KR101710333B1 - Organicinorganic hybrid paint composition for floor finish and construction method using thereof - Google Patents
Organicinorganic hybrid paint composition for floor finish and construction method using thereof Download PDFInfo
- Publication number
- KR101710333B1 KR101710333B1 KR1020160076701A KR20160076701A KR101710333B1 KR 101710333 B1 KR101710333 B1 KR 101710333B1 KR 1020160076701 A KR1020160076701 A KR 1020160076701A KR 20160076701 A KR20160076701 A KR 20160076701A KR 101710333 B1 KR101710333 B1 KR 101710333B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- curing agent
- agent
- reactive diluent
- Prior art date
Abstract
Description
본 발명은 본 발명은 유ㆍ무기 하이브리드 바닥마감용 도료 조성물 및 이를 이용한 시공방법에 관한 것으로, 0.5~3.0mm 도막두께로 시공이 가능한 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 관한 것이다.The present invention relates to a paint composition for organic / inorganic hybrid flooring and a method of applying the same, and relates to a paint composition for organic / inorganic hybrid flooring which can be applied with a film thickness of 0.5 to 3.0 mm.
각종 구조물에 있어서 대기 중에 노출된 시멘트ㆍ콘크리트 표면은 외부 환경요인에 의해 부패, 부식, 마모 등이 발생하여 구조물의 수명이 단축하게 된다. 따라서 구조물의 수명연장을 위하여 일반적으로 시멘트ㆍ콘크리트 표면에 도막을 형성하여 보호하고 있다. 특히, 시멘트ㆍ콘크리트 바닥 면에 있어서 내마모성, 내수성, 내화학성 및 내구성을 향상시키기 위하여 에폭시, 아크릴, 우레탄 및 각종 하드너 등을 시공하고 있다.In the case of various structures, exposed surface of cement and concrete in the atmosphere is subject to external environmental factors, resulting in corrosion, corrosion and abrasion, which shortens the life of the structure. Therefore, in order to extend the life of the structure, a coating film is generally formed on the surface of the cement / concrete. In particular, epoxy, acrylic, urethane and various hardeners are applied to improve the abrasion resistance, water resistance, chemical resistance and durability of the cement / concrete floor.
시멘트ㆍ콘크리트 바닥면을 보호하기 위한 도료 제품은 도막의 두께에 따라서 크게 세 가지로 분류되고 있다.Paint products to protect the cement and concrete floor are classified into three types according to the thickness of the coating.
첫 번째로는 시공두께가 0.1~0.3mm로 마감되는 박막형 도료로서, 시공이 간편하고, 공사기간이 짧기 때문에 시공단가가 저렴하여 건축현장에 많이 적용되고 있다. 그러나, 도막두께가 얇기 때문에 소지면의 요철 등으로 인하여 미관이 좋지 못하고, 통행량이 많은 코너나 램프부위 등이 쉽게 마모되거나 벗겨지는 문제점이 있다.The first is a thin film type coating with a construction thickness of 0.1 ~ 0.3mm, which is easy to construct and has a low construction cost due to its short construction period. However, since the thickness of the coating film is thin, the aesthetics and the like of the base paper are poor and the corners and lamp parts having a large traffic amount are easily worn or peeled off.
두 번째로는 시공두께가 0.5~3.0mm로 마감되는 후막형 도료로서, 시공두께가 두껍게 마감되기 때문에 소지면의 요철을 은폐하여 미관적으로 우수하고, 고강도이기 때문에 반영구적으로 사용할 수 있지만, 상기 박막형 도료보다 비용이 높게 들어가는 문제점이 있다.Secondly, it is a thick film type coating which is finished with a construction thickness of 0.5 to 3.0 mm. Since the construction thickness is thickly finished, it can be used semi-permanently because it hides the irregularities of the surface and is aesthetically excellent and has high strength. However, There is a problem that the cost is higher.
세 번째로는 시공두께가 3.0~5.0mm로 마감되는 레진몰탈로서 에폭시, 우레탄 등의 수지에 0.4~1.5㎜의 규사를 적정비율로 혼합한 후 기계로 미장하여 마감한다. 상기의 도료 제품 중에서 강도가 가장 높기 때문에 중장비공장이나 화물터미널 등과 같이 중차량의 이동이 빈번한 곳에 사용되고 있지만, 비용이 가장 높은 단점이 있다. The third is a resin mortar with a construction thickness of 3.0 ~ 5.0mm. The resin is mixed with 0.4 ~ 1.5mm of silica with epoxy resin and urethane resin. Since the paint has the highest strength among the above paint products, it is used in places where heavy vehicles move frequently, such as a heavy equipment factory or a cargo terminal, but it has the highest disadvantage.
상기와 같은 도료 제품 중에서 강도가 우수하고 내구성이 높은 에폭시계가 가장 널리 사용되고 있지만, 시멘트ㆍ콘크리트 바닥면과의 부착력이 좋지않기 때문에 탈락하는 경우가 빈번하게 발생하게 된다. 이 경우 탈락부위를 제거하고 보수공사를 하지만, 기존의 도막과 이색이 나타나기 때문에 미관이 불량해지는 문제점이 있다.Among the above painted products, an epoxy system having high strength and high durability is most widely used. However, since the adhesive strength to the cement / concrete floor is not good, the epoxy system often falls off. In this case, the removed part is removed and the repair work is performed.
따라서 시멘트ㆍ콘크리트에 에폭시계 도료의 부착력을 높이기 위하여 블랜드방법과 졸-겔법을 이용한 하이브리드화 기술이 소개되고 있다.Therefore, hybridization techniques using a blend method and a sol - gel method have been introduced to improve the adhesion of epoxy coatings to cement and concrete.
우선, 블랜드방법으로 Norman R. Mowrer 등이 발표한 US Patent 5,618,860 “Polysiloxane coating and Flooring Compositions”에는 비스페놀-A 타입의 에폭시수지와 알콕시기를 갖는 폴리실록산(무기고분자)를 블랜딩한 주제와, 2관능형 아민 변성 실란커플링제와 용매를 혼합한 경화제로 구성하였다. 이 코팅제는 기존 에폭시수지보다 내후성, 내약품성 등이 우수하고 제조방법이 매우 간단하지만, 에폭시수지와 폴리실록산의 완벽한 혼합에 문제점이 발생하여 도막이 혼탁해지는 문제점이 있다. First, US Patent 5,618,860 " Polysiloxane coating and Flooring Compositions ", published by Norman R. Mowrer et al., By blending method, includes a blend of bisphenol-A type epoxy resin and polysiloxane (alkenylpolysiloxane) And a curing agent in which a modified silane coupling agent and a solvent were mixed. This coating is superior to the conventional epoxy resin in weatherability, chemical resistance, etc., and the manufacturing method is very simple. However, there is a problem in that the epoxy resin and the polysiloxane are mixed perfectly, resulting in a haze of the coating film.
다음으로, 졸-겝법은 에폭시수지와 부분가수분해된 실란 모노머 및 실란커플링제를 혼합하고, 70~80℃에서 반응시켜 분자단위로 에폭시수지 사슬에 무기입자를 결합시켜 유ㆍ무기 하이브리드 코팅제를 제조하는 방법이다. M. Ochi 등은 “structure and mechanical and adhesion properties ofepoxy/silica hybrids”42 (2001) 5151~5158)에서 비스페놀-A계 에폭시 수지와 에폭시 변성 실란커플링제 혹은 테트라메틸오르소실리케이트(TMOS)를 사용하여 졸-겔법으로 유ㆍ무기 하이브리드 코팅제를 개발하여 부착강도, 내마모성이 크게 향상된 결과를 얻었지만, 가열경화를 해야 하기 문제점이 있어 건축용으로 실용적이지 못한 문제점이 있다.Next, the sol-gel process is a process in which an epoxy resin, a partially hydrolyzed silane monomer and a silane coupling agent are mixed and reacted at 70 to 80 ° C. to bind inorganic particles to an epoxy resin chain in a molecular unit to produce an organic / inorganic hybrid coating agent . M. Ochi et al. Have reported that by using a bisphenol-A epoxy resin and an epoxy-modified silane coupling agent or tetramethyl orthosilicate (TMOS) in " structure and mechanical and adhesion properties of epoxy / silica hybrids " 42 (2001) 5151-5158 Sol-gel hybrid coatings have been developed to improve adhesion strength and abrasion resistance. However, there is a problem in that it requires heat curing, which is not practical for construction.
한편, 상온에서 경화가 가능하도록 한국등록특허공보 제10-1081431호 "유무기 하이브리드 하드 코팅제의 제조방법"과 한국등록특허공보 제10-0970461호 "유무기 하이브리드 방식 코팅제 조성물 밑 그 제조방법" 한국등록특허공보 제10-0956752호 "상온 경화형 유-무기 하이브리드 코팅제", 한국등록특허공보 제10-1463860호 "2액형 유ㆍ무기 하이브리드 코팅제 및 이를 제조하는 방법"등 다양한 선행기술이 개시되어 있으나, 도막의 두께가 0.1~0.3mm인 박막형이기 때문에 소지면을 완벽하게 보호하지 못하는 한계점을 노출하고 있다. On the other hand, Korean Patent Registration No. 10-1081431 entitled " Method for producing an organic hybrid hard coating agent "and Korean Patent Registration No. 10-0970461 for " A variety of prior arts have been disclosed, such as "a room temperature curing type organic-inorganic hybrid coating agent", a Korean Patent Registration No. 10-1463860 "a two-component type organic-inorganic hybrid coating agent and a method of manufacturing the same" Since the thickness of the film is 0.1 to 0.3 mm, it exposes the limitation of not fully protecting the surface.
현재까지 졸-겝법은 기존의 에폭시 및 우레탄계 바닥재보다 내마모성 및 난연성이 우수하고, 부착성이 높으며, 방수성, 내산 및 내알칼리성, 내오염성 등이 우수하기는 하나, 용매 함량이 높기 때문에 1회 도장으로 0.5~3.0mm의 후막형 도막을 제조하는 경우 수축에 의해 균열이 발생하는 문제점이 있다.Until now, the sol-gel process has superior abrasion resistance and flame retardancy than conventional epoxy and urethane flooring materials, has high adhesiveness, and is excellent in water resistance, acid resistance, alkali resistance and stain resistance. However, since the solvent content is high, When a thick film having a thickness of 0.5 to 3.0 mm is produced, cracks are generated due to shrinkage.
상기한 배경기술로서 설명된 사항들은 본 발명의 배경에 대한 이해 증진을 위한 것일 뿐, 이 기술분야에서 통상의 지식을 가진 자에게 이미 알려진 종래기술에 해당함을 인정하는 것으로 받아들여져서는 안 될 것이다.It should be understood that the foregoing description of the background art is merely for the purpose of promoting an understanding of the background of the present invention and is not to be construed as adhering to the prior art already known to those skilled in the art.
이에 본 발명은 상기와 같은 문제점을 해결하기 위한 것으로, 외관과 기능이 우수하면서도 경제성을 향상시킬 수 있도록, 0.5~3.0mm 도막두께로 시공 가능한 유ㆍ무기 하이브리드 바닥마감용 도료 조성물과 이를 이용한 시공방법을 제공하고자 하는 것이다.Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a coating composition for organic / inorganic hybrid flooring which can be applied with a coating thickness of 0.5 to 3.0 mm so as to improve the appearance and function, .
상기 목적을 달성하기 위한 본 발명은 주제부와 경화제부로 이루어지는 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 있어서, 상기 주제부는 에폭시당량 180~220 g/eq의 비스페놀 A형 또는 비스페놀 F형의 액상 에폭시수지 60~80 중량부; 에폭시 실란(Glycideoxypropyltrimethoxysilane, 이하 GPTMS로 표기) 10~25 중량부; 반응성 촉매로 DBTDL(dibutyl tin dilaurate, 이하 DBTDL로 표기) 0.1~0.5 중량부; 질산, 염산 중에서 선택되는 1종 이상의 무기산 0.1~0.5 중량부; BGE(butyl glycidyl ether), LGE(aliphatic glycidyl ether (C12~C14)), EHGE(2-ethylhexyl glycidyl ether), PGE(phenyl gylcidyl ether), CGE(0-cresol glycidyl ether), 1,4BDDGE(1,4-butandiol diglycidyl ether) 중에서 선택되는 1종 이상의 반응성 희석제 5~20 중량부; 비반응성 희석제로서 벤질알콜 1~3 중량부; 소포제, 분산제, 레벨링제 중에서 선택되는 1종 이상의 첨가제 0.5~3.0 중량부를 포함하여 이루어지고, 상기 경화제부는 투명성과 강도가 높게 발현될 수 있는 TAV(total amine value)가 220~400 범위의 변성 지환족 아민 80~90 중량부, 벤질 알콜, 도데실 페놀(dodecyl phenol) 중에서 선택되는 1종 이상의 비반응성 희석제 10~20 중량부를 포함하여 이루어지는 것을 특징으로 하는 유ㆍ무기 하이브리드 바닥마감용 도료 조성물을 제공한다.In order to accomplish the above object, the present invention provides a coating composition for organic / inorganic hybrid flooring comprising a main part and a curing agent part, wherein the main part is a bisphenol A or bisphenol F type liquid epoxy resin having an epoxy equivalent of 180 to 220 g / eq 60 to 80 parts by weight; 10-25 parts by weight of epoxy silane (Glycideoxypropyltrimethoxysilane, hereinafter referred to as GPTMS); 0.1 to 0.5 parts by weight of DBTDL (dibutyltin dilaurate, hereinafter referred to as DBTDL) as a reactive catalyst; 0.1 to 0.5 parts by weight of at least one inorganic acid selected from nitric acid and hydrochloric acid; BGE (butyl glycidyl ether), LGE (aliphatic glycidyl ether (C12-C14)), EHGE (2-ethylhexyl glycidyl ether), PGE (phenylglycidyl ether), CGE (0- 5 to 20 parts by weight of at least one reactive diluent selected from 4-butanediol diglycidyl ether; 1 to 3 parts by weight of benzyl alcohol as a non-reactive diluent; 0.5 to 3.0 parts by weight of at least one additive selected from the group consisting of an antifoaming agent, a dispersing agent and a leveling agent. The curing agent part has a total amine value (TAV) of 220 to 400, And 80 to 90 parts by weight of an amine, 10 to 20 parts by weight of at least one non-reactive diluent selected from benzyl alcohol and dodecyl phenol, and a coating composition for organic / inorganic hybrid floor finishing .
본 발명에 있어서 바람직하게는 상기 조성물은 0.5~3.0mm의 도막 두께로 바닥마감 시공이 가능한 것을 특징으로 한다.In the present invention, it is preferable that the composition is capable of performing floor finish with a film thickness of 0.5 to 3.0 mm.
또한 본 발명은 소지면을 전처리하는 단계; 상기의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물의 주제부와 경화제를 중량비로 2~3 : 1로 혼합하는 단계; 혼합 조성물을 에어리스 스프레이(Airless Spray) 방법으로 바닥면에 도포하여 도막을 형성하는 단계를 포함하는 바닥마감재의 시공방법을 제공한다. 본 발명에 있어서 바람직하게는 상기 형성된 도막의 두께는 0.5~3.0mm인 것을 특징으로 한다.The present invention also provides a method of manufacturing a semiconductor device, Mixing the main portion and the curing agent of the organic / inorganic hybrid floor coating composition at a weight ratio of 2 to 3: 1; And applying the mixed composition to a floor surface by an airless spray method to form a coated film. In the present invention, preferably, the thickness of the formed coating film is 0.5 to 3.0 mm.
상술한 바와 같은 본 발명의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물은 그 도료성분 배합에 의하여 에폭시 실란은 경화과정에서 에폭시기는 에폭시수지와 반응하고, 알콕시기는 시멘트ㆍ콘크리트 표면과 반응하여 부착력이 크게 향상되어 시멘트ㆍ콘크리트 표면을 보호하게 된다.As described above, the coating composition for organic / inorganic hybrid flooring of the present invention is characterized in that the epoxy silane reacts with the epoxy resin in the curing process, and the alkoxy group reacts with the cement-concrete surface, Thereby protecting the cement / concrete surface.
또한 본 발명의 시공방법은 내구성, 내충격성, 부착강도, 내약품성, 내마모성 등의 물성이 양호하게 향상시킨 효과가 있다.Further, the construction method of the present invention has the effect of satisfactorily improving physical properties such as durability, impact resistance, adhesion strength, chemical resistance, and abrasion resistance.
본 명세서 및 청구 범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 안 되며, 발명자는 그 자신의 발명의 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms and words used in the present specification and claims should not be construed as limited to ordinary or preliminary meaning and the inventor may properly define the concept of a term to describe it in its best mode of its own invention It should be construed as meaning and concept consistent with the technical idea of the present invention.
따라서 본 명세서에 기재된 실험 예, 참조 예 및 도면에 기술된 사항은 본 발명의 가장 바람직한 일 예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들은 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.Therefore, it should be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined in the appended claims. It should be understood that various equivalents and modifications may be present.
실시예Example 1. 유1. Yu ㆍ무기 ㆍ Weapons 하이브리드hybrid 바닥마감용 도료 조성물의 제조 Preparation of coating compositions for floor finishes
(1) 유ㆍ무기 (1) Weapons and weapons 하이브리드hybrid 바닥마감용 도료 조성물의 구성 Composition of coating composition for floor finish
이하 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명은 주제부와 경화제부로 이루어지는 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 관한 것으로, 비스페놀 A형 또는 비스페놀 F형 액상 에폭시수지와 GPTMS, DBTDL, 무기산, 반응성 희석제와 비반응성 희석제 및 첨가제를 포함하여 이루어지는 주제부와, 변성 지환족 아민과 비반응성 희석제를 포함하여 이루어지는 경화제부로 이루어지는 0.5~3.0mm 두께로 시공이 가능한 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 관한 것이다.The present invention relates to a coating composition for organic / inorganic hybrid flooring comprising a main part and a curing agent part, which comprises a bisphenol A type or bisphenol F type liquid epoxy resin and GPTMS, DBTDL, inorganic acid, a reactive diluent and a nonreactive diluent, And a curing agent part comprising a modified alicyclic amine and a non-reactive diluent. The present invention relates to a coating composition for organic / inorganic hybrid flooring which can be applied in a thickness of 0.5 to 3.0 mm.
(2) (2) 주제부의Subject matter 중량 조성 Weight composition
본 발명에 있어서 상기 주제부는 에폭시당량 180~220 g/eq의 비스페놀 A형 또는 비스페놀 F형의 액상 에폭시수지 60~80 중량부; 에폭시 실란(Glycideoxypropyltrimethoxysilane, 이하 GPTMS로 표기) 10~25 중량부; 반응성 촉매로 DBTDL(dibutyl tin dilaurate, 이하 DBTDL로 표기) 0.1~0.5 중량부; 질산, 염산 중에서 선택되는 1종 이상의 무기산 0.1~0.5 중량부; BGE(butyl glycidyl ether), LGE(aliphatic glycidyl ether (C12~C14)), EHGE(2-ethylhexyl glycidyl ether), PGE(phenyl gylcidyl ether), CGE(0-cresol glycidyl ether), 1,4BDDGE(1,4-butandiol diglycidyl ether) 중에서 선택되는 1종 이상의 반응성 희석제 5~20 중량부; 비반응성 희석제로서 벤질알콜 1~3 중량부; 소포제, 분산제, 레벨링제 중에서 선택되는 1종 이상의 첨가제 0.5~3.0 중량부를 포함하여 이루어진다.In the present invention, the main portion may comprise 60 to 80 parts by weight of a bisphenol A or bisphenol F liquid epoxy resin having an epoxy equivalent of 180 to 220 g / eq; 10-25 parts by weight of epoxy silane (Glycideoxypropyltrimethoxysilane, hereinafter referred to as GPTMS); 0.1 to 0.5 parts by weight of DBTDL (dibutyltin dilaurate, hereinafter referred to as DBTDL) as a reactive catalyst; 0.1 to 0.5 parts by weight of at least one inorganic acid selected from nitric acid and hydrochloric acid; BGE (butyl glycidyl ether), LGE (aliphatic glycidyl ether (C12-C14)), EHGE (2-ethylhexyl glycidyl ether), PGE (phenylglycidyl ether), CGE (0- 5 to 20 parts by weight of at least one reactive diluent selected from 4-butanediol diglycidyl ether; 1 to 3 parts by weight of benzyl alcohol as a non-reactive diluent; 0.5-3.0 parts by weight of at least one additive selected from the group consisting of an antifoaming agent, a dispersing agent and a leveling agent.
상기에서 에폭시수지는 도막을 형성하는 주성분으로서 에폭시당량 170~230 g/eq의 비스페놀 A형 또는 비스페놀 F형 액상 에폭시수지 60~80 중량부로 함유되고, 에폭시수지의 함량이 80 중량부보다 많으면 제품의 점도가 높아 균일한 혼합이 힘들고, 60 중량부보다 낮으면 도막을 형성하는 주성분의 함량이 적어 도막형성이 불량해진다. 이러한 액상 에폭시 수지의 구체적인 예로는 YD-114, YD-115, YD-117, YD-119, YD-128, YD-129, YDF-162, YDF-165, YDF-170 등이 있으며 이에 한정하는 것은 아니다. The epoxy resin is contained in an amount of 60 to 80 parts by weight of bisphenol A type or bisphenol F type liquid epoxy resin having an epoxy equivalent of 170 to 230 g / eq as a main component forming the coating film. When the content of the epoxy resin is more than 80 parts by weight, If the amount is less than 60 parts by weight, the content of the main component forming the coating film is small and the coating film formation becomes poor. Specific examples of such a liquid epoxy resin include YD-114, YD-115, YD-117, YD-119, YD-128, YD-129, YDF-162, YDF-165 and YDF- no.
상기 GPTMS는 에폭시수지와 시멘트ㆍ콘크리트 표면을 화학결합시켜 부착강도를 높여주는 커플링제로 10~25 중량부로 함유되고, GPTMS의 함량이 25 중량부보다 많으면 제품의 가격이 너무 높아지고, 부착강도의 개선효과가 더 이상 증가하지 않고, 10 중량부보다 낮으면 부착강도 개선효과가 미비하다. The GPTMS is contained in an amount of 10 to 25 parts by weight as a coupling agent for increasing the bonding strength by chemically bonding the epoxy resin to the cement / concrete surface. If the GPTMS content is more than 25 parts by weight, the product becomes too expensive, The effect is not further increased, and if it is lower than 10 parts by weight, the effect of improving the adhesion strength is insufficient.
상기 DBTDL 및 무기산은 GPTMS의 알콕시기의 반응성을 높여 시멘트ㆍ콘크리트 표면과 반응속도를 향상시키기 위해 각각 0.1~0.5 중량부를 함유한다. 각각 0.5 중량부보다 많아도 반응속도가 더 이상 향상하지 않고, 0.1 중량부보다 낮으면 반응속도를 향상시키는 효과가 미비하다.The DBTDL and the inorganic acid each contain 0.1 to 0.5 parts by weight in order to increase the reactivity of the alkoxy group of GPTMS and improve the cement-concrete surface and the reaction rate. If the amount is more than 0.5 part by weight, the reaction rate is not improved any more, and if it is less than 0.1 part by weight, the effect of improving the reaction rate is insufficient.
상기 반응성 희석제는 에폭시수지의 점도를 낮추면서 경화도막의 경도를 높이기 위해서 첨가하며, 5~20 중량부 범위 내에서 사용한다. 반응성 희석제가 20 중량부를 초과하여 사용되면 도막물성이 오히려 저하하며, 반응성 희석제가 5 중량부 미만으로 사용되면 점도를 낮추는 효과가 미비하여 시공시 작업성이 좋지 않게 된다. 반응성 희석제의 구체적인 예로는 BGE(butyl glycidyl ether), LGE(aliphatic glycidyl ether (C12~C14)), EHGE(2-ethylhexyl glycidyl ether), PGE(phenyl gylcidyl ether), CGE(0-cresol glycidyl ether), 1,4BDDGE(1,4-butandiol diglycidyl ether) 등이 있으며 이에 한정하는 것은 아니다.The reactive diluent is added to increase the hardness of the cured coating film while lowering the viscosity of the epoxy resin, and is used within a range of 5 to 20 parts by weight. If the reactive diluent is used in an amount exceeding 20 parts by weight, the physical properties of the coating film are lowered. If the reactive diluent is used in an amount of less than 5 parts by weight, the effect of lowering the viscosity is insufficient. Specific examples of the reactive diluent include BGE (butyl glycidyl ether), LGE (aliphatic glycidyl ether (C12 to C14)), EHGE (2-ethylhexyl glycidyl ether), PGE (phenylglycidyl ether), CGE 1,4-butanediol diglycidyl ether, and the like.
상기 비반응성 희석제는 벤질알콜을 1~3 중량부 범위 내에서 사용하는 것이 바람직하다. 사용량이 3.0 중량부를 초과하면 도료 점도가 묽어져 저장성이 나빠지고, 사용량이 1.0 중량부 미만이면 점도가 높아 작업성이 나빠지게 된다.It is preferable that the non-reactive diluent is used in an amount of 1 to 3 parts by weight of benzyl alcohol. If the amount is more than 3.0 parts by weight, the viscosity of the coating becomes poor and the storage property is deteriorated. If the amount is less than 1.0 part by weight, the viscosity is high and the workability is deteriorated.
상기 첨가제는 소포제, 분산제, 레벨링제 중에서 1종 이상 선택하여 0.5~3.0 중량부 만큼 사용하는데, 1 중량부 보다 적으면 사용량이 미비하여 각각의 제 기능을 발휘하지 못하고 3.0 중량부보다 많으면 과량을 사용하게 되므로 화학적 성능이 저하된다.When the amount of the additive is less than 1 part by weight, the amount of the additive is insufficient to exert the respective functions. When the amount of the additive is more than 3.0 parts by weight, an excess amount of the additive is used The chemical performance is degraded.
(3) (3) 경화제부의Hardener 중량 조성 Weight composition
또한 본 발명에 있어서 상기 경화제부는 투명성과 강도가 높게 발현될 수 있는 TAV(total amine value)가 220~400 범위의 변성 지환족 아민 80~90 중량부, 벤질 알콜, 도데실 페놀(dodecyl phenol) 중에서 선택되는 1종 이상의 비반응성 희석제 10~20 중량부를 포함하여 이루어지는 것을 특징으로 한다.Also, in the present invention, the curing agent may include 80 to 90 parts by weight of a modified alicyclic amine having a total amine value (TAV) in the range of 220 to 400, which can be expressed with high transparency and strength, benzyl alcohol, dodecylphenol And 10 to 20 parts by weight of at least one kind of non-reactive diluent selected from the group consisting of
상기 변성지환족 아민은 80~90 중량부를 사용한다. 사용량이 적거나 많으면 에폭시수지의 경화가 불량하여 도막경도가 약하고 내화학성 등이 나빠진다. 상기 변성지환족 아민의 구체적인 예로는 국도화학의 KH-816, KH-819, KH-825 및 KH-831 등이 있다.The modified aliphatic amine is used in an amount of 80 to 90 parts by weight. If the amount is small or large, hardening of the epoxy resin is poor, resulting in poor film hardness and poor chemical resistance. Specific examples of the above-mentioned denatured aliphatic amines include KH-816, KH-819, KH-825 and KH-831 of Kukdo Chemical.
상기 경화제부에 포함되는 비반응성 희석제는 벤질알콜, 도데실 페놀을 1종 이상 선택하여 10~20 중량부를 사용한다. 이것들은 하이드록시기(-OH)를 함유하고 있는데 이는 에폭시 반응의 촉매역할을 하여 경화시간을 단축시키는 역할을 하므로 사용량을 적절히 조절하여야 하며, 사용량이 적으면 경화제의 점도가 높아 작업성이 나빠지고 사용량이 많으면 점도가 묽고 경화도막의 경도가 약해지는 경향이 있다.The non-reactive diluent contained in the curing agent may be at least one selected from the group consisting of benzyl alcohol and dodecyl phenol and 10 to 20 parts by weight. They contain a hydroxyl group (-OH), which serves as a catalyst for the epoxy reaction and shortens the curing time. Therefore, the amount to be used should be appropriately controlled. If the amount is small, the viscosity of the curing agent is high, If the amount is large, the viscosity tends to be low and the hardness of the cured coating film tends to be weak.
또한 본 발명의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 있어서, 상기 주제부와 경화제부는 2~3:1의 중량비로 혼합되는 것을 특징으로 한다. 본 발명의 일 실시예에서는 2.5:1의 중량비로 혼합하여 시공하였다.In the coating composition for organic / inorganic hybrid flooring of the present invention, the main portion and the curing agent portion are mixed at a weight ratio of 2 to 3: 1. In one embodiment of the present invention, the mixture was mixed at a weight ratio of 2.5: 1.
또한 본 발명의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물에 있어서, 상기 조성물은 0.5~3.0mm의 도막 두께로 바닥마감 시공이 가능한 것을 특징으로 한다.In the coating composition for organic / inorganic hybrid flooring of the present invention, the composition may be applied to a floor finish with a film thickness of 0.5 to 3.0 mm.
본 발명의 다른 양태로서, 본 발명은 소지면을 전처리하는 단계; 상기의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물의 주제부와 경화제를 중량비로 2~3 : 1로 혼합하는 단계; 혼합 조성물을 에어리스 스프레이(Airless Spray) 방법으로 바닥면에 도포하여 도막을 형성하는 단계를 포함하는 바닥마감재의 시공방법을 제공한다. 본 발명에 있어서 바람직하게는 상기 형성된 도막의 두께는 0.5~3.0mm인 것을 특징으로 한다.According to another aspect of the present invention, Mixing the main portion and the curing agent of the organic / inorganic hybrid floor coating composition at a weight ratio of 2 to 3: 1; And applying the mixed composition to a floor surface by an airless spray method to form a coated film. In the present invention, preferably, the thickness of the formed coating film is 0.5 to 3.0 mm.
이하 실시예에서 본 발명을 더욱 구체적으로 설명하는데 이는 본 발명의 보호범위를 한정하거나 제한하고자 하는 것이 아니며, 또한 해당분야에서 통상적인 지식을 가진 사람이라면 본 발명의 기술적 범위 내에서 다양한 다른 형태로 구현할 수 있을 것이다.The present invention will now be described more specifically with reference to the following examples, which should not be construed as limiting or limiting the scope of protection of the present invention. Those skilled in the art will appreciate that various modifications, additions and substitutions are possible, It will be possible.
실험예Experimental Example 1. 유ㆍ무기 1. Weapons and weapons 하이브리드hybrid 바닥마감용 도료 조성물의 물성시험 Physical Properties Test of Coating Composition for Floor Finishing
(1) 실험시료 준비(1) Preparation of test samples
하기 표 1에 나타낸 배합비(중량부)로 각각의 원료를 순서대로 넣으면서 교반하여 균일액상을 제조한 후 경화비율을 중량비 2.5:1로 혼합하여 유ㆍ무기 하이브리드 바닥마감용 도료 조성물을 제조하였다.The respective raw materials were added in the order of the mixing ratios (parts by weight) shown in Table 1 in order and stirred to prepare a homogeneous liquid phase, and then the curing ratio was mixed at a weight ratio of 2.5: 1 to prepare a coating composition for organic / inorganic hybrid floor finish.
(주제부:경화제부)Curing ratio [weight ratio]
(Main part: hardener part)
(2) 실험방법(2) Experimental method
상기의 표 1의 배합비에 따른 시료 1~3에 의하여 제조되는 도료 조성물에 대하여 물성시험을 진행하였다.The physical properties of the coating compositions prepared by Samples 1 to 3 according to the compounding ratios in Table 1 were tested.
먼저, 저장안정성은, 주제 제조 후 6개월간 실온에서 방치한 다음 굳어 있는지의 여부를 확인하여 시험하였다.First, the storage stability was evaluated by confirming whether or not it was hardened after standing at room temperature for 6 months after the production of the subject matter.
지촉건조시간은 손가락 끝에 도막을 가볍게 대었을 때 손가락에 묻어나지 않을 때의 시간을 측정하였으며, 경화건조시간은 도막에 엄지손가락을 90도로 힘껏 눌러 비틀어도 도막에 이상이 없을 때의 시간을 측정하였다.The drying time of the fingertip was measured when the fingertip was lightly put on the fingertip and the time when the fingertip was not finged was measured. The time of the hardening drying time was measured when the fingertip was twisted with the thumb at 90 degrees.
한편 대한주택공사 전문시방서 및 KS 규격에 의하여 도막의 물성을 시험하였다.On the other hand, the physical properties of the coating film were tested according to the KSH specification and the KS standard.
(3) 실험결과(3) Experimental results
상기와 같은 시험방법에 의한 물성시험결과를 하기 표 2에 나타내었다.The results of the physical properties test by the above test method are shown in Table 2 below.
(주제, 6개월)Storage stability
(Subject, 6 months)
전문시방서Korea National Housing Corp.
Professional Specification
전문시방서Korea National Housing Corp.
Professional Specification
전문시방서Korea National Housing Corp.
Professional Specification
전문시방서Korea National Housing Corp.
Professional Specification
2812-1KS M ISO
2812-1
(72시간)Salt spray test
(72 hours)
상기 표 2에서 확인할 수 있는 바와 같이 시료 1 내지 3은 시험했던 모든 항목에서 양호한 결과를 나타냈고, 대한주택공사 전문시방서 및 KS 규격 시험에서도 양호한 결과를 나타내었다.As can be seen from Table 2, Samples 1 to 3 showed satisfactory results in all the items tested, and good results were also shown in the Korea National Housing Corporation Specification and the KS Standards Test.
따라서 본 발명의 유ㆍ무기 하이브리드 바닥마감용 도료 조성물은 0.5~3.0mm 두께로의 시공이 가능하며 이를 이용한 시공방법으로 건축용 바닥재로 적용함에 있어서 외관이 우수한 것으로 판단되었다.Accordingly, the organic / inorganic hybrid floor coating composition of the present invention can be applied to a thickness of 0.5 to 3.0 mm, and it is judged that the coating composition is excellent in appearance when applied as a flooring for construction.
본 발명은 특정한 실시 예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 제공되는 본 발명의 기술적 사상을 벗어나지 않는 한도 내에서, 본 발명이 다양하게 개량 및 변화될 수 있다는 것은 당 업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.While the present invention has been particularly shown and described with reference to specific embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the following claims It will be apparent to those of ordinary skill in the art.
Claims (5)
주제부와 경화제부를 포함하도록 구성되며,
상기 주제부는 에폭시당량 170~230 g/eq 의 비스페놀 A형 또는 비스페놀 F형 액상 에폭시수지 60~80 중량부;
커플링제로 사용되는 에폭시 실란(Glycideoxypropyltrimethoxysilane) 10~25 중량부;
반응성 촉매로 사용되는 DBTDL(dibutyl tin dilaurate) 0.1~0.5 중량부;
질산, 염산 중에서 선택되는 1종 이상의 무기산 0.1~0.5 중량부;
BGE(butyl glycidyl ether), LGE(aliphatic glycidyl ether (C12~C14)), EHGE(2-ethylhexyl glycidyl ether), PGE(phenyl gylcidyl ether), CGE(0-cresol glycidyl ether), 1,4BDDGE(1,4-butandiol diglycidyl ether) 중에서 선택되는 1종 이상의 반응성 희석제 5~20 중량부;
비반응성 희석제로 사용되는 벤질알콜 1~3 중량부;
소포제, 분산제, 레벨링제 중에서 선택되는 1종 이상의 첨가제 0.5~3.0 중량부를 포함하여 이루어지고,
상기 경화제부는 TAV(total amine value)가 220~400 범위의 변성 지환족 아민 80~90 중량부;
벤질 알콜, 도데실 페놀(dodecyl phenol) 중에서 선택되는 1종 이상의 비반응성 희석제 10~20 중량부를 포함하여 이루어지고,
상기 주제부와 경화제부는 접착강도 개선, 투명성과 강도 개선을 위해 2~3(주제부):1(경화제부)의 중량비로 혼합되고, 상기 주제부와 경화제부로 구성되는 조성물은 0.5~3.0mm의 도막 두께로 바닥마감 시공이 가능한 것을 특징으로 하는 유ㆍ무기 하이브리드 바닥마감용 도료 조성물.
A two-part organic / inorganic hybrid floor coating composition comprising a main portion and a hardener portion,
Comprising a main portion and a curing agent portion,
60 to 80 parts by weight of a bisphenol A type or bisphenol F type liquid epoxy resin having an epoxy equivalent of 170 to 230 g / eq;
10-25 parts by weight of epoxy silane (Glycideoxypropyltrimethoxysilane) used as a coupling agent;
0.1 to 0.5 parts by weight of DBTDL (dibutyltin dilaurate) used as a reactive catalyst;
0.1 to 0.5 parts by weight of at least one inorganic acid selected from nitric acid and hydrochloric acid;
BGE (butyl glycidyl ether), LGE (aliphatic glycidyl ether (C12-C14)), EHGE (2-ethylhexyl glycidyl ether), PGE (phenylglycidyl ether), CGE (0- 5 to 20 parts by weight of at least one reactive diluent selected from 4-butanediol diglycidyl ether;
1 to 3 parts by weight of benzyl alcohol used as a non-reactive diluent;
0.5 to 3.0 parts by weight of at least one additive selected from the group consisting of an antifoaming agent, a dispersing agent and a leveling agent,
Wherein the curing agent is 80 to 90 parts by weight of a modified alicyclic amine having a total amine value (TAV) in the range of 220 to 400;
10 to 20 parts by weight of at least one non-reactive diluent selected from benzyl alcohol, dodecyl phenol,
The topical portion and the curing agent portion are mixed at a weight ratio of 2 to 3 (subject portion): 1 (curing agent portion) for improving the bonding strength, transparency and strength, and the composition comprising the subject portion and the curing agent portion is 0.5 to 3.0 mm And a floor finish can be applied with a thickness of the coating layer.
주제부와 경화제부를 2~3(주제부):1(경화제부)의 중량비로 혼합하는 단계;
상기 주제부와 경화제부의 혼합 조성물을 에어리스 스프레이 방법으로 바닥면에 도포하여 0.5~3.0mm 두께의 도막을 형성하는 단계를 포함하며,
상기 주제부는 에폭시당량 170~230 g/eq 의 비스페놀 A형 또는 비스페놀 F형 액상 에폭시수지 60~80 중량부;
커플링제로 사용되는 에폭시 실란(Glycideoxypropyltrimethoxysilane) 10~25 중량부;
반응성 촉매로 사용되는 DBTDL(dibutyl tin dilaurate) 0.1~0.5 중량부;
질산, 염산 중에서 선택되는 1종 이상의 무기산 0.1~0.5 중량부;
BGE(butyl glycidyl ether), LGE(aliphatic glycidyl ether (C12~C14)), EHGE(2-ethylhexyl glycidyl ether), PGE(phenyl gylcidyl ether), CGE(0-cresol glycidyl ether), 1,4BDDGE(1,4-butandiol diglycidyl ether) 중에서 선택되는 1종 이상의 반응성 희석제 5~20 중량부;
비반응성 희석제로 사용되는 벤질알콜 1~3 중량부;
소포제, 분산제, 레벨링제 중에서 선택되는 1종 이상의 첨가제 0.5~3.0 중량부를 포함하여 이루어지고,
상기 경화제부는 TAV(total amine value)가 220~400 범위의 변성 지환족 아민 80~90 중량부;
벤질 알콜, 도데실 페놀(dodecyl phenol) 중에서 선택되는 1종 이상의 비반응성 희석제 10~20 중량부를 포함하여 이루어지는 것을 특징으로 하는 바닥마감재의 시공방법.Pretreating the substrate;
Mixing the main portion and the curing agent portion in a weight ratio of 2 to 3 (subject portion): 1 (curing agent portion);
Applying a mixed composition of the subject part and a curing agent part to a bottom surface by an airless spray method to form a coating film having a thickness of 0.5 to 3.0 mm,
60 to 80 parts by weight of a bisphenol A type or bisphenol F type liquid epoxy resin having an epoxy equivalent of 170 to 230 g / eq;
10-25 parts by weight of epoxy silane (Glycideoxypropyltrimethoxysilane) used as a coupling agent;
0.1 to 0.5 parts by weight of DBTDL (dibutyltin dilaurate) used as a reactive catalyst;
0.1 to 0.5 parts by weight of at least one inorganic acid selected from nitric acid and hydrochloric acid;
BGE (butyl glycidyl ether), LGE (aliphatic glycidyl ether (C12-C14)), EHGE (2-ethylhexyl glycidyl ether), PGE (phenylglycidyl ether), CGE (0- 5 to 20 parts by weight of at least one reactive diluent selected from 4-butanediol diglycidyl ether;
1 to 3 parts by weight of benzyl alcohol used as a non-reactive diluent;
0.5 to 3.0 parts by weight of at least one additive selected from the group consisting of an antifoaming agent, a dispersing agent and a leveling agent,
Wherein the curing agent is 80 to 90 parts by weight of a modified alicyclic amine having a total amine value (TAV) in the range of 220 to 400;
And 10 to 20 parts by weight of at least one non-reactive diluent selected from benzyl alcohol, dodecyl phenol, and the like.