KR101850382B1 - A B ST omitted - Google Patents
A B ST omitted Download PDFInfo
- Publication number
- KR101850382B1 KR101850382B1 KR1020160140967A KR20160140967A KR101850382B1 KR 101850382 B1 KR101850382 B1 KR 101850382B1 KR 1020160140967 A KR1020160140967 A KR 1020160140967A KR 20160140967 A KR20160140967 A KR 20160140967A KR 101850382 B1 KR101850382 B1 KR 101850382B1
- Authority
- KR
- South Korea
- Prior art keywords
- boron nitride
- tio
- nitride nano
- nano
- carbon
- Prior art date
Abstract
Description
본 발명은The present invention
1. 1) 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 질화 붕소 나노 ST (질화 붕소 나노 시트 나노 튜브)에 TiO2 나노 분말을 첨가 혼합시켜 구성한 a.TiO2·질화 붕소 나노 ST1. 1) a. TiO 2 · boron nitride nano-ST (boron nitride nano-sheet) composed of a mixture of boron nitride nanosheets and boron nitride nanotubes and adding TiO 2 nanoparticles to boron nitride nano ST
2) a.TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT (그래핀과 CNT를 혼합하여 구성) 중에서 하나를 선택한 탄소를 첨가 혼합시켜 b.탄소·TiO2·질화 붕소 나노 ST 구성하여2) a.TiO 2 · boron nitride Nano ST · graphene · CNT · graphene CNT (composed of graphene and CNT mixed) · carbon · TiO 2 · boron nitride nano Configure ST
2. 1) 나노 섬유 내에 a.TiO2·질화 붕소 나노 ST가 내재된 A형 질화 붕소 나노 ST 나노 섬유를 구성하거나, 또는2. 1) A type boron nitride nano ST nanofiber with a .TiO 2 · boron nitride nano ST embedded in the nanofiber, or
2) 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST가 내재된 B형 질화 붕소 나노 ST 나노 섬유를 구성하고자 하는것이다2) In order to construct B-type boron nitride nano ST nanofibers having carbon · TiO 2 · boron nitride nano ST embedded in nanofiber
본 발명에 있어.In the present invention.
① 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 구성한 질화 붕소 나노 ST의 특성은 - 절연체로써, 방사능차폐 및 수소저장 기능을 나타내며, 질화 붕소 나노 시트나 질화 붕소 나노 튜브 보다 강도성, 방열성이 우수하면서, CNT나 그래핀보다 내열성, 내산화성, 내마모성이 우수하다.① The characteristics of boron nitride nanostructures composed of boron nitride nanosheets and boron nitride nanotubes - As an insulator, it exhibits radioactivity shielding and hydrogen storage function, and is superior in strength and heat dissipation to boron nitride nanosheets and boron nitride nanotubes. , It is superior in heat resistance, oxidation resistance and abrasion resistance than CNT and graphene.
② TiO2 나노 분말의 특성은 - 정전기 방지 및 광촉매 기능과 정화 기능을 나타내며.② The characteristics of TiO 2 nanoparticles - Antistatic and photocatalytic function and purification function.
③ 그래핀, CNT, 그래핀 CNT 중에서 하나를 선택한 탄소의 특성은 - 전기 전도성, 강도성, 방열성이 우수한 특성을 나타내는 바.③ The characteristics of carbon selected from among graphene, CNT and graphene CNT are characterized by excellent electrical conductivity, strength and heat dissipation.
본 발명은The present invention
1. 1) 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 질화 붕소 나노 ST를 구성한 후, TiO2 나노 분말을 첨가 혼합시켜 a.TiO2·질화 붕소 나노 ST를 구성하거나.1. 1) A boron nitride nano-ST is formed by mixing a boron nitride nanosheet and a boron nitride nanotube, and then a TiO 2 nano powder is added and mixed to form a .TiO 2 · boron nitride nano ST.
2) a.TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT 중에서 하나를 선택한 탄소를 첨가 혼합시켜 b.탄소·TiO2·질화 붕소 나노 ST를 구성한 후2) a.TiO 2 · boron nitride Nano ST · graphene · CNT · graphene CNT · carbon · TiO 2 · boron nitride nano ST
2. 1) 용매에 a.TiO2·질화 붕소 나노 ST와 계면 활성제를 첨가 초음파로 분산시킨 후, 고분자 분말을 첨가하고 60℃~100℃에서 교반하여 용해시켜 TiO2·질화 붕소 나노 ST/고분자 용액을 구성하거나, 또는2. 1) a.TiO 2 · boron nitride Nano ST and a surfactant are added to the solvent and dispersed by ultrasonication. Polymer powder is added and dissolved by stirring at 60 ° C to 100 ° C to form TiO 2 · boron nitride nano ST / polymer Solution, or
2) 용매에 b.탄소·TiO2·질화 붕소 나노 ST와 계면 활성제를 첨가하고 초음파로 분산시킨후, 고분자 분말을 첨가하고 60℃~100℃에서 교반하여 용해시켜 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 구성한 후.2) Carbon, TiO 2 · Boron nitride NNO and surfactant are added to the solvent and dispersed by ultrasonic wave. Polymer powder is added and dissolved by stirring at 60 ° C to 100 ° C to form carbon · TiO 2 · boron nitride nano After constructing the ST / polymer solution.
3. 1) TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사법으로 나노 섬유내에 a.TiO2·질화 붕소 나노 ST를 내재시켜서 직경 20nm~80nm의 TiO2·질화 붕소 나노 ST의 특성을 나타내는 나노 섬유인 A형 질화 붕소 나노 ST 나노 섬유를 구성하거나3. 1) TiO 2 · by the boron nitride, nano-ST / polymer solution inherent a.TiO 2 · boron nitride nano-ST in the nanofiber by electrospinning a high voltage representing a TiO 2 · Properties of boron nitride, nano-ST having a diameter of 20nm ~ 80nm Type N nanofiber N-type STN nanofiber
탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사법으로 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST를 내재시켜서 직경 20nm~80nm의 탄소·TiO2·질화 붕소 나노 ST의 특성을 나타내는 나노 섬유인 B형 질화 붕소 나노 ST 나노 섬유를 구성하고자 하는것이다.Carbon · TiO 2 · Boron nitride Nano ST · Polymer solution by high-voltage electrospinning in nanofiber b. Carbon · TiO 2 · Boron nitride Nano ST By incorporating ST in a carbon, TiO 2 · Boron nitride nano ST Type N-type STN nanofibers, which is a nanofiber B-type nitride nanowire.
본 발명은The present invention
1. 1) 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 질화 붕소 나노 ST를 구성한 후, TiO2 나노 분말을 첨가 혼합시켜 a.TiO2·질화 붕소 나노 ST를 구성하거나1. 1) A boron nitride nano-ST is formed by mixing a boron nitride nanosheet and a boron nitride nanotube, and then a TiO 2 nano powder is added and mixed to form a TiO 2 · boron nitride nano ST
2) a.TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT 중에서 하나를 선택한 탄소를 첨가 혼합시켜 b.탄소·TiO2·질화 붕소 나노 ST를 구성한 후,2) aTiO 2 · boron nitride nano ST · graphene · CNT · graphene CNT · carbon · TiO 2 · boron nitride nano ST,
2 1). 전기 방사법으로 나노 섬유 내에 a.TiO2·질화 붕소 나노 ST가 내재된 A형 질화 붕소 나노 ST 나노 섬유를 구성하거나 또는2 1). A nanotubes of type A boron nitride nanotubes containing a.TiO 2 · boron nitride nanostructures are formed in the nanofiber by electrospinning, or
2) 전기 방사법으로 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST가 내재된 B형 질화 붕소 나노 ST 나노 섬유를 구성하는 것이 해결하고자 하는 과제이다.2) Formation of B-type boron nitride STN nanofibers with carbon · TiO 2 · boron nitride nano-ST embedded in nanofiber by electrospinning is a problem to be solved.
따라서 본 발명은.Therefore,
1단계 : 1) a.TiO2·질화 붕소 나노 ST 2) b.탄소·TiO2·질화 붕소 나노 ST 제조 단계Step 1: a) TiO 2 · Boron nitride Nano ST 2) b) Carbon · TiO 2 · Boron nitride Nano ST
1) a.TiO2·질화 붕소 나노 ST 구성.1) a.TiO 2 · boron nitride nano ST configuration.
질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 질화 붕소 나노 ST를 구성한 후 TiO2 나노 분말을 첨가 혼합시켜 a.TiO2·질화 붕소 나노 ST를 구성하고A boron nitride nano-ST is formed by mixing a boron nitride nanosheet and a boron nitride nanotube, and then a TiO 2 nano powder is added and mixed to form a TiO 2 · boron nitride nano ST
2) b.탄소·TiO2·질화 붕소 나노 ST 구성.2) b. Carbon · TiO 2 · boron nitride nano ST configuration.
a. TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT(그래핀과 CNT를 혼합시켜 구성) 중에서 하나를 선택한 탄소를 첨가 혼합시켜서 b.탄소·TiO2·질화 붕소 나노 ST를 구성한후a. TiO 2 · Nitride Nitrogen ST · Carbide · TiO 2 · Nitride Nitrogen ST · After forming carbon · TiO 2 · Nitrogen Nitride ST by adding carbon selected from among carbon grains and CNT graphene CNT
2단계: 1) TiO2·질화 붕소 나노 ST/고분자 용액 2) 탄소·TiO2·질화 붕소 나노 ST/고분자 용액 제조 단계Step 2: 1) TiO 2 · boron nitride nano ST / polymer solution 2) carbon · TiO 2 · boron nitride nano ST / polymer solution
1) TiO2·질화 붕소 나노 ST/고분자 용액 구성.1) Structure of TiO 2 · boron nitride nano ST / polymer solution.
NMP, DMF, THF, 톨루엔, 아세톤, 알콜 중에서 선택한 용매에 a.TiO2·질화 붕소 나노 ST와 계면 활성제(소듐 도데 설페이트)를 넣고 초음파로 분산시킨후, 고분자 분말을 첨가하고 60℃~100℃로 교반하여 용해시켜서 TiO2·질화 붕소 나노 ST/고분자 용액을 구성하거나A.TiO 2 · boron nitride Nano ST and a surfactant (sodium dodecyl sulfate) are added to a solvent selected from NMP, DMF, THF, toluene, acetone and alcohol, and dispersed by ultrasonic waves. To form a TiO 2 · boron nitride nano-ST / polymer solution or
(용매에 TiO2(고분자 분말의 0.1~3%)·질화 붕소 나노 ST(고분자 분말의 0.1~5%)와 계면 활성제(용매의 0.001~0.005%)와 고분자 분말(용매의 10~30%)을 첨가 60℃~100℃로 교반하여 용해시켜 구성한 TiO2·질화 붕소 나노 ST/고분자 용액)(0.1 to 3% of TiO 2 (0.1 to 3% of polymer powder), 0.1 to 5% of boron nitride nano ST (polymer powder), 0.001 to 0.005% of solvent and a polymer powder (10 to 30% of solvent) TiO 2 · boron nitride nano ST / polymer solution prepared by mixing and stirring at 60 ° C to 100 ° C)
2) 탄소·TiO2·질화 붕소 나노 ST/고분자 용액 구성.2) Composition of carbon · TiO 2 · boron nitride nano ST / polymer solution.
NMP, DMF, THF, 톨루엔, 아세톤, 알콜 중에서 선택한 용매에 b.탄소·TiO2·질화 붕소 나노 ST와 계면 활성제(소듐 도데 설페이트)를 넣고 초음파로 분산시킨후, 고분자 분말을 첨가하고 60℃~100℃로 교반하여 용해시켜서 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 구성한후B) Carbon, TiO 2 · Boron nitride Nano ST and a surfactant (sodium dodecyl sulfate) are added to the solvent selected from NMP, DMF, THF, toluene, acetone and alcohol, and dispersed by ultrasonic wave. And the mixture was stirred at 100 ° C for dissolution to form a carbon · TiO 2 · boron nitride nano ST / polymer solution
(용매에 탄소(고분자 분말의 0.1~5%)·TiO2(고분자 분말의 0.1~3%)·질화 붕소 나노 ST(고분자 분말의 0.1~5%)와 계면 활성제(용매의 0.001~0.005%)와 고분자 분말(용매의 10~30%)을 첨가 60℃~100℃로 교반하여 용해시켜 구성한 탄소·TiO2·질화 붕소 나노 ST/고분자 용액)(0.1 to 5% of the polymer powder), TiO 2 (0.1 to 3% of the polymer powder), boron nitride nano-ST (0.1 to 5% of the polymer powder) and the surfactant (0.001 to 0.005% of the solvent) And a polymer powder (10 to 30% of solvent) were added and dissolved by stirring at 60 ° C to 100 ° C to prepare a carbon · TiO 2 · boron nitride nano ST / polymer solution)
* 고분자 분말 : 폴리 카보네이트, 폴리 비닐 알콜, 폴리 메틸 메타 아크릴레이트, 폴리 에스테르, 폴리 아미드, 폴리 우레탄, 폴리 스티렌, 셀룰로오스, 폴리 비닐 아세테이트, 폴리 비닐 클로라이드, 폴리 아크릴산 수지, 폴리 올레핀, 폴리 에테르 우레탄, 셀룰로오스 아세테이트, 폴리 아미드/폴리 비닐리덴 플루오라이드, 폴리 에테르 우레탄, 폴리 메틸 아크릴레이트, 폴리 비닐 피롤리돈, 폴리 프로필렌 옥사이드, 폴리 에틸렌 옥사이드, 폴리 비닐 클로라이드, 폴리 아마이드, 폴리 아크릴로니트릴, 폴리 카프로락톤, 폴리 비닐리덴 플루오라이드 공중합체, 폴리 아크릴 공중합체, 폴리 비닐 아세테이트 공중합체.* Polymer powder: Polycarbonate, polyvinyl alcohol, polymethylmethacrylate, polyester, polyamide, polyurethane, polystyrene, cellulose, polyvinyl acetate, polyvinyl chloride, polyacrylic resin, polyolefin, polyether urethane, Polyvinylidene fluoride, polyvinylidene fluoride, polymethyl acrylate, polyvinyl pyrrolidone, polypropylene oxide, polyethylene oxide, polyvinyl chloride, polyamide, polyacrylonitrile, polycaprolactone , Polyvinylidene fluoride copolymer, polyacrylic copolymer, polyvinyl acetate copolymer.
3단계 : 1) A형 질화 붕소 나노 ST 나노 섬유 2) B형 질화 붕소 나노 ST 나노 섬유 제조 단계Step 3: 1) A-type boron nitride STN nanofibers 2) B-type boron nitride STN nanofibers
1) A형 질화 붕소 나노 ST 나노 섬유 구성(고전압 전기 방사법)1) Type A boron nitride nano ST nanofiber composition (high-voltage electrospinning)
TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사기의 노즐 방사구를 통해 전기 방사(전압 15kv~30kv, 방사속도 0.5~1.5ml/hr)시키고, 공급 노즐과 컬렉터 사이(거리 12cm~19cm)에 전기장을 형성시켜서 연신시킨후, 열처리(400℃~500℃) 시켜 나노 섬유 내에 a.TiO2·질화 붕소 나노 ST를 내재시켜서 a.TiO2·질화 붕소 나노 ST의 특성을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 A형 질화 붕소 나노 ST 나노 섬유TiO 2 · boron nitride Nano ST / polymer solution was electrospun (voltage 15kv ~ 30kv, emission rate 0.5 ~ 1.5ml / hr) through the nozzle discharge port of the high voltage electrospinning device and between the feed nozzle and collector (distance 12cm ~ 19cm) (400 ° C to 500 ° C), and a TiO 2 · boron nitride nano-ST is incorporated in the nanofiber to form a TiO 2 · boron nitride nano-ST having a diameter of 20 nm to 800 nm A-type boron nitride nano ST nanofibers composed of nanofibers
2) B형 질화 붕소 나노 ST 나노 섬유 구성(고전압 전기 방사법)2) B-type boron nitride nano ST nanofiber composition (high-voltage electrospinning)
탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사기의 노즐 방사구를 통해 전기 방사(전압 15kv~30kv, 방사속도 0.5~1.5ml/hr)시키고, 공급 노즐과 컬렉터 사이(거리 12cm~19cm)에 전기장을 형성시켜서 연신시킨후, 열처리(400℃~500℃)시켜 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST를 내재시켜서 b.탄소·TiO2·질화 붕소 나노 ST의 특성을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 B형 질화 붕소 나노 ST 나노 섬유 The carbon, TiO 2 , boron nitride Nano ST / polymer solution was electrospun (voltage 15kv ~ 30kv, radiation rate 0.5 ~ 1.5ml / hr) through the nozzle discharge port of the high voltage electrospinning device, B) Carbon, TiO 2 , and boron nitride nano-ST in the nanofiber, and b) Carbon, TiO 2 , and boron nitride nano-ST properties are obtained by annealing (400 ° C. to 500 ° C.) B-type boron nitride nano ST nanofibers composed of nanofibers having a diameter of 20 nm to 800 nm
본 발명인 1) A형 질화 붕소 나노 ST 나노 섬유는 - 나노 섬유 내에 a.TiO2·질화 붕소 나노 ST가 내재되어서 TiO2·질화 붕소 나노 ST의 특성을 나타내어 절연체로써, 방사능 차폐 및 수소 저장 기능을 나타내면서, 보다 강도성 내열성, 내산화성, 방열성, 내마모성이 우수하고, 정전기 방지 및 정화 기능을 나타내는 보다 기능적인 나노 섬유로 구성되어서, 방사능 차폐 나노 섬유나 수소 저장 나노 섬유, 내열 나노 섬유, 방탄 나노 섬유를 구성할수 있어 효과적이며,1) A-type boron nitride nano ST nanofibers of the present invention exhibit the characteristics of TiO 2 · boron nitride nano ST due to the presence of a .TiO 2 · boron nitride nano ST in the nanofiber. And is composed of more functional nanofibers exhibiting excellent strength, heat resistance, oxidation resistance, heat resistance and abrasion resistance, and exhibiting functions of preventing and purifying static electricity, so that radiation shielding nano fiber, hydrogen storage nano fiber, heat resistant nanofiber, It is effective,
2) B형 질화 붕소 나노 ST 나노 섬유는 - 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST가 내재되어서 탄소·TiO2·질화 붕소 나노 ST의 특성을 나타내어, 전기 전도성이 있으면서, 방사능 차폐 및 전자파 차폐와 수소 저장 기능을 나타내며, 강도성, 내열성, 내산화성, 방열성, 내마모성이 우수하고, 정전기 방지 및 정화 기능을 나타내는 보다 기능적인 나노 섬유로 구성되어서 방사능 차폐 및 전자파 차폐 나노 섬유나 방사능 차폐 및 수소 저장 나노 섬유, 내열 나노 섬유, 방사능 차폐 및 방탄 나노 섬유를 구성할수 있어 효과적이다.2) B-type boron nitride, nano-ST nano-fibers - be b a carbon · TiO 2 · boron nitride nano ST inherent in the nanofibers exhibits a carbon · TiO 2 · Properties of boron nitride, nano-ST, while the electrical conductivity, radiation shielding And electromagnetic shielding and hydrogen storage function. It is composed of more functional nanofibers which are excellent in strength, heat resistance, oxidation resistance, heat resistance and abrasion resistance and exhibit antistatic and purifying function, so that radioactive shielding and electromagnetic shielding nano fiber or radioactive shielding And hydrogen storage nanofibers, heat-resistant nanofibers, radiation shielding and anti-scattering nanofibers.
본 발명에 있어In the present invention
① 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 구성한 질화 붕소 나노 ST의 특성은 - 절연체로써, 방사능 차폐 및 수소 저장 기능을 나타내며, 질화 붕소 나노 시트나 질화 붕소 나노 튜브 보다 강도성, 방열성이 우수하고, CNT나 그래핀보다 내열성, 내산화성, 내마모성이 우수하다① The characteristics of boron nitride nanostructures composed of boron nitride nanosheets and boron nitride nanotubes - As an insulator, it exhibits radioactivity shielding and hydrogen storage function, and is superior in strength and heat dissipation to boron nitride nanosheets and boron nitride nanotubes. And is superior in heat resistance, oxidation resistance and abrasion resistance to CNT and graphene
② TiO2 나노 분말의 특성은 - 정전기 방지 및 광촉매 기능과 정화 기능을 나타내고② The characteristics of TiO 2 nanoparticles - Antistatic and photocatalytic function and purifying function
③ 그래핀, CNT, 그래핀 CNT 중에서 하나를 선택한 탄소의 특성은 - 전기 전도성, 강도성, 방열성이 우수하고, 전자파 차폐의 기능을 나타내는바,③ The characteristics of carbon selected from among graphene, CNT and graphene CNT are as follows: - Excellent electrical conductivity, strength and heat dissipation, and show the function of electromagnetic shielding.
본 발명은The present invention
1. 1) 질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합시켜 질화 붕소 나노 ST를 구성한 후, TiO2 나노 분말을 첨가 혼합시켜 a.TiO2·질화 붕소 나노 ST를 구성하거나 또는1. 1) A boron nitride nano-ST is formed by mixing a boron nitride nanosheet and a boron nitride nanotube, and then a TiO 2 nano powder is added to prepare a .TiO 2 · boron nitride nano ST or
2) a.TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT 중에서 하나를 선택한 탄소를 첨가 혼합시켜 b.탄소·TiO2·질화 붕소 나노 ST를 구성한 후.2) a. TiO 2 · boron nitride nano ST · graphene · CNT · graphene CNT · carbon · TiO 2 · boron nitride nano ST.
2. 1) 나노 섬유 내에 a.TiO2·질화 붕소 나노 ST가 내재된 A형 질화 붕소 나노 ST 나노 섬유를 구성하거나, 또는2. 1) A type boron nitride nano ST nanofiber with a .TiO 2 · boron nitride nano ST embedded in the nanofiber, or
2) 나노 섬유 내에 b.탄소·TiO2·질화 붕소 나노 ST가 내재된 B형 질화 붕소 나노 ST 나노 섬유를 구성하는것이 목적이다.2) The purpose is to make B-type boron nitride STN nanofibers with carbon · TiO 2 · boron nitride nano ST embedded in nanofiber.
따라서 본 발명은.Therefore,
1단계 : 1) a.TiO2·질화 붕소 나노 ST 2) b.탄소·TiO2·질화 붕소 나노 ST 제조 단계Step 1: a) TiO 2 · Boron nitride Nano ST 2) b) Carbon · TiO 2 · Boron nitride Nano ST
1) a.TiO2·질화 붕소 나노 ST 구성.1) a.TiO 2 · boron nitride nano ST configuration.
질화 붕소 나노 시트와 질화 붕소 나노 튜브를 혼합하여 질화 붕소 나노 ST를 구성한 후, TiO2 나노 분말을 첨가 혼합시켜서 a.TiO2·질화 붕소 나노 ST를 구성하고,A boron nitride nano-ST is formed by mixing a boron nitride nanosheet and a boron nitride nanotube, and then a TiO 2 nano powder is added and mixed to form a TiO 2 · boron nitride nano ST,
2) b.탄소·TiO2·질화 붕소 나노 ST 구성.2) b. Carbon · TiO 2 · boron nitride nano ST configuration.
a.TiO2·질화 붕소 나노 ST에 ㉠ 그래핀 ㉡ CNT ㉢ 그래핀 CNT(그래핀과 CNT를 혼합하여 구성) 중에서 하나를 선택한 탄소를 첨가 혼합시켜서 b.탄소·TiO2·질화 붕소 나노 ST를 구성한후a.TiO 2 · boron nitride Nano ST · graphene · CNT · graphene CNT (composed of a mixture of graphene and CNT), b. carbon · TiO 2 · boron nitride nano ST After configuring
2단계 : 1) TiO2·질화 붕소 나노 ST/고분자 용액 2) 탄소·TiO2·질화 붕소 나노 ST/고분자 용액 제조 단계Step 2: 1) TiO 2 · boron nitride nano ST / polymer solution 2) carbon · TiO 2 · boron nitride nano ST / polymer solution
1) TiO2·질화 붕소 나노 ST/고분자 용액 구성.1) Structure of TiO 2 · boron nitride nano ST / polymer solution.
NMP, DMF, THF, 톨루엔, 아세톤, 알콜 중에서 선택한 용매에 a.TiO2·질화 붕소 나노 ST와 계면 활성제(소듐 도데 설페이트)를 넣고 초음파로 분산시킨후, 고분자 분말을 첨가하고 60℃~100℃로 교반하여 용해시켜서 TiO2·질화 붕소 나노 ST/고분자 용액을 구성하거나A.TiO 2 · boron nitride Nano ST and a surfactant (sodium dodecyl sulfate) are added to a solvent selected from NMP, DMF, THF, toluene, acetone and alcohol, and dispersed by ultrasonic waves. To form a TiO 2 · boron nitride nano-ST / polymer solution or
(용매에 TiO2(고분자 분말의 0.1~3%)·질화 붕소 나노 ST(고분자 분말의 0.1~5%)와 계면 활성제(용매의 0.001~0.005%)와 고분자 분말(용매의 10~30%)을 넣고 60℃~100℃로 교반하여 용해시켜서 TiO2·질화 붕소 나노 ST/고분자 용액을 구성하거나(0.1 to 3% of TiO 2 (0.1 to 3% of polymer powder), 0.1 to 5% of boron nitride nano ST (polymer powder), 0.001 to 0.005% of solvent and a polymer powder (10 to 30% of solvent) And the mixture is stirred and dissolved at 60 ° C to 100 ° C to form a TiO 2 · boron nitride nano-ST / polymer solution
2) 탄소·TiO2·질화 붕소 나노 ST/고분자 용액 구성.2) Composition of carbon · TiO 2 · boron nitride nano ST / polymer solution.
NMP, DMF, THF, 톨루엔, 아세톤, 알콜 중에서 선택한 용매에 b.탄소·TiO2·질화 붕소 나노 ST와 계면 활성제(소듐 도데 설페이트)를 넣고 초음파로 분산시킨후, 고분자 분말을 첨가하고 60℃~100℃로 교반하여 용해시켜서 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 구성한후B) Carbon, TiO 2 · Boron nitride Nano ST and a surfactant (sodium dodecyl sulfate) are added to the solvent selected from NMP, DMF, THF, toluene, acetone and alcohol, and dispersed by ultrasonic wave. And the mixture was stirred at 100 ° C for dissolution to form a carbon · TiO 2 · boron nitride nano ST / polymer solution
(용매에 탄소(고분자 분말 0.1~5%)·TiO2(고분자 분말의 0.1~3%)·질화 붕소 나노 ST(고분자 분말의 0.1~5%)와 계면 활성제(용매의 0.001~0.005%)와 고분자 분말(용매의 10~30%)을 넣고 60℃~100℃로 교반하여 용해시켜서 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 구성한후.(0.1 to 5% of polymer powder) 0.1 to 3% of TiO 2 (0.1 to 3% of polymer powder) Boron nitride Nano ST (0.1 to 5% of polymer powder) and surfactant (0.001 to 0.005% of solvent) Polymer powder (10-30% of solvent) is added and dissolved by stirring at 60 ° C ~ 100 ° C to form carbon · TiO 2 · boron nitride nano ST / polymer solution.
* 고분자 분말 : 폴리 카보네이트, 폴리 비닐 알콜, 폴리 메틸 메타 아크릴레이트, 폴리 에스테르, 폴리 아미드, 폴리 우레탄, 폴리 스티렌, 셀룰로오스, 폴리 비닐 아세테이트, 폴리 비닐 클로라이드, 폴리 아크릴산 수지, 폴리 올레핀, 폴리 에테르 우레탄, 셀룰로오스 아세테이트, 폴리 아미드/폴리 비닐리덴 플루오라이드, 폴리 에테르 우레탄, 폴리 메틸 아크릴레이트, 폴리 비닐 피롤 리돈, 폴리 프로필렌 옥사이드, 폴리 에틸렌 옥사이드, 폴리 비닐 클로라이드, 폴리 아마이드, 폴리 아크릴로니트릴, 폴리 카프로락톤, 폴리 비닐리덴 플루오라이드 공중합체, 폴리 아크릴 공중합체, 폴리 비닐 아세테이트 공중합체 중에서 선택한 고분자 분말.* Polymer powder: Polycarbonate, polyvinyl alcohol, polymethylmethacrylate, polyester, polyamide, polyurethane, polystyrene, cellulose, polyvinyl acetate, polyvinyl chloride, polyacrylic resin, polyolefin, polyether urethane, Polyvinylidene fluoride, polyvinylidene fluoride, polymethyl acrylate, polyvinylpyrrolidone, polypropylene oxide, polyethylene oxide, polyvinyl chloride, polyamide, polyacrylonitrile, polycaprolactone, A polymer powder selected from polyvinylidene fluoride copolymer, polyacrylic copolymer, and polyvinyl acetate copolymer.
3단계 : 1) A형 질화 붕소 나노 ST 나노 섬유 2) B형 질화 붕소 나노 ST 나노 섬유 제조 단계Step 3: 1) A-type boron nitride STN nanofibers 2) B-type boron nitride STN nanofibers
1) A형 질화 붕소 나노 ST 나노 섬유 구성(고전압 전기 방사법)1) Type A boron nitride nano ST nanofiber composition (high-voltage electrospinning)
TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사기의 노즐 방사구를 통해 전기 방사(전압 15kv~30kv, 방사 속도 0.5~1.5ml/hr)시키고, 공급 노즐과 컬렉터 사이(거리 12cm~19cm)에 전기장을 형성시켜서 연신시킨후, 열처리(400℃~500℃)시켜 나노 섬유에 a.TiO2·질화 붕소 나노 ST를 내재시켜서 a.TiO2·질화 붕소 나노 ST의 특성(절연체로써, 방사능 차폐 및 수소 저장 기능과 강도성, 내열성, 내산화성, 방열성, 내마모성이 우수하고 정전기 방지 및 광촉매 기능과 정화 기능)을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 A형 질화 붕소 나노 ST 나노 섬유.TiO 2 · boron nitride Nano ST / polymer solution was electrospun (voltage 15kv ~ 30kv, emission rate 0.5 ~ 1.5ml / hr) through the nozzle discharge port of the high voltage electrospinning device and between the feed nozzle and collector (distance 12cm ~ 19cm) (400 캜 to 500 캜), and then a .TiO 2 · boron nitride nano-ST is incorporated in the nanofiber. The characteristics of a .TiO 2 · boron nitride nano-ST (as an insulator, And N-type STN nanofibers composed of nanofibers having a diameter of 20 nm to 800 nm and exhibiting hydrogen storage function, strength, heat resistance, oxidation resistance, heat resistance, abrasion resistance, antistatic function and photocatalytic function and purification function.
2) B형 질화 붕소 나노 ST 나노 섬유 구성(고전압 전기 방사법)2) B-type boron nitride nano ST nanofiber composition (high-voltage electrospinning)
탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사기의 노즐 방사구를 통해 전기 방사(전압 15kv~30kv, 방사 속도 0.5~1.5ml/hr)시키고, 공급 노즐과 컬렉터 사이(거리 12cm~19cm)에 전기장을 형성시켜서 연신시킨후, 열처리(400℃~500℃)시켜 나노 섬유에 b.탄소·TiO2·질화 붕소 나노 ST를 내재시켜서 b.탄소·TiO2·질화 붕소 나노 ST의 특성(전기 전도성이 있으면서, 방사능 차폐 및 전자파 차폐와 수소 저장 기능을 나타내고, 강도성, 내열성, 내산화성, 방열성, 내마모성이 우수하고, 정전기 방지 및 광촉매 기능과 정화 기능)을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 B.탄소·TiO2·질화 붕소 나노 ST/나노 섬유.The carbon, TiO 2 , boron nitride Nano ST / polymer solution was electrospun (voltage 15kv ~ 30kv, radiation rate 0.5 ~ 1.5ml / hr) through the nozzle discharge port of the high voltage electrospinning device, B) Carbon · TiO 2 · Boron nitride nano ST · b · Carbon · TiO 2 · Boron nitride nano ST Characteristics of carbon · TiO 2 · Nitride of boron nitride ST is embedded in nanofiber by heat treatment (400 ℃ ~ 500 ℃) (Having electrical conductivity and exhibiting radioactivity shielding, electromagnetic wave shielding and hydrogen storage function, and excellent in strength, heat resistance, oxidation resistance, heat resistance and abrasion resistance, antistatic function and photocatalytic function and purification function) B. Carbon · TiO 2 · boron nitride Nano ST / Nano fiber composed of fibers.
Claims (2)
NMP, DMF, THF, 알콜 중에서 선택한 용매에 상기 TiO2·질화 붕소 나노 ST와 계면 활성제를 첨가 분산시킨후 고분자 분말을 첨가하고, 60℃~100℃에서 교반하여 용해시켜 구성한 TiO2·질화 붕소 나노 ST/고분자 용액을 제조하는 제2단계;
상기 TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사법으로 방사시켜 나노 섬유 내에 TiO2·질화 붕소 나노 ST를 내재시켜 상기 TiO2·질화 붕소 나노 ST의 특성을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 A형 질화 붕소 나노 ST 나노 섬유를 제조하는 제3단계; 를 포함하는 제조 공정을 거쳐서 구성한 A형 질화 붕소 나노 ST 나노 섬유.After forming the boron nitride nano ST by mixing the boron nitride nanosheet and the boron nitride nanotube. A first step of preparing a TiO 2 · boron nitride nano-ST by adding and mixing a TiO 2 nano powder;
A TiO 2 · boron nitride nano-ST and a surfactant are added to and dispersed in a solvent selected from NMP, DMF, THF, and alcohol, and the polymer powder is added and dissolved at 60 ° C. to 100 ° C. to dissolve the TiO 2 · boron nitride nano A second step of preparing an ST / polymer solution;
The TiO 2 · boron nitride nano ST / polymer solution was inherent in the TiO 2 · boron nitride nano-ST in the nanofiber by the radiation to a high voltage electrospinning process showing the characteristics of the TiO 2 · boron nitride nano ST diameter 20nm ~ 800nm nanofibers of A third step of producing the A-type boron nitride nano ST nanofiber composed of the boron nitride nanoparticles; A-type boron nitride nano ST nanofibers constituted by a manufacturing process comprising the steps of:
NMP, DMF, THF, 알콜 중에서 선택한 용매에 상기 탄소·TiO2·질화 붕소 나노 ST와 계면 활성제를 첨가 분산시킨후. 고분자 분말을 첨가하고 60℃~100℃에서 교반하여 용해시켜 구성한 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 제조하는 제2단계;
상기 탄소·TiO2·질화 붕소 나노 ST/고분자 용액을 고전압 전기 방사법으로 방사시켜 나노 섬유 내에 탄소·TiO2·질화 붕소 나노 ST를 내재시켜 상기 탄소·TiO2·질화 붕소 나노 ST의 특성을 나타내는 직경 20nm~800nm의 나노 섬유로 구성한 B형 질화 붕소 나노 섬유를 제조하는 제3단계; 를 포함하는 제조 공정을 거쳐서 구성한 B형 질화 붕소 나노 ST 나노 섬유
A boron nitride nanosheet is mixed with a boron nitride nanotube to form a boron nitride nano ST, and TiO 2 · niobium nitride nano ST formed by adding and mixing TiO 2 nano powder is mixed with one selected from graphene, CNT or a mixture thereof A first step of preparing carbon · TiO 2 · boron nitride nano ST composed of a mixture;
After the carbon · TiO 2 · boron nitride nano-ST and the surfactant are added and dispersed in a solvent selected from NMP, DMF, THF and alcohol, A second step of preparing a carbon · TiO 2 · boron nitride nano ST / polymer solution prepared by adding a polymer powder and stirring at 60 ° C. to 100 ° C. to dissolve the polymer;
The carbon · TiO 2 · boron nitride nano ST / polymer solution was spun by high voltage electrospinning to incorporate carbon · TiO 2 · boron nitride nano ST in the nanofiber to measure the diameter of the carbon · TiO 2 · boron nitride nano ST A third step of producing B-type boron nitride nanofibers composed of nanofibers of 20 nm to 800 nm; Type boron nitride nano ST nanofibers constituted through a manufacturing process including