KR101963234B1 - Contact lens consisting of hydroxyethylmethacrylate and sorbitol solution polymer coating and the method of manuacturing the same - Google Patents

Contact lens consisting of hydroxyethylmethacrylate and sorbitol solution polymer coating and the method of manuacturing the same Download PDF

Info

Publication number
KR101963234B1
KR101963234B1 KR1020170144463A KR20170144463A KR101963234B1 KR 101963234 B1 KR101963234 B1 KR 101963234B1 KR 1020170144463 A KR1020170144463 A KR 1020170144463A KR 20170144463 A KR20170144463 A KR 20170144463A KR 101963234 B1 KR101963234 B1 KR 101963234B1
Authority
KR
South Korea
Prior art keywords
sorbitol
contact lens
hydroxyethyl methacrylate
hema
lens
Prior art date
Application number
KR1020170144463A
Other languages
Korean (ko)
Inventor
박화성
Original Assignee
(주)지오메디칼
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)지오메디칼 filed Critical (주)지오메디칼
Priority to KR1020170144463A priority Critical patent/KR101963234B1/en
Application granted granted Critical
Publication of KR101963234B1 publication Critical patent/KR101963234B1/en

Abstract

The present invention relates to a contact lens coated with a hydroxyethyl methacrylate and a sorbitol solution polymer and a method for preparing the contact lens. More particularly, as sorbitol surface coating (SSC) technique, the surface of a contact lens is coated with a polymer prepared by combining hydrophilic 2-hydroxyethyl methacrylate (HEMA) and wettable sorbitol in a contact lens manufacturing step for coating layer formation or a printing layer is formed by mixing with printing ink. As a result, a moisture layer that does not dry is formed, contact lens dehydration is prevented, and a comfortable wearing feeling is provided for at least 12 hours.

Description

하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈 및 그 제조방법{Contact lens consisting of hydroxyethylmethacrylate and sorbitol solution polymer coating and the method of manuacturing the same}TECHNICAL FIELD The present invention relates to a contact lens coated with hydroxyethyl methacrylate and a sorbitol solution polymer and a method of manufacturing the contact lens,

본 발명은 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈 및 그 제조방법에 관한 것으로서, 더욱 상세하게는 솔비톨 표면코팅(Sorbitol Surface Coating ; SSC) 기술로서, 콘택트렌즈 제조단계에서 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate)와 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 콘택트렌즈 표면에 코팅하여 코팅층을 형성하거나, 인쇄잉크에 혼합하여 인쇄층을 형성하여 마르지 않는 수분층을 형성함으로써 콘택트렌즈의 탈수가 방지되고 12시간 이상 편안하고 촉촉한 착용감을 제공하기 위한 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈 및 그 제조방법에 관한 것이다.The present invention relates to a contact lens coated with a hydroxyethyl methacrylate and a sorbitol solution polymer and a process for preparing the contact lens. More particularly, the present invention relates to a sorbitol surface coating (SSC) A polymer prepared by combining 2-hydroxyethyl methacrylate (HEMA) and sorbitol (wettable) in solution is coated on the surface of a contact lens to form a coating layer, or a printing layer is formed by mixing with a printing ink The present invention relates to a contact lens coated with a hydroxyethyl methacrylate and a sorbitol solution polymer for preventing contact lens dehydration by forming a non-dried water layer and providing a comfortable and moist feeling for more than 12 hours, and a method for producing the same.

일반적으로 콘택트렌즈(Contact lens)는 생활에 다소 불편함이 있는 안경을 대신하여 눈의 각막에 직접 접촉시켜 사용하는 크기가 작은 렌즈로서, 그 용도에 따라 눈의 보호, 각막의 굽은 정도를 변경, 망막의 치료 등을 목적으로 하는 치료용 렌즈, 근시, 난시, 원시 등을 보정 하기 위한 시력보정용 렌즈, 미용용 렌즈로 분류할 수 있다.In general, a contact lens is a small-sized lens that is used in direct contact with the cornea of the eye instead of glasses which are somewhat inconvenient for life. It is used for protecting the eyes, changing the degree of bending of the cornea, A therapeutic lens for the purpose of treating the retina, a lens for correcting the visual acuity for correcting nearsightedness, astigmatism, and the like, and a cosmetic lens.

이러한 콘택트렌즈는 안구에 직접 접촉함으로써, 눈의 안전과 효능을 유지하는 동시에 콘택트렌즈의 투명성과 표면 습윤성을 유지해야 하고, 각안구의 각막을 향해 산소를 잘 투과하여야 한다.Such contact lenses must maintain contact lens transparency and surface wettability while maintaining eye safety and efficacy by direct contact with the eyeball, and should transmit oxygen well to the cornea of each eye.

즉, 콘택트렌즈는 안구 및 각막을 보호함과 동시에 눈물 층의 흐름이 원활해야 하고, 눈꺼풀과 눈 표면과의 과다한 마찰도 피해야 하는 임상학적인 측면도 고려하여 설계되어야 하며, 기계적 강도(tensile strength), 생체적합성(biocompatibility), 무독성(non toxicity),광학적 투명도(optical transparent), 굴절율(refractive index), 표면친수성(surface wetability), 각막에 적합한 함수율(water content), 팽윤비(welling rate), 산소투과성(oxygen permeability) 등의 조건들을 충족시켜야 한다.In other words, the contact lens should be designed in consideration of the clinical aspects in which the eyeball and the cornea should be protected and the flow of the tear layer should be smooth and the excessive friction between the eyelid and the eye surface should be avoided, and the tensile strength, It is well known that biocompatibility, non toxicity, optical transparency, refractive index, surface wetability, water content suitable for the cornea, welling rate, oxygen permeability).

상기와 같은 콘택트렌즈는 재료에 따라 크게 하드(hard) 콘택트렌즈와 소프트(soft) 콘택트렌즈로 나눌 수 있으며, 기능에 따라 시력교정용, 치료용, 미용 콘택트렌즈 등으로 분류되며, 최근에는 하이드로겔 소프트 콘택트렌즈가 대부분 현대인들의 시력교정 및 치료 등의 목적으로 사용되고 있다.The contact lens may be divided into a hard contact lens and a soft contact lens depending on the material. The contact lens is categorized into a contact lens for vision correction, a treatment, and a cosmetic contact lens according to functions. In recent years, Soft contact lenses are used mostly for modern vision correction and treatment.

하드 콘택트렌즈는 시력교정이 우수하며 산소투과성이 매우 높고 수명이 길며 세척이 쉬우며 눈에 삽입, 제거도 쉽지만 적응기간이 오래 걸려 적응에 실패하는 경우도 많으며 착용감이 다소 떨어진다. Hard contact lenses are excellent in vision correction, have high oxygen permeability, have a long life, are easy to clean, easy to insert and remove in the eyes, but often take a long time to adapt and fail to adapt, and feel less comfortable.

소프트 콘택트렌즈의 경우 렌즈가 파손되거나 찢어지기 쉽기만 적응기간이 짧고 착용감이 좋으며 각막손상의 발생빈도 또한 낮다. 무엇보다 소프트 콘택트렌즈의 크기와 유연성 때문에 각막과 밀착되어 있어 먼지 등과 같은 이물질들이 렌즈와 각막 사이로 잘들어가지 않아 편안하게 사용할 수 있다.In soft contact lenses, the lens is easy to break or tear, but it has a short adaptation period, good fit, and the incidence of corneal damage is also low. Above all, because of the size and flexibility of the soft contact lens, it is in close contact with the cornea, so that foreign substances such as dust can not enter the lens and the cornea.

하이드로겔 콘택트렌즈는 높은 친수성으로 편안한 착용감 때문에 많은 사람들이 선호하고 있지만, 낮은 산소투과율에 의한 저산소증(각막 부종), 렌즈 표면에 부착된 누액성분들로 인한 렌즈표면의 습윤성 저하와 같은 문제점이 있으므로 하이드로겔 콘택트렌즈는 우수한 착용감은 물론, 높은 산소투과율 및 습윤성 등이 요구되었다.Although hydrogel contact lenses are preferred by many people because of their high hydrophilicity and comfortable fit, there are problems such as hypoxia (corneal edema) due to low oxygen permeability (corneal edema) and wettability of the lens surface due to leakage components attached to the lens surface, Gel contact lenses were required to have excellent fit, high oxygen permeability and wettability.

이에 높은 산소투과율을 위해 개발된 실리콘 하이드로겔 콘택트렌즈를 착용하게 되면, 눈에 충분한 산소가 공급되어 저산소증에 의한 각막 부종이라는 부작용이 없게 되지만, 소수성으로 인해 렌즈 표면의 친수성은 감소하게 되므로 착용자에게 불편함을 주고 눈자극, 각막 착색, 각막에 대한 렌즈의 부착 등의 문제가 발생하였다.If a silicone hydrogel contact lens developed for high oxygen permeability is worn, sufficient oxygen is supplied to the eye, and there is no adverse effect of corneal edema due to hypoxia. However, since the hydrophilic property of the lens surface is reduced due to hydrophobicity, And problems such as eye irritation, corneal staining, lens attachment to the cornea, and the like have occurred.

이러한 단점을 극복하기 위하여, 한국등록특허 제10-0594414호(특허문헌 0001)에 따르면 초기 제1세대 실리콘 하이드로겔 콘택트렌즈 제품들은 렌즈 표면을 플라즈마 표면 처리하여 친수성을 증가시키는 방법을 사용하였으나, 이는 여전히 표면의 습윤성이 낮아 사용자의 불편이 있어 왔으며, 제조공정상에 플라즈마 표면처리라는 복잡한 공정이 추가되어 생산원가의 상승을 야기하였다.In order to overcome these disadvantages, according to Korean Patent No. 10-0594414 (Patent Document 0001), early first generation silicone hydrogel contact lens products use plasma surface treatment of lens surface to increase hydrophilicity, The wettability of the surface is still low and the user is inconvenienced, and a complicated process such as plasma surface treatment is added to the top of the manufacturing process, resulting in an increase in the production cost.

또한, 제2세대 실리콘 하이드로겔 콘택트렌즈로서, 한국등록특허 제10-0748379호(특허문헌 0002)에는 내부습윤제(internal wetting agent) 성분으로서 폴리비닐 피롤리돈(PVP ; polyvinyl pyrrolidone) 고분자를 사용하여, 습윤성과 함수율을 증가시키고, 플라즈마 후처리 공정이 필요 없이 실리콘 하이드로겔 렌즈를 만들 수 있는 기술이 공지되었으나, 이는 내부습윤제(PVP)가 렌즈 밖으로 서서히 빠져나오면서 점차 착용감이 나빠지므로, 이 또한 렌즈 착용시의 불편함(discomfort)이 여전히 존재하였다.As a second-generation silicone hydrogel contact lens, Korean Patent No. 10-0748379 (Patent Document 0002) discloses a method of using a polyvinyl pyrrolidone (PVP) polymer as an internal wetting agent component , A technique capable of increasing the wettability and water content and making a silicone hydrogel lens without the need for a post-plasma treatment process has been known. However, since the inner wetting agent (PVP) gradually slips out of the lens, The discomfort of poetry still existed.

제3세대 실리콘 하이드로겔 콘택트렌즈로서, 한국공개특허 제10-2007-0067679호(특허문헌 0003)에는 원료자체에 친수성을 부여한 실리콘 거대단량체(macromer)를 합성하여 콘택트렌즈를 제조하는 기술이 공지되었으나, 이는 원료에 대한 고도의 분자설계 및 합성기술이 필요하고, 원료의 제조방법이 복잡하며 여러 단계의 공정이 요구되어 최종제품에 원료제조시의 자극성의 잔류물질이 남는 문제점이 있었다.As a third-generation silicone hydrogel contact lens, Korean Patent Laid-Open No. 10-2007-0067679 (Patent Document 0003) discloses a technique for manufacturing a contact lens by synthesizing a macromer having hydrophilicity imparted to a raw material itself , Which requires a high degree of molecular design and synthesis technology for the raw materials, a complicated manufacturing method of the raw materials, and a need for several stages of processing, and there is a problem that the residual material remains irritating when the raw material is produced in the final product.

한편, 컬러 콘택트렌즈는 색소 결핍증, 홍채 외상 등과 같은 비정상적인 눈의 외관을 정상적인 상태로 보이게 하는데 사용되는 의료용구였으나, 삶의 질이 높아지면서 외모에 대한 관심이 늘어나고, 많은 연예인이 더욱 아름다운 눈을 표현하기 위해 가시 홍채가 크게 보이고 또렷하게 보이게 하는 미용 컬러 콘택트렌즈를 착용하고 활동함에 따라 사람들의 관심도가 기하급수적으로 높아졌고, 특히 미용 컬러 콘택트렌즈는 10대~20대들 사이에서 유행이 되어 판매량이 급격히 늘고 있다.Color contact lenses, on the other hand, were medical devices used to make the appearance of abnormal eyes such as pigment deficiency and iris trauma normal. However, as the quality of life increased, interest in the appearance increased, and many entertainers expressed more beautiful eyes In addition, the beauty contact lenses have become popular among teenagers and teenagers in the 20s, and their sales volume has increased rapidly. have.

이러한 컬러 콘택트렌즈는 눈에 무리를 주지 않으며 홍채에 맞아야 하고 편안하게 사용할 수 있도록 컬러 인쇄층이 어떻게 구성되느냐 하는 것은 매우 중요하게 되었다.It is very important to know how these color contact lenses are constructed so that they do not damage the eyes, are fit to the iris, and are comfortable to use.

그러나 상기한 컬러 콘택트렌즈는 렌즈 착용 후 눈을 깜박거릴 때마다 렌즈와 눈꺼풀이 마찰 되어 직접적으로 인쇄층이 눈에 닿아 각막에 염증 등을 유발하며 시간경과에 따라 콘택트렌즈 표면에 부착되어 있는 인쇄층으로 인해 부착력의 감소로 인쇄층이 떨어지는 등의 문제점이 있었을 뿐만 아니라, 착색된 인쇄층은 콘택트렌즈 재질보다 함수율이 떨어져 컬러 콘택트렌즈를 사용하였을 때 오랜 시간 사용하지 못하는 문제점이 있었다.However, in the color contact lens described above, the lens and the eyelid are rubbed each time the eye is blinked after wearing the lens, so that the print layer directly contacts the eye, causing irritation or the like to the cornea, There is a problem that the printing layer is dropped due to the decrease of the adhesive force, and in addition, the color printed layer has a water content lower than that of the contact lens material, so that the color contact lens can not be used for a long time when the color contact lens is used.

이에 따라 본 발명자들은 종래의 소프트 콘택트렌즈, 실리콘 하이드로겔 콘택트렌즈 및 컬러 콘택트렌즈의 친수성 및 함수성을 증가시키기 위하여 노력한 결과, 솔비톨 표면코팅(Sorbitol Surface Coating ; SSC) 기술로서 콘택트렌즈 제조단계에서 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate)와 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 콘택트렌즈에 코팅하여 코팅층을 형성하거나, 인쇄잉크에 혼합하여 인쇄층을 형성하면 친수성, 습윤성, 함수율이 우수한 것을 확인하고 본 발명을 완성하게 되었다.Accordingly, the present inventors have made efforts to increase the hydrophilicity and water-solubility of conventional soft contact lenses, silicone hydrogel contact lenses and color contact lenses, and as a result, they have found that, as a sorbitol surface coating (SSC) A polymer prepared by combining 2-hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) in solution is coated on a contact lens to form a coating layer, or a printing layer is formed by mixing with a printing ink Hydrophilicity, wettability, and water content, thereby completing the present invention.

한국등록특허 제10-0594414호Korea Patent No. 10-0594414 한국등록특허 제10-0748379호Korean Patent No. 10-0748379 한국공개특허 제10-2007-0067679호Korean Patent Publication No. 10-2007-0067679

본 발명은 상기한 문제점을 해결하기 위하여 솔비톨 표면코팅(Sorbitol Surface Coating ; SSC) 기술로서, 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate)와 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 콘택트렌즈에 코팅하여 코팅층을 형성하거나, 인쇄잉크에 혼합하여 인쇄층을 형성하여 마르지 않는 수분층을 형성함으로써 콘택트렌즈의 탈수가 방지되고 12시간 이상 편안하고 촉촉한 착용감을 제공하기 위한 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈 및 그 제조방법을 제공하는 것을 해결하고자 하는 과제로 한다.In order to solve the above-mentioned problems, the present invention has been made to solve the above-mentioned problems by solubilizing hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) as a sorbitol surface coating (SSC) The polymer thus prepared is coated on a contact lens to form a coating layer, or a printing layer is formed by mixing with a printing ink to form a non-drying water layer, thereby preventing dehydration of the contact lens and providing a comfortable and moist feeling for 12 hours or more. Ethyl methacrylate and sorbitol solution coated with a polymer and a process for producing the same.

본 발명은 상기 과제를 해결하기 위하여, 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체로 형성되는 렌즈성형층;과 상기 렌즈성형층이 각막과 접촉되는 내측면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하여 형성된 코팅층;을 포함하여 구성되는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈를 과제의 해결수단으로 한다.In order to solve the above-described problems, the present invention provides a lens comprising: a lens molding layer formed of a hydrophilic hydroxyethyl methacrylate (HEMA) polymer; and a hydrophilic hydro- A hydroxyethyl methacrylate and a sorbitol solution comprising a coating layer formed by coating a polymer prepared by combining hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) .

상기 렌즈성형층과 상기 코팅층 사이에는 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄한 인쇄층;이 형성되는 것을 과제의 해결수단으로 한다.A printed layer printed with an ink containing a polymer prepared by adding a solution of hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) solution between the lens forming layer and the coating layer; As a solution.

또한, 본 발명은 콘택트렌즈 제조용 숫몰드 표면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하고 경화하여 코팅층을 형성하는 단계;와 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체가 채워진 암몰드에 상기 코팅층이 형성된 숫몰드를 결합하여 경화하고 암몰드를 분리하여 렌즈성형층을 형성하는 단계;를 포함하여 구성되는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈의 제조방법을 과제의 해결수단으로 한다.The present invention also relates to a method for producing a contact lens, comprising the steps of coating a polymer prepared by adding a hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol to a surface of a male mold for preparing a contact lens, and curing the polymer to form a coating layer, A step of bonding a male mold having the coating layer formed thereon to an arm mold filled with 2-hydroxyethyl methacrylate (HEMA) polymer to cure the lens mold and separating the lens mold to form a lens molding layer Hydroxyethyl methacrylate, and sorbitol solution polymer coated on the surface of the contact lens.

상기 코팅층을 형성하는 단계 후에 상기 코팅층 위에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄하고 경화하여 인쇄층을 형성하는 단계를 더 포함하여 구성되는 것을 과제의 해결수단으로 한다.And printing and curing the printed layer with an ink including a polymer prepared by adding a solution of hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) onto the coating layer after the step of forming the coating layer As a solution to the problem.

본 발명의 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체로 표면코팅된 콘택트렌즈는 하이드록시에틸메타크릴레이트(HEMA)와 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 콘택트렌즈 표면에 코팅하여 코팅층을 형성하거나, 인쇄잉크에 혼합하여 인쇄층을 형성하여 마르지 않는 수분층을 형성함으로써 콘택트렌즈의 탈수가 방지되고 12시간 이상 편안하고 촉촉한 착용감을 제공할 수 있는 우수한 효과가 있다.The contact lens coated with the hydroxyethyl methacrylate and sorbitol solution polymer of the present invention is obtained by coating a polymer prepared by solution-combining hydroxyethyl methacrylate (HEMA) and wettable sorbitol on the surface of a contact lens There is an advantageous effect that dehydration of the contact lens is prevented by forming a coating layer or a printed layer by mixing with printing ink to form a non-dried water layer, and a comfortable and moist feeling can be provided for 12 hours or more.

도 1은 본 발명의 일실시예에 따른 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈를 나타내는 분해사시도
도 2는 본 발명의 또 다른 실시예에 따른 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈를 나타내는 분해사시도1 is an exploded perspective view showing a contact lens coated with a hydroxyethyl methacrylate and sorbitol solution polymer according to an embodiment of the present invention;
2 is an exploded perspective view showing a contact lens coated with a hydroxyethyl methacrylate and sorbitol solution polymer according to another embodiment of the present invention

본 발명은, 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체로 형성되는 렌즈성형층;과 상기 렌즈성형층이 각막과 접촉되는 내측면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하여 형성된 코팅층;을 포함하여 구성되는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈를 기술구성의 특징으로 한다.The present invention relates to a lens molding comprising a lens molding layer formed of a hydrophilic hydroxyethyl methacrylate (HEMA) polymer and a hydrophilic hydroxyethyl methacrylate (hereinafter referred to as " hydroxyethyl methacrylate " HEMA) and a wettable Sorbitol. The contact lens is coated with a hydroxyethyl methacrylate solution and a sorbitol solution polymer.

상기 렌즈성형층과 상기 코팅층 사이에는 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄한 인쇄층;이 형성되는 것을 기술구성의 특징으로 한다.And a printing layer printed with an ink containing a polymer prepared by adding a hydrophilic hydroxyethyl methacrylate (HEMA) and a wetting sorbitol (Sorbitol) solution between the lens forming layer and the coating layer. .

또한, 본 발명은 콘택트렌즈 제조용 숫몰드 표면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하고 경화하여 코팅층을 형성하는 단계;와 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체가 채워진 암몰드에 상기 코팅층이 형성된 숫몰드를 결합하여 경화하고 암몰드를 분리하여 렌즈성형층을 형성하는 단계;를 포함하여 구성되는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈의 제조방법을 기술구성의 특징으로 한다.The present invention also relates to a method for producing a contact lens, comprising the steps of coating a polymer prepared by adding a hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol to a surface of a male mold for preparing a contact lens, and curing the polymer to form a coating layer, A step of bonding a male mold having the coating layer formed thereon to an arm mold filled with 2-hydroxyethyl methacrylate (HEMA) polymer to cure the lens mold and separating the lens mold to form a lens molding layer Hydroxyethyl methacrylate, and sorbitol solution polymer coated on the surface of the contact lens.

상기 코팅층을 형성하는 단계 후에 상기 코팅층 위에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄하고 경화하여 인쇄층을 형성하는 단계를 더 포함하여 구성되는 것을 기술구성의 특징으로 한다.And printing and curing the printed layer with an ink including a polymer prepared by adding a solution of hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) onto the coating layer after the step of forming the coating layer And a control unit for controlling the operation of the control unit.

이하에서는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 도면을 통하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구형될 수 있으며, 여기에서 설명하는 도면에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. However, the present invention can be spherical in various different forms, and is not limited to the drawings described here.

먼저, 본 발명의 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈는 [도 1]에 도시한 바와 같이, 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체로 형성되는 렌즈성형층(20);과 상기 렌즈성형층이 각막과 접촉되는 내측면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하여 형성된 코팅층(10);을 포함하여 구성된다.First, the contact lens coated with the hydroxyethyl methacrylate and sorbitol solution polymer of the present invention is formed of a hydrophilic hydroxyethyl methacrylate (HEMA) polymer as shown in FIG. 1 (HEMA) and wettable sorbitol (Sorbitol) are coated on the inner surface of the lens forming layer in contact with the cornea to form a lens molding layer And a coating layer (10).

상기 코팅층(10)은 시력교정용 또는 치료용의 경우에는 투명하게 형성하여야 함은 물론이다.It is needless to say that the coating layer 10 should be formed transparent for vision correction or treatment.

상기 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체로 형성되는 렌즈성형층(20)은 렌즈 본체를 형성하는 것으로 인체에 무해한 재질이며 친수성이며 재질 자체가 부드럽고 함수성이 높고 산소투과성이 매우 높아 각막에 무리를 주지 않고 각막을 보호하는 재질로서 통상적으로 사용하고 있다.The lens molding layer 20 formed of the hydrophilic hydroxyethyl methacrylate (HEMA) polymer forms a lens body, which is harmless to the human body and is hydrophilic. The material itself is soft and highly water-soluble. And is widely used as a material for protecting the cornea without giving too much to the cornea.

즉, 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체는 다음 화학구조식으로 표시되며, 친수성기인 -OH기가 말단에 터미네이트 되어 있어 함수율이 높은 성질을 가진다.That is, the 2-hydroxyethyl methacrylate (HEMA) polymer is represented by the following chemical structural formula, and the -OH group, which is a hydrophilic group, is terminated at the terminal and has a high water content.

Figure 112017108283475-pat00001
Figure 112017108283475-pat00001

상기 렌즈성형층이 각막과 접촉되는 내측면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하여 형성된 코팅층(10)은 콘택트렌즈의 가장 안쪽에 위치하며 안구에 직접적으로 닿아 사용하는 부분이기 때문에 눈에 자극을 주지 않는 재질로서, 습윤성 재질이다.The coating layer 10 formed by coating a hydrophilic hydroxyethyl methacrylate (HEMA) and a wettable sorbitol solution on the inner surface of the lens forming layer in contact with the cornea, It is a material that does not irritate the eyes because it is a part that is used inside when it touches directly to the eyeball, and it is a wettable material.

즉, 상기 솔비톨(Sorbitol)은 백색의 분말로 청량한 단맛이 있으며, 일반적으로 약 70%의 수용액으로서 시판되고 있다. 솔비톨은 분자량이 182.18이며 포도당을 고압첨가, 환원시켜 얻어진다. 6개의 수산기(-OH)를 가진 당알코올로서 D-sorbitol 또는 D-glucitol이라고도 불리어지는데, 자연계에 광범위하게 존재하며 특히 과실류(1∼2%), 해조류(13%)에 다량 함유되어 있다. 솔비톨은 프랑스의 화학자 Jean-Baptiste Boussingault가 1872년 산딸기, 마가목의 열매로부터 추출하여 결정을 얻은 것이 최초이고, 그 어원은 마가목의 Sorbus Aucuparia에서 유래 되었다. 백색 무취의 투명한 용액으로서 청량감과 감미도가 있고 순수한 솔비톨은 물에 매우 잘 용해되고 온도가 올라감에 따라 증가한다. That is, the sorbitol is a white powder and has a refreshing sweet taste, and is generally commercially available as an aqueous solution of about 70%. Sorbitol has a molecular weight of 182.18 and is obtained by adding glucose at high pressure and reducing it. D-sorbitol or D-glucitol is a sugar alcohol with six hydroxyl groups (-OH). It is widely found in nature, especially in fruits (1-2%) and seaweed (13%). Sorbitol was first discovered by French chemist Jean-Baptiste Boussingault in 1872, extracted from the fruit of the raspberry, Raspberry, and its origin was derived from Sorbus Aucuparia, White, odorless, clear solution with refreshing feel and sweetness. Pure sorbitol dissolves very well in water and increases with increasing temperature.

또한, 솔비톨은 수분을 강하게 흡수하는 성질이 있으므로 습윤조정제 또는 보습제 이외에 가소제, 유연제 그리고 광택제로서도 작용하며 타첨가물보다 흡습속도가 느려 제품에 대해 비교적 수분의 흡수와 발산에 큰 영향을 주지 않아 제품의 신선도와 유연성을 유지하고, 건조, 균열, 중량손실을 방지하여 품질 및 저장성을 향상시켜 준다. 그외 단백질 변성방지 효과(protein protection effect), 킬레이트 효과(chelate effect), 효소와 곰팡이의 성장에 대한 세균발육 저지력을 가지고 있어 세균발육 저지력은 다른 분야의 용도에 사용될 수 있다.In addition, since sorbitol has a property of absorbing moisture strongly, it acts as a plasticizer, a softener and a brightener in addition to a wetting agent or a moisturizer, and has a slow moisture absorption rate than other additives, And flexibility, and prevents drying, cracking and weight loss, improving quality and storage. In addition to its protein protection effect, chelate effect, and bacterial growth inhibition on growth of enzymes and fungi, bacterial growth inhibition can be used in other applications.

아울러, 솔비톨은 다음 화학구조식으로 표시되며, 친수성기인 -OH기가 주쇄에 다량 존재하므로 상기 하이드록시에틸메타크릴레이트(HEMA)와 용액중합체를 형성하여 상기 하이드록시에틸메타크릴레이트(HEMA)의 친수성기를 크가 증가시켜 함수율을 증가시킨다.In addition, sorbitol is represented by the following chemical structural formula. Since a -OH group as a hydrophilic group exists in a large amount in the main chain, sorbitol forms a solution polymer with the hydroxyethyl methacrylate (HEMA), and the hydrophilic group of the hydroxyethyl methacrylate (HEMA) Increases the moisture content.

Figure 112017108283475-pat00002
Figure 112017108283475-pat00002

따라서, 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 상기 렌즈성형층이 각막과 접촉되는 내측면에 코팅하여 코팅층(10)을 형성하게 되면 마르지 않는 수분층을 형성해 이로 인한 렌즈의 탈수가 방지되고 12시간 이상 촉촉한 착용감을 제공할 수 있게 된다.Therefore, when a polymer prepared by combining hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol in solution is coated on the inner surface of the lens forming layer in contact with the cornea to form the coating layer 10 It is possible to prevent the dehydration of the lens due to the formation of the non-dried water layer and to provide a feeling of comfort that is moist for 12 hours or more.

본 발명의 또 다른 실시예로서, 컬러 콘택트렌즈의 경우에는 [도 2]에 도시한 바와 같이, 상기 렌즈성형층(20)과 상기 코팅층(10) 사이에는 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄한 인쇄층(30);이 더 형성될 수 있다.As another embodiment of the present invention, in the case of a color contact lens, hydrophilic hydroxyethyl methacrylate (HEMA) is added between the lens forming layer 20 and the coating layer 10, And a printing layer 30 printed with an ink containing a polymer prepared by wet-blending sorbitol (Sorbitol).

상기 인쇄층(30)은 상기 코팅층(10)의 상측 표면에 인쇄하며, 사용자가 원하는 색상을 고를 수 있도록 다양한 색상으로 인쇄할 수 있으며 인쇄시 사용되는 염료는 염료 중에서도 색상이 선명하고 장시간 사용해도 색상이 변하지 않도록 세탁에 견딜 수 있어야 하며 빛에도 강한 반응성 염료(Reactive dyes)를 사용하는 것이 바람직하다.The printing layer 30 is printed on the upper surface of the coating layer 10 and can be printed in various colors so that the user can select a desired color. The dyes used in the printing are color in the dye, It is preferable to use reactive dyes which are resistant to washing and resistant to light.

다음으로 상기와 같이 구성되는 본 발명에 따른 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈를 제조하기 위한 개략적인 제조방법을 설명한다.Next, a schematic manufacturing method for manufacturing a contact lens coated with hydroxyethyl methacrylate and sorbitol solution polymer according to the present invention will be described.

먼저, 본 발명의 일 실시예에 따른 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈의 제조방법은 콘택트렌즈 제조용 숫몰드 표면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하고 경화하여 코팅층(10)을 형성하는 단계;와 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체가 채워진 암몰드에 상기 코팅층이 형성된 숫몰드를 결합하여 경화하고 암몰드를 분리하여 렌즈성형층(20)을 형성하는 단계;를 포함하여 구성된다.First, a method for producing a contact lens coated with a hydroxyethyl methacrylate and a sorbitol solution polymer according to an embodiment of the present invention is characterized in that a hydrophilic hydroxyethyl methacrylate (HEMA) and a wettable Coating and polymerizing a polymer prepared by adding sorbitol to the coating layer 10 to form a coating layer 10 and a coating layer 10 having a hydrophilic hydroxyethyl methacrylate (HEMA) Bonding the formed male molds to each other, curing the resin molds, and separating the molds to form the lens molding layer 20. [

이때, 선택적으로 컬러 콘택트렌즈를 제조하기 위하여는 상기 코팅층(10)을 형성하는 단계 후에 상기 코팅층 위에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄하고 경화하여 인쇄층(30)을 형성하는 단계를 더 포함하여 구성될 수 있다.At this time, in order to selectively manufacture a color contact lens, a polymer prepared by adding hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol (Sorbitol) onto the coating layer after the step of forming the coating layer 10 And forming the print layer 30 by printing and curing the ink with the ink.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위 내에서 다양한 수정, 변경 및 치환이 가능할 것이다. 따라서, 본 발명에 개시된 도면은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호범위는 아래의 청구 범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리 범위에 포함되는 것으로 해석되어야 할 것이다.It will be apparent to those skilled in the art that various modifications, substitutions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. will be. Therefore, the drawings disclosed in the present invention are intended to illustrate rather than limit the technical spirit of the present invention, and the scope of the technical idea of the present invention is not limited by these drawings. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.

10 : 코팅층 20 : 렌즈성형층 30 : 인쇄층10: coating layer 20: lens forming layer 30: printing layer

Claims (4)

친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체로 형성되는 렌즈성형층;과 상기 렌즈성형층이 각막과 접촉되는 내측면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하여 형성된 코팅층;과 상기 렌즈성형층과 상기 코팅층 사이에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄한 인쇄층;을 포함하여 구성되는 것을 특징으로 하는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈
A lens molding layer formed of a hydrophilic hydroxyethyl methacrylate (HEMA) polymer; and a hydrophilic hydroxyethyl methacrylate (HEMA) and a wettability A hydrophilic hydroxyethyl methacrylate (HEMA) and a wettable sorbitol are added between the lens forming layer and the coating layer in a solution, and a solution of the hydrophilic hydroxyethyl methacrylate (HEMA) and the wetting sorbitol And a printing layer printed with an ink containing the polymer produced. The hydroxyethyl methacrylate and sorbitol solution are contact lens coated polymers
삭제delete 콘택트렌즈 제조용 숫몰드 표면에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 코팅하고 경화하여 코팅층을 형성하는 단계;와 상기 코팅층 위에 친수성인 하이드록시에틸메타크릴레이트(HEMA) 및 습윤성인 솔비톨(Sorbitol)을 용액중합하여 제조한 중합체를 포함하는 잉크로 인쇄하고 경화하여 인쇄층을 형성하는 단계;와 친수성인 하이드록시에틸메타크릴레이트(HEMA ; 2-hydroxyethyl methacrylate) 중합체가 채워진 암몰드에 상기 코팅층이 형성된 숫몰드를 결합하여 경화하고 암몰드를 분리하여 렌즈성형층을 형성하는 단계;를 포함하여 구성되는 것을 특징으로 하는 하이드록시에틸메타크릴레이트 및 솔비톨 용액중합체가 코팅된 콘택트렌즈의 제조방법A method for producing a contact lens, comprising the steps of: coating a surface of a male mold with a hydrophilic hydroxyethyl methacrylate (HEMA) and wettable sorbitol to form a coating layer; (HEMA) and hydrophilic (Sorbitol) in an ink containing a polymer prepared by solution polymerization and curing to form a print layer, and a hydrophilic hydroxy ethyl methacrylate (HEMA; 2-hydroxyethyl methacrylate (PSA) polymer is filled with a male mold having the coating layer formed thereon and cured, and the mold is separated to form a lens molding layer. And sorbitol solution polymer-coated contact lens 삭제delete
KR1020170144463A 2017-11-01 2017-11-01 Contact lens consisting of hydroxyethylmethacrylate and sorbitol solution polymer coating and the method of manuacturing the same KR101963234B1 (en)