KR101877792B1 - Electroconductive coating composition for remanufacturing of charge rollers, and preparation method thereof - Google Patents
Electroconductive coating composition for remanufacturing of charge rollers, and preparation method thereof Download PDFInfo
- Publication number
- KR101877792B1 KR101877792B1 KR1020160132963A KR20160132963A KR101877792B1 KR 101877792 B1 KR101877792 B1 KR 101877792B1 KR 1020160132963 A KR1020160132963 A KR 1020160132963A KR 20160132963 A KR20160132963 A KR 20160132963A KR 101877792 B1 KR101877792 B1 KR 101877792B1
- Authority
- KR
- South Korea
- Prior art keywords
- charge roller
- inorganic powder
- amine
- conductive coating
- remanufacturing
- Prior art date
Abstract
본 발명은 차지롤러의 재제조를 위한 전도성 코팅액 및 이의 제조방법에 관한 것으로, 보다 구체적으로는 이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제와, 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상을 포함하되, 평균 입경이 10㎚ 내지 10㎛ 인 것을 특징으로 하는 무기 분말과, 상기 무기 분말의 표면에 지속적으로 흡착되어 상기 무기 분말의 분산성을 향상시키는 아민기가 포함된 FATTY AMINE(fatty tallow amine), TEPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류를 포함하고, 상기 용제, 아민류 및 무기 분말은 50~80: 5~20: 15~30의 중량비로 포함하는 것을 특징으로 하는 차지롤러의 재제조를 위한 전도성 코팅액을 개시한다. The present invention relates to a conductive coating liquid for remanufacturing a charge roller and a method for producing the conductive coating liquid, and more particularly, to a conductive coating liquid for recharging a charge roller, An inorganic powder comprising at least one solvent selected from the group consisting of carbon black, polyphenol and polythiophene and having an average particle diameter of 10 nm to 10 μm; And at least one amine selected from the group consisting of FATTY AMINE (fatty tallow amine), TEPA (tetraethylenepentamine) and BHMT (bishexamethylenetriamine), which has an amine group which is adsorbed and improves the dispersibility of the inorganic powder, Is contained at a weight ratio of 50 to 80: 5 to 20: 15 to 30, based on the total weight of the charge roller.
Description
본 발명은 차지롤러의 재제조를 위한 전도성 코팅액 및 이의 제조방법에 관한 것이다. The present invention relates to a conductive coating liquid for remanufacturing charge rollers and a method of manufacturing the same.
사무기기(office appliance, OA)에는 팩스, 컴퓨터, 복사기, 스캐너 및 소모성 토너와 카트리지 등이 포함되는데 최근에는 사무 능률과 공간 효율 향상을 목적으로 하는 복합 사무기기의 수요가 현저하게 증가하는 추세에 있다. 이에 따라 사무기기를 제조하는 관련 IT 산업에서도 복합 사무기기의 개발과 제조를 활발하게 진행하고 있다. 그런데 문제는 이러한 복합 사무기기의 핵심 부품 및 모듈의 기능에 문제가 생겨서 기능의 전부 또는 일부를 구현할 수 없게 되면 신품으로 교체하는 경우가 대부분이므로 향후 (복합)사무기기의 폐기물 또한 비례하여 증가할 것으로 예측된다.Office appliances (office appliances) include fax machines, computers, copiers, scanners and consumable toners and cartridges. In recent years, there has been a significant increase in the demand for office equipment for the purpose of improving office efficiency and space efficiency . As a result, the related IT industry manufacturing office equipment is actively developing and manufacturing complex office equipment. However, the problem is that if the functions of core parts and modules of such office equipments are in trouble, and if all or part of the functions can not be implemented, most of them will be replaced with new ones, so that the waste of office equipment will increase proportionally Is predicted.
한편, 재제조(再製造, remanufacturing)란, 재활용(recycle), 재이용(reuse)과는 다른 개념으로 사용 후 제품을 체계적으로 회수하여 분해, 세척, 검사, 보수ㆍ조정, 재조립 등 일련의 과정을 거쳐 원래의 성능을 유지할 수 있도록 하는 것을 의미한다. 미국, 일본과 같은 선진국의 경우 재제조의 경제 활동 영역이 비교적 명확히 정의되어 있는데 일례로 미국의 사무기기 재제조 규모는 대략 71억 달러, 고용효과 약 8만 명으로 추산된다. 우리나라는 2005년 재제조 산업 육성을 위한 법률적 근거가 확보되면서 관련 산업의 발전을 위한 중요한 토대가 마련되어 2006년부터 프린터, 복사기, 팩스등 사무기기의 생산자책임 재활용제도(EPR, Extended Producer Responsibility)를 의무 시행하여, 생산자에게 재활용 의무를 이행하도록 하고 있으나 사무기기 재제조 산업의 수준은 여전히 초보적 단계에 머물러 있다. 특히 사무기기 재제조 산업 중 가장 활성화되어 있는 토너 잉크 카트리지 재제조 산업의 시초는 1980년대 사용 후 카트리지를 재사용하는 것으로 이후 IMF를 겪으면서 관련수요가 폭발적으로 증가하였다.On the other hand, remanufacturing is a concept that is different from recycle and reuse. It is a system that collects the products after use and processes them in a series of processes such as disassembly, cleaning, inspection, maintenance, To maintain the original performance. In developed countries such as the United States and Japan, the economic activity area of remanufacturing is relatively well defined. For example, the US office equipment manufacturing scale is estimated at approximately $ 7.1 billion and the employment effect is estimated at about 80,000. Korea has secured the legal basis for the re-manufacturing industry in 2005, and since 2006, it has established an important foundation for the development of the related industries. From 2006, it has extended the Producer Responsibility (EPR) system of office equipment such as printer, The obligation is imposed on producers to fulfill their recycling obligations, but the level of office equipment remanufacturing industry is still at an early stage. In particular, toner ink cartridge manufacturing industry, which is most active in the office equipment remanufacturing industry, is beginning to reuse cartridges after use in the 1980s.
한편, 프린터 토너 카트리지를 재제조하는 경우 일반적으로, ① 사용한 토너 카트리지를 회수 및 입고, ② 회수된 토너 카트리지를 검사하여 재제조 가능 여부를 확인, ③ 토너 카트리지를 분해하여 내부를 세척, ④ 토너 카트리지의 부품을 교체하고 파우더를 충전, ⑤ 재제조된 토너 카트리지의 출력 테스트를 실시, ⑥ 토너 카트리지를 포장한 후 출고 등의 과정을 거친다.On the other hand, in the case of remanufacturing a printer toner cartridge, it is common to (1) collect and use the used toner cartridge, (2) inspect the recovered toner cartridge to check whether it can be remanufactured, Replacing parts of the toner cartridges, charging the powder, performing the output test of the remanufactured toner cartridge, and (6) packaging the toner cartridge and discharging it.
특히 레이저 프린터의 토너 카트리지는 OPC 드럼, 현상롤러, 차지롤러, 닥터브레이드, 토너 등으로 구성되며, 카트리지 내 토너는 일반적으로 자성을 갖고 있지 않는 상태이고, 현광드럼(OPC)에 토너를 현상하기 위해서는 토너가 (-)차지를 가져야 하며, 상기 현광드럼을 -차지 상태로 대전시키기 위한 롤러가 차지롤러이다. 구체적으로 차지롤러는 스테인레스 혹은 철에 녹 방지를 위하여 니켈을 입힌 심재(shaft)와, 상기 심재의 외부에 롤러 역할을 하기 위한 탄성의 고분자층(탄성층)으로 이루어져 있다. 이러한 차지롤러는 인쇄 품질에 영향을 주는 매우 중요한 소모성 부품이다. 즉, 토너 및 형광드럼에 계속적인 마찰로 두께가 일부분 마모되면 탄성을 잃고 인쇄에 악영향을 미치게 됨으로 수명이 다하게 된다. 토너가 보통 3-8㎛정도의 크기를 가지고 있으며, 일반적으로 차지롤러의 마모가 토너크기의 30%에 이르면 토너의 대전에 악영향을 미치게 된다. 현제 레이져 프린터 카트리지내의 차지롤러는 4000매 이상의 구동에 2㎛이상의 마모를 보이고 있다. 따라서 수명이 다한 차지롤러는 폐기되고 있으며, 이에 따라 환경의 오염이 심각하게 우려되는 실정이다. 이러한 차지롤러는 토너 카트리지의 재제조시 교체비율이 50~100% 정도로, 교체비율을 낮추기 위한 기술개발이 필요한 실정이다. In particular, the toner cartridge of the laser printer is composed of an OPC drum, a developing roller, a charge roller, a doctor blade, a toner, etc., and the toner in the cartridge is generally in a state of not having magnetic properties. The toner must have a negative charge, and the roller for charging the light-sensitive drum into the -charged state is the charge roller. Specifically, the charge roller comprises a nickel-coated shaft for preventing rust in stainless steel or iron, and an elastic polymer layer (elastic layer) for acting as a roller on the outside of the core. These charge rollers are very important consumable parts that affect print quality. That is, when the toner and the fluorescent drum are partially worn due to continuous friction, they lose elasticity and adversely affect printing, resulting in a short life. The toner usually has a size of about 3-8 mu m, and when the wear of the charge roller reaches 30% of the toner size in general, it adversely affects the charging of the toner. Charge rollers in current laser printer cartridges wear more than 2 ㎛ for driving over 4000 sheets. Therefore, the charge rollers whose lifetime has expired are being discarded, and environmental pollution is seriously concerned. Such a charge roller requires a replacement ratio of 50 to 100% when the toner cartridge is remanufactured, and a technique for lowering the replacement ratio is required.
이에 본 발명자는 전도성 코팅액을 이용하여 카트리지 핵심부품인 차지롤러를 재제조할 수 있음을 확인하고, 본 발명을 완성하였다. Accordingly, the present inventor confirmed that charge roller, which is a core component of a cartridge, can be remanufactured using a conductive coating liquid, and completed the present invention.
따라서 본 발명은 폐 토너 카트리지를 분해하여 폐 차지롤러를 회수하고, 상기 회수된 폐 차지롤러를 세척한 후, 상기 차지롤러의 표면에 전도성 코팅층을 형성하여 차지롤러를 재제조하기 위한 전도성 코팅액을 제공하는 것을 기술적 해결과제로 한다.Therefore, the present invention provides a conductive coating solution for remanufacturing the charge roller by disassembling the waste toner cartridge to recover the waste charge roller, cleaning the recovered waste charge roller, and forming a conductive coating layer on the surface of the charge roller As a technical solution.
또한 본 발명은 상기 전도성 코팅액의 제조방법을 제공하는 것을 다른 해결과제로 한다. Another object of the present invention is to provide a method for producing the conductive coating liquid.
상기 과제를 해결하기 위하여 본 발명은,
폐 토너 카트리지를 분해하여 폐 차지롤러를 회수하고, 상기 회수된 폐 차지롤러를 세척한 후, 상기 차지롤러의 표면에 전도성 코팅층을 형성하여 차지롤러를 재제조하기 위한 전도성 코팅액으로서, 이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제와, 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상을 포함하되, 평균 입경이 10㎚ 내지 10㎛ 인 것을 특징으로 하는 무기 분말과, 상기 무기 분말의 표면에 지속적으로 흡착되어 상기 무기 분말의 분산성을 향상시키는 아민기가 포함된 FATTY AMINE(fatty tallow amine), TEPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류;를 포함하고, 상기 용제, 아민류 및 무기 분말은 50~80: 5~20: 15~30의 중량비로 포함하는 것을 특징으로 한다.
아울러, 본 발명은 폐 토너 카트리지를 분해하여 폐 차지롤러를 회수하고, 상기 회수된 폐 차지롤러를 세척한 후, 상기 차지롤러의 표면에 전도성 코팅층을 형성하여 차지롤러를 재제조하기 위한 전도성 코팅액의 제조방법으로서,
이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제에, 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상의 무기 분말을 혼합 및 교반하여 상기 무기 분말을 분산시킨 1차 분산액을 제조하는 1차 분산단계와, 상기 1차 분산액에 분산된 무기 분말의 표면에 접착되는 아민기를 포함하는 FATTY AMINE(fatty tallow amine), EPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류를 더 혼합 및 교반하는 2차 분산단계를 포함하여 이루어지고, 상기 용제, 아민류 및 무기 분말은 50~80: 5~20: 15~30의 중량비로 포함되는 것을 특징으로 한다.According to an aspect of the present invention,
A conductive coating solution for remanufacturing a charge roller by disassembling a waste toner cartridge to recover a waste charge roller, cleaning the recovered waste charge roller, and forming a conductive coating layer on the surface of the charge roller, At least one solvent selected from isopropyl alcohol, ethyl acetate and methyl ethyl ketone, and at least one solvent selected from carbon black, polyphenol and polythiophene, (TATA), which comprises an inorganic powder and an amine group which is continuously adsorbed on the surface of the inorganic powder and improves the dispersibility of the inorganic powder, and TATA (Tetraethylenepentamine) BHMT (bishexamethylenetriamine), wherein the solvent, amine and inorganic powder have a weight ratio of 50 to 80: 5 to 20: 15 to 30 It characterized in that it comprises.
The present invention also relates to a method of manufacturing a charge roller, comprising the steps of disassembling a waste toner cartridge to recover a waste charge roller, cleaning the recovered waste charge roller, forming a conductive coating layer on the surface of the charge roller, As a production method,
At least one inorganic powder selected from carbon black, polyphenol and polythiophene is added to at least one solvent selected from the group consisting of isopropyl alcohol, ethyl acetate and methyl ethyl ketone, A first dispersion in which the inorganic powder is dispersed by mixing and stirring to prepare a primary dispersion, a FATTY AMINE (fatty tallow amine), an EPA (amine tallow amine) containing an amine group bonded to the surface of the inorganic powder dispersed in the primary dispersion And a secondary dispersion step of further mixing and stirring at least one amine selected from the group consisting of tetraethylenepentamine (BETA) and bis (hexamethylenetriamine) (BHMT), wherein the solvent, the amine and the inorganic powder have a composition of 50 to 80: 5 to 20:15 to 30 By weight.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
본 발명에 따르면 폐 토너 카트리지를 분해하여 회수한 폐 차지롤러의 제조시 상기 본 발명의 전도성 코팅액을 이용하여 재제조함으로써 종래보다 단순하고 간단한 공정에 의하여 기사용된 차지 롤러를 물리, 화학적으로 복원시킴으로써, 폐기되는 비율을 현저하게 감소시키고 친환경적으로 폐 토너 카트리지를 재제조할 수 있는 효과가 있다. According to the present invention, the waste charge roller recovered by disassembling the waste toner cartridge is remanufactured using the conductive coating solution of the present invention to physically and chemically restore the charge roller previously used by a simple and simple process , It is possible to remarkably reduce the waste rate and to remake the waste toner cartridge in an environmentally friendly manner.
도 1은 토너 카트리지의 구조를 나타낸 것이다. 1 shows a structure of a toner cartridge.
이하, 본 발명을 상세히 설명하기로 한다.Hereinafter, the present invention will be described in detail.
본 발명은 폐 토너 카트리지를 분해하여 폐 차지롤러를 회수하고, 상기 회수된 폐 차지롤러를 세척한 후, 상기 차지롤러의 표면에 전도성 코팅층을 형성하는 차지롤러의 재제조에 관한 것이다. The present invention relates to remanufacturing of charge rollers that disassemble a waste toner cartridge to recover a waste charge roller, clean the recovered waste charge roller, and form a conductive coating layer on the surface of the charge roller.
본 발명에 있어서 상기 전도성 코팅층은, 전도성 코팅액을 도포함으로써 형성하게 되는 바, 상기 전도성 코팅액은 이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제와, FATTY AMINE(fatty tallow amine), TEPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류 및 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상의 무기 분말로 이루어지고, 상기 용제, 아민류 및 무기 분말은 50~80: 5~20: 15~30의 중량비로 포함하는 것을 특징으로 한다. In the present invention, the conductive coating layer is formed by applying a conductive coating liquid, and the conductive coating liquid may include one or more selected from the group consisting of isopropyl alcohol, ethyl acetate, and methyl ethyl ketone. At least one kind of inorganic powder selected from among carbon black, polyphenol and polythiophene, at least one solvent selected from the group consisting of FATTY AMINE (fatty tallow amine), TEPA (tetraethylenepentamine) and BHMT (bishexamethylenetriamine) , The solvent, the amine and the inorganic powder in a weight ratio of 50 to 80: 5 to 20:15 to 30.
이 때, 상기 전도성 코팅액에 있어서 사용되는 무기 분말의 경우 입자의 크기는 10㎚ ~ 10㎛의 입경을 가지는 것이 바람직하다. 전도성 무기 분말의 입경이 10㎚ 미만이면, 입자가 너무 미세하여 입자들이 서로 덩어리지는 현상이 발생할 수 있어 실제로 매우 큰 입자들처럼 거동하게 되어 차지롤러의 표면에 도포가 잘 되지 않을 수 있다. 또한, 입경이 10㎛를 초과하면 도포성이 현저히 떨어지게 되어 실제로 사용 중에 입자들이 차지롤러의 표면에서 떨어져 나올 수 있다. 따라서, 프린트를 계속 진행함에 따라 초기에는 오염 방지 효과를 일부 나타내나 초기를 지나면 그 효과가 없어지는 단점을 나타내는 것을 알 수가 있다.At this time, in the case of the inorganic powder used in the conductive coating liquid, the particle size preferably has a particle size of 10 nm to 10 μm. When the particle diameter of the conductive inorganic powder is less than 10 nm, the particles may become too fine to cause the particles to agglomerate with each other, so that they act like very large particles and may not be applied to the surface of the charge roller. On the other hand, when the particle diameter exceeds 10 mu m, the coatability is remarkably deteriorated and the particles may come off from the surface of the charge roller during use. Therefore, it can be seen that, as the printing continues, the contamination prevention effect is partially displayed at the initial stage, but the effect is lost at the initial stage.
또한 본 발명에 있어서 상기 전도성 코팅액이 차지롤러에 도포되는 두께는 일반적으로 0.05 ~ 1㎛ 정도가 바람직하다. 두께가 0.05㎛ 미만인 경우에는 두께가 너무 얇아서 전도성 입자들의 효과가 미약하게 되고, 1㎛을 초과하는 경우에는 두께가 너무 두꺼워서 차지롤러의 원래 기능인 감광드럼표면의 균일한 대전성을 유지시키는 성능이 떨어지게 된다.Also, in the present invention, the thickness of the conductive coating liquid applied to the charge roller is generally about 0.05 to 1 mu m. When the thickness is less than 0.05 mu m, the thickness of the charge roller is too thin, so that the effect of the conductive particles becomes weak. When the thickness exceeds 1 mu m, the thickness is too thick, do.
또한 본 발명에 있어서 상기 전도성 코팅액은, 이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제에, 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상의 무기 분말을 혼합 및 교반하는 1차 분산단계; 및 상기 1차 분산액에 FATTY AMINE(fatty tallow amine), TEPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류를 더 혼합 및 교반하는 2차 분산단계;를 포함하여 이루어질 수 있다. In the present invention, the conductive coating liquid may contain at least one solvent selected from the group consisting of isopropyl alcohol, ethyl acetate and methyl ethyl ketone, carbon black, polyphenol, A primary dispersing step of mixing and stirring at least one inorganic powder selected from among pentane; And a secondary dispersion step of further mixing and stirring the primary dispersion with at least one amine selected from fatty tallow amines (TATA), tetraethylenepentamine (TEPA), and bishexamethylenetriamine (BHMT).
본 발명에 있어서, 상기 전도성 코팅액에 혼합되는 무기 분말은 입자의 크기가 작고 표면적이 넓어 응집체를 형성하려는 경향이 강하므로, 응집체가 형성되는 것을 억제하면서 분산성을 향상시키는 것이 요구되므로 1차적으로 분산시킨 후, 아민류를 더 혼합하여 교반하여 줌으로써 2차적으로 분산시키는 것이 중요하다. 상기 2차 분산단계에서 상기 아민류의 아민기가 무기 분말 입자와 친화력을 가짐에 따라 무기 분말의 표면에 강하고 지속적으로 흡착되어 무기 분말의 분산성을 향상시킬 수 있게 되는 것이다. In the present invention, since the inorganic powder mixed in the conductive coating liquid is required to improve the dispersibility while suppressing formation of aggregates, since the particle size is small and the surface area is wide and the tendency to form agglomerates is strong, It is important to further disperse the amines by further mixing and stirring. As the amine groups of the amines have an affinity with the inorganic powder particles in the secondary dispersion step, they are strongly adsorbed on the surfaces of the inorganic powders and are continuously adsorbed to improve the dispersibility of the inorganic powders.
또한, 상기 1차 분산 및 2차 분산시 무기 분말 입자의 분산성을 더욱 향상시키기 위하여 혼합 및 교반이 이루어지게 되는 바, 무기 분말 입자의 분산성을 더욱 효과적으로 향상시키기 위해서는 100 내지 500 rpm으로 교반될 수 있으며, 상기 교반 시간은 약 5분 내지 10분으로 조절될 수 있다. In order to further improve the dispersibility of the inorganic powder particles in the primary dispersion and the secondary dispersion, mixing and stirring are performed. In order to further improve the dispersibility of the inorganic powder particles, stirring is carried out at 100 to 500 rpm And the stirring time may be adjusted to about 5 minutes to 10 minutes.
이 때, 상기 혼합 및 교반시 이용되는 장비는 예를 들어, 쉐이커, 오비탈 쉐이커, 호모 믹서, 자전-공전 믹서, 균질기, 고압 균질기, 볼 밀, 샌드 밀, 어트리터 밀, 펄 밀, 3본 롤 밀, 제트 밀 등을 이용하여 분산성이 향상된 전도성 코팅액을 제조할 수 있다. The equipment used in the mixing and stirring is, for example, a shaker, an orbital shaker, a homomixer, a rotating-static mixer, a homogenizer, a high-pressure homogenizer, a ball mill, a sand mill, A conductive coating liquid having improved dispersibility can be prepared using the present roll mill, jet mill or the like.
이하, 본 발명을 실시예에 의거하여 더욱 구체적으로 설명하나, 본 발명이 다음 실시예에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described more specifically based on examples, but the present invention is not limited by the following examples.
<실시예> 전도성 코팅액의 제조<Examples> Preparation of Conductive Coating Liquid
IPA를 50~80중량부 카본블랙 15~30중량부를 이용하여서 1ℓ 비어커에 넣고 교반기에서 50rpm으로 1차 5분간 분산을 시켰다. 여기에 Tallow amine을 5~20 중량부를 교반기에서 50rpm으로 2차 5분간 분산을 시켰다. 50 to 80 parts by weight of IPA and 15 to 30 parts by weight of carbon black were put into a 1 L beaker and dispersed for 5 minutes at 50 rpm in an agitator. 5 to 20 parts by weight of tallow amine was dispersed in the agitator at 50 rpm for 5 minutes.
<실험예> <Experimental Example>
PCR의 1차 세척을 위해서 우선 천으로 에탄올로 1차 세척을 한 다음, 전도성 코팅액을 PCR에 0.5㎛로 도포하였다. 이후 칼라프린터 HP2400에서 A4 용지(Double A)를 이용하여 검사테스트를 실시하고 그 기준 및 결과를 표 2 및 표 3에 나타내었다. For the first washing of the PCR, first, the cloth was washed with ethanol first, and then the conductive coating solution was applied to the PCR by 0.5 탆. Thereafter, an inspection test was carried out using A4 paper (Double A) in a color printer HP2400, and the standards and the results are shown in Tables 2 and 3.
상기 표 2에서 확인할 수 있는 바와 같이, 사용등급에 따라 화상균일성이 달라지는데 재제조를 위해서는 4급 이상을 만족하여야 한다. As can be seen from the above Table 2, the image uniformity varies depending on the usage class. For remanufacturing, it is required to satisfy level 4 or higher.
또한 표 3에서 확인할 수 있는 바와 같이 실시예 1, 2에 따른 전도성 코팅액의 도포시에는 사용등급이 2급이고, 실시예 3, 4에 따른 경우에는 사용등급이 3인 것을 확인할 수 있었다. Further, as shown in Table 3, it was confirmed that the application grade of the conductive coating solution according to Examples 1 and 2 was grade 2, and the grade 3 was used according to Examples 3 and 4.
따라서 상기 실시예로부터 폐 토너 카트리지의 재제조시 부품인 차지롤러의 표면에 전도성 코팅액을 도포하여 재제조할 수 있음을 확인할 수 있다. 이에 따라 차지롤러가 폐기되는 비율을 현저하게 감소시키고 친환경적으로 폐 토너 카트리지를 재제조할 수 있을 것으로 기대된다. Therefore, it can be seen from the above embodiment that the conductive coating liquid can be applied to the surface of the charge roller, which is a component in remanufacturing the waste toner cartridge, and remanufactured. Accordingly, it is expected that the rate at which the charge rollers are discarded can be remarkably reduced and the waste toner cartridge can be remanufactured eco-friendly.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것일 뿐 한정적이 아닌 것으로 이해되어야만 한다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the embodiments described above are intended to be illustrative, but not limiting, in all respects.
Claims (3)
이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제;
카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상을 포함하되, 평균 입경이 10㎚ 내지 10㎛ 인 것을 특징으로 하는 무기 분말; 및
상기 무기 분말의 표면에 지속적으로 흡착되어 상기 무기 분말의 분산성을 향상시키는 아민기가 포함된 FATTY AMINE(fatty tallow amine), TEPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류;를 포함하고,
상기 용제, 아민류 및 무기 분말은,
50~80: 5~20: 15~30의 중량비로 포함하는 것을 특징으로 하는 차지롤러의 재제조를 위한 전도성 코팅액.
A conductive coating liquid for remanufacturing a charge roller by disassembling a waste toner cartridge to recover a waste charge roller, cleaning the recovered waste charge roller, and forming a conductive coating layer on a surface of the charge roller,
At least one solvent selected from the group consisting of isopropyl alcohol, ethyl acetate and methyl ethyl ketone;
Carbon black, polyphenol and polythiophene, and has an average particle diameter of 10 nm to 10 μm; And
And one or more amines selected from fatty tallow amine (FATTY AMINE), tetraethylenepentamine (TEPA), and bishexamethylenetriamine (BHMT) containing an amine group that is continuously adsorbed on the surface of the inorganic powder and improves the dispersibility of the inorganic powder and,
The above-mentioned solvents, amines and inorganic powders,
50 to 80: 5 to 20: 15 to 30, based on the weight of the charge roller.
이소프로필알콜(Isopropyl Alcohol), 에틸아세테이트(Ethyl acetate) 및 메틸에틸케톤(Methyl Ethyl Ketone) 중에서 선택되는 1종 이상의 용제에, 카본블랙, 폴리피놀 및 폴리티오펜 중에서 선택되는 1종 이상의 무기 분말을 혼합 및 교반하여 상기 무기 분말을 분산시킨 1차 분산액을 제조하는 1차 분산단계; 및
상기 1차 분산액에 분산된 무기 분말의 표면에 접착되는 아민기를 포함하는 FATTY AMINE(fatty tallow amine), EPA(Tetraethylenepentamine) 및 BHMT(Bishexamethylenetriamine) 중에서 선택되는 1종 이상의 아민류를 더 혼합 및 교반하는 2차 분산단계;를 포함하여 이루어지고,
상기 용제, 아민류 및 무기 분말은 50~80: 5~20: 15~30의 중량비로 포함되는 것을 특징으로 하는, 차지롤러의 재제조를 위한 전도성 코팅액의 제조방법.A method of manufacturing a conductive coating solution for remanufacturing a charge roller by disassembling a waste toner cartridge to recover a waste charge roller, cleaning the recovered waste charge roller, and forming a conductive coating layer on a surface of the charge roller,
At least one inorganic powder selected from carbon black, polyphenol and polythiophene is added to at least one solvent selected from the group consisting of isopropyl alcohol, ethyl acetate and methyl ethyl ketone, A primary dispersion step of producing a primary dispersion in which the inorganic powder is dispersed by mixing and stirring; And
(2) additionally mixing and stirring one or more amines selected from fatty tallow amines (FATTY AMINE), tetraethylenepentamine (EPA) and bishexamethylenetriamine (BHMT) containing an amine group bonded to the surface of the inorganic powder dispersed in the primary dispersion, And a dispersion step,
Wherein the solvent, the amine and the inorganic powder are contained in a weight ratio of 50 to 80: 5 to 20:15 to 30, respectively.