KR101470699B1 - Manufacturing method of rectangular beam using pipe - Google Patents

Manufacturing method of rectangular beam using pipe Download PDF

Info

Publication number
KR101470699B1
KR101470699B1 KR1020120124789A KR20120124789A KR101470699B1 KR 101470699 B1 KR101470699 B1 KR 101470699B1 KR 1020120124789 A KR1020120124789 A KR 1020120124789A KR 20120124789 A KR20120124789 A KR 20120124789A KR 101470699 B1 KR101470699 B1 KR 101470699B1
Authority
KR
South Korea
Prior art keywords
pipe
manufacturing
radius
work
present
Prior art date
Application number
KR1020120124789A
Other languages
Korean (ko)
Other versions
KR20140058132A (en
Inventor
김동학
김광순
Original Assignee
현대하이스코 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 현대하이스코 주식회사 filed Critical 현대하이스코 주식회사
Priority to KR1020120124789A priority Critical patent/KR101470699B1/en
Publication of KR20140058132A publication Critical patent/KR20140058132A/en
Application granted granted Critical
Publication of KR101470699B1 publication Critical patent/KR101470699B1/en

Abstract

원형 단면을 가지는 파이프를 이용하여 모서리가 라운드진 각관 성형체를 제조하는 방법에 관하여 개시한다.
본 발명은 원형 단면을 가지는 소재 파이프를 성형홈을 구비하는 금형으로 가압하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.A method for manufacturing a corrugated pipe with corners rounded by using a pipe having a circular cross section is disclosed.
The present invention is characterized in that a work pipe having a circular cross section is pressed by a mold having a forming groove to form a rectangular pipe having a rectangular cross section whose edge is rounded, And a step of preparing the tubular molded body.

Description

원형 소재 파이프를 이용한 각관 성형체 제조방법{MANUFACTURING METHOD OF RECTANGULAR BEAM USING PIPE}TECHNICAL FIELD [0001] The present invention relates to a method of manufacturing a square pipe,

본 발명은 원형 단면을 가지는 파이프를 이용하여 모서리가 라운드진 각관 성형체를 제조하는 방법에 관한 것이다.
The present invention relates to a method of manufacturing a corrugated tube with corners rounded by using a pipe having a circular cross section.

차량은 지속적으로 경량화와 원가절감이 요구되고 있으며, 이에 따라 차량부품에는 다양한 형상의 관재들이 사용되고 있다.Vehicles are constantly required to be lightweight and cost-effective. Accordingly, various shapes of pipes are used for vehicle parts.

차량 성능에 있어서 중요한 요소중의 하나는 충돌시 탑승자를 보호할 수 있는 충돌 성능이다.One of the important factors in vehicle performance is crash performance, which can protect occupants in a crash.

그런데, 동일한 두께와 동일한 중량을 가지는 원형의 관재와 사각형의 관재의 충돌 성능을 비교하면, 원형 관재의 충돌 성능을 100% 라고 할때 사각형 관재의 충돌 성능은 130% 로 원형 관재보다 우수한 충돌 성능을 나타내게 된다.However, when the collision performance between the circular tube having the same thickness and the same weight and the rectangular tube is compared with the collision performance of the circular tube with 100%, the collision performance of the rectangular tube is 130% .

그런데, 원형 파이프의 경우 차량 부품이외에도 수요처가 많아 원형 파이프 전용 제조 설비(조관 설비)에 의한 양산이 이루어지고 있지만, 각형 강관의 경우 그렇지 못한 실정이다.However, in the case of circular pipes, there are many customers in addition to automobile parts, so mass production is being done by a manufacturing facility for circular pipes (tube making facility).

본 발명은 원형 파이프를 이용하여 각형 강관을 제조할 수 있는 방법을 제공하기 위한 것이다.
The present invention is to provide a method of manufacturing a square steel pipe using a circular pipe.

본 발명의 목적은 원형 소재 파이프를 이용하여 각관 성형체를 제조하기 위한 방법을 제공하기 위한 것이다.It is an object of the present invention to provide a method for manufacturing a square tube shaped body using a circular work pipe.

본 발명의 다른 목적은 충돌 성능이 우수한 차량 부품용 각관 성형체를 제조하는 방법을 제공하기 위한 것이다.
Another object of the present invention is to provide a method for manufacturing a square tube formed body for vehicle parts excellent in collision performance.

본 발명은 원형 단면을 가지는 소재 파이프를 성형홈을 구비하는 금형으로 가압하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.The present invention is characterized in that a work pipe having a circular cross section is pressed by a mold having a forming groove to form a rectangular pipe having a rectangular cross section whose edge is rounded, And a step of preparing the tubular molded body.

이 때, 상기 성형홈의 높이는 상기 소재 파이프의 반지름의 50~200% 범위인 것이 바람직하며,At this time, the height of the forming groove is preferably in the range of 50 to 200% of the radius of the work pipe,

상기 성형홈의 폭은 상기 소재 파이프의 직경과 동일하거나 직경보다 큰 것이 바람직하다.The width of the forming groove is preferably equal to or larger than the diameter of the work pipe.

또한, 상기 성형홈의 모서리의 곡률 반경은 상기 소재 파이프 반지름의 40~100% 범위인 것이 바람직하다.
It is preferable that the radius of curvature of the edge of the forming groove is in the range of 40 to 100% of the radius of the workpiece pipe.

그리고, 본 발명은 원형 단면을 가지는 소재 파이프를 가열한 상태에서 성형홈을 구비하는 금형을 이용하여 가압하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 열간 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.According to the present invention, a material pipe having a circular cross section is heated by using a mold having a molding groove in a heated state, hot-molded into a rectangular pipe having a rectangular cross section whose edges are rounded, And the circumferential length of the pipe corresponding to the circumferential length of the work pipe.

이 때, 상기 성형홈의 높이는 상기 소재 파이프의 반지름의 50~200% 범위인 것이 바람직하며, At this time, the height of the forming groove is preferably in the range of 50 to 200% of the radius of the work pipe,

상기 성형홈의 폭은 상기 소재 파이프의 직경과 동일하거나 직경보다 큰 것이 바람직하다.The width of the forming groove is preferably equal to or larger than the diameter of the work pipe.

또한, 상기 성형홈의 모서리의 곡률 반경은 상기 소재 파이프 반지름의 40~100% 범위인 것이 바람직하다.
It is preferable that the radius of curvature of the edge of the forming groove is in the range of 40 to 100% of the radius of the workpiece pipe.

또한, 본 발명은 원형 단면을 가지는 소재 파이프를 가열한 상태에서 성형홈을 구비하는 금형을 이용하여 가압하여 성형하며 급속냉각하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 핫스탬핑 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.Further, the present invention is characterized in that, in a state where a work pipe having a circular cross section is heated, a die having a forming groove is used to pressurize the material pipe, and the material pipe is rapidly cooled and hot stamped with a rectangular pipe having a rectangular cross- , And the circumferential length of the inner circumferential surface of the forming groove corresponds to the circumferential length of the work pipe.

이 때, 상기 성형홈의 높이는 상기 소재 파이프의 반지름의 50~200% 범위인 것이 바람직하며, At this time, the height of the forming groove is preferably in the range of 50 to 200% of the radius of the work pipe,

상기 성형홈의 폭은 상기 소재 파이프의 직경과 동일하거나 직경보다 큰 것이 바람직하다.The width of the forming groove is preferably equal to or larger than the diameter of the work pipe.

또한, 상기 성형홈의 모서리의 곡률 반경은 상기 소재 파이프 반지름의 40~100% 범위인 것이 바람직하다.
It is preferable that the radius of curvature of the edge of the forming groove is in the range of 40 to 100% of the radius of the workpiece pipe.

본 발명은 원형 소재 파이프를 이용하여 각관 성형체를 제조할 수 있는 방법을 제공한다.The present invention provides a method for manufacturing a square tube formed by using a circular work pipe.

본 발명으로 제조되는 각관 성형체를 자동차 부품에 사용하는 경우 원형 소재 파이프에 비하여 차량의 충돌 성능을 향상시키는 효과를 가져온다.
When the square pipe formed according to the present invention is used for an automobile part, the collision performance of the vehicle is improved as compared with the circular pipe.

도 1은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 소재 파이프를 나타낸 단면도,
도 2는 성형 불량이 발생한 상태를 나타낸 단면도,
도 3은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법으로 제조되는 각관 성형체를 나타낸 단면도,
도 4은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 금형을 나타낸 단면도,
도 5는 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 핫스탬핑 금형을 나타낸 단면도,BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a cross-sectional view showing a work pipe used in a method of manufacturing a round pipe with a circular work pipe according to the present invention;
Fig. 2 is a cross-sectional view showing a state in which molding defects have occurred,
FIG. 3 is a cross-sectional view of a square pipe formed by the method of manufacturing a square pipe according to the present invention,
FIG. 4 is a cross-sectional view showing a mold used in a method of manufacturing a square tube using the circular work pipe according to the present invention,
5 is a cross-sectional view illustrating a hot stamping mold used in a method of manufacturing a square pipe according to the present invention,

이하, 첨부된 도면들을 참조하여 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법의 실시예를 설명한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of a method for manufacturing a square pipe using the circular work pipe according to the present invention will be described with reference to the accompanying drawings.

이러한 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다.In this process, the thicknesses of the lines and the sizes of the components shown in the drawings may be exaggerated for clarity and convenience of explanation.

또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로써 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다.In addition, the terms described below are defined in consideration of the functions of the present invention, which may vary depending on the intention or custom of the user, the operator.

그러므로, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.
Therefore, definitions of these terms should be made based on the contents throughout this specification.

도 1은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 소재 파이프를 나타낸 단면도이고, 도 2는 성형 불량이 발생한 상태를 나타낸 단면도이고, 도 3은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법으로 제조되는 각관 성형체를 나타낸 단면도이다.FIG. 1 is a cross-sectional view showing a work pipe used in a method of manufacturing a round pipe according to the present invention, FIG. 2 is a sectional view showing a state where a molding failure occurs, Sectional view showing a square tube formed by the method of manufacturing a square tube using the same.

본 발명은 원형 소재 파이프를 이용한 각관 성형체 제조방법에 관한 것으로, 도 1에 도시한 바와 같이 원형의 단면을 가지는 소재 파이프(100)를 이용하여, 도 3에 도시된 바와 같은 모서리가 라운드진 사각형의 단면을 가지는 각관 성형체(200)를 제조하기 위한 방법을 제공하기 위한 것이다.[0001] The present invention relates to a method of manufacturing a square tube using a circular work pipe, and a method of manufacturing a square pipe by using a work pipe 100 having a circular cross section as shown in Fig. 1, To provide a method for manufacturing a square tube shaped body 200 having a cross section.

원형의 단면을 가지는 소재 파이프(100)의 규격은 직경(d)(파이프의 직경은 외경과 내경이 있으나, 본 명세서에서 파이프의 직경은 외경을 의미한다.)과 두께(t), 그리고 길이로 표시할 수 있다.The standard of the workpiece pipe 100 having a circular cross section is the diameter d (the diameter of the pipe is the outer diameter and the inner diameter, but the diameter of the pipe in this specification means the outer diameter), the thickness t, Can be displayed.

그런데, 길이는 필요에 따라 절단하여 사용할 수 있는 것이므로, 소재 파이프(100)의 단면 형상은 직경(d)과 두께(t)만으로 특정할 수 있다.However, since the length can be cut and used as needed, the cross-sectional shape of the workpiece pipe 100 can be specified only by the diameter d and the thickness t.

각관 성형체(200)의 둘레 길이에 대응하는 외주면 길이(다시말해, 원주 dπ)를 가지는 소재 파이프(100)를 성형하여, 각관 성형체(200)를 제조하는 방법을 제공하기 위한 것이다. 이러한 성형 방법에서는 두께 변화가 발생하지 않게 되므로, 소재 파이프(100)의 두께(t1)와 각관 성형체(200)의 두께는 동일해진다.The present invention is intended to provide a method for manufacturing a rectangular pipe shaped body 200 by molding a work pipe 100 having an outer circumferential length corresponding to the peripheral length of the rectangular pipe formed body 200 (i.e., a circumference d?). The thickness t1 of the workpiece pipe 100 and the thickness of the tube-shaped body 200 become the same.

여기서 각관 성형체의 둘레 길이와 소재 파이프의 외주면 길이(dπ)가 대응한 다는 것은, 동일하거나 ㅁ5% 수준의 오차 범위 내에 있다는 것을 의미한다.Here, the fact that the circumferential length of the tube-shaped formed body corresponds to the length (d?) Of the outer circumferential surface of the workpiece pipe means that it is within the same or an error range of about 5%.

소재 파이프(100)를 성형홈을 구비하는 금형을 이용하여 상하 방향으로 압축하여, 각관 성형체(200)를 제조한다.The work pipe 100 is compressed in the up and down direction by using a mold having a molding groove to manufacture the pipe shape forming body 200.

금형에는 각관 성형체(200)의 외형에 대응하는 성형홈이 구비되는데, 금형의 형상에 관해서는 도 4를 참조하여 후술한다.The mold is provided with a molding groove corresponding to the outer shape of the tube-shaped formed body 200, and the shape of the mold will be described later with reference to FIG.

소재 파이프(100)를 상하 방향으로 가압 성형할 때, 금형의 설계가 적절하지 못하면, 원하는 각관의 형태로 성형되지 못하고 도 2에 도시한 바와 같이 꺾임부(152)가 발생하여 땅콩 모양의 단면을 가지는 성형 불량이 발생하게 된다.
When the material pipe 100 is press-formed in the vertical direction, if the design of the metal mold is not appropriate, it can not be formed into a desired shape of a pipe, and a bent portion 152 is generated as shown in FIG. Resulting in a molding failure.

도 4은 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 금형을 나타낸 단면도이다.4 is a cross-sectional view illustrating a mold used in the method of manufacturing a square pipe using the circular work pipe according to the present invention.

도시한 바와 같이, 금형은 상부 금형(320)과, 하부 금형(340)으로 분할 형성되며, 성형하고자 하는 각관 성형체의 외형에 대응하는 성형홈(325, 345)을 구비하고 있다.As shown in the drawing, the mold is divided into an upper mold 320 and a lower mold 340, and has molding grooves 325 and 345 corresponding to the outer shape of the respective pipe forming body to be molded.

성형홈(325, 325)의 높이(h)는 각관 성형체(도 3의 200)의 높이에 대응하는 것으로, 소재 파이프(도 1의 100)의 직경(d)보다 작아야 한다. 여기서 성형홈의 높이라 함은 상부 금형(320)과 하부 금형(320)이 닫힌 상태에서의 성형홈의 높이를 의미한다.The height h of the forming grooves 325 and 325 corresponds to the height of the tube-shaped body (200 in Fig. 3) and should be smaller than the diameter d of the work pipe (100 in Fig. 1). Here, the height of the forming groove means the height of the forming groove when the upper mold 320 and the lower mold 320 are closed.

즉, 원형의 소재 파이프(100)를 상하로 가압하여 각관 성형체(200)로 성형 하여야 하므로, 소재 파이프(100)에 압력이 가해지기 위해서는 성형홈의 높이(h)가 소재 파이프(100)의 반지름(d/2)의 50~200% 범위인 것이 바람직하다.In order to apply pressure to the work pipe 100, the height h of the work groove must be equal to the radius of the work pipe 100, (d / 2) in the range of 50 to 200%.

성형홈의 높이가 반지름의 200%를 초과하면 가압력의 전달이 적어 성형불량이 발생하게 되며, 반대로 성형홈의 높이가 50% 미만인 경우에는 가압력이 과다하여 성형불량이 발생하게 된다.If the height of the forming groove exceeds 200% of the radius, the transfer of the pressing force is small and the forming defects occur. Conversely, if the height of the forming groove is less than 50%, the pressing force is excessive and molding failure occurs.

가압력이 적은 경우에는 각관 성형체(200)의 직선면의 성형이 탄성복원으로 인하여 제대로 성형되지 못하게 되며, 가압력이 과다한 경우 도 2와 같이 꺾임부(152)가 발생하는 성형불량 발생이 많아지게 된다.If the pressing force is small, the forming of the straight surface of the rectangular tube shaped body 200 is not properly formed due to the elastic restoration. If the pressing force is excessive, the occurrence of the molding defects in which the bent portions 152 are generated as shown in FIG.

소재 파이프(100)를 상하로 가압하게 되므로, 성형홈(325, 345)의 폭(w)은 소재 파이프의 직경과 동일하거나, 소재 파이프의 직경보다 넓은 것이 바람직하다.The width w of the forming grooves 325 and 345 is preferably equal to or larger than the diameter of the work pipe because the work pipe 100 is pressed upward and downward.

상하방향의 가압력으로 원형의 소재 파이프(100)를 단면이 라운드진 사각형 형상의 각관 성형체(200)를 제조하는 것인데, 이 때, 상기 성형홈(325, 345)의 모서리 곡률 반경(r)은 소재 파이프(100)의 반지름(d/2)의 40~100% 범위인 것이 바람직하다.The corner radius r of the forming grooves 325 and 345 is set to be the same as the radius of curvature of the material Is preferably in the range of 40 to 100% of the radius (d / 2) of the pipe 100.

모서리 곡률 반경(r)이 소재 파이프 반지름(d/2)의 40% 미만인 경우 곡률 반경의 축소가 과다하여, 도 2와 같은 꺾임 부위가 발생하는 성형 불량이 발생할 수 있으며, 반대로 모서리 곡률 반경(r)이 소재 파이프 반지름(d/2)의 100%를 초과하는 경우에는 변형량이 적어 탄성 복원으로 인하여 원하는 형상을 얻을 수 없는 문제점이 발생한다.
If the radius of curvature r of the corner is less than 40% of the radius of the workpiece pipe (d / 2), the reduction of the radius of curvature is excessive and molding defects such as those shown in Fig. 2 may occur. Conversely, ) Exceeds 100% of the material pipe radius (d / 2), there is a problem that the desired shape can not be obtained due to the elastic restoration because the amount of deformation is small.

본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법은 냉간 성형, 열간 성형, 핫스탬핑 성형에 모두 적용될 수 있다.The method of manufacturing a square pipe according to the present invention can be applied to both cold forming, hot forming and hot stamping.

본 발명은 원형 단면을 가지는 소재 파이프를 가열한 상태에서 성형홈을 구비하는 금형을 이용하여 가압하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 열간 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.In the present invention, the material pipe having a circular cross section is heated by using a mold having a forming groove in a heated state, hot-formed into a rectangular pipe having a rectangular cross section whose edges are rounded, And the length corresponds to the outer circumferential length of the work pipe.

열간 성형은 냉간 성형이 용이하지 않은 고강도 소재를 사용할 경우 적용될 수 있는 방법으로, 가열된 소재 파이프를 성형홈을 구비하는 금형으로 가열하는 방식을 사용하거나, 가열된 금형을 이용하여 소재를 성형하는 방식으로 할 수 있다.
Hot forming is a method that can be applied when using a high strength material that is not easy to cold form, either by heating the heated material pipe with a mold having a forming groove, or by using a method of molding a material using a heated mold .

그리고 본 발명은 원형 단면을 가지는 소재 파이프를 가열한 상태에서 성형홈을 구비하는 금형을 이용하여 가압하여 성형하며 급속냉각하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 핫스탬핑 성형하되, 상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하는 것을 특징으로 하는 각관 성형체 제조방법을 제공한다.According to the present invention, the material pipe having a circular cross section is hot pressed by using a mold having a forming groove in a heated state, rapidly cooled, hot-stamp-molded into a rectangular pipe having a rectangular cross- And the circumferential length of the inner circumferential surface of the molding groove corresponds to the circumferential length of the work pipe.

핫스탬핑 성형의 경우, 열간 성형 후 급속 냉각하여 소재의 형상 성형과 열처리를 일괄 수행할 수 있는 방법으로, 경화능을 가지는 소재를 사용할 경우 소재의 형상 성형과 함께 강도 향상의 효과를 얻을 수 있다. 경화능을 가지는 소재를 이용하여 핫스탬핑 성형하는 경우 상변태 온도(AC3) 이상의 온도에서 성형이 이루어지게 된다.In the case of hot stamping molding, rapid cooling after hot forming can perform batch molding of the shape and heat treatment of the material. When the material having hardenability is used, the effect of the shape shaping of the material and the strength improvement effect can be obtained. When hot stamping molding is performed using a material having hardenability, molding is performed at a temperature equal to or higher than the phase transformation temperature AC3.

도 5는 본 발명에 따른 원형 소재 파이프를 이용한 각관 성형체 제조방법에 사용되는 핫스탬핑 금형을 나타낸 단면도이다.5 is a cross-sectional view illustrating a hot stamping mold used in the method of manufacturing a square pipe using the circular work pipe according to the present invention.

핫스탬핑 성형을 하는 경우에는 도 5에 도시한 바와 같이, 금형(320, 340)에 냉매 유로(350)를 형성하여, 금형을 급속 냉각할 수 있도록 하는 것이 바람직하다.
In the case of hot stamping molding, it is preferable that the coolant passage 350 is formed in the molds 320 and 340 so that the mold can be rapidly cooled as shown in Fig.

첨부된 도면을 참조하여 본 발명의 실시예들을 설명하였으나, 본 발명은 상기 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 변형될 수 있으며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
While the present invention has been described with reference to exemplary embodiments, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. It is to be understood that the invention may be embodied in many other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.

100 : 소재 파이프
200 : 각관 성형체
320 : 상부금형
340 : 하부금형
325, 345 : 성형홈
d : 소재 파이프 직경
t : 두께
r : 곡률 반경
h : 높이
w : 폭100: Material pipe
200: Each tube formed body
320: Upper mold
340: Lower mold
325, 345: Molding groove
d: Material pipe diameter
t: Thickness
r: Curvature radius
h: Height
w: Width

Claims (12)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 원형 단면을 가지는 소재 파이프를 가열한 상태에서 성형홈을 구비하는 금형을 이용하여 가압하여 성형하며 급속냉각하여, 단면이 모서리가 라운드진 사각형 형상을 가지는 각관 성형체로 핫스탬핑 성형하되,
상기 성형홈의 내주면의 둘레 길이는 소재 파이프의 외주면 길이에 대응하도록 하고,
상기 성형홈의 높이는 상기 소재 파이프의 반지름의 50~200% 범위가 되도록 하고, 상기 성형홈의 폭은 상기 소재 파이프의 직경과 동일하게 하는 것을 특징으로 하는 각관 성형체 제조방법.
Hot-stamping the material pipe having a circular cross-section with a rectangular pipe having a rectangular cross-section with rounded corners,
The circumferential length of the inner circumferential surface of the forming groove corresponds to the length of the circumferential surface of the work pipe,
Wherein a height of the molding groove is in a range of 50 to 200% of a radius of the work pipe, and a width of the molding groove is equal to a diameter of the work pipe.
삭제delete 삭제delete 제 9 항에 있어서,
상기 성형홈의 모서리의 곡률 반경은
상기 소재 파이프 반지름의 40~100% 범위인 것을 특징으로 하는 각관 성형체 제조방법.
10. The method of claim 9,
The radius of curvature of the edge of the forming groove
Wherein the diameter of the material pipe is in the range of 40 to 100% of the radius of the material pipe.
KR1020120124789A 2012-11-06 2012-11-06 Manufacturing method of rectangular beam using pipe KR101470699B1 (en)