KR101426471B1 - A manufacturing method of natural acidic fiber jelly sponge for washing and natural acidic fiber jelly sponge manufactured by the same method - Google Patents
A manufacturing method of natural acidic fiber jelly sponge for washing and natural acidic fiber jelly sponge manufactured by the same method Download PDFInfo
- Publication number
- KR101426471B1 KR101426471B1 KR1020130080841A KR20130080841A KR101426471B1 KR 101426471 B1 KR101426471 B1 KR 101426471B1 KR 1020130080841 A KR1020130080841 A KR 1020130080841A KR 20130080841 A KR20130080841 A KR 20130080841A KR 101426471 B1 KR101426471 B1 KR 101426471B1
- Authority
- KR
- South Korea
- Prior art keywords
- sponge
- skin
- washing
- acid
- fiber
- Prior art date
Abstract
Description
본 발명은 세안 및 목욕에 사용되는 약산성 천연 식이섬유 젤리 스폰지 및 그 제조 방법에 관한 것이다.
The present invention relates to a weakly acidic natural fiber jelly sponge used for cleansing and bathing, and a method for producing the same.
식이섬유는 다당류와 다당류 유도체의 난소화성 고분자 물질로 보수성, 용해성, 점질성, 겔화, 양이온 교환성, 흡착성 등의 특성이 있다. 즉 식이섬유는 우리 몸 속에서 물을 흡수하여 체적 증가 및 팽윤하여 겔화하면 3차원적 그물구조를 취하여 용매에 녹지 않게 되어 장을 통과하면서 “배변활동”을 촉진하고, 유분을 흡수하여 “콜레스테롤 조절”하며, 독성물질, 노폐물, 불순물을 흡착, 배출하여 “식후혈당상승억제”에 도움을 주게 된다.
Dietary fiber is an indigestible polymer substance of polysaccharides and polysaccharide derivatives and has properties such as water retention, solubility, viscosity, gelation, cation exchange ability, and adsorption. In other words, dietary fiber absorbs water in our body, increases volume and swells to gel, and when it becomes gelled, it takes a three-dimensional net structure and dissolves in solvent so that it passes through the bowel, promotes "bowel movement", absorbs oil, "And absorbs and releases toxic substances, wastes, and impurities, thereby helping to" suppress postprandial rise in blood glucose. "
본 발명은 이러한 기능을 피부에도 동일한 작용을 할 수 있도록 겔화된 식이섬유를 비가역적 가열반응 및 냉동/해동 과정을 통하여 스폰지화 하여 물을 흡수하였을 경우 젤리처럼 투명하고 촉촉하고 부드러운 3차원 그물구조를 갖게 되어 피부에 자극을 주지 않는 젤리 스폰지를 제조하고, 다시 젤리 스폰지가 약산성을 갖게 함으로써 세안과 목욕 시 약산성인 인체의 피부보호막은 보호하고, 피부에 수분은 보충하면서 유분, 피지는 흡착하고 불순물, 노폐물 등은 효율적으로 제거할 수 있는 약산성 식이섬유 젤리 스폰지 및 그 제조 방법에 관한 것이다.
In the present invention, when the gelled dietary fiber is spongeed through irreversible heating reaction and freezing / thawing process to absorb the water to achieve the same function to the skin, the present invention provides a transparent, moist and smooth three-dimensional net structure It protects the skin protection membrane of the human body which is weak acidic in the cleansing and bathing by making the jelly sponge which does not irritate the skin by making it have weak acidity again, and the moisture and the oil are supplemented while the oil and sebum are adsorbed, The present invention relates to a weakly acidic fiber-type jelly sponge capable of efficiently removing wastes and the like and a method for producing the same.
일반적으로 세안 및 목욕이란 얼굴을 포함한 피부를 깨끗이 하기 위하여 피부 표면의 노폐물, 땀, 피지, 먼지, 화장품 등을 제거함으로써 피부를 청결히 하는 것으로 피부 관리에서 가장 중요한 기본 단계이다.In general, cleansing and bathing is the most important basic step in skin care by cleansing the skin by removing waste products, sweat, sebum, dust, cosmetics, etc. to clean the skin including the face.
그러나, 화장이나 자외선 크림을 바르고 낮 동안 열심히 활동한 이후에 피부 곳곳을 모공 속까지 딥클렌징 해주지 않으면 화장찌꺼기와 낮 동안 활동으로 쌓인 먼지, 대기오염, 땀, 각질, 피지는 물론 세정제 찌꺼기까지 어우러져, 피부에 흡수되거나 자체적으로 서서히 분해 혹은 산화되어 피부자극을 일으키며, 피부의 산화와 과산화지질을 형성하여 피부 노화를 재촉하게 된다. 또한, 노화되고 막힌 모공은 제대로 된 영양을 공급하여도 효율적인 흡수가 이루어지지 않아 아무리 좋고 값비싼 화장품, 영양성분을 공급해 준다고 하여도 그 효능을 제대로 전달하지 못하게 된다. 또, 어떤 경우에는 세균, 박테리아, 모낭충 등이 번식할 수 있는 환경을 제공하게 되어 또 다른 피부 트러블의 원인이 되기도 한다.
However, if you apply makeup or UV cream and work hard during the day and do not deep cleanse the skin to the inside of your pores, cosmetic dirt, dust, air pollution, sweat, keratin, sebum, It is absorbed by the skin or it gradually decomposes or oxidizes itself, causing skin irritation, and oxidizing and lipid peroxidation of the skin to promote skin aging. In addition, the aged and clogged pores do not absorb efficiently even if they supply proper nutrition, and even if they provide good and expensive cosmetics and nutrients, they can not deliver the efficacy properly. In addition, in some cases, bacteria, bacteria, fungus and the like can reproduce the environment provides another cause of skin trouble.
따라서 평소에 세안이나 목욕을 제대로 하는 것은 거듭 강조하여도 지나치지 않는 건강하고 아름다운 피부를 유지하기 위한 모든 피부 관리의 시작이라고 할 수 있다.Therefore, proper skin cleansing and bathing is usually the beginning of all skin care to maintain healthy and beautiful skin that is not overstated.
평소 올바로 세안이나 목욕을 한다는 것은, 첫째, 피부에 자극을 주지 않아야 하고, 둘째, 피부 구석구석 깨끗하게 세정이 이루어져야 하며, 셋째, 피부보호막을 보호하고 피부 유수분(pH도) 밸런스를 유지할 수 있어야 하고, 마지막으로 넷째, 생활 속에서 날마다 하기 쉽고 간편해야 한다는 것이다.In general, proper washing or bathing should be done firstly, not to irritate the skin, secondly, cleanly cleaned every corner of the skin, thirdly, to protect the skin barrier and maintain the balance of the skin's pH (pH) Fourth, the last thing is to be easy and simple every day in life.
대부분의 사람들의 경우, 손에 세정제를 묻혀서 거품을 내서 세안이나 목욕을 하는 것을 선호하는 데, 그 이유는 손을 대신해서 피부에 자극을 주지 않고 세안이나 목욕을 할 수 있는 도구가 없다는 것과 손으로 하는 것이 간단하고 쉽다는 것을 들 수 있다. For most people, they prefer to wash their hands with a cleanser to bubble or bathe, because there is no tool to clean or bathe without irritating the skin, It is simple and easy to do.
하지만 손에 세정제를 묻혀서 거품을 내서 세안이나 목욕을 하는 것은 마치 양치질을 손으로 하거나 설거지를 손으로 하는 것과 같아서 세정 효과가 떨어질 것은 불을 보듯 명확하다고 할 수 있다.
However, it is obvious that the effect of washing is low because it is like hand washing or brushing dishes by hand or putting a cleanser in the hand and bubbling and washing or bathing.
따라서, 양치질을 할 때 손대신 칫솔을 사용하고 설거지를 할 때 손대신 스폰지를 사용하는 것과 같이 세안이나 목욕을 할 때, 세정효과를 높일 수 있도록 손대신 사용할 수 있으며 손보다 더 피부에 자극이 없고 날마다 사용하기에 쉽고 간편한 세정도구의 개발이 절실하다고 하겠다.Therefore, you can use your toothbrush instead of your hand when brushing your teeth, use a sponge instead of your hand to wash your dishes, and use it instead of your hands to increase your cleansing effect when washing or bathing. It is urgent to develop cleaning tools that are easy to use and easy to use every day.
이러한 세정도구의 조건을 보면, 첫째, 풍부한 거품에 의한 세정 능력이 우수해야 하고 생활 속에서 날마다 사용하기 쉽고 간편해야 하므로 이미 익숙한 스폰지 형태를 갖는 것이 바람직하다. 둘째, 피부에 자극이 없고 인체에 해가 없는 친환경 천연제품이어야 한다. 세안이나 목욕 시 몸에 자극이 되고 해로울 수 있는 합성스폰지를 사용하는 것은 오히려 피부 건강을 해치는 것이니 반드시 친환경 천연제품을 사용해야 하며 생태계를 파괴할 수 있는 동물성 제품보다는 쉽게 재배 가능한 식물성 제품이 바람직하다고 할 수 있다. 셋째, 손보다 더 피부에 자극이 없기 위해서는 물리적으로 손보다 더 부드러워야 하는 것은 물론이고 화학적으로도 약산성인 피부보호막을 손상시키지 않도록 약산성인 세정스폰지가 필요한 것은 당연하다고 하겠다. 넷째, 건강한 피부를 위해서는 세안이나 목욕 후에 피부의 유수분(pH도) 밸런스가 유지되어야 하기 때문에 그러한 기능을 가지고 있는 천연 식이섬유 즉 젤리 성상의 세정스폰지가 바람직하다. 특히, 신생아, 영유아, 아토피, 여드름 등 민감피부의 경우, 정상적인 성인의 피부 pH도 범위인 pH4.5~6의 범위를 벗어나 더 알칼리화되어 있어서 알칼리성 세정제의 사용은 피부 건강을 더 악화시키기 때문에 세정제를 사용하지 않고 물만으로 세안이나 목욕을 해야 하며, 정상적인 성인이라 할지라도 알칼리성 세정제를 사용한 세안이나 목욕 후에는 피부 pH도가 급격하게 알칼리화하기 때문에 남은 세정제 찌꺼기를 제거하고 피부 유수분 균형을 유지하기 위해서 물만으로 정리세안을 해주는 것이 좋다. 이와 같이 물과 세정스폰지 만을 사용해서 세안이나 목욕을 해야하는 상황과 욕구가 증가하고 있다. 이때 피부에 수분은 보충하고 여분의 유분(피지, 기름기)은 흡착하고 불순물이나 노폐물은 원할하게 제거할 수 있는 천연 식이섬유(젤리)의 특성을 갖춘 세정스폰지라면 더욱 바람직할 것이다. The condition of such a cleaning tool is as follows: First, it should be excellent in cleaning ability by abundant foam, easy to use every day in daily life, and therefore it is preferable to have a sponge shape that is already familiar. Second, it should be an eco-friendly natural product that has no skin irritation and no harm to human body. Using a synthetic sponge that is irritating and harmful to the body when cleansing or bathing can cause harm to your skin health. You should use eco-friendly natural products, and you can say that it is preferable to plant products that can be grown easily rather than animal products that can destroy ecosystems. have. Third, in order not to stimulate the skin more than the hand, it is natural that it is necessary to have a weakly acidic washing sponge so as not to be physically softer than the hand and also to chemically weakly protect the skin protective film. Fourth, healthy skin is required to maintain the balance of the skin's pH (pH) after cleansing or bathing. Therefore, a natural fiber such as a jelly-like cleansing sponge having such a function is preferable. Especially, for sensitive skin such as newborn, infant, atopic, acne, etc., the alkaline detergent is more alkaline than the normal pH range of the adult skin pH 4.5 to 6. Therefore, the use of the alkaline detergent deteriorates the skin health. It is necessary to wash or bath with water without using it. Even normal adult will alkalize the pH of the skin after cleansing or bathing with alkaline detergent. Therefore, it is necessary to remove the remaining detergent residue, It is good to wash. In this way, the situation and desire to wash or bathe using only water and a cleaning sponge are increasing. It would be even more desirable if the cleaning sponge had the characteristics of natural dietary fiber (jelly) which can replenish moisture to the skin and adsorb excess oil (sebum, grease) and remove impurities and waste materials.
따라서 이러한 조건들을 모두 충족시키기 위해서는, 보수성, 용해성, 점질성, 겔화,양이온 교환성, 흡착성 등의 특성이 있는 식이섬유 가운데 한가지 혹은 혼합물을 원료로 하는 약산성 천연 식이섬유 젤리 스폰지의 개발이 절실하게 되는 것이다.
Therefore, in order to meet all of these conditions, it is necessary to develop a weakly acidic natural fiber jelly sponge made of one or a mixture of dietary fibers having properties such as water retention, solubility, viscosity, gelation, cation exchangeability and adsorption property will be.
종래의 세정스폰지들이 시판되고 있으나 세안, 목욕용으로서 꼭 갖춰야 할 위와 같은 조건들 가운데 기본적인 일부만 갖추고 있어서 올바른 세안, 목욕이 불가능하다. 예를 들어 합성스폰지들은 거품은 잘 나지만 피부에 자극이 있고 약산성이 아니며 박테리아나 곰팡이 방지를 위하여 보통 트라이클로산과 같은 화학 살균성분이 투입되어 있다. 거품은 잘 나지만 세정제 없이 사용하면 피부에 자극이 있고 약산성도 아닌 천연 펄프도 있고, 거품은 잘나고 부드럽지만 세정제 없이 사용하면 피부에 자극이 있고 약산성도 아니며 과도한 채취로 바다 생태계 파괴가 우려되는 동물성 천연 해면도 있으며, 거품은 잘나고 부드럽고 피부에 물리적인 자극은 적으나 화학적으로 자극이 되는 약알칼리 특성을 가진 곤약스폰지 등도 있다. Conventional cleaning sponges are on the market, but they are only part of the basic requirements for cleansing and bathing, so proper cleansing and bathing are impossible. Synthetic sponges, for example, are well foamed but have a stimulant to the skin and are not mildly acidic and usually contain chemical sterilizing agents such as triacic acid to prevent bacteria and fungi. If you use it without a detergent, there is irritation to your skin. There is also a natural pulp that is not weak acid. It is soft and bubble smooth. But if you use it without detergent, it will irritate your skin and it will not be acidic. There are also sponges, bubbles are fine and soft, and there are few physical irritants to the skin, but there are also konjac sponges with weakly alkaline properties that are chemically stimulating.
피부가 정상범위 pH4.5~6인 경우에는 피부투과장벽이 유지되어 외부로부터 피부를 보호하고 피부의 결합력과 응집력이 유지되어 탄력이 있고 세균, 박테리아, 모낭충 등에 대한 항균력이 있어서 건강한 피부 상태를 유지한다. 그러나 알칼리화되면 알레르기 반응이 증가하거나 유독물질이 피부에 더 많이 유입되거나 각종 감염질환이 증가하게 되고 피부의 수분 보유능력은 떨어지고 표피는 두꺼워지는 등 아토피, 여드름, 뾰루지, 트러블, 건성, 각질, 민감피부 등이 되게 된다. 반대로 산성화하여 pH가 3.7~4.5 사이가 되면 피부단백질인 케라틴이 응고되면서 피부가 푸석푸석하고 탄력을 잃게 된다. 또한 피부 분비선의 활동이 어렵게 되며 피부세포의 대사활동에 장애를 받게 된다.When the skin is in the normal range pH 4.5 to 6, the skin permeation barrier is maintained and protects the skin from the outside. The skin's cohesion and cohesion are maintained, and it has elasticity. It has antibacterial power against bacteria, bacteria, do. However, when it is alkalized, allergic reactions are increased, toxic substances are more infiltrated into the skin, various infectious diseases are increased, the ability of the skin to retain moisture is lowered, and the epidermis becomes thicker. Atopic, acne, rash, trouble, dryness, And so on. Conversely, when the pH is between 3.7 and 4.5, the skin protein keratin is clotted and the skin becomes crumbly and loses its elasticity. In addition, the activity of the skin glands is difficult and the skin cells are subject to the metabolic activity.
따라서 현대인의 건강한 아름다운 피부에 대한 열망과 약산성에 대한 요구는 날로 증가하고 있어서 화장품, 자외선차단제는 물론 물비누, 심지어 고체비누 조차 세정력의 핵심인 알칼리성을 포기한 약산성 고체비누가 인기를 끌고 있는 추세이다. 하물며 세정제와 함께 풍성한 거품을 내야 할 세정스폰지가 약산성이어야 하는 것은 너무도 당연한 결과이고, 신생아/영유아 목욕, 아토피, 여드름, 민감피부 세안/목욕 등과 정상인의 아침 세안, 정리세안 등 세정제를 사용하지 않고 세안이나 목욕을 해야하는 경우와 상황이 더욱 많아지는 추세에서 세안과 목욕을 도와주는 유일한 도구인 약산성이면서 식이섬유 젤리 성상의 세정스폰지는 반드시 필요한 발명이라고 할 수 있다.As a result, the desire for healthy and beautiful skin and the need for weak acidity are increasing day by day, so weak acidic solid soap which is abandoning alkalinity which is the core of washing power, such as cosmetics, sunscreen, water soap, and even solid soap, is becoming popular. It is a very natural result that the cleaning sponge that should give a lot of foam with the cleaning agent is weak acid, and it is a natural result that the cleaning sponge of the newborn / infant bath, atopy, acne, sensitive skin cleansing / bath, normal morning cleaning, And the need to take a bath, and in a situation where the situation is getting more and more, a cleaning sponge of a weak acidity and a dietary fiber jelly form, which is the only tool that helps wash and bathe, is a necessary invention.
본 발명은 이러한 시대적 추세와 욕구를 반영하여 세계 최초로 탄생한 인체에 해가 없는 약산성 식이섬유 젤리 스폰지 및 제조공정에 대한 것이다.
The present invention relates to a weakly acidic fiber jelly sponge and its manufacturing process which are the first in the world to reflect the trend and desire of the times.
본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명에서 해결하고자 하는 과제는 약산성 식이섬유를 선택해서 친환경 공정을 통하여, 탁월한 세정효과를 보장하고 동시에 세정제 없이 물만으로 세안이나 목욕하는 경우에도 피부자극은 최소화하고 수분은 보충하고 유분은 흡착하고 불순물, 노폐물은 제거할 수 있도록 젤리처럼 투명하고 촉촉하고 부드러운 3차원 그물구조를 갖춘 스폰지를 만들고, 조직 자체가 피부층의 산성도와 동일한 약산성을 갖도록 만드는, 세안 및 목욕용 약산성 식이섬유 젤리 스폰지의 제조 방법 및 이로부터 제조되는 약산성 식이섬유 젤리 스폰지를 제공하고자 하는 것이다.
DISCLOSURE Technical Problem The present invention has been conceived to solve the problems of the prior art as described above, and it is an object of the present invention to provide a method and apparatus for selecting weakly acidic dietary fiber to provide an excellent cleaning effect through an eco-friendly process, Even if you take a bath to minimize skin irritation, replenish moisture, adsorb oil, remove impurities and waste products, such as jelly-like transparent, moist and soft three-dimensional net structure to make a sponge, the tissue itself is the same as the acidity of the skin layer Acidic fiber-like jelly sponge for cleansing and bathing, and a weakly acidic fiber-type jelly sponge produced therefrom.
상기와 같은 과제를 해결하기 위하여, 본 발명은 (1) 정제수, 유화제, 기포제 및 식이섬유를 혼합 및 교반하여 수성 졸을 형성시키고, 겔화제를 첨가하여 교반하는 교반단계; (2) 상기 단계 (1)의 결과물을 성형틀에 부어 넣어 형상을 형성하는 분주단계; (3) 상기 단계 (2)의 결과물이 안정적으로 겔화하도록 상온에서 1~24시간 동안 숙성하는 숙성단계; (4) 상기 단계 (3)의 결과물을 85~120℃에서 1~5시간 동안 증기가열하여 비가역적 가열반응을 통하여 스폰지화하는 가열단계; (5) 상기 단계 (4)의 결과물을 상온에서 1~5시간 동안 냉각시키는 서냉단계; (6) 상기 단계 (5)의 결과물을 영하 20℃ 이하에서 1~5일 동안 냉동시키는 냉동단계; (7) 상기 단계 (6)의 결과물을 해동시켜서 스폰지 조직을 강화하고 반응에 참여하고 남은 유화제, 기포제, 겔화제를 제거하기 위하여 세척하는 해동세척단계; (8) 상기 단계 (7)의 결과물에 남아있을 수 있는 염기를 완전히 제거하고 약산성 특성을 복구하기 위하여 식용 유기산에 1~24시간 담가두는 침지단계; (9) 상기 단계 (8)의 결과물을 세척, 소독, 탈수, 건조하는 건조단계; 및 (10) 상기 단계 (9)의 결과물을 밀봉 포장하는 포장단계를 포함하는 것을 특징으로 하는 세안 및 목욕용 약산성 식이섬유 젤리 스폰지의 제조 방법을 제공한다.
In order to solve the above-mentioned problems, the present invention provides a method for producing a water-soluble polymer, comprising: (1) stirring an aqueous sol by mixing and stirring purified water, an emulsifier, a foaming agent and dietary fiber, adding a gelling agent and stirring; (2) dividing the result of step (1) into a molding die to form a shape; (3) aging for aging at room temperature for 1 to 24 hours so that the resultant product of step (2) stably gels; (4) heating the result of the step (3) by steam heating at 85 to 120 ° C for 1 to 5 hours to effect spongy heating through an irreversible heating reaction; (5) a slow cooling step of cooling the resultant of step (4) at room temperature for 1 to 5 hours; (6) a freezing step of freezing the result of step (5) for 1 to 5 days at a temperature of minus 20 ° C; (7) a defrosting washing step of defrosting the result of step (6) to strengthen the sponge structure and washing to remove the remaining emulsifier, foaming agent and gelling agent; (8) immersing in the edible organic acid for 1 to 24 hours so as to completely remove the base remaining in the result of step (7) and to restore the weak acidic property; (9) a step of washing, disinfecting, dehydrating and drying the result of step (8); And (10) a packaging step of encapsulating and packaging the result of step (9). The present invention also provides a method of manufacturing a weak acidic fiber jelly sponge for cleansing and bathing.
상기 단계 (1)의 배합비율은 정제수 100ml에 대하여, 기포제 0.1~1.0g, 유화제 0.01~1ml, 식이섬유 2~10g, 겔화제 0.005~1ml의 비율로 혼합되는 것이 바람직하다.
The mixing ratio of the step (1) is preferably 0.1 to 1.0 g of a foaming agent, 0.01 to 1 ml of an emulsifier, 2 to 10 g of a dietary fiber, and 0.005 to 1 ml of a gelling agent per 100 ml of purified water.
상기 단계 (1)의 식이섬유는 (a) 글루코만난; (b) 구아검 또는 구아검가수분해물, 차전자피, 난소화성 말토덱스트린, 대두식이섬유, 목이, 밀식이섬유, 보리식이섬유, 귀리, 아라비아검, 이눌린 및 치커리 추출물, 폴리덱스트로스, 셀룰로스, 호로파종자 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 식물성 식이섬유; 및 (c) 아가, 아가로이드, 아가로즈, 알긴산, 카라기난, 커들란, 겔란, 펙틴, 이들의 겔 형성 화학 유도체 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 겔 형성체로 이루어지는 것이 바람직하다.
The dietary fiber of step (1) comprises (a) glucomannan; (b) extracts of guar gum or guar gum hydrolysates, porcine females, indigestible maltodextrins, soybean fiber, throat, wheat germ, barley fiber, oats, gum arabic, inulin and chicory extract, polydextrose, cellulose, fenugreek and Vegetable dietary fiber selected from the group consisting of mixtures thereof; And (c) a gel-formed body selected from the group consisting of agar, agaroid, agarose, alginic acid, carrageenan, curdlan, gellan, pectin, gel-forming chemical derivatives thereof and mixtures thereof.
상기 단계 (1)의 식이섬유의 비율은 (a) 글루코만난 100중량부에 대하여, (b) 식물성 식이섬유 10~100중량부 및 겔 형성체 10~200중량부인 것이 바람직하다.
The proportion of the dietary fiber in step (1) is preferably 10 to 100 parts by weight of the vegetable fiber (b) and 10 to 200 parts by weight of the gel-formed body, relative to 100 parts by weight of glucomannan.
상기 단계 (8)의 식용 유기산이 글리콜산, 락트산, 사과산, 구연산, 주석산, 만델산, 살리실산 및 초산으로 이루어지는 군으로부터 1종 이상 선택되는 것이 바람직하다.
It is preferable that the edible organic acid in step (8) is at least one selected from the group consisting of glycolic acid, lactic acid, malic acid, citric acid, tartaric acid, mandelic acid, salicylic acid and acetic acid.
상기 단계 (9)의 건조는 35~55℃ 온도에서 15~40 시간 동안 건조하여 수분 함량을 15% 이하로 건조하는 것이 바람직하다.
The drying of step (9) is preferably performed at a temperature of 35 to 55 ° C for 15 to 40 hours to dry the moisture content to 15% or less.
또한, 본 발명은 본 발명의 상기 제조 방법으로 제조되는 것을 특징으로 하는 세안 및 목욕용 약산성 식이섬유 젤리 스폰지를 제공한다.
In addition, the present invention provides a weak acidic fiber jelly sponge for cleansing and bathing, which is produced by the above-described manufacturing method of the present invention.
본 발명의 제조 방법에 따른 세안 및 목욕용 약산성 식이섬유 젤리 스폰지는 식이섬유를 원료로 하여 피부층의 산성도와 같은 약산성을 갖도록 제조된다. 물을 흡수하면 팽윤하여 젤리처럼 투명하고 촉촉하고 부드러운 3차원 그물구조를 갖게 되어 피부 자극 없이 탁월한 세정효과를 보장하고, 세정제 없이 물만으로 세안이나 목욕하는 경우에도 피부자극은 최소화하고 수분은 보충하고 유분은 흡착하고 불순물, 노폐물들은 효과적으로 제거할 수 있다. 피부 유수분도가 정상범위(pH 4.5~6.0)에 있는 경우는 탁월한 세정과 행굼 후 정리세안을 통하여 촉촉하고 매끄러운 세안 및 목욕을 보장하고, 정상범위를 벗어난 아토피(pH8.0), 여드름(pH7.5), 신생아/영유아(pH6.5~6.8), 뾰루지, 트러블, 건성, 각질, 민감피부 등 피부가 알칼리화되어 세안이나 목욕 시 알칼리 세정제 영향을 많이 받는 경우에는, 알칼리세정제 사용 없이 본 발명품만으로 물세안이나 물목욕을 하게 되면 피부 pH도를 낮추는 데 도움을 주면서도 유분은 흡착하고 이물질은 제거하여 충분한 세정효과를 기대할 수 있어서 피부 건강에 획기적인 도움이 될 것이다.
The weakly acidic fiber jelly sponge for cleansing and bathing according to the production method of the present invention is manufactured to have a weak acidity such as the acidity of the skin layer using dietary fiber as a raw material. When water is absorbed, it swells and becomes transparent like a jelly. It has a moist and soft three-dimensional net structure, which ensures excellent cleaning effect without skin irritation. Minimizes skin irritation even when washing or bathing with water without detergent. Adsorbs, and impurities and waste can effectively be removed. When the skin oil level is within the normal range (pH 4.5 ~ 6.0), it guarantees moist and smooth cleansing and bathing through excellent cleansing and post-rinse cleansing. It also provides atopy (pH 8.0), acne (pH7.0) 5), newborn / infant (pH 6.5 ~ 6.8), rash, trouble, dryness, keratin, sensitive skin, etc. If the skin is alkalized and is affected by alkaline detergent when cleansing or bathing, When cleansing or bathing with water, it helps lowering the pH of the skin, but it can absorb oil and remove foreign matter and expect a sufficient cleaning effect, which will be a great help to skin health.
도 1은 본 발명의 세안 및 목욕용 약산성 천연 식이섬유 젤리 스폰지의 제조 공정을 모식적으로 나타낸 것이다.
도 2는 본 발명의 제조 방법에 따른 세안 및 목욕용 약산성 천연 식이섬유 젤리 스폰지 및 pH 측정치를 나타낸 것이다.
도 3은 본 발명의 세안 및 목욕용 약산성 천연 식이섬유 젤리 스폰지의 현미경 100배 확대 사진을 나타낸 것이다.
도 4a 내지 도 4d는 기존의 여러 세안 및 목욕용 스폰지(a는 극세사 면, b는 PVA 클렌징 퍼프, c는 폴리우레탄 스폰지 및 d는 천연펄프)의 현미경 확대 사진을 나타낸 것이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic view showing a manufacturing process of a weakly acidic natural fiber fiber jelly sponge for cleansing and bathing according to the present invention.
FIG. 2 shows a mild acidic natural fiber fiber jelly sponge and pH measurement for cleansing and bathing according to the production method of the present invention.
FIG. 3 is an enlarged view of a microscope 100 times magnification of a slightly acidic natural fiber fiber jelly sponge for cleansing and bathing of the present invention.
Figs. 4A to 4D are microscope enlarged photographs of various existing facial and bath sponges (a is microfiber, b is PVA cleansing puff, c is polyurethane sponge, and d is natural pulp).
이하, 본 발명을 상세하게 설명한다.
Hereinafter, the present invention will be described in detail.
본 발명의 발명자는 종래 세안 및 목욕에 부적합한 스폰지 제품들의 단점을 보완하고 특히 피부 유수분(pH도) 밸런스가 필요한 현대인들의 피부 관리의 시작인 올바른 세안과 목욕을 위한 최적의 약산성 젤리 성상의 세정스폰지를 위한 연구를 거듭한 결과, 본래 재료 자체가 약산성을 가진 글루코만난과 같은 식이섬유를 겔화하는 과정에서 투입된 염기의 잔여물을 식용 유기산으로 처리하여 완벽히 제거하므로써, 제조된 스폰지가 약산성을 띄게 되어 피부 보호막의 손상이 없이 효과적으로 세안 및 목욕이 가능함을 확인하고 본 발명을 완성하였다.
The inventor of the present invention has been made to solve the problems of the conventional sponge products which are unsuitable for cleansing and bathing, and it is an object of the present invention to provide a cleansing sponge of a weakly acidic jelly-like shape optimal for cleansing and bathing, As a result, it has been found that the sponge produced by the present invention is weakly acidified by treating the residual base of the base with edible organic acid completely during the process of gelling the dietary fiber such as glucomannan, The present invention has been accomplished by confirming that cleansing and bathing are possible without damage.
본 발명의 세안 및 목욕용 약산성 식이섬유 젤리 스폰지의 제조 방법은 도 1에서 도시된 바와 같이, (1) 정제수, 유화제, 기포제 및 식이섬유를 혼합 및 교반하여 수성 졸을 형성시키고, 겔화제를 첨가하여 교반하는 교반단계; (2) 상기 단계 (1)의 결과물을 성형틀에 부어 넣어 형상을 형성하는 분주단계; (3) 상기 단계 (2)의 결과물이 안정적으로 겔화하도록 상온에서 1~24시간 동안 숙성하는 숙성단계; (4) 상기 단계 (3)의 결과물을 85~120℃에서 1~5시간 동안 증기가열하여 비가역적 가열반응을 통하여 스폰지화하는 가열단계; (5) 상기 단계 (4)의 결과물을 상온에서 1~5시간 동안 냉각시키는 서냉단계; (6) 상기 단계 (5)의 결과물을 영하 20℃ 이하에서 1~5일 동안 냉동시키는 냉동단계; (7) 상기 단계 (6)의 결과물을 해동시켜서 스폰지 조직을 강화하고 반응에 참여하고 남은 유화제, 기포제, 겔화제를 제거하기 위하여 세척하는 해동세척단계; (8) 상기 단계 (7)의 결과물에 남아있을 수 있는 염기를 완전히 제거하고 약산성 특성을 복구하기 위하여 식용 유기산에 1~24시간 담가두는 침지단계; (9) 상기 단계 (8)의 결과물을 세척, 소독, 탈수, 건조하는 건조단계; 및 (10) 상기 단계 (9)의 결과물을 밀봉 포장하는 포장단계로 이루어진다.
As shown in FIG. 1, (1) a method for producing a weak acidic fiber fibrin jelly sponge for cleansing and bathing according to the present invention comprises the steps of (1) mixing an aqueous emulsion by mixing and stirring purified water, emulsifier, foaming agent and dietary fiber, Stirring step; (2) dividing the result of step (1) into a molding die to form a shape; (3) aging for aging at room temperature for 1 to 24 hours so that the resultant product of step (2) stably gels; (4) heating the result of the step (3) by steam heating at 85 to 120 ° C for 1 to 5 hours to effect spongy heating through an irreversible heating reaction; (5) a slow cooling step of cooling the resultant of step (4) at room temperature for 1 to 5 hours; (6) a freezing step of freezing the result of step (5) for 1 to 5 days at a temperature of minus 20 ° C; (7) a defrosting washing step of defrosting the result of step (6) to strengthen the sponge structure and washing to remove the remaining emulsifier, foaming agent and gelling agent; (8) immersing in the edible organic acid for 1 to 24 hours so as to completely remove the base remaining in the result of step (7) and to restore the weak acidic property; (9) a step of washing, disinfecting, dehydrating and drying the result of step (8); And (10) packaging the resulting product of step (9).
상기 단계 (1)의 교반단계는 정제수, 기포제, 유화제, 식이섬유를 배합하여 졸을 형성시킨 후 겔화제를 넣고 교반기로 교반하며 혼합하는 것이다.
The stirring step of step (1) is a step of mixing a purified water, a foaming agent, an emulsifier, and dietary fiber to form a sol, adding a gelling agent thereto, and stirring the mixture with a stirrer.
상기 단계의 배합비율은 정제수 100ml에 대하여, 기포제 0.1~1.0g, 유화제 0.01~1ml, 식이섬유 2~10g, 겔화제 0.005~1ml의 비율로 혼합되는 것이 바람직하다.
The mixing ratio of the above step is preferably 0.1 to 1.0 g of a foaming agent, 0.01 to 1 ml of an emulsifier, 2 to 10 g of a dietary fiber, and 0.005 to 1 ml of a gelling agent per 100 ml of purified water.
상기 정제수는 상기 교반단계에서 식이섬유를 졸화하는 매질 역할을 한다.
The purified water serves as a medium for solubilizing the dietary fiber in the stirring step.
상기 기포제는 천연기포제로 교반단계를 거친 식이섬유를 후술할 가열단계에서 스폰지화할 때 기포가 원활하게 형성될 수 있도록 하기 위하여 첨가되는 것으로서 상기에서 설명한 바와 같이, 정제수 100ml에 대하여 0.1~1.0g이 첨가된다.
The foaming agent is added so that the bubbles can be smoothly formed when the dietary fiber subjected to the stirring step with the natural foaming agent is spongeed in a heating step to be described later. As described above, 0.1 to 1.0 g is added to 100 ml of purified water do.
상기 유화제는 상술한 정제수, 기포제, 식이섬유, 겔화제가 원활하게 혼합되도록 하기 위하여 첨가되는 것으로서 다른 혼합물의 혼합비율을 저해하지 않으며 유화제 본연의 효능을 얻을 수 있도록 물 100ml에 대하여 0.01~1ml가 첨가된다.
The emulsifier is added so that the above-mentioned purified water, foaming agent, dietary fiber and gelling agent are mixed smoothly, and 0.01 to 1 ml is added to 100 ml of water so as not to interfere with the mixing ratio of the other mixture and obtain the original efficacy of the emulsifier .
상기 겔화제는 졸화된 식이섬유를 겔화하기 위하여 첨가되는 것으로 상기 졸의 pH가 상기 겔화제를 첨가하므로써 약 9.0 내지 12.0으로 조정될 수 있도록 정제수 100ml에 대하여 0.05~1g이 첨가된다. 상기 겔화제의 예는 특별히 한정되는 것은 아니나, 수산화 암모늄, 알칼리 금속 하이드록사이드 또는 카보네이트 및 알칼리 토금속 하이드록사이드 또는 카보네이트로 이루어지는 군으로부터 1종 이상 선택될 수 있다.
The gelling agent is added to gellify the solubilized dietary fiber, and 0.05 to 1 g is added to 100 ml of purified water so that the pH of the sol can be adjusted to about 9.0 to 12.0 by adding the gelling agent. Examples of the gelling agent include, but are not limited to, ammonium hydroxide, an alkali metal hydroxide or a carbonate and an alkaline earth metal hydroxide or a carbonate.
상기 단계 (1)의 식이섬유는 (a) 곤약(konjac)으로부터 유도되는 글루코만난; (b) 구아검 또는 구아검가수분해물, 차전자피, 난소화성 말토덱스트린, 대두식이섬유, 목이, 밀식이섬유, 보리식이섬유, 귀리, 아라비아검, 이눌린 및 치커리 추출물, 폴리덱스트로스, 셀룰로스, 호로파종자 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 식물성 식이섬유; 및 (c) 아가, 아가로이드, 아가로즈, 알긴산, 카라기난, 커들란, 겔란, 펙틴, 이들의 겔 형성 화학 유도체 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 겔 형성체로 이루어진다.
The dietary fiber of step (1) comprises (a) glucomannan derived from konjac; (b) extracts of guar gum or guar gum hydrolysates, porcine females, indigestible maltodextrins, soybean fiber, throat, wheat germ, barley fiber, oats, gum arabic, inulin and chicory extract, polydextrose, cellulose, fenugreek and Vegetable dietary fiber selected from the group consisting of mixtures thereof; And (c) a gel-formed body selected from the group consisting of agar, agaroid, agarose, alginic acid, carrageenan, curdlan, gellan, pectin, gelation-forming chemical derivatives thereof and mixtures thereof.
상기 단계 (1)의 식이섬유의 비율은 (a) 글루코만난 100중량부에 대하여, (b) 식물성 식이섬유 10~100중량부 및 겔 형성체 10~200중량부일 수 있다. 또한, 상기 식이섬유는 정제수 100ml에 대하여 2~10g이다.
The proportion of the dietary fiber in the step (1) may be 10 to 100 parts by weight of the vegetable fiber (b) and 10 to 200 parts by weight of the gel-formed body, relative to 100 parts by weight of glucomannan. The dietary fiber is 2 to 10 g per 100 ml of purified water.
상기 단계 (2)의 분주단계는 상기 교반단계를 통하여 혼합된 반죽을 성형틀에 부어 넣어 형상을 형성하는 것이다.
In the dispensing step of the step (2), the dough mixed through the stirring step is poured into a mold to form a shape.
이는 상기 교반단계를 통하여 졸화된 식이섬유가 분부 및 숙성 단계를 거쳐 후술할 가열단계를 통하여 기포를 형성하여 원하는 스폰지의 형상을 형성하기 위하여 진행되는 것이다.
This is because the solubilized dietary fiber through the stirring step proceeds to form a desired sponge by forming bubbles through a heating step, which will be described later, through a spraying and aging step.
이때, 상기 성형틀은 인체에 환경호르몬으로 인한 해가 없도록 폴리프로필렌재질로 90℃ 이상의 내열온도를 이루는 성형틀을 사용하는 것이 바람직하며, 상기 성형틀의 형상은 사용자의 선택에 따라 다양하게 변경하여 적용할 수 있는 것이다.
At this time, it is preferable to use a molding frame made of polypropylene which has a heat-resistant temperature of 90 ° C or higher so that there is no harm caused by environmental hormones in the human body. The shape of the molding frame may be variously changed It can be applied.
상기 단계 (3)의 숙성단계는 졸화된 식이섬유가 안정적으로 겔화할 수 있도록 밀폐된 공간에서 상온으로 1~24시간 동안 숙성하는 단계이다.
The aging step of step (3) is a step of aging the sealed fiber in an enclosed space at room temperature for 1 to 24 hours so that the fiber can be stably gelled.
상기 단계 (4)의 가열단계는 겔화된 식이섬유를 85~120℃를 이루는 증기가열기에 넣고 1~5시간 동안 증기가열하여 비가역적 가열반응을 통하여 3차원 그물구조의 스폰지 형상을 이루도록 형성하는 것이다.
In the heating step (4), the gelled dietary fiber is formed into a sponge shape of a three-dimensional net structure through irreversible heating reaction by heating in steam heat of 85 to 120 ° C for 1 to 5 hours will be.
이때, 겔화된 식이섬유는 기포 발생단계를 거쳐 기포를 유지하고 고착화하는 단계를 거쳐 조직이 단단해지는 과정을 거쳐 스폰지화하게 된다.
At this time, the gelled dietary fiber passes through the bubble generating step, and then the bubble is retained and fixed, and the tissue becomes hardened and spongeed.
상기 단계 (5)의 냉각단계는 상기 증기가열단계를 통하여 형성된 스폰지를 상온에서 1~4시간 동안 서냉하는 단계이다.
The cooling step of step (5) is a step of slowly cooling the sponge formed through the steam heating step at room temperature for 1 to 4 hours.
상기 단계 (6)의 냉동단계는 상기 냉각단계를 거친 스폰지를 영하 20℃ 이하에서 1~5일 냉동시키는 것이다.
The refrigeration step in the step (6) is to freeze the sponge that has undergone the cooling step at -120 ° C for 1 to 5 days.
이는 스폰지의형상과 식이섬유의 3차원 그물 구조가 견고하게 유지되고 질겨지도록 하기 위한 것이다. 냉동을 시키게 되면 스폰지에 남아있던 수분과 그물 구조가 분리되게 된다. 이때 냉동시간과 스폰지의 질김, 내구성은 큰 연관이 있다.
This is to ensure that the shape of the sponge and the three dimensional network structure of the dietary fiber are firmly maintained and concealed. When frozen, the moisture and net structure remaining in the sponge are separated. At this time, there is a great relation between the freezing time and the durability of the sponge.
상기 단계 (7)의 해동세척단계는 상기 냉동단계를 거쳐 냉동된 스폰지를 25~35℃의 물속에서 해동시켜 냉동과정에서 분리된 스폰지의 수분과 그물조직을 배출시켜 조직을 강화하고 상기 교반단계에서 첨가된 정제수, 기포제, 유화제, 겔화제를 제거하는 단계이다.
In the defrosting step of the step (7), the frozen sponge is thawed in water at 25 to 35 ° C through the freezing step, the moisture and net tissue of the sponge separated during the freezing process are discharged to reinforce the tissue, Removing the added purified water, foaming agent, emulsifier and gelling agent.
스폰지를 깨끗한 정수에 침수시켜 해동시키고 꺼내어 탈수하는 과정을 반복 수행함으로써 스폰지에 남아있을 수 있는 첨가물 및 각종 불순물을 완전히 제거하여 사용자의 피부와 접촉하여 피부 트러블을 일으킬 수 있는 문제를 미연에 방지할 수 있게 되는 것이다.
The sponge is submerged in a clean water and thawed and taken out and dewatered repeatedly to completely remove additives and various impurities that may remain in the sponge to prevent problems that can cause skin troubles by contacting the user's skin It will be.
상기 단계 (8)의 침지단계는 상기 해동세척단계 이후에도 잔류할 수 있는 겔화제를 완전히 제거하고 스폰지가 원래의 약산성을 회복할 수 있도록 식용유기산에 1~24시간 침지하는 단계이다.
The immersion step (8) is a step of completely removing the gelling agent remaining after the thawing cleaning step and immersing the sponge in the vegetable oil base for 1 to 24 hours so as to recover the original weak acidity.
식용 유기산은 글리콜산, 락트산, 사과산, 구연산, 주석산, 만델산, 살리실산 및 초산으로 이루어지는 군으로부터 1종 이상 선택되는 것이 바람직하며, 정제수 100중량부에 대하여 10 내지 100중량부로 혼합하여 사용할 수 있다.
The edible organic acid is preferably selected from the group consisting of glycolic acid, lactic acid, malic acid, citric acid, tartaric acid, mandelic acid, salicylic acid and acetic acid, and may be used in an amount of 10 to 100 parts by weight per 100 parts by weight of purified water.
상기 단계 (9)의 건조단계는 상기 침지 단계를 거친 스폰지를 세척, 소독, 탈수, 건조하는 단계이다. 건조기의 35~55℃ 온도에서 15~40 시간 동안 건조하여 수분 함량을 15% 이하로 건조한다.
The drying step (9) is a step of washing, disinfecting, dehydrating and drying the sponge after the immersion step. Dry the product at 35-55 ° C for 15-40 hours to dry the product at a moisture content of 15% or less.
상기 단계 (10)의 포장단계는 수분이 침투할 수 없도록 상기 건조된 스폰지를 밀봉 포장하는 단계이다.
The packaging step of the step (10) is a step of sealing the dried sponge so that moisture can not permeate.
본 발명은 특정한 실시예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 제공되는 본 발명의 정신이나 분야를 벗어나지 않는 한도 내에서 본 발명이 다양하게 개량 및 변화될 수 있다는 것을 당 업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
While the present invention has been particularly shown and described with reference to specific embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the following claims It will be apparent to those of ordinary skill in the art.
Claims (7)
(1) 정제수, 유화제, 기포제 및 식이섬유를 혼합 및 교반하여 수성 졸을 형성시키고, 겔화제를 첨가하여 교반하는 교반단계;
(2) 상기 단계 (1)의 결과물을 성형틀에 부어 넣어 형상을 형성하는 분주단계;
(3) 상기 단계 (2)의 결과물이 안정적으로 겔화하도록 상온에서 1~24시간 동안 숙성하는 숙성단계;
(4) 상기 단계 (3)의 결과물을 85~120℃에서 1~5시간 동안 증기가열하여 비가역적 가열반응을 통하여 스폰지화하는 가열단계;
(5) 상기 단계 (4)의 결과물을 상온에서 1~5시간 동안 냉각시키는 서냉단계;
(6) 상기 단계 (5)의 결과물을 영하 20℃ 이하에서 1~5일 동안 냉동시키는 냉동단계;
(7) 상기 단계 (6)의 결과물을 해동시켜서 스폰지 조직을 강화하고 반응에 참여하고 남은 유화제, 기포제, 겔화제를 제거하기 위하여 세척하는 해동세척단계;
(8) 상기 단계 (7)의 결과물에 남아있을 수 있는 염기를 완전히 제거하고 약산성 특성을 복구하기 위하여 식용 유기산에 1~24시간 담가두는 침지단계;
(9) 상기 단계 (8)의 결과물을 세척, 소독, 탈수, 건조하는 건조단계; 및
(10) 상기 단계 (9)의 결과물을 밀봉 포장하는 포장단계.
A method for preparing a weakly acidic fiber jelly sponge for cleansing and bathing, comprising the steps of:
(1) stirring step in which an aqueous sol is formed by mixing and stirring purified water, an emulsifier, a foaming agent and dietary fiber, and a gelling agent is added and stirred;
(2) dividing the result of step (1) into a molding die to form a shape;
(3) aging for aging at room temperature for 1 to 24 hours so that the resultant product of step (2) stably gels;
(4) heating the result of the step (3) by steam heating at 85 to 120 ° C for 1 to 5 hours to effect spongy heating through an irreversible heating reaction;
(5) a slow cooling step of cooling the resultant of step (4) at room temperature for 1 to 5 hours;
(6) a freezing step of freezing the result of step (5) for 1 to 5 days at a temperature of minus 20 ° C;
(7) a defrosting washing step of defrosting the result of step (6) to strengthen the sponge structure and washing to remove the remaining emulsifier, foaming agent and gelling agent;
(8) immersing in the edible organic acid for 1 to 24 hours so as to completely remove the base remaining in the result of step (7) and to restore the weak acidic property;
(9) a step of washing, disinfecting, dehydrating and drying the result of step (8); And
(10) A packaging step for encapsulating and packaging the result of step (9).
상기 단계 (1)의 배합비율은 정제수 100ml에 대하여, 기포제 0.1~1.0g, 유화제 0.01~1ml, 식이섬유 2~10g, 겔화제 0.005~1ml의 비율로 혼합되는 것을 특징으로 하는 제조 방법.
The method according to claim 1,
Wherein the mixing ratio of the step (1) is 0.1 to 1.0 g of a foaming agent, 0.01 to 1 ml of an emulsifier, 2 to 10 g of a dietary fiber, and 0.005 to 1 ml of a gelling agent, based on 100 ml of purified water.
상기 단계 (1)의 식이섬유는 (a) 글루코만난; (b) 구아검 또는 구아검가수분해물, 차전자피, 난소화성 말토덱스트린, 대두식이섬유, 목이, 밀식이섬유, 보리식이섬유, 귀리, 아라비아검, 이눌린 및 치커리 추출물, 폴리덱스트로스, 셀룰로스, 호로파종자 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 식물성 식이섬유; 및 (c) 아가, 아가로이드, 아가로즈, 알긴산, 카라기난, 커들란, 겔란, 펙틴, 이들의 겔 형성 화학 유도체 및 이들의 혼합물로 이루어지는 군으로부터 선택되는 겔 형성체로 이루어지는 것을 특징으로 하는 제조 방법.
The method according to claim 1,
The dietary fiber of step (1) comprises (a) glucomannan; (b) extracts of guar gum or guar gum hydrolysates, porcine females, indigestible maltodextrins, soybean fiber, throat, wheat germ, barley fiber, oats, gum arabic, inulin and chicory extract, polydextrose, cellulose, fenugreek and Vegetable dietary fiber selected from the group consisting of mixtures thereof; And (c) a gel-formed body selected from the group consisting of agar, agaroid, agarose, alginic acid, carrageenan, curdlan, gellan, pectin, gel-forming chemical derivatives thereof and mixtures thereof.
상기 단계 (1)의 식이섬유의 비율은 (a) 글루코만난 100중량부에 대하여, (b) 식물성 식이섬유 10~100중량부 및 겔 형성체 10~200중량부인 것을 특징으로 하는 제조 방법.
The method of claim 3,
Wherein the ratio of dietary fiber in step (1) is 10 to 100 parts by weight of vegetable fiber (b) and 10 to 200 parts by weight of gel-formed body, with respect to 100 parts by weight of glucomannan.
상기 단계 (8)의 식용 유기산이 글리콜산, 락트산, 사과산, 구연산, 주석산, 만델산, 살리실산 및 초산으로 이루어지는 군으로부터 1종 이상 선택되는 것을 특징으로 하는 제조 방법.
The method according to claim 1,
Wherein the edible organic acid in step (8) is at least one selected from the group consisting of glycolic acid, lactic acid, malic acid, citric acid, tartaric acid, mandelic acid, salicylic acid and acetic acid.
상기 단계 (9)의 건조는 35~55℃ 온도에서 15~40 시간 동안 건조하여 수분 함량을 15% 이하로 건조하는 것을 특징으로 하는 제조 방법.
The method according to claim 1,
Wherein the drying of step (9) is performed at a temperature of 35 to 55 ° C for 15 to 40 hours to dry the moisture content to 15% or less.
A weak acidic fiber jelly sponge for cleansing and bathing, which is produced by the method of any one of claims 1 to 6.