KR101354533B1 - The method for preparing of jewel lighting panel - Google Patents
The method for preparing of jewel lighting panel Download PDFInfo
- Publication number
- KR101354533B1 KR101354533B1 KR1020120089006A KR20120089006A KR101354533B1 KR 101354533 B1 KR101354533 B1 KR 101354533B1 KR 1020120089006 A KR1020120089006 A KR 1020120089006A KR 20120089006 A KR20120089006 A KR 20120089006A KR 101354533 B1 KR101354533 B1 KR 101354533B1
- Authority
- KR
- South Korea
- Prior art keywords
- panel
- jewelry
- epoxy resin
- jewel
- beads
- Prior art date
Abstract
Description
본 발명은 장식물의 제조방법에 관한 것으로서, 보다 상세하게는 실내건물 천정, 벽체, 바닥가구, 가전제품장식등, 벽걸이액자 및 여러 부분 직,간접 장식등에 사용하는 보석조명판넬의 제조방법 에 관한 것이다.
The present invention relates to a method for manufacturing a decoration, and more particularly, to a method for manufacturing a jewelry lighting panel for use in indoor building ceilings, walls, floor furniture, home appliance decorations, wall hanging frames, and various direct and indirect decorations. .
종래에는 장식등에서 나오는 빛을 그대로 사용하면서 장식등 외관의 모양, 색채, 형상 및 이들의 결합에 의해 심미감을 더해주는 것이 통상적이었다. 또한, 종래에는 장식등에 실제 설치된 전등의 수의 배수로 점등이 되도록 하여 보다 입체적으로 보이거나 하여 종래에는 단순히 미적향상을 위하여 독특한 아이디어로 색상을 달리하거나, 장식기법을 도입하여 특이하게 장식물을 장식하여 왔다.Conventionally, it is common to add aesthetics by the shape, color, shape, and combination of the appearance of the decoration lamp while using the light from the decoration lamp as it is. In addition, in the past, the lighting is turned on in multiples of the number of lamps actually installed in the decoration lamp, which may be more three-dimensional, and in the past, simply decorate a decoration by changing the color with a unique idea or introducing a decoration technique for aesthetic improvement. .
예를 들면, 국내등록특허공보 등록번호 제1003589000000 (20021016)호에는 양면 접착테이프(1)에 양면에 이형지(3)를 붙인 다음, 이형지(3) 뒷면에 모양의 밑그림을 그린 후, 그림선을 따라 잘라내어 모양을 형성한 다음, 한쪽 이형지(3)를 떼어내어 원적외선을 방출하는 자연석(자갈이나, 천연옥) 및 조개껍질 및 나무뿌리 등을 장식을 하면서 접착층(2)에 붙인 후, 수지를 붓으로 칠하여 수지층(6)을 형성한 다음, 완전경화가 되기 전에 또 다른 이형지(3)를 떼어내어 원하는 장식물(5)의 표면에 붙인 후, 건조실에서 열풍으로 건조실의 온도를 60~80 상태에서 2시간 건조시킨 다음 장식물(5)에서 탈락시켜 제조함을 특징으로 하는 원적외선 장식물의 제조방법 및 조명등갓 장식물이 공개되어 있으며, For example, in Korean Patent Publication No. 1003589000000 (20021016), a release paper (3) is attached to both sides on a double-sided adhesive tape (1), and then a drawing line is drawn on the back surface of the release paper (3), and a drawing line is drawn. After cutting along to form a shape, remove one release paper (3) and attach it to the adhesive layer (2) while decorating the natural stone (gravel, natural jade) and shells and tree roots that emit far infrared rays, and then apply the resin with a brush. Paint to form the
국내등록실용신안공보 등록번호 제20-168525호에는 장식기능과 아울러 효과적인 방향 기능을 겸하는 부착용장식물이 기재되어 있으며,Registered Utility Model Registration No. 20-168525 describes attachments for both decorative and effective directional functions.
동 공보 제20-177969호에는 팔각기둥, 동물 조류, 건축 등의 형상으로 된 몸체 상면에 투명수정구가 안착되도록 반구홈을 형성하고 반구홈 내에는 불경 등이 인쇄된 인쇄물이 삽입될 수 있는 요홈을 형성시킨 장식물과, Publication No. 20-177969 has a recess in which a hemispherical groove is formed on the upper surface of the body in the shape of an octagonal pillar, an animal bird, or a building, and a printed material printed with a recession can be inserted in the hemisphere groove. With the ornament which I formed,
동 공보 제20-183287호에는 틀재의 내측면과 외측면에 도배지 은폐홈과 천장판에 맞추어 못으로 틀재를 천장구조물에 부착하기 위한 취부용 돌출리브를 각각설치하고, 틀재의 대응하는 연결모서리 등으로 구성된 조립식 천장 장식물이기재되어 있으며,In Publication No. 20-183287, a protruding rib for attaching the frame member to the ceiling structure with nails is provided on the inner side and the outer side of the frame, respectively, and the corresponding connecting edges of the frame are provided. Prefabricated ceiling fixtures,
특허공보 공고번호 특1991-5425호에는 폐유리자재를 이용하여 장식성과 내구성이 극히 양호한 유리타일의 제조방법이 기재되어 있고,Patent Publication No. 1991-5425 describes a method for producing a glass tile having extremely high decoration and durability using waste glass materials.
동 공보 공고번호 제76-482호에는 무늬를 투사시킨 유리판상에 시멘트 모르타르를 튜브로 압출하여 해당무늬 모양의 구획돌조를 간설케하고, 구획돌조에 의하여 간설된 함입부에 공지의 방법에 따라 유색모르타르를 충입하여 경화시킨 무늬판표층을 연마하여서 된 장식용 타일의 제조방법이 공개되어 있음을 알 수 있다.
Publication No. 76-482 discloses that a cement mortar is extruded into a tube on a glass plate on which a pattern is projected, so as to enclose a partition block of a corresponding pattern shape, and to color the indentation formed by the partition block according to a known method. It can be seen that a method for producing a decorative tile obtained by polishing a patterned surface layer filled with mortar and cured is disclosed.
종래의 조명판넬은 아름다운 빛을 발현하기 위한 장식의 효과를 이용하였을 뿐 보석과, 배경의 여백용 불투명안료에폭시수지층에 의한 엘이디판넬을 부착시켜 아름다운 빛을 발산하는 조명판넬을 실현하지 못하는 문제점이 본 발명이 해결하고자 하는 과제인 것이다.
Conventional lighting panels use the effect of decoration to express beautiful light, but the problem of failing to realize the lighting panel that emits beautiful light by attaching the LED and the LED panel by the epoxy resin layer to the opaque pigment for the margin of the background. The present invention is to be solved.
본 발명은 상기 문제점을 해결 하고자, 본 출원인이 선출원한 특허출원번호 제10-2000-34376호, 발명의 명칭 원적외선 장식물의 제조방법, 및 특허출원번호 제10-2005-0013569(등록번호; 100616249) 발명의 명칭; 장식물의 제조방법, 실용신안등록출원번호 제20-2000-0017734 및 조명등갓 장식물을 개량 한 것으로서, 본 발명은 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에 1mm 두께 되도록 적층시킨 후 80 에서 40분정도 경화시켜 보석판넬을 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 접착 및 고정시킨 보석조명판넬의 제조방법 을 제공하는 것이 본 발명의 과제해결 수단인 것이다.
The present invention, in order to solve the above problems, the patent application No. 10-2000-34376 filed by the applicant of the present invention, the name of the invention manufacturing method of far-infrared decoration, and patent application No. 10-2005-0013569 (registration number; 100616249) The name of the invention; The manufacturing method of the decoration, utility model registration application No. 20-2000-0017734 and the lighting lampshade decoration is improved, the present invention is decorated with jewelry, jewelry beads so as not to overlap the upper portion of the light transmitting layer (that is, jewelry, After decorating with jewel beads and laminating them to other parts (margin) of the light transmitting layer to 1mm thickness, curing them for 80 to 40 minutes and then jewel panel is bonded and fixed on acrylic light panel such as LED light panel, light guide plate or LED part . It is a problem solving means of the present invention to provide a manufacturing method .
본 발명은 천연보석의 신비한 색상과 천연보석에 휘절된 빛과 보석의 색깔이 어우러져, 아름답고 영롱함이 엘이디 광원에 투과되어 고품격 감성 의 빛으로 심신의 안정감을 누릴 수 있으며 에너지절약과 얇고, 가벼워 경제성과 실용성으로 건축인테리어조명 및 여러 부분 직,간접 조명장식 등으로 활용 할 수 있는 효과와 경제적인 장점이 있는 것이다.
The present invention is a combination of the mysterious color of natural gemstones and the color of gemstones and natural gemstones, the beautiful and brilliant is transmitted through the LED light source, you can enjoy the sense of mind and body with high-quality emotional light, energy saving and thin, light and economical With practicality, it has the effect and economic advantage that can be utilized for architectural interior lighting, various parts direct and indirect lighting decoration.
도1 본 발명의 보석조명판넬 전체도
도2 본 발명의 보석조명판넬 상세도
도3 본 발명의 보석조명판넬을 이용한 장식조명 판넬 상세도1 is a view of the entire jewelry lighting panel of the present invention
2 is a detailed view of a jewelry lighting panel of the present invention
3 is a detailed view of a decorative lighting panel using a jewelry lighting panel of the present invention
상기와 같은 목적을 달성하기 위하여, 본 발명은 실내건물 천정 .벽체. 바닥 . 가구 .가전제품장식등 . 벽걸이액자, 여러 부분 간접 장식등에 사용되며, 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 적층시킨 후 80 에서 40분정도 경화시켜 보석판넬을 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 접착 및 고정시킨 보석조명판넬의 제조방법 에 관한 것이다.
In order to achieve the above object, the present invention is an indoor building ceiling. floor . Furniture, home appliances and decorations Used for wall hanging frame, indirect decoration of various parts, and decorated with jewels, jewelry beads so that they do not overlap on the upper part of the light transmitting layer (that is, decorated with jewels, jewelry beads, and other parts of the light transmitting layer (margin)) The present invention relates to a method of manufacturing a jewelry lighting panel in which a jewelry panel is bonded and fixed to an acrylic plate such as an LED light panel, a light guide plate, or an LED fabric by curing the laminate to a thickness of about 80 to 40 minutes.
본 발명의 보석판넬에 사용되는 보석장식, 보석구슬은 투명하거나 반투명한 천연보석. 자수정. 수정 .마노. 옥돌 .자연석, 유리구슬 . 자개 .기타 미적소재 등을 슬라이스 절단 및 구슬 .자갈. 문양 가공 연마하여 에폭시나 우레탄 수지에 접착하여 제조된다.Jewelry decoration used in the jewelry panel of the present invention, jewelry beads are transparent or translucent natural gemstones. amethyst. Crystal. Agate. Jade stone, natural stone, glass beads. Mother-of-Pearl .Other aesthetic materials such as slice cutting and beads .Pebbles. It is manufactured by attaching to epoxy or urethane resin by pattern processing polishing.
또 보석판넬을 엘이디 라이트패널 도광판 및 직부등 아크릴에 접착 하여 제조된 보석조명판넬의 제조방법 에 관한 것이다.The present invention also relates to a method of manufacturing a jewelry lighting panel manufactured by bonding a jewelry panel to an acrylic, such as an LED light panel, a light guide plate, and a straight portion.
본 발명에서 사용되는 수지는 접착의 효과와, 경화 후의 미려한 광택의 효과가 있는 통상의 수지를 사용한 것으로서, As the resin used in the present invention, ordinary resin having the effect of adhesion and the effect of beautiful gloss after curing is used.
에폭시계 또는 우레탄계수지계 수지가 사용되며, 에폭시수지가 더 바람직하다. Epoxy or urethane resins are used, and epoxy resins are more preferred.
또 바탕에 적층되는 수지는 숯분말, 황토분말, 옥분말 및 안료에서 선택된 어느 하나의 화합물과 수지를 혼합하여 사용할 수 있다.In addition, the resin laminated on the ground may be used by mixing any one compound and resin selected from charcoal powder, ocher powder, jade powder and pigment.
제조방법은Manufacturing method
1 . 이형판 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,One . After installing the light transmitting layer on the upper part of the release board with jewels and jewelry beads,
3. 상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화(건조)시켜 투명 에폭시 수지층을 형성한 다음, 3. Decorate with jewelery, jewelery beads and pour epoxy resin to the top of the light transmitting layer 1mm thick to cure (dry) at 60 ℃ ~ 70 ℃ 1 hour to form a transparent epoxy resin layer,
4 . 에폭시수지 100 g과 숯분말, 황토분말, 옥분말, 자수정분말 및 안료에서 선택된 어느 하나의 분말 20 g을 혼합 하여 불투명안료에폭시수지 를 보석장식, 보석구슬로 장식한 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 여백용 불투명안료에폭시수지층 을 형성하되 1mm 두께 되도록 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화(건조)시켜 보석판넬을 제조한 후에,4 . 100 g of epoxy resin and 20 g of any powder selected from charcoal powder, ocher powder, jade powder, amethyst powder and pigments are mixed so that the opaque pigment epoxy resin is not overlapped on top of the light transmitting layer decorated with jewelery or gem beads. Form an opaque pigment epoxy resin layer for the margin (ie, decorate with jewelery, jewelery beads, and other parts of the light transmitting layer ) and laminate it to 1mm thickness, and then cure at 60 ℃ ~ 70 ℃ for 1 hour (dry). After making the jewelry panel,
5 이형판 형틀에서 보석판넬을 때어낸 다음,5 Remove the jewel panel from the mold release frame,
엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 보석판넬을 접착및 고정시켜 보석조명판넬을 제조하였다. (엘이디라이트패널 . 엘이디 직부등 아크릴판은 일반적으로 시중에 유통되는 것을 사용한다.)
A jewelry lighting panel was manufactured by bonding and fixing a jewelry panel to an acrylic plate such as an LED light panel, a light guide plate, or an LED portion. (LED light panel. Acrylic boards such as LED direct printing are generally used in the market.)
다른 제조방법은Other manufacturing methods
1. 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판의 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,1. After installing the light transmissive layer by decorating with jewelery or jewelry beads on the upper part of the acrylic light panel such as LED light panel or LED part,
3. 상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화(건조)시켜 투명 에폭시 수지층을 형성한 다음, 3. Decorate with jewelery, jewelery beads and pour epoxy resin to the top of the light transmitting layer 1mm thick to cure (dry) at 60 ℃ ~ 70 ℃ 1 hour to form a transparent epoxy resin layer,
4 . 에폭시수지 100 g과 숯분말, 황토분말, 옥분말, 자수정분말 및 안료에서 선택된 어느 하나의 분말 20 g을 혼합 하여 불투명안료에폭시수지 를 보석장식, 보석구슬로 장식한 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 여백용 불투명안료에폭시수지층 을 형성하되 1mm 두께 되도록 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석조명판넬을 제조하였다.
4 . 100 g of epoxy resin and 20 g of any powder selected from charcoal powder, ocher powder, jade powder, amethyst powder and pigments are mixed so that the opaque pigment epoxy resin is not overlapped on top of the light transmitting layer decorated with jewelery or gem beads. Form an opaque pigment epoxy resin layer for margins (ie, decorate with jewelery, jewelery beads, and other parts of the light-transmitting layer ), laminate it to 1mm thickness, and harden it at 60 ℃ ~ 70 ℃ for 1 hour. The lighting panel was prepared.
기타 상기 보석조명판넬의 테두리에 "ㄷ" 자형 알미늄바 안에 엘이디스틱바를 접착 엘이디 도광판 과 보석조명판넬 접착 결합하여 엘이디스틱 전구에 두께면이 일치되도록 하여 알미늄바 또는 액자타입 틀에 조립하여 장식조명판넬을 제조하였다.
Others The LED light bar and the LED light guide panel are bonded to the edge of the jewel light panel by the LED light guide plate and the jewel light panel. The thickness of the LED light bulb is matched to the aluminum bar or the frame type frame to assemble the decorative light panel. Was prepared.
이하 본 발명을 실시예를 통하여 상세히 설명하면 다음과 같다.
Hereinafter, the present invention will be described in detail with reference to examples.
실시예1Example 1
이형판 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,After installing the light transmitting layer on the upper part of the release board with jewels and jewelry beads,
상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음, After decorating with jewels, jewelry beads and poured an epoxy resin so that the thickness of the light transmitting layer 1mm on the upper part 1 hour to cure at 60 ℃ ~ 70 ℃ to form a transparent epoxy resin layer,
에폭시수지100 g 과 숯분말 20 g을 혼합 하여 혼합된 불투명안료에폭시수지 를 보석장식, 보석구슬로 장식한 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 여백용 불투명안료에폭시수지층 을 적층시킨 후 60℃ ~ 70℃ 에서 1시간 경화시켜 보석판넬을 제조한 후에, 이형판 형틀에서 보석판넬을 때어낸 다음, 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 보석판넬을 접착 및 고정시켜 보석조명판넬을 제조하였다.
100 g of epoxy resin and 20 g of charcoal powder are mixed so that the mixed opaque epoxy resin does not overlap the upper part of the light transmitting layer decorated with jewelery or jewelry beads (i.e., decorated with jewelery or jewelry beads, After laminating the opaque pigment epoxy resin layer for the margin to 1mm thickness to another part (margin) and curing for 1 hour at 60 ℃ ~ 70 ℃ , the jewelry panel was removed from the mold, and then the LED was removed. A jewelry lighting panel was manufactured by bonding and fixing a jewelry panel to an acrylic panel such as a light panel light guide plate or an LED portion.
실시예2Example 2
엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판의 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 살치한 후에,After decorating the light transmissive layer by decorating the upper part of the acrylic light panel such as LED light panel or LED part with jewels and jewelry beads,
상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음, After decorating with jewels, jewelry beads and poured an epoxy resin so that the thickness of the light transmitting layer 1mm on the upper part 1 hour to cure at 60 ℃ ~ 70 ℃ to form a transparent epoxy resin layer,
에폭시수지100 g 과 황토분말 20 g을 혼합 하여 혼합된 불투명안료에폭시수지를 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 여백용 불투명안료에폭시수지층을 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석조명판넬을 제조하였다.
100 g of epoxy resin and 20 g of ocher powder are mixed to decorate the opaque pigment epoxy resin mixed with jewels and jewelry beads so that they do not overlap on top of the light transmitting layer (ie, jewels and jewelry beads On the other part (margin)) after laminating the opaque pigment epoxy resin layer for margin to 1mm thick, it was cured at 60 ℃ ~ 70 ℃ 1 hour to prepare a jewelry lighting panel.
실시예3Example 3
이형판 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,After installing the light transmitting layer on the upper part of the release board with jewels and jewelry beads,
상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음, After decorating with jewels, jewelry beads and poured an epoxy resin so that the thickness of the light transmitting layer 1mm on the upper part 1 hour to cure at 60 ℃ ~ 70 ℃ to form a transparent epoxy resin layer,
에폭시수지100 g 과 옥분말 20 g을 혼합 하여 혼합된 불투명안료에폭시수지를 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 여백용 불투명안료에폭시수지층을 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석판넬을 제조한 후에,100 g of epoxy resin and 20 g of jade powder are mixed and the opaque pigment epoxy resin is mixed with jewels and jewelry beads so as not to overlap the upper part of the light transmitting layer (i.e., jewels and jewelry beads After laminating the opaque pigment epoxy resin layer for the margin to 1 mm thick in another part (margin), and cured at 60 ° C ~ 70 ° C for 1 hour to prepare a jewelry panel,
이형판 형틀에서 보석판넬을 때어낸 다음, 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 보석판넬을 접착 및 고정시켜 보석조명판넬을 제조하였다.
After the jewelry panel was removed from the mold of the release plate, the jewelry panel was manufactured by bonding and fixing the jewelry panel to an acrylic plate such as an LED light panel, a light guide plate, or an LED fabric.
실시예4Example 4
엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판의 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 살치한 후에,After decorating the light transmissive layer by decorating the upper part of the acrylic light panel such as LED light panel or LED part with jewels and jewelry beads,
상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음, After decorating with jewels, jewelry beads and poured an epoxy resin so that the thickness of the light transmitting layer 1mm on the upper part 1 hour to cure at 60 ℃ ~ 70 ℃ to form a transparent epoxy resin layer,
에폭시수지100 g 과 자수정분말 20 g을 혼합 하여 혼합된 불투명안료에폭시수지를 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 여백용 불투명안료에폭시수지층을 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석조명판넬을 제조하였다.
100 g of epoxy resin and 20 g of amethyst powder are mixed to decorate the opaque pigment epoxy resin with jewels and jewelry beads so that they do not overlap on top of the light transmission layer (i.e., jewels and jewelry beads On the other part (margin)) after laminating the opaque pigment epoxy resin layer for margin to 1mm thick, it was cured at 60 ℃ ~ 70 ℃ 1 hour to prepare a jewelry lighting panel.
실시예 5Example 5
이형판 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,After installing the light transmitting layer on the upper part of the release board with jewels and jewelry beads,
상기 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음, After decorating with jewels, jewelry beads and poured an epoxy resin so that the thickness of the light transmitting layer 1mm on the upper part 1 hour to cure at 60 ℃ ~ 70 ℃ to form a transparent epoxy resin layer,
에폭시수지100 g 과 코발트안료 20g을 혼합 하여 혼합된 불투명안료에폭시수지층를 보석장식, 보석구슬로 장식하여 빛 투과층의 상부에 겹치지 않도록(즉, 보석장식, 보석구슬로 장식하여 빛 투과층의 다른 부분(여백)에) 1mm 두께 되도록 여백용 불투명안료에폭시수지층을 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석판넬을 제조한 후에,100 g of epoxy resin and 20 g of cobalt pigment are mixed to decorate the mixed opaque pigment epoxy resin layer with jewels and jewelry beads so that they do not overlap the upper part of the light transmission layer (ie After laminating an opaque pigment epoxy resin layer for margins to a thickness of 1 mm in the part (margin), and cured at 60 ℃ ~ 70 ℃ for 1 hour to prepare a jewelry panel,
이형판 형틀에서 보석판넬을 때어낸 다음, 엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 보석판넬을 접착 및 고정시켜 보석조명판넬을 제조하였다.
After the jewelry panel was removed from the mold of the release plate, the jewelry panel was manufactured by bonding and fixing the jewelry panel to an acrylic plate such as an LED light panel, a light guide plate, or an LED fabric.
실시예6Example 6
상기 실시예 1 내지 5로 제조된 보석조명판넬의 테두리에 "ㄷ" 자형 알미늄바 안에 엘이디스틱바를 접착 엘이디 도광판 과 보석조명판넬 접착 결합하여 엘이디스틱 전구에 두께면이 일치되도록 하여 알미늄바 또는 액자타입 틀에 조립하여 장식조명판넬을 제조하였다.
Bonding the LED bar in the "테두리" shaped aluminum bar on the rim of the jewel light panel manufactured in Examples 1 to 5 by bonding the LED light guide plate and the jewel light panel adhesive to match the thickness of the aluminum bulb or frame type Assembled in the frame to prepare a decorative lighting panel.
이하 도면을 참고하여 설명하면 다음과 같다.Hereinafter, a description will be made with reference to the drawings.
도1 본 발명의 보석조명판넬 전체도, 도2 본 발명의 보석조명판넬 상세도, 도3 본 발명의 보석조명판넬을 이용한 장식조명 판넬 상세도를 도시한 것이며, 엘이디 라이트 패널도광판(1), 빛투과층(3), 에폭시수지층(4), 여백용 불투명안료에폭시수지층(5), "ㄷ" 자형 알미늄바(6)을 나타낸 것임을 알 수 있다.
1 is a view showing the entire jewelry lighting panel of the present invention, Figure 2 is a detailed view of the jewelry lighting panel of the present invention, Figure 3 is a detailed view of the decorative lighting panel using the jewelry lighting panel of the present invention, LED light panel light guide plate (1), It can be seen that the light transmitting layer (3), the epoxy resin layer (4), the opaque pigment epoxy resin layer (5) for the margin, the "c" shaped aluminum bar (6).
구조를 살펴보면, 본 발명의 보석조명판넬은 도1 및 도2에 도시된 바와 같이, Looking at the structure, the jewelry lighting panel of the present invention, as shown in Figures 1 and 2,
삭제delete
하부에 설치된 엘이디 라이트 패널도광판(1)과, 상기 엘이디라이트패널도광판(1)의 상부에 보석으로 장식된 빛투과층(3)과, 상기 빛투과층(3)의 상부에 설치된 투명 에폭시수지층(4), 상기 투명에폭시수지층(4)의 상부이며 빛투과층(3)을 제외한 여백에 적층되며 숯분말, 황토분말, 옥분말, 자수정분말 및 안료에서 선택된 어느 하나의 분말을 사용한 여백용 불투명안료에폭시수지층(5)으로 구성된 보석조명판넬임을 알 수 있다.
The LED light panel LGP 1 provided at the lower part, the light transmitting layer 3 decorated with gems on the LED light panel LGP 1, and the transparent epoxy resin layer formed on the light transmitting layer 3. (4), the upper part of the transparent epoxy resin layer (4) and laminated on the margin except the light transmitting layer (3) for the margin using any powder selected from charcoal powder, ocher powder, jade powder, amethyst powder and pigment It can be seen that the jewelry lighting panel composed of an opaque pigment epoxy resin layer (5).
도3은 본 발명의 장식조명판넬을 도시한 것으로서,Figure 3 shows a decorative lighting panel of the present invention,
상기 도1의 보석조명판넬 테두리에 설치된 "ㄷ" 자형 알미늄바가 더추가되어 있음을 특징으로 하는 장식조명판넬의 구조인 것이다.1 is a structure of a decorative lighting panel, characterized in that the "c" shaped aluminum bar installed on the edge of the jewelry lighting panel is further added.
실험예(관능검사)
Experimental Example (Sensory Test)
본 발명의 실시예1에서 제조된 보석조명판넬을 종래의 조명판넬과 비교하여 40~50대의 20명을 대상으로 하여 관능검사를 실시하였다. 관능검사는 기호도 등에 대해 실시하였다. The jewelry lighting panel prepared in Example 1 of the present invention was compared with a conventional lighting panel, and the sensory test was conducted for 20 people in their 40s to 50s. Sensory tests were conducted on preference.
보석조명판넬Example 1
Jewelry lighting panel
관능평점 - 1 : 아주 나쁘다, 아주 불편하다Sensory rating - 1: Very bad, very uncomfortable
2 : 나쁘다, 불편하다2: bad, inconvenient
3 : 보통이다3: It is normal.
4 : 좋다, 불편함이 심하다4: Good, inconvenient.
5 : 아주 좋다, 아주 불편하다.5: very good, very uncomfortable.
관능검사결과 본 발명 실시예1의 보석조명판넬의 전체적인 느낌이 종래의 조명판넬보다 편안하고 아름답게 보여 심리적으로 안정감을 갖게 하였다.
As a result of the sensory test, the overall feeling of the jewelry lighting panel of Example 1 of the present invention was shown to be more comfortable and beautiful than the conventional lighting panel, thereby providing psychological stability.
엘이디 라이트 패널도광판(1), 빛투과층(3), 투명 에폭시수지층(4), 여백용 불투명안료에폭시수지층(5), "ㄷ" 자형 알미늄바(6).An LED light panel light guide plate (1), a light transmitting layer (3), a transparent epoxy resin layer (4), an opaque pigment epoxy resin layer (5) for margins, and a "c" shaped aluminum bar (6).
Claims (4)
이형판 상부에 보석장식, 보석구슬로 장식하여 빛 투과층을 설치한 후에,
상기 보석장식, 보석구슬로 장식한 빛 투과층의 상부에 1mm 두께 되도록 에폭시수지를 부어 60℃ ~ 70℃ 에서 1시간 경화시켜 투명 에폭시 수지층을 형성한 다음,
에폭시수지100 g 과 숯분말, 옥분말, 자수정분말 및 안료에서 선택된 어느 하나의 분말 20 g을 혼합 하여 혼합된 불투명안료에폭시수지 를 보석장식, 보석구슬로 장식한 빛 투과층의 상부에 겹치지 않도록 1mm 두께 되도록 여백용 불투명안료에폭시수지층 을 적층시킨 후, 60℃ ~ 70℃ 에서 1시간 경화시켜 보석판넬을 제조한 후에, 이형판 형틀에서 보석판넬을 때어낸 다음,
엘이디 라이트 패널도광판 이나 엘이디직부등 아크릴판에 보석판넬을 접착 및 고정시켜 제조함을 특징으로 하는 보석조명판넬의 제조방법.In the method of manufacturing a jewel lighting panel,
After installing the light transmitting layer on the upper part of the release board with jewels and jewelry beads,
The epoxy resin is poured into the upper portion of the light transmitting layer decorated with jewelery and jewelery beads to be 1 mm thick, and cured at 60 ° C. to 70 ° C. for 1 hour to form a transparent epoxy resin layer.
100 mm of epoxy resin and 20 g of any powder selected from charcoal powder, jade powder, amethyst powder and pigment are mixed so that the mixed opaque pigment epoxy resin is not overlapped on top of the light transmitting layer decorated with jewelery or jewelry beads. After laminating the epoxy resin layer for the margin opaque pigment to a thickness, and cured for 1 hour at 60 ℃ ~ 70 ℃ to prepare a jewel panel, and then peel off the jewel panel in a mold release mold,
LED light panel A method of manufacturing a jewelry lighting panel, characterized in that the manufacturing by adhering and fixing the jewelry panel to the acrylic plate, such as light guide plate or LED direct portion.