KR101875527B1 - Method of manufacturing dried bio-cellulose sheet and dried bio-cellulose sheet therefrom - Google Patents

Abstract

The present invention relates to a method for manufacturing a dried bio-cellulose sheet, and according to one embodiment of the present invention, provided is the method for manufacturing a dried bio-cellulose sheet, which has a natural preservative ability and a moisturizing effect harmless to human body by using a mixture, as a composite extract developed by the present inventors, which contains methyl propanediol, hydroxyacetophenone, a Pinus sylvestris extract, sorbitol and remainder of water, and which can be restored to moist bio-cellulose when exposed to moisture.

Description

건조 바이오셀룰로오스 시트의 제조방법 및 이로부터 제조된 건조 바이오셀룰로오스 시트{METHOD OF MANUFACTURING DRIED BIO-CELLULOSE SHEET AND DRIED BIO-CELLULOSE SHEET THEREFROM}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a method for producing a dried bio-cellulosic sheet, and a dried bio-cellulosic sheet produced therefrom,

본 발명은 친환경적이고, 세균 번식에 강하며 위생적으로 관리가 가능하고, 발효배양 시간을 획기적으로 단축시킬 수 있으며, 건조된 후 겔화하는 시간을 단축할 수 있고 상온에서 장기간 보관할 수 있으며, 생산비용을 대폭 절감할 수 있는 건조 바이오셀룰로오스 시트의 제조방법 및 이로부터 제조된 건조 바이오셀룰로오스 시트에 관한 것이다.The present invention is environmentally friendly, strong against bacterial propagation, hygienically manageable, can dramatically shorten the fermentation culture time, can shorten the gelation time after drying, can be stored at room temperature for a long time, The present invention relates to a method for producing a dried bio-cellulose sheet and a dried bio-cellulose sheet produced therefrom.

종래, 화장품 분야에서 시트(sheet) 타입의 마스크팩은 손으로 바를 필요 없이 얼굴 형태로 제작된 시트를 붙이는 것으로 보습 및 청정효과 등을 얻을 수 있는 제품이며, 얼굴 전체를 덮을 수 있는 디자인의 시트나 상/하단의 2장으로 나뉜 시트, 눈밑/눈가/입가 등의 특정 부위에 맞춘 시트 등 다양한 형태로 시장에 나와 있다.Conventionally, in the field of cosmetics, a sheet-type mask pack is a product which can obtain a moisturizing and cleansing effect by attaching a face-shaped sheet to a face without needing to be hand-worn. Sheets are available in various forms such as sheets divided into two sheets at the top / bottom, sheets tailored to specific areas such as under the eyes / eyes / mouth.

시트 타입의 마스크팩은 일반적인 화장유액에 비해서 오랫동안 피부에 작용할 수 있도록 유액을 담지할 수 있는 지지체를 갖고 있고, 해당 지지체가 제공하는 폐쇄효과(Occlusive effect)에 의한 피부 효능 성분의 피부침투효과 증진으로 인해 보습효과, 피부미용효과가 탁월한 화장 제품 형태이다.The sheet-type mask pack has a support capable of supporting the emulsion so that it can act on the skin for a long period of time as compared with general cosmetic lotion, and by enhancing the skin penetration effect of the skin effect component by the occlusive effect provided by the support This is a form of cosmetic product with excellent moisturizing effect and skin care effect.

이러한 화장용 마스크팩의 시트는 일반적으로 주로 코튼이나 펄프에서 나온 식물 셀룰로오스 섬유나 혹은 합성 섬유로 만든 부직포를 화장유액의 담수체 겸 마스크 모양의 지지체로 사용한다. 이 때 적용하는 부직포의 재질이나 종류, 원재료에 따라서 다양한 사용감과 효능을 부여할 수 있으며, 섬유 부직포 외에도 다양하고 독특한 재질의 지지체들이 화장유액의 담수체로 사용될 수 있고, 사용감, 착용감, 효능 등에 있어서 차별화하기 위한 다양한 소재연구가 시도되고 있다. The sheet of the cosmetic mask pack generally uses plant cellulose fiber or synthetic fiber non-woven fabric mainly from cotton or pulp as a fresh water body or mask-like support of cosmetic lotion. In addition to the fibrous nonwoven fabric, diverse and unique supports can be used as the fresh water body of the cosmetic lotion, and they are differentiated in terms of feel, fit, and efficacy. Various materials researches have been attempted.

한편, 미생물 배양을 통해 만들어진 셀룰로오스는 바이오셀룰로오스(Biocellulose) 혹은 미생물 셀룰로오스(microbial cellulose)로 불리며, 의약품용 화상처리제나 화장용 마스크팩의 소재로서 활용되고 있다. 일반적인 바이오셀룰로오스(Biocellulose)의 제조는 주로 과일주스의 배양액에서의 균체 배양을 통해서 이루어지는데, 바이오셀룰로오스(Biocellulose)의 생산균주는 아세토박터(Acetobacter)속, 라이조비움(Rhizobium)속, 그리고 아그로박터(Agrobacterium)속 등이 있으나, 생산수율이 우수한 균주는 아세토박터속으로 아세토박터 자일리늄이 가장 많이 알려진 미생물(참조: 한국등록특허 제0405776호)이다. 또한, 생산수율을 올리기 위해서, 바이오셀룰로오스(Biocellulose)를 생산하는 아세토박터속 미생물과, 잡균 오염을 방지하는 박테리오신을 생산하는 젖산균을 정치 혼합 배양 또는 교반 혼합 배양하는 것을 특징으로 하는 바이오셀룰로오스(Biocellulose)의 생산방법에 관한 시도(한국공개특허 제2002-0067226호)도 있었다.On the other hand, cellulose produced through microbial cultivation is called biocellulose or microbial cellulose, and is used as a material for an image processor for pharmaceuticals and a mask pack for cosmetics. Generally, the production of biocellulose is carried out by culturing the cells in a culture medium of fruit juice. The production strains of Biocellulose include strains of Acetobacter, Rhizobium, and Agrobacter Agrobacterium), but the strains with excellent yields are the most commonly known microorganisms (see Korean Patent No. 0405776) with acetobacterium xylenium in acetobacterium. In order to increase the production yield, a biocellulose characterized in that an acetobacterium microorganism producing a biocellulose and a lactic acid bacterium producing a bacteriocin to prevent contamination with a microorganism are mixed in a stationary mixture or a stirred mixture, (Korean Patent Publication No. 2002-0067226).

바이오셀룰로오스(Biocellulose)는 다수의 박테리아, 특히 아세토박터속 균주의 배양에 의해서 생산되는 고분자 물질로서, 정치배양 조건에서는 배양액상에 반투명한 막(pellicle) 형태로 생성된다(참조: 영국특허 제2131701호). 바이오셀룰로오스(Biocellulose)는 식물로부터 얻어지는 셀룰로오스와 같이 글루코오스가 β-1,4로 결합된 폴리머이나, 그의 섬유폭은 식물셀룰로오스보다 훨씬 적고, 3차원 망상구조를 이루고 있어 보수성이 우수하고 하이드로겔 마스크와 같은 부드러운 질감과 매끄러운 착용감을 줄 수 있어 식물 셀룰로오스보다 산업적으로 이용 가치가 크다. 또한, 제조된 바이오셀룰로오스(Biocellulose)를 화장용 시트마스크로 적용하려면, 발효를 위해 주입된 균의 사멸 및 배양액 제거가 필수적인데, 이를 위해 배양 이후의 시트마스크 제작 공정에 있어서도 효율적인 공정의 적용이 요구된다.Biocellulose is a polymeric material produced by culturing a large number of bacteria, particularly an acetobacterium strain, in the form of a translucent pellicle on a culture medium under constant culture conditions (cf. British Patent No. 2131701 ). Biocellulose is a polymer in which glucose is bonded with β-1,4 as in cellulose obtained from plants, but its fiber width is much smaller than that of plant celluloses, and it has a three-dimensional network structure and is excellent in water retention. It has the same soft texture and smooth fit, so it is more industrially useful than plant cellulose. In order to apply biocellulose as a cosmetic sheet mask, it is necessary to kill bacteria injected for fermentation and to remove the culture liquid. For this purpose, it is necessary to apply an efficient process to the sheet mask manufacturing process after culturing do.

인삼은 잘 알려진 동양의 약재이며, 한의약, 건강산업 분야뿐만 아니라 화장품분야에서도 널리 사용되고 있다. 인삼의 대표성분인 진세노사이드의 피부 세포 작용에 대한 다양한 연구가 시도되고 있는데, 인체 세포에 존재하는 히알루론산 합성효소(hyaluronic acid synthase, HAS)의 유전자 발현을 증가시킴으로써, 인체의 히알루론산(hyaluronic acid)) 생성작용을 활성화시킨다는 연구가 대표적이다. 이를 통해서 인삼의 진세노사이드는 피부세포에 대해 항노화, 항산화 및 항염 활동 등 피부 미용에 서도 아주 뛰어난 효능을 가지며, 이런 피부 미용 효과를 활용하기 위해서 다양한 형태의 제품 개발 및 응용이 행해졌다. Ginseng is a well-known Oriental medicine, and it is widely used not only in oriental medicine, health industry, but also in cosmetics field. Various studies on skin cell action of ginsenoside, which is a representative component of ginseng, have been attempted. It is known that hyaluronic acid synthase (HAS) gene expression in human cells is increased, acid) production activity is typical. Through this, ginsenoside of ginseng has very good effects on skin cells, such as anti-aging, antioxidant and anti-inflammatory activity, and various types of products have been developed and applied in order to take advantage of such skin-beauty effects.

따라서 세균 번식에 강하고 건조된 후 겔화 하는 시간을 단축할 수 있는 건조 바이오셀룰로오스 시트의 개발이 절실한 실정이다.Therefore, development of a dry bio-cellulose sheet capable of shortening the gel-forming time after drying and drying is strong.

한국등록특허 제0405776호Korea Patent No. 0405776 한국공개특허 제2002-0067226호Korean Patent Publication No. 2002-0067226 영국특허 제2131701호British Patent No. 2131701 한국공개특허 제2002-0067226호Korean Patent Publication No. 2002-0067226

본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로서, 본 발명의 목적은 복합추출물을 사용하여 종래의 세균 번식에 취약한 바이오셀룰로오스 시트의 단점을 보완하여 위생적으로 관리 가능하고 건조된 후 겔화 하는 시간을 단축할 수 있는 건조 바이오셀룰로오스 시트의 제조방법 및 이로부터 제조된 건조 바이오셀룰로오스 시트를 제공하고자 하는 것이다. DISCLOSURE OF THE INVENTION The object of the present invention is to solve the above problems, and an object of the present invention is to provide a bio-cellulosic sheet which is hygienically manageable by supplementing the disadvantages of conventional bio- And a dried bio-cellulose sheet produced therefrom. The present invention also provides a method for producing a dried bio-cellulosic sheet.

또한 본 발명은 상온에서 장기간 보관할 수 있으며, 생산 시간 및 비용을 대폭 절감할 수 있는 건조 바이오셀룰로오스 시트의 제조방법 및 이로부터 제조된 건조 바이오셀룰로오스 시트를 제공하고자 하는 것이다.The present invention also provides a method for producing a dried bio-cellulose sheet which can be stored at room temperature for a long period of time, and can greatly reduce production time and cost, and a dried bio-cellulose sheet produced therefrom.

본 발명의 상기 및 다른 목적과 이점은 바람직한 실시예를 설명한 하기의 설명으로부터 보다 분명해 질 것이다.These and other objects and advantages of the present invention will become more apparent from the following description of a preferred embodiment thereof.

상기 목적은, 코코넛, 사탕수수 또는 열대 과일 주스를 발효 배양 초기부터 1 내지 5mm로 얇게 배양하여 바이오셀룰로오스를 제조하는 제1단계; 바이오셀룰로오스를 세척하는 제2단계; 세척한 바이오셀룰로오스를 압착 탈수하는 제3단계; 탈수된 바이오셀룰로오스를 커팅하는 제4단계; 커팅된 바이오셀룰로오스를 복합추출물에 침적하는 제5단계; 및 침적된 바이오셀룰로오스를 건조하는 제6단계; 를 포함하는 것을 특징으로 하는 건조 바이오셀룰로오스 시트의 제조방법에 의해 달성된다.The object of the present invention is achieved by a method for producing bio-cellulose, comprising the steps of: preparing bio-cellulose by cultivating coconut, sugar cane or tropical fruit juice thinly at 1 to 5 mm from the beginning of fermentation; A second step of washing the bio-cellulose; A third step of squeezing and dewatering the washed bio-cellulose; A fourth step of cutting dehydrated bio-cellulose; A fifth step of immersing the cut bio-cellulose into the complex extract; And a sixth step of drying the deposited bio-cellulose; The present invention relates to a method for producing a dried bio-cellulose sheet.

여기서, 상기 제2단계와 상기 3단계 사이에 바이오셀룰로오스를 폴리프로필렌(PP), 부직포, 페브릭 메쉬, 펄지 또는 필름지 중 적어도 하나를 이용하여 바이오셀룰로오스의 두면에 합지하는 단계를 더 포함하는 것을 특징으로 한다.The method may further comprise the step of laminating bio-cellulose on the two sides of the bio-cellulose using at least one of polypropylene (PP), a non-woven fabric, a fabric mesh, a papermill or a film sheet between the second step and the third step do.

바람직하게는, 상기 제5단계는 복합추출물 0.2 내지 15중량%의 수용액에 커팅된 바이오셀룰로오스를 1분 내지 2시간 침적하는 단계인 것을 특징으로 한다.Preferably, the fifth step is a step of immersing the cut bio-cellulose in an aqueous solution of 0.2 to 15% by weight of the combined extract for 1 minute to 2 hours.

바람직하게는, 상기 제6단계는 쿨링 챔버를 이용하여 바이오셀룰로오스를 -5℃ 내지 15℃에서 10분 내지 1시간 동안 건조하는 단계인 것을 특징으로 한다.Preferably, the sixth step is a step of drying the bio-cellulose using a cooling chamber at -5 ° C to 15 ° C for 10 minutes to 1 hour.

바람직하게는, 상기 복합추출물은 메틸프로판디올, 하이드록시아세토페논, 구주소나무 추출물, 소르비톨 및 잔량의 정제수를 포함하는 혼합물인 것을 특징으로 한다.Preferably, the complex extract is a mixture comprising methylpropanediol, hydroxyacetophenone, pine extract, sorbitol and remaining purified water.

바람직하게는, 상기 복합추출물은 메틸프로판디올 60 내지 85중량%, 하이드록시아세토페논 10 내지 20중량%, 구주소나무 추출물 4 내지 10중량%, 소르비톨 0.5 내지 4.5중량% 및 잔량의 정제수를 포함하는 것을 특징으로 한다.Preferably, the complex extract contains 60 to 85% by weight of methylpropanediol, 10 to 20% by weight of hydroxyacetophenone, 4 to 10% by weight of a pine extract of Sucrose, 0.5 to 4.5% by weight of sorbitol and a remaining amount of purified water .

바람직하게는, 상기 복합추출물은 복합추출물 100중량 당 알리신을 70℃로 가온하여 분획한 아존 0.1 ~ 0.6중량부를 더 포함하는 것을 특징으로 한다.Preferably, the complex extract further comprises 0.1 to 0.6 parts by weight of azone which is obtained by heating allysine at 70 DEG C per 100 parts by weight of the combined extract.

바람직하게는, 상기 제1단계는 바이오셀룰로오스를 배양하는 중간에 펄 안료 또는 스크럽 입자를 더 포함하여 배양하는 것을 특징으로 한다.Preferably, the first step is characterized in that the pearl pigment or the scrub particles are further contained in the middle of culturing the bio-cellulose.

또한 상기 목적은, 상술한 건조 바이오셀룰로오스 시트의 제조방법에 의해 제조된 것을 특징으로 하는, 건조 바이오셀룰로오스 시트에 의해 달성된다.The above object is also achieved by a dry bio-cellulose sheet characterized by being produced by the above-described method for producing a dry bio-cellulose sheet.

또한 상기 목적은, 상술한 건조 바이오셀룰로오스 시트에 항산화제, 항균제, 항염증제, 항생제, 성장 인자로 이루어진 군에서 선택된 하나 이상의 첨가물을 더 포함하는 것을 특징으로 하는, 의료용 바이오셀룰로오스 시트에 의해 달성된다.The above object can also be achieved by a medical bio-cellulose sheet characterized in that the above-mentioned dried bio-cellulose sheet further comprises at least one additive selected from the group consisting of an antioxidant, an antibacterial agent, an anti-inflammatory agent, an antibiotic and a growth factor.

또한 상기 목적은, 상술한 건조 바이오셀룰로오스 시트을 수중유형 에멀젼에 함침시켜 제조된 것을 특징으로 하는, 화장용 마스크팩에 의해 달성된다.The above object is also achieved by a cosmetic mask pack characterized in that the above-mentioned dry bio-cellulose sheet is manufactured by impregnating an underwater type emulsion.

본 발명에 따르면, 코코넛 발효액을 이용하므로 친환경적이고, 세균 번식에 강하며 위생적으로 관리가 가능한 등의 효과가 있다. INDUSTRIAL APPLICABILITY According to the present invention, there is provided an effect of being eco-friendly by using a coconut fermentation broth, being strong against the propagation of germs, and hygienically managing it.

나아가, 본 발명은 발효 배양 초기 단계부터 얻고자 하는 균일한 높이로 발효 배양된 바이오셀룰로오스를 양산할 수 있고, 이를 통해 바이오셀룰로오즈 블록을 슬라이스하는 공정이 필요 없고, 슬라이스 시 일정한 두께로 슬라이스되지 않거나 바이오셀룰로오스 시트의 손상 문제를 해결할 수 있는 등의 효과가 있다.Furthermore, the present invention can mass produce bio-cellulose that has been fermented and cultured at a uniform height to be obtained from the initial stage of fermentation culture, thereby eliminating the need for a step of slicing the bio-cellulosic block, And the problem of damage of the cellulose sheet can be solved.

또한 본 발명은 발효배양 시간을 획기적으로 단축시킬 수 있는 등의 효과가 있다.The present invention also has the effect of drastically shortening the fermentation culture time.

또한 본 발명은 건조된 후 겔화하는 시간을 단축할 수 있는 등의 효과를 가진다.Further, the present invention has the effect of shortening the time for gelation after drying.

또한 본 발명에 따르면, 운반 및 생산과정에서 미생물류에 의해 오염되는 것을 방지할 수 있고, 제조 과정에서 별도의 항균 시스템이 필요하지 않아 상온에서 장기간 보관할 수 있으며, 멸균 과정이 필요하지 않으므로 생산비용을 대폭 절감할 수 있는 등의 효과를 가진다. In addition, according to the present invention, it is possible to prevent contamination by microorganisms during transportation and production, and it is possible to store for a long time at room temperature because no separate antimicrobial system is required in the manufacturing process. It is possible to greatly reduce the effect.

다만, 본 발명의 효과들은 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다. However, the effects of the present invention are not limited to the above-mentioned effects, and other effects not mentioned can be clearly understood by those skilled in the art from the following description.

도 1은 종래의 배양된 바이오셀룰로오스 블록을 슬라이스하여 바이오셀룰로오스를 제조하는 과정을 도식적으로 보여주는 도면이다.
도 2는 종래의 슬라이스된 바이오셀룰로오스의 사진이다.
도 3은 본 발명의 바람직한 실시형태에 따른 제1단계에서 배양한 바이오셀룰로오스를 도식적으로 보여주는 도면이다.
도 4는 본 발명의 바람직한 실시형태에 따른 제1단계에서 배양한 바이오셀룰로오스의 사진이다.
도 5는 본 발명의 바람직한 실시형태에 따른 제1단계에서 배양된 바이오셀룰로오스를 보여주는 사진이다.
도 6은 본 발명의 바람직한 실시형태에 따른 배양판과 종래의 배양판을 비교하기 위해 도식적으로 도시한 도면이다.1 is a diagram schematically illustrating a process of slicing a conventional cultured bio-cellulose block to produce bio-cellulose.
2 is a photograph of a conventional sliced bio-cellulose.
FIG. 3 is a diagram schematically showing a bio-cellulose cultured in a first step according to a preferred embodiment of the present invention.
4 is a photograph of the bio-cellulose cultured in the first step according to the preferred embodiment of the present invention.
5 is a photograph showing the bio-cellulose cultured in the first step according to the preferred embodiment of the present invention.
6 is a diagram schematically showing a comparison between a culture plate according to a preferred embodiment of the present invention and a conventional culture plate.

이하, 본 발명의 실시예와 도면을 참조하여 본 발명을 상세히 설명한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위해 예시적으로 제시한 것일 뿐, 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 당업계에서 통상의 지식을 가지는 자에 있어서 자명할 것이다.Hereinafter, the present invention will be described in detail with reference to embodiments and drawings of the present invention. It will be apparent to those skilled in the art that these embodiments are provided by way of illustration only for the purpose of more particularly illustrating the present invention and that the scope of the present invention is not limited by these embodiments .

달리 정의되지 않는 한, 본 명세서에서 사용되는 모든 기술적 및 과학적 용어는 본 발명이 속하는 기술 분야의 숙련자에 의해 통상적으로 이해되는 바와 동일한 의미를 갖는다. 상충되는 경우, 정의를 포함하는 본 명세서가 우선할 것이다. 또한 본 명세서에서 설명되는 것과 유사하거나 동등한 방법 및 재료가 본 발명의 실시 또는 시험에 사용될 수 있지만, 적합한 방법 및 재료가 본 명세서에 기재된다.Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In case of conflict, the present specification, including definitions, will control. Also, although methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, suitable methods and materials are described herein.

도 1은 종래의 배양된 바이오셀룰로오스 블록을 슬라이스하여 바이오셀룰로오스를 제조하는 과정을 도식적으로 보여주는 도면이고, 도 2는 종래의 슬라이스된 바이오셀룰로오스의 사진이다. 또한 도 3은 본 발명의 바람직한 실시형태에 따른 제1단계에서 발효 배양 초기부터 얇게 배양한 바이오셀룰로오스를 도식적으로 보여주는 도면이고, 도 4는 본 발명의 바람직한 실시형태에 따른 제1단계에서 배양한 바이오셀룰로오스의 사진이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view showing a process of slicing a conventional cultured bio-cellulosic block to produce bio-cellulose, and FIG. 2 is a photograph of a conventional sliced bio-cellulose. FIG. 3 is a diagram schematically showing a bio-cellulose thinly cultured from the beginning of fermentation culture in the first step according to a preferred embodiment of the present invention, and FIG. 4 is a graph showing the bio-cellulose cultivated in the first step according to the preferred embodiment of the present invention It is a photograph of cellulose.

본 발명의 일 양상에 따른 건조 바이오셀룰로오스 시트의 제조방법에 따르면, 코코넛, 사탕수수 또는 열대 과일 주스를 발효 배양 초기부터 1 내지 5mm로 얇게 배양하여 바이오셀룰로오스를 제조하는 제1단계; 바이오셀룰로오스를 세척하는 제2단계; 세척한 바이오셀룰로오스를 압착 탈수하는 제3단계; 탈수된 바이오셀룰로오스를 커팅하는 제4단계; 커팅된 바이오셀룰로오스를 복합추출물에 침적하는 제5단계; 및 침적된 바이오셀룰로오스를 건조하는 제6단계; 를 포함한다.According to an aspect of the present invention, there is provided a method for producing a bio-cellulosic sheet, comprising the steps of: preparing bio-cellulose by cultivating coconut, sugar cane or tropical fruit juice thinly to 1 to 5 mm from the beginning of fermentation; A second step of washing the bio-cellulose; A third step of squeezing and dewatering the washed bio-cellulose; A fourth step of cutting dehydrated bio-cellulose; A fifth step of immersing the cut bio-cellulose into the complex extract; And a sixth step of drying the deposited bio-cellulose; .

제1단계는 바이오셀룰로오스를 제조하는 단계로서, 종래의 슬라이스 공정 단계를 줄여 공정을 단순화함으로써 세균 감염의 위험성을 낮출 수 있다. 즉 제1단계에서는 코코넛, 사탕수수 또는 열대 과일 주스를 발효 배양 초기부터 1 내지 5mm로 얇게 배양하는 것에 특징이 있다. 이를 위해 본 발명의 일 실시예에서는 배양판의 높이를 조절함으로써, 종래의 1.5 ~ 2.5cm로 발효된 바이오셀룰로오스 블록(도 1 및 도 2 참조)을 이용하여 슬라이스 시 일정한 두께로 슬라이스되지 않거나 바이오셀룰로오스 시트가 손상되는 단점과 바이오셀룰로오스 블록을 반드시 멸균시켜야 하는 단점을 보완하여 발효 배양 초기 단계부터 얻고자 하는 균일한 높이로 발효 배양된 바이오셀룰로오스를 양산할 수 있다(도 3 및 도 4 참조). 이를 통해 종래 10~14일 이상 소요되는 발효배양 시간을 1 내지 3일 이내로 획기적으로 단축시킬 수 있고, 또한 바이오셀룰로오스 블록 슬라이스 시 일정한 두께로 슬라이스되지 않거나 바이오셀룰로오스 시트가 손상되고 또한 제조된 바이오셀룰로오스 블록을 멸균시켜야 하는 종래 기술의 단점을 해결할 수 있게 되는 것이다.The first step is the step of producing bio-cellulose, which reduces the risk of bacterial infection by simplifying the process by reducing the conventional slicing process steps. That is, in the first step, coconut, sugarcane or tropical fruit juice is characterized in that it is thinly cultured to 1 to 5 mm from the beginning of fermentation. For this purpose, in one embodiment of the present invention, by adjusting the height of the culture plate, a conventional bio-cellulosic block (see FIGS. 1 and 2) fermented at 1.5 to 2.5 cm is used to slice the bio- The disadvantage that the sheet is damaged and the disadvantage that the bio-cellulosic block must be sterilized can be compensated, so that the bio-cellulose which has been fermented and cultured at a uniform height to be obtained from the initial stage of the fermentation culture can be produced (see FIGS. 3 and 4). Thus, it is possible to drastically shorten the fermentation culture time required for 10 to 14 days or more in the past within 1 to 3 days, and to prevent the biocellulose block from being sliced to a predetermined thickness or to damage the bio-cellulosic sheet when the bio- It is possible to solve the disadvantages of the prior art that must be sterilized.

도 6은 본 발명의 바람직한 실시형태에 따른 배양판(오른쪽 그림)과 종래의 배양판(왼쪽 그림)을 비교하기 위해 도식적으로 도시한 도면이다.FIG. 6 is a diagram schematically showing a comparison between a culture plate (right side) according to a preferred embodiment of the present invention and a conventional culture plate (left side).

또한 본 발명의 일 실시예에 따르면, 제1단계는 높이 3.0 내지 7.0mm로 조절된 배양판에 코코넛 배양액을 넣은 다음 배양균주를 주입하고, 약 30℃에서 3일간 배양하여 1 내지 5mm 두께의 바이오셀룰로오스를 얻는데, 바이오셀룰로오스를 배양하는 중간에 펄 안료 또는 스크럽 입자 같은 가루 입자를 필요에 맞게 삽입하여 바이오셀룰로오스의 색상을 달리할 수도 있고, 바이오셀룰로오스에 무늬를 넣을 수도 있다. 도 5는 본 발명의 바람직한 실시형태에 따른 제1단계에서 배양된 바이오셀룰로오스로서 펄 안료를 넣어 배양한 바이오셀룰로오스를 보여주는 사진이다.According to an embodiment of the present invention, in the first step, a culture medium containing coconut is placed in a culture plate adjusted to a height of 3.0 to 7.0 mm, and then a culture strain is injected, followed by culturing at about 30 ° C for 3 days. To obtain cellulose, a powder of particles such as a pearl pigment or a scrub particle may be appropriately inserted in the middle of culturing the bio-cellulose to change the color of the bio-cellulose, or to insert the pattern into the bio-cellulose. FIG. 5 is a photograph showing a bio-cellulose obtained by culturing the bio-cellulose cultured in the first step according to a preferred embodiment of the present invention with a pearl pigment.

또한 본 명세서에서 기재한 열대 과일 쥬스는 열대 과일로부터 제조된 쥬스를 말하며, 열대 과일은 두리안 , 망고스틴, 람부탄 , 용안, 리치, 망고, 로즈애플, 드래곤프루츠, 잭프루츠, 포멜로 등을 들 수 있으나 이에 제한되지 않는다. In addition, the tropical fruit juice described in this specification refers to juice made from tropical fruit, and tropical fruits include durian, mangosteen, rambutan, yuan, rich, mango, rose apple, dragon fruit, jack fruit, pomelo and the like But is not limited thereto.

제2단계는 배양된 바이오셀룰로오스를 세척하는 단계이다. 종래에는 배양된 바이오셀룰로오스 블록을 제조하여 슬라이스하여야 하고 슬라이스하는 도중에 감염될 수 있기 때문에 세척단계 이후 멸균과정을 반드시 거쳐야 하지만 본 발명에서는 제1단계에서 발효 배양 초기 단계부터 얻고자 하는 균일한 높이로 발효 배양된 바이오셀룰로오스를 양산할 수 있어 멸균 단계를 생략할 수 있어 종래에 비해 공정 시간이 매우 단축되고 감염 우려가 거의 없게 되는 것이다. The second step is to wash the cultured bio-cellulose. Conventionally, the cultured bio-cellulosic block must be prepared and sliced. Since it can be infected during slicing, the sterilization process must be performed after the washing step. In the present invention, the fermentation is performed at a uniform height The cultured bio-cellulose can be mass-produced, and the sterilization step can be omitted, so that the process time is shortened and there is little fear of infection.

또한 얻어진 바이오셀룰로오스를 세척하는 제2단계 이후 바이오셀룰로오스를 폴리프로필렌(PP), 부직포, 페브릭 메쉬, 펄지 또는 필름지 중 적어도 하나를 이용하여 바이오셀룰로오스의 두면에 합지하는 단계를 더 포함할 수 있다. 폴리프로필렌(PP), 부직포, 페브릭 메쉬, 펄지 또는 필름지는 바이오셀룰로오스를 지지하는 기능을 하며, 마스크 팩 착용 시에는 이를 제거하고 사용한다.The second step of washing the obtained bio-cellulose may further include laminating bio-cellulose on two sides of the bio-cellulose using at least one of polypropylene (PP), non-woven fabric, fabric mesh, papermill or film. Polypropylene (PP), a nonwoven fabric, a fabric mesh, a papermill or a film sheet has a function of supporting bio-cellulose, and it is used when a mask pack is worn.

제3단계는 바이오셀룰로오스를 압착 탈수하는 단계로서 압착 탈수 과정을 거쳐서 일차적으로 80% 정도 수분을 제거한 후 바이오셀룰로오스 시트를 제조할 수 있다. The third step is a step of compressing and dewatering the bio-cellulose, and the bio-cellulosic sheet can be manufactured after removing about 80% of the moisture through the compression dehydration process.

제4단계는 탈수된 바이오셀룰로오스를 커팅하는 단계로서 수분이 제거된 바이오셀룰로오스 시트를 얼굴 모양 혹은 아이 패치, 볼 패치 등의 다양한 형태의 부분 패치 형태 등 용도에 맞게 커팅할 수 있다. In the fourth step, the dehydrated bio-cellulose sheet can be cut to suit the application such as face shape, partial patch pattern of various shapes such as eye patch, ball patch, and the like.

제5단계는 커팅된 바이오셀룰로오스를 복합추출물에 침적하는 단계로서 살균력과 복원력을 주기 위한 단계이다. 이때 복합추출물 0.2 내지 15중량%의 수용액에 커팅된 바이오 셀룰로오즈를 1분 내지 2시간 침적하는 것이 바람직하다.이를 통해 바이오셀룰로오스에서 세균 또는 진균 등을 제거할 수 있다.The fifth step is a step for immersing the cut bio-cellulose into the complex extract and giving a sterilizing power and restoring force. At this time, it is preferable to immerse the bio-cellulose cut into an aqueous solution of 0.2 to 15% by weight of the complex extract for 1 minute to 2 hours, thereby removing bacteria or fungi from the bio-cellulose.

종래에는 두께가 두꺼운 바이오셀룰로오스 블록을 제조한 다음 슬라이스 하여야 하기 때문에 바이오셀룰로오스 블록을 제조한 후 반드시 멸균 과정을 거쳐야 했으나 본 발명에 따르면 이러한 멸균 과정이 필요 없이 제5단계를 통해 멸균이 되므로 종래에 비해 훨씬 비용 면이나 시간적인 면에서 우수한 효과가 있음을 알 수 있다.Since a thick bio-cellulosic block must be prepared and then sliced, a bio-cellulosic block must be sterilized after it is manufactured. However, according to the present invention, sterilization is performed through the fifth step without the necessity of such a sterilization process. It can be seen that there is an excellent effect in terms of cost and time.

본 명세서에서 사용되는 복합추출물이라 함은 메틸프로판디올, 하이드록시아세토페논, 구주소나무 추출물, 소르비톨 및 잔량의 정제수를 포함하는 혼합물을 의미하고, 이러한 복합추출물은, 종래의 바이오셀룰로오스를 이용하여 제조하는 바이오셀룰로오스에 대해 바이오셀룰로오스 내부에 무늬 혹은 가루 입자를 삽입한 후 발효하여 건조한 형태인 바이오셀룰로오스를 제조하는 기술을 바탕으로 본 발명자들이 자체 개발한 천연 살균제 및 보존제로서 이를 이용하여 복원력을 지닌 바이오셀룰로오스 시트를 제조할 수 있게 되는 것이다.As used herein, the term "complex extract" refers to a mixture comprising methylpropanediol, hydroxyacetophenone, pine tree extract, sorbitol and remaining purified water. Such a complex extract may be prepared using conventional bio-cellulose A natural bactericide and preservative developed by the inventors of the present invention based on the technology of producing bio-cellulose which is in the form of dry by fermenting after inserting patterns or powder particles into bio-cellulose for bio-cellulose, and using this as a bio-cellulosic sheet Can be manufactured.

또한 복합추출물은 코코넛의 셀룰로오스가 침적되어 제조된 건조 바이오셀룰로오스 시트가 수초 혹은 수분 내에 종래의 습윤 상태의 바이오셀룰로오스로 복원될 수 있도록 하는 복원제 역할을 함과 동시에 건조 바이오셀룰로오스 시트 자체의 방부능력을 부여하는 기능을 한다.In addition, the combined extract serves as a restorer for restoring the dried bio-cellulose sheet prepared by immersing cellulose of coconut into conventional wet bio-cellulose in a few seconds or a few minutes, and at the same time, is capable of restoring the preservative ability of the dry bio- .

일 실시예에서 복합추출물은 메틸프로판디올 60 내지 85중량%, 하이드록시아세토페논 10 내지 20중량%, 구주소나무 추출물 4 내지 10중량%, 소르비톨 0.5 내지 4.5중량% 및 잔량의 정제수를 포함할 수 있다.In one embodiment, the combined extract may comprise 60-85% by weight methylpropanediol, 10-20% by weight hydroxyacetophenone, 4-10% by weight pearl pine extract, 0.5-5.5% by weight sorbitol and remaining balance purified water .

상기 소르비톨은 침적 과정을 통해 바이오셀룰로오스 시트의 표면을 포함한 전체에 침적될 수 있다.The sorbitol may be immersed in the entirety including the surface of the bio-cellulose sheet through the immersion process.

또한 구주소나무 추출물에 포함되어 있는 테르펜 화합물은 식물의 잎과 꽃 부위에 함유되어 있는데, 구주소나무의 경우 잎에 다량 함유되어 있어 항세균 효과, 항진균효과 및 항균효과 등을 가지고 있어 바이오셀룰로오스 시트에 코팅시킬 경우 살균력을 부여할 수 있다.In addition, the terpene compound contained in the pine extract of Sukjoo is contained in the leaf and flower part of the plant. In the case of the pear tree of Sukjoo, it is contained in a large amount on the leaf and has antimicrobial effect, antifungal effect and antibacterial effect, It is possible to impart a sterilizing power.

일 실시예에서 복합추출물은 아존(ajoene)을 복합추출물 100중량 당 0.1 ~ 0.6중량부를 포함하는 것이 바람직하다. 아존(ajoene)은 마늘의 주요 효능 성분인 알리신(allicin)을 25-100℃의 온도로 가열하면 자연적으로 생성되는 물질로서 알리신을 모체로 하는 지용성 성분이고, 더 이상 분해되지 않는 매우 안정한 물질이다. 본 발명의 실시예에서는 시중에 시판되고 있는 알리신(Wako, 504-36801)을 구입하여 70℃로 가온한 다음 분획한 아존을 사용하였다. In one embodiment, the complex extract preferably contains 0.1 to 0.6 parts by weight of ajoene per 100 parts by weight of the combined extract. Ajoene is a naturally occurring substance, which is a lipophilic component made of allysine as a matrix, and is a very stable substance which is not decomposed any more when heated to a temperature of 25-100 ° C, which is a major component of garlic. In the examples of the present invention, alizine (Wako, 504-36801) commercially available in the market was purchased and heated to 70 ° C, and then fractionated azon was used.

제6단계는 살균력과 복원력이 부여된 바이오셀룰로오스를 건조하는 단계로서 이를 통해 본 발명의 일 양상에 따른 바이오셀룰로오스 시트를 제조하게 되는 것이다. The sixth step is a step of drying the bio-cellulose to which the sterilizing power and the restoring force are imparted, thereby producing a bio-cellulose sheet according to an aspect of the present invention.

이러한 건조 단계는 쿨링 챔버를 이용하여 -5℃ 내지 15℃의 비교적 낮은 온도에서 10분 내지 1시간 동안 수분을 제거하는 것이 바람직하다. 종래에는 고온의 열풍 건조를 통해 바이오셀룰로오스의 수분을 제거하는 건조 단계를 수행하였으나 이 경우 원단 자체의 유효성분이 파괴되는 문제점이 발생되지만, 본 발명에 따른 건조 단계는 쿨링 챔버를 이용하여 -5℃ 내지 15℃로 10분 내지 1시간 동안 비교적 낮은 온도에서 수분을 제거하기 때문에 바이오셀룰로오스 원단 자체의 손상을 최소화시킬 수 있는 등의 효과를 얻을 수 있다.It is preferred that this drying step uses a cooling chamber to remove water for 10 minutes to 1 hour at a relatively low temperature of from -5 캜 to 15 캜. Conventionally, a drying step of removing moisture of bio-cellulose through high-temperature hot air drying has been performed. However, in this case, there is a problem that the effective ingredient of the fabric itself is broken. However, in the drying step according to the present invention, The water is removed at a relatively low temperature for 10 minutes to 1 hour at 15 DEG C, so that the damage of the bio-cellulose fabric itself can be minimized.

본 발명의 다른 실시 태양에 따르면 상술한 건조 바이오셀룰로오스 시트에 항산화제, 항균제, 항염증제, 항생제, 성장 인자로 이루어진 군에서 선택된 하나 이상의 첨가물을 더 포함하는, 의료용 바이오셀룰로오스 시트를 제공할 수 있다.According to another embodiment of the present invention, a bio-cellulose sheet for medical use can be provided which further comprises at least one additive selected from the group consisting of an antioxidant, an antibacterial agent, an anti-inflammatory agent, an antibiotic and a growth factor in the dry bio-cellulose sheet.

본 발명의 다른 실시 태양에 따르면 상술한 건조 바이오셀룰로오스 시트를 수중유형 에멀젼에 함침시켜 제조된 화장용 마스크팩을 제공할 수 있다. 화장용 마스크팩은 상술한 건조 바이오셀룰로오스 시트를 얼굴 형태로 성형, 재단한 다음 수중유형 에멀젼에 함침시켜 제조할 수 있다.According to another embodiment of the present invention, it is possible to provide a cosmetic mask pack prepared by impregnating the above dried bio-cellulose sheet with an underwater type emulsion. The cosmetic mask pack can be produced by molding and cutting the above-mentioned dried bio-cellulose sheet into a facial form, and then impregnating it with an underwater type emulsion.

수중유형 에멀젼은 유성 성분으로 하이드로제네이티드 폴리데센, 디메치콘, 글리세릴스테아레이트SE/ 피이지-100스테아레이트, 폴리글리세릴-3 메틸글루코스디스테아레이트와 수성 성분으로 디소듐 이디티에이, 글리세린, 부틸렌글리콜, 트리에탄올아민, 카보머, 방부제, 향과 정제수를 사용하고, 유성 성분과 수성 성분을 각각 65~70℃로 가열한 후 균일하게 혼합한 다음 약 70℃를 유지한 상태로 혼합된 수성 성분에 유성 성분을 교반하면서 서서히 투입한 후에 냉각시켜 제조할 수 있다. The water-in-oil type emulsion is composed of an oil-based component such as hydrogenated polydecene, dimethicone, glyceryl stearate SE / PIG-100 stearate, polyglyceryl-3 methyl glucose distearate and aqueous components such as disodium edetate, glycerin, Butene glycol, triethanolamine, carbomer, preservative, fragrance and purified water were used, and the oily component and the aqueous component were heated to 65 to 70 DEG C, respectively, and uniformly mixed. Then, And slowly adding the oily component to the component while stirring and cooling the component.

또한 화장용 마스크팩에는 화장유액을 더 포함할 수 있다. 화장유액은 바이오셀룰로오스를 통해 피부에 흡수되어 주름 개선, 미백, 보습, 재생 효과 등을 나타내는 것으로, 글리세린, 히알루론산, 세라마이드, 비타민 A, 비타민 D, 비타민 C, 비타민 E, 콜라겐, 상피 세포 성장 인자(EGF, Epidermal growth factor), 혈소판 유래 성장 인자-AA(PDGF-AA, Platelet-derived growth factor-AA) 및 인슐린 유사 성장 인자-1(IGF-1, Insulin-like growth factor 1), 티트리, 알로에농축액, 식물 추출물, 달팽이 점액, 인삼, 홍삼, 로얄젤리, 알부틴, 위치하젤, 나이아신아마이드, 아데노신, 레티놀, 알란토인 등을 사용할 수 있다.The cosmetic mask pack may further include a cosmetic lotion. Cosmetic milky lotion is absorbed into the skin through bio-cellulose and shows wrinkle improvement, whitening, moisturizing, regenerating effect and the like. It contains glycerin, hyaluronic acid, ceramide, vitamin A, vitamin D, vitamin C, vitamin E, collagen, (EGF, Epidermal growth factor), platelet-derived growth factor-AA (AAF), and insulin-like growth factor-1 (IGF- Ginseng, red ginseng, royal jelly, arbutin, positional hazel, niacinamide, adenosine, retinol, allantoin and the like can be used.

본 발명에 따른 건조 바이오셀룰로오스 시트는 수분 동안 수분에 노출 시 습윤 바이오셀룰로오스로 복원될 수 있고, 화장유액 또는 유액 타입의 약용 성분에 건조 바이오셀룰로오스 시트가 침지되는 경우, 특정 성분을 함유하는 습윤 발효 바이오셀룰로오스로 복원될 수 있다. The dried bio-cellulose sheet according to the present invention can be restored to wet bio-cellulose upon exposure to moisture for a few minutes, and when the dry bio-cellulose sheet is immersed in a cosmetic lotion or a milky lotion-type medicinal component, Cellulose can be restored.

따라서 본 발명에 따르면, 코코넛 발효액을 이용하므로 친환경적이고, 수초 내지 수 분 내로 신속하게 겔화되어 약용 물질을 전달하는 미용 또는 의료용 재료로 사용될 수 있다. Therefore, according to the present invention, since the coconut fermentation broth is used, it can be used as a cosmetic or medical material which is environmentally friendly and quickly gelled in a few seconds to several minutes to deliver a medicinal substance.

또한 본 발명에 따르면, 건조 바이오셀룰로오스 시트의 제조방법에서 본 발명자들이 개발한 복합추출물로서 메틸프로판디올, 하이드록시아세토페논, 구주소나무 추출물, 소르비톨 및 잔량의 정제수를 포함하는 혼합물을 이용하여 인체에 무해한 천연 방부능력과 보습효과를 가지고, 수분에 노출 시 습윤 바이오셀룰로오스로 복원이 가능한 바이오셀룰로오스 시트를 제공할 수 있다.Further, according to the present invention, by using a mixture containing methylpropane diol, hydroxyacetophenone, pine extract, sorbitol and sorbitol as a complex extract developed by the present inventors in the process for producing a dry bio-cellulose sheet, It is possible to provide a bio-cellulose sheet which has natural preservative ability and moisturizing effect and can be restored to wet bio-cellulose upon exposure to moisture.

이하, 실시예와 비교예를 통하여 본 발명의 구성 및 그에 따른 효과를 보다 상세히 설명하고자 한다. 그러나, 본 실시예는 본 발명을 보다 구체적으로 설명하기 위한 것이며, 본 발명의 범위가 이들 실시예에 한정되는 것은 아니다.Hereinafter, the structure and effect of the present invention will be described in more detail with reference to examples and comparative examples. However, this embodiment is intended to explain the present invention more specifically, and the scope of the present invention is not limited to these embodiments.

[실시예][Example]

제조예 1: 구주소나무 추출물의 제조Production Example 1: Preparation of a pine extract

먼저, 질량 비율 1 : 2로 1,3-부틸렌 글리콜과 에탄올을 약 50분간 혼합교반하여 단일상의 공용매를 제조한 다음, 완전 건조된 구주소나무 잎을 직경 약 0.1㎝ 이하로 분쇄하고 분쇄된 구조소나무 잎과 공용매를 약 1:2의 질량비로 약 30분간 혼합교반한 후 혼합된 혼합물을 초임계 추출조에 투입하여 초임계 추출조를 밀봉한다. 다음으로 밀봉된 초임계 추출조에 고압 기체 펌프를 사용하여 이산화탄소를 공급하여 추출조의 압력을 높이고, 또한 초임계 추출조 내부온도를 0.1℃/min속도로 40℃까지 승온하여 약 60분간 유지시킨다. 그리고 다시 이산화탄소를 공급하면서 추출물을 방출시키고 상압으로 감압한다. 분리된 이산화탄소는 대기로 방출시키고 구주소나무 추출물을 얻었다.First, 1,3-butylene glycol and ethanol were mixed and stirred at a mass ratio of 1: 2 for about 50 minutes to prepare a single-phase cosolvent. Then, the completely dried pine leaf was pulverized to a diameter of about 0.1 cm or less, The pine leaves and the co-solvent are mixed and stirred at a mass ratio of about 1: 2 for about 30 minutes, and the mixed mixture is put into a supercritical extraction tank to seal the supercritical extraction tank. Next, the pressure in the extraction tank is increased by supplying carbon dioxide to the sealed supercritical extraction tank by using a high pressure gas pump, and the temperature inside the supercritical extraction tank is raised to 40 ° C at a rate of 0.1 ° C / min and maintained for about 60 minutes. Then, while supplying carbon dioxide again, the extract is released and the pressure is reduced to normal pressure. Separated carbon dioxide was released into the atmosphere and the extract of the pine tree was obtained.

제조예 2: 아존의 제조Production Example 2: Preparation of azone

시중에 시판되고 있는 알리신(Wako, 504-36801)을 구입하여 70℃로 가온한 다음 아존을 분획하여 아존을 제조하였다.Alicin (Wako, 504-36801), which is commercially available in the market, was purchased and heated to 70 ° C, and azone was fractionated to prepare azone.

제조예 3-1: 복합추출물 A의 제조Production Example 3-1: Preparation of Compound Extract A

메틸프로판디올 70중량%, 하이드록시아세토페논 10중량%, 구주소나무 추출물 4중량%, 소르비톨 0.5중량% 및 잔량의 정제수를 교반기를 이용하여 실온에서 혼합 교반하여 복합추출물 A를 제조하였다.Compound extract A was prepared by mixing and stirring 70% by weight of methylpropanediol, 10% by weight of hydroxyacetophenone, 4% by weight of pine needle extract, 0.5% by weight of sorbitol and remaining amount of purified water at room temperature using a stirrer.

제조예 3-2: 복합추출물 B의 제조Production Example 3-2: Preparation of complex extract B

상기 제조예 3-1에서 제조된 복합추출물 A 100중량에 대해 상기 제조예 2에서 제조된 아존 0.3중량부를 더 추가하여 복합추출물 B를 제조하였다.The complex extract B was prepared by further adding 0.3 part by weight of the azone prepared in Preparation Example 2 to 100 parts by weight of the complex extract A prepared in Preparation Example 3-1.

제조예 4: 건조 바이오셀룰로오스 시트의 제조Preparation Example 4: Preparation of dry bio-cellulose sheet

먼저, 숙성된 코코넛액 1000mL을 온도 100℃로 30분 가열한 후 수크로오스 90g, 유산암모늄 10g을 첨가하고, 아세트산을 사용하여 pH 4.0로 맞춘 다음 교반하여 코코넛 배양약을 제조한 다음, 코코넛 배양액 100mL에 전배양으로 아세토박터자일리넘을 접종한 후 온도 30℃에서 4일 동안 진탕배양하여 배양균주를 생산한 후 높이 3.0mm로 조절된 배양판에 코코넛 배양액을 넣은 다음 배양균주를 5mL 주입하고, 30℃에서 3일간 배양하여 1.5 mm 두께의 바이오셀룰로오스를 얻었다.First, 1000 mL of the aged coconut solution was heated to 100 DEG C for 30 minutes, 90 g of sucrose and 10 g of ammonium sulfate were added, and the pH was adjusted to 4.0 with acetic acid. The mixture was stirred to prepare a coconut culture drug. After incubation with acetobacterium xylumen in pre-culture, the culture was incubated with shaking at 30 ° C for 4 days to produce a culture. Cultures of coconut were placed in a culture plate adjusted to a height of 3.0 mm, and 5 ml of the culture broth was added. And cultured for 3 days to obtain 1.5-mm-thick bio-cellulose.

다음으로, 얻어진 바이오셀룰로오스를 세척한 다음 바이오셀룰로오스의 일면에 부직포를 부착하고 타면에는 펄지를 부착한 후 압착 탈수 과정을 거쳐서 일차적으로 80% 정도 수분을 제거한 후 바이오셀룰로오스 시트를 제조하였다. 수분이 제거된 바이오셀룰로오스 시트를 얼굴 모형 형태로 절단하고, 복합추출물 A에 30분 동안 침적하여 바이오셀룰로오스 시트를 코팅하였다. 복합추출물 A가 처리된 바이오셀룰로오스 시트를 쿨링 챔버 건조 라인에서 15℃로 20분 동안 통과시켜 2차로 수분을 99% 이상 탈수한 다음 건조 바이오셀룰로오스 시트를 제조하였다.Next, the obtained bio-cellulose was washed, and then a non-woven fabric was attached to one side of the bio-cellulose, followed by a peripheral squeeze dehydration process to remove moisture of about 80% to prepare a bio-cellulose sheet. The moisture-free bio-cellulose sheet was cut into a facial model, and the bio-cellulose sheet was coated on the composite extract A for 30 minutes. The bio-cellulose sheet treated with the complex extract A was passed through a cooling chamber drying line at 15 ° C for 20 minutes to dehydrate water at least 99% in a second order, and then a dried bio-cellulose sheet was prepared.

제조예 5: 건조 바이오셀룰로오스 시트의 제조Production Example 5: Preparation of dry bio-cellulose sheet

상기 제조예 4에서 복합추출물 A를 복합추출물 B로 대체한 것을 제외하고는 동일하게 제조하여 건조 바이오셀룰로오스 시트를 제조하였다.A dried bio-cellulose sheet was prepared in the same manner as in Preparation Example 4 except that the complex extract A was replaced with the complex extract B.

제조예 6: 건조 바이오셀룰로오스 시트의 제조Preparation Example 6: Preparation of dry bio-cellulose sheet

상기 제조예 4에서 바이오셀룰로오스 시트를 복합추출물 A에 침적하지 않은 것을 제외하고는 동일하게 제조하여 건조 바이오셀룰로오스 시트를 제조하였다.The dried bio-cellulose sheet was prepared in the same manner as in Preparation Example 4, except that the bio-cellulose sheet was not immersed in the composite extract A.

제조예 7: 건조 바이오셀룰로오스 시트의 제조Preparation Example 7: Preparation of dry bio-cellulose sheet

상기 제조예 5에서 바이오셀룰로오스 시트를 복합추출물 B에 침적하지 않은 것을 제외하고는 동일하게 제조하여 건조 바이오셀룰로오스 시트를 제조하였다.The dried bio-cellulose sheet was prepared in the same manner as in Preparation Example 5, except that the bio-cellulose sheet was not immersed in the composite extract B.

제조예 8: 수중유형 에멀젼의 제조Production Example 8: Preparation of an underwater type emulsion

하기 표 1에 기재된 조성으로 에멀젼을 제조하였다. 구체적으로는 표 1에 기재된 유성성분과 수성성분을 각각 약 70℃로 가열한 후 균일하게 혼합하였다. 약 70℃를 유지한 상태로 혼합된 수성성분에 유성성분을 교반하면서 서서히 투입한 후에 냉각시켜 수중유형 에멀젼을 제조하였다.Emulsions were prepared with the compositions shown in Table 1 below. Specifically, the oily component and the aqueous component shown in Table 1 were each heated to about 70 DEG C and then mixed uniformly. While maintaining the temperature at about 70 캜, the oily component was gradually added to the mixed aqueous component while stirring, and then cooled to prepare an underwater type emulsion.

원료Raw material 함량(중량%)Content (% by weight) 유성meteor 하이드로제네이티드 폴리데센Hydrogenated polydecene 9.09.0 디메치콘Dimethicone 1.01.0 글리세릴스테아레이트SE/ 피이지-100스테아레이트Glyceryl stearate SE / peptide-100 stearate 0.80.8 폴리글리세릴-3 메틸글루코스디스테아레이트Polyglyceryl-3 methyl glucoside distearate 0.50.5 수성Mercury 디소듐 이디티에이Disodium edetate 0.010.01 글리세린glycerin 4.04.0 부틸렌글리콜Butylene glycol 9.09.0 트리에탄올아민Triethanolamine 0.10.1 카보머Carbomer 0.10.1 방부제antiseptic 0.050.05 향incense 적량Suitable amount 정제수 Purified water 잔량Balance

[실시예 1][Example 1]

제조예 4에서 제조된 건조 바이오셀룰로오스 시트를 제조예 8에서 제조된 수중유형 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.The dried bio-cellulose sheet prepared in Production Example 4 was impregnated with 30 g of the water-in-oil emulsion prepared in Production Example 8 to prepare a mask pack.

[실시예 2][Example 2]

제조예 5에서 제조된 건조 바이오셀룰로오스 시트를 제조예 8에서 제조된 수중유형 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.The dry bio-cellulose sheet prepared in Preparation Example 5 was impregnated with 30 g of the water-in-oil emulsion prepared in Preparation Example 8 to prepare a mask pack.

[비교예 1][Comparative Example 1]

제조예 6에서 제조된 건조 바이오셀룰로오스 시트를 제조예 8에서 제조된 수중유형 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.The dried bio-cellulose sheet prepared in Preparation Example 6 was impregnated with 30 g of the water-in-oil type emulsion prepared in Production Example 8 to prepare a mask pack.

[비교예 2][Comparative Example 2]

제조예 7에서 제조된 건조 바이오셀룰로오스 시트를 제조예 8에서 제조된 수중유형 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.The dried bio-cellulose sheet prepared in Preparation Example 7 was impregnated with 30 g of the water-in-oil type emulsion prepared in Preparation Example 8 to prepare a mask pack.

[비교예 3][Comparative Example 3]

시판되고 있는 레이온 원단(천우 글로텍스, 평량: 40 gsm ㅁ5)을 얼굴 형태로 성형, 재단한 다음 제조예 8에서 제조된 수중유형 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.A commercially available rayon fabric (Cheonwoo Grom Tex, basis weight: 40 gsm ㅁ 5) was shaped and cut into a face shape, and then impregnated with 30 g of the water type emulsion prepared in Production Example 8 to prepare a mask pack.

[비교예 4][Comparative Example 4]

시판되고 있는 하이드로셀 원단(천우 글로텍스, 평량: 40 gsm ㅁ5)을 얼굴 형태로 성형, 재단한 다음 제조예 8에서 제조된 에멀젼 30g에 함침시켜 마스크팩을 제조하였다.A commercially available hydrocell fabric (Cheonwoo Grom Tex, basis weight: 40 gsm? 5) was formed and cut into a face shape, and then impregnated with 30 g of the emulsion prepared in Production Example 8 to prepare a mask pack.

상기 실시예 1 내지 2 및 비교예 1 내지 4에 따른 마스크팩을 사용하여 다음과 같은 실험예를 통해 물성을 측정하였다.Using the mask packs according to Examples 1 to 2 and Comparative Examples 1 to 4, physical properties were measured by the following experimental examples.

[실험예][Experimental Example]

[실험예 1][Experimental Example 1]

실시예 1, 2 및 비교예 1 내지 4의 마스크팩을 사용하여 피부탄력 개선 효과를 측정하였다. 이를 위해 온도 약 20℃, 습도 65% 하에서 20세 이상의 건강한 여성 50명을 선정하여 2개조로 나누었다. 매일 2회씩 5주간 실시예 1 및 비교예 1 내지 3의 마스크팩을 얼굴에 부친 다음 피부탄력측정기(Cutometer C+K, Germany)를 이용하여 피부탄력을 측정하여 그 결과를 하기 표 2에 나타내었다. 개선 정도는 Ur/Uf를 parameter로 사용하였다.The skin elasticity improving effect was measured using the mask packs of Examples 1 and 2 and Comparative Examples 1 to 4. For this purpose, 50 healthy women aged 20 years or older at a temperature of about 20 ° C and humidity of 65% were selected and divided into two groups. The skin elasticity was measured using a skin elasticity tester (Cutometer C + K, Germany) after the mask packs of Example 1 and Comparative Examples 1 to 3 were applied to the face twice a day for 5 weeks, and the results are shown in Table 2 below . The degree of improvement was used as a parameter of Ur / Uf.

구분division 탄력 개선율(%, n=30)Elasticity improvement rate (%, n = 30) 실시예 1Example 1 18.718.7 실시예 2Example 2 19.119.1 비교예 1Comparative Example 1 13.913.9 비교예 2Comparative Example 2 12.812.8 비교예 3Comparative Example 3 11.711.7 비교예 4Comparative Example 4 9.89.8

위 표 2에서 확인할 수 있는 바와 같이, 본 발명의 실시예 1과 2에 따른 마스크팩의 경우 비교예 1 내지 3의 마스크팩을 사용한 경우보다 화장료 조성물을 피부로 보다 효과적으로 전달함으로써 피부탄력 개선 효과가 매우 우수함을 알 수 있다. 또한 실험 중 실시예 1에 따른 마스크팩에 의한 부작용이나 피부 자극은 없었다.As can be seen from the above Table 2, in the case of the mask pack according to Examples 1 and 2 of the present invention, the cosmetic composition is more effectively delivered to the skin than the case of using the mask packs of Comparative Examples 1 to 3, It is very good. There was no side effect or skin irritation caused by the mask pack according to Example 1 during the experiment.

[실험예 2][Experimental Example 2]

실시예 1, 2 및 비교예 1 내지 4의 마스크팩을 사용하는 중에 시험 대상자가 느낀 밀착감과 사용 후의 보습감과 전체적인 만족도를 평가하기 위하여 실험예 1의 여성 50명을 대상으로 실시예 1 및 비교예 1 내지 4의 마스크팩을 매일 2회씩 각각 1주일씩 사용하게 한 후 설문조사를 실시한 후 그 결과를 표 3에 나타내었다. 하기 표 3에 있는 숫자는 설문조사에서 응답한 시험 대상자의 수이다.50 women of Experimental Example 1 were evaluated in order to evaluate the feeling of adhesion felt by the test subjects during use of the mask packs of Examples 1 and 2 and Comparative Examples 1 to 4, the moisturizing feeling after use, and the overall satisfaction, 1 to 4 mask packs were used twice a day for one week each, and the results were shown in Table 3. The numbers in Table 3 below are the number of subjects who responded to the survey.

구분division 밀착감 좋음Good adhesion 보습감 좋음Good moisturizing 전체 만족도 좋음Overall satisfaction is good 실시예 1Example 1 4545 4040 4242 실시예 2Example 2 4242 4545 4343 비교예 1Comparative Example 1 3636 3535 3636 비교예 2Comparative Example 2 3434 3636 3535 비교예 3Comparative Example 3 3131 3232 3030 비교예 4Comparative Example 4 2929 2020 2828

위 표 3에서 확인할 수 있는 바와 같이, 본 발명의 실시예 1과 2에 따른 마스크팩의 경우 사용 중 밀착감, 사용 후 보습감 및 만족도 있어서 비교예 1 내지 4에 따른 마스크팩 보다 훨씬 우수함을 알 수 있다. As can be seen from the above Table 3, it can be seen that the mask pack according to Examples 1 and 2 of the present invention is much better than the mask pack according to Comparative Examples 1 to 4 in terms of adhesion feeling, .

본 명세서에서는 본 발명자들이 수행한 다양한 실시예 가운데 몇 개의 예만을 들어 설명하는 것이나 본 발명의 기술적 사상은 이에 한정하거나 제한되지 않고, 당업자에 의해 변형되어 다양하게 실시될 수 있음은 물론이다.It is to be understood that the present invention is not limited to the above embodiments and various changes and modifications may be made by those skilled in the art without departing from the spirit and scope of the invention.

Claims (11)

코코넛, 사탕수수 또는 열대 과일 주스를 발효 배양 초기부터 1 내지 5mm로 얇게 배양하여 바이오셀룰로오스를 제조하는 제1단계;
바이오셀룰로오스를 세척하는 제2단계;
세척한 바이오셀룰로오스를 압착 탈수하는 제3단계;
탈수된 바이오셀룰로오스를 커팅하는 제4단계;
커팅된 바이오셀룰로오스를 복합추출물에 침적하는 제5단계; 및
침적된 바이오셀룰로오스를 건조하는 제6단계; 를 포함하고, 상기 복합추출물은 메틸프로판디올, 하이드록시아세토페논, 구주소나무 추출물, 소르비톨 및 잔량의 정제수를 포함하는 혼합물인 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법.A first step of cultivating coconut, sugar cane or tropical fruit juice thinly to 1 to 5 mm from the beginning of fermentation culture to produce bio-cellulose;
A second step of washing the bio-cellulose;
A third step of squeezing and dewatering the washed bio-cellulose;
A fourth step of cutting dehydrated bio-cellulose;
A fifth step of immersing the cut bio-cellulose into the complex extract; And
A sixth step of drying the deposited bio-cellulose; Wherein the complex extract is a mixture comprising methylpropanediol, hydroxyacetophenone, pine extract, sorbitol and a remaining amount of purified water. 제1항에 있어서,
상기 제2단계와 상기 3단계 사이에 바이오셀룰로오스를 폴리프로필렌(PP), 부직포, 페브릭 메쉬, 펄지 또는 필름지 중 적어도 하나를 이용하여 바이오셀룰로오스의 두면에 합지하는 단계를 더 포함하는 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법.The method according to claim 1,
Further comprising the step of laminating bio-cellulose between the second step and the third step on two sides of the bio-cellulose using at least one of polypropylene (PP), a non-woven fabric, a fabric mesh, Dried bio-cellulose sheet. 제1항에 있어서,
상기 제5단계는 복합추출물 0.2 내지 15중량%의 수용액에 커팅된 바이오셀룰로오스를 1분 내지 2시간 침적하는 단계인 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법.The method according to claim 1,
Wherein the fifth step is a step of immersing the cut bio-cellulose in an aqueous solution of 0.2 to 15% by weight of the combined extract for 1 minute to 2 hours. 제1항에 있어서,
상기 제6단계는 쿨링 챔버를 이용하여 바이오셀룰로오스를 -5℃ 내지 15℃에서 10분 내지 1시간 동안 건조하는 단계인 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법.The method according to claim 1,
Wherein the sixth step is a step of drying the bio-cellulose at -5 ° C to 15 ° C for 10 minutes to 1 hour by using a cooling chamber. 삭제delete 제1항에 있어서,
상기 복합추출물은 메틸프로판디올 60 내지 85중량%, 하이드록시아세토페논 10 내지 20중량%, 구주소나무 추출물 4 내지 10중량%, 소르비톨 0.5 내지 4.5중량% 및 잔량의 정제수를 포함하는 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법. The method according to claim 1,
Characterized in that the complex extract comprises 60 to 85% by weight of methylpropanediol, 10 to 20% by weight of hydroxyacetophenone, 4 to 10% by weight of a pine extract of Sucrose, 0.5 to 4.5% by weight of sorbitol, Dried bio-cellulose sheet. 제6항에 있어서,
상기 복합추출물은 복합추출물 100중량 당 알리신을 70℃로 가온하여 분획한 아존 0.1 ~ 0.6중량부를 더 포함하는 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법. The method according to claim 6,
Wherein the combined extract further comprises 0.1 to 0.6 parts by weight of azone obtained by heating allysine at 70 DEG C per 100 parts by weight of the combined extract. 제1항에 있어서,
상기 제1단계는 바이오셀룰로오스를 배양하는 중간에 펄 안료 또는 스크럽 입자를 더 포함하여 배양하는 것을 특징으로 하는, 건조 바이오셀룰로오스 시트의 제조방법.The method according to claim 1,
Wherein the first step comprises culturing the culture medium further comprising pearl pigment or scrub particles in the middle of culturing the bio-cellulose. 제1항 내지 제4항 및 제6항 내지 제8항 중 어느 한 항에 따른 건조 바이오셀룰로오스 시트의 제조방법에 의해 제조된 것을 특징으로 하는, 건조 바이오셀룰로오스 시트. A dry bio-cellulose sheet produced by a method for producing a dry bio-cellulose sheet according to any one of claims 1 to 4 and 6 to 8. 제9항의 건조 바이오셀룰로오스 시트에 항산화제, 항균제, 항염증제, 항생제, 성장 인자로 이루어진 군에서 선택된 하나 이상의 첨가물을 더 포함하는 것을 특징으로 하는, 의료용 바이오셀룰로오스 시트.The medical bio-cellulose sheet according to claim 9, further comprising at least one additive selected from the group consisting of an antioxidant, an antibacterial agent, an anti-inflammatory agent, an antibiotic, and a growth factor. 제9항의 건조 바이오셀룰로오스 시트을 수중유형 에멀젼에 함침시켜 제조된 것을 특징으로 하는, 화장용 마스크팩.A cosmetic mask pack produced by impregnating the dried bio-cellulose sheet of claim 9 with an underwater type emulsion.

Images