KR101758725B1 - Construction finishing composition that includes nonmetallic mineral and mixed compsitions for coloration and manufacturing method of construction finishing materials by using the same - Google Patents
Construction finishing composition that includes nonmetallic mineral and mixed compsitions for coloration and manufacturing method of construction finishing materials by using the same Download PDFInfo
- Publication number
- KR101758725B1 KR101758725B1 KR1020160073987A KR20160073987A KR101758725B1 KR 101758725 B1 KR101758725 B1 KR 101758725B1 KR 1020160073987 A KR1020160073987 A KR 1020160073987A KR 20160073987 A KR20160073987 A KR 20160073987A KR 101758725 B1 KR101758725 B1 KR 101758725B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- composition
- parts
- coloring
- mineral
- Prior art date
Abstract
본 발명은 비금속광물 착색용 조성물 및 이를 이용한 착색된 비금속 광물의 제조방법에 관한 것으로, 본 발명의 일 실시예에 따른 비금속광물 착색용 조성물은 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 경화제 및 상기 경화제 100 중량부에 대하여 폴리옥시알킬렌 폴리올(polyoxyalkylene polyol) 30 내지 700 중량부가 포함되는 것일 수 있다.The present invention relates to a composition for coloring nonmetal minerals and a method for preparing colored nonmetallic minerals using the same, wherein the composition for coloring nonmetal minerals according to an embodiment of the present invention comprises at least one selected from the group consisting of methylene diphenyl diisocyanate, A curing agent selected from the group consisting of polymethylene polyphenyl isocyanate and a mixture thereof, and from 30 to 700 parts by weight of polyoxyalkylene polyol relative to 100 parts by weight of the curing agent.
Description
비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물 및 이를 포함하는 건축마감재에 관한 것이다. 보다 상세하게는 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 사용하여 건축물의 내벽, 외벽 또는 바닥에 착색된 인조석재 시공을 할 수 있고, 상기 시공된 마감재는 건축물의 내벽, 외벽 또는 바닥에 강하게 부착되며 높은 내구성을 가질 뿐만 아니라, 스프레이 방식 등으로 간단한 공정으로 건축물의 외벽, 내벽 또는 바닥층에 착색된 외벽층을 마감하는 시공을 할 수 있다는 장점을 가진다.Nonmetallic minerals and a coloring composition, and a building finish material comprising the same. More specifically, it is possible to apply artificial stone colored on an inner wall, an outer wall or a floor of a building by using a composition for building finishing including a nonmetallic mineral and a mixing composition for coloring, It is strongly attached to the floor and has high durability. In addition, it has a merit of being able to finish the colored outer wall layer on the outer wall, inner wall or bottom floor of the building by a simple process such as spraying.
일반적으로 건축물에서 많이 사용되고 있는 천연 석재는 그 자체가 지니고 있는 문양과 질감 및 석재 자체의 특성(내구성, 내화학성, 내식성, 고강도 등)에 의하여 건축재 등으로 널리 사용되고 있으나, 생산량에 가격과 생산량에 제한이 있고, 특히 석재의 물성 내지 석재가 가진 무늬 등이 일정하지 않기 때문에 사용할 수 있는 천연석이 제한적이라는 문제점이 있다.Natural stone, which is generally used in buildings, is widely used as a building material due to its own pattern, texture and characteristics of stone itself (durability, chemical resistance, corrosion resistance, high strength, etc.) There is a problem that the natural stone which can be used is limited because the physical properties of the stone or the pattern of the stone are not constant.
이에 천연석의 색상 및 무늬 등의 특성과 유사한 형태를 가지도록 하는 인조 석재 또는 석재에 붙이는 필름, 기타 석재의 가공품으로서 등으로서 다양한 방면으로 천연 석재를 대체하기 위한 연구가 진행되어 왔으며, 그 결과 다양한 방식에 의해서 천연 석재와 유사한 형태를 가지는 인테리어 등의 제품이 개발되어 다양한 용도로 고급화 되고 있다.As a result, studies have been carried out to replace natural stone in various ways as artificial stone or film attached to stone to make shapes similar to those of natural stone, such as color and pattern, and as a processed product of other stone, And the like, which have a shape similar to that of natural stone, have been developed and are being advanced for various purposes.
크기가 큰 천연석재 또는 제조된 인조석재 자체에 직접 착색을 하는 경우 그 질감의 표현이나 착색층의 형성이 자연스럽지 못하다는 문제가 있다. 따라서, 일반적으로는 일정한 크기의 비금속광물을 착색하여 착색층을 형성하고 상기 착색층이 형성된 일정한 크기의 비금속광물을 가공하여 일정한 무늬나 질감 등을 표현하면서 인테리어 등으로 사용할 수 있는 인조석재를 제조하는 방법이 활용되고 있는 실정이다.There is a problem in that when the natural stones having a large size or the artificial stone itself are directly colored, the expression of the texture and the formation of the colored layer are not natural. Therefore, in general, a non-metallic mineral of a predetermined size is colored to form a colored layer, and a non-metallic mineral having a predetermined size formed with the colored layer is processed to produce a synthetic stone that can be used as an interior while expressing a certain pattern or texture The method is utilized.
특히 건축물의 외벽, 내벽 또는 바닥 등에 직접 착색을 하는 경우 착색층이 고르게 형성되도록 시공하는 것이 어렵고, 내구성이 약할 뿐만 아니라 자연스러운 질감 또는 무늬를 표현하기 어렵다는 문제가 있다.In particular, when coloring directly on an outer wall, an inner wall or a floor of a building, it is difficult to construct the colored layer uniformly, and the durability is weak and it is difficult to express a natural texture or pattern.
따라서 일정한 크기의 작은 석재를 착색하거나 소성하여 상기 작은 석재에 색을 입히고 착색된 작은 석재를 압축 성형하는 등의 방법으로 제조된 인조석재를 상기 건축물의 외벽, 내벽 또는 바닥 등에 시공하는 방법이 많이 활용되고 있다. 이 경우 제작된 인조석재 또는 천연석재를 일정한 크기의 마감재로 제작하고, 상기 제작된 마감재를 건출물의 일정한 위치에 부착하는 공정이 필요하기 때문에 건출물에 따라 공정이 다양해지거나 인력이 많이 필요로 하게 되는 문제가 있다. Therefore, a method of constructing artificial stone made by a method of coloring or firing a small stone of a predetermined size to color the small stone and compression molding a colored small stone is applied to the outer wall, inner wall or floor of the building . In this case, since it is necessary to manufacture the artificial stone or the natural stone by using a finishing material having a predetermined size and to attach the finished material to a predetermined position of the dry material, .
즉, 인조석재를 사용하는 경우에도 천연석재와 마찬가지로 건축물에 맞도록 석재를 가공하여 건축물에 부착하는 시공이 필요하고, 최근 건축물의 형태가 다양해지고 있으며 인건비가 상승 등으로 상기 시공에 따른 비용이 많아지고 있다.In other words, even when artificial stone is used, it is necessary to apply stone to the building by machining the stone so as to fit the same structure as the natural stone. Recently, the shape of the building has been diversified and labor costs have increased, ought.
따라서 건축물의 외벽, 내벽 또는 바닥을 마감하는 마감재를 일정한 조성물로 구현하여 작업현장에서 직접 분사함으로서 건축물의 마감재가 형성 및 건축물에 부착되도록 하면서도 높은 내구성 뿐만 아니라 석재의 질감, 색감이 자연스럽게 구현될 수 있도록 하는 방안이 필요하다.Therefore, the finishing material which finishes the outer wall, the inner wall or the floor of the building is realized with a certain composition and is injected directly at the work site, so that the finishing material of the building can be attached to the building and the structure, while the durability as well as the texture and color of the stone can be realized naturally It is necessary to plan.
관련 선행기술을 보면, 선행기술 1(KR 10-0342176 B1)에는 에폭시 수지조성물에 합성수지 필름칼라 칩을 혼합한 수지 혼합물에 경화제를 첨가한 조성물을 개시하고 있으며, 이를 이용하여 코팅대상의 표면에 소정 두께를 가지도록 도포하고 경화시켜 인조 대리석을 제조하는 방법이 개시되어 있으나, 이 경우 코팅면이 외부자극에 의해 벗겨지거나 마모되는 단점이 있고, 또한 장시간 자외선에 노출시 탈색되는 현상이 발생하여 본래의 코팅 색감을 잃어버리는 단점이 있다. 특히 본원발명에서 지적하는 바와 같은 공정의 단순화를 이룰 수 없다는 문제가 남는다.Prior Art 1 (KR 10-0342176 B1) discloses a composition prepared by adding a curing agent to a resin mixture obtained by mixing a resin film composition with an epoxy resin composition, and by using the composition, And the coating surface is peeled off or worn by the external stimuli. In addition, when the coating surface is exposed to ultraviolet rays for a long period of time, there is a phenomenon of discoloration of the artificial marble, There is a drawback that the color of the coating is lost. In particular, there remains a problem that the process can not be simplified as pointed out in the present invention.
또한, 선행기술 2(KR 10-0366568 B1)에는 에폭시 수지조성물을 30 내지 100℃로 가열한 상태에서 수지조성물에 합성수지 필름 칼라 칩을 혼합한 혼합물을 감압상태에서 교반하여 기포나 수분을 제거하고, 상기 수지 혼합물에 경화제를 첨가하여 재차 감압 탈포한 후, 상기 감압 탈포된 혼합물을 형틀에 부어 성형하고, 성형된 성형제를 지촉경화 상태가 되도록 하는 1차 경화단계 및 1차 경화가 완료된 성형체를 일정시간 유지시켜 성형체의 완전한 경화가 이루어지도록 하는 단계로 이루어진 인조 대리석의 제조방법이 개시되어 있다.In the prior art 2 (KR 10-0366568 B1), a mixture obtained by mixing an epoxy resin composition with a synthetic resin film color chip in a resin composition at 30 to 100 캜 is stirred under reduced pressure to remove bubbles and moisture, A first curing step in which a curing agent is added to the resin mixture and the mixture is vacuum degassed again and then the mixture is poured into a mold to cause the molded molding agent to be in a touched state; So as to allow complete curing of the molded body.
그러나, 상기와 같은 제조방법으로 제조되는 인조 대리석의 경우 내·외장재로 요구되는 강도를 만족시키고, 내마모성, 내수축성, 내수성 및 내한성과 내화학성 면에서 우수한 성질을 가지나, 이 또한 장시간 자외선에 노출시 탈색되는 현상을 보여 본래의 색감을 잃어버리는 단점이 있다. 나아가 이 역시 공정의 특성상 본원발명이 인식하는 건축물의 내벽, 외벽 또는 바닥을 마감하는 공정을 단순화 하는 조성물로 활용할 수 없다는 문제가 있다.However, the artificial marble produced by the above-described production method satisfies the strength required for interior and exterior materials and has excellent properties in terms of abrasion resistance, shrink resistance, water resistance, cold resistance and chemical resistance, It is disadvantageous in that the original color is lost due to the phenomenon of discoloration. Furthermore, this process also has a problem in that it can not be utilized as a composition for simplifying the process of closing the inner wall, outer wall or floor of a building recognized by the present invention.
본 발명의 목적은 변색이 거의 없어 색지속성이 우수하고, 원하는 다양한 색상 및 질감을 연출할 수 있는 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 관한 것이다. An object of the present invention is to provide a composition for architectural finishing which contains a non-metallic mineral and a coloring composition capable of exhibiting various colors and textures as desired with excellent color sustainability with little discoloration.
또한 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 의하는 경우 마감시공이 필요한 건축물의 내벽, 외벽 또는 바닥에 바로 시공하여 인조석재와 같은 연출을 할 수 있으므로 공정효율이 상당히 높다.In addition, when the composition for building finishing including the nonmetallic mineral and the coloring composition is used, it can be directly applied to the inner wall, the outer wall or the floor of the building requiring finishing construction to produce the same effect as the artificial stone.
그리고 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 의하는 경우 형성된 마감시공층의 내구성 및 색감이 우수하고 상기 비금속광물과 착색용 혼합조성물의 접착성 및 건축물에 대한 접합성이 높아 건축물에 안정적인 마감시공층을 형성할 수 있다.In addition, when the composition for building finishing includes the non-metallic mineral and the composition for coloring, the finishing construction layer formed thereon is excellent in durability and color, and the adhesion of the non-metallic mineral and the coloring composition and the bonding property to the building are high, A stable finishing construction layer can be formed.
본 발명의 다른 목적은 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 이용한 건축마감재를 제공하는 것이다.Another object of the present invention is to provide a building finishing material using the composition for architectural finishing including the nonmetallic mineral and the coloring composition.
상기 건축마감재에 의하는 경우 마감층이 되는 석재 또는 기타 마감재료에 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 도포하여 원하는 형태의 색상 및 질감을 가진 인조석재를 바로 제작하여 사용할 수 있다.When the building finishing material is applied to a stone or other finishing material to be a finishing layer, a composition for a building finishing including the nonmetal mineral and a coloring composition is applied to produce a synthetic stone having a desired color and texture, .
특히 상기 건축물의 마감시공이 필요한 곳에 필요한 형태로 마감재료를 선정 및 가공하고 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 도포하여 다양한 형태의 석재마감재를 제공할 수 있게 하는 것이다.In particular, it is possible to select and process a finishing material in a form necessary for finishing construction of the building, and to apply a composition for architectural finishing including the nonmetallic mineral and a coloring composition to provide various types of stone finishing materials.
본 발명의 목적을 달성하기 위하여, 본 발명의 일 실시예에 따른 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 활석, 석고, 방해석, 형석, 인회석, 장석, 석영, 황옥, 강옥, 금강석 및 이들의 혼합물로 이루어진 비금속광물, 조색제, 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 경화제 및 상기 경화제 100 중량부에 대하여 폴리옥시알킬렌 폴리올(polyoxyalkylene polyol) 30 내지 700 중량부, 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 10 내지 700 중량부를 포함하는 제1 착색혼합물, 그리고 증점제, 데카논산(decanoic acid), 라우르산(lauric acid),미리스틱산(myristic acid), 팔미틱산(palmitic acid), 스테아릭산(stearic acid), 올레익산(oleic acid), 미네랄유(mineral oil), 옥시스테아린(oxystearine), 디메틸폴리실록산(dimethyl polysiloxane), 이산화규소(silicon dioxide), 소르비탄모노스테아레이트(sorbitanmonostearate) 및 이들의 혼합물로 이루어진 군에서 선택된 표면 안정제 및 상기 표면 안정제 100 중량부에 대하여 프로판디올 (Propanediol) 10 내지 300 중량부를 포함하는 제2 착색혼합물을 포함하는 것이다.In order to achieve the object of the present invention, a composition for architectural finishing including a non-metallic mineral and a coloring composition according to an embodiment of the present invention may be selected from the group consisting of talc, gypsum, calcite, fluorite, apatite, feldspar, quartz, A curing agent selected from the group consisting of nonmetal minerals consisting of cemented carbide, cemented carbide, and a mixture thereof, a colorant, methylene diphenyl diisocyanate, polymethylene polyphenyl isocyanate, and a mixture thereof, And 30 to 700 parts by weight of polyoxyalkylene polyol per 100 parts by weight of at least one selected from the group consisting of toluene, methyl ethyl ketone, xylene, cyclohexanone, polyethylene glycol polyethylene glycol, methyl isobutylketone, and mixtures thereof. A first coloring mixture comprising 10 to 700 parts by weight of a colorant selected from the group consisting of thickeners, decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, The composition of the present invention may be prepared by dissolving or dispersing a mixture of an acid, oleic acid, mineral oil, oxystearine, dimethyl polysiloxane, silicon dioxide, sorbitan monostearate, And a second coloring mixture comprising 10 to 300 parts by weight of propanediol per 100 parts by weight of the surface stabilizer.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 비금속광물 및 제1 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합되고, 상기 비금속광물 및 제2 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합된 것일 수 있다.Wherein the non-metallic mineral and the first colored mixture are mixed in a weight ratio of 1:10 to 10: 1, and the non-metallic mineral and the second colored mixture are mixed in a ratio of 1:10 to 10: 10: 1 by weight.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 표면 안정제 100 중량부에 대하여 하기의 화학식 1로 이루어진 중화제 10 내지 300 중량부를 더 포함하는 것일 수 있다.The composition for architectural finishing including the nonmetal mineral and the coloring composition may further comprise 10 to 300 parts by weight of a neutralizing agent represented by the following chemical formula 1 with respect to 100 parts by weight of the surface stabilizer.
[화학식 1][Chemical Formula 1]
(X는 수소 또는 탄소수 1 내지 10의 알킬기) (X is hydrogen or an alkyl group having 1 to 10 carbon atoms)
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 제2 착색혼합물이 하기의 화학식 2로 이루어진 첨가제를 더 포함하는 것일 수 있다.The composition for building finishing including the nonmetal mineral and the coloring composition may further comprise an additive having the following formula (2).
[화학식 2](2)
(n은 1 ~ 200의 자연수)(n is a natural number of 1 to 200)
본 발명의 다른 일 실시예에 따른 건축마감재는 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 포함하는 것이다.The architectural finishing material according to another embodiment of the present invention includes the composition for architectural finishing including the nonmetal mineral and the coloring composition.
이하, 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 일 실시예에 따른 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 활석, 석고, 방해석, 형석, 인회석, 장석, 석영, 황옥, 강옥, 금강석 및 이들의 혼합물로 이루어진 비금속광물, 조색제, 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 경화제 및 상기 경화제 100 중량부에 대하여 폴리옥시알킬렌 폴리올(polyoxyalkylene polyol) 30 내지 700 중량부, 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 10 내지 700 중량부를 포함하는 제1 착색혼합물, 그리고 증점제, 데카논산(decanoic acid), 라우르산(lauric acid),미리스틱산(myristic acid), 팔미틱산(palmitic acid), 스테아릭산(stearic acid), 올레익산(oleic acid), 미네랄유(mineral oil), 옥시스테아린(oxystearine), 디메틸폴리실록산(dimethyl polysiloxane), 이산화규소(silicon dioxide), 소르비탄모노스테아레이트(sorbitanmonostearate) 및 이들의 혼합물로 이루어진 군에서 선택된 표면 안정제 및 상기 표면 안정제 100 중량부에 대하여 프로판디올 (Propanediol) 10 내지 300 중량부를 포함하는 제2 착색혼합물을 포함하는 것이다.The composition for architectural finishing including the nonmetallic mineral and the coloring composition according to an embodiment of the present invention may be selected from the group consisting of talc, gypsum, calcite, fluorite, apatite, feldspar, quartz, , A colorant, a curing agent selected from the group consisting of methylene diphenyl diisocyanate, polymethylene polyphenyl isocyanate, and mixtures thereof, and a curing agent selected from the group consisting of polyoxyalkylene polyol 30 to 700 parts by weight of a polyoxyalkylene polyol and at least one member selected from the group consisting of toluene, methyl ethyl ketone, xylene, cyclohexanone, polyethylene glycol, methyl isobutyl ketone ( methyl isobutylketone), and mixtures thereof, and 10 to 700 parts by weight of any one selected from the group consisting of A first coloring mixture and a thickener, decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, A surface stabilizer selected from the group consisting of mineral oil, oxystearine, dimethyl polysiloxane, silicon dioxide, sorbitan monostearate, and mixtures thereof; And 10 to 300 parts by weight of propanediol relative to 100 parts by weight of the surface stabilizer.
상기 활석, 석고, 방해석, 형석, 인회석, 장석, 석영, 황옥, 강옥, 금강석 및 이들의 혼합물은 착색되어 자연스러운 형태의 색감과 질감을 가지도록 하는 석재로서 비금속 광물을 말한다.The above-mentioned talc, gypsum, calcite, fluorite, apatite, feldspar, quartz, topaz, corundum, diamond, and mixtures thereof are colored non-metallic minerals that have natural color and texture.
바람직하게 상기 비금속광물은 운모를 말한다. 운모를 사용하는 경우 상기 제1 착색혼합물 및 제2 착색혼합물에 따라 착색층이 자연스럽게 형성될 수 있으며, 마감재로 도포하는 경우 운도에 내구성 및 접착성이 우수한 착색층을 형성할 수 있다.Preferably the non-metallic mineral refers to mica. In the case of using mica, the colored layer can be formed naturally according to the first colored mixture and the second colored mixture, and when applied with a finishing material, a colored layer having excellent durability and adhesiveness can be formed.
더 바람직하게 상기 비금속광물은 평균직경이 0.1 내지 10mm인 것일 수 있다. 상기 범위에 의하는 경우 착색된 운모가 서로 달라붙지 않으면서 자연스러운 착색층을 연출할 수 있고, 형성된 착색층이 벗겨지거나 마감재로 사용할 때 상기 운모가 떨어져나가는 문제를 방지할 수 있다.More preferably, the non-metallic mineral may have an average diameter of 0.1 to 10 mm. According to the above range, the colored mica does not stick to each other and a natural coloring layer can be produced, and the problem that the colored layer is peeled off or the mica falls off when used as a finishing material can be prevented.
가장 바람직하게는 상기 비금속광물은 평균직경이 0.5 내지 2mm인 운모 100 중량부, 상기 평균직경이 0.5 내지 2mm인 운모에 대하여 평균직경이 1 내지 3mm인 운모 100 내지 500 중량부 및 평균직경이 3 내지 8mm인 운모 100 내지 500 중량부인 것일 수 있다. 상기 범위에 의하는 경우 자연석과 같은 질감 및 색상 연출이 될 수 있을 뿐만 아니라 운모끼리 들러붙어 착색되지 않는 부분이 발생하는 문제를 해결할 수 있다.Most preferably, the non-metallic mineral comprises 100 parts by weight of mica having an average diameter of 0.5 to 2 mm, 100 to 500 parts by weight of mica having an average diameter of 1 to 3 mm with respect to the mica having an average diameter of 0.5 to 2 mm, And 100 to 500 parts by weight of mica having a diameter of 8 mm. According to the above-mentioned range, it is possible to provide a texture and color reproduction similar to a natural stone, and also to solve the problem that a portion which is stuck to the mica and is not colored occurs.
상기 제1 착색혼합물은 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 경화제 및 상기 경화제 100 중량부에 대하여 폴리옥시알킬렌 폴리올(polyoxyalkylene polyol) 30 내지 700 중량부가 포함되는 것일 수 있다.Wherein the first colored mixture is selected from the group consisting of methylene diphenyl diisocyanate, polymethylene polyphenyl isocyanate, and mixtures thereof, and a curing agent selected from the group consisting of polyoxy And 30 to 700 parts by weight of a polyoxyalkylene polyol.
바람직하게 상기 폴리옥시알킬렌 폴리올은 상기 경화제 100 중량부에 대하여 50 내지 310 중량부로 포함된 것일 수 있다. 상기 범위에 의하는 경우 조색제의 색감을 살리면서도 내구성이 강하고 색지속성이 우수한 착색층을 형성할 수 있다.The polyoxyalkylene polyol may be contained in an amount of 50 to 310 parts by weight based on 100 parts by weight of the curing agent. According to the above range, it is possible to form a coloring layer which is strong in durability and excellent in color sustainability while utilizing the color of the coloring agent.
더 바람직하게는 상기 폴리옥시알킬렌 폴리올은 상기 경화제 100 중량부에 대하여 80 내지 240 중량부로 포함된 것일 수 있다. 상기 범위에 의하는 경우 조색제 사용과 함께 색의 표현성이 우수하면서도 착색층의 색지속력과 착색층의 내구성, 비금속광물에 대한 접착성이 급격히 높아질 수 있다.More preferably, the polyoxyalkylene polyol may be contained in an amount of 80 to 240 parts by weight based on 100 parts by weight of the curing agent. In this range, the color sustainability of the colored layer, the durability of the colored layer, and the adhesion to non-metallic minerals can be drastically enhanced, as well as excellent color reproducibility with the use of a coloring agent.
특히 상기 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate)를 사용하는 경우 표면이 불규칙한 규사에 대하여 부착성 및 내구성이 우수하고 색연출에 용이할 수 있다. 상기 경화제는 착색된 비금속광물에 경화된 착색층을 형성하기 위한 것으로 상기 폴리옥시알킬렌 폴리올과 결합하여 내구성이 우수한 착색층을 형성한다.In particular, when methylene diphenyl diisocyanate is used, adhesion and durability to irregular silica sand are excellent and color rendering can be facilitated. The curing agent is for forming a cured colored layer in a colored nonmetallic mineral and is combined with the polyoxyalkylene polyol to form a colored layer having excellent durability.
한편, 상기 폴리옥시칼릴렌 폴리올을 사용해야 경화성이 우수할 수 있어 색지속 및 색의 표현성이 높아질 수 있다.On the other hand, the use of the polyoxycalylene polyol may be excellent in curability and the color sustainability and color reproducibility may be enhanced.
상기 경화제는 메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate)이 혼합된 것일 수 있으며, 바람직하게는 1 : 1 내지 1 : 10 중량비로 혼합된 것일 수 있다.The curing agent may be a mixture of methylene diphenyl diisocyanate and polymethylene polyphenyl isocyanate, preferably in a weight ratio of 1: 1 to 1:10.
보다 바람직하게는 35 : 100 내지 45 : 100 중량비로 혼합된 것일 수 있다. 상기 범위에 의한 경우 상기 착색층의 내구성이 매우 우수하며, 조색제의 변색을 막는 효과가 매우 탁월할 수 있다.More preferably from 35: 100 to 45: 100 by weight. According to the above range, the coloring layer has excellent durability, and the effect of preventing the discoloration of the coloring agent can be remarkably excellent.
상기 제1 착색 혼합물 및 제2 착색 혼합물의 점도는 0.9 내지 1.2 cP인 것일 수 있다. 점도가 0.9 cP 미만인 경우 상기 운모 등 비금속 광물에 착색층이 너무 얇게 생성될 뿐만 아니라 운모의 기계적 강도를 보강하는 효과가 저하되고 착색 이후에 색변색의 문제가 있다. 또한, 점도가 1.2 cP를 초과하는 경우 상기 제1 또는 제2 착색 혼합물의 혼합이 잘 이루어지지 않으며, 상기 운모 등 비금속광물에 착색층이 고르게 분산되지 않아 표현하는 색채 또는 질감이 제대로 표현되지 않을 수 있다.The viscosity of the first colored mixture and the second colored mixture may be 0.9 to 1.2 cP. When the viscosity is less than 0.9 cP, not only the colored layer is too thin in the nonmetallic mineral such as mica but also the effect of reinforcing the mechanical strength of the mica is lowered and there is a problem of color discoloration after coloring. If the viscosity exceeds 1.2 cP, the first or second colored mixture may not be mixed well, and the colored layer may not be uniformly dispersed in the non-metallic mineral such as mica, have.
상기 경화제로 에폭시 수지, 아크릴 수지, 우레탄 수지를 사용하는 경우 착색층의 내구성이 저하되는 문제를 극복하기 어렵고, 특히 형성된 착색층 안에서 변색이 발생하는 문제를 해결할 수가 없다. 그러나 상기 비금속광물 착색용 조성물의 구성 및 그 함량 및 점도 범위에 의하는 경우 형성된 착색층의 높은 내구성과 특히 착색층이 변색되지 않아 장기간 색감과 질감을 유질할 수 있다는 장점을 가진다.When an epoxy resin, an acrylic resin or a urethane resin is used as the curing agent, it is difficult to overcome the problem that the durability of the colored layer is lowered, and in particular, the problem of discoloration in the formed colored layer can not be solved. However, according to the composition and content and viscosity range of the composition for non-metallic mineral coloring, the coloring layer formed has high durability and coloring layer is not discolored, so that coloring and texture can be maintained for a long time.
상기 비금속광물 착색용 조성물은 상기 경화제 100 중량부에 대하여 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느하나를 10 내지 700 중량부 더 포함하는 것일 수 있다.The composition for coloring non-metallic minerals may further comprise at least one selected from the group consisting of toluene, methyl ethyl ketone, xylene, cyclohexanone, polyethylene glycol, methyl Methyl isobutyl ketone, and a mixture thereof. In addition, it may further comprise 10 to 700 parts by weight of any one selected from the group consisting of methyl isobutyl ketone and mixtures thereof.
상기 경화제 100 중량부에 대하여 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나는 용제로 사용되어, 상기 비금속광물 착색용 조성물의 점도를 조정하는데 사용하는 것일 수 있다.Methylene isobutylketone, cyclohexanone, polyethylene glycol, and methyl isobutylketone are added to 100 parts by weight of the curing agent, And a mixture thereof may be used as a solvent to be used for adjusting the viscosity of the nonmetal mineral coloring composition.
상기 비금속광물 착색용 조성물은 조색제를 더 포함하는 것일 수 있다. 상기 조색제는 유기안료 및 무기안료로서 해당분야에서 통상의 지식을 가진 자가 사용할 수 있는 모든 범위의 안료를 포함하는 것으로 본다.The non-metallic mineral coloring composition may further comprise a coloring agent. The colorant may be considered to include a whole range of pigments that can be used by those skilled in the art as organic pigments and inorganic pigments.
한편, 상기 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 용제가 상기 경화제 100 중량부에 대하여 10 중량부 미만인 경우 분산에 문제가 생길 수 있어, 상기 상도 코팅층이 상기 착색층과 강하게 결합되기 어려울 뿐만 아니라 착색층의 변색을 막는 효과가 저하되는 문제가 있고, 200 중량부를 초과하는 경우 상기 착색층에 대한 결합력 접착력 감소 및 기계적 내구성 저하의 문제가 있다. 또한 색감의 표현이 달라져 착색층의 자연스러운 연출이 어렵다는 문제가 있다.On the other hand, the above-mentioned toluene, methyl ethyl ketone, xylene, cyclohexanone, polyethylene glycol, methyl isobutylketone, and mixtures thereof Is less than 10 parts by weight based on 100 parts by weight of the curing agent, there is a problem of dispersion, and it is difficult for the top coat layer to be strongly bonded to the coloring layer and also to prevent discoloration of the coloring layer There is a problem that the effect is deteriorated. When the amount exceeds 200 parts by weight, there is a problem of a decrease in bonding force for the colored layer and a decrease in mechanical durability. In addition, there is a problem that the expression of color is changed so that it is difficult to produce a colored layer naturally.
바람직하게는 상기 용제는 30 내지 110 중량부로 포함되는 것일 수 있다. 상기 범위에 의하는 경우 형성된 상기 상도 코팅층이 상기 착색층과 강하게 결합될 수 있는 장점이 있고, 상기 착색층의 변색을 효과적으로 방지할 수 있다.Preferably, the solvent is contained in an amount of 30 to 110 parts by weight. According to the above-mentioned range, the upper coating layer formed can be strongly bonded to the coloring layer, and discoloration of the coloring layer can be effectively prevented.
또한, 바람직하게는 상기 용제는 톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나 일 수 있다. 점도의 조절 및 높은 휘발성에 의해 공정효율이 높아질 뿐만 아니라 상기 상도 코팅층이 상기 착색층에 강하게 결합되면서 상기 착색층이 변색을 방지하는 상도 코팅층이 형성될 수 있기 때문이다.Preferably, the solvent may be any one selected from the group consisting of toluene, methyl ethyl ketone, and mixtures thereof. Control of viscosity and high volatility increase the process efficiency not only because the top coating layer is strongly bonded to the coloring layer, but also the top coating layer preventing the coloring layer from discoloring can be formed.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 증점제를 사용하여 점도가 조정된 것일 수 있다. 즉, 상기 제1 착색 혼합물 및 제2 착색 혼합물의 점도를 일정한 정도로 낮추고 상기 증점제가 혼합되면서 조성물 전체의 점도를 높이도록 한 것이다.The composition for architectural finishing including the non-metallic mineral and the coloring composition may be one whose viscosity has been adjusted using a thickener. That is, the viscosity of the first colored mixture and the second colored mixture is lowered to a certain degree and the viscosity of the entire composition is increased while the thickening agent is mixed.
따라서 제1 착색혼합물 및 제2 착색혼합물은 점도가 0.9 내지 1.2 cP가 되게 하여 각 착색혼합물의 배합이 원활하게 이루어질 수 있도록 하고, 상기 운모에 고르게 분산되어 운모 표면의 기계적 강도를 높이고 착색층을 형성하게 하는 것이다. 나아가 상기 증점제를 사용하는 경우 운모가 포함된 조성물 전체의 점도를 높여 상기 조성물로 시공된 마감재의 강도를 높이고, 상기 조성물을 사용한 마감재의 시공이 원활히 이루어지게 하는 것일 수 있다.Accordingly, the first colored mixture and the second colored mixture have a viscosity of 0.9 to 1.2 cP so that the mixing of each colored mixture can be smoothly performed, and evenly dispersed in the mica to increase the mechanical strength of the mica surface and form a colored layer . Further, when the thickener is used, the viscosity of the entire composition including mica may be increased to increase the strength of the finish material applied with the composition, and the finish material using the composition may be smoothly applied.
바람직하게 상기 증점제는 셀룰로스, 젤라틴, 팩틴, 구아검, 잔탄 및 이들의 혼합물로 이루어진 증점다당류 군에서 선택된 어느하나 일 수 있다. 상기 증점다당류를 사용하는 경우 조성물 전체의 점도를 높이는 것일 수 있다.Preferably, the thickening agent may be selected from the group consisting of cellulose, gelatin, pectin, guar gum, xanthan gum, and mixtures thereof. If the thickening polysaccharide is used, the viscosity of the entire composition may be increased.
더 바람직하게 상기 증점제는 구아검 및 잔탄이 2 : 1 중량비로 혼합된 것이고, 상기 표면안정제 100 중량부에 대하여 10 내지 200 중량부로 포함된 것일 수 있다. 상기 범위에 의하는 경우 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 포함된 제1 착색 혼합물과 제2 착색 혼합물이 혼합되고, 상기 혼합된 제1 착색 혼합물과 제2 착색 혼합물이 운모 표면에 고르게 분산된 후에 조성물 전체의 점성이 증가할 수 있어 효과적이다. 즉 조성물의 점성이 빠르게 높아지면 상기 착색 혼합물의 혼합이 잘 이루어지지 않고 운모에 착색되지 않은 부분이 발생하거나 운모 표면에 기계적 강도를 보강하는 효과가 저하되는 문제가 있다.More preferably, the thickener is a mixture of guar gum and xanthan gum at a weight ratio of 2: 1, and may be contained in an amount of 10 to 200 parts by weight based on 100 parts by weight of the surface stabilizer. According to the above range, the first coloring mixture and the second coloring mixture contained in the composition for building finishing including the nonmetallic mineral and the coloring composition are mixed, and the first coloring mixture and the second coloring mixture are mixed in the mica The viscosity of the entire composition can be increased after being evenly dispersed on the surface, which is effective. That is, if the viscosity of the composition is rapidly increased, the colored mixture may not be mixed well and the uncoloured portion may be formed or the effect of reinforcing the mechanical strength on the mica surface may deteriorate.
가장 바람직하게는 상기 증점제는 구아검 및 잔탄이 4 : 1 내지 1 : 4 중량비로 혼합된 것이고, 상기 표면안정제 100 중량부에 대하여 10 내지 200 중량부로 포함되고, 상기 표면안정제 100 중량부에 대하여 제2인산칼륨이 0.01 내지 0.5 중량부로 포함된 것일 수 있다.Most preferably, the thickener is a mixture of guar gum and xanthan gum in a weight ratio of 4: 1 to 1: 4, and is contained in an amount of 10 to 200 parts by weight based on 100 parts by weight of the surface stabilizer, 0.01 to 0.5 parts by weight of potassium diphosphate may be included.
상기 제2인산칼륨이 포함된 경우 상기 증점제에 사용에 따른 조성물 전체의 점도가 증가하는 속도를 늦출 수 있어 상기 착색 혼합물과 운모가 효과적으로 혼합되고 조성물 전체의 점도를 높이게 할 수 있다. 상기 제2 인산캄륨이 0.01 중량부 미만으로 포함되는 경우 증점에 대한 지연효과가 거의 없으며, 0.5 중량부를 초과하여 포함되는 경우 증점효과가 발생하지 않는 문제가 있다.When the second potassium phosphate is included, the rate at which the viscosity of the composition as a whole increases with use of the thickener can be slowed, so that the colored mixture and the mica can be effectively mixed and the viscosity of the entire composition can be increased. When the second potassium phosphate is contained in an amount of less than 0.01 part by weight, there is almost no retarding effect on the thickening, and when it exceeds 0.5 part by weight, the thickening effect does not occur.
즉, 본 발명은 각 혼합물이 순차적으로 혼합하여 착색하던 공정을 점도를 이용하여 한번에 혼합되고 최종적으로 착색된 비금속광물을 제조하는 것으로 공정효율이 상당히 높다는 장점을 가진다.That is, the present invention has an advantage in that the process efficiency is remarkably high by mixing the blend sequentially and coloring the blend in one step by using the viscosity and finally producing the colored nonmetallic mineral.
상기 조색제는 무기 도료 또는 유기 도료를 사용하는 것일 수 있으며, 해당 분야에서 통상의 지식을 가진 자가 사용할 수 있는 도료를 모두 포함하는 것으로 본다.The coloring agent may be an inorganic paint or an organic paint, and may be considered to include all kinds of paint that can be used by a person skilled in the art.
상기 표면 안정제는 데카논산(decanoic acid), 라우르산(lauric acid),미리스틱산(myristic acid), 팔미틱산(palmitic acid), 스테아릭산(stearic acid), 올레익산(oleic acid), 미네랄유(mineral oil), 옥시스테아린(oxystearine), 디메틸폴리실록산(dimethyl polysiloxane), 이산화규소(silicon dioxide), 소르비탄모노스테아레이트(sorbitanmonostearate) 및 이들의 혼합물로 이루어진 군에서 선택된 것일 수 있다.The surface stabilizer may be selected from the group consisting of decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, and may be selected from the group consisting of mineral oil, oxystearine, dimethyl polysiloxane, silicon dioxide, sorbitan monostearate, and mixtures thereof.
상기 표면 안정제를 사용하는 경우 운모를 포함하는 상기 비금속광물에 착색되지 않은 부분이 발생하지 않고, 상기 착색 혼합물의 사용에 따른 운모의 기계적 강도가 고르게 높아지게 되어 조성물의 혼합과정 및 혼합된 조성물을 사용한 마감재의 시공과정에서 운모가 부서지는 문제를 방지할 수 있어 공정효율을 높일 수 있는 장점이 있다.When the surface stabilizer is used, uncolored portions are not generated in the nonmetallic mineral including mica, and the mechanical strength of the mica according to the use of the colored mixture is uniformly increased. Thus, the mixing process of the composition and the finish material It is possible to prevent the problem of the mica being broken in the construction process, thereby improving the process efficiency.
바람직하게 상기 표면 안정제는 미네랄유(mineral oil) 및 옥시스테아린(oxystearine)이 1 : 3 내지 3 : 1 중량비로 포함되는 것일 수 있다. 상기 범위에 의하는 경우 표면 안정제 사용에 따른 착색 혼합물의 색감에 영향을 미치지 않아 자연스러운 색감과 질감을 얻을 수 있다.Preferably, the surface stabilizer may include mineral oil and oxystearine in a weight ratio of 1: 3 to 3: 1. In the above range, the color tone of the color mixture due to the use of the surface stabilizer is not affected, and natural color and texture can be obtained.
상기 제2 착색혼합물은 상기 표면 안정제 100 중량부에 대하여 프로판디올(Propanediol) 10 내지 300 중량부로 포함되는 것이다.And the second colored mixture comprises 10 to 300 parts by weight of propanediol per 100 parts by weight of the surface stabilizer.
상기 프로판디올을 사용하는 경우 착색된 운모끼리 들러붙는 문제를 방지할 수 있을 뿐만 아니라 자연스러운 색감을 연출할 수 있는 장점을 가진다.When the propanediol is used, it is possible to prevent the colored mica from sticking to each other and also to produce a natural color feeling.
특히 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 종래 기술과 달리 혼합물을 순차적으로 배합하고 배합된 혼합물을 석재 등에 도포하는 방식이 아니라, 석재를 포함하는 비금속광물 및 착색조성물 전체를 한번에 배합하여 사용하는 것이기 때문에 운모에 착색되지 않거나 표면의 기계적 강도가 보강되지 않은 부분이 발생할 수 있고, 전체적인 내구성이 저하되는 문제가 있다. 특히 상기 제2 착색 혼합물을 사용하지 않는 경우 운모끼리 들러붙어 전체적으로 자연스러운 질감이 연출되지 않으며 착색되지 않는 부분이 많이 발생하는 문제가 있다.In particular, the composition for architectural finishing including the nonmetallic mineral and the coloring composition is not a method in which the mixture is sequentially compounded and the compounded mixture is applied to a stone or the like, unlike the prior art, but the nonmetal mineral including the stone and the whole coloring composition There is a problem that a portion which is not colored in the mica or the surface of which mechanical strength is not reinforced may occur, and the durability as a whole deteriorates. Particularly, when the second coloring mixture is not used, there is a problem that the mica is stuck between the mica, so that a natural texture is not entirely produced and a lot of uncolored portions are generated.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 비금속광물 및 제1 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합되고, 상기 비금속광물 및 제2 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합된 것일 수 있다.Wherein the non-metallic mineral and the first colored mixture are mixed in a weight ratio of 1:10 to 10: 1, and the non-metallic mineral and the second colored mixture are mixed in a ratio of 1:10 to 10: 10: 1 by weight.
상기 범위에 의하는 경우 운모 등 비금속광물의 표면 강화 및 고른 착색층을 형성할 수 있다.According to the above range, surface strengthening of non-metallic minerals such as mica and uniform coloring layer can be formed.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 표면 안정제 100 중량부에 대하여 하기의 화학식 1로 이루어진 중화제 10 내지 300 중량부를 더 포함하는 것일 수 있다.The composition for architectural finishing including the nonmetal mineral and the coloring composition may further comprise 10 to 300 parts by weight of a neutralizing agent represented by the following chemical formula 1 with respect to 100 parts by weight of the surface stabilizer.
[화학식 1][Chemical Formula 1]
(X는 수소 또는 탄소수 1 내지 10의 알킬기) (X is hydrogen or an alkyl group having 1 to 10 carbon atoms)
상기 화학식 1로 표시되는 중화제를 사용하는 경우 착색층이 운모에 강하게 형성되어 기계적 강도가 높아질 수 있으며, 착색 혼합물 사용에 따른 자연스러운 색감과 질감을 연출할 수 있다.When the neutralizing agent represented by the above formula (1) is used, the colored layer is formed strongly on the mica and the mechanical strength can be increased, and the natural color and texture can be produced by using the colored mixture.
상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 제2 착색혼합물이 하기의 화학식 2로 이루어진 첨가제를 더 포함하는 것일 수 있다.The composition for building finishing including the nonmetal mineral and the coloring composition may further comprise an additive having the following formula (2).
[화학식 2](2)
(n은 1 ~ 200의 자연수)(n is a natural number of 1 to 200)
상기 화학식 2로 표시되는 첨가제를 사용하는 경우 운모의 기계적 강도가 높아지고 착색층의 색감이 자연스러울 뿐만 아니라 착색층의 자외선에 의한 색변색이 방지될 수 있다.When the additive represented by the general formula (2) is used, the mechanical strength of the mica is increased, the color of the colored layer is natural, and color discoloration due to ultraviolet rays of the colored layer can be prevented.
바람직하게 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 경화제 100 중량부에 대하여 아크릴 에멀전(Acrylate emulsion) 50 내지 400 중량부를 포함하는 것일 수 있다. 상기 아크릴 에멀전을 사용하는 경우 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 사용하여 시공한 마감층의 기계적 강도가 크게 높아질 수 있는 장점이 있다. 즉 마감재 전체의 강도가 높아지고 자연스러운 색연출 효과를 낼 수 있다.Preferably, the composition for architectural finishing including the non-metallic mineral and the coloring composition may include 50 to 400 parts by weight of an acryl emulsion based on 100 parts by weight of the curing agent. When the acrylic emulsion is used, the mechanical strength of the finish layer formed using the composition for architectural finishing including the non-metallic mineral and the coloring composition can be greatly increased. That is, the strength of the entire finish material is increased and a natural color rendering effect can be obtained.
상기 아크릴 에멀전이 50 중량부 미만으로 포함되는 경우 기계적 강도 보강효과가 저하되며, 400 중량부를 초과하여 포함되는 경우 색감에 영향을 미쳐 마감재의 자연스러운 색감과 질감을 연출하기 곤란하다는 문제가 있다.When the acrylic emulsion is contained in an amount of less than 50 parts by weight, the effect of reinforcing mechanical strength is deteriorated. When the acrylic emulsion is contained in an amount exceeding 400 parts by weight, there is a problem that it is difficult to produce a natural color and texture of the finishing material.
더 바람직하게 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 상기 경화제 100 중량부에 대하여 아크릴 에멀전(Acrylate emulsion) 50 내지 400 중량부 및 하이드록시 암모늄(Ammonia aqueous)를 0.01 내지 1 중량부로 포함하는 것일 수 있다.More preferably, the composition for architectural finishing comprising the non-metallic mineral and the coloring composition comprises 50 to 400 parts by weight of an acryl emulsion and 0.01 to 1 part by weight of an aqueous ammonia, based on 100 parts by weight of the curing agent It may be included as part.
상기 하이드록시 암모늄을 포함하는 경우 기계적 강도가 높아지는 효과가 극대화될 수 있어 상기 조성물 사용에 따라 마감재가 안정적으로 설치될 수 있으며, 색감에 영향이 미치지 않아 자연스러운 색연출이 가능할 수 있다. 상기 하이드록시 암모늄염이 0.01 중량부 미만으로 포함되는 경우 기계적 강도 보강효과가 없으며, 1 중량부를 초과하여 포함되는 경우 아크릴 에멀전 사용에 따른 기계적 강도가 오히려 저하되는 문제가 발생한다.When the hydroxyammonium is included, the effect of increasing the mechanical strength can be maximized, so that the finishing material can be stably installed according to the use of the composition, and natural coloring can be achieved without affecting the color. When the hydroxyammonium salt is contained in an amount of less than 0.01 part by weight, there is no mechanical strength reinforcing effect. When the amount of the hydroxyammonium salt is more than 1 part by weight, the mechanical strength of the acrylic emulsion is lowered.
본 발명의 다른 일 실시예에 따른 건축마감재는 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 포함하는 것이다.The architectural finishing material according to another embodiment of the present invention includes the composition for architectural finishing including the nonmetal mineral and the coloring composition.
본 발명의 효과는 변색이 거의 없어 색지속성이 우수하고, 원하는 다양한 색상 및 질감을 연출할 수 있는 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 제공하는 것이다.The effect of the present invention is to provide a composition for architectural finishing which contains a non-metallic mineral and a coloring composition capable of exhibiting a desired color and texture with excellent color persistence due to little discoloration.
또한 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 의하는 경우 마감시공이 필요한 건축물의 내벽, 외벽 또는 바닥에 바로 시공하여 인조석재와 같은 연출을 할 수 있으므로 공정효율이 상당히 높다는 장점을 가진다.In addition, when the composition for building finishing including the non-metallic mineral and the coloring composition is used, it can be directly applied to the inner wall, outer wall or floor of a building requiring finishing construction to produce the same effect as artificial stone, .
그리고 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물에 의하는 경우 형성된 마감시공층의 내구성 및 색감이 우수하고 상기 비금속광물과 착색용 혼합조성물의 접착성 및 건축물에 대한 접합성이 높아 건축물에 안정적인 마감시공층을 형성할 수 있다.In addition, when the composition for building finishing includes the non-metallic mineral and the composition for coloring, the finishing construction layer formed thereon is excellent in durability and color, and the adhesion of the non-metallic mineral and the coloring composition and the bonding property to the building are high, A stable finishing construction layer can be formed.
본 발명의 다른 실시예로서 건축마감재는 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 이용한 것이다.In another embodiment of the present invention, the architectural finishing material is a composition for architectural finishing including the nonmetal mineral and the coloring composition.
상기 건축마감재에 의하는 경우 마감층이 되는 석재 또는 기타 마감재료에 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 도포하여 원하는 형태의 색상 및 질감을 가진 인조석재를 바로 제작하여 사용할 수 있다.When the building finishing material is applied to a stone or other finishing material to be a finishing layer, a composition for a building finishing including the nonmetal mineral and a coloring composition is applied to produce a synthetic stone having a desired color and texture, .
특히 상기 건축물의 마감시공이 필요한 곳에 필요한 형태로 마감재료를 선정 및 가공하고 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물을 도포하여 다양한 형태의 석재마감재를 제공할 수 있다.In particular, it is possible to select and process a finishing material in a form necessary for finishing construction of the building, and to apply a composition for architectural finishing including the non-metallic mineral and a coloring composition to provide various types of stone finishing materials.
나아가 상기 비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물은 각 조성물을 순차적으로 배합하고 필요한 석재에 도포하여 착색하는 단계를 거치는 것이 아니라 각 조성물 전체와 비금속광물이 한번에 배합되어 착색된 비금속광물을 필요한 곳에 바로 시공할 수 있도록 하는 장점을 가진다.Further, the composition for architectural finishing including the non-metallic mineral and the coloring composition is not a process of sequentially compounding the respective compositions and applying the composition to the required stone to perform coloring, but the whole composition and the non-metallic mineral are blended together to form a colored non- So that it can be installed immediately where it is needed.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention. The present invention may, however, be embodied in many different forms and should not be construed as limited to the embodiments set forth herein.
[제조예 1: 착색된 비금속 광물의 제조][Preparation Example 1: Preparation of colored nonmetallic mineral]
하기의 표 1과 같은 구성의 조성물을 사용하여 하기의 비교예 및 실시예에 따른 착색된 비금속광물을 제조하였다. 운모 및 각 조성물을 시간의 차이를 두지 않고 한번에 배합하여 사용하였다.Colored nonmetallic minerals according to the following comparative examples and examples were prepared using compositions having the compositions shown in Table 1 below. Mica and each composition were blended at once without any difference in time.
(단위: 중량부)(Unit: parts by weight)
- 운모: 평균입경이 0.5 내지 8mm인 운모.Mica: mica with an average particle diameter of 0.5 to 8 mm.
- 조색제: 유성 조색제- Concentrate: Oily Concentrate
- 증점제: 옥시스테아린- Thickening agent: Oxystearin
- 증점제: 구아검 및 잔탄 2 : 1 중량비 혼합- Thickener: mixed with guar gum and xanthan gum at a weight ratio of 2: 1
- 중화제: [화학식 1]로 표현되는 화합물- neutralizing agent: a compound represented by the formula (1)
(X는 수소 또는 탄소수 1 내지 10의 알킬기) (X is hydrogen or an alkyl group having 1 to 10 carbon atoms)
- 첨가제: [화학식 2]로 표현되는 화합물- additive: a compound represented by the formula (2)
(n은 1 ~ 200의 자연수)(n is a natural number of 1 to 200)
[[ 실험예Experimental Example 1: 배합방법에 따른 1: Depending on the mixing method 착색유무Presence or absence of coloration 평가] evaluation]
상기 비교예 1 및 2에 의하는 경우 의하는 경우 상기 운모와 상기 조성물을 한번에 배합하였을 때, 운모에 착색되지 않는 부분이 생기거나 운모끼리 들러붙는 문제가 발생하여 한번에 배합하는 공정으로는 착색된 운모를 생성할 수 없는 것을 확인하였다.According to the above-mentioned Comparative Examples 1 and 2, when the mica and the composition were blended together at once, there was a problem that a portion not colored in the mica occurred, or the mica adhered to each other, Can not be generated.
상기 실시예 1 내지 6에 의하는 경우 운모에 일정한 착색층이 형성되었으며, 이에 따라 실시예에 따른 착색층에 대한 색감, 기계적 강도 및 시공성을 평가하였다.In Examples 1 to 6, a colored layer was formed on the mica, and the color, mechanical strength and workability of the colored layer according to the examples were evaluated.
[[ 실험예Experimental Example 2: 2: 실시예의Example 물성평가] Property evaluation]
본 발명에서 목적으로 하는 공정에 따라 착색된 비금속광물이 형성되지 않는 비교예를 제외하고 상기 제조예에 따라 제조된 실시예 1 내지 6에 따른 내구성, 내열성, 착색된 색채, 질감 및 색지속성을 비교하여 지수로 표현하였다. 상기 지수는 모든 항목에서 가장 우수한 결과를 얻은 실시예 1을 10으로 하고, 상기 실시예 1과 비교하여 1 내지 10의 지수로 평가하였다. 따라서 상기 지수가 높을수록 평가항목에 대한 결과가 우수한 것이다.Comparing the durability, heat resistance, colored color, texture and color persistence according to Examples 1 to 6 prepared according to the above Preparation Example, except for the Comparative Example in which no colored metallic mineral was formed according to the aimed process of the present invention . The index was evaluated as an index of 1 to 10 as compared to Example 1, with Example 1 having the best results in all items. Therefore, the higher the index, the better the results for the evaluation items.
(단위: 지수)(Unit: index)
상기 표 2를 참조하면, 본 발명의 구성에 따른 실시예에 의하는 경우 한번에 각 조성물과 운모를 한번에 배합하여도 운모에 일정한 착색층을 형성할 수 있어 공정효율을 크게 높일 수 있다는 것을 알 수 있다.Referring to Table 2, according to the embodiment of the present invention, it can be seen that even when the compositions and mica are blended at once, a uniform coloring layer can be formed on the mica, and the process efficiency can be greatly increased .
실시예 1 내지 6에 의하는 경우 한번에 배합 및 시공할 수 있어 마감재를 시공하는 공정에 대한 공정효율이 크게 높아질 수 있다.According to Examples 1 to 6, it is possible to formulate and apply the composition at one time, and the process efficiency for the step of applying the finishing material can be greatly increased.
특히 실시예 4 내지 6에 의하는 경우 착색정도가 우수하였을 뿐만 아니라 아크릴 에멀전에 사용된 실시예 5 및 6의 경우 내구성, 질감 및 색지속성이 상당히 우수하다는 사실을 확인할 수 있다.In particular, the examples 4 to 6 show not only excellent coloring degree but also excellent durability, texture and color persistence in Examples 5 and 6 used in the acrylic emulsion.
또한 제2 인산칼륨이 포함되는 경우 조성물이 충분히 배합되고 운모에 착색층이 형성된 뒤에 점도가 높아지게 되므로 낮은 점도에서 배합이 충분히 일어난 뒤 증점제 사용에 따른 점도 증가효과가 발생하게 되어 효과적인 혼합 이후 증점효과로 운모에 대한 착색과 표면 보강효과가 높을 뿐만 아니라 착색층의 질감이 상당히 우수해진다는 사실을 확인할 수 있었다.In addition, when potassium diphosphate is included, the composition is sufficiently compounded and after the coloring layer is formed on the mica, the viscosity becomes high. Therefore, after the compounding is sufficiently carried out at low viscosity, viscosity increase effect is caused by the use of the thickener, It was confirmed that the coloring and surface reinforcement effect on the mica was high and the texture of the colored layer was remarkably improved.
이상에서 본 발명의 바람직한 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, Of the right.
Claims (5)
조색제,
메틸렌 다이페닐 디이소시아네이트(methylene diphenyl diisocyanate), 폴리메틸렌 폴리페닐 이소시아네이트 (polymethylene polyphenyl isocyanate) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나인 경화제 및
상기 경화제 100 중량부에 대하여 폴리옥시알킬렌 폴리올(polyoxyalkylene polyol) 30 내지 700 중량부,
톨루엔(toluene), 메틸에톤케톤(methyl ethyl ketone), 자일렌(xylene), 사이클로헥사논(cyclohexanone), 폴리에틸렌글리콜(polyethylene glycol), 메틸이소부틸케톤(methyl isobutylketone) 및 이들의 혼합물로 이루어진 군에서 선택된 어느 하나를 10 내지 700 중량부를 포함하는 제1 착색혼합물, 그리고
증점제,
데카논산(decanoic acid), 라우르산(lauric acid),미리스틱산(myristic acid), 팔미틱산(palmitic acid), 스테아릭산(stearic acid), 올레익산(oleic acid), 미네랄유(mineral oil), 옥시스테아린(oxystearine), 디메틸폴리실록산(dimethyl polysiloxane), 이산화규소(silicon dioxide), 소르비탄모노스테아레이트(sorbitanmonostearate) 및 이들의 혼합물로 이루어진 군에서 선택된 표면 안정제 및
상기 표면 안정제 100 중량부에 대하여 프로판디올 (Propanediol) 10 내지 300 중량부를 포함하는 제2 착색혼합물을 포함하는 것이고,
상기 비금속광물 및 제1 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합되고,
상기 비금속광물 및 제2 착색혼합물은 1 : 10 내지 10 : 1 중량비로 혼합된 것이고,
상기 표면 안정제 100 중량부에 대하여
하기의 화학식 1로 이루어진 중화제 10 내지 300 중량부를 포함하는
비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물.
[화학식 1]
(X는 수소 또는 탄소수 1 내지 10의 알킬기) Nonmetallic minerals consisting of talc, gypsum, calcite, fluorite, apatite, feldspar, quartz, topaz, corundum,
Coloring agent,
A curing agent selected from the group consisting of methylene diphenyl diisocyanate, polymethylene polyphenyl isocyanate, and mixtures thereof; and
30 to 700 parts by weight of a polyoxyalkylene polyol relative to 100 parts by weight of the curing agent,
And is preferably a mixture of toluene, methyl ethyl ketone, xylene, cyclohexanone, polyethylene glycol, methyl isobutylketone, and mixtures thereof. And 10 to 700 parts by weight of any one selected from
Thickener,
Stearic acid, oleic acid, mineral oil, and the like. The term " acidic " or " acidic " A surface stabilizer selected from the group consisting of oxystearine, dimethyl polysiloxane, silicon dioxide, sorbitan monostearate, and mixtures thereof, and
And 10 to 300 parts by weight of propanediol relative to 100 parts by weight of the surface stabilizer.
The non-metallic mineral and the first colored mixture are mixed in a weight ratio of from 1:10 to 10: 1,
The non-metallic mineral and the second colored mixture are mixed in a weight ratio of 1:10 to 10: 1,
With respect to 100 parts by weight of the surface stabilizer
And 10 to 300 parts by weight of a neutralizing agent represented by the following formula
A nonmetallic mineral and a coloring composition.
[Chemical Formula 1]
(X is hydrogen or an alkyl group having 1 to 10 carbon atoms)
상기 제2 착색혼합물은
하기의 화학식 2로 이루어진 첨가제를 더 포함하는 것인
비금속광물 및 착색용 혼합 조성물이 포함된 건축마감용 조성물.
[화학식 2]
(n은 1 ~ 200의 자연수)The method according to claim 1,
The second colored mixture
And further comprising an additive of the following formula (2)
A nonmetallic mineral and a coloring composition.
(2)
(n is a natural number of 1 to 200)
건축마감재.A non-metallic mineral according to any one of claims 1 to 4, and a composition for architectural finishing including a coloring composition.
Architectural finish.