KR101437095B1 - Matt Colorless Coating Composite and Coating Method thereof - Google Patents
Matt Colorless Coating Composite and Coating Method thereof Download PDFInfo
- Publication number
- KR101437095B1 KR101437095B1 KR1020130013977A KR20130013977A KR101437095B1 KR 101437095 B1 KR101437095 B1 KR 101437095B1 KR 1020130013977 A KR1020130013977 A KR 1020130013977A KR 20130013977 A KR20130013977 A KR 20130013977A KR 101437095 B1 KR101437095 B1 KR 101437095B1
- Authority
- KR
- South Korea
- Prior art keywords
- coating
- resin
- coating composition
- coating layer
- resin mixture
- Prior art date
Abstract
무광 투명성을 갖는 코팅 조성물 및 이를 이용한 코팅방법이 개시된다. 본 발명에 따른 무광 투명성을 갖는 코팅 조성물은 폴리에스테르 계열 레진과 니트로셀룰로오스 레진이 혼입되어 형성된 레진혼합물; 레진혼합물에 혼합되는 희석제; 레진혼합물에 혼합되는 중화제;를 포함하는 것으로, 대상물의 표면에 특정 로고를 인쇄하는 1단계; 상기 코팅 조성물을 대상물의 표면에 도포하여 일정 두께의 코팅층을 형성하는 2단계; 2단계의 코팅층을 형성한 후 건조시켜 코팅층이 경화되도록 하는 3단계;를 포함하는 방법에 의해 코팅이 완료된다.
이에 따르면, 대상물의 외면에 인쇄된 로고가 지워지지 않고 오랫동안 안정적으로 보존될 수 있어 상품성이 향상될 수 있고, 또한 원래의 색상이 선명하게 오랜기간 유지할 수 있으며 외면의 스크래치와 같은 손상을 방지할 수 있어 상품성이 제고될 수 있는 효과가 있다.A coating composition having matte transparency and a coating method using the same are disclosed. A coating composition having matting transparency according to the present invention comprises a resin mixture formed by incorporating a polyester-based resin and a nitrocellulose resin; A diluent to be mixed with the resin mixture; A neutralizing agent to be mixed with the resin mixture, the method comprising: a first step of printing a specific logo on the surface of the object; A second step of coating the surface of the object with the coating composition to form a coating layer having a predetermined thickness; And a third step of forming a coating layer in two steps and then drying the coating layer so as to cure the coating.
According to this, the logo printed on the outer surface of the object is not erased and can be stably stored for a long time, so that the merchantability can be improved, the original color can be maintained for a long period of time and the damage such as scratch on the outer surface can be prevented There is an effect that the merchantability can be improved.
Description
본 발명은 무광 투명성을 갖는 코팅 조성물 및 이를 이용한 코팅방법에 관한 것으로, 더욱 상세하게는 이어컵과 같은 상품의 외면에 인쇄되는 로고와 같은 문양이 오랫동안 안정적으로 보존될 수 있도록 코팅되고, 선명한 색상과 외면 손상을 방지할 수 있어 상품성이 제고될 수 있도록 하는 무광 투명성을 갖는 코팅 조성물 이를 이용한 코팅방법에 관한 것이다. The present invention relates to a coating composition having a matte transparency and a coating method using the coating composition. More particularly, the present invention relates to a coating composition for a long period of time, such as a logo printed on an outer surface of a product such as an ear cup, A coating composition having matte transparency which can prevent damage to the outer surface and improve the merchantability.
일반적으로 헤드폰은 귀에 밀착되는 컵 형상의 이어컵과, 이어컵을 연결하며 머리를 감싸는 헤드밴드로 구성된다.Generally, the headphone is composed of a cup-shaped ear cup which comes into close contact with the ear, and a head band which connects the ear cup and surrounds the head.
통상 이어폰은 플라스틱 성형에 의해 제조되는데 플라스틱 성형제품은 내후성과 광택성 및 스크래치 방지 등의 목적으로 외면에 유색 또는 무색의 코팅층이 형성된다. Generally, earphones are manufactured by plastic molding. For plastic molding products, a colorless or colorless coating layer is formed on the outer surface for the purpose of weather resistance, gloss and scratch prevention.
이후 해당 상품의 상품명 또는 제조업체의 상호와 같은 로고가 인쇄된다. 통상의 인쇄방법인 실크 스크린이나 패드 프린트 방식에 의해 로고가 인쇄되는 것이다.Thereafter, a logo such as the name of the product or the name of the manufacturer is printed. The logo is printed by a silk screen or a pad printing method which is a normal printing method.
상술한 코팅층의 형성은 코팅제를 분사하여 상품의 표면에 일정한 두께로 코팅하는 것으로, 바람직하게는 내구성 코팅 필름 형성용 코팅제가 많이 사용되고 있는데, 가수분해성 오르가노실란을 가수분해 또는 부분 가수분해시킴으로써 수득되는 코팅제, 또는 코팅용 조성물에 콜로이드성 실리카를 혼합한 코팅제가 공지되어 있다.The coating layer is formed by spraying a coating agent onto the surface of a product to a predetermined thickness. Preferably, a coating agent for forming a durable coating film is used in many cases. The coating layer is preferably formed by hydrolyzing or partially hydrolyzing a hydrolysable organosilane A coating agent or a coating agent in which colloidal silica is mixed with a coating composition is known.
이에 관련된 선행기술로는 일본 특허 공개 공보 제51-2736호, 제51-2737호, 제53-130732호 및 제63-168470호에 알콕시기가 과량의 물에 의해 실란올로 전환되는 오르가노알콕시실란, 상기 오르가노알콕시실란의 가수분해물 및/또는 부분 축합물, 및 콜로이드성 실리카를 함유하는 코팅제가 개시된 바 있다.Prior art related to this are Japanese Patent Application Laid-Open Nos. 51-2736, 51-2737, 53-130732 and 63-168470, which disclose organoalkoxysilanes in which an alkoxy group is converted to silanol by an excess of water , A hydrolyzate and / or a partial condensate of the organoalkoxysilane, and a colloidal silica.
그러나, 상기 코팅제로 부터 수득되는 코팅필름은 이들의 높은 경도 및 양호한 내후성에 기인하여 기재 보호 용도에 매우 유용하나, 인성이 불충분하며, 필름 두께가 10μm 이상인 코팅 필름의 경우, 가열 경화 공정 동안에, 그리고 옥외 사용시나 급격한 온도변화 발생시에 손쉽게 균열이 발생한다. However, the coating films obtained from these coatings are very useful for substrate protection applications due to their high hardness and good weatherability, but they are insufficient in toughness, in the case of coating films having a film thickness of 10 m or more, during the heat- Cracks easily occur when using outdoors or when sudden temperature changes occur.
또한, 코팅 공정시, 코팅 필름의 두께를 10μm 이하로 엄격하게 조절하기가 어려우며, 특히 코팅 표면 또는 코팅 제품의 주변 또는 코팅 표면의 오목한 부분에서 필름 두께는 10μm를 초과함으로써, 제조 불량을 유발한다. Further, it is difficult to strictly control the thickness of the coating film to 10 m or less in the coating process, and in particular, the film thickness exceeds 10 m in the vicinity of the coating surface, the periphery of the coating product, or the concave portion of the coating surface.
따라서 목적하는 코팅 필름 특성을 수득하기 위해서, 상기 코팅제로부터 수득되는 코팅 필름은 약 100℃ 이상의 고온에서 또는 장시간 동안 열처리할 필요가 있으며, 따라서 상기 코팅제는 성형 방법이나 기재의 크기, 또는 내후성, 또는 옥외 및 기타 장소에 따라서, 몇몇 경우에는 편리하게 사용할 수 없다. Therefore, in order to obtain the desired coating film properties, the coating film obtained from the coating agent needs to be heat-treated at a high temperature of about 100 DEG C or higher for a long time, And in some places, it may not be convenient to use in some cases.
또한, 상기 코팅용 수지 조성물은 알콕시 실란의 가수분해로부터 산출되는 실란올의 반응성이 매우 높아, 실온에서도 이들의 축합 반응이 단계적으로 진행됨으로써, 겔화가 발생하며, 안정성이 불량해지는 결과를 초래하는 것으로 알려져 있다. In addition, the resin composition for coating has a very high reactivity of the silanol produced from the hydrolysis of the alkoxysilane, so that the condensation reaction progresses stepwise at room temperature, causing gelation, resulting in poor stability It is known.
특히, 도료의 전색제로서 안료를 첨가하여 상기 코팅용 조성물로부터 도료를 유도하는 경우, 상기 안정성은 또다시 저하되어, 상기 코팅용 수지 조성물이 도료로 형성될 수 없게 된다.Particularly, when a pigment is added as a vehicle coloring agent to induce a paint from the coating composition, the stability is lowered again, and the resin composition for coating can not be formed into a paint.
일본 특허 공개 공보 제64-168호에 개시된 바와 같이, 또한 코팅 공정 직전에 알콕시실란의 부분 가수분해물 또는 부분 축합물에 경화제로서 물과 촉매를 첨가함으로써 알콕시기가 실란올로 전환되는 코팅제가 제안되었다. As disclosed in Japanese Patent Application Laid-Open No. 64-168, a coating agent has also been proposed in which an alkoxy group is converted to silanol by adding water and a catalyst as a curing agent to a partial hydrolyzate or partial condensate of an alkoxysilane immediately before the coating process.
그러나, 상기 코팅제는 또한 인성이 불량하여, 10μm 이상의 필름 두께에서는 균열이 손쉽게 발생한다. 상기 코팅제는 저장성이 우수하고, 안료 첨가에 의해 도료로 형성시키는 경우에도 비교적 안정성을 유지하는 반면, 목적하는 코팅 필름 특성을 수득하기 위해서는, 상기 코팅제를 약 100℃ 이상의 고온에서 또는 장시간 동안 열처리하는 것이 필요하다. 따라서, 상기 코팅제는 성형 방법이나 기재의 크기, 또는 내후성, 또는 옥외 및 기타 장소에 따라서 사용될 수 없었다.However, the coatings also have poor toughness, and cracking easily occurs at film thicknesses of 10 탆 or more. The coating agent is excellent in storage stability and is relatively stable even when it is formed into a coating material by the addition of a pigment. In order to obtain a desired coating film property, the coating agent is heat-treated at a high temperature of about 100 ° C or more for a long time need. Therefore, the coating agent could not be used depending on the molding method, the size of the substrate, weather resistance, or outdoors and other places.
한편 종래 기술은 상품 표면에 코팅제를 코팅한 후 경화된 다음 로고가 인쇄되는데 장시간 사용하게 되면 대개 로고가 지워지거나 손상되므로 상품 외관이 훼손되고 광고 효과가 반감되는 문제점이 있었다. On the other hand, in the prior art, when a coating material is coated on a surface of a product, the logo is printed after being cured, and when the product is used for a long time, the logo is erased or damaged, thereby deteriorating the appearance of the product and reducing the advertising effect.
본 발명은 상기한 종래 기술의 문제점을 해소하기 위해 안출된 것으로, 플라스틱 성형품, 특히 이어컵의 외면에 인쇄되는 로고와 같은 문양이 오랫동안 안정적으로 보존될 수 있도록 그 표면에 코팅되고, 아울러 상품 본연의 색상을 선명하게 오랜기간 유지할 수 있으며 외면의 스크래치와 같은 손상을 방지할 수 있어 상품성이 제고될 수 있도록 하는 무광 투명성을 갖는 코팅 조성물 및 이를 이용한 코팅방법을 제공하는데 그 목적이 있다.Disclosure of the Invention The present invention has been conceived in order to solve the problems of the prior art described above, and it is an object of the present invention to provide a plastic molded article, especially a logo printed on the outer surface of an ear cup, coated on the surface thereof so as to be stably stored for a long time, The present invention provides a coating composition having matte transparency that can maintain color sharply for a long period of time and can prevent damage such as scratches on the outer surface, thereby enhancing the merchantability, and a coating method using the coating composition.
상기한 본 발명의 목적은, 폴리에스테르 계열 레진과 니트로셀룰로오스 레진이 혼입되어 형성된 레진혼합물; 상기 레진혼합물에 혼합되는 희석제; 상기 레진혼합물에 혼합되는 중화제;를 포함하는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물에 의해 달성될 수 있다.It is an object of the present invention to provide a resin mixture formed by mixing a polyester-based resin and a nitrocellulose resin; A diluent to be mixed with the resin mixture; And a neutralizing agent to be mixed with the resin mixture.
상기 코팅 조성물 100 중량부에 대해 레진혼합물은 3~6 중량부, 희석제는 0.5~2 중량부, 중화제는 0.4~0.6 중량부가 혼합되는 것을 특징으로 한다. 3 to 6 parts by weight of a resin mixture, 0.5 to 2 parts by weight of a diluent, and 0.4 to 0.6 parts by weight of a neutralizing agent are mixed with 100 parts by weight of the coating composition.
상기 레진혼합물은 폴리에스테트 폴리올 레진, 니트로셀룰로오스 레진으로 이루어진 수지와; 히드로카본, 아세테이트, 케톤으로 이루어진 용제와; 카본 블랙, 화이트, 오가닉 블루, 오가닉 옐로우, 실리카로 이루어진 안료와; 왁스와 아크릴로 이루어진 첨가제;를 포함하는 것을 특징으로 한다. Wherein the resin mixture comprises a resin comprising a polyester polyol resin and a nitrocellulose resin; A solvent consisting of hydrocarbons, acetates, and ketones; A pigment made of carbon black, white, organic blue, organic yellow, silica; And an additive composed of wax and acrylic.
상기 희석제는 케톤 타입 용제인 것을 특징으로 한다. The diluent is a ketone type solvent.
상기 중화제는 폴리이소시아네이트 레진 20~30wt%, 히드로카본 타입 용제 35~45wt%, 아세테이트 타입 용제 25~35wt%가 혼합된 것을 특징으로 한다. The neutralizer is a mixture of 20 to 30 wt% of a polyisocyanate resin, 35 to 45 wt% of a hydrocarbon type solvent, and 25 to 35 wt% of an acetate type solvent.
한편 상기한 코팅 조성물을 이어컵과 같은 대상물에 코팅하는 방법에 있어서, 상기 대상물의 표면에 특정 로고를 인쇄하는 1단계; 폴리에스테르 계열 레진과 니트로셀룰로오스 레진이 혼입되어 형성된 레진혼합물과, 희석제 및 중화제로 구성된 코팅 조성물을 대상물의 표면에 스프레이 방식으로 도포하여 일정 두께의 코팅층을 형성하는 2단계; 상기 2단계의 코팅층을 형성한 후 건조실에서 가열 건조 또는 자연 건조시켜 코팅층이 경화되도록 하는 3단계;를 포함하는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물을 이용한 코팅방법에 의해 달성될 수 있다.Meanwhile, a method of coating a coating composition on an object such as a ear cup may include a first step of printing a specific logo on the surface of the object; A second step of applying a coating composition composed of a resin mixture formed by mixing polyester resin and nitrocellulose resin with a coating composition composed of a diluent and a neutralizing agent to the surface of the object by spraying to form a coating layer having a predetermined thickness; And a third step of curing the coating layer by heating or drying in a drying chamber after forming the coating layer in the second step.
상기 3단계의 가열 건조는 70~80℃에서 20~40분간 건조시키는 것을 특징으로 한다. The three-step heat drying is characterized by drying at 70 to 80 ° C for 20 to 40 minutes.
상기 자연 건조는 상온에서 방치하여 건조시키는 것을 특징으로 한다. The natural drying is characterized in that it is allowed to stand at room temperature for drying.
본 발명에 따르면, 대상물인 이어컵의 외면에 인쇄된 로고가 지워지지 않고 오랫동안 안정적으로 보존될 수 있어 상품성이 향상될 수 있고, 또한 원래의 색상이 선명하게 오랜기간 유지할 수 있으며 외면의 스크래치와 같은 손상을 방지할 수 있어 상품성이 제고될 수 있는 효과가 있다.According to the present invention, the logo printed on the outer surface of the ear cup, which is the object, can be stably stored for a long time without being erased, so that the merchandise can be improved. Also, the original color can be maintained for a long time, It is possible to improve the commerciality.
도 1은 본 발명에 따른 무광 투명성을 갖는 코팅 조성물을 이용한 코팅 공정을 나타낸 흐름도,
도 2는 본 발명에 따른 무광 투명성을 갖는 코팅 조성물이 코팅된 이어컵의 일 예를 나타낸 사시도.1 is a flow chart showing a coating process using a coating composition having matte transparency according to the present invention,
2 is a perspective view showing an example of an ear cup coated with a coating composition having matte transparency according to the present invention.
이하 본 발명의 바람직한 실시예를 첨부된 도면을 토대로 상세하게 설명하면 다음과 같다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
첨부된 도면 중에서, 도 1은 본 발명에 따른 무광 투명성을 갖는 코팅 조성물을 이용한 코팅 공정을 나타낸 흐름도, 도 2는 본 발명에 따른 무광 투명성을 갖는 코팅 조성물이 코팅된 이어컵의 일 예를 나타낸 사시도이다.
2 is a perspective view showing an example of an ear cup coated with a coating composition having a matte transparency according to the present invention; to be.
본 발명의 일 실시예에 따른 무광 투명성을 갖는 코팅 조성물은, 폴리에스테르 계열 레진과 니트로셀룰로오스 레진이 혼입되어 형성된 레진혼합물; 상기 레진혼합물에 혼합되는 희석제; 상기 레진혼합물에 혼합되는 중화제;를 혼합하여 이루어진다.A coating composition having a matte transparency according to an embodiment of the present invention includes a resin mixture formed by mixing a polyester-based resin and a nitrocellulose resin; A diluent to be mixed with the resin mixture; And a neutralizing agent to be mixed with the resin mixture.
바람직하게는 상기 코팅 조성물 100 중량부에 대해 레진혼합물은 3~6 중량부, 희석제는 0.5~2 중량부, 중화제는 0.4~0.6 중량부가 혼합된다.Preferably, 3 to 6 parts by weight of the resin mixture, 0.5 to 2 parts by weight of the diluent, and 0.4 to 0.6 parts by weight of the neutralizing agent are mixed with respect to 100 parts by weight of the coating composition.
레진혼합물은 폴리에스테트 폴리올 레진, 니트로셀룰로오스 레진으로 이루어진 수지와; 히드로카본, 아세테이트, 케톤으로 이루어진 용제와; 카본 블랙, 화이트, 오가닉 블루, 오가닉 옐로우, 실리카로 이루어진 안료; 왁스와 아크릴로 이루어진 첨가제;가 혼합되어 이루어진다. The resin mixture comprises a resin composed of polyester polyol resin and nitrocellulose resin; A solvent consisting of hydrocarbons, acetates, and ketones; Pigments made of carbon black, white, organic blue, organic yellow, silica; And an additive consisting of wax and acrylic.
수지는 폴리에스테르 폴리올 레진 30~31 wt%, 니트로셀룰로오스 레진 3~4wt%가 혼합되어 이루어진다.The resin is composed of 30 to 31 wt% of a polyester polyol resin and 3 to 4 wt% of a nitrocellulose resin.
용제는 히드로카본 21~22wt%, 아세테이트 19~20wt%, 케톤 7~8wt%가 혼합되어 이루어진다.The solvent is composed of 21 to 22 wt% of hydrocarbons, 19 to 20 wt% of acetate, and 7 to 8 wt% of ketone.
안료는 카본 블랙 2~3wt%, 화이트 1~2wt%, 오가닉 블루1~2wt%, 오가닉 옐로우 0.08~0.12wt%, 실리카 0.4~0.6wt%가 혼합되어 이루어진다.The pigment is composed of 2 to 3 wt% of carbon black, 1 to 2 wt% of white, 1 to 2 wt% of organic blue, 0.08 to 0.12 wt% of organic yellow, and 0.4 to 0.6 wt% of silica.
첨가제는 왁스 1.3~1.5wt%와 아크릴 2~3wt%가 혼합되어 이루어진다.The additive is composed of 1.3 to 1.5 wt% of wax and 2 to 3 wt% of acrylic.
한편 희석제는 케톤 타입 용제이며, 통상 '시너'로 일컬어진다. On the other hand, the diluent is a ketone type solvent and is generally referred to as a " thinner ".
중화제는 폴리이소시아네이트 레진 20~30wt%, 히드로카본 타입 용제 35~45wt%, 아세테이트 타입 용제 25~35wt%가 혼합되어 이루어진다. The neutralizing agent is composed of 20 to 30 wt% of a polyisocyanate resin, 35 to 45 wt% of a hydrocarbon type solvent, and 25 to 35 wt% of an acetate type solvent.
상술한 코팅 조성물을 이어컵과 같은 대상물에 코팅하는 방법을 설명하면 다음과 같다.A method of coating the above-mentioned coating composition on an object such as a ear cup will be described as follows.
도 1 및 도 2에 도시된 바와 같이, 본 발명에 따른 무광 투명성을 갖는 코팅 조성물을 이용한 코팅방법은, 대상물(100), 즉 이어컵의 표면에 특정 로고(200)를 인쇄하는 1단계(S1); 폴리에스테르 계열 레진과 니트로셀룰로오스 레진이 혼입되어 형성된 레진혼합물과, 희석제 및 중화제로 구성된 코팅 조성물을 대상물(100)의 표면에 스프레이 방식으로 도포하여 일정 두께의 코팅층(300)을 형성하는 2단계(S2); 상기 2단계(S2)의 코팅층(300)을 형성한 후 건조실에서 가열 건조 또는 자연 건조시켜 코팅층(300)이 경화되도록 하는 3단계(S3);를 포함한다.1 and 2, a coating method using a coating composition having a matte transparency according to the present invention includes a first step S1 for printing a
상기 1단계(S1)는 대상물(100)의 표면에 다양한 색상이나 문양으로 이루어진 로고(200)를 인쇄하는 것으로, 실크 프린트 또는 패드 프린트 기법을 이용하여 인쇄시킨다. In the first step S1, the
로고(200)를 인쇄한 후 10~15분간 상온에 방치하여 인쇄된 로고(200)가 충분히 건조되도록 한 후 상기 2단계(S2)의 코팅층(300)을 형성한다.After the
즉 무광 투명인 코팅 조성물을 분무기를 통해 스프레이 방식으로 분사하여 대상물(100)의 표면 코팅시키되 1회에 일정 두께로 코팅시키거나 또는 수회에 걸쳐 코팅을 반복함으로써 일정 두께의 코팅층(300)이 형성되도록 한다. That is, the coating composition that is non-transparent and transparent is sprayed through a sprayer to form a
이렇게 코팅 조성물이 코팅된 이후에는 건조실에서 가열 건조 또는 자연 건조시킨다.After the coating composition is coated, it is heated or dried naturally in a drying chamber.
가열건조의 경우 건조실 내의 온도를 약 70~80℃로 유지한 채 20~40분간 건조시키게 된다. In the case of heating and drying, the temperature in the drying chamber is maintained at about 70 to 80 ° C., and the drying is performed for 20 to 40 minutes.
물론 자연 건조는 상온에서 방치하여 건조시키는 것이다.
Of course, natural drying is to leave the room at room temperature to dry.
따라서 도 2에 도시된 바와 같이, 대상물(100)인 이어컵의 외면에 로고(200)가 인쇄된 후 그 외면에 코팅층(300)이 형성됨으로써 로고(200)가 외부로 노출되지 않게 되어 오랫동안 안정적으로 보존될 수 있어 상품성이 향상될 수 있다.Accordingly, as shown in FIG. 2, after the
또한 코팅층(300)으로 인해 이어컵의 원래의 색상이 선명하게 오랜기간 유지할 수 있으며 외면의 스크래치와 같은 손상을 방지할 수 있어 상품성이 제고될 수 있다.
Also, the
비록 본 발명이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정 및 변형이 가능한 것은 당업자라면 용이하게 인식할 수 있을 것이며, 이러한 변경 및 수정은 모두 첨부된 청구의 범위에 속함은 자명하다.Although the present invention has been described in connection with the above-mentioned preferred embodiments, it will be apparent to those skilled in the art that various modifications and variations can be made without departing from the spirit and scope of the invention, It is obvious that the claims fall within the scope of the claims.
100 : 대상물 200 : 로고
300 : 코팅층 S1 : 1단계
S2 ; 2단계 S3 : 3단계100: Object 200: Logo
300: Coating layer S1: Step 1
S2; Step 2:
Claims (6)
상기 레진혼합물에 케톤 타입 용제인 희석제가 혼합되고;
상기 레진혼합물에 중화제가 혼합되며,
상기 중화제는
폴리이소시아네이트 레진 20~30wt%, 히드로카본 타입 용제 35~45wt%, 아세테이트 타입 용제 25~35wt%가 혼합된 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물.A resin mixture formed by mixing a polyester-based resin and a nitrocellulose resin;
A diluent which is a ketone type solvent is mixed with the resin mixture;
A neutralizing agent is mixed with the resin mixture,
The neutralizing agent
20 to 30 wt% of a polyisocyanate resin, 35 to 45 wt% of a hydrocarbon type solvent, and 25 to 35 wt% of an acetate type solvent are mixed.
상기 코팅 조성물 100 중량부에 대해 레진혼합물은 3~6 중량부, 희석제는 0.5~2 중량부, 중화제는 0.4~0.6 중량부가 혼합되는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물.The method according to claim 1,
Wherein the resin mixture comprises 3 to 6 parts by weight, the diluent is 0.5 to 2 parts by weight, and the neutralizer is 0.4 to 0.6 parts by weight based on 100 parts by weight of the coating composition.
상기 레진혼합물은
폴리에스테르 폴리올 레진 30~31 wt%, 니트로셀룰로오스 레진 3~4wt%로 이루어진 수지와,
히드로카본 21~22wt%, 아세테이트 19~20wt%, 케톤 7~8wt%로 이루어진 용제와,
카본 블랙 2~3wt%, 화이트 1~2wt%, 오가닉 블루1~2wt%, 오가닉 옐로우 0.08~0.12wt%, 실리카 0.4~0.6wt%로 이루어진 안료와,
왁스 1.3~1.5wt%와 아크릴 2~3wt%로 이루어진 첨가제;
를 포함하는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물.The method according to claim 1,
The resin mixture
30 to 31 wt% of a polyester polyol resin, and 3 to 4 wt% of a nitrocellulose resin,
A solvent composed of 21 to 22 wt% of hydrocarbons, 19 to 20 wt% of acetate and 7 to 8 wt% of ketone,
A pigment comprising 2 to 3 wt% of carbon black, 1 to 2 wt% of white, 1 to 2 wt% of organic blue, 0.08 to 0.12 wt% of organic yellow, and 0.4 to 0.6 wt%
An additive comprising 1.3 to 1.5 wt% of wax and 2 to 3 wt% of acrylic;
≪ / RTI > wherein the coating composition has a matte transparency.
상기 대상물의 표면에 특정 로고를 인쇄하는 1단계;
상기 코팅 조성물을 대상물의 표면에 스프레이 방식으로 도포하여 일정 두께의 코팅층을 형성하는 2단계;
상기 2단계의 코팅층을 형성한 후 건조실에서 가열 건조 또는 자연 건조시켜 코팅층이 경화되도록 하는 3단계;
를 포함하는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물을 이용한 코팅방법.A method for coating a coating composition according to any one of claims 1 to 3 on a subject,
A first step of printing a specific logo on the surface of the object;
A second step of applying the coating composition to the surface of the object by spraying to form a coating layer having a predetermined thickness;
Forming a coating layer in the second step and drying the coating layer in a drying chamber or drying the coating layer in a drying chamber to cure the coating layer;
≪ / RTI > wherein the coating composition has a matte transparency.
상기 3단계의 가열 건조는 70~80℃에서 20~40분간 건조시키는 것을 특징으로 하는 무광 투명성을 갖는 코팅 조성물을 이용한 코팅방법.6. The method of claim 5,
Wherein the three-step thermal drying is performed at 70 to 80 ° C for 20 to 40 minutes.