KR101547663B1 - Eco-Friendly Repairing Mortar Having Water-Proofing Composition Using Seaweeds and Constructing Methods Using Thereof - Google Patents
Eco-Friendly Repairing Mortar Having Water-Proofing Composition Using Seaweeds and Constructing Methods Using Thereof Download PDFInfo
- Publication number
- KR101547663B1 KR101547663B1 KR1020150016775A KR20150016775A KR101547663B1 KR 101547663 B1 KR101547663 B1 KR 101547663B1 KR 1020150016775 A KR1020150016775 A KR 1020150016775A KR 20150016775 A KR20150016775 A KR 20150016775A KR 101547663 B1 KR101547663 B1 KR 101547663B1
- Authority
- KR
- South Korea
- Prior art keywords
- parts
- weight
- eco
- mortar composition
- friendly
- Prior art date
Abstract
Description
본 발명은 해조류를 이용한 친환경 보수용 몰탈 조성물 및 이를 이용한 시공방법에 관한 것으로서, 보다 상세하게는 도로, 고속도로, 활주로, 및/또는 철로 등의 토목 구조물이나 건축구조물의 손상부를 신속히 복원시키는 시공에 적용 가능하도록 하고 고성능의 휨강도, 부착강도, 균열방지, 및 방수성능을 제공하는 특성을 갖는 해조류를 이용한 친환경 보수용 몰탈 조성물 및 이를 이용한 시공방법에 관한 것이다.
The present invention relates to a mortar composition for eco-friendly repair using seaweeds, and more particularly to a construction method for rapidly restoring damaged parts of civil engineering structures such as roads, highways, runways, and / And to provide a high-performance bending strength, adhesion strength, crack prevention, and waterproof performance, and to a method of using the same.
일반적으로 도로의 노면, 활주로, 철로 및/또는 건물 등의 콘크리트 구조물의 손상부위를 보수 및/또는 보강하기 위한 보수공사에는 조강 포틀랜드 시멘트가 사용되고 있다.In general, crude steel Portland cement is used for repairing and / or repairing damaged areas of concrete structures such as road surfaces, runways, railways, and / or buildings.
조강 포틀랜드 시멘트는 일반 시멘트에 비하여 시공성이 우수한 장점이 있으나, 투수성이 높아 염화물이나 수분의 침투가 발생하여 콘크리트가 부식되는 문제가 있다.Although crude steel Portland cement is superior in workability to general cement, there is a problem that concrete is corroded due to penetration of chloride or water due to high permeability.
특히, 조강 포틀랜드 시멘트는 그 특성상 콘크리트가 경화되는 양생시간이 오래 소요되기 때문에 작업의 특성상 짧은 시간 내에 마무리하여야 하는 긴급 보수공사에 사용하기 곤란한 점이 있다.Especially, since the curing time of cement concrete is long due to its characteristics, it is difficult to use it for urgent repair work which must be completed within a short time due to the characteristics of the work.
최근 긴급 보수공사에 사용되는 조강 포틀랜드 시멘트의 단점을 보완하기 위해 콘크리트에 폴리머 에멀젼을 첨가한 폴리머 시멘트 콘크리트의 사용이 점차 증가하고 있다.Recently, polymer cement concrete with polymer emulsion added to concrete has been increasingly used to overcome the shortcomings of crude steel Portland cement used for emergency repair.
그러나 기존 폴리머 시멘트 콘크리트는 고가의 폴리머 디스퍼젼을 사용함으로써 공사비의 상승 원인을 제공한다.However, the existing polymer cement concrete provides a cause of increase of the construction cost by using expensive polymer dispersion.
또한, 속경성 폴리머 시멘트 콘크리트는 그 재료 자체의 특성으로 인해 초기 수분 증발이 신속이 진행되어 초기에 플라스틱 균열이 발생할 가능성이 있고, 건조 수축 및 수화열이 높아 균열발생이 용이하다.Also, in the case of the quick-setting polymer-cement concrete, due to the characteristics of the material itself, the early water evaporation proceeds rapidly, and there is a possibility that plastic cracks are generated at the beginning, and the cracks are easily generated due to high shrinkage and hydration heat.
더욱이, 콘크리트 구조물의 손상면을 신속하게 보수하기 위해 에폭시 수지를 이용하여 보수하는 방법이 사용되고 있지만, 상기 에폭시 수지가 콘크리트 손상면에 적용될 경우, 모세관현상에 의해 습기가 콘크리트 손상면과 에폭시 수지에 작용하여 서로 탈리되는 현상이 종종 발생하는 문제점이 있다.Furthermore, in order to quickly repair the damaged surface of the concrete structure, a method of repairing the epoxy resin is used. However, when the epoxy resin is applied to the damaged surface of the concrete, moisture is caused to act on the concrete damage surface and the epoxy resin by the capillary phenomenon There is a problem that the phenomenon of being separated from each other often occurs.
이러한 문제점을 극복하기 위해, 급결제를 사용하여 콘크리트를 신속하게 경화시키는 방법을 사용할 수 있다.In order to overcome such a problem, a method of rapidly curing concrete using a rapid setting agent can be used.
한편, 현재 국내에서 일반적으로 사용되는 급결제로는 소듐실리케이트 및/또는 포타슘실리케이트를 주성분으로 하는 무기염계 급결제가 있고, 하소한 명반석으로 수산화칼슘과 반응하여 칼슘알루미네이트 수화물, 에트링가이트 등을 생성시켜 시멘트를 급결시키는 급경성 광물을 포함하는 급결제가 있으며, 칼슘알루미네이트 및/또는 칼슘설포알루미네이트계를 포함하는 시멘트계 급결제가 있다.On the other hand, in the present invention, there is an inorganic salt type quick-setting admixture mainly comprising sodium silicate and / or potassium silicate, and calcium aluminate hydrate, etringing etc. And a quick-setting material containing a rapid-hardening mineral which rapidly cures the cement. There is a cement-based quick-setting material containing calcium aluminate and / or calcium sulfoaluminate.
여기서, 상기 시멘트계 급결제는 전술한 무기염계 및 급경성 광물을 포함하는 급결제 보다 장기 강도가 우수하다. Here, the cementitious quick-setting admixture is superior in long-term strength to that of the quick-setting admixture containing the inorganic salt and the hard hard mineral.
하지만, 상기 시멘트계 급결제는 알칼리성을 띄므로 이를 다량 사용하면 폐쇄공간 등의 특정장소에서 작업하기 곤란하고, 주변토양을 오염시킬 가능성이 있다.
However, the above-mentioned cement-based quick-setting material is alkaline, and if it is used in a large amount, it is difficult to work in a specific place such as a closed space, and there is a possibility to pollute nearby soil.
본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로서, 도로의 노면, 활주로, 철로 등의 토목 구조물이나 건축 구조물의 손상부위를 보수 및/또는 보강하기 위한 몰탈 조성물이 요구하는 충분한 압축강도, 휨강도, 부착강도, 균열방지, 내구성능 및 방수성능을 제공하고자 한다.
SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and it is an object of the present invention to provide a mortar composition for repairing and / or reinforcing civil engineering structures such as road surface, runway, , Adhesion strength, crack prevention, durability performance and waterproof performance.
본 발명은
시멘트 100중량부를 기준으로,
가시파래, 납작파래, 구멍갈파래, 홀파래, 매생이, 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 불가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 부채살, 비단풀, 단박, 돌가사리, 석목, 작은톱니 지누아리 또는 이들의 혼합물인 해조류 10 내지 60중량부;
메틸메타아크릴레이트 20 내지 80중량부;
폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 프리폴리머 10 내지 60중량부;
경화제 5 내지 30중량부;
고기능성 파우더 5 내지 15중량부;
소포제 5 내지 10중량부;
실리카퓸 10 내지 30중량부;
저수축제 1 내지 10중량부;
열화방지제 1 내지 5중량부; 및
감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물에,
카본파이버를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,
아미노메틸폴리디메틸실록산을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 3 내지 10중량부로 더 포함하며,
흡수성 폴리머로서 폴리아크릴산염을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.2 내지 10중량부로 더 포함하고,
옥틸트리에톡시실란을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
지연제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.05 내지 0.2중량부로 더 포함하고,
폴리옥사이드계 평활제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,The present invention
Based on 100 parts by weight of cement,
It is a kind of fish in the sea. It is a fish which is a kind of fish. It is a fish, It is also known that it is a kind of gambia which is a kind of gambia which is a kind of gambia. 10 to 60 parts by weight of algae which are hair, true gambling, kashiiu, fan, silkworm, short twig, rock scarf, gypsum, small sawtooth or mixtures thereof;
20 to 80 parts by weight of methyl methacrylate;
10 to 60 parts by weight of a prepolymer which is a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least one selected from these;
5 to 30 parts by weight of a curing agent;
5 to 15 parts by weight of high-performance powder;
5 to 10 parts by weight of a defoaming agent;
10 to 30 parts by weight of silica fume;
1 to 10 parts by weight of a water reducing festival;
1 to 5 parts by weight of an anti-deterioration agent; And
1 to 5 parts by weight of a water reducing agent is added to an eco-friendly repair mortar composition using algae,
The carbon fiber further comprises 1 to 10 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition,
Further comprising aminomethyl polydimethylsiloxane in an amount of 3 to 10 parts by weight based on 100 parts by weight of an eco-friendly mortar composition,
Further comprising 0.2 to 10 parts by weight of a polyacrylate as the water absorbent polymer based on 100 parts by weight of the eco-friendly repair mortar composition,
Octyltriethoxysilane is further contained in an amount of 1 to 5 parts by weight based on 100 parts by weight of an eco-friendly mortar composition,
Further comprising 0.05 to 0.2 parts by weight based on 100 parts by weight of the mortar composition for eco-friendly repair,
Further comprising 1 to 10 parts by weight of a polyoxide-based smoothing agent based on 100 parts by weight of an eco-friendly repair mortar composition,
유리 비드를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 10 내지 50중량부로 더 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 제공한다.
A mortar composition for eco-friendly repair using algae further comprising glass beads in an amount of 10 to 50 parts by weight based on 100 parts by weight of an eco-friendly repair mortar composition.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
또한, 본 발명은
시공 대상표면의 이물질을 제거하는 이물질 제거단계;
상기 이물질 제거단계가 종료된 표면에 시멘트 100중량부를 기준으로, 가시파래, 납작파래, 구멍갈파래, 홀파래, 매생이, 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 불가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 부채살, 비단풀, 단박, 돌가사리, 석목, 작은톱니 지누아리 또는 이들의 혼합물인 해조류 10 내지 60중량부, 메틸메타아크릴레이트 20 내지 80중량부, 폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 프리폴리머 10 내지 60중량부, 경화제 5 내지 30중량부, 고기능성 파우더 5 내지 15중량부, 소포제 5 내지 10중량부, 실리카퓸 10 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물에, 카본파이버를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 아미노메틸폴리디메틸실록산을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 3 내지 10중량부로 더 포함하며, 흡수성 폴리머로서 폴리아크릴산염을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.2 내지 10중량부로 더 포함하고, 옥틸트리에톡시실란을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 지연제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.05 내지 0.2중량부로 더 포함하고, 폴리옥사이드계 평활제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 유리 비드를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 10 내지 50중량부로 더 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 적층하는 적층단계;
상기 적층단계가 종료된 후 해조류를 이용한 친환경 보수용 몰탈 조성물을 경화하는 경화단계; 및
상기 경화단계가 종료된 후 시공면을 건조시키는 건조단계를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물의 시공방법을 제공한다.
In addition,
A foreign matter removing step of removing foreign matter on a surface to be applied;
The surface on which the foreign matter removing step has been completed is coated with 100 parts by weight of cement based on 100 parts by weight of cement based on 100 parts by weight of cement based on 100 parts by weight of cement, , Starfish, starfish, starfish, starfish, starfish, starfish, starfish, mackerel, starfish, starfish, starfish, starfish, starfish, 10 to 60 parts by weight of seaweed which is a mixture of gambling, barking, round starch, bamboo shoots, bamboo shoots, chopped bamboo shoots, crocodile bamboo shoots, true gambling, bamboo shoots, , 20 to 80 parts by weight of methyl methacrylate, 10 to 60 parts by weight of a prepolymer which is a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least one selected from these, 5 to 30 parts by weight of a high-performance powder, 5 to 10 parts by weight of a defoaming agent, 10 to 30 parts by weight of a silica fume, 1 to 10 parts by weight of a water-reducing agent, 1 to 5 parts by weight of a deterioration inhibitor, To 5 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, the aminomethyl polydimethyl siloxane is added to the eco-friendly repair mortar composition 100 Further comprising 3 to 10 parts by weight based on 100 parts by weight of the water-absorbing polymer, wherein the polyacrylate is further contained in an amount of 0.2 to 10 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, and octyltriethoxysilane is used as an eco- 1 to 5 parts by weight based on 100 parts by weight of the mortar composition for environmental protection, wherein the retarder is 0.05 to 0.2 parts by weight based on 100 parts by weight of the eco- Wherein the glass beads are further contained in an amount of 10 to 50 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, wherein the glass beads are further contained in an amount of 1 to 10 parts by weight based on 100 parts by weight of the eco- A laminating step of laminating an eco-friendly repair mortar composition containing seaweeds;
A curing step of curing the eco-friendly repair mortar composition using seaweeds after the laminating step is completed; And
And a drying step of drying the surface to be dried after the curing step is completed. The present invention also provides a method of constructing an eco-friendly repair mortar composition using algae.
삭제delete
삭제delete
삭제delete
본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 보수시공에 사용되는 몰탈 조성물이 요구하는 충분한 압축강도, 휨강도, 부착강도, 균열방지, 내구성능 및 방수성능을 제공하는 효과가 있다.
The mortar composition for eco-friendly repair using seaweeds according to the present invention has an effect of providing sufficient compressive strength, bending strength, adhesion strength, anti-cracking, durability and waterproof performance required for mortar composition used for maintenance work.
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
한 가지 관점에서, 본 발명은 시멘트 100중량부를 기준으로, 해조류 10 내지 60중량부; 메틸메타아크릴레이트 20 내지 80중량부; 프리폴리머 10 내지 60중량부; 경화제 5 내지 30중량부; 고기능성 파우더 5 내지 15중량부; 소포제 5 내지 10중량부; 실리카퓸 10 내지 30중량부; 저수축제 1 내지 10중량부; 열화방지제 1 내지 5중량부; 및 감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 제공한다.In one aspect, the present invention relates to a cement composition comprising, based on 100 parts by weight of cement, 10 to 60 parts by weight of seaweeds; 20 to 80 parts by weight of methyl methacrylate; 10 to 60 parts by weight of a prepolymer; 5 to 30 parts by weight of a curing agent; 5 to 15 parts by weight of high-performance powder; 5 to 10 parts by weight of a defoaming agent; 10 to 30 parts by weight of silica fume; 1 to 10 parts by weight of a water reducing festival; 1 to 5 parts by weight of an anti-deterioration agent; And 1 to 5 parts by weight of a water reducing agent.
다른 관점에서, 본 발명은 시공 대상표면의 이물질을 제거하는 이물질 제거단계; 상기 이물질 제거단계가 종료된 표면에 시멘트 100중량부를 기준으로, 해조류 10 내지 60중량부, 메틸메타아크릴레이트 20 내지 80중량부, 프리폴리머 10 내지 60중량부,경화제 5 내지 30중량부, 고기능성 파우더 5 내지 15중량부, 소포제 5 내지 10중량부, 실리카퓸 10 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 적층하는 적층단계; 상기 적층단계가 종료된 후 해조류를 이용한 친환경 보수용 몰탈 조성물을 경화하는 경화단계; 및 상기 경화단계가 종료된 후 시공면을 건조시키는 건조단계를 포함하는 친환경 보수용 몰탈 조성물의 시공방법을 제공한다.According to another aspect of the present invention, there is provided a method of manufacturing a semiconductor device, comprising: a foreign matter removing step of removing foreign matters on a surface to be applied; 10 to 60 parts by weight of algae, 20 to 80 parts by weight of methyl methacrylate, 10 to 60 parts by weight of a prepolymer, 5 to 30 parts by weight of a curing agent, 10 to 60 parts by weight of a high- 5 to 15 parts by weight of an antifoaming agent, 5 to 10 parts by weight of a defoaming agent, 10 to 30 parts by weight of a silica fume, 1 to 10 parts by weight of a water reducing agent, 1 to 5 parts by weight of a deterioration inhibitor and 1 to 5 parts by weight of a water reducing agent A laminating step of laminating the repair mortar composition; A curing step of curing the eco-friendly repair mortar composition using seaweeds after the laminating step is completed; And a drying step of drying the construction surface after the curing step is completed.
본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 건축물, 일반도로, 고속도로, 활주로 및/또는 철로 등의 콘크리트 구조물의 손상부를 신속히 복원시키고 방수성능을 제공하는 시공에 적용 가능한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 보수용 몰탈 조성물이라면 특별히 한정되지 않는다.The mortar composition for eco-friendly repair using seaweeds according to the present invention is applicable to a construction in which damaged parts of concrete structures such as buildings, general roads, highways, runways and / or railways are rapidly restored and waterproofing performance is provided. And is not particularly limited so long as it is a conventional repair mortar composition.
본 발명에 따른 시멘트로는 일반 포틀랜드 시멘트 또는 고로슬래그시멘트, 초미분말시멘트, 마이크로시멘트 등의 특수 시멘트를 사용할 수 있다. 나머지 성분들의 함량은 시멘트 100중량부를 기준으로 한다.As the cement according to the present invention, special cements such as general portland cement, blast furnace slag cement, ultra fine powder cement, and micro cement can be used. The content of the remaining components is based on 100 parts by weight of cement.
바람직한 시멘트로는 마이크로시멘트를 사용하는 것을 추천한다.It is recommended to use micro cement as the preferred cement.
상기 마이크로시멘트는 시멘트 초기강도 및 시멘트 경화체의 장기강도를 증진시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 마이크로시멘트라면 특별히 한정되지 않는다.The microcement is intended to improve the initial strength of cement and the long-term strength of cured cement, and is not particularly limited as long as it is conventional microcement in the art having such a purpose.
특히, 상기 마이크로시멘트는 보통 포틀랜드 시멘트의 블레인 분말도 약 2,800 내지 3,500㎠/g과 비교하여 매우 미립으로 구성되어 물과 접촉하여 시멘트의 수화반응이 빠르게 진행되기 때문에 시멘트의 초기강도를 증진시킬 수 있을 뿐만 아니라, 시멘트 경화제의 장기강도 역시 증진된다.Particularly, since the microcement usually has very fine grains compared to about 2,800 to 3,500 cm2 / g of the blast powder of the Portland cement, the hydration reaction of the cement rapidly proceeds in contact with water, so that the initial strength of the cement can be enhanced In addition, the long term strength of the cement hardener is also enhanced.
더욱이, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 상기 마이크로시멘트를 포함함으로써, 휨강도 및 압축강도가 우수하다.Further, the mortar composition for eco-friendly repair using seaweeds according to the present invention is excellent in bending strength and compressive strength by including the microcement.
상기 마이크로시멘트의 바람직한 블레인(blaine) 비표면적은 4,000 내지 12,000cm2/g, 보다 바람직하게는 7,000 내지 10,000cm2/g, 추천하기로는 약 8,000cm2/g인 것이 좋다.Preferred Blaine (blaine) a specific surface area of the micro-cement is preferably in from 4,000 to 12,000cm 2 / g, more preferably from 7,000 to 10,000cm 2 / g, like decided from about 8,000cm 2 / g.
본 발명에 따른 해조류는 보수용 몰탈 조성물을 구성하는 구성성분들의 결합을 촉진시키고, 균열을 방지할 수 있도록 하는 것으로서, 이러한 목적을 갖는 해조류라면 어떠한 것을 사용하여도 무방하다.The seaweed according to the present invention promotes bonding of components constituting the repair mortar composition and prevents cracks, and any seaweed having such a purpose may be used.
여기서, 상기 해조류는 세계적으로 약 8,000 종, 한국 근해에는 약 500여 종이 서식하고 있으므로, 이들 모두를 사용할 수 있지만, 바람직한 해조류로서 녹조류, 갈조류, 홍조류 또는 이들로부터 선택된 적어도 하나 이상을 사용하는 것이 좋다.Here, since about 8,000 species of algae live in the world and about 500 species live in the sea of Korea, all of them can be used, but it is preferable to use at least one of green algae, brown algae, red algae, or at least one of them as preferable algae.
바람직한 해조류로 대표적인 것은 녹조류로는 가시파래, 납작파래, 구멍갈파래, 홀파래, 매생이, 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말 등이 사용될 수 있으나 이에 한정되는 것은 아니며, 상기 갈조류로는 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳 등이 사용될 수 있으나 이에 한정되는 것은 아니며, 상기 홍조류로는 김, 우뭇가사리, 불등가사리, 불가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 부채살, 비단풀, 단박, 돌가사리, 석목, 작은톱니 지누아리 등이 사용될 수 있으나 이에 한정되는 것은 아니다.Examples of the preferable algae include, but are not limited to, green algae such as prickly pearl, flat pearl, perforated coral reef, hole pearl, mulberry, mulberry, The brown algae may be selected from the group consisting of seaweed, kelp, horsetail, leek, lobster, horsetail, seaweed, horsetail, moxa, rhubarb, It is not the red algae mentioned above. Examples of the red algae include red ginseng, red ginseng, red ginseng, starfish, kotoni, dog gambling, round ginseng, Stone scarf, gypsum, small sawtooth, and the like, but the present invention is not limited thereto.
특정 양태로서, 본 발명에 따른 해조류는 건조된 해조류, 분말 형태의 해조류 또는 끊여서 농축시킨 농축액 형태를 사용할 수도 있지만, 추천하기로는 농축액을 사용하는 것이 좋다.In a specific embodiment, seaweeds according to the present invention may be used in the form of dried seaweeds, seaweeds in the form of powders or concentrates obtained by concentrating the concentrates, but it is advisable to use concentrates.
바람직한 해조류의 사용량은 시멘트 100중량부를 기준으로 10 내지 60중량부인 것이 좋다.Preferably, the amount of the seaweed to be used is 10 to 60 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 메틸메타아크릴레이트(MMA: Methyl MethAcrylate)는 보수용 몰탈 조성물, 특정적으로 해조류를 이용한 친환경 보수용 몰탈 조성물이 우수한 접착력을 갖도록 하는 동시에, 우수한 바인더 물성 및 기계적 물성을 유지하여 타설 후 신속한 경화를 진행하여도 크랙 및 탈락현상을 현저하게 개선할 수 있다.Methyl methacrylate (MMA) according to the present invention can be applied to a mortar composition for maintenance, specifically, an eco-friendly mortar composition using seaweed, to have excellent adhesive strength and maintain excellent binder physical properties and mechanical properties, Cracks and dropouts can be remarkably improved even if rapid curing is carried out.
특정 양태로서, 본 발명에 따른 메틸메타아크릴레이트는 점도가 10 내지 1,000cps인 저점도 메틸메타크릴레이트(MMA) 수지 49 내지 70중량%와, 점도가 2,000 내지 20,000cps인 고점도 메틸메타크릴레이트(MMA) 20 내지 50중량%를 혼합하여 얻어지는 메틸메타크릴레이트 혼합물에 SIS(stylene isoprene stylene), SBR(stylene butadiene rubber), SBS(stylene butadiene stylene) 중에서 선택된 하나 이상의 혼합물 1 내지 10중량%를 혼합한 변성 메틸메타아크릴레이트를 사용할 수도 있다.In a particular embodiment, the methylmethacrylate according to the present invention comprises from 49 to 70% by weight of a low viscosity methylmethacrylate (MMA) resin having a viscosity of from 10 to 1,000 cps and a high viscosity methyl methacrylate having a viscosity of from 2,000 to 20,000 cps 1 to 10% by weight of a mixture of at least one selected from styrene isoprene styrene (SIS), styrene butadiene rubber (SBR) and styrene butadiene styrene (SBS) is mixed with a methyl methacrylate mixture obtained by mixing 20 to 50% Modified methyl methacrylate may also be used.
이때, 상기 SIS, SBR 및/또는 SBS의 함량이 1중량% 미만인 경우에는 투입시에 내충격성 저하로 인한 크랙이 발생할 수 있고, 10중량%를 초과하는 경우에는 변성 메틸메타크릴레이트 수지의 점도상승으로 인하여 작업성에 문제가 발생될 수 있기 때문에 바람직하지 못하다.When the content of SIS, SBR and / or SBS is less than 1% by weight, cracks may occur due to lowering of impact resistance at the time of charging. When the content exceeds 10% by weight, the viscosity of the modified methyl methacrylate resin Which may cause problems in workability.
바람직한 메틸메타아크릴레이트의 사용량은 시멘트 100중량부를 기준으로 20 내지 80중량부인 것이 좋다.The preferred amount of methylmethacrylate used is 20 to 80 parts by weight based on 100 parts by weight of cement.
본 발명에 따른 프리폴리머는 해조류를 이용한 친환경 보수용 몰탈 조성물이 시공면에 타설, 예를 들면 보수하고자 하는 시공면에 타설된 후 신속히 경화될 수 있도록 하는 고분자 수지로서, 이러한 목적을 갖는 당업계의 통상적인 프리폴리머라면 특별히 한정되지 않는다.The prepolymer according to the present invention is a polymer resin that enables an environmentally friendly repair mortar composition using seaweeds to be laid on a construction site, for example, to be quickly cured after being placed on a construction site to be repaired. Is not particularly limited.
바람직한 프리폴리머로는 폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.As the preferable prepolymer, it is preferable to use a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least one selected from these.
특정적으로, 본 발명에 따른 프리폴리머는 폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들 중 선택된 적어도 두 개 이상의 혼합물 25 내지 30중량%와 메틸렌 디페닐 디이소시아네이트 70 내지 75중량%를 반응시켜 제조한 폴리우레탄을 사용하는 것을 추천한다.Specifically, the prepolymer according to the present invention comprises from 25 to 30% by weight of a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least two thereof selected from the group consisting of methylene diphenyl diisocyanate 70 to 75 It is recommended to use polyurethane which is produced by reacting polyisocyanate in an amount of 1 to 50% by weight.
여기서, 상기 프리폴리머에 포함된 폴리올은 경화 전에는 유동성, 작업성에 영향을 주고, 경화 후에는 물리적, 화학적 성능에 영향을 주며, 과다하게 사용 시 경화 중 표면에 블리스터링(Blistering) 현상과 얼룩이 발생할 수 있으므로, 그 사용량을 적절히 조절하는 것이 바람직하며, 추천하기로는 시멘트 100중량부 기준으로, 10 내지 60중량부인 것이 좋다.Here, the polyol contained in the prepolymer affects fluidity and workability before curing, affects physical and chemical performance after curing, and blistering phenomenon and unevenness may occur on the surface during curing when the polyol is used excessively , It is preferable to appropriately adjust the amount of the cement to be used, and it is recommended that the amount of the cement is 10 to 60 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 경화제는 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 포함된 메틸메타아크릴레이트 및/또는 프리폴리머를 신속히 경화시키기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 경화제라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 시멘트 100중량부 기준으로 5 내지 30중량부를 사용하는 것을 추천한다.The curing agent according to the present invention is used for rapidly curing methyl methacrylate and / or prepolymer contained in the mortar composition for eco-friendly repair using the seaweeds. For this purpose, any of the curing agents conventionally used in the art can be used And it is recommended to use 5 to 30 parts by weight based on 100 parts by weight of cement.
바람직한 경화제로는 2-디에틸아미노에틸아민, N-부틸디에탄올아민, 2-디이소프로필아미노에틸아민, 3-디메틸아미노-1-프로필아민, 3-디에틸아미노프로필아민, 트리에탄올아민, 트리이소프로판올아민, 3-디부틸아미노프로필아민, 트리프로판올아민, 메틸아민, N,N-디메틸 에탄올아민, 사이클로헥실아민, 3-디메틸아미노프로, 헥사메틸렌 디이소시아네이트(HDI), 톨루엔 디이소시아네이트(TDI), 이소포론 디이소시아네이트(IPDI), 4,4' 메틸렌 비스(사이클로 헥실 이소시아네이트), 피마자유, 예를 들면 피마자유, 수소화피마자유 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.Preferred curing agents include 2-diethylaminoethylamine, N-butyldiethanolamine, 2-diisopropylaminoethylamine, 3-dimethylamino-1-propylamine, 3- diethylaminopropylamine, triethanolamine, tri N, N-dimethylethanolamine, cyclohexylamine, 3-dimethylaminopropane, hexamethylene diisocyanate (HDI), toluene diisocyanate (TDI), isopropanolamine, isopropanolamine, , Isophorone diisocyanate (IPDI), 4,4'-methylenebis (cyclohexylisocyanate), castor oil such as castor oil, hydrogenated castor oil, or a mixture of at least one selected from these.
여기서, 상기 프리폴리머를 경화시키기 위해서 사용되는 경화제로는 피마자유를 사용하는 것을 추천하는바, 바람직하게는 상기 경화제 전체 중량을 기준으로 10 내지 30중량%의 피마자유를 포함하는 것이 좋다.It is recommended to use castor oil as the curing agent used for curing the prepolymer. Preferably, it contains 10 to 30% by weight of castor oil based on the total weight of the curing agent.
특정적으로, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 보다 신속한 경화를 위해 부가적으로 경화촉진제를 더 포함할 수 있다.In particular, the eco-friendly mortar composition using seaweeds according to the present invention may further include a curing accelerator in order to accelerate curing.
이때, 상기 경화촉진제는 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부 기준으로 0.2 내지 2중량부를 포함할 수 있다.At this time, the curing accelerator may include 0.2 to 2 parts by weight based on 100 parts by weight of the mortar composition for eco-friendly repair using algae.
바람직한 경화촉진제로는 특별히 한정되는 것은 아니지만, 금속염계 코발트, 디메틸 아크릴 아마이드(dimethyl acrylamide), 아민계 촉진제 중에서 선택된 하나 이상의 혼합물을 사용하는 것이 좋다.The preferred curing accelerator is not particularly limited, but it is preferable to use at least one selected from metal salt cobalt, dimethyl acrylamide, and amine accelerator.
본 발명에 따른 고기능 파우더는 몰탈 조성물의 바인더 역할을 수행하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 고기능 파우더라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 아연분말, 벤토나이트 석영 중합체, 규사 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 5 내지 15중량부인 것이 좋다.The high-performance powder according to the present invention serves to perform a binder function of the mortar composition. Any high-performance powder commonly used in the art may be used for this purpose, but zinc powder, bentonite quartz polymer, It is preferable to use silica or a mixture thereof, and the amount thereof is preferably 5 to 15 parts by weight based on 100 parts by weight of cement.
또한, 상기 파우더의 입도는 특별히 제한되지 않지만, 수마이크로미터 또는 수나노미터 단위를 갖는 것을 추천한다.In addition, the particle size of the powder is not particularly limited, but it is recommended to have a particle size of several micrometers or several nanometers.
본 발명에 따른 소포제는 연행공기의 발생으로 인한 공기량의 증가를 감소시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 소포제라면 특별히 한정되지 않는다.The antifoaming agent according to the present invention is intended to reduce an increase in the amount of air due to the generation of entrained air, and is not particularly limited as long as it is a conventional antifoaming agent of the related art.
바람직한 소포제로는 등유, 파라핀 등과 같은 광유계 소포제, 동식물유, 참기름, 피마자유와 이들의 알킬렌옥사이드 부가물 등과 같은 유지계 소포제, 올레인산, 스테아린산과 이들의 알킬렌옥사이드 부가물 등과 간은 지방산계 소포제, 글리세린모노리시놀레이트, 알케닐호박산 유동체, 솔비톨모노라울에이트, 솔비톨트리올레이트, 천연 왁스 등과 같은 지방산 에스테르계 소포제, 폴리옥시알킬렌류, (폴리)옥시알킬에테르류, 아세틸렌에테르류, (폴리)옥시알킬렌알킬인산에스테르류, (폴리)옥시알킬렌알킬아민류,(폴리)옥시알킬렌아미드 등과 같은 옥시알킬렌계 소포제, 옥틸알콜, 헥사데실알콜, 아세틸렌알콜, 글리콜류 등과 같은 알콜계 소포제, 아크릴레이트폴리아민 등과 같은 아미드계 소포제, 인산트리부틸, 나트륨옥틸포스페이트 등과 같은 인산에스테르계 소포제, 알루미늄스테아레이트, 칼슘올레이트 등과 같은 금속비누계 소포제, 디메틸실리콘유, 실리콘 페이슷, 실리콘 에멀젼, 유기변성 폴리실록산(디메틸폴리실록산 등의 폴리오르가노실록산). 플루오로실리콘유 등과 같은 실리콘계 소포제로 이루어진 군에서 선택되는 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니다.Preferred examples of defoaming agents include mineral oil defoaming agents such as kerosene and paraffin, preservative defoaming agents such as animal and vegetable oils, sesame oil, castor oil and castor oil and their alkylene oxide adducts, oleic acid, stearic acid and alkylene oxide adducts thereof, Fatty acid ester type antifoaming agents such as antifoaming agents, glycerin monoricinolate, alkenyl succinic acid liquid, sorbitol monolaurate, sorbitol trioleate, and natural wax, polyoxyalkylene ethers, (poly) oxyalkyl ethers, acetylene ethers, Oxyalkylene antifoaming agents such as (poly) oxyalkylene alkylphosphoric acid esters, (poly) oxyalkylene alkylamines and (poly) oxyalkylene amides, alcohol-based defoaming agents such as octyl alcohol, hexadecyl alcohol, acetylene alcohol, Amide antifoaming agents such as acrylate polyamines and the like, phosphorus tributyl phosphate, sodium octyl phosphate and the like Metal soap defoaming agents such as acid ester defoaming agents, aluminum stearate, calcium oleate, and the like; dimethyl silicone oils, silicone fats, silicone emulsions, and organic modified polysiloxanes (polyorganosiloxanes such as dimethylpolysiloxane). And silicone-based antifoaming agents such as fluorosilicone oil, etc., but is not limited thereto.
상기 소포제의 사용량은 특별히 제한되는 것은 아니지만, 바람직하게는 시멘트 100중량부를 기준으로 5 내지 10중량부인 것이 좋다.The amount of the antifoaming agent to be used is not particularly limited, but is preferably 5 to 10 parts by weight based on 100 parts by weight of cement.
본 발명에 따른 실리카퓸(silica fume)은 금속 실리콘 또는 규소 합금을 제조할 때에 발생하는 부산물로서, 무정형 이산화규소이다. The silica fume according to the present invention is a by-product produced when a metal silicon or a silicon alloy is produced, and is amorphous silicon dioxide.
상기 실리카퓸은 시멘트 100중량부를 기준으로, 10 내지 30중량부를 사용하는 것이 바람직하다.The silica fume is preferably used in an amount of 10 to 30 parts by weight based on 100 parts by weight of the cement.
특정 양태로서, 본 발명에 따란 실리카퓸은 지르코늄 실리카퓸을 포함할 수 있다.In a particular embodiment, the silica fume according to the present invention may comprise zirconium silica fume.
이때, 상기 지르코늄 실리카퓸은 지르코니아의 제조시 발생하는 부산물로서, 3 내지 5중량%의 산화지르코늄을 포함하고, 200 내지 300kg/m3의 단위용적중량을 가지며, 100,000 내지 150,000cm2/g의 분말도와 0.3 내지 1마이크로미터의 입자크기를 갖는 것이 바람직하다.At this time, the zirconium silica fume is a by-product generated in the production of zirconia, which contains zirconium oxide in an amount of 3 to 5% by weight and has a unit volume weight of 200 to 300 kg / m 3 and a powder of 100,000 to 150,000 cm 2 / g And a particle size of from 0.3 to 1 micrometer.
여기서, 상기 실리카퓸은 그 입자크기가 시멘트 입자크기 보다 작아 아스콘 조성물 등에 첨가하면 점성이 증가하고 높은 압축 강도를 얻을 수 있다.When the particle size of the silica fume is smaller than the cement particle size, the viscosity of the silica fume increases and the high compressive strength can be obtained.
또한, 상기 지르코늄 실리카퓸은 입자크기가 커서 시멘트 입자사이에 잘 분산되어 점성을 낮추고 유동성을 향상시킬 수 있다.In addition, the zirconium silica fume has a large particle size and is well dispersed among the cement particles, thereby lowering viscosity and improving fluidity.
또한, 상기 지르코늄 실리카퓸은 고온에서 생성되어 포졸란 활성이 우수한 비정질 상태이며 산화규소 함량이 높아 강도 증가에 유리한 점이 있다.The zirconium silica fumarate is an amorphous zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium zirconium
이에, 본 발명에 따른 실리카퓸은 실리카퓸, 예를 들면 무정형 이산화규소 및 지르코늄 실리카퓸을 혼합하여 사용 가능하며, 이러한 경우 지르코늄 실리카퓸은 전체 실리카퓸의 중량 기준으로 10 내지 70중량% 범위에서 사용되는 것이 좋다.Thus, the silica fume according to the present invention can be used by mixing silica fume, for example, amorphous silicon dioxide and zirconium silica fume. In this case, the zirconium silica fume is used in a range of 10 to 70% by weight based on the weight of the total silica fume .
본 발명에 따른 저수축제는 해조류를 이용한 친환경 보수용 몰탈 조성물이 수축되는 것을 방지하기 위한 것으로서, 이러한 목적을 위한 저숙축제라면 특별히 한정되지 않지만, 바람직하게는 폴리에스터계 저수축제, 특정적으로 불포화 폴리에스터 수지로 이루어진 저수축제를 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 1 내지 10중량부를 사용하는 것이 바람직하다.The water-reducing agent according to the present invention is intended to prevent shrinkage of an eco-friendly mortar composition using algae, and is not particularly limited as long as it is a low-melting agent for this purpose. Preferably, it is a polyester- It is preferable to use a water-reducing agent composed of an ester resin, and the amount thereof used is preferably 1 to 10 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 열화방지제는 해조류를 이용한 친환경 보수용 몰탈 조성물의 열화를 방지하기 위한 것이다.The deterioration inhibitor according to the present invention is for preventing deterioration of the mortar composition for eco-friendly repair using algae.
특히, 상기 열화방지제, 특정적으로 오존열화방지제는 6PPD (N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및/또는 TAPDT(2,4,6-tris-(N-Particularly, the deterioration inhibitor, specifically the ozone deterioration inhibitor, is preferably selected from the group consisting of N- (1,3-dimethylutyl) -N'-phenyl-p-phenylenediamine and / or TAPDT (2,4,6-
1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)를 포함하여 수중에서 활성화된 오존라디칼의 산화작용에 의한 몰탈 조성물의 촉진열화작용을 오존열화방지제 분자구조에 아민과 결합된 방향족 고리화합물 거대분자의 이중결합부분이 자유전자 이동현상에 의해 활성화된 오존라디칼과 상쇄되어 보수용 몰탈 조성물의 열화 방지 및 열화를 지연시킬 수 있다.The effect of accelerated deterioration of the mortar composition due to oxidation of the ozone radicals activated in water, including 1,4-dimethylpentyl-p-phenylenediamino) -1,3,5-triazine, The double bond portion of the aromatic ring compound macromolecule may be counteracted with the ozone radical activated by the free electron transfer phenomenon to delay deterioration prevention and deterioration of the repair mortar composition.
즉, 상기 오존열화방지제는 페닐렌디아민(Phenylenediamine-based)계 왁스를 사용할 수 있고, 6PPD와 TAPDT을 포함하는 혼합수지 조성을 사용하거나 라디칼 생성이 활발한 방향족 폴리아민계 등을 사용할 수 있으며, 특히 페닐렌디아민계를 사용하는 것이 바람직하다.That is, the ozone deterioration inhibitor may be a phenylenediamine-based wax, a mixed resin composition containing 6PPD and TAPDT, or an aromatic polyamine system in which radical generation is active. In particular, phenylenediamine- It is preferable to use a system.
바람직한 열화방지제의 사용량은 시멘트 100중량부를 기준으로 1 내지 5중량부인 것이 좋다.The preferred amount of the deterioration inhibitor to be used is 1 to 5 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 감수제는 시멘트 입자를 대전시켜 각 입자를 분산시키기고, 감수작용으로 단위수량을 저감시켜 강도를 증가시키기 위한 것으로서, 이를 부가함에 따라 시멘트의 사용량을 감소시킬 수 있다.The water reducing agent according to the present invention is intended to disperse each particle by charging cement particles and to reduce the unit water by the water reducing action to increase the strength, and the amount of the cement to be used can be reduced by adding the water reducing agent.
상기 감수제는 당업계에서 통상적으로 사용하는 감수제라면 특별히 한정되지 않지만, 바람직하게는 멜라민형 및/또는 아미노 술폰산형 감수제를 사용하는 것이 좋다.The water reducing agent is not particularly limited as long as it is a water reducing agent usually used in the art, but preferably a melamine type and / or aminosulfonic acid type water reducing agent is used.
바람직한 감수제의 사용량은 시멘트 100중량부 기준으로 1 내지 5중량부인 것이 좋다.The amount of the water reducing agent is preferably 1 to 5 parts by weight based on 100 parts by weight of the cement.
특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 유해물질의 용출을 배제시키면서 유동성을 향상시키고, 속성경화가 가능하면서 충분한 압축강도 및 휨강도를 가질 수 있도록 하는 슬래그를 더 포함할 수 있다.In a specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further include a slag which improves fluidity while eliminating the release of harmful substances, and has sufficient compressive strength and bending strength while allowing property hardening have.
바람직한 슬래그로는 제강 슬래그(PS Ball) 및/또는 고로 슬래그를 사용할 수 있다. The preferred slag may be steel-making slag (PS ball) and / or blast furnace slag.
이때, 상기 제강 슬래그 및/또는 고로 슬래그는 폐기 처분되던 제강 및/또는 고로 슬래그를 회수하여 재활용함으로써 부수적으로 자원 재활용 효과를 얻을 수 있다.At this time, the steelmaking slag and / or the blast furnace slag may be recycled by recycling steelmaking and / or blast furnace slag to be recycled.
특정적으로, 본 발명에 따른 제강 슬래그 및/또는 고로 슬래그는 제철 또는 제강공정에서 부산물로 발생하는 것을 포집하여 사용할 수 있다.Specifically, the steelmaking slag and / or blast furnace slag according to the present invention can be used by collecting what is generated as a by-product in a steelmaking or steelmaking process.
바람직한 슬래그의 사용량은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부 기준으로 20 내지 30중량부인 것이 좋고, 슬래그의 분말도는 3,700 내지 4,000cm2/g, 바람직하게는 약 3,850cm2/g이고, 밀도는 2.9 내지 3.5g/cm3, 바람직하게는 약 3.1g/cm3인 것이 좋다.The amount of the preferred slag may be environmentally friendly repair mortar composition 100 parts by weight based on the wife 20 to 30 parts by weight for using the marine algae, the fineness of the slag is 3,700 to 4,000cm 2 / g, preferably from about 3,850cm 2 / g, The density is preferably 2.9 to 3.5 g / cm 3 , and preferably about 3.1 g / cm 3 .
다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 몰탈 조성물의 압축강도, 휨강도 및 균열저항성 등을 향상시키기 위하여, 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부의 파이버(fiber)를 더 포함할 수 있다. In another specific embodiment, in order to improve the compressive strength, the bending strength and the crack resistance of the mortar composition, the mortar composition for eco-friendly repair using seaweeds according to the present invention may contain 1 to 10 parts by weight, based on 100 parts by weight of the mortar composition for eco- And may further include a fiber of weight part.
여기서, 상기 파이버는 당업계의 통상적인 파이버라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 카본파이버, 합성섬유, 유리섬유, 비닐섬유 및 아라미드 섬유, 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다. The fiber may be any fiber as long as it is a conventional fiber in the art, but it is preferable to use at least one of carbon fiber, synthetic fiber, glass fiber, vinyl fiber and aramid fiber or a mixture thereof good.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 실온에서 효과적으로 경화하고 내열성, 저온 성능, 내화학성, 내용매성 및 내유성과 같은 개선된 특성을 제공하기 위하여 아미노기 함유 실록산(Aminofunctional siloxan)을 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention is an aminofunctional siloxane for effectively curing at room temperature and providing improved properties such as heat resistance, low temperature performance, chemical resistance, solvent resistance and oil resistance siloxan).
상기 아미노 함유 실록산은 특별히 제한되는 것은 아니며, 일례로서 아미노메틸폴리디메틸실록산을 들 수 있으며, 그 사용량은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부를 기준으로 3 내지 10중량부인 것을 추천한다.The amino-containing siloxane is not particularly limited, and examples thereof include aminomethylpolydimethylsiloxane. The amount of the amino-containing siloxane is preferably 3 to 10 parts by weight based on 100 parts by weight of the eco-friendly mortar composition using algae.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 몰탈 혼합시 물을 흡수하여 모르타르의 작업성을 좋게 해주고, 이로 인하여 몰탈 중의 단위 수량을 감소시키고 강도증진에 탁월한 흡수성 폴리머를 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention absorbs water during mortar mixing to improve workability of the mortar, thereby reducing the unit water content in the mortar and improving the strength of the absorbent polymer .
상기 흡수성 폴리머로는 폴리아크릴산염 및 그 유도체 및 폴리에틸렌옥사이드 유도체에서 선택된 어느 하나 이상이 사용될 수 있으며, 그 사용량은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.2 내지 10중량부인 것을 추천한다.The water absorbent polymer may be at least one selected from the group consisting of a polyacrylate, a derivative thereof and a polyethylene oxide derivative. The amount of the water absorbent polymer to be used is preferably 0.2 to 10 parts by weight based on 100 parts by weight of an eco-friendly mortar composition for repairing algae.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 몰탈의 접착성 및 부착강도 향상을 위하여 옥틸트리에톡시실란을 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further contain octyltriethoxysilane for improving adhesion and adhesion strength of the mortar.
상기 옥틸트리에톡시실란은 단량체 형태로 사용가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋고, 그 사용량은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 5중량부인 것을 추천한다.The octyltriethoxysilane may be used in the form of a monomer. The molecular weight of the monomer is not particularly limited, but is preferably 150 to 450 Da. The amount of the octyltriethoxysilane to be used is 100 parts by weight of an eco- Is preferably 1 to 5 parts by weight.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 작업시간 및/또는 강도발현 속도 조절을 위해 지연제를 더 포함할 수 있으며, 그 사용량은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.05 내지 0.2중량부인 것을 추천한다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further comprise a retarding agent for controlling the working time and / or the rate of strength development, and the amount of the mortar composition for eco- 0.05 to 0.2 parts by weight based on 100 parts by weight.
상기 지연제로서 바람직한 것은 타르타르산, 구연산, 글루콘산 등의 카르복시산 또는 그 염으로 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다. Preferred as the retarder is a carboxylic acid such as tartaric acid, citric acid, gluconic acid, or a salt thereof, or a mixture of at least one selected from these.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부 기준으로 1 내지 10중량부의 평활제를 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further contain 1 to 10 parts by weight of a smoothing agent based on 100 parts by weight of an eco-friendly mortar composition for repairing algae.
상기 평활제는 페이스트의 셀프 레벨링(자기충전성능)을 개선하기 위하여서 첨가되는 것으로, 폴리옥사이드계, 우레탄계 및 폴리카본산계 중에서 선택된 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 통상적으로 사용되는 종류가 사용될 수 있다.The smoothing agent is added in order to improve the self-leveling (self-charging performance) of the paste, and any one or more selected from the group consisting of a polyoxide system, a urethane system and a polycarboxylic acid system may be used. However, May be used.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 보수용 몰탈 조성물 100중량부 기준으로 1 내지 5중량부의 수축저감제를 더 포함할 수 있다. In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further comprise 1 to 5 parts by weight of a shrinkage reducing agent based on 100 parts by weight of the repair mortar composition.
상기 수축저감제는 몰탈 조성물 경화체의 건조수축을 방지하기 위하여 첨가되는 것으로, 폴리에테르계, 에틸렌글리콜 및 프로필렌글리콜 중에서 선택된 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니며, 당업계에서 통상적으로 사용되는 종류가 사용될 수 있다.The shrinkage reducing agent is added in order to prevent drying shrinkage of the mortar composition cured product, and any one or more selected from among polyether type, ethylene glycol and propylene glycol may be used, but not limited thereto, Can be used.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부 기준으로 유리비드 10 내지 50중량부를 사용할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may use 10 to 50 parts by weight of glass beads on the basis of 100 parts by weight of the mortar composition for eco-friendly repair using algae.
상기 유리 비드(glass bead)는 유리 비드의 볼 베어링 효과(ball bearing effect)에 의하여 매우 우수한 유동성을 제공하여 본 발명의 보수용 몰탈 조성물이 좁은 틈 및 깊숙한 곳까지 도달할 수 있도록 침투성을 증가시키는 역할을 하며, 다른 혼합물에 대하여 우수한 분산성을 제공한다. The glass beads provide very good flowability by the ball bearing effect of the glass beads, thereby increasing the permeability so that the repair mortar composition of the present invention can reach narrow gaps and deep places And provides excellent dispersibility for other mixtures.
더욱이, 상기 유리비드는 시멘트, 수지 및 건조상태의 혼합물이 장기 보관된 후에도 단순 교반만으로 잘 혼합되는 우수한 저장성을 나타내도록 하며, 강도 및 경도가 높아 보수용 몰탈 조성물의 경화체에 대하여 우수한 강도 및 내충격성을 제공하고, 높은 비열로 경화시 발생하는 수화열을 흡수하여 대량시공을 가능하게 할 수 있다.Furthermore, the glass beads are excellent in storage stability that the mixture of cement, resin and dry state is well mixed even after long-term storage, and exhibit excellent strength and hardness, so that the glass beads have excellent strength and impact resistance And it is possible to absorb a heat of hydration which occurs upon curing with a high specific heat to enable mass production.
상기 유리 비드는 다양한 입자 크기의 것을 사용할 수 있으며, 유리, 파유리, 유리 섬유, 또는 유리 커렛 등을 분쇄하여 얻는 유리 분말을 처리하여 얻어지는 것으로, 유리 조성은 A, C, E, 내알칼리성 유리 분말 조성 등 수지 및 시멘트와 상용성이 있는 것이라면 특별히 한정되지 않는다.The glass beads having various particle sizes can be used. The glass beads can be obtained by treating a glass powder obtained by grinding a glass, a wave glass, a glass fiber, a glass cut or the like. The glass composition includes A, C, E, It is not particularly limited as long as it is compatible with resin and cement.
상기 유리 비드는 구형, 타원형, 또는 이에 준하는 모든 형상의 유리 비드가 사용될 수 있으며, 다양한 크기가 분포된 것부터 일정한 크기만을 선별한 것까지 모두 사용할 수 있다.The glass beads may be spherical, elliptical, or all kinds of glass beads of the same type, and they may be used in various sizes ranging from a uniform size to a selected one.
상기 유리 비드의 입경은 시공 대상에 따라서 적절히 선정하여 사용할 수 있으며, 바람직하게는 1 ㎛ 내지 3 ㎜인 것이 사용될 수 있다. 또한 이들은 수 ㎛의 작은 입도와 수 ㎜의 큰 입도의 비드들의 조합에 의하여 다양한 형태 및 물성을 나타내게 할 수 있다. 그러나, 상기 유리 비드의 입경이 3 ㎜를 초과할 경우에는 분산성이 낮아지거나 효율적으로 사용될 수 없다.The particle diameter of the glass beads can be appropriately selected according to the object to be applied and can be used, and preferably 1 mu m to 3 mm can be used. Also, they can exhibit various shapes and properties by combining beads having a small particle size of several mu m and a large particle size of several millimeters. However, when the particle size of the glass beads exceeds 3 mm, the dispersibility is lowered or can not be used efficiently.
특히, 상기 유리 비드는 몰탈이나 콘크리트의 사용량이 많을 경우에는 입도가 큰 비드를 상대적으로 많은 양으로 사용되는 것이 바람직하고, 몰탈의 사용량이 적을 경우에는 입도가 작은 비드를 많은 양으로 사용하는 것이 바람직하다.In particular, when the amount of mortar or concrete used is large, the glass beads are preferably used in a relatively large amount, and when the amount of mortar used is small, it is preferable to use a small amount of beads in a large amount Do.
또 다른 특정 양태로서, 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물은 해조류를 이용한 친환경 보수용 몰탈 조성물 100중량부 기준으로 첨가제 0.1 내지 5중량부를 더 포함할 수 있다.In another specific embodiment, the mortar composition for eco-friendly repair using seaweeds according to the present invention may further include 0.1 to 5 parts by weight of an additive based on 100 parts by weight of an eco-friendly mortar composition for repairing algae.
이때, 상기 첨가제는 당업계에서 통상적으로 사용되는 첨가제라면 특별히 한정되지 않지만, 바람직하게는 안정제, 노화방지제(age-protecting agent), 항산화제, 오존화 방At this time, the additive is not particularly limited as long as it is a commonly used additive in the art, but it is preferably a stabilizer, an age-protecting agent, an antioxidant,
지제, 광 보호제(light protection agent), 자외선 안정제, 자외선 흡수제, 무기 열안정제, 유기 열안정제, 광라이트너(optical lightener), 가공보조제(processing aids), 유동보조제(flow aid), 윤활제, 성형-이형제(mould-release agent), 연화제 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.
Light stabilizers, light stabilizers, optical lighteners, processing aids, flow aids, lubricants, shaping agents, light stabilizers, UV stabilizers, UV absorbers, A mold-release agent, a softening agent, or a mixture of at least one selected from these.
이와 같은 구성을 갖는 본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물의 시공방법을 설명하면 다음과 같다. 여기서, 하기 시공방법은 해조류를 이용한 친환경 보수용 몰탈 조성물의 일 시공양태로서, 이에 한정되지 않고, 당업계의 통상적인 보수용 몰탈 조성물의 시공방법이라면 어떠한 것을 사용하여도 무방하다.A construction method of the mortar composition for eco-friendly repair using the seaweed according to the present invention having the above-described structure will be described as follows. Herein, the following method is a construction method of an eco-friendly repair mortar composition using seaweeds, but not limited thereto, and any method may be used as long as it is a conventional method of constructing a repair mortar composition in the art.
본 발명에 따른 해조류를 이용한 친환경 보수용 몰탈 조성물 시공방법은 시공 대상표면의 이물질을 제거하는 이물질 제거단계;A method for constructing an eco-friendly repair mortar composition using seaweeds according to the present invention comprises: a foreign matter removing step of removing foreign matters on a surface of a work subject;
상기 이물질 제거단계가 종료된 표면에 시멘트 100중량부를 기준으로, 해조류 10 내지 60중량부, 메틸메타아크릴레이트 20 내지 80중량부, 프리폴리머 10 내지 60중량부,경화제 5 내지 30중량부, 고기능성 파우더 5 내지 15중량부, 소포제 5 내지 10중량부, 실리카퓸 10 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 적층하는 적층단계; 10 to 60 parts by weight of algae, 20 to 80 parts by weight of methyl methacrylate, 10 to 60 parts by weight of a prepolymer, 5 to 30 parts by weight of a curing agent, 10 to 60 parts by weight of a high- 5 to 15 parts by weight of an antifoaming agent, 5 to 10 parts by weight of a defoaming agent, 10 to 30 parts by weight of a silica fume, 1 to 10 parts by weight of a water reducing agent, 1 to 5 parts by weight of a deterioration inhibitor and 1 to 5 parts by weight of a water reducing agent A laminating step of laminating the repair mortar composition;
상기 적층단계가 종료된 후 해조류를 이용한 친환경 보수용 몰탈 조성물을 경화하는 경화단계; 및 A curing step of curing the eco-friendly repair mortar composition using seaweeds after the laminating step is completed; And
상기 경화단계가 종료된 후 시공면을 건조시키는 건조단계를 포함한다.
And drying the dried surface after the curing step is completed.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
[실시예 1][Example 1]
포틀랜드 시멘트 100g, 해조류로서 다시마 30g, 메틸메타아크릴리에트 40g, 폴리에테르 폴리올 30g, 2-디에틸아미노에틸아민 15g, 아연분말 10g, 글리세린모노리시놀레이트 7g, 지르코늄 실리카퓸 15g, 불포화 폴리에스터 수지로 이루어진 저수축제 5g, 6PPD 2.5g 및 아미노 술폰산형 감수제 2.5g을 혼합하여 해조류를 이용한 친환경 보수용 몰탈 조성물을 제조하였다.
100 g of Portland cement, 30 g of seaweed as seaweed, 40 g of methyl methacrylate, 30 g of polyether polyol, 15 g of 2-diethylaminoethylamine, 10 g of zinc powder, 7 g of glycerin monoricinolate, 15 g of zirconium silica fumarate, , 2.5 g of 6PPD and 2.5 g of aminosulfonic acid type water reducing agent were mixed to prepare an eco-friendly mortar composition using algae.
[실시예 2][Example 2]
실시예 1과 동일한 방법으로 실시하되, 포틀랜드 시멘트 100g 대신 마이크로시멘트 100g을 사용하여 실시하였다.
The procedure of Example 1 was repeated except that 100g of microcement was used instead of 100g of Portland cement.
[실시예 3][Example 3]
실시예 1과 동일한 방법으로 실시하되, 해조류로서 다시마 30g 대신 작은톱니 지누아리 30g을 사용하여 실시하였다.
The same procedure as in Example 1 was carried out except that 30 g of tortoise agar instead of 30 g of kelp was used as seaweed.
[실시예 4][Example 4]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 3,850cm2/g의 분말도와 3.1g/cm3의 밀도를 갖는 제강 슬래그 60g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 60 g of steel-making slag having a density of 3,850 cm 2 / g and a density of 3.1 g / cm 3 was further added to the mortar composition for eco-friendly repair using the seaweeds.
[실시예 5][Example 5]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 카본파이버 12g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 12 g of carbon fiber was further added to the mortar composition for eco-friendly repair using the algae.
[실시예 6][Example 6]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 폴리옥사이드계를 포함하는 평활제 6g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was conducted except that 6 g of a smoothing agent containing a polyoxide system was further added to the mortar composition for eco-friendly remediation using the algae.
[실시예 7][Example 7]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 폴리에테르계를 포함하는 수축저감제 6g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 6 g of a shrinkage reducing agent containing polyether was further added to the mortar composition for eco-friendly repair using the seaweeds.
[실시예 8][Example 8]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 아미노메틸폴리디메틸실록산 9g을 더 추가하여 실시하였다.The same procedure as in Example 1 was carried out except that 9 g of aminomethyl polydimethylsiloxane was further added to the mortar composition for eco-friendly repair using the algae.
[실시예 9][Example 9]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 옥틸트리에톡시실란 8g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 8 g of octyltriethoxysilane was further added to the mortar composition for eco-friendly repair using the seaweeds.
[실시예 10][Example 10]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 흡수성폴리머로서 폴리아크릴산염 10g을 더 추가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 10 g of polyacrylate as an absorbent polymer was further added to the mortar composition for eco-friendly repair using the seaweeds.
[실시예 11][Example 11]
실시예 1과 동일한 방법으로 실시하되, 상기 해조류를 이용한 친환경 보수용 몰탈 조성물에 약 10마이크로미터 크기의 유리비드 40g을 더 추가하여 실시하였다
The same procedure as in Example 1 was carried out except that 40 g of glass beads having a size of about 10 micrometers was further added to the mortar composition for eco-friendly remediation using the algae
[비교예 1][Comparative Example 1]
실시예 1과 동일한 방법으로 실시하되, 해조류인 다시마 및 메틸메타아크릴레이트를 제외하고 실시하였다.
The same procedure as in Example 1 was carried out except that sea tangle kelp and methyl methacrylate were excluded.
[비교예 2][Comparative Example 2]
실시예 1과 동일한 방법으로 실시하되, 폴리에테르 폴리올 및 2-디에틸아미노에틸아민을 제외하고 실시하였다.
The procedure of Example 1 was repeated except that polyether polyol and 2-diethylaminoethylamine were excluded.
[비교예 3][Comparative Example 3]
실시예 1과 동일한 방법으로 실시하되, 메틸메타아크릴레이트, 폴리에테르 폴리올 및 2-디에틸아미노에틸아민을 제외하고 실시하였다.
Was carried out in the same manner as in Example 1 except that methyl methacrylate, polyether polyol and 2-diethylaminoethylamine were excluded.
[실험][Experiment]
실시예 및 비교예에 따라 제조된 조성물을 시공면에 도포한 후 기계적 물성, 예를 들면 겔타임, 보수성, 압축강도, 휨강도, 부착강도 등을 측정하였다.The compositions prepared according to the examples and comparative examples were applied to a surface to be dried, and mechanical properties such as gel time, water retention, compressive strength, bending strength and adhesion strength were measured.
그 결과를 표 1로 나타냈다.
The results are shown in Table 1.
표 1에 나타난 바와 같이, 실시예 1 내지 실시예 11에 따라 제조된 해조류를 이용한 친환경 보수용 몰탈 조성물은 압축강도와 휨강도가 높은 것으로 나타났지만, 비교예1 내지 비교예3은 6시간이 지나도 겔화가 이루어지지 않을 뿐만 아니라, 압축강도와 휨강도 및 부착강도가 실시예들과 비교하여 좋지 않은 것으로 나타났다.
As shown in Table 1, the mortar compositions for eco-friendly repair using seaweeds prepared according to Examples 1 to 11 showed high compressive strength and flexural strength, while Comparative Examples 1 to 3 showed gelation And the compressive strength, the bending strength and the bond strength were not as good as those of the examples.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the scope of the present invention.
Claims (5)
가시파래, 납작파래, 구멍갈파래, 홀파래, 매생이, 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 불가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 부채살, 비단풀, 단박, 돌가사리, 석목, 작은톱니 지누아리 또는 이들의 혼합물인 해조류 10 내지 60중량부;
메틸메타아크릴레이트 20 내지 80중량부;
폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 프리폴리머 10 내지 60중량부;
경화제 5 내지 30중량부;
고기능성 파우더 5 내지 15중량부;
소포제 5 내지 10중량부;
실리카퓸 10 내지 30중량부;
저수축제 1 내지 10중량부;
열화방지제 1 내지 5중량부; 및
감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물에,
카본파이버를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,
아미노메틸폴리디메틸실록산을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 3 내지 10중량부로 더 포함하며,
흡수성 폴리머로서 폴리아크릴산염을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.2 내지 10중량부로 더 포함하고,
옥틸트리에톡시실란을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 5중량부로 더 포함하며,
지연제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.05 내지 0.2중량부로 더 포함하고,
폴리옥사이드계 평활제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고,
유리 비드를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 10 내지 50중량부로 더 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물.
Based on 100 parts by weight of cement,
It is a kind of fish in the sea. It is a fish which is a kind of fish. It is a fish, It is also known that it is a kind of gambia which is a kind of gambia which is a kind of gambia. 10 to 60 parts by weight of algae which are hair, true gambling, kashiiu, fan, silkworm, short twig, rock scarf, gypsum, small sawtooth or mixtures thereof;
20 to 80 parts by weight of methyl methacrylate;
10 to 60 parts by weight of a prepolymer which is a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least one selected from these;
5 to 30 parts by weight of a curing agent;
5 to 15 parts by weight of high-performance powder;
5 to 10 parts by weight of a defoaming agent;
10 to 30 parts by weight of silica fume;
1 to 10 parts by weight of a water reducing festival;
1 to 5 parts by weight of an anti-deterioration agent; And
1 to 5 parts by weight of a water reducing agent is added to an eco-friendly repair mortar composition using algae,
The carbon fiber further comprises 1 to 10 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition,
Further comprising aminomethyl polydimethylsiloxane in an amount of 3 to 10 parts by weight based on 100 parts by weight of an eco-friendly mortar composition,
Further comprising 0.2 to 10 parts by weight of a polyacrylate as the water absorbent polymer based on 100 parts by weight of the eco-friendly repair mortar composition,
Octyltriethoxysilane is further contained in an amount of 1 to 5 parts by weight based on 100 parts by weight of an eco-friendly mortar composition,
Further comprising 0.05 to 0.2 parts by weight based on 100 parts by weight of the mortar composition for eco-friendly repair,
Further comprising 1 to 10 parts by weight of a polyoxide-based smoothing agent based on 100 parts by weight of an eco-friendly repair mortar composition,
Wherein the glass beads further comprise 10 to 50 parts by weight based on 100 parts by weight of the mortar composition for eco-friendly repair.
상기 이물질 제거단계가 종료된 표면에 시멘트 100중량부를 기준으로, 가시파래, 납작파래, 구멍갈파래, 홀파래, 매생이, 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 불가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 부채살, 비단풀, 단박, 돌가사리, 석목, 작은톱니 지누아리 또는 이들의 혼합물인 해조류 10 내지 60중량부, 메틸메타아크릴레이트 20 내지 80중량부, 폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들로부터 선택된 적어도 하나 이상의 혼합물인 프리폴리머 10 내지 60중량부, 경화제 5 내지 30중량부, 고기능성 파우더 5 내지 15중량부, 소포제 5 내지 10중량부, 실리카퓸 10 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 감수제 1 내지 5중량부를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물에, 카본파이버를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 아미노메틸폴리디메틸실록산을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 3 내지 10중량부로 더 포함하며, 흡수성 폴리머로서 폴리아크릴산염을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.2 내지 10중량부로 더 포함하고, 옥틸트리에톡시실란을 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 5중량부로 더 포함하며, 지연제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 0.05 내지 0.2중량부로 더 포함하고, 폴리옥사이드계 평활제를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 1 내지 10중량부로 더 포함하고, 유리 비드를 친환경 보수용 몰탈 조성물 100중량부를 기준으로 10 내지 50중량부로 더 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물을 적층하는 적층단계;
상기 적층단계가 종료된 후 해조류를 이용한 친환경 보수용 몰탈 조성물을 경화하는 경화단계; 및
상기 경화단계가 종료된 후 시공면을 건조시키는 건조단계를 포함하는 해조류를 이용한 친환경 보수용 몰탈 조성물의 시공방법.
A foreign matter removing step of removing foreign matter on a surface to be applied;
The surface on which the foreign matter removing step has been completed is coated with 100 parts by weight of cement based on 100 parts by weight of cement based on 100 parts by weight of cement based on 100 parts by weight of cement, , Starfish, starfish, starfish, starfish, starfish, starfish, starfish, mackerel, starfish, starfish, starfish, starfish, starfish, 10 to 60 parts by weight of seaweed which is a mixture of gambling, barking, round starch, bamboo shoots, bamboo shoots, chopped bamboo shoots, crocodile bamboo shoots, true gambling, bamboo shoots, , 20 to 80 parts by weight of methyl methacrylate, 10 to 60 parts by weight of a prepolymer which is a polyether polyol, a polyester polyol, a copolymer polyol, ethylene glycol, propylene glycol or a mixture of at least one selected from these, 5 to 30 parts by weight of a high-performance powder, 5 to 10 parts by weight of a defoaming agent, 10 to 30 parts by weight of a silica fume, 1 to 10 parts by weight of a water-reducing agent, 1 to 5 parts by weight of a deterioration inhibitor, To 5 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, the aminomethyl polydimethyl siloxane is added to the eco-friendly repair mortar composition 100 Further comprising 3 to 10 parts by weight based on 100 parts by weight of the water-absorbing polymer, wherein the polyacrylate is further contained in an amount of 0.2 to 10 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, and octyltriethoxysilane is used as an eco- 1 to 5 parts by weight based on 100 parts by weight of the mortar composition for environmental protection, wherein the retarder is 0.05 to 0.2 parts by weight based on 100 parts by weight of the eco- Wherein the glass beads are further contained in an amount of 10 to 50 parts by weight based on 100 parts by weight of the eco-friendly repair mortar composition, wherein the glass beads are further contained in an amount of 1 to 10 parts by weight based on 100 parts by weight of the eco- A laminating step of laminating an eco-friendly repair mortar composition containing seaweeds;
A curing step of curing the eco-friendly repair mortar composition using seaweeds after the laminating step is completed; And
And a drying step of drying the dried surface after the curing step is completed.