KR102013773B1 - Soil improvement agent composition enabling slope plantation to vegetation and slope protection construction method using same - Google Patents
Soil improvement agent composition enabling slope plantation to vegetation and slope protection construction method using same Download PDFInfo
- Publication number
- KR102013773B1 KR102013773B1 KR1020190043036A KR20190043036A KR102013773B1 KR 102013773 B1 KR102013773 B1 KR 102013773B1 KR 1020190043036 A KR1020190043036 A KR 1020190043036A KR 20190043036 A KR20190043036 A KR 20190043036A KR 102013773 B1 KR102013773 B1 KR 102013773B1
- Authority
- KR
- South Korea
- Prior art keywords
- soil
- weight
- slope
- vegetation
- composition
- Prior art date
Abstract
Description
본 발명은 사면 녹화시 대상지반 토양을 개량하는 토양 개량제 조성물 및 토양 개량제를 이용한 사면보호 시공방법에 관한 것으로, 보다 상세하게는 현지토, 부엽토, 한약재 찌꺼기 및 섬유재로 이루어지는 주재와 결합재, 경화제, 분말증점제, 고흡수성 폴리머 및 보습제로 이루어지는 첨가제와 pH 농도가 7.2~7.6을 이루는 약알칼리수를 포함하여 이루어지는 토양 개량제 조성물을 제공하고, 상기 조성물로 이루어지는 토양 개량제를 이용하여 사면 지반 개량을 실시하는 시공방법에 관한 것이다.The present invention relates to a soil protector composition for improving the soil of the subject during greening of the slope and to a slope protection construction method using the soil improver, and more particularly, a main material and a binder, a hardener, and a local soil, a foliar soil, herbal remnants and textiles. Construction method which provides the soil improver composition which consists of the additive which consists of a powder thickener, a super absorbent polymer, and a moisturizing agent, and the weak alkali water which has a pH concentration of 7.2-7.6, and performs slope improvement using the soil improver which consists of said composition. It is about.
일반적으로 경사면 식생공법은 경사면 방호의 일반적인 공법으로써 식물을 사면 및 경사면 상에 초목이 무성하게 자라게 하여 경사면 침식을 방지하고, 근계(根系)에 의해 표층 흙을 고정하는 효과를 가지며, 경관 및 토지의 보전을 도모하는 것으로 식생공이 적합하지 않은 조건 아래에서는 두꺼운 층 기재 내 뿜는 공법이나 객토 종자 내 뿜는 공법이 사용되고 있다.In general, the slope vegetation method is a general method of protection of slopes, and vegetation grows on slopes and slopes to prevent erosion of slopes and to fix surface soil by root system. Under the condition that the vegetation hole is not suitable for the conservation, the thick layer base material spraying method or the seed seed spraying method is used.
상기 종자와 함께 내 뿜는 공법은 종자를 인공토양과 함께 살포하여 식생의 생육기반을 인공적으로 조성하는 것을 의미한다. 대부분의 흙사면은 식물이 자랄 수 있도록 식생기반토양을 충분히 제공하지만 절토 이후 절개면에서는 종자가 식생 가능하도록 물과 양분을 공급해 줄 수 있는 토양이 극히 부족하기 때문에 식물이 성장한는 것에 있어서는 제약이 따르고 있다.The method of flushing with the seed means to artificially create a growth base of the vegetation by spraying the seed together with artificial soil. Most soil slopes provide enough vegetation-based soil for plants to grow, but after cutting, there is a limit to the growth of plants because of the lack of soil that can supply water and nutrients for seeds to grow. .
특히 우리나라의 지형 지질 조건은 약 67%가 산악지형이며, 토층의 깊이가 얕은 암반지역을 형성하고 있기 때문에 식물의 성장이 어려운 환경이 조성되어 있으므로 식물의 성장기반을 조성을 위한 토양 개량제 개발이 필요하다.In particular, about 67% of the topographical geological conditions in Korea are mountainous topography, and because of the shallow rock formations, the environment is difficult to grow. Therefore, it is necessary to develop soil improvers for the growth of the plant. .
종래 녹생토를 위한 인공 토양의 주재료는 제지공장에서 폐기물로 발생되고 있는 제지 슬러지, 제지 슬러지 소각재, 화력발전소에서 발생하는 슬러지 및 토탄과 하수슬러지를 일부 발효시킨 것으로 여기에 분뇨, 비료 성분과 식물의 종자를 혼합하여 제조되어 사용되고 있다.The main material of artificial soil for green soil is fermentation of paper sludge, paper sludge incinerator, sludge from coal-fired power plant, and peat and sewage sludge, which are produced as wastes at the paper mill. It is manufactured and used by mixing.
그러나, 종래 녹생토를 위한 토양 개량제는 폐기물의 재사용으로 인한 토양오염의 문제가 발생되고 있고, 단단한 지반 상부에 사용시 내구성 문제가 발생되고 있으므로 내구성 강화와 친환경적인 토양 개량제의 개발이 요구되고 있다.However, the conventional soil improver for rust soil is a problem of soil pollution due to the reuse of waste, and the durability problem occurs when used on the top of the solid ground is required to strengthen the durability and development of environmentally friendly soil improver.
사면 토양 개량제 조성물 및 사면 보호 시공방법의 선행기술들로는 한국등록특허 제10-0921711호(2009.10.13.) 산업의 부산물인 비산제를 기반으로 하는 식생이 가능한 토양 개량제를 세굴 및 침식에 취약한 흙과 교반하여 표층을 보강함으로써, 우기시 비탈면의 토사유실 및 세굴에 따른 파괴를 방지할 수 있고, 아울러 붕괴된 비탈면의 경우 파괴된 현장 흙과 토양 개량제를 혼합 교반하여 시공하여 단시간에 효과적으로 복구할 수 있는 토양 안정 및 개량제를 이용한 사면보호 시공방법을 제공하고, 한국공개특허 제10-2015-0061761호(2015.06.05.)는 인공지반의 녹화에 커피찌꺼기, 톱밥과 같은 폐자원을 재활용한 인공 지반의 녹화를 위한 인공토양 조성물 및 그 제조방법으로 커피찌꺼기를 포함하는 개량토;와, 상기 개량토의 중량을 기준으로 0.1~3 중량%의 고화제;로서 설정된 비율로 물에 희석되어 구비되는 고화제;가 혼합되어 형성되는 인공 지반의 녹화를 위한 인공토양 조성물이 제공하고 있다.Prior arts of slope soil modifier composition and slope protection construction method include vegetative soil modifier based on fugitive, which is a by-product of Korea Patent Registration No. 10-0921711 (October 13, 2009). By reinforcing the surface layer by agitation, it is possible to prevent the destruction due to soil loss and scour of the slope during the rainy season, and in the case of the collapsed slope, it is possible to effectively recover in a short time by mixing and mixing the destroyed site soil and soil modifier. A slope protection construction method using soil stabilization and improving agent is provided, and Korean Laid-Open Patent Publication No. 10-2015-0061761 (2015.06.05.) Is an artificial ground that recycles waste resources such as coffee grounds and sawdust. Artificial soil composition for greening and improved soil containing coffee grounds as a manufacturing method thereof; and 0.1 to 3% by weight of solidifying agent based on the weight of the improved soil; It is provided with an artificial soil composition for greening the artificial ground is formed by mixing;
상기 선행기술들을 살펴보면 종래의 산업 부산물을 사용하고 있으므로 환경 오염 문제를 여전히 가지고 있고, 단순 커피 찌꺼기등의 재료를 이용하여 개량제를 제조하였을때 내구성이 약해지고, 사면 녹화의 효율이 검증이 어렵다는 문제점을 가지고 있다.Looking at the prior art, there is still a problem of environmental pollution since the use of conventional industrial by-products, and when the improver is manufactured using materials such as simple coffee grounds, the durability becomes weak, and the efficiency of slope greening is difficult to verify. have.
본 발명이 이루고자 하는 기술적 과제는 상기와 같은 종래기술과 선행기술들이 가지고 있는 문제점인 산업부산물로 이루어진 토양 개량제에 의해서 발생되는 환경오염을 방지하고, 토양 개량제 시공 후 토사면의 표층의 강도를 높이며, 식물 생장이 잘 이루어질 수 있는 토양 개량제의 조성물을 제공하고, 상기 토양 개량제를 이용한 사면보호 시공방법을 제공하는 것이다.The technical problem to be achieved by the present invention is to prevent environmental pollution caused by the soil improver consisting of industrial by-products, which is a problem with the prior art and the prior art as described above, to increase the strength of the surface layer of the soil after construction of the soil improver, It is to provide a composition of a soil improver that can be well grown plants, and to provide a slope protection construction method using the soil improver.
상기와 같은 문제점을 해결하고 목적을 달성하기 위하여 본 발명의 일 실시예에 따른 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물은 현지토, 부엽토, 한약재 찌꺼기 및 섬유재로 이루어지는 주재; 결합재, 경화제, 분말증점제, 고흡수성 폴리머(SAP, Super Absorbent Polymer) 및 보습제로 이루어지는 첨가제; 및 pH 농도가 7.2~7.6을 이루는 약알칼리수;를 포함하여 이루어진다.In order to solve the above problems and achieve the object, the soil improver composition to allow vegetation in the slope greening according to an embodiment of the present invention is a main material consisting of local soil, foliar soil, herbal remnants and fiber materials; Additives comprising a binder, a hardener, a powder thickener, a super absorbent polymer (SAP) and a moisturizer; And weak alkaline water having a pH concentration of 7.2 to 7.6.
상기 주재는 82~84 중량%, 첨가제는 7~10 중량% 및 약알칼리수 7~10 중량%로 이루어진다.The main material is 82 to 84% by weight, the additive is composed of 7 to 10% by weight and weak alkaline water 7 to 10% by weight.
상기 주재는 현지토 69~75 중량%, 부엽토 9~16 중량%, EM(Effective Micro-organisms)발효액으로 발효된 한약재 찌꺼기 7~13 중량% 및 야자열매 껍질, 대마 및 볏짚 섬유질 재료 중 선택된 하나 이상으로 이루어진 섬유재 1~5 중량%로 이루어진다.The host material is 69-75% by weight of local soil, 9-16% by weight of foliar soil, 7-13% by weight of medicinal herb residue fermented with Effective Micro-organisms (EM) fermentation solution, and at least one selected from coconut shell, hemp and rice straw fiber materials. It consists of 1 to 5% by weight of the fiber material.
상기 첨가제는 결합재 39~51 중량%, 경화제 29~41 중량%, 분말증점제 3~7 중량%, 고흡수성 폴리머 1~3 중량% 및 보습제 7~13 중량%로 이루어진다.The additive consists of 39 to 51% by weight of the binder, 29 to 41% by weight of the curing agent, 3 to 7% by weight of the powder thickener, 1 to 3% by weight of the super absorbent polymer, and 7 to 13% by weight of the moisturizing agent.
상기 결합재는 마이크로 시멘트 33~37 중량%, 아윈계 시멘트 8~12 중량% 및 반수석고 53~57 중량%로 이루어진다.The binder is composed of 33 to 37% by weight of micro cement, 8 to 12% by weight of Arwin-based cement, and 53 to 57% by weight of hemihydrate gypsum.
상기 경화제는 팽창형 경화제이고, 분말증점제는 몬모릴로 나이트계 벤토나이트(Sodium Bentonite)분말이며, 보습제는 폴리카본산계 고분자 액상 가소제인 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물을 제공한다.The hardener is an expandable hardener, the powder thickener is a montmorillonite-based bentonite powder, and the moisturizing agent is a polycarboxylic acid-based polymer liquid plasticizer to provide a soil improver composition for vegetation on slope greening.
또한, 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법은 a) 시공되는 지반의 표층을 계획되는 깊이까지 깎는 땅깎기 단계;In addition, the slope protection construction method using a soil modifier composition to allow vegetation for slope greening comprises: a) a ground cutting step of cutting the surface layer of the ground to be planned depth;
b) 상기 땅깎기 단계에서 수득된 현지토에 부엽토, 한약재 찌꺼기 및 섬유재를 교반하여 생성된 주재와 결합재, 경화제, 분말증점제, 고흡수성 폴리머 및 보습제로 이루어진 첨가제와 약알칼리수를 교반혼합하여 토양 개량제를 제조하는 혼합단계; c) 상기 혼합단계에서 제조된 토양 개량제를 시공되는 지반에 포설하는 포설단계; 및 d) 상기 포설단계에서 포설된 토양 개량제와 표층면의 대상토를 5회이상 혼합하고, 다짐하는 다짐단계;로 이루어진다.b) a soil improver by stirring and mixing additives and weak alkali water, consisting of a main material, a binder, a hardener, a powder thickener, a superabsorbent polymer, and a moisturizer, produced by stirring the subleaf soil, herbal remnants, and fiber materials on the local soil obtained in the grounding step. Mixing step to prepare; c) laying step of laying the soil improver prepared in the mixing step on the ground to be constructed; And d) a compaction step of mixing and compacting at least five times the soil improver and the target soil of the surface layer laid in the laying step.
상기 땅깎기 단계는 표면유실 및 세굴로 인한 교란층 이상까지 실시되되 시공 위치에 유수가 있거나 지하수위가 높을 경우 가배수를 위한 트랜치를 설치하여 유수의 유입을 방지하고, 표면층의 수분을 제거하는 공정을 더한다.The grounding step is carried out up to the disturbance layer due to surface loss and scour, but when the water flows in the construction location or the groundwater level is high, install a trench for drainage drainage to prevent the inflow of the flow of water, and remove the water of the surface layer Add.
상기 포설 단계는 1㎡ 당 개량될 대상토의 중량대비 토양 개량제를 9~30% 이상 포설하고, 2시간 안에 대상토와 혼합교반하고 다짐을 완료시켜야 하며, 기온이 1~5℃일 때는 보온 덮개를 이용하여 다짐단계 후 보온처리를 실시하되 기온이 영하로 떨어지면 시공을 중단한다.The laying step is to install more than 9 to 30% of the soil improver to the weight of the target soil to be improved per 1㎡, to stir and mix with the target soil within 2 hours, when the temperature is 1 ~ 5 ℃ to cover the insulation After the compaction step, conduct heat treatment, but stop construction when the temperature drops below zero.
상기 토양 개량제는 주재 82~84 중량%, 첨가제 7~10 중량% 및 약알칼리수 7~10 중량%로 혼합되어 이루어지는 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법을 제공한다.The soil modifier provides a slope protection construction method using a soil modifier composition to allow vegetation in the slope greening is mixed with a main material 82 ~ 84% by weight, additives 7 ~ 10% by weight and weak alkaline water 7 ~ 10% by weight.
이상에서 설명한 바와 같이 본 발명에 의한 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물 및 이를 이용한 사면보호 시공방법은 다음과 같은 효과가 있다.As described above, the soil improver composition and slope protection construction method using the same for allowing vegetation in slope greening according to the present invention have the following effects.
(1) 본 발명은 주재가 현지토, 부엽토, 한약재 찌꺼기 및 섬유재 등의 친환경적인 조성물로 이루어져 사면 시공 후 발생 될 수 있는 환경오염을 저감시키며, 식물 발아에 도움이 된다.(1) The present invention is made of environmentally friendly compositions such as local soil, foliar soil, herbal remnants, and textile materials to reduce the environmental pollution that can occur after construction, and helps plant germination.
(2) 본 발명은 첨가제를 더하여 표층면을 형성하는 본 발명의 토양 개량제의 강도를 높여 사면 표면층 내구성이 향상된다.(2) The present invention improves the slope surface layer durability by increasing the strength of the soil improving agent of the present invention which forms an surface layer by adding an additive.
(3) 본 발명은 약알칼리수를 이용하여 식물 생장에 도움이 되도록 pH농도를 조절하여 화학 원료에 의한 pH농도 조절을 실시하지 않으므로 친환경적이다.(3) The present invention is environmentally friendly because it does not control the pH concentration by chemical raw materials by adjusting the pH concentration to help plant growth using weak alkaline water.
도 1은 본 발명의 바람직한 일 실시예에 따른 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법을 나타내는 공정도이다.1 is a process chart showing a slope protection construction method using a soil modifier composition to enable vegetation in the slope greening according to an embodiment of the present invention.
본 발명의 명칭은 "사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물 및 이를 이용한 사면보호 시공방법"으로 통상의 기술자가 쉽게 알 수 있도록 구체적인 내용을 기재하고, 충분히 유추 가능한 별도의 기재는 생략하며, 필요경우 실시예 및 도면을 기재한다. 또한, 본 명세서 및 특허청구범위에서 정의된 용어들은 한정 해석하지 아니하며, 운용자의 의도 또는 관례등에 따라 달라질 수 있고, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야 한다.The name of the present invention is "a soil improver composition to allow vegetation for slope greening and slope protection construction method using the same" to describe the specific details so that a person skilled in the art can easily know, a separate description that can be sufficiently inferred is omitted, necessary Examples and drawings are described. In addition, terms defined in the present specification and claims are not limited to interpretation and may vary according to the intention or custom of the operator and should be interpreted as meanings and concepts corresponding to the technical spirit of the present invention.
본 발명의 일면에 있어서,In one aspect of the invention,
상기 식생 개량제 조성물은 The vegetation modifier composition is
현지토, 부엽토, 한약재 찌꺼기 및 섬유재로 이루어지는 주재;A main material consisting of local soil, side leaf soil, herbal remnants and textile materials;
결합재, 경화제, 분말증점제, 고흡수성 폴리머(SAP, Super Absorbent Polymer) 및 보습제로 이루어지는 첨가제; 및Additives comprising a binder, a hardener, a powder thickener, a super absorbent polymer (SAP) and a moisturizer; And
pH 농도가 7.2~7.6을 이루는 약알칼리수;를 포함하여 이루어진다.It comprises a weak alkaline water; pH concentration is 7.2 ~ 7.6.
상기 주재는 82~84 중량%, 첨가제는 7~10 중량% 및 약알칼리수 7~10 중량%로 이루어진다.The main material is 82 to 84% by weight, the additive is composed of 7 to 10% by weight and weak alkaline water 7 to 10% by weight.
상기 주재는 현지토 69~75 중량%, 부엽토 9~16 중량%, EM(Effective Micro-organisms)발효액으로 발효된 한약재 찌꺼기 7~13 중량% 및 야자열매 껍질, 대마 및 볏짚 섬유질 재료 중 선택된 하나 이상으로 이루어진 섬유재 1~5 중량%로 이루어진다.The host material is 69-75% by weight of local soil, 9-16% by weight of foliar soil, 7-13% by weight of medicinal herb residue fermented with Effective Micro-organisms (EM) fermentation solution, and at least one selected from coconut shell, hemp and rice straw fiber materials. It consists of 1 to 5% by weight of the fiber material.
상기 부엽토는 일반적인 천연부엽토를 사용하되 바크퇴비를 더 혼합하여 제조되어 보수력, 보비력을 향상시켜 사면 환경에 대한 적응력을 강화시킬 수 있으며, 식재지 토양의 pH, 양분 보유력 및 완충력을 개선할 수 있다.The foliar soil is prepared by using a general natural foliar soil mixed with more bark compost to improve the water holding capacity, the bobbin power to enhance the adaptability to the slope environment, can improve the pH, nutrient retention and buffering capacity of the planting soil.
사익 한약재 찌꺼기는 효모, 유산균, 광합성 세균 유익한 미생물들이 배양된 EM(Effective Micro-organisms)발효액을 이용하여 발효시킨 것으로 식물 발아에 도움이 된다.Sik herb residue is fermented with yeast, lactic acid bacteria, photosynthetic bacteria and fermentation of EM (Effective Micro-organisms) cultured beneficial microorganisms are helpful for plant germination.
상기 첨가제는 결합재 39~51 중량%, 경화제 29~41 중량%, 분말증점제 3~7 중량%, 고흡수성 폴리머 1~3 중량% 및 보습제 7~13 중량%로 이루어진다.The additive consists of 39 to 51% by weight of the binder, 29 to 41% by weight of the curing agent, 3 to 7% by weight of the powder thickener, 1 to 3% by weight of the super absorbent polymer, and 7 to 13% by weight of the moisturizing agent.
상기 결합재는 마이크로 시멘트 33~37 중량%, 아윈계 시멘트 8~12 중량% 및 반수석고 53~57 중량%로 이루어진다.The binder is composed of 33 to 37% by weight of micro cement, 8 to 12% by weight of Arwin-based cement, and 53 to 57% by weight of hemihydrate gypsum.
상기 마이크로 시멘트는 일반 시중에서 판매되고 있는 것으로 포틀랜드 시멘트와 동일하게 무기물질로 구성되어 있으며, 독성과 냄새가 없는 무공해 주입재로 화학성분은 보통시멘토아 차이가 있다. 또한, 초미립로 초기수화 속도를 조절할 수 있도록 성분이 조정된 것으로 입도가 일반적인 시멘트보다 적으며, 토립자 사이 또는 미세균열로 침투가 높다.The micro cement is commercially available and is composed of inorganic materials as in Portland cement, and is a pollution-free injection material without toxicity and odor. In addition, the ultrafine particles have been adjusted to control the initial hydration rate, the particle size is less than the general cement, and the penetration between the particles and the fine crack is high.
상기 아윈계 시멘트는 생활폐기물 소각재, 정수 슬러지, 석고, 형석 및 탄화규소를 혼합 후 소성하여 제조된 것이다.The Irwin-based cement is manufactured by mixing and burning the municipal waste incinerator, water purification sludge, gypsum, fluorite and silicon carbide.
상기 반수석고(gypsum hemihydrate)는 소석고로 자체적으로 바인더 역할을 수행하는 것으로 무기 복합 결합재가 필요없고, 자체 비표면적이 높기 때문에 화성금속군의 코팅량 조절이 용이하다.The gypsum hemihydrate is a calcined gypsum, which performs its own role as a binder, and does not require an inorganic composite binder, and because of its high specific surface area, it is easy to control the coating amount of the chemical group.
상기 경화제는 팽창형 경화제이고, 분말증점제는 몬모릴로 나이트계 벤토나이트(Sodium Bentonite)분말이며, 보습제는 폴리카본산계 고분자 액상 가소제이다.The hardener is an expandable hardener, the powder thickener is a montmorillonite-based bentonite powder, and the moisturizer is a polycarboxylic acid-based polymer liquid plasticizer.
상기 팽창형 경화제는 황산 칼슘의 수화물로 된 광물인 석고이고, 상기 벤토나이트는 물리적 특성상 물과 반응하며, 본래 체적보다 13~16 배정도 팽창하고, 무게의 5배까지 물을 흡수하여 토사와 혼합층을 만들시 물의 투수계수가 미소하여 지하수 오염을 방지할 수 있다.The expandable curing agent is gypsum, a mineral made of calcium sulfate hydrate, and bentonite reacts with water due to its physical properties, expands about 13 to 16 times larger than its original volume, absorbs water up to 5 times its weight, and forms soil and mixed layers. The water permeability coefficient of city water is small, which can prevent groundwater contamination.
상기 고흡수성 폴리머(SAP, Super Absorbent Polymer)는 일반적으로 사용하는 것을 사용하여도 무방하나 셀룰로오스계열 흡수체와 벤토나이트계열 고분자화합물로 이루어진 것을 사용하여 결합제와 결합력을 높이는 것이 바람직하다.The super absorbent polymer (SAP) may be generally used, but it is preferable to increase the binding strength with the binder by using a cellulose-based absorber and a bentonite-based polymer compound.
또한, 결합재 및 경화제는 강알칼리성을 띄고 있으므로 약알칼리수를 이용하여 식생의 생육에 적합한 pH로 조절한다.In addition, since the binder and the curing agent exhibit strong alkalinity, it is adjusted to a pH suitable for growth of vegetation using weak alkaline water.
실시예Example : : 결합재Binder 배합 combination
본 발명의 첨가제 중 결합재인 마이크로 시멘트, 아윈계 시멘트 및 반수석고를 하기 표 1과 같이 각각 중량대비 배합하여 경화시켰다.Among the additives of the present invention, the binder, micro cement, Irwin-based cement, and hemihydrate gypsum were cured by blending the respective weights as shown in Table 1 below.
시험예Test Example : : 결합재Binder 압축강도 시험 Compressive strength test
상기 실시예에서 배합비율 별로 제조된 1 내지 4의 결합재의 압축강도 시험을 실시하였다. 상기 배합비율로 경화 시킨 후 30일이 경과후 압축강도를 측정하였고, 1은 43 압축강도(MPa), 2는 49 압축강도(MPa), 3은 41 압축강도(MPa), 4는 34 압축강도(MPa)로 나타나 2의 압축강도가 높은 것으로 나타났다.In the above embodiment, the compressive strength test of the binder of 1 to 4 prepared for each mixing ratio was performed. 30 days after curing at the compounding ratio, the compressive strength was measured, 1 is 43 compressive strength (MPa), 2 is 49 compressive strength (MPa), 3 is 41 compressive strength (MPa), 4 is 34 compressive strength The compressive strength of 2 was found to be high as (MPa).
따라서, 상기 결합재의 배합은 실시예의 2와 동일한 배합비율로 제조되어 사면 표층면 대상토와 본 발명의 토양 개량제를 배합시 표층면의 강도가 높아져 흘러내리거나 붕괴되는 사고를 방지할 수 있다.Therefore, the combination of the binder is prepared in the same compounding ratio as in Example 2 to prevent the accident of flowing down or collapse by increasing the strength of the surface layer when mixing the soil surface of the slope and the soil improver of the present invention.
추가의 일면에 있어서,In a further aspect,
상기 고흡수성 폴리머는 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지로 대체하여 사용할 수 있으며, 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지의 제조는 박테리아에서 생성된 미세섬유상 구조의 분말형태를 이루는 바이오 셀룰로오스와 홍조류인 식용 해초를 채취하여 건조시킨 후 분쇄된 분말을 가열된 정제수와 교반하고, 염화칼륨으로 용해한 뒤 상온에서 냉각시켜 겔상태를 생성시키고, 분쇄기에 에탄올과 함께 주입하여 분쇄하되 추가로 에탄올을 주입하여 교반하고, 탈수 및 건조하여 제조된 것이다.The superabsorbent polymer may be used in place of a super absorbent polymer composed of bio cellulose and carrageenan. The preparation of the super absorbent polymer composed of bio cellulose and carrageenan is biocellulose and red algae forming a powder form of microfibrous structure produced by bacteria. After collecting and drying the edible seaweed, the pulverized powder was stirred with heated purified water, dissolved with potassium chloride and cooled at room temperature to produce a gel state. The pulverized powder was injected with ethanol and pulverized. It is prepared by dehydration and drying.
상기 염화칼륨(KCl)의 양은 준비단계에서 준비된 홍조류 분말과 염화칼륨을 중량대비 1:0.004~0.006으로 하는 것이 바람직하다.The amount of potassium chloride (KCl) is preferably 1: 0.004 to 0.006 by weight of red algae powder and potassium chloride prepared in the preparation step.
따라서, 친환경적인 고흡수성 수지를 사용하여 환경오염과 결합재에서 나오는 불순물을 흡착시켜 토양오염을 방지할 수 있다.Therefore, it is possible to prevent soil pollution by adsorbing impurities from environmental pollution and binder using environmentally friendly superabsorbent resin.
본 발명의 일면에 있어서,In one aspect of the invention,
도 1은 본 발명의 바람직한 일 실시예에 따른 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법을 나타내는 공정도로 상기 도 1을 참고하여 토양 개량제 조성물을 이용한 사면보호 시공방법을 하기에 설명한다.1 is a process diagram showing a slope protection construction method using a soil modifier composition to enable vegetation on the slope greening according to an embodiment of the present invention with reference to FIG. Explain.
사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물을 이용한 사면호보 시공방법에 있어서,In the slope hobo construction method using the soil improver composition to allow vegetation for slope greening,
상기 사면보호 시공방법은 The slope protection construction method
a) 시공되는 지반의 표층을 계획되는 깊이까지 깎는 땅깎기 단계;a) pruning, cutting the surface of the ground under construction to the planned depth;
b) 상기 땅깎기 단계에서 수득된 현지토에 부엽토, 한약재 찌꺼기 및 섬유재를 교반하여 생성된 주재와 결합재, 경화제, 분말증점제, 고흡수성 폴리머 및 보습제로 이루어진 첨가제와 약알칼리수를 교반혼합하여 토양 개량제를 제조하는 혼합단계;b) a soil improver by stirring and mixing additives and weak alkali water, consisting of a main material, a binder, a hardener, a powder thickener, a superabsorbent polymer, and a moisturizer, produced by stirring the subleaf soil, herbal remnants, and fiber materials on the local soil obtained in the grounding step. Mixing step to prepare;
c) 상기 혼합단계에서 제조된 토양 개량제를 시공되는 지반에 포설하는 포설단계; 및c) laying step of laying the soil improver prepared in the mixing step on the ground to be constructed; And
d) 상기 포설단계에서 포설된 토양 개량제와 표층면의 대상토를 5회이상 혼합하여 고른 혼합이 되어야 하며, 혼합얼룩 및 토사가 뭉치지 않도록 한다음 다짐하는 다짐단계;로 이루어진다.d) mixing the soil improver and the target soil of the surface layer installed in the laying step 5 times or more to be mixed evenly, compacting step so as not to clump mixed stains and soil.
본 발명은 천층혼합처리공법으로 실시하는 것으로 표층면의 두께를 20~50㎝ 개량시키는 것으로 표층을 고결시키는 것으로 요우가 심하게 비탈면 유실이 발생되는 구간, 비탈면 상부 지형이 집수가 용이한 오목한 형상을 갖는 구간, 붕적층이 분포하는 구간, 비탈면 내의 계곡 구간 중 도수로 시공 구간, 통층의 세굴 및 유실이 심하게 발생되는 비탈면 위치에서 실시된다.The present invention is carried out by the top layer mixing treatment method to improve the thickness of the surface layer by 20 ~ 50 ㎝ by solidifying the surface layer of the yaw is severely sloped area is generated, the top surface of the slope has a concave shape easy to collect In the section, the section where the strata are distributed, and the valley section in the slope, the construction of the raceway, the scour and loss of the channel layer are performed at the slope.
상기 땅깎기 단계는 표면유실 및 세굴로 인한 교란층 이상까지 실시되되 시공 위치에 유수가 있거나 지하수위가 높을 경우 가배수를 위한 트랜치를 설치하여 유수의 유입을 방지하고, 표면층의 수분을 제거하는 공정을 더한다.The grounding step is carried out up to the disturbance layer due to surface loss and scour, but when the water flows in the construction location or the groundwater level is high, install a trench for drainage drainage to prevent the inflow of the flow of water, and remove the water of the surface layer Add.
또한, 사면 배면에서 지하수 유출시 해당 구간에 다발관이나 망암거를 설치하여 지하수를 배출시켜야 바람직하다.In addition, when the groundwater outflow from the back of the slope it is preferable to install the bund or network culvert in the corresponding section to discharge the groundwater.
상기 포설 단계는 1㎡ 당 개량될 대상토의 중량대비 토양 개량제를 9~30% 이상 포설하고, 2시간 안에 대상토와 혼합교반하고 다짐을 완료시켜야 하며, 기온이 1~5℃일 때는 보온 덮개를 이용하여 다짐단계 후 보온처리를 실시하되 기온이 영하로 떨어지면 시공을 중단한다.The laying step is to install more than 9 to 30% of the soil improver to the weight of the target soil to be improved per 1㎡, to stir and mix with the target soil within 2 hours, when the temperature is 1 ~ 5 ℃ to cover the insulation After the compaction step, conduct heat treatment, but stop construction when the temperature drops below zero.
포설은 기계 또는 인력으로 실시하고, 포설공정시 처리대상토의 두께를 감안한 단위 면적 및 중량당 초설량을 계산하여 포설하는 것이 바람직하다.It is preferable to perform laying by machine or manpower, and to calculate and install the amount of snow per unit area and weight of snow in consideration of the thickness of the treated soil during the laying process.
상기 토양 개량제는 주재 82~84 중량%, 첨가제 7~10 중량% 및 약알칼리수 7~10 중량%로 혼합되어 이루어진다.The soil modifier is made of a mixture of 82 to 84% by weight of the main agent, 7 to 10% by weight of additives and 7 to 10% by weight of weak alkali water.
추가의 일면에 있어서,In a further aspect,
상기 다짐단계는 롤러 장비를 이용하여 실시할 수 있고, 있때 선처리로 스크리드 장치로 평탄화 한다음 롤러 장비로 다짐을 실시하되 사면의 상부에서 하방으로 실시하는 것이 바람직하다.The compacting step can be carried out by using a roller equipment, when it is flattened with a screed device by a pretreatment, and then compacted with a roller equipment, it is preferable to perform downward from the top of the slope.
이상에서 설명한 바와 같이 본 발명에 의한 사면 녹화에 식생 가능하도록 하는 토양 개량제 조성물 및 이를 이용한 사면보호 시공방법은 주재가 현지토, 부엽토, 한약재 찌꺼기 및 섬유재 등의 친환경적인 조성물로 이루어져 사면 시공 후 발생 될 수 있는 환경오염을 저감시키며, 식물 발아에 도움이 되고, 첨가제를 더하여 표층면을 형성하는 본 발명의 토양 개량제의 강도를 높여 사면 표면층 내구성이 향상되며, 약알칼리수를 이용하여 식물 생장에 도움이 되도록 pH농도를 조절하여 화학 원료에 의한 pH농도 조절을 실시하지 않으므로 친환경적이다.As described above, the soil improver composition and the slope protection construction method using the same for allowing vegetation in the slope greening according to the present invention are made after the slope construction is made of environmentally friendly compositions such as local soil, leafy soil, herbal remnants and textile materials. To reduce the environmental pollution, and to help plant germination, increase the strength of the soil improver of the present invention to form a surface layer by adding additives to improve the surface layer durability, and to help the plant growth by using weak alkaline water It is eco-friendly because it does not control the pH concentration by chemical raw materials by adjusting the pH concentration as much as possible.
이상과 같이 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었지만, 본 발명은 이것에 의해 한정되지 않으며, 본 발명이 속하는 기술은 발명의 기술 사상과 아래에 기재될 특허청구범위의 균등 범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.As mentioned above, although this invention was demonstrated by the limited embodiment and drawing, this invention is not limited by this, The technique to which this invention belongs is within the equal range of the technical idea of the invention, and a claim to be described below. Various modifications and variations are possible, of course.
Claims (10)
상기 식생 개량제 조성물은
현지토, 부엽토, 한약재 찌꺼기 및 섬유재로 이루어지는 주재;
결합재, 경화제, 분말증점제, 고흡수성 폴리머(SAP, Super Absorbent Polymer) 및 보습제로 이루어지는 첨가제; 및
pH 농도가 7.2~7.6을 이루는 약알칼리수;를 포함하여 이루어지고,
상기 경화제는 팽창형 경화제이고, 분말증점제는 몬모릴로 나이트계 벤토나이트(Sodium Bentonite)분말이며, 보습제는 폴리카본산계 고분자 액상 가소제이며,
상기 고흡수성 폴리머는 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지로 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지의 제조는 박테리아에서 생성된 미세섬유상 구조의 분말형태를 이루는 바이오 셀룰로오스와 홍조류인 식용 해초를 채취하여 건조시킨 후 분쇄된 분말을 가열된 정제수와 교반하고, 염화칼륨으로 용해한 뒤 상온에서 냉각시켜 겔상태를 생성시키고, 분쇄기에 에탄올과 함께 주입하여 분쇄하되 추가로 에탄올을 주입하여 교반하고, 탈수 및 건조하여 제조된 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물.In the vegetation modifier composition for slope greening,
The vegetation modifier composition is
A main material consisting of local soil, side leaf soil, herbal remnants and textile materials;
Additives comprising a binder, a hardener, a powder thickener, a super absorbent polymer (SAP) and a moisturizer; And
Weak alkaline water; pH concentration is 7.2 ~ 7.6;
The curing agent is an expandable curing agent, the powder thickener is montmorillonite-based bentonite powder, the moisturizing agent is a polycarboxylic acid-based polymer liquid plasticizer,
The super absorbent polymer is a super absorbent polymer composed of bio cellulose and carrageenan, and the preparation of the super absorbent polymer composed of bio cellulose and carrageenan is obtained by drying edible seaweeds, which are biocellulose and red algae, which form a powder having a microfibrous structure produced by bacteria. After the pulverized powder is stirred with heated purified water, dissolved with potassium chloride and cooled at room temperature to produce a gel state. The mixture is pulverized by injecting with ethanol in a pulverizer, and further injected by stirring with ethanol, dehydrated and dried. Soil improver composition to allow vegetation to be sloped greening.
상기 주재는 82~84 중량%, 첨가제는 7~10 중량% 및 약알칼리수 7~10 중량%로 이루어지는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물.According to claim 1,
The main material is 82 to 84% by weight, additives are 7 to 10% by weight and weak alkali water 7 to 10% by weight of the soil improver composition to enable vegetation in the slope greening.
상기 주재는 현지토 69~75 중량%, 부엽토 9~16 중량%, EM(Effective Micro-organisms)발효액으로 발효된 한약재 찌꺼기 7~13 중량% 및 야자열매 껍질, 대마 및 볏짚 섬유질 재료 중 선택된 하나 이상으로 이루어진 섬유재 1~5 중량%로 이루어지는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물.According to claim 1,
The host material is 69-75% by weight of local soil, 9-16% by weight of foliar soil, 7-13% by weight of medicinal herb residue fermented with Effective Micro-organisms (EM) fermentation solution, and at least one selected from coconut shell, hemp and rice straw fiber materials. Soil modifier composition to enable vegetation in the slope greening, characterized in that consisting of 1 to 5% by weight of the fiber material.
상기 첨가제는 결합재 39~51 중량%, 경화제 29~41 중량%, 분말증점제 3~7 중량%, 고흡수성 폴리머 1~3 중량% 및 보습제 7~13 중량%로 이루어지는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물.According to claim 1,
The additive is a vegetation for slope greening, characterized in that consisting of 39 to 51% by weight of binder, 29 to 41% by weight of hardener, 3 to 7% by weight of powder thickener, 1 to 3% by weight of superabsorbent polymer, and 7 to 13% by weight of humectant. Soil modifier compositions that make it possible.
상기 결합재는 마이크로 시멘트 33~37 중량%, 아윈계 시멘트 8~12 중량% 및 반수석고 53~57 중량%로 이루어지는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물.The method of claim 4, wherein
The binder is 33 to 37% by weight of micro cement, 8 to 12% by weight of the Ayn cement and 53-57% by weight of gypsum plaster soil improving composition to enable vegetation in the slope greening.
상기 사면보호 시공방법은
a) 시공되는 지반의 표층을 계획되는 깊이까지 깎는 땅깎기 단계;
b) 상기 땅깎기 단계에서 수득된 현지토에 부엽토, 한약재 찌꺼기 및 섬유재를 교반하여 생성된 주재와 결합재, 경화제, 분말증점제, 고흡수성 폴리머(SAP, Super Absorbent Polymer) 및 보습제로 이루어진 첨가제와 약알칼리수를 교반혼합하여 토양 개량제를 제조하는 혼합단계;
c) 상기 혼합단계에서 제조된 토양 개량제를 시공되는 지반에 포설하는 포설단계; 및
d) 상기 포설단계에서 포설된 토양 개량제와 표층면의 대상토를 5회이상 혼합하고, 다짐하는 다짐단계;로 이루어지고,
상기 경화제는 팽창형 경화제이고, 분말증점제는 몬모릴로 나이트계 벤토나이트(Sodium Bentonite)분말이며, 보습제는 폴리카본산계 고분자 액상 가소제이며,
상기 고흡수성 폴리머는 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지로 바이오 셀룰로오스와 카라기난으로 이루어진 고흡수성 수지의 제조는 박테리아에서 생성된 미세섬유상 구조의 분말형태를 이루는 바이오 셀룰로오스와 홍조류인 식용 해초를 채취하여 건조시킨 후 분쇄된 분말을 가열된 정제수와 교반하고, 염화칼륨으로 용해한 뒤 상온에서 냉각시켜 겔상태를 생성시키고, 분쇄기에 에탄올과 함께 주입하여 분쇄하되 추가로 에탄올을 주입하여 교반하고, 탈수 및 건조하여 제조된 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법.In the slope protection construction method using a soil improver composition to allow vegetation for slope greening,
The slope protection construction method
a) pruning, cutting the surface of the ground under construction to the planned depth;
b) additives and medicines composed of a main material, a binder, a hardener, a powder thickener, a super absorbent polymer (SAP), and a moisturizer, produced by stirring the subleaf soil, herbal remnants and textiles on the local soil obtained in the grounding step; Mixing and mixing alkaline water to prepare a soil improving agent;
c) laying step of laying the soil improver prepared in the mixing step on the ground to be constructed; And
d) a compaction step of mixing and compacting at least five times the soil improver and the target soil of the surface layer laid in the laying step;
The curing agent is an expandable curing agent, the powder thickener is montmorillonite-based bentonite powder, the moisturizing agent is a polycarboxylic acid-based polymer liquid plasticizer,
The super absorbent polymer is a super absorbent polymer composed of bio cellulose and carrageenan, and the preparation of the super absorbent polymer composed of bio cellulose and carrageenan is obtained by drying edible seaweeds, which are biocellulose and red algae, which form a powder having a microfibrous structure produced by bacteria. After the pulverized powder is stirred with heated purified water, dissolved with potassium chloride and cooled at room temperature to form a gel state. The mixture is pulverized by injecting with ethanol in a pulverizer. Slope protection construction method using a soil improver composition to allow vegetation to be sloped green.
상기 땅깎기 단계는 표면유실 및 세굴로 인한 교란층 이상까지 실시되되 시공 위치에 유수가 있거나 지하수위가 높을 경우 가배수를 위한 트랜치를 설치하여 유수의 유입을 방지하고, 표면층의 수분을 제거하는 공정을 더하는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법.The method of claim 7, wherein
The grounding step is carried out up to the disturbance layer due to surface loss and scour, but when the water flows in the construction location or the groundwater level is high, install a trench for drainage drainage to prevent the inflow of the flow of water, and remove the water of the surface layer Slope protection construction method using a soil modifier composition to enable vegetation in the slope greening, characterized in that the addition.
상기 포설 단계는 1㎡ 당 개량될 대상토의 중량대비 토양 개량제를 9~30% 이상 포설하고, 2시간 안에 대상토와 혼합교반하고 다짐을 완료시켜야 하며, 기온이 1~5℃일 때는 보온 덮개를 이용하여 다짐단계 후 보온처리를 실시하되 기온이 영하로 떨어지면 시공을 중단하는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물을 이용한 사면보호 시공방법.The method of claim 7, wherein
The laying step is to install more than 9 to 30% of the soil improver to the weight of the target soil to be improved per 1㎡, stir the mixture and compaction with the target soil within 2 hours, when the temperature is 1 ~ 5 ℃ Slope protection construction method using a soil modifier composition to allow vegetation in the slope greening, characterized in that to perform a thermal treatment after the compaction step, but stops construction when the temperature drops below zero.
상기 토양 개량제는 주재 82~84 중량%, 첨가제 7~10 중량% 및 약알칼리수 7~10 중량%로 혼합되어 이루어지는 것을 특징으로 하는 사면 녹화에 식생 가능 하도록 하는 토양 개량제 조성물을 이용한 사면호보 시공방법.
The method of claim 7, wherein
The soil improver construction method using the soil improver composition to allow vegetation in the slope greening, characterized in that the mixture is made of 82 ~ 84% by weight, additives 7 ~ 10% by weight and weak alkaline water 7 ~ 10% by weight.