KR101758772B1 - Film type packing material manufacture method and thin-film micro-current cell using thereof with toothbrush - Google Patents

Film type packing material manufacture method and thin-film micro-current cell using thereof with toothbrush Download PDF

Info

Publication number
KR101758772B1
KR101758772B1 KR1020170016694A KR20170016694A KR101758772B1 KR 101758772 B1 KR101758772 B1 KR 101758772B1 KR 1020170016694 A KR1020170016694 A KR 1020170016694A KR 20170016694 A KR20170016694 A KR 20170016694A KR 101758772 B1 KR101758772 B1 KR 101758772B1
Authority
KR
South Korea
Prior art keywords
microcurrent
thin film
cell
tourmaline
film
Prior art date
Application number
KR1020170016694A
Other languages
Korean (ko)
Inventor
최석호
Original Assignee
최석호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최석호 filed Critical 최석호
Priority to KR1020170016694A priority Critical patent/KR101758772B1/en
Priority to PCT/KR2017/001870 priority patent/WO2018147494A1/en
Application granted granted Critical
Publication of KR101758772B1 publication Critical patent/KR101758772B1/en

Abstract

본 발명은 필름형 충진재 제조방법, 이를 이용하여 제조된 필름형 충진재를 포함하는 박막형 미세전류셀 및 이를 포함하는 칫솔에 관한 것이다. 구체적으로는 화학전지와 같은 별도의 외부전지 없이 미세전류가 발생하는 박막형 미세전류셀을 내장하는 구조의 칫솔로써 양치질 시 박막형 미세전류셀에서 발생하는 미세전류에 의해 치약의 불소성분이 치아의 손상된 에나멜질(enamel)을 코팅하여 시린 이 개선과 충치를 예방할 수 있도록 하는 칫솔에 관한 것이다. 본 발명의 일 실시예에 따른 필름형 충진재 제조방법은, 1000 내지 10000 매쉬(mesh)로 분쇄된 토르말린(tourmaline) 분말에 포함된 철분을 자력을 이용하여 제거하는 정제 단계(S100); 상기 정제된 토르말린(tourmaline) 분말을 베이스와 1:0.4 내지 1:1.8 비율로 혼합하는 혼합 단계(S200); 상기 혼합 단계를 거친 토르말린(tourmaline) 분말에 전도성 첨가제 및 용매를 첨가하여 초음파 분산시키는 토르말린(tourmaline) 겔 제조 단계(S300); 상기 제조된 토르말린(tourmaline) 겔을 박막 형태로 도포 후 압착 롤러에 통과시켜 필름 형태로 성형하는 단계(S400); 및 상기 압착롤러를 통과한 토르말린(tourmaline) 겔을 건조시켜 필름형 충진재(120)를 제조하는 단계(S500);를 포함한다.The present invention relates to a thin film type microcurrent cell including a film-type filler, a film-type filler prepared using the same, and a toothbrush including the same. Specifically, a toothbrush having a thin film type microcurrent cell in which a micro current is generated without a separate external battery such as a chemical cell is used. As a result, micro-current generated in a thin film type microcurrent cell during tooth brushing, The present invention relates to a toothbrush which is coated with an enamel to prevent acne and prevent tooth decay. A method of manufacturing a film-type filler according to an embodiment of the present invention includes: a purifying step (S100) of removing iron powder contained in tourmaline powder pulverized to 1000 to 10000 mesh by using a magnetic force; Mixing (S200) mixing the purified tourmaline powder with the base at a ratio of 1: 0.4 to 1: 1.8; A tourmaline gel preparation step (S300) in which a conductive additive and a solvent are added to the tourmaline powder through the mixing step and ultrasonically dispersed; Coating the prepared tourmaline gel in the form of a thin film, passing the gel through a pressing roller to form a film (S400); And drying the tourmaline gel that has passed through the squeeze roller to produce a film-like filler 120 (S500).

Description

필름형 충진재 제조방법, 이를 이용하여 제조된 필름형 충진재를 포함하는 박막형 미세전류셀 및 이를 포함하는 칫솔{FILM TYPE PACKING MATERIAL MANUFACTURE METHOD AND THIN-FILM MICRO-CURRENT CELL USING THEREOF WITH TOOTHBRUSH}TECHNICAL FIELD [0001] The present invention relates to a thin film type microcurrent cell including a film type filling material and a film type filling material produced using the film type filling material, and a toothbrush including the film type filling material. BACKGROUND OF THE INVENTION 1. Field of the Invention [0002]

본 발명은 필름형 충진재 제조방법, 이를 이용하여 제조된 필름형 충진재를 포함하는 박막형 미세전류셀 및 이를 포함하는 칫솔에 관한 것이다. 구체적으로는 화학전지와 같은 별도의 외부전지 없이 미세전류가 발생하는 박막형 미세전류셀을 내장하는 구조의 칫솔로써 양치질 시 박막형 미세전류셀에서 발생하는 미세전류에 의해 치약의 불소성분이 치아의 손상된 에나멜질(enamel)을 코팅하여 시린 이 개선과 충치를 예방할 수 있도록 하는 칫솔에 관한 것이다.The present invention relates to a thin film type microcurrent cell including a film-type filler, a film-type filler prepared using the same, and a toothbrush including the same. Specifically, a toothbrush having a thin film type microcurrent cell in which a micro current is generated without a separate external battery such as a chemical cell is used. As a result, micro-current generated in a thin film type microcurrent cell during tooth brushing, The present invention relates to a toothbrush which is coated with an enamel to prevent acne and prevent tooth decay.

토르말린(tourmaline)은 육방정계에 속하는 천연 광물로 그 화학 성분은 철, 마그네슘, 알칼리금속 등과 알루미늄의 복잡한 봉규산염이다. 토르말린(tourmaline)은 그 자체가 전기를 발생하는 특성 때문에 전기석이라고 불리며, 또한 지구상에 존재하는 광물 중에서 유일하게 영구적인 전기 특성을 가지고 있어 극성 결정체라고도 불린다.Tourmaline is a natural mineral belonging to the hexagonal system and its chemical constituents are complex borosilicates of iron, magnesium, alkali metals and aluminum. Tourmaline is called tourmaline because of its electricity-generating characteristics, and is also called polar crystalline, because it has the only permanent electrical property among the minerals on earth.

선행기술 1(KR 10-2008-0026823 A)는 리튬이온 전지의 양극, 음극, 전해질, 분리막 등 구성부재의 일부 내지 전부에 토르말린(tourmaline)을 첨가하는 것으로 토르말린(tourmaline) 분말이 코팅된 것에 불과하다. 따라서, 선행기술 1은 토르말린(tourmaline)의 미세전류 발생을 향상시키는 것이 목적이 아니며, 선행기술 1에는 미세전류 발생을 향상시키기 위한 구성이 제시된 바 없다.Prior Art 1 (KR 10-2008-0026823 A) discloses that tourmaline is added to some or all of the constituent members of a lithium ion battery such as an anode, a cathode, an electrolyte, a separator, and the like, and only tourmaline powder is coated thereon Do. Therefore, the prior art 1 is not intended to improve the micro current generation of tourmaline, and the prior art 1 does not disclose a structure for improving micro current generation.

또한, 선행기술 1은 리튬이온 전지에 토르말린(tourmaline)을 첨가하는 구성이므로, 제조 공정이 복잡하며, 제조 단가가 상승하는 문제점이 있었다.In addition, prior art 1 has a structure in which tourmaline is added to a lithium ion battery, so that the manufacturing process is complicated and the manufacturing cost is increased.

KR 10-2008-0026823 AKR 10-2008-0026823 A

본 발명은 화학전지와 같은 별도의 외부전지 없이 일정 크기의 미세전류를 발생시키며, 일정 두께 이하의 박막형으로 제조되어 탈부착이 용이한 박막형 미세전류셀을 제공하기 위한 것이다.The present invention is to provide a thin film type microcurrent cell which generates a microcurrent of a predetermined size without a separate external cell such as a chemical cell and is manufactured in a thin film thickness of less than a predetermined thickness and is easy to detach and attach.

또한, 미세전류가 발생되는 박막형 미세전류셀을 칫솔에 부착하여 치약의 불소성분이 미세전류에 의해 치아의 손상된 에나멜질(enamel)을 코팅하여 시린 이 개선과 충치를 예방할 수 있는 박막형 미세전류셀이 부착된 칫솔을 제공하기 위한 것이다.In addition, a thin-film microcurrent cell, in which a thin-film microcurrent cell in which a microcurrent is generated is attached to a toothbrush and fluorine components of the toothpaste are coated with enamel damaged by a micro current, To provide an attached toothbrush.

본 발명의 목적은 여기에 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The objects of the present invention are not limited thereto, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.

본 발명의 일 실시예에 따른 필름형 충진재 제조방법은, 1000 내지 10000 매쉬(mesh)로 분쇄된 토르말린(tourmaline) 분말에 포함된 철분을 자력을 이용하여 제거하는 정제 단계(S100); 상기 정제된 토르말린(tourmaline) 분말을 베이스와 1:0.4 내지 1:1.8 비율로 혼합하는 혼합 단계(S200); 상기 혼합 단계를 거친 토르말린(tourmaline) 분말에 전도성 첨가제 및 용매를 첨가하여 초음파 분산시키는 토르말린(tourmaline) 겔 제조 단계(S300); 상기 제조된 토르말린(tourmaline) 겔을 박막 형태로 도포 후 압착 롤러에 통과시켜 필름 형태로 성형하는 단계(S400); 및 상기 압착롤러를 통과한 토르말린(tourmaline) 겔을 건조시켜 필름형 충진재(120)를 제조하는 단계(S500);를 포함한다.A method of manufacturing a film-type filler according to an embodiment of the present invention includes: a purifying step (S100) of removing iron powder contained in tourmaline powder pulverized to 1000 to 10000 mesh by using a magnetic force; Mixing (S200) mixing the purified tourmaline powder with the base at a ratio of 1: 0.4 to 1: 1.8; A tourmaline gel preparation step (S300) in which a conductive additive and a solvent are added to the tourmaline powder through the mixing step and ultrasonically dispersed; Coating the prepared tourmaline gel in the form of a thin film, passing the gel through a pressing roller to form a film (S400); And drying the tourmaline gel that has passed through the squeeze roller to produce a film-like filler 120 (S500).

상기 제조방법의, 상기 정제 단계(S100)는 상기 토르말린(tourmaline) 분말을 자력을 갖는 거름망에 통과시켜 철분을 제거하고, 순수한 토르말린(tourmaline) 분말만을 거름망 아래로 낙하시키는 중력분산방식의 건식 철분 제거 방법을 사용하는 것을 특징으로 한다.The purification step (S100) of the above manufacturing method is a method of removing the iron powder by passing the tourmaline powder through a magnetic force having a magnetic force and removing the pure iron powder of the tourmaline Method is used.

상기 제조방법의, 상기 정제 단계(S100)는 하부면에 자기장이 발생되는 용기에 물을 담고, 분쇄된 토르말린(tourmaline) 분말을 용기 내부에 투입하여, 자기장에 의해 철분을 침전시켜 제거하는 침전자기장 방식의 습식 철분 제거 방법을 사용하는 것을 특징으로 한다.The purifying step (S100) of the above manufacturing method is a purifying step (S100) in which water is contained in a container in which a magnetic field is generated on the lower surface, crushed tourmaline powder is put into the container, Type wet iron removing method is used.

상기 제조방법은, 상기 압착롤러는 제1롤러 및 제2롤러를 포함하며, 상기 성형하는 단계(S400)에서 상기 제1롤러에는 (+)전압을 인가시키고, 상기 제2롤러에는 (-)전압을 인가시키는 것을 특징으로 한다.(-) voltage is applied to the second roller, and the negative voltage is applied to the second roller in the forming step (S400). The method according to claim 1, wherein the pressing roller includes a first roller and a second roller, Is applied.

상기 제조방법은, 상기 제1롤러 및 상기 제2롤러에 인가되는 전압의 크기는 DC 3~28V이고, 상기 제1롤러 및 상기 제2롤러에 전압이 인가되는 시간은 0.1~7 초인 것을 특징으로 한다.Wherein the voltage applied to the first roller and the second roller is DC 3 to 28 V and the voltage applied to the first roller and the second roller is 0.1 to 7 seconds. do.

상기 제조방법은, 상기 베이스는 셀룰로이드, 실리콘, 펄프, 플라스틱 중 적어도 어느 하나 이상이고, 상기 전도성 첨가제는 토르말린(tourmaline) 입자간 전기적 회로망이 구성되도록 그라파이트(Graphite), CNT(Carbon nanotube), 및 금속분말 중 적어도 어느 하나 이상인 것을 특징으로 한다.In the manufacturing method, the base is at least one of celluloid, silicone, pulp and plastic, and the conductive additive is graphite, carbon nanotube (CNT), and metal And a powder.

본 발명의 또 다른 실시 예에 따른 박막형 미세전류셀은, 일측에 돌기(111)가 돌출형성된 판상의 음극(110); 상기 음극(110)을 감싸며, 상기 돌기(111)가 관통되는 돌기홀(121)을 구비한 필름형 충진재(120); 및 상기 필름형 충진재(120)가 내부에 안착되고, 상기 돌기(111)가 돌출되는 돌출홀(131)을 구비한 양극(130);을 포함한다.The thin film type microcurrent cell according to another embodiment of the present invention includes: a plate-shaped cathode 110 having protrusions 111 protruded on one side; A film type filler 120 surrounding the cathode 110 and having a protrusion hole 121 through which the protrusion 111 passes; And an anode 130 having a protruding hole 131 in which the protrusion 111 is protruded and the film-like filler 120 is seated inside.

상기 박막형 미세전류셀은, 상기 음극(110)을 감싸는 상기 필름형 충진재(120)의 일측에 배치되어, 상기 음극(110) 및 상기 필름형 충진재(120)에 이물질이 유입되는 것을 방지하는 필터부재(140);를 더 포함한다.The thin film type microcurrent cell is disposed at one side of the film type filler 120 surrounding the cathode 110 and has a filter member for preventing foreign substances from entering the cathode 110 and the film type filler 120. [ (140).

상기 박막형 미세전류셀은, 상기 돌기(111)의 측면과 상기 돌출홀(131)의 외주면은 일정간격 이격되도록 배치되는 것을 특징으로 한다.The thin film type microcurrent cell is characterized in that a side surface of the protrusion 111 and an outer circumferential surface of the protrusion hole 131 are spaced apart from each other by a predetermined distance.

본 발명의 또 다른 실시 예에 따른 박막형 미세전류셀이 부착된 칫솔은, 일측에는 다수 개의 칫솔모(211)가 구비되고, 타측에는 미세전류가 발생되는 박막형 미세전류셀(100)이 부착된 헤드(210); 및 상기 헤드(210)와 연결되어 상기 헤드(210)의 길이방향을 따라 연장형성되는 손잡이(220);를 포함한다.A toothbrush with a thin film type microcurrent cell according to another embodiment of the present invention includes a plurality of bristles 211 on one side and a head 20 on which a thin film type microcurrent cell 100 having minute currents is generated on the other side 210); And a handle 220 connected to the head 210 and extending along the longitudinal direction of the head 210.

상기 칫솔은, 상기 칫솔모(211)는, 상기 헤드(210)의 일측에 위치하는 제1모(211a); 상기 헤드(210)의 타측에 위치하는 제2모(211b); 및 상기 제1모(211a)와 상기 제2모(211b)의 사이에 위치하는 제3모(211c);를 포함한다.The toothbrush of the present invention is characterized in that the bristles 211 include a first hair 211a located at one side of the head 210; A second hair 211b positioned on the other side of the head 210; And a third hair 211c positioned between the first hair 211a and the second hair 211b.

상기 칫솔은, 상기 헤드(210)는, 일측은 상기 박막형 미세전류셀(100)의 음극(110)과 접촉하고, 타측은 상기 제1모(211a)와 접촉하는 음극부재(212); 및 일측은 상기 박막형 미세전류셀(100)의 양극(130)과 접촉하고, 타측은 상기 제2모(211b)와 접촉하는 양극부재(213);를 더 포함한다.The toothbrush includes a cathode member 212, the head 210 having one side contacting the cathode 110 of the thin film type microcurrent cell 100 and the other side contacting the first hair 211a; And an anode member 213 having one side in contact with the anode 130 of the thin film type microcurrent cell 100 and the other side in contact with the second mother 211b.

상기 칫솔은, 상기 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록, 상기 음극부재(212) 및 상기 양극부재(213)는 도전성을 갖는 재질로 형성되는 것을 특징으로 한다.The toothbrush is characterized in that the cathode member (212) and the anode member (213) are made of a conductive material so that a minute current generated in the thin film type microcurrent cell (100) flows.

상기 칫솔은, 상기 제1모(211a) 및 상기 제2모(211b)는 상기 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록 도전성을 갖는 재질로 형성되며, 상기 제3모(211c)는 절연체로 이루어지는 것을 특징으로 한다.The first hair 211a and the second hair 211b of the toothbrush are formed of a conductive material so that a minute current generated in the thin film type microcurrent cell 100 flows, and the third hair 211c ) Is made of an insulator.

본 발명의 일 실시 예에 의하면, 일정 두께 이하의 박막형으로 제조되어 칫솔 등 인체에 직접 접촉하는 기구에 용이하게 부착되며, 화학전지와 같은 별도의 외부전지 없이 인체에 일정 크기의 미세전류를 안정적으로 전달할 수 있다.According to an embodiment of the present invention, a thin film having a thickness less than a predetermined thickness can be easily attached to a mechanism that directly contacts a human body, such as a toothbrush, and a micro-current of a predetermined size can be stably .

또한, 미세전류가 발생되는 박막형 미세전류셀을 칫솔에 부착하여, 치약의 불소성분이 미세전류에 의해 치아의 손상된 에나멜질(enamel)을 코팅함으로써, 시린 이 개선과 충치를 예방할 수 있다.In addition, thin film type microcurrent cells in which micro currents are generated can be attached to the toothbrush, and the fluorine component of the toothpaste can coat the damaged enamel of the teeth due to the microcurrent, thereby improving the sickness and preventing tooth decay.

본 발명의 효과가 상술한 효과들로 한정되는 것은 아니며, 언급되지 아니한 효과들은 본 명세서 및 첨부된 도면으로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확히 이해될 수 있을 것이다.The effects of the present invention are not limited to the above-mentioned effects, and the effects not mentioned can be clearly understood by those skilled in the art from the present specification and attached drawings.

도 1은 본 발명에 따른 박막형 미세전류셀이 부착된 칫솔의 사시도이다.
도 2는 본 발명에 따른 박막형 미세전류셀의 사시도이다.
도 3은 본 발명에 따른 박막형 미세전류셀의 분해사시도이다.
도 4는 본 발명에 따른 박막형 미세전류셀의 단면도이다.
도 5는 본 발명의 일 실시예에 따른 미세전류셀의 분해사시도이다.
도 6은 본 발명의 일 실시예에 따른 미세전류셀의 단면도이다.
도 7은 본 발명에 따른 칫솔에 부착된 박막형 미세전류셀의 단면도이다.
도 8은 본 발명의 일 실시예에 따른 칫솔에 부착된 박막형 미세전류셀의 단면도이다.
도 9는 본 발명에 따른 칫솔모를 나타낸 도면이다.
도 10은 본 발명에 따른 필름형 충진재의 제조방법을 나타낸 순서도이다.
도 11은 본 발명에 따른 토르말린(tourmaline) 겔을 이용한 필름형 충진재의 제조방법을 나타낸 모식도이다.
도 12는 본 발명에 따른 압축롤러를 이용하여 전압을 인가한 토르말린(tourmaline) 겔을 나타낸 도면이다.1 is a perspective view of a toothbrush with a thin film microcurrent cell according to the present invention.
2 is a perspective view of a thin film type microcurrent cell according to the present invention.
3 is an exploded perspective view of a thin film type microcurrent cell according to the present invention.
4 is a cross-sectional view of a thin film type microcurrent cell according to the present invention.
5 is an exploded perspective view of a microcurrent cell according to an embodiment of the present invention.
6 is a cross-sectional view of a microcurrent cell according to an embodiment of the present invention.
7 is a cross-sectional view of a thin film microcurrent cell attached to a toothbrush in accordance with the present invention.
8 is a cross-sectional view of a thin film microcurrent cell attached to a toothbrush in accordance with one embodiment of the present invention.
9 is a view of a bristle according to the present invention.
10 is a flowchart showing a method of manufacturing a film-type filler according to the present invention.
11 is a schematic view showing a method for producing a film-type filler using a tourmaline gel according to the present invention.
12 is a diagram showing a tourmaline gel to which a voltage is applied using a compression roller according to the present invention.

이하, 본 발명의 실시 예를 첨부된 도면들을 참조하여 더욱 상세하게 설명한다. 본 발명의 실시 예는 여러 가지 형태로 변형할 수 있으며, 본 발명의 범위가 아래의 실시 예들로 한정되는 것으로 해석되어서는 안 된다. 본 실시 예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 더욱 완전하게 설명하기 위해 제공되는 것이다. 따라서 도면에서의 요소의 형상은 보다 명확한 설명을 강조하기 위해 과장된 것이다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. The embodiments of the present invention can be modified in various forms, and the scope of the present invention should not be construed as being limited to the following embodiments. This embodiment is provided to more fully describe the present invention to those skilled in the art. The shape of the elements in the figures is therefore exaggerated to emphasize a clearer description.

도 1은 본 발명에 따른 박막형 미세전류셀이 부착된 칫솔의 사시도이고, 도 2는 본 발명에 따른 박막형 미세전류셀의 사시도이며, 도 3은 본 발명에 따른 박막형 미세전류셀의 분해사시도이고, 도 4는 본 발명에 따른 박막형 미세전류셀의 단면도이다.2 is a perspective view of a thin film type microcurrent cell according to the present invention, FIG. 3 is an exploded perspective view of a thin film type microcurrent cell according to the present invention, and FIG. 4 is a cross-sectional view of a thin film type microcurrent cell according to the present invention.

도 1 내지 도 4를 참조하면, 박막형 미세전류셀이 부착된 칫솔(10)은 박막형 미세전류셀(100) 및 칫솔(200)을 포함할 수 있다.Referring to FIGS. 1 to 4, a toothbrush 10 with a thin film microcurrent cell may include a thin film microcurrent cell 100 and a toothbrush 200.

박막형 미세전류셀(100)은 음극(110), 필름형 충진재(120), 양극(130) 및 필터부재(140)를 포함할 수 있다.The thin film microcurrent cell 100 may include a cathode 110, a film-like filler 120, an anode 130, and a filter member 140.

음극(110)은 일측에 돌기(111)가 돌출형성될 수 있다. 도 2에 도시된 돌기(111)는 타원형으로 도시되었지만, 사용자의 기호에 맞게 변형 가능하다. 음극(110)은 판상의 형태로 형성될 수 있다.The cathode 110 may have a protrusion 111 formed on one side thereof. Although the projection 111 shown in Fig. 2 is shown as an ellipse, it is deformable to fit the taste of the user. The cathode 110 may be formed in a plate-like shape.

필름형 충진재(120)는 음극(110)을 감싸며, 돌기(111)가 관통되는 돌기홀(121)이 구비될 수 있다. 돌기홀(121)은 돌기(111)의 형상과 대응되는 형태로 형성될 수 있다. 필름형 충진재(120)는 일정 두께를 갖는 필름 형태로 형성될 수 있다. 필름형 충진재(120)는 음극(110)을 감싸서 고정하도록, 복수 개의 충진재접이부재(122)을 포함할 수 있다.The film type filler 120 may include a protrusion hole 121 surrounding the cathode 110 and through which the protrusion 111 passes. The protrusion hole 121 may be formed in a shape corresponding to the shape of the protrusion 111. The film-like filler 120 may be formed in the form of a film having a predetermined thickness. The film-like filler 120 may include a plurality of filler-material folding members 122 to enclose and fix the cathode 110.

필름형 충진재(120)의 제조방법에 대해서는 아래에서 자세히 설명하도록 한다.A method of manufacturing the film-type filler 120 will be described in detail below.

도 10은 본 발명에 따른 필름형 충진재의 제조방법을 나타낸 순서도이며, 도 11은 본 발명에 따른 토르말린(tourmaline) 겔을 이용한 필름형 충진재의 제조방법을 나타낸 모식도이고, 도 12는 본 발명에 따른 압축롤러를 이용하여 전압을 인가한 토르말린(tourmaline) 겔을 나타낸 도면이다.FIG. 10 is a flow chart showing a method for producing a film-type filler according to the present invention, FIG. 11 is a schematic view showing a method for producing a film-type filler using a tourmaline gel according to the present invention, And a tourmaline gel to which a voltage is applied using a compression roller.

도 10 내지 도 12를 참조하면, 필름형 충진재(120) 제조방법은 토르말린(tourmaline)을 1000 내지 10000 매쉬(mesh)로 분쇄한 후, 분쇄된 토르말린(tourmaline)에 포함된 철분을 자력을 이용하여 제거하는 정제 단계(S100)를 포함한다. 여기서, 토르말린(tourmaline)에 포함된 철분을 제거하기 위해 자력을 갖는 거름망에 통과 시켜 철분은 걸러지고, 순수한 토르말린(tourmaline)은 거름망 아래로 낙하하는 중력분산방식의 건식 철분 제거 방법이 사용될 수 있다. 또는, 하부면에 자기장이 발생되는 용기에 물을 담고 분쇄된 토르말린(tourmaline)을 담아 자기장에 의해 토르말린(tourmaline)에 포함된 철분이 침전되는 침전자기장 방식의 습식 철분 제거 방법이 사용될 수 있다. 건식 철분 제거 방법은 철분이 제거된 토르말린(tourmaline) 분말이 습식 철분 제거 방법에 비해 외부충격에 강할 수 있다. 또한, 많은 양의 토르말린(tourmaline) 분말의 철분을 제거할 때 용이하다. 습식 철분 제거 방법은 제조의 편리성이 뛰어나다.10 to 12, a method for manufacturing the film-type filler 120 is a method in which tourmaline is pulverized into 1000 to 10000 mesh, and iron powder contained in pulverized tourmaline is pulverized using magnetic force (S100). ≪ / RTI > Here, a gravitational dispersion type dry iron removing method may be used in which tourmaline is passed through a screen having a magnetic force to remove iron powder, and iron powder is filtered, and pure tourmaline drops down a sieve. Alternatively, a precipitation magnetic field type wet iron removal method in which water contained in a container in which a magnetic field is generated on the lower surface is crushed tourmaline and iron contained in tourmaline is precipitated by a magnetic field can be used. The dry iron removal method may be more resistant to external impact than the wet iron removal method. It is also easy to remove iron from a large amount of tourmaline powder. The wet iron removal method is excellent in manufacturing convenience.

필름형 충진재 제조방법은 정제 단계(S100) 후, 정제된 토르말린(tourmaline) 분말을 베이스와 1:0.4 내지 1:1.8 비율로 혼합하는 혼합 단계(S200)를 포함한다. 베이스는 셀룰로이드, 실리콘, 펄프, 플라스틱 중 적어도 어느 하나 이상 포함될 수 있다. 여기서, 혼합되는 방법은 회전이나 진동에 의한 혼합이 사용될 수 있다. 혼합 단계(S200)를 통해 토르말린(tourmaline) 분말은 결집력이 강화되고 물리적 우수성이 향상될 수 있다. 즉, 상기 베이스의 비율이 0.4 미만인 경우에는 후술할 토르말린 겔의 결집력이 지나치게 낮아 필름형 충진재의 강도가 낮아지고, 상기 베이스의 비율이 1.8을 초과하는 경우에는 후술할 토르말린 겔의 결집력이 지나치게 강해 베이스에 혼합된 입자의 재배열이 어려워지며, 압축롤러에 의한 가공이 어려운 문제점이 있다.The method of manufacturing a film-type filler includes a mixing step (S200) of mixing the purified tourmaline powder with the base at a ratio of 1: 0.4 to 1: 1.8 after the purification step (S100). The base may include at least one of celluloid, silicone, pulp, and plastic. Here, as the mixing method, mixing by rotation or vibration may be used. Through the mixing step (S200), the tourmaline powder can have enhanced cohesion and improved physical excellence. That is, when the ratio of the base is less than 0.4, the aggregation force of the tourmaline gel to be described below is too low to lower the strength of the film-type filler. When the ratio of the base exceeds 1.8, the aggregation force of the tourmaline gel to be described later is too strong, It is difficult to re-arrange the particles mixed in the pressing roller.

필름형 충진재 제조방법은 혼합 단계(S200) 후, 혼합된 토르말린(tourmaline) 분말은 금속분말 및 용매와 초음파를 이용하여 분산 혼합되는 토르말린(tourmaline) 겔 제조 단계(S300)를 포함한다. 전도성 첨가제는 그라파이트(Graphite), CNT(Carbon nanotube), 금속분말 중 적어도 어느 하나 이상이 포함될 수 있다. 금속분말은 은, 구리 및 알류미늄을 포함할 수 있다. 전도성 첨가제는 토르말린 입자에 의해 발생하는 미세전류가 원활하게 흐르도록, 토르말린(tourmaline) 입자들을 전기적으로 연결하는 역할을 한다. 용매는 토르말린(tourmaline) 분말을 겔화 시키며, 상기 용매에는 증류수가 포함될 수 있으나, 반드시 이에 한정되는 것은 아니고, 설계자의 의도에 따라 다른 용매가 사용될 수도 있다.The method of manufacturing a film-type filler includes a tourmaline gel preparation step (S300) in which mixed tourmaline powders are dispersed and mixed using a metal powder and a solvent and an ultrasonic wave after a mixing step (S200). The conductive additive may include at least one of graphite, carbon nanotube (CNT), and metal powder. The metal powder may include silver, copper and aluminum. The conductive additives serve to electrically connect the tourmaline particles so that the microcurrent generated by the tourmaline particles flows smoothly. The solvent gelled tourmaline powder, and the solvent may include distilled water, but not always limited thereto, and other solvents may be used depending on the designer's intention.

필름형 충진재 제조방법은 토르말린(tourmaline) 겔 제조 단계(S300) 후, 제조된 토르말린(tourmaline) 겔을 박막 형태로 도포 후 압착 롤러에 통과시켜 필름 형태로 성형하는 단계(S400)를 포함한다. 도 10을 참조하면, 토르말린(tourmaline) 겔은 분사장치를 통해 컨베이어 벨트로 토출되고, 토출된 토르말린(tourmaline) 겔은 일정 두께로 평평하게 펴진 후, 진동장치를 통해 균일하게 섞이고, 압축 롤러를 통과하여 필름 형태로 성형될 수 있다. 이때, 압축 롤러는 제1롤러 및 제2롤러를 포함할 수 있다. 토르말린(tourmaline) 겔이 통과함에 있어, 제1롤러에는 (+)전압이 인가되고 제2롤러에는 (-)전압이 인가되어, 토르말린(tourmaline) 겔 내부의 각각의 토르말린 분말을 극성에 따라 정렬시킨다(도 11 참조). The method for preparing a film-type filler comprises the step of forming a tourmaline gel (S300), applying the prepared tourmaline gel in a thin film form, and passing the gel through a pressing roller (S400) into a film form. Referring to FIG. 10, a tourmaline gel is discharged onto a conveyor belt through an injection device. The discharged tourmaline gel is uniformly mixed through a vibration device after being flatly spread to a predetermined thickness, To form a film. At this time, the pressing roller may include a first roller and a second roller. In passing the tourmaline gel, the positive (+) voltage is applied to the first roller and the negative (-) voltage is applied to the second roller to align the respective tourmaline powder within the tourmaline gel according to polarity (See FIG. 11).

즉, 도 12를 참조하면, 컨베이어 벨트 일측에 위치한 (+)전압이 인가되는 제1롤러로 인해 제1롤러와 맞닿는 토르말린 겔의 일측은 (-)극이 배치될 수 있다. 또한, 컨베이어 벨트 타측에 위치한 (-)전압이 인가되는 제2롤러로 인해 제2롤러와 맞닿는 토르말린 겔의 타측은 (+)극이 배치될 수 있다. 따라서, (+)와 (-) 전압을 인가하면 전하 입자들이 물리적으로 일관된 극성위치로 재배열될 수 있다. 이때, 토르말린 겔에 포함된 전도성 첨가제로 인해 토르말린 겔의 전기적 결집력이 향상될 수 있다.That is, referring to FIG. 12, one side of the tourmaline gel contacting the first roller due to the first roller to which a (+) voltage is applied may be disposed on the conveyor belt. In addition, a positive electrode may be disposed on the other side of the tourmaline gel contacting the second roller due to the second roller to which a negative voltage is applied on the other side of the conveyor belt. Thus, applying positive (+) and negative (-) voltages allows charge particles to be rearranged to physically consistent polarity positions. At this time, the electric cohesion of the tourmaline gel can be improved due to the conductive additive contained in the tourmaline gel.

이에 따라, 성형되는 토르말린(tourmaline) 필름은 미세전류 방출에 용이한 구조로 성형될 수 있다. 제1롤러 및 제2롤러에 인가되는 전압의 크기는 DC 3 ~ 28V일 수 있다. 제1롤러 및 제2롤러에 전압이 인가되는 시간은 0.1 ~ 7초일 수 있다. Accordingly, a tourmaline film to be formed can be formed into a structure that is easy to emit minute current. The magnitude of the voltage applied to the first roller and the second roller may be DC 3-28V. The time for which the voltage is applied to the first roller and the second roller may be 0.1 to 7 seconds.

즉, 제1롤러 및 제2롤러에 인가되는 전압이 3V보다 낮을 경우, 입자 재배열시간이 길어져 생산성이 떨어질 수 있다. 인가 전압이 28V 이상일 경우, 오옴의 법칙(I=E/R)에 의해 토르말린 겔 내부에 흐르는 전류가 증가되어 토르말린 겔에 열이 발생되므로 재배열된 입자가 파괴될 수도 있다.That is, when the voltage applied to the first roller and the second roller is lower than 3 V, the time for rearrangement of particles may become longer and the productivity may be lowered. When the applied voltage is higher than 28V, the current flowing inside the tourmaline gel is increased due to the Ohm's law (I = E / R), so that the re-arrayed particles may be destroyed as heat is generated in the tourmaline gel.

제1롤러 및 제2롤러에 전압이 인가되는 시간이 0.1 미만일 경우, 입자 재배열율이 급격히 감소될 수 있다. 전압이 인가되는 시간이 7초 이상일 경우, 생산성이 급격히 떨어질 수 있다.When the time for which the voltage is applied to the first roller and the second roller is less than 0.1, the particle rearrangement rate can be drastically reduced. If the voltage is applied for more than 7 seconds, the productivity may drop sharply.

필름형 충진재 제조방법은 성형하는 단계(S400) 후, 압착롤러를 통과한 토르말린(tourmaline) 겔을 건조시켜 필름형 충진재(120)를 제조하는 단계(S500)를 포함한다. 토르말린(tourmaline) 겔을 건조시키는 단계는 압착롤러를 통과한 토르말린(tourmaline) 겔을 일정온도의 열을 발생하는 건조기 내부로 통과시켜 성형된 형태 그대로 건조시키는 단계이다. 위와 같은 과정을 통해 토르말린(tourmaline) 겔은 필름형 충진재(120)로 제조될 수 있다. The method of manufacturing a film-type filler includes a step (S 400) of forming a film-like filler 120 by drying a tourmaline gel passed through a press roller after molding (S 400). The step of drying the tourmaline gel is a step of passing the tourmaline gel passed through the pressing roller into a dryer which generates heat at a certain temperature and drying it in a molded form. The tourmaline gel can be made of the film-like filler 120 through the above process.

이와 같이 제조된 필름형 충진재(120)의 입자 재배열 공식은 아래와 같다.The particle rearrangement formula of the film-like filler 120 thus produced is as follows.

Figure 112017012555213-pat00001
Figure 112017012555213-pat00001

여기서 Rv=rearrange voltage(출력전압), Rp=rearrange percentage(재배열 성공률), f=filler(충진양), m=mesh(입자크기), a=area(전극 면접)을 뜻한다.Here, Rv = rearrange voltage, Rp = rearrange percentage, f = filler, m = mesh, and a = area.

즉, 토르말린 입자의 재배열을 통해 제조된 미세전류 전지의 전류 출력 및 전기적 편차는 각각의 토르말린 입자들이 전기적으로 일관되게 연결되었는지 여부에 따라 달라질 수 있다. 다시 말해서, 상기 미세전류 전지의 특성을 결정짓는 여러가지 요인 중 토르말린 입자들의 재배열 성공율이 미세전류 전지의 성능에 가장 큰 영향을 미친다.That is, the current output and electrical deviation of the microcurrent cell produced through rearrangement of the tourmaline particles may vary depending on whether the respective tourmaline particles are electrically connected in a coherent manner. In other words, among the various factors determining the characteristics of the microcurrent cell, the success rate of rearrangement of the tourmaline particles has the greatest influence on the performance of the microcurrent cell.

따라서, 미세전류 전지의 성능을 최대로 발휘하기 위해, Rp(재배열 성공율)을 극대화할 필요가 있으며, 다수의 실험에 의해 m(입자크기)가 3000 ~ 5000 메쉬, 양극의 재질은 백금, 동, 스테인레스로 형성되며, 음극은 알루미늄 및 아연으로 형성될 때, 재배열 성공율이 향상되고, 출력 전류의 편차가 안정적일 수 있다.Therefore, it is necessary to maximize the Rp (rearrangement success rate) in order to maximize the performance of the microcurrent battery. In many experiments, m (particle size) is 3000 to 5000 mesh, the material of the anode is platinum, And stainless steel, and when the negative electrode is formed of aluminum and zinc, the rearrangement success rate is improved and the deviation of the output current can be stable.

양극(130) 내부에는 필름형 충진재(120)가 안착될 수 있다. 양극(130)은 돌기(111)가 돌출되는 돌출홀(131)을 구비할 수 있다. 양극(130)은 음극(110)을 감싸서 고정하도록, 복수 개의 양극접이부재(132)을 포함할 수 있다. 양극(130)과 양극접이부재(132)의 이음새(133)는 망사 형태로 이루어져 물은 통과하고 일정 두께 이상의 이물질이 유입되는 것을 방지할 수 있다(도3 참조). 돌기(111)의 측면과 돌출홀(131)의 외주면은 일정간격 이격되도록 배치되어 서로 접촉하지 않는다.The film-like filler 120 may be placed inside the anode 130. The anode 130 may include a protrusion hole 131 through which the protrusion 111 protrudes. The anode 130 may include a plurality of anode coupling members 132 so as to surround and fix the cathode 110. The joint 133 between the anode 130 and the anode coupling member 132 is formed in a mesh shape to prevent water from passing through and a foreign matter having a predetermined thickness or more from entering. The side surfaces of the projections 111 and the outer circumferential surfaces of the projecting holes 131 are spaced apart from each other by a predetermined distance and do not contact each other.

필터부재(140)는 음극(110)을 감싸는 필름형 충진재(120) 일측에 배치될 수 있다. 도 4를 참조하면, 필터부재(140)는 음극(110)을 감싸고 있는 돌기홀(121)의 반대편에 위치하는 필름형 충진재(120) 일측에 배치될 수 있다. 필터부재(140)는 망사형으로 형성되어 물은 통과하며 이물질이 유입되는 것을 방지할 수 있다.The filter member 140 may be disposed on one side of the film-like filler 120 surrounding the cathode 110. Referring to FIG. 4, the filter member 140 may be disposed on one side of the film-type filler 120 located on the opposite side of the protrusion hole 121 surrounding the cathode 110. The filter member 140 is formed in a mesh shape so that water can pass therethrough and foreign matter can be prevented from being introduced.

이에 따라 결합되는 박막형 미세전류셀(100)은 액체와 접촉시 액체를 매개로 하여 필름형 충진재(120)에서 미세전류가 발생하고, 발생된 미세전류는 음극(110) 및 양극(130)을 따라 외부로 방출될 수 있다.The thin film type microcurrent cell 100 thus coupled generates a microcurrent in the film-type filler material 120 via the liquid in contact with the liquid, and the generated microcurrent flows along the cathode 110 and the anode 130 And can be discharged to the outside.

도 7은 본 발명에 따른 칫솔에 부착된 박막형 미세전류셀의 단면도이다.7 is a cross-sectional view of a thin film microcurrent cell attached to a toothbrush in accordance with the present invention.

도 7을 참조하면, 칫솔(200)은 헤드(210) 및 손잡이(220)를 포함할 수 있으며, 헤드(210)는 칫솔모(211) 포함할 수 있다.Referring to FIG. 7, the toothbrush 200 may include a head 210 and a handle 220, and the head 210 may include bristles 211.

칫솔모(211)는 헤드(210) 일측에 구비되며, 제1모(211a), 제2모(211b) 및 제3모(211c)를 포함할 수 있다. 도 9는 본 발명에 따른 칫솔모(211)를 나타낸 도면이다. 도 9를 참조하면, 제1모(211a)는 헤드(210)의 일측에 구비될 수 있다. 제2모(211b)는 헤드(210)의 타측에 구비될 수 있다. 제3모(211c)는 제1모(211a)와 제2모(211b) 사이에 구비될 수 있다.The bristles 211 are provided on one side of the head 210 and may include a first hair 211a, a second hair 211b and a third hair 211c. Figure 9 is a view of the bristles 211 according to the present invention. Referring to FIG. 9, the first hair 211a may be provided on one side of the head 210. Referring to FIG. The second hair 211b may be provided on the other side of the head 210. The third hair 211c may be provided between the first hair 211a and the second hair 211b.

손잡이(220)는 헤드(210)와 연결되어 헤드(210)의 길이방향을 따라 연장형성될 수 있다.The handle 220 may be connected to the head 210 and extend along the longitudinal direction of the head 210.

헤드(210)의 타측에는 미세전류가 발생되는 박막형 미세전류셀(100)이 부착될 수 있다.The thin film type microcurrent cell 100 generating a fine current may be attached to the other side of the head 210.

이에 따라, 미세전류셀(100)이 부착된 칫솔(200)로 양치를 할 경우, 박막형 미세전류셀(100)에서 발생하는 미세전류에 의해 치약의 불소성분이 치아의 손상된 에나멜질(enamel)을 코팅하여 시린 이 개선과 충치를 예방할 수 있다.Accordingly, when brushing with the toothbrush 200 to which the microcurrent cell 100 is attached, the fluorine component of the toothpaste causes the damaged enamel of the tooth due to the microcurrent generated in the thin film type microcurrent cell 100 Coating can help improve acin and prevent tooth decay.

아래에서는, 박막형 미세전류셀(100)과 박막형 미세전류셀(100)이 부착된 칫솔(200)의 다른 실시예를 들어 설명하도록 한다. 또한, 중복되는 내용은 생략하도록 한다.Hereinafter, another embodiment of the thin film type micro current cell 100 and the toothbrush 200 to which the thin film type micro current cell 100 is attached will be described. In addition, redundant contents are omitted.

도 5는 본 발명의 일 실시예에 따른 미세전류셀의 분해사시도이고, 도 6은 본 발명의 일 실시예에 따른 미세전류셀의 단면도이다.FIG. 5 is an exploded perspective view of a microcurrent cell according to an embodiment of the present invention, and FIG. 6 is a cross-sectional view of a microcurrent cell according to an embodiment of the present invention.

도 5 내지 도 6을 참조하면, 박막형 미세전류셀(100)은 절연체(150)를 더 포함할 수 있다. 절연체(150)의 일측은 필터부재(140)와 접촉될 수 있다. 음극(110)은 타측에 연장형성된 음극접이부재(112)가 구비될 수 있다. 음극접이부재(112)는 절연체(150)의 타측에 접촉되어 외부로 노출될 수 있다. 이에 따라, 절연체(150)는 음극접이부재(112)를 지지하여, 외부로 노출된 음극접이부재(112)가 박막형 미세전류셀(100)의 내측방향으로 만곡되어 양극(130)에 접촉을 방지할 수 있다.5 to 6, the thin film type microcurrent cell 100 may further include an insulator 150. One side of the insulator 150 may be in contact with the filter member 140. The cathode 110 may include an anode coupling member 112 formed on the other side thereof. The cathode shifting member 112 may contact the other side of the insulator 150 and be exposed to the outside. The insulator 150 supports the cathode shift member 112 to prevent the cathode diffusion member 112 exposed to the outside from curving inward of the thin film type microcurrent cell 100 to prevent contact with the anode 130 can do.

도 8은 본 발명의 일 실시예에 따른 칫솔에 부착된 박막형 미세전류셀의 단면도이다. 도 8을 참조할 때, 헤드(210)는 음극부재(212) 및 양극부재(213)를 포함할 수 있다.8 is a cross-sectional view of a thin film microcurrent cell attached to a toothbrush in accordance with one embodiment of the present invention. Referring to FIG. 8, the head 210 may include a cathode member 212 and an anode member 213.

음극부재(212)는 헤드(210) 내측에 구비되어 일측은 박막형 미세전류셀(100)의 음극접이부재(112)와 접촉되고, 타측은 제1모(211a)와 접촉될 수 있다.The cathode member 212 is provided inside the head 210 so that one side thereof is in contact with the cathode shift member 112 of the thin film type microcurrent cell 100 and the other side is in contact with the first mother 211a.

양극부재(213)는 헤드(210) 내측에 구비되어 일측은 박막형 미세전류셀(100)의 양극(130)과 접촉되고, 타측은 제2모(211b)와 접촉될 수 있다.The anode member 213 is provided inside the head 210 so that one side of the anode member 213 is in contact with the anode 130 of the thin film type microcurrent cell 100 and the other side thereof is in contact with the second mother 211b.

또한, 음극부재(212) 및 양극부재(213)는 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록, 도전성을 갖는 재질로 형성될 수 있다.The cathode member 212 and the anode member 213 may be formed of a conductive material so that a minute current generated in the thin film type microcurrent cell 100 flows.

또한, 제1모(211a) 및 제2모(211b)는 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록 도전성을 갖는 재질로 형성될 수 있다. 제3모(211c)는 제1모(211a)와 제2모(211b) 사이의 합선을 방지하기 위해 절연체로 이루어지는 것이 바람직하다.The first and second modules 211a and 211b may be formed of a conductive material so that a minute current generated in the thin film type microcurrent cell 100 flows. The third hair 211c is preferably made of an insulator to prevent a short circuit between the first hair 211a and the second hair 211b.

(추가)(Add)

이에 따라, 박막형 미세전류셀(100)에서 발생되는 미세전류가 칫솔모(211)를 따라 치아에 직접 방출되므로, 치약의 불소성분이 치아의 손상된 에나멜질(enamel)을 코팅하여 시린 이 개선과 충치 예방에 더욱 더 효과적이다.Thus, since the micro current generated in the thin film type microcurrent cell 100 is directly discharged to the teeth along the bristles 211, the fluorine component of the toothpaste coats the damaged enamel of the tooth, . ≪ / RTI >

이상의 상세한 설명은 본 발명을 예시하는 것이다. 또한 전술한 내용은 본 발명의 바람직한 실시 형태를 나타내어 설명하는 것이며, 본 발명은 다양한 다른 조합, 변경 및 환경에서 사용할 수 있다. 즉 본 명세서에 개시된 발명의 개념의 범위, 저술한 개시 내용과 균등한 범위 및/또는 당업계의 기술 또는 지식의 범위내에서 변경 또는 수정이 가능하다. 전술한 실시예는 본 발명의 기술적 사상을 구현하기 위한 최선의 상태를 설명하는 것이며, 본 발명의 구체적인 적용 분야 및 용도에서 요구되는 다양한 변경도 가능하다. 따라서 이상의 발명의 상세한 설명은 개시된 실시 상태로 본 발명을 제한하려는 의도가 아니다. 또한, 첨부된 청구범위는 다른 실시 상태도 포함하는 것으로 해석되어야 한다.The foregoing detailed description is illustrative of the present invention. In addition, the foregoing is intended to illustrate and explain the preferred embodiments of the present invention, and the present invention may be used in various other combinations, modifications, and environments. That is, it is possible to make changes or modifications within the scope of the concept of the invention disclosed in this specification, within the scope of the disclosure, and / or within the skill and knowledge of the art. The above-described embodiments illustrate the best mode for carrying out the technical idea of the present invention, and various modifications required for specific application fields and uses of the present invention are also possible. Accordingly, the detailed description of the invention is not intended to limit the invention to the disclosed embodiments. In addition, the appended claims should be construed to include other embodiments.

10 : 박막형 미세전류셀이 부착된 칫솔
100 : 박막형 미세전류셀
110 : 음극
111 : 돌기
112 : 음극접이부재
120 : 필름형 충진재
121 : 돌기홀
122 : 충진재접이부재
130 : 양극
131 : 돌출홀
132 : 양극접이부재
133 : 이음새
140 : 필터부재
150 : 절연체
200 : 칫솔
210 : 헤드
211 : 칫솔모
211a : 제1모
211b : 제2모
211c : 제3모
212 : 음극부재
213 : 양극부재
220 : 손잡이10: Toothbrush with thin film micro current cell
100: thin film type micro current cell
110: cathode
111: projection
112: negative pole folding member
120: Film-type filler
121: projection hole
122: filler material folding member
130: anode
131: protruding hole
132: positive electrode folding member
133: Seam
140: Filter element
150: Insulator
200: Toothbrush
210: Head
211: bristles
211a: First parent
211b: second mother
211c: Third mother
212: cathode member
213: anode member
220: Handle

Claims (14)

1000 내지 10000 매쉬(mesh)로 분쇄된 토르말린(tourmaline) 분말에 포함된 철분을 자력을 이용하여 제거하는 정제 단계(S100);
상기 정제된 토르말린(tourmaline) 분말을 베이스와 1:0.4 내지 1:1.8 비율로 혼합하는 혼합 단계(S200);
상기 혼합 단계를 거친 토르말린(tourmaline) 분말에 전도성 첨가제 및 용매를 첨가하여 초음파 분산시키는 토르말린(tourmaline) 겔 제조 단계(S300);
상기 제조된 토르말린(tourmaline) 겔을 박막 형태로 도포 후 압착 롤러에 통과시켜 필름 형태로 성형하는 단계(S400); 및
상기 압착 롤러를 통과한 토르말린(tourmaline) 겔을 건조시켜 필름형 충진재(120)를 제조하는 단계(S500);를 포함하되,
상기 압착 롤러는 제1롤러 및 제2롤러를 포함하며,
상기 성형하는 단계(S400)에서 상기 제1롤러에는 (+)전압을 인가시키고, 상기 제2롤러에는 (-)전압을 인가시키는 것을 특징으로 하는 필름형 충진재 제조방법.
A purifying step (S100) of removing iron powder contained in the tourmaline powder pulverized by 1000 to 10000 mesh by using a magnetic force;
Mixing (S200) mixing the purified tourmaline powder with the base at a ratio of 1: 0.4 to 1: 1.8;
A tourmaline gel preparation step (S300) in which a conductive additive and a solvent are added to the tourmaline powder through the mixing step and ultrasonically dispersed;
Coating the prepared tourmaline gel in the form of a thin film, passing the gel through a pressing roller to form a film (S400); And
(S500) drying the tourmaline gel passed through the pressing roller to produce a film-like filler (120)
Wherein the pressing roller includes a first roller and a second roller,
Wherein a positive voltage is applied to the first roller and a negative voltage is applied to the second roller in the molding step S400.
제 1항에 있어서,
상기 정제 단계(S100)는
상기 토르말린(tourmaline) 분말을 자력을 갖는 거름망에 통과시켜 철분을 제거하고, 순수한 토르말린(tourmaline) 분말만을 거름망 아래로 낙하시키는 중력분산방식의 건식 철분 제거 방법을 사용하는 것을 특징으로 하는 필름형 충진재 제조방법.
The method according to claim 1,
The purification step (SlOO)
The method of claim 1, wherein the powder of Tourmaline is passed through a screen having a magnetic force to remove iron powder, and only pure tourmaline powder is dropped under a screen. Way.
제 1항에 있어서,
상기 정제 단계(S100)는
하부면에 자기장이 발생되는 용기에 물을 담고, 분쇄된 토르말린(tourmaline) 분말을 용기 내부에 투입하여, 자기장에 의해 철분을 침전시켜 제거하는 침전자기장 방식의 습식 철분 제거 방법을 사용하는 것을 특징으로 하는 필름형 충진재 제조방법.
The method according to claim 1,
The purification step (SlOO)
There is used a wet iron removing method of a precipitating magnetic field type in which water is contained in a container in which a magnetic field is generated on the lower surface and tourmaline powder which is pulverized is put into a container to precipitate and remove iron powder by a magnetic field. Wherein the film-type filler is a film-shaped filler.
삭제delete 제 1항에 있어서,
상기 제1롤러 및 상기 제2롤러에 인가되는 전압의 크기는 DC 3~28V이고,
상기 제1롤러 및 상기 제2롤러에 전압이 인가되는 시간은 0.1~7 초인 것을 특징으로 하는 필름형 충진재 제조방법.
The method according to claim 1,
The magnitude of the voltage applied to the first roller and the second roller is DC 3 to 28 V,
Wherein the voltage applied to the first roller and the second roller is 0.1 to 7 seconds.
제 1항에 있어서,
상기 베이스는 셀룰로이드, 실리콘, 펄프, 플라스틱 중 적어도 어느 하나 이상이고,
상기 전도성 첨가제는 토르말린(tourmaline) 입자간 전기적 회로망이 구성되도록 그라파이트(Graphite), CNT(Carbon nanotube), 및 금속분말 중 적어도 어느 하나 이상인 것을 특징으로 하는 필름형 충진재 제조방법.
The method according to claim 1,
Wherein the base is at least one of celluloid, silicone, pulp and plastic,
Wherein the conductive additive is at least one of graphite, carbon nanotube (CNT), and metal powder so as to constitute a tourmaline inter-particle electrical network.
일측에 돌기(111)가 돌출형성된 판상의 음극(110);
제 1항 내지 제 3항 및 제 5항 내지 제 6항 중 어느 하나의 제조방법에 의해 제조되고, 상기 음극(110)을 감싸며, 상기 돌기(111)가 관통되는 돌기홀(121)을 구비한 필름형 충진재(120); 및
상기 필름형 충진재(120)가 내부에 안착되고, 상기 돌기(111)가 돌출되는 돌출홀(131)을 구비한 양극(130);
을 포함하는 박막형 미세전류셀.
A plate-like cathode 110 having protrusions 111 projected on one side;
A manufacturing method of a cathode active material according to any one of claims 1 to 3 and 5 to 6 and further comprising a protrusion hole (121) through which the protrusion (111) Film type filler 120; And
An anode 130 having the film-type filler 120 mounted thereon and having a protruding hole 131 through which the protrusion 111 protrudes;
Wherein the thin film type microcurrent cell comprises:
제 7항에 있어서,
상기 음극(110)을 감싸는 상기 필름형 충진재(120)의 일측에 배치되어, 상기 음극(110) 및 상기 필름형 충진재(120)에 이물질이 유입되는 것을 방지하는 필터부재(140);
를 더 포함하는 것을 특징으로 하는 박막형 미세전류셀.
8. The method of claim 7,
A filter member 140 disposed at one side of the film type filler 120 surrounding the cathode 110 to prevent foreign substances from entering the cathode 110 and the film type filler 120;
Wherein the thin film type microcurrent cell further comprises:
제 8항에 있어서,
상기 돌기(111)의 측면과 상기 돌출홀(131)의 외주면은 일정간격 이격되도록 배치되는 것을 특징으로 하는 박막형 미세전류셀.
9. The method of claim 8,
Wherein a side surface of the protrusion (111) and an outer circumferential surface of the protrusion hole (131) are spaced apart from each other by a predetermined distance.
일측에는 다수 개의 칫솔모(211)가 구비되고, 타측에는 미세전류가 발생되는 제 9항의 박막형 미세전류셀(100)이 부착된 헤드(210); 및
상기 헤드(210)와 연결되어 상기 헤드(210)의 길이방향을 따라 연장형성되는 손잡이(220);
를 포함하는 박막형 미세전류셀이 부착된 칫솔.
A head (210) having a plurality of bristles (211) on one side and a thin-film microcurrent cell (100) on the other side of which a microcurrent is generated; And
A handle 220 connected to the head 210 and extending along the longitudinal direction of the head 210;
Wherein the thin film microcurrent cell is attached to the toothbrush.
제 10항에 있어서,
상기 칫솔모(211)는,
상기 헤드(210)의 일측에 위치하는 제1모(211a);
상기 헤드(210)의 타측에 위치하는 제2모(211b); 및
상기 제1모(211a)와 상기 제2모(211b)의 사이에 위치하는 제3모(211c);
를 포함하는 박막형 미세전류셀이 부착된 칫솔.
11. The method of claim 10,
The bristles (211)
A first hair 211a positioned at one side of the head 210;
A second hair 211b positioned on the other side of the head 210; And
A third hair 211c positioned between the first hair 211a and the second hair 211b;
Wherein the thin film microcurrent cell is attached to the toothbrush.
제 11항에 있어서,
상기 헤드(210)는,
일측은 상기 박막형 미세전류셀(100)의 음극(110)과 접촉하고, 타측은 상기 제1모(211a)와 접촉하는 음극부재(212); 및
일측은 상기 박막형 미세전류셀(100)의 양극(130)과 접촉하고, 타측은 상기 제2모(211b)와 접촉하는 양극부재(213);
를 더 포함하는 것을 특징으로 하는 박막형 미세전류셀이 부착된 칫솔.
12. The method of claim 11,
The head 210 may be,
An anode member 212 having one side in contact with the cathode 110 of the thin film type microcurrent cell 100 and the other side in contact with the first mother 211a; And
An anode member 213 having one side in contact with the anode 130 of the thin film type microcurrent cell 100 and the other side in contact with the second mother 211b;
Further comprising a plurality of thin film microcurrent cells.
제 12항에 있어서,
상기 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록, 상기 음극부재(212) 및 상기 양극부재(213)는 도전성을 갖는 재질로 형성되는 것을 특징으로 하는 박막형 미세전류셀이 부착된 칫솔.
13. The method of claim 12,
Wherein the cathode member (212) and the anode member (213) are formed of a conductive material so that a minute current generated in the thin film type microcurrent cell (100) flows. The thin film type microcurrent cell .
제 11항에 있어서,
상기 제1모(211a) 및 상기 제2모(211b)는 상기 박막형 미세전류셀(100)에서 발생되는 미세전류가 흐르도록 도전성을 갖는 재질로 형성되며,
상기 제3모(211c)는 절연체로 이루어지는 것을 특징으로 하는 박막형 미세전류셀이 부착된 칫솔.
12. The method of claim 11,
The first and second molds 211a and 211b are formed of a conductive material so that a minute current generated from the thin film type microcurrent cell 100 flows,
And the third hair (211c) is made of an insulator.
KR1020170016694A 2017-02-07 2017-02-07 Film type packing material manufacture method and thin-film micro-current cell using thereof with toothbrush KR101758772B1 (en)