KR101862681B1 - KR-slag-based soil amendment composition and method for producing the same - Google Patents
KR-slag-based soil amendment composition and method for producing the same Download PDFInfo
- Publication number
- KR101862681B1 KR101862681B1 KR1020170091026A KR20170091026A KR101862681B1 KR 101862681 B1 KR101862681 B1 KR 101862681B1 KR 1020170091026 A KR1020170091026 A KR 1020170091026A KR 20170091026 A KR20170091026 A KR 20170091026A KR 101862681 B1 KR101862681 B1 KR 101862681B1
- Authority
- KR
- South Korea
- Prior art keywords
- gypsum
- slag
- present
- phosphoric acid
- weight
- Prior art date
Abstract
Description
본 발명은 KR슬래그를 이용한 토양 개량제 조성물 및 그의 제조방법에 관한 것으로, 더욱 상세하게는 인산부산석고에 KR슬래그를 혼합하여 안정화시키고 짧은 시간 내에 함수율을 감소시켜 토양 개량제로 활용할 수 있도록 하는 KR슬래그를 이용한 토양 개량제 조성물 및 그의 제조방법에 관한 것이다.
The present invention relates to a soil improving agent composition using KR slag and a method for producing the same, and more particularly, to KR slag, which is used as a soil conditioner by reducing the water content in a short time by mixing and stabilizing a KR slag in a phosphate gypsum And a method for producing the same.
일반적으로 인산부산석고는 인산 비료의 제조과정 중 생기는 부산물이며, 우리나라 대부분의 농가에서 사용하는 인산 비료는 주로 인광석을 가공해서 만든다.In general, Phosphorus gypsum is a byproduct produced during the manufacturing process of phosphoric acid fertilizer. Phosphoric acid fertilizer used in most farmhouses in Korea is mainly made by processing phosphorus.
여기서 인광석은 매년 150만톤, 8000만 달러 규모가 수입되고, 인광석을 이용한 인산비료 생산 공정을 마치면 인산부산석고가 쌓이게 되는데, 연간 이렇게 쌓인 인산부산석고의 양은 무려 450 만톤에 달한다.Phosphoric acid gypsum gypsum is accumulated every year when 1.5 million tons and 80 million dollars of phosphorus are imported and phosphoric acid phosphate fertilizer production process is completed. The amount of phosphorus gypsum gypsum accumulated this year is about 4.5 million tons.
특히 인산부산석고는 건자재나 화공약품, 시멘트 부자재 등으로 사용할 수 있지만 인산비료를 만든 인산부산석고는 카드뮴, 납 등 인체에 해로운 중금속이 너무 많아 그동안 크게 재활용되지 못했다.In particular, phosphorus gypsum gypsum can be used as building material, chemical agent, and cement auxiliary material, but phosphorus gypsum gypsum made from phosphoric acid fertilizer has not been recycled greatly because of heavy metals such as cadmium and lead which are harmful to human body.
그러나 인산부산석고는 석고보드뿐만 아니라 석고플라스터, 소석고, 석고수지몰탈 등으로 활용되며 포장도로나 공유수면매립지의 토양 개량제조성물 혹은 콘크리트나 시멘트 부자재 등으로 활용하는 등 재활용 가치가 높은 폐기물이다.However, phosphorus gypsum gypsum is used not only as gypsum board but also as gypsum plaster, gypsum gypsum, gypsum resin mortar, etc. It is a highly recycled waste material, for example, as a soil improvement agent composition for pavement roads or a shared water surface landfill, or as concrete or cement auxiliary materials.
이러한 인산부산석고는 지금까지는 전량 시멘트회사로 보내 몰탈에 혼합하여 시멘트 제조 용도로 쓰이고 있으며, 최근 설비의 증설로 발생량은 증가하고 있으나 건설경기 하강으로 재활용률이 급감하여 신규 재활용 방안이 시급한 실정이다.These gypsum gypsum gypsum gypsum has been sent to cement companies so far and mixed with mortar to manufacture cement. Recently, the amount of gypsum has been increasing due to facility expansion, but the recycling rate has dropped sharply due to the downturn of the construction industry.
한편, KR슬래그는 고로에서 생산된 용선(쇳물)의 탄소량을 줄이고 불순물(인과 유황)을 제거하는 용선예비처리공정에서 발생하는 슬래그의 일종으로 규산 및 알칼리 성분인 MgO가 다량 함유되어 있으나, 현실적으로 재활용 빈도가 낮은 실정이다.
On the other hand, KR slag is a kind of slag generated in the pre-treatment process of molten iron that reduces the amount of carbon in molten iron produced in the blast furnace and removes impurities (phosphorus and sulfur), and contains a large amount of silicic acid and alkaline MgO. However, Recycling frequency is low.
이처럼 본 발명은 상기와 같은 종래의 문제점을 해결하기 위해 안출한 것으로서,The present invention has been made to solve the above-mentioned problems occurring in the prior art,
본 발명은 알칼리 성분을 포함한 KR슬래그를 이용하여 중금속 성분을 포함한 인산부산석고를 안정화시켜 폐기물 발생량을 줄이고 고화물의 중금속 용출농도 환경기준을 만족하는 KR슬래그를 이용한 토양 개량제 조성물 및 그의 제조방법을 제공함에 목적이 있다.
Provided is a soil amendment composition using a KR slag and a method for manufacturing the same, which stabilizes phosphorus gypsum containing heavy metal components by using KR slag containing an alkali component, thereby reducing the amount of waste generated and satisfying the environmental standard of heavy metal leaching concentration There is purpose in.
상기 목적을 달성하기 위한 본 발명 KR슬래그를 이용한 토양 개량제 조성물 제조방법은,In order to accomplish the above object, the present invention provides a method for preparing a soil conditioner composition using KR slag,
인산부산석고를 분쇄하는 제1단계; A first step of pulverizing phosphorus gypsum gypsum;
상기 분쇄된 인산부산석고에 KR슬래그를 혼합하여 안정화시키는 제2단계; A second step of mixing and stabilizing the crushed phosphate gypsum with KR slag;
상기 안정화된 혼합물에 산성물질 및 코크스 탈황석고를 혼합하여 중화시키는 제3단계; A third step of mixing and neutralizing the stabilized mixture with an acidic substance and cokesulfurized gypsum;
상기 중화된 혼합물을 양생하는 제4단계;를 포함하는 것을 특징으로 한다.And a fourth step of curing the neutralized mixture.
여기서 상기 제1단계는 분쇄기를 이용하여 인산부산석고를 50 내지 100㎛ 크기의 미세분말로 분쇄시키는 것을 특징으로 한다.The first step is characterized by pulverizing the phosphorus gypsum with fine powder having a size of 50 to 100 mu m using a pulverizer.
또한, 상기 제2단계는 분쇄된 인산부산석고 100중량부를 기준으로 KR슬래그 20 내지 30중량부를 혼합하는 것을 특징으로 한다.In the second step, 20 to 30 parts by weight of KR slag is mixed based on 100 parts by weight of pulverized phosphorus gypsum.
이때 상기 제2단계에서 pH 2 내지 4의 인산부산석고와 pH 10 내지 14의 KR슬래그를 포함하는 것을 특징으로 한다.In this case, in the second step, the phosphorus gypsum of pH 2 to 4 and the KR slag of pH 10 to 14 are included.
한편, 상기 제3단계는 안정화된 혼합물 100중량부를 기준으로 산성물질 1 내지 5중량부, 코크스 탈황석고 50 내지 80중량부를 포함하는 것을 특징으로 한다.Meanwhile, the third step is characterized by containing 1 to 5 parts by weight of an acidic substance and 50 to 80 parts by weight of a coke desulfurization gypsum based on 100 parts by weight of the stabilized mixture.
특히 상기 제3단계에서 상기 혼합물의 pH 농도가 6 내지 8을 만족하도록 산성물질 및 코크스 탈황석고를 인산부산석고를 혼합하는 것을 특징으로 한다.The acidic substance and the cokes desulfurized gypsum are mixed with the gypsum phosphate gypsum so that the pH of the mixture is 6 to 8 in the third step.
그리고 상기 제4단계는 중화된 혼합물을 1일 내지 5일 동안 양생하는 것을 특징으로 한다.And the fourth step is characterized in that the neutralized mixture is cured for 1 to 5 days.
아울러 상기 목적을 달성하기 위한 본 발명 KR슬래그를 이용한 토양 개량제 조성물은,According to another aspect of the present invention, there is provided a soil improver composition using KR slag,
상기의 KR슬래그를 이용한 토양 개량제 조성물 제조방법에 의하여 제조하는 것을 특징으로 한다.
And a soil improving agent composition using the KR slag.
본 발명은 인산부산석고에 포함된 중금속 유해물질을 기준치 이하로 감소시켜 유용한 토양 개량제로 활용할 수 있는 효과를 갖는다.The present invention has the effect of reducing heavy metal harmful substances contained in the phosphorus gypsum gypsum to below the standard value and utilizing it as a useful soil conditioner.
특히 본 발명은 인산부산석고의 pH를 중성 수준으로 유지시켜 토양 개량제의 활용범위를 향상할 수 있는 효과를 갖는다.In particular, the present invention has the effect of improving the application range of the soil conditioner by maintaining the pH of the gypsum phosphate gypsum at a neutral level.
또한, 본 발명은 토양의 중성화를 통해 작물의 생장을 촉진할 수 있는 유익한 효과를 갖는다.Further, the present invention has a beneficial effect of promoting the growth of crops through neutralization of the soil.
아울러 본 발명은 폐기되는 인산부산석고 및 KR슬래그를 재활용함으로써 환경오염 피해를 줄일 수 있음은 물론 토양 개량제 제조에 있어 비용 절감 효과를 갖는다.
In addition, the present invention has the effect of reducing environmental pollution damage by recycling disused phosphorus gypsum and KR slag, as well as cost saving in the production of soil amendment agent.
도 1은 본 발명 KR슬래그를 이용한 토양 개량제 조성물 제조방법에 대한 개략적인 순서도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic flow diagram of a method for preparing a soil conditioner composition using KR slag according to the present invention. FIG.
상기한 바와 같이 본 발명의 구성을 첨부한 도면에 의해 상세히 설명하면 다음과 같다.As described above, the construction of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명 KR슬래그를 이용한 토양 개량제 조성물 제조방법에 대한 개략적인 순서도를 도시한 것이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic flow diagram of a method for preparing a soil conditioner composition using KR slag according to the present invention.
이하에서는 본 발명 KR슬래그를 이용한 토양 개량제 조성물 제조방법의 바람직한 실시예에 관하여 상세하게 설명하기로 한다.Hereinafter, preferred embodiments of the method for producing a soil conditioner composition using the KR slag of the present invention will be described in detail.
본 발명 KR슬래그를 이용한 토양 개량제 조성물 제조방법은,The present invention provides a method for producing a soil conditioner composition using KR slag,
인산부산석고를 분쇄하는 제1단계; A first step of pulverizing phosphorus gypsum gypsum;
상기 분쇄된 인산부산석고에 KR슬래그를 혼합하여 안정화시키는 제2단계; A second step of mixing and stabilizing the crushed phosphate gypsum with KR slag;
상기 안정화된 혼합물에 산성물질 및 코크스 탈황석고를 혼합하여 중화시키는 제3단계; A third step of mixing and neutralizing the stabilized mixture with an acidic substance and cokesulfurized gypsum;
상기 중화된 혼합물을 양생하는 제4단계;를 포함하는 것을 특징으로 한다.And a fourth step of curing the neutralized mixture.
1. 이하 상기 제1단계를 설명한다.1. The first step will be described below.
상기 제1단계는 인산부산석고를 해머밀 또는 분쇄와 혼합이 동시에 이루어지는 해머밀 믹서를 이용하여 50 내지 100㎛ 크기의 미세분말로 분쇄시킨다.In the first step, phosphorus gypsum is pulverized into a fine powder having a size of 50 to 100 탆 by using a hammer mill or a hammer mill mixer which is simultaneously pulverized and mixed.
여기서 상기 인산부산석고의 분말 입자 크기가 50㎛ 미만인 경우 바람이 불면 비산 현상이 심하여 재료의 손실이 발생하고, 반대로 100㎛ 초과할 경우 KR슬래그와 혼합효율이 저하되는 한계를 갖는다.If the particle size of the phosphorus gypsum gypsum is less than 50 탆, the material is lost due to excessive scattering when the wind is blown. On the contrary, when the size is more than 100 탆, the mixing efficiency with the KR slag is limited.
본 발명에서 상기 KR슬래그는 내부에 포함한 철성분을 제거하기 위해서 물리적 방식과 화학적 방식을 적용하였다.In the present invention, the KR slag is subjected to a physical method and a chemical method in order to remove the iron component contained in the KR slag.
이때 상기 물리적 방식으로 부유 비중의 차이를 이용하여 철 성분을 선별하여 제거하거나, 화학적 방식으로 500 내지 800℃의 열처리 과정을 통하여 철 성분을 화학적으로 환원한 후 자성체를 이용하여 철분을 제거할 수 있다.At this time, the iron component may be selectively removed using the difference in floating specific gravity, or the iron component may be chemically reduced through a heat treatment process at 500 to 800 ° C by a chemical method, and then the iron component may be removed using a magnetic body .
2. 이하 상기 제2단계를 설명한다.2. The second step will be described below.
상기 제2단계는 분쇄된 인산부산석고 100중량부를 기준으로 KR슬래그 20 내지 30중량부를 혼합하여 KR슬래그에 포함한 알칼리 성분이 인산부산석고에 포함한 중금속 성분을 안정화시킨다.In the second step, 20 to 30 parts by weight of KR slag is mixed based on 100 parts by weight of pulverized phosphorus gypsum, thereby stabilizing heavy metal components contained in the KR slag in alkali phosphate gypsum.
여기서 KR슬래그가 20중량부 미만일 경우 인산부산석고의 중금속 성분을 효과적으로 제거할 수 없으며, 반대로 30중량부를 초과할 경우 불필요하게 과다적용으로 토양에 알칼리 성분이 축적되는 문제를 갖는다.If the KR slag is less than 20 parts by weight, the heavy metal component of the gypsum gypsum phosphate can not be effectively removed. On the contrary, if the amount exceeds 30 parts by weight, the alkali component is accumulated in the soil unnecessarily.
3. 이하 상기 제3단계를 설명한다.3. The third step will be described below.
상기 제3단계는 안정화된 혼합물 100중량부를 기준으로 산성물질 1 내지 5중량부, 코크스 탈황석고 50 내지 80중량부를 혼합한다.In the third step, 1 to 5 parts by weight of an acidic substance and 50 to 80 parts by weight of cokesulfurized gypsum are mixed based on 100 parts by weight of the stabilized mixture.
여기서 상기 산성물질은 중화반응을 활성화하기 위해 산성물질로 황산, 황산제이철, 인산, 황산제일철 또는 이들 중 어느 하나 이상을 포함한다.Here, the acidic substance includes sulfuric acid, ferric sulfate, phosphoric acid, ferrous sulfate or any one or more of these as an acidic substance for activating the neutralization reaction.
이때 상기 산성물질 1중량부 미만을 경우 안정화된 혼합물의 중화효율이 저하되고, 반대로 산성물질이 5중량부 초과할 경우 상기 KR슬래그와 인위적인 발열반응을 증가하는 문제를 갖는다.At this time, if the acidic substance is less than 1 part by weight, the neutralization efficiency of the stabilized mixture is lowered. On the other hand, if the acidic substance exceeds 5 parts by weight, the KR slag and the artificial exothermic reaction are increased.
또한, 상기 코크스 탈황석고 50중량부 미만일 경우 유동성이 저하되어 상기한 성능발현이 이루어지지 않으며, 반대로 80중량부를 초과할 경우 과다 사용으로 인해 중화효율이 저하되는 문제를 갖는다.When the cokes desulfurization gypsum is less than 50 parts by weight, the fluidity is lowered and the performance is not exhibited. On the contrary, when the cokes desulfurization gypsum is more than 80 parts by weight, the neutralization efficiency is lowered due to excessive use.
4. 이하 상기 제4단계를 설명한다.4. The fourth step will be described below.
상기 제4단계는 중화된 혼합물을 1일 내지 5일 동안 양생한다.In the fourth step, the neutralized mixture is cured for 1 to 5 days.
특히 상기 제4단계에서는 산과 알칼리 중화반응이 일어나 발열이 진행되며, 코크스 탈황석고에 다량 함유된 산화칼슘이 지속적인 수화반응 및 포졸란 반응을 일으키면서 안정화된다. Particularly, in the fourth step, an acid and an alkali neutralization reaction occur and heat generation proceeds, and calcium oxide contained in a large amount in the coke desulfurization gypsum is stabilized while causing continuous hydration reaction and pozzolan reaction.
이하, 상기 목적을 이루기 위한 본 발명의 구체적인 실시예를 살펴보기로 한다.Hereinafter, specific embodiments of the present invention will be described in order to accomplish the above object.
통상 산성화된 토양은 생장이 왕성한 어린잎의 선단이 희어지고 얼마 후에 갈색으로 고사하게 되기 때문에 우선은 각 작물별로 알맞은 토양 pH로 토양산도를 조절해 주어야 하는데, 여기에 사용된 토양 개량제로서 본 발명의 인산부산석고와 KR슬래그 혼합물 및 산성물질과 코크스 탈황석고를 사용한다.In general, acidified soils have to be adjusted to the soil pH at the appropriate soil pH for each crop, since the tip of the young leaf, which grows vigorously, is usually whitened and shortly brown afterwards. Phosphoric acid gypsum and KR slag mixture, acidic material and coke desulfurized gypsum are used.
즉, 본 발명의 토양 개량제는 pH 2 내지 4의 인산부산석고와, 알칼리성 제재인 pH 10 내지 14의 KR슬래그를 혼합하여 안정화하고, pH 농도가 6 내지 8을 만족하도록 산성물질 및 코크스 탈황석고를 안정화된 인산부산석고에 혼합함이 바람직하다.That is, the soil amendment agent of the present invention is prepared by mixing and stabilizing a phosphoric acid gypsum of pH 2 to 4 with a KR slag of pH 10 to 14, which is an alkaline agent, and acidic substances and cokesulfurized gypsum so that the pH concentration is 6 to 8 It is preferable to mix it with stabilized phosphoric acid gypsum.
상기에서 pH 농도를 10 내지 14로 한정하는 이유는 pH 농도가 10 미만일 경우 토양의 산성화로 인해 작물내 세포액이 산성으로 되어서 각종 병해를 받기 쉽게 되고 뿌리의 세포분열이 정지되고, 또한 토양이 산성으로 되기 때문에 알루미늄, 철, 망간, 아연 등이 용해되기 쉽게 되어서 이들의 과잉흡수 장애가 나타나게 된다.The reason for limiting the pH concentration to 10 to 14 is that when the pH is less than 10, the acidity of the soil causes the cell liquid in the crop to become acidic, which is liable to cause various diseases, and the cell division of the root is stopped, Aluminum, iron, manganese, zinc, and the like are liable to be dissolved.
또한, pH가 14를 초과할 경우 토양 개량제를 사용하게 되면 토양이 알칼리성 쪽으로 변하게 되어 철, 망간, 아연, 붕소 등이 용해되기 어렵게 되고, 작물은 이들 원소의 결핍증을 보이게 된다. Also, when the pH is above 14, the use of a soil conditioner causes the soil to become alkaline, making it difficult for iron, manganese, zinc, and boron to dissolve, and the crops show deficiency of these elements.
따라서 석회성분을 적당하게 흡수시키려면 채소 등을 심기전에 상기 농도범위 내에서 pH를 적당히 조절하여 각 작물에 적당한 농도가 되도록 조절해야 한다.Therefore, in order to properly absorb lime components, the pH should be adjusted appropriately to the appropriate concentration in each crop before planting the vegetables.
한편, KR슬래그를 기본 원료로 하는 본 발명 토양 개량제 사용 시 작물의 생육특성 효과를 확인하기 위해 호밀과 보리 각각에 대한생육특성을 비교해 보았으며, 그에 따른 결과를 하기 실시예를 통해 살펴보기로 한다.On the other hand, in order to confirm the effect of the growth characteristics of the present invention on the use of the soil improving agent of the present invention using KR slag as a basic raw material, the growth characteristics of each of rye and barley were compared and the results thereof will be described with reference to the following examples .
본 실시예에서는 본 발명의 토양 개량제를 첨가한 토양에서 호밀의 생육특성을 실험하였으며, 이를 기존의 일반토양과 KR슬래그 또는 인산부산석고 단독으로 처리하였을 때와 비교한 결과를 하기 표 1에 나타내었다.In this example, the growth characteristics of rye in the soil with the soil remediation agent of the present invention were tested, and the results are shown in Table 1 as compared with that of the conventional soil, KR slag or phosphate gypsum alone .
상기 결과를 통해 알 수 있듯이, 호밀의 수확 후 완전히 건조를 한 후의 건물 무게를 비교한 결과, 인산부산석고와 KR슬래그를 혼합한 본 발명의 토양 개량제의 사용 시 동일 면적당 곡물 수확량이 가장 높게 나타남을 확인할 수 있었다.As can be seen from the above results, when the weights of the rye after harvesting were compared with each other, the grain yield per area was highest in the case of using the soil improving agent of the present invention in which phosphorus gypsum plaster and KR slag were mixed I could confirm.
본 실시예에서는 보리파종을 한 것으로 결과를 하기의 표 2에 나타내었다.In this Example, barley seeding was performed, and the results are shown in Table 2 below.
상기 결과에 따른 건물률을 비교해 보아도, 본 발명의 토양 개량제를 사용한 토양에서의 보리 건물률이 가장 높게 나타남을 확인할 수 있었다.As a result of comparing the building rates according to the above results, it was confirmed that the barley building ratio in the soil using the soil improvement agent of the present invention is the highest.
이처럼 상기와 같이 본 발명의 실시한 예에 대하여 상세히 설명하였으나, 본 발명의 권리범위는 이에 한정되지 않으며, 본 발명의 실시한 예와 실질적으로 균등의 범위에 있는 것까지 본 발명의 권리범위가 포함되는 것은 당연하다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Of course.
Claims (8)
상기 분쇄된 인산부산석고에 KR슬래그를 혼합하여 안정화시키는 제2단계;
상기 안정화된 혼합물에 산성물질 및 코크스 탈황석고를 혼합하여 중화시키는 제3단계;
상기 중화된 혼합물을 양생하는 제4단계;를 포함하되,
상기 제1단계는 분쇄기를 이용하여 인산부산석고를 50 내지 100㎛ 크기의 미세분말로 분쇄하는 것이고, 상기 제2단계는 분쇄된 인산부산석고 100중량부를 기준으로 KR슬래그 20 내지 30중량부를 포함하며, 상기 제2단계에서 pH 2 내지 4의 인산부산석고와 pH 10 내지 14의 KR슬래그를 혼합하고, 상기 KR슬래그는 내부에 포함한 철성분을 제거하기 위해서 물리적 방식 또는 화학적 방식을 적용하되, 상기 물리적 방식으로 부유 비중의 차이를 이용하여 철 성분을 선별하여 제거하고, 상기 화학적 방식으로 500 내지 800℃의 열처리 과정을 통하여 철 성분을 화학적으로 환원한 후 자성체를 이용하여 철분을 제거하는 것이며, 상기 제3단계는 안정화된 혼합물 100중량부를 기준으로 산성물질 1 내지 5중량부, 코크스 탈황석고 50 내지 80중량부를 포함하고, 상기 제3단계에서 상기 혼합물의 pH 농도가 6 내지 8이 되도록 산성물질 및 코크스 탈황석고를 인산부산석고를 혼합하며, 상기 제3단계에서 상기 산성물질은 중화반응을 활성화하기 위해 산성물질로 황산, 황산제이철, 인산, 황산제일철 또는 이들 중 어느 하나 이상을 포함하는 것이고, 상기 제4단계는 중화된 혼합물을 1일 내지 5일 동안 양생하는 것을 특징으로 하는 KR슬래그를 이용한 토양 개량제 조성물 제조방법.A first step of pulverizing phosphorus gypsum gypsum;
A second step of mixing and stabilizing the crushed phosphate gypsum with KR slag;
A third step of mixing and neutralizing the stabilized mixture with an acidic substance and cokesulfurized gypsum;
And a fourth step of curing the neutralized mixture,
In the first step, the phosphorus gypsum is pulverized into fine powder having a size of 50 to 100 탆 using a pulverizer, and the second step includes 20 to 30 parts by weight of KR slag based on 100 parts by weight of pulverized phosphorus gypsum gypsum , The phosphorus gypsum of pH 2 to 4 and the KR slag of pH 10 to 14 are mixed in the second step and the KR slag is subjected to a physical or chemical method in order to remove the iron component contained therein, The iron component is chemically reduced through the heat treatment at 500 to 800 ° C by the chemical method and the iron component is removed by using the magnetic substance, Step 3 comprises 1 to 5 parts by weight of an acidic substance based on 100 parts by weight of the stabilized mixture, and 50 to 80 parts by weight of cokesulfurized gypsum, The acidic substance and the cokes desulfurized gypsum are mixed with the gypsum phosphate gypsum so that the pH of the mixture is 6 to 8. In the third step, the acidic substance is mixed with sulfuric acid, ferric sulfate, phosphoric acid, Ferrous sulfate or any one of them, and the fourth step is to cure the neutralized mixture for 1 to 5 days.