KR101790390B1 - Preparation method of spherical silica aerogel granules - Google Patents
Preparation method of spherical silica aerogel granules Download PDFInfo
- Publication number
- KR101790390B1 KR101790390B1 KR1020140013864A KR20140013864A KR101790390B1 KR 101790390 B1 KR101790390 B1 KR 101790390B1 KR 1020140013864 A KR1020140013864 A KR 1020140013864A KR 20140013864 A KR20140013864 A KR 20140013864A KR 101790390 B1 KR101790390 B1 KR 101790390B1
- Authority
- KR
- South Korea
- Prior art keywords
- spherical silica
- water glass
- glass solution
- surfactant
- hydrophobic spherical
- Prior art date
Abstract
본 발명은 미세하고 균일한 입자크기를 갖는 소수성의 구형 실리카 에어로겔을 과립을 제조하기 위한 것으로, 더 구체적으로는 무기산에 물유리 용액을 첨가하여 혼합물을 제조한 후, 비극성 유기용매 및 계면활성제를 첨가하여 실리카 졸 액적을 제조하는 단계 및 상기 실리카 졸 액적에 표면개질제와 무기산을 첨가하고 반응시키는 단계를 포함하는 소수성의 구형 실리카 에어로겔 과립의 제조방법 및 상기의 방법으로 제조된 소수성의 구형 실리카 에어로겔 과립에 관한 것이다. 이에 따른 제조방법은 단순화된 공정으로 10 ㎛ 내지 500 ㎛의 균일한 입자크기를 갖는, 비산 되지 않아 취급이 용이한 소수성의 구형 실리카 에어로겔 과립을 제조할 수 있을 뿐 아니라, 상기 입자크기를 용이하게 조절할 수 있다.The present invention relates to a method for producing granules by making hydrophobic spherical silica aerogels having a fine and uniform particle size, more specifically, by preparing a mixture by adding a water glass solution to an inorganic acid, adding a nonpolar organic solvent and a surfactant A process for preparing a hydrophobic spherical silica aerogel granule comprising the steps of: preparing a silica sol droplet; and adding and reacting a surface modifier and an inorganic acid to the silica sol droplet, and a hydrophobic spherical silica aerogel granule produced by the above method will be. The manufacturing method according to the present invention is not only capable of producing hydrophobic spherical silica aerogel granules having a uniform particle size of 10 탆 to 500 탆 in a simplified process and can not easily be scattered and easy to handle, .
Description
본 발명은 미세하고 균일한 입자크기를 갖는 소수성의 구형 실리카 에어로겔과립을 제조하기 위한 것으로, 더 구체적으로는 무기산에 물유리 용액을 첨가하여 혼합물을 제조한 후, 비극성 유기용매 및 계면활성제를 첨가하여 실리카 졸 액적을 제조하는 단계 및 상기 실리카 졸 액적에 표면개질제와 무기산을 첨가하고 반응시키는 단계를 포함하는 소수성의 구형 실리카 에어로겔 과립의 제조방법 및 상기의 방법으로 제조된 소수성의 구형 실리카 에어로겔 과립에 관한 것이다.
The present invention relates to a process for producing hydrophobic spherical silica aerogel granules having a fine and uniform particle size and more specifically to a process for preparing a mixture by adding a water glass solution to an inorganic acid and then adding a nonpolar organic solvent and a surfactant to the silica A method for preparing hydrophobic spherical silica aerogel granules comprising the steps of preparing sol-gel droplets and adding the surface modifier and inorganic acid to the silica sol droplets and reacting them, and hydrophobic spherical silica aerogel granules prepared by the above method .
에어로겔(aerogel)은 90~99.9% 정도의 기공율과 1~100 nm 범위의 기공크기를 갖는 초다공성의 고비표면적(≥500 m2/g) 물질로서, 뛰어난 초경량/초단열/초저유전 등의 특성을 갖는 재료이기 때문에 에어로겔 소재 개발연구는 물론 투명단열재 및 환경 친화적 고온형 단열재, 고집적 소자용 극저유전 박막, 촉매 및 촉매 담체, 슈퍼 커패시터용 전극, 해수 담수화용 전극 재료로서의 응용연구도 활발히 진행되고 있다.
Aerogel is a super porous, high specific surface area (≥500 m 2 / g) material with a porosity of about 90 to 99.9% and a pore size in the range of 1 to 100 nm. It has excellent super lightweight / super insulation / Research on the development of aerogel materials as well as research on applications as transparent insulation materials, environmentally friendly high temperature insulation materials, ultra low dielectric thin films for highly integrated devices, catalysts and catalyst carriers, electrodes for supercapacitors, and electrode materials for desalination of seawater have been actively carried out .
에어로겔의 가장 큰 장점은 종래 스티로폼 등의 유기 단열재보다 낮은 0.300 W/m·K 이하의 열전도율을 보이는 슈퍼단열성(super-insulation)이다. 또한, 유기단열재의 치명적인 약점인 화재 취약성과 화재시 유해가스 발생을 해결할 수도 있다.
The biggest advantage of aerogels is super-insulation, which has a thermal conductivity of 0.300 W / m · K or lower, which is lower than that of organic insulation materials such as conventional styrofoam. In addition, it is possible to solve the fatal vulnerability of fatal organic fires and the generation of harmful gases in case of fire.
일반적으로 에어로겔은 물유리, TEOS 등의 실리카 전구체로부터 습윤겔을 제조하고, 습윤겔 내부의 액체성분을 미세구조 파괴 없이 제거하여 제조된다. 대표적인 실리카 에어로겔의 형태는 분말, 과립, 모노리스의 세 가지로 나눌 수 있으며, 일반적으로 분말의 형태로 제조된다.
Generally, aerogels are prepared by preparing a wet gel from a silica precursor such as water glass, TEOS, etc., and removing the liquid component in the wet gel without destroying the microstructure. Typical forms of silica airgel can be divided into three types, powder, granule and monolith, and they are generally produced in the form of powder.
분말의 경우 섬유와 복합화하여 에어로겔 블랑켓(blanket) 또는 에어로겔 시트(sheet) 등과 같은 형태로의 제품화가 가능하며, 블랑켓 또는 시트의 경우 유연성을 가지고 있어 임의의 크기나 형태로 굽히거나 접거나 자를 수 있다. 이에, LNG 선의 단열패널, 공업용 단열재와 우주복, 교통 및 차량, 전력생산용 단열재 등과 같은 공업용으로의 응용뿐 아니라 재킷이나 운동화류 등과 같은 생활용품에도 적용이 가능하다. 또한 아파트와 같은 주택에서 지붕이나 바닥뿐만 아니라 방화문에서 실리카 에어로겔을 사용할 경우 화재 예방에 큰 효과가 있다.
Powder can be mixed with fiber and can be commercialized as aerogel blanket or airgel sheet. In the case of blanket or sheet, it is flexible and can bend, fold or cut in any size or shape. . Accordingly, the present invention can be applied not only to industrial applications such as heat insulation panels for LNG carriers, industrial insulation materials and spacesuits, transportation and automobiles, and insulation materials for electric power production, but also household goods such as jackets and sports shoes. In addition, the use of silica airgel in fireproof doors as well as roofs and floors in apartment houses has a great effect on fire prevention.
그러나 실리카 에어로겔 분말은 높은 다공성과 매우 낮은 겉보기 밀도 및 작은 입자 크기로 인하여 비산되므로 취급이 어려우며, 충진 또한 용이하지 않을 수 있다.
However, the silica airgel powder is difficult to handle because of its high porosity, very low apparent density and small particle size, and may not be easy to fill.
또한, 모노리스의 경우 가시광선 영역에 대하여 높은 투명도를 갖으나, 제조할 수 있는 크기가 제한적이며 다양한 형태로 성형하기 어렵고 쉽게 깨지는 단점이 있다.
In addition, the monolith has a high transparency with respect to the visible light region, but has a limited size that can be manufactured, and is difficult to be molded into various shapes and easily broken.
상기와 같은 실리카 에어로겔 분말과 모노리스 형태의 단점을 해결하기 위해서 크기가 0.5 mm 이상 되는 실리카 에어로겔 과립을 제조하여 취급 용이성과 형상 대응성을 높이고자 하는 시도가 행하여져 왔다. 일례로, 알콕시 실란을 가수분해한 반응용액을 충전체로 제조한 후 촉매와 함께 중축합반응하여 겔화하고, 소수화제와 반응시켜 소수화 처리한 후 초임계 건조하여 소수성 실리카 에어로겔 과립을 얻는 방법; 부가제, 첨가제 및 결합제를 부과한 에어로겔 입자를 성형장치에 공급하고 압축하여 실리카 에어로겔 과립을 제조하는 방법 등이 있다.
Attempts have been made to improve ease of handling and shape responsiveness by producing silica aerogel granules having a size of 0.5 mm or more in order to solve the drawbacks of the silica airgel powder and the monolith form. For example, a method of preparing a reaction solution obtained by hydrolyzing an alkoxysilane as a packed product, polycondensation reaction with a catalyst to form a gel, reacting with a hydrophobizing agent, hydrophobizing and supercritical drying to obtain a hydrophobic silica aerogel granule; A method of producing silica aerogel granules by feeding airgel particles impregnated with additives, additives and binders to a molding apparatus and compressing them.
그러나, 상기와 같은 방법들은 부수적인 과립화 장치 및 결합제와 같은 첨가제를 사용하므로 기술적으로 복잡한 공정과 긴 공정시간이 요구되는 단점이 있을 뿐 아니라, 상기와 같은 방법으로 실리카 에어로겔을 대량생산 할 경우에는 복잡한 처리 절차와 많은 투자비가 소요되며, 결과적으로 많은 시간과 고가의 화학물질이 요구되고, 그로 인해 생산단가가 상승하는 문제가 있을 뿐 아니라 최종적으로 얻을 수 있는 실리카 에어로겔의 입자 크기가 균일하지 않거나 너무 크다는 단점이 있다.
However, since the above methods use additive such as an auxiliary granulating device and a binder, a technically complicated process and a long process time are required. In addition, when the silica airgel is mass produced by the above- A complicated processing procedure and a large investment cost are required. As a result, a large amount of time and expensive chemicals are required, thereby causing a problem of an increase in production cost. In addition, the particle size of the silica airgel finally obtained is not uniform There is a drawback that it is big.
상기와 같은 배경 하에, 본 발명자들은 미세하고 균일한 입자를 갖는 비산성이 낮아 취급이 용이한 실리카 에어로겔을 효율적으로 제조할 수 있는 방법을 연구하던 중, 무기산에 물유리 용액을 첨가하여 혼합하고, 비극성 유기용매 및 계면활성제를 순차적으로 첨가하여 실리카 졸 액적을 제조한 후 표면개질제와 무기산을 첨가하여 반응시킴으로써 미세하고 균일한 입자를 갖는 소수성의 구형 실리카 에어로겔 과립을 얻을 수 있음을 확인함으로써 본 발명을 완성하였다.
Under the above background, the inventors of the present invention have studied how to efficiently produce a silica airgel which has fine and uniform particles and is low in acidity and which can be handled easily, while adding a water glass solution to inorganic acid, Organic solvent and surfactant are sequentially added to prepare a silica sol liquid droplet, and then the surface modifier and inorganic acid are added and reacted to obtain hydrophobic spherical silica airgel granules having fine and uniform particles. Respectively.
본 발명의 목적은 미세하고 균일한 입자 크기를 갖는, 비산성이 낮아 취급이 용이한 소수성의 구형 실리카 에어로겔 과립의 제조방법을 제공하는 것이다.It is an object of the present invention to provide a method for producing hydrophobic spherical silica aerogel granules having a fine and uniform particle size, low in acidity and easy to handle.
본 발명의 다른 목적은 상기의 제조방법에 의해 제조된 소수성의 구형 실리카 에어로겔 과립을 제공하는 것이다.
Another object of the present invention is to provide hydrophobic spherical silica aerogel granules produced by the above-mentioned production method.
상기 과제를 해결하기 위하여, 본 발명은 무기산에 물유리 용액을 첨가하여 혼합물을 제조한 후, 비극성 유기용매 및 계면활성제를 첨가하고 혼합하여 실리카 졸 액적을 형성하는 단계(단계 1); 상기 실리카 졸 액적에 표면개질제 및 무기산을 첨가하고 반응시켜 소수성의 구형 실리카 습윤겔을 제조하는 단계(단계 2); 및 상기 습윤겔을 세척 및 건조하는 단계(단계 3)를 포함하는 소수성의 구형 실리카 에어로겔 과립의 제조방법을 제공한다.
In order to solve the above problems, the present invention provides a method for producing a silica sol liquid, comprising: preparing a mixture by adding a water glass solution to an inorganic acid, adding and mixing a nonpolar organic solvent and a surfactant to form a silica sol droplet; Adding a surface modifier and an inorganic acid to the silica sol droplet and reacting to prepare a hydrophobic spherical silica wet gel (step 2); And washing and drying the wet gel (step 3). ≪ IMAGE >
또한, 본 발명은 상기의 제조방법에 의해 제조된 소수성의 구형 실리카 에어로겔 과립을 제공한다.
The present invention also provides the hydrophobic spherical silica aerogel granules prepared by the above-mentioned production method.
본 발명에 따른 제조방법은 단순화된 공정으로 10 ㎛ 내지 500 ㎛의 균일한 입자크기를 갖는, 비산되지 않아 취급이 용이한 소수성의 구형 실리카 에어로겔 과립을 제조할 수 있을 뿐 아니라, 상기 입자크기를 용이하게 조절할 수 있다. The manufacturing method according to the present invention is capable of producing hydrophobic spherical silica aerogel granules having a uniform particle size of 10 μm to 500 μm in a simplified process and not scattered and easy to handle, .
또한, 본 발명의 제조방법에 따라 제조된 소수성의 구형 실리카 에어로겔 과립은 단열재, 흡착제, 담체 등 다양한 산업에 유용하게 적용할 수 있다.
In addition, the hydrophobic spherical silica aerogel granules produced according to the production method of the present invention can be applied to various industries such as heat insulating materials, adsorbents, carriers and the like.
도 1은, 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 과립의 제조방법의 순서를 개략적으로 나타낸 것이다.
도 2는, 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 과립의 형성과정을 도식적으로 나타낸 것이다.
도 3은, 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 과립의 주사전자현미경 측정 결과를 나타낸 것이다.
도 4는, 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 습윤겔을 세척 및 건조하기 위한 속실렛 추출기의 개략도를 나타낸 것이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 schematically shows a procedure of a method for producing hydrophobic spherical silica aerogel granules according to an embodiment of the present invention.
Figure 2 schematically illustrates the formation of hydrophobic spherical silica aerogel granules according to one embodiment of the present invention.
FIG. 3 is a scanning electron microscope (SEM) measurement result of hydrophobic spherical silica airgel granules according to an embodiment of the present invention.
Figure 4 shows a schematic view of a Soxlet extractor for washing and drying a hydrophobic spherical silica aerogels wet gel according to an embodiment of the present invention.
이하, 본 발명에 대한 이해를 돕기 위하여 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in detail in order to facilitate understanding of the present invention.
본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
The terms and words used in the present specification and claims should not be construed as limited to ordinary or dictionary terms and the inventor may appropriately define the concept of the term in order to best describe its invention It should be construed as meaning and concept consistent with the technical idea of the present invention.
본 발명은 단순화된 공정 단계을 통한 미세하고 균일한 입자크기를 갖는, 쉽게 비산되지 않아 취급이 용이한 소수성의 구형 실리카 에어로겔 과립의 제조방법을 제공한다.
The present invention provides a process for the production of hydrophobic spherical silica aerogel granules having a fine and uniform particle size through simplified process steps and which are not easily scattered and easy to handle.
일반적으로 물유리를 이용하여 제조된 실리카 습윤겔은 동공이 용매인 물로 채워진 형태를 취하게 되며, 상기 용매를 단순히 건조하여 제거하게 되면 액상의 용매가 기상으로 기화하면서 기/액 계면에서의 물의 높은 표면장력으로 인하여 기공구조의 수축 및 균열이 발생하기 쉬우며, 이에 따른 표면적 감소 및 기공구조의 변화를 일으키게 된다.In general, silica wet gel prepared by using water glass is filled with water, which is a solvent. When the solvent is simply dried and removed, the liquid solvent evaporates in the gas phase while the high surface of water at the vapor / liquid interface The shrinkage and cracking of the pore structure are liable to occur due to the tensile force, resulting in a decrease in the surface area and a change in the pore structure.
또한, 상기와 같은 상태로 건조된 실리카 에어로겔은 건조 과정 중 실리카 표면의 실라놀기(Si-OH)의 친수성에 의해 서로 축합반응이 일어나게 되고, 2차적으로 공기 중의 물을 흡수하게 되어 기공구조를 붕괴시켜 열전도율이 높아지는 단점이 있다.
Also, the silica airgel dried in the above-mentioned state is condensed with each other due to hydrophilicity of the silanol group (Si-OH) on the surface of the silica during the drying process, and secondarily absorbs water in the air, And the thermal conductivity is increased.
따라서, 기공구조를 유지하기 위해서는 물을 유기용매로 치환할 필요가 있으며, 낮은 열전도율을 유지하기 위해서는 실리카 에어로겔 표면을 소수성으로 개질할 필요가 있다.
Therefore, in order to maintain the pore structure, it is necessary to replace water with an organic solvent, and in order to maintain a low thermal conductivity, it is necessary to modify the surface of the silica airgel to be hydrophobic.
이에, 본 발명의 제조방법은 실리카 에어로겔의 기공구조와 낮은 열전도율을 유지하면서도, 미세하고 균일한 입자크기를 갖는 비산성이 낮은 취급이 용이한 소수성의 구형 실리카 에어로겔 과립을 제조하기 위하여, 무기산, 비극성 유기용매 및 표면개질제를 사용하여 용매치환, 표면개질 및 겔화를 동시에 진행하였을 뿐 아니라, 계면활성제를 반응에 첨가시킴으로써 안정화된 구형의 실리카 에어로겔 과립을 형성하였다.
Thus, in order to produce a hydrophobic spherical silica aerogel granule having a fine and uniform particle size and low acidity and easy handling, while maintaining the pore structure of the silica airgel and low thermal conductivity, inorganic acid, nonpolar The organic solvent and the surface modifier were used to simultaneously perform solvent substitution, surface modification and gelation, and stabilized spherical silica aerogel granules were formed by adding a surfactant to the reaction.
이하, 도 1에 의하여 본 발명에 따른 소수성의 구형 실리카 에어로겔 과립의 제조방법을 구체적으로 설명한다.Hereinafter, a method for producing hydrophobic spherical silica aerogel granules according to the present invention will be described in detail with reference to FIG.
도 1은 본 발명의 일 실시예에 따른 제조방법의 순서도를 개략적으로 나타낸 것이다.1 schematically shows a flow chart of a manufacturing method according to an embodiment of the present invention.
본 발명의 일 실시예에 따른 상기 소수성의 구형 실리카 에어로겔 과립의 제조방법은 무기산에 물유리 용액을 첨가하여 혼합물을 제조한 후, 비극성 유기용매 및 계면활성제를 첨가하고 혼합하여 실리카 졸 액적을 형성하는 단계(단계 1); 상기 실리카 졸 액적에 표면개질제 및 무기산을 첨가하고 반응시켜 소수성의 구형 실리카 습윤겔을 제조하는 단계(단계 2); 및 상기 습윤겔을 세척 및 건조하는 단계(단계 3)를 포함하는 것을 특징으로 한다.The hydrophobic spherical silica aerogel granules according to an embodiment of the present invention may be prepared by adding a water glass solution to inorganic acid to prepare a mixture, adding a nonpolar organic solvent and a surfactant, and mixing to form a silica sol droplet (Step 1); Adding a surface modifier and an inorganic acid to the silica sol droplet and reacting to prepare a hydrophobic spherical silica wet gel (step 2); And washing and drying the wet gel (step 3).
상기 단계 1은, 안정화된 균일한 크기의 실리카 졸 액적을 형성시키기 위한것으로, 상기 무기산에 물유리 용액을 첨가하고 혼합하여 혼합물을 제조한 후, 비극성 유기용매 및 계면활성제를 첨가하고 혼합하여 실리카 졸 액적을 형성하는 단계이다. The above step 1 is for forming a stabilized silica sol liquid droplet having a uniform size. A water glass solution is added to the inorganic acid and mixed to prepare a mixture. Then, a nonpolar organic solvent and a surfactant are added and mixed to prepare a silica sol liquid It is the step of forming the enemy.
상기 혼합은 교반을 통하여 수행할 수 있으며, 상기 교반은 마그네틱 바를 이용하여 400 rpm 내지 800 rpm으로 10분 내지 1시간 동안 수행할 수 있으나, 이에 제한되는 것은 아니다.
The mixing may be carried out by stirring, and the stirring may be performed using a magnetic bar at 400 rpm to 800 rpm for 10 minutes to 1 hour, but the present invention is not limited thereto.
상기 물유리 용액은 무기산에 첨가하여 혼합물을 형성할 수 있으며, 상기 물유리 용액의 pH는 11 내지 13일 수 있다.The water glass solution may be added to inorganic acid to form a mixture, and the pH of the water glass solution may be 11 to 13.
구체적으로, 상기 물유리 용액은 무기산에 교반을 하면서 첨가되어 혼합물을 형성할 수 있으며, 상기 혼합물은 물유리 용액과 무기산이 반응함으로 인하여 생성된 실리카 졸(silicic acid, Si(OH)4)과 부산물(나트륨 화합물) 그리고 미반응한 무기산이 공존하는 형태일 수 있다. 이에, 후술하는 표면개질제와 반응하여 표면개질 및 겔화가 보다 용이하게 이루어질 수 있다.
Specifically, the water glass solution may be added to the inorganic acid while stirring to form a mixture. The mixture may contain silica sol (Si (OH) 4 ) produced by reacting the water glass solution with inorganic acid and a by- Compound) and unreacted inorganic acid may coexist. Thus, surface modification and gelation can be more easily performed by reacting with a surface modifying agent described later.
상기 무기산은 질산, 염산, 아세트산, 황산 및 불산으로 이루어진 군으로부터 선택된 1종 이상인 것일 수 있다.
The inorganic acid may be at least one selected from the group consisting of nitric acid, hydrochloric acid, acetic acid, sulfuric acid and hydrofluoric acid.
상기 물유리 용액은 물유리에 증류수를 첨가하고 혼합한 희석 용액으로, 상기 물유리는 특별히 한정하는 것은 아니나, 28 중량% 내지 30 중량%의 실리카(SiO2 )를 함유하는 것일 수 있다. 증류수를 첨가하여 희석한 상기 물유리 용액은 0.1 중량% 내지 10 중량%의 실리카를 함유하고 있는 것일 수 있다.
The water glass solution is a diluted solution prepared by adding distilled water to water glass. The water glass is not particularly limited, but may contain silica (SiO 2 ) in an amount of 28% by weight to 30% by weight. The water glass solution diluted by adding distilled water may contain 0.1 to 10% by weight of silica.
상기 비극성 유기용매와 계면활성제는 순차적으로 상기 무기산과 물유리 용액 혼합물에 첨가하거나, 또는 동시에 첨가할 수 있다. 바람직하게는, 비극성 유기용매를 첨가하고 이어서 계면활성제를 첨가하는 것일 수 있다.
The nonpolar organic solvent and the surfactant may be added to the mixture of the inorganic acid and the waterglass solution sequentially or simultaneously. Preferably, a nonpolar organic solvent may be added and then a surfactant may be added.
상기 계면활성제는 비극성 유기용매 내에서 상기 물유리 용액과 무기산이 반응함으로 인하여 생성된 실리카 졸을 안정화시켜 균일한 크기의 액적을 형성할 뿐 아니라 상기 액적의 크기를 조절하는 역할을 한다.The surfactant stabilizes the silica sol produced by the reaction of the water glass solution with the inorganic acid in the nonpolar organic solvent to form droplets of a uniform size and also controls the size of the droplets.
구체적으로, 본 발명의 일 실시예에 따른 상기 계면활성제(surfactant)는, 통상적으로 극성(친수성)을 갖는 'head'부분과 비극성(소수성)을 갖는 'tail'부분으로 나누어져 있어, 용매에 따라 미셀(micelle) 또는 역미셀, 즉 구형의 입자를 형성할 수 있다. 예컨대, 극성 용매(친수성) 내에 첨가될 경우에는 용매 내에 계면활성제 각 분자들이 서로 모여 극성인 부분(head)은 용매와 닿으려고 하고 비극성인 부분(tail)은 용매와 닿지 않으려고 함으로써 미셀을 형성하게 된다.
Specifically, the surfactant according to an embodiment of the present invention is divided into a 'head' portion having a polarity (hydrophilic) and a 'tail' portion having a non-polar (hydrophobic) Micelles, or reverse micelles, that is, spherical particles. For example, when added in a polar solvent (hydrophilic), the molecules of the surfactant are gathered together in the solvent so that the polar head tries to contact the solvent and the non-polar tail tries to avoid contact with the solvent to form micelles do.
상기와 같은 계면활성제의 특성에 의하여, 본 발명의 일 실시예에 따른 상기 실리카 졸 액적은 비극성 유기용매 내에서 상기 무기산과 물유리 용액의 혼합물이 역미셀을 형성한 계면활성제 내에 존재하는 형태일 수 있다. 이때, 상기 무기산과 물유리 용액의 혼합물은 앞서 언급한 바와 같이, 상기 무기산과 물유리 용액의 반응에 의하여 생성된 실리카 졸과 나트륨 화합물 그리고 미반응한 무기산이 공존하는 형태일 수 있다. Depending on the characteristics of the surfactant, the silica sol liquid according to an embodiment of the present invention may be a mixture of the inorganic acid and the water glass solution in the nonpolar organic solvent in the presence of the reversed micelle-forming surfactant . At this time, the mixture of the inorganic acid and the water glass solution may be a form in which the silica sol and the sodium compound produced by the reaction of the inorganic acid and the water glass solution and the unreacted inorganic acid coexist.
또한, 상기 계면활성제는 비극성 유기용매 내에 균일한 크기의 액적을 형성시키고 상기 액적을 안정화시킬 수 있으며, 첨가되는 계면활성제의 양에 따라 생성되는 액적의 크기를 조절할 수도 있다. 예컨대, 계면활성제의 첨가량이 증가할수록 생성되는 액적의 크기는 감소할 수 있다.
The surfactant may form droplets of a uniform size in the nonpolar organic solvent, stabilize the droplets, and adjust the size of droplets generated according to the amount of the surfactant added. For example, as the amount of surfactant added increases, the size of the resulting droplets may decrease.
상기 물유리 용액, 계면활성제 및 비극성 유기용매는 1:0.1 내지 0.5:1 내지상기 2의 부피비로 첨가될 수 있다. 즉, 상기 물유리 용액 대 계면활성제 대 비극성 유기용매는 1:0.1 내지 0.5:1 내지 2의 부피비를 갖는 것일 수 있다. 만약, 상기 계면활성제가 상기의 비율 미만으로 첨가될 경우에는 계면활성제의 첨가량이 너무 적어 균일한 크기의 액적을 형성하기 어려울 수 있으며, 이에 반해 상기의 비율을 초과하여 첨가될 경우에는 계면활성제가 과량으로 첨가되어 액적 간의 응집 문제가 발생할 수 있다. 이때, 상기 물유리 용액은 앞서 언급한 바와 같이 0.1 중량% 내지 10 중량%의 실리카를 함유하고 있는 것일 수 있다.
The water glass solution, the surfactant and the nonpolar organic solvent may be added at a ratio of 1: 0.1 to 0.5: 1 to 2: 1. That is, the water glass solution to surfactant to nonpolar organic solvent may have a volume ratio of 1: 0.1 to 0.5: 1 to 2. If the amount of the surfactant is less than the above range, the addition amount of the surfactant may be too small to form droplets of a uniform size. On the other hand, when the surfactant is added in excess of the above ratio, So that a problem of agglomeration between droplets may occur. At this time, the water glass solution may contain 0.1 wt% to 10 wt% of silica as mentioned above.
상기 계면활성제는 비이온성 계면활성제이면 특별히 제한하는 것은 아니나, 예컨대 소르비탄 모노올리에이트, 소르비탄 모노스테아레이트, 소르비탄 모노팔미테이트 및 소르비탄 모노라우레이트로 이루어진 군으로부터 선택된 1종 이상인 것일 수 있다.
The surfactant may be one or more selected from the group consisting of sorbitan monooleate, sorbitan monostearate, sorbitan monopalmitate and sorbitan monolaurate, although it is not particularly limited as long as it is a nonionic surfactant .
상기 비극성 유기용매는 헥산, 헵탄, 톨루엔, 크실렌 또는 이들 혼합물인 것일 수 있으나, 이에 제한되는 것은 아니다. 바람직하게는 헥산일 수 있다.The nonpolar organic solvent may be hexane, heptane, toluene, xylene, or a mixture thereof, but is not limited thereto. Preferably hexane.
본 발명의 일 실시예에 따른 상기 비극성 유기용매는 후술하는 단계 2에서 제조된 소수성의 구형 실리카 습윤겔의 동공 내에 존재하는 물을 상기 유기용매로 치환함으로써 상기 소수성의 구형 실리카 습윤겔의 건조 시 상기 습윤겔 동공 내에 존재하는 물이 기상으로 기화하면서 발생시킬 수 있는 기공의 수축 및 균열을 방지할 수 있다. 이에, 상기 소수성의 구형 실리카 습윤겔의 건조 시 발생하는 표면적 감소 및 기공구조의 변화를 방지할 수 있다.
The nonpolar organic solvent according to an embodiment of the present invention may be prepared by substituting the organic solvent for the water present in the pores of the hydrophobic spherical silica wet gel prepared in Step 2 described below to obtain the hydrophobic spherical silica wet gel, It is possible to prevent shrinkage and cracking of pores that can be generated while water present in the wet gel pores is vaporized into the vapor phase. Thus, it is possible to prevent the reduction of the surface area and the change of the pore structure that occur during the drying of the hydrophobic spherical silica wet gel.
상기 단계 2는 소수성의 구형 실리카 습윤겔을 제조하기 위하여 상기 단계 1의 실리카 졸 액적에 표면개질제와 무기산을 첨가하고 반응시키는 단계이다. The step 2 is a step of adding a surface modifier and an inorganic acid to the silica sol droplet of the step 1 to produce a hydrophobic spherical silica wet gel, and reacting.
본 발명의 일 실시예에 따른 제조방법은 상기 실리카 졸 액적에 표면개질제와 무기산을 함께 첨가함으로써, 상기 무기산이 표면개질제와 반응하여 표면개질제를 분해하고, 이에 표면개질제와 상기 실리카 졸의 반응을 촉진하여 실리카 졸 표면의 개질을 용이하게 수행할 뿐 아니라, 이와 동시에 암모니아를 생성함으로써 겔화를 더욱 촉진할 수 있다.
The method according to one embodiment of the present invention is characterized in that the inorganic acid is reacted with the surface modifier to decompose the surface modifier by adding the surface modifier and the inorganic acid to the silica sol liquid droplet to accelerate the reaction between the surface modifier and the silica sol Thereby facilitating the modification of the surface of the silica sol and simultaneously promoting the gelation by generating ammonia.
본 발명의 일 실시예에 따른 상기 표면개질제는 pH 8 정도의 염기성 용액으로, 표면개질과 동시에 겔화를 수행할 수 있으며, 앞서 언급한 바와 같이 함께 첨가하는 무기산 또는 상기 단계 1의 혼합물 내에 존재할 수 있는 미반응한 무기산에 의하여 상기의 활성이 더욱 촉진될 수 있다.The surface modifying agent according to an embodiment of the present invention may be a basic solution having a pH of about 8 and may perform surface modification and gelation at the same time. As mentioned above, the inorganic acid to be added together, The above-mentioned activity can be further promoted by unreacted inorganic acid.
상기 표면개질제는 상기 단계 1에서 사용된 물유리 용액에 대하여 0.05 부피비 내지 0.3 부피비로 첨가될 수 있으며, 바람직하게는 0.05 부피비 내지 0.12 부피로 첨가될 수 있다. 즉, 상기 물유리 용액과 표면개질제는 1:0.05 부피비 내지 1:0.3의 부피비, 바람직하게는 1:0.05 부피비 내지 1:0.12 부피비를 갖는 것일 수 있다. 만약, 상기 표면개질제가 0.05 부피비 미만일 경우에는 표면개질 속도가 느려지고 최종 생성되는 과립의 밀도가 증가할 수 있을 뿐 아니라 건조 시 과립의 치밀화가 일어나 기공크기가 작고 다공성을 이루지 못하는 문제가 발생할 수 있으며, 상기 표면개질제가 0.3 부피비를 초과할 경우에는 표면개질이 급격하게 일어나 상기 실리카 습윤겔의 형상이 유지되기 어려울 수 있을 뿐 아니라 최종 생성되는 과립의 강도가 낮아 구형이 유지되기 어려운 문제가 발생할 수 있다. 이때, 상기 물유리 용액은 앞서 언급한 바와 같이 0.1 중량% 내지 10 중량%의 실리카를 함유하고 있는 것일 수 있다.
The surface modifier may be added to the water glass solution used in step 1 at a ratio of 0.05 to 0.3, preferably 0.05 to 0.12. That is, the water glass solution and the surface modifier may have a volume ratio of 1: 0.05 volume ratio to 1: 0.3 volume ratio, preferably 1: 0.05 volume ratio to 1: 0.12 volume ratio. If the amount of the surface modifier is less than 0.05 parts by volume, the surface modifying rate may be slowed down and the density of the final formed granules may increase. In addition, densification of the granules may occur during drying, resulting in small pore size and poor porosity. If the amount of the surface modifier is more than 0.3 volume ratio, surface modification may occur rapidly and the shape of the silica wet gel may be difficult to maintain, and the strength of the final formed granules may be low, so that the spherical shape may be difficult to maintain. At this time, the water glass solution may contain 0.1 wt% to 10 wt% of silica as mentioned above.
상기 표면개질제는 헥사알킬디실라잔, 테트라알킬디실라잔 및 수화된 헥사알킬디실라잔으로 이루어진 군으로부터 선택된 1종 이상인 것일 수 있으며, 바람직하게는 헥사메틸디실라잔, 테트라메틸디실라잔 및 수화된 헥사메틸디실라잔으로 이루어진 군으로부터 선택된 1종 이상인 것일 수 있다. 가장 바람직하게는 헥사메틸디실라잔일 수 있다. 여기에서, 상기 수화된 헥사메틸디실라잔은 헥사메틸디실라잔과 증류수를 혼합하여 제조한 것일 수 있다.The surface modifier may be one or more selected from the group consisting of hexaalkyldisilazane, tetraalkyldisilazane and hydrated hexaalkyldisilazane, preferably hexamethyldisilazane, tetramethyldisilazane and And hydrated hexamethyldisilazane. [0035] The term " a " Most preferred is hexamethyldisilazane. Here, the hydrated hexamethyldisilazane may be prepared by mixing hexamethyldisilazane and distilled water.
이하, 도 2를 참고하여 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 과립의 형성 과정을 설명한다. Hereinafter, a process for forming a hydrophobic spherical silica aerogel granule according to an embodiment of the present invention will be described with reference to FIG.
도 2에 나타난 바와 같이, 본 발명의 일 실시예에 따른 비극성 유기용매 내에 형성된 실리카 졸 액적은, 무기산과 물유리 용액이 반응하여 생성된 실리카 졸과 나트륨 화합물 그리고 미반응한 무기산이 공존하는 형태일 수 있는 혼합물이 계면활성제에 의하여 형성된 미셀의 내에 존재하는 형태일 수 있으며, 이때 상기 실리카 졸 액적의 표면은 친수성일 수 있다. 여기에 표면개질제를 첨가하고 반응시킴으로써, 염기성인 표면개질제에 의하여 일부 겔화와 표면개질이 진행될 수 있으며, 상기 표면개질제와 함께 첨가되는 무기산에 의하여 상기 표면개질제가 무기산 또는 상기 혼합물 내에 존재할 수 있는 미반응한 무기산과 반응하여 분해되면서 실리카 졸과 용이하게 반응하여 친수성인 실리카 졸 액적 표면을 소수성으로 표면개질 함과 동시에 암모니아를 생성함으로써 겔화를 더욱 촉진할 수 있다. 이에, 용매치환, 겔화 및 표면개질이 동시에 진행될 수 있으며, 단순화된 공정으로 소수성의 구형 실리카 습윤겔을 수득할 수 있다.
As shown in FIG. 2, the silica sol liquid droplets formed in the nonpolar organic solvent according to an embodiment of the present invention may have a form in which a silica sol and a sodium compound produced by the reaction of an inorganic acid and a water glass solution react with each other and unreacted inorganic acid The mixture may be in a form present in the micelle formed by the surfactant, wherein the surface of the silica sol droplet may be hydrophilic. By adding a surface modifier thereto and reacting, a part of gelation and surface modification can proceed by a basic surface modifier. By the addition of the inorganic acid added together with the surface modifier, the surface modifier can be reacted with an inorganic acid or an unreacted The silica sol is reacted with an inorganic acid to easily react with the silica sol, thereby hydrophilizing the hydrophilic surface of the silica sol droplet and modifying the surface of the silica sol droplet to generate ammonia, thereby further promoting gelation. Thus, solvent substitution, gelation and surface modification can proceed simultaneously, and a hydrophobic spherical silica wet gel can be obtained by a simplified process.
따라서, 본 발명의 일 실시예에 따른 소수성의 구형 실리카 에어로겔 과립은 무기산에 물유리 용액을 첨가하여, 실리카 졸을 포함할 수 있는 혼합물을 얻고, 여기에 비극성 유기용매, 계면활성제 및 표면개질제와 무기산을 첨가하고 반응시켜 제조함으로써 별도의 겔화를 위한 물질을 필요로 하지 않고, 상기 무기산이 표면개질제와 반응하여 표면개질제를 분해함으로써 표면개질제와 실리카 졸과의 반응을 촉진하여 표면개질을 용이하게 수행할 뿐 아니라 암모니아를 생성함으로써 겔화를 촉진할 수 있다.
Therefore, the hydrophobic spherical silica aerogel granules according to an embodiment of the present invention can be obtained by adding a water glass solution to inorganic acid to obtain a mixture which can contain silica sol, and adding a nonpolar organic solvent, a surfactant, a surface modifier, The inorganic acid reacts with the surface modifier to decompose the surface modifier, thereby facilitating the surface modification by promoting the reaction between the surface modifier and the silica sol But it can promote gelation by generating ammonia.
상기 단계 3은 소수성의 구형 실리카 에어로겔 과립을 수득하기 위하여 상기 단계 2에서 제조된 소수성의 구형 실리카 습윤겔을 세척하고 건조하는 단계이다. Step 3 is a step of washing and drying the hydrophobic spherical silica wet gel prepared in step 2 to obtain hydrophobic spherical silica aerogel granules.
상기 세척은 반응 중 발생되는 불순물(나트륨 이온, 미반응물, 부산물 등)을 제거하여, 고순도의 실리카 에어로겔 과립을 얻기 위한 것으로, 본 발명의 일 실시예에 따른 상기 세척은 건조와 동시에 수행하거나, 혹은 건조와 분리하여 순차적으로 수행할 수 있다.
The washing is performed to remove high-purity silica airgel granules by removing impurities (sodium ions, unreacted materials, by-products, etc.) generated during the reaction. The washing according to an embodiment of the present invention may be performed simultaneously with drying, Followed by drying and separation.
상기 세척과 건조를 동시에 수행할 경우에는 속실렛 추출기를 이용한 용매추출법에 의하여 수행할 수 있다.When washing and drying are performed simultaneously, the solvent extraction method using a Soxhlet extractor can be used.
이하, 도 4를 통하여 본 발명의 일 실시예에 따른 속실렛 추출기를 이용한 용매추출법을 설명한다. Hereinafter, a solvent extraction method using a Soxlet extractor according to an embodiment of the present invention will be described with reference to FIG.
도 4는, 본 발명의 일 실시예에 따른 속실렛 추출기(100)의 개략도를 나타낸 것이다.4 is a schematic diagram of a Soxlet extractor 100 according to an embodiment of the present invention.
상기 속실렛 추출기(100)는 재비기(30), 재비기(30) 상단에 응축기(40) 및 응축기 우측에 추출기(50)를 포함하고, 부가적으로 재비기(30) 좌측에 추출용매 저장조(10)를 포함하며, 응축기(40) 좌측에 냉각수의 온도 유지를 위한 냉각순환조(70)를 포함하고, 추출기(50) 우측에 추출용매를 추출기(50)에서 배출시키기 위한 사이폰 암(60)을 포함할 수 있다.The soxhlet extractor 100 includes a
상기 재비기(30), 응축기(40) 및 추출기(50)는 관으로 연결되어 루프 1을 형성하고, 상기 응축기(40)는 냉각순환조(70)와 관으로 연결되어 루프 2를 형성할 수 있다. 상기 루프 1은 추출용매가 지나가는 순환통로이며, 상기 루프 2는 냉각수가 지나가는 순환통로이다.
The
본 발명의 일 실시예에 따른 상기의 속실렛 추출기(100)를 이용한 용매추출법은 하기의 단계를 통하여 수행할 수 있다:The solvent extraction method using the Soxlet extractor 100 according to an embodiment of the present invention can be performed through the following steps:
1) 상기 단계 1에서 제조된 소수성의 구형 실리카 습윤겔을 채운 속실렛 팀블(thimble)을 추출기 안으로 넣는 단계;1) placing a centrifugal thimble filled with the hydrophobic spherical silica wet gel prepared in step 1 into the extractor;
2) 재비기에 담긴 추출용매를 응축기를 거쳐 상기 소수성의 구형 실리카 습윤겔이 들어있는 추출기 안으로 흘려보내 추출을 진행하는 단계; 및2) flowing the extraction solvent contained in the reboiler into an extractor containing the hydrophobic spherical silica wet gel through a condenser to conduct extraction; And
3) 상기 추출기로부터 추출용매를 배출(venting)하는 단계.
3) venting the extraction solvent from the extractor.
상기 추출용매는 이산화탄소 또는 디메틸 에테르(DME)일 수 있다.
The extraction solvent may be carbon dioxide or dimethyl ether (DME).
상기 단계 1)은 소수성의 구형 실리카 습윤겔의 내부에 있는 불순물을 제거하고, 건조된 소수성의 구형 셀리카 에어로겔 과립을 수득하기 위하여, 상기 소수성의 구형 실리카 습윤겔을 추출기(50) 안에 넣고 추출기(50)를 조립하는 단계이다.
The above step 1) comprises the steps of removing the impurities present inside the hydrophobic spherical silica wet gel and introducing the hydrophobic spherical silica wet gel into the
상기 단계 2)는 추출용매를 추출기(50) 내부로 주입하여 불순물을 추출하기 위하여, 재비기(30)에 담긴 추출용매를 응축기(40)를 거쳐 상기 소수성의 구형 실리카 습윤겔이 들어있는 추출기(50) 안으로 흘려보내 속실렛 추출을 진행하는 단계이다.
In step 2), the extraction solvent contained in the
상기 추출용매는 재비기(30)에서 기화되어 관을 통해 응축기(40)로 이송되고, 이송된 추출용매는 응축기(40)에 의해 액화되어 관을 통해 추출기(50)로 주입되며, 추출기(50) 내부의 반응온도에 의하여 다시 액화되어 재비기(30)로 돌아온다. 즉, 상기 추출용매는 재비기(30)>>응축기(40)>>추출기(50)>>재비기(30)의 순으로 루프 1을 따라 순환하면서 상기 소수성의 구형 실리카 습윤겔 내에 불순물을 추출할 수 있다. 특히, 사이폰 암(60)으로 인하여, 액화된 추출용매가 사이폰 암(60) 높이만큼 추출기(50) 내에 채워지면 중력에 의하여 추출기(50) 내의 추출용매가 모두 재비기(30)로 자동 이송되며, 이러한 속실렛 추출 과정이 반복되면서 불순물의 추출이 용이하게 이뤄질 수 있다.
The extraction solvent is vaporized in the
상기 추출은 1시간 내지 10시간 동안 수행할 수 있으나, 이에 제한되는 것은 아니다.
The extraction can be performed for 1 to 10 hours, but is not limited thereto.
상기 속실렛 추출 시, 상기 재비기(30)의 온도는 25℃ 내지 40℃, 응축기(40)의 온도는 -20℃ 내지 10℃일 수 있으며, 상기 속실렛 추출은 5 bar 내지 70 bar의 압력에서 수행하는 것일 수 있다.
The temperature of the
상기 압력은 사용하는 추출용매에 따라 상이할 수 있으며, 상기 추출용매는 이산화탄소 또는 디메틸에테르일 수 있다. The pressure may vary depending on the extraction solvent used and the extraction solvent may be carbon dioxide or dimethyl ether.
구체적으로, 상기 추출용매가 이산화탄소일 경우에는 상기 속실렛 추출은 40 bar 내지 70 bar의 압력에서 수행하는 것일 수 있으며, 바람직하게는 40 bar 내지 60 bar의 압력에서 수행하는 것일 수 있다. 상기 추출용매가 디메틸에테르일 경우에는 상기 속실렛 추출은 5 bar 내지 20 bar의 압력에서 수행하는 것일 수 있다.
Specifically, when the extraction solvent is carbon dioxide, the Soxlet extraction may be performed at a pressure of 40 bar to 70 bar, preferably at a pressure of 40 bar to 60 bar. If the extraction solvent is dimethyl ether, the Soxhlet extraction may be performed at a pressure of 5 bar to 20 bar.
상기 단계 3)은 불순물이 제거된, 건조된 소수성의 구형 실리카 에어로겔 과립을 수득하기 위하여, 상기 재비기(30)와 응축기(40)을 끄고 추출기(50) 온도를 서서히 상승시키면서 추출기(50)의 밸브를 열어 추출용매를 배출(venting)하는 단계이다.The step 3) is performed to remove the impurities from the
상기 추출용매가 모두 배출되어 상압에 도달하면, 추출기(50)을 열어서 소수성의 구형 실리카 에어로겔 과립을 수득할 수 있으며, 남아 있을 수 있는 추출용매의 제거를 위하여 상온에서 일정시간 이상 추가로 진공건조할 수 있다.
When all of the extraction solvent has been discharged and the pressure has reached atmospheric pressure, the
상기와 같이 속실렛 추출기를 통하여 세척 및 건조를 동시에 수행할 경우, 상기 소수성의 구형 실리카 습윤겔 내의 계면활성제 및 미반응 표면개질제를 효과적으로 추출할 수 있을 뿐 아니라 추가적인 건조 공정 없이 소수성의 구형 실리카 에어로겔 과립을 수득할 수 있다. 또한, 부가적으로 용매치환되지 않은 소수성의 구형 실리카 습윤겔의 용매치환을 세척과 동시에 수행할 수도 있다.
When washing and drying are simultaneously carried out through the Soxhlet extractor, the surfactant and the unreacted surface modifier in the hydrophobic spherical silica wet gel can be effectively extracted, and hydrophobic spherical silica aerogel granules Can be obtained. In addition, solvent substitution of an additionally unsubstituted hydrophobic spherical silica wet gel may be performed simultaneously with washing.
한편, 상기 세척과 건조를 분리하여 순차적으로 수행할 경우에는, 상기 세척과 건조는 특별히 한정하지 않고 당업계에 통상적으로 공지된 방법에 의하여 수행할 수 있다. Meanwhile, when washing and drying are separated and performed sequentially, the washing and drying are not particularly limited, and can be carried out by a conventionally known method in the art.
예컨대, 상기 세척은 소수성의 구형 실리카 습윤겔에 비극성 유기용매를 첨가하고, 20분 내지 1시간 동안 교반하여 수행할 수 있다. 상기 비극성 유기용매는 앞서 언급한 단계 2에서 사용된 물질과 동일하거나, 상기 단계 2에서 사용될 수 있는 비극성 유기용매에 포함되는 물질일 수 있다. For example, the washing may be performed by adding a non-polar organic solvent to a hydrophobic spherical silica wet gel and stirring for 20 minutes to 1 hour. The nonpolar organic solvent may be the same as the substance used in the above-mentioned step 2, or may be a substance included in the nonpolar organic solvent which can be used in the step 2.
예컨대, 상기 건조는 세척된 소수성의 구형 실리카 습윤겔에서 수층을 분리하여 제거한 후 60℃ 내지 100℃의 오븐에서 6시간 내지 12시간 동안 상압건조하여 수행할 수 있다.
For example, the drying can be carried out by separating and removing the aqueous layer from the washed hydrophobic spherical silica wet gel, followed by drying at 60 ° C to 100 ° C in an oven for 6 hours to 12 hours at atmospheric pressure.
또한, 본 발명은 상기의 제조방법에 의해 제조된 소수성의 구형 실리카 에어로겔 과립을 제공한다.The present invention also provides the hydrophobic spherical silica aerogel granules prepared by the above-mentioned production method.
본 발명에 따른 상기 소수성의 구형 실리카 에어로겔 과립은 10 ㎛ 내지 500 ㎛ 범위의 입자크기를 갖는 것일 수 있다.The hydrophobic spherical silica aerogel granules according to the present invention may have a particle size in the range of 10 [mu] m to 500 [mu] m.
상기 소수성의 구형 실리카 에어로겔 과립은 500 m2/g 내지 900 m2/g의 비표면적을 갖는 것일 수 있다.
The hydrophobic spherical silica aerogel granules may have a specific surface area of 500 m 2 / g to 900 m 2 / g.
이하, 하기 실시예 및 실험예에 의하여 본 발명을 보다 더 상세히 설명한다. 그러나, 하기 실시예 및 실험예는 본 발명을 예시하기 위한 것으로 본 발명의 범위가 이들 만으로 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to the following examples and experimental examples. However, the following examples and experimental examples are provided for illustrating the present invention, and the scope of the present invention is not limited thereto.
실시예Example : 소수성의 구형 실리카 : Hydrophobic spherical silica 에어로겔의Aerogel 제조 Produce
물유리(영일화성, 실리카 함량 28~30 중량%, SiO2:Na2O=3.52:1)에 증류수를 넣어 실리카(SiO2) 함량이 4.35 중량%가 되도록 물유리 용액을 제조한 후, 상기 물유리 용액 100 g(약 100 ㎖)을 70% HNO3 5 g이 들어있는 반응기에 교반하면서 첨가하여 혼합하였다. 그 후, 상기 반응기에 n-헥산 120 ㎖와 계면활성제로서 소르비탄 모노올리에이트 40 ㎖를 차례로 첨가하여 약 30분 정도 마그네틱 바로 600 rpm으로 교반시켜 실리카 졸 액적을 형성하였다. 그 후, 교반하면서 마이크로 피펫을 이용하여 헥사메틸디실라잔 11.6 ㎖를 첨가하고 10분 동안 600 rpm으로 교반하여 소수성의 구형 실리카 습윤겔을 제조하였다. 이때, 헥사메틸디실리잔을 첨가한 후 70% HNO3 1 ㎖를 추가로 첨가하였다. 제조된 소수성의 구형 실리카 습윤겔에 240 ㎖의 n-헥산 용액을 첨가하여 30분 동안 교반하여 미반응물을 세척하고, 수층을 분리한 후 상기 습윤겔은 80℃의 오븐에서 6시간 동안 상압건조하여 소수성의 구형 실리카 에어로겔 과립을 수득하였다.
Distilled water was added to water glass (Young's Chemical Co., silica content 28 ~ 30 wt.%, SiO 2 : Na 2 O = 3.52: 1) to prepare a water glass solution having a silica (SiO 2 ) content of 4.35 wt% 100 g (about 100 ㎖) 70% HNO 3 Was added to the reaction vessel containing 5 g while stirring. Subsequently, 120 ml of n-hexane and 40 ml of sorbitan monooleate as a surfactant were added to the reactor, and the mixture was stirred at 600 rpm for about 30 minutes to form a silica sol droplet. Then, while stirring, 11.6 ml of hexamethyldisilazane was added using a micropipette, and the mixture was stirred at 600 rpm for 10 minutes to prepare a hydrophobic spherical silica wet gel. At this time, after addition of hexamethyldisilane, 70% HNO 3 1 Ml was further added. 240 ml of n-hexane solution was added to the prepared hydrophobic spherical silica wet gel, and the unreacted material was washed by stirring for 30 minutes. After separating the water layer, the wet gel was dried at atmospheric pressure in an oven at 80 DEG C for 6 hours Hydrophobic spherical silica aerogel granules were obtained.
실험예Experimental Example : 주사전자현미경 분석: Scanning Electron Microscopy Analysis
상기 실시예에서 제조한 소수성의 구형 실리카 에어로겔 과립의 구조를 주사전자현미경으로 관찰하였다. 결과를 도 3에 나타내었다.
The structure of the hydrophobic spherical silica aerogel granules prepared in the above Example was observed with a scanning electron microscope. The results are shown in Fig.
도 3에 나타난 바와 같이, 본 발명에 따른 상기 실시예의 소수성의 구형 실리카 에어로겔 과립은 비교적 균일한 크기의 구형 입자를 이루고 있음을 확인하였다.
As shown in FIG. 3, it was confirmed that the hydrophobic spherical silica aerogel granules of the example according to the present invention had spherical particles of relatively uniform size.
100: 속실렛 추출기
10: 추출용매 저장조
30: 재비기
40: 응축기
50: 추출기
60: 사이폰 암
70: 냉각 순환조100: Soxylet extractor
10: Extraction solvent storage tank
30: Rebuilding
40: condenser
50: extractor
60: Siphon arm
70: cooling circulation tank
Claims (14)
2) 상기 실리카 졸 액적에 표면개질제 및 무기산을 첨가하고 반응시켜 소수성의 구형 실리카 습윤겔을 제조하는 단계; 및
3) 상기 습윤겔을 세척 및 건조하는 단계를 포함하는 소수성의 구형 실리카 에어로겔 과립의 제조방법으로서,
상기 제조방법은 상기 실리카 졸 액적의 겔화, 용매치환 및 표면개질을 동시에 수행하는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
1) adding a water glass solution to an inorganic acid to prepare a mixture, adding a non-polar organic solvent and a surfactant, and mixing to form a silica sol droplet;
2) adding a surface modifier and an inorganic acid to the silica sol droplet and reacting to prepare a hydrophobic spherical silica wet gel; And
3) washing and drying the wet gel, which comprises the steps of:
Wherein the hydrophilic spherical silica aerogel granules are simultaneously subjected to gelation, solvent substitution and surface modification of the silica sol liquid droplets.
상기 단계 1)의 무기산과 물유리 용액의 혼합물은 0.2 내지 4의 pH를 갖는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the mixture of mineral acid and waterglass solution in step 1) has a pH of 0.2 to 4. < RTI ID = 0.0 > 11. < / RTI >
상기 물유리 용액은 0.1 중량% 내지 10 중량%의 실리카를 함유하고 있는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the water glass solution contains from 0.1% to 10% by weight of silica.
상기 물유리 용액, 계면활성제 및 비극성 유기용매는 1:0.1 내지 0.5:1 내지2(물유리 용액:계면활성제:비극성 유기용매)의 부피비로 첨가되는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the water glass solution, the surfactant, and the nonpolar organic solvent are added in a volume ratio of 1: 0.1 to 0.5: 1 to 2 (water glass solution: surfactant: nonpolar organic solvent).
상기 계면활성제는 소르비탄 모노올리에이트, 소르비탄 모노스테아레이트, 소르비탄 모노팔미테이트 및 소르비탄 모노라우레이트로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the surfactant is at least one selected from the group consisting of sorbitan monooleate, sorbitan monostearate, sorbitan monopalmitate, and sorbitan monolaurate.
상기 단계 2)의 표면개질제는 상기 물유리 용액에 대하여 1:0.05 내지 0.3의 부피비(물유리 용액:표면개질제)로 첨가되고;
상기 물유리 용액은 0.1 중량% 내지 10 중량%의 실리카를 함유하는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
The surface modifier of step 2) is added to the water glass solution in a volume ratio of 1: 0.05 to 0.3 (water glass solution: surface modifier);
Wherein the water glass solution contains from 0.1% to 10% by weight of silica. ≪ RTI ID = 0.0 > 11. < / RTI >
상기 표면개질제는 헥사알킬디실라잔, 테트라알킬디실라잔 및 수화된 헥사알킬디실라잔으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the surface modifier is at least one member selected from the group consisting of hexaalkyldisilazane, tetraalkyldisilazane, and hydrated hexaalkyldisilazane.
상기 표면개질제는 헥사메틸디실라잔, 테트라메틸디실라잔 및 수화된 헥사메틸디실라잔으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the surface modifier is at least one selected from the group consisting of hexamethyldisilazane, tetramethyldisilazane, and hydrated hexamethyldisilazane.
상기 무기산은 질산, 염산, 황산, 아세트산 및 불산으로 이루어진 군으로부터 선택된 1종 이상인 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the inorganic acid is at least one selected from the group consisting of nitric acid, hydrochloric acid, sulfuric acid, acetic acid, and hydrofluoric acid.
상기 비극성 유기용매는 헥산, 헵탄, 톨루엔, 크실렌 또는 이들 혼합물인 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립의 제조방법.
The method according to claim 1,
Wherein the nonpolar organic solvent is hexane, heptane, toluene, xylene or a mixture thereof.
11. Hydrophobic spherical silica aerogel granules prepared by the process of any one of claims 1 and 3 to 11.
상기 구형 실리카 에어로겔 과립은 10 ㎛ 내지 500 ㎛ 범위의 입자크기를 갖는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립.
13. The method of claim 12,
Wherein said spherical silica aerogel granules have a particle size in the range of 10 [mu] m to 500 [mu] m.
상기 구형 실리카 에어로겔 과립은 500 m2/g 내지 900 m2/g의 비표면적을 갖는 것을 특징으로 하는 소수성의 구형 실리카 에어로겔 과립.13. The method of claim 12,
Wherein the spherical silica aerogel granules have a specific surface area of 500 m 2 / g to 900 m 2 / g.