KR102016420B1 - Manufacturing method for anti-insect master batch chips and anti-insect products using the same - Google Patents
Manufacturing method for anti-insect master batch chips and anti-insect products using the same Download PDFInfo
- Publication number
- KR102016420B1 KR102016420B1 KR1020180056385A KR20180056385A KR102016420B1 KR 102016420 B1 KR102016420 B1 KR 102016420B1 KR 1020180056385 A KR1020180056385 A KR 1020180056385A KR 20180056385 A KR20180056385 A KR 20180056385A KR 102016420 B1 KR102016420 B1 KR 102016420B1
- Authority
- KR
- South Korea
- Prior art keywords
- insect
- weight
- worm
- parts
- master batch
- Prior art date
Abstract
Description
본 발명은 항충 마스터 배치 칩의 제조방법 및 이를 이용하여 제조된 항충 제품에 관한 것으로서, 더욱 상세하게는 항충, 방충 성분이 포함된 조성물을 포함하여 항충 효과를 나타내는 항충 마스터 배치 칩을 제조하고 이를 이용하여 항충 제품을 제조함으로써, 곤충이나 해충이 기피하여 항충 및 방충 효과를 발휘할 수 있는 항충 마스터 배치 칩의 제조방법 및 이를 이용하여 제조된 항충 제품에 관한 것이다.The present invention relates to a method for manufacturing an anti-worm master batch chip and an anti-worm product manufactured using the same, and more particularly, to produce an anti-worm master batch chip having an anti-worm effect including a composition including an anti-worm and insect repellent component and using the same. The present invention relates to a method for producing an anti-worm master batch chip capable of exhibiting anti-worm and insect repellent effects by avoiding insects or pests by manufacturing an anti-worm product and an anti-worm product manufactured using the same.
요즈음 생활수준이 향상되면서 방충과 방균처리에 대한 소비자들의 기호와 요구가 증가하는 추세에 있다.As living standards improve these days, consumers' preferences and demands for insect repellent and antibacterial treatment are on the rise.
이에 각종 산업용품, 생활용품 등에 항균 처리가 되고 있는 제품들이 늘어나고 있는데, 세균, 곰팡이에 의한 피해뿐만 아니라 해충에 의한 피해를 입기 쉬운 부분에 대해 방충처리 요구가 증가하는 추세에 있다.Accordingly, products that are antibacterial to various industrial products, household goods, etc. are increasing, and the demand for insect repellent treatment is increasing not only for the damage caused by bacteria and mold, but also for the parts easily affected by pests.
일반적으로 식품 포장, 담배 외부 포장, 과자류 포장, 과수봉지용 포장 등에 일반적으로 사용되는 플라스틱 필름 포장은 포장되어 있는 내용물을 외부 환경으로부터 보호하여 장기간 보관할 수 있는 상태로 유지시키는 것을 목적으로 하고 있다.In general, plastic film packaging, which is generally used for food packaging, tobacco outer packaging, confectionery packaging, fruit bag packaging, and the like, aims to keep the packaged contents from external environment for long-term storage.
그러나 포장 내용물에 의해서 발생하는 방향 성분으로 인하여 다양한 곤충 및 벌레 등을 포장물에 접근시키고, 접근된 곤충 및 벌레 등은 필름 포장물을 손상시킨 후 포장 내부로 침입하여 내용물을 손상시키는 문제점을 지니고 있다.However, due to the aroma component generated by the contents of the package, various insects and bugs, etc. approach the package, and the approached insects and bugs have a problem of damaging the contents by invading the inside of the package after damaging the film package.
이러한 문제점을 해결하기 위하여 방충성분을 제품 포장에 포함하는 다양한 방안이 고려되었으며, 그 방안 중 하나가 방충 필름이다. 방충 필름을 사용하는 경우 방충 필름에 존재하는 방충제로 인하여 곤충이나 벌레 등의 접근을 막고 이러한 곤충 및 벌레에 의해서 발생하는 제품 손상을 방지할 수 있는 장점을 가지고 있다.In order to solve this problem, various methods for including the insect repellent in the product packaging have been considered, one of the methods is the insect repellent film. In the case of using the insect repellent film, the insect repellent present in the insect repellent film has an advantage of preventing access to insects or insects and preventing product damage caused by these insects and insects.
이러한 방충 필름의 하나로써, 해충의 방제에 효과를 갖는 방충제를 폴리올레핀계 필름에 투입하여 사용하게 되면 직접 방충제를 뿌리는 것에 비하여 꼭 필요한 장소에만 약제를 살포하는 효과 및 필름 안에 들어 있는 방충제가 서서히 방출되는 특성으로 인하여 효과적인 해충 방제법의 하나로 알려져 있다.As one of such insect repellent films, when insect repellents having an effect on controlling insects are used in a polyolefin-based film, the effect of spraying the medicine only at the necessary place as compared to spraying the insect repellent and the insect repellent in the film are gradually released. Due to its properties, it is known as one of the effective pest control methods.
그러나 일반적으로 방충제가 폴리올레핀수지와 상용성이 없어 방충제의 필름내 분산이 매우 어렵고, 필름 성형 후에도 곧바로 방충제가 표면으로 이행되면서 방충효과가 단명하는 문제점이 있다. 물론 방충제의 적절한 분산을 위해 알려진 기술중에는 다공성 플라스틱 펠렛을 이용하여 방충 마스터 배치를 만들고, 이것을 수지와 건식 혼합하여 필름을 성형하는 방법이 있다.However, in general, the insect repellent is incompatible with the polyolefin resin, so it is very difficult to disperse the insect repellent in the film, and the insect repellent is short-lived as the insect repellent is transferred to the surface immediately after film forming. Of course, one of the known techniques for proper dispersion of the insect repellent is to make a insect repellent masterbatch using porous plastic pellets and dry mix it with the resin to form a film.
그러나 이 경우 방충제의 분산에는 문제가 없으나 마스터 배치의 베이스가 플라스틱인 만큼 필름 성형시 용융되어 형체가 없어지기 때문에 방충제의 필름표면으로의 이행을 억제시키는 효과가 없어 방충효과가 단명하게 된다.However, in this case, there is no problem in dispersion of the insect repellent, but since the base of the master batch is plastic, it melts when forming the film and the mold disappears, so there is no effect of suppressing the transition of the insect repellent to the film surface, thereby shortening the insect repellent effect.
본 발명은 항충, 방충 성분이 포함된 조성물을 포함하여 항충 효과를 나타내는 마스터 배치 칩을 제조하고 이를 이용하여 항충 제품을 제조함으로써, 곤충이나 해충이 기피하여 항충 및 방충 효과를 발휘할 수 있는 항충 마스터 배치 칩의 제조방법 및 이를 이용하여 제조된 항충 제품을 제공하는데 있다.The present invention comprises a master batch chip exhibiting an anti-worm effect, including a composition containing an anti-worm, insect repellent component and by using the same to prepare an anti-worm product, anti-worm master batch that can exhibit the anti-worm and insect repellent effect to avoid insects or pests To provide a method for manufacturing a chip and an anti-worm product manufactured using the same.
또한, 본 발명은 종래 휘발성 방충제의 비산으로 인한 냄새 유발 및 방충 효과의 저하 등을 효과적으로 방지할 수 있고 방충 및 항충 효과를 장기간 안정적으로 발현할 수 있는 항충 마스터 배치 칩의 제조방법 및 이를 이용하여 제조된 항충 제품을 제공하는데 있다.In addition, the present invention can effectively prevent the odor induced by the scattering of the conventional volatile insect repellent and the deterioration of the insect repellent effect, and the method of manufacturing an anti-worm master batch chip that can stably express the insect repellent and anti-insect effect for a long time and manufactured using the same To provide antibacterial products.
또한, 본 발명은 농업, 원예업, 임업, 가정집, 골프장 등에 사용되는 비닐 또는 플라스틱 제품 등에 적용되어 사용될 수 있는 항충 마스터 배치 칩의 제조방법 및 이를 이용하여 제조된 항충 제품을 제공하는데 있다.In addition, the present invention is to provide a method of manufacturing an anti-worm master batch chip that can be applied to vinyl or plastic products used in agriculture, horticulture, forestry, homes, golf courses, etc. and anti-worm products manufactured using the same.
본 발명이 해결하고자 하는 다양한 과제들은 이상에서 언급한 과제들에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.Various problems to be solved by the present invention are not limited to the above-mentioned problems, and other tasks not mentioned will be clearly understood by those skilled in the art from the following description.
본 발명에 따른 항충 마스터 배치 칩의 제조방법은 항충 물질을 준비하는 항충 물질 준비 단계(S100); 칩 상태로 제조된 폴리프로필렌(PP:PolyProphlene), 폴리에틸렌(PE: PolyEthylene) 및 EVA(Ethylene Vinyl Acetate Copolymer) 수지를 모두 압출기에 투입하고, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지가 투입된 압출기에 열을 가하여 용용 시킨 후, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지를 교반하여 칩을 제조하고, 상기 칩을 냉각하여 절단함으로써 배치 칩을 제조하는 배치 칩 제조 단계(S200); 및 상기 배치 칩과 항충 물질을 혼합하여 마스터 배치 칩을 제조하는 마스터 배치 칩 제조 단계(S300)를 포함한다.The method of manufacturing an anti-worm master batch chip according to the present invention includes an anti-worm material preparing step of preparing an anti-worm material (S100); Polypropylene (PP: PolyProphlene), Polyethylene (PE: PolyEthylene) and EVA (Ethylene Vinyl Acetate Copolymer) resins prepared in a chip state are all added to an extruder, and heat is applied to the extruder into which the polypropylene, polyethylene, and EVA resin are added. After dissolution, a batch chip manufacturing step (S200) of manufacturing a batch chip by stirring the polypropylene, polyethylene, and EVA resin to manufacture a chip, and cooling and cutting the chip; And a master batch chip manufacturing step S300 of mixing the batch chip and the anti-worm material to produce a master batch chip.
상기 항충 물질로는 유기 염소계(Organochlorides) 항충 물질, 피레트로이드계(Pyrethroids) 항충 물질, 유기인산염계(Organophosphates) 항충 물질, 카바메이트계(Carbamates) 항충 물질, 네오니코티노이드계(Neonicotinoids) 항충물질 및 식물 유래 항충 물질로 이루어진 군에서 선택된 적어도 하나 이상이 사용될 수 있다.The anti-worm material includes organic chlorine (Organochlorides) anti-worm material, Pyrethroids anti-worm material, organic phosphate (Organophosphates) anti-worm material, carbamates anti-worm material, neonicotinoids (Neonicotinoids) And at least one selected from the group consisting of plant-derived antiparasitic substances.
상기 항충 물질로는 알레트린(Allethrin), 바이펜트린(Bifenthrin), 사이할로트린(Cyhalothrin), 사이페르메트린(Cypermethrin), 사이플루트린(Cyfluthrin), 델타메트린(Deltamethrin), 에토펜프록스(Etofenprox), 펜발레레이트(Fenvalerate), 페르메트린(Permethrin), 페노트린(Phenothrin), 프랄레트린(Prallethrin), 레스메트린(Resmethrin), 테트라메트린(Tetramethrin), 트랄로메트린(Tralomethrin) 및 트랜스플루트린(Transfluthrin)으로 이루어진 군에서 선택된 적어도 어느 하나 이상이 사용될 수 있다.The antiparasitic substances include Allethrin, Bifenthrin, Cyhalothrin, Cypermethrin, Cyfluthrin, Deltamethrin, Etofen Etofenprox, Fenvalerate, Permethrin, Phenothrin, Pralethrin, Resmethrin, Tetramethrin, Tralomethrin At least one selected from the group consisting of (Tralomethrin) and Transfluthrin may be used.
상기 항충 물질 준비 단계(S100)에서 상기 항충 물질 이외에 기능성 물질 및 편백나무 추출액을 더 포함하되, 상기 기능성 물질은 상기 항충 물질 100 중량부에 대해 50 내지 150 중량부의 중량 비율로 사용되고, 상기 기능성 물질은 이산화규소 나노입자 5 내지 10 중량부, 견운모 1 내지 3 중량부, 광촉매 0.5 내지 1.5 중량부, 활성탄 0.1 내지 1 중량부 및 황토 0.1 내지 0.5 중량부의 중량 비율로 포함되고, 상기 광촉매는 이산화티탄(TiO2) 2 내지 4 중량부 및 나노은 분말 0.5 내지 1.5 중량부의 중량비율로 혼합되어 제조되고, 상기 편백나무 추출액은 상기 항충 물질 100 중량부에 대해 1 내지 3 중량부의 중량 비율로 포함될 수 있다.In addition to the antiparasitic material in the antiparasitic material preparation step (S100) further comprises a functional material and cypress extract, wherein the functional material is used in a weight ratio of 50 to 150 parts by weight based on 100 parts by weight of the antiparasitic material, the functional material is 5 to 10 parts by weight of silicon dioxide nanoparticles, 1 to 3 parts by weight of mica, 0.5 to 1.5 parts by weight of photocatalyst, 0.1 to 1 parts by weight of activated carbon and 0.1 to 0.5 parts by weight of ocher, the photocatalyst is titanium dioxide (TiO 2 ) 2 to 4 parts by weight and nano-silver powder 0.5 to 1.5 parts by weight is prepared by mixing, the cypress extract may be included in a weight ratio of 1 to 3 parts by weight based on 100 parts by weight of the anti-worm material.
또한, 본 발명은 상기한 항충 마스터 배치 칩을 이용하여 제조된 항충 제품을 포함하되, 상기 항충 제품으로는, 폴리에스테르, 나이론, 폴리에틸렌, 액상 불포료 폴리에스테르, 폴리염화비닐지수판, pvc바닥재, 가교화 폴리에틸렌, 표장용 폴리에틸렌 필름, 폴리에틸렌관, 가용성 폴리에틸렌관, 폴리메틸펜텐-PMP, 폴리메틸펜텐-PMP, 폴리아릴레이트-PAR, 폴리아세탈-POM, 폴리에테르에테르케톤-PEEK, 폴리에틸렌-PE, 폴리우레탄-PU, 폴리페닐렌설파이드-PPS, 아크릴수지, 폴리이미드-PI, 폴리페닐렌에테르-PPE, 폴리메타크릴스티렌-MS, 폴리아미드-PA, 폴리카보네이트-PC, 폴리염화비닐-PVC, 폴리카보네이트-PC, 폴리프로필렌-PP, 플라스틱, 농자재 및 건설자재로 이루어진 군에서 선택된 어느 하나 이상에 적용된다.In addition, the present invention includes an anti-worm product manufactured using the above-described anti-worm master batch chip, wherein the anti-worm product, polyester, nylon, polyethylene, liquid non-polyester polyester, polyvinyl chloride index plate, pvc flooring material, crosslinking Polyethylene, Marked Polyethylene Film, Polyethylene Tube, Soluble Polyethylene Tube, Polymethylpentene-PMP, Polymethylpentene-PMP, Polyarylate-PAR, Polyacetal-POM, Polyetheretherketone-PEEK, Polyethylene-PE, Poly Urethane-PU, polyphenylene sulfide-PPS, acrylic resin, polyimide-PI, polyphenylene ether-PPE, polymethacrylstyrene-MS, polyamide-PA, polycarbonate-PC, polyvinyl chloride-PVC, poly It is applied to any one or more selected from the group consisting of carbonate-PC, polypropylene-PP, plastic, agricultural materials and construction materials.
기타 실시 예들의 구체적인 사항들은 상세한 설명에 포함되어 있다.Specific details of other embodiments are included in the detailed description.
본 발명에 따른 항충 마스터 배치 칩의 제조방법은 항충, 방충 성분이 포함된 조성물을 포함하여 항충 효과를 나타내는 항충 마스터 배치 칩을 제조하고 이를 이용하여 항충 제품을 제조함으로써, 곤충이나 해충이 기피하여 항충 및 방충 효과를 발휘할 수 있다.The method of manufacturing the anti-worm master batch chip according to the present invention includes an anti-worm, insect-insulating component comprising a composition containing an anti-worm insect master batch chip having an anti-worm effect, and by using the same to prepare an anti-worm product, insects or pests to avoid anti-worm And an insect repellent effect.
또한, 본 발명에 따라 제조된 항충 제품은 종래 휘발성 방충제의 비산으로 인한 냄새 유발 및 방충 효과의 저하 등을 효과적으로 방지할 수 있고 방충 및 항충 효과를 장기간 안정적으로 발현할 수 있다.In addition, the anti-worm products prepared according to the present invention can effectively prevent the odor induced by the scattering of the conventional volatile insect repellent, and the deterioration of the insect repellent effect, etc. and can stably express the insect repellent and anti-insect effect for a long time.
또한, 본 발명에 따라 제조된 항충 제품은 농업, 원예업, 임업, 가정집, 골프장 등에 사용되는 비닐 또는 플라스틱 제품 등에 적용되어 사용될 수 있다.In addition, the anti-worm products manufactured according to the present invention can be applied to the vinyl or plastic products used in agriculture, horticulture, forestry, homes, golf courses and the like.
본 발명의 기술적 사상의 실시예는, 구체적으로 언급되지 않은 다양한 효과를 제공할 수 있다는 것이 충분히 이해될 수 있을 것이다.It will be fully understood that embodiments of the inventive concept may provide various effects that are not specifically mentioned.
도 1은 본 발명에 따른 항충 마스터 배치 칩의 제조방법을 설명하기 위한 순서도이다.
도 2 및 도 3은 본 발명에 따른 항충 제품의 일 예로, 설탕물을 수용한 항충 비닐에 대하여 꿀벌의 기피 여부를 관찰한 사진이다.1 is a flowchart illustrating a method of manufacturing an anti-worm master batch chip according to the present invention.
2 and 3 is an example of an anti-worm product according to the present invention, is a photograph observing whether or not to avoid bees against the anti-insect vinyl containing sugar water.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다.Advantages and features of the present invention and methods for achieving them will be apparent with reference to the embodiments described below in detail. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided so that the disclosure may be made thorough and complete, and to fully convey the spirit of the present invention to those skilled in the art.
본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다.The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting of the present invention. Singular expressions include plural expressions unless the context clearly indicates otherwise.
다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다.Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art. Terms such as those defined in the commonly used dictionaries should be construed as having meanings consistent with the meanings in the context of the related art and shall not be construed in ideal or excessively formal meanings unless expressly defined in this application. Do not.
한편, 본 발명의 기술적 사상의 일 실시예에 따른 항충 마스터 배치 칩의 제조방법에서는 항충 효과를 나타내는 마스터 배치 칩을 이용하여 항충 제품을 제조하는 것을 일 예로 들어 설명하나, 본 발명의 기술적 사상은 상기한 항충 제품 이외에만 한정되는 것은 아니고, 본 발명에 따라 제조된 혼합 칩을 이용하여 각종 제품에 사용되는 첨가물로 사용하여 항충 제품을 제조하는 기술적 사상에도 유사하게 적용될 수 있다.On the other hand, in the manufacturing method of the anti-worm master batch chip according to an embodiment of the technical idea of the present invention will be described using an example of manufacturing an anti-worm product using a master batch chip showing the anti-worm effect, the technical idea of the present invention is It is not limited to only one anti-worm product, but may be similarly applied to the technical idea of manufacturing the anti-worm product by using the mixed chip manufactured according to the present invention as an additive used in various products.
또한, 본 발명의 기술적 사상의 일 실시예에 따른 항충 제품은 농업, 원예업, 임업, 가정집, 골프장 등에 사용되는 각종 제품 등에 적용되어 사용될 수 있다.In addition, the anti-worm products according to an embodiment of the present invention may be applied to various products used in agriculture, horticulture, forestry, homes, golf courses, and the like.
이하, 첨부된 도면을 참조하여 본 발명에 따른 항충 칩의 제조방법에 대하여 더욱 상세하게 설명하기로 한다.Hereinafter, a method of manufacturing an anti-worm chip according to the present invention will be described in more detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 항충 마스터 배치 칩의 제조방법을 설명하기 위한 순서도이다.1 is a flowchart illustrating a method of manufacturing an anti-worm master batch chip according to the present invention.
도 1을 참조하면, 본 발명에 따른 항충 마스터 배치 칩의 제조방법은 항충 물질 준비 단계(S100), 배치 칩 제조 단계(S200) 및 마스터 배치 칩 제조 단계(S300)를 포함하고, 상기 마스터 배치 칩을 이용하여 항충 제품 제조 단계(S400)를 거침으로써 항충 제품을 제조할 수 있다.Referring to Figure 1, the manufacturing method of the anti-worm master batch chip according to the present invention includes an anti-worm material preparation step (S100), batch chip manufacturing step (S200) and master batch chip manufacturing step (S300), the master batch chip By using the anti-worm product manufacturing step (S400) can be prepared anti-worm products.
1. 항충 물질 준비 단계(S100)1. Anti-insect material preparation step (S100)
상기 항충 물질 준비 단계(S100)는 해충 기피 효과를 발휘할 수 있는 항충 물질을 준비하는 단계이다.The anti-insect material preparation step (S100) is a step of preparing an anti-insect material that can exert a pest repelling effect.
상기 항충 물질 준비 단계(S100)에서 상기 항충 물질은 곤충 또는 해충 등의 기피 물질을 준비하는 것으로, 상기 항충 물질로는 유기 염소계(Organochlorides) 항충 물질, 피레트로이드계(Pyrethroids) 항충 물질, 유기인산염계(Organophosphates) 항충 물질, 카바메이트계(Carbamates) 항충 물질, 네오니코티노이드계(Neonicotinoids) 항충물질 및 식물 유래 항충 물질로 이루어진 군에서 선택된 적어도 하나 이상일 수 있는데, 예를 들어, 상기 항충 물질로는 알레트린(Allethrin), 바이펜트린(Bifenthrin), 사이할로트린(Cyhalothrin), 사이페르메트린(Cypermethrin), 사이플루트린(Cyfluthrin), 델타메트린(Deltamethrin), 에토펜프록스(Etofenprox), 펜발레레이트(Fenvalerate), 페르메트린(Permethrin), 페노트린(Phenothrin), 프랄레트린(Prallethrin), 레스메트린(Resmethrin), 테트라메트린(Tetramethrin), 트랄로메트린(Tralomethrin) 및 트랜스플루트린(Transfluthrin)으로 이루어진 군에서 선택된 적어도 어느 하나 이상이고, 더욱 구체적으로는 N,N-디에틸-m-톨루아미드(N,N-diethyl-m-toluamide) 또는 1-피페리딘카르복실산-2-(2-하이드록시에틸)-1-메틸프로필에스테르[1-piperidinecarboxylic acid-2-(2-hydroxyethyl)-1-methylpropyl ester]에서 선택된 어느 하나 이상일 수 있다.In the anti-worm material preparation step (S100), the anti-worm material prepares a repellent material such as an insect or a pest, and the anti-worm material includes organic chlorides (Organochlorides) anti-insect material, Pyrethroids anti-worm material, organophosphate (Organophosphates) at least one selected from the group consisting of an anti-worm material, a carbamates anti-worm material, a neonicotinoids anti-worm material and a plant-derived anti-worm material, for example, Allethrin, Bifenthrin, Cyhalothrin, Cypermethrin, Cyfluthrin, Deltamethrin, Etofenprox, Fenvalerate, Permethrin, Phenothrin, Pralethrin, Resmethrin, Tetramethrin, Tralometrin hrin) and at least one selected from the group consisting of Transfluthrin, more specifically N, N-diethyl-m-toluamide or 1- It may be any one or more selected from piperidinecarboxylic acid-2- (2-hydroxyethyl) -1-methylpropyl ester [1-piperidinecarboxylic acid-2- (2-hydroxyethyl) -1-methylpropyl ester].
한편, 상기 항충 물질 준비 단계(S100)에서는 상기 항충 물질 이외에 원적외선과 음이온이 다량 방사되고 오염 물질에 대한 항균, 탈취 효과가 있는 기능성 물질을 더 포함할 수 있는데, 상기 기능성 물질은 상기 항충 물질 100 중량부에 대해 50 내지 150 중량부의 중량 비율로 사용될 수 있다.On the other hand, in the anti-worm material preparation step (S100), in addition to the anti-worm material may include a large amount of far infrared rays and anions, and further includes a functional material having an antibacterial and deodorizing effect on the pollutant, the functional material 100 weight It can be used in the weight ratio of 50 to 150 parts by weight relative to the part.
상기 기능성 물질로는 이산화규소 나노입자, 견운모, 광촉매, 활성탄 및 황토가 포함되고, 상기 광촉매는 이산화티탄(TiO2) 및 나노은 분말이 이용됨으로써, 본 발명에 따른 항충 비닐이 생활 용품에 이용되는 경우에도 안전하게 사용될 수 있다.The functional material includes silicon dioxide nanoparticles, biotite, photocatalyst, activated carbon and loess, and the photocatalyst is titanium dioxide (TiO 2 ) and nano silver powder is used, whereby the anti-worm vinyl according to the present invention is used in household goods Can be used safely.
또한, 본 발명에서 상기 기능성 물질은 이산화규소 나노입자 5 내지 10 중량부, 견운모 1 내지 3 중량부, 광촉매 0.5 내지 1.5 중량부, 활성탄 0.1 내지 1 중량부 및 황토 0.1 내지 0.5 중량부의 중량 비율로 포함되고, 상기 광촉매는 이산화티탄(TiO2) 2 내지 4 중량부 및 나노은 분말 0.5 내지 1.5 중량부의 중량비율로 혼합되어 제조될 수 있다.In addition, the functional material in the present invention comprises 5 to 10 parts by weight of silicon dioxide nanoparticles, 1 to 3 parts by weight of mica, 0.5 to 1.5 parts by weight of photocatalyst, 0.1 to 1 parts by weight of activated carbon and 0.1 to 0.5 parts by weight of loess The photocatalyst may be prepared by mixing 2 to 4 parts by weight of titanium dioxide (TiO 2 ) and 0.5 to 1.5 parts by weight of nanosilver powder.
상기 이산화규소(Silicon dioxide, SiO2)는 규소의 산화물로 실리카(silica) 라고도 하며 원적외선을 방출하는 것으로 잘 알려진 뮬라이트(mullite), 근청석, 황토 등의 주요 구성요소로 사용된다. 상기 이산화규소는 적은 양으로도 많은 양의 원적외선을 방출하는 효능을 가지며 값도 저렴한데, 비결정성 실리카는 인체 발암성이 없는 것으로 평가되어 화장품의 주된 원료로 사용되며, 인체에 유해성은 알려진 바 없다.Silicon dioxide (SiO 2 ) is an oxide of silicon, also called silica, and is used as a major component of mullite, cordierite, loess, and the like, which are known to emit far infrared rays. The silicon dioxide has the effect of releasing a large amount of far infrared rays in a small amount and is inexpensive, but amorphous silica is used as a main raw material of cosmetics because it is evaluated as non-carcinogenic to humans, and there is no known harmful to human body. .
상기 견운모(sericite)는 철분(Fe), 마그네슘(Mg), 아연(Zn), 망간(Mn), 구리(Cu), 몰리브덴(Mo), 셀레늄(Se), 게르마늄(Ge), 규소(Si), 바나듐(V) 및 스트론튬(Sr) 등의 다양한 인체 필수 미네랄을 내포하는 점토성 광물로, 강한 환원력을 지닌 활성산소의 분해용도로 사용되는 운모족 광물로서 생리활성물질이며, 살균작용을 한다. The sericite is iron (Fe), magnesium (Mg), zinc (Zn), manganese (Mn), copper (Cu), molybdenum (Mo), selenium (Se), germanium (Ge), silicon (Si) As a clay mineral containing various human essential minerals such as vanadium (V) and strontium (Sr), it is a mica-based mineral used for the decomposition of active oxygen with strong reducing power, and is a bioactive substance and has a sterilizing effect.
또한, 본 발명에서 상기 견운모는 발포하여 분말화하여 사용하므로 분체 내부에 공기층이 형성되어 습도 조절이 가능함은 물론 탈취 효과나 곰팡이의 발생 방지 및 음이온과 원적외선 효과가 있다.In addition, the biotite in the present invention is used to form a powder by foaming, so that the air layer is formed inside the powder is capable of controlling the humidity, as well as the deodorizing effect or the occurrence of mold and anion and far-infrared effect.
또한, 상기 견운모는 분말화되기 전에 강도의 증가를 위해 1400 내지 1550℃의 범위 내에서 열처리를 진행할 수 있다. 이때, 열처리의 가열온도가 1400℃ 미만인 경우에는 견운모가 적정 강도를 얻을 수 없고, 가열온도가 1550℃를 초과하는 경우에는 견운모가 소실될 우려가 있다.In addition, the biotite may be heat-treated in the range of 1400 to 1550 ° C. to increase the strength before powdering. At this time, if the heating temperature of the heat treatment is less than 1400 ° C., the villi may not obtain the appropriate strength, and if the heating temperature exceeds 1550 ° C., the villi may be lost.
또한, 상기 열처리된 견운모는 코팅층을 구성하는 조성물과 혼합되기에 앞서 균일하게 혼합되도록 하기 위하여 10 내지 200nm의 입자크기로 분말화되어 포함될 수 있는데, 상기 견운모가 10nm 미만으로 분말화되는 경우에는 분말화 작업하기 어려운 문제가 발생할 뿐만 아니라 원적외선 방사 및 음이온의 방출 효율이 떨어지게 되는 문제가 발생할 수 있고, 200nm를 초과하여 분말화되는 경우에는 코팅액을 구성하는 조성물들 사이에서 균일하게 혼합되기 어려운 문제가 발생할 수 있다.In addition, the heat treated biotite may be powdered in a particle size of 10 to 200nm to be uniformly mixed before mixing with the composition constituting the coating layer, if the biotite is powdered to less than 10nm Not only can the problem be difficult to work, but also the efficiency of far-infrared radiation and anion emission can be deteriorated, and when it is powdered beyond 200 nm, it can be difficult to uniformly mix between the compositions constituting the coating solution. have.
상기 광촉매는(光觸媒, photocatalyst)는 빛을 받아들여 화학반응을 촉진시키는 물질을 말하는 것으로, 이러한 광촉매는 주로 띠 간격에너지(band gap energy) 이상의 빛 에너지가 조사되었을 때 전자와 정공을 발생시키고, 발생된 정공에 의해 수산화라디칼(-OH)이 생성되게 되며, 상기 수산화라디칼의 강력한 산화력을 통해 그 표면에 흡착된 기상 또는 액상의 유기물을 분해하는 이른바 '광산화반응'을 일으키는 물질을 말한다.The photocatalyst refers to a material that receives light and promotes a chemical reaction. The photocatalyst generates electrons and holes when light energy of more than a band gap energy is irradiated. Hydrogen radical (-OH) is generated by the holes, and refers to a substance causing so-called 'photooxidation reaction' that decomposes organic substances in gaseous or liquid phase adsorbed on the surface through the strong oxidizing power of the radical.
본 발명에서 상기 광촉매는 빛 에너지를 흡수함으로써 촉매활성을 나타내게 되는데, 이때 발생하는 강력한 산화력으로 유해물질을 산화, 분해하게 된다. 이러한 광촉매는 그 특성을 이용하여 박테리아, 미생물, 유기물질들을 분해하는 유기오탁수의 정화에 주로 활용되고 있다. In the present invention, the photocatalyst exhibits catalytic activity by absorbing light energy, and oxidizes and decomposes harmful substances with strong oxidizing power generated at this time. These photocatalysts are mainly used for the purification of organic polluted water that decomposes bacteria, microorganisms, and organic substances using their properties.
본 발명에서 상기 광촉매는 이산화티탄(TiO2) 및 나노은 분말이 혼합된 혼합분말이 사용될 수 있는데, 상기 광촉매는 이산화티탄(TiO2) 2 내지 4 중량부 및 나노은 분말 0.5 내지 1.5 중량부의 중량비율로 혼합되어 제조될 수 있다.In the present invention, the photocatalyst may be a mixed powder in which titanium dioxide (TiO 2 ) and nano silver powder are mixed. The photocatalyst may be used in a weight ratio of 2 to 4 parts by weight of titanium dioxide (TiO 2 ) and 0.5 to 1.5 parts by weight of nano silver powder. It can be prepared by mixing.
상기 이산화티탄은 빛을 받으면 벤젠ㆍ톨루엔ㆍ포름알데히드 등과 같은 유해물질을 분해하여 물과 이산화탄소로 만드는 특성이 있고, 저렴하고 인체에 무해하는 등 여러 가지 장점이 있고, 상기 나노은(Ag)은 이산화티탄과 함께 혼합되어 항균성 광촉매의 효과를 증진시키기 위하여 첨가되며, 상기 나노은(Ag)을 첨가함으로써, 광산화반응을 촉진하고 혼합성 및 도포성을 좋게 하며, 항균성, 항곰팡이성을 높일 수 있다.The titanium dioxide decomposes harmful substances such as benzene, toluene, formaldehyde, etc. when it receives light, and has properties such as water and carbon dioxide, and is inexpensive and harmless to the human body. The nano silver (Ag) has titanium dioxide. It is mixed with and added to enhance the effect of the antimicrobial photocatalyst, and by adding the nano silver (Ag), it promotes the photooxidation reaction, improves the mixing and coating properties, and can increase the antimicrobial and antifungal properties.
상기 황토는 입자들 사이의 공간으로 불순물, 오염물질을 흡착 분해하며, 산소가 풍부하고, 원적외선을 방출한다. 상기 황토에서 나오는 원적외선은 파장이 8 내지 14㎛으로 인체의 에너지 영역과 거의 일치하며, 상기 황토의 원적외선은 세포의 분자를 활성화해 신진 대사를 촉진한다. 황토에서는 원적외선을 복사하여 인체에 흡수, 신진대사 및 혈액순환을 활성화시켜 인체의 노화방지, 만성피로 등 각종 성인병을 예방할 수 있다. 상기 황토에서 원적외선을 방사 받게 되면 인체 내의 각종 발병의 원인이 되는 세균이 그 열작용으로 인하여 약화되며, 인체내 모세혈관을 확장시켜 혈액 순환을 촉진함은 물론 세포 조직의 생성 촉진 등을 도와줄 수 있다.The loess adsorbs and decomposes impurities and contaminants into the spaces between the particles, and is rich in oxygen and emits far infrared rays. Far infrared rays emitted from the loess have a wavelength of 8 to 14 µm and almost coincide with the energy region of the human body. The far infrared rays of the loess promote metabolism by activating a molecule of a cell. In ocher, it absorbs far infrared rays and absorbs it into human body, activates metabolism and blood circulation, and can prevent various adult diseases such as aging of human body and chronic fatigue. When the far-infrared ray is radiated from the loess, bacteria causing the various diseases in the human body are weakened due to its thermal action, and the capillaries in the human body can be expanded to promote blood circulation as well as to promote the production of cellular tissues. .
또한, 상기 항충 물질 준비 단계(S100)에서는 상기 항충 물질 이외에 해충 기피, 항균, 탈취 등의 효과가 있는 편백나무 추출액을 더 포함할 수 있는데, 상기 편백나무 추출액은 상기 항충 물질 100 중량부에 대해 1 내지 3 중량부의 중량 비율로 포함될 수 있다.In addition, the anti-worm material preparation step (S100) may further include a cypress extract having an effect such as pest avoidance, antibacterial, deodorization, in addition to the anti-worm material, the cypress extract is 1 per 100 parts by weight of the anti-worm material To 3 parts by weight may be included.
상기 편백나무(Chamaecyparis obtusa)는 노송나무라고도 하며, 겉씨식물 구과목 측백나무과의 상록교목으로서, 일본이 원산지이지만 개발을 통해 우리나라 남부 지방에서 조림수종으로 널리 재배되고 있는데, 편백나무 특유의 향으로 인해 탈취제, 항균제 등으로 사용되고 있다.The Cypress ( Chamaecyparis obtusa ), also called cypress, is an evergreen arborescent of the cypressaceae, which is a seedling plant. It is native to Japan, but is widely grown as a plantation species in the southern part of Korea through its development. It is used.
편백나무에서 생산되는 피톤치드는 식물의 자기방어물질로써, 병원균 및 해충, 곰팡이 등에 저항하기 위해 식물이 내뿜거나 분비하는 물질로 그 자체에 살균, 살충성분이 포함되어 있다 피톤치드의 구성물질은 테르펜을 비롯한 페놀 화합물, 알칼로이드 성분, 글리코시드 등으로 이루어진 유기화합물이며, 항균작용, 진정작용, 탈취작용, 스트레스 해소작용 등을 하는 것으로 알려져 있다. 이러한 피톤치드는 화학합성 물질이 아닌 천연물질이고, 인간의 신체에 무리 없이 흡수되며, 인간에게 해로운 균들을 선택적으로 살균한다.Phytoncide, produced from cypress, is a plant's self-defense substance, which is emitted or secreted by plants to resist pathogens, pests, and fungi. It contains sterilization and insecticides. It is an organic compound consisting of a phenol compound, an alkaloid component, glycoside, and the like, and is known to have antibacterial, sedative, deodorant, and stress relief effects. Such phytoncide is a natural substance, not a chemical synthetic substance, is absorbed into the human body without difficulty, and selectively sterilizes harmful bacteria.
또한, 피톤치드는 항균작용, 소취작용, 진정작용 및 스트레스 해소 작용 등 수많은 기능을 하는 것으로 알려져 있다. 또한, 피톤치드는 뛰어난 살균, 항균, 세정작용으로 피부를 깨끗하게 하고 보습작용도 하며, 체내의 면역기능을 강화한다.In addition, phytoncide is known to have a number of functions, such as antibacterial, deodorant, sedative and stress relief. In addition, phytoncide cleanses and moisturizes the skin with excellent sterilization, antibacterial and cleansing action, and strengthens the body's immune function.
본 발명에서 편백나무 추출액은 하기의 제조방법을 거쳐 제조될 수 있다.Cypress extract in the present invention can be prepared through the following manufacturing method.
즉, 본 발명에서 상기 편백나무 추출액은 편백나무를 준비한 후, 볼 밀링(ball milling) 장치와 같은 분쇄기를 이용하여 편백나무 분말을 제조할 수 있는데, 상기 편백나무 분말은 500 내지 5000㎛의 입경을 가지고, 50 내지 3000m2/g의 비표면적을 가지도록 분쇄될 수 있다.That is, in the present invention, the cypress extract is prepared after the cypress tree, can be produced a cypress powder by using a mill such as a ball milling (ball milling), the cypress powder has a particle size of 500 to 5000㎛ And may be ground to have a specific surface area of 50 to 3000 m 2 / g.
상기 편백나무 분말이 500㎛의 입경 또는 50m2/g의 비표면적 미만으로 분쇄되는 경우에는 분쇄 시간이 지연되고 분진이나 미세 분말에 의해 작업성이 떨어지는 문제가 발생할 수 있고, 5000㎛의 입경 또는 3000m2/g의 비표면적을 초과하여 분쇄되는 경우에는 상기 편백나무 분말 내부에 함유되어 있는 유효성분들이 용이하게 추출되지 못하는 문제가 발생할 수 있다.When the cypress powder is ground to a particle size of 500 μm or less than a specific surface area of 50 m 2 / g, the grinding time may be delayed and workability may be deteriorated by dust or fine powder, and the particle size of 5000 μm or 3000 m When it is pulverized exceeding the specific surface area of 2 / g may cause a problem that the active ingredients contained in the cypress powder is not easily extracted.
다음으로, 상기 분쇄된 편백나무 분말을 건조하여 수분을 제거할 수 있다.Next, the pulverized cypress powder may be dried to remove moisture.
상기 분쇄된 편백나무 분말의 건조는 햇빛 건조시 상기 편백나무 분말의 식물세포 또는 엽록소가 파괴되고 편백나무의 유용성분이 감소되는 것을 방지하기 위하여 일정한 온도 및 습도가 유지되는 건조기에서 수행될 수 있는데, 예를 들어, 상기 분쇄된 편백나무 분말의 건조는 온도 20 내지 25℃ 및 습도 35 내지 45%로 유지되는 건조기에서 5 내지 10시간 동안 건조함으로써 상기 분쇄된 편백나무 분말의 수분 함량은 처음 분쇄된 편백나무 분말의 전체 중량에 대하여 30 내지 40 중량%가 되도록 할 수 있다.Drying of the pulverized cypress powder may be carried out in a dryer maintained at a constant temperature and humidity in order to prevent the destruction of plant cells or chlorophyll of the cypress powder and the useful components of the cypress upon drying the sun, for example For example, the dried cypress powder is dried for 5 to 10 hours in a drier maintained at a temperature of 20 to 25 ° C. and a humidity of 35 to 45%. It may be 30 to 40% by weight relative to the total weight of the powder.
즉, 상기 분쇄된 편백나무 분말의 건조는 상기와 같은 공정 조건의 건조기에서 건조하여 상기 편백나무 분말에 포함되어 있는 수분이 점진적으로 고르게 증발되도록 함으로써, 편백나무의 유용성분을 보다 용이하게 발휘시킬 수 있고, 편백나무 분말의 세포조직의 파괴로 공기의 침투를 용이하게 하여 편백나무 분말의 유용성분이 진하게 추출될 수 있도록 할 수 있다.That is, the pulverized cypress powder is dried in a drier under the above process conditions so that the moisture contained in the cypress powder is gradually evaporated evenly, thereby more easily exposing the useful components of the cypress wood. In addition, it is possible to facilitate the penetration of air by the destruction of cellular tissues of the cypress powder, so that useful components of the cypress powder can be concentrated.
그 다음으로, 상기 건조된 편백나무 분말을 증숙하여 수증기로 찔 수 있다.The dried cypress powder can then be steamed and steamed with water vapor.
상기 건조된 편백나무 분말의 증숙은 일정한 압력하에서 일정한 온도의 수증기로 가열함으로써 수행될 수 있는데, 예를 들어, 상기 건조된 편백나무 분말을을 150 내지 160℃의 온도 및 1 내지 2kgf/cm2의 압력에서 1 내지 3시간 동안 수증기로 가열함으로써 진행될 수 있다.Steaming of the dried cypress powder may be carried out by heating with a constant temperature steam under a constant pressure, for example, the dried cypress powder is heated to a temperature of 150 to 160 ℃ and 1 to 2 kgf / cm 2 It can proceed by heating with steam for 1 to 3 hours at pressure.
본 발명에서 상기 건조된 편백나무 분말의 증숙이 상기한 공정 조건의 하한 미만으로 수행되는 경우에는 편백나무 분말이 충분히 증숙되지 못하여 추후 공정에서 짧은 시간 내에 충분한 추출물을 제조하기 어려운 문제가 발생할 수 있고, 상기한 공정 조건의 상한을 초과하여 수행되는 경우에는 편백나무 분말의 유효성분이 휘발되거나 더 이상의 증숙의 효과 증가가 미미할 수 있다.In the present invention, if the steaming of the dried cypress powder is carried out below the lower limit of the above process conditions, the cypress powder may not be sufficiently steamed, so that it may be difficult to prepare a sufficient extract in a short time in a later process, If it is carried out above the upper limit of the process conditions, the active ingredient of the cypress powder may be volatilized or the effect of further steaming may be insignificant.
이어서, 상기 증숙된 편백나무 분말에 초음파를 가한 후 상기 편백나무 분말 고형분을 제거하여 1차 편백나무 추출액을 제조할 수 있다.Subsequently, an ultrasonic wave is applied to the steamed cypress powder to remove the cypress powder solids, thereby preparing a primary cypress extract.
상기 1차 편백나무 추출액을 제조하기 위하여 상기 증숙된 편백나무 분말을 용매와 혼합하여 혼합액을 제조한 후, 초음파 추출기에 투입하여 상기 혼합액에 초음파를 가함으로써 1차 편백나무 추출액을 제조할 수 있는데, 상기 용매로는 물 또는 탄소수 1 내지 4(C1 내지 C4)의 알코올 중에서 선택된 어느 하나 이상의 용매가 사용될 수 있다.In order to prepare the primary cypress extract, after mixing the steamed cypress powder with a solvent to prepare a mixed solution, the primary cypress extract may be prepared by adding ultrasonic waves to the mixed solution by adding an ultrasonic extractor. As the solvent, any one or more solvents selected from water or alcohols having 1 to 4 carbon atoms (C1 to C4) may be used.
또한, 상기 1차 편백나무 추출액을 제조하기 위하여 상기 혼합액에 가해지는 초음파는 30 내지 80KHz의 진동주파수에서 100 내지 200분 동안 100 내지 200와트(watt)의 출력을 이용하여 추출할 수 있다.In addition, the ultrasonic wave applied to the mixed solution to prepare the primary cypress extract can be extracted using an output of 100 to 200 watts (watt) for 100 to 200 minutes at a vibration frequency of 30 to 80KHz.
다음으로, 상기 1차 편백나무 추출액을 분리한 후 원심분리할 수 있다.Next, after separating the primary cypress extract can be centrifuged.
상기 1차 편백나무 추출액에는 용매 및 편백나무의 유용성분이 침출되어 있는데, 상기 편백나무의 유효성분들이 침출되어 있는 1차 편백나무 추출액을 원심분리함으로써, 편백나무 분말의 미세 불순물들이 위치하는 하층액과, 상기 하층액 상부에 위치하는 중층액 및 상층액으로 위치적으로 구분하여 분리할 수 있다.The primary cypress extract extracts the solvent and useful components of the cypress, and by centrifuging the primary cypress extract from which the active ingredients of the cypress are leached, the lower layer solution in which the fine impurities of the cypress powder are located. It can be separated by separating the position into the stratified liquid and the supernatant located in the upper layer liquid.
그 다음으로, 상기 원심분리된 정제수의 중층액 및 상층액을 분리한 후, 상기 중층액 및 상층액을 가열하여 편백나무 추출액을 제조할 수 있다.Subsequently, after separating the supernatant and the supernatant of the centrifuged purified water, the supernatant and the supernatant may be heated to produce a cypress extract.
상기 단계에서는 상기 원심분리된 1차 편백나무 추출액의 중층액 및 상층액을 분리한 후, 110 내지 120℃의 온도로 가열하여 용매를 제거함으로써 편백나무의 유효성분들이 침출되어 형성된 겔 상태의 편백나무 추출액을 제조할 수 있다.In the step, after separating the middle layer and the supernatant of the centrifuged primary cypress extract, heated to a temperature of 110 to 120 ℃ to remove the solvent to extract the active ingredients of the cypress, the cypress of the gel state formed Extracts can be prepared.
2. 배치 칩 제조 단계(S200)2. Batch Chip Manufacturing Step (S200)
상기 배치 칩 제조 단계(S200)는 칩 상태로 제조된 폴리프로필렌(PP:PolyProphlene), 폴리에틸렌(PE: PolyEthylene) 및 EVA(Ethylene Vinyl Acetate Copolymer) 수지를 모두 압출기에 투입하고, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지가 투입된 압출기에 열을 가하여 용용 시킨 후, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지를 교반하여 칩을 제조하고, 상기 칩을 냉각하여 절단함으로써 배치 칩을 제조하는 단계이다.In the batch chip manufacturing step (S200), all polypropylene (PP: PolyProphlene), polyethylene (PE: PolyEthylene), and EVA (Ethylene Vinyl Acetate Copolymer) resins prepared in a chip state are introduced into an extruder, and the polypropylene, polyethylene, and After melting the polypropylene, polyethylene, and EVA resin by applying heat to the extruder to which the EVA resin is added, the chip is prepared, and the batch chip is manufactured by cooling and cutting the chip.
본 발명에서 상기 폴리에틸렌(PE)은 플라스틱 제품 중 초경량에 속하면서 우수한 쿠션력과 내수성 및 내저온 충격성을 가지고, 상기 폴리프로필렌(PP)은 상기 폴리에틸렌(PE)과 매우 유사한 성질을 가지면서도 투명성 및 항장력 등이 우수한 특성을 가지며, 상기 EVA 수지는 에틸렌과 비닐아세테이트의 공중합체 수지로서 투명성, 유연성, 저온 취성 등이 매우 우수한 특성을 가짐과 동시에 매우 친환경적인 수지이다.In the present invention, the polyethylene (PE) belongs to the ultra-light in the plastic products, has excellent cushioning power, water resistance and low temperature impact resistance, the polypropylene (PP) has properties very similar to the polyethylene (PE), but also transparency and tensile strength, etc. The EVA resin is a copolymer resin of ethylene and vinyl acetate, and has excellent properties such as transparency, flexibility, low temperature brittleness, and is a very environmentally friendly resin.
상기 배치 칩 제조 단계(S200)에서 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지는 각각 폴리프로필렌 20 내지 40 중량부, 폴리에틸렌 40 내지 60 중량부 및 EVA 수지 10 내지 20 중량부의 중량비율로 혼합될 수 있고, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지가 투입된 압출기는 EVA 수지가 용융될 수 있도록 220 내지 250℃의 온도로 열이 가해질 수 있다.In the batch chip manufacturing step (S200), the polypropylene, polyethylene, and EVA resin may be mixed in a weight ratio of 20 to 40 parts by weight of polypropylene, 40 to 60 parts by weight of polyethylene, and 10 to 20 parts by weight of EVA resin, respectively. The extruder in which the polypropylene, polyethylene, and EVA resin are added may be heated to a temperature of 220 to 250 ° C. so that the EVA resin may be melted.
또한, 본 발명에서는 상기 칩을 냉각하여 절단함으로써 배치 칩을 제조하는데, 상기 냉각은 냉각기에서 진행되고, 50 내지 60℃의 온도에서 수행될 수 있다.In addition, in the present invention, the batch chip is manufactured by cooling and cutting the chip, wherein the cooling is performed in a cooler, and may be performed at a temperature of 50 to 60 ° C.
3. 마스터 배치 칩 제조 단계(S300)3. Master batch chip manufacturing step (S300)
상기 마스터 배치 칩 제조 단계(S300)는 상기 배치 칩과 항충 물질을 혼합하여 항충 효과를 나타내는 마스터 배치 칩을 제조하는 단계이다.The master batch chip manufacturing step (S300) is a step of manufacturing a master batch chip having an anti-worm effect by mixing the batch chip and the anti-worm material.
상기 마스터 배치 칩 제조 단계(S300)는 상기 배치 칩 및 항충 물질을 압출기에 투입하고, 상기 배치 칩 및 항충 물질이 투입된 압출기에 열을 가하여 용용 시킨 후, 상기 용융된 배치 칩 및 항충 물질을 혼합한 후 교반하고 냉각하여 절단함으로써 마스터 배치 칩을 제조할 수 있다.In the master batch chip manufacturing step (S300), the batch chip and the antiworm material are introduced into an extruder, and the molten batch chip and the antiworm material are mixed after applying the heat to the extruder into which the batch chip and the antiworm material are added. After stirring, cooling and cutting, the master batch chip can be produced.
상기 마스터 배치 칩 제조 단계(S300)에서 상기 배치 칩 및 항충 물질은 각각 배치 칩 100 내지 300 중량부 및 항충 물질 5 내지 15 중량부의 중량 비율로 혼합되고, 220 내지 240℃의 온도로 가열되어 용융될 수 있다.In the master batch chip manufacturing step (S300), the batch chip and the anti-worm material are mixed at a weight ratio of 100 to 300 parts by weight of the batch chip and 5 to 15 parts by weight of the anti-worm material, respectively, and heated to a temperature of 220 to 240 ° C. to be melted. Can be.
또한, 상기 마스터 배치 칩 제조 단계(S300)에서 상기 마스터 배치 칩은 상기 용융된 배치 칩 및 항충 물질을 혼합하고 교반한 후 냉각하고 절단함으로써 제조될 수 있는데, 상기 냉각은 40 내지 50℃ 온도를 유지하는 냉각기에서 수행될 수 있다.In addition, in the master batch chip manufacturing step (S300), the master batch chip may be manufactured by mixing, stirring, cooling, and cutting the molten batch chip and the anti-worm material, wherein the cooling is maintained at a temperature of 40 to 50 ° C. May be performed in a cooler.
한편, 상기 마스터 배치 칩 제조 단계(S300)에서는 상기 배치 칩 및 항충 물질을 혼합하여 마스터 배치 칩을 제조하는 것 이외에, 원적외선과 음이온이 다량 방사되고 오염 물질에 대한 항균, 탈취 효과가 있는 기능성 물질을 더 혼합하여 혼합 칩을 제조할 수 있는데, 상기 기능성 물질은 상기 항충 물질 100 중량부에 대해 50 내지 150 중량부의 중량 비율로 사용될 수 있다.On the other hand, in the master batch chip manufacturing step (S300), in addition to manufacturing the master batch chip by mixing the batch chip and the anti-worm material, a large amount of far-infrared rays and anions are radiated and the antibacterial, deodorizing effect on the contaminant functional material The mixture may be further mixed to prepare a mixed chip. The functional material may be used in a weight ratio of 50 to 150 parts by weight based on 100 parts by weight of the anti-worm material.
또한, 상기 마스터 배치 칩 제조 단계(S300)에서는 상기 배치 칩 및 항충 물질을 혼합하여 마스터 배치 칩을 제조하는 것 이외에, 해충 기피, 항균, 탈취 등의 효과가 있는 편백나무 추출액을 더 혼합하여 마스터 배치 칩을 제조할 수 있는데, 상기 편백나무 추출액은 상기 항충 물질 100 중량부에 대해 1 내지 3 중량부의 중량 비율로 사용될 수 있다.In addition, in the master batch chip manufacturing step (S300), in addition to preparing the master batch chip by mixing the batch chip and the anti-insect material, the master batch by further mixing the cypress extract with the effects of pest avoidance, antibacterial, deodorant, etc. Chips may be prepared, and the cypress extract may be used in a weight ratio of 1 to 3 parts by weight based on 100 parts by weight of the antiparasitic material.
본 발명은 상기 마스터 배치 칩 제조 단계(S300)에서 제조된 항충 마스터 배치 칩을 이용하여 항충 제품을 제조할 수 있는데, 상기 마스터 배치 칩 제조 단계(S300)에서 제조된 항충 마스터 배치 칩을 원료에 포함하여 다양한 종류의 항충 제품을 제조하는 공정은 제품마다 다양할 수 있고, 각각의 제품을 생산하는 공정은 공지의 기술인바 이에 대한 구체적인 제조 공정은 생략하기로 한다.The present invention can produce an anti-worm product using the anti-worm master batch chip manufactured in the master batch chip manufacturing step (S300), the anti-worm master batch chip prepared in the master batch chip manufacturing step (S300) as a raw material Therefore, the process of manufacturing various kinds of anti-worm products may vary from product to product, and the process of producing each product is a well-known technology, so a detailed manufacturing process thereof will be omitted.
또한, 본 발명에서 상기 항충 효과를 가지는 마스터 배치 칩을 이용하여 제조할 수 있는 항충 제품으로는, 예를 들어, 폴리에스테르, 나이론, 폴리에틸렌, 액상 불포료 폴리에스테르, 폴리염화비닐지수판, pvc바닥재, 가교화 폴리에틸렌, 표장용 폴리에틸렌 필름, 폴리에틸렌관, 가용성 폴리에틸렌관, 폴리메틸펜텐-PMP, 폴리메틸펜텐-PMP, 폴리아릴레이트-PAR, 폴리아세탈-POM, 폴리에테르에테르케톤-PEEK, 폴리에틸렌-PE, 폴리우레탄-PU, 폴리페닐렌설파이드-PPS, 아크릴수지, 폴리이미드-PI, 폴리페닐렌에테르-PPE, 폴리메타크릴스티렌-MS, 폴리아미드-PA, 폴리카보네이트-PC, 폴리염화비닐-PVC, 폴리카보네이트-PC, 폴리프로필렌-PP, 플라스틱, 농자재 및 건설자재로 이루어진 군에서 선택된 어느 하나 이상에 적용될 수 있으며, 상기와 같이 열거된 제품 이외에도 공지된 다양한 제품에 적용 가능하고, 본 발명의 기술적 사상은 이외의 제품에도 적용됨을 밝힌다.In addition, in the present invention, the anti-worm products that can be produced using the master batch chip having the anti-worm effect, for example, polyester, nylon, polyethylene, liquid non-polyester polyester, polyvinyl chloride index plate, pvc flooring, Crosslinked polyethylene, polyethylene film for marking, polyethylene tube, soluble polyethylene tube, polymethylpentene-PMP, polymethylpentene-PMP, polyarylate-PAR, polyacetal-POM, polyetheretherketone-PEEK, polyethylene-PE, Polyurethane-PU, Polyphenylene sulfide-PPS, Acrylic resin, Polyimide-PI, Polyphenylene ether-PPE, Polymethacrylstyrene-MS, Polyamide-PA, Polycarbonate-PC, Polyvinyl chloride-PVC, It can be applied to any one or more selected from the group consisting of polycarbonate-PC, polypropylene-PP, plastic, agricultural and construction materials, and known in addition to the products listed above Applicable to a variety of products, and reveals the technical concept is applied to other than the products of the present invention.
이하, 첨부된 도면을 참조하여 본 발명에 따른 항충 마스터 배치 칩을 이용한 실시예를 들어 더욱 구체적으로 설명하기로 한다.Hereinafter, with reference to the accompanying drawings an embodiment using an anti-worm master batch chip according to the present invention will be described in more detail.
< 실시예 1 ><Example 1>
먼저, 바이펜트린(Bifenthrin)으로 이루어진 항충 물질 및 배치 칩을 준비하고, 항충 물질 10 중량부 및 마스터 배치 칩 200 중량부의 중량 비율로 혼합한 후 230℃의 온도로 가열하고 45℃ 온도에서 냉각하여 마스터 배치 칩을 제조하였다.First, an anti-worm material and a batch chip made of Bifenthrin are prepared, mixed at a weight ratio of 10 parts by weight of the anti-worm material and 200 parts by weight of the master batch chip, and then heated to a temperature of 230 ° C. and cooled at 45 ° C. Master batch chips were prepared.
이어서, 상기 마스터 배치 칩을 비닐의 원료에 포함하여 항충 선형저밀도 폴리에틸렌(LLDPE) 비닐을 제조하였다.Subsequently, the master batch chip was included as a raw material of vinyl to prepare anti-worm linear low density polyethylene (LLDPE) vinyl.
< 실시예 2 ><Example 2>
실시예 1과 동일한 방법으로 선형저밀도 폴리에틸렌(LLDPE) 비닐을 제조하였는데, 실시예 2에서는 항충 물질 100 중량부에 대하여 기능성 물질 100 중량부 및 편백나무 추출액 2 중량부의 중량 비율로 더 포함되도록 하여 항충 선형저밀도 폴리에틸렌(LLDPE) 비닐을 제조하였다.Linear low-density polyethylene (LLDPE) vinyl was prepared in the same manner as in Example 1, but in Example 2 it was further included in the weight ratio of 100 parts by weight of the functional material and 2 parts by weight of cypress extract with respect to 100 parts by weight of the antibacterial material. Low density polyethylene (LLDPE) vinyl was made.
< 비교예 ><Comparative Example>
항충 물질을 사용하지 않은 선형저밀도 폴리에틸렌(LLDPE) 비닐을 준비하였고, 이를 비교예로 사용하였다.Linear low density polyethylene (LLDPE) vinyl was prepared without the use of anti-worm material, and this was used as a comparative example.
상기와 같이 제조된 선형저밀도 폴리에틸렌(LLDPE) 비닐을 이용하여 실험을 수행하였고, 그 결과를 하기의 표에 나타내었다.The experiment was performed using the linear low density polyethylene (LLDPE) vinyl prepared as described above, the results are shown in the table below.
1. 탈취 실험1. Deodorization experiment
실시예 2에 따라 제조된 선형저밀도 폴리에틸렌(LLDPE)과 비교예에 따른 선형저밀도 폴리에틸렌(LLDPE) 비닐의 탈취 실험을 수행하였고, 그 결과를 하기의 [표 1]에 나타내었다.The deodorization experiment of the linear low density polyethylene (LLDPE) prepared according to Example 2 and the linear low density polyethylene (LLDPE) vinyl according to the comparative example was performed, and the results are shown in the following [Table 1].
상기 [표 1]을 참조하면, 암모니아의 시험가스 및 FTIR을 이용한 가스농도측정에 의해 얻어진 탈취시험 결과이며, 실시예 2에 따라 제조된 선형저밀도 폴리에틸렌(LLDPE) 비닐은 시간이 지날수록 탈취율이 향상됨을 알 수 있다.Referring to [Table 1], the test gas of ammonia and deodorization test results obtained by gas concentration measurement using FTIR, linear low density polyethylene (LLDPE) vinyl prepared according to Example 2 is improved deodorization rate over time It can be seen.
2. 항균 시험2. Antibacterial test
상기 실시예 2에 따라 제조된 선형저밀도 폴리에틸렌(LLDPE) 비닐을 이용하여 사용균주 Escherichia coil ATCC 25922 및 Pseudomonas aeruginosa ATCC 15442을 이용하여 항균 시험을 수행하였으며, 그 결과를 하기의 [표 2]에 나타내었다.The antibacterial test was performed using the strain Escherichia coil ATCC 25922 and Pseudomonas aeruginosa ATCC 15442 using the linear low density polyethylene (LLDPE) vinyl prepared according to Example 2, and the results are shown in the following [Table 2]. .
상기 [표 2]를 참조하면, 비교예에 따른 선형저밀도 폴리에틸렌(LLDPE) 비닐은 시간이 경과함에 따라 세균이 증가하고 있으나, 실시예 2에 따른 선형저밀도 폴리에틸렌(LLDPE) 비닐은 세균이 감소하는 것을 확인할 수 있었다.Referring to [Table 2], the linear low-density polyethylene (LLDPE) vinyl according to the comparative example is increased bacteria over time, the linear low-density polyethylene (LLDPE) vinyl according to Example 2 shows that the bacteria is reduced I could confirm it.
여기서, 농도의 단위 중 CFU는 Colony Forming Unit를 의미하며 40p는 0.04mL를 의미한다.Here, CFU means Colony Forming Unit and 40p means 0.04 mL.
3. 항충 효과3. Antibacterial effect
실시예 1에 따라 제조된 선형저밀도 폴리에틸렌(LLDPE) 비닐을 종이에 부착한 후, 개미가 이동하는 통로에 부착하여 항충 효과를 육안으로 관찰하였다.The linear low density polyethylene (LLDPE) vinyl prepared according to Example 1 was attached to paper, and then attached to a passage through which ants traveled to observe the anti-worm effect visually.
도 2 및 도 3은 본 발명에 따른 항충 제품의 일 예로, 설탕물을 수용한 항충 비닐에 대하여 꿀벌의 기피 여부를 관찰한 사진이다.2 and 3 is an example of an anti-worm product according to the present invention, is a photograph observing whether or not to avoid bees against the anti-insect vinyl containing sugar water.
도 2 및 도 3을 참조하면, 실시예 1에 따른 항충 비닐에 꿀벌이 좋아하는 설탕물을 수용한 후, 박스 내에서 꿀벌의 이동을 육안으로 관찰한 결과, 꿀벌이 설탕물이 수용된 항충 비닐로 이동하지 않고, 설탕물이 수용된 항충 비닐을 기피하는 것을 확인할 수 있었다.2 and 3, after receiving the bees' favorite sugar water in the anti-insect vinyl according to Example 1, and visually observed the movement of the bees in the box, the honey bee into the anti-insect vinyl containing sugar water It was confirmed that avoiding anti-worm vinyl containing sugar water without moving.
이를 통해 실시예 1에 따른 항충 비닐은 해충(꿀벌)이 기피하는 항충 효과가 우수함을 확인할 수 있다.Through this, it can be confirmed that the anti-insect vinyl according to Example 1 has an excellent anti-worm effect avoided by pests (bees).
4. 진드기 기피성 시험4. Mite repellency test
상기 실시예 2와 같이 제조된 선형저밀도 폴리에틸렌(LLDPE)을 1m x 1m의 길이의 시료편을 제조하였고, 이를 이용하여 진드기 기피성 시험을 수행하였다.A linear low density polyethylene (LLDPE) prepared as in Example 2 was prepared a sample piece of 1m x 1m in length, using the mite repellency test.
상기 [표 3] 및 [표 4]는 한국소비과학연구센터에서 시행한 진드기 기피성 시험 결과이며, 사용공시충 큰다리 먼지 진드기(D.farinae) 및 세로무늬 먼지 진드기 (D.pteronyssinus)에 대해 침입 저지법에서 93 ~ 94.8% 및 94.6 ~ 95.5%, 시험관법에서 모두 99.9%의 기피율을 나타내어 진드기 억제에도 효과가 있음을 알 수 있다.[Table 3] and [Table 4] are the results of the tick avoidance test conducted by the Korea Consumer Science Research Center, and the use of the specimens for the large leg dust mites (D.farinae) and vertical pattern dust mites (D.pteronyssinus) The invasion inhibition method showed 93 to 94.8% and 94.6 to 95.5%, and in vitro, 99.9% evasion rate.
이상, 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.As mentioned above, although one preferred embodiment of the present invention has been described, those skilled in the art will understand that the present invention can be implemented in other specific forms without changing the technical spirit or essential features. Could be. Therefore, it should be understood that one embodiment described above is illustrative in all respects and not restrictive.
Claims (5)
칩 상태로 제조된 폴리프로필렌(PP:PolyProphlene), 폴리에틸렌(PE: PolyEthylene) 및 EVA(Ethylene Vinyl Acetate Copolymer) 수지를 모두 압출기에 투입하고, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지가 투입된 압출기에 열을 가하여 용용 시킨 후, 상기 폴리프로필렌, 폴리에틸렌 및 EVA 수지를 교반하여 칩을 제조하고, 상기 칩을 냉각하여 절단함으로써 배치 칩을 제조하는 배치 칩 제조 단계(S200); 및
상기 배치 칩과 항충 물질을 혼합하여 마스터 배치 칩을 제조하는 마스터 배치 칩 제조 단계(S300)를 포함하되,
상기 항충 물질로는 알레트린(Allethrin), 바이펜트린(Bifenthrin), 사이할로트린(Cyhalothrin), 사이페르메트린(Cypermethrin), 사이플루트린(Cyfluthrin), 델타메트린(Deltamethrin), 에토펜프록스(Etofenprox), 펜발레레이트(Fenvalerate), 페르메트린(Permethrin), 페노트린(Phenothrin), 프랄레트린(Prallethrin), 레스메트린(Resmethrin), 테트라메트린(Tetramethrin), 트랄로메트린(Tralomethrin) 및 트랜스플루트린(Transfluthrin)으로 이루어진 군에서 선택된 적어도 어느 하나 이상이 사용되고,
상기 항충 물질 준비 단계(S100)에서 상기 항충 물질 이외에 기능성 물질 및 편백나무 추출액을 더 포함하되,
상기 기능성 물질은 상기 항충 물질 100 중량부에 대해 50 내지 150 중량부의 중량 비율로 사용되고, 상기 기능성 물질은 이산화규소 나노입자 5 내지 10 중량부, 견운모 1 내지 3 중량부, 광촉매 0.5 내지 1.5 중량부, 활성탄 0.1 내지 1 중량부 및 황토 0.1 내지 0.5 중량부의 중량 비율로 포함되고, 상기 광촉매는 이산화티탄(TiO2) 2 내지 4 중량부 및 나노은 분말 0.5 내지 1.5 중량부의 중량비율로 혼합되어 제조되고,
상기 편백나무 추출액은 상기 항충 물질 100 중량부에 대해 1 내지 3 중량부의 중량 비율로 포함되는 것을 특징으로 하는 항충 마스터 배치 칩의 제조방법.Anti-worm material preparing step of preparing an anti-worm material (S100);
Polypropylene (PP: PolyProphlene), Polyethylene (PE: PolyEthylene) and EVA (Ethylene Vinyl Acetate Copolymer) resins prepared in a chip state are all added to an extruder, and heat is applied to the extruder into which the polypropylene, polyethylene, and EVA resin are added. After dissolution, a batch chip manufacturing step (S200) of manufacturing a batch chip by stirring the polypropylene, polyethylene, and EVA resin to manufacture a chip, and cooling and cutting the chip; And
Including a master batch chip manufacturing step (S300) for mixing the batch chip and the anti-worm material to produce a master batch chip,
The antiparasitic substances include Allethrin, Bifenthrin, Cyhalothrin, Cypermethrin, Cyfluthrin, Deltamethrin, Etofen Etofenprox, Fenvalerate, Permethrin, Phenothrin, Pralethrin, Resmethrin, Tetramethrin, Tralomethrin (Tralomethrin) and at least one selected from the group consisting of Transfluthrin is used,
Further comprising a functional material and a cypress extract in addition to the anti-worm material in the anti-worm material preparation step (S100),
The functional material is used in a weight ratio of 50 to 150 parts by weight based on 100 parts by weight of the anti-worm material, the functional material is 5 to 10 parts by weight of silicon dioxide nanoparticles, 1 to 3 parts by weight of mica, 0.5 to 1.5 parts by weight of a photocatalyst, 0.1 to 1 parts by weight of activated carbon and 0.1 to 0.5 parts by weight of loess, the photocatalyst is prepared by mixing at a weight ratio of 2 to 4 parts by weight of titanium dioxide (TiO 2 ) and 0.5 to 1.5 parts by weight of nanosilver powder,
The cypress extract is a method for producing an anti-worm master batch chip, characterized in that contained in a weight ratio of 1 to 3 parts by weight based on 100 parts by weight of the anti-worm material.