KR102038609B1 - The light guide plate having pattern consisted of plural dots - Google Patents
The light guide plate having pattern consisted of plural dots Download PDFInfo
- Publication number
- KR102038609B1 KR102038609B1 KR1020170104029A KR20170104029A KR102038609B1 KR 102038609 B1 KR102038609 B1 KR 102038609B1 KR 1020170104029 A KR1020170104029 A KR 1020170104029A KR 20170104029 A KR20170104029 A KR 20170104029A KR 102038609 B1 KR102038609 B1 KR 102038609B1
- Authority
- KR
- South Korea
- Prior art keywords
- dot
- light guide
- guide plate
- light
- weight
- Prior art date
Abstract
본 발명은 도광판에 대한 것으로, 더 자세하게는 본 발명은 기재; 및 상기 기재의 적어도 일면에 형성되며, 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴;을 구비하는 도광판에 관한 것이다.
본 발명의 도광판은 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴을 채택하여 광 확산 특성에 대한 조정이 용이하고, 슬림화가 가능하다. 특히, 제1 도트와 제2 도트는 선택적으로 가우시안 분포 반사와 램버시안 분포 반사를 일으키도록 할 수 있으므로, 광 확산 효율을 높일 수 있다.The present invention relates to a light guide plate, and more particularly, the present invention; And a pattern formed on at least one surface of the substrate and having a first dot and a second dot having different compositions from each other.
The light guide plate of the present invention adopts a pattern composed of first dots and second dots having different compositions, thereby making it easy to adjust the light diffusing characteristics and to be slim. In particular, since the first dot and the second dot can selectively cause Gaussian distribution reflection and Lambertian distribution reflection, the light diffusion efficiency can be improved.
Description
본 발명은 도트 패턴을 구비하는 도광판에 관한 것이다. 더 자세하게는 본 발명은 조성이 서로 상이한 복수의 도트로 이루어진 패턴을 구비하는 도광판에 대한 것이다.The present invention relates to a light guide plate having a dot pattern. More specifically, the present invention relates to a light guide plate having a pattern composed of a plurality of dots having different compositions.
일반적으로 도광판은 백라이트 유니트의 휘도와 균일한 조명 기능을 수행하는 부품으로, 액정 표시 장치(LCD) 내에서 빛을 액정에 인도하는 백라이트 유니트 안에 조립되어 있는 플라스틱 사출물을 의미한다. 즉, 통상 광원(예를들면, 냉음극 형광램프 등)에서 발산되는 빛을 LCD 전체 면에 균일하게 전달하는 역할을 하는 플라스틱 성형 렌즈의 하나이다.Generally, a light guide plate is a component that performs the brightness and uniform illumination function of a backlight unit, and refers to a plastic injection molded product that is assembled in a backlight unit to guide light to liquid crystal in a liquid crystal display (LCD). That is, it is one of the plastic molded lenses that normally serves to uniformly transmit the light emitted from the light source (for example, cold cathode fluorescent lamp) to the entire LCD surface.
상기 도광판은 광원을 통하여 일 측면으로 입사된 광을 반대 측면으로 도파시키고, 그 중 일부를 상부 방향으로 고르게 편향시켜서 빛의 편차를 방지한다. 이러한 도광판은 패널 형태를 이루도록 아크릴과 같은 플라스틱 계열의 투명한 물질로 형성되어 있으며, 광원으로부터 발생한 광이 도광판을 경유하여 상부에 안착되는 액정패널 쪽으로 진행되도록 한다. 이때, 도광판의 하면에는 광원으로부터 발생한 광의 진행 방향을 액정패널 쪽으로 변환시키기 위하여 패턴이 형성된다.The light guide plate guides the light incident to one side through the light source to the opposite side, and evenly deflects a portion of the light guide to the upper side to prevent the deviation of the light. The light guide plate is formed of a plastic-based transparent material such as acryl to form a panel, and the light generated from the light source is propagated toward the liquid crystal panel seated on the upper part via the light guide plate. At this time, a pattern is formed on the lower surface of the light guide plate to convert the traveling direction of the light generated from the light source toward the liquid crystal panel.
최근에는 초박형 디스플레이에 대한 수요가 증대하고 있어, 슬림화된 도광판이 요구되고 있으며, 이를 위해 도광판에 대하여 다양한 기술 개발이 시도되고 있지만, 광확산 효율이 우수한 슬림한 도광판의 제공에 실패하고 있다.Recently, as the demand for ultra-thin displays is increasing, a slimmer light guide plate is required, and various technology developments have been attempted for the light guide plate, but fail to provide a slim light guide plate having excellent light diffusion efficiency.
본 발명은 초박형 디스플레이에 적합한 광확산 효율이 우수한 슬림형 도광판을 제공하는 것을 목적으로 한다.An object of the present invention is to provide a slim light guide plate having excellent light diffusion efficiency suitable for an ultra-thin display.
상기 과제를 해결하기 위하여 본 발명은 기재; 및 상기 기재의 적어도 일면에 형성되며, 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴;을 구비하며, 상기 제1 도트와 상기 제2 도트는 상호 인접하는 것을 특징으로 하는 도광판을 제공한다.The present invention to solve the above problems; And a pattern formed on at least one surface of the substrate and having a first dot and a second dot having different compositions from each other, wherein the first dot and the second dot are adjacent to each other. .
바람직한 일 실시예에 따르면, 본 발명의 제1 도트는 가우시안 분포 반사 광확산제를 포함하는 조성물이 UV경화되어 형성된 것을 사용할 수 있다.According to one preferred embodiment, the first dot of the present invention can be used that is formed by UV-curing a composition comprising a Gaussian distribution reflective light diffusing agent.
또한, 바람직한 일 실시예에 따르면, 본 발명의 제2 도트는 램버시안 분포 반사 광확산제를 포함하는 조성물이 UV경화되어 형성된 것을 사용할 수 있다.In addition, according to a preferred embodiment, the second dot of the present invention can be used that is formed by UV-curing a composition comprising a Lambertian distributed reflective light diffusing agent.
본 발명의 도광판은 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴을 채택하여 광 확산 특성에 대한 조정이 용이하고, 슬림화가 가능하다.The light guide plate of the present invention adopts a pattern composed of first dots and second dots having different compositions, thereby making it easy to adjust the light diffusing characteristics and to be slim.
특히, 제1 도트와 제2 도트는 선택적으로 가우시안 분포 반사와 램버시안 분포 반사를 일으키도록 할 수 있으므로, 광 확산 효율을 높일 수 있다.In particular, since the first dot and the second dot can selectively cause Gaussian distribution reflection and Lambertian distribution reflection, the light diffusion efficiency can be improved.
가우시안 특성은 특정 입사각에서 휘도 특성을 가장 좋게 하는 특징이 있습니다. 이를 이용해서 정면 및 사선(45도)에서 휘도 특성이 가장 좋을 수 있으며, 램버시안의 경우 각도 영향 없이 휘도 특성이 좋으나, 확산제의 함량이 매우 많지 않을 경우 전체적인 intensity가 좋지 않지만, 본 발명은 이를 상호 보완할 수 있다.Gaussian characteristics have the best luminance characteristics at certain angles of incidence. In this case, the brightness characteristics may be the best at the front and oblique lines (45 degrees), and in the case of Lambertian, the brightness characteristics are good without the angle effect, but the overall intensity is not good when the content of the diffusion agent is not very high, but the present invention does not Can complement each other.
본 명세서에 첨부되는 다음의 도면들은 본 발명의 바람직한 실시예를 예시하는 것이며, 전술한 발명의 내용과 함께 본 발명의 기술사상을 더욱 이해시키는 역할을 하는 것이므로, 본 발명은 그러한 도면에 기재된 사항에만 한정되어 해석되어서는 아니된다.
도 1은 본 발명의 일 실시예에 따른 도광판의 도트 패턴을 나타내는 도면이다.
도 2는 본 발명의 일 실시예에 따른 도광판의 도트 패턴을 나타내는 도면이다.The following drawings, which are attached to this specification, illustrate preferred embodiments of the present invention, and together with the contents of the present invention serve to further understand the technical spirit of the present invention, the present invention is limited to the matters described in such drawings. It should not be construed as limited.
1 illustrates a dot pattern of a light guide plate according to an exemplary embodiment of the present invention.
2 illustrates a dot pattern of a light guide plate according to an exemplary embodiment of the present invention.
이하에서는 첨부된 도면들을 참조하여 본 발명의 바람직한 실시 예를 상세하게 설명한다. 각 도면은 명확한 설명을 위해 일부가 간략하거나 과장되게 표현되었다. 각 도면의 구성 요소들에 참조 번호를 부가함에 있어서, 동일한 구성 요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 동일한 부호를 가지도록 도시되었음에 유의해야 한다. 또한, '포함(또는 구비)한다'로 언급된 구성 요소 및 동작은 하나 이상의 다른 구성요소 및 동작의 존재 또는 추가를 배제하지 않는다. 더불어, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the present invention. Each drawing is partly or exaggerated for clarity. In adding reference numerals to the components of each drawing, it should be noted that the same components are shown with the same reference numerals as much as possible, even if displayed on different drawings. In addition, components and operations referred to as 'includes (or includes)' do not exclude the presence or addition of one or more other components and operations. In addition, in describing the present invention, when it is determined that the detailed description of the related known configuration or function may obscure the gist of the present invention, the detailed description thereof will be omitted.
도 1 및 도 2를 참조하면, 본 발명의 도광판은 기재(3); 및 상기 기재의 적어도 일면에 형성되며, 조성이 서로 상이한 제1 도트(1) 및 제2 도트(2)로 이루어진 패턴;을 구비하며, 상기 제1 도트(1)와 상기 제2 도트(2)는 상호 인접하는 것을 특징으로 한다.1 and 2, the light guide plate of the present invention is a substrate (3); And a pattern formed on at least one surface of the substrate, the
본 발명의 도광판은 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴을 채택하여 광 확산 특성에 대한 조정이 용이하다. 즉, 제1 도트와 제2 도트의 조성을 달리하여 반사특성을 조정할 수 있다. 예를 들면, 제1 도트는 가우시안(Gaussian) 분포 반사 특성을 갖도록 하고, 제2 도트는 램버시안(Lambertian) 분포 반사 특성을 갖도록 성분을 달리할 수 있으며, 이러한 조합을 통하여 광 확산 특성을 극대화할 수 있다.The light guide plate of the present invention adopts a pattern composed of first dots and second dots having different compositions, thereby making it easy to adjust the light diffusion characteristics. That is, the reflection characteristics may be adjusted by changing the composition of the first dot and the second dot. For example, the first dot may have a Gaussian distribution reflection characteristic, and the second dot may have a component that has a Lambertian distribution reflection characteristic, and the combination may maximize light diffusion characteristics. Can be.
본 발명의 도광판은 상기 제1 도트와 상기 제2 도트가 상호 인접하는 것을 특징으로 하는 도광판일 수 있다. 이와 같이 상기 제1 도트와 제2 도트가 인접하는 경우에는 수직방향으로의 집광효과를 나타낼 수 있다.The light guide plate of the present invention may be a light guide plate, wherein the first dot and the second dot are adjacent to each other. As such, when the first dot and the second dot are adjacent to each other, the light converging effect in the vertical direction may be exhibited.
본 발명의 바람직한 일 실시예에 따르면, 상기 제1 도트는 가우시안 분포 반사 광확산제를 포함하는 조성물이 UV경화되어 형성된 것일 수 있다. 상기 가우시안 분포 반사 광확산제를 포함하는 제1 도트는 가우시안 분포 반사 특성을 갖는다. 이러한 가우시안 분포 반사는 리플렉터 표면의 각에 따른 반사광의 세기가 법선과 반사광의 방향 사이의 각이 가우시안 함수값으로 변하는 반사를 의미한다.According to a preferred embodiment of the present invention, the first dot may be formed by UV curing a composition comprising a Gaussian distribution reflective light diffusing agent. The first dot including the Gaussian distributed reflective light diffusing agent has Gaussian distributed reflective characteristics. Such Gaussian distributed reflection refers to a reflection in which the intensity of reflected light according to the angle of the reflector surface is changed to a Gaussian function by the angle between the normal and the direction of the reflected light.
이러한 가우시안 분포 반사 광확산제로는 이산화규소(SiO2) 또는 황산바륨(BaSO4) 등이 사용될 수 있으며, 바람직하게는 이산화규소(SiO2)를 사용할 수 있다.As the Gaussian distribution reflective light diffusing agent, silicon dioxide (SiO 2 ) or barium sulfate (BaSO 4 ) may be used, and silicon dioxide (SiO 2 ) may be preferably used.
또한, 본 발명의 바람직한 일 실시예에 따르면, 상기 제1 도트는 우레탄 아크릴레이트 수지 100 중량부에 대하여, 아크릴계 단량체 30 ~ 100 중량부, 광개시제 0.1 ~ 10 중량부 및 가우시안 분포 반사 광확산제 0.1 ~ 30 중량부를 포함하는 조성물이 UV경화되어 형성된 것을 사용할 수 있다.In addition, according to a preferred embodiment of the present invention, the first dot is 30 to 100 parts by weight of the acrylic monomer, 0.1 to 10 parts by weight of the photoinitiator and Gaussian distribution reflective light diffuser 0.1 to about 100 parts by weight of the urethane acrylate resin. A composition containing 30 parts by weight may be used that is formed by UV curing.
상기 우레탄 아크릴레이트 수지는 굴절율이 1.47이상의 특성을 가지고 있으므로, 가우시안 분포 반사에 적합하다.Since the urethane acrylate resin has a characteristic of refractive index of 1.47 or more, it is suitable for Gaussian distribution reflection.
상기 아크릴 단량체는 함량에 따른 휘도 및 가공성 변화 특성을 가지고 있으며, 30 중량부 미만으로 사용하는 경우에는 휘도 intensity가 약하다는 단점이 존재하며, 100 중량부를 초과하여 사용하는 경우에는 잉크의 점도가 너무 낮아 가공이 어려운 문제점이 발생할 수 있다.The acrylic monomer has a change in brightness and processability according to the content, there is a disadvantage that the brightness intensity is weak when used less than 30 parts by weight, the viscosity of the ink is too low when used over 100 parts by weight Difficult processing may occur.
상기 광개시제는 UV를 조사하는 경우에 중합이 시작되도록 하는 역할을 하며, 0.1 미만으로 사용되는 경우에는 중합이 발생하기 어려우며, 10 중량부를 초과하여 사용하는 경우에는 광반응 속도를 제어하기 어려운 문제점이 발생할 수 있다.The photoinitiator serves to start the polymerization when irradiated with UV, it is difficult to occur polymerization when used less than 0.1, it is difficult to control the photoreaction rate when used in excess of 10 parts by weight Can be.
그리고, 상기 광개시제로는 특별히 그 종류를 한정하는 것은 아니지만, 1-Hydroxycyclohexyl phenyl ketone 등으로 사용할 수 있다.The photoinitiator is not particularly limited in kind, but may be used as 1-hydroxycyclohexyl phenyl ketone or the like.
본 발명의 바람직한 일 실시예에 따르면, 상기 제2 도트는 램버시안 분포 반사 광확산제를 포함하는 조성물이 UV경화되어 형성된 것일 수 있다. 상기 램버시안 분포 반사 광확산제를 포함하는 제2 도트는 램버시안 분포 반사 특성을 갖는다. 이러한 램버시안 분포 반사는 리플렉터 표면의 각에 따른 반사광의 세기가 법선과 반사광의 방향 사이의 각이 코사인 함수값으로 변하는 반사를 의미한다.According to an exemplary embodiment of the present invention, the second dot may be formed by UV curing a composition including a Lambertian distribution reflective light diffusing agent. The second dot including the Lambertian distributed reflective light diffusing agent has Lambertian distributed reflective characteristics. Such Lambertian distributed reflection refers to a reflection in which the intensity of reflected light according to the angle of the reflector surface changes as the cosine function value between the normal and the direction of the reflected light.
이러한 램버시안 분포 반사 광확산제로는 PMMA 비드(PMMA Bead), PC 비드(PC Bead) 또는 실리콘 비드(Silicone Bead) 등이 사용될 수 있으며, 바람직하게는 PMMA 비드를 사용할 수 있다.As the Lambertian distributed reflective light diffusing agent, PMMA beads, PC beads, or silicon beads may be used. Preferably, PMMA beads may be used.
또한, 본 발명의 바람직한 일 실시예에 따르면, 상기 제2 도트는 아크릴 아크릴레이트 수지 100 중량부에 대하여, 아크릴계 단량체 30 ~ 100 중량부, 광개시제 0.1 ~ 10 중량부 및 램버시안 분포 반사 광확산제 0.1 ~ 30 중량부를 포함하는 조성물이 UV경화되어 형성된 것을 사용할 수 있다.In addition, according to a preferred embodiment of the present invention, the second dot is 30 to 100 parts by weight of the acrylic monomer, 0.1 to 10 parts by weight of the photoinitiator and Lambertian distribution reflective light diffuser 0.1 with respect to 100 parts by weight of the acrylic acrylate resin. The composition including the 30 parts by weight can be used that is formed by UV curing.
상기 아크릴 아크릴레이트 수지는 굴절율이 1.43이하의 특성을 가지고 있으므로, 램버시안 분포 반사에 적합하다.Since the acryl acrylate resin has a refractive index of 1.43 or less, it is suitable for Lambertian distribution reflection.
상기 아크릴 단량체는 함량에 따른 휘도 및 가공성 변화 특성을 가지고 있으며, 30 중량부 미만으로 사용하는 경우에는 노광량을 많이 해야 반응이 일어난다는 단점이 존재하며, 100 중량부를 초과하여 사용하는 경우에는 잉크의 점도가 너무 낮아 가공이 어려운 문제점이 발생할 수 있다.The acrylic monomer has a change in brightness and processability according to the content, there is a disadvantage that the reaction occurs when the exposure amount is increased when using less than 30 parts by weight, the viscosity of the ink when used in excess of 100 parts by weight Too low a problem may occur that is difficult to machine.
상기 광개시제는 UV를 조사하는 경우에 라디칼을 형성하여 자외선 경화형 수지 성분 중 이중결합 반응하여 라디칼 반응으로 중합이 시작되도록 하는 역할을 하며, 0.1 미만으로 사용되는 경우에는 중합이 발생하기 어려우며, 10 중량부를 초과하여 사용하는 경우에는 광반응 속도를 제어하기 어려운 문제점이 발생할 수 있다.The photoinitiator forms a radical when irradiated with UV and plays a role of causing a double bond reaction in the ultraviolet curable resin component to initiate polymerization by a radical reaction, and when used at less than 0.1, polymerization is difficult to occur and 10 parts by weight In the case of excessive use, it may be difficult to control the photoreaction rate.
그리고, 상기 광개시제로는 특별히 그 종류를 한정하는 것은 아니지만, 2-Hydroxy-2-methyl-1-phenyl propan-1-one 등을 사용할 수 있다.The photoinitiator is not particularly limited in kind, but 2-Hydroxy-2-methyl-1-phenyl propan-1-one may be used.
다음에서는 본 발명에 대하여 실시예를 통하여 상세하게 설명한다. 다음의 실시예 및 비교예는 본 발명을 좀 더 상세히 설명하는 것이지만, 본 발명의 범주를 한정하는 것은 아니다.Next, the present invention will be described in detail with reference to Examples. The following examples and comparative examples illustrate the invention in more detail, but do not limit the scope of the invention.
실시예Example
실시예Example 1. 제1 1. The first 도트와With dots 제2 2nd 도트가Dot is 인접된 도광판의 제조 Fabrication of adjacent light guide plates
1) 제 1도트 조성물1) First Dot Composition
무게평균 분자량이 20,000인 우레탄 아크릴레이트 수지 100g, 아크릴계 단량체 65g, 광개시제(1-Hydroxycyclohexyl phenyl ketone) 5g 및 가우시안 분포 반사 광확산제(직경이 10㎛인 이산화규소) 15g를 혼합하여 제 1도트 조성을 준비하였다.A first dot composition is prepared by mixing 100 g of a urethane acrylate resin having a weight average molecular weight of 20,000, 65 g of an acrylic monomer, 5 g of a photoinitiator (1-Hydroxycyclohexyl phenyl ketone), and 15 g of a Gaussian distributed reflective light diffuser (diameter of 10 μm in diameter). It was.
2) 제 2도트 조성물2) second dot composition
무게평균 분자량이 20,000인 아크릴 아크릴레이트 수지 100g, 아크릴계 단량체 65g, 광개시제(2-Hydroxy-2-methyl-1-phenyl propan-1-one) 5g 및 램버시안 분포 반사 광확산제(직경이 10㎛인 PMMA 비드) 15g을 혼합하여 제 2도트 조성물을 준비하였다.100 g of acrylic acrylate resin having a weight average molecular weight of 20,000, 65 g of acrylic monomers, 5 g of photoinitiator (2-Hydroxy-2-methyl-1-phenyl propan-1-one), and Lambertian distribution reflective light diffusing agent (diameter of 10 μm) 15 g of PMMA beads) were mixed to prepare a second dot composition.
3) 도광판3) Light guide plate
600mm×600mm의 PMMA시트를 준비하였다.A 600 mm × 600 mm PMMA sheet was prepared.
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 제 1도트 조성물을 사용하여 1차 패턴인쇄 후에 UV광을 조사하여 경화하였다.The 600 mm × 600 mm PMMA sheet was cured by irradiating UV light after primary pattern printing using the first dot composition by inkjet method.
이후에 상기 1차 패턴인쇄된 도트에 인접하도록 잉크젯 방식으로 제 2도트 조성물을 사용하여 2차 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.Subsequently, after the second pattern printing using the second dot composition by an inkjet method so as to be adjacent to the first pattern printed dots, UV light was irradiated and cured to prepare a light guide plate.
실시예Example 2. 제2 2. Second 도트와With dot 제1 First 도트가Dot is 인접된 도광판의 제조 Fabrication of adjacent light guide plates
600mm×600mm의 PMMA시트를 준비하였다.A 600 mm × 600 mm PMMA sheet was prepared.
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 제 2도트 조성물을 사용하여 1차 패턴인쇄 후에 UV광을 조사하여 경화하였다.The 600 mm × 600 mm PMMA sheet was cured by irradiating UV light after the first pattern printing using the second dot composition by an inkjet method.
이후에 상기 1차 패턴인쇄된 도트에 인접하도록 잉크젯 방식으로 제 1도트 조성물을 사용하여 2차 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.Subsequently, after the second pattern printing using the first dot composition by the inkjet method so as to be adjacent to the primary pattern printed dots, UV light was irradiated and cured to prepare a light guide plate.
비교예Comparative example 1. 제1 1. The first 도트dot 도광판의 제조 Manufacture of light guide plate
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 상기 제1 도트 조성물을 사용하여, 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.A light guide plate was manufactured by irradiating and curing UV light after pattern printing using the first dot composition on the 600 mm × 600 mm PMMA sheet by an inkjet method.
비교예Comparative example 2. 제2 2. Second 도트dot 도광판의 제조 Manufacture of light guide plate
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 상기 제2 도트 조성물을 사용하여, 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.Using the second dot composition in the inkjet method to the 600mm × 600mm PMMA sheet, after printing the pattern was irradiated with UV light and cured to prepare a light guide plate.
비교예Comparative example 3. 제1 3. The first 도트dot 인접된 도광판의 제조 Fabrication of adjacent light guide plates
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 제 1도트 조성물을 사용하여 1차 패턴인쇄 후에 UV광을 조사하여 경화하였다.The 600 mm × 600 mm PMMA sheet was cured by irradiating UV light after primary pattern printing using the first dot composition by inkjet method.
이후에 상기 1차 패턴인쇄된 도트에 인접하도록 잉크젯 방식으로 제 1도트 조성물을 사용하여 2차 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.Subsequently, after the second pattern printing using the first dot composition by the inkjet method so as to be adjacent to the primary pattern printed dots, UV light was irradiated and cured to prepare a light guide plate.
비교예Comparative example 4. 제2 4. Second 도트dot 인접된 도광판의 제조 Fabrication of adjacent light guide plates
상기 600mm×600mm의 PMMA시트에 잉크젯 방식으로 제 2도트 조성물을 사용하여 1차 패턴인쇄 후에 UV광을 조사하여 경화하였다.The 600 mm × 600 mm PMMA sheet was cured by irradiating UV light after the first pattern printing using the second dot composition by an inkjet method.
이후에 상기 1차 패턴인쇄된 도트에 인접하도록 잉크젯 방식으로 제 2도트 조성물을 사용하여 2차 패턴인쇄 후에 UV광을 조사하여 경화하여 도광판을 제조하였다.Subsequently, after the second pattern printing using the second dot composition by an inkjet method so as to be adjacent to the first pattern printed dots, UV light was irradiated and cured to prepare a light guide plate.
시험예Test Example
휘도 측정Luminance measurement
상기 실시예 1-2 및 비교예 1-4의 도광판 투명지지체 위에 설계한 제판을 놓고, 실크스크린 인쇄한 후 일정한 도막과 표면상태를 휘도계 (ca-2000)을 사용하여, 일정하게 화면 전체에서 9 point로 나눈 뒤 휘도를 측정하여 평균값을 표 1에 나타내었다.Placing the designed plate on the transparent support of the light guide plate of Example 1-2 and Comparative Example 1-4, after silk-screen printing using a luminance meter (ca-2000), a constant coating film and surface state, evenly throughout the screen After dividing by 9 point, the luminance was measured and the average value is shown in Table 1.
균일도 측정Uniformity Measurement
상기 실시예 1-2 및 비교예 1-4의 도광판 투명지지체 위에 설계한 제판을 놓고, 실크스크린 인쇄한 후 일정한 도막과 표면상태를 휘도계 (ca-2000)을 사용하여, 일정하게 화면 전체에서 9 point로 나눈뒤 휘도를 측정하여 MIN/MAX를 %로 표기해 표 1에 나타내었다..Placing the designed plate on the transparent support of the light guide plate of Example 1-2 and Comparative Example 1-4, after silk-screen printing using a luminance meter (ca-2000), a constant coating film and surface state, evenly throughout the screen After dividing by 9 point, the luminance was measured and MIN / MAX was expressed in%.
상기 휘도 및 균일도 측정 결과 실시예 1-2의 측정값이 비교예 1-4에 비해 높은 수치를 나타내는 것으로 확인되었다.As a result of measuring the brightness and uniformity, it was confirmed that the measured value of Example 1-2 showed a higher value than Comparative Example 1-4.
1 : 제1 도트
2 : 제2 도트
3 : 기재1: first dot
2: second dot
3: description
Claims (3)
상기 기재의 적어도 일면에 형성되며, 조성이 서로 상이한 제1 도트 및 제2 도트로 이루어진 패턴;을 구비하며,
상기 제1 도트와 상기 제2 도트는 상호 인접하는 것을 특징으로 하며,
상기 제1 도트는 우레탄 아크릴레이트 수지 100 중량부에 대하여, 아크릴계 단량체 30 ~ 100 중량부, 광개시제 0.1 ~ 10 중량부 및 가우시안 분포 반사 광확산제 0.1 ~ 30 중량부를 포함하는 조성물이 UV경화되어 형성되고,
상기 제2도트는 아크릴 아크릴레이트 수지 100 중량부에 대하여, 아크릴계 단량체 30 ~ 100 중량부, 광개시제 0.1 ~ 10 중량부 및 램버시안 분포 반사 광확산제 0.1 ~ 30 중량부를 포함하는 조성물이 UV경화되어 형성된 것을 특징으로 하는 도광판.materials; And
A pattern formed on at least one surface of the substrate, the first dot and the second dot having different compositions;
The first dot and the second dot are adjacent to each other,
The first dot is formed by UV curing a composition comprising 30 to 100 parts by weight of an acrylic monomer, 0.1 to 10 parts by weight of a photoinitiator and 0.1 to 30 parts by weight of a Gaussian distribution reflective light diffusing agent, based on 100 parts by weight of a urethane acrylate resin. ,
The second dot is formed by UV curing a composition comprising 30 to 100 parts by weight of the acrylic monomer, 0.1 to 10 parts by weight of the photoinitiator and 0.1 to 30 parts by weight of the Lambertian distribution reflective light diffusing agent, based on 100 parts by weight of the acrylic acrylate resin. Light guide plate, characterized in that.