KR101547306B1 - Artificial soil for planting plants and manufacturing method of the same - Google Patents

Artificial soil for planting plants and manufacturing method of the same Download PDF

Info

Publication number
KR101547306B1
KR101547306B1 KR1020150031447A KR20150031447A KR101547306B1 KR 101547306 B1 KR101547306 B1 KR 101547306B1 KR 1020150031447 A KR1020150031447 A KR 1020150031447A KR 20150031447 A KR20150031447 A KR 20150031447A KR 101547306 B1 KR101547306 B1 KR 101547306B1
Authority
KR
South Korea
Prior art keywords
weight
potassium
parts
organic material
group
Prior art date
Application number
KR1020150031447A
Other languages
Korean (ko)
Inventor
김정호
Original Assignee
김정호
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김정호 filed Critical 김정호
Priority to KR1020150031447A priority Critical patent/KR101547306B1/en
Application granted granted Critical
Publication of KR101547306B1 publication Critical patent/KR101547306B1/en

Abstract

The purpose of the present invention is to provide an artificial soil kit to be used for various purposes. The artificial soil comprises fermented organic matters, minerals, carbide, natural soil, a fertilizer containing calcium and magnesium, and absorbent polymers. The present invention is configured to be excellent in holding water and nutrients; consistently provide nutrients necessary to plant; have properties of water supply and ventilation adequate for plant growth; and minimize water and soil pollution. Accordingly, when making an artificial garden or a flower bed on rooftops, in pocket parks, or indoors such as a veranda or a terrace, it is possible to enhance initial germination of plants and maximize amount of growth and harvests as well as normal growth in order to form soil creating planting layers if solely using the artificial soil or mixing with natural soil according to the present invention. The artificial soil capable of embodying a variety of color and size of particles also can be used for interior design and education.

Description

식물 식재용 인공토양 및 이의 제조방법{Artificial soil for planting plants and manufacturing method of the same}Technical Field [0001] The present invention relates to an artificial soil for plant material,

본 발명은 인공토양, 이의 제조방법 등에 관한 것으로서, 더 상세하게는 수분 보유능이 우수한 기능성 수지를 포함하여 베란다나 테라스와 같은 건물 실내, 건물 옥상, 미니공원 등에 화단 또는 인공 정원을 조성할 때 식물 식재층 형성 용도로 사용가능한 인공토양 및 이의 제조방법 등에 관한 것이다.The present invention relates to an artificial soil and a method of manufacturing the same, and more particularly, to a method for producing a plant material or an artificial garden such as a veranda or a terrace, Artificial soil usable for layer formation, a method for producing the same, and the like.

산업이 발달하고 도시화가 진전되면서 도시의 환경개선을 위해 도심지 녹화에 대한 관심이 증폭되고 있다. 그러나, 산업 및 업무시설이 집중되고 인구밀도가 높은 도심지 환경에서 대규모의 공원이나 숲과 같은 녹지를 조성하는 것은 정책적 또는 비용적 측면에서 볼 때 쉽지 않은 일이다.As the industry develops and urbanization progresses, there is a growing interest in urban greening to improve the urban environment. However, it is not easy to create large-scale parks and forest-like green areas in densely populated and densely populated industrial and business facilities, in terms of policy or cost.

이를 해결하기 위해 도심지의 콘크리트 바닥에 식물을 식재할 수 있는 인공지반을 형성하여 녹지를 형성하거나, 건물의 옥상 또는 실내에 식물을 식재할 수 있도록 인공토양을 포설하여 건물녹화를 수행함으로써 환경을 개선하고자 하는 노력이 기울여지고 있다. 그러나, 인공토양으로 조성된 식재층은 자연지반과는 달리 물, 양분 등이 단절되어있는 시스템(Closed system)이기 때문에 식재된 식물의 생육이 불량해지기 쉽다. 따라서, 베란다나 테라스와 같은 건물 실내, 건물 옥상, 미니공원 등에 인공 정원을 조성할 때 식물 식재층을 형성하기 위해 사용되는 인공토양은 우수한 보수력과 보비력을 가져야 하고, 나아가 식물에 필요한 영양분을 지속적으로 공급할 수 있어야 하고 식물의 정상적인 생장을 위해 적정 수준의 배수성과 통기성을 가져야 하며, 토양 오염을 최소화하여야 한다.In order to solve this problem, it is necessary to improve the environment by forming green spaces by forming artificial grounds capable of planting plants on the concrete floor in urban areas, or by laying artificial soil on the rooftop or inside of the buildings so as to plant the buildings Efforts are being made. However, the planting layer composed of artificial soil is a closed system in which water and nutrients are disconnected unlike the natural ground, so that the growth of planted plants is likely to become poor. Therefore, the artificial soil used to form the planting material layer when constructing the artificial garden in a building such as a veranda or a terrace, a rooftop of a building, a mini park, etc. should have excellent water holding capacity and bending strength, Be able to supply, have adequate levels of drainage and ventilation for normal plant growth, and minimize soil contamination.

또한, 최근에는 일반 가정이나 학교에서 인테리어 목적 또는 교육 목적으로 투명한 유리 또는 플라스틱 재질의 화분에 인공토양을 넣고 식물을 가꾸는 수요가 증가하고 있기 때문에, 이러한 용도로 사용되는 인공토양은 다양한 색상 등을 구현할 수 있어야 한다.In recent years, since the demand for planting artificial soil in transparent glass or plastic pots for interior purpose or education purpose is increasing in ordinary households or schools, the artificial soil used for this purpose can realize various colors Should be able to.

옥상 녹화, 건물 입체 녹화 또는 화분 등에 사용되는 인공토양과 관련하여 선행기술들이 다수 개시되어 있다. 예를 들어, 대한민국 등록특허공보 제10-1415949호에는 부직포 100 중량부, 우레탄폼 90 내지 110 중량부, 저융점 본딩사 90 내지 110 중량부, 흡수성 고분자 5 내지 10 중량부, 숯가루 0.3 내지 1 중량부 및 제오라이트 분말 0.3 내지 1 중량부로 이루어지는 것을 특징으로 하는 인공토양 조성물이 개시되어 있다. 또한, 대한민국 등록특허공보 제10-0315525호에는 150㎛ 이하의 입도를 갖는 유리분말 100중량부에 대하여 탄산칼슘, 탄소분말 또는 탄산나트륨으로 구성되는 군으로부터 선택된 적어도 1종의 발포제를 0.5 ∼ 2중량부 혼합하고, 산화철, 산화니켈, 산화크롬 또는 산화코발트로 구성되는 군으로 부터 선택된 적어도 1종의 착색제 0.2 ∼ 2중량부를 혼합하여 열처리로에 투입한 다음, 6 ∼ 8℃/분으로 승온하여 700 ∼ 1,000℃의 온도에서 발포하고 냉각분쇄하여 제조된 입상의 다포유리와 난분해성 또는 기숙성된 유기물로 인공토양을 구성하되, 상기 유기물을 상기 입상의 다포유리에 대하여 부피비로 1 ∼ 50% 혼합한 것을 특징으로 하는 인공토양이 개시되어 있다. 또한, 대한민국 등록특허공보 제10-1117116호에는 지렁이분변토 5 내지 10중량%, 버섯폐배지 2 내지 10중량%, 동애등에 부산물 5 내지 10중량%, 고흡수성 폴리아크릴산 3 내지 8중량%, 목분 5 내지 15중량%, 부엽토 5 내지 10중량%, 토탄 5 내지 15 중량%, 제오라이트 3 내지 8중량%, 토양미생물 0.1 내지 5중량% 및 잔량으로서 유기질비료를 포함하는 것을 특징으로 하는 수직형 벽체의 녹화를 위한 인공토양조성물이 개시되어 있다. 또한, 대한민국 등록특허공보 제10-1090949호에는 왕겨숯 60~70 중량%, 코코피트 10~20 중량%, 퍼라이트 5~10 중량%, 및 왕겨 5~10 중량%으로 혼합된 혼합물; 및 상기 혼합물 100 중량부에 대하여 30~40 중량부의 물을 첨가하여 구성되고, 상기 물에는 900~1100배로 희석된 유효미생물이 첨가된 것을 특징으로 하는 왕겨숯을 이용한 녹화용 경량 인공토양 조성물이 개시되어 있다.Background Art [0002] Many prior art related to artificial soil used for rooftop greening, building three-dimensional greening or pollen have been disclosed. For example, in Korean Patent Registration No. 10-1415949, 100 parts by weight of a nonwoven fabric, 90 to 110 parts by weight of a urethane foam, 90 to 110 parts by weight of a low melting point bonding yarn, 5 to 10 parts by weight of an absorbent polymer, And 0.3 to 1 part by weight of a zeolite powder. Korean Patent Registration No. 10-0315525 discloses that 0.5 to 2 parts by weight of at least one blowing agent selected from the group consisting of calcium carbonate, carbon powder or sodium carbonate is added to 100 parts by weight of glass powder having a particle size of 150 mu m or less And 0.2 to 2 parts by weight of at least one kind of coloring agent selected from the group consisting of iron oxide, nickel oxide, chromium oxide or cobalt oxide are mixed, and the mixture is heated to a temperature of 6-8 ° C / Granular glass produced by foaming and cooling milling at a temperature of 1,000 ° C and refractory or aged organic matter, wherein the organic matter is mixed with the granular glass at a volume ratio of 1 to 50% Which is characterized in that the artificial soil is used. In addition, Korean Patent Publication No. 10-1117116 discloses that 5 to 10% by weight of earthworm fungi, 2 to 10% by weight of mushroom waste medium, 5 to 10% by weight of byproducts on Donghae, 3 to 8% by weight of superabsorbent polyacrylic acid, Characterized in that the organic fertilizer comprises organic fertilizer as a residual amount of 15 to 15% by weight, humus 5 to 10% by weight, peat 5 to 15% by weight, zeolite 3 to 8% by weight, soil microbes 0.1 to 5% ≪ / RTI > are disclosed. Also, in Korean Patent Registration No. 10-1090949, a mixture of 60 to 70 wt% of chaff charcoal, 10 to 20 wt% of coco peat, 5 to 10 wt% of perlite, and 5 to 10 wt% of rice hull; And 30 to 40 parts by weight of water are added to 100 parts by weight of the mixture, and the water is added with an effective microorganism diluted to 900 to 1100 times. The light weight artificial soil composition for greening using the chaff charcoal .

본 발명은 종래의 기술적 배경하에서 도출된 것으로서, 본 발명의 목적은 보수력 및 보비력이 우수하고, 식물에 필요한 영양분을 지속적으로 공급할 수 있고, 식물 생장에 적합한 배수성 및 통기성을 가지며, 토양 내지 수질의 오염을 최소화할 수 있는 인공토양 및 이의 제조방법을 제공하는데에 있다.SUMMARY OF THE INVENTION The present invention has been made under the background of the prior art, and an object of the present invention is to provide a method for producing a plant which is excellent in water holding capacity and bending strength, can continuously supply nutrients necessary for plants, has drainage property and air permeability suitable for plant growth, And to provide a method for manufacturing the artificial soil.

또한, 본 발명의 목적은 다양한 용도로 사용될 수 있는 인공토양 키트를 제공하는데에 있다.It is also an object of the present invention to provide an artificial soil kit which can be used for various purposes.

상기 목적을 해결하기 위하여, 본 발명의 일 예는 발효 유기물 100 중량부 당 광물질 50~200 중량부, 탄화물질 50~150 중량부, 칼슘-마그네슘 함유 비료 10~100 중량부 및 흡수성 고분자 1~20 중량부를 포함하는 조성물 형태의 인공토양을 제공한다. 이때, 상기 발효 유기물은 식물성 유기물 및 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium), 로도박터 캡슐라타(Rhodobacter capsulata) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)로 이루어진 군에서 선택된 2종 이상의 미생물을 포함하는 혼합 미생물을 첨가하고 발효시켜 형성한 것이다. 또한, 상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 탄화물질은 활성탄, 바텀애쉬, 왕겨훈탄, 코코넛탄 및 이탄(peat)으로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상을 포함한다. 또한, 상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체를 포함한다.In order to solve the above-mentioned object, an example of the present invention is a fermented organic food comprising 50 to 200 parts by weight of a mineral substance, 50 to 150 parts by weight of a carbonized material, 10 to 100 parts by weight of a calcium-magnesium containing fertilizer, By weight based on the total weight of the composition. At this time, the fermentation organic material is mixed with an organic material mixture containing a vegetable organic material and an animal organic material, such as Bacillus subtilis pumilus), Bacillus subtilis (Bacillus subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis ), Bacillus megaterium megaterium , Rhodobacter capsulata , and Rhodobacter sphaeroides , and fermenting the microorganism. In addition, the above-mentioned minerals include at least one selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite. In addition, the carbonized material may include at least one selected from the group consisting of activated carbon, bottom ash, chaff hard coal, coconut charcoal and peat. The calcium-magnesium-containing fertilizer may be at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, lime lime, gypsum lime, gypsum lime and gypsum plaster, magnesium hydroxide, magnesium sulfate, At least one member selected from the group consisting of magnesium, hydroxide goto, carbonated goto, carbonated lime goto, sulfuric acid goto, lime goto, soluble phosphoric acid and goto superphosphate. Further, the water absorbing polymer may be a copolymer of a first monomer selected from carboxylic acid having an ethylenically unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenic unsaturated bond, or a copolymer having an ethylenically unsaturated bond A copolymer of a third monomer selected from an amide and an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond.

또한, 상기 목적을 해결하기 위하여, 본 발명의 일 예는 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium), 로도박터 캡슐라타(Rhodobacter capsulata) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)로 이루어진 군에서 선택된 2종 이상의 미생물을 포함하는 혼합 미생물을 첨가하고 발효시켜 발효 유기물을 수득하는 단계; 및 상기 발효 유기물 100 중량부 당 광물질 50~200 중량부, 탄화물질 50~150 중량부, 흡수성 고분자 1~20 중량부 및 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합하여 최종 조성물을 수득하는 단계를 포함하는 인공토양의 제조방법을 제공한다. 이때, 상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 탄화물질은 활성탄, 바텀애쉬, 왕겨훈탄, 코코넛탄 및 이탄(peat)으로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상을 포함한다. 또한, 상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체를 포함한다.Further, in order to solve the above object, another aspect of the invention is Bacillus Fu milreoseu (Bacillus pumilus) to the organic mixture material a mixture of animal organic material comprising vegetable organic matter and manure and slaughter by-products, including bark and sawdust, Bacillus subtilis Bacillus subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis ), Bacillus megaterium megaterium , Rhodobacter capsulata and Rhodobacter sphaeroides , and fermenting the mixture to obtain a fermented organic material; And 50 to 200 parts by weight of a mineral material, 50 to 150 parts by weight of a carbonized material, 1 to 20 parts by weight of an absorbent polymer and 10 to 100 parts by weight of a calcium-magnesium-containing fertilizer per 100 parts by weight of the fermented organic material, The method comprising the steps of: At this time, the mineral includes at least one selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite. In addition, the carbonized material may include at least one selected from the group consisting of activated carbon, bottom ash, chaff hard coal, coconut charcoal and peat. The calcium-magnesium-containing fertilizer may be at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, lime lime, gypsum lime, gypsum lime and gypsum plaster, magnesium hydroxide, magnesium sulfate, At least one member selected from the group consisting of magnesium, hydroxide goto, carbonated goto, carbonated lime goto, sulfuric acid goto, lime goto, soluble phosphoric acid and goto superphosphate. Further, the water absorbing polymer may be a copolymer of a first monomer selected from carboxylic acid having an ethylenically unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenic unsaturated bond, or a copolymer having an ethylenically unsaturated bond A copolymer of a third monomer selected from an amide and an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond.

또한, 본 발명의 목적을 해결하기 위하여 전술한 인공토양 또는 전술한 방법으로 제조된 인공토양 및 상기 인공토양과 별도로 제공되고 색상을 갖는 흡수성 고분자를 포함하는 인공토양 키트를 제공한다. 이때, 상기 색상을 갖는 흡수성 고분자는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체이다.Also, in order to solve the object of the present invention, there is provided an artificial soil kit comprising the above artificial soil or an artificial soil prepared by the above-mentioned method, and an absorbent polymer provided separately from the artificial soil and having a color. Here, the absorbing polymer having the hue is a copolymer of a third monomer selected from an amide having an ethylenically unsaturated bond and an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond.

본 발명에 따른 인공토양은 보수력 및 보비력이 우수하고, 식물에 필요한 영양분을 지속적으로 공급할 수 있고, 식물 생장에 적합한 배수성 및 통기성을 가지며, 토양 내지 수질의 오염을 최소화할 수 있다. 따라서, 베란다나 테라스와 같은 건물 실내, 건물 옥상, 미니공원 등에 화단 또는 인공 정원을 조성할 때 식물 식재층을 형성하기 위해 본 발명에 따른 인공토양을 단독으로 사용하거나 자연 토양과 혼합하여 사용하는 경우 식물의 초기 발아를 크게 증대시킬 수 있고 식물의 정상적 생장은 물론 생장량 내지 수확량을 극대화할 수 있다. 또한, 본 발명에 따른 인공토양 키트는 다양한 색상 및 입도 크기의 구현이 가능하므로 인테리어용 토양, 교육용 토양 등으로 활용될 수 있다.The artificial soil according to the present invention is excellent in water retention and bending strength, can continuously supply nutrients necessary for plants, has drainage and ventilation suitable for plant growth, and can minimize contamination of soil or water quality. Therefore, when artificial soil according to the present invention is used alone or in combination with natural soil to form a planting material layer when a flower bed or artificial garden is formed in a building such as a veranda or a terrace, a building roof, It is possible to greatly increase the initial germination of the plant and to maximize the growth and yield of the plant as well as the normal growth. In addition, the artificial soil kit according to the present invention can be used as an interior soil, an educational soil, etc. since it can realize various colors and size sizes.

도 1은 시험군별 보리 종자 및 유채 종자의 생장 시험 결과를 나타낸 사진이다.Fig. 1 is a photograph showing growth test results of barley seeds and rapeseed seeds according to the test groups.

이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.

본 발명의 일 측면은 식물 식재시 별도의 첨가물 없이 식물 생장에 적합한 자연 토양을 대체하거나, 자연 토양과 혼합하여 사용될 수 있는 인공토양 및 이의 제조방법에 관한 것이다.One aspect of the present invention relates to an artificial soil which can be used as a natural plant for plant growth without any additives, or can be used in combination with natural soil, and a method for producing the same.

본 발명에 따른 인공토양은 발효 유기물, 광물질, 탄화물질, 칼슘-마그네슘 함유 비료 및 흡수성 고분자를 포함하는 조성물의 형태를 가진다. 이하, 본 발명에 따른 인공토양을 구성성분별로 나누어 설명한다.
The artificial soil according to the present invention has the form of a composition containing a fermentation organic material, a mineral substance, a carbonized material, a calcium-magnesium-containing fertilizer, and an absorbent polymer. Hereinafter, the artificial soil according to the present invention will be divided into constituent components.

발효 유기물Fermented organic matter

본 발명에서 발효 유기물은 유기물로부터 유래되고 식물이 이용할 수 있는 화학적 형태의 양분으로 존재하는 퇴비를 말하며, 질소, 인산, 칼륨을 식물이 쉽게 이용할 수 있는 가급태 형태로 포함한다. 구체적으로 본 발명에서 발효 유기물은 식물성 유기물 및 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium), 로도박터 캡슐라타(Rhodobacter capsulata) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)로 이루어진 군에서 선택된 2종 이상의 미생물을 포함하는 혼합 미생물을 첨가하고 발효시켜 형성한 것으로서, 함수율이 10~40%이고 총 유기물 대 질소의 비(OM/N)가 20~40인 것을 특징으로 한다. 이때, 상기 유기물 혼합 원료를 구성하는 식물성 유기물은 바람직하게는 수피와 톱밥을 포함한다. 또한, 상기 유기물 혼합 원료를 구성하는 동물성 유기물은 바람직하게는 계분과 도축 부산물을 포함한다. 상기 수피는 나무의 껍질에 해당하는 것으로서, 토양에 양분을 공급할 뿐만 아니라 물리적 통기성을 개선하는 역할을 한다. 상기 톱밥은 총 유기물 대 질소의 비(OM/N)가 높은 원료로서 수분 흡수율이 좋아 토양의 보수성을 향상시킨다. 상기 계분은 닭똥이라고 하는 것으로서, 질소, 인산 및 칼륨 성분이 상대적으로 높고 분해속도가 빨라 발효를 촉진하고 발효에 의해 가급태 양분을 공급한다. 또한, 도축 부산물은 소, 돼지, 닭 등과 같은 가축을 도축할 때 발생하는 폐기물로서, 돈모, 우모, 계모를 포함하는 각종 동물털은 물론 동물들의 발톱, 미처리 불가식 부분 등을 포함한다. 도축 부산물은 유기물 함량이 매우 높고 발효 후 토양의 지력을 상승시키는 작용을 하므로 작물의 생장에 도움을 준다. 상기 유기물 혼합 원료는 혼합 미생물에 의해 함수율이 10~40%이고 총 유기물 대 질소의 비(OM/N)가 20~40이며 약 알칼리성인 가급태 유기물 퇴비로 변환된다. 이때, 상기 유기물 혼합 원료를 구성하는 식물성 유기물 대 동물성 유기물의 중량비는 1:1 내지 1:2인 것이 바람직하고, 1:1 내지 1:1.5인 것이 더 바람직하다. 또한, 상기 식물성 유기물을 구성하는 수피 대 톱밥의 중량비는 1:0.5 내지 1:10인 것이 바람직하고, 1:0.5 내지 1:4인 것이 더 바람직하다. 또한, 상기 동물성 유기물을 구성하는 계분 대 도축 부산물의 중량비는 1:0.5 내지 1:2인 것이 바람직하고 1:0.5 내지 1:1.5인 것이 더 바람직하다. 또한, 상기 혼합 미생물의 첨가량은 유기물 혼합 원료 100 중량부 당 0.05~1 중량부인 것이 바람직하고, 0.1~0.5 중량부인 것이 더 바람직하다. 또한, 본 발명에서 상기 발효 유기물은 바람직하게는 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물을 포함하는 혼합 미생물을 첨가한 후 호기성 조건의 발효조에서 15~40일 동안 1차 발효하고 노지에서 60~300일 동안 2차 발효하여 형성한 것이다. 상기 혼합 미생물 중 바실러스속 미생물은 유기물 혼합 원료의 발효를 촉진하고 동시에 악취를 제거하는 역할을 한다. 또한, 상기 혼합 미생물 중 로도박터속 미생물은 발효 대사산물로 아미노산, 비타민, 핵산, 미네랄, 호르몬, 지방산 등의 물질을 합성하고 항균 작용에 의해 유기물 혼합 원료의 발효에 악 영향을 끼치는 미생물인 바실러스 세레우스 등을 저감시키는 역할을 한다.
In the present invention, the fermentation organic matter refers to a compost which is derived from an organic matter and exists in a chemical form of nutrients available to the plant, and includes nitrogen, phosphoric acid, and potassium in a form of a readily available plant. Specifically, in the present invention, the fermentation organic material is obtained by mixing Bacillus subtilis with Bacillus subtilis pumilus), Bacillus subtilis (Bacillus subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis , Bacillus megaterium , Rhodobacter capsulata , and Rhodobacter sphaeroides . The water content is 10 to 40% and the ratio of total organic matter to nitrogen (OM / N) is in the range of 20 to 40. At this time, the vegetable organic material constituting the organic material mixing material preferably includes bark and sawdust. In addition, the animal organic material constituting the organic material mixing raw material preferably includes counterparts and slaughter by-products. The bark, which corresponds to the bark of a tree, plays a role not only to supply nutrients to the soil but also to improve physical ventilation. The sawdust is a raw material having a high total organic matter to nitrogen (OM / N) ratio and is excellent in water absorption rate, thereby improving water retention. The above flour is called chicken dung, and it has a relatively high nitrogen, phosphoric acid and potassium content and has a high decomposition rate, thereby promoting fermentation and supplying viable nutrients by fermentation. In addition, slaughter by-products are wastes generated when slaughtering livestock such as cattle, pigs, chickens, and the like, including various animal fur including ponytail, wool, stepmother, as well as claws and untreated parts of animals. By-products of slaughter are very high in organic matter and increase the soil's strength after fermentation, thus helping to grow crops. The organic material mixing raw material is converted into a weak alkaline organic material compost having a water content of 10 to 40% and a ratio of total organic matter to nitrogen (OM / N) of 20 to 40 due to mixed microorganisms. At this time, the weight ratio of the vegetable organic material to the animal organic material constituting the organic material mixture material is preferably 1: 1 to 1: 2, more preferably 1: 1 to 1: 1.5. The weight ratio of bark to sawdust constituting the vegetable organic material is preferably 1: 0.5 to 1:10, more preferably 1: 0.5 to 1: 4. In addition, the weight ratio of staple to slaughter by-products constituting the animal organic material is preferably 1: 0.5 to 1: 2, more preferably 1: 0.5 to 1: 1.5. The amount of the mixed microorganism added is preferably 0.05 to 1 part by weight, more preferably 0.1 to 0.5 part by weight per 100 parts by weight of the organic material mixture. In addition, in the present invention, the fermentation organic material is preferably added to an organic material mixed material obtained by mixing vegetable organic materials including bark and sawdust and animal organic materials including stem and slaughter by-products, such as Bacillus subtilis pumilus), Bacillus subtilis (Bacillus subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis ) and Bacillus megaterium , and at least one microorganism belonging to the genus Bacillus such as Rhodobacter capsulata) or Rhodobacter spheroid's (Rhodobacter sphaeroides , and then fermented in a fermentation tank under aerobic conditions for 15 to 40 days and then fermented for 60 to 300 days in a non-fermented state. Among the mixed microorganisms, the microorganism of the genus Bacillus promotes the fermentation of the organic material mixture and at the same time removes odors. Among the above-mentioned mixed microorganisms, Rhodobacter microorganism is a fermentation metabolite that synthesizes substances such as amino acids, vitamins, nucleic acids, minerals, hormones, fatty acids and the like, and is a microorganism that has a bad influence on the fermentation of organic material- And the like.

광물질Minerals

본 발명에서 광물질은 인공토양의 양이온교환용량(cation exchange capacity, CEC)를 증대시키고 중금속 및 유해물질을 불용화 내지 치환에 의해 제거하는 역할을 한다. 상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택된 1종 이상을 포함할 수 있고, 인공토양을 구성하는 다른 성분들과의 유기적 결합에 의한 상승 효과 내지 경제성을 고려할 때 제오라이트인 것이 바람직하다. 본 발명에 따른 인공토양에서 광물질의 함량은 발효 유기물 100 중량부 당 50~200 중량부이고, 75~150 중량부인 것이 바람직하고, 75~125 중량부인 것이 더 바람직하다.
In the present invention, the mineral enhances the cation exchange capacity (CEC) of artificial soil and removes heavy metals and toxic substances by insolubility and substitution. The mineral may include at least one member selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite, and may be an elevation due to organic bonding with other components constituting the artificial soil It is preferable that zeolite is used in consideration of the effect and economical efficiency. The content of the mineral in the artificial soil according to the present invention is 50-200 parts by weight, preferably 75-150 parts by weight, and more preferably 75-125 parts by weight per 100 parts by weight of the fermentation organic material.

탄화물질Carbonized material

본 발명에서 탄화물질은 자체의 미세기공을 통해 인공토양의 통기성 및 배수성을 적정 수준으로 유지하고 보수력 및 보비력을 증대시키는 역할을 한다. 상기 탄화물질은 활성탄, 바텀애쉬, 왕겨훈탄, 코코넛탄 및 이탄(peat)으로 이루어진 군에서 선택된 1종 이상을 포함할 수 있고, 인공토양을 구성하는 다른 성분들과의 유기적 결합에 의한 상승 효과 및 경제성을 고려할 때 바텀애쉬인 것이 바람직하다. 상기 활성탄은 석탄계 활성탄 및 식물계 활성탄을 모두 포함하는 개념이다. 본 발명에 따른 인공토양에서 탄화물질의 함량은 발효 유기물 100 중량부 당 50~150 중량부이고, 75~150 중량부인 것이 바람직하고, 75~125 중량부인 것이 더 바람직하다.In the present invention, the carbonaceous material maintains the air permeability and drainage of the artificial soil at an appropriate level through the micropores of the carbonaceous material, and increases the water holding capacity and the bending strength. The carbonized material may include at least one selected from the group consisting of activated carbon, bottom ash, rice husk coal, coconut charcoal, and peat, and the synergistic effect by organic bonding with other components constituting the artificial soil, Bottom ash is preferable considering economical efficiency. The activated carbon includes both coal-based activated carbon and plant-based activated carbon. The content of the carbide in the artificial soil according to the present invention is 50 to 150 parts by weight, preferably 75 to 150 parts by weight, and more preferably 75 to 125 parts by weight per 100 parts by weight of the fermentation organic material.

칼슘-마그네슘 함유 비료Calcium-magnesium-containing fertilizer

본 발명에서 칼슘-마그네슘 함유 비료는 토양의 입단화를 촉진하는 등의 토양의 물리적 성질을 개선하는 역할을 한다. 상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 인공토양을 구성하는 다른 성분들과의 유기적 결합에 의한 상승 효과를 고려할 때 소석회, 탄산석회, 규산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토 및 석회고토로 이루어진 군에서 선택되는 1종 이상을 포함하는 것이 바람직하다. 본 발명에 따른 인공토양에서 칼슘-마그네슘 함유 비료의 함량은 발효 유기물 100 중량부 당 10~100 중량부이고, 25~100 중량부인 것이 바람직하고, 25~75 중량부인 것이 더 바람직하다.
In the present invention, the calcium-magnesium-containing fertilizer plays a role in improving the physical properties of the soil, such as promoting the incorporation of the soil. Wherein the calcium-magnesium-containing fertilizer is at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, heavy lime lime, gypsum, lime lime and gypsum plaster and magnesium hydroxide, magnesium sulfate, magnesium carbonate, And may include at least one member selected from the group consisting of hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, Considering the synergistic effect, at least one selected from the group consisting of calcium hydroxide, carbonate lime, calcium silicate lime, gypsum, plaster lime and gypsum, and magnesium hydroxide, magnesium sulfate, magnesium carbonate, hydroxide goto, carbonated goto, carbonated lime goto, And at least one member selected from the group consisting of gypsum and calcined gypsum. The content of the calcium-magnesium-containing fertilizer in the artificial soil according to the present invention is 10-100 parts by weight, preferably 25-100 parts by weight, more preferably 25-75 parts by weight, per 100 parts by weight of the fermentation organic material.

흡수성 고분자Absorbent polymer

본 발명에서 흡수성 고분자는 수분을 매개로 한 수축과 팽창의 반복을 통해 인공토양 내에 빈 공간을 형성하고 인공토양의 보수력, 보비력을 증가시키고 식물의 생장에 필요한 미량 원소를 지속적으로 공급하는 역할을 한다. 상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체(이하, '기능성 수지 A'라 칭함) 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체(이하, '기능성 수지 B'라 칭함)를 포함할 수 있다.In the present invention, the water-absorbing polymer forms voids in the artificial soil through repeated water contraction and expansion, increases the water holding capacity and the bending strength of the artificial soil, and continuously supplies trace elements required for plant growth . The water absorbing polymer is a copolymer of a first monomer selected from carboxylic acid having an ethylenic unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenic unsaturated bond (hereinafter referred to as 'functional resin A' (Hereinafter referred to as " functional resin B ") selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond and a third monomer selected from an amide having an ethylenically unsaturated bond .

이때, 상기 기능성 수지 A를 형성하는 제1단량체는 아크릴산, 메타크릴산, 이타코닉산, 말레익산 및 푸마릭산으로 이루어진 군에서 선택되는 1종 이상이고, 제2단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다. 또한, 인공토양을 구성하는 다른 성분들과의 유기적 결합에 의한 상승 효과를 고려할 때 상기 제1단량체는 아크릴산, 메타크릴산 및 말레익산으로 이루어진 군에서 선택되는 1종 이상이고, 제2단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 말레익산나트륨 및 말레익산칼륨으로 이루어진 군에서 선택되는 1종 이상인 것이 더 바람직하다. 상기 기능성 수지 A의 구체적인 예로는 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x], 아크릴산/아크릴산칼륨 공중합체[Acrylic acid/potassim acrylate copolymer; CAS 등록번호 : 25608-12-2; 분자식 : (C3H4O2.C3H3O2.Na)x], 폴리아크릴산 부분 나트륨염[Poly(acrylic acid) partial sodium salt; CAS 등록번호 : 76774-25-9] 등이 있다. 상기 아크릴산/아크릴산나트륨 공중합체는 폴리아크릴산 부분 나트륨염 용액[Poly(acrylic acid) partial sodium salt solution]이라고도 불리우며 형태 안정성 내지 수축과 팽창의 지속성을 고려할 때 가교화된 형태인 것이 바람직하다. 또한, 상기 아크릴산/아크릴산칼륨 공중합체는 폴리아크릴산 부분 나트륨염 부분 칼륨염[Poly(acrylic acid) partial potassium salt]으로도 불리우며, 형태 안정성 내지 수축과 팽창의 지속성을 고려할 때 가교화된 형태인 것이 바람직하다.At this time, the first monomer forming the functional resin A is at least one selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid, and fumaric acid, and the second monomer is at least one selected from the group consisting of sodium acrylate, At least one member selected from the group consisting of potassium carbonate, potassium carbonate, sodium carbonate, potassium carbonate, potassium carbonate, sodium carbonate, potassium carbonate, potassium carbonate, sodium carbonate, potassium carbonate, sodium carbonate, potassium carbonate, Also, considering the synergistic effect by organic bonding with other components constituting the artificial soil, the first monomer is at least one selected from the group consisting of acrylic acid, methacrylic acid and maleic acid, and the second monomer is acrylic acid More preferably at least one member selected from the group consisting of sodium, potassium acrylate, sodium methacrylate, potassium methacrylate, sodium maleate and potassium maleate. Specific examples of the functional resin A include acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer]. CAS registration number: 9033-79-8; Molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x], acrylic acid / potassium acrylate copolymer [Acrylic acid / potassium acrylate copolymer; CAS registration number: 25608-12-2; Molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x], poly (acrylic acid) partial sodium salt; CAS registration number: 76774-25-9]. The acrylic acid / sodium acrylate copolymer is also referred to as a polyacrylic acid partial sodium salt solution (poly (acrylic acid) partial sodium salt solution), and it is preferably in a crosslinked form when considering morphological stability or continuity of shrinkage and expansion. The acrylic acid / potassium acrylate copolymer is also called a polyacrylic acid partial potassium salt [poly (acrylic acid) partial potassium salt], and it is preferably a crosslinked form when considering morphological stability, Do.

상기 기능성 수지 B를 형성하는 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다. 또한, 인공토양을 구성하는 다른 성분들과의 유기적 결합에 의한 상승 효과를 고려할 때 상기 제3단량체는 아크릴아마이드, 메타크릴아마이드 및 말레익산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 말레익산나트륨 및 말레익산칼륨으로 이루어진 군에서 선택되는 1종 이상인 것이 더 바람직하다. 상기 기능성 수지 B의 구체적인 예로는 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2), 아크릴아마이드/아크릴산나트륨 공중합체(Acrylamide/sodium acrylate copolymer; CAS 등록번호 : 25987-30-8), 폴리(아크릴아마이드-아크릴산) 부분 나트륨염[Poly(acrylamide-co-acrylic acid) partial sodium salt; CAS 등록번호 : 62649-23-4] 등이 있다. 상기 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2)는 폴리(아크릴아마이드-아크릴산) 칼륨염[Poly(acrylamide-co-acrylic acid) potassium salt]으로도 불리우며, 형태 안정성 내지 수축과 팽창의 지속성을 고려할 때 가교화된 형태인 것이 바람직하다. 또한, 상기 아크릴아마이드/아크릴산나트륨 공중합체(Acrylamide/sodium acrylate copolymer; CAS 등록번호 : 25987-30-8), 폴리(아크릴아마이드-아크릴산) 부분 나트륨염[Poly(acrylamide-co-acrylic acid) partial sodium salt; CAS 등록번호 : 62649-23-4] 등도 형태 안정성 내지 수축과 팽창의 지속성을 고려할 때 가교화된 형태인 것이 바람직하다.Wherein the third monomer forming the functional resin B is at least one member selected from the group consisting of acrylamide, methacrylamide, maleic acid amide and fumaric acid amide, and the fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate , Potassium methacrylate, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate, and sodium fumarate. Also, considering the synergistic effect by organic bonding with other constituents of the artificial soil, the third monomer is at least one selected from the group consisting of acrylamide, methacrylamide and maleic acid amide, and the fourth monomer Is more preferably one or more selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, potassium methacrylate, sodium maleate and potassium maleate. Specific examples of the functional resin B include an acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2), an acrylamide / sodium acrylate copolymer (CAS registration number: : 25987-30-8), poly (acrylamide-co-acrylic acid) partial sodium salt [Poly (acrylamide-co-acrylic acid) partial sodium salt; CAS registration number: 62649-23-4]. The acrylamide / potassium acrylate copolymer (CAS Registration Number: 31212-13-2) may also be used as a poly (acrylamide-co-acrylic acid) potassium salt , And it is preferably a crosslinked form when considering morphological stability or continuity of shrinkage and expansion. Also, the above-mentioned acrylamide / sodium acrylate copolymer (CAS registration number: 25987-30-8), poly (acrylamide-co-acrylic acid) partial sodium salt; CAS registration number: 62649-23-4] or the like is preferably a crosslinked form when considering morphological stability or continuity of shrinkage and expansion.

또한, 본 발명에서 흡수성 고분자는 기능성 수지 A 및 기능성 수지 B의 조합으로 이루어지는 것이 더 바람직하다. 기능성 수지 B는 기능성 수지 A의 보수력 또는 보비력을 더욱 개선시키는 역할을 한다. 이때, 흡수성 고분자 내에서 기능성 수지 A 대 기능성 수지 B의 중량비는 크게 제한되지 않으며, 예를 들어 1:9 내지 9:1의 범위에서 선택될 수 있다.Further, in the present invention, it is more preferable that the water absorbent polymer is composed of a combination of the functional resin A and the functional resin B. The functional resin B further improves the water holding capacity or the bending strength of the functional resin A. In this case, the weight ratio of the functional resin A to the functional resin B in the water absorbing polymer is not particularly limited, and may be selected in the range of, for example, 1: 9 to 9: 1.

본 발명에 따른 인공토양에서 흡수성 고분자의 함량은 발효 유기물 100 중량부 당 1~20 중량부이고, 1~15 중량부인 것이 바람직하고, 2~10 중량부인 것이 더 바람직하다.
The content of the water absorbent polymer in the artificial soil according to the present invention is 1 to 20 parts by weight, preferably 1 to 15 parts by weight, more preferably 2 to 10 parts by weight, per 100 parts by weight of the fermentation organic material.

기타 물질Other substances

본 발명에 따른 인공토양은 바람직하게는 질소 함유 비료, 인 함유 비료, 칼륨 함유 비료 또는 식물의 생장에 필요한 미량 원소 함유 물질을 더 포함할 수 있다. The artificial soil according to the present invention may further preferably contain nitrogen-containing fertilizer, phosphorus-containing fertilizer, potassium-containing fertilizer or a trace element-containing material necessary for plant growth.

상기 질소 함유 비료는 식물에 질소를 이온 형태로 공급하는 물질로서, 공지의 질소 비료 범위에서 다양하게 선택될 수 있으며, 바람직한 일 예로 요소, 황산암모늄, 질산암모늄, 염화암모늄, 인산암모늄, 질산나트륨 및 석회질소로 이루어진 군에서 선택되는 1종 이상으로 구성될 수 있다. 본 발명에 따른 인공토양에서 질소 함유 비료의 함량은 발효 유기물 100 중량부 당 2~20 중량부인 것이 바람직하고 5~10 중량부인 것이 바람직하다.The nitrogen-containing fertilizer is a substance that supplies nitrogen to plants in an ionic form, and may be variously selected from a range of known nitrogen fertilizers. Preferred examples thereof include urea, ammonium sulfate, ammonium nitrate, ammonium chloride, ammonium phosphate, And lime scale. The content of the nitrogen-containing fertilizer in the artificial soil according to the present invention is preferably 2 to 20 parts by weight, more preferably 5 to 10 parts by weight, per 100 parts by weight of the fermentation organic material.

상기 인 함유 비료는 식물에 인을 이온 형태로 공급하는 물질로서, 공지의 인산 비료 범위에서 다양하게 선택될 수 있으며, 바람직한 일 예로 인산칼륨, 인산암모늄, 인산칼슘, 인산나트륨 및 과인산석회로 이루어진 군에서 선택되는 1종 이상으로 구성될 수 있다. 또한, 인산칼륨은 제1인산칼륨(KH2PO4), 제2인산칼륨(K2HPO4) 또는 제3인산칼륨(K3PO4)에서 선택될 수 있다. 본 발명에 따른 인공토양에서 인 함유 비료의 함량은 발효 유기물 100 중량부 당 2~20 중량부인 것이 바람직하고 5~10 중량부인 것이 바람직하다.The phosphorus-containing fertilizer is a substance which supplies phosphorus in the form of an ion in the form of a plant. The phosphorus-containing fertilizer may be selected from a variety of known phosphorus fertilizers, and examples thereof include potassium phosphate, ammonium phosphate, calcium phosphate, sodium phosphate, , And the like. Also, the potassium phosphate can be selected from potassium monophosphate (KH 2 PO 4 ), potassium diphosphate (K 2 HPO 4 ) or potassium trisphosphate (K 3 PO 4 ). The content of the phosphorus-containing fertilizer in the artificial soil according to the present invention is preferably 2 to 20 parts by weight, more preferably 5 to 10 parts by weight, per 100 parts by weight of the fermentation organic material.

상기 칼륨 함유 비료는 식물에 칼륨을 이온 형태로 공급하는 물질로서, 공지의 칼륨 비료 범위에서 다양하게 선택될 수 있으며, 바람직한 일 예로 수산화칼륨, 황산칼륨, 질산칼륨, 염화칼륨 및 인산칼륨으로 이루어진 군에서 선택되는 1종 이상으로 구성될 수 있다. 본 발명에 따른 인공토양에서 칼륨 함유 비료의 함량은 발효 유기물 100 중량부 당 2~20 중량부인 것이 바람직하고 5~10 중량부인 것이 바람직하다.The potassium-containing fertilizer is a substance which supplies potassium to plants in an ionic form. The potassium-containing fertilizer can be variously selected from a range of known potassium fertilizers. Preferred examples thereof include potassium hydroxide, potassium sulfate, potassium nitrate, potassium chloride and potassium phosphate And may be composed of at least one kind selected. The content of the potassium-containing fertilizer in the artificial soil according to the present invention is preferably 2 to 20 parts by weight, more preferably 5 to 10 parts by weight, per 100 parts by weight of the fermentation organic material.

상기 미량 원소 물질은 식물의 생장에 필요한 미량 원소를 제공하는 물질로서, 예를 들어 붕소 함유 물질, 아연 함유 물질, 철 함유 물질, 망간 함유 물질, 구리 함유 물질 및 몰리브덴 함유 물질로 이루어진 군에서 선택되는 2종 이상으로 구성될 수 있고, 바람직하게는 3종 이상으로 구성될 수 있다. 특히, 식물의 생장에 미치는 영향을 고려할 때, 상기 미량 원소 함유 물질은 붕소 함유 물질, 아연 함유 물질 및 몰리브덴 함유 물질을 포함하는 것이 더 바람직하다. 상기 붕소 함유 물질로는 붕사, 붕산 등이 있고, 아연 함유 물질로는 Zn(OH)2, ZnSO4 , ZnCl2 등이 있고, 철 함유 물질로는 Fe(OH)2, Fe(OH)3, FeCl2 , FeCl3 , FeSO4 등이 있고, 망간 함유 물질로는 Mn(OH)2, MnCl2, MnSO4 등이 있고, 구리 함유 물질로는 Cu(OH)2, CuCl2 , CuSO4 등이 있고, 몰리브덴 함유 물질로는 (NH4)6Mo7O24 등이 있다.The trace element material is selected from the group consisting of a boron-containing substance, a zinc-containing substance, an iron-containing substance, a manganese-containing substance, a copper-containing substance, and a molybdenum-containing substance It may be composed of two or more kinds, preferably three or more kinds. In particular, in consideration of the influence on plant growth, it is more preferable that the trace element-containing substance includes a boron-containing substance, a zinc-containing substance and a molybdenum-containing substance. To the boron-containing material to may the borax, boric acid, zinc-containing material is Zn (OH) 2, ZnSO 4 , the Fe (OH) 2, Fe ( OH) with ZnCl 2 and the like, iron-containing substance 3, and the like FeCl 2, FeCl 3, FeSO 4, is a manganese-containing material, such as Mn (OH) 2, MnCl 2 , MnSO 4 a, and is a copper-containing material, such as Cu (OH) 2, CuCl 2 , CuSO 4 (NH 4 ) 6 Mo 7 O 24 and the like can be used as the molybdenum-containing material.

하기 표 1 내지 및 표 2는 본 발명의 인공토양을 구성하는 성분 및 이의 특징을 정리한 것이다.The following Tables 1 to 2 summarize the components constituting the artificial soil of the present invention and their characteristics.

구성성분Constituent 특징Characteristic 발효 유기물Fermented organic matter - 동물성 유기물과 식물성 유기물을 호기성 미생물에 의하여 발효시킨 유기물
- 발효된 유기물은 점토광물과 결합하여 입단을 형성 통기, 배수 촉진 작용을 함
- 질소, 인산, 칼륨 등 양분이온의 함유량이 높음
- 토양 내 유기물은 자기 무게의 4~6배의 물을 흡수하여 보수력 증대 효과 작용
- 양이온치환용량이 20배 이상 높아 보비력 증대 작용
- 유기물 내 질소 고정균이 유기물 함량의 1%에 해당하는 질소비료를 만들어 냄
- 생장 부적합 토양 산도에 대한 완충능이 커서 토양 반응 조절
- 토양 유기물은 중금속에 대한 피해 경감
- 유효인산의 고정을 억제하여 인산시용 효과 높임
- 유기물 내에는 호르몬 및 비타민이 존재하여 식물과 미생물의 생육을 도와줌- Organic materials that have been fermented by aerobic microorganisms for animal and plant organic matter
- Fermented organics combine with clay minerals to form a mouth and to facilitate aeration and drainage.
- Nitrogen, phosphoric acid, high potassium ion content such as potassium
- Soil organic matter absorbs 4 ~ 6 times of its own weight and increases the water holding capacity.
- Cation substitution capacity is more than 20 times higher than bibby force
- nitrogen fertilizer in organic matter produces nitrogen fertilizer corresponding to 1% of organic matter content
- Inadequate growth condition Soil acidity
- Soil organic matter reduces the damage to heavy metals
- Suppresses fixation of effective phosphoric acid and increases phosphoric acid application effect
- Hormones and vitamins exist in the organic matter to help grow plants and microorganisms. 광물질Minerals - 제오라이트, 일라이트, 펄라이트, 벤토나이트 등
- 흡수능 이상의 수분은 배수를 촉진시켜 식물의 뿌리가 썩지 않도록 유도함
- 토양의 이온교환용량을 증가시켜 보비력 증대
- 정글짐 구조로 미세기공의 부피만큼의 약 20배 이상의 수분 및 양분이온을 흡수
- 미세기공에 농약을 흡수하여 농약 성분의 극심한 유출을 막아주고 비료를 시비하였을 경우, 비료성분을 흡수하여 과잉 시비를 예방, 방지함
- 표면이 넓은 벌집 구조로 많은 공간이 복층구조를 이루고 있으며 이러한 스펀지 같은 구멍 안에는 원적외선이 다량 흡수, 저장되어 있어 열을 받으면 발산하여 다른 물체의 분자 활동을 자극- zeolite, ilite, perlite, bentonite, etc.
- Moisture above absorbing ability promotes drainage and induce plant roots to decay
- Increasing the ionic exchange capacity of the soils
- Junggim structure absorbs water and nutrients ions about 20 times more than the volume of micropores.
- Prevent and prevent excessive fertilization by absorbing fertilizer ingredient when fertilizer is fertilized by absorbing pesticide to micro pore to prevent extreme outflow of pesticide ingredient.
- It has a large honeycomb structure with a large surface area and has a multi-layered structure. A large amount of far infrared rays are absorbed and stored in such a sponge-like hole, and when it receives heat, 미량 원소 물질Trace element material - B, Zn, Fe, Mn, Cu, Mo 등
- 식물의 생장에 필요한 미량 원소 공급- B, Zn, Fe, Mn, Cu, Mo, etc.
- Supply of trace elements required for plant growth

구성성분Constituent 특징Characteristic 기능성 수지 AFunctional resin A - 수분 보유능 40배 이상 및 입도 300㎛ 이하의 폴리머(Polymer)
- 수분을 흡수하면 부피가 확대되고 다시 식물이 수분을 흡수하면 다시 작아지며 수축과 팽창을 반복하여 토양 내에서 빈 공간이 생기게 되어 물리성 개량을 촉진시킴
- 수분 보유능에서 40배 이상(약 4,000% 이상)의 수분을 흡수, 저장하고 식물이 필요로 할 때 방출
- 미량 원소 및 미네랄을 함유하고 있으며 수분 함유에 따른 팽창시 방출되어 미량 영양소 및 미네랄 제공
- 관수비용이 30%이상 절감되고 이에 관수에 의한 식물이 이용하는 비료의 유실량이 적어져 사용량이 15% 이상 절감되어 유지관리 비용 절감
- 이러한 수분 보유능, 비료성분 유실량 감소 등으로 식재 초기 생존율이 증대되고 성장촉진이 되며 식물의 수확량 증대
- 이러한 수분 보유능, 비료성분 유실량 감소 등으로 주변 수질 및 토양 오염 방지A polymer having a water holding capacity of 40 times or more and a particle size of 300 占 퐉 or less;
- When the water is absorbed, the volume is enlarged. When the plant absorbs the water again, it becomes smaller again. It repeats the contraction and expansion, thereby creating voids in the soil, thereby promoting physical improvement.
- Absorbs and stores more than 40 times (about 4,000% or more) of the moisture in the water holding ability and releases when the plant needs it.
- Contains trace elements and minerals. Releases upon expansion due to water content, providing micronutrients and minerals.
- Reduced water cost by more than 30%, thus reducing the amount of fertilizer used by the irrigation water and reducing the use cost by more than 15%.
- This ability to retain moisture and reduce the amount of fertilizer component loss increases the initial survival rate of plants, promotes growth and increases the yield of plants
- Prevention of pollution of the surrounding water and soil due to such ability of water retention and reduction of fertilizer component loss 기능성 수지 BFunctional resin B - 수분 보유능 5배 이상 및 입도 0.1~10㎜의 폴리머(Polymer)
- 컬러를 가지는 물질로 구성하여 시각적 인테리어 효과 극대화
- 물 흡수 후에도 입도를 그대로 가지고 있음
- 레드, 블루, 옐로우, 그린 등의 색과 입자 크기로 투명한 화분, 유리병, 어항 등에 인공토양을 포설하여 식물을 식재함으로 시각적 효과 및 교육자재로의 활용 가능- a polymer having a water holding capacity of 5 times or more and a particle size of 0.1 to 10 mm;
- Maximize visual interior effect by composing material with color
- Even after the water absorption, the particle size remains intact.
- Artificial soil such as red, blue, yellow, green, etc., can be used as a visual effect and education material by planting plants such as transparent pots, glass bottles, 탄화물질Carbonized material - 석탄계 활성탄, 식물계 활성탄, 바텀애쉬, 왕겨훈탄, 코코넛탄, 이탄 등
- 자체에 미세기공이 많아(공극률 45~55%) 통기, 배수, 보수력 및 보비력 우수
- 강한 강도와 수명이 반영구적인 재질 특성을 가지고 있으며 식물 생장에 도움이 되는 다량의 미네랄 함유
- 양이온치환용량이 높으며, 악취 제거, 중금속 흡착 등의 작용- coal-based activated carbon, plant-based activated carbon, bottom ash, rice husk dry, coconut charcoal, peat, etc.
- It has a lot of fine pores in itself (porosity 45 ~ 55%), excellent ventilation, drainage, water holding capacity and bending strength
- It has semi-permanent material properties with strong strength and long life, and it contains a large amount of minerals to help plant growth.
- High cation exchange capacity, odor removal, heavy metal adsorption 칼슘-마그네슘 함유 비료Calcium-magnesium-containing fertilizer - 고토, 부산석고, 탄산마그네슘, 소석회 등
- 토양의 물리성 개선
- 칼슘이 서서히 용출되어 토양 내 나트륨 이온과 교환이 되며 입단화 촉진됨
- 산도 교정
- 도심지 오염 물질 및 임해매립지 토양은 산도(pH)가 알칼리성을 띄는 경우가 많아 알칼리성 토양을 개량하는 석고혼합물 이용
- 산림지역, 농사지역의 경우 석회혼합물 이용- Goto, Busan gypsum, Magnesium carbonate, Lime lime, etc.
- Improvement of physical properties of soil
- Calcium slowly dissolves and exchanges with sodium ions in the soil, facilitating the incorporation.
- pH calibration
- Urban pollutants and reclamation land Soils are often alkaline with acidity (pH), so use gypsum mixture to improve alkaline soil
- use of lime mixture in forest area and farming area 질소 함유 비료, 인 함유 비료, 칼륨 함유 비료Nitrogen-containing fertilizer, phosphorus-containing fertilizer, potassium-containing fertilizer
- 식물 생육에 필요한 3대 영양소인 질소, 인산, 칼륨 등 공급
- 다량 원소 공급
- Supplied nitrogen, phosphoric acid, potassium, etc., the three nutrients required for plant growth
- Massive element supply

하기 표 3은 본 발명의 인공토양이 가지는 전체적인 특징 및 용도를 정리한 것이다.Table 3 below summarizes the overall characteristics and uses of the artificial soil of the present invention.

전체 특징Full feature 1) 양질의 유기물과 유익 미생물 배양 공급 - 식물 생장에 적정한 토양
- 물리성, 화학성 개량, 동계 지온 상승, 토양 고결화 방지, 관수시 표토 부유, 침식, 강수시 표토 유실, 건조시 표토 비산 방지 개량 작용
- 용토 내의 유기물 작용에 의한 토양 물리성, 화학성의 개량, 유기물과 미생물의 교질 작용으로 지표 온도가 식물 생장에 맞도록 유지되어져 예상되는 동결피해 방지, 토양 입단의 떼알 조직화의 지속적 작용으로 토양의 고결화와 관수시 표토 부유, 침식, 강우시 표토 유실, 건조시 표토 비산 방지 개량 작용
2) 양이온치환용량(CEC)값을 높이는 광물질을 각각의 적정량으로 구성
- 생장에 필요한 양분의 공급과 보관할 수 있는 양이온치환용량(CEC)값을 높이는 비중 0.8~1.0의 광물질 구성으로 식재층 높이로 부족한 CEC값을 높임
3) 보수력 증대 물질의 적정량 공급 - 정상적 생장, 경제적 관리 개량 작용
- 적정의 수분 공급, 지속적 공급이 되는 물질의 공급으로 생장에 필요한 수분 공급이 되어져 정상적 생장과 관수측면의 경제성을 높임
4) 경제적 생장, 환경친화적 개량 작용 물질 공급
- 경제적 생장 촉진 물질의 작용과 시용된 무기양분, 농약의 흡수 이용율, 식물이 이용할 수 있는 형태의 수용성율, 이용할 수 있는 형태로 토양에 잔존되어있는 토양 잔존율을 높여 동 시비량 비 2배 이상의 생장량 증대
- 시용 공급된 무기양분 등의 흡수 이용율, 수용성율, 토양잔존율 증대로 관행 시비에서 이용되지 못하고 유실되는 무기양분의 유실, 용탈로 수질, 토양 환경이 오염되는 것을 예방, 방지
5) 생장에 필요한 요구도별 양분 공급 - 정상적 생장, 경제적 생장
- 질소, 인산, 칼륨 등의 생장에 필요한 삼대 필수 영양소와 다량원소, 미량원소 등을 요구도별 해당 적정량 공급으로 정상적 생장, 재배목적에 맞는 생장이 되는 개량
6) 보수력 증대, 환경친화적 개량 작용물질 공급 - 경제적 관리 개량 작용
- 보수력 증대 물질 공급과 환경친화적 개량 물질의 작용으로 관행 관수 횟수를 1/5 이하, 생장에 필요한 양분의 시용량을 1/3 이하로 절감하는 경제적 관리 개량 작용
7) 각종 컬러 및 입도크기 구현
- 인테리어 토양, 교육용 토양으로 활용 가능1) Supply of high quality organic matter and beneficial microorganism culture - Suitable soil for plant growth
- Improvement of physical property, chemical property, elevation of winter temperature, prevention of soil cementation, flooding of soil when flooded, erosion, topsoil loss during precipitation,
- Improvement of soil physical properties and chemical properties by the action of organic matter in the soil, keeping the surface temperature in accordance with the plant growth by keeping the organic matter and microorganism in colloidal action, and preventing the freezing damage, Improvement of prevention of scattering of topsoil during drying, in case of flooding and erosion during flooding, erosion,
2) Constitute each appropriate amount of minerals that increase cation exchange capacity (CEC) value
- Increase CEC value by planting layer height with minerals composition of specific gravity 0.8 ~ 1.0 which increase the value of cation exchange capacity (CEC) that can supply and store necessary nutrients for growth
3) Supply of proper amount of material to increase water holding capacity - Improvement of normal growth and economic management
- Proper water supply, continuous supply of the supply of the necessary water supply for the growth of the normal growth and improve the efficiency of the water side
4) Economic Growth, Supply of Environmentally Friendly Improving Agents
- The effects of economic growth promoting substances and the inorganic nutrients used, the absorption and utilization rate of pesticides, the water-soluble rate of plants available, and the residual rate of soil remaining in the available form, increase
- Prevention and prevention of contamination of water quality and soil environment due to loss of inorganic nutrients that are not used in customary fertilization and leaching, by leaching of inorganic nutrients, etc.
5) Nutrient supply by need for growth - normal growth, economic growth
- Three essential essential nutrients required for growth of nitrogen, phosphoric acid, potassium, etc., And massive elements and trace elements.
6) Improvement of water conservation ability, supply of environmentally friendly modified actives - Improvement of economic management
- Improvement of economic management to reduce the number of watering practices to 1/5 or less and the amount of nutrients required for growth to 1/3 or less due to the increase of water holding capacity and the operation of environmentally friendly improving substances
7) Implementation of various color and particle size
- It can be used as interior soil, educational soil 용도Usage - 가정용 화분, 화단, 정원, 베란다 및 테라스 인테리어
- 수벽, 미니 공원, 실내 및 실외 조경 사업
- 화분갈이용 토양, 컬러 토양
- 전원주택, 아파트 단지, 옥상정원, 테라스 시공
- 농사용 상토, 인공용토, 경량토
- 식물 친화적, 환경 친화적 농업 생장용
- 임해매립지, 척박지, 중금속오염지, 쓰레기매립지 등 특수 토양 개량용
- 보비력, 보수력 증대용 기능성 토양
- 교육용 토양- House pots, flower beds, garden, porch and terrace interior
- Water wall, mini park, indoor and outdoor landscaping business
- Potting soil, color soil
- Power house, apartment complex, roof garden, terrace construction
- Agricultural land, artificial soil, light soil
- Plant-friendly, environment-friendly for agricultural growth
- Improvement of special soil such as landfill, barge, heavy metal pollution site, landfill
- Functional soil for improving bibbling and water holding capacity
- Educational soil

본 발명에 따른 인공토양은 식물의 생장에 적합한 자연 토양을 대체할 수도 있으나, 바람직하게는 자연 토양과 혼합하여 사용되는 것이 바람직하다. 식물 식재층을 형성하기 위해 본 발명에 따른 인공토양과 혼합될 수 있는 자연 토양은 밭, 논, 산, 강, 임해매립지, 척박지 등과 같은 자연적인 환경에서 채취할 수 있는 흙이라면 그 종류가 크게 제한되지 않으며, 인공토양에서 부족한 천연성분을 보충하고 인공토양의 경제성을 담보하는 역할을 한다. 또한, 본 발명의 인공토양과 혼용되는 자연 토양은 인공토양을 구성하는 성분들과의 유기적 결합에 의한 상승 효과를 고려할 때 황토인 것이 바람직하다. 본 발명에 따른 인공토양은 자연 토양과 약 20:80 내지 80:20의 중량비로 혼합되어 사용될 수 있고, 40:60 내지 60:40의 중량비로 혼합되어 사용되는 것이 바람직하다.
The artificial soil according to the present invention may replace natural soil suitable for plant growth, but is preferably used in combination with natural soil. The natural soil that can be mixed with the artificial soil according to the present invention to form the planting material layer is largely limited if the soil can be collected from a natural environment such as field, rice field, mountain, river, reclaimed land, It replenishes insufficient natural ingredients in artificial soil and assures the economical efficiency of artificial soil. The natural soil mixed with the artificial soil of the present invention is preferably a loess soil in consideration of the synergistic effect by organic bonding with the components constituting the artificial soil. The artificial soil according to the present invention may be mixed with natural soil at a weight ratio of about 20:80 to 80:20, and may be used by mixing at a weight ratio of 40:60 to 60:40.

본 발명에 따른 인공토양의 제조방법은 인공토양 부분에서 전술한 구성성분의 종류, 구성성분의 기능, 구성성분의 함량 관계 등을 모두 참조하며, 이하, 본 발명에 따른 인공토양의 제조방법 중 특징적인 부분을 설명한다.The method for producing an artificial soil according to the present invention refers to the kind of the constituent components, the function of the constituent components, the content of the constituent components, and the like in the artificial soil part. Hereinafter, I will explain the part.

본 발명에 따른 인공토양의 제조방법은 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium), 로도박터 캡슐라타(Rhodobacter capsulata) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)로 이루어진 군에서 선택된 2종 이상의 미생물을 포함하는 혼합 미생물을 첨가하고 발효시켜 발효 유기물을 수득하는 단계; 및 상기 발효 유기물 100 중량부 당 광물질 50~200 중량부, 탄화물질 50~150 중량부, 흡수성 고분자 1~20 중량부 및 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합하여 최종 조성물을 수득하는 단계를 포함한다. 이때, 상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 탄화물질은 활성탄, 바텀애쉬, 왕겨훈탄, 코코넛탄 및 이탄(peat)으로 이루어진 군에서 선택된 1종 이상을 포함한다. 또한, 상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상을 포함한다. 또한, 상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체를 포함한다.The method for producing artificial soil according to the present invention is characterized in that Bacillus pumilus , Bacillus subtilis ( Bacillus subtilis), Bacillus subtilis ( Bacillus subtilis), and Bacillus subtilis are added to an organic material mixed material obtained by mixing vegetable organic materials including bark and sawdust, subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis ), Bacillus megaterium megaterium , Rhodobacter capsulata and Rhodobacter sphaeroides , and fermenting the mixture to obtain a fermented organic material; And 50 to 200 parts by weight of a mineral material, 50 to 150 parts by weight of a carbonized material, 1 to 20 parts by weight of an absorbent polymer and 10 to 100 parts by weight of a calcium-magnesium-containing fertilizer per 100 parts by weight of the fermented organic material, . At this time, the mineral includes at least one selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite. In addition, the carbonized material may include at least one selected from the group consisting of activated carbon, bottom ash, chaff hard coal, coconut charcoal and peat. The calcium-magnesium-containing fertilizer may be at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, lime lime, gypsum lime, gypsum lime and gypsum plaster, magnesium hydroxide, magnesium sulfate, At least one member selected from the group consisting of magnesium, hydroxide goto, carbonated goto, carbonated lime goto, sulfuric acid goto, lime goto, soluble phosphoric acid and goto superphosphate. Further, the water absorbing polymer may be a copolymer of a first monomer selected from carboxylic acid having an ethylenically unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenic unsaturated bond, or a copolymer having an ethylenically unsaturated bond A copolymer of a third monomer selected from an amide and an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond.

본 발명에 따른 인공토양의 제조방법 중 상기 발효 유기물을 수득하는 단계는 바람직하게는 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물을 포함하는 혼합 미생물을 첨가한 후 호기성 조건의 발효조에서 15~40일 동안 1차 발효시키고 노지에서 60~300일 동안 2차 발효시키는 것으로 구성된다.The step of obtaining the fermentation organic material according to the present invention is preferably a step of mixing the organic material mixed with the vegetable organic material including the bark and sawdust and the animal organic material including the straw and the slaughter by- Bacillus pumilus), Bacillus subtilis (Bacillus subtilis), Bacillus Lee Kenny Po Ms (Bacillus licheniformis ) and Bacillus megaterium , and at least one microorganism belonging to the genus Bacillus such as Rhodobacter capsulata or Rhodobacter sphaeroides , and then fermented for 15 to 40 days in a fermentation tank under aerobic conditions and incubated for 60 to 300 days Lt; / RTI > during the second fermentation.

상기 발효 유기물을 수득하는 단계에서 상기 유기물 혼합 원료를 구성하는 식물성 유기물 대 동물성 유기물의 중량비는 1:1 내지 1:2이고, 상기 식물성 유기물을 구성하는 수피 대 톱밥의 중량비는 1:0.5 내지 1:10이고, 상기 동물성 유기물을 구성하는 계분 대 도축 부산물의 중량비는 1:0.5 내지 1:2이고, 상기 혼합 미생물의 첨가량은 유기물 혼합 원료 100 중량부 당 0.05~1 중량부인 것이 바람직하다.The weight ratio of the vegetable organic material to the animal organic material constituting the organic material mixture raw material in the step of obtaining the fermentation organic material is 1: 1 to 1: 2, and the weight ratio of the bark to sawdust constituting the vegetable organic material is 1: 0.5 to 1: 10, and the weight ratio of the staple to the slaughter byproduct constituting the animal organic material is 1: 0.5 to 1: 2, and the amount of the mixed microorganism to be added is preferably 0.05 to 1 part by weight per 100 parts by weight of the organic material mixture.

본 발명에 따른 인공토양의 제조방법 중 상기 최종 조성물을 수득하는 단계는 바람직하게는 (a) 상기 발효 유기물을 1차 기초물질로 하여, 여기에 발효 유기물 100 중량부를 기준으로 광물질 50~200 중량부 및 탄화물질 50~150 중량부를 첨가하고 혼합하여 2차 기초물질을 제조하는 단계; (b) 상기 2차 기초물질에 발효 유기물 100 중량부를 기준으로 흡수성 고분자 1~20 중량부를 고르게 분사하여 3차 기초물질을 제조하는 단계; 및 (c) 상기 3차 기초물질에 발효 유기물 100 중량부를 기준으로 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합하여 최종 조성물을 제조하는 단계로 구성된다. 본 발명에 따른 인공토양의 구성성분 중 흡수성 고분자는 소정의 입도를 가지고 있으며, 수분을 흡수하기 때문에 분사하는 방식으로 2차 기초물질에 균일하게 흡착시킨 후 혼합하는 것이 바람직하다. 본 발명에서 2차 기초물질은 약 50~60%의 함수율을 가지기 때문에 만약 흡수성 고분자를 2차 기초물질에 분사시키지 않고 한번에 첨가하는 경우 덩어리째로 팽윤되어 균일한 혼합이 원활하지 않게 된다. 또한, 본 발명에서 2차 기초물질은 컨베이어 벨트를 통해 이동되는데, 이때 컨베이어 벨트의 온도는 원활한 혼합을 위해 약 40~60℃로 가열되는 것이 바람직하다. 또한, 상기 (c) 단계는 바람직하게는 3차 기초물질에 발효 유기물 100 중량부를 기준으로 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합한 후, 여기에 질소 함유 비료, 인 함유 비료, 칼륨 함유 비료 또는 식물의 생장에 필요한 미량 원소 함유 물질을 첨가하고 혼합하여 최종 조성물을 제조하는 단계로 구성된다.In the method for producing artificial soil according to the present invention, the step of obtaining the final composition preferably comprises: (a) using the fermentation organic substance as a primary basic substance, wherein 50 to 200 parts by weight of a mineral substance And 50 to 150 parts by weight of a carbonaceous material are added and mixed to prepare a secondary base material; (b) uniformly spraying 1 to 20 parts by weight of the water absorbent polymer on the basis of 100 parts by weight of the fermentation organic material to the secondary basic substance to prepare a tertiary basic substance; And (c) adding 10 to 100 parts by weight of calcium-magnesium-containing fertilizer based on 100 parts by weight of the fermentation organic material to the tertiary basic substance and mixing to prepare a final composition. Among the constituents of the artificial soil according to the present invention, the water absorbent polymer has a predetermined particle size and it is preferable to adsorb it uniformly on the secondary basic material in a spraying method since it absorbs moisture and then mix. In the present invention, the secondary base material has a water content of about 50 to 60%. Therefore, if the absorbent polymer is added to the secondary basic material in one shot without spraying the secondary basic material, the bulk material is swollen and the uniform mixing is not smooth. Also, in the present invention, the secondary base material is moved through the conveyor belt, wherein the temperature of the conveyor belt is preferably heated to about 40-60 ° C for smooth mixing. In the step (c), preferably, 10 to 100 parts by weight of calcium-magnesium-containing fertilizer is added to and mixed with 100 parts by weight of the fermentation organic material in the tertiary basic material, Containing fertilizer or a trace element-containing material necessary for the growth of the plant, and mixing the mixture to prepare a final composition.

또한, 상기 제1단량체는 아크릴산, 메타크릴산, 이타코닉산, 말레익산 및 푸마릭산으로 이루어진 군에서 선택되는 1종 이상이고, 제2단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다. 또한, 상기 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다.
The first monomer is at least one selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid and fumaric acid, and the second monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, At least one member selected from the group consisting of sodium, potassium, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate, and sodium fumarate. The third monomer is at least one selected from the group consisting of acrylamide, methacrylamide, maleic acid amide and fumaric acid amide. The fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, methacrylic acid At least one member selected from the group consisting of potassium, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate is preferable.

본 발명의 다른 측면은 인공토양의 용도에 관한 것으로서, 특히 인테리어용 또는 교육용으로 사용할 수 있는 인공토양 키트를 제공한다. 본 발명에 따른 인공토양 키트는 전술한 인공토양 또는 전술한 방법으로 제조된 인공토양 및 상기 인공토양과 별도로 제공되고 색상을 갖는 흡수성 고분자를 포함한다. 이때, 상기 색상을 갖는 흡수성 고분자는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체인 것을 특징으로 한다. 또한, 상기 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것이 바람직하다. 본 발명에 따른 인공토양 키트를 구성하는 흡수성 고분자는 인공토양 부분에서 전술한 기능성 수지 B와 동일한 것으로서, 입도가 기능성 수지 A보다 크고, 빨강, 파랑, 노랑, 초록, 연두 등과 같은 색상을 띄기 때문에 매우 뛰어난 시각적 효과를 가진다. 또한, 기능성 수지 B를 인공토양과 함께 포장하여 제품화하는 경우 사용자는 인공토양으로 식재층을 형성할 때 식재층 내의 기능성 수지 B의 함량을 다양한 범위에서 조절할 수 있고, 그로 인해 기능성 수지 A와의 상승 효과 및 기능성 수지 B의 시각적 효과를 모두 도모할 수 있다.
Another aspect of the invention relates to the use of artificial soil, and in particular to an artificial soil kit that can be used for interior or educational purposes. The artificial soil kit according to the present invention includes the above-described artificial soil or an artificial soil prepared by the above-mentioned method, and an absorbent polymer provided separately from the artificial soil and having a color. Here, the water-absorbing polymer having the hue is characterized by being a copolymer of a third monomer selected from an amide having an ethylenically unsaturated bond and an alkali metal salt of a carboxylic acid having an ethylenic unsaturated bond. The third monomer is at least one selected from the group consisting of acrylamide, methacrylamide, maleic acid amide and fumaric acid amide. The fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, methacrylic acid At least one member selected from the group consisting of potassium, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate is preferable. The absorbent polymer constituting the artificial soil kit according to the present invention is the same as the above-mentioned functional resin B in the artificial soil part and has a particle size larger than the functional resin A and has a color such as red, blue, yellow, green, It has excellent visual effect. In addition, when the functional resin B is packaged together with artificial soil, the user can control the content of the functional resin B in the plant material layer in various ranges when the plant material layer is formed of the artificial soil, And the visual effect of the functional resin B can all be achieved.

이하, 본 발명을 실시예를 통하여 보다 구체적으로 설명한다. 다만, 하기 실시예는 본 발명의 기술적 특징을 명확하게 예시하기 위한 것일 뿐 본 발명의 보호범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to examples. However, the following examples are intended to clearly illustrate the technical features of the present invention and do not limit the scope of protection of the present invention.

1. 인공토양의 제조1. Manufacture of artificial soil

(1) A 타입의 인공토양 제조(1) Production of artificial soil of type A

제조예 1.Production Example 1

도축 부산물 20 중량부, 계분 30 중량부, 수피 10 중량부 및 톱밥 40 중량부를 혼합한 유기물 혼합 원료를 로터리식 발효조에 넣고, 여기에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis) 및 로도박터 캡슐라타(Rhodobacter capsulata)를 포함하는 혼합 미생물 0.1 중량부를 접종한 후 약 15일 동안 1차 발효시켜 1차 발효 유기물을 수득하였다. 1차 발효시 발효조 바닥에 구비된 산소 공급 장치를 이용하여 호기 조건을 유지하였고, 발효조 내에 구비된 임펠러로 유기물 혼합 원료와 혼합 미생물을 고르게 교반하였다. 1차 발효시 발효조 내 온도 프로파일은 초기에는 40℃ 이하로 유지되었다가 이후 점진적으로 80℃까지 상승하였다. 1차 발효된 유기물은 함수율이 약 50%이었고, 산도는 약 알칼리성이었다. 1차 발효된 유기물을 발효조에서 꺼내어 노지에 방치하고 약 300일 동안 2차 발효시켜 2차 발효 유기물을 수득하였다. 2차 발효시 10일 간격으로 1차 발효 유기물을 뒤집어서 산소를 전체적으로 공급하고 혐기성 발효를 방지하였다. 2차 발효 유기물은 함수율이 약 30%이었고, 총 유기물 대 질소의 비(OM/N)가 약 27이었다.20 parts by weight of slaughter by-products, 30 parts by weight of a grain, 10 parts by weight of bark, and 40 parts by weight of sawdust were placed in a rotary fermenter, to which Bacillus pumilus), Bacillus subtilis (Bacillus Subtilis and Rhodobacter capsulata were inoculated and then primary fermented for about 15 days to obtain a primary fermentation organism. During the first fermentation, the aerobic condition was maintained by using the oxygen supply device provided at the bottom of the fermenter, and the organic material mixture and the mixed microorganism were evenly stirred with the impeller provided in the fermenter. During the first fermentation, the temperature profile in the fermenter initially remained below 40 ° C, then gradually increased to 80 ° C. The primary fermented organic matter had a water content of about 50%, and the acidity was weakly alkaline. The primary fermented organic matter was taken out of the fermentation tank, left in the oven and subjected to secondary fermentation for about 300 days to obtain a secondary fermentation organism. During the second fermentation, the primary fermentation organism was turned over at intervals of 10 days to supply oxygen as a whole and prevent anaerobic fermentation. The secondary fermentation organic matter had a water content of about 30% and a ratio of total organic matter to nitrogen (OM / N) of about 27.

이후, 상기 2차 발효 유기물 100 중량부, 제오라이트 100 중량부 및 바텀애쉬 100 중량부를 균일하게 혼합하여 1차 혼합물을 제조하였다. 이후, 상기 1차 혼합물을 컨베이어 벨트로 이동시키면서 1차 혼합물 위에 흡습성 고분자인 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 1.75 중량부를 고르게 분사하고 약 40~60℃에서 흡착시켜 2차 혼합물을 제조하였다. 이후, 상기 2차 혼합물에 칼슘-마그네슘 함유 비료(소석회 비료와 수산화고토 비료를 동량으로 혼합한 것) 50 중량부를 첨가하고 균일하게 혼합하여 3차 혼합물 형태의 인공토양을 제조하였다.
Then, 100 parts by weight of the secondary fermentation organic material, 100 parts by weight of zeolite and 100 parts by weight of bottom ash were uniformly mixed to prepare a primary mixture. Then, while the primary mixture was transferred to a conveyor belt, a white acrylic acid / sodium acrylate copolymer, which is a hygroscopic polymer, was added to the primary mixture. CAS registration number: 9033-79-8; 1.75 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x was uniformly sprayed and adsorbed at about 40 to 60 ° C to prepare a secondary mixture. Then, 50 parts by weight of a calcium-magnesium-containing fertilizer (a mixture of the same amount of calcium hydroxide fertilizer and hydroxide gypsum fertilizer) was added to the secondary mixture and uniformly mixed to prepare a tertiary mixture type artificial soil.

제조예 2.Production Example 2

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 3.5 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; An artificial soil was prepared in the same manner as in Preparation Example 1 except that 3.5 parts by weight of the molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x was used.

제조예 3.Production Example 3

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 7.0 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; An artificial soil was prepared in the same manner as in Preparation Example 1, except that 7.0 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x was used.

제조예 4.Production Example 4

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 0.875 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 0.875 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 0.875 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ) Were used in place of 0.875 parts by weight of the water-soluble polymer.

제조예 5.Production Example 5

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 1.75 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 1.75 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 1.75 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ) Was used instead of 1.75 parts by weight of a water-soluble organic solvent.

제조예 6.Production Example 6

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 3.5 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 3.5 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 3.5 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ) Was used in place of 3.5 parts by weight of the water-soluble polymer.

비교제조예 1.Comparative Production Example 1

도축 부산물 20 중량부, 계분 30 중량부, 수피 10 중량부 및 톱밥 40 중량부를 혼합한 유기물 혼합 원료를 로터리식 발효조에 넣고, 여기에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis) 및 로도박터 캡슐라타(Rhodobacter capsulata)를 포함하는 혼합 미생물 0.1 중량부를 접종한 후 약 15일 동안 1차 발효시켜 1차 발효 유기물을 수득하였다. 1차 발효시 발효조 바닥에 구비된 산소 공급 장치를 이용하여 호기 조건을 유지하였고, 발효조 내에 구비된 임펠러로 유기물 혼합 원료와 혼합 미생물을 고르게 교반하였다. 1차 발효시 발효조 내 온도 프로파일은 초기에는 40℃ 이하로 유지되었다가 이후 점진적으로 80℃까지 상승하였다. 1차 발효된 유기물은 함수율이 약 50%이었고, 산도는 약 알칼리성이었다. 1차 발효된 유기물을 발효조에서 꺼내어 노지에 방치하고 약 300일 동안 2차 발효시켜 2차 발효 유기물을 수득하였다. 2차 발효시 10일 간격으로 1차 발효 유기물을 뒤집어서 산소를 전체적으로 공급하고 혐기성 발효를 방지하였다. 2차 발효 유기물은 함수율이 약 30%이었고, 총 유기물 대 질소의 비(OM/N)가 약 27이었다.20 parts by weight of slaughter by-products, 30 parts by weight of a grain, 10 parts by weight of bark, and 40 parts by weight of sawdust were placed in a rotary fermenter, to which Bacillus pumilus), Bacillus subtilis (Bacillus Subtilis and Rhodobacter capsulata were inoculated and then primary fermented for about 15 days to obtain a primary fermentation organism. During the first fermentation, the aerobic condition was maintained by using the oxygen supply device provided at the bottom of the fermenter, and the organic material mixture and the mixed microorganism were evenly stirred with the impeller provided in the fermenter. During the first fermentation, the temperature profile in the fermenter initially remained below 40 ° C, then gradually increased to 80 ° C. The primary fermented organic matter had a water content of about 50%, and the acidity was weakly alkaline. The primary fermented organic matter was taken out of the fermentation tank, left in the oven and subjected to secondary fermentation for about 300 days to obtain a secondary fermentation organism. During the second fermentation, the primary fermentation organism was turned over at intervals of 10 days to supply oxygen as a whole and prevent anaerobic fermentation. The secondary fermentation organic matter had a water content of about 30% and a ratio of total organic matter to nitrogen (OM / N) of about 27.

이후, 상기 2차 발효 유기물 100 중량부, 제오라이트 100 중량부 및 바텀애쉬 100 중량부를 균일하게 혼합하여 1차 혼합물을 제조하였다. 이후, 상기 1차 혼합물에 칼슘-마그네슘 함유 비료(소석회 비료와 수산화고토 비료를 동량으로 혼합한 것) 50 중량부를 첨가하고 균일하게 혼합하여 2차 혼합물 형태의 인공토양을 제조하였다.
Then, 100 parts by weight of the secondary fermentation organic material, 100 parts by weight of zeolite and 100 parts by weight of bottom ash were uniformly mixed to prepare a primary mixture. Thereafter, 50 parts by weight of a calcium-magnesium-containing fertilizer (a mixture of the same amount of calcium hydroxide fertilizer and hydroxyapatite fertilizer) was added to the primary mixture and uniformly mixed to prepare a secondary mixture type artificial soil.

(2) B 타입의 인공토양 제조(2) Production of artificial soil of type B

제조예 7.Production Example 7

도축 부산물 40 중량부, 계분 20 중량부, 수피 20 중량부 및 톱밥 20 중량부를 혼합한 유기물 혼합 원료를 로터리식 발효조에 넣고, 여기에 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)를 포함하는 혼합 미생물 0.5 중량부를 접종한 후 약 40일 동안 1차 발효시켜 1차 발효 유기물을 수득하였다. 1차 발효시 발효조 바닥에 구비된 산소 공급 장치를 이용하여 호기 조건을 유지하였고, 발효조 내에 구비된 임펠러로 유기물 혼합 원료와 혼합 미생물을 고르게 교반하였다. 1차 발효시 발효조 내 온도 프로파일은 초기에는 40℃ 이하로 유지되었다가 이후 점진적으로 75℃까지 상승하였다. 1차 발효된 유기물은 함수율이 약 58%이었고, 산도는 약 알칼리성이었다. 1차 발효된 유기물을 발효조에서 꺼내어 노지에 방치하고 약 100일 동안 2차 발효시켜 2차 발효 유기물을 수득하였다. 2차 발효시 5일 간격으로 1차 발효 유기물을 뒤집어서 산소를 전체적으로 공급하고 혐기성 발효를 방지하였다. 2차 발효 유기물은 함수율이 약 34%이었고, 총 유기물 대 질소의 비(OM/N)가 약 32이었다.40 parts by weight of slaughter by-products, 20 parts by weight of grain, 20 parts by weight of bark, and 20 parts by weight of sawdust were placed in a rotary fermenter, followed by addition of Bacillus subtilis licheniformis ), Bacillus megaterium megaterium and Rhodobacter sphaeroides , and then primary fermentation was carried out for about 40 days to obtain a primary fermentation organism. During the first fermentation, the aerobic condition was maintained by using the oxygen supply device provided at the bottom of the fermenter, and the organic material mixture and the mixed microorganism were evenly stirred with the impeller provided in the fermenter. During the first fermentation, the temperature profile in the fermenter initially remained below 40 ° C, then gradually increased to 75 ° C. The primary fermented organic matter had a water content of about 58%, and the acidity was weakly alkaline. The first fermented organic matter was taken out of the fermenter, allowed to stand in the oven, and subjected to secondary fermentation for about 100 days to obtain a secondary fermentation organism. During the second fermentation, the primary fermentation organic material was turned over at 5-day intervals to supply oxygen as a whole and prevent anaerobic fermentation. The secondary fermentation organic matter had a water content of about 34% and a ratio of total organic matter to nitrogen (OM / N) of about 32.

이후, 상기 2차 발효 유기물 100 중량부, 제오라이트 100 중량부, 바텀애쉬 100 중량부 및 황토 150 중량부를 균일하게 혼합하여 1차 혼합물을 제조하였다. 이후, 상기 1차 혼합물을 컨베이어 벨트로 이동시키면서 1차 혼합물 위에 흡습성 고분자인 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 2.5 중량부를 고르게 분사하고 약 40~60℃에서 흡착시켜 2차 혼합물을 제조하였다. 이후, 상기 2차 혼합물에 칼슘-마그네슘 함유 비료(부산석고 비료와 탄산고토 비료를 동량으로 혼합한 것) 50 중량부를 첨가하고 균일하게 혼합하여 3차 혼합물 형태의 인공토양을 제조하였다.
Then, 100 parts by weight of the secondary fermentation organic material, 100 parts by weight of zeolite, 100 parts by weight of bottom ash and 150 parts by weight of yellow soil were uniformly mixed to prepare a primary mixture. Then, while the primary mixture was transferred to a conveyor belt, a white acrylic acid / sodium acrylate copolymer, which is a hygroscopic polymer, was added to the primary mixture. CAS registration number: 9033-79-8; 2.5 parts by weight of (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x] was uniformly sprayed and adsorbed at about 40 to 60 ° C to prepare a secondary mixture. Then, 50 parts by weight of a calcium-magnesium-containing fertilizer (a mixture of an equivalent amount of a gypsum fertilizer and a carbonate goto fertilizer) was added to the secondary mixture and uniformly mixed to prepare a tertiary mixture type artificial soil.

제조예 8.Production Example 8

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 5.0 중량부를 사용한 점을 제외하고는 제조예 7과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; An artificial soil was prepared in the same manner as in Production Example 7, except that 5.0 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x was used.

제조예 9.Production Example 9

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 10.0 중량부를 사용한 점을 제외하고는 제조예 7과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; An artificial soil was prepared in the same manner as in Production Example 7 except that 10.0 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x was used.

제조예 10.Production Example 10.

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 1.25 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 1.25 중량부를 사용한 점을 제외하고는 제조예 7과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 1.25 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ) Was used in place of 1.25 parts by weight of the water-soluble polymer.

제조예 11.Production Example 11.

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 2.5 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 2.5 중량부를 사용한 점을 제외하고는 제조예 7과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 2.5 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and 2 parts by weight of a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ), 2.5 parts by weight, were used.

제조예 12.Production Example 12.

흡습성 고분자로 백색의 아크릴산/아크릴산나트륨 공중합체[Acrylic acid/sodium acrylate copolymer; CAS 등록번호 : 9033-79-8; 분자식 : (C3H4O2.C3H3O2.Na)x] 5.0 중량부 및 청색의 아크릴아마이드/아크릴산칼륨 공중합체(Acrylamide/potassium acrylate copolymer; CAS 등록번호 : 31212-13-2) 5.0 중량부를 사용한 점을 제외하고는 제조예 7과 동일한 방법으로 인공토양을 제조하였다.
As a hygroscopic polymer, white acrylic acid / sodium acrylate copolymer [Acrylic acid / sodium acrylate copolymer; CAS registration number: 9033-79-8; 5.0 parts by weight of a molecular formula: (C 3 H 4 O 2 .C 3 H 3 O 2 .Na) x and a blue acrylamide / potassium acrylate copolymer (CAS registration number: 31212-13-2 ), 5.0 parts by weight were used in place of the water-soluble organic solvent.

비교제조예 2.Comparative Preparation Example 2

도축 부산물 40 중량부, 계분 20 중량부, 수피 20 중량부 및 톱밥 20 중량부를 혼합한 유기물 혼합 원료를 로터리식 발효조에 넣고, 여기에 바실러스 리케니포미스(Bacillus licheniformis), 바실러스 메가테리움(Bacillus megaterium) 및 로도박터 스페로이드스(Rhodobacter sphaeroides)를 포함하는 혼합 미생물 0.5 중량부를 접종한 후 약 40일 동안 1차 발효시켜 1차 발효 유기물을 수득하였다. 1차 발효시 발효조 바닥에 구비된 산소 공급 장치를 이용하여 호기 조건을 유지하였고, 발효조 내에 구비된 임펠러로 유기물 혼합 원료와 혼합 미생물을 고르게 교반하였다. 1차 발효시 발효조 내 온도 프로파일은 초기에는 40℃ 이하로 유지되었다가 이후 점진적으로 75℃까지 상승하였다. 1차 발효된 유기물은 함수율이 약 58%이었고, 산도는 약 알칼리성이었다. 1차 발효된 유기물을 발효조에서 꺼내어 노지에 방치하고 약 100일 동안 2차 발효시켜 2차 발효 유기물을 수득하였다. 2차 발효시 5일 간격으로 1차 발효 유기물을 뒤집어서 산소를 전체적으로 공급하고 혐기성 발효를 방지하였다. 2차 발효 유기물은 함수율이 약 34%이었고, 총 유기물 대 질소의 비(OM/N)가 약 32이었다.40 parts by weight of slaughter by-products, 20 parts by weight of grain, 20 parts by weight of bark, and 20 parts by weight of sawdust were placed in a rotary fermenter, followed by addition of Bacillus subtilis licheniformis ), Bacillus megaterium megaterium and Rhodobacter sphaeroides , and then primary fermentation was carried out for about 40 days to obtain a primary fermentation organism. During the first fermentation, the aerobic condition was maintained by using the oxygen supply device provided at the bottom of the fermenter, and the organic material mixture and the mixed microorganism were evenly stirred with the impeller provided in the fermenter. During the first fermentation, the temperature profile in the fermenter initially remained below 40 ° C, then gradually increased to 75 ° C. The primary fermented organic matter had a water content of about 58%, and the acidity was weakly alkaline. The first fermented organic matter was taken out of the fermenter, allowed to stand in the oven, and subjected to secondary fermentation for about 100 days to obtain a secondary fermentation organism. During the second fermentation, the primary fermentation organic material was turned over at 5-day intervals to supply oxygen as a whole and prevent anaerobic fermentation. The secondary fermentation organic matter had a water content of about 34% and a ratio of total organic matter to nitrogen (OM / N) of about 32.

이후, 상기 2차 발효 유기물 100 중량부, 제오라이트 100 중량부, 바텀애쉬 100 중량부 및 황토 150 중량부를 균일하게 혼합하여 1차 혼합물을 제조하였다. 이후, 상기 1차 혼합물에 칼슘-마그네슘 함유 비료(부산석고 비료와 탄산고토 비료를 동량으로 혼합한 것) 50 중량부를 첨가하고 균일하게 혼합하여 2차 혼합물 형태의 인공토양을 제조하였다.
Then, 100 parts by weight of the secondary fermentation organic material, 100 parts by weight of zeolite, 100 parts by weight of bottom ash and 150 parts by weight of yellow soil were uniformly mixed to prepare a primary mixture. Then, 50 parts by weight of a calcium-magnesium-containing fertilizer (a mixture of an equal amount of a gypsum fertilizer and a carbonate goto fertilizer) was added to the above primary mixture and uniformly mixed to prepare a secondary mixture type artificial soil.

2. 인공토양의 물성 시험2. Physical properties of artificial soil

(1) A 타입 인공토양의 물성 시험(1) Property test of type A artificial soil

제조예 1 내지 제조예 6 및 비교제조예 1에서 제조한 인공토양의 보수력, 보비력 및 수질에 대한 영향을 아래와 같은 방법으로 시험하였다.The effects of the artificial soil prepared in Preparation Examples 1 to 6 and Comparative Preparation Example 1 on the water holding capacity, bravely strength and water quality were tested by the following methods.

하부에 미세한 개구를 가진 시험관을 준비한 후 여기에 자갈을 충전하여 4㎝ 높이의 배수층을 형성하였다. 이후, 시험관 내부의 배수층 위에 인공토양을 200g씩 충전하여 12㎝ 높이의 인공토양층을 형성하였다. 이후, 시험관 상부에 수돗물 100㎖를 공급하고 24시간이 지났을 때 시험관을 투과한 물의 양을 측정하였다(1차 투과 시험). 이후, 시험관 상부에 수돗물 50㎖를 공급하고 24시간이 지났을 때 시험관을 투과한 물의 양 및 인공토양층의 높이를 측정하였다(2차 투과 시험). 또한, 1차 투과수와 2차 투과수를 합한 총 투과수의 생물학적 산소 요구량(BOD), 화학적 산소 요구량(COD), 총 인 함량 및 총 질소 함량을 측정하여 인공토양의 수질에 대한 영향을 평가하였다.A test tube with fine openings at the bottom was prepared and filled with gravel to form a drainage layer having a height of 4 cm. Then, 200g of artificial soil was charged on the drainage layer inside the test tube to form a 12cm high artificial soil layer. Thereafter, 100 ml of tap water was supplied to the top of the test tube, and the amount of water passed through the test tube was measured after 24 hours (first permeation test). Then, 50 ml of tap water was supplied to the top of the test tube, and the amount of water passed through the test tube and the height of the artificial soil layer after 24 hours were measured (secondary permeation test). In addition, the biological oxygen demand (BOD), chemical oxygen demand (COD), total phosphorus content and total nitrogen content of the total permeated water combined with the primary permeated water and the secondary permeated water were measured to evaluate the effect on the water quality of the artificial soil Respectively.

하기 표 4는 인공토양층 별로 1차 투과 시험시 투과수의 양, 2차 투과 시험시 투과수의 양 및 총 투과수의 양을 나타낸 것이다. 또한, 하기 표 5는 인공토양층 별로 2차 투과 시험 종료 후 인공토양층의 높이를 나타낸 것이다. 또한, 하기 표 6은 인공토양층 별로 총 투과수의 생물학적 산소 요구량(BOD), 화학적 산소 요구량(COD), 총 인 함량 및 총 질소 함량을 나타낸 것이다.Table 4 shows the amount of permeated water in the first permeation test, the amount of permeated water in the second permeation test, and the amount of total permeated water in the artificial soil layer. Table 5 below shows the height of the artificial soil layer after completion of the secondary permeation test for each artificial soil layer. Table 6 below shows the biological oxygen demand (BOD), chemical oxygen demand (COD), total phosphorus content and total nitrogen content of the total permeate water for each artificial soil layer.

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer 1차 투과수 양(㎖)Amount of primary permeated water (ml) 2차 투과수 양(㎖)Secondary permeated water (ml) 총 투과수 양(㎖)Total permeated water (ml) 제조예 1Production Example 1 3333 4141 7474 제조예 2Production Example 2 2929 3434 6363 제조예 3Production Example 3 2222 2525 4747 제조예 4Production Example 4 3030 4141 7171 제조예 5Production Example 5 2222 4141 6363 제조예 6Production Example 6 1616 3030 4646 비교제조예 1Comparative Preparation Example 1 4343 4141 8484

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer 2차 투과 시험 후 인공토양층 높이(㎝)After the second permeation test, the height of artificial soil layer (㎝) 제조예 1Production Example 1 12.412.4 제조예 2Production Example 2 13.113.1 제조예 3Production Example 3 14.014.0 제조예 4Production Example 4 12.812.8 제조예 5Production Example 5 13.413.4 제조예 6Production Example 6 14.514.5 비교제조예 1Comparative Preparation Example 1 10.910.9

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer BOD
(㎎/ℓ)BOD
(Mg / l) COD
(㎎/ℓ)COD
(Mg / l) 총 인 함량
(㎎/ℓ)Total phosphorus content
(Mg / l) 총 질소 함량
(㎎/ℓ)Total nitrogen content
(Mg / l) 제조예 1Production Example 1 1.11.1 5.25.2 2.982.98 3.513.51 제조예 2Production Example 2 0.60.6 4.94.9 2.622.62 3.073.07 제조예 3Production Example 3 0.40.4 5.05.0 2.102.10 3.053.05 제조예 4Production Example 4 1.31.3 5.05.0 2.932.93 3.673.67 제조예 5Production Example 5 0.50.5 4.34.3 2.752.75 3.373.37 제조예 6Production Example 6 0.40.4 4.04.0 2.212.21 2.932.93 비교제조예 1Comparative Preparation Example 1 2.02.0 8.78.7 2.972.97 3.713.71

(2) B 타입 인공토양의 물성 시험(2) Test of physical properties of artificial soil of type B

제조예 7 내지 제조예 12 및 비교제조예 2에서 제조한 인공토양에 대해 A 타입 인공토양의 물성 시험과 동일한 방법으로 인공토양의 보수력, 보비력 및 수질에 대한 영향을 측정하였다.The effects on the water holding capacity, bending strength and water quality of the artificial soil were measured in the same manner as the physical property test of the artificial soil type A with respect to the artificial soil prepared in Production Examples 7 to 12 and Comparative Production Example 2.

하기 표 7은 인공토양층 별로 1차 투과 시험시 투과수의 양, 2차 투과 시험시 투과수의 양 및 총 투과수의 양을 나타낸 것이다. 또한, 하기 표 8은 인공토양층 별로 2차 투과 시험 종료 후 인공토양층의 높이를 나타낸 것이다. 또한, 하기 표 9는 인공토양층 별로 총 투과수의 생물학적 산소 요구량(BOD), 화학적 산소 요구량(COD), 총 인 함량 및 총 질소 함량을 나타낸 것이다.Table 7 shows the amount of permeated water in the first permeation test, the amount of permeated water in the second permeation test, and the amount of total permeated water in the artificial soil layer. Table 8 below shows the height of the artificial soil layer after completion of the second permeation test for each artificial soil layer. Table 9 below shows the BOD, COD, total phosphorus, and total nitrogen content of total permeable water for each artificial soil layer.

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer 1차 투과수 양(㎖)Amount of primary permeated water (ml) 2차 투과수 양(㎖)Secondary permeated water (ml) 총 투과수 양(㎖)Total permeated water (ml) 제조예 7Production Example 7 3232 4040 7272 제조예 8Production Example 8 2828 3333 6161 제조예 9Production Example 9 2121 2424 4545 제조예 10Production Example 10 2929 4040 6969 제조예 11Production Example 11 2121 4040 6161 제조예 12Production Example 12 1616 3030 4646 비교제조예 2Comparative Production Example 2 4242 4040 8282

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer 2차 투과 시험 후 인공토양층 높이(㎝)After the second permeation test, the height of artificial soil layer (㎝) 제조예 7Production Example 7 12.812.8 제조예 8Production Example 8 13.513.5 제조예 9Production Example 9 14.414.4 제조예 10Production Example 10 13.213.2 제조예 11Production Example 11 13.813.8 제조예 12Production Example 12 14.914.9 비교제조예 2Comparative Production Example 2 11.211.2

인공토양층 형성시 사용한 인공토양 구분Artificial Soil used in Formation of Artificial Soil Layer BOD
(㎎/ℓ)BOD
(Mg / l) COD
(㎎/ℓ)COD
(Mg / l) 총 인 함량
(㎎/ℓ)Total phosphorus content
(Mg / l) 총 질소 함량
(㎎/ℓ)Total nitrogen content
(Mg / l) 제조예 7Production Example 7 1.11.1 5.05.0 2.892.89 3.413.41 제조예 8Production Example 8 0.60.6 4.84.8 2.542.54 2.982.98 제조예 9Production Example 9 0.40.4 4.94.9 2.042.04 2.962.96 제조예 10Production Example 10 1.31.3 4.94.9 2.842.84 3.563.56 제조예 11Production Example 11 0.50.5 4.24.2 2.672.67 3.273.27 제조예 12Production Example 12 0.40.4 3.93.9 2.152.15 2.842.84 비교제조예 2Comparative Production Example 2 1.91.9 8.48.4 2.882.88 3.603.60

3. 인공토양을 이용한 식물 생장 시험3. Plant growth test using artificial soil

식재용 포트(pot)에 염분에 의해 오염된 토양(대조 시험군, 총 2개 포트), 제조예 2에서 제조한 인공토양과 염분에 의해 오염된 토양을 동량으로 혼합한 토양(A 타입 시험군, 총 8개 포트), 제조예 8에서 제조한 인공토양(B 타입 시험군, 총 8개 포트)을 충전하여 식재층을 형성하고, 여기에 보리 종자를 파종한 후 15일이 경과하였을 때 발아율과 생장율을 측정하였다.(Soil) contaminated by saline (control test group, total of 2 ports), artificial soil prepared in Preparation Example 2 and soil contaminated with salt by the same amount (soil type A test group , Total of 8 ports), and the artificial soil (B type test group, total 8 ports) manufactured in Production Example 8 was filled to form a planting layer. When 15 days passed after seeding the barley seeds, And growth rate were measured.

또한, 유채 종자에 대해서도 동일한 생장 시험을 진행하였다.The same growth test was also performed on rapeseed seeds.

도 1은 시험군별 보리 종자 및 유채 종자의 생장 시험 결과를 나타낸 사진이고, 표 10은 이를 정량적인 데이터로 표시한 것이다.Fig. 1 is a photograph showing growth test results of barley seeds and rapeseed seeds according to the test group, and Table 10 shows quantitative data thereof.

시험군 구분Test group classification 평균 발아율(%)Average germination rate (%) 평균 생장율(%)Average Growth Rate (%) 보리barley 유채Rapeseed 보리barley 유채Rapeseed 대조 시험군Control test group 00 25.0025.00 00 6.686.68 A 타입 시험군A type test group 77.8877.88 79.3779.37 73.9473.94 56.0756.07 B 타입 시험군B type test group 83.6583.65 83.1283.12 88.3488.34 80.5380.53

* 상기 표 10에서 각 식물 종자의 평균 생장율은 A 타입 시험군 및 B 타입 시험군에 존재하는 총 16개의 식재용 포트 중에서 최대 생장량을 보인 식재용 포트의 값을 100으로 하여 상대적으로 나타낸 것이다.
* In Table 10, the average growth rate of each plant seed is represented by a value of 100 for the planting pot showing the maximum growth among 16 planting pots existing in the A-type test group and the B-type test group.

이상에서와 같이 본 발명을 상기의 실시예를 통해 설명하였지만 본 발명이 반드시 여기에만 한정되는 것은 아니며 본 발명의 범주와 사상을 벗어나지 않는 범위 내에서 다양한 변형실시가 가능함은 물론이다. 따라서, 본 발명의 보호범위는 본 발명에 첨부된 특허청구의 범위에 속하는 모든 실시 형태를 포함하는 것으로 해석되어야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Therefore, the scope of the present invention should be construed as including all embodiments falling within the scope of the appended claims.

Claims (16)

발효 유기물 100 중량부 당 광물질 50~200 중량부, 바텀애쉬 50~150 중량부, 칼슘-마그네슘 함유 비료 10~100 중량부 및 흡수성 고분자 1~20 중량부를 포함하는 조성물 형태의 인공토양으로서,
상기 발효 유기물은 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물로 구성되는 혼합 미생물을 첨가하고 발효시켜 형성한 것이고,
상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택되는 1종 이상으로 구성되고,
상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상으로 구성되고,
상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체로 구성되고,
상기 제1단량체는 아크릴산, 메타크릴산, 이타코닉산, 말레익산 및 푸마릭산으로 이루어진 군에서 선택되는 1종 이상이고, 제2단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상이고,
상기 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것을 특징으로 하는 식물 식재용 인공토양.
An artificial soil in the form of a composition comprising 50 to 200 parts by weight of mineral matter per 100 parts by weight of fermentation organic matter, 50 to 150 parts by weight of bottom ash, 10 to 100 parts by weight of calcium-magnesium containing fertilizer and 1 to 20 parts by weight of water absorbing polymer,
Wherein the fermentation organic material is selected from the group consisting of Bacillus pumilus , Bacillus subtilis , Bacillus subtilis , and Bacillus subtilis to an organic material mixed raw material obtained by mixing vegetable organic materials including bark and sawdust, One or more microorganisms of the genus Bacillus selected from the group consisting of Bacillus licheniformis and Bacillus megaterium and at least one strain selected from Rhodobacter capsulata or Rhodobacter sphaeroides Which is formed by adding a mixed microorganism composed of microorganisms of the genus Escherichia,
Wherein the mineral is at least one selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite,
Wherein the calcium-magnesium-containing fertilizer is at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, heavy lime lime, gypsum, lime lime and gypsum plaster and magnesium hydroxide, magnesium sulfate, magnesium carbonate, At least one member selected from the group consisting of hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides,
Wherein the water absorbing polymer is a copolymer of a first monomer selected from a carboxylic acid having an ethylenically unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond or an amide having an ethylenically unsaturated bond A copolymer of a fourth monomer selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond and a third monomer to be selected,
Wherein the first monomer is at least one selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid and fumaric acid, and the second monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, potassium methacrylate , At least one selected from the group consisting of sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate,
Wherein the third monomer is at least one selected from the group consisting of acrylamide, methacrylamide, maleic acid amide and fumaric acid amide, and the fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, potassium methacrylate, Wherein the at least one selected from the group consisting of potassium bicarbonate, potassium bicarbonate, potassium bicarbonate, potassium bicarbonate, potassium bicarbonate, potassium bicarbonate, potassium bicarbonate, potassium bicarbonate,
제 1항에 있어서, 상기 발효 유기물은 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물로 구성되는 혼합 미생물을 첨가한 후 호기성 조건의 발효조에서 15~40일 동안 1차 발효하고 노지에서 60~300일 동안 2차 발효하여 형성한 것을 특징으로 하는 식물 식재용 인공토양.
The fermentation organic material according to claim 1, wherein the fermentation organic material is selected from the group consisting of Bacillus pumilus , Bacillus subtilis , and Bacillus subtilis to an organic material mixed raw material obtained by mixing vegetable organic materials including bark and sawdust, ), Bacillus licheniformis and Bacillus megaterium , and one or more microorganisms selected from the group consisting of Rhodobacter capsulata or Rhodobacter sphaeroides , In a fermentation tank under aerobic condition for 15 to 40 days and secondary fermentation for 60 to 300 days in a non-fermented state. The microorganism according to any one of claims 1 to 5, Artificial soil for planting.
제 1항에 있어서, 상기 유기물 혼합 원료를 구성하는 식물성 유기물 대 동물성 유기물의 중량비는 1:1 내지 1:2이고, 상기 식물성 유기물을 구성하는 수피 대 톱밥의 중량비는 1:0.5 내지 1:10이고, 상기 동물성 유기물을 구성하는 계분 대 도축 부산물의 중량비는 1:0.5 내지 1:2이고, 상기 혼합 미생물의 첨가량은 유기물 혼합 원료 100 중량부 당 0.05~1 중량부인 것을 특징으로 하는 식물 식재용 인공토양.
The method of claim 1, wherein the weight ratio of the vegetable organic material to the animal organic material constituting the organic material mixture material is 1: 1 to 1: 2, and the weight ratio of the bark to sawdust constituting the vegetable organic material is 1: 0.5 to 1:10 , The weight ratio of the staple to the slaughter by-product constituting the animal organic material is 1: 0.5 to 1: 2, and the amount of the mixed microorganism to be added is 0.05 to 1 part by weight per 100 parts by weight of the organic material mixed material. .
제 1항에 있어서, 상기 조성물은 질소 함유 비료, 인 함유 비료, 칼륨 함유 비료 또는 식물의 생장에 필요한 미량 원소 함유 물질을 더 포함하는 것을 특징으로 하는 식물 식재용 인공토양.
The artificial soil for planting material according to claim 1, wherein the composition further comprises a nitrogen-containing fertilizer, a phosphorus-containing fertilizer, a potassium-containing fertilizer or a trace element-containing substance necessary for plant growth.
삭제delete 삭제delete 삭제delete 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물로 구성되는 혼합 미생물을 첨가하고 발효시켜 발효 유기물을 수득하는 단계; 및
상기 발효 유기물 100 중량부 당 광물질 50~200 중량부, 바텀애쉬 50~150 중량부, 흡수성 고분자 1~20 중량부 및 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합하여 최종 조성물을 수득하는 단계를 포함하고,
상기 광물질은 제오라이트, 일라이트(illite), 펄라이트(perlite), 버미큐라이트 및 벤토나이트로 이루어진 군에서 선택되는 1종 이상으로 구성되고,
상기 칼슘-마그네슘 함유 비료는 생석회, 소석회, 탄산석회, 규산석회, 과인산석회, 중과인산석회, 석고, 부산소석회 및 부산석고로 이루어진 군에서 선택되는 1종 이상과 수산화마그네슘, 황산마그네슘, 탄산마그네슘, 수산화고토, 탄산고토, 탄산석회고토, 황산고토, 석회고토, 용성인산 및 고토과인산으로 이루어진 군에서 선택되는 1종 이상으로 구성되고,
상기 흡수성 고분자는 에틸렌성 불포화 결합을 가진 카르복실산에서 선택되는 제1단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제2단량체의 공중합체 또는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체로 구성되고,
상기 제1단량체는 아크릴산, 메타크릴산, 이타코닉산, 말레익산 및 푸마릭산으로 이루어진 군에서 선택되는 1종 이상이고, 제2단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상이고,
상기 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것을 특징으로 하는 식물 식재용 인공토양의 제조방법.
 Bacillus pumilus , Bacillus subtilis , Bacillus licheniformis, and Bacillus licheniformis are added to an organic material mixing raw material obtained by mixing vegetable organic materials including bark and sawdust and animal organic materials including grains and slaughter by- ) And Bacillus megaterium , and at least one microorganism belonging to the genus Rhodobacter selected from Rhodobacter capsulata or Rhodobacter sphaeroides . Adding a mixed microorganism constituted and fermenting to obtain a fermentation organism; And
Adding 50 to 200 parts by weight of mineral matter, 50 to 150 parts by weight of bottom ash, 1 to 20 parts by weight of an absorbent polymer and 10 to 100 parts by weight of calcium-magnesium-containing fertilizer per 100 parts by weight of the fermentation organic material to obtain a final composition Lt; / RTI >
Wherein the mineral is at least one selected from the group consisting of zeolite, illite, perlite, vermiculite and bentonite,
Wherein the calcium-magnesium-containing fertilizer is at least one selected from the group consisting of quicklime, lime, calcium carbonate, lime lime, lime lime, heavy lime lime, gypsum, lime lime and gypsum plaster and magnesium hydroxide, magnesium sulfate, magnesium carbonate, At least one member selected from the group consisting of hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides, hydroxides,
Wherein the water absorbing polymer is a copolymer of a first monomer selected from a carboxylic acid having an ethylenically unsaturated bond and a second monomer selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond or an amide having an ethylenically unsaturated bond A copolymer of a fourth monomer selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond and a third monomer to be selected,
Wherein the first monomer is at least one selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, maleic acid and fumaric acid, and the second monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, potassium methacrylate , At least one selected from the group consisting of sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate,
Wherein the third monomer is at least one selected from the group consisting of acrylamide, methacrylamide, maleic acid amide and fumaric acid amide, and the fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate, potassium methacrylate, Wherein the at least one compound is at least one compound selected from the group consisting of sodium itaconic acid, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate.
제 8항에 있어서, 상기 발효 유기물을 수득하는 단계는 수피와 톱밥을 포함하는 식물성 유기물 및 계분과 도축 부산물을 포함하는 동물성 유기물을 혼합한 유기물 혼합 원료에 바실러스 푸밀러스(Bacillus pumilus), 바실러스 서브틸리스(Bacillus subtilis), 바실러스 리케니포미스(Bacillus licheniformis) 및 바실러스 메가테리움(Bacillus megaterium)로 이루어진 군에서 선택된 1종 이상의 바실러스속 미생물과 로도박터 캡슐라타(Rhodobacter capsulata) 또는 로도박터 스페로이드스(Rhodobacter sphaeroides)에서 선택된 1종 이상의 로도박터속 미생물로 구성되는 혼합 미생물을 첨가한 후 호기성 조건의 발효조에서 15~40일 동안 1차 발효시키고 노지에서 60~300일 동안 2차 발효시키는 것으로 구성되는 것을 특징으로 하는 식물 식재용 인공토양의 제조방법.
[9] The method of claim 8, wherein the step of obtaining the fermentation organic material comprises the steps of adding Bacillus pumilus , Bacillus subtilis, and Bacillus subtilis to an organic material mixture containing vegetable organic materials including bark and sawdust and animal organic materials including stem and slaughter by- At least one microorganism belonging to the genus Bacillus subtilis , Bacillus licheniformis and Bacillus megaterium , and at least one microorganism selected from the group consisting of Rhodobacter capsulata or Rhodobacter spp. ( Rhodobacter sphaeroides ), followed by primary fermentation for 15 to 40 days in a fermentation tank under aerobic conditions and secondary fermentation for 60 to 300 days in a non-fermented state ≪ / RTI > wherein the method comprises the steps of:
제 8항에 있어서, 상기 유기물 혼합 원료를 구성하는 식물성 유기물 대 동물성 유기물의 중량비는 1:1 내지 1:2이고, 상기 식물성 유기물을 구성하는 수피 대 톱밥의 중량비는 1:0.5 내지 1:10이고, 상기 동물성 유기물을 구성하는 계분 대 도축 부산물의 중량비는 1:0.5 내지 1:2이고, 상기 혼합 미생물의 첨가량은 유기물 혼합 원료 100 중량부 당 0.05~1 중량부인 것을 특징으로 하는 식물 식재용 인공토양의 제조방법.
The method of claim 8, wherein the weight ratio of the vegetable organic material to the animal organic material constituting the organic material mixture material is 1: 1 to 1: 2, and the weight ratio of the bark to sawdust constituting the vegetable organic material is 1: 0.5 to 1:10 , The weight ratio of the staple to the slaughter by-product constituting the animal organic material is 1: 0.5 to 1: 2, and the amount of the mixed microorganism to be added is 0.05 to 1 part by weight per 100 parts by weight of the organic material mixed material. ≪ / RTI >
제 8항에 있어서, 상기 최종 조성물을 수득하는 단계는
(a) 상기 발효 유기물을 1차 기초물질로 하여, 여기에 발효 유기물 100 중량부를 기준으로 광물질 50~200 중량부 및 바텀애쉬 50~150 중량부를 첨가하고 혼합하여 2차 기초물질을 제조하는 단계;
(b) 상기 2차 기초물질에 발효 유기물 100 중량부를 기준으로 흡수성 고분자 1~20 중량부를 고르게 분사하여 3차 기초물질을 제조하는 단계; 및
(c) 상기 3차 기초물질에 발효 유기물 100 중량부를 기준으로 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합하여 최종 조성물을 제조하는 단계로 구성되는 것을 특징으로 하는 식물 식재용 인공토양의 제조방법.
9. The method of claim 8, wherein obtaining the final composition comprises:
(a) adding 50 to 200 parts by weight of mineral and 50 to 150 parts by weight of a bottom ash to the fermentation organic material as a primary basic material and mixing the fermented organic material with 100 parts by weight of the fermentation organic material to prepare a secondary basic material;
(b) uniformly spraying 1 to 20 parts by weight of the water absorbent polymer on the basis of 100 parts by weight of the fermentation organic material to the secondary basic substance to prepare a tertiary basic substance; And
(c) adding 10 to 100 parts by weight of a calcium-magnesium-containing fertilizer based on 100 parts by weight of the fermentation organic material to the tertiary basic substance to prepare a final composition. Way.
제 11항에 있어서, 상기 (c) 단계는 3차 기초물질에 발효 유기물 100 중량부를 기준으로 칼슘-마그네슘 함유 비료 10~100 중량부를 첨가하고 혼합한 후, 여기에 질소 함유 비료, 인 함유 비료, 칼륨 함유 비료 또는 식물의 생장에 필요한 미량 원소 함유 물질을 첨가하고 혼합하여 최종 조성물을 제조하는 단계로 구성되는 것을 특징으로 하는 식물 식재용 인공토양의 제조방법.
12. The method according to claim 11, wherein in step (c), 10 to 100 parts by weight of a calcium-magnesium-containing fertilizer is added to and mixed with a tertiary basic substance based on 100 parts by weight of fermentation organic material, A potassium-containing fertilizer or a trace element-containing material necessary for plant growth is added and mixed to prepare a final composition.
삭제delete 삭제delete 제 1항 내지 제 4항 중 어느 한 항의 인공토양 또는 제 8항 내지 제 12항 중 어느 한 항의 방법으로 제조된 인공토양 및 상기 인공토양과 별도로 제공되고 색상을 갖는 흡수성 고분자를 포함하고,
상기 색상을 갖는 흡수성 고분자는 에틸렌성 불포화 결합을 가진 아마이드에서 선택되는 제3단량체와 에틸렌성 불포화 결합을 가진 카르복실산의 알칼리금속염에서 선택되는 제4단량체의 공중합체인 것을 특징으로 하는 식물 식재용 인공토양 키트.
An artificial soil prepared by the method of any one of claims 1 to 4 or an artificial soil produced by the method of any one of claims 8 to 12 and an absorbent polymer provided separately from the artificial soil and having a color,
Wherein the absorbent polymer having the hue is a copolymer of a fourth monomer selected from an alkali metal salt of a carboxylic acid having an ethylenically unsaturated bond and a third monomer selected from an amide having an ethylenically unsaturated bond. Soil kit.
제 15항에 있어서, 상기 제3단량체는 아크릴아마이드, 메타크릴아마이드, 말레익산 아마이드 및 푸마릭산 아마이드로 이루어진 군에서 선택되는 1종 이상이고, 제4단량체는 아크릴산나트륨, 아크릴산칼륨, 메타크릴산나트륨, 메타크릴산칼륨, 이타코닉산나트륨, 이타코닉산칼륨, 말레익산나트륨, 말레익산칼륨, 푸마릭산칼륨 및 푸마릭산나트륨으로 이루어진 군에서 선택되는 1종 이상인 것을 특징으로 하는 식물 식재용 인공토양 키트.16. The method of claim 15, wherein the third monomer is at least one selected from the group consisting of acrylamide, methacrylamide, maleic acid amide, and fumaric acid amide, and the fourth monomer is at least one selected from the group consisting of sodium acrylate, potassium acrylate, sodium methacrylate , At least one selected from the group consisting of potassium methacrylate, sodium itaconic acid, potassium itaconic acid, sodium maleate, potassium maleate, potassium fumarate and sodium fumarate. .
KR1020150031447A 2015-03-06 2015-03-06 Artificial soil for planting plants and manufacturing method of the same KR101547306B1 (en)