KR101818341B1 - Flexible, transparent and conductive metal nanowire film and it's fabrication method at low temperature - Google Patents

Flexible, transparent and conductive metal nanowire film and it's fabrication method at low temperature Download PDF

Info

Publication number
KR101818341B1
KR101818341B1 KR1020160059826A KR20160059826A KR101818341B1 KR 101818341 B1 KR101818341 B1 KR 101818341B1 KR 1020160059826 A KR1020160059826 A KR 1020160059826A KR 20160059826 A KR20160059826 A KR 20160059826A KR 101818341 B1 KR101818341 B1 KR 101818341B1
Authority
KR
South Korea
Prior art keywords
polymer
plasticizer
metal nanowire
polymer interlayer
transparent electrode
Prior art date
Application number
KR1020160059826A
Other languages
Korean (ko)
Other versions
KR20170129015A (en
Inventor
김희탁
조원희
최재호
강홍석
Original Assignee
한국과학기술원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한국과학기술원 filed Critical 한국과학기술원
Priority to KR1020160059826A priority Critical patent/KR101818341B1/en
Publication of KR20170129015A publication Critical patent/KR20170129015A/en
Application granted granted Critical
Publication of KR101818341B1 publication Critical patent/KR101818341B1/en

Abstract

본 발명은 금속 나노와이어를 이용한 유연 투명 전극 및 저온 공정 제작법에 관한 것으로, 가소제를 포함하는 폴리머 인터레이어에 서로 접합되어 형성된 금속 나노와이어 네트워크가 침투되어 있는 것을 특징으로 하는 유연 투명 전극을 제공하며,
가소제와 폴리머를 혼합한 폴리머 인터레이어의 제조 단계;
플라스틱 기판 위에 상기 폴리머 인터레이어를 필름 형태로 캐스팅하는 단계;
금속 나노와이어를 정전 스프레이 방식으로 코팅하여 금속 나노와이어 네트워크를 형성하는 단계; 및
상기 금속 나노와이어 네트워크를 상기 폴리머 인터레이어 내부로 물리적 방식으로 침투시키는 단계를 포함하는 것을 특징으로 하는 금속 나노와이어 네트워크를 포함하는 유연 투명 전극의 제조 방법을 제공한다.The present invention relates to a flexible transparent electrode using a metal nanowire and a low temperature process for fabricating the flexible transparent electrode, characterized in that a metal nanowire network formed by joining together a polymer interlayer including a plasticizer is infiltrated,
A step of preparing a polymer interlayer in which a plasticizer and a polymer are mixed;
Casting the polymeric interlayer onto a plastic substrate in the form of a film;
Coating the metal nanowires with an electrostatic spraying method to form a metal nanowire network; And
And physically penetrating the metal nanowire network into the polymer interlayer. The method of fabricating a flexible transparent electrode includes the steps of:

Description

금속 나노와이어를 이용한 유연 투명 전극 및 그 저온 공정 제작법{Flexible, transparent and conductive metal nanowire film and it's fabrication method at low temperature} TECHNICAL FIELD [0001] The present invention relates to a flexible transparent electrode using a metal nanowire and a low temperature process for fabricating the same,

본 발명은 다수의 금속 나노와이어들의 네트워크를 이용한 유연 투명 전극에 관한 것으로서, 더욱 상세하게는, 폴리머 인터레이어에 가소제가 첨가되어 저온 공정을 통해 제조되는 유연 투명 전극 및 그 제작 방법에 관한 것이다. The present invention relates to a flexible transparent electrode using a network of a plurality of metal nanowires, and more particularly, to a flexible transparent electrode manufactured through a low temperature process by adding a plasticizer to a polymer interlayer and a method of manufacturing the flexible transparent electrode.

최근 IT산업의 눈부신 발전으로 인해 플렉서블 디스플레이, OLED, 터치스크린, 웨어러블 기기와 같은 flat한 형태의 1세대 전자 기기를 넘어서 flexible한 형태의 2세대 전자 기기의 수요가 급격히 증가하고 있다. 이러한 기술적 흐름은 자연스레 flexible 전자 기기의 핵심 부품인 유연 투명 전극 기술에 대한 관심의 증가로 이어지고 있다. Due to the remarkable development of the IT industry in recent years, there is a rapid increase in the demand for second-generation electronic devices that are flexible beyond the flat-type first-generation electronic devices such as flexible displays, OLEDs, touch screens and wearable devices. This technological trend has led to increased interest in flexible transparent electrode technology, a key component of naturally flexible electronic devices.

현재 투명 전극에 가장 널리 사용되고 있는 전도성 물질은 ITO(Indium Tin Oxide)로서 80% 이상의 투과도를 가지며 10 ~ 100 Ω/Sq의 저항을 가진다. 그러나, 인듐 소재의 희소성으로 인해 유동적으로 변하는 높은 가격과 구부러졌을 때 생기는 크랙으로 인한 전도성의 급감은 플랙서블 기기에 있어서 ITO의 사용을 제한시킨다. 또한, 높은 품질의 ITO 필름 제조에는 고온(~200℃)의 스퍼터링 또는 화학기상증착 공정이 포함되어야 한다. 이러한 고온열처리가 포함되는 공정은 주로 유리전이온도(Tg)가 낮은 플라스틱을 기판으로 하는 플랙서플 필름의 손상과 변형을 야기할 수 있고, 이것은 플랙서블 기판 제작에 있어 ITO 사용의 제약이 된다.Currently, the most widely used conductive material for transparent electrodes is ITO (Indium Tin Oxide), which has a transmittance of 80% or more and a resistance of 10 to 100 Ω / Sq. However, due to the scarcity of the indium material, the fluctuating high price and the sharp reduction of the conductivity due to the bending crack limit the use of ITO in flexible devices. In addition, high-quality ITO film production should include high-temperature (~ 200 ° C) sputtering or chemical vapor deposition processes. Such a process that includes the high-temperature heat treatment can be mostly cause damage and deformation of the flag the supple film of the lower plastic glass transition temperature (T g) of the substrate, which in the flexible substrate produced is the constraints of ITO used.

따라서 ITO의 대체 물질로서 카본나노튜브(CNT), 그래핀과 PEDOT:PSS와 같은 전도성 고분자 등의 전도성 물질에 대한 연구가 활발히 이루어지고 있다. 그 중에서 높은 투과도와 전기전도성을 가지는 은 나노와이어가 ITO의 대체물질로 각광을 받고 있다. 기판 위에 뿌려진 은 나노와이어는 10 ~ 100nm의 직경과 15 ~ 20 ㎛의 높은 종횡비를 가지고 있기에 소량을 통해서도 전자가 이동할 수 있는 네트워크를 만들 수 있다.Therefore, research on conductive materials such as carbon nanotube (CNT), conductive polymer such as graphene and PEDOT: PSS has been actively studied as an alternative material for ITO. Among them, silver nanowires having high transmittance and electrical conductivity are attracting attention as substitutes for ITO. Since the silver nanowires scattered on the substrate have a diameter of 10 to 100 nm and a high aspect ratio of 15 to 20 μm, it is possible to make a network in which electrons can move even through a small amount.

그러나 이러한 장점을 가지는 은 나노와이어를 이용한 투명 전극도 해결해야 하는 여러 문제점들이 존재한다. 먼저, 내구성의 측면에서 은 나노와이어의 외기에 의한 산화와 기판과의 낮은 결착력으로 인한 은 나노와이어의 탈리는 영구적으로 기판의 전기전도성을 떨어뜨릴 수 있는 요인이 된다. 둘째로, 은이 가지는 높은 전기전도성에도 불구하고 전자의 이동 경로인 네트워크를 형성함에 있어서 은 나노와이어 사이에 형성되는 교차점에서 높은 접촉 저항이 발생하고, 이것은 기판 전체의 전기전도성의 하락을 야기한다. 따라서 소량의 은 나노와이어를 사용하여 접촉 저항을 최소화하여야만 전기전도성을 높일 뿐 아니라 광투과도 또한 높일 수 있다. However, there are various problems to be solved for a transparent electrode using silver nanowires having such advantages. First, from the viewpoint of durability, the oxidation of silver nanowires by ambient air and the desorption of silver nanowires due to a low binding force with the substrate may permanently deteriorate the electrical conductivity of the substrate. Second, despite the high electrical conductivity of silver, high contact resistance occurs at the junctions formed between the silver nanowires in forming a network that is the path of electrons, which causes a decrease in the electrical conductivity of the entire substrate. Therefore, using a small amount of silver nanowires to minimize contact resistance not only enhances electrical conductivity but also increases light transmittance.

이러한 문제들을 해결하기 위해 다양한 연구들이 진행되어왔다. 은 나노와이어 위에 추가적으로 전도성 물질의 첨가를 통해 문제점을 해결하려는 시도를 비롯하여 고온(~200℃)의 어닐링으로 은 나노와이어를 용융시키거나 고압(25MPa)으로 네트워크를 일체화하는 등의 방법도 있었다. 그러나 각각의 방법들은 위에서 기술된 문제점들 중 일부만을 해결할 수 있었으며, 동시에 모든 문제점들을 한번에 해결하는 실용적인 방법은 아직까지 크게 다뤄진 바가 없다. Various studies have been conducted to solve these problems. There has been an attempt to solve the problem by additionally adding a conductive material on the nanowire, melting the silver nanowire by annealing at a high temperature (~ 200 ° C), or integrating the network with high pressure (25 MPa). However, each of these methods solves only some of the problems described above, and at the same time, a practical method of solving all the problems at once has not been discussed so far.

구체적으로 본 발명의 목적은, More specifically,

첫째, 가소제가 함유된 폴리머를 투명 기판 위에 균일하게 캐스팅하고 First, the plasticizer-containing polymer is uniformly cast on a transparent substrate

둘째, 금속 나노와이어를 정전 스프레이(electrostatic spray) 방식을 이용하여 캐스팅된 폴리머 위에 코팅하고Second, the metal nanowires are coated on the cast polymer using an electrostatic spray method

셋째, 금속 나노와이어가 코팅되어있는 기판에 가소화된 폴리머의 낮아진 유리전이온도(Tg) 근처의 온도에서 핫프레싱을 통해 금속 나노와이어 네트워크의 접촉 저항을 감소시키며, 동시에 폴리머 인터레이어에 금속 나노와이어를 침투시킴으로써 외부에 대한 안정성(산화 안정성, 기판과의 결착력 등)을 향상시키고Third, the contact resistance of the metal nanowire network is reduced by hot pressing at a temperature near the lowered glass transition temperature (T g ) of the plasticized polymer on the substrate coated with the metal nanowire, and at the same time, By infiltrating the wire, stability to the outside (oxidation stability, adhesion with the substrate, etc.) is improved

넷째, 상기의 과정을 거쳐 금속 나노와이어를 이용한 높은 투과도와 전기전도도를 가지는 우수한 성능의 유연 투명 전극 및 그 제조방법에 대한 것이다.Fourth, the present invention relates to a flexible transparent electrode having a high transmittance and electrical conductivity using a metal nanowire, and a method for manufacturing the same.

상술한 문제를 해결하기 위해, 본 발명은 가소제를 포함하는 폴리머 인터레이어에 서로 접합되어 형성된 금속 나노와이어 네트워크가 침투되어 있는 것을 특징으로 하는 유연 투명 전극을 제공한다.In order to solve the above problems, the present invention provides a flexible transparent electrode characterized in that a metal nanowire network formed by bonding to a polymer interlayer including a plasticizer is permeated.

본 발명의 일 실시예에 따르면, 상기 금속은 은이며, 상기 가소제를 통해 상기 폴리머 인터레이어를 가소화하여 유리 전이온도(Tg)를 80~100℃ 범위로 낮출 수 있고, 상기 금속 나노와이어 네트워크를 물리적 방식에 의하여 상기 폴리머 인터레이어 내부로 침투시킬 수 있다.According to one embodiment of the invention, the metal is, to plasticize the polymer interlayer over the plasticizer can lower the temperature (T g) The glass transition by 80 ~ 100 ℃ range, the metal nanowire network Can be penetrated into the polymer interlayer by a physical method.

또한, 본 발명은 가소제와 폴리머를 혼합하여 폴리머 인터레이어를 제조하는 단계, 플라스틱 기판 위에 상기 폴리머 인터레이어를 필름 형태로 캐스팅하는 단계, 금속 나노와이어를 정전 스프레이 방식으로 코팅하여 금속 나노와이어 네트워크를 형성하는 단계 및 상기 금속 나노와이어 네트워크를 상기 폴리머 인터레이어 내부로 물리적 방식으로 침투시키는 단계를 포함하는 유연 투명 전극 제조방법을 제공한다. The present invention also relates to a method of manufacturing a polymer nanowire comprising the steps of: preparing a polymer interlayer by mixing a plasticizer and a polymer; casting the polymer interlayer onto a plastic substrate in the form of a film; coating the metal nanowires with an electrostatic spray method And physically penetrating the metal nanowire network into the polymer interlayers.

상기 침투시키는 단계 시, 상기 금속 나노와이어 네트워크는 변형이나 반응이 없으며, 상기 금속 나노와이어가 은 나노와이어일 수 있다.During the impregnation step, the metal nanowire network is free from deformation or reaction, and the metal nanowires may be silver nanowires.

상기 폴리머와 가소제는 메탄올, 에탄올, 톨루엔, IPA, 사이클로벤젠, 사염화탄소, 벤젠 중 적어도 하나 이상의 유기용매에 용해되어 폴리머 인터레이어를 형성할 수 있다.The polymer and the plasticizer may be dissolved in at least one organic solvent selected from the group consisting of methanol, ethanol, toluene, IPA, cyclobenzene, carbon tetrachloride, and benzene to form a polymer interlayer.

상기 폴리머 인터레이어는 닥터블레이드, 메이어로드, 스핀코팅 중 하나의 방식을 통하여 13~17㎛ 두께의 필름으로 균일하게 캐스팅될 수 있다.The polymer interlayers can be uniformly cast into a film having a thickness of 13 to 17 mu m through one of a doctor blade, a Meyer rod, and a spin coating method.

상기 가소제는 상기 폴리머 인터레이어에 첨가되어 상기 폴리머의 유리 전이온도(Tg)를 80~100℃ 범위의 온도로 낮추어 상기 폴리머 인터레이어를 연화시킬 수 있다.The plasticizer may be added to the polymer interlayers to soften the polymer interlayers by lowering the glass transition temperature (T g ) of the polymer to a temperature in the range of 80-100 ° C.

상기 물리적 방식은 50~100℃에서 상기 은 나노와이어 네트워크를 핫프레싱하는 방식으로 진행될 수 있다.The physical method may be performed by hot pressing the silver nanowire network at 50-100 < 0 > C.

또한, 본 발명은 상기 제조방법에 따른 상기 유연 투명 전극을 포함하는 전자 소자를 제공한다.In addition, the present invention provides an electronic device including the flexible transparent electrode according to the above manufacturing method.

본 발명은 금속 나노와이어 네트워크를 이용한 유연 투명 전극 제작에 관한 것으로 보다 구체적으로는, 가소제가 포함되어있는 폴리머 인터레이어의 도입으로 이전의 발명들에 비해 낮은 온도 범위에서 물리적 방식을 통해 기판의 손상을 야기하지 않고 은 나노와이어 간의 교차점에서 접합하여 은 나노와이어 네트워크를 형성하고, 상기 은 나노와이어 네트워크를 상기 폴리머 인터레이어에 침투시킬 수 있다.The present invention relates to the production of flexible transparent electrodes using a metal nanowire network and more particularly to the use of polymer interlayers containing plasticizers to reduce substrate damage through physical methods at lower temperature ranges than previous inventions Without interfering with the nanowire at the junction of the nanowires to form a silver nanowire network that can penetrate the polymer nanowire network.

이때 상기 은 나노와이어에 가해진 압력에 의해 상기 은 나노와이어 사이의 접촉이 monolithic한 접합형태를 형성시켜 상기 은 나노와이어 네트워크 사이 접촉 저항이 감소되며, 동시에 접합된 상기 은 나노와이어가 투명한 상기 폴리머 인터레이어 내로 침투 및 고정되어 상기 은 나노와이어의 기판에 대한 높은 결착력, 낮은 표면 거칠기(Rrms < 20nm), 외기로부터의 노출 감소에 의한 표면산화 억제의 효과를 갖는다. Wherein the contact between the silver nanowires forms a monolithic junction shape due to the pressure applied to the silver nanowires, thereby reducing the contact resistance between the silver nanowire networks, and at the same time, (Rrms < 20 nm) and surface oxidation inhibition by reducing the exposure from outside air. The silver nanowire has a high adhesion to the substrate, low surface roughness (Rrms &lt;

또한, 본 발명은 80~99%의 투과도 및 1 ~ 200Ω/Sq의 범위의 면저항을 가지며, 정전 스프레이 방식을 활용하여 공정 단가가 저렴하며 대면적에 적합하여 실제 상용화 관점에서도 매우 유리하다. Further, the present invention has a sheet resistance of 80 to 99% and a sheet resistance of 1 to 200? / Sq, and is advantageous from the viewpoint of practical commercialization because it is low in process cost and suitable for large area by utilizing electrostatic spraying method.

도 1은 본 발명에 따른 금속 나노와이어 네트워크를 포함하는 유연 투명 전극의 제조방법을 도시한 단계도이다.
도 2는 본 발명의 일 실시예에 따른 유연 투명 전극 제작의 전체적인 공정 모식도이다.
도 3은 폴리머 인터레이어에 가소제를 함유시키기 전과 후의 유리전이온도(Tg)를 보여주는 시차주사열량계(DSC) 그래프이다.
도 4는 본 발명의 가소제가 함유된 폴리머 인터레이어 단면의 주사전자현미경(SEM) 사진이다.
도 5는 핫프레싱 전과 후의 은 나노와이어의 주사전자현미경(SEM)사진이다.
도 6은 본 발명의 일 실시예에 따른 유연 투명 전극의 광투과도 분석 그래프이다.
도 7은 본 발명의 일 실시예에 따른 유연 투명 전극의 시간에 따른 전기전도도의 변화 값을 보여주는 그래프이다.
도 8은 본 발명의 일 실시예에 따른 유연 투명 전극의 구부러짐의 횟수와 구부러짐 반경에 따른 전기전도도의 변화 값을 보여주는 그래프이다.
도 9는 본 발명의 일 실시예에 따른 유연 투명 전극의 테이핑 테스트 후에 기판에 남아있는 은 나노와이어의 주사현미경(SEM) 사진이다.FIG. 1 is a view illustrating a method of manufacturing a flexible transparent electrode including a metal nanowire network according to the present invention.
FIG. 2 is a schematic process diagram of a flexible transparent electrode according to an exemplary embodiment of the present invention. Referring to FIG.
3 is a differential scanning calorimetry (DSC) graph showing the glass transition temperature (T g ) before and after containing the plasticizer in the polymer interlayer.
4 is a scanning electron microscope (SEM) photograph of a cross-section of a polymer interlayer containing the plasticizer of the present invention.
5 is a scanning electron microscope (SEM) photograph of silver nanowires before and after hot pressing.
FIG. 6 is a graph of light transmittance analysis of a transparent transparent electrode according to an embodiment of the present invention.
FIG. 7 is a graph showing a change in electrical conductivity of a transparent transparent electrode according to an exemplary embodiment of the present invention. Referring to FIG.
FIG. 8 is a graph showing changes in electrical conductivity according to the number of bends and the bending radius of a flexible transparent electrode according to an exemplary embodiment of the present invention. Referring to FIG.
9 is a scanning electron microscope (SEM) photograph of silver nanowires remaining on a substrate after taping test of a flexible transparent electrode according to an embodiment of the present invention.

본 발명은 다수의 금속 나노와이어들의 네트워크를 이용한 유연 투명 전극에 관한 것이며, 상기 금속 나노와이어로 은 나노와이어를 사용할 수 있으며, 은 나노와이어들이 서로 접합되어 은 나노와이어 네트워크를 형성할 수 있다.The present invention relates to a flexible transparent electrode using a network of a plurality of metal nanowires, wherein the metal nanowire can use silver nanowires, and silver nanowires can be bonded together to form a silver nanowire network.

일반적으로, 고온에서의 핫프레싱 공정은 열에 민감한 플라스틱 기판의 손상을 유발시켜 광투과도와 내구성에 있어서의 성능 손실을 야기하지만, 본 발명은 저온에서의 물리적 방식을 통해 플라스틱 기판의 손상을 방지하고 안정된 플라스틱 기판을 바탕으로 높은 광투과도를 가지는 유연 투명 전극을 제작할 수 있다.In general, the hot-pressing process at a high temperature causes damage to the heat-sensitive plastic substrate to cause a loss in performance in light transmittance and durability. However, the present invention can prevent the plastic substrate from being damaged by a physical method at a low temperature, A flexible transparent electrode having high light transmittance can be produced based on a plastic substrate.

본 발명은 상기 가소제를 통해 상기 폴리머 인터레이어를 가소화하여 유리 전이온도(Tg)를 80~100℃로 낮추어 연화시킬 수 있다. In the present invention, the polymer interlayers may be plasticized through the plasticizer to lower the glass transition temperature (T g ) to 80 to 100 ° C. to soften the polymer interlayers.

그 결과 50~100℃의 비교적 저온에서도 핫프레싱과 같은 물리적 방식에 의해 폴리머 인터레이어 내부로, 상기 폴리머 인터레이어상에 형성된 금속 나노와이어 네트워크를 변형 없이 그대로 침투시킬 수 있다.As a result, the metal nanowire network formed on the polymer interlayer can be penetrated intact into the polymer interlayer by a physical method such as hot pressing, even at a relatively low temperature of 50 to 100 ° C.

또한, 본 발명에 따른 금속 나노와이어 네트워크를 포함하는 유연 투명 전극의 제조방법은 가소제와 폴리머를 유기용매에서 혼합한 후 진행되는 폴리머 인터레이어의 제조 단계, 플라스틱 기판 위에 상기 폴리머 인터레이어를 필름 형태로 캐스팅하는 단계, 금속 나노와이어를 정전 스프레이 방식으로 코팅하여 금속 나노와이어 네트워크를 형성하는 단계 및 상기 금속 나노와이어 네트워크를 상기 폴리머 인터레이어로 변형이나 반응 없이 그대로 침투시키는 단계를 포함한다. In addition, the method for fabricating a flexible transparent electrode including a metal nanowire network according to the present invention comprises the steps of preparing a polymer interlayer after mixing a plasticizer and a polymer in an organic solvent, forming the polymer interlayer on a plastic substrate in a film form Casting, coating the metal nanowires with an electrostatic spraying method to form a metal nanowire network, and infiltrating the metal nanowire network directly into the polymer interlayer without modification or reaction.

본 발명은 상기 금속 나노와이어로 은 나노와이어를 사용할 수 있으며, 은 나노와이어들이 서로 접합되어 은 나노와이어 네트워크를 형성할 수 있다.In the present invention, silver nanowires may be used as the metal nanowires, and silver nanowires may be bonded to each other to form a silver nanowire network.

상기 폴리머와 가소제는 메탄올, 에탄올, 톨루엔, IPA, 사이클로벤젠, 사염화탄소, 벤젠 중 적어도 하나 이상의 유기용매에 용해되어 폴리머 인터레이어를 형성할 수 있으며, 상기 가소제는 상기 폴리머 인터레이어를 가소화하여 연화시킬 수 있다. 특히 본 발명에 따른 유기용매는 상기 폴리머와 가소제를 모두 용해시키는 것으로, 가소제를 폴리머에 균일하게 혼합시키는 물질이 바람직하다.The polymer and the plasticizer may be dissolved in at least one organic solvent selected from the group consisting of methanol, ethanol, toluene, IPA, cyclobenzene, carbon tetrachloride, and benzene to form a polymer interlayer, and the plasticizer may be prepared by plasticizing and softening the polymer interlayer . In particular, the organic solvent according to the present invention dissolves both the polymer and the plasticizer, and is preferably a material that uniformly mixes the plasticizer with the polymer.

본 발명의 일 실시예에서 상기 폴리머 인터레이어는 닥터블레이드, 메이어로드, 스핀코팅 중 하나의 방식에 의해 필름으로 균일하게 캐스팅될 수 있다.In one embodiment of the present invention, the polymer interlayers may be uniformly cast into a film by one of the following methods: doctor blade, Meyer rod, or spin coating.

본 발명의 일 실시예에서 상기 금속은 은으로, 은 나노와이어는 PVP, AgCl, EG 등을 이용한 폴리올 환원 공정을 통하여 얻을 수 있으며, 상기 은 나노와이어는 정전 스프레이 방식으로 분사되어 기판 위에 코팅될 수 있다. In one embodiment of the present invention, the metal may be silver and the silver nanowire may be obtained through a polyol reduction process using PVP, AgCl, EG, etc., and the silver nanowire may be sprayed by an electrostatic spray method to be coated on the substrate have.

상기 가소제는 상기 폴리머 인터레이어에 첨가되어 유리 전이온도(Tg)를 80~100℃로 낮추어 상기 폴리머 인터레이어와 상기 기판을 연화 시키고, 50~100℃에서 물리적 방식에 의해 상기 은 나노와이어 네트워크가 형성되고 상기 폴리머 인터레이어로 변형이나 반응 없이 그대로 침투될 수 있다.The plasticizer is added to the polymer interlayer glass transition lowering the temperature (T g) in 80 ~ 100 ℃ and softening the substrate and the polymer interlayer, it is by a physical method from 50 ~ 100 ℃ wherein the nanowire network And can be intruded into the polymer interlayer without modification or reaction.

이하, 본 발명의 바람직한 실시예를 첨부한 도면을 참조하여 당해 분야의 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 설명하기로 한다. 또한, 본 발명을 설명함에 있어 관련된 공지의 기능 또는 공지의 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략하기로 한다. 그리고 도면에 제시된 어떤 특징들은 설명의 용이함을 위해 확대 또는 축소 또는 단순화된 것이고, 도면 및 그 구성요소들이 반드시 적절한 비율로 도시되어 있지는 않다. 그러나 당업자라면 이러한 상세 사항들을 쉽게 이해할 것이다.Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings so that those skilled in the art can easily carry out the present invention. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. And certain features shown in the drawings are to be enlarged or reduced or simplified for ease of explanation, and the drawings and their components are not necessarily drawn to scale. However, those skilled in the art will readily understand these details.

본 발명에 따른 일 실시예는 은 나노와이어를 이용하여 높은 투과도와 전기전도도를 가지는 고성능 유연 투명 전극을 저온에서 제작할 수 있도록, 하기 화학식 1(Dibutyl phthalate(DBP)와 같은 가소제)이 포함된 화학식 2(PMMA와 같은 폴리머)의 인터레이어를 제공한다.One embodiment of the present invention relates to a method for preparing a high-performance flexible transparent electrode having high transmittance and electrical conductivity by using silver nanowires, comprising the steps of: reacting a compound represented by Chemical Formula (2) with a compound represented by Chemical Formula 1 (plasticizer such as Dibutyl phthalate (A polymer such as PMMA).

[화학식 1] - Dibutyl phthalate(DBP)Dibutyl phthalate (DBP)

Figure 112016046767663-pat00001
Figure 112016046767663-pat00001

[화학식 2] - Poly(methyl methacrylate)(PMMA) Poly (methyl methacrylate) (PMMA)

Figure 112016046767663-pat00002
Figure 112016046767663-pat00002

상기 화학식 1로 표시되는 화합물은 가소제로서 폴리머의 유리전이온도(Tg)를 낮추어 상기 폴리머 인터레이어 및 기판에 유연성을 부여한다.The compound represented by the formula (1) lowers the glass transition temperature (T g ) of the polymer as a plasticizer to impart flexibility to the polymer interlayer and the substrate.

상기 화합물들은 메탄올, 에탄올, 톨루엔, IPA, 사이클로벤젠, 사염화탄소, 벤젠 등의 유기용매에 용해되어 닥터블레이드, 메이어로드, 스핀코팅 등의 방식으로 캐스팅되어 건조 과정을 거친 뒤 13~17㎛ 두께의 균일한 필름을 형성한다,These compounds are dissolved in an organic solvent such as methanol, ethanol, toluene, IPA, cyclobenzene, carbon tetrachloride, benzene, etc. and cast by a doctor blade, Meyer rod, spin coating, One film is formed,

상기 은 나노와이어는 메탄올, 에탄올, IPA, 물에 1~100 mg/ml의 농도로 분산되어 보관되고 정전 스프레이 방식으로 코팅되며, 이때 정전 스프레이는 10~30kV의 인가전압과 1~10ml/hr의 용액 분사 속도, 직경 2mm 이하의 노즐 사이즈를 이용하여 분사되며 기판위에 코팅된다.The silver nanowires are dispersed in methanol, ethanol, IPA and water at a concentration of 1 to 100 mg / ml and electrostatically sprayed. The electrostatic spray is applied at a voltage of 10 to 30 kV and a voltage of 1 to 10 ml / hr Sprayed using a solution injection speed, a nozzle size of 2 mm or less in diameter, and coated on a substrate.

상기 가소제를 통해 유연성을 갖는 상기 폴리머 인터레이어 및 기판을 50 ~ 100℃의 저온에서 500 ~ 1000psi의 압력 범위로 물리적 방식 중 하나인 핫프레싱을 통해 압력을 가하면 상기 은 나노와이어 간의 교차점에서 접합이 이루어지며 네트워크가 형성되고 상기 네트워크는 변형이나 반응 없이 그대로 상기 폴리머 인터레이어에 침투된다.When the polymer interlayer and the substrate having flexibility through the plasticizer are pressurized through hot pressing, which is one of physical methods at a low temperature of 50 to 100 ° C and a pressure range of 500 to 1000 psi, bonding is performed at the intersections between the silver nanowires A network is formed and the network is permeated into the polymer interlayer without modification or reaction.

이때 상기 은 나노와이어에 가해진 압력에 의해 상기 은 나노와이어 사이의 접촉이 monolithic한 접합형태를 형성시켜 상기 은 나노와이어 네트워크 사이 접촉 저항이 감소되며, 동시에 접합된 상기 은 나노와이어가 투명한 상기 폴리머 인터레이어 내로 침투 및 고정되어 상기 은 나노와이어의 기판에 대한 높은 결착력, 낮은 표면 거칠기, 외기로부터의 노출 감소에 의한 표면산화 억제의 효과를 지닌다.Wherein the contact between the silver nanowires forms a monolithic junction shape due to the pressure applied to the silver nanowires, thereby reducing the contact resistance between the silver nanowire networks, and at the same time, So that the silver nanowire has a high binding force to the substrate, low surface roughness, and the effect of surface oxidation inhibition by reducing the exposure from outside air.

(실험예) 실시예에 따른 유연 투명 전극의 성능 Test(Experimental Example) The performance test of the transparent transparent electrode according to Example

상기 실시예의 공정(도 2)에 따라 (6inch ㅧ 6inch)의 유연 투명 전극을 제작하고, TSP에 적용시켜 구동하였다. According to the process of the embodiment (FIG. 2), a flexible transparent electrode (6 inches by 6 inches) was fabricated and applied to the TSP.

상기 유연 투명전극은 도 3에서 알 수 있듯 약 35℃ 낮아진 유리전이온도(Tg)를 가지는 균일한 폴리머 인터레이어(도 4)를 포함하고 있으며, 도 5로부터 핫프레싱을 통해 은 나노와이어 네트워크를 형성하며, 상기 은 나노와이어 네트워크는 상기 폴리머 인터레이어에 침투되어있음을 확인할 수 있다. The flexible transparent electrode includes a uniform polymer interlayer (FIG. 4) having a glass transition temperature (T g ) that is lowered by about 35 ° C. as seen in FIG. 3, and from FIG. 5, a silver nanowire network , And that the silver nanowire network has penetrated the polymer interlayer.

또한, 도 6으로부터 동일 전도도의 상용 ITO 대비 약 5% 높은 투과도를 보임을 확인할 수 있다.Also, it can be seen from FIG. 6 that the transmittance is about 5% higher than that of the commercial ITO having the same conductivity.

도 7로부터 시간에 따른 전기전도도의 변화를 확인함으로써 상기 은 나노와이어의 침강 및 고정을 통해 산화 내구성이 우수함을 확인할 수 있다.From FIG. 7, it can be confirmed that the oxidation durability is excellent through the precipitation and fixation of the silver nanowire by confirming the change of the electric conductivity with time.

도 9는 상기 유연 투명 전극의 테이핑 테스트 후에 기판에 남아있는 은 나노와이어의 주사전자현미경(SEM) 사진으로 은 나노와이어가 기판에 침투되어 있어 높은 기판 결착력을 가지는 것을 알 수 있으며, 상기 높은 기판 결착력으로 Bending test 100회 이후 초기 전도도 대비 92%의 전도도를 가지는 것을 확인(도 8)함으로써 높은 유연성과 안정성을 지닌 것을 알 수 있다.FIG. 9 is a scanning electron microscope (SEM) photograph of silver nanowires remaining on the substrate after the taping test of the flexible transparent electrode. It can be seen that silver nanowires are penetrated into the substrate and have a high substrate binding force. (FIG. 8) that it has a conductivity of 92% as compared with the initial conductivity after 100 times of the bending test. Thus, it can be seen that it has high flexibility and stability.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예는 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.

Claims (12)

가소제를 포함하는 폴리머 인터레이어에 서로 접합되어 형성된 금속 나노와이어 네트워크가 침투되어 있는 것을 특징으로 하는 유연 투명 전극에 있어서,
상기 가소제는 하기의 화학식 1의 구조를 가지는 디부틸 프탈레이트(DBP)이며,
[화학식 1]
Figure 112017075884756-pat00012

상기 가소제를 통해 상기 폴리머 인터레이어를 가소화하여 유리 전이온도 (Tg)를 80~100℃ 범위로 낮추는 것을 특징으로 하는 유연 투명 전극.Wherein a metal nanowire network formed by joining together a polymer interlayer comprising a plasticizer is infiltrated,
The plasticizer is dibutyl phthalate (DBP) having a structure represented by the following formula (1)
[Chemical Formula 1]
Figure 112017075884756-pat00012

Flexible transparent electrode, characterized in that to lower the temperature (T g) The glass transition to plasticize the polymer interlayer through said plasticizer to 80 ~ 100 ℃ range. 제 1항에 있어서,
상기 금속은 은인 것을 특징으로 하는 유연 투명 전극.The method according to claim 1,
Wherein the metal is silver. 삭제delete 제 1항에 있어서,
상기 금속 나노와이어 네트워크는 물리적 방식에 의하여 상기 폴리머 인터레이어 내부로 침투된 것을 특징으로 하는 유연 투명 전극.The method according to claim 1,
Wherein the metal nanowire network is penetrated into the polymer interlayer by a physical method. 가소제와 폴리머를 혼합하여 폴리머 인터레이어를 제조하는 단계;
플라스틱 기판 위에 상기 폴리머 인터레이어를 필름 형태로 캐스팅하는 단계;
금속 나노와이어를 정전 스프레이 방식으로 코팅하여 금속 나노와이어 네트워크를 형성하는 단계; 및
상기 금속 나노와이어 네트워크를 상기 폴리머 인터레이어 내부로 물리적 방식으로 침투시키는 단계를 포함하는 것을 특징으로 하는 유연 투명 전극 제조방법에 있어서,
상기 가소제는 하기의 화학식 1의 구조를 가지는 디부틸 프탈레이트(DBP)이며,
[화학식 1]
Figure 112017075884756-pat00013

상기 가소제를 통해 상기 폴리머 인터레이어를 가소화하여 유리 전이온도 (Tg)를 80~100℃ 범위로 낮추는 것을 특징으로 하는 유연 투명전극 제조방법.Mixing a plasticizer and a polymer to prepare a polymer interlayer;
Casting the polymeric interlayer onto a plastic substrate in the form of a film;
Coating the metal nanowires with an electrostatic spraying method to form a metal nanowire network; And
And physically penetrating the metal nanowire network into the polymer interlayer, the method comprising:
The plasticizer is dibutyl phthalate (DBP) having a structure represented by the following formula (1)
[Chemical Formula 1]
Figure 112017075884756-pat00013

Flexible transparent electrode method, characterized in that to lower the temperature (T g) The glass transition to plasticize the polymer interlayer through said plasticizer to 80 ~ 100 ℃ range. 제 5항에 있어서,
상기 침투시키는 단계 시, 상기 금속 나노와이어 네트워크는 변형이나 반응이 없는 것을 특징으로 하는 유연 투명 전극의 제조 방법. 6. The method of claim 5,
Wherein the metal nanowire network is free from deformation or reaction during the infiltration step. 제 5항에 있어서,
상기 금속 나노와이어가 은 나노와이어인 것을 특징으로 하는 유연 투명 전극.6. The method of claim 5,
Wherein the metal nanowire is a silver nanowire. 제 5항에 있어서,
상기 폴리머와 가소제는 메탄올, 에탄올, 톨루엔, IPA, 사이클로벤젠, 사염화탄소, 벤젠 중 적어도 하나 이상의 유기용매에 용해되어 폴리머 인터레이어를 형성하는 것을 특징으로 하는 유연 투명 전극의 제조 방법.6. The method of claim 5,
Wherein the polymer and the plasticizer are dissolved in at least one organic solvent selected from the group consisting of methanol, ethanol, toluene, IPA, cyclobenzene, carbon tetrachloride, and benzene to form a polymer interlayer. 제 5항에 있어서,
상기 폴리머 인터레이어는 닥터블레이드, 메이어로드, 스핀코팅 중 하나의 방식을 통하여 13~17㎛ 두께의 필름으로 균일하게 캐스팅되는 것을 특징으로 하는 유연 투명 전극의 제조 방법. 6. The method of claim 5,
Wherein the polymer interlayers are uniformly cast into a film having a thickness of 13 to 17 占 퐉 through one of a doctor blade, a Meyer rod, and a spin coating method. 제 5항에 있어서,
상기 가소제는 상기 폴리머 인터레이어에 첨가되어 상기 폴리머의 유리 전이온도(Tg)를 80~100℃ 범위의 온도로 낮추어 상기 폴리머 인터레이어를 연화시키는 것을 특징으로 하는 유연 투명 전극의 제조 방법.6. The method of claim 5,
The plasticizer is process for producing a flexible, transparent electrode, comprising a step is added to the polymer interlayer to lower the glass transition temperature (T g) of the polymer to 80 to a temperature of 100 ℃ softening range of the polymer interlayer. 제 5항에 있어서,
상기 물리적 방식은 50~100℃에서 상기 금속 나노와이어 네트워크를 핫프레싱하는 방식으로 진행되는 것을 특징으로 하는 유연 투명 전극의 제조 방법.6. The method of claim 5,
Wherein the physical method is performed by hot pressing the metal nanowire network at 50-100 &lt; 0 &gt; C. 제 5항 내지 제 11항 중 어느 한 항에 따른 방법으로 제조되는 유연 투명 전극을 포함하는 전자 소자.An electronic device comprising a flexible transparent electrode produced by a process according to any one of claims 5 to 11.
KR1020160059826A 2016-05-16 2016-05-16 Flexible, transparent and conductive metal nanowire film and it's fabrication method at low temperature KR101818341B1 (en)