KR101508721B1 - Heat resistant ceramic composition and method for manufacturing the same - Google Patents
Heat resistant ceramic composition and method for manufacturing the same Download PDFInfo
- Publication number
- KR101508721B1 KR101508721B1 KR20130056424A KR20130056424A KR101508721B1 KR 101508721 B1 KR101508721 B1 KR 101508721B1 KR 20130056424 A KR20130056424 A KR 20130056424A KR 20130056424 A KR20130056424 A KR 20130056424A KR 101508721 B1 KR101508721 B1 KR 101508721B1
- Authority
- KR
- South Korea
- Prior art keywords
- glass frit
- heat
- composition
- heat resistant
- pyrophyllite
- Prior art date
Abstract
본 발명은 도자기용 소지조성물에 대한 것으로, 보다 구체적으로는 특정 조성의 유리 프리트를 포함함으로써 내열충격성이 향상된 내열자기용 소지조성물 및 상기 소지조성물 제조방법에 관한 것이다.
More specifically, the present invention relates to a heat-resistant self-supporting composition having improved thermal shock resistance by including a glass frit having a specific composition and a method for producing the above-mentioned base composition.
Description
본 발명은 도자기용 소지조성물에 대한 것으로, 보다 구체적으로는 특정 조성의 유리 프리트를 포함함으로써 내열충격성이 향상된 내열자기용 소지조성물 및 상기 소지조성물 제조방법에 관한 것이다.
More specifically, the present invention relates to a heat-resistant self-supporting composition having improved thermal shock resistance by including a glass frit having a specific composition and a method for producing the above-mentioned base composition.
일반적으로 물이나 음식을 끓이기 위해서 사용하는 용기를 통상적으로 내열 용기라고 하는데, 요업제품인 내열 용기로는 유리제 용기, 법랑 용기, 도자기제 용기가 있다. Generally, a container used for boiling water or food is usually called a heat-resistant container. Examples of heat-resistant containers for ceramic articles include glass containers, enamel containers, and pottery containers.
이 중 도자기제 용기인 내열자기는 담고 있는 수용물에 열을 가할 수 있도록 제조된 도자용기로서, 예를 들면 차나 음식물을 끓이고 졸이거나 약을 달이는 데 이용되는 도자기로 된 용기를 들 수 있다. 내열자기가 이와 같은 용도로 이용되고 있는 데에는 그것이 가지고 있는 다양한 장점 때문이다. 즉 내열자기는 가열시 원적외선 등을 발산할 수 있는 세라믹 재료로 구성되어 생체에 유익한 영향을 줄 뿐만 아니라 통상의 도자기가 가지는 기공성, 통기성, 비산화성이 있으며, 더 나아가 일단 가열이 되고 난 후에는 쉽게 식지 않는 보열, 보온성이 뛰어나기 때문이다.Among them, heat resistant porcelain is a porcelain container made to be able to apply heat to the contained water, for example, a container made of porcelain which is used for boiling, solving or pouring tea or food. Heat resistance is used for this purpose because of its various advantages. That is, the heat-resistant magnet is formed of a ceramic material capable of emitting far-infrared rays during heating, and not only has a beneficial effect on the living body, but also has porosity, air permeability and non-oxidization property of ordinary ceramics. Further, Because it does not easily cool down, it is excellent in warmth.
하지만 주로 사용되는 도자기 내열용기인 뚝배기의 경우 흡수율이 10∼12% 정도로서 거의 도기(陶器)와 유사하다. 또한 엽장석(petalite:페타라이트)을 사용하여 만든 것은 흡수율이 6∼8% 정도로서 경질 도기와 거의 유사하다. 따라서 식기를 설거지 할 때 설거지 국물이 기물 속에 흡수되었다가 다시 가열할 때 기물 속에서 굽부분이나 균열이 이루어진 유약 사이의 설거지 국물이 음식 속으로 들어갈 수도 있게 되므로 비위생적이다. However, in the case of pots, pottery heat-resistant containers, the absorption rate is about 10 ~ 12%, which is almost similar to pottery. In addition, petalite (petalite) made using the water absorption rate of about 6-8% is similar to hard pottery. Therefore, when the dishes are washed, the dishes are absorbed into the objects, and when they are heated again, the dishes and the cracks between the glazed dishes may enter into the food, which is unsanitary.
이와 같이 내열자기가 흡수율이 높은 것은 내열자기가 화기 또는 열에 직접 접촉한다는 점에서 일반적인 도자기 보다는 더 높은 내열성을 갖지만 가열과 냉각이 지속적으로 반복되기 때문에 도자기의 몸체를 이루게 되는 소지 조성물과 자기의 표면에 입혀지는 유약 조성물의 열팽창계수 차이로 인해 표면에 미세한 균열이 발생하기 쉬운 특성으로 인해서이다. 또한, 일단 표면에 균열이 발생하면 내열자기 자체의 수명이 단축될 뿐만 아니라 그 부위에 불순물이 끼이게 되어 위생적으로 좋지 않은 것은 분명하다. As described above, the high heat absorption rate of the heat-resistant magnet has a higher heat resistance than that of general ceramics in that heat-resistant magnetism directly contacts fire or heat, but since the heating and cooling are continuously repeated, Due to the characteristic that the surface is slightly cracked due to the difference in the thermal expansion coefficient of the glaze composition to be coated. In addition, once cracks are formed on the surface, it is obvious that the life of the heat-resistant self is shortened, and impurities are trapped in the surface, which is not hygienic.
이에 대해, 일반적으로 유리나 법랑의 경우에는 기물의 흡수성이 거의 없어, 위생적인 것으로 평가받는다. 따라서, 흡수율이 높다는 것은 도자기제 내열용기 즉 내열자기의 치명적인 결함일 수 있다. On the other hand, in general, in the case of glass or enamel, there is little absorption of the material, and it is regarded as hygienic. Therefore, a high absorption rate may be a fatal defect in a ceramic heat-resistant container, i.e., a heat-resistant magnet.
일반적으로 알려진 엽장석을 이용한 내열자기는 그 소지로서 고령토나 2차 점토 또는 샤모트 등을 혼합하여 습식분쇄 하여 여과공정을 거친 후 일상생활에 필요한 형태의 조리용기를 성형하는 공정을 거치고 이를 800℃ 전, 후에서 초벌 소성한 후, 재벌로서 내열자기에 유약으로서 엽장석 60~70중량%, 카리장석과 석회석의 혼합물 10~15중량%, 활석과 규석 5~10%중량 등의 혼합비율로 이루어진 유약조성물을 이용하여 내열자기를 생산하였다.Heat-resistant porcelain, commonly known as feldspar, is made by mixing kaolin, secondary clay, or chamois, wet milling it, filtering it, and then shaping a cooking vessel of the type required for daily life. , And then glazed with a mixing ratio of 60 to 70% by weight of foliar friezes, 10 to 15% by weight of a mixture of feldspar and limestone, 5 to 10% by weight of talc and zircon as glaze, The composition was used to produce heat resistant magnets.
그러나, 상기한 종래의 방법에 의하여 생산된 내열자기는 흡수율이 높은 것은 물론 일반적으로 충격강도가 약하여 주방에서 사용하던 중 떨어지거나 다른 물체와 부딪쳐 충격을 받을 때는 쉽게 부서지거나 균열이 생기는 등의 문제점이 있었다.However, the heat-resistant magnetic material produced by the above-described conventional method has a high water absorption rate and generally has a low impact strength, so that it can be easily broken or cracked when it is used in a kitchen or hit by other objects there was.
이러한 문제를 극복하기 위해 내열자기 제조용 물질 조성물에 대한 다양한 연구가 진행되고 있으나, 수없이 반복적으로 가열, 냉각되는 내열자기로는 여전히 부족함이 있으며, 더욱 개선된 물성을 가지는 내열자기 제조용 물질 조성물이 요구되고 있다.
In order to overcome such a problem, various studies have been made on a composition for heat resistant self-production, but there is still a lack of heat resistant magnetic materials which are repeatedly heated and cooled many times, and a material composition for heat resistant self- .
본 발명자들은 이러한 문제점을 해결하기 위하여 연구 노력한 결과 새로운 조성을 갖는 유리 프리트(glass frit)를 포함하는 내열자기용 소지조성물을 개발함으로써 본 발명을 완성하였다.The inventors of the present invention have made efforts to solve these problems and have completed the present invention by developing a thermoplastic self-supporting composition containing glass frit having a novel composition.
따라서, 본 발명의 목적은 유리화를 촉진시켜 흡수율이 거의 0%에 이르는 치밀한 재질의 내열자기를 형성할 수 있는 내열자기용 소지조성물 및 상기 소지조성물 제조방법을 제공하는 것이다.Accordingly, an object of the present invention is to provide a heat resistant self-supporting composition capable of promoting vitrification and forming a heat-resistant magnetic material of a dense material having a water absorption rate of almost 0% and a method for producing the above base resin composition.
본 발명의 다른 목적은 저팽창성 특성으로 인해 열팽창계수를 낮추는 특성을 갖는 유리 프리트를 포함함으로써 우수한 내화성 및 내열충격성을 갖는 내열자기용 소지조성물 및 상기 소지조성물 제조방법을 제공하는 것이다.Another object of the present invention is to provide a heat resistant self-supporting composition having excellent fire resistance and thermal shock resistance by including a glass frit having a characteristic of lowering its thermal expansion coefficient due to its low expansibility, and a method for producing the aforementioned composition.
본 발명의 또 다른 목적은 유약을 발라 소성하는 과정에서 소지와 유약 사이의 열팽창계수의 차이를 약화시켜 소지에 균열이 발생하는 것을 방지할 수 있는 내열자기용 소지조성물 및 상기 소지조성물 제조방법을 제공하는 것이다.It is still another object of the present invention to provide a base material for a heat resistant magnetic material and a method for manufacturing the base material composition, which can prevent a crack from occurring in the base material by weakening the difference in thermal expansion coefficient between the base material and the glaze during the baking process of the glaze .
본 발명의 목적들은 이상에서 언급한 목적들로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
The objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned can be clearly understood by those skilled in the art from the following description.
상술된 본 발명의 목적을 달성하기 위해, 먼저, 본 발명은 내열자기용 유리프리트 40 내지 50 중량%, 납석 10 내지 20중량%, 및 점토광물 30 내지 40 중량%를 포함하는 내열자기용 소지조성물을 제공한다.In order to achieve the object of the present invention, first, the present invention provides a heat resistant self-supporting composition comprising 40 to 50 wt% of heat resistant magnetic glass frit, 10 to 20 wt% of pyrophyllite, and 30 to 40 wt% .
바람직한 실시예에 있어서, 상기 점토광물은 카올린계 점토광물이다. In a preferred embodiment, the clay mineral is a kaolin clay mineral.
바람직한 실시예에 있어서, 장석 및 활석 중 하나 이상을 10 내지 20중량% 더 포함한다. In a preferred embodiment, it further comprises 10 to 20% by weight of at least one of feldspar and talc.
바람직한 실시예에 있어서, 상기 내열자기용 유리프리트는 산화리튬(Li2O) 9 내지 16 중량%를 포함한다. In a preferred embodiment, the glass frit for heat-resistant magnet comprises 9 to 16% by weight of lithium oxide (Li 2 O).
바람직한 실시예에 있어서, 상기 내열자기용 유리프리트는 실리카(SiO2) 64 내지 78중량% 및 산화알루미늄(Al203) 11 내지 20중량%를 더 포함한다. In a preferred embodiment, the heat resistant magnetic glass frit further comprises 64 to 78 wt% of silica (SiO 2 ) and 11 to 20 wt% of aluminum oxide (Al 2 O 3 ).
바람직한 실시예에 있어서, 상기 내열자기용 유리프리트는 K2O 1 내지 3 중량%, Na2O 0.3 내지 0.5중량% 및 MgO, CaO, BaO 중 어느 하나 이상 3 내지 10중량%를 더 포함한다. In a preferred embodiment, the glass frit for heat-resistant magnet further comprises K 2 O 1 to 3 wt%, Na 2 O 0.3 to 0.5 wt%, and 3 to 10 wt% of any one of MgO, CaO and BaO.
또한, 본 발명은 준비된 납석 및 점토광물과 물을 볼밀에 삽입하는 삽입단계; 상기 볼밀에서 납석 및 점토광물을 미분쇄하는 동시에 배합하는 1차 배합단계; 및 1차 배합단계에서 형성된 납석 및 점토광물이 포함된 1차 배합 슬러리에 내열자기용 유리프리트를 첨가하여 소지조성물용 슬러리를 형성하는 2차 배합단계;를 포함하는 것을 특징으로 하는 내열자기용 소지조성물 제조방법을 제공한다. In addition, the present invention provides a method of manufacturing a ball mill, comprising the steps of: inserting prepared pyrophyllite and clay minerals and water into a ball mill; A first mixing step of finely grinding and mixing pyroxene and clay minerals in the ball mill; And a second blending step of adding a heat-resistant magnetic glass frit to a primary blend slurry containing the pyrophyllite and clay minerals formed in the first blending step to form a slurry for a base composition, A method for preparing a composition is provided.
바람직한 실시예에 있어서, 상기 2차 배합단계는 2 시간미만으로 수행된다. In a preferred embodiment, the secondary compounding step is performed in less than 2 hours.
바람직한 실시예에 있어서, 상기 2차 배합단계에서 첨가되는 내열자기용 유리프리트는 1㎛ ~ 44㎛ 직경을 갖는다. In a preferred embodiment, the heat resistant magnetic glass frit added in the second mixing step has a diameter of 1 to 44 mu m.
바람직한 실시예에 있어서, 상기 삽입단계에서 장석 및 활석 중 하나 이상이 더 삽입된다.In a preferred embodiment, at least one of the feldspar and talc is inserted in the inserting step.
바람직한 실시예에 있어서, 상기 납석과 점토광물의 중량비는 1 ~ 2 : 3 ~ 4이다. In a preferred embodiment, the weight ratio of pyrophyllite to clay mineral is 1 to 2: 3 to 4.
바람직한 실시예에 있어서, 상기 납석과 내열자기용 유리프리트의 중량비는 1 ~ 2 : 4 ~ 5이다. In a preferred embodiment, the weight ratio of the pyrophyllite to the heat resistant glass frit is 1 to 2: 4 to 5.
본 발명은 다음과 같은 우수한 효과를 갖는다.The present invention has the following excellent effects.
먼저, 본 발명의 내열자기용 소지조성물 및 상기 소지조성물 제조방법에 의하면 유리화를 촉진시켜 흡수율이 거의 0%에 이르는 치밀한 재질의 내열자기를 형성할 수 있다.First, according to the heat resistant self-supporting composition of the present invention and the method of producing the above-mentioned base resin composition, vitrification can be promoted to form a heat resistant magnetic material having a denseness of almost 0%.
또한, 본 발명의 내열자기용 소지조성물 및 상기 소지조성물 제조방법에 의하면 저팽창성 특성으로 인해 열팽창계수를 낮추는 특성을 갖는 유리 프리트를 포함함으로써 내열자기가 우수한 내화성 및 내열충격성을 갖는다.Further, according to the heat resistant self-supporting composition of the present invention and the method of producing the above-mentioned base composition, the glass frit having the characteristic of lowering the thermal expansion coefficient due to the low expansion property is included, so that it has excellent fire resistance and thermal shock resistance.
또한, 본 발명의 내열자기용 소지조성물 및 상기 소지조성물 제조방법에 의하면 유약을 발라 소성하는 과정에서 소지와 유약 사이의 열팽창계수의 차이를 약화시켜 소지에 균열이 발생하는 것을 방지할 수 있다.
Also, according to the heat resistant self-supporting composition of the present invention and the method of manufacturing the base composition, the difference in thermal expansion coefficient between the base and the glaze can be minimized in the process of baking the glaze, thereby preventing cracks from being generated.
도 1 및 도 2는 본 발명의 실시예들에서 얻어진 내열자기용 소지조성물에 포함되는 내열자기용 유리프리트의 분쇄 및 배합시간에 따른 소지조성물용 슬러리의 pH를 측정한 실험결과 그래프이다.
도 3은 본 발명의 실시예들에서 얻어진 내열자기용 소지조성물로 제조된 소성시편의 온도 구간별 열팽창계수를 측정한 결과그래프이다.
도 4는 본 발명의 실시예들에서 얻어진 내열자기용 소지조성물로 제조된 소성제품의 내열충격성 평가 방법 사진이다.
도 5는 본 발명의 실시예들에서 얻어진 내열자기용 소지조성물로 제조된 소성제품의 내열충격성 평가 결과 사진이다.FIG. 1 and FIG. 2 are graphs showing experimental results of measuring the pH of a slurry for a base composition according to the pulverization and blending time of a heat resistant magnetic glass frit contained in a base paper for heat resistant magnetism obtained in Examples of the present invention.
FIG. 3 is a graph showing the results of measurement of the thermal expansion coefficient of each of the temperature ranges of the fired test piece made of the thermoplastic self-supporting base composition obtained in the examples of the present invention.
Fig. 4 is a photograph of a method for evaluating thermal shock resistance of a fired product manufactured from the thermoplastic self-supporting composition obtained in Examples of the present invention.
Fig. 5 is a photograph of thermal shock resistance evaluation results of a fired product made of a heat resistant magnetic bead composition obtained in Examples of the present invention. Fig.
본 발명에서 사용되는 용어는 가능한 현재 널리 사용되는 일반적인 용어를 선택하였으나, 특정한 경우는 출원인이 임의로 선정한 용어도 있는데 이 경우에는 단순한 용어의 명칭이 아닌 발명의 상세한 설명 부분에 기재되거나 사용된 의미를 고려하여 그 의미가 파악되어야 할 것이다.Although the terms used in the present invention have been selected as general terms that are widely used at present, there are some terms selected arbitrarily by the applicant in a specific case. In this case, the meaning described or used in the detailed description part of the invention The meaning must be grasped.
이하, 첨부한 도면 및 바람직한 실시예들을 참조하여 본 발명의 기술적 구성을 상세하게 설명한다.Hereinafter, the technical structure of the present invention will be described in detail with reference to the accompanying drawings and preferred embodiments.
그러나, 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화 될 수도 있다. 명세서 전체에 걸쳐 본 발명을 설명하기 위해 사용되는 동일한 참조번호는 동일한 구성요소를 나타낸다.However, the present invention is not limited to the embodiments described herein but may be embodied in other forms. Like reference numerals used to describe the present invention throughout the specification denote like elements.
본 발명의 제 1 기술적 특징은 흡수율이 거의 0%에 이르는 치밀한 재질의 내열자기를 형성할 수 있을 뿐만 아니라 내열충격성 또한 향상시킬 수 있는 새로운 조성의 내열자기용 소지조성물에 있다. 즉, 본 발명의 내열자기용 소지조성물은 내열자기의 특성을 보다 향상시킬 수 있도록 특정 조성으로 제조된 내열자기용 유리프리트를 포함하고 있기 때문이다.The first technical feature of the present invention resides in a novel composition for heat-resistant magnet with which heat-resistant magnetic material having a water absorption rate of almost 0% can be formed, as well as thermal shock resistance can be improved. That is, the heat resistant self-supporting composition of the present invention includes a heat resistant magnetic glass frit made of a specific composition so as to further improve the heat resistant magnetic properties.
따라서, 본 발명은 이러한 기술적 특징을 구현하기 위하여 내열자기용 유리프리트 40 내지 50 중량%, 납석 10 내지 20중량%, 및 점토광물 30 내지 40 중량%를 포함하는 내열자기용 소지조성물을 제공한다.Accordingly, the present invention provides a heat resistant self-supporting composition comprising 40 to 50% by weight of heat resistant magnetic glass frit, 10 to 20% by weight of pyrophyllite, and 30 to 40% by weight of clay mineral in order to realize this technical feature.
여기서, 각 구성요소의 함량범위는 무수한 실험을 통해 결정된 최적비로서 각 구성요소의 함량이 상술된 범위를 벗어나게 되면 원하는 내열자기의 특성이 나타나지 않음을 실험적으로 확인할 수 있었다. Here, the content range of each component is experimentally confirmed that the desired heat-resistant magnetic characteristics are not exhibited when the content of each component deviates from the above-described range as an optimum ratio determined through a number of experiments.
먼저, 본 발명의 내열자기용 소지조성물에 포함된 내열자기용 유리프리트는 비결정질로서 산화리튬(Li2O) 9 내지 16 중량%를 포함한다. 이에 더하여, 실리카(SiO2) 64 내지 78중량% 및 산화알루미늄(Al203) 11 내지 20중량%를 포함할 수 있는데, 경우에 따라서는 K2O 1 내지 3 중량%, Na2O 0.3 내지 0.5중량% 및 MgO, CaO, BaO 중 어느 하나 이상 3 내지 10중량%를 더 포함할 수 있다. First, the glass frit for heat resistant magnet contained in the heat resistant self-supporting composition of the present invention is amorphous and contains 9 to 16% by weight of lithium oxide (Li 2 O). In addition, silica (SiO 2) 64 to 78% and aluminum oxide by weight (
특히, 본 발명의 내열자기용 유리프리트는 산화리튬을 일정량 함유하고 있어야 하는데, 산화리튬이 유리프리트에 필수구성요소로 존재하게 되면 실리카(SiO2)의 높은 용융온도를 저하시킴으로서 용융을 촉진시키고 유리의 점도를 저하시키는 성분으로 작용할 수 있기 때문이다. 그 결과 산화리튬이 포함된 유리프리트가 내열자기용 소지조성물에 사용되면 소결과정에서 소지가 저팽창성을 갖기 때문에 내열충격성이 향상될 수 있다. In particular, the heat-resistant magnetic glass frit of the present invention must contain a certain amount of lithium oxide. When lithium oxide is present as an essential component in the glass frit, the high melting temperature of silica (SiO 2 ) is lowered, As a component for lowering the viscosity of the resin. As a result, when a glass frit containing lithium oxide is used in a base composition for heat resistant magnet, the thermal shock resistance can be improved because the base has low expansion property in the sintering process.
본 발명의 내열자기용 유리프리트가 소지조성물에 포함됨으로써 유리화특성이 향상되어 흡수율이 거의 0%인 치밀한 재질의 내열자기를 형성하는데 상당부분 기여하고 있는 것으로 예측된다. It is predicted that the vitrification property is improved by incorporating the glass frit for heat resistant magnet of the present invention into the base composition, and thus contributes to forming a heat resistant magnet of a dense material having a water absorption rate of substantially 0%.
또한, 본 발명의 소지조성물은 납석을 포함하는데, 납석이 SiO2와 Al2O3 공급원으로 작용하여 소지의 유리화특성을 보다 향상시키기 때문이다. 특히 납석은 국내에서 용이하게 공급 가능한 광물이므로 국내산 납석의 활용을 위해 사용하였을 뿐만 아니라 SiO2와 Al2O3 공급원으로 본 발명과 같이 납석을 사용한 경우 다른 광물을 사용한 경우보다 내열자기의 재질이 더 치밀하게 형성되었다.
In addition, the base composition of the present invention includes pyrophyllite because pyrophosphate acts as a source of SiO 2 and Al 2 O 3 to further improve vitrification characteristics of the substrate. In particular, since pyrophyllite is an easily available mineral in Korea, it is used not only for utilization of domestic pyrophyllite but also for materials of SiO 2 and Al 2 O 3 , .
또한, 본 발명의 소지조성물에 포함되는 점토광물은 고령토, 백토 등 카올린계 점토광물이 바람직하다. The clay minerals contained in the base composition of the present invention are preferably kaolin clay minerals such as kaolin and clay.
한편, 경우에 따라서는 본 발명의 소지조성물이 장석 및 활석 중 하나 이상을 10 내지 20중량% 더 포함할 수 있는데, 본 발명에 사용되는 유리프리트의 조성에서 알칼리성분이 부족하면 유리의 융점이 높고, 내열자기 소지의 유리화 성분이 부족하기 때문이다. On the other hand, depending on the case, the base composition of the present invention may further contain at least one of feldspar and talc in an amount of 10 to 20% by weight. When the amount of the alkaline component is insufficient in the composition of the glass frit used in the present invention, This is because vitrification components of heat-resistant self-supporting are insufficient.
다음으로, 본 발명은 준비된 납석 및 점토광물과 물을 볼밀에 삽입하는 삽입단계; 상기 볼밀에서 납석 및 점토광물을 미분쇄하는 동시에 배합하는 1차 배합단계; 및 1차 배합단계에서 형성된 납석 및 점토광물이 포함된 1차 배합 슬러리에 내열자기용 유리프리트를 첨가하여 소지조성물용 슬러리를 형성하는 2차 배합단계;를 포함하는 것을 특징으로 하는 내열자기용 소지조성물 제조방법을 제공한다. Next, the present invention provides a method for manufacturing a ball mill, comprising the steps of: inserting prepared pyrophyllite and clay minerals and water into a ball mill; A first mixing step of finely grinding and mixing pyroxene and clay minerals in the ball mill; And a second blending step of adding a heat-resistant magnetic glass frit to a primary blend slurry containing the pyrophyllite and clay minerals formed in the first blending step to form a slurry for a base composition, A method for preparing a composition is provided.
일반적으로 소지의 제조방법은 건식과 습식이 있으며, 원료의 성질,처리방법, 사용목적 등에 따라 알맞은 방법을 택한다. 건식 방법은 원료를 곱게 분쇄하여 원료별로 저장된 것 중에서 필요한 양을 각각 저울로 달아서 혼합하며, 이때 적당량의 물을 첨가해서 균일하게 혼합이 되도록 잘 섞는다. 습식방법은 백색 소지의 도기나 자기의 경우에 주로 이용되며, 수비한 점토와 각각 미분쇄한 원료들을 적당량씩 달아서 혼합하고 물을 사용하여 이장(泥漿:slip)으로 만들어 잘 저어서 균일하게 배합이 되도록 한다. 이 방법 외에 최근 많이 사용되는 것은 본 발명이 채택하고 있는 것처럼 괴상(塊狀)의 원료들을 조 크러셔(jaw crusher) 또는 플랫 밀(plat mill)로 조분쇄, 중간분쇄한 각 원료의 필요량과 점토의 적당량을 달아서 적당량의 물과 함께 볼 밀(ball mill)에 넣고, 미분쇄와 동시에 혼합하는 방법을 주로 택하고 있다. 이 때 볼 밀은 두꺼운 철판으로 된 원통형의 내면에 알루미나 질의 블록을 붙이고 그 속에 구석(球石)을 넣은 것이며, 원료와 물을 넣고 회전시키므로 원료의 마쇄와 혼합을 동시에 할 수 있게 되어 있다. In general, the manufacturing method of the substrate is dry and wet, and a proper method is selected according to the nature of the raw material, the treatment method, the purpose of use. In the dry method, the raw materials are crushed finely, and the required amount of each raw material is weighed and mixed with each balance, and an appropriate amount of water is added thereto, and the mixture is homogeneously mixed. The wet method is mainly used for white porcelain or porcelain. It mixes the defective clay and each of the fine pulverized raw materials in an appropriate amount, mixes it with water, slips it into water and mixes it uniformly. . In addition to this method, the most recently used method is to mix raw materials of masses in the form of a jaw crusher or a plat mill as required by the present invention, A suitable amount is added to a ball mill together with an appropriate amount of water, and the mixture is mixed with fine pulverization. In this case, the ball mill is made of a thick steel plate with an inner alumina block attached to the inner surface of the cylinder, and a round stone is placed in the ball mill. It is possible to simultaneously polish and mix the raw material by rotating the raw material and water.
다만, 본 발명의 소지조성물 제조방법은 볼밀을 이용하는 공지된 소지제조방법과는 달리 소지조성물에 포함된 모든 구성요소를 볼밀에 넣고 분쇄 및 배합하지 않는 점에서 상이한데, 공지된 소지에 포함되지 않는 특정 조성의 내열자기용 유리프리트를 필수구성요소로 포함하기 때문이다.However, unlike a known method of producing a base paper using a ball mill, the method of manufacturing the base paper of the present invention is different from the known base paper manufacturing method in that all components included in the base paper are put into a ball mill and are not pulverized and blended, This is because the glass frit for heat resistance of a specific composition is included as an essential component.
즉, 본 발명의 소지조성물에 포함되는 내열자기용 유리프리트는 슬러리 상태로 장시간 배합시 소지조성물용 슬러리의 pH를 높여서 소지의 성형성을 좋지 않게 하기 때문이다.That is, the heat-resistant magnetic glass frit contained in the base composition of the present invention increases the pH of the slurry for the base composition when blended for a long time in a slurry state, so that the formability of the base is poor.
따라서, 본 발명의 소지조성물 제조방법은 상술된 바와 같이 내열자기용 유리프리트를 제외한 나머지 구성요소들을 1차 배합하여 1차 배합 슬러리를 형성하고, 1차 배합 슬러리에 내열자기용 유리프리트를 첨가하여 소지조성물용 슬러리를 형성하는 2차 배합단계로 구분되는데, 2차 배합단계는 적어도 소지조성물용 슬러리를 구성하는 모든 구성요소가 균일하게 배합될 수 있는 최소시간이 확보되어야 하며, 최대는 내열자기용 유리프리트의 조성 및 배합시간을 고려하여 5 시간 이내로 수행될 수 있지만 바람직하게는 2 시간미만으로 수행될 수 있다. Therefore, in the method for producing the base composition of the present invention, the above-described components other than the heat resistant magnetic glass frit are firstly compounded to form a primary blended slurry, and a heat-resistant magnetic glass frit is added to the primary blended slurry And a second blending step of forming a slurry for a substrate composition. In the second blending step, a minimum time is required to ensure that at least all the constituents constituting the slurry for the substrate composition are uniformly blended, Can be carried out within 5 hours in consideration of the composition and the mixing time of the glass frit, but it can be preferably carried out at less than 2 hours.
2차 배합단계에서 첨가되는 내열자기용 유리프리트는 1㎛ ~ 44㎛ 직경을 가질 수 있는데, 내열자기용 유리프리트가 1차 배합단계에서 형성된 1차 배합슬러리에 포함된 구성요소들과 거의 동일한 크기를 갖도록 하여 볼밀에서의 분쇄 및 배합과정을 짧은 시간 동안 수행하기 위해서이다. The heat-resistant magnetic glass frit added in the second blending step may have a diameter of 1 to 44 탆. The heat-resistant magnetic glass frit may have substantially the same size as the components contained in the primary blending slurry formed in the first blending step So that the milling and blending process in the ball mill can be performed for a short time.
경우에 따라서는 삽입단계에서 장석 및 활석 중 하나 이상이 더 삽입될 수 있는데, 소지조성물의 구성요소가 갖는 유리화성분 특히 내열자기용 유리프리트의 조성을 고려하여 그 함량이 결정될 수 있다.In some cases, at least one of feldspar and talc may be inserted in the inserting step. The content of vitrification component of the component of the base composition, particularly the composition of the glass frit for heat-resistant magnetism, may be determined.
또한, 삽입단계에서 볼밀에 삽입되는 납석과 점토광물의 중량비는 1 ~ 2 : 3 ~ 4일 수 있으며, 2차 배합단계에서 1차 배합슬러리에 첨가되는 내열자기용 유리프리트의 함량은 납석과 내열자기용 유리프리트의 중량비가 1 ~ 2 : 4 ~ 5가 되도록 첨가될 수 있다.
In addition, the weight ratio of the pyrophyllite and clay minerals to be inserted into the ball mill in the inserting step may be 1 to 2: 3 to 4, and the content of the heat-resistant magnetic glass frit added to the primary compounding slurry in the second compounding stage is pyrophyllite and heat resistance Magnetic glass frit may be added in a weight ratio of 1 to 2: 4 to 5.
실시예 1. 내열자기용 유리프리트의 준비Example 1 Preparation of glass frit for heat resistant magnet
표 1과 같은 조성(단위:중량%)으로 원료조성물을 준비하여 용융로에 넣고 950℃에서 1시간동안 처리하여 원료조성물을 완전히 용융시킨 후, 용융물을 찬물에부어 유리화물질을 얻었다. 그 후 얻어진 유리화물질을 0.01mm ~ 0.2mm크기로 1차 분쇄하여 내열자기용 유리프리트를 제조하였다. 제조된 내열자기용 유리프리트를 건식분쇄기를 이용하여 1㎛ ~ 44㎛직경을 갖도록 2차 분쇄하여 실시예2 내지 실시예9에 사용될 수 있는 내열자기용 유리프리트1 내지 8(GNR1 내지 GNR8)을 준비하였다. The raw material composition was prepared in the composition (unit: wt%) as shown in Table 1, put into a melting furnace, treated at 950 ° C for 1 hour to completely melt the raw material composition, and the melted material was poured into cold water to obtain a vitrification material. Thereafter, the obtained vitrified material was first pulverized to a size of 0.01 mm to 0.2 mm to prepare a glass frit for heat resistant magnetism. The prepared heat-resistant magnetic glass frit was subjected to secondary grinding to have a diameter of 1 to 44 mu m using a dry grinder to obtain heat resistant
장석Carly
실시예 2 내지 9 : 소지조성물의 준비Examples 2 to 9: Preparation of base composition
표 2와 같은 조성(단위 : 중량%)으로 준비된 구성요소들을 다음과 같이 볼밀에서 1차 및 2차 배합하여 소지조성물 1 내지 8(NR-1 내지 NR-8)을 제조하였다.
(NR-1)Example 2
(NR-1)
(NR-2)Example 3
(NR-2)
(NR-3)Example 4
(NR-3)
(NR-4)Example 5
(NR-4)
(NR-5)Example 6
(NR-5)
(NR-6)Example 7
(NR-6)
(NR-7)Example 8
(NR-7)
(NR-8)Example 9
(NR-8)
표 2와 같은 조성으로 원료조성물을 준비하여 볼밀에 GNR1 내지 GNR8을 제외한 구성요소들의 총합산량 60g 당 80cc의 물을 삽입한 다음 7시간동안 분쇄 및 배합하여 1차 배합슬러리를 형성하였다. 그 후 1차 배합슬러리에 GNR1 내지 GNR8을 첨가하여 20분 동안 배합하여 소지조성물용 슬러리를 형성하였다. 그 후 소지조성물용 슬러리를 탈수하여 소지조성물1 내지 8(NR-1 내지 GNR-8)을 얻었다.
A raw material composition was prepared as shown in Table 2, and 80 cc of water was added per 60 g of the total amount of the components excluding GNR1 to GNR8 to the ball mill, followed by pulverization and blending for 7 hours to form a primary blend slurry. GNR1 to GNR8 were then added to the primary blend slurry and blended for 20 minutes to form a slurry for the base composition. Thereafter, the slurry for the substrate composition was dewatered to obtain the
실험예 1Experimental Example 1
실시예1에서 얻어진 내열자기용 유리프리트1 내지 8(GNR1 내지 GNR8)의 화학성분을 분석하고 그 결과를 표 3에 나타내었다.The chemical components of the heat resistant
프리트1
(NF-1)Glass
(NF-I)
프리트2
(NF-2)Glass
(NF-2)
프리트3
(NF-3)Glass
(NF-3)
프리트4
(NF-4)Glass
(NF-4)
프리트5
(NF-5)Glass
(NF-5)
프리트6
(NF-6)Glass
(NF-6)
프리트7
(NF-7)Glass
(NF-7)
프리트 8
(NF-8)Glass
(NF-8)
타group
Get
실험예 2Experimental Example 2
실시예1에서 얻어진 내열자기용 유리프리트1 내지 8(GNR1 내지 GNR8)을 공지된 소지제조방법과 같이 볼밀에 처음부터 삽입하여 분쇄 및 배합하였을 때 내열자기용 유리프리트에 함유된 리튬이 리튬 이온으로 용출되어 나오는지를 확인하기 위하여 분쇄 및 배합시간에 따른 슬러리의 pH를 pH meter를 이용하여 측정하고 그 결과를 도 1 및 도 2에 나타내었다.When the heat-resistant
도 1 및 도 2로부터, 유리 프리트에 포함된 산화리튬의 함량이 많을수록 pH가 높은 것을 확인할 수 있다.1 and 2, it can be seen that the higher the content of lithium oxide contained in the glass frit is, the higher the pH is.
즉, 도 1에 도시된 소지조성물1 내지 3(NR-1, NR-2 및 NR-3)에 포함된 내열자기용 유리프리트 1 내지 3인 GNR-1, GNR-2 및 GNR-3은 각각 9.5 12.1 15.4의 산화리튬이 첨가된 것이고, 도 2에 도시된 소지조성물4 내지 8(NR-4 내지 NR-8)에 포함된 내열자기용 유리프리트 4 내지 8인 GNR-4, GNR-5, GNR-6, GNR-7 및 GNR-8은 각각 12.4, 9.6, 12.6, 12.9, 12.7의 산화리튬이 첨가된 것이기 때문이다.That is, GNR-1, GNR-2 and GNR-3, which are the
이러한 실험결과는 산화리튬이 petalite의 광물상으로 존재하지 않는 것이고 유리의 융제로서 작용한 산화리튬이 용출되어 pH를 증가시키는 것을 보여주는 것으로 예측된다. 또한 실시예1과 같이 내열자기용 유리프리트 제조시 산화리튬 함량을 높여서 제조한다 하더라도 유리프리트가 포함된 내열자기용 소지조성물에서도 산화리튬의 함량이 증가하지 않음을 의미하는 것으로 해석될 수 있다. These results suggest that lithium oxide is not present as a mineral phase of petalite and that lithium oxide, which acts as a glass frit, is eluted to increase the pH. Also, even when the content of lithium oxide is increased in the production of the glass frit for heat-resisting magnets as in Example 1, it can be interpreted that the content of lithium oxide does not increase even in the base composition for heat resistance containing glass frit.
따라서 내열자기용 유리프리트에 포함된 산화리튬의 함량이 증가할수록 산화리튬이 함유된 유리프리트가 볼밀에서 분쇄 및 배합시 사용되는 물과 반응하여 리튬 수산화물(LiOH 및 이의 수산화물 LiOHㅇH2O)을 형성하여 물에 용해되어 pH를 높일 가능성이 크다 할 것이다. Therefore, as the content of lithium oxide contained in the glass frit for heat resistant magnet increases, the glass frit containing lithium oxide reacts with the water used for crushing and blending in the ball mill to form lithium hydroxide (LiOH and its hydroxide LiOH H 2 O) And it is likely to be dissolved in water to increase the pH.
보다 구체적으로 살펴보면, 먼저, 유리 프리트 GNF3(산화리튬 9.5%)을 원료로 사용하여 제조한 소지조성물 NR-3 경우도 볼밀에서의 분쇄 및 배합시간이 1시간 후의 pH는 7.8로 산화리튬이 용출되어 나오지는 않지만, 분쇄 및 배합시간이 증가함에 따라 리튬이 용출되어 초기 급속도로 pH가 증가하다가 5시간 이후 계속 증가함을 볼 수 있다. 따라서 내열자기용 유리프리트가 포함된 상태에서 분쇄 및 배합시간은 5시간 이내에서 끝내는 것이 바람직할 수 있다. More specifically, first, in the case of the base composition NR-3 prepared by using glass frit GNF3 (lithium oxide 9.5%) as a raw material, the pH after grinding and mixing time in the ball mill was 7.8, and lithium oxide was eluted However, as the pulverization and mixing time increases, lithium is eluted and the pH rapidly increases at an initial rapid rate, and then it increases continuously after 5 hours. Therefore, it is preferable that the milling and mixing time is finished within 5 hours in the state that the heat resistant magnetic glass frit is contained.
또한, 내열자기용 유리프리트 GNF1을 원료로 사용한 소지조성물 NR-1의 경우 분쇄 및 배합시간이 1시간 경과한 후의 pH가 9.4로 상당히 높은 값을 나나태고 있는데, 이는 GNF-1의 산화리튬이 petalite의 광물상보다는 유리상에 상당히 많이 존재하고 있으며, 이 유리상에 존재하는 산화리튬이 분쇄 시 물과 반응하여 유리상에서 물로 용출되어 나오는 것으로 예측된다. 따라서 실시예1과 같이 내열자기용 유리프리트 제조 시 탄산리튬의 함량이 30wt% 이상이면 내열자기용 소지조성물의 원료로 사용이 곤란할 것으로 판단되었다. Also, in the case of the base composition NR-1 using the glass frit GNF1 as a raw material for heat-resistant magnetism, the pH value after the crushing and the mixing time of 1 hour has reached a considerably high value of 9.4, indicating that lithium oxide of GNF- And it is predicted that lithium oxide present in the glass phase reacts with water during the pulverization and elute from the glass phase to water. Therefore, it was judged that when the content of lithium carbonate was 30 wt% or more in preparing the glass frit for heat-resistant magnet as in Example 1, it would be difficult to use it as a raw material for a heat resistant magnetic bearing composition.
또한, 칼리장석과 알칼리토산화물이 첨가된 내열자기용 유리프리트 GNF4 내지 GNF8을 원료로 사용한 소지조성물 NR-4 내지 NR-8의 경우도 분쇄 및 배합시간에 길어지면 pH가 높아지는 변화를 나타내고 있음을 알 수 있다.Also, in the case of base compositions NR-4 to NR-8 using glass frit GNF4 to GNF8 as heat resistant magnetic glass frit added with calcite and alkaline earth oxides, the pH of the composition rises as the crushing and mixing time increases Able to know.
이러한 실험결과들은, 소지조성물용 슬러리의 pH가 증가하면 배토의 가소성은 떨어지게 되는데 pH가 9.5 이상이 되면 소지 배토의 가소성은 급격히 떨어져 성형하기 곤란하게 되는 점을 고려하면, 본 발명과 같이 가능한 내열자기용 유리프리트가 물과 반응할 시간을 짧게 하기 위해 1차배합단계와 2차배합단계로 나누어 소지조성물을 제조하는 것이 바람직함을 보여 준다할 것이다.
These experimental results show that when the pH of the slurry for the substrate composition is increased, the plasticity of the clay is deteriorated. When the pH is 9.5 or more, the plasticity of the clay is sharply reduced, It is preferable to prepare the substrate composition by dividing into a first mixing step and a second mixing step in order to shorten the time for the glass frit for water to react with water.
실험예 3Experimental Example 3
실시예2 내지 실시예9에서 얻어진 내열자기용 소지조성물1 내지 8(NR-1 내지 NR-8)을 대상으로 pH , 성형성 및 부피비중을 평가하고 그 결과를 표 4에 나타내었다. pH는 pH미터로 측정하였고, 성형성 및 부피비중은 점토의 가소성(可塑性)측정 방법 중 phefferkorn 방식을 응용하여 평가하였으며, 성형성 평가 결과는 1(매우 낮음), 2(낮음),3(보통), 4(높음), 5(매우 높음)으로 표시하였다. The pH, the formability and the bulk specific gravity of the heat resistant self-supporting
(NR-1)Example 2
(NR-1)
(NR-2)Example 3
(NR-2)
(NR-3)Example 4
(NR-3)
(NR-4)Example 5
(NR-4)
(NR-5)Example 6
(NR-5)
(NR-6)Example 7
(NR-6)
(NR-7)Example 8
(NR-7)
(NR-8)Example 9
(NR-8)
비중volume
importance
실험예 4Experimental Example 4
실시예2 내지 실시예9에서 얻어진 내열자기용 소지조성물1 내지 8(NR-1 내지 NR-8)로 제조된 시편을 1350℃에서 소성하여 얻어진 소성시편1 내지 8(소성시편 NR-1 내지 소성시편 NR-8)을 KSL 3114에 의거 흡수율을 측정하였다. 소성시편 NR-1의 경우 0.14, 소성시편 NR-2는 0.13인 흡수율을 나타내었으며, 소성시편 NR-3 내지 NR-8은 모두 0의 흡수율을 보였다. 소성시편 NR-1 및 NR-2의 경우 내열자기용 유리프리트 GNR1 및 GNR2가 납석과 탄산리튬으로만 구성되면 유리의 융제성분이 부족하여 소지조성물 소성시 액상이 부족하여 치밀화되지 못한 것으로 판단되었다. 하지만, 소성시편 NR-4 내지 NR-8의 경우는 소지조성물에 포함된 유리프리트 GNR4 내지 GNR8을 제조할 때 칼리장석과 기타 알칼리 토금속 성분이 들어감으로써 내열자기 소지조성물 소성시 충분한 액상을 형성되었기 때문인 것으로 예측된다.
The
실험예 5Experimental Example 5
실시예6에서 얻어진 소지조성물 NR-5를 1350℃에서 소성하여 얻어진 소성시편 NR-5를 대상으로 온도 구간별 열팽창계수를 측정하고 그 결과를 도 3에 나타내었다.The thermal expansion coefficient of the fired sample NR-5 obtained by firing the substrate composition NR-5 obtained in Example 6 at 1350 ° C was measured at each temperature section, and the results are shown in FIG.
도 3으로부터, 실제 내열자기가 사용되는 온도대인 500℃에서 소성시편 NR-5의 열팽창계수는 1.68 x 10-6(1/K) 이었음을 알 수 있다.
3, it can be seen that the thermal expansion coefficient of the fired specimen NR-5 was 1.68 x 10 < -6 > (1 / K) at 500 DEG C, which is the temperature at which the actual heat resistant magnet is used.
실험예 6Experimental Example 6
실시예2 내지 실시예9에서 얻어진 내열자기용 소지조성물1 내지 8(NR-1 내지 NR-8)로 제조된 시편을 1350℃에서 소성하여 얻어진 φ80㎜ x 8㎜ 크기의 소성시편1 내지 8(소성시편 NR-1 내지 소성시편 NR-8)을 대상으로 내열충격성을 평가하였다.(1) to (8) of a size of 80 mm x 8 mm obtained by firing a specimen made of the heat-resistant
먼저, 소성시편 NR-1 내지 소성시편 NR-8을 직접 가스레인지에서 550℃까지 가열한 후 바로 물에 담그는 방법으로 평가하였는데, 모든 시편에서 균열(crack)이 발생하지 않음을 확인하였다.First, the fired specimens NR-1 to NR-8 were heated directly from the gas range to 550 ° C and immediately immersed in water. The cracks did not occur in all the specimens.
다음으로, 실시예2 내지 실시예9에서 얻어진 소지조성물 NR-1 내지 NR-8로 용기로 제조하여 소성한 제품을 대상으로 열충격 시편을 제조하여 450℃로 가열한 후 찬물에 급냉하는 방법으로 도 4에 도시된 것과 같이 2차 평가를 실시하였고 그 결과 사진을 도 5a 및 5b에 도시하였다.Next, a hot shock test specimen was manufactured using the substrate compositions NR-1 to NR-8 obtained in Examples 2 to 9 and baked in a container, heated to 450 DEG C, and then quenched in cold water A secondary evaluation was conducted as shown in Fig. 4, and the resulting photographs are shown in Figs. 5A and 5B.
도 5a 및 5b에 도시된 바와 같이, 소지조성물 NR-1 ~ NR-8로 제조한 모든 제품이 균열이 발생하지 않은 것을 확인할 수 있었다. As shown in FIGS. 5A and 5B, it was confirmed that all products made of the base compositions NR-1 to NR-8 did not crack.
이상의 실험결과들로부터, 본 발명의 소지조성물로 제조된 내열자기는 조리 시 발생되는 열충격에 대한 안정성이 확보되었음을 알 수 있다.
From the above experimental results, it can be seen that the heat-resistant magnet made from the base composition of the present invention has stability against thermal shock generated during cooking.
본 발명은 이상에서 살펴본 바와 같이 바람직한 실시 예를 들어 도시하고 설명하였으나, 상기한 실시 예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변경과 수정이 가능할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, Various changes and modifications will be possible.
Claims (12)
And 10 to 20% by weight of pyrophyllite, and 30 to 40% by weight of clay mineral, wherein the glass frit comprises 9 to 16% by weight of lithium oxide (Li 2 O).
상기 점토광물은 카올린계 점토광물인 것을 특징으로 하는 내열자기용 소지조성물.
The method according to claim 1,
Wherein the clay mineral is a kaolin clay mineral.
장석 및 활석 중 하나 이상을 10 내지 20중량% 더 포함하는 것을 특징으로 하는 소지 조성물.
The method according to claim 1,
Feldspar and at least one of talc and talc.
상기 내열자기용 유리프리트는 실리카(SiO2) 64 내지 78중량% 및 산화알루미늄(Al203) 11 내지 20중량%를 더 포함하는 것을 특징으로 하는 내열자기용 소지조성물.
The method according to claim 1,
Wherein the heat resistant magnetic glass frit further comprises 64 to 78 wt% of silica (SiO 2 ) and 11 to 20 wt% of aluminum oxide (Al 2 O 3 ).
상기 내열자기용 유리프리트는 K2O 1 내지 3 중량%, Na2O 0.3 내지 0.5중량% 및 MgO, CaO, BaO 중 어느 하나 이상 3 내지 10중량%를 더 포함하는 것을 특징으로 하는 내열자기용 소지조성물.
The method according to claim 1,
Wherein the heat resistant magnetic glass frit further contains K 2 O 1 to 3 wt%, Na 2 O 0.3 to 0.5 wt%, and at least one of MgO, CaO, and BaO 3 to 10 wt% The composition of claim 1,
상기 볼밀에서 납석 및 점토광물을 미분쇄하는 동시에 배합하는 1차 배합단계; 및
1차 배합단계에서 형성된 납석 및 점토광물이 포함된 1차 배합 슬러리에 내열자기용 유리프리트를 첨가하여 소지조성물용 슬러리를 형성하는 2차 배합단계를 포함하고,
상기 내열자기용 유리프리트는 산화리튬(Li2O) 9 내지 16 중량%를 포함하는 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
An inserting step of inserting prepared pyrophyllite and clay mineral and water into a ball mill;
A first mixing step of finely grinding and mixing pyroxene and clay minerals in the ball mill; And
And a second blending step of forming a slurry for a base composition by adding a heat resistant magnetic glass frit to a first blending slurry containing pyrophyllite and clay minerals formed in a first blending step,
Wherein the glass frit for heat-resistant magnet comprises 9 to 16% by weight of lithium oxide (Li 2 O).
상기 2차 배합단계는 2 시간미만으로 수행되는 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
8. The method of claim 7,
Wherein the second mixing step is performed for less than 2 hours.
상기 2차 배합단계에서 첨가되는 내열자기용 유리프리트는 1㎛ ~ 44㎛직경을 갖는 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
8. The method of claim 7,
Wherein the heat-resistant magnetic glass frit added in the secondary blending step has a diameter of 1 탆 to 44 탆.
상기 삽입단계에서 장석 및 활석 중 하나 이상이 더 삽입되는 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
8. The method of claim 7,
Wherein at least one of feldspar and talc is further inserted in the inserting step.
상기 납석과 점토광물의 중량비는 1 ~ 2 : 3 ~ 4인 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
8. The method of claim 7,
Wherein the weight ratio of the pyrophyllite to the clay mineral is 1 to 2: 3 to 4.
상기 납석과 내열자기용 유리프리트의 중량비는 1 ~ 2 : 4 ~ 5인 것을 특징으로 하는 내열자기용 소지조성물 제조방법.
8. The method of claim 7,
Wherein the weight ratio of the pyrophyllite to the heat resistant magnetic glass frit is 1: 2 to 4: 5.