KR101557830B1 - Ship Interial Material For Textiles Wallpaper - Google Patents

Ship Interial Material For Textiles Wallpaper Download PDF

Info

Publication number
KR101557830B1
KR101557830B1 KR1020140146084A KR20140146084A KR101557830B1 KR 101557830 B1 KR101557830 B1 KR 101557830B1 KR 1020140146084 A KR1020140146084 A KR 1020140146084A KR 20140146084 A KR20140146084 A KR 20140146084A KR 101557830 B1 KR101557830 B1 KR 101557830B1
Authority
KR
South Korea
Prior art keywords
fiber
sheet portion
wallpaper
woven
yarn
Prior art date
Application number
KR1020140146084A
Other languages
Korean (ko)
Inventor
박종희
오상훈
Original Assignee
엑스플로어(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엑스플로어(주) filed Critical 엑스플로어(주)
Priority to KR1020140146084A priority Critical patent/KR101557830B1/en
Application granted granted Critical
Publication of KR101557830B1 publication Critical patent/KR101557830B1/en

Abstract

The present invention relates to a fabric wall paper for a ship interior material manufactured by using a composite fiber material. More particularly, the fabric wall paper is attached to the wall in a ship and comprises: a back surface fabric sheet unit attached to the wall; and a front surface fabric sheet unit arranged on one side of the back surface fabric sheet. The fabric wall paper for a ship interior material manufactured by using a composite fiber material is woven to have a double structure comprising the front surface fabric sheet unit and the back surface fabric sheet unit. The front surface fabric sheet unit is made of flame retardant yarns or PET fibers and is processed to have flame retardant properties and anti-fouling properties. The back surface fabric sheet unit is made of low melting (LM) fibers or basalt fibers and is processed to have antibacterial properties and deodorant properties. Therefore, the fabric wall paper for a ship interior material has flame retardant, anti-fouling, antibacterial, and deodorant functions.

Description

복합 섬유 소재를 이용한 선박 내장재용 직물 벽지 { Ship Interial Material For Textiles Wallpaper }{Ship Interial Material For Textiles Wallpaper}

본 발명은 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지에 관한 것으로서, 보다 상세하게는 이중직으로 직조하여 표면직물시트부와 이면직물시트부를 형성하고, 표면직물시트부는 난연사 또는 PET섬유로 형성시키고 방염가공 및 방오가공하며, 이면직물시트부는 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암 섬유)로 형성시키고 항균가공 및 소취가공을 함으로서, 방염 및 방오기능과 향균 및 소취기능을 갖는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지에 관한 것이다.
The present invention relates to a woven wallpaper for a ship interior material using a composite fiber material, and more particularly, to a woven wall fabric for a ship interior material, which is woven in a double-woven form to form a surface textile sheet portion and a back textile sheet portion, The fabric is made of LM fiber (Low Melting fiber) or basalt fiber (basalt fiber) and processed by antimicrobial and deodorizing process, and it is possible to produce composite fiber material having flame retardant and antifouling function and antibacterial and deodorizing function. To a woven wallpaper for a ship interior material.

일반적으로 벽지(wallpaper)란 장식의 목적으로 벽면에 붙이는 시트(sheet) 종류를 총칭하는바, 초기에는 주로 종이재질이 사용되었지만 최근에는 비닐, 직물, 무기질, 목재 등 여러 가지 다양한 소재가 개발되어 목적과 기능, 심미감에 따른 선택의 폭을 넓히고 있다.Generally, a wallpaper is a general term for a sheet attached to a wall for decoration purpose. In the beginning, a paper material was used. However, recently, various materials such as vinyl, fabric, And a wider selection of functions and aesthetics.

이러한 벽지는 통상적으로 소재나 제조방법에 따라 구분하지만, 실제 제조에서는 여러 가지 소재와 제조방법을 조합하므로 양자를 연관지어 고려하는 것이 일반적이다.Such wallpaper is generally classified according to a material or a manufacturing method. However, in actual manufacturing, it is common to consider a combination of materials and manufacturing methods so that they are related to each other.

이때, 종이벽지 중에서 엠보싱(embossing) 벽지는 이른바 합지(合紙) 벽지라 불리는 그것으로서, 종이 두 장을 배접한 후 엠보싱과 프린트 과정을 거쳐 여러 가지 문양을 표시하며, 천연종이를 사용함에 따라 인체에 무해하고 가격이 저렴하여 90년대 벽지의 주종을 이루었다. 또한, 비닐벽지 중에서 염화비닐벽지는 이른바 실크(silk) 벽지라 불리는 그것으로서, PVC와 종이가 쉽게 박리 되므로 재시공이 용이하고 오염 등을 쉽게 지울 수 있어 현재 가장 널리 사용된다.In this paper, embossing wall paper among paper wall paper is called so-called interlaced paper wallpaper. After embedding two sheets of paper, embossing and printing process, various patterns are displayed. When natural paper is used, Harmless and inexpensive, making it the mainstream of wallpaper in the 90s. Among vinyl wallpapers, vinyl chloride wallpapers are so-called silk wallpapers, and they are easy to re-work because PVC and paper are easily peeled off, and they can be easily cleaned.

한편, 일반적인 벽지는 심미감을 추구하는 것 이외에 건축용 내장재로서 여러 가지 기능을 담당한다. 예를 들어 벽면 내 외부의 온도차에 따른 결로(結露) 현상을 방지하는 방로성(防露性), 충격을 흡수하는 탄력성(彈力性), 태양광선 및 시간경과에 따라 색깔이 변하지 않는 내후성(耐候性), 통기성(通氣性) 및 내수성(耐水性), 보온성(保溫性), 흡음성(吸音性), 시공성(施工性) 등은 벽지를 선택하는데 있어서 중요한 기준이 된다. 아울러 최근 들어 환경에 대한 관심이 높아지면서 친환경 벽지가 주목받고 있으며, 동(同) 추세에 따라 합성수지를 이용하는 비닐벽지 보다는 친환경 소재인 종이벽지나 대한민국 출원번호 제10-2007-0123447호에서와 같이 직물벽지가 주목되는 실정인바, 직물벽지는 특히 여타의 소재에서 찾아보기 힘든 고품위의 아름다움을 느낄 수 있는 동시에 방로성, 탄력성, 내후성, 통기성 및 내수성, 보온성, 흡음성이 뛰어난 소재로 각광받고 있다.On the other hand, in addition to pursuing a sense of beauty, a typical wallpaper has various functions as a building interior material. For example, it can be used as a waterproofing material to prevent condensation due to a difference in temperature inside and outside of a wall, elasticity to absorb impact, weather resistance that does not change in color depending on the sunlight, Waterproofness, heat insulation, sound absorption, and workability are important criteria for selecting a wallpaper. In recent years, as the interest in the environment has increased, eco-friendly wallpaper has attracted attention. According to the trend, paper wall paper, which is an eco-friendly material rather than vinyl wallpaper using synthetic resin, and Korean Patent Application No. 10-2007-0123447, Wallpaper is attracting attention, and textile wallpapers are attracting attention as materials that are high in quality that can not be found in other materials, and that are excellent in the properties of toughness, elasticity, weatherability, breathability, water resistance, warmth and sound absorption.

그러나, 해상의 선박의 사용되는 직물벽지의 경우 육상보다 높은 습기나 습도에 노출되므로 부식되거나 곰팡이 등에 오염되는 문제점이 빈번하게 발생되고 있으며, 이를 개선하고자 선박에 사용되는 직물벽지에 방오,난연,향균 등 기능성을 갖는 직물벽지의 개발이 시급히 요구되고 있다.
However, in the case of woven wallpaper used in marine vessels, problems such as corrosion and fouling are frequently caused due to exposure to moisture and humidity higher than those on land, and in order to improve such problems, there is a problem that stain, It is urgently required to develop a textile wallpaper having a functional property.

전술한 발명은 본 발명이 속하는 기술분야의 배경기술을 의미하며, 종래 기술을 의미하는 것은 아니다.
The above-mentioned invention means the background art of the technical field to which the present invention belongs, and does not mean the prior art.

본 발명은 상기한 종래의 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 이중직으로 직조하여 표면직물시트부와 이면직물시트부를 형성하고, 표면직물시트부는 난연사 또는 PET섬유로 형성시키고 방염가공 및 방오가공하며, 이면직물시트부는 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암 섬유)로 형성시키고 항균가공 및 소취가공을 함으로서, 방염 및 방오기능과 향균 및 소취기능을 갖는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지를 제공하는데 그 목적이 있다.SUMMARY OF THE INVENTION The present invention has been made to overcome the above-mentioned problems of the prior art, and it is an object of the present invention to provide a surface textile sheet portion and a back textile sheet portion by weaving in a double- The fabric is made of LM fiber (low melting fiber) or basalt fiber (basalt fiber) and processed by antimicrobial treatment and deodorization to produce a composite fiber material having flame retardant and antifouling function and antibacterial and deodorizing function And to provide a woven wallpaper for a ship interior material.

또한, PET섬유와 LM섬유(Low Melting섬유)로 직조한 후 열처리함으로서, 작업성이 용이하고 특수한 접착제 없이 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있는 특수 접착제 없이 일반적인 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있도록 하는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지를 제공하는데 다른 목적이 있다.
In addition, by weaving with PET fiber and LM fiber (Low Melting fiber) and heat treatment, it is easy to work and without any special adhesive, natural grass or water-soluble grass or stationary paste, Another object is to provide a textile wallpaper for a ship interior material using a composite fiber material which can be adhered to a wall surface with a water-soluble grass or stationary grass.

본 발명은 선박의 실내 벽면에 부착되는 직물 벽지로서, 상기 직물 벽지는 벽면에 부착되는 이면직물시트부와, 상기 이면직물시트부의 일면에 마련되는 표면직물시트부로 이루어진 것을 특징으로 한다.The present invention is a fabric wallpaper adhered to an interior wall surface of a ship, wherein the fabric wallpaper comprises a back fabric sheet portion attached to a wall surface and a surface fabric sheet portion provided on one surface of the back fabric sheet portion.

또한, 상기 표면직물시트부의 표면원사는 난연사 또는 PET섬유(폴리에스테르섬유)중 어느하나가 사용되고, 상기 이면직물시트부는 이면원사는 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암 섬유)중 어느하나가 사용되는 것을 특징으로 한다.The surface yarn of the surface fabric sheet portion may be one of a fire retardant yarn or PET fiber (polyester fiber), and the back surface yarn portion may be any of LM fiber (low melting fiber) or basalt fiber One is used.

또한, 상기 표면직물시트부의 표면원사는 난연사 및 PET섬유(폴리에스테르섬유)가 사용되고, 상기 이면직물시트부는 이면원사는 LM섬유(Low Melting 섬유) 및 basalt섬유(현무암 섬유)가 사용되는 것을 특징으로 한다.It is preferable that the surface yarn of the surface cloth sheet portion is made of fire retardant yarn and PET fiber (polyester fiber), and the back surface yarn portion is made of LM fiber (low melting fiber) and basalt fiber (basalt fiber) .

또한, 상기 표면원사는 방염가공 및 방오가공한 후 직조하여 상기 표면직물시트부를 형성하도록 되고, 상기 이면원사는 항균가공 및 소취가공한 후 직조하여 상기 이면직물시트부를 형성하도록 된 것을 특징으로 한다.The surface yarn is subjected to flame-proofing and antifouling, and then woven to form the surface textile sheet portion. The backside yarn is formed by antibacterial processing, deodorization, and weaving to form the back textile sheet portion.

또한, 상기 직물 벽지는 이중직(二重織)으로 직조되어, 상기 이면직물시트부와 상기 표면직물시트부가 상호 엮여 형성된 것을 특징으로 한다.
Further, the fabric wallpaper is woven in a double weave, and the back fabric sheet portion and the surface fabric sheet portion are interlaced and formed.

본 발명인 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지는 이중직으로 직조하여 표면직물시트부와 이면직물시트부를 형성하고, 표면직물시트부는 난연사 또는 PET섬유로 형성시키고 방염가공 및 방오가공하며, 이면직물시트부는 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암 섬유)로 형성시키고 항균가공 및 소취가공을 함으로서, 방염 및 방오기능과 향균 및 소취기능을 갖는 효과가 있다.The woven wallpaper for a ship interior material using the composite fiber material of the present invention is woven in a double woven fabric to form a surface woven sheet portion and a back woven sheet portion, the surface woven sheet portion is formed of a fire retardant or PET fiber, The seat portion is formed of LM fiber (low melting fiber) or basalt fiber (basalt fiber), and has antibacterial processing and deodorization processing, and has an effect of flame retarding and antifouling function, antibacterial and deodorizing function.

또한, PET섬유와 LM섬유(Low Melting섬유)로 직조한 후 열처리함으로서, 작업성이 용이하고 특수한 접착제 없이 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있는 특수 접착제 없이 일반적인 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있도록 하는 효과가 있다.
In addition, by weaving with PET fiber and LM fiber (Low Melting fiber) and heat treatment, it is easy to work and without any special adhesive, natural grass or water-soluble grass or stationary paste, The water-soluble paste or the stationary paste can be attached to the wall surface.

도 1은 본 발명에 따른 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지를 나타낸 단면도이다.1 is a cross-sectional view of a fabric wallpaper for a ship interior material using a composite fiber material according to the present invention.

이하, 첨부된 도면들을 참조하여 본 발명에 따른 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지의 바람직한 실시예를 첨부된 도면을 참조하여 설명한다. 이 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다. 또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다. 그러므로, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of a textile wallpaper for a ship interior material using a composite fiber material according to the present invention will be described with reference to the accompanying drawings. In this process, the thicknesses of the lines and the sizes of the components shown in the drawings may be exaggerated for clarity and convenience of explanation. In addition, the terms described below are defined in consideration of the functions of the present invention, which may vary depending on the intention or custom of the user, the operator. Therefore, definitions of these terms should be made based on the contents throughout this specification.

또한, 하기 실시예는 본 발명의 권리범위를 한정하는 것이 아니라 단지 예시로 제시하는 것이며, 본 기술 사상을 통해 구현되는 다양한 실시예가 있을 수 있다.In addition, the following embodiments are not intended to limit the scope of the present invention, but merely as an example, and various embodiments may be implemented through the present invention.

도 1은 본 발명에 따른 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지를 나타낸 단면도이다.1 is a cross-sectional view of a fabric wallpaper for a ship interior material using a composite fiber material according to the present invention.

도면에 도시된 바와 같이 본 발명인 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지(10)(이하 설명의 편의상 직물벽지라 명명함)는 선박의 실내 벽면에 부착되는 직물 벽지로서, 이에 이와같은 직물벽지(10)는 표면직물시트부(20)와 이면직물시트부(30)로 이루어진다.
As shown in the drawings, a woven wallpaper 10 (hereinafter referred to as a woven fabric wallpaper) for a ship interior material using a composite fiber material according to the present invention is a woven wallpaper adhered to an indoor wall of a ship, 10 comprises a surface fabric sheet portion 20 and a back fabric sheet portion 30.

상기 이면직물시트부(30)는 선박의 내실이나 주거공간의 벽면에 부착되며, 상기 표면직물시트부(20)는 상기 이면직물시트부(30)의 일면에 마련된다.The back fabric sheet portion 30 is attached to a wall of an inner chamber or a housing space of a ship and the surface fabric sheet portion 20 is provided on one surface of the back fabric sheet portion 30. [

상기 이면직물시트부(30)는 접착제 또는 융착제로 상기 선박의 내실 벽면에 접착고정시키는 것이 바람직하다.Preferably, the back fabric sheet portion 30 is adhered and fixed to the inner wall surface of the ship with an adhesive or a welding agent.

상기 표면직물시트부(20)는 상기 이면직물시트부(30)에 접착 또는 박음질하여 고정시키는 것도 가능하며, 바람직하게는 후술될 이중직 방식의 직조방법으로 이면직물시트부(30)와 표면직물시트부(20)가 직조되면서 상호 연결,고정되도록 하는 것이 바람직하다.
The surface textile sheet portion 20 may be adhered to or stitched on the back textile sheet portion 30 and is preferably fixed to the back textile sheet portion 30 by a double- It is preferable that the portions 20 are mutually connected and fixed while being woven.

이때, 상기 표면직물시트부(20)의 표면원사(21)는 난연사 또는 PET섬유(폴리에스테르섬유)중 어느하나가 사용되며, 상기 이면직물시트부(30)는 이면원사(31)는 저융점 섬유인 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암섬유)중 어느하나가 사용된다.
The surface yarn 21 of the surface fabric sheet portion 20 may be one of a fire retardant yarn or PET fiber Either LM fiber (Low Melting fiber) or basalt fiber (basalt fiber) is used as the melting point fiber.

다르게는, 상기 표면직물시트부(20)의 표면원사(21)는 난연사 및 PET섬유가 함께 사용하는 것도 가능하며, 상기 이면직물시트부(30)는 이면원사(31)는 LM섬유 및 basalt섬유를 함께 사용하는 것도 가능하다.
Alternatively, the surface yarn 21 of the surface fabric sheet portion 20 may be used together with the fire retardant yarn and the PET fibers, and the back surface yarn sheet portion 30 may include the back yarn 31, It is also possible to use fibers together.

상기한 표면원사(21) 및 이면원사(31) 이외에 난연,항균성 등 기능성을 갖는 원사를 대체하여 사용하는 것도 가능하다.
In addition to the surface yarn 21 and the back yarn 31 described above, it is also possible to use a yarn having a function such as flame retardance and antibacterial property.

여기서, 직물 벽지를 PET섬유와 LM섬유(Low Melting섬유)로 직조한 후 열처리하여 패널형태로 뻣뻣하게 함으로서, 작업성이 용이하고 직물용 특수 접착제 없이 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있는 특수한 접착제 없이 일반적인 천연풀이나 수용성풀 또는 문구용 풀로도 벽면에 부착할 수 있게 된다.
Here, woven wallpaper is woven with PET fiber and LM fiber (Low Melting fiber) and then heat treated to stiff in panel form, so that it is easy to work and can be applied to the wall without any special glue for fabric, It can be attached to a wall by a general natural paste or a water-soluble paste or a stationary paste without special adhesive which can be attached.

상기 표면원사(21)는 방염성을 주어 가연성(可燃性)을 방지하는 가공인 방염가공(flame retardant finish, 防焰加工) 및 섬유 표면에 진흙, 부유먼지 등의 건조성 오물, 음료, 잉크 등의 수성오물, 기름, 유지 등의 유성 오물이 묻지 않는 또는 세탁하면 쉽게 제거되도록 하는 직물의 가공인 방오가공(antisoil finishing, 防汚加工)한 후 직조하여 상기 표면직물시트부(20)를 형성하도록 되고, 상기 이면원사(31)는 항균가공 및 소취가공한 후 직조하여 상기 이면직물시트부(30)를 형성하도록 된다.
The surface yarn 21 is provided with flame retardant finish (flame retardant finish) which imparts flame retardancy and prevents flammability, and a surface of the fiber yarn 21 on which the surface of the yarn 21 is coated with dry dust such as mud, (Antisoil finishing, antifouling), which is a process of fabric which does not adhere to oily dirt such as water dirt, oil, grease or oil, or which is easily removed by washing, and then forms the surface cloth sheet portion 20 , The back yarn 31 is subjected to antibacterial processing and deodorization and then woven to form the back textile sheet portion 30. [

이때, 상기 직물 벽지(10)는 이중직(二重織)으로 직조되어, 상기 이면직물시트부(30)와 상기 표면직물시트부(20)가 상호 엮여 형성된다.At this time, the fabric wallpaper 10 is woven in a double weave, and the back fabric sheet portion 30 and the surface fabric sheet portion 20 are interlaced.

즉, 상기 표면원사(21)와 상기 이면원사(31)를 이중직으로 직조하여 일면에 상기 표면직물시트부(20)가 형성되게 하고 타면에 이면직물시트부(30)가 형성되게 한다.That is, the surface yarn 21 and the back yarn 31 are woven in a double-woven form to form the surface fabric sheet portion 20 on one side and the back side fabric sheet portion 30 on the other side.

이러한, 이중직 직조는 경사를 직물의 표면에 나올 것과 뒷면에 나올 것의 두 가지를 쓰고, 위사 역시 표면에 나올 것과 뒷면에 나올 것 두 가지를 사용해 짜는 안팎 이중으로 된 직물이다.
These double - woven fabrics are double - fabric fabrics that weave both on the surface of the fabric and on the back, and weft using both the surface and the back.

상기와 같이 구성되는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지의 제조방법을 설명하면 먼저 표면원사(21)를 방염가공 및 방오가공하는 표면원사가공단계(S1)를 거친 후 이면원사(31)를 항균가공 및 소취가공하는 이면원사가공단계(S2)를 거친 다음 상기 표면원사(21)와 상기 이면원사(31)를 이중직으로 직조하여 이면직물시트부(30)와 표면직물시트부(20)로 이루어진 직물 벽지(10)를 형성하는 벽지형성단계(S3)를 거친 후 상기 직물 벽지(10)를 제단 및 포장하는 마감단계(S4)를 거침으로서, 일련의 과정을 마치게 된다.
The method of manufacturing a textile wallpaper for a ship interior material using the composite fiber material having the above-described structure is as follows. First, the front yarn 21 is subjected to a surface yarn processing step S1 for flame-proofing and fouling processing, The surface yarn 21 and the back yarn 31 are woven in a double-woven manner to form a back fabric sheet portion 30 and a surface fabric sheet portion 20 After completing the wallpaper forming step S3 forming the fabric wallpaper 10, the fabric wallpaper 10 is finished and wrapped in a finishing step S4 to complete a series of processes.

10 : 직물벽지
20 : 표면직물시트부
30 : 이면직물시트부
21 : 표면원사
31 : 이면원사
S1 : 표면원사가공단계
S2 : 이면원사가공단계
S3 : 벽지형성단계
S4 : 마감단계10: Fabric wallpaper
20: surface fabric sheet portion
30: back fabric sheet portion
21: Surface yarn
31: back yarn
S1: Surface yarn processing step
S2: Back yarn processing step
S3: Wall formation step
S4: Finishing step

Claims (5)

선박의 실내 벽면에 부착되는 직물 벽지로서,
상기 직물 벽지는 벽면에 부착되는 이면직물시트부와,
상기 이면직물시트부의 일면에 마련되는 표면직물시트부로 이루어진 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지에 있어서,
상기 표면직물시트부의 표면원사는 난연사 및 PET섬유(폴리에스테르섬유)가 사용되고, 상기 이면직물시트부는 이면원사는 LM섬유(Low Melting 섬유) 및 basalt섬유(현무암 섬유)가 사용되는 것을 특징으로 하는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지.
A fabric wallpaper attached to an interior wall surface of a ship,
The fabric wallpaper includes a back fabric sheet portion attached to a wall surface,
And a surface textile sheet portion provided on one surface of the back textile sheet portion,
Wherein the surface yarn of the surface woven sheet portion is made of fire retardant yarn and PET fiber (polyester fiber), and the back surface yarn portion is made of LM fiber (low melting fiber) and basalt fiber (basalt fiber) Fabric wallpaper for ship interior materials using composite fiber material.
제 1 항에 있어서,
상기 표면직물시트부의 표면원사는 난연사 또는 PET섬유(폴리에스테르섬유)중 어느하나가 사용되고, 상기 이면직물시트부는 이면원사는 LM섬유(Low Melting섬유) 또는 basalt섬유(현무암 섬유)중 어느하나가 사용되는 것을 특징으로 하는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지.
The method according to claim 1,
The surface yarn of the surface fabric sheet portion may be one of a fire retardant yarn or PET fiber (polyester fiber), and the back surface yarn may be one of LM fiber (Low Melting fiber) or basalt fiber (basalt fiber) Characterized in that it is used as a woven wallpaper for a ship interior material using a composite fiber material.
삭제delete 제 1 항에 있어서,
상기 표면원사는 방염가공 및 방오가공한 후 직조하여 상기 표면직물시트부를 형성하도록 되고, 상기 이면원사는 항균가공 및 소취가공한 후 직조하여 상기 이면직물시트부를 형성하도록 된 것을 특징으로 하는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지.
The method according to claim 1,
Wherein the front surface yarn is subjected to flame proofing and antifouling and then woven to form the front surface cloth sheet portion, and the back surface yarn is subjected to antibacterial processing and deodorization and then woven to form the back surface cloth sheet portion. Woven wallpaper for ship interior materials using.
제 1 항에 있어서,
상기 직물 벽지는 이중직(二重織)으로 직조되어, 상기 이면직물시트부와 상기 표면직물시트부가 상호 엮여 형성된 것을 특징으로 하는 복합 섬유 소재를 이용한 선박 내장재용 직물 벽지.



The method according to claim 1,
Wherein the fabric wallpaper is woven in a double weave wherein the back textile sheet portion and the surface textile sheet portion are intertwined with one another to form a textile wallpaper for a ship interior material using a composite fiber material.



KR1020140146084A 2014-10-27 2014-10-27 Ship Interial Material For Textiles Wallpaper KR101557830B1 (en)