 보수보강용 난연패널을 상호 고정하는 2차 고정단계를 포함하는 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널 시공방법이 제공된다.According to another feature of the invention, the chipping step of chipping the concrete structure (1) to be constructed, the injection pipe (A) and the blocking plate (B) to fill the epoxy resin (D) to the chipped concrete structure (1) And an installation step of installing the discharge pipe (C), and filling the epoxy resin (D) into the concrete structure (1) through the injection pipe (A) to see whether the epoxy resin (D) leaks through the discharge pipe (C). Filling step of filling the epoxy resin (D) while checking, and the coating step of applying the primer (E) to the surface of the concrete structure (1) filled with the epoxy resin (D), and the surface of the primer (E) 100 parts by weight of tetraglycidyl ether diaminodiphenyl methane, a tetrafunctional epoxy resin, 20 to 50 parts by weight of diaminodiphenyl methane, an aromatic amine curing agent for curing an epoxy group, and poly, a thermoplastic resin for modifying an epoxy resin. 10 to 30 parts by weight of ether sulfone The adhesive layer forming step of applying the configured epoxy resin adhesive to form an adhesive layer (F), and cut the flame-retardant panel for repairing the reinforced concrete structure wound to the winding roll (67a) to an appropriate length and the concrete structure on the epoxy resin adhesive layer (F) Fixing the flame retardant panel for repairing the concrete structure with an anchor bolt (7) after attaching the flame retardant panel for repairing and reinforcing, and fixing member (69) to the protruding rib (2c) formed in the flame retardant panel for repairing the concrete structure (69). There is provided a method of constructing a flame retardant panel for reinforcing concrete structures comprising a secondary fixing step of fixing the flame retardant panels for reinforcing concrete structures to each other.

본 발명의 또 다른 특징에 따르면, 상기 치핑단계에서는 콘크리트 구조물(1)의 손상부분(1a)을 파쇄하여 콘크리트 구조물(1)의 내부에 매립된 철근(6)의 부식부위가 외부 노출되도록 하고, 상기 치핑단계에서 노출된 철근(6)의 부식부위를 절단하는 절단단계와, 상기 파쇄단계에서 노출된 콘크리트 구조물(1)의 손상부분(1a)철근(6)의 표면에 부착된 이물질을 제거하는 세척단계와, 상기 절단단계에서 절단된 철근(6)에 연결구(G)를 결합하여 절단된 철근(6)을 상호 연결하는 연결단계를 더 포함하며, 상기 연결구(G)는 상기 철근(6)의 길이방향으로 연장된 관체형상으로 구성되고 길이방향으로 연장된 절단선(14)에 의해 복수개의 결합편(13)으로 분할되어 절단된 철근(6)의 외측 둘레부에 각각 결합되며 외주면에는 나사산(15)이 형성된 제1 및 제2 결합관(11,12)과, 상기 제1 및 제2 결합관(11,12)의 나사산(15)에 각각 나사결합되며 인접단에는 결합공(21a)과 상기 결합공(21a)에 나사결합되는 나사축(22a)이 각각 형성된 제1 및 제2 고정관(21,22)과, 기단부에는 상기 나사축(22a)이 관통하는 관통공(31)이 형성되어 상기 제1 및 제2 고정관(21,22)의 사이에 결합고정되는 제1 지지바(30)와, 상기 제1 지지바(30)의 선단부에 각도조절가능하게 결합되며 선단부에는 고정브라켓(41)이 형성된 제2 지지바(40)를 포함하고, 상기 결합편(13)의 내주면에는 상기 철근(6)의 둘레면에 형성된 오목홈(4)에 삽입되는 돌기(16)가 형성되고, 상기 결합편(13)의 외주면에 형성된 나사산(15)과 상기 나사축(22a)에 형성된 나사산(22b)은 동일한 피치를 갖도록 구성되며, 상기 고정브라켓(41)에는 앵커볼트(44)가 결합되는 관통공(41a)이 형성되어, 상기 관통공(41a)에 결합되는 앵커볼트(44)를 이용하여 상기 제2 지지바(40)를 콘크리트 구조물(1)의 손상부분(1a)에 고정함으로써, 상기 연결구(G)를 콘크리트 구조물(1)의 손상부분(1a)에 고정할 수 있도록 구성되며, 상기 제1 및 제2 결합관(11,12)을 이루는 결합편(13)의 전후단에는 전후방향으로 연장된 호형상의 연장부(17)가 형성되고, 상기 연장부(17)의 외측둘레부에 결합되어 상기 결합편(13)이 원통형을 이루도록 탄성적으로 가압하는 고무재질의 탄성링체(18)와, 상기 결합편(13)의 내주면에 접착고정되며 내부에는 접착제가 저장된 합성수지재질의 저장관체(50)를 더 포함하여, 상기 결합편(13)을 상기 철근(6)의 둘레면에 결합한 후, 상기 결합편(13)의 외측면을 가압하면, 상기 저장관체(50)가 가압되어 파손되면서 내부에 저장된 접착제가 유출되어, 상기 결합편(13)이 철근(6)의 둘레부에 접착고정되도록 구성된 것을 특징으로 하는 콘크리트 구조물 보수보강용 난연패널 시공방법이 제공된다.According to another feature of the present invention, in the chipping step, the damaged portion (1a) of the concrete structure (1) to fracture so that the corrosion site of the reinforcement (6) embedded in the interior of the concrete structure (1) is exposed to the outside, The cutting step of cutting the corrosion portion of the reinforcing bar 6 exposed in the chipping step, and to remove the foreign matter attached to the surface of the damaged portion (1a) of the reinforcing bar 6 of the concrete structure (1) exposed in the crushing step Further comprising a washing step and a connecting step of interconnecting the cut bar (6) by coupling the connector (G) to the cut bar (6) cut in the cutting step, the connector (G) is the reinforcing bar (6) It is composed of a tubular shape extending in the longitudinal direction of and is divided into a plurality of coupling pieces 13 by the cutting line 14 extending in the longitudinal direction is respectively coupled to the outer peripheral portion of the cut bar 6, the thread on the outer peripheral surface First and second coupling pipes (11, 12) formed with (15), The first and second coupling pipes (11, 12) of the screw thread (15), respectively, and screwed into the coupling end (21a) and the coupling hole (21a) screw holes (22a) are formed respectively Through holes 31 through which the screw shaft 22a penetrates are formed in the first and second fixing pipes 21 and 22 and the proximal end thereof, and are coupled and fixed between the first and second fixing pipes 21 and 22. A first support bar 30 and the second support bar 40 is coupled to the front end of the first support bar 30 so that the angle is adjustable and the fixing bracket 41 is formed on the front end, the coupling piece ( 13 is formed on the inner circumferential surface of the projection 16 is inserted into the concave groove 4 formed on the circumferential surface of the reinforcing bar 6, the thread 15 and the screw shaft (formed on the outer circumferential surface of the coupling piece 13) The thread 22b formed at 22a is configured to have the same pitch, and the fixing bracket 41 is formed with a through hole 41a to which the anchor bolt 44 is coupled, and is formed in the through hole 41a. By fixing the second support bar 40 to the damaged portion (1a) of the concrete structure (1) by using an anchor bolt 44, the connector (G) damaged portion (1a) of the concrete structure (1) Is configured to be fixed to, the front and rear ends of the coupling piece 13 forming the first and second coupling pipes (11, 12) is formed in the arc-shaped extension portion 17 extending in the front and rear direction, It is bonded to the outer periphery of the extension portion 17 and the elastic ring body 18 of a rubber material to elastically press the coupling piece 13 to form a cylindrical, and fixed to the inner peripheral surface of the coupling piece 13 and the inside The adhesive further comprises a storage tube 50 made of a synthetic resin material, the coupling piece 13 is coupled to the circumferential surface of the reinforcing bar 6, and then press the outer surface of the coupling piece 13, As the storage pipe 50 is damaged due to pressurization, the adhesive stored therein flows out, and the coupling piece 13 is around the reinforcing bar 6. The concrete rehabilitation method for construction retardant panel, characterized in that the adhesive is configured to be fixed and provided to.

본 발명에 따르면, 난연패널의 성분을 이루는 각각의 재질이 서로 유사하기 때문에 열팽창계수의 상이함에 기인한 국부적 변형이 발생되지 않으며, 경량이므로 콘크리트 구조물(1)에 부가적인 하중을 가하지 않으므로 하중에 따른 변형을 방지할 수 있으며, 우수한 내후성 및 내화성으로 인하여 열악한 외부환경으로부터 콘크리트 구조물(1)을 보호할 수 있으며, 내구성이 우수하여 보수작업에 소요되는 비용을 절감할 수 있을 뿐 아니라, 앵커볼트(7)와 에폭시 충전재(2b)에 의해 콘크리트 구조물(1)과 완전히 일체로 거동함으로써, 콘크리트 구조물(1)의 보수 및 보강효과가 극대화되는 장점이 있다.According to the present invention, since each material constituting the flame-retardant panel is similar to each other, no local deformation occurs due to the difference of the coefficient of thermal expansion, and because it is lightweight, no additional load is applied to the concrete structure 1, It can prevent deformation, protect the concrete structure (1) from the poor external environment due to excellent weather resistance and fire resistance, and it is excellent in durability to reduce the cost of repair work, anchor bolt (7 By fully behaving integrally with the concrete structure (1) and the epoxy filler (2b), there is an advantage that the repair and reinforcement effect of the concrete structure (1) is maximized.

도 1은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널을 도시한 정단면도,
도 2 는 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널을 제조하기 위한 난연패널 제조장치를 도시한 구성도,
도 3은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널을 제조하기 위한 난연패널 제조장치의 압출성형금형을 도시한 정면도,
도 4 및 도 5는 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널의 시험성적서
도 6 내지 도 13은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법을 도시한 참고도,
도 14 및 도 15는 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예를 도시한 참고도,
도 16은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예에 사용되는 연결구의 측단면도,
도 17은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예에 사용되는 연결구의 분해상태를 도시한 참고도,
도 18은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예에 사용되는 연결구를 도시한 평단면도,
도 19는 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예에 사용되는 연결구의 요부를 도시한 측단면도,
도 20은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널 시공방법의 제2 실시예에 사용되는 연결구의 사용방법을 도시한 참고도이다.1 is a front sectional view showing a flame retardant panel for reinforcing concrete structures according to the present invention;
Figure 2 is a block diagram showing a flame retardant panel manufacturing apparatus for manufacturing a flame retardant panel for reinforcement of concrete structures according to the present invention,
Figure 3 is a front view showing an extrusion molding of a flame retardant panel manufacturing apparatus for manufacturing a flame retardant panel for repairing concrete structures according to the present invention,
4 and 5 is a test report of the flame retardant panel for repairing concrete structures according to the present invention
6 to 13 is a reference diagram showing a method for constructing a flame retardant panel for repairing concrete structures according to the present invention;
14 and 15 is a reference diagram showing a second embodiment of the construction method of the flame retardant panel for reinforcement of concrete structures according to the present invention,
16 is a side cross-sectional view of the connector used in the second embodiment of the method for constructing a flame retardant panel for repairing concrete structures according to the present invention;
17 is a reference diagram showing an exploded state of the connector used in the second embodiment of the method of constructing a flame retardant panel for repairing concrete structures according to the present invention;
18 is a plan sectional view showing the connector used in the second embodiment of the method of constructing a flame retardant panel for reinforcing concrete structures according to the present invention;
Figure 19 is a side cross-sectional view showing the main portion of the connector used in the second embodiment of the method of constructing a flame retardant panel for repairing concrete structures according to the present invention;
20 is a reference diagram showing a method of using the connector used in the second embodiment of the method for constructing a flame retardant panel for repairing concrete structures according to the present invention.

이하, 본 발명을 첨부된 예시도면에 의거하여 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널을 도시한 것으로, 패널본체(2)와, 상기 패널본체(2)의 상면에 적층된 로빙크로스 섬유매쉬(3)와, 상기 로빙크로스 섬유매쉬(3)의 상면에 적층된 에폭시수지접착제(4)와, 상기 에폭시수지접착제(4)의 상면에 적층된 이형지(5)로 구성된다.1 illustrates a flame retardant panel for reinforcing concrete structures according to the present invention, a panel body 2, a roving cross fiber mesh 3 laminated on an upper surface of the panel body 2, and the roving cross fiber It consists of the epoxy resin adhesive 4 laminated | stacked on the upper surface of the mesh 3, and the release paper 5 laminated | stacked on the upper surface of the said epoxy resin adhesive 4.

상기 패널본체(2)는 유리섬유, 아라미드섬유, 또는 탄소섬유 등의 고인장 섬유 가운데 적어도 한 종류 이상이 일방향으로 고르게 분포된 섬유심(2a) 70∼80 중량%에 150℃ 이상의 고온에서 경화되는 난연성 수지가 주를 이루는 충전재(2b)가 20∼30중량% 함침되어 두께 20mm 이하, 폭 2,000mm 이하로 이루어진다.The panel body 2 is cured at a high temperature of 150 ° C. or higher to 70 to 80 wt% of fiber cores 2a having at least one kind of high tensile fibers such as glass fibers, aramid fibers, or carbon fibers evenly distributed in one direction. The filler 2b, which is mainly composed of flame retardant resin, is impregnated with 20 to 30% by weight, and has a thickness of 20 mm or less and a width of 2,000 mm or less.

이때, 상기 충전재(2b)는 폴리에스테르수지와 비닐에스테르수지, 에폭시 수지 또는 이들의 혼합물로 이루어진 원료에 인계 난연재를 3~5중량%를 혼합하여 구성된다.At this time, the filler (2b) is composed of 3 to 5% by weight of the phosphorus-based flame retardant mixed with a raw material consisting of a polyester resin, a vinyl ester resin, an epoxy resin or a mixture thereof.

그리고, 상기 패널본체(2)의 하측면에는 상호 측방향으로 이격되도록 복수개의 돌출리브(2c)가 구비되어, 상기 패널본체(2)의 강도를 보강도록 구성된다.The lower surface of the panel body 2 is provided with a plurality of protruding ribs 2c so as to be laterally spaced apart from each other, so as to reinforce the strength of the panel body 2.

상기 에폭시수지접착제(4)는 4관능성 에폭시 수지인 테트라글리시딜 에테르 디아미노디페닐 메탄 100중량부, 에폭시기의 경화를 위한 방향족 아민 경화제인 디아미노디페닐 메탄 20 내지 50중량부 및 에폭시 수지의 개질을 위한 열가소성 수지인 폴리에테르술폰 10 내지 30중량부로 구성된다.The epoxy resin adhesive (4) is 100 parts by weight of tetraglycidyl ether diaminodiphenyl methane, a tetrafunctional epoxy resin, 20 to 50 parts by weight of diaminodiphenyl methane, an aromatic amine curing agent for curing an epoxy group, and an epoxy resin. It consists of 10 to 30 parts by weight of a polyether sulfone which is a thermoplastic resin for modification of the.

상기 이형지(5)는 폴리에틸렌필름을 이용한다.The release paper 5 uses a polyethylene film.

도 2 및 도 3은 이와 같이 구성된 상기 콘크리트 구조물 보수보강용 난연패널을 제조하는 난연패널 제조장치를 도시한 것으로, 둘레면에 상기 섬유심(2a)이 권취된 다수개의 릴(61)과, 상기 릴(61)의 후방에 구비되며 충전재(2b)가 저장된 배스(62)와, 상기 배수의 후방에 구비되며 상기 배스(62)를 통과한 섬유심(2a)의 상면에 로빙크로스 섬유매쉬(3)를 공급하는 로빙크로스 섬유매쉬공급롤(63)과, 상기 로빙크로스 섬유매쉬공급롤(63)의 후방에 구비되며 상기 콘크리트 구조물 보수보강용 난연패널의 단면형상에 대응되는 성형공(64a)이 전후면을 관통하도록 형성된 압출성형금형(64)과, 상기 압출성형금형(64)의 후방에 구비된 건조기(65)와, 상기 건조기(65)의 후방에 구비된 이송로울러(66)와, 상기 이송로울러(66)의 후방에 구비되며 권취롤(67a)이 구비된 권취기(67)와, 상기 이송로울러(66)와 권취기(67)의 사이에 구비된 절단기(68)로 구성된다.2 and 3 illustrate a flame-retardant panel manufacturing apparatus for manufacturing a flame-retardant panel for repairing the concrete structure configured as described above, a plurality of reels 61 wound around the fiber core (2a), and the A roving cross fiber mesh 3 provided on the rear surface of the reel 61 and provided with a bath 62 in which a filler 2b is stored, and an upper surface of the fiber core 2a provided in the rear of the drainage and passed through the bath 62. Roving cross fiber mesh supply roll 63 for supplying a) and a molding hole 64a provided at the rear of the roving cross fiber mesh supply roll 63 and corresponding to the cross-sectional shape of the flame retardant panel for repairing the concrete structure are provided. An extruded mold 64 formed to penetrate the front and rear surfaces, a dryer 65 provided at the rear of the extruded mold 64, a transfer roller 66 provided at the rear of the dryer 65, and Winding machine 67 provided at the rear of the transfer roller 66 and provided with a winding roll 67a. , Consists of a cutter 68 is provided between the transfer roller 66 and the winder (67).

상기 압출성형금형(64)의 성형공(64a)은 도 3에 도시한 바와 같이, 상기 콘크리트 구조물 보수보강용 난연패널의 패널본체(2)의 단면형상과 동일하게 구성된다.As shown in FIG. 3, the molding hole 64a of the extrusion mold 64 is configured in the same manner as the cross-sectional shape of the panel body 2 of the flame retardant panel for repairing the concrete structure.

이와 같이 구성된 난연패널 제조장치를 이용하여 콘크리트 구조물 보수보강용 난연패널을 제조하는 방법을 설명하면 다음과 같다.Referring to the method of manufacturing a flame retardant panel for reinforcement of a concrete structure using the apparatus for manufacturing a flame retardant panel configured as described above is as follows.

우선 상기 릴(61)에서 풀려나온 섬유심(2a)은 상기 배스(62)를 통과하면서 배스(62)에 저장된 충전재(2b)에 함침되어 섬유심(2a)의 둘레부레 충전재(2b)가 부착되도록 한다.First, the fiber core 2a released from the reel 61 is impregnated into the filler 2b stored in the bath 62 while passing through the bath 62 so that the perimeter filler 2b of the fiber core 2a is attached. Be sure to

그리고, 이와 같이 충전재(2b)가 부착된 섬유심(2a)가 상기 로빙크로스 섬유매쉬공급롤(63)의 하측을 통과하면, 상기 로빙크로스 섬유매쉬공급롤(63)에서 풀려나온 로빙크로스 섬유매쉬가 섬유심(2a)의 상면에 적층된다.Then, when the fiber core 2a having the filler 2b attached passes through the lower side of the roving cross fiber mesh supply roll 63, the roving cross fiber mesh released from the roving cross fiber mesh supply roll 63. Is laminated on the upper surface of the fiber core 2a.

그리고, 로빙크로스 섬유매쉬(3)가 적층된 섬유심(2a)은 상기 압출성형금형(64)의 성형공(64a)을 통과하면서 패널형태로 성형되고, 이와 같이 성형된 패널은 상기 건조기(65)를 통과하면서 건조된다.In addition, the fiber core 2a on which the roving cross fiber mesh 3 is laminated is formed into a panel while passing through the molding hole 64a of the extrusion molding 64, and the panel thus formed is the dryer 65. Dried).

그리고, 이와 같이 건조된 패널은 상기 권취기(67)에 권취되어 롤형태로 감기게 되며, 일정길이의 패널이 상기 권취기(67)의 권취롤(67a)에 감기면, 상기 절단기(68)를 이용하여 패널을 절단함으로써, 콘크리트 구조물 보수보강용 난연패널을 제조할 수 있다.Then, the dried panel is wound on the winding machine 67 and wound in a roll form, and when the panel of a predetermined length is wound on the winding roll 67a of the winding machine 67, the cutter 68 By cutting the panel using, it is possible to manufacture a flame retardant panel for reinforcement of concrete structures.

한편, 상기 로빙크로스 섬유매쉬(3)의 상면에 적층된 에폭시수지접착제(4)와, 상기 에폭시수지접착제(4)의 상면에 적층된 이형지(5)는 상기 건조기(65)를 통과한 패널의 상면에 별도의 도포수단과 공급장치를 이용하여 적층할 수 있으며, 필요에 따라, 에폭시수지접착제(4)와 이형지(5)는 생략될 수 있다.On the other hand, the epoxy resin adhesive (4) laminated on the upper surface of the roving cross fiber mesh (3), and the release paper (5) laminated on the upper surface of the epoxy resin adhesive (4) of the panel passed through the dryer (65) The upper surface may be laminated using a separate coating means and a supply device, and, if necessary, the epoxy resin adhesive 4 and the release paper 5 may be omitted.

그리고, 이와 같이 제조된 콘크리트 구조물 보수보강용 난연패널은 상기 권취롤(67a)에 권취된 상태로 보관 및 운반된다.In addition, the flame-retardant panel for repair and reinforcement of the concrete structure manufactured as described above is stored and transported in a wound state on the winding roll 67a.

이와 같이 구성된 콘크리트 구조물 보수보강용 난연패널의 시공방법을 설명하면 다음과 같다.Referring to the construction method of the flame-retardant panel for reinforcement of concrete structures configured as described above are as follows.

우선, 도 6에 도시한 바와 같이, 콘크리트 구조물(1)에 손상이 발생되면, 콘크리트 구조물(1)의 손상범위에 비해 넓은 면적의 콘크리트 구조물 보수보강용 난연패널을 제조한다.First, as shown in Figure 6, when the damage occurs in the concrete structure (1), to produce a flame retardant panel for repairing and strengthening the concrete structure of a large area compared to the damage range of the concrete structure (1).

그리고, 도 7에 도시한 바와 같이, 콘크리트 구조물(1)의 손상부분(1a)을 치핑함으로써, 즉, 손상부분(1a)의 표면을 넓게 깍아냄으로써, 콘크리트구조물(1)의 열화된 부분을 제거한다.As shown in FIG. 7, the deteriorated portion of the concrete structure 1 is removed by chipping the damaged portion 1a of the concrete structure 1, that is, by shaving the surface of the damaged portion 1a widely. do.

이때, 콘크리트구조물(1)의 철근(6)이 드러날 경우, 드러난 철근(6)에 발생된 녹을 함께 제거한 후, 철근(6)부위에 아초산염 처리를 한 후, 방청모르타르를 도포함으로써, 철근(6)에 부식이 발생되는 것을 방지한다.At this time, when the reinforcing bars 6 of the concrete structure 1 are exposed, the rust generated in the exposed reinforcing bars 6 is removed together, the acetic acid treatment is performed on the reinforcing bars 6 and the anti-rust mortar is applied to the reinforcing bars ( 6) to prevent corrosion.

그리고, 도 8에 도시한 바와 같이, 치핑된 콘크리트 구조물(1)에 주입관(A)과 차단판(B) 및 배출관(C)을 설치하여, 에폭시수지를 주입할 수 있는 준비를 마친다.Then, as shown in Figure 8, the injection pipe (A), the blocking plate (B) and the discharge pipe (C) is installed in the chipped concrete structure (1), the epoxy resin is ready to inject.

그리고, 주입관(A)과 차단판(B) 및 배출관(C)의 설치가 완료되면, 작업자는 도 9에 도시한 바와 같이, 상기 주입관(A)을 통해 콘크리트 구조물(1)의 손상부분(1a)의 내부에 에폭시수지(D)를 충전한다.And, when the installation of the injection pipe (A) and the blocking plate (B) and the discharge pipe (C) is completed, the worker is damaged portion of the concrete structure (1) through the injection pipe (A), as shown in FIG. The epoxy resin (D) is filled in the inside of (1a).

이때, 작업자는 상기 배출관(C)을 통해 에폭시수지(D)가 누출되는지를 확인하면서 에폭시수지(D)를 충전한다.At this time, the worker fills the epoxy resin (D) while checking whether the epoxy resin (D) leaks through the discharge pipe (C).

그리고, 도 10에 도시한 바와 같이, 상기 에폭시수지(D)가 충전된 콘크리트 구조물(1)의 표면에 프라이머(E)를 도포한다.And, as shown in Figure 10, the primer (E) is applied to the surface of the concrete structure (1) filled with the epoxy resin (D).

상기 프라이머(E)는 우레탄 아크릴레이트 수지와 폴리메틸 메타크릴레이트 수지가 10~60:90~40 중량 비율로 혼합된 우레탄수지 혼합물 70∼90중량%와 라텍스수지 10∼30%로 구성된다The primer (E) comprises a urethane acrylate resin and a polymethyl methacrylate resin 70 to 90% by weight and 10 to 30% of a latex resin mixture of 10 to 60:90 to 40 weight ratio

그리고, 상기 프라이머(E)가 경화되면, 도 11에 도시한 바와 같이, 상기 프라이머(E)의 표면에 에폭시 수지 접착제를 도포하여 접착층(F)을 형성한다.And, when the primer (E) is cured, as shown in Figure 11, by applying an epoxy resin adhesive on the surface of the primer (E) to form an adhesive layer (F).

상기 접착층(F)에 사용되는 에폭시 수지 접착제는 4관능성 에폭시 수지인 테트라글리시딜에테르 디아미노디페닐 메탄 100중량부, 에폭시기의 경화를 위한 방향족 아민 경화제인 디아미노디페닐 메탄 20 내지 50중량부 및 에폭시 수지의 개질을 위한 열가소성 수지인 폴리에테르술폰 10 내지 30중량부로 구성된다.The epoxy resin adhesive used for the adhesive layer (F) is 100 parts by weight of tetraglycidyl ether diaminodiphenyl methane which is a tetrafunctional epoxy resin, 20 to 50 weight of diaminodiphenyl methane which is an aromatic amine curing agent for curing an epoxy group. Part and 10 to 30 parts by weight of a polyether sulfone which is a thermoplastic resin for modification of the epoxy resin.

이때, 상기 에폭시 수지 접착제는 상기 콘크리트 구조물(1)의 손상부분(1a)에 비해 넓게 도포된다.At this time, the epoxy resin adhesive is widely applied than the damaged portion (1a) of the concrete structure (1).

그리고, 작업자는 상기 권취롤(67a)에 권취된 콘크리트 구조물 보수보강용 난연패널을 적절한 길이로 절단한 후, 콘크리트 구조물 보수보강용 난연패널에 부착된 이형지(5)를 제거한 후, 도 12에 도시한 바와 같이, 콘크리트 구조물 보수보강용 난연패널을 상기 접착층(F)에 접착하고, 앵커볼트(7)를 이용하여 콘크리트 구조물 보수보강용 난연패널을 고정한다. Then, after the worker cuts the concrete structure maintenance reinforcement flame retardant panel wound on the winding roll (67a) to an appropriate length, after removing the release paper (5) attached to the concrete structure maintenance reinforcement flame retardant panel, shown in Figure 12 As described above, the flame retardant panel for repairing concrete structures is bonded to the adhesive layer (F), and the flame retardant panel for repairing concrete structures is fixed using an anchor bolt (7).

이때, 상기 손상부분(1a)의 면적이 넓을 경우, 도 13에 도시한 바와 같이, 복수개의 콘크리트 구조물 보수보강용 난연패널을 측면이 상호 근접되도록 고정한다.At this time, when the area of the damaged portion (1a) is large, as shown in Figure 13, a plurality of concrete structure repair reinforcement flame retardant panel is fixed so that the sides are close to each other.

그리고, 상기 콘크리트 구조물 보수보강용 난연패널에 형성된 돌출리브(2c)에 고정부재(69)를 결합하고, 앵커볼트(7)를 이용하여 상기 고정부재(69)를 고정함으로써, 콘크리트 구조물 보수보강용 난연패널의 설치를 완료한다.In addition, the fixing member 69 is coupled to the protruding rib 2c formed on the flame retardant panel for repairing the concrete structure, and the fixing member 69 is fixed by using the anchor bolt 7 to repair the concrete structure. Complete the installation of the flame retardant panels.

상기 고정부재(69)는 상기 콘크리트 구조물 보수보강용 난연패널과 동일한 재질로 구성된 것으로, 상기 돌출리브(2c)가 삽입되는 오목홈(69a)이 형성되어, 상호 근접되도록 배치된 콘크리트 구조물 보수보강용 난연패널의 양측에 형성된 돌출리브(2c)를 덮도록 상기 고정부재(69)를 결합하면, 인접된 콘크리트 구조물 보수보강용 난연패널의 측면이 상호 고정된다.The fixing member 69 is made of the same material as the flame retardant panel for reinforcement of the concrete structure, and the concave groove 69a into which the protruding ribs 2c are inserted is formed, and the reinforcement for the concrete structure disposed to be in close proximity to each other. When the fixing member 69 is coupled to cover the protruding ribs 2c formed on both sides of the flame retardant panel, the side surfaces of adjacent concrete structure repair reinforcement flame retardant panels are fixed to each other.

이와 같이 구성된 콘크리트 구조물 보수보강용 난연패널은 패널본체(2)의 성분을 이루는 각각의 재질이 서로유사하기 때문에 열팽창계수의 상이함에 기인한 국부적 변형이 발생되지 않으며, 경량이므로 콘크리트 구조물(1)에 부가적인 하중을 가하지 않으므로 하중에 따른 변형을 방지하는 장점이 있다.As the flame-retardant panels for reinforcing and reinforcing concrete structures configured as described above are similar to each other, each component constituting the panel body 2 does not generate local deformation due to the difference of the coefficient of thermal expansion. Since no additional load is applied, there is an advantage of preventing deformation due to the load.

또한, 상기 패널본체(2)는 난연성 수지의 일반적인 특성에 따른 우수한 내후성 및 내화성으로 인하여 열악한 외부환경으로부터 콘크리트 구조물(1)을 보호할 수 있으며, 내구성이 우수하여 보수작업에 소요되는 비용을 절감하는 장점이 있다.In addition, the panel body (2) can protect the concrete structure (1) from poor external environment due to the excellent weather resistance and fire resistance according to the general characteristics of the flame-retardant resin, and excellent durability to reduce the cost of repair work There is an advantage.

특히, 상기 패널본체(2)는 난연성 수지조성물로 유리섬유를 함침시켜 콘크리트 구조물(1) 보강용 패널을 제조시 접착력 및 경도 등의 콘크리트 구조물(1) 보강용패널에 필요한 물성을 유지하면서도 화재시 유독성 가스가 발생되지 아니하므로 귀중한 인명의 손실 및 막대한 재산상의 손실을 방지할 수 있는 효과가 있다.In particular, the panel body (2) is impregnated with glass fibers in a flame-retardant resin composition when manufacturing the concrete structure (1) reinforcement panel while maintaining the properties required for the concrete structure (1) reinforcement panel, such as adhesive strength and hardness in case of fire Since no toxic gas is generated, it has the effect of preventing the loss of valuable lives and the enormous loss of property.

그리고, 본 발명에 따른 콘크리트 구조물 보수보강용 난연패널에 따르면, 앵커볼트(7)와 에폭시 충전재(2b)에 의해 콘크리트 구조물(1)과 완전히 일체로 거동함으로써, 콘크리트 구조물(1)의 보수 및 보강효과가 극대화될 뿐 아니라, 시공이 용이하며, 공사기간을 단축할 수 있으며, 공사비용을 절감할 수 있는 장점이 있다.In addition, according to the flame retardant panel for repair and reinforcement of the concrete structure according to the present invention, the anchor bolt (7) and the epoxy filler (2b) by fully acting integrally with the concrete structure (1), repair and reinforcement of the concrete structure (1) In addition to maximizing the effect, it is easy to construct, can shorten the construction period, and has the advantage of reducing the construction cost.

또한, 난연패널의 접착제로 콘크리트 구조물(1)의 접착제와 동일한 물성의 에폭시 수지가 사용됨으로, 난연패널의 내충격성이 향상되고, 콘크리트 구조물(1)과의 부착력이 증대되는 이점이 있다.In addition, since the epoxy resin of the same physical properties as the adhesive of the concrete structure 1 is used as the adhesive of the flame-retardant panel, the impact resistance of the flame-retardant panel is improved, and the adhesion to the concrete structure 1 is increased.

그리고, 콘크리트 구조물(1)에 발생된 손상부분(1a)의 내부를 에폭시수지(D)로 충전한 후, 그 표면을 난연패널을 부착하여 시공함으로써 시공부위의 크기나 형상 그리고 균열정도에 맞춰 간편하게 시공할 수 있는 이점이 있다.Then, after filling the interior of the damaged part (1a) generated in the concrete structure (1) with epoxy resin (D), the surface is attached to the flame retardant panel to be installed to easily fit the size, shape and cracking of the construction site There is an advantage that can be constructed.

도 14 내지 도 20은 본 발명에 따른 다른 실시예를 도시한 것으로, 상기 치핑단계에서 콘크리트 구조물(1)의 내부에 매립된 철근(6)의 부식부위가 외부 노출될 경우, 도 14에 도시한 바와 같이, 상기 치핑단계에서 노출된 철근(6)의 부식부위를 절단하는 절단한 후, 상기 파쇄단계에서 노출된 콘크리트 구조물(1)의 손상부분(1a)과 철근(6)의 표면에 부착된 이물질을 제거하고, 도 15에 도시한 바와 같이, 절단된 철근(6)에 연결구(G)를 결합하여 절단된 철근(6)을 상호 연결함으로써, 철근(6)을 보강하는 과정이 더 추가된다.14 to 20 show another embodiment according to the present invention. In the chipping step, the corrosion site of the reinforcing bar 6 embedded in the concrete structure 1 is exposed to the outside. As described above, after cutting the corroded portion of the rebar (6) exposed in the chipping step, attached to the damaged portion (1a) and the surface of the reinforcement (6) of the concrete structure (1) exposed in the fracture step 15, the process of reinforcing the reinforcing bar 6 is further added by interconnecting the cut bar 6 by connecting the connector G to the cut bar 6 as shown in FIG. 15. .

상기 철근(6)의 부식부위를 절단할 때는 상기 철근(6)을 톱이나 절단기(68)를 이용하여 절단한다.When cutting the corrosion part of the reinforcing bar 6, the reinforcing bar 6 is cut using a saw or a cutter (68).

그리고, 구조물(1)의 손상부분(1a)과 철근(6)의 표면에 부착된 이물질을 제거할 때는, 샌드블라스터를 이용하여 상기 파쇄단계에서 노출된 콘크리트 구조물(1)의 손상부분(1a)과 철근(6)의 표면에 고속으로 모래를 분사함으로써, 콘크리트의 손상부분(1a)과 철근(6)의 표면에 남은 이물질 또는 콘크리트의 잔해 등을 1차 제거한 후, 상기 파쇄단계에서 노출된 콘크리트 구조물(1)의 손상부분(1a)과 철근(6)의 표면에 물을 고압으로 분사함으로써 이물질을 2차 제거하고, 물이 완전히 건조된 후 철근(6)의 둘레면에 방청 코팅제를 도포하여 방청한다.And, when removing the foreign matter attached to the surface of the damaged portion (1a) and the reinforcing bar 6 of the structure (1), the damaged portion (1a) of the concrete structure (1) exposed in the crushing step using a sandblasting machine By spraying sand at the surface of the reinforcing bar 6 at high speed, the foreign matter remaining on the surface of the concrete portion 1a and the reinforcing bar 6 or the debris of the concrete, etc. are first removed, and then the concrete exposed in the crushing step. By spraying water on the damaged part 1a of the structure 1 and the surface of the reinforcing bar 6 at a high pressure, foreign matters are secondarily removed, and after the water is completely dried, an antirust coating is applied to the circumferential surface of the reinforcing bar 6 Listen.

그리고, 절단된 철근(6)을 상호 연결하는데 사용되는 연결구(G)는 도 16 내지 도 20에 도시한 바와 같이, 상기 철근(6)의 길이방향으로 연장된 관체형상으로 구성되고 길이방향으로 연장된 절단선(14)에 의해 복수개의 결합편(13)으로 분할되어 절단된 철근(6)의 외측 둘레부에 각각 결합되며 외주면에는 나사산(15)이 형성된 제1 및 제2 결합관(11,12)과, 상기 제1 및 제2 결합관(11,12)의 나사산(15)에 각각 나사결합되며 인접단에는 결합공(21a)과 상기 결합공(21a)에 나사결합되는 나사축(22a)이 각각 형성된 제1 및 제2 고정관(21,22)과, 기단부에는 상기 나사축(22a)이 관통하는 관통공(31)이 형성되어 상기 제1 및 제2 고정관(21,22)의 사이에 결합고정되는 제1 지지바(30)와, 상기 제1 지지바(30)의 선단부에 각도조절가능하게 결합되며 선단부에는 고정브라켓(41)이 형성된 제2 지지바(40)로 구성된다.And, the connector (G) used to interconnect the cut reinforcement (6) is composed of a tubular shape extending in the longitudinal direction of the reinforcement (6), as shown in Figure 16 to 20 and extend in the longitudinal direction The first and second coupling pipes 11, each of which is divided into a plurality of coupling pieces 13 by the cut lines 14 and is coupled to the outer periphery of the reinforcing bar 6, and the threads 15 are formed on the outer circumferential surface thereof. 12 and screw shafts 22a screwed to the threaded portions 15 of the first and second coupling pipes 11 and 12, respectively, and coupled to the coupling holes 21a and the coupling holes 21a at adjacent ends thereof. ) And first and second fixing tubes 21 and 22, respectively, and a protruding hole 31 through which the screw shaft 22a penetrates is formed at the proximal end thereof, so as to provide a gap between the first and second fixing tubes 21 and 22, respectively. A first support bar 30 coupled to and fixed to the second end so as to be angularly adjustable at the front end of the first support bar 30 and having a fixing bracket 41 formed at the front end; It consists of Chiba 40.

상기 제1 및 제2 결합관(11,12)은 강도가 높은 금속재로 구성된다.The first and second coupling pipes 11 and 12 are made of metal having high strength.

상기 결합편(13)은 상기 제1 및 제2 결합관(11,12)을 2개로 분할한 형태로 구성되며, 내주면에는 상기 철근(6)의 둘레면에 형성된 오목홈(4)에 삽입되는 돌기(16)가 형성된다.The coupling piece 13 is configured by dividing the first and second coupling pipes 11 and 12 into two, and the inner peripheral surface is inserted into the concave groove 4 formed in the circumferential surface of the reinforcing bar 6. The projection 16 is formed.

즉, 일반적인 건축물에 사용되는 철근(6)은 둘레면에 오목홈(4)이 일정간격으로 형성된 이형철근(6)을 이용하는데, 결합편(13)의 내주면에는 상기 철근(6)의 오목홈(4)에 대응되는 간격으로 돌기(16)가 형성되어, 상기 결합편(13)을 철근(6)의 둘레면에 결합하면, 상기 돌기(16)가 상기 오목홈(4)에 삽입되어 결합편(13)이 철근(6)의 외측에 약간의 유격을 갖도록 고정된다.That is, the reinforcing bar 6 used in a general building uses a deformed steel bar 6 having concave grooves 4 formed on the circumferential surface at regular intervals, and the concave groove of the bar 6 on the inner circumferential surface of the coupling piece 13. When the projections 16 are formed at intervals corresponding to (4), and the coupling pieces 13 are coupled to the circumferential surface of the reinforcing bar 6, the projections 16 are inserted into the concave grooves 4 and engaged. The piece 13 is fixed to have a little play on the outside of the reinforcing bar 6.

그리고, 도 17 및 도 18에 도시한 바와 같이, 결합편(13)의 전후단에는 전후방향으로 연장된 호형상의 연장부(17)가 형성되고, 상기 연장부(17)의 외측둘레부에는 상기 결합편(13)이 원통형을 이루도록 탄성적으로 가압하는 고무재질의 탄성링체(18)가 결합된다.17 and 18, an arc-shaped extension portion 17 extending in the front-rear direction is formed at the front and rear ends of the engaging piece 13, and the outer peripheral portion of the extension portion 17 An elastic ring body 18 made of a rubber material that is elastically pressurized to form the coupling piece 13 has a cylindrical shape.

또한, 도 19에 도시한 바와 같이, 상기 결합편(13)의 내주면에는 내부에는 접착제가 저장된 합성수지재질의 저장관체(50)가 접착고정되어, 상기 접착제의 접착력에 의해 상기 결합편(13)이 상기 철근(6)의 둘레면에 고정되도록 구성된다.In addition, as shown in Figure 19, the inner circumferential surface of the coupling piece 13 is fixed to the storage tube 50 made of a synthetic resin material stored therein adhesive, the coupling piece 13 by the adhesive force of the adhesive It is configured to be fixed to the circumferential surface of the reinforcing bar (6).

이를 위해, 상기 저장관체(50)는 취성이 높은 합성수지재질로 구성되며, 상기 결합편(13)의 외측단, 즉, 상기 제1 및 제2 결합관(11,12)의 인접단의 반대쪽에 위치되도록 구비된다.To this end, the storage tube 50 is made of a synthetic resin material of high brittleness, the outer end of the coupling piece 13, that is, opposite to the adjacent ends of the first and second coupling pipe (11, 12) It is provided to be positioned.

이때, 상기 접착제는 금속을 상호 접착고정할 수 있는 접착력이 강한 것을 이용한다.At this time, the adhesive uses a strong adhesive force capable of bonding the metal to each other.

따라서, 도 18의 (a)와 도 19에 도시한 바와 같이, 상기 결합편(13)을 벌려 상기 철근(6)의 외측에 결합하면, 상기 탄성링체(18)의 탄성에 의해 결합편(13)이 상호 인접방향으로 가압되어, 도 18의 (b)와 도 16에 도시한 바와 같이, 철근(6)의 외측에 결합된다.Therefore, as shown in FIGS. 18A and 19, when the coupling piece 13 is opened and coupled to the outside of the reinforcing bar 6, the coupling piece 13 is caused by the elasticity of the elastic ring body 18. ) Are pressed in mutually adjacent directions, and are coupled to the outside of the reinforcing bar 6 as shown in FIGS. 18B and 16.

이때, 상기 철근(6)의 둘레면에 결합된 결합편(13)의 외측면을 가압하면, 상기 저장관체(50)가 가압되어 파손되면서 내부에 저장된 접착제가 유출되어, 상기 결합편(13)이 철근(6)의 둘레부에 접착고정된다.At this time, when pressing the outer surface of the coupling piece 13 coupled to the circumferential surface of the reinforcing bar 6, the storage pipe 50 is pressed and damaged while the adhesive stored therein flows out, the coupling piece 13 Adhesively fixed to the periphery of this reinforcing bar 6.

상기 제1 및 제2 고정관(21,22)은 도 15에 도시한 바와 같이, 외주면이 육각형의 단면형상으로 구성된 금속재질의 관체형상으로 구성된다.As shown in FIG. 15, the first and second fixing pipes 21 and 22 have a tubular shape of a metal material having an outer circumferential surface formed in a hexagonal cross-sectional shape.

이때, 상기 나사축(22a)은 상기 제2 고정관(22)의 단부에 상기 제1 고정관(21)쪽으로 연장되도록 구비되며, 상기 결합공(21a)은 상기 제1 고정관(21)의 단부에 형성된다.In this case, the screw shaft (22a) is provided to extend toward the first fixing tube 21 at the end of the second fixing tube 22, the coupling hole (21a) is formed at the end of the first fixing tube (21) do.

그리고, 상기 결합편(13)의 외주면에 형성된 나사산(15)과 상기 나사축(22a)에 형성된 나사산(22b)은 동일한 피치를 갖는 우나사로 구성된다.The screw thread 15 formed on the outer circumferential surface of the coupling piece 13 and the screw thread 22b formed on the screw shaft 22a are constituted by a right screw having the same pitch.

상기 제1 지지바(30)는 강도가 높은 금속재질의 판형상으로 구성된다.The first support bar 30 is formed in a plate shape of a high strength metal material.

상기 제2 지지바(40)는 기단부를 관통하도록 결합된 고정볼트(42)에 의해 상기 제1 지지바(30)의 선단부에 측방향으로 회동가능하게 결합된다.The second support bar 40 is rotatably coupled laterally to the front end of the first support bar 30 by a fixing bolt 42 coupled to penetrate the proximal end.

이때, 상기 고정볼트(42)에는 너트(43)가 결합되어, 상기 제2 지지바(40)를 회동시켜 각도를 조절한 후, 상기 고정볼트(42)와 너트(43)를 조여, 제2 지지바(40)가 움직이지 않도록 고정할 수 있다.At this time, the nut 43 is coupled to the fixing bolt 42, the second support bar 40 is rotated to adjust the angle, and then tighten the fixing bolt 42 and the nut 43, the second The support bar 40 can be fixed so as not to move.

그리고, 상기 고정브라켓(41)에는 앵커볼트(44)가 결합되는 관통공(41a)이 형성되어, 상기 관통공(41a)에 결합된 앵커볼트(44)에 의해 상기 콘크리트 구조물(1)의 손상부분(1a)에 고정결합된다.In addition, the fixing bracket 41 is formed with a through hole 41a to which the anchor bolt 44 is coupled, and the damage of the concrete structure 1 by the anchor bolt 44 coupled to the through hole 41a. It is fixedly coupled to the portion 1a.

이와 같이 구성된 연결구(G)를 설치하는 방법을 설명하면 다음과 같다.Referring to the method of installing the connector (G) configured as described above are as follows.

우선, 전술한 바와 같이, 도 20에 도시한 바와 같이, 상기 제1 결합관(11)과 제2 결합관(12)을 절단된 철근(6)의 양단에 각각 결합하고, 상기 제1 결합관(11)과 제2 결합관(12)의 외측에 상기 제1 및 제2 고정관(21,22)을 각각 나사결합한다.First, as described above, as shown in FIG. 20, the first coupling pipe 11 and the second coupling pipe 12 are respectively coupled to both ends of the cut bar 6, and the first coupling pipe The first and second fixing pipes 21 and 22 are screwed to the outside of the 11 and the second coupling pipe 12, respectively.

그리고, 상기 제1 결합관(11)의 나사축(22a)에 상기 제1 지지바(30)의 기단부에 형성된 관통공(31)을 결합한 후, 상기 제1 및 제2 결합관(11,12)을 반대방향으로 회전시켜 상호 인접방향으로 전진되도록 하면, 도 16에 도시한 바와 같이, 상기 나사축(22a)이 상기 결합공(21a)에 결합된다.Then, after coupling the through-hole 31 formed in the proximal end of the first support bar 30 to the screw shaft (22a) of the first coupling pipe 11, the first and second coupling pipe (11, 12) ) Is rotated in the opposite direction to advance in the mutually adjacent direction, as shown in Figure 16, the screw shaft 22a is coupled to the coupling hole (21a).

그리고, 상기 제1 및 제2 결합관(11,12)을 강하게 조여 결합하면, 상기 제1 지지바(30)가 상기 제1 및 제2 결합관(11,12)의 사이에 가압고정된다.When the first and second coupling pipes 11 and 12 are tightly coupled to each other, the first support bar 30 is press-fixed between the first and second coupling pipes 11 and 12.

그리고, 상기 제2 지지바(40)의 각도를 조절하여 상기 고정브라켓(41)이 콘크리트구조물(1)의 손상부분(1a)에 밀착되도록 한 후, 도 15에 도시한 바와 같이, 상기 앵커볼트(44)를 이용하여 상기 고정브라켓(41)을 콘크리트구조물(1)의 손상부분(1a)에 고정함으로써, 연결구(G)의 설치를 완료할 수 있다.Then, by adjusting the angle of the second support bar 40 so that the fixing bracket 41 is in close contact with the damaged portion (1a) of the concrete structure (1), as shown in Figure 15, the anchor bolt By using the 44 to fix the fixing bracket 41 to the damaged portion (1a) of the concrete structure (1), the installation of the connector (G) can be completed.

그리고, 이와 같이 연결구(G)를 이용하여 절단된 철근(6)을 상호 연결한 후, 치핑된 콘크리트 구조물(1)에 주입관(A)과 차단판(B) 및 배출관(C)을 설치하여, 에폭시수지를 주입하고, 상기 에폭시수지(D)가 충전된 콘크리트 구조물(1)의 표면에 프라이머(E)를 도포한 후, 상기 프라이머(E)의 표면에 에폭시 수지 접착제를 도포하여 접착층(F)을 형성하고, 상기 콘크리트 구조물 보수보강용 난연패널을 고정함으로서, 콘크리트 구조물 보수보강용 난연패널의 시공을 완료할 수 있다.Then, after connecting the cut reinforcement (6) using the connector (G) in this way, by installing the injection pipe (A) and the blocking plate (B) and the discharge pipe (C) to the chipped concrete structure (1) After injecting the epoxy resin, applying the primer (E) to the surface of the concrete structure (1) filled with the epoxy resin (D), and then applying an epoxy resin adhesive on the surface of the primer (E) to the adhesive layer (F) ) And by fixing the flame retardant panel for reinforcement of the concrete structure, the construction of the flame retardant panel for reinforcement of the concrete structure can be completed.

이와 같은 콘크리트 구조물 보수보강용 난연패널 시공방법에 따르면, 부식된 철근(6)을 절단한 후, 연결구(G)를 이용하여 절단된 철근(6)을 연결하고, 연결구를 콘크리트 구조물(1)에 고정함으로써, 철근(6)을 더욱 견고하게 보강할 수 있는 장점이 있다.According to the method of constructing a flame retardant panel for reinforcing concrete structures, after cutting the corroded reinforcing bar 6, the cut bar 6 is connected using the connector G, and the connector is connected to the concrete structure 1. By fixing, there is an advantage that can reinforce the reinforcement 6 more firmly.

1. 구조물 2. 패널본체
3. 섬유매쉬 4. 에폭시 수지 접착제
5. 이형지 G. 연결구1. Structure 2. Panel Body
3. fiber mesh 4. epoxy resin adhesive
5. Release paper G. End connections

Claims (6)

치핑에 의해 시공 대상 콘크리트 구조물에 형성된 홀에 충전된 에폭시 수지(D)와;
측면이 상호 근접하도록 상기 에폭시 수지(D) 상에 배치된 난연패널들 -상기 난연패널들 각각은 유리섬유, 아라미드섬유, 또는 탄소섬유를 포함하는 고인장 섬유 가운데 적어도 한 종류 이상이 일방향으로 고르게 분포된 섬유심(2a) 70∼80 중량%에 150℃ 이상의 고온에서 경화되는 난연성 수지를 포함하는 충전재(2b)가 20∼30중량% 함침되어 두께 20mm 이하, 폭 2,000mm 이하로 이루어지는 패널본체(2)와, 상기 패널본체(2)의 상면에 적층된 로빙크로스 섬유매쉬(3)를 포함하고, 상기 패널본체(2)의 하측면에는 상호 측방향으로 이격되도록 복수개의 돌출리브(2c)가 구비됨-과;
한 쌍의 오목홈(69a)들과 상기 한 쌍의 오목홈(69a)들 사이에 형성된 돌출부를 포함하되, 상기 한 쌍의 오목홈(69a)들에 상기 난연패널들의 이웃하는 돌출리브(2c)들이 삽입되도록 배치되고, 상기 돌출부는 에폭시 수지(D) 중 이웃하는 패널본체(2) 사이에 존재하는 에폭시 수지와 마주하는, 고정부재(69)와;
상기 돌출부가 형성된 상기 고정부재(69)의 중앙을 관통하여 상기 에폭시 수지에 체결되는 앵커볼트(7)을 포함하는 것을 특징으로 하는 콘크리트 구조물의 보수보강 구조물.An epoxy resin (D) filled in holes formed in the concrete structure to be constructed by chipping;
Flame-retardant panels disposed on the epoxy resin (D) so that the sides are close to each other-each of the flame-retardant panels are evenly distributed in one direction at least one kind of high tensile fibers including glass fibers, aramid fibers, or carbon fibers 20 to 30% by weight of a filler 2b containing a flame retardant resin cured at a high temperature of 150 ° C. or more to 70 to 80% by weight of the fiber core 2a, wherein the panel body is 20 mm or less in thickness and 2,000 mm or less in width (2) ) And a roving cross fiber mesh 3 laminated on the upper surface of the panel body 2, and a plurality of protruding ribs 2c are provided on the lower side of the panel body 2 so as to be laterally spaced apart from each other. -And;
A protrusion formed between the pair of concave grooves 69a and the pair of concave grooves 69a, and protruding ribs 2c adjacent to the pair of concave grooves 69a of the flame-retardant panels. Fastening members (69) facing the epoxy resin existing between the adjacent panel bodies (2) of the epoxy resin (D);
Repairing reinforcement structure of a concrete structure, characterized in that it comprises an anchor bolt (7) is fastened to the epoxy resin penetrating the center of the fixing member 69 formed with the protrusion. 제 1항에 있어서,
상기 충전재(2b)는 폴리에스테르수지, 비닐에스테르수지 및 에폭시 수지 중 적어도 하나를 포함하는 원료에 인계 난연재를 3~5중량%를 혼합하여 구성된 것을 특징으로 하는 콘크리트 구조물의 보수보강 구조물.The method of claim 1,
The filler (2b) is a reinforcement structure of a concrete structure, characterized in that by mixing 3 to 5% by weight of the phosphorus-based flame retardant to the raw material comprising at least one of polyester resin, vinyl ester resin and epoxy resin. 제 1항에 있어서,
상기 홀을 통해 노출된 철근(6)의 절단된 두분 사이를 연결하도록 결합된 연결구(G)를 포함하며,
상기 연결구(G)는,
상기 철근(6)의 길이방향으로 연장된 관체형상으로 구성되고 길이방향으로 연장된 절단선(14)에 의해 복수개의 결합편(13)으로 분할되어 절단된 철근(6)의 외측 둘레부에 각각 결합되며 외주면에는 나사산(15)이 형성된 제1 및 제2 결합관(11,12)과,
상기 제1 및 제2 결합관(11,12)의 나사산(15)에 각각 나사결합되며 인접단에는 결합공(21a)과 상기 결합공(21a)에 나사결합되는 나사축(22a)이 각각 형성된 제1 및 제2 고정관(21,22)과,
기단부에는 상기 나사축(22a)이 관통하는 관통공(31)이 형성되어 상기 제1 및 제2 고정관(21,22)의 사이에 결합고정되는 제1 지지바(30)와,
상기 제1 지지바(30)의 선단부에 각도조절가능하게 결합되며 선단부에는 고정브라켓(41)이 형성된 제2 지지바(40)를 포함하고,
상기 결합편(13)의 내주면에는 상기 철근(6)의 둘레면에 형성된 오목홈(4)에 삽입되는 돌기(16)가 형성되고,
상기 결합편(13)의 외주면에 형성된 나사산(15)과 상기 나사축(22a)에 형성된 나사산(22b)은 동일한 피치를 갖도록 구성되며,
상기 고정브라켓(41)에는 앵커볼트(44)가 결합되는 관통공(41a)이 형성되어, 상기 관통공(41a)에 결합되는 앵커볼트(44)를 이용하여 상기 제2 지지바(40)를 콘크리트 구조물(1)의 손상부분(1a)에 고정함으로써, 상기 연결구(G)를 콘크리트 구조물(1)의 손상부분(1a)에 고정할 수 있도록 구성되며,
상기 제1 및 제2 결합관(11,12)을 이루는 결합편(13)의 전후단에는 전후방향으로 연장된 호형상의 연장부(17)가 형성되고,
상기 연장부(17)의 외측둘레부에 결합되어 상기 결합편(13)이 원통형을 이루도록 탄성적으로 가압하는 고무재질의 탄성링체(18)와,
상기 결합편(13)의 내주면에 접착고정되며 내부에는 접착제가 저장된 합성수지재질의 저장관체(50)를 더 포함하여,
상기 결합편(13)을 상기 철근(6)의 둘레면에 결합한 후, 상기 결합편(13)의 외측면을 가압하면, 상기 저장관체(50)가 가압되어 파손되면서 내부에 저장된 접착제가 유출되어, 상기 결합편(13)이 철근(6)의 둘레부에 접착고정되도록 구성된 것을 특징으로 하는 콘크리트 구조물의 보수 보강 구조물.The method of claim 1,
A connector (G) coupled to connect between the two cut portions of the reinforcing bar (6) exposed through the hole,
The connector (G),
The outer periphery of the reinforcing bar 6, which is composed of a tubular shape extending in the longitudinal direction of the reinforcing bar 6 and is divided into a plurality of coupling pieces 13 by the cutting line 14 extending in the longitudinal direction, respectively. Coupled to the outer circumferential surface of the first and second coupling pipes (11, 12) having a thread (15),
The first and second coupling pipes (11, 12) of the screw thread (15), respectively, are screwed in the adjacent end coupling hole 21a and the screw shaft (22a) screwed to the coupling hole (21a) are formed, respectively First and second fixing pipes (21, 22),
A first support bar 30 is formed in the proximal end through-hole 31 through which the screw shaft 22a penetrates and is fixedly coupled between the first and second fixing pipes 21 and 22,
The second support bar 40 is coupled to the front end of the first support bar 30 so that the angle adjustment is possible, the fixing bracket 41 is formed on the front end,
On the inner circumferential surface of the coupling piece 13 is formed a projection 16 inserted into the concave groove 4 formed on the circumferential surface of the reinforcing bar 6,
The thread 15 formed on the outer circumferential surface of the coupling piece 13 and the thread 22b formed on the screw shaft 22a are configured to have the same pitch,
The fixing bracket 41 is formed with a through hole 41a to which the anchor bolt 44 is coupled to the second support bar 40 by using the anchor bolt 44 coupled to the through hole 41a. By fixing to the damaged portion (1a) of the concrete structure (1), the connector (G) is configured to be fixed to the damaged portion (1a) of the concrete structure (1),
Arc-shaped extension portions 17 extending in the front-rear direction are formed at the front and rear ends of the coupling pieces 13 forming the first and second coupling pipes 11 and 12,
Is coupled to the outer peripheral portion of the extension portion 17 is an elastic ring body 18 of rubber material to elastically press the coupling piece 13 to form a cylindrical,
Adhesively fixed to the inner circumferential surface of the coupling piece 13 and further comprises a storage pipe 50 made of a synthetic resin material stored therein,
After the coupling piece 13 is coupled to the circumferential surface of the reinforcing bar 6, and when the outer surface of the coupling piece 13 is pressed, the storage pipe 50 is pressed and broken and the adhesive stored therein is leaked out. , Reinforcing reinforcement structure of the concrete structure, characterized in that the coupling piece 13 is configured to be fixed to the periphery of the reinforcing bar (6). 제 1항에 있어서,
상기 콘크리트 구조물 보수보강용 난연패널은 다수개의 릴(61)에서 풀려나온 섬유심(2a)을 배스(62)에 저장된 충전재(2b)에 함침시키는 함침단계와,
상기 함침단계를 통과한 섬유심(2a)의 상면에 로빙크로스 섬유매쉬(3)를 적층하는 적층단계와,
로빙크로스 섬유매쉬(3)가 적층된 섬유심(2a)를 압출성형금형(64)의 성형공(64a)을 통과시켜 패널형태로 성형하는 성형단계와,
상기 성형단계를 통과한 패널을 가열하여 건조시키는 건조단계와,
상기 건조단계를 통과하여 건조된 패널을 권취롤(67a)에 권취하는 권취단계를 통해 제작되는 것을 특징으로 하는 콘크리트 구조물의 보수 보강 구조물.The method of claim 1,
The flame retardant panel for repairing the concrete structure includes an impregnation step of impregnating the fiber core 2a released from the plurality of reels 61 into the filler 2b stored in the bath 62;
A laminating step of laminating a roving cross fiber mesh 3 on an upper surface of the fiber core 2a having passed through the impregnation step;
A molding step of molding the fiber core 2a having the roving cross fiber mesh 3 laminated therein through a molding hole 64a of the extrusion molding 64 to form a panel;
A drying step of heating and drying the panel that has passed the forming step;
Repair reinforcement structure of a concrete structure, characterized in that it is produced through the winding step of winding the panel dried through the drying step on the winding roll (67a). 삭제delete 콘크리트 구조물의 보수 보강 구조물을 시공하는 방법으로서,
시공 대상 콘크리트 구조물(1)을 치핑하는 치핑단계와,
치핑된 콘크리트 구조물(1)에 에폭시수지(D)를 충전하도록 주입관(A)과 차단판(B) 및 배출관(C)을 설치하는 설치단계와,
상기 주입관(A)을 통해 콘크리트 구조물(1)의 내부에 에폭시수지(D)를 충전하면서 배출관(C)을 에폭시수지(D)가 누출되는지를 확인하면서 에폭시수지(D)를 충전하는 충전단계와,
상기 에폭시수지(D)가 충전된 콘크리트 구조물(1)의 표면에 프라이머(E)를 도포하는 도포단계와,
상기 프라이머(E)의 표면에 4관능성 에폭시 수지인 테트라글리시딜에테르 디아미노디페닐 메탄 100중량부, 에폭시기의 경화를 위한 방향족 아민 경화제인 디아미노디페닐 메탄 20 내지 50중량부 및 에폭시 수지의 개질을 위한 열가소성 수지인 폴리에테르술폰 10 내지 30중량부로 구성된 에폭시 수지 접착제를 도포하여 접착층(F)을 형성하는 접착층형성단계와,
권취롤에 권취된 콘크리트 구조물 보수보강용 난연패널을 적절한 길이로 절단하고 상기 에폭시 수지 접착층(F)에 콘크리트 구조물 보수보강용 난연패널을 부착한 후 상기 콘크리트 구조물 보수보강용 난연패널을 앵커볼트(7)로 고정하는 고정단계와,
상기 콘크리트 구조물 보수보강용 난연패널에 형성된 돌출리브(2c)에 고정부재(69)를 결합하여 콘크리트 구조물 보수보강용 난연패널을 상호 고정하는 2차 고정단계를 포함하며,
상기 치핑단계에서는 콘크리트 구조물(1)의 손상부분(1a)을 파쇄하여 콘크리트 구조물(1)의 내부에 매립된 철근(6)의 부식부위가 외부 노출되도록 하고,
상기 치핑단계에서 노출된 철근(6)의 부식부위를 절단하는 절단단계와,
상기 파쇄단계에서 노출된 콘크리트 구조물(1)의 손상부분(1a)철근(6)의 표면에 부착된 이물질을 제거하는 세척단계와,
상기 절단단계에서 절단된 철근(6)에 연결구(G)를 결합하여 절단된 철근(6)을 상호 연결하는 연결단계를 더 포함하며,
상기 연결구(G)는
상기 철근(6)의 길이방향으로 연장된 관체형상으로 구성되고 길이방향으로 연장된 절단선(14)에 의해 복수개의 결합편(13)으로 분할되어 절단된 철근(6)의 외측 둘레부에 각각 결합되며 외주면에는 나사산(15)이 형성된 제1 및 제2 결합관(11,12)과,
상기 제1 및 제2 결합관(11,12)의 나사산(15)에 각각 나사결합되며 인접단에는 결합공(21a)과 상기 결합공(21a)에 나사결합되는 나사축(22a)이 각각 형성된 제1 및 제2 고정관(21,22)과,
기단부에는 상기 나사축(22a)이 관통하는 관통공(31)이 형성되어 상기 제1 및 제2 고정관(21,22)의 사이에 결합고정되는 제1 지지바(30)와,
상기 제1 지지바(30)의 선단부에 각도조절가능하게 결합되며 선단부에는 고정브라켓(41)이 형성된 제2 지지바(40)를 포함하고,
상기 결합편(13)의 내주면에는 상기 철근(6)의 둘레면에 형성된 오목홈(4)에 삽입되는 돌기(16)가 형성되고,
상기 결합편(13)의 외주면에 형성된 나사산(15)과 상기 나사축(22a)에 형성된 나사산(22b)은 동일한 피치를 갖도록 구성되며,
상기 고정브라켓(41)에는 앵커볼트(44)가 결합되는 관통공(41a)이 형성되어, 상기 관통공(41a)에 결합되는 앵커볼트(44)를 이용하여 상기 제2 지지바(40)를 콘크리트 구조물(1)의 손상부분(1a)에 고정함으로써, 상기 연결구(G)를 콘크리트 구조물(1)의 손상부분(1a)에 고정할 수 있도록 구성되며,
상기 제1 및 제2 결합관(11,12)을 이루는 결합편(13)의 전후단에는 전후방향으로 연장된 호형상의 연장부(17)가 형성되고,
상기 연장부(17)의 외측둘레부에 결합되어 상기 결합편(13)이 원통형을 이루도록 탄성적으로 가압하는 고무재질의 탄성링체(18)와,
상기 결합편(13)의 내주면에 접착고정되며 내부에는 접착제가 저장된 합성수지재질의 저장관체(50)를 더 포함하여,
상기 결합편(13)을 상기 철근(6)의 둘레면에 결합한 후, 상기 결합편(13)의 외측면을 가압하면, 상기 저장관체(50)가 가압되어 파손되면서 내부에 저장된 접착제가 유출되어, 상기 결합편(13)이 철근(6)의 둘레부에 접착고정되도록 구성된 것을 특징으로 하는 콘크리트 구조물의 보수 보강 구조물 시공방법.As a method of constructing a repair reinforcement structure of a concrete structure,
A chipping step of chipping the concrete structure 1 to be constructed;
An installation step of installing an injection pipe (A), a blocking plate (B), and an discharge pipe (C) to fill an epoxy resin (D) in the chipped concrete structure (1),
Filling step of filling the epoxy resin (D) while checking whether the epoxy resin (D) leaks the discharge pipe (C) while filling the epoxy resin (D) inside the concrete structure (1) through the injection pipe (A) Wow,
An application step of applying a primer (E) to the surface of the concrete structure (1) filled with the epoxy resin (D),
100 parts by weight of tetraglycidyl ether diaminodiphenyl methane which is a tetrafunctional epoxy resin on the surface of the primer (E), 20 to 50 parts by weight of diaminodiphenyl methane which is an aromatic amine curing agent for curing an epoxy group, and an epoxy resin An adhesive layer forming step of forming an adhesive layer (F) by applying an epoxy resin adhesive consisting of 10 to 30 parts by weight of polyether sulfone which is a thermoplastic resin for modification of
Cut the flame retardant panel for reinforcement of the concrete structure wound on the winding roll to an appropriate length, attach the flame retardant panel for reinforcement of the concrete structure to the epoxy resin adhesive layer (F), and then anchor the flame retardant panel for the reinforcement of the concrete structure (7). Fixing step),
And a second fixing step of fixing the flame retardant panel for repairing the concrete structure by coupling the fixing member 69 to the protruding rib 2c formed on the flame retardant panel for repairing the concrete structure,
In the chipping step, the damaged part 1a of the concrete structure 1 is crushed so that the corrosion site of the reinforcing bar 6 embedded in the concrete structure 1 is exposed to the outside.
A cutting step of cutting a corrosion portion of the rebar 6 exposed in the chipping step;
A washing step of removing foreign substances attached to the surface of the damaged part 1a of the concrete structure 1 exposed in the crushing step 1;
Further comprising a connection step of connecting the cutting bar (6) to each other by coupling the connector (G) to the cut bar (6) cut in the cutting step,
The connector (G) is
The outer periphery of the reinforcing bar 6, which is composed of a tubular shape extending in the longitudinal direction of the reinforcing bar 6 and is divided into a plurality of coupling pieces 13 by the cutting line 14 extending in the longitudinal direction, respectively. Coupled to the outer circumferential surface of the first and second coupling pipes (11, 12) having a thread (15),
The first and second coupling pipes (11, 12) of the screw thread (15), respectively, are screwed in the adjacent end coupling hole 21a and the screw shaft (22a) screwed to the coupling hole (21a) are formed, respectively First and second fixing pipes (21, 22),
A first support bar 30 is formed in the proximal end through-hole 31 through which the screw shaft 22a penetrates and is fixedly coupled between the first and second fixing pipes 21 and 22,
The second support bar 40 is coupled to the front end of the first support bar 30 so that the angle adjustment is possible, the fixing bracket 41 is formed on the front end,
On the inner circumferential surface of the coupling piece 13 is formed a projection 16 inserted into the concave groove 4 formed on the circumferential surface of the reinforcing bar 6,
The thread 15 formed on the outer circumferential surface of the coupling piece 13 and the thread 22b formed on the screw shaft 22a are configured to have the same pitch,
The fixing bracket 41 is formed with a through hole 41a to which the anchor bolt 44 is coupled to the second support bar 40 by using the anchor bolt 44 coupled to the through hole 41a. By fixing to the damaged portion (1a) of the concrete structure (1), the connector (G) is configured to be fixed to the damaged portion (1a) of the concrete structure (1),
Arc-shaped extension portions 17 extending in the front-rear direction are formed at the front and rear ends of the coupling pieces 13 forming the first and second coupling pipes 11 and 12,
Is coupled to the outer peripheral portion of the extension portion 17 is an elastic ring body 18 of rubber material to elastically press the coupling piece 13 to form a cylindrical,
Adhesively fixed to the inner circumferential surface of the coupling piece 13 and further comprises a storage pipe 50 made of a synthetic resin material stored therein,
After the coupling piece 13 is coupled to the circumferential surface of the reinforcing bar 6, and when the outer surface of the coupling piece 13 is pressed, the storage pipe 50 is pressed and broken and the adhesive stored therein is leaked out. , Reinforcement structure construction method of the concrete structure, characterized in that the coupling piece 13 is configured to be fixed to the circumference of the reinforcing bar (6).
KR1020190052865A 2019-05-07 2019-05-07 Structure for Repairing and Reinforcing Concrete Structure1s and Its Application Method KR102061572B1 (en)