KR102024258B1 - Pressure sensitive adheisve and flexible organic light emitting diode display device - Google Patents
Pressure sensitive adheisve and flexible organic light emitting diode display device Download PDFInfo
- Publication number
- KR102024258B1 KR102024258B1 KR1020160047770A KR20160047770A KR102024258B1 KR 102024258 B1 KR102024258 B1 KR 102024258B1 KR 1020160047770 A KR1020160047770 A KR 1020160047770A KR 20160047770 A KR20160047770 A KR 20160047770A KR 102024258 B1 KR102024258 B1 KR 102024258B1
- Authority
- KR
- South Korea
- Prior art keywords
- light emitting
- emitting diode
- sensitive adhesive
- pressure
- organic light
- Prior art date
Abstract
본 출원은 점착제 및 이를 포함하는 플렉서블 유기발광다이오드 표시장치에 관한 것으로, 본 출원의 점착제는 플렉서블 유기발광다이오드 표시장치의 박형화, 구조의 단순화와 동시에 광 추출 효율을 증대시킬 수 있다. The present application relates to a pressure-sensitive adhesive and a flexible organic light emitting diode display including the same. The pressure-sensitive adhesive of the present application can increase the light extraction efficiency while reducing the thickness and structure of the flexible organic light emitting diode display.
Description
본 출원은 점착제 및 이를 포함하는 플렉서블 유기발광다이오드 표시장치에 관한 것이다. The present application relates to an adhesive and a flexible organic light emitting diode display device including the same.
최근 본격적인 정보화시대를 맞이하여 전기적 정보신호를 시각적으로 표현하는 디스플레이(display)분야가 급속도로 발전하며 박형화, 경량화, 저소비전력화의 우수한 성능을 가지는 평판 표시장치가 개발되어 사용되고 있다. In recent years, the display field for visually expressing electrical information signals has been rapidly developed in the age of full-scale informatization, and flat panel display devices having excellent performance of thinning, light weight, and low power consumption have been developed and used.
여기서 평판 표시장치 중에서도 액정표시장치(liquid crystal display device: LCD), 유기발광다이오드(organic light emitting diode:OLED) 표시장치가 널리 사용되고 있는 추세에 있다. Liquid crystal display devices (LCDs) and organic light emitting diode (OLED) displays have been widely used among flat panel displays.
특히, 유기발광다이오드 표시장치는 자발광소자를 이용함으로써 별도의 광원인 백라이트 유닛을 필요로 하는 액정표시장치에 비해 경량 박형의 구현이 가능한 이점을 가진다. In particular, the organic light emitting diode display device has a merit of enabling a light weight and thinness as compared to a liquid crystal display device requiring a backlight unit which is a separate light source by using a self-light emitting device.
또한, 유기발광다이오드 표시장치는 액정표시장치에 비해 시야각 및 명암 대비비가 비교적 우수하며 응답속도가 빠르고, 낮은 소비전력을 소모하며 직류 저 전압 구동이 가능하므로 구동회로의 제작 및 설계가 용이한 이점을 가진다. 또한, 내부 구성요소가 고체이기 때문에 외부충격에 강하고, 사용 온도범위도 넓은 장점을 가진다.In addition, the organic light emitting diode display device has a relatively superior viewing angle and contrast ratio compared to the liquid crystal display device, has a fast response speed, consumes low power consumption, enables direct low voltage driving, and thus makes it easy to manufacture and design a driving circuit. Have In addition, since the internal components are solid, they are resistant to external shocks, and have a wide range of use temperature ranges.
이러한 장점들을 가지는 유기발광다이오드 표시장치는, 휴대용 컴퓨터는 물론 데스크톱 컴퓨터 모니터 및 벽걸이 형 텔레비전 등 보다 넓은 사용영역에서 적용될 수 있도록 연구되고 있으며, 특히 보다 넓은 디스플레이 면적을 가질 수 있도록 대면적화 하기 위한 연구가 활발히 진행되고 있다. The organic light emitting diode display device having these advantages is being studied to be applied to a wider use area such as a desktop computer monitor and a wall-mounted television as well as a portable computer, and in particular, a study for large area to have a larger display area has been studied. It is actively underway.
이러한 유기발광다이오드 표시장치는 자발광을 위한 유기발광 층과, 유기발광 층을 발광시키기 위한 제1 및 제2전극으로 이루어지는 유기발광다이오드를 포함하는 표시패널을 포함한다. The organic light emitting diode display device includes a display panel including an organic light emitting layer for self-emission, and an organic light emitting diode including first and second electrodes for emitting the organic light emitting layer.
이러한 유기발광다이오드 표시장치는 제1전극과 제2전극에 전압이 인가되면 제1전극과 제2전극으로부터 각각 주입된 전자와 정공이 유기발광층 내부에서 결합하여 엑시톤(exciton)을 생성하며, 생성된 엑시톤이 여기 상태로부터 기저상태로 떨어지면서 발광하는 원리를 이용한다. In the organic light emitting diode display, when a voltage is applied to the first electrode and the second electrode, electrons and holes injected from the first electrode and the second electrode, respectively, are combined within the organic light emitting layer to generate excitons. Exciton uses the principle of emitting light falling from the excited state to the ground state.
최근에는 플렉서블 표시장치에 대한 관심이 높아지면서 유기발광다이오드 표시장치에 플렉서블 기판을 사용하는 기술에 대한 수요가 증가하고 있다. 그러나 플렉서블 기판을 유기발광다이오드 표시장치에 적용하는 경우 유기발광다이오드 소자 및 플렉서블 기판과 점착제 사이의 굴절률의 차이가 특정 입사각에서 빛이 소재를 투과할 때 나타나는 전반사를 유발하여 소자의 광 효율을 저하시키는 문제점이 있다. 이러한 문제점을 해소하기 위하여 유기발광다이오드 소자의 내부 또는 외부에 광 추출 필름을 배치하는 기술이 알려져 있으나, 이러한 기술은 별도의 광 추출 필름을 제조 및 부착하여야 하므로 공정이 복잡하고, 최종 소자의 두께가 두꺼워지는 단점이 있다. Recently, as the interest in flexible display devices increases, the demand for a technique of using a flexible substrate for an organic light emitting diode display device is increasing. However, when the flexible substrate is applied to the organic light emitting diode display device, the difference in refractive index between the organic light emitting diode device and the flexible substrate and the adhesive causes total reflection when light passes through the material at a specific angle of incidence, thereby reducing the light efficiency of the device. There is a problem. In order to solve this problem, a technique for disposing a light extracting film inside or outside the organic light emitting diode device is known, but such a technique is complicated because a separate light extracting film must be manufactured and attached, and the thickness of the final device is increased. There is a drawback to thickening.
본 출원은 플렉서블 유기발광다이오드 표시장치의 박형화, 구조의 단순화와 동시에 광 추출 효율을 증대시킬 수 있는 점착제 및 이를 포함하는 플렉서블 유기발광다이오드 표시장치를 제공한다. The present application provides a flexible organic light emitting diode display including a pressure-sensitive adhesive that can increase the light extraction efficiency and at the same time thinning the structure of the flexible organic light emitting diode display.
본 출원은 점착제에 관한 것이다. 본 출원의 점착제는 플렉서블 유기발광다이오드 표시장치에 사용될 수 있다. 본 출원의 예시적인 점착제는 점착 수지 및 유무기 복합 입자를 포함할 수 있다. 상기 유무기 복합 입자는 무기 나노 입자를 함유하는 유기 비드일 수 있다. 하나의 예시에서, 상기 투과율이 80% 이상일 수 있다. 하나의 예시에서, 상기 점착제는 헤이즈가 70% 이상일 수 있다.The present application relates to an adhesive. The adhesive of the present application may be used in a flexible organic light emitting diode display. Exemplary pressure-sensitive adhesive of the present application may include a pressure-sensitive adhesive resin and organic-inorganic composite particles. The organic-inorganic composite particles may be organic beads containing inorganic nanoparticles. In one example, the transmittance may be 80% or more. In one example, the pressure-sensitive adhesive may have a haze of 70% or more.
본 출원의 점착제는 고 투과율, 고 굴절률 및 고 헤이즈를 가지므로, 유기발광다이오드 소자 및 플렉서블 기판과의 굴절률 차이를 감소시켜 각 층 사이의 굴절률 격차에서 발생하는 전반사를 줄일 수 있고, 비드에 의한 광산란 효과로 인해 광 추출 효율을 증대시킬 수 있다. 또한, 본 출원은 유기발광다이오드 소자에 별도의 광추출 필름을 사용하는 대신 점착제의 투과율을 저하시키지 않으면서 굴절률 및 헤이즈를 높이는 기술이므로, 소자의 박형화 및 구조의 단순화와 동시에 광 추출 효율을 증대시킬 수 있다. Since the pressure-sensitive adhesive of the present application has a high transmittance, a high refractive index, and a high haze, the difference in refractive index between the organic light emitting diode device and the flexible substrate can be reduced to reduce the total reflection occurring in the refractive index gap between the layers, and light scattering by the beads The effect can increase the light extraction efficiency. In addition, the present application is a technology to increase the refractive index and haze without lowering the transmittance of the pressure-sensitive adhesive instead of using a separate light extraction film for the organic light emitting diode device, it is possible to increase the light extraction efficiency while at the same time thinning and simplifying the structure of the device Can be.
이하, 본 출원의 점착제에 대하여 구체적으로 설명한다.Hereinafter, the adhesive of this application is demonstrated concretely.
하나의 예시에서, 유무기 복합 입자는 상기 점착 수지에 분산된 상태로 존재할 수 있다. 유무기 복합 입자는 무기 입자와 비교하여 유기 매질과의 계면 속성이 비슷하며 밀도가 낮아 유기 비드 매질 내 분산이 용이하다는 장점이 있다. 따라서, 유무기 복합 입자를 사용하는 경우 광 추출 성능을 더욱 향상시킬 수 있다.In one example, the organic-inorganic composite particles may be present in a dispersed state in the adhesive resin. The organic-inorganic composite particles have an advantage of having similar interfacial properties with the organic medium and lower density than the inorganic particles, so that the organic-inorganic composite particles can be easily dispersed in the organic bead medium. Therefore, when using the organic-inorganic composite particles can further improve the light extraction performance.
하나의 예시에서, 점착 수지로는 플렉서블 유기발광다이오드 표시장치에 사용될 수 있는 것으로 공지된 점착 수지를 사용할 수 있다. 점착 수지로는 예를 들어 아크릴레이트 수지, 실리콘 수지, 러버 수지, 스티렌 수지, 에폭시 수지 폴리올레핀 수지, 폴리옥시알킬렌 수지, 폴리에스테르 수지, 폴리염화비닐 수지, 폴리카보네이트 수지 및 폴리아미드 수지로 이루어지는 군으로부터 선택되는 1종 이상을 사용할 수 있다. 본 출원의 일 실시예에 의하면 점착 수지로 아크릴레이트 수지를 사용할 수 있고, 보다 구체적으로 부틸아크릴레이트(Butyl acrylate), 이소보닐아크릴레이트(Isobornyl acrylate), 페녹시에틸아크릴레이트(Phenoxyethyl acrylate) 및 2-히드록시에틸아크릴레이트(2-Hydroxyethyl acrylate)의 공중합체를 사용할 수 있다.In one example, the adhesive resin may be an adhesive resin known to be used in a flexible organic light emitting diode display. As adhesive resin, the group which consists of an acrylate resin, a silicone resin, a rubber resin, a styrene resin, an epoxy resin polyolefin resin, a polyoxyalkylene resin, a polyester resin, a polyvinyl chloride resin, a polycarbonate resin, and a polyamide resin, for example One or more types selected from can be used. According to the exemplary embodiment of the present application, an acrylate resin may be used as the adhesive resin, and more specifically, butyl acrylate, isobornyl acrylate, phenoxyethyl acrylate, and 2 Copolymers of 2-hydroxyethyl acrylate may be used.
하나의 예시에서, 유무기 복합 입자는 점착 수지 100 중량부에 대하여 10 내지50의 중량부 비율로 포함될 수 있다. 상기 함량 비율을 만족하는 경우 점착제의 광 추출 효율을 효과적으로 증대시킬 수 있다. In one example, the organic-inorganic composite particles may be included in a proportion of 10 to 50 parts by weight based on 100 parts by weight of the adhesive resin. When the content ratio is satisfied, the light extraction efficiency of the pressure-sensitive adhesive can be effectively increased.
도 4는 상기 유무기 복합 입자의 구조를 예시적으로 나타낸다. 유무기 복합 입자는 무기 나노 입자(1)를 함유하는 유기 비드(2)일 수 있다. 본 명세서에서 유기 비드는 유기물로 이루어지는 구형 입자를 의미할 수 있다. 무기 나노 입자는 유기 비드 내에 분산된 상태로 존재할 수 있다. 4 exemplarily shows a structure of the organic-inorganic composite particles. The organic-inorganic composite particles may be
하나의 예시에서, 유무기 복합 입자는 비닐계 단량체의 가교 폴리머를 포함하는 비드 및 상기 비드의 가교 구조 내에 무기 나노 입자를 포함할 수 있다. In one example, the organic-inorganic composite particles may include beads including a crosslinked polymer of a vinyl monomer and inorganic nanoparticles in the crosslinked structure of the beads.
하나의 예시에서, 유무기 복합 입자는 수계 분산액에 단량체 혼합물을 첨가하여 액적 형태로 분산시켜 균질화시킨 후 반응시킴으로써 제조할 수 있다. 수계 분산액으로는 예를 들어 물, 인산나트륨, 염화칼슘 및 염산을 혼합하고 교반하여 인산칼슘결정이 석출된 형태의 수계 분산액을 사용할 수 있다. 단량체 혼합물은 예를 들어 비닐계 단량체, 가교제, 전하조절제, 무기 나노 입자 분산액 및 개시제를 포함할 수 있다. 비닐계 단량체로는 예를 들어 스티렌을 사용할 수 있고, 가교제로는 예를 들어 디비닐벤젠을 사용할 수 있으며, 전하조절제로는 설폰산기를 포함한 스티렌-아크릴계 고분자 전하조절제를 사용할 수 있고, 개시제로는 아조니트릴계 개시제를 사용할 수 있다. In one example, the organic-inorganic composite particles can be prepared by adding a monomer mixture to the aqueous dispersion, dispersing it in the form of droplets, homogenizing and reacting. As the aqueous dispersion, for example, water, sodium phosphate, calcium chloride and hydrochloric acid may be mixed and stirred to form an aqueous dispersion in which calcium phosphate crystals are precipitated. The monomer mixture may include, for example, a vinyl monomer, a crosslinking agent, a charge control agent, an inorganic nanoparticle dispersion and an initiator. Styrene may be used as the vinyl monomer, for example, divinylbenzene may be used as the crosslinking agent, and a styrene-acrylic polymer charge controlling agent including a sulfonic acid group may be used as the charge control agent. Azonitrile-based initiators can be used.
하나의 예시에서, 유무기 복합 입자는 고 굴절률 입자일 수 있다. 하나의 예로, 유무기 복합 입자의 400nm 내지 800nm파장의 광에 대한 굴절률은 1.4 내지 2.0일 수 있다. 이러한 유무기 복합 입자는 점착제의 굴절률을 증가시키므로 전반사 감소와 함께 광 산란 효과로 인해 광추출 효율을 향상시킬 수 있다. 유무기 복합 입자의 굴절률은 유기 비드 내의 무기 나노 입자의 함량을 조절함으로써 조절할 수 있다.In one example, the organic-inorganic composite particles can be high refractive index particles. As an example, the refractive index of the organic-inorganic composite particles with respect to light of 400 nm to 800 nm wavelength may be 1.4 to 2.0. Since the organic-inorganic composite particles increase the refractive index of the pressure-sensitive adhesive, it is possible to improve the light extraction efficiency due to the light scattering effect with the total reflection decrease. The refractive index of the organic-inorganic composite particles can be controlled by adjusting the content of the inorganic nanoparticles in the organic beads.
본 명세서에서 특별한 언급이 없는 한 굴절률은 공지의 굴절률 측정 장비, 예를 들어 Prism Coupler SPA-4000 장비를 이용하여, 약 400nm 내지 800nm, 예를 들어, 약 632.8 nm 파장의 광에 대하여 측정한 값일 수 있다. Unless stated otherwise in the present specification, the refractive index may be a value measured for light having a wavelength of about 400 nm to 800 nm, for example, about 632.8 nm, using a known refractive index measuring apparatus such as a Prism Coupler SPA-4000 apparatus. have.
하나의 예시에서, 유무기 복합 입자의 입경은 1㎛ 내지 5㎛ 일 수 있다. 유무기 복합 입자의 입경이 상기 범위를 만족하는 경우 점착제의 투과율을 감소시키지 않으면서 헤이즈를 증가시킬 수 있으므로 광 추출 효율을 효과적으로 증대시킬 수 있다. 입자 크기로 인한 광산란 효과는 광 추출 효율을 높여주며, 광산란 효과로 인하여 점착제의 헤이즈가 증가될 수 있다.In one example, the particle size of the organic-inorganic composite particles may be 1㎛ to 5㎛. When the particle diameter of the organic-inorganic composite particles satisfies the above range, the haze can be increased without reducing the transmittance of the pressure-sensitive adhesive, so that the light extraction efficiency can be effectively increased. The light scattering effect due to the particle size increases the light extraction efficiency, and the haze of the pressure-sensitive adhesive may be increased due to the light scattering effect.
하나의 예시에서, 무기 나노 입자는 고 굴절률 입자일 수 있다. 하나의 예로, 무기 나노 입자는 400 nm 내지 800 nm 파장의 광에 대한 굴절률이 2.0 내지 2.5일 수 있다. 이러한 무기 나노 입자는 점착제의 굴절률을 증가시키므로 전반사 감소 효과로 인해 광추출 효율을 향상시킬 수 있다.In one example, the inorganic nanoparticles can be high refractive index particles. As one example, the inorganic nanoparticles may have a refractive index of 2.0 to 2.5 for light having a wavelength of 400 nm to 800 nm. Since the inorganic nanoparticles increase the refractive index of the adhesive, the light extraction efficiency can be improved due to the total reflection reduction effect.
하나의 예시에서, 무기 나노 입자의 입경은 1 nm 이상 내지 50 nm 이하일 수 있다. 무기 나노 입자의 입경이 상기 범위를 만족하는 경우 유기 비드 내에 분산 안정성을 확보하여 광 추출 효율을 효과적으로 증대시킬 수 있다.In one example, the particle diameter of the inorganic nanoparticles may be 1 nm or more and 50 nm or less. When the particle diameter of the inorganic nanoparticles satisfies the above range, the dispersion stability may be secured in the organic beads to effectively increase the light extraction efficiency.
하나의 예시에서, 무기 나노 입자로는 금속 산화물을 사용할 수 있다. 무기 나노 입자로는 예를 들어 이산화규소(SiO2), 산화알루미늄(Al2O3), 산화티타늄(TiO2), 산화주석(SnO2), 산화철(FeO3), 산화아연(ZnO), 산화마그네슘(MgO), 산화지르코늄(ZrO2), 산화세륨(CeO2), 산화 리튬(LiO2), 산화은(AgO) 및 산화안티몬(Sb2O3)로 이루어진 군으로부터 선택되는 1종 이상의 금속 산화물을 사용할 수 있다. 본 출원의 일 실시예에 의하면 산화지르코늄(ZrO2)를 사용할 수 있다. In one example, a metal oxide may be used as the inorganic nanoparticles. Examples of the inorganic nanoparticles include silicon dioxide (SiO 2 ), aluminum oxide (Al 2 O 3 ), titanium oxide (TiO 2 ), tin oxide (SnO 2 ), iron oxide (FeO 3 ), zinc oxide (ZnO), At least one metal selected from the group consisting of magnesium oxide (MgO), zirconium oxide (ZrO 2 ), cerium oxide (CeO 2 ), lithium oxide (LiO 2 ), silver oxide (AgO), and antimony oxide (Sb 2 O 3 ) Oxides can be used. According to one embodiment of the present application, zirconium oxide (ZrO 2 ) may be used.
하나의 예시에서, 유기 비드로는 폴리스티렌 및 폴리메틸메타아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상을 사용할 수 있다. In one example, the organic beads may be used one or more selected from the group consisting of polystyrene and polymethyl methacrylate.
하나의 예시에서, 유무기 복합 입자 내 무기 나노 입자의 함량은 10 중량% 내지 30 중량%일 수 있다. 함량 비율이 이를 만족하는 경우 광 추출 효율을 효과적으로 증대시킬 수 있다. 본 출원의 일 실시예에 의하면 유무기 복합 입자 내 무기 나노 입자의 함량은 약 20 중량%일 수 있다. In one example, the content of the inorganic nanoparticles in the organic-inorganic composite particles may be 10% by weight to 30% by weight. If the content ratio satisfies this, the light extraction efficiency can be effectively increased. According to an embodiment of the present application, the content of the inorganic nanoparticles in the organic-inorganic composite particles may be about 20 wt%.
점착제의 두께는 본 출원의 목적을 고려하여 적절히 선택될 수 있다. 하나의 예시에서, 점착제의 두께는 15㎛ 내지 25㎛일 수 있다. 점착제의 두께가 상기 범위를 만족하는 경우 광 추출 효율을 효과적으로 증대시킬 수 있다. 점착제의 두께가 너무 얇은 경우 제조가 어려우며 광 산란 효과가 저감되는 측면이 있고, 점착제의 두께가 너무 두꺼운 경우 점착제의 투과율이 감소될 수 있다.The thickness of the pressure-sensitive adhesive may be appropriately selected in consideration of the purpose of the present application. In one example, the adhesive may have a thickness of 15 μm to 25 μm. When the thickness of the adhesive satisfies the above range, the light extraction efficiency can be effectively increased. When the thickness of the pressure-sensitive adhesive is too thin, it is difficult to manufacture and the light scattering effect is reduced, and when the thickness of the pressure-sensitive adhesive is too thick, the transmittance of the pressure-sensitive adhesive may be reduced.
본 출원의 점착제는 고 굴절율을 나타낼 뿐만 아니라, 고 투과율 및 고 헤이즈를 나타낼 수 있다. The pressure-sensitive adhesive of the present application may exhibit high refractive index as well as high transmittance and high haze.
하나의 예시에서, 점착제의 투과율은 80% 이상, 구체적으로 85% 이상, 보다 구체적으로 88% 이상일 수 있다. 본 명세서에서 투과율은 400 nm 내지 800 nm 파장의 광에 대한 투과율을 의미할 수 있다. 하나의 예로, 본 명세서에서 투과율은 400 nm 내지 800 nm 파장 중 어느 하나의 파장의 광에 대한 투과율, 혹은 400 nm 내지 800 nm 파장의 광에 대한 평균 투과율을 의미할 수 있다. 이와 같이, 점착제가 높은 투과율을 나타내는 경우 광 효율을 더욱 증대시킬 수 있다. In one example, the transmittance of the pressure-sensitive adhesive may be at least 80%, specifically at least 85%, more specifically at least 88%. In the present specification, the transmittance may mean transmittance for light having a wavelength of 400 nm to 800 nm. As one example, in the present specification, the transmittance may mean a transmittance for light of any wavelength of 400 nm to 800 nm, or an average transmittance for light of 400 nm to 800 nm. As such, when the pressure-sensitive adhesive exhibits high transmittance, the light efficiency can be further increased.
하나의 예시에서, 점착제의 헤이즈는 70% 이상, 구체적으로 80% 이상, 보다 구체적으로 90%일 수 있다. 이와 같이 점착제가 높은 헤이즈를 나타내는 경우 산란 효과 증대로 인하여 광 추출 효율을 효과적으로 증대시킬 수 있다. In one example, the haze of the pressure sensitive adhesive may be at least 70%, specifically at least 80%, more specifically at 90%. As such, when the pressure-sensitive adhesive exhibits high haze, light extraction efficiency may be effectively increased due to an increase in scattering effects.
본 출원은 또한 플렉서블 유기발광다이오드 표시장치에 관한 것이다. 본 출원의 예시적인 표시장치는 상기 점착제, 플렉서블 기판 및 유기발광다이오드 소자를 포함할 수 있다. The present application also relates to a flexible organic light emitting diode display. An exemplary display device of the present application may include the adhesive, the flexible substrate, and the organic light emitting diode device.
도 1은 본 출원의 제 1 실시예의 표시장치를 예시적으로 나타낸다. 도 1에 따르면, 상기 점착제(10)는 플렉서블 기판(20의 일면에 존재하고, 유기발광다이오드 소자(30)는 플렉서블 기판의 상기 점착제 반대 측에 배치될 수 있다. 1 exemplarily shows a display device of a first embodiment of the present application. According to FIG. 1, the pressure-
플렉서블 기판으로는 플렉서블 표시장치에 사용되는 것으로 공지된 플렉서블 기판을 사용할 수 있다. 플렉서블 기판으로는 폴리에테르술폰, 폴리에틸렌나프탈레이트, 폴리에틸렌테레프탈레이트, 폴리카보네이트 및 폴리이미드로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 기판을 사용할 수 있다. As the flexible substrate, a flexible substrate known to be used in a flexible display device may be used. As the flexible substrate, a substrate containing at least one member selected from the group consisting of polyether sulfone, polyethylene naphthalate, polyethylene terephthalate, polycarbonate and polyimide can be used.
플렉서블 기판의 400 nm 내지 800 nm 파장의 광에 대한 굴절률이 1.45 내지 1.75일 수 있다. 본 출원의 점착제는 이러한 플렉서블 기판과의 굴절률 차이를 감소시켜 전반사를 감소시켜 광 추출 효율을 증가시킬 수 있다. The refractive index of light of 400 nm to 800 nm of the flexible substrate may be 1.45 to 1.75. The pressure-sensitive adhesive of the present application may increase light extraction efficiency by reducing total reflection by reducing a difference in refractive index with the flexible substrate.
유기발광다이오드 소자는 대향 배치된 제1 및 제 2 전극 및 상기 제 1 및 제 2 전극 사이에 유기발광 층을 포함할 수 있다. 이하에서 구별을 위하여 플렉서블 기판에 인접한 전극을 제 1 전극으로 호칭하고, 반대 측 전극을 제 2 전극으로 호칭한다. The organic light emitting diode device may include an organic light emitting layer between the first and second electrodes disposed opposite to each other and the first and second electrodes. In the following description, the electrode adjacent to the flexible substrate is referred to as a first electrode, and the opposite electrode is referred to as a second electrode.
하나의 예시에서, 제 1 전극을 투명 전극으로 하고 제 2 전극을 반사 전극으로 하는 경우 유기발광 층에서 발생한 광이 기판 측으로 방사되는 하부 발광형 소자를 구현할 수 있다.In one example, when the first electrode is a transparent electrode and the second electrode is a reflective electrode, a lower light emitting device in which light generated in the organic light emitting layer is radiated to the substrate side may be implemented.
유기발광 층은, 예를 들면, 이 분야에 공지된 다양한 형광 또는 인광 유기 재료를 사용하여 형성할 수 있다. 발광층의 재료로는, 트리스(4-메틸-8-퀴놀리놀레이트)알루미늄(III)(tris(4-methyl-8-quinolinolate)aluminum(III))(Alg3), 4-MAlq3 또는 Gaq3 등의 Alq 계열의 재료, C-545T(C26H26N2O2S), DSA-아민, TBSA, BTP, PAP-NPA, 스피로-FPA, Ph3Si(PhTDAOXD), PPCP(1,2,3,4,5-pentaphenyl-1,3-cyclopentadiene) 등과 같은 시클로페나디엔(cyclopenadiene) 유도체, DPVBi(4,4’-bis(2,2’-diphenylyinyl)-1,1’-biphenyl), 디스티릴 벤젠 또는 그 유도체 또는 DCJTB(4-(Dicyanomethylene)-2-tert-butyl-6-(1,1,7,7,-tetramethyljulolidyl-9-enyl)-4H-pyran), DDP, AAAP, NPAMLI, ; 또는 Firpic, m-Firpic, N-Firpic, bon2Ir(acac), (C6)2Ir(acac), bt2Ir(acac), dp2Ir(acac), bzq2Ir(acac), bo2Ir(acac), F2Ir(bpy), F2Ir(acac), op2Ir(acac), ppy2Ir(acac), tpy2Ir(acac), FIrppy(fac-tris[2-(4,5’-difluorophenyl)pyridine-C’2,N] iridium(III)) 또는 Btp2Ir(acac)(bis(2-(2’-benzo[4,5-a]thienyl)pyridinato-N,C3’) iridium(acetylactonate)) 등과 같은 인광 재료 등이 예시될 수 있지만, 이에 제한되는 것은 아니다. 발광층은, 상기 재료를 호스트(host)로 포함하고, 또한 페릴렌(perylene), 디스티릴비페닐(distyrylbiphenyl), DPT, 퀴나크리돈(quinacridone), 루브렌(rubrene), BTX, ABTX 또는 DCJTB 등을 도펀트로 포함하는 호스트-도펀트 시스템(Host-Dopant system)을 가질 수도 있다.The organic light emitting layer can be formed using, for example, various fluorescent or phosphorescent organic materials known in the art. Examples of the material of the light emitting layer include tris (4-methyl-8-quinolinolate) aluminum (III) (tris (4-methyl-8-quinolinolate) aluminum (III)) (Alg3), 4-MAlq3 or Gaq3. Alq series materials, C-545T (C 26 H 26 N 2 O 2 S), DSA-amine, TBSA, BTP, PAP-NPA, Spiro-FPA, Ph 3 Si (PhTDAOXD), PPCP (1,2,3 Cyclopenadiene derivatives such as, 4,5-pentaphenyl-1,3-cyclopentadiene), DPVBi (4,4'-bis (2,2'-diphenylyinyl) -1,1'-biphenyl), distyryl Benzene or derivatives thereof or DCJTB (4- (Dicyanomethylene) -2-tert-butyl-6- (1,1,7,7, tetramethyljulolidyl-9-enyl) -4H-pyran), DDP, AAAP, NPAMLI,; Or Firpic, m-Firpic, N-Firpic, bon 2 Ir (acac), (C 6 ) 2 Ir (acac), bt 2 Ir (acac), dp 2 Ir (acac), bzq 2 Ir (acac), bo 2 Ir (acac), F 2 Ir (bpy), F 2 Ir (acac), op 2 Ir (acac), ppy 2 Ir (acac), tpy 2 Ir (acac), FIrppy (fac-tris [2- ( 4,5'-difluorophenyl) pyridine-C'2, N] iridium (III)) or Btp 2 Ir (acac) (bis (2- (2'-benzo [4,5-a] thienyl) pyridinato-N, Phosphorescent materials such as C3 ') iridium (acetylactonate)) and the like can be exemplified, but is not limited thereto. The light emitting layer includes the material as a host, and further includes perylene, distyrylbiphenyl, DPT, quinacridone, rubrene, BTX, ABTX, or DCJTB. It may have a host-dopant system including a dopant.
유기발광다이오드 소자는 유기발광 층을 포함하는 한 이 분야에 공지된 다른 다양한 기능성층을 추가로 포함하는 다양한 구조로 형성될 수 있고, 상기 기능성층으로는 전자 주입층, 정공 저지층, 전자 수송층, 정공 수송층 및 정공 주입층 등이 예시될 수 있다.The organic light emitting diode device may be formed in various structures further including various other functional layers known in the art as long as the organic light emitting diode is included, and the functional layer may include an electron injection layer, a hole blocking layer, an electron transport layer, A hole transport layer, a hole injection layer, etc. can be illustrated.
하나의 예시에서, 플렉서블 기판 상에는 화소 구동 층이 형성될 수 있고, 유기발광다이오드 소자는 상기 화소 구동 층 상에 형성될 수 있다. 화소 구동 층은 예를 들어 구동 박막트랜지스터와 스위칭 박막트랜지스터 및 컬러필터 층을 포함할 수 있다. In one example, a pixel driving layer may be formed on the flexible substrate, and an organic light emitting diode device may be formed on the pixel driving layer. The pixel driving layer may include, for example, a driving thin film transistor, a switching thin film transistor, and a color filter layer.
상기 표시장치는 필요에 따라 추가로 봉지 구조를 더 포함할 수 있다. 상기 봉지 구조는, 유기발광다이오드 소자의 유기발광 층으로 수분이나 산소 등과 같은 외래 물질이 유입되지 않도록 하는 보호 구조일 수 있다. 봉지 구조는, 예를 들면, 글라스캔 또는 금속캔 등과 같은 캔이거나, 상기 유기발광 층의 전면을 덮고 있는 필름일 수 있다.The display device may further include an encapsulation structure as needed. The encapsulation structure may be a protective structure to prevent foreign substances such as moisture or oxygen from flowing into the organic light emitting layer of the organic light emitting diode device. The encapsulation structure may be, for example, a can such as a glass can or a metal can, or a film covering the entire surface of the organic light emitting layer.
상기 표시장치는 배리어 층을 더 포함할 수 있다. 본 명세서서 용어 「배리어층」은 대기 중의 산소, 수분, 질소 산화물, 황 산화물 또는 오존의 투과를 방지하는 기능을 갖는 층을 의미할 수 있다. 배리어 층은 상기 기능을 갖는 한, 특별히 한정되지 않으며 의도된 용도에 따라서 적합하게 선택될 수 있다.The display device may further include a barrier layer. As used herein, the term "barrier layer" may mean a layer having a function of preventing permeation of oxygen, moisture, nitrogen oxides, sulfur oxides, or ozone in the atmosphere. The barrier layer is not particularly limited as long as it has the above function, and may be appropriately selected depending on the intended use.
상기 배리어 층은 유기발광다이오드 소자와 플렉서블 기판의 사이에 존재하거나 또는 상기 점착제의 플렉서블 기판의 반대 측면에 존재할 수 있다. 유기발광다이오드 소자와 플렉서블 기판의 사이에 존재하는 경우 내부 배리어 층으로 호칭하고, 상기 점착제의 플렉서블 기판의 반대 측면에 존재하는 경우 외부 배리어 층으로 호칭할 수 있다. The barrier layer may be present between the organic light emitting diode device and the flexible substrate or on an opposite side of the flexible substrate of the pressure-sensitive adhesive. When present between the organic light emitting diode device and the flexible substrate may be referred to as the inner barrier layer, and when present on the opposite side of the flexible substrate of the pressure-sensitive adhesive may be referred to as the outer barrier layer.
도 2는 본 출원 제 2 실시예의 표시장치를 예시적으로 나타낸다. 도 2에 도시된 바와 같이 표시장치는 점착제(10), 플렉서블 기판(20), 내부 배리어층(40) 및 유기발광다이오드 소자(30)을 순차로 포함할 수 있다. 도 3은 본 출원 제 3 실시예의 표시장치를 예시적으로 나타낸다. 도 3에 도시된 바와 같이 표시장치는 외부 배리어 층(50), 점착제(10), 플렉서블 기판(20), 내부 배리어층(40) 및 유기발광다이오드 소자(30)을 순차로 포함할 수 있다.2 exemplarily shows a display device of the second embodiment of the present application. As illustrated in FIG. 2, the display device may sequentially include an adhesive 10, a
배리어층의 재료는 수분 및 산소 등의 소자 열화를 촉진하는 물질들이 소자로 들어가는 것을 방지하는 기능을 갖는 재료일 수 있다. 배리어층의 구체적인 예는 배리어층의 구체적인 예는 In, Sn, Pb, Au, Cu, Ag, Al, Ti 및 Ni 등의 금속; TiO, TiO2, Ti3O3 , Al2O3, MgO, SiO, SiO2, GeO, NiO, CaO, BaO, Fe2O3, Y2O3, ZrO2, Nb2O3 및, CeO2및 등의 금속 산화물; SiN 등의 금속 질화물; SiON 등의 금속 산질화물; MgF2, LiF, AlF3 및 CaF2 등의 금속 불화물; 폴리에틸렌, 폴리프로필렌, 폴리메틸메타크릴레이트, 폴리이미드, 폴리우레아, 폴리테트라플루오로에틸렌, 폴리클로로트리플루오로에틸렌, 폴리디클로로디플루오로에틸렌, 또는 클로로트리플루오로에틸렌과 디클로로디플루오로에틸렌의 공중합체; 적어도 1종의 코모노머를 포함한 코모노머 혼합물과 테트라플루오로에틸렌의 공중합에 의해 획득된 공중합체; 공중합 주쇄에 환상 구조를 갖는 함불소 공중합체; 흡수율 1% 이상인 흡수성 재료; 및 흡수 계수 0.1% 이하인 방습성 재료를 포함한다.The material of the barrier layer may be a material having a function of preventing substances entering the device, such as moisture and oxygen, from degrading the device. Specific examples of the barrier layer include specific examples of the barrier layer include metals such as In, Sn, Pb, Au, Cu, Ag, Al, Ti, and Ni; TiO, TiO 2 , Ti 3 O 3 , Al 2 O 3 , MgO, SiO, SiO 2 , GeO, NiO, CaO, BaO, Fe 2 O 3 , Y2O 3 , ZrO 2 , Nb 2 O 3 and CeO 2 and Metal oxides such as; Metal nitrides such as SiN; Metal oxynitrides such as SiON; Metal fluorides such as MgF 2 , LiF, AlF 3 and CaF 2 ; Polyethylene, polypropylene, polymethylmethacrylate, polyimide, polyurea, polytetrafluoroethylene, polychlorotrifluoroethylene, polydichlorodifluoroethylene, or chlorotrifluoroethylene and dichlorodifluoroethylene Copolymers; Copolymers obtained by copolymerizing a comonomer mixture comprising at least one comonomer with tetrafluoroethylene; Fluorine-containing copolymer which has a cyclic structure in a copolymer main chain; An absorbent material having an absorption rate of 1% or more; And a moisture proof material having an absorption coefficient of 0.1% or less.
하나의 예시에서, 배리어층의 단층 구조이거나 또는 복층 구조일 수 있다. 예를 들면, 배리어층은, Al2O3층 및 TiO2층이 순차적으로 적층된 복층 구조 일 수 있다. In one example, the barrier layer may be a single layer structure or a multilayer structure. For example, the barrier layer may be an Al 2 O 3 layer and It may be a multilayer structure in which the TiO 2 layers are sequentially stacked.
본 출원의 점착제가 플렉서블 유기발광다이오드 표시장치에 적용될 경우에 그 밖의 다른 부품이나 그 장치의 구성 방법은 특별히 제한되지 않고, 상기 점착제가 적용되는 한 해당 분야에서 공지되어 있는 임의의 재료나 방식이 모두 채용될 수 있다.When the pressure-sensitive adhesive of the present application is applied to the flexible organic light emitting diode display device, any other component or a method of configuring the device is not particularly limited, and any material or method known in the art may be used as long as the pressure-sensitive adhesive is applied. Can be employed.
본 출원은 플렉서블 유기발광다이오드 표시장치의 박형화, 구조의 단순화와 동시에 광 추출 효율을 증대시킬 수 있는 점착제 및 이를 포함하는 플렉서블 유기발광다이오드 표시장치를 제공한다. The present application provides a flexible organic light emitting diode display including a pressure-sensitive adhesive that can increase the light extraction efficiency and at the same time thinning the structure of the flexible organic light emitting diode display.
도 1은 본 출원 제 1 실시예의 표시장치의 모식도이다.
도 2는 본 출원 제 2 실시예의 표시장치의 모식도이다.
도 3은 본 출원 제 3 실시예의 표시장치의 모식도이다.
도 4는 유무기 복합 입자의 단면 모식도이다. 1 is a schematic view of a display device of a first embodiment of the present application.
2 is a schematic view of a display device of a second embodiment of the present application.
3 is a schematic view of a display device of a third embodiment of the present application.
4 is a cross-sectional schematic diagram of organic-inorganic composite particles.
이하, 본 출원에 따른 실시예 및 본 출원에 따르지 않는 비교예를 통하여 본 출원을 보다 구체적으로 설명하지만, 본 출원의 범위가 하기 제시된 실시예에 의해 제한되는 것은 아니다.Hereinafter, the present application will be described in more detail through examples according to the present application and comparative examples not according to the present application, but the scope of the present application is not limited to the examples given below.
측정예Measurement example 1. 투과율 측정 1. Transmittance Measurement
Nippon denshoku 400 장비를 이용하여 400nm 내지 800nm 파장의 광에 대한 투과율을 측정하였다.The transmittance of light with a wavelength of 400 nm to 800 nm was measured using a Nippon denshoku 400 device.
측정예Measurement example 2 2 헤이즈Haze 측정 Measure
Nippon denshoku 400 장비를 이용하여 헤이즈를 측정하였다.Haze was measured using a Nippon denshoku 400 instrument.
평가예Evaluation example 1 양자 효율 평가 1 Quantum Efficiency Assessment
OTSUKA사의 적분반구 장치를 이용하여 양자 효율을 측정하였다.Quantum efficiency was measured using an integrating hemisphere apparatus of OTSUKA Corporation.
실시예Example 1 One
유무기 복합 입자의 제조Preparation of Organic-Inorganic Composite Particles
<유무기 입자 제조 방법><Organic inorganic particle manufacturing method>
1. 수계 분산액 제조 단계: 물 200g에 인산나트륨 6.5g, 1M 염화칼슘 25.2g, 35% 염산 0.8g을 혼합하고, 20분간 교반하여 인산칼슘 결정이 석출된 형태의 수계 분산액을 제조하였다.1. Preparation of Aqueous Dispersion: 200 g of water was mixed with 6.5 g of sodium phosphate, 25.2 g of 1M calcium chloride, and 0.8 g of 35% hydrochloric acid, and stirred for 20 minutes to prepare an aqueous dispersion in which calcium phosphate crystals were precipitated.
2. 단량체 혼합물 제조 단계: 스티렌(Styrene) 28.6g, 가교제로 디비닐벤젠(Divinyl benzene) 3.2g, 중량 평균 분자량이 16,500인 설폰산기를 포함한 스티렌-아크릴계 고분자 전하조절제 1.2g, 30% 지르코니아 분산액 (ZA10, CIK NANOTEK) 27g을 혼합한다. 아조니트릴계 개시제(Azo nitrile: V65, Waco Chemical) 0.6g을 첨가하고 5분간 추가로 교반하여 단량체 혼합물을 제조하였다.2. Preparation of monomer mixture: 28.6 g of styrene, 3.2 g of divinyl benzene as crosslinking agent, 1.2 g of styrene-acrylic polymer charge control agent containing sulfonic acid group having a weight average molecular weight of 16,500, 30% zirconia dispersion ( Mix 27 g of ZA10, CIK NANOTEK). 0.6 g of azo nitrile initiator (Azo nitrile: V65, Waco Chemical) was added and stirred for 5 minutes to prepare a monomer mixture.
3. 균질화 단계: 상기 수계 분산액에 상기 단량체 혼합물을 첨가하고, 호모게나이저를 이용하여 13,000rpm의 속도로 전단력을 가하여 상기 수계 분산액에 상기 단량체 혼합물을 미세한 액적 형태로 분산시켜 균질화하였다.3. Homogenization step: The monomer mixture was added to the aqueous dispersion, and a homogenizer was used to apply shear force at a rate of 13,000 rpm to homogenize the monomer mixture in the aqueous dispersion by dispersing it in the form of fine droplets.
4. 입자 제조: 상기 균질화를 통하여 미세한 액적 형태로 상기 수계 분산액에 분산된 단량체 혼합물을 패들 형식의 교반기로 400rpm에서 교반하면서 60℃에서 15시간 동안 반응하여 최종적으로 지르코니아가 분산된 고분자 입자 슬러리를 제조하였다.4. Particle preparation: Through the homogenization, the monomer mixture dispersed in the aqueous dispersion in the form of fine droplets was reacted at 60 ° C. for 15 hours while stirring at 400 rpm with a paddle type stirrer to finally prepare a slurry of polymer particles in which zirconia was dispersed. It was.
<입자 세척 및 건조>Particle Wash and Dry
1. 세척 단계: 지르코니아가 분산된 고분자 입자의 슬러리에 염산을 첨가하여 pH를 2이하로 조정하고, 인산칼슘을 용해시켰다. 그리고, 여과장치를 이용하여 물을 제거한 후, 전체 중량 대비 2배의 증류수를 첨가하여 희석하고, 다시 물을 제거하는 과정을 반복적으로 진행하여 고분자 입자 표면의 인산칼슘 및 기타 불순물을 제거하였다.1. Washing step: pH was adjusted to 2 or less by adding hydrochloric acid to a slurry of polymer particles in which zirconia was dispersed, and calcium phosphate was dissolved. Then, after the water was removed using a filtration apparatus, distilled water twice as much as the total weight was added and diluted, and the water was repeatedly removed to remove calcium phosphate and other impurities on the surface of the polymer particles.
2. 건조 단계: 최종적으로 여과를 통해 수분을 제거한 후, 진공 오븐에 넣고 48시간 상온에서 진공 건조하였다. 2. Drying step: After finally removing moisture through filtration, it was placed in a vacuum oven and vacuum dried at room temperature for 48 hours.
3. 고분자 입경 측정: 제조된 고분자 입자의 크기는 입경이 1㎛ 내지 5㎛이며, 입자 내 지르코니아의 함량은 20%이다. 입경은 SEM및 OM을 이용하여 측정하였으며, 지르코니아 함량은 TGA를 이용하여 측정하였다. 3. Measurement of Polymer Particle Size: The prepared polymer particles have a particle size of 1 µm to 5 µm and a zirconia content of 20%. The particle size was measured using SEM and OM, and the zirconia content was measured using TGA.
점착제의 제조Preparation of pressure sensitive adhesive
제조된 복합입자를 MEK(Methyl Ethyl Ketone) 용액에 stirring 및 sonication을 이용하여 분산시켰다. 분산된 복합입자 분산 용액을 점착수지로서 부틸아크릴레이트 (BA), 이소보닐아크릴레이트(IBOA), 페녹시에틸아크릴레이트(PEA) 및 2- 히드록시에틸아크릴레이트의 공중합체에 혼합하였다. 하루 동안 stirring 및 sonication하여 점착 수지 내에 충분히 분산시켰다. 제조된 점착 수지 용액을 이형 처리된 폴리에틸렌테레프탈레이트(PET) 필름에 바 코팅 방식으로 코팅하고, 오븐에서 120℃, 2분간 건조시킨 후, 바로 이형 PET 필름을 적층하여 점착제를 제조하였다. 제조된 점착제의 두께는 약 20㎛이고, 점착제 내의 유무기 복합 입자의 함량은 점착 수지 100 중량부 대비 15 중량부였다.The prepared composite particles were dispersed in MEK (Methyl Ethyl Ketone) solution by stirring and sonication. The dispersed multi-particle dispersion solution was mixed with a copolymer of butyl acrylate (BA), isobornyl acrylate (IBOA), phenoxyethyl acrylate (PEA) and 2-hydroxyethyl acrylate as an adhesive resin. After stirring and sonication for one day, it was sufficiently dispersed in the adhesive resin. The pressure-sensitive adhesive resin solution was coated on a release-treated polyethylene terephthalate (PET) film by a bar coating method, dried at 120 ° C. for 2 minutes in an oven, and immediately after the release PET film was laminated to prepare an adhesive. The prepared pressure-sensitive adhesive was about 20 μm, and the content of the organic-inorganic composite particles in the pressure-sensitive adhesive was 15 parts by weight based on 100 parts by weight of the pressure-sensitive adhesive resin.
플렉서블Flexible 유기발광다이오드 표시장치의 제조 Fabrication of Organic Light Emitting Diode Display
상기 제조된 점착제(10), 400 nm 내지 800 nm 파장의 광에 대한 굴절률이 1.75인 플라스틱 기판(20) 및 공지의 유기발광다이오드 소자(30)를 도 1과 같은 구조로 배치한 표시장치를 제조하였다. A display device including the
실시예Example 2 2
점착제 제조 시에, 유무기 복합 입자의 함량을 점착 수지 100 중량부 대비 30 중량부로 변경한 것을 제외하고는 실시예 1과 동일한 방식으로 표시장치를 제조하였다.In preparing the adhesive, the display device was manufactured in the same manner as in Example 1, except that the content of the organic-inorganic composite particles was changed to 30 parts by weight based on 100 parts by weight of the adhesive resin.
비교예Comparative example 1 One
점착제 제조 시에, 유무기 복합 입자를 첨가하지 않은 것을 제외하고는 실시예 1과 동일한 방식으로 표시장치를 제조하였다.A display device was manufactured in the same manner as in Example 1, except that the organic-inorganic composite particles were not added when the pressure-sensitive adhesive was prepared.
실시예 1 내지 2 및 비교예 1에 대하여 점착제의 투과율 및 헤이즈를 측정하고, 표시 장치의 양자 효율을 평가하여 그 결과를 하기 표 1에 기재하였다.For Examples 1 to 2 and Comparative Example 1, the transmittance and haze of the pressure-sensitive adhesive were measured, the quantum efficiency of the display device was evaluated, and the results are shown in Table 1 below.
1: 무기 나노 입자
2: 유기 비드
10; 점착제
20: 플렉서블 기판
30: 유기발광다이오드
40: 내부 배리어층
50: 외부 배리어층1: inorganic nanoparticles
2: organic beads
10; adhesive
20: flexible substrate
30: organic light emitting diode
40: inner barrier layer
50: outer barrier layer
Claims (19)
And an organic-inorganic composite particle having an adhesive resin and a particle size of 1 to 5 µm, wherein the organic-inorganic composite particle is an organic bead containing inorganic nanoparticles, and has a transmittance of 80% or more and a haze of 70% or more.
The pressure sensitive adhesive of claim 1, wherein the pressure sensitive adhesive is applied to a flexible organic light emitting diode display.
The pressure-sensitive adhesive of claim 1, wherein the organic-inorganic composite particles are present in a dispersed state in the pressure-sensitive adhesive resin.
The method of claim 1, wherein the adhesive resin is an acrylate resin, a silicone resin, a rubber resin, a styrene resin, an epoxy resin polyolefin resin, a polyoxyalkylene resin, a polyester resin, a polyvinyl chloride resin, poly Pressure-sensitive adhesive containing at least one member selected from the group consisting of carbonate resins and polyamide resins.
The pressure-sensitive adhesive according to claim 1, wherein the organic-inorganic composite particles are contained in a ratio of 10 parts by weight to 50 parts by weight with respect to 100 parts by weight of the adhesive resin.
The pressure-sensitive adhesive of claim 1, wherein the organic-inorganic composite particles have a refractive index of 1.4 to 2.0 with respect to light having a wavelength of 400 nm to 800 nm.
The pressure-sensitive adhesive of claim 1, wherein the inorganic nanoparticles have a refractive index of 2.0 to 2.5 with respect to light having a wavelength of 400 nm to 800 nm.
The method of claim 1, wherein the inorganic nanoparticles are silicon dioxide (SiO 2 ), aluminum oxide (Al 2 O 3 ), titanium oxide (TiO 2 ), tin oxide (SnO 2 ), iron oxide (FeO 3 ), zinc oxide (ZnO). ), Magnesium oxide (MgO), zirconium oxide (ZrO 2 ), cerium oxide (CeO 2 ), lithium oxide (LiO 2 ), silver oxide (AgO) and antimony oxide (Sb 2 O 3 ) Adhesive containing the above metal oxide.
The pressure-sensitive adhesive according to claim 1, wherein the organic beads comprise at least one member selected from the group consisting of polystyrene and polymethylmethacrylate.
The pressure-sensitive adhesive of claim 1, wherein the content of the inorganic nanoparticles in the organic-inorganic composite particles is 10 wt% to 50 wt%.
The pressure-sensitive adhesive of claim 1, wherein the pressure-sensitive adhesive has a thickness of 15 µm to 25 µm.
A flexible organic light emitting diode display device comprising the pressure sensitive adhesive of claim 1, a flexible substrate, and an organic light emitting diode device.
The flexible organic light emitting diode display of claim 13, wherein the pressure-sensitive adhesive is present on one surface of the flexible substrate, and the organic light emitting diode element is disposed on the opposite side of the pressure-sensitive adhesive of the flexible substrate.
The flexible organic light emitting diode display of claim 13, wherein the flexible substrate comprises at least one member selected from the group consisting of polyether sulfone, polyethylene naphthalate, polyethylene terephthalate, polycarbonate, and polyimide.
The flexible organic light emitting diode display of claim 13, wherein the flexible substrate has a refractive index of 1.45 to 1.75 for light having a wavelength of 400 nm to 800 nm.
The flexible organic light emitting diode display of claim 13, wherein the organic light emitting diode device comprises an organic light emitting layer disposed between the first and second electrodes facing each other and the first and second electrodes.
The flexible organic light emitting diode display of claim 13, further comprising a barrier layer.