KR101602649B1 - Manufacturing method of activated carbon for carbon dioxide adsorption - Google Patents

Manufacturing method of activated carbon for carbon dioxide adsorption Download PDF

Info

Publication number
KR101602649B1
KR101602649B1 KR1020130160938A KR20130160938A KR101602649B1 KR 101602649 B1 KR101602649 B1 KR 101602649B1 KR 1020130160938 A KR1020130160938 A KR 1020130160938A KR 20130160938 A KR20130160938 A KR 20130160938A KR 101602649 B1 KR101602649 B1 KR 101602649B1
Authority
KR
South Korea
Prior art keywords
activated carbon
carbon dioxide
metal
carbon
activated
Prior art date
Application number
KR1020130160938A
Other languages
Korean (ko)
Other versions
KR20150074236A (en
Inventor
박수진
이슬이
Original Assignee
인하대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 인하대학교 산학협력단 filed Critical 인하대학교 산학협력단
Priority to KR1020130160938A priority Critical patent/KR101602649B1/en
Publication of KR20150074236A publication Critical patent/KR20150074236A/en
Application granted granted Critical
Publication of KR101602649B1 publication Critical patent/KR101602649B1/en

Abstract

본 발명은 이산화탄소 흡착용 활성탄소의 제조방법에 관한 것으로서, 더욱 상세하게는 실내 대기 내의 이산화탄소를 저농도를 유지하기 위한 이산화탄소 흡착용 활성탄소를 제조하는 방법에 관한 것이다.
상기와 같은 본 발명에 따르면, 상용화된 활성탄소를 활성화제로 활성화하고 금속산화물을 담지시켜 고 나노기공, 고 비표면적을 갖는 이산화탄소 흡착용 활성탄소를 제조함으로써, 실내 이산화탄소를 효율적으로 제거하여 잠수함, 우주선, 철도, 차 등의 실내 이산화탄소를 저농도로 유지하는 효과가 있다.The present invention relates to a method for producing activated carbon for adsorbing carbon dioxide, and more particularly, to a method for producing activated carbon for adsorbing carbon dioxide for maintaining a low concentration of carbon dioxide in an indoor air.
According to the present invention as described above, activated carbon is activated as an activator and metal oxide is supported to produce activated carbon for adsorbing carbon dioxide having high nano pore and high specific surface area, thereby efficiently removing indoor carbon dioxide, , Railway, car, etc., at low concentration.

Description

이산화탄소 흡착용 활성탄소의 제조방법{MANUFACTURING METHOD OF ACTIVATED CARBON FOR CARBON DIOXIDE ADSORPTION}TECHNICAL FIELD [0001] The present invention relates to a method for producing activated carbon for carbon dioxide adsorption,

본 발명은 이산화탄소 흡착용 활성탄소의 제조방법에 관한 것으로서, 더욱 상세하게는 실내 대기 내의 이산화탄소를 저농도를 유지하기 위한 이산화탄소 흡착용 활성탄소를 제조하는 방법에 관한 것이다.The present invention relates to a method for producing activated carbon for adsorbing carbon dioxide, and more particularly, to a method for producing activated carbon for adsorbing carbon dioxide for maintaining a low concentration of carbon dioxide in an indoor air.

기존에는 실내 공간의 미세먼지를 공기의 오염물질로 분류하여 이를 정화하였으나, 최근에는 이산화탄소에 대한 관심이 급증하고 있다. 또한, 차량의 주행 중에는 기압 차이로 형성된 공기의 흐름에 의해 차량 내부의 공기가 자연스럽게 외부로 배출되도록 되어 있으나, 저속 주행시나 주정차시에는 환기가 되지 못하는 문제가 발생하여 차 실내의 이산화탄소 양은 증가하게 된다. 차의 창문으로 환기를 시킴으로써 이산화탄소 양을 감소시킬 수 있지만, 차 실내에 사람이 증가할 경우 이산화탄소 양이 급격히 증가하기 때문에 환기 용량에 맞출 수가 없고, 이를 방지하기 위해 차 실내에 환기를 자주시킬 경우 겨울과 여름철에 에너지 소비량이 급격하게 증가할 수 있다. In the past, fine dusts of indoor space were classified as air pollutants and purified, but recently, interest in carbon dioxide has been increasing rapidly. Also, while the vehicle is traveling, the air inside the vehicle is naturally discharged to the outside by the flow of air formed by the air pressure difference, but the problem of not being ventilated at the time of low-speed driving or driving is increased, and the amount of carbon dioxide in the car interior is increased . Although the amount of carbon dioxide can be reduced by ventilation through the window of the car, the amount of carbon dioxide increases rapidly when the number of people in the room increases. Therefore, And the energy consumption in the summer can increase sharply.

이산화탄소는 0.03~0.04 %의 소량이 대기 중에 포함되어 있으며 일반적으로 인체의 건강에 큰 영향을 미치지 않는다. 그러나, 이산화탄소의 농도가 증가하게 되면 차 실내 공간에서 호흡에 필요한 산소의 양이 감소하게 되어 이산화탄소 농도가 1000~2000 ppm인 경우 인체는 답답함을 느끼며 2000 ppm 이상에서는 졸음을 유발시켜 차량 사고로 이어질 수 있어 이산화탄소 농도 제어는 중요한 기술로 평가받고 있다. Carbon dioxide is contained in the air in a small amount of 0.03-0.04% and does not generally affect the health of the human body. However, when the concentration of carbon dioxide increases, the amount of oxygen required for respiration in the car interior space decreases. If the concentration of carbon dioxide is in the range of 1000 to 2000 ppm, the human body may feel frustrated. The control of carbon dioxide concentration is regarded as an important technology.

실내 이산화탄소의 양을 제거하는 방법으로 최근 흡착법에 관한 연구가 활발히 이루어지고 있으며, 관련 선행기술로 한국 공개특허 10-2013-0070405(이산화탄소 흡탈착 장치 및 그 방법) 등이 있다. 흡착법은 에너지 소비가 적고 회수를 다시 할 수 있어 경제적인 저감기술로서 응용이 간편하다는 장점을 가지고 있다. 또한, 낮은 농도와 낮은 온도에서 적용이 가능하며 낮은 에너지 비용으로 저농도의 실내 이산화탄소 제어가 가능하다. Recently, studies on adsorption methods have been actively conducted as methods for removing the amount of indoor carbon dioxide. Korean Prior Art 10-2013-0070405 (Carbon dioxide adsorption / desorption device and its method) is a related prior art. The adsorption method is advantageous in that it is easy to apply as an economical abatement technique because it can reduce the energy consumption and recollect. In addition, it can be applied at low and low temperatures, and low-energy indoor carbon dioxide control at low concentrations is possible.

현재까지 개발된 흡착제로는 MOF(Metal Organic Framework), 제올라이트, 활성탄소, 금속산화물, 실리카겔, 활성알루미나 등이 있다. 이산화탄소 흡착제 중 하나인 활성탄소는 기공 구조가 주로 미세기공으로 이루어져 있으며 흡착 표면적이 넓어 흡착 용량이 크고 가격이 저렴할 뿐만 아니라 사용이 간편하여 유용한 소재로 사용되고 있다. 하지만 순수한 활성탄으로는 이산화탄소에 대한 선택적 흡착 성능이 낮은 단점이 있어 흡착 성능의 개선을 위하여 표면개질에 대한 연구가 진행되고 있으며 이산화탄소의 선택적 흡착능의 개선 및 향상이 필요한 실정이다.The adsorbent developed to date includes MOF (Metal Organic Framework), zeolite, activated carbon, metal oxide, silica gel, and activated alumina. Activated carbon, which is one of the carbon dioxide adsorbents, has a pore structure mainly composed of microcapsules, and has a large adsorption surface area, which is used as a useful material because of its large adsorption capacity, low cost, and easy to use. However, since pure activated carbon has a disadvantage of low selective adsorption performance for carbon dioxide, surface modification is being studied for improvement of adsorption performance, and it is necessary to improve and improve the selective adsorption capacity of carbon dioxide.

본 발명의 목적은 실내 이산화탄소를 효율적으로 제거하여 이산화탄소를 저농도로 유지시키기 위해 상용화된 활성탄소를 활성화제로 활성화 및 금속산화물을 담지시켜 이산화탄소 흡착용 활성탄소를 제조함에 있다.It is an object of the present invention to provide an activated carbon for adsorbing carbon dioxide by activating commercial activated carbon as an activator and supporting a metal oxide in order to efficiently remove the indoor carbon dioxide and maintain the concentration of carbon dioxide at a low concentration.

상기 목적을 달성하기 위하여, 본 발명은 (1) 활성탄소와 KOH, Na2CO3, NaOH, ZnCl2, MgCl2 및 H3PO4을 포함하는 군에서 선택되는 1 이상의 활성화제를 혼합하여 활성화 처리된 활성탄소의 전구체를 제조하는 단계; (2) 상기 활성화 처리된 활성탄소의 전구체와 Ni, Mn, Ca, Mg, Co 및 Cu를 포함하는 군에서 선택되는 1 이상의 금속을 혼합하여 금속이 담지된 활성탄소의 전구체를 제조하는 단계; (3) 상기 금속이 담지된 활성탄소의 전구체를 비활성 기체 분위기 하의 600 내지 1500 ℃에서 탄화하는 단계; (4) 산 용액으로 처리하고 pH가 5 내지 7이 될 때까지 세척한 후 건조시켜 활성화 처리 및 금속이 담지된 활성탄소를 제조하는 단계; 및 (5) 상기 (4)단계에서 제조한 활성탄소를 산소 분위기 하의 150 내지 600 ℃에서 산화하여 표면처리하는 단계;를 포함하는 이산화탄소 흡착용 활성탄소의 제조방법을 제공한다.In order to achieve the above object, the present invention provides a process for producing activated carbon comprising the steps of (1) mixing activated carbon with at least one activator selected from the group consisting of KOH, Na 2 CO 3 , NaOH, ZnCl 2 , MgCl 2 and H 3 PO 4 , Producing a treated precursor of activated carbon; (2) mixing the activated carbon precursor precursor with at least one metal selected from the group consisting of Ni, Mn, Ca, Mg, Co, and Cu to prepare a precursor of activated carbon; (3) carbonizing the metal-supported activated carbon precursor at 600 to 1500 占 폚 in an inert gas atmosphere; (4) treating with an acid solution, washing until the pH is 5 to 7, and then drying to produce an activated carbon and a metal-supported activated carbon; And (5) oxidizing the activated carbon prepared in the step (4) at 150 to 600 ° C. under an oxygen atmosphere to perform a surface treatment.

상기 (1)단계에서 활성탄소와 활성화제는 1 : 0.001 내지 1 : 4의 중량비로 혼합되는 것을 특징으로 한다.In the step (1), the active carbon and the activator are mixed in a weight ratio of 1: 0.001 to 1: 4.

상기 (2)단계에서 활성화 처리된 활성탄소의 전구체와 금속은 각각 95 내지 99 중량%와 1 내지 5 중량%로 혼합되는 것을 특징으로 한다.The precursor of activated carbon activated in the step (2) and the metal are mixed in an amount of 95 to 99 wt% and 1 to 5 wt%, respectively.

상기 (4)단계에서 건조공정은 100 내지 150 ℃에서 24 내지 48 시간 동안 진행되는 것을 특징으로 한다.In the step (4), the drying process is performed at 100 to 150 ° C for 24 to 48 hours.

상기 이산화탄소 흡착용 활성탄소는 이산화탄소 농도 측정장치 또는 이산화탄소 농도 제어장치에 이용되는 것을 특징으로 한다.The activated carbon for adsorbing carbon dioxide is used in a carbon dioxide concentration measuring apparatus or a carbon dioxide concentration controlling apparatus.

상기와 같은 본 발명에 따르면, 상용화된 활성탄소를 활성화제로 활성화하고 금속산화물을 담지시켜 고 나노기공, 고 비표면적을 갖는 이산화탄소 흡착용 활성탄소를 제조함으로써, 실내 이산화탄소를 효율적으로 제거하여 잠수함, 우주선, 철도, 차 등의 실내 이산화탄소를 저농도로 유지하는 효과가 있다.According to the present invention as described above, activated carbon is activated as an activator and metal oxide is supported to produce activated carbon for adsorbing carbon dioxide having high nano pore and high specific surface area, thereby efficiently removing indoor carbon dioxide, , Railway, car, etc., at low concentration.

도 1은 본 발명에 따른 활성탄소의 질소흡착등온선.
도 2는 실내 이산화탄소 측정 시스템 안에서 측정한 본 발명에 따른 활성탄소의 이산화탄소 감소율을 나타낸 그래프. 1 is a nitrogen adsorption isotherm of activated carbon according to the present invention.
2 is a graph showing the carbon dioxide reduction rate of the activated carbon according to the present invention measured in an indoor carbon dioxide measuring system.

이하, 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.

본 발명에서는 실제 잠수함, 우주선, 철도 및 차의 실내 내부와 비슷한 조건을 구현하여 내부 순환이 되도록 챔버를 제작하였으며, 활성화제의 혼합 비율을 조절하여 활성화 처리된 활성탄소를 제조하고 금속을 이용하여 금속산화물이 담지된 활성탄소를 제조하여 챔버의 내부에 이산화탄소 흡착제로 이용하였다.In the present invention, chambers are constructed to achieve internal circulation by realizing conditions similar to those of actual submarines, spaceships, railways, and cars. Activated carbon is prepared by controlling the mixing ratio of the activator, Activated carbon bearing oxides was prepared and used as carbon dioxide adsorbent in the chamber.

더욱 구체적으로, 챔버에 미니선풍기를 달아 일정한 풍속으로 공기 순환이 되도록 하였으며, 활성화제의 종류와 혼합 비율을 조절하여 새로운 구조를 갖는 활성화 처리된 활성탄소 및 금속의 종류와 함유량을 달리하여 금속산화물이 담지된 활성탄소를 제조하였다. 챔버 내부의 흡착제의 종류 및 양에 따라 이산화탄소를 흡착하는 초기 흡착량과 흡착량이 평형에 도달하는 시간을 측정함으로써 실제 잠수함, 우주선, 철도 및 차 실내 조건에서 흡착제의 종류 및 양이 이산화탄소의 흡착에 미치는 영향을 알 수 있다.More specifically, a mini fan was installed in the chamber to allow air circulation at a constant air velocity. By adjusting the kind and mixing ratio of the activator, the activated carbon having a new structure, The supported activated carbon was prepared. By measuring the amount of initial adsorption of carbon dioxide and the time of equilibrium reaching the adsorption amount depending on the type and amount of adsorbent in the chamber, the kind and amount of the adsorbent in actual submarine, spacecraft, railroad and car interior conditions affects the adsorption of carbon dioxide The effect can be known.

본 발명은 (1) 활성탄소와 KOH, Na2CO3, NaOH, ZnCl2, MgCl2 및 H3PO4을 포함하는 군에서 선택되는 1 이상의 활성화제를 혼합하여 활성화 처리된 활성탄소의 전구체를 제조하는 단계; (2) 상기 활성화 처리된 활성탄소의 전구체와 Ni, Mn, Ca, Mg, Co 및 Cu를 포함하는 군에서 선택되는 1 이상의 금속을 혼합하여 금속이 담지된 활성탄소의 전구체를 제조하는 단계; (3) 상기 금속이 담지된 활성탄소의 전구체를 비활성 기체 분위기 하의 600 내지 1500 ℃에서 탄화하는 단계; (4) 산 용액으로 처리하고 pH가 5 내지 7이 될 때까지 세척한 후 건조시켜 활성화 처리 및 금속이 담지된 활성탄소를 제조하는 단계; 및 (5) 상기 (4)단계에서 제조한 활성탄소를 산소 분위기 하의 150 내지 600 ℃에서 산화하여 표면처리하는 단계;를 포함하는 이산화탄소 흡착용 활성탄소의 제조방법을 제공한다.The present invention relates to (1) a method for producing activated carbon precursors by mixing activated carbon with at least one activator selected from the group consisting of KOH, Na 2 CO 3 , NaOH, ZnCl 2 , MgCl 2 and H 3 PO 4 ; (2) mixing the activated carbon precursor precursor with at least one metal selected from the group consisting of Ni, Mn, Ca, Mg, Co, and Cu to prepare a precursor of activated carbon; (3) carbonizing the metal-supported activated carbon precursor at 600 to 1500 占 폚 in an inert gas atmosphere; (4) treating with an acid solution, washing until the pH is 5 to 7, and then drying to produce an activated carbon and a metal-supported activated carbon; And (5) oxidizing the activated carbon prepared in the step (4) at 150 to 600 ° C. under an oxygen atmosphere to perform a surface treatment.

상기 (1)단계에서 활성탄소와 활성화제는 1 : 0.001 내지 1 : 4의 중량비로 혼합하고, 상기 혼합물을 함유하는 수용액을 70 내지 90 ℃, 바람직하게는 80 ℃에서 12 내지 24 시간 동안 교반하여 활성화 처리된 활성탄소의 전구체를 제조하는 것이 바람직하다. 상기 활성화제가 2종이 혼합될 경우 혼합되는 활성화제의 중량비는 1 : 0.001 내지 1 : 4인 것이 바람직하다.In the step (1), the activated carbon and the activator are mixed in a weight ratio of 1: 0.001 to 1: 4, and the aqueous solution containing the mixture is stirred at 70 to 90 ° C, preferably at 80 ° C for 12 to 24 hours It is preferable to produce the activated carbon precursor precursor. When two activators are mixed, the weight ratio of the activator mixed is preferably 1: 0.001 to 1: 4.

상기 (2)단계에서 활성화 처리된 활성탄소의 전구체와 금속은 각각 95 내지 99 중량%와 1 내지 5 중량%로 혼합하고, 상기 혼합물을 함유하는 수용액을 40 내지 60 ℃, 바람직하게는 50 ℃에서 12 내지 24 시간 동안 교반하여 금속이 담지된 활성탄소의 전구체를 제조하는 것이 바람직하다.The precursor of the activated carbon activated in the step (2) and the metal are mixed at 95 to 99 wt% and 1 to 5 wt%, respectively, and the aqueous solution containing the mixture is heated at 40 to 60 ° C, For 24 hours to prepare a precursor of activated carbon supported with a metal.

상기 (4)단계에서 건조공정은 100 내지 150 ℃, 바람직하게는 120 ℃에서 24 내지 48 시간 동안 진행되는 것이 바람직하다.In the step (4), the drying step is preferably performed at 100 to 150 ° C, preferably 120 ° C for 24 to 48 hours.

상기 (5)단계에서 산화공정은 10 내지 60 분간 진행되는 것이 바람직하다.In the step (5), the oxidation process preferably proceeds for 10 to 60 minutes.

상기 이산화탄소 흡착용 활성탄소는 이산화탄소 농도 측정장치 또는 이산화탄소 농도 제어장치에 이용될 수 있다. 공기 순환이 가능한 저농도의 이산화탄소 측정 시스템에서 본 발명에 따른 활성탄소를 이용하여 시간 변화에 따른 실내 이산화탄소 감소량을 확인하여 잠수함, 우주선, 철도 및 차와 같은 실내의 이산화탄소 양을 제어할 수 있다.The activated carbon for adsorbing carbon dioxide may be used in a carbon dioxide concentration measuring apparatus or a carbon dioxide concentration control apparatus. The amount of carbon dioxide in a room such as a submarine, a spacecraft, a railroad, and a car can be controlled by checking the decrease in the amount of indoor carbon dioxide with time using the activated carbon according to the present invention in a low concentration carbon dioxide measuring system capable of air circulation.

이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로서, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지 않는 것은 당업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.Hereinafter, the present invention will be described in more detail with reference to Examples. It is to be understood by those skilled in the art that these embodiments are merely illustrative of the present invention and that the scope of the present invention is not construed as being limited by these embodiments.

비교예 1.Comparative Example 1

TCI 제품의 활성탄소의 기공을 활성화하기 위해 120 ℃의 진공오븐에서 48 시간 동안 열처리를 시켰다. 이렇게 제조된 활성탄소는 실제 이산화탄소를 흡착하는 흡착제로 사용된다. To activate the pores of the activated carbon of the TCI product, heat treatment was performed in a vacuum oven at 120 ° C for 48 hours. The activated carbon thus produced is actually used as an adsorbent for adsorbing carbon dioxide.

실시예 1.Example 1.

본 발명에 따른 이산화탄소 흡착제의 성능 평가를 위하여 40 L의 쳄버를 준비하였다. 실험에 필요한 이산화탄소 전용분석기 및 미니선풍기는 동일한 위치에 두어 실험에 변이요소가 없도록 하였다. 또한, 시간 변화에 따른 정확한 이산화탄소 측정을 위해 미니선풍기를 챔버의 중앙에 연결하여 일정 풍량이 유지되도록 하였다. 챔버의 기체 투입로에 기체가 빠져나가지 않도록 septa를 이용하여 구멍을 막았으며 주사기를 이용하여 4500 ppm의 이산화탄소를 챔버의 내부로 주입하였다. 내부에 이산화탄소 전용분석기를 사용해 이산화탄소 농도가 4500 ppm이 되는지 4~5회 확인하였다. For evaluation of the performance of the carbon dioxide adsorbent according to the present invention, a 40 L chamber was prepared. Experimental CO2 analyzer and mini fan were placed in the same position so that there was no variation in the experiment. In addition, a mini fan was connected to the center of the chamber to maintain a constant air volume for accurate carbon dioxide measurement with time. In order to prevent the gas from escaping into the gas inlet of the chamber, the hole was closed using a septa, and 4500 ppm of carbon dioxide was injected into the chamber using a syringe. It was confirmed 4 to 5 times that the concentration of carbon dioxide was 4500 ppm using a dedicated carbon dioxide analyzer.

실시예 2.Example 2.

사용된 활성화 처리된 활성탄소의 혼합물은 활성탄소와 활성화제인 KOH를 균질하게 섞음으로써 제작되었다. 활성탄소와 KOH 양을 무게비 1:1로 수행하였으며, 100 ml 증류수를 넣어 용액이 섞이도록 교반한 후 80 ℃에서 24 시간 동안 교반하여 활성화 처리된 활성탄소의 전구체를 제조하였다. 건조된 활성화 처리된 활성탄소의 전구체는 튜브형 탄화로(tube furnace)를 이용한 탄화공정을 통해 활성화 처리된 활성탄소로 제조되었다. 활성화 처리된 활성탄소의 전구체는 튜브형 탄화로(tube furnace)의 중심 부분에 넣고 질소 분위기 하의 900 ℃에서 1 시간 동안 탄화하였고, 승온속도는 2 ℃/min으로 고정하였다. 탄화 후 제조된 활성화 처리된 활성탄소는 칼륨 이온 및 불순물을 제거하기 위하여 0.5 M HCl 용액으로 처리한 후, 증류수로 중성이 될 때까지 세척하는 과정을 3에서 4회 실시하였다. 또한, 필터링을 하여 최종 활성화 처리된 활성탄소를 제조하여 오븐에 120 ℃의 온도에서 24 시간 건조하였다. The activated carbon mixture used was prepared by homogeneously mixing the activated carbon with the activator KOH. Activated carbon and KOH were mixed at a weight ratio of 1: 1. 100 ml of distilled water was added to the mixture to stir the mixture. The mixture was stirred at 80 ° C for 24 hours to prepare activated carbon precursor. The precursors of the activated and activated activated carbon were prepared as activated carbon activated by carbonization process using a tube furnace. The activated carbon precursor precursor was placed in the center of a tube furnace and carbonized at 900 ° C for 1 hour under a nitrogen atmosphere. The rate of temperature increase was fixed at 2 ° C / min. Activated carbon prepared after carbonization was treated with 0.5 M HCl solution to remove potassium ions and impurities and then washed with distilled water until it became neutral. In addition, the activated carbon which was finally activated by filtering was prepared and dried in an oven at a temperature of 120 ° C for 24 hours.

실시예 3.Example 3.

활성탄소와 KOH 양을 무게비 1:2로 수행하였으며, 상기 실시예 2과 동일한 과정으로 800 ℃에서 이산화탄소 흡착용 활성화 처리된 활성탄소를 제조하였다.Activated carbon and activated carbon for carbon dioxide adsorption at 800 ° C. were prepared by the same procedure as in Example 2 except that the weight ratio of activated carbon to KOH was 1: 2.

실시예 4.Example 4.

활성탄소와 KOH 양을 무게비 1:3으로 수행하였으며, 상기 실시예 2과 동일한 과정으로 900 ℃에서 이산화탄소 흡착용 활성화 처리된 활성탄소를 제조하였다.Activated carbon and KOH were mixed at a weight ratio of 1: 3. Activated carbon activated carbon adsorption at 900 ° C was prepared in the same manner as in Example 2.

실시예 5.Example 5.

활성탄소와 KOH 양을 무게비 1:4로 수행하였으며, 상기 실시예 2과 동일한 과정으로 900 ℃에서 이산화탄소 흡착용 활성화 처리된 활성탄소를 제조하였다.Activated carbon and KOH were mixed at a weight ratio of 1: 4. Activated carbon for carbon dioxide adsorption at 900 ° C was prepared in the same manner as in Example 2.

실시예 6.Example 6.

상기 실시예 2과 동일하게 과정을 실시하되, 활성화제는 KOH와 NaOH를 무게 비율 3:1로 혼합하여 사용하였으며, 활성탄소와 혼합 활성화제의 비율을 1:4로 하여 900 ℃에서 이산화탄소 흡착용 활성화 처리된 활성탄소를 제조하였다. The same procedure as in Example 2 was carried out except that KOH and NaOH were mixed at a weight ratio of 3: 1 and the activated carbon was mixed with the mixed activator at a ratio of 1: 4, Activated carbon was prepared.

실시예 7.Example 7.

사용된 금속 담지된 활성탄소는 활성탄소와 금속물질 Mn, Ni을 균질하게 섞음으로써 제작되었다. 활성탄소와 2 %의 금속 MnO/NiO으로 수행하였으며, 30 ml의 촉매 역할을 하는 KOH 수용액을 넣어 물질이 잘 섞이도록 교반한 후 50 ℃에서 12 시간 동안 교반하여 금속이 담지된 활성탄소의 전구체를 제조하였다. 건조된 금속이 담지된 활성탄소의 전구체는 튜브형 탄화로(tube furnace)를 이용한 탄화공정을 통해 금속이 담지된 활성탄소로 제조되었다. 금속이 담지된 활성탄소의 전구체는 튜브형 탄화로(tube furnace)의 중심 부분에 넣고 질소 분위기 하의 800 ℃에서 1 시간 동안 탄화하였고, 승온속도는 2 ℃/min으로 고정하였다. 탄화 후 제조된 금속이 담지된 활성탄소는 칼륨 이온 및 불순물을 제거하기 위하여 0.5 M HCl 용액으로 처리한 후 증류수로 중성이 될 때까지 세척하는 과정을 3에서 4회 실시하였다. 또한, 필터링을 하여 최종 금속이 담지된 활성탄소를 제조하여 오븐에 120 ℃의 온도에서 24 시간 건조하였다. 또한, 금속산화물을 만들기 위해 탄화로(furnace)에 넣고 산소 분위기 하의 350 ℃에서 1 시간 동안 열처리하였다. The metal supported activated carbons used were made by homogeneously mixing the active carbon with the metallic materials Mn and Ni. Activated carbon and 2% metal MnO / NiO were added, and 30 ml of KOH aqueous solution was added. The mixture was stirred until the material was well mixed and then stirred at 50 ° C for 12 hours to prepare a precursor of metal- Respectively. The precursor of the activated carbon supported on the dried metal was prepared as a carbon supported activated carbon through a carbonization process using a tube furnace. The precursor of the metal-supported activated carbon was put into the center of a tube furnace and carbonized at 800 ° C for 1 hour under a nitrogen atmosphere, and the heating rate was fixed at 2 ° C / min. Activated carbon supported on metal after carbonization was treated with 0.5 M HCl solution to remove potassium ions and impurities and then washed with distilled water until neutral. Further, activated carbon having the final metal supported thereon was produced by filtering, and was then dried in an oven at 120 DEG C for 24 hours. Further, in order to make a metal oxide, it was put into a furnace and heat-treated at 350 ° C for 1 hour in an oxygen atmosphere.

실시예 8.Example 8.

상기 실시예 2와 동일한 방법으로 KOH 활성화 처리를 하되, 활성탄소와 KOH의 활성화는 무게비로 1:4로 수행하였다. 또한, 실시예 7과 동일한 과정으로 금속 담지를 실시하되, 활성탄소의 Mn, Cu 금속의 비율을 5 %로 하였으며, 탄화 온도는 900 ℃로 하여 이산화탄소 흡착용 MnO/CuO 금속이 담지된 활성탄소를 제조하였다. KOH activation treatment was carried out in the same manner as in Example 2, except activation of activated carbon and KOH was carried out at a weight ratio of 1: 4. In addition, the same procedure as in Example 7 was carried out to carry out the metal deposition. The ratio of Mn and Cu metal in the activated carbon was set to 5%, and the carbonization temperature was set to 900 ° C to produce activated carbon bearing the MnO / CuO metal for adsorbing carbon dioxide Respectively.

실시예 9.Example 9.

상기 실시예 7과 동일한 방법으로 금속 담지를 실시하되, Ni, Co 금속을 사용하였으며, 금속의 비율은 1 %로 하고, 탄화 온도는 800 ℃로 하여 이산화탄소 흡착용 NiO/CoO 금속이 담지된 활성탄소를 제조하였다. Ni, and Co metal were used in the same manner as in Example 7, except that the ratio of metal was 1%, the carbonization temperature was 800 ° C., and the activated carbon having NiO / CoO metal for carbon dioxide adsorption .

실시예 10.Example 10.

상기 실시예 2와 동일한 방법으로 활성화 처리를 하되, 활성화제는 KOH와 NaOH를 무게비율 4:1로 혼합하여 사용하였으며, 활성탄소와 혼합 활성화제의 비율은 1:1로 하여 수행하였다. 또한, 상기 실시예 7과 동일하게 금속 담지 과정을 실시하되, Ni, Co 금속을 사용하였으며, 금속의 비율은 5 %로 하고, 탄화 온도는 700 ℃로 하여 이산화탄소 흡착용 NiO/CoO 금속이 담지된 활성탄소를 제조하였다. Activation was carried out in the same manner as in Example 2 except that KOH and NaOH were mixed at a weight ratio of 4: 1, and the ratio of activated carbon to mixed activator was 1: 1. Further, the same procedure as in Example 7 was carried out except that Ni and Co metal were used, the ratio of metal was 5%, the carbonization temperature was 700 ° C, and NiO / CoO metal for carbon dioxide adsorption Activated carbon.

실시예 11.Example 11.

상기 실시예 2와 동일한 방법으로 활성화 처리를 하되, 활성화제는 KOH와 NaOH를 무게비율 1:1로 혼합하여 사용하였으며, 활성탄소와 혼합 활성화제의 비율은 1:4로 하여 수행하였다. 또한, 상기 실시예 7과 동일한 방법으로 금속 담지 과정을 실시하되, Mn, Co 금속을 사용하였으며, 금속의 비율은 5 %로 하고, 탄화 온도는 400 ℃로 하여 이산화탄소 흡착용 MnO/CoO 금속이 담지된 활성탄소를 제조하였다. Activation was carried out in the same manner as in Example 2 except that KOH and NaOH were mixed at a weight ratio of 1: 1, and the ratio of activated carbon to mixed activator was 1: 4. In addition, Mn and Co metal were used to carry out the metal deposition process in the same manner as in Example 7, the metal ratio was 5%, the carbonization temperature was 400 ° C, and the MnO / Lt; / RTI >

실시예 12.Example 12.

상기 실시예 7과 동일하게 과정을 실시하되, 활성탄소에 Co, Cu 금속을 사용하였으며, 금속의 비율은 5 %으로 하고, 탄화 온도는 800 ℃로 하여 이산화탄소 흡착용 CoO/CuO 금속이 담지된 활성탄소를 제조하였다. The same procedure as in Example 7 was carried out except that Co and Cu metal were used as the activated carbon. The ratio of the metal was 5%, the carbonization temperature was 800 ° C, and the CoO / CuO metal- Carbon.

실시예 13.Example 13.

상기 실시예 2와 동일한 방법으로 활성화 처리를 하되, 활성탄소와 KOH 활성화제의 비율을 1:4로 하여 수행하였다. 또한, 상기 실시예 7과 동일한 방법으로 금속 담지를 실시하되, Cu 금속을 사용하였으며, 금속의 비율은 2 %로 하고, 탄화 온도는 900 ℃로 하여 이산화탄소 흡착용 CuO 금속이 담지된 활성탄소를 제조하였다. Activation treatment was carried out in the same manner as in Example 2, except that the ratio of active carbon to KOH activator was 1: 4. In addition, the same procedure as in Example 7 was carried out to carry out the metal deposition, and Cu metal was used. The ratio of metal was 2% and the carbonization temperature was 900 ° C to produce activated carbon carrying CuO metal for adsorption of carbon dioxide Respectively.

실시예 14.Example 14.

상기 실시예 2와 동일한 방법으로 활성화 처리를 하되, 활성화제는 KOH와 NaOH를 무게비율 4:1로 혼합하여 사용하였으며, 활성탄소와 혼합 활성화제의 비율은 1:4로 하여 수행하였다. 또한, 상기 실시예 7과 동일한 방법으로 금속 담지를 실시하되, 활성탄소에 Mn 금속을 사용하였으며, 금속의 비율은 5 %로 하고, 탄화 온도는 800 ℃로 하여 이산화탄소 흡착용 MnO 금속이 담지된 활성탄소를 제조하였다. Activation was carried out in the same manner as in Example 2 except that KOH and NaOH were mixed at a weight ratio of 4: 1, and the ratio of activated carbon to mixed activator was 1: 4. In addition, metal carrying was carried out in the same manner as in Example 7, except that Mn metal was used as the activated carbon, the metal ratio was 5%, the carbonization temperature was 800 ° C, and the MnO metal- Carbon.

측정예 1. 이산화탄소 흡착용 활성탄소의 표면 관찰Measurement example 1. Surface observation of activated carbon for carbon dioxide adsorption

전자현미경(scanning electron microscope, Hitach S-4300SE)을 통해 본 발명에서 제조한 고효율 이산화탄소 흡착용 염기성 활성화제로 활성화 및 금속 담지된 활성탄소의 표면을 관찰하였다.The surface of activated and metal-supported activated carbon was observed with a basic activator for high-efficiency carbon dioxide adsorption prepared by the present invention through an electron microscope (scanning electron microscope, Hitach S-4300SE).

측정예 2. 이산화탄소 흡착용 활성탄소의 기공구조 특성Measurement example 2. Characteristic of pore structure of activated carbon for carbon dioxide adsorption

염기성 활성화제로 활성화 및 금속 담지된 활성탄소의 기공구조는 77K 액체 질소 분위기 하에서 시료 약 0.3 g을 채취하여 질소 기체를 흡착질로 하여 흡착량을 측정하였다. 시료의 전처리는 200 ℃에서 시료 내 잔류 압력이 10-3 torr 이하로 될 때까지 약 12 시간 동안 탈기시키고, 질소등온흡착 시험 후에는 P/P0(P: 부분압력; P0: 포화 증기압)이 약 0.05에서 0.25까지 범위의 흡착량에 대해서 BET 파라미터 변환 후, 직선의 기울기를 이용하여 BET 비표면적을 구하였다. 또한, 전체 기공부피는 P/P0가 0.99인 점에서 흡착된 양을 기초로 하여 구하였다.The pore structure of the activated carbon supported on basic activator was measured by adsorption of nitrogen gas to adsorbed 0.3g of sample under 77K liquid nitrogen atmosphere. P / P 0 (P: partial pressure; P 0 : saturation vapor pressure) after degassing for about 12 hours until the residual pressure in the sample becomes less than 10 -3 torr at 200 ° C., The BET specific surface area was determined using the slope of the straight line after the BET parameter conversion for the adsorption amount ranging from about 0.05 to 0.25. Also, the total pore volume was determined based on the adsorbed amount at a P / P 0 of 0.99.

측정예 3. 이산화탄소 흡착용 활성탄소의 실제 실내 조건에서의 이산화탄소 흡착량 측정Measurement example 3. Measurement of carbon dioxide adsorption amount of activated carbon for adsorption of carbon dioxide under actual indoor conditions

염기성 활성화제로 활성화 및 금속 담지된 활성탄소의 이산화탄소 흡착량을 측정하기 위해, 각 시료를 120 ℃의 진공오븐에서 활성화시킨 후, 이산화탄소 흡착 시스템을 가진 데시게이터 안에 일정량의 이산화탄소를 주입하여 흡착소재에 따른 이산화탄소 흡착량을 측정하였다. 1회의 이산화탄소 양은 4500 ppm으로 하였다. In order to measure the amount of carbon dioxide adsorbed on the activated and metal-impregnated activated carbon by the basic activator, each sample was activated in a vacuum oven at 120 ° C., and then a certain amount of carbon dioxide was injected into the desiccator having the carbon dioxide adsorption system. The adsorption amount was measured. The amount of carbon dioxide at one time was 4500 ppm.

Figure 112013117367610-pat00001
Figure 112013117367610-pat00001

Figure 112013117367610-pat00002
Figure 112013117367610-pat00002

이상, 본 발명내용의 특정한 부분을 상세히 기술하였는바, 당업계의 통상의 지식을 가진 자에게 있어서, 이러한 구체적인 기술은 단지 바람직한 실시태양일 뿐이며, 이에 의해 본 발명의 범위가 제한되는 것이 아닌 점은 명백할 것이다. 따라서 본 발명의 실질적인 범위는 첨부된 청구항들과 그것들의 등가물에 의해 정의된다고 할 것이다.
Having described specific portions of the present invention in detail, it will be apparent to those skilled in the art that this specific description is only a preferred embodiment and that the scope of the present invention is not limited thereby. It will be obvious. Accordingly, the actual scope of the present invention will be defined by the appended claims and their equivalents.

Claims (5)

(1) 활성탄소와 KOH, Na2CO3, NaOH, ZnCl2, MgCl2 및 H3PO4을 포함하는 군에서 선택되는 1 이상의 활성화제를 혼합하여 활성화 처리된 활성탄소의 전구체를 제조하는 단계;
(2) 상기 활성화 처리된 활성탄소의 전구체와 Mn, Co 및 Cu를 포함하는 군에서 선택되는 1 이상의 금속을 혼합하여 금속이 담지된 활성탄소의 전구체를 제조하는 단계;
(3) 상기 금속이 담지된 활성탄소의 전구체를 비활성 기체 분위기 하의 600 내지 1500 ℃에서 탄화하는 단계;
(4) 산 용액으로 처리하고 pH가 5 내지 7이 될 때까지 세척한 후 건조시켜 활성화 처리 및 금속이 담지된 활성탄소를 제조하는 단계; 및
(5) 상기 (4)단계에서 제조한 활성탄소를 산소 분위기 하의 150 내지 600 ℃에서 산화하여 표면처리하는 단계;를 포함하며,
상기 (1)단계에서 활성탄소와 활성화제는 1 : 4의 중량비로 혼합되며,
상기 (2)단계에서 활성화 처리된 활성탄소의 전구체와 금속은 각각 95 중량%와 5 중량%로 혼합되는 것을 특징으로 하는 이산화탄소 흡착용 활성탄소의 제조방법.
(1) preparing the activated carbon with KOH, Na 2 CO 3, NaOH , ZnCl 2, MgCl 2 , and H 3 PO 4 mixed with at least one activator selected from the group comprising the active process activated carbon precursor;
(2) mixing the activated carbon precursor precursor with at least one metal selected from the group consisting of Mn, Co and Cu to produce a precursor of activated carbon supported with metal;
(3) carbonizing the metal-supported activated carbon precursor at 600 to 1500 占 폚 in an inert gas atmosphere;
(4) treating with an acid solution, washing until the pH is 5 to 7, and then drying to produce an activated carbon and a metal-supported activated carbon; And
(5) oxidizing the activated carbon prepared in the step (4) by oxidation at 150 to 600 ° C under an oxygen atmosphere,
In the step (1), the active carbon and the activator are mixed at a weight ratio of 1: 4,
Wherein the precursor of the activated carbon activated in the step (2) and the metal are mixed at 95 wt% and 5 wt%, respectively.
삭제delete 삭제delete 제 1항에 있어서,
상기 (4)단계에서 건조공정은 100 내지 150 ℃에서 24 내지 48 시간 동안 진행되는 것을 특징으로 하는 이산화탄소 흡착용 활성탄소의 제조방법.
The method according to claim 1,
Wherein the drying step is carried out at 100 to 150 ° C for 24 to 48 hours in the step (4).
제 1항에 있어서,
상기 이산화탄소 흡착용 활성탄소는 이산화탄소 농도 측정장치 또는 이산화탄소 농도 제어장치에 이용되는 것을 특징으로 하는 이산화탄소 흡착용 활성탄소의 제조방법.

The method according to claim 1,
Wherein the activated carbon for adsorbing carbon dioxide is used in a carbon dioxide concentration measuring apparatus or a carbon dioxide concentration control apparatus.

KR1020130160938A 2013-12-23 2013-12-23 Manufacturing method of activated carbon for carbon dioxide adsorption KR101602649B1 (en)