KR101546240B1 - Antimicrobial porous ceramic tile and method of manufacturing the same - Google Patents
Antimicrobial porous ceramic tile and method of manufacturing the same Download PDFInfo
- Publication number
- KR101546240B1 KR101546240B1 KR1020120121622A KR20120121622A KR101546240B1 KR 101546240 B1 KR101546240 B1 KR 101546240B1 KR 1020120121622 A KR1020120121622 A KR 1020120121622A KR 20120121622 A KR20120121622 A KR 20120121622A KR 101546240 B1 KR101546240 B1 KR 101546240B1
- Authority
- KR
- South Korea
- Prior art keywords
- porous ceramic
- ceramic tile
- active material
- parts
- carbonate
- Prior art date
Abstract
γ-알루미나 및 항균 활성물질을 포함하는 다공성 세라믹 타일을 제공한다.
γ-알루미나 및 항균활성물질을 혼합하여 세라믹 성형체를 형성하는 단계; 상기 세라믹 성형체를 건식 프레스 성형하여 다공성 세라믹 타일을 제조하는 단계; 상기 성형된 다공성 세라믹 타일을 건조하는 단계; 상기 건조된 다공성 세라믹 타일에 유약으로 시유하는 단계; 및 상기 시유된 다공성 세라믹 타일을 열분해하여 소성하는 단계를 포함하는 다공성 세라믹 타일 제조방법을 제공한다.A porous ceramic tile including γ-alumina and an antibacterial active material is provided.
forming a ceramic formed body by mixing? -alumina and an antibacterial active material; A step of dry-pressing the ceramic formed body to produce a porous ceramic tile; Drying the shaped porous ceramic tile; Dipping the dried porous ceramic tile into a glaze; And thermally decomposing and sintering the sintered porous ceramic tile to obtain a porous ceramic tile.
Description
항균 다공성 세라믹 타일 및 이의 제조방법에 관한 것이다.
To an antibacterial porous ceramic tile and a method for manufacturing the same.
기존의 항균타일은 항균 물질을 물과 혼합하여 현탁액을 만들고 타일의 표면 위에 도포하거나 유약과 섞어 함께 표면에 바르는 방식으로 형성되는 것이 보통이었다. 그러나 이러한 방식은 다공성 세라믹 타일 내부에 넓은 표면적에 고르게 분포시키기 힘들며, 일부 항균 물질이 뭉쳐진 경우에는 다공성 세라믹 타일 내부의 기공을 막아 흡방습성을 떨어뜨리는 부작용을 낼 수 있기 때문에, 수많은 기공을 포함함으로써 흡방습성을 보이는 다공성 타일에 적용하기에는 어려운 점이 있었다. Conventional antimicrobial tiles are usually formed by mixing the antimicrobial material with water to form a suspension, applying it on the surface of the tile, or applying it to the surface together with the glaze. However, this method is difficult to uniformly distribute in a large surface area inside the porous ceramic tile, and when some antimicrobial materials are aggregated, the pores inside the porous ceramic tile can be blocked, resulting in a side effect that lowers the moisture absorptive and desorptive properties. It has been difficult to apply it to a porous tile exhibiting moisture resistance.
또한 단순한 도포 방식에 의한 항균 물질은 시간이 지남에 따라 물리적인 접촉, 환경의 온도, 습도 변화에 의한 영향을 받아 다공성 세라믹 타일 표면에서 이탈된 우려가 있어 계속적인 효과를 보기에는 주기적인 재도포의 작업이 필요하기에 편의성, 경제성 측면에서 한계를 가지고 있다.In addition, antimicrobial materials by a simple application method may be detached from the surface of the porous ceramic tiles due to physical contact, environmental temperature, and humidity change over time, It is necessary to work and has limitations in terms of convenience and economy.
그러므로, 다공성 세라믹 타일 내부에 항균물질을 포함하여 이를 고르게 분포시킬 수 있는 방법에 대한 연구가 계속되고 있다.
Therefore, research on a method of evenly distributing the antimicrobial material in the porous ceramic tile is being continued.
본 발명의 일 구현예는 항균 활성물질을 포함하는 다공성 세라믹 타일을 제공한다.One embodiment of the present invention provides a porous ceramic tile comprising an antimicrobial active material.
본 발명의 다른 구현예는 상기 다공성 세라믹 타일의 제조방법을 제공한다.
Another embodiment of the present invention provides a method of making the porous ceramic tile.
본 발명의 일 구현예에서, γ-알루미나 및 항균 활성물질을 포함하는 다공성 세라믹 타일을 제공한다.In one embodiment of the present invention, there is provided a porous ceramic tile comprising gamma -alumina and an antibacterial active material.
상기 항균 활성물질은 금속 탄산염일 수 있다. The antimicrobial active material may be a metal carbonate.
상기 금속 탄산염은 탄산칼슘, 탄산칼륨, 탄산바륨, 탄산마그네슘, 탄산나트륨 및 이들의 조합으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함할 수 있다.The metal carbonate may include at least one selected from the group consisting of calcium carbonate, potassium carbonate, barium carbonate, magnesium carbonate, sodium carbonate, and combinations thereof.
상기 항균 활성물질은 모물질 100중량부에 대하여 약 3중량부 내지 약 30중량부를 포함할 수 있다. The antimicrobial active material may include about 3 parts by weight to about 30 parts by weight based on 100 parts by weight of the parent material.
상기 모물질은 점토, 백토, 황토 및 이들의 조합으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함할 수 있다.The parent material may include at least one selected from the group consisting of clay, clay, loess, and combinations thereof.
상기 다공성 세라믹 타일은 평균 직경이 약 1nm 내지 약 1mm인 기공을 포함할 수 있다. The porous ceramic tile may include pores having an average diameter of about 1 nm to about 1 mm.
상기 기공의 기공률이 약 30% 내지 약 60%일 수 있다. The porosity of the pores may be from about 30% to about 60%.
상기 기공 표면의 pH가 약 11이상일 수 있다.
The pore surface may have a pH of about 11 or higher.
본 발명의 다른 구현예에서, γ-알루미나 및 항균활성물질을 혼합하여 세라믹 성형체를 형성하는 단계; 상기 세라믹 성형체를 건식 프레스 성형하여 다공성 세라믹 타일을 제조하는 단계; 상기 성형된 다공성 세라믹 타일을 건조하는 단계; 상기 건조된 다공성 세라믹 타일에 유약으로 시유하는 단계; 및 상기 시유된 다공성 세라믹 타일을 열분해하여 소성하는 단계를 포함하는 다공성 세라믹 타일 제조방법을 제공한다.In another embodiment of the present invention, there is provided a method for producing a ceramic molded body, comprising the steps of: forming a ceramic formed body by mixing? -Alumina and an antibacterial active material; A step of dry-pressing the ceramic formed body to produce a porous ceramic tile; Drying the shaped porous ceramic tile; Dipping the dried porous ceramic tile into a glaze; And thermally decomposing and sintering the sintered porous ceramic tile to obtain a porous ceramic tile.
상기 열분해는 약 800℃ 내지 약 1000℃의 온도에서 수행되는 것을 특징으로 할 수 있다. The pyrolysis may be performed at a temperature of about 800 < 0 > C to about 1000 < 0 > C.
상기 열분해는 약 1분 내지 약 15분의 시간동안 수행되는 것을 특징으로 할 수 있다.
The pyrolysis may be performed for a time of about 1 minute to about 15 minutes.
상기 다공성 세라믹 타일의 항균성에 의해 세균 및 곰팡이의 증식을 억제할 수 있고, 실내 공기 중 부유 미생물 발생도 저감시킬 수 있어, 실내의 쾌적한 환경을 유지시킬 수 있다.It is possible to inhibit the growth of bacteria and fungi by the antibacterial property of the porous ceramic tile and also to reduce the occurrence of airborne microorganisms in the room air and to maintain a comfortable environment in the room.
상기 다공성 세라믹 타일의 제조방법에 의해 제조공정상 편의성, 경제성이 향상될 수 있다.
The manufacturing convenience and economic efficiency of the porous ceramic tile can be improved by the manufacturing method of the porous ceramic tile.
도 1은 다공성 세라믹 타일 및 다공성 세라믹 타일이 포함하는 기공을 도식화하여 나타낸 것이다.
도 2는 다공성 세라믹 타일의 제조방법을 도식화하여 나타낸 것이다.FIG. 1 schematically illustrates the pores included in the porous ceramic tile and the porous ceramic tile.
2 is a schematic representation of a method of making a porous ceramic tile.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구항의 범주에 의해 정의될 뿐이다.
Hereinafter, embodiments of the present invention will be described in detail. However, the present invention is not limited thereto, and the present invention is only defined by the scope of the following claims.
다공성 세라믹 타일Porous ceramic tile
본 발명의 일 구현예에서, γ-알루미나 및 항균 활성물질을 포함하는 다공성 세라믹 타일을 제공한다.
In one embodiment of the present invention, there is provided a porous ceramic tile comprising gamma -alumina and an antibacterial active material.
상기 다공성 세라믹 타일은 세라믹 분말 등을 압축성형하여 제조될 수 있고, 원료는 대부분 분체로, 소석고나 시멘트의 경화제처럼 수화에 의해 경화되는 것도 있지만, 분체를 소결하여 형성될 수 있다. 상기 다공성 세라믹 타일은 γ-알루미나 및 항균 활성물질을 포함할 수 있다.
The porous ceramic tile can be produced by compression molding ceramics powder or the like, and the raw material is mostly powder, and may be formed by sintering the powder, though it may be hardened by hydration like a curing agent of cement or cement. The porous ceramic tile may include? -Alumina and an antibacterial active material.
항균 활성물질을 포함하여 다공성 세라믹 타일을 형성하는 경우, 다공성 세라믹 타일의 제조과정을 통해 변형된 항균 활성 물질을 통해 다공성 세라믹 타일에 항균성을 부여할 수 있다. 다공성 세라믹 타일을 상온에 두고 사용하는데 있어서, 다공성 세라믹 타일이 포함하는 기공을 통해 흡습이 이루어질 수 있고, 이 때 다공성 세라믹 타일에 균일하게 분포된 항균 활성물질과 수분이 접촉할 수 있다. 수분과의 접촉을 통해 변형된 항균 활성물질에 화학변화가 일어날 수 있고, 이로 인해 다공성 세라믹 타일의 기공 표면에 알칼리성이 부여되어 항균성능을 발휘할 수 있다. 상기 다공성 세라믹 타일의 항균성에 의해 세균 및 곰팡이의 증식을 억제할 수 있고, 실내 공기 중 부유 미생물 발생도 저감시킬 수 있어, 실내의 쾌적한 환경을 유지시킬 수 있다.
When the porous ceramic tile including the antimicrobial active material is formed, the porous ceramic tile can be imparted with antimicrobial activity through the modified antimicrobial active material through the manufacturing process of the porous ceramic tile. When the porous ceramic tile is used at room temperature, moisture can be absorbed through the pores included in the porous ceramic tile. In this case, the antibacterial active material uniformly distributed in the porous ceramic tile can be in contact with the water. Chemical changes may occur in the modified antimicrobial active material due to contact with moisture, thereby imparting alkalinity to the pore surface of the porous ceramic tile, thereby exhibiting antibacterial performance. It is possible to inhibit the growth of bacteria and fungi by the antibacterial property of the porous ceramic tile and also to reduce the occurrence of airborne microorganisms in the room air and to maintain a comfortable environment in the room.
상기 항균 활성물질은 금속 탄산염일 수 있다. 금속 탄산염은 탄산의 수소가 금속으로 치환된 염을 일컫는바, 이산화탄소와 금속산화물 또는 금속수산화물로 구성되는 화합물로 탄산염이 덩어리진 것을 의미한다. 상기 금속 탄산염은 탄산칼슘, 탄산칼륨, 탄산바륨, 탄산마그네슘, 탄산나트륨 및 이들의 조합으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함할 수 있다.
The antimicrobial active material may be a metal carbonate. The metal carbonate refers to a salt in which the hydrogen of carbonic acid is substituted with a metal, which means that the carbonate is a compound composed of carbon dioxide and a metal oxide or a metal hydroxide. The metal carbonate may include at least one selected from the group consisting of calcium carbonate, potassium carbonate, barium carbonate, magnesium carbonate, sodium carbonate, and combinations thereof.
구체적으로, 항균 활성물질이 금속 탄삼염 중 탄산칼슘(CaCO3)인 경우, 다공성 세라믹 타일의 제조과정을 통해 탄산칼슘(CaCO3)이 이산화탄소(CO2) 및 생석회(CaO)로 분해(CaCO3-> CO2+CaO)될 수 있고, 생석회가 다공성 세라믹 타일에 균일하게 분포될 수 있다. 상기 다공성 세라믹 타일의 기공을 통하여 수분을 흡습하는바, 상기 생석회(CaO)가 화학변화를 겪어 소석회(Ca(OH)2)를 형성하게 된다(CaO+H2O->Ca(OH)2). 이때, 생성된 소석회는 다시 수분에 녹아 칼슘이온(Ca+)과 수산화이온(OH-)으로 이온화(Ca(OH)2)->(OH-)+(Ca+))되고, 알칼리 성질을 띄게 하는 수산화이온으로 인해 기공 표면이 알칼리화 되어 다공성 세라믹 타일에 항균성을 부여할 수 있다.
More specifically, when the antibacterial active material a metal bullet calcium carbonate of samyeom (CaCO 3), the porous ceramic of calcium carbonate through a manufacturing process of the tiles (CaCO 3) the carbon dioxide decomposition to (CO 2) and calcium oxide (CaO) (CaCO 3 - > CO 2 + CaO), and the burnt lime can be uniformly distributed in the porous ceramic tile. Bar to water absorption through the pores of the porous ceramic tiles, the calcium oxide (CaO) has undergone a chemical change to form a slaked lime (Ca (OH) 2) ( CaO + H 2 O-> Ca (OH) 2) . At this time, the generated slaked lime is again ionized (Ca (OH) 2 -> (OH -) + (Ca +)) into calcium ions (Ca +) and hydroxide ions Ions can alkalize the surface of the pores to impart antimicrobial properties to the porous ceramic tiles.
보다 구체적으로, 상기 항균 활성물질은 모물질 100중량부에 대하여 약 3중량부 내지 약 30중량부를 포함할 수 있다. 상기 항균 활성물질을 상기 범위를 벗어나서 포함한 경우 다공성 세라믹 타일 자체의 강도가 심각하게 저하되거나, 기공의 기공률이 줄어 들어, 다공성 세라믹 타일의 역할을 할 수 없는 문제점이 있다. 그러므로, 상기 범위 내의 항균 활성물질을 포함함으로써 다공성 세라믹 타일의 항균성을 적당하게 유지할 수 있는 효과를 용이하게 구현할 수 있다.
More specifically, the antimicrobial active material may include about 3 parts by weight to about 30 parts by weight based on 100 parts by weight of the parent material. When the antimicrobial active material is contained outside the above range, there is a problem that the strength of the porous ceramic tile itself is seriously degraded or the porosity of the pore is reduced, so that the porous ceramic tile can not serve as the porous ceramic tile. Therefore, by including the antimicrobial active material within the above range, it is possible to easily realize the effect of appropriately maintaining the antibacterial property of the porous ceramic tile.
상기 모물질은 상기 다공성 세라믹 타일을 구성하는 기초 모재가 되는 물질로서, 상기 다공성 세라믹 타일이 어떤 형태로 제조되는지에 따라 그 종류가 다양하게 적용될 수 있다. The parent material may be a base material that constitutes the porous ceramic tile, and may be variously applied depending on the type of the porous ceramic tile.
예를 들면, 상기 다공성 세라믹 타일용으로 제조되는 경우, 세라믹 타일의 모재로 사용되는 모물질은 점토 백토 및 황토로 이루어진 군으로부터 선택하여 사용될 수 있으나, 상기 기재된 예에 제한되는 것은 아니고, 상기 다공성 세라믹 타일을 구성하기 위하여 기초 재료로 사용될 수 있는 모든 물질을 포함할 수 있다.
For example, when the porous ceramic tile is manufactured for the ceramic tile, the parent material used as the base material of the ceramic tile may be selected from the group consisting of clay clay and loess, but the present invention is not limited to the example described above, And may include any material that can be used as a base material to construct the tile.
상기 모물질의 함량은 특별히 제한되는 것은 아니고, 다공성 세라믹 타일의 적용분야 및 용도에 따라 기타 다른 첨가물이 첨가됨에 따라 그 함량이 달라질 수 있는 것으로, 예를 들면 상기 다공성 세라믹 타일을 형성하는 전체 조성물 100중량부에 대하여 상기 모물질을 약 30중량부 내지 약 70중량부를 포함할 수 있다. 상기 범위의 모물질을 포함함으로써 성형된 다공성 세라믹 타일로의 일정수준의 성형강도를 유지할 수 있고, 소성단계를 거친 후에도 일정수준의 소성강도를 나타낼 수 있다.
The content of the parent material is not particularly limited and may be varied depending on the application field and application of the porous ceramic tile. For example, the total composition 100 forming the porous ceramic tile About 30 parts by weight to about 70 parts by weight of the parent material with respect to parts by weight. By including the parent material in the above range, a predetermined level of molding strength can be maintained with the porous ceramic tiles formed, and a certain degree of plasticity can be exhibited even after the firing step.
한편, 상기 γ-알루미나는 전이상태의 알루미나로써 조습기능을 부여할 수 있다. 일정한 열처리에 의하여 다른 구조상으로 변이가 가능하고, 넓은 비표면적과 미세한 기공 홀을 가지고 있어서 분리막, 촉매, 촉매 담체 및 흡착제로서 우수한 특성을 나타낼 수 있는 물질이다.
On the other hand, the? -Alumina is a transition alumina and can impart a humidity control function. It has a wide specific surface area and fine pore holes and can exhibit excellent properties as a separator, a catalyst, a catalyst carrier and an adsorbent.
상기 γ-알루미나는 기공이 표면에 형성되어 우수한 조습 및 탈취 기능을 가질 수 있다. 이에 따라, 상기 γ-알루미나는 습도가 높을 때에는 기공을 통하여 습기를 흡수하여 실내의 습도를 낮추는 기능을 하고, 반대로 습도가 낮을 때에는 기공 내에 저장되어 있던 습기를 방출하여 실내 습도를 높이는 기능을 한다. 또한, 상기 γ-알루미나는 상용 γ-알루미나를 사용할 수도 있으나, 비용절감 및 효율성의 측면에서, 보다 구체적으로는 저가의 알루미늄 소스를 열처리에 의하여 상 변이시킨 γ-알루미나를 사용할 수 있다.
The? -Alumina may have pores formed on its surface and may have a good humidity and deodorizing function. Accordingly, when the humidity is high, the γ-alumina absorbs moisture through the pores to lower the humidity of the room. On the contrary, when the humidity is low, the γ-alumina emits moisture stored in the pores to increase the room humidity. The γ-alumina may be a commercially available γ-alumina, but in terms of cost reduction and efficiency, more specifically, γ-alumina which is phase-shifted by heat treatment at a low cost aluminum source can be used.
상기 γ-알루미나는 상기 모물질 100중량부에 대하여 약 5중량부 내지 약 40중량부, 구체적으로 약 10중량부 내지 약 35중량부를 포함할 수 있다. 상기 γ-알루미나가 상기 모물질 100중량부에 대하여 약 5중량부 미만인 경우, 충분한 조습 기능을 나타내기 어려워질 우려가 있으며, 약 40중량부를 초과하는 경우, 다공성 세라믹 타일의 소결이 저하됨에 따라 타일의 강도가 저하될 우려가 있다.
The γ-alumina may include about 5 parts by weight to about 40 parts by weight, specifically about 10 parts by weight to about 35 parts by weight, based on 100 parts by weight of the parent material. When the amount of the γ-alumina is less than about 5 parts by weight based on 100 parts by weight of the parent material, the moisture-holding function may be difficult to exhibit. When the amount exceeds about 40 parts by weight, the sintering of the porous ceramic tile is deteriorated, There is a possibility that the strength of the film is lowered.
또한, 상기 γ-알루미나의 비표면적이 특별히 제한되는 것은 아니지만, 예를 들어 약 150㎡/g 내지 약 350㎡/g인 것일 수 있다. 상기 γ-알루미나의 비표면적이 약 150㎡/g 미만인 경우, 충분한 조습기능을 나타낼 수가 없고, 약 350㎡/g를 초과하는 경우, 제조공정의 어려움을 초래할 수 있으며, 제조비용을 상승시킬 우려가 있다.
The specific surface area of the? -Alumina is not particularly limited, but may be, for example, from about 150 m 2 / g to about 350 m 2 / g. When the specific surface area of the? -Alumina is less than about 150 m 2 / g, it can not exhibit a sufficient humidifying function. When the specific surface area exceeds about 350 m 2 / g, the manufacturing process may become difficult, have.
전술한 γ-알루미나 및 항균 활성물질을 포함하는 다공성 세라믹 타일은 흡방습량이 우수하여 조습 및 탈취기능을 가지는 기능성 성형체로 다양한 형태로 사용될 수 있으며, 흡방습량이 크게 우수하므로 다양한 기능성 제품에 적용되어 새집증후군, 아토피 및 새빌딩증후군 등에 의한 피해를 크게 줄일 수 있다.
The porous ceramic tile including the above-mentioned? -Alumina and the antimicrobial active material is a functional molded product having a moisture absorbing and dehumidifying ability and has a humidity controlling and deodorizing function. The porous ceramic tile can be used in various forms. Syndrome, atopy, and new building syndrome.
또한 상기 다공성 세라믹 타일은 기공을 포함하는 타일로, 수분을 빨아들이는 흡습성이 탁월하며, 일정수준의 기계적 강도를 유지함으로써, 건축용 바닥재 및 벽재로 그 활용도가 매우 높다. 상기 다공성 세라믹 타일은 γ-알루미나 및 항균 활성물질을 포함하여 형성되는바, 각각의 성분에 대한 사항은 전술한 바와 같다.
In addition, the porous ceramic tile is a tile containing pores, and has excellent hygroscopicity for absorbing moisture, and maintains a certain level of mechanical strength, so that it is very useful as a flooring for building use and a wall material. The porous ceramic tile is formed of γ-alumina and an antibacterial active material, and the respective components are as described above.
상기 다공성 세라믹 타일은 γ-알루미나 및 항균 활성물질 외에 바인딩 물질 또는 기타 첨가제를 추가로 포함할 수 있다. 상기 바인딩 물질은 그 종류가 특별히 제한되는 것은 아니지만, 예를 들어, 프리트 분말 및 유리 분말을 바인딩 물질로 함유할 수 있다.
The porous ceramic tile may further include a binding substance or other additives in addition to the? -Alumina and the antibacterial active material. The kind of the binding material is not particularly limited. For example, the binding material may contain a frit powder and a glass powder as a binding material.
상기 바인딩 물질로 사용되는 프리트 분말은 화도가 약 750℃ 내지 약 850℃의 프리트 분말이 사용될 수 있다. 이와 같은 프리트 분말을 바인딩 물질로 사용하는 경우, 낮은 온도에서 열처리하더라도 충분한 강도를 나타낼 수 있다는 장점이 있으나, 화도가 약 750℃ 미만의 프리트 분말을 사용할 경우 제조비용이 증가하는 단점이 있다. 또한, 약 850℃을 초과하여 프리트 분말을 사용할 경우는 강도가 충분히 나타나지 않을 수 있다.
The frit powder used as the binding material may be a frit powder having a degree of firing of about 750 ° C to about 850 ° C. When such a frit powder is used as a binding material, it has an advantage that sufficient strength can be exhibited even when heat treatment is performed at a low temperature. However, when the frit powder having a degree of firing less than about 750 캜 is used, manufacturing cost increases. If the frit powder is used in excess of about 850 DEG C, the strength may not be sufficiently exhibited.
상기 바인딩 물질은 상기 모물질 100 중량부에 대하여 약 3중량부 내지 약 20중량부를 포함할 수 있다. 상기 바인딩 물질이 상기 모물질 100 중량부에 대하여 약 3중량부 미만으로 포함되는 경우, 다공성 세라믹 타일의 강도가 저하될 수 있으며, 약 20중량부를 초과하는 경우, 조습기능이 저하될 수 있고 제조비용이 증가할 수 있다.
The binding material may include about 3 parts by weight to about 20 parts by weight based on 100 parts by weight of the parent material. When the binding material is contained in an amount of less than about 3 parts by weight based on 100 parts by weight of the mother material, the strength of the porous ceramic tile may be lowered. When the binding material is more than about 20 parts by weight, Can be increased.
또한, 상기 다공성 세라믹 타일은 프리트 분말, 유리 분말, 규조토, 규석, 장석, 도석, 석회, 황토 및 유백제로 이루어지는 군으로부터 선택된 하나 이상의 첨가물을 추가로 포함할 수 있다. 상기 첨가물의 함량은 특별히 제한되는 것은 아니고, 상기 다공성 세라믹 타일의 기능이 손상되지 않는 범위 내에서 적절하게 채용할 수 있는 것이지만, 예를 들면, 상기 모물질 100 중량부에 대하여 약 3중량부 내지 약 30 중량부를 포함할 수 있다.
The porous ceramic tile may further include at least one additive selected from the group consisting of frit powder, glass powder, diatomaceous earth, silica, feldspar, stones, lime, loess, and milk powder. The content of the additive is not particularly limited and can be appropriately applied within a range that does not impair the function of the porous ceramic tile. For example, about 3 parts by weight to about 100 parts by weight of the parent material 30 parts by weight.
상기 첨가물 중 규조토는 흡수성이 풍부한 다공질로서, 다공성 세라믹 타일 형성에 첨가되는 경우, 흡습 기능을 보다 향상시킬 수 있고, 기타 규석, 장석, 도석 및 석회 등도 각각 적절한 양으로 내에 포함될 수 있다. 아울러, 상기 유백제는 유리 제품에 흰빛이 나게 하기 위하여 첨가하는 분말로서, 그 종류가 특별히 제한되는 것은 아니지만, 염화물, 주석, 티타늄 산화물, 황산염, 인산염, 비산염 및 불화물로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.
The diatomaceous earth among the additives is an absorbent porous material, and when added to the porous ceramic tile formation, the moisture absorption function can be further improved, and other quartz, feldspar, stones and lime can also be contained in appropriate amounts. In addition, the above-mentioned whitening agent is a powder to be added to a glass product in order to give a whiteness. The kind of the whitening agent is not particularly limited, but is preferably at least one selected from the group consisting of chloride, tin, titanium oxide, sulfate, phosphate, . ≪ / RTI >
상기 다공성 세라믹 타일은 평균직경이 약 1nm 내지 약 1mm인 기공을 포함할 수 있다. 상기 기공은 상기 다공성 세라믹 타일에 분포된 기공을 의미하고, 기공의 평균직경은 기공 직경의 산술적인 평균치를 일컫는바, 상기 범위 내의 기공 크기를 유지함으로써 수분 흡수 및 방출, 유해가스 흡착의 역할을 할 수 있다. The porous ceramic tile may include pores having an average diameter of about 1 nm to about 1 mm. The pores mean pores distributed in the porous ceramic tiles. The average diameter of the pores refers to an arithmetic mean value of the pore diameters. By maintaining the pore size within the above range, water absorption and release, and noxious gas adsorption .
상기 기공은 다공성 세라믹 타일을 형성하는 입자 표면에 존재하는 기공뿐 아니라, 다공성 세라믹 타일을 형성하는 입자와 입자 사이에 존재하는 기공 또한 포함하는 것으로 이 때의 기공은 공기의 통로 역할을 할 수 있다.
The pores include not only the pores present on the surface of the particles forming the porous ceramic tile but also the pores existing between the particles forming the porous ceramic tile and the particles, and the pores in this case can serve as air passages.
또한, 상기 기공의 기공률이 약 30% 내지 약 60%일 수 있다. 상기 기공률은 기공의 공극의 정도를 나타내는 수치를 나타내는 바, 기공의 부피의 전 부피에 대한 백분율을 일컫는다. 상기 기공률은, 예를 들어, 미세한 기공에 액체가 침투하는 모세관 현상을 이용하는 수은침투를 이용한 기공률 측정원리 등을 이용하여 기공률(%)을 산출할 수 있다.Also, the porosity of the pores may be from about 30% to about 60%. The porosity indicates a numerical value indicating the degree of pore porosity, and refers to a percentage of the total volume of the pore volume. The porosity can be calculated, for example, by using the principle of porosity measurement using mercury penetration using a capillary phenomenon in which liquid penetrates into fine pores.
또한, 상기 범위의 기공률을 유지함으로써 다공성 세라믹 타일의 강도를 적절하게 유지할 수 있고, 수분 및 유해가스의 통로 역할을 수행할 수 있다.
Also, by maintaining the porosity in the above range, the strength of the porous ceramic tile can be appropriately maintained, and it can serve as a passage for moisture and noxious gas.
상기 기공 표면의 pH가 약 11이상일 수 있다. 상기 pH란 용액의 수소이온지수, 즉 수소이온(H+) 농도를 지수로 나타낸 것으로, 물의 산성이나 알칼리성 정도를 나타내는 수치이다. 상온에서 pH가 약 7인 경우 해당물질의 액성은 중성, pH가 약 7보다 작은 경우 산성, pH가 약 7보다 큰 경우 염기성임을 의미하는바, 상기 기공 표면의 pH는 약 11이상으로 염기성을 가진다.
The pore surface may have a pH of about 11 or higher. The pH is an index representing the hydrogen ion concentration of the solution, that is, the hydrogen ion (H +) concentration, which is a numerical value indicating the acidity or alkaline degree of water. When the pH is about 7 at room temperature, the liquid of the substance is neutral, when the pH is less than about 7, it is acidic, and when the pH is more than about 7, it is basic. The pH of the surface of the pore is about 11 or more .
상기 다공성 세라믹 타일은 항균 활성물질을 포함하여 형성되는 것으로, 다공성 세라믹 타일을 상온에 두고 사용하는 경우, 다공성 세라믹 타일이 포함하는 기공을 통하여 흡습이 이루어질 수 있다. 이 때, 상기 다공성 세라믹 타일 제조시 변형된 상기 항균 활성물질과 수분과의 접촉을 통해 일정한 화학변화가 일어나, 일정농도 이상의 수산화이온을 발생하게 할 수 있고, 상기 발생된 수산화 이온으로 인해 다공성 세라믹 타일의 기공 표면 pH가 약 11이상이 될 수 있다.The porous ceramic tile includes an antibacterial active material. When the porous ceramic tile is used at room temperature, the porous ceramic tile can absorb moisture through the pores included in the porous ceramic tile. At this time, when the porous ceramic tile is manufactured, a certain chemical change occurs due to the contact between the modified antimicrobial active material and moisture, so that hydroxide ions of a certain concentration or more can be generated. Due to the generated hydroxide ion, Lt; RTI ID = 0.0 > 11 < / RTI >
구체적으로, 상기 기공 표면 pH가 약 11미만인 경우 약염기 또는 산성에 가깝게 되어 습기에 의한 누룩곰팡이, 대장균 등 인체에 해로울 수 있는 미생물의 서식을 차단할 수 없고, 부유 미생물 발생을 저감시킬 수 없다. 그러므로, 기공 표면을 pH 약 11이상 유지함으로써 상기 다공성 세라믹 타일을 사용하는 실내의 쾌적한 환경을 유지시킬 수 있다.
Specifically, when the pH of the pore surface is less than about 11, it is difficult to prevent the formation of microorganisms such as koi mold, E. coli and the like which are close to weak bases or acidity due to moisture and can not reduce the occurrence of suspended microorganisms. Therefore, by maintaining the pore surface at a pH of about 11 or more, a pleasant environment of the room using the porous ceramic tile can be maintained.
다공성 세라믹 타일 제조방법Porous ceramic tile manufacturing method
본 발명의 다른 구현예에서, γ-알루미나 및 항균활성물질을 혼합하여 세라믹 성형체를 형성하는 단계; 상기 세라믹 성형체를 건식 프레스 성형하여 다공성 세라믹 타일을 제조하는 단계; 상기 성형된 다공성 세라믹 타일을 건조하는 단계; 상기 건조된 다공성 세라믹 타일에 유약으로 시유하는 단계; 및 상기 시유된 다공성 세라믹 타일을 열분해하여 소성하는 단계를 포함하는 다공성 세라믹 타일 제조방법을 제공한다.
In another embodiment of the present invention, there is provided a method for producing a ceramic molded body, comprising the steps of: forming a ceramic formed body by mixing? -Alumina and an antibacterial active material; A step of dry-pressing the ceramic formed body to produce a porous ceramic tile; Drying the shaped porous ceramic tile; Dipping the dried porous ceramic tile into a glaze; And thermally decomposing and sintering the sintered porous ceramic tile to obtain a porous ceramic tile.
상기 세라믹 성형체를 제조하는 단계(S100)는 γ-알루미나 및 항균활성물질의 혼합물을 제조하는 단계 및 상기 혼합물을 이용하여 세라믹 성형체를 성형하는 단계를 포함할 수 있다. The step (S100) of preparing the ceramic formed body may include a step of preparing a mixture of gamma -alumina and an antibacterial active material, and a step of molding the ceramic compact using the mixture.
상기 혼합물을 제조하는 방법은 특별히 제한되는 것은 아니고, 이 분야에서 공지된 혼합 방법을 모두 포함할 수 있으나, 예를 들면, 우선, 상기 혼합물을 볼밀을 이용하여 균일한 혼합 및 적정한 크기로 분쇄할 수 있으며, 분쇄 시에는 물, 유기바인더, 분산제 및 소포제 등을 적절한 양으로 첨가할 수 있다. 이어서, 상기 전술한 바와 같이 분쇄된 혼합물이 적절한 점도를 가지는 슬러리 형태가 되면, 이를 분무 건조 공정을 통하여 구형 입자를 가지는 과립 분말 형태로 제조할 수 있다.
The method for preparing the mixture is not particularly limited and may include all mixing methods known in the art. For example, the mixture may be homogeneously mixed with a ball mill and pulverized to an appropriate size Water, an organic binder, a dispersing agent, and an antifoaming agent may be added in an appropriate amount when pulverizing. Next, as described above, when the pulverized mixture becomes a slurry having an appropriate viscosity, it can be prepared into a granular powder having spherical particles through a spray drying process.
상기 제조된 세라믹 형성체를 건식 프레스 성형하는 단계(S200)를 통하여 다공성 세라믹 타일을 제조할 수 있다. 상기 제조된 세라믹 성형체, 즉 과립분말 형태의 혼합물을 건식프레스 금형에 투입하여 원하는 형상의 세라믹 성형체를 제조할 수 있다.
Porous ceramic tiles can be manufactured through a dry press molding process (S200) of the ceramic formed body. The prepared ceramic formed body, that is, the mixture in the form of granulated powder, is put into a dry press mold to produce a ceramic shaped body having a desired shape.
그 후, 상기 성형된 다공성 세라믹 타일을 건조하는 단계(S300)를 포함할 수 있다. 상기 건조하는 단계에 있어서, 건조온도가 특별히 제한되는 것은 아니지만, 약 200℃ 내지 약 250℃의 온도에서 건조를 수행할 수 있으며, 이 경우 고온의 가스 연속로를 통과하는 짧은 시간 동안에 성형체가 변형 또는 소지 폭발과 같은 불량을 억제할 수 있다.
And then drying the shaped porous ceramic tile (S300). In the drying step, although the drying temperature is not particularly limited, the drying may be performed at a temperature of about 200 ° C to about 250 ° C. In this case, during a short time passing through the hot gas- It is possible to suppress the defects such as the substrate explosion.
상기 건조된 다공성 세라믹 타일은 유약으로 시유하는 단계(S300)를 포함할 수 있다. 상기 단계(S300)는 다공성 세라믹 타일의 표면에 유약을 입히기 위한 것으로, 시유 방법에 특별히 제한이 있는 것은 아니며, 유약의 슬러리를 이용하는 습식법, 유약의 건분 또는 과립, 프리트의 칼리트를 이용하는 건식법 등을 사용할 수 있다.
The dried porous ceramic tile may include sieving (S300). The step (S300) is for applying a glaze to the surface of the porous ceramic tile. The method is not particularly limited, and a wet method using a slurry of glaze, a dried powder or granule of glaze, a dry method using calt of frit, .
마지막으로, 상기 시유된 다공성 세라믹 타일을 열분해하여 소성하는 단계(S400)를 포함할 수 있다. 열분해란 외부에서 열을 가하여 분자를 활성화시켰을 때, 약한 결합이 끊어져 새로운 물질을 만드는 것을 의미하고, 소성이란 조합된 원료를 가열하여 경화성 물질을 만드는 조작을 일컫는바, 상기 다공성 세라믹 타일에 열을 가하여 분해과정 및 소성과정을 동시에 거침으로써, 다공성 세라믹 타일이 포함하는 물질을 변형 시켜 소성함으로써 항균성을 부여하는 전단계를 유지할 수 있다. Finally, the porous ceramics tile may be pyrolyzed and fired (S400). Pyrolysis is a process of breaking a weak bond when a molecule is activated by applying heat from the outside to produce a new material. Firing is an operation of making a curable material by heating a combined raw material. Heat is applied to the porous ceramic tile By carrying out the decomposition process and the firing process at the same time, it is possible to maintain the previous stage of imparting antimicrobial properties by modifying the material contained in the porous ceramic tile and firing it.
예를 들어, 다공성 세라믹 타일이 포함하는 항균 활성물질이 탄산칼슘(CaCO3)인 경우 열분해 및 소성과정을 통하여 이산화탄소 및 생석회로 분해(CaCO3-> CaO+CO2)될 수 있고, 이때 생성된 생석회는 상기 다공성 세라믹 타일 내부에 고르게 분포될 수 있다. 이 때, 상기 다공성 세라믹 타일의 흡습과정등을 통하여 상기 생성된 생석회가 수분과 접촉하게 되는바, 이로 인해 항균성이 부여되는 과정은 전술한 바와 같다.
For example, if the antimicrobial active material contained in the porous ceramic tile is calcium carbonate (CaCO 3 ), it can be decomposed into carbon dioxide and calcium oxide (CaCO 3 -> CaO + CO 2 ) through pyrolysis and calcination, The burnt lime can be evenly distributed inside the porous ceramic tile. At this time, the generated quicklime is brought into contact with moisture through the moisture absorption process of the porous ceramic tiles, and thus the process of imparting antimicrobial properties is as described above.
상기 열분해는 약 800℃ 내지 약 1000℃의 온도에서 수행될 수 있다. 상기 열분해의 온도에 제한되는 것은 아니나, 상기 범위의 온도에서 열분해를 수행함으로써 항균성을 발휘하는 전단계의 다공성 세라믹 타일을 형성할 수 있다.
The pyrolysis may be carried out at a temperature of from about 800 [deg.] C to about 1000 < 0 > C. Although not limited to the temperature of the pyrolysis, it is possible to form a porous ceramic tile of a previous stage which exhibits antimicrobial activity by performing pyrolysis at the temperature within the above range.
또한, 상기 열분해는 약 1분 내지 약 15분의 시간동안 수행될 수 있다. 상기 열분해 시간을 벗어나서 열처리 하는 경우 열분해가 충분히 이뤄지지 않을 수 있다. 그러므로 상기 범위의 시간동안 열분해를 수행함으로써 항균성을 발휘하는 전단계의 다공성 세라믹 타일을 형성할 수 있고, 생산량 및 에너지 비용 면에서 장점을 가질 수 있다.
In addition, the pyrolysis can be carried out for a time of from about 1 minute to about 15 minutes. If the heat treatment is performed outside the pyrolysis time, pyrolysis may not be sufficiently performed. Therefore, by performing the thermal decomposition for the time in the above range, the porous ceramic tile of the previous stage exhibiting the antibacterial property can be formed, and it can be advantageous in terms of the production amount and the energy cost.
상기 다공성 세라믹 타일 제조방법에 있어서, 열분해 및 소성단계(S400)를 거침으로써 항균 활성물질을 변형시킬 수 있고, 항균성을 발휘할 수 있는 전단계로 다공성 세라믹 타일에 고르게 분포하게 할 수 있다. 그 후, 상기 다공성 세라믹 타일을 사용하는 중 흡습과정을 통해 기공 표면을 염기화하여 다공성 세라믹 타일에 항균성이 자연스럽게 부여될 수 있다.
In the method for manufacturing porous ceramic tiles, the antimicrobial active material can be deformed by pyrolysis and firing (S400), and evenly distributed in the porous ceramic tile with a preliminary stage capable of exhibiting antimicrobial activity. Thereafter, the surface of the pore is basified through the moisture absorption process using the porous ceramic tile, so that the antibacterial property can be naturally imparted to the porous ceramic tile.
이하에서는 본 발명의 구체적인 실시예들을 제시한다. 다만, 하기에 기재된 실시예들은 본 발명을 구체적으로 예시하거나 설명하기 위한 것에 불과하며, 이로서 본 발명이 제한되어서는 아니된다.
Hereinafter, specific embodiments of the present invention will be described. However, the embodiments described below are only intended to illustrate or explain the present invention, and thus the present invention should not be limited thereto.
<<
실시예Example
및 And
비교예Comparative Example
>>
실시예Example
하기 표 1에 기재된 성분들의 혼합물을 볼밀을 이용하여 분쇄하고, 이에 따라 얻어진 슬러리를 분무건조 공정을 통해 균일하게 혼합되고 함수율이 8%, 평균입도 300㎛인 구형의 과립분말을 제조하였다. A mixture of the ingredients shown in Table 1 below was milled using a ball mill, and the resulting slurry was uniformly mixed through a spray drying process to produce a spherical granular powder having a water content of 8% and an average particle size of 300 占 퐉.
이어서, 상기 과립분말을 건식 프레스 성형하여 가로, 세로, 두께가 각각 7cm, 7cm, 0.6cm인 다공성 세라믹 타일을 제조하였다. 다음으로, 상기 다공성 세라믹 타일을 250℃의 연속 건조로에서 건조한 후, 평균입도가 15um이고 화도가 750℃인 프리트 분말과 안료를 물에 분산하여 스프레이 도포하여 시유하였다. Subsequently, the granular powder was dry-pressed to produce porous ceramic tiles of 7 cm, 7 cm, and 0.6 cm in width, length, and thickness, respectively. Next, the porous ceramic tile was dried in a continuous drying furnace at 250 ° C., and then frit powder and pigment having an average particle size of 15 μm and a degree of firing of 750 ° C. were dispersed in water and spray-applied.
마지막으로, 상기 시유된 다공성 세라믹 타일을 가스 연속로(RHK)에 투입하여 850℃의 온도로 10분 동안 열분해하고 소성하여 기공의 평균직경이 5nm이고 기공률이 45%인 다공성 세라믹 타일을 제조하였다.
Finally, the above-mentioned porous ceramic tiles were put into a gas continuous furnace (RHK), pyrolyzed at a temperature of 850 ° C for 10 minutes, and fired to prepare a porous ceramic tile having an average pore diameter of 5 nm and a porosity of 45%.
비교예Comparative Example
하기 표 1에 기재된 성분 중 항균활성물질을 포함하지 않은 것을 제외하고는 상기 실시예와 동일한 방법으로 다공성 세라믹 타일을 제조하였다.
Porous ceramic tiles were prepared in the same manner as in the above example, except that the antimicrobial active materials were not included in the ingredients listed in Table 1 below.
(CaCO3)13.1
(CaCO 3)
<<
실험예Experimental Example
> - 다공성 세라믹 타일의 > - Porous ceramic tile
pHpH
측정 Measure
상기 실시예 및 비교예의 다공성 세라믹 타일을 25℃의 물(100ml)에 10분 동안 담궈두었다. 그 후 시간에 따라 다공성 세라믹 타일이 포함하는 기공에 이온들이 존재하게 되는바 이때 기공 표면의 산도(pH)를 pH측정기를 이용하여 pH값을 측정하였고, 그 결과를 하기 표 2에 나타내었다.
Porous ceramic tiles of the above Examples and Comparative Examples were soaked in water (100 ml) at 25 캜 for 10 minutes. Thereafter, ions were present in pores included in the porous ceramic tiles according to time. At this time, the pH value of the pore surface was measured using a pH meter. The results are shown in Table 2 below.
상기 표 2를 참조하면, 항균 활성 물질을 포함한 실시예의 다공성 세라믹 타일의 경우 다공성 세라믹 타일이 포함하는 기공 표면이 상대적으로 상당히 빠른 시간에 pH11 이상의 염기성을 띄게 됨을 확인 할 수 있었으며, 다공성 세라믹 타일을 상온에서 사용하는 중에 발생하는 흡습으로 인해 기공 표면이 염기화 되는바, 이로 인해 항균 및 항곰팡이 성능이 증대됨을 유추할 수 있다.Referring to Table 2, it can be seen that the porous ceramic tile of the embodiment including the antimicrobial active material exhibits a basicity of pH 11 or more in a relatively short period of time on the pore surface including the porous ceramic tile, It is possible to deduce that the surface of the pores is basified by the hygroscopicity generated during the use of the surfactant, thereby increasing the antibacterial and antifungal performance.
이와 비교하여, 항균 활성 물질을 포함하지 않은 비교예의 다공성 세라믹 타일의 경우 10분이상 시간이 경과하여도, 다공성 세라믹 타일이 포함하는 기공 표면의 pH가 약 9정도에서 멈추었는바 염기성을 띄지 않음을 확인하였고, 다공성 세라믹 타일의 사용 중 발생할 수 있는 세균 번식 저하등의 항균성능을 발휘하지 못함을 유추할 수 있다. In comparison, the comparative porous ceramic tiles not containing the antimicrobial active material showed that the pH of the pore surface including the porous ceramic tiles was stopped at about 9 even after a lapse of 10 minutes or longer, And it can be inferred that it does not exhibit antibacterial performance such as degradation of germs that may occur during use of the porous ceramic tile.
Claims (11)
상기 항균 활성물질은 상기 모물질 100 중량부에 대하여 3 중량부 내지 30 중량부 포함되며,
다공성 세라믹 타일이 평균 직경이 1nm 내지 1mm인 기공을 포함하고, 기공률이 30% 내지 60%이며, 상기 기공 표면의 pH가 11 이상인
다공성 세라믹 타일.
A parent material, gamma -alumina and an antibacterial active material,
Wherein the antimicrobial active material is contained in an amount of 3 to 30 parts by weight based on 100 parts by weight of the mother material,
Wherein the porous ceramic tile includes pores having an average diameter of 1 nm to 1 mm, a porosity of 30% to 60%, and a pH of the pore surface of 11 or more
Porous ceramic tiles.
상기 항균 활성물질은 금속 탄산염인
다공성 세라믹 타일.
The method according to claim 1,
The antimicrobial active substance is a metal carbonate
Porous ceramic tiles.
상기 금속 탄산염은 탄산칼슘, 탄산칼륨, 탄산바륨, 탄산마그네슘, 탄산나트륨 및 이들의 조합으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함하는
다공성 세라믹 타일.
3. The method of claim 2,
The metal carbonate includes at least one selected from the group consisting of calcium carbonate, potassium carbonate, barium carbonate, magnesium carbonate, sodium carbonate, and combinations thereof
Porous ceramic tiles.
상기 모물질은 점토, 백토, 황토 및 이들의 조합으로 이루어진 군으로부터 선택된 어느 하나 이상을 포함하는
다공성 세라믹 타일.
The method according to claim 1,
Wherein the parent material comprises at least one selected from the group consisting of clay, clay, loess, and combinations thereof
Porous ceramic tiles.
상기 세라믹 성형체를 건식 프레스 성형하여 다공성 세라믹 타일을 제조하는 단계;
상기 성형된 다공성 세라믹 타일을 건조하는 단계;
상기 건조된 다공성 세라믹 타일에 유약으로 시유하는 단계; 및
상기 시유된 다공성 세라믹 타일을 열분해하여 소성하는 단계를 포함하고,
상기 항균 활성물질은 상기 모물질 100 중량부에 대하여 3 중량부 내지 30 중량부 혼합하며,
상기 다공성 세라믹 타일은 평균 직경이 1nm 내지 1mm인 기공을 포함하고, 기공률이 30% 내지 60%이며, 상기 기공 표면의 pH가 11 이상인
다공성 세라믹 타일 제조방법.
Forming a ceramic formed body by mixing a mother material,? -Alumina, and an antibacterial active material;
A step of dry-pressing the ceramic formed body to produce a porous ceramic tile;
Drying the shaped porous ceramic tile;
Dipping the dried porous ceramic tile into a glaze; And
And pyrolyzing and baking the sintered porous ceramic tile,
The antimicrobial active material is mixed in an amount of 3 to 30 parts by weight with respect to 100 parts by weight of the mother material,
The porous ceramic tile includes pores having an average diameter of 1 nm to 1 mm, a porosity of 30% to 60%, a pH of the pore surface of 11 or more
A method for manufacturing a porous ceramic tile.
상기 열분해는 800℃ 내지 1000℃의 온도에서 수행되는 것을 특징으로 하는
다공성 세라믹 타일 제조방법.
10. The method of claim 9,
Characterized in that the pyrolysis is carried out at a temperature of 800 ° C to 1000 ° C
A method for manufacturing a porous ceramic tile.
상기 열분해는 1분 내지 15분의 시간동안 수행되는 것을 특징으로 하는
다공성 세라믹 타일 제조방법.10. The method of claim 9,
Characterized in that the pyrolysis is carried out for a time of from 1 minute to 15 minutes
A method for manufacturing a porous ceramic tile.