KR101923545B1 - Waterproof polyurethane resin compounds and mobile device bezel adhesive tape using the same - Google Patents

Waterproof polyurethane resin compounds and mobile device bezel adhesive tape using the same Download PDF

Info

Publication number
KR101923545B1
KR101923545B1 KR1020160153110A KR20160153110A KR101923545B1 KR 101923545 B1 KR101923545 B1 KR 101923545B1 KR 1020160153110 A KR1020160153110 A KR 1020160153110A KR 20160153110 A KR20160153110 A KR 20160153110A KR 101923545 B1 KR101923545 B1 KR 101923545B1
Authority
KR
South Korea
Prior art keywords
composition
diisocyanate
waterproof
adhesive
polyurethane resin
Prior art date
Application number
KR1020160153110A
Other languages
Korean (ko)
Other versions
KR20180055985A (en
Inventor
황진상
김주열
원종우
박정현
이승욱
Original Assignee
황진상
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 황진상 filed Critical 황진상
Priority to KR1020160153110A priority Critical patent/KR101923545B1/en
Publication of KR20180055985A publication Critical patent/KR20180055985A/en
Application granted granted Critical
Publication of KR101923545B1 publication Critical patent/KR101923545B1/en

Abstract

본 발명은 한쌍의 하이드록시기(-OH)를 포함하며, 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상을 포함하는 조성물 A를 준비하는 단계, 상기 조성물 A에 이소시아네이트를 포함하는 화합물 B를 첨가하여 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 제조하는 단계, 상기 조성물 C에 하나의 하이드록시기를 포함한 불소 모노올을 첨가하여 방수성 폴리우레탄 아크릴레이트 올리고머를 제조하는 단계 및 방수성 폴리우레탄 아크릴레이트 올리고머에 적어도 1종 이상의 접착부여제를 혼합하여 폴리우레탄 아크릴레이트 접착 조성물을 제조하는 단계를 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법에 관한 것으로, 이를 통해 방수성이 우수한 접착 테이프를 얻을 수 있으며 모바일 기기의 생활방수 및 완전 방수가 가능한 구조를 구현할 수 있다.The present invention includes a pair of hydroxyl groups (-OH), and includes at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol Preparing a composition A, adding compound B comprising an isocyanate to composition A to prepare a random copolymer composition C comprising a pair of isocyanate (NCO) functional groups, wherein the composition C comprises one hydroxyl group Preparing a polyurethane acrylate adhesive composition by adding a fluorine monool to prepare a waterproof polyurethane acrylate oligomer and mixing at least one adhesive agent to the waterproof polyurethane acrylate oligomer. Polyurethane resin with waterproof The present invention relates to a method for manufacturing a composition, through which an adhesive tape having excellent waterproof property can be obtained and a structure capable of waterproofing and completely waterproofing a mobile device can be realized.

Description

방수성 폴리우레탄 수지 조성물 제조방법 및 이를 이용한 모바일 기기용 접착 테이프{WATERPROOF POLYURETHANE RESIN COMPOUNDS AND MOBILE DEVICE BEZEL ADHESIVE TAPE USING THE SAME}Manufacturing method of waterproof polyurethane resin composition and adhesive tape for mobile device using same {WATERPROOF POLYURETHANE RESIN COMPOUNDS AND MOBILE DEVICE BEZEL ADHESIVE TAPE USING THE SAME}

본 발명은 방수성 폴리우레탄 수지 조성물 제조방법 및 이를 이용한 모바일 기기용 접착 테이프에 관한 것으로, 보다 상세하게는 우수한 방수성을 가지고 있어 아웃도어용 모바일 기기 및 방수가 필요한 전자제품에 적용할 수 있는 방수성 폴리우레탄 수지 조성물 제조방법 및 이를 이용한 모바일 기기용 접착 테이프에 관한 것이다.The present invention relates to a method for manufacturing a waterproof polyurethane resin composition and an adhesive tape for a mobile device using the same. More specifically, the waterproof polyurethane having an excellent waterproof property can be applied to outdoor mobile devices and electronic products requiring waterproofing. It relates to a resin composition manufacturing method and an adhesive tape for a mobile device using the same.

최근 스마트폰 및 스마트 패드로 대표되는 모바일 기기는 전화통화를 위한 단순한 기능뿐 만이 아니라 사진 및 동영상 촬영과 같은 멀티미디어 컨텐츠 생산을 할 수 있고, 더 나아가 저장된 음악, 영화를 재생할 수 있으며, 다양한 어플리케이션을 통해 네이게이션 서비스나 운동량 기록 등 다양한 기능을 사용할 수 있다. 또한, 통신 시스템에 접속하여 실시간으로 멀티미디어 컨텐츠를 다운로드 하거나 업로드 하는 등 다양한 기능을 제공하여 사용자에게 많은 편의를 제공하고 있다. 따라서, 많은 사용자들은 자신의 취미활동과 여가생활에 모바일 기기를 다양한 방법으로 이용하고 있다. Recently, mobile devices represented by smartphones and smart pads can produce not only simple functions for phone calls, but also multimedia contents such as photographing and video recording, and can play stored music and movies. You can use various functions such as navigation service and exercise record. In addition, by providing a variety of functions, such as downloading or uploading the multimedia content in real time by accessing the communication system to provide a lot of convenience to the user. Therefore, many users use mobile devices in various ways for their hobbies and leisure life.

하지만 일반적인 모바일 기기는 내부에 많은 수의 전자부품을 포함하고 있는 정밀한 구조로 제작된다. 따라서 사용자가 수분이 많은 다습한 환경이나 워터파크, 수영장, 해변과 같은 장소에서 수상 레저 활동을 하다가 소유한 모바일 기기에 수분이 다량으로 닿게 되거나 손이나 고정대에서 놓쳐 침수되게 되면, 내부에 수분이 침투하여 기기가 망가지게 된다. 특히 해변과 같은 염분이 다량 함유된 장소나 워터파크, 수영장과 같은 물 정화를 위해 다량의 이온과 미네랄을 강제로 첨가한 장소에서는 삼투압 현상에 의해 수분이 더욱 빠르게 침투하게 됨과 동시에 수분이 닿은 전자장치는 일반 수돗물 대비 더욱 빠르게 부식과 침식이 발생할 수 있다. 이러한 경우 일반적인 건조로는 전자기기를 다시 재사용 할 수 없을뿐더러, 수리 자체가 불가능하여 모바일 기기 전체를 교체해야 하는 우려가 있다.However, typical mobile devices are manufactured with a precise structure that includes a large number of electronic components therein. Therefore, when a user enters a water leisure activity in a humid, humid environment or in a place such as a water park, swimming pool, or beach, a large amount of water gets in contact with a mobile device owned by him or is missed by a hand or a stand, the water penetrates inside. The device will be broken. In particular, in places containing a large amount of salt such as beaches, water parks, swimming pools, etc., where a large amount of ions and minerals are forcibly added, water penetrates more quickly by osmotic pressure, and at the same time, touches electronic devices. Can cause corrosion and erosion faster than regular tap water. In this case, there is a concern that the general drying machine cannot reuse electronic devices again, and that the entire mobile device must be replaced because repair is impossible.

따라서 많은 제조사들은 이러한 문제를 해결하기 위해 케이스가 하나로 이루어진 유니바디 케이스와 같은 구조를 도입하고 있지만, 보다 근본적인 문제를 해결할 수 있는 방법은 아니다. Therefore, many manufacturers are adopting a structure like a unibody case with a single case to solve this problem, but it is not a way to solve the more fundamental problem.

특히, 수상스키나 스킨스쿠버와 같은 수상에서의 격렬한 레저 활동에 노출되는 모바일 기기는 사용자의 활동적인 움직임과 높은 수압으로 인해 높은 수압에 노출되며, 충돌, 낙하, 흔들림과 같은 일반적이지 않은 다양한 외부적인 요인이 모바일 기기에 전달될 수 있고, 이로인해 모바일 기기에 평상적인 사용보다 더욱 강한 스트레스가 가해지게 된다. 이러한 스트레스로 인해 모바일 기기가 더욱 쉽게 파손이 될 수 있으므로 이러한 환경에서 모바일 기기를 보호할 수 있는 방법을 고안할 필요가 있어 왔고, 특히 사용자로 하여금 극한 환경에서 모바일 기기를 용이하게 이용할 수 있게 하기 위해서 방수성을 가진 모바일 기기의 구조를 고안하여 왔다.In particular, mobile devices exposed to intense leisure activities in the water, such as water skiing and skin scuba, are exposed to high water pressure due to the user's active movement and high water pressure, and various uncommon external factors such as collisions, falls, and shaking Factors can be transferred to the mobile device, which places more stress on the mobile device than normal use. Because of this stress, mobile devices can be more easily damaged, and there has been a need to devise ways to protect them in such environments, especially in order to make them easier to use in extreme environments. The structure of a waterproof mobile device has been devised.

그 중 가장 일반적인 방법은 케이스 또는 디스플레이를 접합하기 위한 접착제 또는 접착테이프를 방수가 가능한 구조로 고안하여 모바일 기기에 적용하여왔고, 이러한 방법은 특히 이격면이 존재하는 케이스의 접합면과 디스플레이 접합면에 적용하여, 모바일 기기의 빈틈을 완벽하게 메꾸어 수분으로부터 내부를 보호하는 방법을 제공하여 왔다.The most common method has been applied to mobile devices by devising a waterproof structure of the adhesive or adhesive tape for bonding the case or display, this method is particularly applied to the bonding surface and the display bonding surface of the case where the separation surface exists In application, it has provided a method to completely fill the gaps of mobile devices to protect the interior from moisture.

한국등록특허 제 10-1661501호 향상된 밀착성을 갖는 방수용 테이프의 발명은, 기재층의 일면에 필러층을 구비하여 얇은 두께이어도 양호한 점착성을 나타내며, 내충격성 및 방수성이 뛰어난 향상된 밀착성을 갖는 방수용 테이프를 제공하며, 이를 통해 얇은 두께이어도 양호한 점착성 및 밀착성과 내충격성을 나타내며, 부재와 접착체층 계면에 존재하는 간극까지도 효과적으로 커버할 수 있는 수준의 방수성을 가지는 향상된 밀착성을 갖는 방수용 테이프 및 그 제조방법을 제공하는데 그 주된 목적이 있다. 하지만 상기 발명은 필러층을 반드시 구비해야 하므로 일반적인 테이프와 비교시 다소 두꺼운 두께로 형성되며, 두께가 두꺼워 지면 모바일 기기의 접합면이 육안으로 명확히 구분되며, 이로 인해 심미적인 부분에서 문제를 발생하게 될 수 있다. 또한, 제조 단가가 높아지기 때문에 전체적인 가격이 비싸지게 되며, 공정이 복잡하여 제조 속도가 느리기 때문에 수율이 낮아질 수 있다는 문제가 있다.Korean Patent No. 10-1661501 The invention of the waterproof tape having improved adhesiveness, by providing a filler layer on one surface of the base material layer to provide a good adhesiveness even at a thin thickness, providing a waterproof tape having improved adhesion excellent in impact resistance and waterproofness It provides a good adhesiveness and adhesion and impact resistance even at a thin thickness, and provides a waterproof tape and improved manufacturing method having an improved adhesiveness that can effectively cover even the gap between the member and the adhesive layer interface. Its main purpose is. However, since the present invention must have a filler layer, it is formed to a thicker thickness compared to a general tape, and when the thickness is thick, the joint surface of the mobile device is clearly distinguished by the naked eye, which causes problems in the aesthetic part. Can be. In addition, there is a problem that the overall price is expensive because the manufacturing cost is high, the yield is low because the manufacturing process is slow due to the complicated process.

또한, 한국등록특허 제 10-1625605호 빛샘 방지 및 방수 기능을 갖는 완충 테이프 및 빛샘 방지 기능을 갖는 완충 테이프의 발명은, 발포 성형된 폴리머 발포폼을 구비하여 1차 방수 효과 및 완충 효과를 갖도록 형성되는 완충 필름; 기공율이 1% 내지 50%인 방수 폴리머를 구비하여 2차 방수 효과를 갖도록 형성되는 방수 필름; 및 상기 방수 필름에 인쇄되며 상기 방수 필름과 상기 완충 필름의 사이에 배치되고 유색 물질을 갖는 광차단층을 포함하고, 상기 광차단층은, 방수 폴리머, 유색 안료, 및 산화알루미늄(Al2O3)의 혼합물을 압출 또는 캐스팅 성형하여 생성되는, 빛샘 방지 및 방수 기능을 갖는 완충 테이프를 제공하여, 발포 성형된 폴리머 발포폼의 구성을 통하여, 대상물에 가해지는 충격을 흡수할 수 있다. 이에 따라, 대상물의 파손, 및 충격으로 인한 고장 현상을 상당량 방지할 수 있다. 아울러, 빛샘 방지 기능을 갖는 완충 테이프를 휴대용 단말기의 윈도우 패널 등에 부착하는 경우, 완충 필름에 부착 형성되는 광차단 필름의 구성을 통하여, 휴대용 단말기의 디스플레이 패널로부터 새어나오는 빛을 쉽게 차단할 수 있어, 휴대용 단말기의 마감 품질을 더욱 향상시킬 수 있다. 나아가, 방수 폴리머의 구성을 통해 대상물의 미세 틈새를 견고하게 실링할 수 있어, 대상물에 대하여 방수 기능을 제공할 수 있다. 하지만 상기 발명은 테이프를 구성하는 층이 5층 이상이 구성되어야 하므로 구조가 매우 복잡하므로 저렴한 가격의 방수 모바일 기기용 접착 테이프에 적용하기에는 바람직하다고 볼 수 없다. 또한, 유색안료 및 산화알루미늄을 포함하여 광차단층을 구성하고 있기 때문에 전체적인 색상이 유색을 띄므로 모바일 기기의 접합면이 더욱 도드라지게 보일 수 있다.In addition, the invention of Korean Patent No. 10-1625605 buffer tape having a light leakage prevention and waterproofing function and a buffer tape having a light leakage preventing function is formed to have a primary waterproofing effect and a buffering effect by having a foam-molded polymer foam foam Buffer film; A waterproof film having a waterproof polymer having a porosity of 1% to 50% to have a secondary waterproof effect; And a light blocking layer printed on the waterproof film and disposed between the waterproof film and the buffer film and having a colored material, wherein the light blocking layer extrudes a mixture of the waterproof polymer, the color pigment, and aluminum oxide (Al 2 O 3). Or by providing a buffer tape having a light leakage prevention and waterproofing function produced by casting molding, it is possible to absorb the impact applied to the object through the configuration of the foam molded polymer foam. As a result, it is possible to prevent a considerable amount of failure due to damage to the object and impact. In addition, when the buffer tape having a light leakage preventing function is attached to a window panel of a portable terminal, the light leaking from the display panel of the portable terminal can be easily blocked through the configuration of the light blocking film attached to the buffer film. The finishing quality of the terminal can be further improved. Furthermore, through the construction of the waterproof polymer, it is possible to firmly seal the fine gap of the object, thereby providing a waterproof function for the object. However, the present invention is not preferable to be applied to the adhesive tape for a low-cost waterproof mobile device because the structure of the tape is very complex because five or more layers of the tape should be configured. In addition, since the light blocking layer is composed of colored pigments and aluminum oxide, the overall color may be colored, and thus the bonding surface of the mobile device may appear more sharp.

또한, 한국공개특허 제 10-2002-0094943호 방수테이프용 수용성 접착제 및 그 제조방법의 발명은 폴리비닐알코올 10∼15 중량%, 폴리비닐아세테이트 1∼3 중량%, 산촉매 0.2∼0.3 중량%, 벤즈알데하이드 1∼1.5 중량%, 0.1N 가성소다0.2∼0.3 중량%, 고흡수성수지 25∼30 중량%, 에어로실 0.5∼0.8 중량%, 글라스 버블 1.5∼2 중량%, 라우릴에테르 2∼2.5 중량%, 용제(solvent) 50∼60 중량%로 조성된 방수테이프용 수용성접착제 및 그 제조방법에 관한 것으로, 이를 통해 폴리비닐알코올과 폴리비닐아세테이트를 주성분으로 제조된 접착제를 이용하여 내수성 및 접착력이 우수하며, 고흡수성수지의 투입 과정을 단일화 및 자동화함으로써 제조공정을 간소화하였으며 접착제가 이미 고흡수성수지의 외부를 감싸고 있어 기존의 방수테이프에서 반드시 사용되었던 박막층을 제거함으로써 방수테이프의 기능인 방수 특성을 배가시킬 수 있는 방수테이프용 수용성접착제를 제공한다. 하지만 상기 발명은 솔벤트의 중량이 50 내지 60%로 많이 포함되어 있고 에어로실 및 글라스 버블을 포함하여 두께를 형성한다. 따라서 제조방법이 다소 복잡하고 이를 통해 가격이 높아지므로 보다 단순한 구성의 수용성접착제의 구성이 필요하다.In addition, the invention of the water-soluble adhesive for the waterproof tape and the manufacturing method of Korean Patent Publication No. 10-2002-0094943 and polyvinyl alcohol 10 to 15% by weight, polyvinylacetate 1 to 3% by weight, acid catalyst 0.2 to 0.3% by weight, benz Aldehyde 1 to 1.5% by weight, 0.1N caustic soda 0.2 to 0.3% by weight, superabsorbent resin 25 to 30% by weight, aerosil 0.5 to 0.8% by weight, glass bubble 1.5 to 2% by weight, lauryl ether 2 to 2.5% by weight The present invention relates to a water-soluble adhesive for a waterproof tape composed of 50 to 60% by weight of a solvent, and a method for manufacturing the same. Through this, an adhesive made mainly of polyvinyl alcohol and polyvinylacetate has excellent water resistance and adhesion. In addition, the manufacturing process has been simplified by unifying and automating the process of superabsorbent polymer absorption. Since the adhesive is already enclosing the exterior of the superabsorbent polymer, it removes the thin film layer that was used in the existing waterproof tape. It provides a water-soluble adhesive for a waterproof tape that can double the waterproof characteristics of the waterproof tape. However, the present invention contains a large amount of solvent of 50 to 60% and includes aerosil and glass bubbles to form a thickness. Therefore, the manufacturing method is somewhat complicated and the price is higher through this, it is necessary to configure the water-soluble adhesive of a simpler configuration.

상술한바와 같이 종래의 방수성 테이프 또는 방수성 접착 조성물 구조는 필러를 더 포함하거나, 별도의 방수층을 더 필요로 하는 등 다소 복잡한 구조로 구현되어 있으며, 이를 생산하기 위한 공정 단계가 매우 복잡하여 대량생산에 용이하지 않으며 가격이 비싸지므로 사용자에게 비용적 부담을 향상시킬 수 있다. As described above, the conventional waterproof tape or waterproof adhesive composition structure is implemented in a somewhat complicated structure, including a filler or a separate waterproof layer, and the process steps for producing the same are very complicated. It is not easy and expensive, which can increase the cost burden on the user.

따라서, 본 발명에서는 소수성을 가지는 화합물을 포함하여 단순한 구조를 가지는 방수가 가능한 접착층을 제시하고, 이를 통해 일반적인 기재에 접착층을 도포하였을 시 한층 개선된 방수 효과를 제공하는 것을 목적으로 하는 방수성 폴리우레탄 수지 조성물 제조방법 및 이를 이용한 모바일 기기용 접착 테이프를 제공하고자 한다.Therefore, the present invention provides a waterproof adhesive layer having a simple structure including a compound having a hydrophobic property, and through this waterproof polyurethane resin for the purpose of providing an improved waterproof effect when the adhesive layer is applied to a general substrate The present invention provides a method for producing a composition and an adhesive tape for a mobile device using the same.

1. 한국등록특허 제 10-1661501호1. Korea Patent Registration No. 10-1661501 2. 한국등록특허 제 10-1625605호2. Korean Patent No. 10-1625605 3. 한국공개특허 제 10-2002-0094943호3. Korean Patent Publication No. 10-2002-0094943

본 발명은 상술한 문제점을 모두 해결하는 것을 목적으로 한다.The present invention aims to solve all the above-mentioned problems.

본 발명의 다른 목적은 전단 접착강도가 우수한 방수성 접착 수지 조성물을 제공하는 것이다.Another object of the present invention is to provide a waterproof adhesive resin composition having excellent shear adhesive strength.

본 발명의 다른 목적은 접착력이 높아 피착제를 단단히 고정시킬 수 있는 방수성 접착 수지 조성물을 제공하는 것이다.Another object of the present invention is to provide a waterproof adhesive resin composition having a high adhesive strength and capable of firmly fixing an adherend.

본 발명의 다른 목적은 두께가 얇으면서도 높은 방수성을 가진 모바일 기기용 접착 테이프를 제공하는 것이다.Another object of the present invention is to provide an adhesive tape for a mobile device having a thin thickness and high waterproofness.

본 발명의 다른 목적은 단순한 구조를 통해 대량생산이 용이한 모바일 기기용 접착 테이프를 제공하는 것이다.Another object of the present invention is to provide an adhesive tape for a mobile device that is easy to mass production through a simple structure.

상기한 바와 같은 본 발명의 목적을 달성하고, 후술하는 본 발명의 특징적인 효과를 실현하기 위한, 본 발명의 특징적인 구성은 하기와 같다.The characteristic structure of this invention for achieving the objective of this invention mentioned above, and realizing the characteristic effect of this invention mentioned later is as follows.

본 발명은 한쌍의 하이드록시기(-OH)를 포함하며, 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상을 포함하는 조성물 A를 준비하는 단계, 상기 조성물 A에 이소시아네이트를 포함하는 화합물 B를 첨가하여 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 제조하는 단계, 상기 조성물 C에 하나의 하이드록시기를 포함한 불소 모노올을 첨가하여 방수성 폴리우레탄 아크릴레이트 올리고머를 제조하는 단계 및 방수성 폴리우레탄 아크릴레이트 올리고머에 적어도 1종 이상의 접착부여제를 혼합하여 폴리우레탄 아크릴레이트 접착 조성물을 제조하는 단계를 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법을 제공한다.The present invention includes a pair of hydroxyl groups (-OH), and includes at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol Preparing a composition A, adding compound B comprising an isocyanate to composition A to prepare a random copolymer composition C comprising a pair of isocyanate (NCO) functional groups, wherein the composition C comprises one hydroxyl group Preparing a polyurethane acrylate adhesive composition by adding a fluorine monool to prepare a waterproof polyurethane acrylate oligomer and mixing at least one adhesive agent to the waterproof polyurethane acrylate oligomer. Polyurethane resin with waterproof Provided are methods for preparing the composition.

본 발명의 실시예에 따른 상기 랜덤 공중합체 조성물 C를 제조하는 단계는, 상기 조성물 C 100 중량부를 기준으로 상기 조성물 A 50 내지 80 중량부를 준비하는 단계, 상기 조성물 A를 교반기에 넣어 50 내지 100 rpm으로 교반하는 단계, 상기 조성물 C 100 중량부를 기준으로 상기 상기 화합물 B 20 내지 50 중량부를 상기 교반된 조성물 A에 첨가하는 단계 및 상기 화합물 B가 첨가된 조성물 A에 축중합 촉매를 첨가하여 교반속도 200 내지 300 rpm 및 온도 50 내지 85 ℃ 의 환경에서 중합 반응을 하는 단계를 포함하는 것을 특징으로 한다.In the preparing of the random copolymer composition C according to an embodiment of the present invention, preparing the composition A 50 to 80 parts by weight based on 100 parts by weight of the composition C, putting the composition A in a stirrer 50 to 100 rpm Stirring, adding 20 to 50 parts by weight of the compound B to the stirred composition A based on 100 parts by weight of the composition C, and adding a condensation polymerization catalyst to the composition A to which the compound B is added. To 300 rpm and a temperature of 50 to 85 ° C.

본 발명의 실시예에 따른 상기 축중합 촉매는 2-메틸트라이에틸렌다이아마이드, 1,4-디아자바이싸이클로[2,2,2]옥탄, 비스(2-디메틸아미노에틸)에테르, 트리메틸아미노에틸에탄올아민, N,N,N1,N1,N2-펜타메틸디에틸렌트리아민, N,N1-디메틸에탄올아민, 디메틸아미노프로필아민, N-에틸모르폴린, N,N-디메틸아미노에틸모르폴린, N,N-디메틸싸이클로헥실아민, 2-메틸-2-아자노보네인 을 포함하는 3차 아민, 4차 암모늄과 알카리 금속의 카복시산 염을 포함하는 비양성자성 염 및 구리 나프티네이트, 코발트 나프티네이트, 아연 나프테이트, n-다이부틸틴디라우레이트, 트라이스틸아민, 디부틸틴디아세테이트, 디부틸틴디머캅타이드를 포함하는 유기금속화합물로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 한다.The polycondensation catalyst according to an embodiment of the present invention is 2-methyltriethylenediamide, 1,4-diazabicyclo [2,2,2] octane, bis (2-dimethylaminoethyl) ether, trimethylaminoethylethanol Amine, N, N, N 1 , N 1 , N 2 -pentamethyldiethylenetriamine, N, N 1 -dimethylethanolamine, dimethylaminopropylamine, N-ethylmorpholine, N, N-dimethylaminoethylmor Aprotic salts and copper naphthenates, including poline, N, N-dimethylcyclohexylamine, tertiary amines including 2-methyl-2-azanobonane, carboxylic acid salts of quaternary ammonium and alkali metals, At least one selected from the group consisting of cobalt naphthenate, zinc naphate, n-dibutyl tin dilaurate, tristilamine, dibutyl tin diacetate, and dibutyl tin dimercaptide It is done.

본 발명의 실시예에 따른 상기 이소시아네이트 화합물은, 2,4-톨리엔디이소시아네이트, 2,6-톨리엔디이소시아네이트, 1,3-자일렌디이소시아네이트, 1,4-자일렌디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 2,4-트리렌디이소시아네이트, 2,6-트리렌디이소시아네이트, 1,3-크실렌디이소시아네이트, 디페닐메탄-4,4-디이소시아네이트, 3-메틸-디페닐메탄디이소시아네이트, 메틸렌 다이페닐 디이소시아네이트(MDI), 1,6-헥산디이소시아네이트, 이소포론디이소시아네이트, 디사이클로헥실메탄디이소시아네이트, 헥사메틸렌디이소시아네이트, 1,3-비스(이소시아네이토메틸)싸이클로헥산 및 1,4-비스(이소시아네이트메틸)싸이클로헥산으로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 한다.The isocyanate compound according to an embodiment of the present invention, 2,4- toylene diisocyanate, 2,6-toylene diisocyanate, 1,3-xylene diisocyanate, 1,4-xylene diisocyanate, 1,5-naphthalenedi Isocyanate, 2,4-triene diisocyanate, 2,6-triene diisocyanate, 1,3-xylene diisocyanate, diphenylmethane-4,4-diisocyanate, 3-methyl-diphenylmethane diisocyanate, methylene diphenyl Diisocyanate (MDI), 1,6-hexane diisocyanate, isophorone diisocyanate, dicyclohexyl methane diisocyanate, hexamethylene diisocyanate, 1,3-bis (isocyanatomethyl) cyclohexane and 1,4- Bis (isocyanate methyl) cyclohexane is characterized in that it comprises at least one or more selected from the group consisting of.

본 발명의 실시예에 따른 상기 접착부여제는 하이드록시에틸 아크릴레이트(HEA), 하이드록시프로필 아크릴레이트(HPA), 하이드록시부틸 아크릴레이트(HBA) 및 하이드록시에틸 메타아크릴레이트(2-HEMA)로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 한다.The tackifier according to an embodiment of the present invention is hydroxyethyl acrylate (HEA), hydroxypropyl acrylate (HPA), hydroxybutyl acrylate (HBA) and hydroxyethyl methacrylate (2-HEMA) It characterized in that it comprises one or more selected from the group consisting of.

본 발명의 실시예에 따른 상기 불소 다이올은, 2,3,4,5,6-펜타플루오로벤질 알코올, 4-(트리플루오로메틸)벤질 알코올, [3,5-다이(트리플루오로메틸)페닐]메탄올, 1,1,1,3,3,3-헥사플루오로-2-프로판올, 1,1,1,3,3,3-헥사플루오로-2-메틸이소프로판올, 헥사플루오로-2-(p-톨일)이소프로판올, 4,5,5,6,6,6-헥사플루오로-4-(트라이메틸)-1-헥산올, 4,4,5,5,5-펜타플루오로펜탄올, 펜타플루오로프로피온알데하이드, 1H,1H,5H-옥타플루오로-1-펜탄올 및 펜타플루오로부탄-2-올로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 한다.The fluorine diol according to an embodiment of the present invention, 2,3,4,5,6-pentafluorobenzyl alcohol, 4- (trifluoromethyl) benzyl alcohol, [3,5-di (trifluoro) Methyl) phenyl] methanol, 1,1,1,3,3,3-hexafluoro-2-propanol, 1,1,1,3,3,3-hexafluoro-2-methylisopropanol, hexafluoro 2- (p-tolyl) isopropanol, 4,5,5,6,6,6-hexafluoro-4- (trimethyl) -1-hexanol, 4,4,5,5,5-pentafluoro And at least one selected from the group consisting of lofentanol, pentafluoropropionaldehyde, 1H, 1H, 5H-octafluoro-1-pentanol, and pentafluorobutan-2-ol.

본 발명의 실시예에 따른 방수성 폴리우레탄 아크릴레이트 올리고머를 제조하는 단계는 온도 60 내지 90 ℃의 환경에서 200 내지 500 rpm 으로 교반하는 것을 특징으로 한다.The step of preparing a waterproof polyurethane acrylate oligomer according to an embodiment of the present invention is characterized in that the stirring at 200 to 500 rpm in an environment of temperature 60 to 90 ℃.

본 발명의 실시예에 따른 상기 폴리우레탄 아크릴레이트 접착 조성물을 제조하는 단계는, 상기 방수성 폴리우레탄 아크릴레이트 올리고머 100 중량부에 대하여 상기 접착부여제 0.5 내지 15 중량부를 포함하는 단계 및 상기 단계에서 생성된 조성물을 교반기에 넣어 60 내지 90 ℃의 환경에서 200 내지 500 rpm으로 교반하여 중합 반응을 진행하는 단계를 포함하는 것을 특징으로 한다.The preparing of the polyurethane acrylate adhesive composition according to an embodiment of the present invention comprises the 0.5 to 15 parts by weight of the tackifier with respect to 100 parts by weight of the waterproof polyurethane acrylate oligomer and the step produced in the step Put the composition in a stirrer, characterized in that it comprises the step of proceeding the polymerization reaction by stirring at 200 to 500 rpm in an environment of 60 to 90 ℃.

본 발명은 상기 방수성을 가진 폴리우레탄 수지 조성물의 제조방법에 따라 제조된 것을 특징으로 하는 모바일 기기용 접착 조성물을 제공하는 것을 특징으로 한다.The present invention is characterized in that it provides an adhesive composition for a mobile device, characterized in that produced in accordance with the manufacturing method of the polyurethane resin composition having water resistance.

본 발명의 실시예에 따른 모바일 기기용 접착 조성물을 포함하는 모바일 기기용 접착 테이프에 있어서, 상기 모바일 기기용 접착 조성물이 50 내지 130 μm 두께의 기재에 10 내지 50 μm 도포되는 것을 특징으로 하는 모바일 기기용 접착 테이프를 제공한다.In the adhesive tape for a mobile device comprising the adhesive composition for a mobile device according to an embodiment of the present invention, the mobile device, the adhesive composition for a mobile device is characterized in that 10 to 50 μm applied to a substrate having a thickness of 50 to 130 μm Provide adhesive tape for

본 발명의 실시예에 따른 모바일 기기용 접착 테이프의 투습율은 0.5 내지 10 g/m2.day인 것을 특징으로 한다.Moisture permeability of the adhesive tape for a mobile device according to an embodiment of the present invention is characterized in that 0.5 to 10 g / m 2 .day.

본 발명은 이원 공중합체 또는 삼원 공중합체로 구성된 조성물에 접착 부여제를 포함한 수지 조성물을 제공하여 5Kgf/cm2 이상의 전단 접착강도를 형성하는 효과가 있다.The present invention has an effect of forming a shear adhesive strength of 5 Kgf / cm 2 or more by providing a resin composition including an adhesion imparting agent to a composition composed of a binary copolymer or a terpolymer.

또한, 본 발명은 접착 수지 조성물의 구조를 단순한 방법으로 구현할 수 있는 구조와 방법을 제공하여 대량생산이 용이하고 취급이 간편하며 원가가 낮아져 비용 부담을 줄일 수 있는 효과가 있다.In addition, the present invention provides a structure and a method that can implement the structure of the adhesive resin composition in a simple way, mass production is easy, easy handling and low cost has the effect of reducing the cost burden.

또한, 본 발명은 소수성 특징을 가지는 불소 모노올을 포함하는 이원 공중합체 또는 삼원 랜덤 공중합체로 구성된 접착 수지 조성물을 통해 방수성에 유리한 접착 테이프를 제공하는 효과가 있다.In addition, the present invention has the effect of providing an adhesive tape which is advantageous for waterproofing through an adhesive resin composition composed of a binary copolymer or a ternary random copolymer including a fluorine monool having hydrophobic characteristics.

또한, 본 발명은 얇은 두께를 구현할 수 있으며, 0.5 내지 8 g/m2day의 투습도를 가지는 접착 테이프를 제공하는 효과가 있다.In addition, the present invention can implement a thin thickness, there is an effect of providing an adhesive tape having a water vapor transmission rate of 0.5 to 8 g / m2day.

또한, 본 발명의 접착 테이프를 이용한 모바일 기기는 IPX 6 내지 IPX 8 등급의 방수성을 가지는 효과가 있다.In addition, the mobile device using the adhesive tape of the present invention has the effect of waterproofing IPX 6 to IPX 8 grade.

후술하는 본 발명에 대한 상세한 설명은, 본 발명이 실시될 수 있는 특정 실시예를 예시로서 도시하는 첨부 도면을 참조한다. 이들 실시예는 당업자가 본 발명을 실시할 수 있기에 충분하도록 상세히 설명된다. 본 발명의 다양한 실시예는 서로 다르지만 상호 배타적일 필요는 없음이 이해되어야 한다. 예를 들어, 여기에 기재되어 있는 특정 형상, 구조 및 특성은 일 실시예에 관련하여 본 발명의 정신 및 범위를 벗어나지 않으면서 다른 실시예로 구현될 수 있다. 또한, 각각의 개시된 실시예 내의 개별 구성요소의 위치 또는 배치는 본 발명의 정신 및 범위를 벗어나지 않으면서 변경될 수 있음이 이해되어야 한다. 따라서, 후술하는 상세한 설명은 한정적인 의미로서 취하려는 것이 아니며, 본 발명의 범위는, 적절하게 설명된다면, 그 청구항들이 주장하는 것과 균등한 모든 범위와 더불어 첨부된 청구항에 의해서만 한정된다. 도면에서 유사한 참조부호는 여러 측면에 걸쳐서 동일하거나 유사한 기능을 지칭한다.DETAILED DESCRIPTION The following detailed description of the invention refers to the accompanying drawings that show, by way of illustration, specific embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention. It should be understood that the various embodiments of the present invention are different but need not be mutually exclusive. For example, certain shapes, structures, and characteristics described herein may be embodied in other embodiments without departing from the spirit and scope of the invention with respect to one embodiment. In addition, it is to be understood that the location or arrangement of individual components within each disclosed embodiment may be changed without departing from the spirit and scope of the invention. The following detailed description, therefore, is not to be taken in a limiting sense, and the scope of the present invention, if properly described, is defined only by the appended claims, along with the full range of equivalents to which such claims are entitled. Like reference numerals in the drawings refer to the same or similar functions throughout the several aspects.

이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있도록 하기 위하여, 본 발명의 바람직한 실시예들에 관하여 첨부된 도면을 참조하여 상세히 설명하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily implement the present invention.

본 발명의 실시예에 따른 방수성 폴리우레탄 수지 조성물은 한쌍의 하이드록시(-OH) 그룹을 포함하고 있는 조성물 A 및 디이소시아네이트 화합물 및 이소시아네이트를 포함하는 군에서 선택된 적어도 1종 이상의 화합물 B로부터 합성되는 조성물 C를 포함하며, 조성물 C는 한쌍의 이소시아네이트(NCO) 작용기를 포함하여 구성된다. 조성물 C에 표면 에너지가 낮아 소수성의 특성을 띄는 불소 모노올을 첨가하여 방수성 폴리우레탄 아크릴레이트 올리고머를 구성하고, 방수성 폴리우레탄 아크릴레이트 올리고머에 적어도 1종 이상의 접착부여제를 혼합하여 폴리우레탄 아크릴레이트 접착 조성물을 구성한다.The waterproof polyurethane resin composition according to an embodiment of the present invention is a composition synthesized from composition A comprising a pair of hydroxy (-OH) groups and at least one compound B selected from the group comprising a diisocyanate compound and an isocyanate And C, wherein composition C comprises a pair of isocyanate (NCO) functional groups. Fluorinated monool having low surface energy is added to composition C to form a water-resistant polyurethane acrylate oligomer, and at least one adhesive agent is mixed with the water-resistant polyurethane acrylate oligomer to bond polyurethane acrylate. Configure the composition.

조성물 A는 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상을 포함하여 구성될 수 있다. 보다 상세히 기술하면 조성물 A와 화합물 B의 합성을 통해 조성물 C를 형성한다. 이때, 조성물 C는 이원 또는 삼원 랜덤 공중합체로 구성될 수 있는데, 조성물 A의 군 중에서 2종 이상을 선택하여 포함하여 구성할 수 있다. 이원 랜덤 공중합체로 구성된 조성물 A의 화학식은 하기와 같이 도시될 수 있다.Composition A may comprise at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol. In more detail, composition C is formed through the synthesis of composition A and compound B. At this time, the composition C may be composed of a binary or ternary random copolymer, it may be configured to include two or more selected from the group of the composition A. The formula of composition A composed of binary random copolymers can be shown as follows.

Figure 112016112143104-pat00001
Figure 112016112143104-pat00001

이원 랜덤 공중합체로 구성될 경우, 조성물 A의 군 중에서 2종이 선택되어 조성물이 구성될 수 있다. 이때, 배열이 무작위로 발생하게 되면서 무작위적인 결합 구조를 형성하게 될 수 있다.When composed of binary random copolymers, two may be selected from the group of composition A to constitute the composition. At this time, the arrangement may occur randomly to form a random coupling structure.

삼원 랜덤 공중합체로 구성될 경우, 조성물 A의 군 중에서 3 종이 선택되어 조성물이 구성될 수 있다. 삼원 랜덤 공중합체로 구성된 조성물 A의 화학식은 하기와 같이 도시될 수 있다.When composed of ternary random copolymers, three may be selected from the group of composition A to constitute the composition. The formula of composition A composed of ternary random copolymers can be shown as follows.

Figure 112016112143104-pat00002
Figure 112016112143104-pat00002

랜덤 공중합체로 구성되기 때문에 혼합하는 중량비를 정확하게 평량하지 않아도 무리없이 중합 반응이 발생할 수 있기 때문에 공정이 단순해질 수 있으며 이로 인한 제조 원가 절감을 달성할 수 있으며, 보다 빠른 속도로 대량생산이 가능하게 이루어질 수 있다. 또한 조성물 A는 랜덤 공중합체로 구성되기 때문에 이원 및 삼원 공중합체가 각각 형성되거나 이원과 삼원 공중합체가 함께 형성될 수 있다.Because it is composed of a random copolymer, it is possible to simplify the process because the polymerization reaction can occur without difficulty even if the weight ratio of mixing is not precisely weighed, and thus the manufacturing cost can be reduced, and the mass production can be performed at a higher speed. Can be done. In addition, since the composition A is composed of a random copolymer, binary and tertiary copolymers may be formed, respectively, or binary and tertiary copolymers may be formed together.

상술한바와 같이 조성물 C는 이원 또는 삼원 랜덤 공중합체(이하 이원/삼원 랜덤 공중합체)로 구성된다. 즉, 조성물 A에서 2종 이상을 선택하여 화합물 B를 첨가하여 중합 반응을 통해 조성물 C를 합성하게 된다. 이원/삼원 랜덤 공중합체는 서로 다른 단량체들이 반복하여 공유결합을 형성하여 공중합체를 구성하게 되는데, 단량체들이 무질서하게 연결된 경우를 랜덤 공중합체라고 한다. 따라서 조성물 C는 서로 다른 분자량을 가지는 단량체가 랜덤하게 엮여 있기 때문에 블록 공중합체나 그라프트 공중합체 구조 대비 랜덤 공중합체의 사슬구조가 더욱 엉성하게 구성되어 있으므로, 충격을 흡수할 수 있는 공간이 공중합체 구조의 내부에 더욱 많이 존재하게 됨과 동시에, 보다 탄성력이 높고 외부의 충격을 흡수할 수 있는 효과가 개선될 수 있다.As described above, the composition C is composed of binary or ternary random copolymers (hereafter binary / terminal random copolymers). That is, the composition C is synthesized through the polymerization reaction by selecting two or more kinds in the composition A and adding the compound B. Two-way / three-way random copolymers are copolymerized by forming different covalent bonds of different monomers repeatedly, the case where the monomers are connected randomly is called a random copolymer. Therefore, since the composition C has randomly woven monomers having different molecular weights, the chain structure of the random copolymer is more coarse than that of the block copolymer or the graft copolymer. While more present inside the structure, the effect of higher elasticity and the ability to absorb external shocks can be improved.

조성물 A 중 수첨 폴리부타디엔 다이올은 수첨 폴리올레핀 구조단위중 하나로 1,3-부타디엔, 1,3-펜타디엔, 이소프렌, 2,3-디메틸-1,3-부타디엔, 2-페닐-1,3-부타디엔, 2-프로필-1,3-부타디엔, 1,3-헵타디엔, 6-메틸-1,3-헵타디엔, 1,3-헥사디엔, 5-메틸-1,3-헥사디엔, 2,4-헥사디엔, 2,5-디메틸-2,4-헥사디엔 및 1,3-옥타디엔으로부터 선택되는 1종 이상의 디엔을 중합시켜 얻어지는 폴리디엔 구조단위를 수소화하여 얻어지는 구조단위를 포함할 수 있다. 이들 중에서 바람직한 것으로서는 폴리부타디엔 구조단위를 수소화하여 얻어지는 구조단위, 폴리이소프렌 구조단위를 수소화하여 얻어지는 구조단위 또는 폴리(부타디엔-이소프렌) 구조단위를 수소화하여 얻어지는 구조단위를 포함할 수 있다.Hydrogenated polybutadiene diol in composition A is one of the hydrogenated polyolefin structural units, 1,3-butadiene, 1,3-pentadiene, isoprene, 2,3-dimethyl-1,3-butadiene, 2-phenyl-1,3- Butadiene, 2-propyl-1,3-butadiene, 1,3-heptadiene, 6-methyl-1,3-heptadiene, 1,3-hexadiene, 5-methyl-1,3-hexadiene, 2, A structural unit obtained by hydrogenating a polydiene structural unit obtained by polymerizing at least one diene selected from 4-hexadiene, 2,5-dimethyl-2,4-hexadiene and 1,3-octadiene may be included. . Preferred among these may include a structural unit obtained by hydrogenating a polybutadiene structural unit, a structural unit obtained by hydrogenating a polyisoprene structural unit, or a structural unit obtained by hydrogenating a poly (butadiene-isoprene) structural unit.

조성물 A의 수첨 폴리부타디엔 다이올은 1분자 중에 수산기를 2개 이상 갖는 것이지만, 수산기를 2∼4개 갖는 것이 바람직하다. 또한, 수첨 폴리올레핀 다이올의 수산기가는 10∼80mgKOH/g인 것이 바람직하고, 더욱 바람직하게는 17∼70mgKOH/g, 특히 바람직하게는 23∼65mgKOH/g이다. 수첨 폴리올레핀 폴리올 화합물의 수산기가가 10mgKOH/g보다 작아지면, 전체적인 분자량과 점도가 지나치게 높아져, 취급이 어려워지고 이후 합성에 문제가 발생할 수 있다. 또한, 수첨 폴리올레핀 다이올 화합물의 수산기가가 80mgKOH/g보다 커지면, 합성시의 체적수축률이 지나치게 커지거나, 중합물의 응집력이 지나치게 높아져, 중합물의 점착 성능이 충분히 발휘되지 않으므로 성능이 나빠질 수 있다. 또한, 폴리부타디엔 다이올은 낮은 유리전이온도 값을 나타내고, 높은 입체 규칙성으로 인하여 인장물성, 300 % 모듈러스와 같은 기계적 물성이 우수하므로, 이 화합물들을 우레탄 화합물의 공중합 모노머로 제공하면 높은 입체 규칙성으로 불소 화합물이 균일하게 혼입될 수 있고, 모바일 기기용 접착제 형성 시 접착력 개선 등의 기계적 물성을 향상시키는 효과가 있다.Although the hydrogenated polybutadiene diol of the composition A has two or more hydroxyl groups in 1 molecule, it is preferable to have 2-4 hydroxyl groups. The hydroxyl value of the hydrogenated polyolefin diol is preferably 10 to 80 mgKOH / g, more preferably 17 to 70 mgKOH / g, particularly preferably 23 to 65 mgKOH / g. When the hydroxyl value of the hydrogenated polyolefin polyol compound is less than 10 mgKOH / g, the overall molecular weight and viscosity become too high, making handling difficult and causing problems in the synthesis afterwards. In addition, when the hydroxyl value of the hydrogenated polyolefin diol compound is larger than 80 mgKOH / g, the volume shrinkage rate at the time of synthesis becomes excessively large, or the cohesion force of the polymer is too high, and the adhesion performance of the polymer is not sufficiently exhibited, which may result in poor performance. In addition, polybutadiene diol has a low glass transition temperature value, and due to its high stereoregularity, it has excellent mechanical properties such as tensile properties and 300% modulus. As a fluorine compound can be uniformly mixed, there is an effect of improving the mechanical properties, such as improved adhesion when forming the adhesive for mobile devices.

그리고 조성물 A의 폴리디메틸실록산 다이올은 폴리디메틸실록산(PDMS)의 말단에 하이드록시기를 포함하는 것으로, 방수성이 뛰어나고 함습률이 낮아 방수를 목적으로 하는 조성물을 형성하는데 적합하다고 할 수 있다.In addition, the polydimethylsiloxane diol of the composition A contains a hydroxyl group at the terminal of the polydimethylsiloxane (PDMS), and can be said to be suitable for forming a composition for waterproofing with excellent waterproofness and low moisture content.

조성물 A의 불소 다이올은 한쌍의 하이드록시기를 포함하여 구성될 수 있다. 불소 다이올은 헥사플루오로-2,3-비스(트리플루오로메틸)부탄-2,3-디올, 2,2,3,3,4,4,5,5,6,6,7,7-도데카플루오로-1,8-옥탄디올 또는 3,3,4,4,5,5,6,6-옥타플루오로-1,6-헥산다이올을 포함할 수 있으며, 바람직하게는 헥사플루오로-2,3-비스(트리플루오로메틸)부탄-2,3-디올 또는 2,2,3,3,4,4,5,5,6,6,7,7-도데카플루오로-1,8-옥탄디올를 포함할 수 있다. 불소 다이올은 불소가 치환된 탄소 수가 1 내지 6으로, 독성으로 문제가 되고 있는 탄소수가 8개 이상인 과불화탄소에 비해 탄소수가 적은 불소 다이올을 사용함이 바람직하다. 따라서 환경 부하가 적고, 보다 안경적인 조성물을 제조할 수 있다. 또한, 불소 다이올의 특성상 함습률이 낮고 방수성능이 우수하기 때문에 본 발명의 실시예에 따른 방수성 폴리우레탄 수지 조성물을 형성함에 있어서 방수 효과를 더욱 향상시킬 수 있는 바람직한 화합물이라고 할 수 있다. The fluorine diol of composition A may comprise a pair of hydroxyl groups. Fluorine diol is hexafluoro-2,3-bis (trifluoromethyl) butane-2,3-diol, 2,2,3,3,4,4,5,5,6,6,7,7 Dodecafluoro-1,8-octanediol or 3,3,4,4,5,5,6,6-octafluoro-1,6-hexanediol, preferably hexa Fluoro-2,3-bis (trifluoromethyl) butane-2,3-diol or 2,2,3,3,4,4,5,5,6,6,7,7-dodecafluoro -1,8-octanediol. The fluorine diol is preferably a fluorine diol having 1 to 6 carbon atoms substituted with fluorine and having less carbon than perfluorocarbons having 8 or more carbon atoms, which are problematic for toxicity. Therefore, the environmental load is small and a more speculative composition can be manufactured. In addition, since the moisture content is low and the waterproof performance is excellent due to the characteristics of the fluorine diol, it can be said that it is a preferable compound which can further improve the waterproof effect in forming the waterproof polyurethane resin composition according to the embodiment of the present invention.

불소 다이올은 하이드록시기 뿐만 아니라 카보네이트기를 더 포함할 수 있으며, 바람직하게는 폴리에틸렌 카보네이트 디올을 포함할 수 있다. 카보네이트기를 더 포함하는 불소 화합물은 접착제용 수지 조성물의 제조시 수분투과도 및 산소투과도의 차단 효과가 월등히 상승하는 효과를 나타내며, 카보네이트기를 포함하지 않은 불소 화합물을 적용한 우레탄 화합물에 비해 유리나 PET, PMMA등의 피착재에 우수한 접착력을 보이므로, 불소 화합물의 함량을 기존에 비해 낮추더라도 우수한 발수성 및 접착력을 가지는 효과를 더욱 보강할 수 있으므로 방수성 폴리우레탄 수지 조성물을 구성하는데 더욱 효과적일 수 있다. 아울러, 불소화 알킬기와 카보네이트기가 교차되도록 분자구조를 설계함으로써, 기존의 우레탄 화합물에 비해 내후성, 내광성 등이 우수하며, 내오성도 강한 특징이 있고, 불소화 폴리카보네이트 디올을 제조함에 있어서, 오각형의 고리 구조의 카보네이트를 중간체로 거치며 in-situ로 반응이 진행하므로 수율이 높은 장점이 있다.The fluorine diol may further include a carbonate group as well as a hydroxy group, and may preferably include polyethylene carbonate diol. The fluorine compound further comprising a carbonate group exhibits an effect of significantly blocking the water and oxygen permeability when the resin composition for the adhesive is prepared, and compared to the urethane compound to which the fluorine compound containing no carbonate group is applied, such as glass, PET, and PMMA. Since it shows excellent adhesion to the adherend, even if the content of the fluorine compound lower than the conventional can be more effective in configuring a waterproof polyurethane resin composition because it can further enhance the effect of having excellent water repellency and adhesion. In addition, by designing the molecular structure so that the fluorinated alkyl group and the carbonate group intersect, it has excellent weather resistance, light resistance, etc., compared to the existing urethane compound, and also has strong resistance to oxidation, and in the production of fluorinated polycarbonate diol, a pentagonal ring structure The reaction proceeds in-situ through the carbonate as an intermediate and has a high yield.

화합물 B는 이소시아네이트를 포함하는 화합물로 구성될 수 있다. 이소시아네이트 화합물은 톨루엔 디이소시아네이트, 헥사메틸렌 디이소시아네이트, 이소포론디이소시아네이트, 디시클로헥실메탄 디이소시아네이트 또는 나프탈렌 디이소시아네이트, 2,4-톨리엔디이소시아네이트, 2,6-톨리엔디이소시아네이트, 1,3-자일렌디이소시아네이트, 1,4-자일렌디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 2,4-트리렌디이소시아네이트, 2,6-트리렌디이소시아네이트, 1,3-크실렌디이소시아네이트, 디페닐메탄-4,4-디이소시아네이트, 3-메틸-디페닐메탄디이소시아네이트, 메틸렌 다이페닐 디이소시아네이트(MDI), 1,6-헥산디이소시아네이트, 이소포론디이소시아네이트, 디사이클로헥실메탄디이소시아네이트, 헥사메틸렌디이소시아네이트, 1,3-비스(이소시아네이토메틸)싸이클로헥산 및 1,4-비스(이소시아네이트메틸)싸이클로헥산으로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하여 구성될 수 있다. 또한 필요시 경화제를 더 추가하여 구성할 수 있다. 이소시아네이트는 소수성 및 방수성의 특징을 가지며 이를 포함한 조성물의 함습률을 낮춰주고 방수 성능을 개선시킬 수 있는 효과를 부여하기 때문에 내충격성을 가진 폴리우레탄 수지 조성물에 방수성능을 더 포함함에 있어서 바람직한 화합물이라고 할 수 있다.Compound B may consist of compounds comprising isocyanates. Isocyanate compounds include toluene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, dicyclohexylmethane diisocyanate or naphthalene diisocyanate, 2,4-toliendiisocyanate, 2,6-toliendiisocyanate, 1,3-xylenedi Isocyanate, 1,4-xylene diisocyanate, 1,5-naphthalene diisocyanate, 2,4-triene diisocyanate, 2,6-triylene diisocyanate, 1,3-xylene diisocyanate, diphenylmethane-4,4- Diisocyanate, 3-methyl-diphenylmethane diisocyanate, methylene diphenyl diisocyanate (MDI), 1,6-hexanediisocyanate, isophorone diisocyanate, dicyclohexyl methane diisocyanate, hexamethylene diisocyanate, 1,3 Bis (isocyanatomethyl) cyclohexane and 1,4-bis (isocyanatemethyl) cyclohexane And it may be configured to include at least one or more selected from the group consisting of. In addition, it may be configured by further adding a curing agent if necessary. Isocyanates are hydrophobic and water-resistant, and because they impart the effect of lowering the moisture content of the composition including the same and improving the waterproofing performance, it is a preferable compound in further including the waterproofing performance in the impact-resistant polyurethane resin composition. have.

경화제는 이소시아네이트계, 아민계, 아지리딘계, 폴리이소시아네이트계 경화제와 같은 2관능기 이상의 것을 들수 있으며, 이소시아네이트계 경화제를 예시하면 메틸렌디페닐디이소시아네이트, 헥사메틸렌디이소시아네이트, 4,4-다이사이클로헥실메탄디이소시아네이트, 톨루엔디이소시아네이트 등이 있고, 폴리이소시아네이트계를 예시하면 1,4-테트라메틸렌디이소시아네이트, 1,6-헥사메틸렌디이소시아네이트, 4,4'-디이소시아나토디페닐메탄, 자일렌디이소시아네이트, 이소포론디이소시아네이트 등의 3량체로 이루어지는 폴리이소시아네이트 화합물, 또는 상기 폴리이소시아네이트 화합물과 에틸렌글리콜, 1,3-부틸렌글리콜, 1,4-부틸렌글리콜, 폴리옥시에틸렌글리콜, 긴 사슬 고급 알코올 등의 저분자 활성 수소 화합물 등이 반응하여 이루어지는 복수개의 이소시아네이트기 말단을 분자 중에 갖는 화합물을 들 수 있다. 아울러 이소시아네이트에 경화제를 첨가함에 있어서 경화제를 과도하게 투입할 경우 작업자가 의도하지 않은 시간에 경화되거나 목표보다 더욱 경화될 수 있으므로 경화제 투입에 있어서 유의 할 필요가 있다.The curing agent may be a bifunctional group or more, such as an isocyanate, amine, aziridine or polyisocyanate curing agent. Examples of the isocyanate curing agent include methylene diphenyl diisocyanate, hexamethylene diisocyanate and 4,4-dicyclohexyl methane di. Isocyanate, toluene diisocyanate, etc., If polyisocyanate type is illustrated, 1, 4- tetramethylene diisocyanate, 1, 6- hexamethylene diisocyanate, 4, 4'- diisocyanato diphenylmethane, xylene diisocyanate, iso Polyisocyanate compound which consists of trimers, such as a poron diisocyanate, or the said polyisocyanate compound, low molecular weight, such as ethylene glycol, 1, 3- butylene glycol, 1, 4- butylene glycol, polyoxyethylene glycol, long chain higher alcohol A compound formed by reacting an active hydrogen compound or the like The compound which has several isocyanate group terminal in a molecule | numerator is mentioned. In addition, excessive addition of the curing agent in the addition of the curing agent to the isocyanate needs to be careful in the addition of the curing agent because the worker may be cured at an unintentional time or more than the target.

본 발명의 실시예에 따른 방수성 폴리우레탄 수지 조성물은 적어도 1종 이상의 접착부여제를 포함하여 구성될 수 있다. 접착부여제는 하이드록시에틸 아크릴레이트(HEA), 하이드록시프로필 아크릴레이트(HPA), 하이드록시부틸 아크릴레이트(HBA) 및 하이드록시에틸 메타아크릴레이트(2-HEMA)로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 한다. 접착부여제는 수평균분자량이 200-10000인 것을 사용할 수 있으며, 바람직하게는 수평균분자량이 200-3000, 더욱 바람직하게는 300-1000인 것을 사용할 수 있다. 접착부여제는 상술하였던 조성물 A와 화합물 B의 합성을 통해 얻어진 조성물 C에 첨가하여 접착성능을 부여하거나 더욱 강화할 수 있다.Waterproof polyurethane resin composition according to an embodiment of the present invention may comprise at least one or more tackifiers. The tackifier is one selected from the group consisting of hydroxyethyl acrylate (HEA), hydroxypropyl acrylate (HPA), hydroxybutyl acrylate (HBA) and hydroxyethyl methacrylate (2-HEMA). It is characterized by including the above. The tackifier may be one having a number average molecular weight of 200-10000, preferably a number average molecular weight of 200-3000, more preferably 300-1000 can be used. The tackifier may be added to the composition C obtained through the synthesis of the composition A and the compound B described above to impart or further enhance the adhesive performance.

또한, 본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물은 접착력 강화를 위한 아크릴레이트계 접착제 조성물을 더 포함할 수 있다. 일반적으로 접착제에 적용되는 아크릴레이트계 접착제 조성물은 모두 포함될 수 있으며, 구체적으로 이소보닐(메타)아크릴레이트, 사이클로헥실(메타)아크릴레이트, 다이사이클로펜타디닐(메타)아크릴레이트 및 이들의 조합, 아크릴산알킬에스테르계 수지, 스티렌-부타디엔 공중합체, 폴리이소프렌 고무, 폴리오시부틸렌 고무 등의 고무류나 폴리비닐에테르계, 실리콘계, 말레이미드계, 시아노아크릴레이트계 수지, 염화비닐리덴이나 불화비닐리덴 등의 할로겐화 비닐리덴 수지, 그리고 이들과 불소 함유 알킬아크릴레이트 중합체 성분을 포함하는 불소계 (메타)아크릴수지를 예로 들 수 있으며, 이에 한정되는 것은 아니다.In addition, the waterproof polyurethane resin composition according to an embodiment of the present invention may further include an acrylate-based adhesive composition for strengthening the adhesion. In general, the acrylate-based adhesive composition applied to the adhesive may include all, specifically isobornyl (meth) acrylate, cyclohexyl (meth) acrylate, dicyclopentadinyl (meth) acrylate and combinations thereof, acrylic acid Rubbers such as alkyl ester resins, styrene-butadiene copolymers, polyisoprene rubbers and polyoxybutylene rubbers, polyvinyl ethers, silicones, maleimides, cyanoacrylate resins, vinylidene chloride and vinylidene fluoride Examples of the vinylidene halide resin and a fluorine-based (meth) acrylic resin containing these and a fluorine-containing alkyl acrylate polymer component include, but are not limited to.

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물은 하나의 하이드록시기를 포함한 불소 모노올을 더 포함할 수 있다. 추가적으로 포함되는 불소 모노올은 랜덤 공중합체의 사슬 조직 사이에 위치하여 방수 성능을 더욱 향상시키고, 불소 모노올 자체로 표면 에너지가 낮아 소수성을 띄므로 방수 성능이 더욱 향상될 수 있다. Waterproofing polyurethane resin composition according to an embodiment of the present invention may further include a fluorine monool containing one hydroxyl group. Further included fluorine monool is located between the chain structure of the random copolymer to further improve the waterproofing performance, fluorine monool itself has a low surface energy to show hydrophobicity can further improve the waterproofing performance.

불소 모노올은 우레탄 주쇄의 가운데 들어가는 것이 아니라, 폴리올 화합물과 디이소시아네이트 화합물이 우레탄 반응을 하면, 우레탄 화합물의 말단에 엔드 캡핑 방식으로 치환기가 삽입되는 것으로써 불소 모노올의 사용량에 따라 반응기 수 및 조성물 표면의 불소 노출량에 영향을 미칠 수 있다. 불소 모노올은 CF3[CF2]nOH을 포함하는 단량체 또는 중합체로 구성되어 있으며, 분자구조의 한쪽 끝에는 (-OH)인 하이드록시기를 포함할 수 있다.The fluorine monool does not enter the center of the urethane main chain, but when the polyol compound and the diisocyanate compound undergo urethane reaction, a substituent is inserted into the terminal of the urethane compound in an end capping manner. This may affect the amount of fluorine exposure on the surface. The fluorine monool is composed of a monomer or a polymer containing CF 3 [CF 2 ] n OH, and at one end of the molecular structure may include a hydroxyl group (-OH).

불소 모노올을 이용하여 불소화 수지 조성물의 말단에 불소를 도입하는 반응은 예를 들어, 하기와 같은 메커니즘으로 일어날 수 있다.The reaction of introducing fluorine to the terminal of the fluorinated resin composition using fluorine monool may occur, for example, by the following mechanism.

Figure 112016112143104-pat00003
Figure 112016112143104-pat00003

불소 모노올의 추가적인 첨가를 통해 더욱 안정적인 폴리우레탄 수지 조성물을 구성할 수 있으며, 불소 모노올의 분자구조 끝에 하나의 하이드록시기를 포함하고 있으므로 기재에 도포하여 테이프를 구성함에 있어서 기재와의 밀착성을 더욱 향상시키고, 나아가 피착제에 접착시 접착력을 향상시키는 효과가 있다. 불소 모노올은 불소치환된 알킬 알코올으로 퍼플로로알킬 알코올을 포함할 수 있다.Further addition of fluorine monool can be used to construct a more stable polyurethane resin composition, and since it contains one hydroxyl group at the end of the molecular structure of fluorine monool, the adhesion to the substrate is further increased when applying to the substrate to form a tape. There is an effect of improving, and furthermore, adhesion to the adherend. Fluorine monools may include perfluoroalkyl alcohols as fluorine-substituted alkyl alcohols.

또한, 방수성 폴리우레탄 수지 조성물의 두께를 두껍게 구성하였을 시 신율을 향상시키고 외관의 심미적 효과 향상을 위한 투명성 증대 효과를 위하여 투명화 촉진제를 더 포함할 수 있는데, 에폭시 에스테르 (메타)아크릴레이트는 페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르 (메타)아크릴레이트, (메틸페닐)페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르(메타)아크릴레이트, (t-부틸페닐)페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르(메타)아크릴레이트, (에틸헥실)글리시딜에테르메틸(메타)아크릴레이트와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르(메타)아크릴레이트 등의 탄소수가 1-30의 알킬기를 가진 (메타)아크릴레이트를 포함할 수 있으며, 바람직하게는 페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르 (메타)아크릴레이트, (메틸페닐)페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르(메타)아크릴레이트, (t-부틸페닐)페닐글리시딜에테르와 (메타)아크릴산을 반응시킨 단관능 에폭시 에스테르(메타)아크릴레이트의 방향족 에폭시 에스테르 (메타)아크릴레이트가 좋다. 투명화 촉진제를 접착 부여제와 함께 첨가함으로써 인장 파단 시의 신율을 향상시키고, 투명성을 높여주는 효과가 있으며, 더 나아가 표면의 내열성을 증대시킬 수 있고, 방오성 및 발수성을 극대화시키는 이점이 있으며, 투명성도 향상시킨다.In addition, when the thickness of the waterproof polyurethane resin composition is made thick, it may further include a clearing accelerator to improve the elongation and increase the transparency to improve the aesthetic effect of the appearance, the epoxy ester (meth) acrylate is phenylglycid Monofunctional epoxy ester (meth) acrylate which reacted dimethyl ether and (meth) acrylic acid, Monofunctional epoxy ester (meth) acrylate which reacted (methylphenyl) phenylglycidyl ether and (meth) acrylic acid, (t-butyl Monofunctional epoxy ester (meth) acrylate which made phenyl) phenyl glycidyl ether and (meth) acrylic acid react, and monofunctional epoxy which made (ethylhexyl) glycidyl ether methyl (meth) acrylate and (meth) acrylic acid react (Meth) acrylate which has an alkyl group of 1-30 carbon atoms, such as ester (meth) acrylate, is preferable, and is preferable Preferably monofunctional epoxy ester (meth) acrylate which made phenyl glycidyl ether react with (meth) acrylic acid, and monofunctional epoxy ester (meth) acrylate which made (methylphenyl) phenylglycidyl ether react with (meth) acrylic acid The aromatic epoxy ester (meth) acrylate of the monofunctional epoxy ester (meth) acrylate which made (t-butylphenyl) phenylglycidyl ether and (meth) acrylic acid react is preferable. The addition of the clearing accelerator together with the tackifier improves the elongation at break and improves the transparency. Furthermore, the heat resistance of the surface can be increased, and the antifouling property and water repellency can be maximized. Improve.

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물을 구성하기 위한 유기용제는 일반적인 접착제 조성물을 구성하기 위해 사용될 수 있는 유기용제는 모두 포함될 수 있으며, 보다 자세하게는 아세톤, 메탄올, 에탄올, 메틸에틸케톤, 톨루엔, 에틸아세테이트, 부틸아세테이트, 아세톤, 부틸 카르비톨, 부틸 카르비톨 아세테이트, 부틸 셀로솔브, 부틸 셀로솔브 아세테이트 및 테르피네올을 포함하여 구성된 군으로부터 선택된 1종 이상을 포함하여 구성될 수 있다. 용제는 전체 조성물 100 중량부에 대하여 30중량부 미만으로 포함하는 것이 바람직하며, 30중량부 이상의 용제가 포함되면 점성이 낮아져 테이프를 구성하기 위해 기재에 도포시 흘러내릴 우려가 있고, 용제가 휘발하면서 표면에 기포가 형성될 수 있다. 또한, 30 중량부 미만으로 적용할 때 터치 패널의 내충격성을 향상시킬 수 있으며, 표면의 인쇄 단차를 흡수할 수 있으므로 접착제로서 우수한 특성을 가진다. 따라서 용제 양을 과하지 않게 첨가하는 것이 중요하다. 유기용제는 중합 반응시 농도 조절을 위해 첨가되는 화합물이므로 화합물 제조 단계 어느단계나 포함할 수 있다.The organic solvent for forming a waterproof polyurethane resin composition according to an embodiment of the present invention may include all organic solvents that can be used to constitute a general adhesive composition, more specifically, acetone, methanol, ethanol, methyl ethyl ketone It may comprise one or more selected from the group consisting of, toluene, ethyl acetate, butyl acetate, acetone, butyl carbitol, butyl carbitol acetate, butyl cellosolve, butyl cellosolve acetate and terpineol. It is preferable to include the solvent in less than 30 parts by weight with respect to 100 parts by weight of the total composition, and when more than 30 parts by weight of the solvent is included, the viscosity is low, there is a risk of flowing down during application to the substrate to form a tape, while the solvent is volatilized Bubbles may form on the surface. In addition, when applied to less than 30 parts by weight can be improved the impact resistance of the touch panel, and can absorb the printing step of the surface has excellent properties as an adhesive. Therefore, it is important to add a solvent amount not excessively. Since the organic solvent is a compound added for concentration control during the polymerization reaction, the organic solvent may include any step of preparing the compound.

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물은 조성물 전체 100 중량부에 대하여 0.1 내지 10 중량부의 비율로 첨가제를 더 첨가할 수 있으며, 첨가제는 레벨링제, 소포제, 안정화제, 산화방지제, 계면활성제, 자외선 흡수제. 습윤제, 방청제 중 선택되는 적어도 1종 이상을 포함할 수 있다.Waterproofing polyurethane resin composition according to an embodiment of the present invention may further add an additive in a ratio of 0.1 to 10 parts by weight based on 100 parts by weight of the total composition, the additive is a leveling agent, antifoaming agent, stabilizer, antioxidant, interface Active agent, UV absorber. It may include at least one selected from humectants, rust inhibitors.

이 때, 안정화제는 구체적인 예시로 디에틸에탄올아민, 트리헥실아민과 같은 제3아민, 힌더드 아민, 유기 인산염, 힌더드 페놀, 젤라틴, 메틸셀룰롤오스, 히드록시 에틸셀룰로오스, 히드록시프로필셀룰로오스, 카르복시메틸셀룰로오스, 폴리에틸렌글리콜, 폴리옥시에틸렌-폴리옥시프로필렌 블록 공중합체, 폴리아크릴아미드, 폴리아크릴산, 폴리아크릴산염, 알긴산나트륨, 폴리비닐알코올 부분 비누화물 등의 수용성 고분자, 인산삼칼슘, 산화티탄, 탄산칼슘, 이산화규소 중 어느 하나 이상을 포함할 수 있으나, 이에 제한되는 것은 아니다. 또한, 분산 안정화를 위해 첨가될 수 있는 계면활성제는 구체적인 예시로 도데실벤젠술폰산나트륨, 디알킬술포숙신산에스테르나트륨, 라우릴황산나트륨 또는 폴리에틸렌글리콜노닐페닐에테르 중 어느 하나 이상을 포함할 수 있으나, 이에 제한되는 것은 아니다.In this case, as a specific example, the stabilizing agent may be a third amine such as diethylethanolamine or trihexylamine, hindered amine, organic phosphate, hindered phenol, gelatin, methylcellulose, hydroxy ethyl cellulose or hydroxypropyl cellulose. , Water-soluble polymers such as carboxymethyl cellulose, polyethylene glycol, polyoxyethylene-polyoxypropylene block copolymer, polyacrylamide, polyacrylic acid, polyacrylate, sodium alginate, polyvinyl alcohol partial saponified product, tricalcium phosphate, titanium oxide It may include any one or more of calcium carbonate, silicon dioxide, but is not limited thereto. In addition, the surfactant that may be added for dispersion stabilization may include any one or more of sodium dodecylbenzene sulfonate, sodium dialkyl sulfosuccinate ester, sodium lauryl sulfate or polyethylene glycol nonylphenyl ether, but is not limited thereto. It doesn't happen.

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물은 기재의 표면에 도포하여 접착 테이프를 구성할 수 있다. 기재는 폴리에테르술폰, 폴리아크릴레이트, 폴리에테르 이미드, 폴리에틸렌 나프탈레이트, 폴리에틸렌 테레프탈레이트, 폴리페닐렌 설파이드, 폴리아릴레이트, 폴리비닐 클로라이드, 폴리이미드, 폴리카보네이트, 셀룰로오스 트리 아세테이트 및 셀룰로오스 아세테이트 프로피오네이트로 이루어진 군으로부터 적어도 1종 이상을 포함하는 것을 특징으로 한다. 기재의 두께는 50 μm 내지 130μm인 것이 바람직하며, 연성을 가지고 있어 롤 형태로 보관과 작업 및 취급을 용이하게 할 수 있다. 또한 인장강도는 ASTM D638, ASTM D882, ISO 527, KS M3006의 표준 규격 시험 기준 0.3 내지 1.5 Kgf/mm2인 것이 바람직하다. 특히 기재의 두께가 얇을수록 더욱 높은 인장강도를 보유해야 할 필요가 있으나 그 제한은 두지 않는다.Waterproofing polyurethane resin composition according to an embodiment of the present invention can be applied to the surface of the substrate to form an adhesive tape. The substrate is polyethersulfone, polyacrylate, polyether imide, polyethylene naphthalate, polyethylene terephthalate, polyphenylene sulfide, polyarylate, polyvinyl chloride, polyimide, polycarbonate, cellulose tri acetate and cellulose acetate propio And at least one or more from the group consisting of nates. The thickness of the substrate is preferably 50 μm to 130 μm, and has a ductility to facilitate storage, operation and handling in the form of a roll. In addition, the tensile strength is preferably 0.3 to 1.5 Kgf / mm 2 standard test standards of ASTM D638, ASTM D882, ISO 527, KS M3006. In particular, the thinner the thickness of the substrate needs to have a higher tensile strength, but there is no limitation.

그리고, 접착 테이프의 전단 접착강도(접착력)는 ASTM D-1002, ASTM D3163, KS M 3734-2011의 시험규격으로 측정하며, 전단 접착강도는 4 내지 7 Kgf/cm2 일 수 있고, 보다 바람직하게는 5 내지 6 Kgf/cm2 일 수 있다.And, the shear adhesive strength (adhesive strength) of the adhesive tape is measured by the test standard of ASTM D-1002, ASTM D3163, KS M 3734-2011, the shear adhesive strength may be 4 to 7 Kgf / cm 2 , more preferably May be 5 to 6 Kgf / cm 2 .

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물의 제조방법은 한쌍의 하이드록시기(-OH)를 포함하고 있는 조성물 A를 준비하는 단계, 이소시아네이트를 포함하는 화합물 B를 준비하는 단계, 조성물 A에 화합물 B를 첨가하여 200 내지 300rpm으로 혼합하는 단계, 상기 혼합물에 축중합 촉매를 첨가하여 50 내지 85 ℃로 유지하여 2 내지 3시간 중합 반응을 진행하여 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 합성하는 단계, 상기 조성물 C에 접착 부여제를 첨가하여 60 내지 90 ℃로 승온하여 방수성 가진 폴리우레탄 수지 조성물을 구성하는 단계를 포함한다. 또한, 접착 부여제를 첨가할 때 하나의 하이드록시기를 포함한 불소 모노올을 더 포함할 수 있다.Method for producing a waterproof polyurethane resin composition according to an embodiment of the present invention comprises the steps of preparing a composition A containing a pair of hydroxyl groups (-OH), preparing a compound B containing an isocyanate, composition A Adding a compound B to the mixture at 200 to 300 rpm, adding a polycondensation catalyst to the mixture, maintaining the temperature at 50 to 85 ° C., and performing a polymerization reaction for 2 to 3 hours to include a random pair of isocyanate (NCO) functional groups. Synthesizing copolymer composition C, adding a tackifier to the composition C to increase the temperature to 60 to 90 ℃ to form a waterproof polyurethane resin composition. In addition, when adding the tackifier may further include a fluorine monool containing one hydroxyl group.

본 발명의 실시예에 따른 방수성 가진 폴리우레탄 수지 조성물의 제조방법은 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C 100 중량부에 대하여 접착부여제 0.5 내지 15 중량부를 포함하여 구성할 수 있으며, 조성물 C는 조성물 C 100 중량부에 대하여 조성물 A 50 내지 80 중량부, 화합물 B 20 내지 50 중량부 및 축중합촉매 0.1 내지 10 중량부를 합성하여 구성할 수 있다. 상술한바와 같이 조성물 A는 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상을 포함하여 구성할 수 있다.The method for preparing a waterproof polyurethane resin composition according to an embodiment of the present invention may include 0.5 to 15 parts by weight of a tackifier based on 100 parts by weight of a random copolymer composition C including a pair of isocyanate (NCO) functional groups. In addition, composition C may be composed of 50 to 80 parts by weight of composition A, 20 to 50 parts by weight of compound B and 0.1 to 10 parts by weight of polycondensation catalyst based on 100 parts by weight of composition C. As described above, the composition A may comprise at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol.

실시예Example

이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다.Hereinafter, the configuration and operation of the present invention through the preferred embodiment of the present invention will be described in more detail. However, this is presented as a preferred example of the present invention and in no sense can be construed as limiting the present invention.

여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.Details that are not described herein will be omitted since those skilled in the art can sufficiently infer technically.

제조예 1. 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 제조Preparation Example 1 Preparation of Random Copolymer Composition Comprising a Pair of Isocyanate (NCO) Functional Groups

조성물 C 100 중량부를 기준으로 하여, 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상인 조성물 A 50 내지 80 중량부를 준비한다. 조성물 A는 합성에 앞서 충분한 교반이 필요하며, 교반기에 넣어 50 내지 100 rpm으로 교반 할 필요가 있다. 이어서, 화합물 B를 조성물 A에 첨가한다. 화합물 B는 2,4-톨리엔디이소시아네이트, 2,6-톨리엔디이소시아네이트, 1,3-자일렌디이소시아네이트, 1,4-자일렌디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 2,4-트리렌디이소시아네이트, 2,6-트리렌디이소시아네이트, 1,3-크실렌디이소시아네이트, 디페닐메탄-4,4-디이소시아네이트, 3-메틸-디페닐메탄디이소시아네이트, 메틸렌 다이페닐 디이소시아네이트(MDI), 1,6-헥산디이소시아네이트, 이소포론디이소시아네이트, 디사이클로헥실메탄디이소시아네이트, 헥사메틸렌디이소시아네이트, 1,3-비스(이소시아네이토메틸)싸이클로헥산 및 1,4-비스(이소시아네이트메틸)싸이클로헥산으로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하여 구성할 수 있다. 조성물 A를 온도를 조절할 수 있는 교반기에 투입한 후 화합물 B를 첨가한다. 교반속도는 200 내지 300rpm으로 혼합하고 온도는 50 내지 85 ℃로 유지하여 중합 반응을 진행한다. 이때, 반응의 촉진을 위해 축중합 촉매를 더 첨가할 수 있으며, 축중합 촉매를 첨가시 중합 반응 시간은 2 내지 3시간동안 수행한다. 이를 통해 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 형성할 수 있다.Based on 100 parts by weight of composition C, 50 to 80 parts by weight of composition A, which is at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol, is prepared. Composition A needs sufficient agitation prior to synthesis and needs to be stirred at 50-100 rpm in a stirrer. Compound B is then added to composition A. Compound B is 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,3-xylene diisocyanate, 1,4-xylene diisocyanate, 1,5-naphthalene diisocyanate, 2,4-triylene diisocyanate , 2,6-triene diisocyanate, 1,3-xylene diisocyanate, diphenylmethane-4,4-diisocyanate, 3-methyl-diphenylmethane diisocyanate, methylene diphenyl diisocyanate (MDI), 1,6 Hexane diisocyanate, isophorone diisocyanate, dicyclohexyl methane diisocyanate, hexamethylene diisocyanate, 1,3-bis (isocyanatomethyl) cyclohexane and 1,4-bis (isocyanatemethyl) cyclohexane It may comprise at least one or more selected from the group. Compound A is added to a stirrer capable of controlling temperature and then compound B is added. The stirring speed is mixed at 200 to 300rpm and the temperature is maintained at 50 to 85 ℃ proceeds the polymerization reaction. At this time, a condensation polymerization catalyst may be further added to promote the reaction, and when the condensation polymerization catalyst is added, the polymerization reaction time is performed for 2 to 3 hours. This may form a random copolymer composition C comprising a pair of isocyanate (NCO) functional groups.

제조예 2. 방수성 폴리우레탄 아크릴레이트 올리고머의 제조Preparation Example 2 Preparation of Waterproof Polyurethane Acrylate Oligomer

제조예 1에서 얻은 조성물 C에 불소 모노올을 더 포함하여 방수성 폴리우레탄 아크릴레이트 올리고머를 제조할 수 있다. 불소 모노올은 하나의 하이드록시기를 포함하는 것을 특징으로 하며, 불소 모노올은 퍼플로로알킬 알코올을 포함할 수 있다. 중합반응은 온도 60 내지 90 ℃의 환경에서 200 내지 500 rpm 으로 교반하여 합성하여 중합 반응을 진행한다.The composition C obtained in Preparation Example 1 may further include a fluorine monool to prepare a waterproof polyurethane acrylate oligomer. The fluorine monool is characterized by including one hydroxy group, the fluorine monool may comprise perfluoroalkyl alcohol. The polymerization reaction is synthesized by stirring at 200 to 500 rpm in an environment of temperature 60 to 90 ℃ proceeds the polymerization reaction.

제조예 3. 방수성 폴리우레탄 아크릴레이트 접착 조성물의 제조Preparation Example 3 Preparation of Waterproof Polyurethane Acrylate Adhesive Composition

제조예 2 에서 얻은 조성물에 접착부여제를 첨가하여 방수성 폴리우레탄 아크릴레이트 접착 조성물을 제조할 수 있다. 조성물 C 100 중량부에 대하여 접착부여제 0.5 내지 15 중량부를 포함하여 구성한다. 조성물 C와 접착부여제는 교반기에 넣어 200 내지 500 rpm으로 교반하여 합성하며, 온도는 60 내지 90 ℃ 의 환경에서 중합 반응을 진행하여 올리고머를 제조한다. 접착부여제는 하이드록시에틸 아크릴레이트(HEA), 하이드록시프로필 아크릴레이트(HPA), 하이드록시부틸 아크릴레이트(HBA) 및 하이드록시에틸 메타아크릴레이트(2-HEMA)로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다. 이때 제조되는 방수성 폴리우레탄 아크릴레이트의 표면에너지는 1 내지 18 mN/m이 될 수 있다.A tackifier may be added to the composition obtained in Preparation Example 2 to prepare a waterproof polyurethane acrylate adhesive composition. 0.5 to 15 parts by weight of a tackifier based on 100 parts by weight of composition C. Composition C and the tackifier are synthesized by stirring in a stirrer at 200 to 500 rpm, the temperature is carried out a polymerization reaction in an environment of 60 to 90 ℃ to produce an oligomer. The tackifier is one selected from the group consisting of hydroxyethyl acrylate (HEA), hydroxypropyl acrylate (HPA), hydroxybutyl acrylate (HBA) and hydroxyethyl methacrylate (2-HEMA). It may contain the above. In this case, the surface energy of the waterproof polyurethane acrylate may be 1 to 18 mN / m.

제조예 4. 방수성 폴리우레탄 아크릴레이트 접착 조성물의 제조Preparation Example 4 Preparation of Waterproof Polyurethane Acrylate Adhesive Composition

랜덤 공중합체의 구조를 더욱 잘 구현하기 위하여 다른 공정을 더 포함할 수 있다. 스테인레스스틸로 된 고압반응기를 질소로 퍼징하고, 다시 이산화탄소로 퍼징한 후에 조성물 A와 화합물 B 1 mol과 유기용제를 혼합해 주입한다. 여기에 촉매로 디-t-부틸알루미늄 수화물을 0.5 mmol을 주입한 후 이산화탄소를 5기압으로 가압해 채운다, 반응온도를 약 70 내지 80 ℃로 유지하면서 4시간동안 반응을 진행한다. 반응이 완료되면 물로 불순물을 제거하고, 무수마그네슘으로 남은 수분을 제거하여 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 구성한다. 나머지 공정은 제조예 2 또는 제조예 3과 동일한 방법으로 방수성 폴리우레탄 아크릴레이트 접착 조성물을 제조한다.Other processes may be further included in order to better implement the structure of the random copolymer. A high pressure reactor made of stainless steel is purged with nitrogen, and again purged with carbon dioxide, followed by injecting a mixture of Composition A, Compound B, and an organic solvent. 0.5 mmol of di-t-butylaluminum hydrate was added to the catalyst, and carbon dioxide was charged with 5 atm. The reaction was carried out for 4 hours while maintaining the reaction temperature at about 70 to 80 ° C. Upon completion of the reaction, impurities are removed with water and water remaining with anhydrous magnesium is removed to form a random copolymer composition C comprising a pair of isocyanate (NCO) functional groups. The remaining process produces a waterproof polyurethane acrylate adhesive composition in the same manner as in Preparation Example 2 or Preparation Example 3.

제조예 5. 방수성 폴리우레탄 아크릴레이트 접착 조성물을 포함하는 모바일 기기용 접착 테이프의 제조Preparation Example 5 Preparation of Adhesive Tape for Mobile Devices Comprising Waterproof Polyurethane Acrylate Adhesive Composition

제조예 1 내지 4를 통해 얻어낸 방수성 폴리우레탄 아크릴레이트 접착 조성물을 포함하는 접착 테이프는 기재 및 상기 조성물을 포함하여 구성되는 접착층으로 형성된다. 접착층은 기재의 한면 또는 양면에 도포될 수 있으며, 그 구성에 제한을 두지는 않는다.The adhesive tape including the waterproof polyurethane acrylate adhesive composition obtained through Production Examples 1 to 4 is formed of a substrate and an adhesive layer comprising the composition. The adhesive layer may be applied to one side or both sides of the substrate, and the configuration is not limited.

기재는 폴리에테르술폰, 폴리아크릴레이트, 폴리에테르 이미드, 폴리에틸렌 나프탈레이트, 폴리에틸렌 테레프탈레이트, 폴리페닐렌 설파이드, 폴리아릴레이트, 폴리비닐 클로라이드, 폴리이미드, 폴리카보네이트, 셀룰로오스 트리 아세테이트 및 셀룰로오스 아세테이트 프로피오네이트로 이루어진 군으로부터 적어도 1종 이상을 포함하는 것을 특징으로 한다. 기재의 두께는 50μm 내지 130μm인 것이 바람직하며, 연성을 가지고 있어 롤 형태로 보관과 작업 및 취급을 용이하게 할 수 있다. 또한 인장강도는 ASTM D638, ASTM D882, ISO 527, KS M3006의 표준 규격 시험 기준 0.3 내지 1.5 Kgf/mm2인 것이 바람직하며 더욱 바람직하게는 0.7 내지 1.0 Kgf/mm2인 것이 바람직하다. 특히 기재의 두께가 얇을수록 더욱 높은 인장강도를 보유해야 할 필요가 있다. 또한 기재의 종류에 따라 투습정도가 상이하므로 보다 높은 방수성을 확보하기 위해 조직이 치밀하고 투습도가 낮은 기재를 선택 할 필요가 있다.The substrate is polyethersulfone, polyacrylate, polyether imide, polyethylene naphthalate, polyethylene terephthalate, polyphenylene sulfide, polyarylate, polyvinyl chloride, polyimide, polycarbonate, cellulose tri acetate and cellulose acetate propio And at least one or more from the group consisting of nates. It is preferable that the thickness of a base material is 50 micrometers-130 micrometers, and it is ductile and can facilitate storage, operation | work, and handling in roll form. In addition, the tensile strength is preferably 0.3 to 1.5 Kgf / mm2, and more preferably 0.7 to 1.0 Kgf / mm2, based on the standard test standards of ASTM D638, ASTM D882, ISO 527, and KS M3006. In particular, the thinner the substrate, the higher the tensile strength needs to be. In addition, because the degree of moisture permeability is different depending on the type of substrate, it is necessary to select a substrate having a dense structure and a low moisture permeability in order to secure higher waterproofness.

접착 테이프를 제조하는 순서로는, 기재를 준비하는 단계, 기재의 표면에 코로나 처리를 하는 단계, 기재의 표면에 접착층을 구성하는 단계, 접착층이 형성된 기재를 롤 형태로 권취하는 단계로 구성될 수 있으며, 접착층을 기재의 양면에 구성하는 경우에는 한면에 이형필름을 더 포함하여 구성할 수 있다.The order of manufacturing the adhesive tape may include preparing a substrate, performing a corona treatment on the surface of the substrate, forming an adhesive layer on the surface of the substrate, and winding the substrate on which the adhesive layer is formed in a roll form. And, if the adhesive layer is configured on both sides of the substrate can be configured to further include a release film on one side.

실시예 1 내지 3Examples 1 to 3

제조예 1 내지 5를 통해 제조한 접착 테이프의 성능을 검증하기 위해 각기 다른 기재의 두께와 접착층의 두께를 구성하였다. 실시예 1 내지 3은 인장강도는 0.8 Kgf/mm2의 각기 상이한 두께의 기재를 사용하였다. 실시예 1은 50μm의 PET, 실시예 2는 100μm의 PET 및 실시예 3은 200μm의 PET를 사용하였으며, 접착층은 양면으로 각각 10μm의 두께로 구성하였다.In order to verify the performance of the adhesive tapes prepared in Preparation Examples 1 to 5, the thicknesses of the different substrates and the thickness of the adhesive layer were configured. In Examples 1 to 3, substrates of different thicknesses having a tensile strength of 0.8 Kgf / mm 2 were used. In Example 1, 50 μm PET, Example 2 100 μm PET, and Example 3 200 μm PET were used, and the adhesive layers were each composed of 10 μm thick on both sides.

실시예 4 내지 6Examples 4-6

실시예 4 내지 6은 상이한 두께의 접착층의 두께를 구성하여 접착 테이프의 성능을 검증하였다. 기재의 두께는 120μm 이며 인장강도 0.8 Kgf/mm2의 PET를 사용하였으며, 실시예 4는 접착층의 두께를 10μm, 실시예 5는 접착층의 두께를 30μm, 실시예 6은 접착층의 두께를 50μm로 구성하였다.Examples 4 to 6 configured the thicknesses of the adhesive layers of different thicknesses to verify the performance of the adhesive tapes. The thickness of the substrate is 120μm and the tensile strength of 0.8 Kgf / mm 2 PET was used, Example 4 is the thickness of the adhesive layer 10μm, Example 5 is the thickness of the adhesive layer 30μm, Example 6 is composed of the adhesive layer thickness of 50μm It was.

실시예 7 내지 9Examples 7-9

실시예 7 내지 9는 상이한 종류의 기재를 사용하여 접착 테이프의 성능을 검증하였다. 기재의 종류에 따라 상이한 투습도를 가지고 있기 때문에 다양한 기재를 선택하여 확인할 필요가 있다. 실시예 7은 100μm의 폴리에틸렌 테레프탈레이트(PET) 필름, 실시예 8은 100μm의 폴리에틸렌 나프탈레이트(PEN) 필름, 실시예 9는 100μm의 폴리비닐 클로라이드(PVC) 필름을 이용하였으며, 접착층의 두께는 20μm로 구성하였다. Examples 7-9 validated the performance of adhesive tapes using different kinds of substrates. Since it has different moisture permeability according to the kind of base material, it is necessary to select and confirm various base materials. Example 7 used a 100 μm polyethylene terephthalate (PET) film, Example 8 used a 100 μm polyethylene naphthalate (PEN) film, and Example 9 used a 100 μm polyvinyl chloride (PVC) film, and the adhesive layer had a thickness of 20 μm. It consisted of.

비교예 1 내지 5Comparative Examples 1 to 5

비교예 1 내지 5는 시판하고 있는 모바일 기기용 양면 테이프를 사용하였으며, 비교예 1은 미국 3M사의 150μm 두께를 가지는 방수 기기에 사용하는 방수 전용 양면 테이프, 비교예 2는 미국 3M사의 250μm 두께를 가지는 양면 테이프, 비교예 3은 한국 H사의 220μm 두께를 가지는 양면 테이프, 비교예 4는 한국 H사의 300μm 두께를 가지는 양면 테이프 및 비교예 5는 일본 H사의 210μm 두께를 가지는 양면 테이프를 비교예로 하여 성능을 비교하였다. 비교예 1이 현재 가장 좋은 성능을 보이면서 가장 얇은 두께를 가지는 양면 테이프이며, 비교예 2 내지 5 대비 약 2배 이상의 가격으로 시판되고 있다.Comparative Examples 1 to 5 used commercially available double-sided tape for mobile devices, Comparative Example 1 is a waterproof double-sided tape used in a waterproof device having a 150μm thickness of 3M of the United States, Comparative Example 2 has a 250μm thickness of 3M of the United States Double-sided tape, Comparative Example 3 is a double-sided tape having a thickness of 220μm of Korea H Company, Comparative Example 4 is a double-sided tape having a 300μm thickness of Korea H Company, and Comparative Example 5 is a double-sided tape having a 210μm thickness of Japan H Company as a comparative example Was compared. Comparative Example 1 is a double-sided tape having the thinnest thickness while showing the best performance at present, and is commercially available at about twice the price of Comparative Examples 2 to 5.

1. 투습도 측정1. Water vapor permeability measurement

실시예 1 내지 9 및 비교예 1 내지 5를 준비하여 습도 90%의 환경에서 ASTM D1653 표준에 따라 투습율을 측정한 후 그 결과를 하기 표 1에 나타내었다. 투습율의 단위는 g/m2day이다.Examples 1 to 9 and Comparative Examples 1 to 5 were prepared to measure the moisture permeability according to the ASTM D1653 standard in an environment of humidity of 90% and the results are shown in Table 1 below. The unit of moisture permeability is g / m 2 day.

2. 인장강도 측정2. Tensile strength measurement

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 ASTM D882의 방법에 따라 폭 1.0mm, 길이 15cm로 준비하여 일정한 속도로 시편을 상하로 잡아당겨 파단시켰을 때의 최대 힘을 측정하여 그 결과를 하기 표 1에 나타내었다.Examples 1 to 9 and Comparative Examples 1 to 5 were prepared and prepared in a width of 1.0 mm and a length of 15 cm according to the method of ASTM D882, and the maximum force when the specimen was pulled up and down at a constant speed and broken was measured. It is shown in Table 1 below.

3. 전단접착강도3. Shear adhesion strength

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 유리 기판에 접착시키고 30분 후 시편을 길이 15 Cm, 폭 1 Cm x 1 Cm로 제단하여 ASTM D1002에 따라 접착력(박리강도)을 측정하여 그 결과를 하기 표 1에 나타내었다.Examples 1 to 9 and Comparative Examples 1 to 5 were prepared, bonded to a glass substrate, and after 30 minutes, the specimens were cut to a length of 15 Cm and a width of 1 Cm x 1 Cm to measure adhesion (peel strength) according to ASTM D1002. The results are shown in Table 1 below.

4. 유지력4. Holding force

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 ASTM D-3654 규격에 따라 시험편을 2.5 Cm x 2.5 Xm의 접착 면적으로 부착한 후 하중을 걸고 테이프가 탈착되기까지 걸리는 시간을 측정하여 그 결과를 하기 표 1에 나타내었다.Prepare Examples 1 to 9 and Comparative Examples 1 to 5 and attach the test piece with an adhesive area of 2.5 Cm x 2.5 Xm according to ASTM D-3654 standard, and then measure the time taken to apply the load and detach the tape. It is shown in Table 1 below.

5. 내열성5. Heat resistance

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 ASTM D4498 규격에 따라 시험편을 2.5 Cm x 2.5 Cm의 접착 면적으로 부착한 후, 하중을 걸고 온도를 상승하였을 시 최종 탈착되는 온도를 측정하여 그 결과를 하기 표 1에 나타내었다.Prepare Examples 1 to 9 and Comparative Examples 1 to 5 and attach the test piece with an adhesive area of 2.5 Cm x 2.5 Cm according to ASTM D4498 standard, and then measure the final desorption temperature when the temperature is raised under load. The results are shown in Table 1 below.

6. 접착력6. Adhesion

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 ASTM D-3330 규격에 따라 시험편을 2.5 Cm 폭의 크기로 SUS에 붙여 UTM 기기를 이용하여 강제적으로 90도 박리하였을 시 측정되는 힘을 측정하여 그 결과를 하기 표 1에 나타내었다. 힘의 단위는 힘/폭(Kgf/in)이다.Prepare Examples 1 to 9 and Comparative Examples 1 to 5 and measure the force measured when the test piece was forcibly peeled 90 degrees using a UTM device in accordance with ASTM D-3330 standard by attaching the specimen to the SUS with a size of 2.5 cm width The results are shown in Table 1 below. The unit of force is force / width (Kgf / in).

7. 권취시험7. Winding test

실시예 1 내지 9 및 비교예 1 내지 5를 준비하고 지름 2 Cm의 봉에 일정 속도로 권취하여 권취의 용이함을 관능검사 하였다. 시험 대상은 테이프의 권취를 5년 이상 수행한 전문가 5인을 통해 평가하였으며, 1이 가장 용이하고 5가 가장 용이하지 않다로 하여 점수화 하였다.Examples 1 to 9 and Comparative Examples 1 to 5 were prepared and wound on a rod of 2 cm in diameter at a constant speed to make sensory inspection easy. The test subjects were evaluated by five experts who had rolled up the tape for more than five years, and scored as 1 being the easiest and 5 being the least.

[표 1]TABLE 1

Figure 112016112143104-pat00004
Figure 112016112143104-pat00004

먼저 투습도와 관련하여, 실시예 1 내지 9는 비교예 1 내지 5에 비해 실시예 1을 제외한 나머지 실시예들의 결과가 비교예 1 내지 5 대비 우수하다. 보다 구체적으로는 실시예 1의 기재의 두께가 다른 실시예들 대비 두께가 얇고 접착층이 얇게 구성되어 있으므로 전체적인 테이프의 총 두께 역시 얇게 구성되어 있다. 특히, 필름의 투습도는 필름의 두께와 반비례하므로 이를 고려 할 필요가 있다. 투습도가 낮을수록 더욱 방수가 잘 되는 구조를 구현하므로 기재의 두께, 종류 및 접착??의 두께를 고려하여 테이프의 두께를 결정할 필요가 있다. 먼저, 실시예 1 내지 3의 결과를 살펴보면 PET 필름의 두께가 두꺼워질수록 투습도가 낮아짐을 확인할 수 있다. 100μm 두께의 PET 필름은 6 내지 7 g/m2day의 투습도를 가지며, 두께가 2배 증가한다고 하여 투습도가 그 절반이 되는 것은 아니다. 접착층의 두께를 10 μm로 양면으로 구성하였을 시 투습도는 약 2 g/m2day 정도 낮아진 결과를 얻을 수 있었다. 실시예 4 내지 6의 결과를 살펴보면 PET의 두께는 80μm로 약 8 내지 9 g/m2day의 투습도를 가진다. 접착층의 두께가 두꺼워짐에 따라 투습도가 상당히 낮아짐을 확인할 수 있었는데, 특히 접착층의 두께가 50μm로 구성되게 되면 2 g/m2day 수준의 결과를 얻을 수 있었다. 이어서 실시예 7 내지 9는 동일한 두께의 서로 상이한 재질의 필름을 사용하였는데, 100 μm 두께의 PET 필름은 6 내지 7 g/m2day의 투습도를 가지며, 동일한 두께의 PEN 필름은 2 내지 3 g/m2day, PVC 필름은 15 내지 16 g/m2day의 투습도를 가진다. 가장 좋은 결과를 보이는 기재는 PEN 필름이나, 가격이 비싸고 단단하여 취급이 어렵기 때문에 완전 방수를 필요로 하는 구조에 적용 할 필요가 있다. First, in relation to the moisture permeability, Examples 1 to 9 are superior to Comparative Examples 1 to 5 in comparison with Comparative Examples 1 to 5, except for Example 1. More specifically, since the thickness of the substrate of Example 1 is thinner than other embodiments and the adhesive layer is thin, the total thickness of the entire tape is also thin. In particular, the moisture permeability of the film is inversely proportional to the thickness of the film it is necessary to consider this. The lower the moisture permeability, the more water-proof structure is realized, so it is necessary to determine the thickness of the tape in consideration of the thickness, type, and thickness of the adhesive. First, looking at the results of Examples 1 to 3 it can be seen that the thicker the PET film, the lower the moisture permeability. The 100 μm-thick PET film has a water vapor transmission rate of 6 to 7 g / m 2 day, and the increase in thickness is not half that of the PET film. When the adhesive layer had a thickness of 10 μm on both sides, the moisture permeability was reduced by about 2 g / m 2 day. Looking at the results of Examples 4 to 6, the thickness of PET has a moisture permeability of about 8 to 9 g / m 2 day to 80μm. As the thickness of the adhesive layer became thick, it was confirmed that the moisture permeability was considerably lowered. Particularly, when the thickness of the adhesive layer consisted of 50 μm, a result of 2 g / m 2 day was obtained. Subsequently, Examples 7 to 9 used films of different materials of the same thickness, 100 μm thick PET film has a moisture permeability of 6 to 7 g / m 2 day, PEN film of the same thickness 2 to 3 g / m 2 day, The PVC film has a water vapor transmission rate of 15 to 16 g / m 2 day. The best results are PEN films, but because they are expensive and hard to handle, they need to be applied to structures that require complete waterproofing.

이어서, 인장강도는 기재의 두께와 소재의 종류에 의존한다. 하지만 접착층이 두꺼워질수록 인장강도가 소폭 향상되는 것을 확인할 수 있지만, 그 효과가 오차범위 내에서 형성되므로 인장강도를 향상시키기 위해 접착층을 일부러 두껍게 형성 할 필요는 없다.The tensile strength then depends on the thickness of the substrate and the type of material. However, as the adhesive layer becomes thicker, it can be seen that the tensile strength is slightly improved. However, since the effect is formed within the error range, it is not necessary to deliberately thicken the adhesive layer to improve the tensile strength.

이어서, 전단접착강도는 접착층의 두께에 비례하며, 기재의 두께나 기재의 인장강도 변화에 크게 영향을 미치지는 않음을 확인할 수 있다.Next, the shear adhesion strength is proportional to the thickness of the adhesive layer, it can be seen that does not significantly affect the thickness of the substrate or the change in tensile strength of the substrate.

이어서, 접착 유지력은 기재의 두께가 얇을수록 오래 유지되며, 접착층의 두께가 얇을수록 오래 유지함을 확인할 수 있다. 이는 테이프의 무게에 반비례하며, 접착층이 두껍게 구성되면 접착층 자체가 뜯어지면서 유지력이 약화되는 것을 확인할 수 있었다. 하지만 다른 비교예와 대조하였을 때 최소 2배 이상의 높은 유지력을 형성하고 있으며, 가장 성능이 좋은 비교예 1 대비 거의 대등한 결과를 얻을 수 있었다.Subsequently, the adhesion holding force is maintained longer as the thickness of the substrate is thin, and the longer the thickness is maintained as the thickness of the adhesive layer is thinner. This was inversely proportional to the weight of the tape, and when the adhesive layer was thick, the adhesive layer itself was torn off and the holding force was weakened. However, when compared with other comparative examples, at least two times higher holding force was formed, and almost the same result as in Comparative Example 1 having the best performance was obtained.

이어서, 내열성은 비교예 대비 약 20도 높은 내열성을 얻을 수 있었으나, 인장강도가 약한 기재를 이용한 실시예 7의 경우 온도가 높아짐에 따라 기재가 손상이 발생하는 것을 확인할 수 있었다.Subsequently, the heat resistance was about 20 degrees higher heat resistance than the comparative example, but in Example 7 using a substrate with a weak tensile strength it was confirmed that the substrate is damaged as the temperature increases.

접착력은 실시예 7의 경우 접착력 대비 기재의 인장강도가 낮아 기재가 먼저 파손되어 측정이 불가하였으며, 그 외 나머지 실시예는 비교예 대비 동등하거나 그 이상의 결과를 얻을 수 있었다.In Example 7, the adhesive strength was lower because the tensile strength of the substrate was lower than that of the adhesive, and thus the substrate was first broken, and thus the measurement was not possible. The other examples were equivalent to or greater than the comparative example.

권취시험은 접착층의 두께, 기재의 두께 및 기재의 인장강도에 영향을 받는 것으로 확인할 수 있었으며, 두께 120μm 내지 140μm의 테이프가 권취시 작업자의 용이함을 보였다. 또한, PET, PVC 필름은 강성이 낮아 권취에 용이함을 보인 반면, PEN 필름은 권취에 불편함을 느꼈다.The winding test was confirmed to be affected by the thickness of the adhesive layer, the thickness of the substrate and the tensile strength of the substrate, and showed that the 120-140 μm-thick tape facilitated the operator during the winding. In addition, PET and PVC films showed low stiffness and showed ease of winding, whereas PEN films felt uncomfortable winding.

실시예 1 내지 9를 요약하면 접착층의 두께는 10μm 내지 50μm을 구성하는 것이 바람직하나, 두께가 얇은 박형 기재를 사용하게 될 때에는 접착층의 두께를 보다 두껍게 형성함이 바람직하다. 기재의 두께는 70μm 내지 200μm이 될 수 있으나, 200μm의 경우 그 두께가 두꺼워 일부 결과로 좋지 않은 결과를 얻었다. 따라서 실시예에 제시되지는 않았으나 130μm 두께의 기재를 사용하더라도 충분히 만족할만한 결과를 얻을 수 있다는 것을 해당 분야에 대해 통상의 지식을 가지고 있는 기술자라면 충분히 이를 인지할 수 있을 것이다. 인장강도의 경우 1.5Kgf/cm2의 경우 다소 낮은 결과를 얻었으나 0.7 내지 1.5 Kgf/cm2의 결과가 크게 상이한 차이를 보이지는 않았으며 비교예 1 내지 5와 비교시 충분히 만족할만한 효과를 보이기 때문에, 1.5 Kgf/cm2보다는 다소 낮은 인장강도를 가지는 기재를 사용함이 바람직하다. 보다 자세하게는 기재의 인장강도는 0.7 내지 1.0 Kgf/cm2의 인장강도를 가지는 기재를 사용함이 바람직하다. 하지만 높은 방수를 필요로 하는 모바일 기기에 적용하기 위해 PEN 필름을 사용 할 경우, 인장강도나 권취성을 고려하지 않고 적용 할 필요가 있다.Summarizing Examples 1 to 9, the thickness of the adhesive layer preferably constitutes 10 μm to 50 μm, but when using a thin substrate having a thin thickness, it is preferable to form a thicker adhesive layer. The thickness of the substrate may be from 70 μm to 200 μm, but in the case of 200 μm, the thickness thereof is thick, resulting in some poor results. Therefore, although not shown in the examples, it will be appreciated by those skilled in the art that even if the substrate having a thickness of 130 μm is sufficiently satisfactory, a person having ordinary knowledge in the art will be aware of this. In the case of tensile strength, 1.5Kgf / cm 2 resulted in somewhat lower results, but the results of 0.7 to 1.5 Kgf / cm 2 did not show a significant difference, and the results were sufficiently satisfactory when compared with Comparative Examples 1 to 5. For example, it is preferable to use a substrate having a tensile strength somewhat lower than 1.5 Kgf / cm 2 . More specifically, the tensile strength of the substrate is preferably used a substrate having a tensile strength of 0.7 to 1.0 Kgf / cm 2 . However, when using PEN film for mobile devices requiring high waterproofing, it is necessary to apply it without considering tensile strength or winding property.

또한, 본 발명의 실시예에 따른 모바일 기기용 접착 테이프는 양면 테이프 형태로 구성함에 있어서 두께가 90μm 내지 최대 250μm로 구성할 수 있으므로 사용자의 요구에 맞추어 다양한 두께를 구성하여 필요한 요구 조건에 합당하는 접착 테이프를 제공함이 용이하다.In addition, since the adhesive tape for a mobile device according to an embodiment of the present invention can be configured in the form of a double-sided tape, the thickness can be configured to 90μm up to 250μm, the adhesive to meet the necessary requirements by configuring a variety of thickness to meet the needs of the user It is easy to provide a tape.

더불어, 제조예 1 내지 5를 참조하면 본 발명에 따른 방수성을 가진 폴리우레탄 수지 조성물의 제조 단계는 제조를 위한 조건이 단순하게 구성되어 있기 때문에 생산 속도가 빠르고 대량생산에 용이하다는 특징이 있다. 따라서 제조원가를 절감할 수 있기 때문에 In addition, referring to Preparation Examples 1 to 5, the manufacturing step of the waterproof polyurethane resin composition according to the present invention is characterized by the fact that the production speed is fast and easy for mass production because the conditions for the manufacture are simply configured. Therefore, manufacturing cost can be reduced

8. 제품 방수성능 테스트8. Product waterproof performance test

테이프의 성능을 검증하기 위해 제품 샘플을 구성하여 방수성능을 테스트 할 필요가 있다. 시험 방법으로는 IEC 표준을 적용할 수 있다. 보다 상세하게는 IEC 529, IEC 34-5(IEC 60034-5) 방수 시험 규격에 따라 조립 지그에 윈도우를 올린다. 샘플에 침수라벨을 부착하고, 스펀지를 부착하여 실시예 및 비교예를 위치한다. 그리고 반대면에 또다른 윈도우를 위치한 후 샘플에 압력을 가하여 완벽하게 부착시켜 상온에서 72시간동안 에이징 시킨다. 에이징 된 샘플은 150g, 35cm 높이에서 Dupont Test기를 이용하여 1회 충격을 주고, 트위스트 지그로 샘플 한쪽을 고정시킨 후 손으로 잡고 좌/우 3Kgf의 힘으로 트위스트 시킨 후 침수용 지그에 샘플을 넣는다. 이후 샘플이 장착된 침수 지그를 침수 수조에 넣어 1m 깊이에서 30분동안 방치한 후 침수라벨을 확인하여 침수여부를 확인한다. 이후 결과를 아래 [표 2] 에 도시한다.To verify the performance of the tape, it is necessary to test the waterproof performance by constructing a product sample. As a test method, the IEC standard can be applied. More specifically, the window is mounted on the assembly jig according to IEC 529, IEC 34-5 (IEC 60034-5) waterproof test specification. Immersion labels are attached to the samples, and sponges are attached to position the examples and the comparative examples. After placing another window on the opposite side, the sample is pressurized and completely attached and aged at room temperature for 72 hours. Aged sample is shocked once using Dupont Tester at 150g and 35cm height. After fixing one side of the sample with a twist jig, hold it by hand and twist it with the force of 3Kgf of left / right and put the sample in the immersion jig. Thereafter, the immersion jig equipped with the sample is placed in the immersion tank and left for 30 minutes at a depth of 1 m. Then, the immersion label is checked to check whether the immersion is performed. The results are then shown in Table 2 below.

[표 2]TABLE 2

Figure 112016112143104-pat00005
Figure 112016112143104-pat00005

IPX 방수등급을 요약하면 아래 표 3과 같다.The summary of IPX waterproof rating is shown in Table 3 below.

[표 3] TABLE 3

Figure 112016112143104-pat00006
Figure 112016112143104-pat00006

IPX 7 및 IPX 8은 통상적으로 완전 방수이며, IPX 4 내지 IPX 6은 일반적인 방수, IPX 2 내지 IPX 3은 생활방수 수준으로 볼 수 있다. 따라서 본 발명의 실시예에 따른 방수 폴리우레탄 수지 조성물 및 이를 이용한 모바일 기기용 접착 테이프는 IPX 6 내지 8을 만족하므로 방수를 제대로 구현하고 있으며, 특히 기재와 접착층의 제어를 통해 IPX 7 및 IPX 8을 구현할 수 있으므로 비교예 대비 우위한 결과를 얻어낼 수 있다.IPX 7 and IPX 8 are typically fully waterproof, IPX 4 to IPX 6 are generally waterproof, and IPX 2 to IPX 3 can be seen as waterproof. Therefore, the waterproof polyurethane resin composition and the adhesive tape for a mobile device using the same according to the embodiment of the present invention satisfy IPX 6 to 8, so that the waterproof is properly implemented, and in particular, IPX 7 and IPX 8 are controlled by controlling the substrate and the adhesive layer. Because it can be implemented, the result is superior to the comparative example.

이상에서 본 발명이 구체적인 구성요소 등과 같은 특정 사항들과 한정된 실시예 및 도면에 의해 설명되었으나, 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명이 상기 실시예들에 한정되는 것은 아니며, 본 발명이 속하는 기술분야에서 통상적인 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형을 꾀할 수 있다.Although the present invention has been described by specific embodiments such as specific components and the like, but the embodiments and the drawings are provided to assist in a more general understanding of the present invention, the present invention is not limited to the above embodiments. For those skilled in the art, various modifications and variations can be made from these descriptions.

따라서, 본 발명의 사상은 상기 설명된 실시예에 국한되어 정해져서는 아니 되며, 후술하는 특허청구 범위뿐만 아니라 이 특허청구범위와 균등하게 또는 등가적으로 변형된 모든 것들은 본 발명의 사상의 범주에 속한다고 할 것이다.Accordingly, the spirit of the present invention should not be limited to the embodiments described above, and all of the equivalents or equivalents of the claims, as well as the appended claims, fall within the scope of the spirit of the present invention. I will say.

Claims (11)

한쌍의 하이드록시기(-OH)를 포함하며, 수첨 폴리부타디엔 다이올, 폴리디메틸실록산 다이올, 불소 다이올, 폴리프로필렌글리콜 및 폴리에틸렌글리콜으로 이루어진 군으로부터 선택된 적어도 2종 이상을 포함하는 조성물 A를 준비하는 단계;
상기 조성물 A에 이소시아네이트를 포함하는 화합물 B를 첨가하여 한쌍의 이소시아네이트(NCO) 작용기를 포함하는 랜덤 공중합체 조성물 C를 제조하는 단계;
상기 조성물 C에 하나의 하이드록시기를 포함한 불소 모노올을 첨가하여 방수성 폴리우레탄 아크릴레이트 올리고머를 제조하는 단계; 및
방수성 폴리우레탄 아크릴레이트 올리고머에 적어도 1종 이상의 접착부여제를 혼합하여 폴리우레탄 아크릴레이트 접착 조성물을 제조하는 단계를 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.A composition comprising a pair of hydroxyl groups (-OH) and comprising at least two or more selected from the group consisting of hydrogenated polybutadiene diol, polydimethylsiloxane diol, fluorine diol, polypropylene glycol and polyethylene glycol Preparing;
Adding a compound B including an isocyanate to the composition A to prepare a random copolymer composition C comprising a pair of isocyanate (NCO) functional groups;
Preparing a waterproof polyurethane acrylate oligomer by adding fluorine monool including one hydroxyl group to the composition C; And
A method for producing a waterproof polyurethane resin composition comprising the step of mixing the at least one adhesive adjuvant to a waterproof polyurethane acrylate oligomer to prepare a polyurethane acrylate adhesive composition. 제1항에 있어서,
상기 랜덤 공중합체 조성물 C를 제조하는 단계는,
상기 조성물 C 100 중량부를 기준으로 상기 조성물 A 50 내지 80 중량부를 준비하는 단계;
상기 조성물 A를 교반기에 넣어 50 내지 100 rpm으로 교반하는 단계;
상기 조성물 C 100 중량부를 기준으로 상기 화합물 B 20 내지 50 중량부를 상기 교반된 조성물 A에 첨가하는 단계; 및
상기 화합물 B가 첨가된 조성물 A에 축중합 촉매를 첨가하여 교반속도 200 내지 300 rpm 및 온도 50 내지 85 ℃ 의 환경에서 중합 반응을 하는 단계;를 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
Preparing the random copolymer composition C,
Preparing 50 to 80 parts by weight of the composition A based on 100 parts by weight of the composition C;
Putting the composition A in a stirrer and stirring at 50 to 100 rpm;
Adding 20 to 50 parts by weight of the compound B to the stirred composition A based on 100 parts by weight of the composition C; And
Adding a polycondensation catalyst to the composition A to which the compound B is added to perform a polymerization reaction in an environment having a stirring speed of 200 to 300 rpm and a temperature of 50 to 85 ° C .; Manufacturing method.
제 2항에 있어서,
상기 축중합 촉매는 2-메틸트라이에틸렌다이아마이드, 1,4-디아자바이싸이클로[2,2,2]옥탄, 비스(2-디메틸아미노에틸)에테르, 트리메틸아미노에틸에탄올아민, N,N,N1,N1,N2-펜타메틸디에틸렌트리아민, N,N1-디메틸에탄올아민, 디메틸아미노프로필아민, N-에틸모르폴린, N,N-디메틸아미노에틸모르폴린, N,N-디메틸싸이클로헥실아민, 2-메틸-2-아자노보네인 을 포함하는 3차 아민, 4차 암모늄과 알카리 금속의 카복시산 염을 포함하는 비양성자성 염 및 구리 나프티네이트, 코발트 나프티네이트, 아연 나프테이트, n-다이부틸틴디라우레이트, 트라이스틸아민, 디부틸틴디아세테이트, 디부틸틴디머캅타이드를 포함하는 유기금속화합물로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 2,
The polycondensation catalyst is 2-methyltriethylenediamide, 1,4-diazabicyclo [2,2,2] octane, bis (2-dimethylaminoethyl) ether, trimethylaminoethylethanolamine, N, N, N 1 , N 1 , N 2 -pentamethyldiethylenetriamine, N, N 1 -dimethylethanolamine, dimethylaminopropylamine, N-ethylmorpholine, N, N-dimethylaminoethylmorpholine, N, N-dimethyl Cyclohexylamine, tertiary amines containing 2-methyl-2-azanobonane, aprotic salts including carboxylic acid salts of quaternary ammonium and alkali metals and copper naphthenates, cobalt naphthenates, zinc naphates and at least one selected from the group consisting of n-dibutyl tin dilaurate, tristilamine, dibutyl tin diacetate, and dibutyl tin dimercaptide, and an organometallic compound. Agent of resin composition Way.
제1항에 있어서,
상기 이소시아네이트 화합물은,
2,4-톨리엔디이소시아네이트, 2,6-톨리엔디이소시아네이트, 1,3-자일렌디이소시아네이트, 1,4-자일렌디이소시아네이트, 1,5-나프탈렌디이소시아네이트, 2,4-트리렌디이소시아네이트, 2,6-트리렌디이소시아네이트, 1,3-크실렌디이소시아네이트, 디페닐메탄-4,4-디이소시아네이트, 3-메틸-디페닐메탄디이소시아네이트, 메틸렌 다이페닐 디이소시아네이트(MDI), 1,6-헥산디이소시아네이트, 이소포론디이소시아네이트, 디사이클로헥실메탄디이소시아네이트, 헥사메틸렌디이소시아네이트, 1,3-비스(이소시아네이토메틸)싸이클로헥산 및 1,4-비스(이소시아네이트메틸)싸이클로헥산으로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
The isocyanate compound,
2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 1,3-xylene diisocyanate, 1,4-xylene diisocyanate, 1,5-naphthalene diisocyanate, 2,4-triylene diisocyanate, 2, 6-triene diisocyanate, 1,3-xylene diisocyanate, diphenylmethane-4,4-diisocyanate, 3-methyl-diphenylmethane diisocyanate, methylene diphenyl diisocyanate (MDI), 1,6-hexanedi Isocyanate, isophorone diisocyanate, dicyclohexyl methane diisocyanate, hexamethylene diisocyanate, 1,3-bis (isocyanatomethyl) cyclohexane and 1,4-bis (isocyanatemethyl) cyclohexane A method for producing a polyurethane resin composition having water resistance, characterized in that it comprises at least one or more.
제1항에 있어서,
상기 접착부여제는 하이드록시에틸 아크릴레이트(HEA), 하이드록시프로필 아크릴레이트(HPA), 하이드록시부틸 아크릴레이트(HBA) 및 하이드록시에틸 메타아크릴레이트(2-HEMA)로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
The tackifier is selected from the group consisting of hydroxyethyl acrylate (HEA), hydroxypropyl acrylate (HPA), hydroxybutyl acrylate (HBA) and hydroxyethyl methacrylate (2-HEMA). A method for producing a polyurethane resin composition having water resistance, characterized in that it comprises at least a species.
제1항에 있어서,
상기 불소 다이올은,
2,3,4,5,6-펜타플루오로벤질 알코올, 4-(트리플루오로메틸)벤질 알코올, [3,5-다이(트리플루오로메틸)페닐]메탄올, 1,1,1,3,3,3-헥사플루오로-2-프로판올, 1,1,1,3,3,3-헥사플루오로-2-메틸이소프로판올, 헥사플루오로-2-(p-톨일)이소프로판올, 4,5,5,6,6,6-헥사플루오로-4-(트라이메틸)-1-헥산올, 4,4,5,5,5-펜타플루오로펜탄올, 펜타플루오로프로피온알데하이드, 1H,1H,5H-옥타플루오로-1-펜탄올 및 펜타플루오로부탄-2-올로 이루어진 군으로부터 선택된 적어도 1종 이상을 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
The fluorine diol,
2,3,4,5,6-pentafluorobenzyl alcohol, 4- (trifluoromethyl) benzyl alcohol, [3,5-di (trifluoromethyl) phenyl] methanol, 1,1,1,3 , 3,3-hexafluoro-2-propanol, 1,1,1,3,3,3-hexafluoro-2-methylisopropanol, hexafluoro-2- (p-tolyl) isopropanol, 4,5 , 5,6,6,6-hexafluoro-4- (trimethyl) -1-hexanol, 4,4,5,5,5-pentafluoropentanol, pentafluoropropionaldehyde, 1H, 1H A method for producing a waterproof polyurethane resin composition comprising at least one selected from the group consisting of 5H-octafluoro-1-pentanol and pentafluorobutan-2-ol.
제1항에 있어서,
방수성 폴리우레탄 아크릴레이트 올리고머를 제조하는 단계는 온도 60 내지 90 ℃의 환경에서 200 내지 500 rpm 으로 교반하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
The step of preparing a waterproof polyurethane acrylate oligomer is a method for producing a waterproof polyurethane resin composition, characterized in that the stirring at 200 to 500 rpm in an environment of temperature 60 to 90 ℃.
제1항에 있어서,
상기 폴리우레탄 아크릴레이트 접착 조성물을 제조하는 단계는,
상기 방수성 폴리우레탄 아크릴레이트 올리고머 100 중량부에 대하여 상기 접착부여제 0.5 내지 15 중량부를 포함하는 단계; 및
상기 단계에서 생성된 조성물을 교반기에 넣어 60 내지 90 ℃의 환경에서 200 내지 500 rpm으로 교반하여 중합 반응을 진행하는 단계를 포함하는 것을 특징으로 하는 방수성을 가진 폴리우레탄 수지 조성물의 제조방법.
The method of claim 1,
Preparing the polyurethane acrylate adhesive composition,
Comprising 0.5 to 15 parts by weight of the tackifier based on 100 parts by weight of the waterproof polyurethane acrylate oligomer; And
Putting the composition produced in the step in a stirrer and stirring at 200 to 500 rpm in an environment of 60 to 90 ℃ to proceed with the polymerization reaction characterized in that it comprises a polyurethane resin composition having a waterproof.
제1항 내지 제8항 중 어느 한 항에 따른 방수성을 가진 방수성을 가진 폴리우레탄 수지 조성물의 제조방법을 이용하여 제조된 것을 특징으로 하는 모바일 기기용 접착 조성물.
An adhesive composition for a mobile device, which is prepared using a method for producing a polyurethane resin composition having waterproofness according to any one of claims 1 to 8.
제9항에 따른 모바일 기기용 접착 조성물을 포함하는 모바일 기기용 접착 테이프에 있어서,
상기 모바일 기기용 접착 조성물이 50 내지 130 μm 두께의 기재에 10 내지 50 μm 도포되는 것을 특징으로 하는 모바일 기기용 접착 테이프.
In the adhesive tape for a mobile device comprising the adhesive composition for a mobile device according to claim 9,
Adhesive device for mobile devices, characterized in that the adhesive composition for a mobile device is applied 10 to 50 μm on a 50 to 130 μm thick substrate.
제10항에 있어서,
상기 모바일 기기용 접착 테이프의 투습율은 0.5 내지 10 g/m2.day인 것을 특징으로 하는 모바일 기기용 접착 테이프.The method of claim 10,
Adhesive tape for mobile devices, characterized in that the water vapor transmission rate is 0.5 to 10 g / m 2 .day.
KR1020160153110A 2016-11-17 2016-11-17 Waterproof polyurethane resin compounds and mobile device bezel adhesive tape using the same KR101923545B1 (en)