KR101400553B1 - Water-soluble membrane waterproof agent containing lotus leaf extract, and complex water proof structure using the same and the constructing method thereof - Google Patents
Water-soluble membrane waterproof agent containing lotus leaf extract, and complex water proof structure using the same and the constructing method thereof Download PDFInfo
- Publication number
- KR101400553B1 KR101400553B1 KR1020130102796A KR20130102796A KR101400553B1 KR 101400553 B1 KR101400553 B1 KR 101400553B1 KR 1020130102796 A KR1020130102796 A KR 1020130102796A KR 20130102796 A KR20130102796 A KR 20130102796A KR 101400553 B1 KR101400553 B1 KR 101400553B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- water
- coating film
- weight
- lotus leaf
- Prior art date
Abstract
Description
본 발명은 연잎 추출물이 함유된 수용성 도막방수제와 이를 이용한 복합방수구조 및 그 시공방법에 관한 것으로서, 더욱 상세하게는 도막방수제에 연잎 추출물을 함유시켜 발수성이 뛰어나면서도 환경 친화적일 수 있도록 하면서, 이러한 도막방수제를 다른 재료들과 함께 적절히 이용하여 복합방수구조를 시공함으로써, 방수기능이 현저히 증강되면서 구조물의 크랙 발생도 현저히 저감될 수 있는, 연잎 추출물이 함유된 도막방수제와 이를 이용한 복합방수구조 및 그 시공방법에 관한 것이다.
The present invention relates to a water-soluble film-forming water-repellent agent containing a lotus leaf extract, a composite water-proofing structure using the same, and more particularly to a water- A waterproofing agent containing a leaf extract of a lotus leaf and a composite waterproofing structure using the same, and a waterproofing structure using the waterproofing agent and a waterproofing composition using the waterproofing agent together with other materials so that the waterproofing function can be remarkably enhanced and cracking of the structure can be significantly reduced. ≪ / RTI >
도막방수제는 합성수지 재료를 바탕에 발라 방수도막을 만드는 공법에 사용되는 방수제로서, 고무아스팔트, 아크릴고무 또는 아크릴수지 등이 주성분인 에멀젼형과 클로로프렌이나 클로로설폰화폴리에틸렌이 함유된 용액형 우레탄이나 에폭시 수지가 주성분인 반응형이 있으며, 이들 중 고무아스팔트계와 우레탄계 도막방수제가 많이 사용되고 있다.The waterproofing agent for coatings is a waterproofing agent used in the process of making waterproof coatings by applying synthetic resin materials on the basis of emulsion type which is mainly composed of rubber asphalt, acrylic rubber or acrylic resin, solution type urethane containing chloroprene or chlorosulfonated polyethylene, epoxy resin . Among them, rubber asphalt-based and urethane-based film-coating waterproofing agents are widely used.
고무아스팔트계 도막방수제는 아스팔트에 합성고무와 각종 수지를 혼합하여 고분자의 열가소성 성질을 이용하여 급격히 경화시키는 열공법과 합성라텍스에 아스팔트를 유화시킨 후 수분의 증발에 의해 자연경화시키는 냉공법에 의해 제조되며, 보통 아스팔트에는 스티렌 계통의 중합체, 어탁틱폴리프로필렌, 스티렌부타디엔 라텍스 등이 혼합 사용되고 있다.The rubber asphalt coating film waterproofing agent is manufactured by a thermal process in which asphalt is rapidly cured by mixing synthetic rubber and various resins by using the thermoplastic properties of the polymer and by a cold process in which asphalt is emulsified in a synthetic latex and then naturalized by evaporation of water , Styrene-based polymers, adventitious polypropylene, styrene-butadiene latex, and the like are usually mixed in asphalt.
그리고 우레탄계 도막방수제는 용제형 우레탄계가 많이 사용되며, 최근에는 환경공해나 독성에 대한 작업안전성을 고려하여 폴리우레탄 에멀젼, 폴리우레탄 콜로이드 분산체, 폴리우레탄 수용액 등의 성상으로 수용성 우레탄계 방수제를 개발하여 사용하고 있으나, 아직 내구성을 비롯한 물성면에서는 기존 용제형 우레탄계 방수제보다 미흡한 점이 많다.In recent years, a water-soluble urethane-based waterproofing agent has been developed and used as a property of a polyurethane emulsion, a polyurethane colloidal dispersion, and a polyurethane aqueous solution in consideration of the safety of the environment and toxicity. However, in terms of physical properties including durability, there are many points that are insufficient compared with the conventional solvent type urethane type waterproofing agent.
이상에서 열거한 도막방수제는 건축물 등에서의 누수를 방지코자 하는 방수제로서의 기본기능 이외에, 최근 방수제로서 요구되고 있는 건축물의 부식과 잡초 및 해충의 서식 방지, 건물 옥상의 화단 조성이나 수목 식재가 가능토록 하는 미장성, 그리고 급격한 외부온도의 변화에 의해 발생하는 크랙에 대한 저항성 등에는 문제가 있다. 특히 종래 고무아스팔트 방수제의 경우에도 고무 성분이 적어 건축물의 균열을 방지하는 기능은 거의 갖지 못하고 있다.In addition to the basic functions as a waterproofing agent to prevent leaks in buildings and the like, the coating waterproofing agents enumerated above are used to prevent the corrosion of buildings that are recently required as waterproofing agents, to prevent the formation of weeds and insects, There is a problem in terms of fineness and resistance to cracks caused by a sudden change in external temperature. Particularly, even in the case of conventional rubber asphalt waterproofing agent, there is little function of preventing the cracks of the building due to a small number of rubber components.
이러한 문제점을 개선하기 위하여 등록특허 10-1122254호를 참조하면, 콘크리트 구조물용 수용성 도막방수제 및 그 제조방법이 제안되고 있다. 그러나, 상기한 문헌에 개시된 수용성 도막방수제는 부착강도는 양호하나, 오로지 화학 합성재료만을 혼합 이용하고 있어 환경 친화성이 떨어지는 문제가 있다.In order to solve such problems, a water-repellent coating solution for a concrete structure and a manufacturing method thereof have been proposed with reference to Japanese Patent Application No. 10-1122254. However, the water-soluble film-forming water-repellent agent disclosed in the above-mentioned document has a good adhesion strength, but uses only a chemical synthetic material, resulting in poor environmental compatibility.
또한 등록특허 10-1253028호를 참조하면, 수용성 도막방수제를 이용한 시트복합 방수공법이 제안되고 있다. 그러나 상기한 문헌에 개시된 복합 방수공법 역시 건축물의 균열 대응력에 한계가 있는 것으로 지적되고 있으므로, 구조물의 추가 균열을 방지하면서, 양호한 방수기능을 구현할 수 있는 환경 친화적인 수용성 도막방수제가 제공되는 것이 바람직할 것이다.Also, referring to Japanese Patent Application No. 10-1253028, a sheet composite waterproofing method using a water-soluble film-forming waterproofing agent has been proposed. However, it has been pointed out that the complex waterproofing method disclosed in the above-mentioned document also has a limitation in cracking ability of the building. Therefore, it is desirable to provide an environmentally friendly water-soluble coating film waterproofing agent capable of realizing a good waterproof function while preventing further cracking of the structure will be.
본 발명은 도막방수제에 연잎 추출물을 함유시켜 발수성이 뛰어나면서도 환경 친화적일 수 있도록 하면서, 이러한 도막방수제를 다른 재료들과 함께 적절히 이용하여 복합방수구조를 시공함으로써, 방수기능이 현저히 증강되면서 구조물의 크랙 발생도 현저히 저감될 수 있는, 연잎 추출물이 함유된 도막방수제와 이를 이용한 복합방수구조 및 그 시공방법를 제공하기 위한 것이다.The present invention relates to a water-repellent coating composition comprising a lotion-extracting agent in a water-repellent coating composition to provide water-repellent and environmental-friendly water-repellent compositions, A waterproofing agent containing a lotion extract of a lotus leaf, a complex waterproofing structure using the waterproofing agent, and a method for its construction.
본 발명의 목적은 수용성 에틸렌비닐아세트산 기상공중합체 50 ~ 60중량%; 연잎 추출물 10 ~ 20중량%; 및 폴리부틸아크릴산 공중합체 20 ~ 30중량%를 포함하는 도막제 조성물로 이루어지는, 연잎 추출물이 함유된 수용성 도막방수제에 의하여 달성될 수 있다.An object of the present invention is to provide a water-soluble ethylene vinyl acetate-based copolymer which comprises 50 to 60% by weight of a water-soluble ethylene vinyl acetate acetic acid copolymer; 10 to 20% by weight of lotus leaf extract; And 20 to 30% by weight of a polybutylacrylic acid copolymer, based on the total weight of the composition.
상기 연잎 추출물은 중탕설비를 이용하여 추출되며, 연잎과 물을 1:1 중량비로 이용할 수 있다.The extracted lotus leaf extract is extracted using a bathing plant, and the lotus leaf and water can be used at a weight ratio of 1: 1.
또한 본 발명의 목적은 콘크리트 구조물 상부에 도포되는 프라이머층; 상기 프라이머층 상부에 도포되는 연잎 추출물이 함유된 1차 도막방수제층; 상기 1차 도막방수제층 상부에 포설되는 섬유 포설층; 상기 섬유 포설층 상부에 도포되어 상기 섬유 포설층을 함침시키는 규조토 혼합 방수액층; 상기 규조토 혼합 방수액층 상부에 도포되는 연잎 추출물이 함유된 2차 도막방수제층; 및 상기 2차 도막방수제층 상부에 도포되는 탑코트층을 포함하며, 상기 섬유 포설층의 일면은 UV 열처리되는 것을 특징으로 하는 연잎 추출물이 함유된 수용성 도막방수제를 이용한 복합방수구조에 의해서 달성될 수 있다.It is also an object of the present invention to provide a method of manufacturing a concrete structure, A primary coating film water repellent agent layer containing a lotion extract applied to the top of the primer layer; A fiber laying layer disposed above the primary coating film water repellent layer; A diatomite mixed waterproofing liquid layer applied on the fiber laying layer to impregnate the fiber laying layer; A second coating film water repellent layer containing a lotion extract applied to the top of the diatomite mixed waterproof layer; And a top coat layer applied on top of the secondary coating film water repellent layer, wherein one side of the fiber laying layer is subjected to UV heat treatment, and the composite waterproofing structure using the water- have.
또한 본 발명의 목적은 콘크리트 구조물의 표면을 정리하고 청소한 후 프라이머층을 형성하도록 상기 콘크리트 구조물의 표면에 비닐아세테이트산 복합물로 된 프라이머(Primer)를 도포하는 단계; 상기 프라이머층의 상부에 연잎 추출물이 함유된 도막방수제를 1차로 도포하는 단계; 도포된 상기 1차 도막방수제층 상부에 PE나 PP사로 직조된 부직포를 포설하여 섬유 포설층을 형성하는 단계; 상기 섬유 포설층 상부에 규조토가 혼합된 규조토 방수액을 추가 도포하여 포설된 섬유를 함침시키는 단계; 상기 연잎 추출물이 함유된 도막방수제를 2차로 1 ~ 3회 도포하고 건조시키는 단계; 및 수용성 아크릴 에멀젼 수지로 구성된 탑코트(Top-Coat)를 도포하는 단계;를 포함하며, 상기 부직포의 일면은 UV 열처리되는 것을 특징으로 하는 콘크리크 구조물용 복합방수구조의 시공방법에 의하여도 달성될 있다.
It is also an object of the present invention to provide a method of manufacturing a concrete structure, comprising: applying a primer composed of a vinyl acetate acid composite to the surface of the concrete structure so as to form a primer layer after cleaning and cleaning the surface of the concrete structure; Coating a coating film water repellent agent containing a lotion extract on the top of the primer layer first; Forming a fiber laying layer by laying a nonwoven fabric woven with PE or PP yarn on the coated primary coating film waterproofing agent layer; Further comprising the step of applying a diatomite waterproofing liquid mixed with diatomaceous earth to the upper part of the fiber laying layer to impregnate the laid fibers; Applying the coating water repellent agent containing the extract of the lotus leaf extract to the substrate twice or three times, and drying the coating; And a topcoat composed of a water-soluble acrylic emulsion resin, wherein one side of the nonwoven fabric is subjected to a UV heat treatment, and the method is also achieved by a method of constructing a composite waterproof structure for a concrete structure have.
본 발명에 따르면, 도막방수제에 연잎 추출물을 함유시켜 발수성이 뛰어나면서도 환경 친화적일 수 있도록 하면서, 이러한 도막방수제를 다른 재료들과 함께 적절히 이용하여 복합방수구조를 시공함으로써, 방수기능이 현저히 증강되면서 구조물의 크랙 발생도 현저히 저감될 수 있는 효과가 있다.
According to the present invention, a waterproofing agent is added to a coating film waterproofing agent so as to be excellent in water repellency and environmentally friendly, and by using such a coating waterproofing agent together with other materials, a waterproofing function is remarkably enhanced, It is possible to remarkably reduce the occurrence of cracks in the substrate.
도 1은 본 발명에 의한 콘크리트 구조물의 복합방수구조를 나타낸 단면도이다.
도 2는 도 1에 도시된 콘크리트 구조물의 복합방수구조를 시공하는 방법을 나타낸 흐름도이다.1 is a sectional view showing a composite waterproof structure of a concrete structure according to the present invention.
2 is a flowchart illustrating a method of constructing a composite waterproof structure of the concrete structure shown in FIG.
이하 본 발명에 따른 실시예를 상세히 설명하면 다음과 같다.Hereinafter, embodiments according to the present invention will be described in detail.
본 발명의 일 실시예에 따른 연잎 추출물이 함유된 수용성 도막방수제는 수용성 에틸렌비닐아세트산 기상공중합체 50 ~ 60중량%; 연잎 추출물 10 ~ 20중량%; 및 폴리부틸아크릴산 공중합체 20 ~ 30중량%를 포함하는 도막제 조성물로 이루어진다.According to one embodiment of the present invention, the water-soluble coating film-containing water repellent agent containing the extract of the lotus leaf extract comprises 50 to 60% by weight of a water-soluble ethylene vinyl acetate acetic acid copolymer; 10 to 20% by weight of lotus leaf extract; And 20 to 30% by weight of a polybutylacrylic acid copolymer.
이렇게 이루어진 본 발명의 일 실시예에 따른 연잎 추출물이 함유된 수용성 도막방수제의 고형분 함량은 40~60%, 점도 5,000~10,000cps임이 바람직하다.The solid content of the water-soluble film-forming water-repellent agent containing the lotus leaf extract according to an embodiment of the present invention is preferably 40 to 60% and the viscosity is 5,000 to 10,000 cps.
상기 수용성 에틸렌비닐아세트산(Ethylene-Vinyl Acetate) 기상공중합체는 폴리에틸렌의 평균분자량이 1,000 ~ 12,000 범위의 밀도 0.918 ~ 0.932g/㎤를 갖는 중합체를 기상법으로 제조함으로써 분말형태의 고분자물질을 얻을 수 있으며, 분자량 분포가 좁은 것을 사용하는 것이 제품의 균일성 측면에서 바람직하고, 폴리에틸렌은 그 주쇄에 아크릴산이나 무수말레산 등의 극성을 가진 모노머를 측쇄로 하여 화학적으로 결합시킨 공중합체를 얻을 수 있는데, 본 발명에서는 에틸렌에 비닐아세트산을 그래프트 중합시킨 공중합체를 이용함으로써 제품의 유연성을 증대시키게 되는 것이다.The water-soluble ethylenic-vinyl acetate (VCE) gas phase copolymer can be obtained by polymerizing a polymer having an average molecular weight of 1,000 to 12,000 and a density of 0.918 to 0.932 g / cm 3 by a gas phase method, It is preferable to use a copolymer having a narrow molecular weight distribution in view of the uniformity of the product and a copolymer obtained by chemically bonding polyethylene having a polar group such as acrylic acid or maleic anhydride as a side chain to the main chain thereof. The flexibility of the product is increased by using a copolymer obtained by graft-polymerizing ethylene with vinyl acetic acid.
그리고 상기한 수용성 에틸렌비닐아세트산 기상공중합체는 에틸렌(Ethylene)과 비닐아세트산(Vinyl Acetate)을 공중합하여 생산할 경우 비닐아세트산의 양은 1 ~ 50% 정도이며, 필름용에는 비닐아세트산 함량이 약 1 ~ 25% 정도 사용되지만, 비닐아세트산 함량이 증가하면 할수록 필름의 탄성률과 열접착온도는 낮아지는 반면, 충격강도, 인장강도, 투과도는 증가되므로, 본 발명에서는 비닐아세트산의 함량이 25% 이상인 것을 사용하여 양호한 접착성과 인장강도를 발휘하게 되는데, 이는 저온 하에서도 유연성이 있고 저온 열접착성과 핫택성(hot tack, 열접착 직후의 접착강도)이 좋기 때문이다.When the water-soluble ethylene vinyl acetate-based copolymer is produced by copolymerizing ethylene and vinyl acetate, the amount of vinyl acetate is about 1 to 50%, and the content of vinyl acetate is about 1 to 25% However, as the vinyl acetate content increases, the elastic modulus and the heat bonding temperature of the film are lowered, while the impact strength, tensile strength and permeability are increased. Therefore, in the present invention, when the content of vinyl acetate is 25% or more, (Tensile strength), which is flexible even at low temperatures, and is good at low temperature thermal adhesiveness and hot tack (adhesive strength immediately after heat bonding).
또한, 연잎 추출물은 총 조성물 대비 10 ~ 20중량% 정도로 함유되어 방수 및 발수 성능은 유지한 채, 도막방수제에 자연으로부터 추출한 친환경 성분을 함유시킴으로써, 환경 친화성을 극대화시킬 수 있다. 따라서 건축 구조물이 철거되거나 방수구조가 파손되는 경우에도 종전에 비해 환경오염을 최소화할 수 있게 된다. In addition, the leaf extract is contained in an amount of about 10 to 20% by weight based on the total composition, and the environment-friendliness can be maximized by containing an environmentally-friendly ingredient extracted from nature in the coating film waterproofing agent while maintaining waterproofing and water repellent performance. Therefore, even if the building structure is demolished or the waterproof structure is damaged, the environmental pollution can be minimized.
연잎 추출물은 세척된 연잎과 물을 중량비 1:1로 하여 중탕설비를 이용하여 추출한다. 이렇게 추출된 연잎 추출물에는 연잎이 가지고 있는 소수성을 이루는 나노입자가 포함되어 추출되므로, 이러한 연잎 추출물이 다른 성분들과 혼합하여 발수 기능을 구현함으로써, 제조된 수용성 도막방수제의 방수 및 발수 기능은 천연 재료와 화학재료가 적절히 조합됨으로써 향상된 품질로 발휘될 수 있다. The leaves of the lotus leaf extract are extracted with a water bath with a 1: 1 weight ratio of washed leaves and water. To do this, because the extracted lotus leaf extract, the extract contains the nanoparticles form a hydrophobic in lotus leaf have, such a lotus leaf extract by implementing a repellent function was mixed with other ingredients, water and a water-repellent function of the produced water-soluble film waterproofing agent is a natural material And the chemical material can be exerted with an improved quality by appropriately combining them.
다음으로, 상기한 도막제 조성물에 혼합되는 폴리부틸아크릴산 공중합체는 접착제로 사용되는 것으로, 이는 방수면 표면에 약간의 탄성을 부여하면서 표면의 크랙을 방지하는 효과를 갖게 되는바, 상기한 폴리부틸아크릴산 공중합체의 사용량은 사용 용도에 따라 도막제 조성물을 기준으로 대략 10 ~ 15중량% 정도로 혼합하는 것이 적합하고, 습도가 높은 곳에는 15 ~ 20중량% 정도 혼합하는 것이 방수층 표면의 평활성 측면에서 적합하다.Next, the polybutylacrylic acid copolymer to be mixed with the above-mentioned film forming composition is used as an adhesive. This gives a slight elasticity to the surface of the waterproof surface and has an effect of preventing surface cracking, The amount of the acrylic acid copolymer to be used is suitably about 10 to 15% by weight based on the composition of the coating composition, and 15 to 20% by weight of the acrylic copolymer is suitable for the smoothness of the surface of the waterproof layer Do.
상기한 폴리부틸 아크릴산 공중합체는 폴리부틸아크릴산 호모중합체 13.5중량%, 폴리에틸아크릴산 호모중합체 8.5중량%, 폴리스틸렌 호모중합체 5.2중량%, 폴리아크릴산 호모중합체 1.3중량%의 비율로 물에 의해 유화 중합되어 이루어지는 공중합체로서, 수용성이고 내화성, 내수용성, 내마모성, 내유성, 자외선 저항성 등이 우수하다.The polybutylacrylic acid copolymer was prepared by emulsion-polymerizing with water at a ratio of 13.5 wt% of polybutyl acrylate homopolymer, 8.5 wt% of polyethyl acrylate homopolymer, 5.2 wt% of polystyrene homopolymer, and 1.3 wt% of polyacrylic acid homopolymer As a copolymer, it is water-soluble and excellent in fire resistance, water resistance, abrasion resistance, oil resistance, ultraviolet resistance and the like.
본 발명에 따르는 콘크리트 구조물용 수용성 도막방수제는 상기와 같이 구성되는 도막제 조성물을 혼합용기에 투입하고, 상기 혼합용기를 100 ~ 300rpm의 회전속도로 1 ~ 3시간 동안 교반시켜 고형분 함량 40~ 60%, 점도 5,000 ~ 10,000cps가 되도록 혼합하여 제조된다.
The water-soluble coating film waterproofing agent for a concrete structure according to the present invention is prepared by putting the coating composition having the above composition into a mixing container and stirring the mixture container at a rotation speed of 100 to 300 rpm for 1 to 3 hours to obtain a solid content of 40 to 60% , And viscosity of 5,000 to 10,000 cps.
이하 본 발명에 따른 실시예와 비교예들에 따른 실험예를 비교 설명한다.Hereinafter, experimental examples according to the present invention and comparative examples will be compared and compared.
실시예 1Example 1
수용성 에틸렌 비닐아세트산 기상공중합체 50 중량부에 연잎 추출물 20 중량부 및 폴리부틸 아크릴산 공중합체 30 중량부의 비율로 첨가한 도막제 조성물을 형성하고 가소제와 함께 믹서기에 투입한 후, 상온에서 점도 7,000 cps에 도달할 때까지 약 2시간 동안 200rpm의 회전속도로 교반 혼합시켜 균일한 수용성 도막방수제를 제조하였다.
20 parts by weight of a lotus leaf extract and 30 parts by weight of a polybutylacrylic acid copolymer were added to 50 parts by weight of a water-soluble ethylene-vinyl acetate acetic acid copolymer, and the mixture was added to a blender together with a plasticizer to a viscosity of 7,000 cps And the mixture was stirred at 200 rpm for about 2 hours until it reached a uniform water-soluble film-forming waterproofing agent.
비교예 1Comparative Example 1
배경기술에 언급된 등록특허 제10-1122254호에 따라 수용성 에틸렌 비닐아세트산 기상공중합체 50 중량부에 수용성 아크릴 에멀젼 수지 30 중량부 및 폴리부틸 아크릴산 공중합체 20 중량부의 비율로 첨가한 도막제 조성물을 형성하고 가소제와 함께 믹서기에 투입한 후, 상온에서 점도 7,000 cps에 도달할 때까지 약 2시간 동안 200rpm의 회전속도로 교반 혼합시켜 수용성 도막방수제를 제조하였다.
According to the registered patent No. 10-1122254 mentioned in the background, 30 parts by weight of a water-soluble acrylic emulsion resin and 20 parts by weight of a polybutylacrylic acid copolymer were added to 50 parts by weight of a water-soluble ethylene-vinyl acetate acetic acid copolymer to form a film- The mixture was stirred with a plasticizer at 200 rpm for about 2 hours until the viscosity reached 7,000 cps at room temperature to prepare a water-soluble film-forming waterproofing agent.
비교예 2Comparative Example 2
시중에 유통되는 한국석유공업주식회사의 냉공법용 고무 아스팔트계 도막방수제(품명: AQUA-COAT-CA100)를 사용하였다.
A rubber-asphalt-based coating waterproofing agent (trade name: AQUA-COAT-CA100) for the cooling method of Korea Petroleum Industry Co., Ltd., which is distributed in the market, was used.
상기 실시예 1에 따라 제조된 도막방수제와 비교예 1 및 2의 도막방수제를 비교하여 인장강도, 신장율, 부착강도를 측정하여 그 결과를 다음 표 1에 나타내었다.Tensile strength, elongation and adhesion strength were measured by comparing the coating water repellent prepared in Example 1 and the coating water repellent of Comparative Examples 1 and 2, and the results are shown in Table 1 below.
여기서, 인장강도 및 부착강도는 ASTM D 638-91 및 ASTM D 4541-89 방법에 의거 측정하였고, 신장율은 ASTM D638-91 방법에 따라 측정하였다.
Here, tensile strength and adhesion strength were measured according to ASTM D 638-91 and ASTM D 4541-89, and elongation was measured according to ASTM D638-91.
상기 표 1의 결과로부터 본 발명의 일 실시예에 따른 연잎 추출물이 함유된 수용성 도막방수제는 환경 친화적인 재료를 사용하면서도 비교예1과 비교하여 인장강도, 신장률 및 부착강도에 있어 별다른 차이가 없고 오히려 부착강도는 더 높아진 것을 알 수 있으며, 비교예2의 기존 고무아스팔트계 제품에 비하여는 인장강도, 신장율, 부착강도가 전반적으로 양호한 것을 알 수 있다.
From the results of the above Table 1, it can be seen that the water-soluble film-forming water-repellent agent containing the extract of the lotus leaf extract according to an embodiment of the present invention has no significant difference in tensile strength, elongation and adhesion strength as compared with Comparative Example 1, It can be seen that the adhesive strength is higher and the tensile strength, elongation and adhesion strength are generally better than those of the conventional rubber asphalt product of Comparative Example 2. [
다음은 본 발명에 의한 연잎 추출물이 함유된 수용성 도막방수제를 이용한 콘크리트 구조물의 복합방수구조에 대하여 설명한다.Next, a composite waterproof structure of a concrete structure using a water-soluble film-forming water-repellent agent containing a lotion extract of the present invention will be described.
도 1은 본 발명에 의한 콘크리트 구조물의 복합방수구조를 나타낸 단면도이다.1 is a sectional view showing a composite waterproof structure of a concrete structure according to the present invention.
도 1에 도시된 바와 같이, 본 발명에 따른 콘크리트 구조물의 복합방수구조는 콘크리트 구조물(C) 상에 프라이머층(10), 연잎 추출물이 함유된 1차 도막방수제층(20), 섬유 포설층(30), 규조토 혼합 방수액층(40), 연잎 추출물이 함유된 2차 도막방수제층(50) 및 탑코트층(60)이 순차적으로 적층되어 이루어진다.1, a composite waterproof structure of a concrete structure according to the present invention includes a
도 2는 도 1에 도시된 콘크리트 구조물의 복합방수구조를 시공하는 방법을 나타낸 흐름도이다.2 is a flowchart illustrating a method of constructing a composite waterproof structure of the concrete structure shown in FIG.
먼저, 콘크리트 구조물(C)의 표면을 정리하고 청소한 후 프라이머층(10)을 형성하기 위해 콘크리트 구조물의 표면에 비닐아세테이트산 복합물로 된 프라이머(Primer)를 도포하는 단계(S10)로서, 상기한 비닐아세테이트산 복합물은 물에 용융하기 쉬운 성질로 인해 콘크리트 표면에 침투되는 수분에 의하여 용융되어 콘크리트 구조물 표면의 크랙을 따라가며 메워줄 수 있어 접착성이 우수하고 크랙의 추가 균열을 방지할 수 있게 된다. First, a step (S10) of applying a primer composed of a vinyl acetate acid complex to the surface of a concrete structure to form a
다음으로, 프라이머층(10)이 건조된 후 연잎 추출물이 함유된 도막방수제를 1차로 도포한다(S20). 상술한 바와 같이 본 발명에 따른 연잎 추출물이 함유된 도막방수제는 수용성 에틸렌비닐아세트산 기상공중합체 50 ~ 60중량%; 연잎 추출물 10 ~ 20중량%; 및 폴리부틸아크릴산 공중합체 20 ~ 30중량%를 포함하는 도막제 조성물로 형성되며, 고형분 함량 40 ~ 60%, 점도 5,000 ~ 10,000cps가 되도록 제조된 것을 사용하는 것이 작업성 및 부착성 측면에서 바람직하다.Next, after the
그리고 도포된 1차 도막방수제층 상부에는 PE나 PP사로 직조된 부직포를 포설하여 섬유 포설층(30)을 형성한다(S30). 이때 PE, PP사로 직조된 부직포의 일면은 UV 열처리되는 것이 바람직하다. 따라서 부직포의 일면은 UV 열처리에 의하여 기공이 줄고 조밀해져 타면에 비하여 매끄러움이나 평탄도, 인장강도가 증가하게 된다. Then, a non-woven fabric woven with PE or PP yarn is formed on the upper side of the applied primary coating film waterproofing agent layer to form a fiber laying layer 30 (S30). At this time, one side of the nonwoven fabric woven with PE or PP yarn is preferably subjected to UV heat treatment. Therefore, one side of the nonwoven fabric is reduced in pore size by UV heat treatment, and the smoothness, flatness and tensile strength of the nonwoven fabric are increased as compared with the other side.
이와 같이 섬유 포설층(30)의 일면이 UV 열처리됨으로써, 이후 섬유 포설층(30) 상부에 도포되는 방수제가 섬유 포설층(30)으로 침투하는 양이 줄어들게 된다. 이는 종래에 섬유 포설층(30) 상부에 도포되는 방수제가 섬유 포설층(30)으로 과도하게 함침됨으로써, 섬유 포설층(30)의 상면이 평탄하지 못하고 울퉁 불퉁하게 형성되어 방수구조의 파손이나 수분 침투 가능성을 높이는 문제점이 있었으므로, 본 발명에서는 섬유 포설층(30)에 사용되는 부직포의 일면을 열처리함으로써 이러한 문제를 해결하고 있다. As a result of the UV heat treatment on one side of the
다음으로, 상기 섬유 포설층(30) 상부에는 규조토가 혼합된 규조토 방수액을 추가 도포하여 포설된 섬유를 함침시킨다(S40). 규조토 혼합 방수액은 수용성 아크릴 에멀젼 수지, 규조토, 물을 각각 1 : 1 ~ 3 : 3 ~ 5의 중량비로 혼합하여 형성함이 바람직하다. 이와 같이 규조토 혼합 방수액을 포설된 섬유에 함침하여 건조시키면, 포설된 섬유 내의 기공 사이에 수용성 아크릴 에멀전 수지와 규조토 성분으로 구성된 규조토 혼합 방수액이 조밀하게 충진되어 강한 표면인장력을 갖게 되며며, 콘크리트 구조물의 균열의 추가 발생이나 부식을 예방할 수 있게 된다. Next, a diatomite waterproofing liquid mixed with diatomaceous earth is further applied on the
뿐만 아니라, 규산이 주성분이며 천연적으로 얻어지고 단열·내열성이 높아 난연재로 사용될 수 있는 규조토가 혼합됨으로써, 화재에도 유리하다.In addition, it is advantageous in fire by mixing diatomaceous earth which is mainly composed of silicic acid and is obtained naturally and can be used as flame retardant because heat and heat resistance are high.
규조토 혼합 방수액층(40)이 건조되면, 연잎 추출물이 함유된 도막방수제를 2차로 1 ~ 3회 도포하고 건조시키는 단계(S50)가 진행된다. 상기 도막방수제는 연잎 추출물이 함유됨으로써, 상술한 바와 같이 천연 소재가 사용됨에도 불구하고 소수성이 뛰어나 발수 및 방수 기능 구현에 탁월한 효과를 나타낼 수 있다. When the diatomite mixed
마지막으로, 수용성 아크릴 에멀젼 수지로 구성된 탑코트(Top-Coat)를 도포하는 단계(S60)로서, 상기 도막방수제 시공면에 0.3㎏/㎡의 양으로 코트재을 도포한 후 상온에서 24시간 이상 건조 양생시킨다. 상기 탑코트는 습도가 높은 곳에서도 건조가 빠른 속건형으로 작업성이 우수하며, 내후성, 내약품성, 전기절연성, 내수성, 광택성, 내마모성 등이 양호하고 인화성이 없고, 무독성(납, 크롬, 수은, 카드뮴 등 미포함)으로 환경친화적이며, 높은 고형분 용적비(약 40%, ASTM D2697, 7일간)을 가지므로 도장시 건조도막 두께가 두꺼워 내구성이 양호하다. 아울러 상기 탑코트는 색상발현이 가능하도록 무기 또는 유기안료를 추가적으로 포함함으로써 주변 구조물과의 색상을 자연스럽게 유지하고 수지 자체의 탈색이나 변색을 발생시키지 않으며, 그 사용량은 탑코트 전체중량을 기준으로 5중량부 이내로 하는 것이 도막의 강도 등 물성을 저하시키지 않는다.Finally, a step (S60) of applying a topcoat composed of a water-soluble acrylic emulsion resin was carried out by applying a coating material in an amount of 0.3 kg / m < 2 > to the surface of the coating film water repellent agent, . The topcoat is a quick drying type which is quick drying even in a high humidity and has excellent workability and is excellent in weather resistance, chemical resistance, electrical insulation, water resistance, gloss, abrasion resistance, etc. and is non-toxic (lead, chrome, mercury , Cadmium, etc.). It is environmentally friendly and has a high solids volume ratio (about 40%, ASTM D2697, 7 days). In addition, the top coat additionally contains inorganic or organic pigments to enable color development to naturally maintain the color with the surrounding structure and does not cause discoloration or discoloration of the resin itself. The amount of the top coat is preferably 5 wt% The physical properties such as the strength of the coating film do not deteriorate.
이러한 본 발명에 따라 시공된 복합방수구조는 연잎 추출물이 함유된 도막방수제에 의하여 환경 친화적일 뿐만 아니라 표면 장력이 증대되어 발수 성능이 극대화됨으로써, 콘크리트 구조물의 방수 기능 구현에 효과적이다. The composite waterproof structure constructed according to the present invention is environmentally friendly as well as maximized in water repellency by increasing the surface tension due to the coating water repellent agent containing the extract of the lotus leaf extract, thereby being effective in implementing the waterproof function of the concrete structure.
따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.Accordingly, the spirit of the present invention should not be construed as being limited to the embodiments described, and all of the equivalents or equivalents of the claims, as well as the following claims, belong to the scope of the present invention .
10 : 프라이머층 20 : 연잎 추출물이 함유된 1차 도막방수제층
30 : 포설 섬유층 40 : 규조토 방수액층
50 : 연잎 추출물이 함유된 2차 도막방수제층 60 : 탑코트층10: Primer layer 20: Primer coating water-repellent layer containing lotus leaf extract
30: laying fiber layer 40: diatomaceous earth waterproof layer
50: secondary coat water repellant containing lotus leaf extract layer 60: top coat layer
Claims (6)
상기 프라이머층 상부에 도포되는 연잎 추출물이 함유된 1차 도막방수제층;
상기 1차 도막방수제층 상부에 포설되는 섬유 포설층;
상기 섬유 포설층 상부에 도포되어 상기 섬유 포설층을 함침시키는 규조토 혼합 방수액층;
상기 규조토 혼합 방수액층 상부에 도포되는 연잎 추출물이 함유된 2차 도막방수제층; 및
상기 2차 도막방수제층 상부에 도포되는 탑코트층을 포함하며,
상기 섬유 포설층의 일면은 UV 열처리되며,
상기 연잎 추출물이 함유된 1차 및 2차 도막방수제층은,
수용성 에틸렌비닐아세트산 기상공중합체 50 ~ 60중량%;
연잎 추출물 10 ~ 20중량%; 및
폴리부틸아크릴산 공중합체 20 ~ 30중량%를 포함하는 도막제 조성물로 이루어지며,
상기 규조토 혼합 방수액층은 수용성 아크릴 에멀젼 수지, 규조토 및 물을 혼합하여 형성되는 것을 특징으로 하는 연잎 추출물이 함유된 수용성 도막방수제를 이용한 복합방수구조.
A primer layer formed by applying a primer composed of a vinyl acetate acid complex on the concrete structure;
A primary coating film water repellent agent layer containing a lotion extract applied to the top of the primer layer;
A fiber laying layer disposed above the primary coating film water repellent layer;
A diatomite mixed waterproofing liquid layer applied on the fiber laying layer to impregnate the fiber laying layer;
A second coating film water repellent layer containing a lotion extract applied to the top of the diatomite mixed waterproof layer; And
And a topcoat layer applied over the secondary coating film water repellent layer,
One side of the fiber laying layer is UV heat treated,
The first and second coating film water repellent layers,
50 to 60% by weight of a water-soluble ethylene vinyl acetate-based copolymer;
10 to 20% by weight of lotus leaf extract; And
And 20 to 30% by weight of a polybutylacrylic acid copolymer,
Wherein the diatomite mixed waterproofing liquid layer is formed by mixing a water-soluble acrylic emulsion resin, diatomaceous earth and water.
상기 프라이머층의 상부에 연잎 추출물이 함유된 도막방수제를 1차로 도포하는 단계;
도포된 상기 1차 도막방수제층 상부에 PE나 PP사로 직조된 부직포를 포설하여 섬유 포설층을 형성하는 단계;
상기 섬유 포설층 상부에 규조토가 혼합된 규조토 방수액을 추가 도포하여 포설된 섬유를 함침시키는 단계;
상기 연잎 추출물이 함유된 도막방수제를 2차로 1 ~ 3회 도포하고 건조시키는 단계; 및
수용성 아크릴 에멀젼 수지로 구성된 탑코트(Top-Coat)를 도포하는 단계;를 포함하며,
상기 부직포의 일면은 UV 열처리되며,
상기 연잎 추출물이 함유된 도막방수제는,
수용성 에틸렌비닐아세트산 기상공중합체 50 ~ 60중량%;
연잎 추출물 10 ~ 20중량%; 및
폴리부틸아크릴산 공중합체 20 ~ 30중량%를 포함하는 도막제 조성물로 이루어지며,
상기 규조토 혼합 방수액층은 수용성 아크릴 에멀젼 수지, 규조토 및 물을 혼합하여 형성되는 것을 특징으로 하는 콘크리크 구조물용 복합방수구조의 시공방법.
Applying a primer composed of a vinyl acetate acid complex to the surface of the concrete structure so as to form a primer layer after cleaning and cleaning the surface of the concrete structure;
Coating a coating film water repellent agent containing a lotion extract on the top of the primer layer first;
Forming a fiber laying layer by laying a nonwoven fabric woven with PE or PP yarn on the coated primary coating film waterproofing agent layer;
Further comprising the step of applying a diatomite waterproofing liquid mixed with diatomaceous earth to the upper part of the fiber laying layer to impregnate the laid fibers;
Applying the coating water repellent agent containing the extract of the lotus leaf extract to the substrate twice or three times, and drying the coating; And
Applying a topcoat comprised of a water-soluble acrylic emulsion resin,
One side of the nonwoven fabric is subjected to UV heat treatment,
The coating film water repellent agent containing the lotion extract,
50 to 60% by weight of a water-soluble ethylene vinyl acetate-based copolymer;
10 to 20% by weight of lotus leaf extract; And
And 20 to 30% by weight of a polybutylacrylic acid copolymer,
Wherein the diatomite mixed waterproofing liquid layer is formed by mixing a water-soluble acrylic emulsion resin, diatomaceous earth, and water.