KR101276497B1 - Insert mold transcription film having improved contamination resistance and method for fabricating the same - Google Patents

Insert mold transcription film having improved contamination resistance and method for fabricating the same Download PDF

Info

Publication number
KR101276497B1
KR101276497B1 KR1020110033335A KR20110033335A KR101276497B1 KR 101276497 B1 KR101276497 B1 KR 101276497B1 KR 1020110033335 A KR1020110033335 A KR 1020110033335A KR 20110033335 A KR20110033335 A KR 20110033335A KR 101276497 B1 KR101276497 B1 KR 101276497B1
Authority
KR
South Korea
Prior art keywords
layer
poly
hard coating
coating layer
transfer film
Prior art date
Application number
KR1020110033335A
Other languages
Korean (ko)
Other versions
KR20120115803A (en
Inventor
이명진
이승훈
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020110033335A priority Critical patent/KR101276497B1/en
Publication of KR20120115803A publication Critical patent/KR20120115803A/en
Application granted granted Critical
Publication of KR101276497B1 publication Critical patent/KR101276497B1/en

Abstract

본 발명은 내오염성이 우수한 인서트 몰드 전사 필름 및 이를 제조하는 방법에 관한 것으로, 기재필름 상부에 이형층을 형성하는 단계와, 상기 이형층 상부에 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층을 형성하는 단계와, 상기 제1하드코팅층 상부에 제2하드코팅층을 형성하는 단계와, 상기 제2하드코팅층 상부에 인쇄층을 형성하는 단계와, 상기 인쇄층 상부에 프라이머층을 형성하는 단계 및 상기 프라이머층 상부에 접착층을 형성하는 단계를 포함하여, 최상부 하드코팅층인 제1하드코팅층이 불소 함유 아크릴계 중합체를 포함하고 있어서 그 표면부가 내인공땀 효과와 같은 내오염성이 우수한 효과를 구현하는 것을 특징으로 한다.The present invention relates to an insert mold transfer film having excellent stain resistance and a method of manufacturing the same, forming a release layer on the base film, and forming a first hard coating layer including a fluorine-containing acrylic polymer on the release layer. And forming a second hard coating layer on the first hard coating layer, forming a printing layer on the second hard coating layer, forming a primer layer on the printing layer, and the primer. Including the step of forming an adhesive layer on the upper layer, the first hard coating layer, which is a top hard coating layer comprises a fluorine-containing acrylic polymer, the surface portion is characterized in that the effect of excellent pollution resistance such as artificial sweat effect .

Description

내오염성이 우수한 인서트 몰드 전사 필름 및 이를 제조하는 방법{INSERT MOLD TRANSCRIPTION FILM HAVING IMPROVED CONTAMINATION RESISTANCE AND METHOD FOR FABRICATING THE SAME}Insert mold transfer film excellent in stain resistance and a method for manufacturing the same {INSERT MOLD TRANSCRIPTION FILM HAVING IMPROVED CONTAMINATION RESISTANCE AND METHOD FOR FABRICATING THE SAME}

본 발명은 내오염성이 우수한 인서트 몰드 전사 필름 및 이를 제조하는 방법 에 관한 것으로서, 더욱 상세하게는 인서트 몰드 전사 필름의 하드코팅층 최상부에 불소를 함유하는 아크릴계 중합체가 포함된 하드코팅층을 더 적층하여 내오염성이 우수한 인서트 몰드 전사 필름을 제조하는 기술에 관한 것이다.
The present invention relates to an insert mold transfer film having excellent stain resistance and a method of manufacturing the same, and more particularly, to a top layer of the hard coat layer of the insert mold transfer film, in which a hard coating layer containing an acrylic polymer containing fluorine is further laminated. A technique for producing this excellent insert mold transfer film.

일반적으로 휴대폰 등과 같은 소형 전자제품의 케이스는 합성수지재로 사출성형하여 사출물로 제작하게 되며, 이러한 휴대폰 케이스 등의 사출물은 표면을 보호하거나 미려하게 하기 위해 UV코팅 또는 인쇄필름을 코팅 한다.In general, a case of a small electronic product such as a mobile phone is manufactured by injection molding by using a synthetic resin material, the injection molding such as a mobile phone case is coated with a UV coating or a printing film to protect the surface or beauty.

한편, 휴대폰이나 노트북 등 사용자의 터치가 많은 제품을 생산하게 되면서 그 외관에 내지문성, 내인공땀 등 내오염성 기능이 부여된 제품의 수요가 늘어나고 있다.On the other hand, as the production of a user's touch, such as a mobile phone or a laptop has increased the demand for products that are given a stain-resistant function, such as fingerprint resistance, artificial sweat on the appearance.

그러나, 종래 인서트 몰드 전사 필름의 하드코팅층은 상기와 같은 내지문성, 내인공땀 효과 등이 부족하여 도막이 손상되는 등의 문제점이 있다.
However, the hard coating layer of the conventional insert mold transfer film has a problem such that the coating film is damaged due to lack of the above fingerprint resistance, artificial sweat effect and the like.

본 발명은 전사필름의 표면부에 내인공땀 효과와 같은 내오염성을 개선하기 위한 것으로 전사필름에 특정 성분이 포함되는 하드코팅층을 형성하여 내오염성을 개선할 수 있는 인서트 몰드 전사 필름 제조 방법을 제공하는 것을 그 목적으로 한다.The present invention provides an insert mold transfer film manufacturing method which can improve fouling resistance by forming a hard coating layer containing a specific component on the transfer film to improve fouling resistance such as endogenous sweat effect on the surface of the transfer film. It is for that purpose.

아울러, 본 발명은 기재필름 및 이형층의 상부에 특정 성분이 포함되는 하드코팅층을 형성하여 내오염성을 개선할 수 있는 인서트 몰드 전사 필름의 구조를 제공하는 것을 그 목적으로 한다.
In addition, an object of the present invention is to provide a structure of an insert mold transfer film that can improve the stain resistance by forming a hard coating layer containing a specific component on the base film and the release layer.

본 발명의 일 실시예에 따른 인서트 몰드 전사 필름 제조 방법은 기재필름 상부에 이형층을 형성하는 단계와 상기 이형층 상부에 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층을 형성하는 단계, 상기 제1하드코팅층 상부에 제2하드코팅층을 형성하는 단계, 상기 제2하드코팅층 상부에 인쇄층을 형성하는 단계, 상기 인쇄층 상부에 프라이머층을 형성하는 단계 및 상기 프라이머층 상부에 접착층을 형성하는 단계를 포함하는 것을 특징으로 한다.Insert mold transfer film manufacturing method according to an embodiment of the present invention comprises the steps of forming a release layer on the base film and forming a first hard coating layer containing a fluorine-containing acrylic polymer on the release layer, the first Forming a second hard coating layer on the hard coating layer, forming a printing layer on the second hard coating layer, forming a primer layer on the printing layer, and forming an adhesive layer on the primer layer. It is characterized by including.

아울러, 본 발명의 일 실시예에 따른 인서트 몰드 전사 필름은 위로부터, 기재필름, 이형층, 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층, 제2하드코팅층, 인쇄층, 프라이머층 및 접착층이 순차적으로 적층된 구조를 포함하는 것을 특징으로 한다.
In addition, the insert mold transfer film according to an embodiment of the present invention, the base film, a release layer, a first hard coating layer, a second hard coating layer, a printing layer, a primer layer, and an adhesive layer containing a fluorine-containing acrylic polymer are sequentially. It characterized in that it comprises a laminated structure.

본 발명에 따른 인서트 몰드 전사 필름 및 이를 제조하는 방법은 인서트 몰드 전사필름의 제1하드코팅층이 불소 함유 아크릴계 중합체를 포함하여 상기 전사필름의 표면부가 내인공땀 효과와 같은 내오염성이 우수한 장점을 갖는다.
The insert mold transfer film and the method of manufacturing the same according to the present invention have the advantage that the first hard coating layer of the insert mold transfer film includes a fluorine-containing acrylic polymer and the surface portion of the transfer film has excellent stain resistance such as an artificial sweat effect. .

도 1은 본 발명의 일 실시예에 따른 내오염성이 우수한 인서트 몰드 전사 필름 제조 방법을 도시한 순서도이다.
도 2는 본 발명의 일 실시예에 따른 내오염성이 우수한 인서트 몰드 전사 필름 구조를 나타낸 단면도이다.1 is a flowchart illustrating a method of manufacturing an insert mold transfer film having excellent stain resistance according to an embodiment of the present invention.
2 is a cross-sectional view showing the insert mold transfer film structure excellent in fouling resistance according to an embodiment of the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나, 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다.Advantages and features of the present invention and methods for achieving them will be apparent with reference to the embodiments described below in detail with the accompanying drawings. It should be understood, however, that the invention is not limited to the disclosed embodiments, but is capable of many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, To fully disclose the scope of the invention to those skilled in the art, and the invention is only defined by the scope of the claims. Like reference numerals refer to like elements throughout the specification.

이하, 첨부된 도면을 참조하여 본 발명에 따른 내오염성이 우수한 인서트 몰드 전사 필름 및 이를 제조하는 방법에 대하여 상세히 설명하면 다음과 같다.
Hereinafter, an insert mold transfer film excellent in fouling resistance according to the present invention and a method of manufacturing the same will be described in detail with reference to the accompanying drawings.

먼저, 기재필름에 이형층을 형성하고 제1하드코팅층, 제2하드코팅층, 인쇄층, 프라이머층 및 접착층을 순차적으로 코팅하는 인서트 몰드 전사 필름 제조 방법을 따른다.First, an insert mold transfer film manufacturing method of forming a release layer on a base film and sequentially coating a first hard coating layer, a second hard coating layer, a printing layer, a primer layer, and an adhesive layer is performed.

이때, 실제 사출물과 접합되는 부분은 접착층으로, 접착층을 기준으로 할 경우 아래로부터, 접착층, 프라이머층, 인쇄층, 제2하드코팅층, 제2하드코팅층, 이형층 및 기재필름의 순서로 형성되는 구조가 된다.At this time, the part to be bonded to the actual injection molding is an adhesive layer, the structure formed in the order of the adhesive layer, primer layer, printing layer, the second hard coating layer, the second hard coating layer, the release layer and the base film from below, based on the adhesive layer Becomes

따라서, 본 발명에 따른 인서트 몰드 전사 필름은 상부 또는 하부라는 표현에 의해서 제한되는 것이 아니며, 전체적인 적층 순서를 기준으로 이해 되어야 할 것이다.
Therefore, the insert mold transfer film according to the present invention is not limited by the expression of upper or lower, and should be understood based on the overall lamination order.

도 1은 본 발명의 일 실시예에 따른 내오염성이 우수한 인서트 몰드 전사 필름 제조 방법을 도시한 순서도이다.1 is a flowchart illustrating a method of manufacturing an insert mold transfer film having excellent stain resistance according to an embodiment of the present invention.

도 1을 참조하면, 기재필름 상부에 이형층을 형성하는 단계(S110)와 상기 이형층 상부에 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층을 형성하는 단계(S120)와, 상기 제1하드코팅층 상부에 제2하드코팅층을 형성하는 단계(S130)와, 상기 제2하드코팅층 상부에 인쇄층을 형성하는 단계(S140)와, 상기 인쇄층 상부에 프라이머층을 형성하는 단계(S150) 및 상기 프라이머층 상부에 접착층을 형성하는 단계(S160)를 수행한다.Referring to Figure 1, the step of forming a release layer on the base film (S110) and the step of forming a first hard coating layer containing a fluorine-containing acrylic polymer on the release layer (S120), and the first hard coating layer Forming a second hard coating layer on the upper surface (S130), forming a printing layer on the second hard coating layer (S140), forming a primer layer on the printing layer (S150), and the primer Forming an adhesive layer on the layer (S160) is performed.

여기까지의 공정으로 내오염성이 우수한 인서트 몰드 전사 필름 형태를 완성할 수 있다. 다음으로, 상기 접착층을 사출물에 전사시키는 단계 및 상기 기재필름과 상기 유광 및 무광 이형층을 제거하는 단계를 더 수행하여 인몰드 전사 필름이 전사된 사출물을 제조할 수 있다.
The process up to this point can complete the shape of the insert mold transfer film excellent in stain resistance. Next, the step of transferring the adhesive layer to the injection molding and the step of removing the base film and the gloss and matte release layer may be further carried out to prepare an injection molded product transferred to the in-mold transfer film.

이상에서 설명한 방법에 의해서 제조된 본 발명의 인서트 몰드 전사 필름 구조에 대해서 보다 상세히 살펴보면 다음과 같다.
Looking at the insert mold transfer film structure of the present invention manufactured by the method described above in more detail as follows.

도 2는 본 발명의 일 실시예에 따른 내오염성이 우수한 인서트 몰드 전사 필름의 구조를 나타낸 단면도이다.Figure 2 is a cross-sectional view showing the structure of the insert mold transfer film excellent in stain resistance according to an embodiment of the present invention.

도 2를 참조하면, 본 발명에 따른 인서트 몰드 전사 필름 구조로서 도시된 상태의 상부에서부터 하부로 기재필름(1), 이형층(2), 제1하드코팅층(3), 제2하드코팅층(4), 인쇄층(5), 프라이머층(6) 및 접착층(7)이 구비된다.Referring to FIG. 2, the base film 1, the release layer 2, the first hard coating layer 3, and the second hard coating layer 4 from the top to the bottom in the state shown as the insert mold transfer film structure according to the present invention. ), A printing layer 5, a primer layer 6 and an adhesive layer 7.

다음으로, 접착층(7) 하부에 사출물(8)이 구비되어, 사출물(8)의 표면에 본 발명에 따른 인서트 몰드 전사 필름이 전사되도록 하는 것이다.Next, the injection molding 8 is provided under the adhesive layer 7 so that the insert mold transfer film according to the present invention is transferred to the surface of the injection molding 8.

여기서, 설명의 편의상 도시된 바에 따라서 상부에서 하부 순서로 설명하였으나, 실제로 인서트 몰드 전사 필름은 하부에 기재필름(1)을 놓고, 그 상부에 다른 층들을 적층하는 순서로 형성된다. 따라서, 본 발명에 따른 인서트 몰드 전사 필름의 실제 제조 방법에 대해 설명하면 다음과 같다.
Here, for convenience of description, the description is made in the order from the top to the bottom, but in practice, the insert mold transfer film is formed by placing the base film 1 on the bottom and stacking other layers on the top. Therefore, the actual manufacturing method of the insert mold transfer film according to the present invention will be described.

먼저 기재필름(1) 재질은 공지의 물질을 사용할 수 있으나, PET(Poly Ethylene Terephthalate) 또는 PETG(Poly Ethylene Terephthalate Glycol) 수지를 이용하여 제조하는 것이 바람직하다. PET 또는 PETG 수지는 일반적 기재필름 소재보다 더 우수한 가온신율을 가지고 있으므로, 본 발명에 따른 인서트 몰드 전사 필름은 PET 또는 PETG 수지가 사용하여 성형성을 극대화 시킬 수 있다.
First, the material of the base film 1 may be a known material, but is preferably manufactured by using PET (Poly Ethylene Terephthalate) or PETG (Poly Ethylene Terephthalate Glycol) resin. PET or PETG resin has a better elongation than the general base film material, the insert mold transfer film according to the present invention can be used to maximize the moldability PET or PETG resin.

다음으로, 이형층(2)에 사용되는 이형제는 공지의 이형제를 사용할 수 있으나, 멜라민계 이형제 또는 실리콘계 이형제를 이용하는 것이 바람직하다. 멜라민계 또는 실리콘계 이형제는 액상으로 얇게 도포 될 수 있으므로, 기재필름(1)과 후속 공정에서 형성되는 제1하드코팅층(3)을 밀착시키는 재료로 적합하며, 제1하드코팅층(3)이 완전 경화된 후에는 두 층이 용이하게 떨어질 수 있도록 하는 특성을 제공한다.
Next, although the mold release agent used for the mold release layer 2 can use a well-known mold release agent, it is preferable to use a melamine type mold release agent or a silicone type mold release agent. Since the melamine-based or silicone-based release agent may be applied in a thin liquid, it is suitable as a material for closely contacting the base film 1 and the first hard coating layer 3 formed in a subsequent process, and the first hard coating layer 3 is completely cured. Once it is done, it provides a property that allows the two layers to fall off easily.

본 발명에 따른 인서트 몰드 전사 필름은 하드코팅층이 두개의 층으로 적층된다. 상기 기재필름(1)과 이형층(2)을 제거한 후, 인서트 몰드 전사 필름의 최상부에 위치하는 구성이 제1하드코팅층(3)이며 그 하부에는 제2하드코팅층(4)이 위치한다.In the insert mold transfer film according to the present invention, a hard coating layer is laminated in two layers. After removing the base film 1 and the release layer 2, the first hard coating layer 3 is positioned at the top of the insert mold transfer film, and the second hard coating layer 4 is positioned below.

상기 제1하드코팅층(3)은 인서트 몰드 전사 필름이 사출물에 접착되고, 상기 전사필름에서 기재필름(1)과 이형층(2)이 제거된 후, 전사필름 표면의 최상부에 위치하게 된다. 즉, 상기 제1하드코팅층(3)은 외부에 직접적으로 노출되는 구조이며 내구성 등과 더불어 내오염성이 요구된다. 본 발명에 따른 인서트 몰드 전사필름의 제1하드코팅층(3)은 불소 함유 아크릴계 중합체가 포함되어 형성되므로 외부 충격에 대한 표면 보호 기능뿐 아니라, 내지문성이나 내인공땀 효과와 같은 내오염 기능을 수행할 수 있다.The first hard coating layer 3 is positioned on the top of the transfer film surface after the insert mold transfer film is adhered to the injection molding and the base film 1 and the release layer 2 are removed from the transfer film. That is, the first hard coating layer 3 has a structure directly exposed to the outside and is required to be stain resistant in addition to durability. Since the first hard coating layer 3 of the insert mold transfer film according to the present invention includes a fluorine-containing acrylic polymer, the first hard coating layer 3 includes not only surface protection against external impact, but also stain resistance such as fingerprint resistance or artificial sweat effect. can do.

상기 불소 함유 아크릴계 중합체는 공지된 고분자 (공)중합체를 사용할 수 있으나, 제1하드코팅층(3)의 표면 경도, 내오염성 측면에서 폴리(트리플루오로메틸메타크릴레이트), 폴리(2,2,2-트리플루오로에틸아크릴레이트), 폴리(2,2,2-트리플루오로에틸메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(2-(트리플루오로메틸)에틸아크릴레이트), 폴리(2-(트리플루오로메틸)에틸메타크릴레이트)가 바람직하다. 상기 (공)중합체의 하나 이상을 혼합하여 불소 함유 아크릴계 수지를 제조할 수 도 있다. The fluorine-containing acrylic polymer may be a known polymer (co) polymer, but in terms of surface hardness and stain resistance of the first hard coating layer 3, poly (trifluoromethyl methacrylate), poly (2,2, 2-trifluoroethylacrylate), poly (2,2,2-trifluoroethylmethacrylate), poly (1,1,1,3,3,3-hexafluoro-2-propylmethacryl Rate), poly (1,1,1,3,3,3-hexafluoro-2-propylmethacrylate), poly (2- (trifluoromethyl) ethylacrylate), poly (2- (tri Fluoromethyl) ethyl methacrylate) is preferred. One or more of the (co) polymers may be mixed to produce a fluorine-containing acrylic resin.

불소 함유 아크릴계 중합체의 제조 방법은 일반적으로 사용되는 방법이면 특별히 한정되지 않고 사용된다. 예를 들면, 불소 함유 아크릴레이트를 포함하는 중합성 단량체, 분산 안정제, 중합 개시제 및 이온 교환수를 중합 용기에 투입하고 현탁 중합을 수행할 수 있다.
The method for producing the fluorine-containing acrylic polymer is not particularly limited as long as it is a generally used method. For example, a polymerizable monomer containing a fluorine-containing acrylate, a dispersion stabilizer, a polymerization initiator, and ion-exchanged water may be added to the polymerization vessel, and suspension polymerization may be performed.

본 발명에 따른 인서트 몰드 전사필름의 상기 제1하드코팅층(3)은 이중경화성 제1하드코팅층을 형성하되, 엠보 벨트 또는 롤러를 사용하여 상기 제1하드코팅층의 코팅액을 도포한 후, UV를 조사하여 반경화 상태로 형성할 수 있다.The first hard coating layer 3 of the insert mold transfer film according to the present invention forms a double-curable first hard coating layer, and after applying the coating liquid of the first hard coating layer using an emboss belt or roller, irradiating UV It can be formed in a semi-cured state.

상기 이중경화성 제1하드코팅층이란 엠보 벨트 또는 롤러를 이용하여 코팅 물질을 이형층의 상부에 도포한 후, 1차 UV 조사 공정을 수행하여 부분 경화시킨 상태의 UV 경화성 하드코팅층을 의미한다.The double-curable first hard coating layer refers to a UV curable hard coating layer of a partially cured state by applying a coating material on top of the release layer using an emboss belt or roller, and then performing a first UV irradiation process.

제1하드코팅층(3)은 엠보 벨트 또는 롤러를 이용하여 코팅 물질을 이형층(2)의 상부에 도포하여 형성하므로, 상기 제1하드코팅층(3)의 표면에는 입체 패턴의 형성도 가능하다. Since the first hard coating layer 3 is formed by applying a coating material on the upper part of the release layer 2 using an emboss belt or a roller, a three-dimensional pattern may be formed on the surface of the first hard coating layer 3.

또한, 상기 이중경화성 제1하드코팅층은 특히 내오염성의 측면에서 광경화성 고형물 100중량%를 기준으로 불소 함유 아크릴계 중합체가 90 중량% 이상인 물질을 사용하는 것이 바람직하다.
In addition, the double hardenable first hard coating layer is particularly preferably used a material having a fluorine-containing acrylic polymer of at least 90% by weight based on 100% by weight of the photocurable solids in terms of stain resistance.

본 발명에 따른 인서트 몰드 전사필름의 제2하드코팅층(4)은 이중경화성 제2하드코팅층을 형성하되, 엠보 벨트 또는 롤러를 사용하여 상기 제2하드코팅층의 코팅액을 도포한 후, UV를 조사하여 반경화 상태로 형성할 수 있다.The second hard coating layer 4 of the insert mold transfer film according to the present invention forms a double hardenable second hard coating layer, and after applying the coating liquid of the second hard coating layer using an emboss belt or roller, by irradiating UV It can be formed in a semi-cured state.

상기 이중경화성 제2하드코팅층이란 엠보 벨트 또는 롤러를 이용하여 코팅 물질을 제1하드코팅층(3)의 상부에 도포한 후, 1차 UV 조사 공정을 수행하여 부분 경화시킨 상태의 UV 경화성 하드코팅층을 의미한다.The double hardenable second hard coat layer is a UV curable hard coat layer which is partially cured by applying a coating material on the first hard coat layer 3 using an emboss belt or roller, and then performing a primary UV irradiation process. it means.

제2하드코팅층(4)은 엠보 벨트 또는 롤러를 이용하여 코팅 물질을 제1하드코팅층(3)의 상부에 도포하여 형성하므로, 상기 제2하드코팅층(4)의 표면에는 입체 패턴의 형성도 가능하다.Since the second hard coating layer 4 is formed by applying a coating material on the first hard coating layer 3 using an emboss belt or roller, a three-dimensional pattern may be formed on the surface of the second hard coating layer 4. Do.

또한, 상기 이중경화성 제2하드코팅층은 경도, 내열성, 성형성, 적층 대상물과의 접착성 등의 측면에서 광경화성 고형물 100중량%를 기준으로 아크릴계 중합체가 90 중량% 이상인 물질을 사용하는 것이 바람직하다.In addition, it is preferable to use a material having an acrylic polymer of at least 90% by weight based on 100% by weight of the photocurable solid in terms of hardness, heat resistance, moldability, adhesiveness to a lamination object, and the like. .

상기 아크릴계 중합체는 공지된 물질을 사용할 수 있으나, 경도, 내열성, 성형성, 적층 대상물과의 접착성 등의 측면에서 우레탄 아크릴레이트, 우레탄 메타아크릴레이트, 에폭시 아크릴레이트, 에폭시 메타아크릴레이트, 에스터 아크릴레이트, 에스터 메타아크릴레이트, 아크릴릭 아크릴레이트, 폴리에스텔 아크릴 레이트, 아민변성 아크릴레이트 중 하나 이상을 사용하는 것이 바람직하다.
The acrylic polymer may be a known material, but urethane acrylate, urethane methacrylate, epoxy acrylate, epoxy methacrylate, and ester acrylate in terms of hardness, heat resistance, moldability, and adhesion to a laminated object. Preference is given to using at least one of ester methacrylate, acrylic acrylate, polyester acrylate, and amine modified acrylate.

그 다음으로, 제2하드코팅층(4) 상부에 인쇄층(5)을 형성하는 단계를 수행한다. 상기 인쇄층(5)은 금속효과층, 펄잉크층 및 미러잉크층 중 하나 이상을 포함하되, 상기 금속효과층은 알루미늄, 구리 및 티타늄 중 선택된 하나 이상을 사용하여 형성할 수 있다.Next, the printing layer 5 is formed on the second hard coating layer 4. The print layer 5 may include at least one of a metal effect layer, a pearl ink layer, and a mirror ink layer, and the metal effect layer may be formed using at least one selected from aluminum, copper, and titanium.

아울러, 고분자수지를 이용한 인쇄층(5)을 형성할 수도 있는데, 이 경우 바인더를 이루는 합성수지 100 중량부에 대하여 안료 25중량부, 합성수지 15중량부, 경화제 5중량부를 포함하여 이루어지는 소재로 형성하는 것이 바람직하다.In addition, it is possible to form a printed layer 5 using a polymer resin, in which case it is formed of a material comprising 25 parts by weight of pigment, 15 parts by weight of synthetic resin, and 5 parts by weight of hardener based on 100 parts by weight of the synthetic resin forming the binder. desirable.

이때, 경화제는 우레탄공중합체를 약 40％ 포함하는 합성수지로 이루어지는 소재를 사용하는 것이 더욱 바람직하다.At this time, it is more preferable to use a material made of a synthetic resin containing about 40% of a urethane copolymer.

또한, 인쇄층(5)은 다중색상 그라비어 인쇄 윤전기(Multi-color Gravuer Printing Machine)를 이용하여 형성되는데, 다중 그라비어 인쇄 윤전기에서 정해진 인쇄 도수에서 운전된다. 이때, 인쇄층(5)은 1.0 ~ 1.5㎛의 두께를 갖도록 형성하고, 건조는 100℃에서 10초 동안 진행되고 건조과정을 거친 후 40℃에서 24시간 동안 숙성을 거쳐 인쇄층(5)의 가교가 완료되도록 한다.In addition, the printing layer 5 is formed using a multi-color gravure printing machine, and is operated at a printing frequency determined in the multi-gravure printing machine. At this time, the print layer 5 is formed to have a thickness of 1.0 ~ 1.5㎛, drying is carried out for 10 seconds at 100 ℃ and after drying the cross-linking of the print layer 5 through aging for 24 hours at 40 ℃ To complete.

그 외에는 인쇄층(5)의 접착력을 향상시키고, 인쇄 후 잉크를 흡수하는 성질을 향상시키기 위하여, 투명 또는 반투명 평탄화층을 더 형성할 수 있다.
Otherwise, a transparent or semitransparent flattening layer may be further formed to improve the adhesion of the printing layer 5 and to improve the property of absorbing ink after printing.

한편, 여기서 인쇄층(5)은 단독으로 전체 전사 무늬를 표현 할 수도 있으나, 부분적으로 인쇄되어 다양한 디자인, 캐릭터 또는 상표 등을 여러가지 색으로 나타내는 역할을 할 수 있으며, 이 경우 데코레이션(Decoration)층으로서 금속효과층이라 할 수 있다.On the other hand, the print layer 5 may represent the entire transfer pattern alone, but may be partially printed to play a role of representing various designs, characters or trademarks in various colors, in this case as a decoration layer (Decoration) layer It can be called a metal effect layer.

이때, 금속효과층은 알루미늄, 구리 및 티타늄 중 선택된 하나 이상을 사용하여 스퍼터링(Sputtering) 증착 공정을 이용하여 형성하는 것이 바람직하며, 50 ~ 150Å의 두께로 형성하는 것이 바람직하다. At this time, the metal effect layer is preferably formed using a sputtering deposition process using at least one selected from aluminum, copper, and titanium, it is preferable to form a thickness of 50 ~ 150Å.

금속효과층이 50Å 미만의 두께로 형성되는 경우 충분한 금속 질감 효과를 얻을 수 없으며, 150Å을 초과하는 두께로 형성되는 경우에는 무광 무늬에 의해서 얻어질 수 있는 고유의 질감이 무너질 수 있고, 전체 인서트 몰드 전사 필름의 두께를 증가시켜, 성형성의 저하를 초래하는 문제가 있을 수 있다.If the metal effect layer is formed to a thickness of less than 50Å, sufficient metal texture effect may not be obtained. If the metal effect layer is formed to a thickness of more than 150Å, the inherent texture that may be obtained by the matte pattern may collapse, and the entire insert mold There may be a problem that the thickness of the transfer film is increased, resulting in a deterioration in formability.

아울러, 본 발명에 따른 금속효과층은 고유의 금속 색깔 이외에 다른 색을 가질 수 있는 배경 인쇄층을 더 포함할 수 있다. 이 경우 금속 질감 효과를 얻어야 하는 로고 등의 부분에만 스퍼터링 증착공정을 수행한 후 나머지 영역은 상기 인쇄층 형성 공정에 따라서, 배경 인쇄층으로 형성할 수 있다.
In addition, the metal effect layer according to the present invention may further include a background printing layer which may have a different color in addition to the unique metal color. In this case, after the sputtering deposition process is performed only on a portion of the logo or the like to obtain the metal texture effect, the remaining area may be formed as a background printing layer according to the printing layer forming process.

본 발명에 따른 인서트 몰드 전사필름의 인쇄층(5) 상부에는 프라이머층(6)이 형성된다. 프라이머층(6)은 잉크 흡수성이 우수한 아크릴폴리올 또는 우레탄공중합체로 이루어진 물질을 이용하여 형성하는 것이 바람직하다.The primer layer 6 is formed on the print layer 5 of the insert mold transfer film according to the present invention. The primer layer 6 is preferably formed using a material made of acryl polyol or urethane copolymer having excellent ink absorption.

아울러, 프라이머층(6)은 제1 및 제2하드코팅층(3, 4) 및 인쇄층(5)과 소정의 굴절률을 가지도록 형성하는 것이 바람직하며, 이는 레인보우(Rainbow) 현상을 방지하기 위함이다.In addition, the primer layer 6 is preferably formed to have a predetermined refractive index with the first and second hard coating layers 3 and 4 and the printing layer 5, which is to prevent the rainbow phenomenon. .

아울러, 본 발명에 따른 프라이머층(6)은 인쇄층(5)과 후속의 접착층(7)의 결합이 보다 용이하게 이루어질 수 있도록 하는 접착 보조층으로서의 기능도 할 수 있다.In addition, the primer layer 6 according to the present invention can also function as an adhesion auxiliary layer to facilitate bonding of the printing layer 5 and the subsequent adhesive layer 7.

따라서, 프라이머층(6) 상부에 접착층(7)을 형성하여, 본 발명에 따른 인서트 몰드 전사 필름이 사출물(8)에 원활하게 접착될 수 있도록 한다.
Therefore, the adhesive layer 7 is formed on the primer layer 6 so that the insert mold transfer film according to the present invention can be smoothly adhered to the injection molding 8.

본 발명에서는 상기와 같이, 불소 함유 아크릴계 중합체를 사용하여 제1하드코팅층을 제조함으로써 내오염성이 우수한 인서트 몰드 전사 필름을 제조할 수 있다.In the present invention, as described above, by inserting the first hard coating layer using a fluorine-containing acrylic polymer, it is possible to produce an insert mold transfer film excellent in stain resistance.

다음으로, 이상에서 실시한 본 발명의 인서트 몰드 전사 필름 특성에 대하여 살펴 보면 아래와 같다.
Next, look at with respect to the insert mold transfer film properties of the present invention carried out above.

[실험예][Experimental Example]

[실시예1][Example 1]

PET 재질의 기재 필름 표면에 멜라민계 이형필름을 형성하였다. Melamine-based release film was formed on the surface of the PET film base material.

다음으로 상기 이형필름 상부에 2,2,2-트리플루오로에틸메타크릴레이트를 주성분으로 하는 불소 아크릴 수지 조성물을 이용하여 제1하드코팅층을 형성하였다. 그리고 상기 제1하드코팅층의 상부에는 에폭시 메타아크릴레이트를 주성분으로 하는 아크릴 수지 조성물을 이용하여 제2하드코팅층을 형성하였다.Next, a first hard coat layer was formed on the release film by using a fluorine acrylic resin composition containing 2,2,2-trifluoroethyl methacrylate as a main component. The second hard coating layer was formed on the first hard coating layer using an acrylic resin composition containing epoxy methacrylate as a main component.

그 다음으로, 인쇄층으로서 150Å의 두께를 갖는 알루미늄 금속효과층을 형성하고, 금속효과층 상부에 프라이머층 및 접착층을 형성하여 인서트 몰드 전사 필름 제조를 완료하였다.Next, an aluminum metal effect layer having a thickness of 150 kPa was formed as a print layer, and a primer layer and an adhesive layer were formed on the metal effect layer to complete the manufacture of the insert mold transfer film.

그 다음으로, 상기 인서트 몰드 전사 필름을 사출물에 전사시키고, 상기 기재필름 및 이형필름을 제거하였다.Next, the insert mold transfer film was transferred to the injection molded product, and the base film and the release film were removed.

이때, 기재필름 및 이형필름의 제거 전에 상기 제1하드코팅층 및 제2하드코팅층을 완전 경화시켜, 제거 공정이 용이해 질 수 있도록 한다.
In this case, the first hard coating layer and the second hard coating layer are completely cured before the removal of the base film and the release film, so that the removal process may be facilitated.

[실시예2][Example 2]

상기 실시예1과 모든 공정을 동일하게 수행하되, 제1하드코팅층은 트리플루오로메틸메타크릴레이트를 주성분으로 하는 불소 수지 조성물을 이용하였다.
All processes were performed in the same manner as in Example 1, but the first hard coat layer was a fluororesin composition containing trifluoromethyl methacrylate as a main component.

[실시예3][Example 3]

상기 실시예1과 모든 공정을 동일하게 수행하되, 제1하드코팅층은 2,2,2-트리플루오로에틸아크릴레이트를 주성분으로 하는 불소 수지 조성물을 이용하였다.
All processes were performed in the same manner as in Example 1, but the first hard coat layer was a fluororesin composition containing 2,2,2-trifluoroethyl acrylate as a main component.

[비교예1][Comparative Example 1]

상기 실시예1과 모든 공정을 동일하게 수행하되, 이형층의 상부에 제1하드코팅층 형성단계를 배제하고 제2하드코팅층만을 형성한 인서트 몰드 전사 필름을 제조하였다.
Performing the same process as in Example 1, except that the first hard coating layer forming step on the upper part of the release layer to prepare an insert mold transfer film formed only a second hard coating layer.

상기 실시예 및 비교예의 특성을 살펴보기 위하여, 각 실시예 또는 비교예 별로 10개의 샘플을 제작하여 테스트를 수행하였다.In order to examine the characteristics of the Examples and Comparative Examples, 10 samples were prepared for each Example or Comparative Example and tested.

상기 테스트는 기재필름 및 이형필름을 제거한 전사필름의 표면에 인공땀을 떨어뜨려 온도 75℃, 상대습도 90%의 조건을 갖는 항온조에서 24시간 동안 방치한 후에 상기 표면의 자국 생성 여부와 외관 손상 여부를 살펴보았다.The test was performed by dropping artificial sweat on the surface of the transfer film from which the base film and the release film were removed, and leaving the surface of the transfer film for 24 hours in a thermostat having a temperature of 75 ° C. and a relative humidity of 90%. I looked at it.

상기 테스트의 결과로서, 내오염성이 우수하여 표면에 자국이 잘 남지 않는 전사필름은 상 등급, 표면에 어느 정도 자국이 남지만 양호한 정도는 중 등급, 자국이 심하게 남고 외관이 손상되는 경우는 하 등급으로 분류하였다.As a result of the test, the transfer film having excellent stain resistance and hardly leaving traces on the surface has an upper grade, and some marks remain on the surface, but a good grade is medium grade, and if the marks are severely left and the appearance is damaged, the grade is lower grade. Classified.

또한, 인공땀으로 인해 표면에 자국이 심하게 남아서 제품화하기 어려운 샘플은 불량품으로 판정하였다.
In addition, samples that were difficult to commercialize due to severe marks left on the surface due to artificial sweat were judged as defective products.

[표 1][Table 1]

Figure 112011026375188-pat00001
Figure 112011026375188-pat00001

상기 표 1을 참조하면 알 수 있는 바와 같이, 본 발명에 따른 인서트 몰드 전사 필름은 내오염성이 개선되어 내인공땀 효과가 우수하였다. 하지만, 비교예1의 경우는 인공땀에 의하여 전사필름의 표면에 자국이 발생하고 외관이 손상되는 문제점이 있었다.
As can be seen with reference to Table 1, the insert mold transfer film according to the present invention has improved stain resistance and was excellent in artificial sweat effect. However, in the case of Comparative Example 1, there was a problem that marks appeared on the surface of the transfer film due to artificial sweating and appearance was damaged.

이상과 같이 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 이는 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. 따라서, 본 발명 사상은 아래에 기재된 특허청구범위에 의해서만 파악되어야 하고, 이의 균등 또는 등가적 변형 모두는 본 발명 사상의 범주에 속한다고 할 것이다.
As described above, the present invention has been described by way of limited embodiments and drawings, but the present invention is not limited to the above-described embodiments, which can be variously modified and modified by those skilled in the art to which the present invention pertains. Modifications are possible. Accordingly, the spirit of the present invention should be understood only in accordance with the following claims, and all equivalents or equivalent variations thereof are included in the scope of the present invention.

1 : 기재필름
2 : 이형층
3 : 제1하드코팅층
4 : 제2하드코팅층
5 : 인쇄층
6 : 프라이머층
7 : 접착층
8 : 사출물1: base film
2: release layer
3: first hard coating layer
4: second hard coating layer
5: printing layer
6: primer layer
7: adhesive layer
8: injection molding

Claims (16)

기재필름 상부에 이형층을 형성하는 단계;
상기 이형층 상부에 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층을 형성하는 단계;
상기 제1하드코팅층 상부에 제2하드코팅층을 형성하는 단계;
상기 제2하드코팅층 상부에 인쇄층을 형성하는 단계;
상기 인쇄층 상부에 프라이머층을 형성하는 단계; 및
상기 프라이머층 상부에 접착층을 형성하는 단계;를 포함하고,
상기 제1하드코팅층은
이중경화성 제1하드코팅층을 형성하되, 엠보 벨트 또는 롤러를 사용하여 상기 제1하드코팅층을 도포한 후, UV를 조사하여 반경화 상태로 형성하고,
상기 제2하드코팅층은
이중경화성 제2하드코팅층을 형성하되, 상기 제1하드코팅층의 상부에 엠보 벨트 또는 롤러를 사용하여 상기 제2하드코팅층을 도포한 후, UV를 조사하여 반경화 상태로 형성하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
Forming a release layer on the base film;
Forming a first hard coating layer including a fluorine-containing acrylic polymer on the release layer;
Forming a second hard coat layer on the first hard coat layer;
Forming a printing layer on the second hard coating layer;
Forming a primer layer on the printed layer; And
Forming an adhesive layer on the primer layer;
The first hard coating layer is
Forming a double hardening first hard coating layer, after applying the first hard coating layer using an emboss belt or roller, it is formed in a semi-cured state by irradiation with UV,
The second hard coating layer
The second hard coating layer is formed of a double curable layer, and the second hard coating layer is applied to the upper part of the first hard coating layer by using an emboss belt or a roller. Mold transfer film manufacturing method.
제1항에 있어서,
상기 기재필름은
PET(Poly Ethylene Terephthalate) 또는 PETG(Poly Ethylene Terephthalate Glycol) 수지를 이용하여 제조하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 1,
The base film is
Method for producing an insert mold transfer film, characterized in that it is produced using PET (Poly Ethylene Terephthalate) or PETG (Poly Ethylene Terephthalate Glycol) resin.
제1항에 있어서,
상기 이형층은
멜라민계 이형제 또는 실리콘계 이형제를 이용하여 형성하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 1,
The release layer is
Method for producing an insert mold transfer film, characterized in that formed using a melamine-based release agent or a silicone-based release agent.
제1항에 있어서,
상기 불소 함유 아크릴계 중합체는
폴리(트리플루오로메틸메타크릴레이트), 폴리(2,2,2-트리플루오로에틸아크릴레이트), 폴리(2,2,2-트리플루오로에틸메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(2-(트리플루오로메틸)에틸아크릴레이트), 폴리(2-(트리플루오로메틸)에틸메타크릴레이트) 중 하나 이상을 포함하는 물질을 사용하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.

The method of claim 1,
The fluorine-containing acrylic polymer
Poly (trifluoromethylmethacrylate), poly (2,2,2-trifluoroethylacrylate), poly (2,2,2-trifluoroethylmethacrylate), poly (1,1, 1,3,3,3-hexafluoro-2-propylmethacrylate), poly (1,1,1,3,3,3-hexafluoro-2-propylmethacrylate), poly (2- (Trifluoromethyl) ethyl acrylate) and poly (2- (trifluoromethyl) ethyl methacrylate). A method for producing an insert mold transfer film, comprising using a material containing at least one of (trifluoromethyl) ethyl methacrylate).

삭제delete 삭제delete 제1항에 있어서,
상기 이중경화성 제1하드코팅층은
광경화성 고형물 100중량%를 기준으로 불소 함유 아크릴계 중합체가 90중량% 이상인 물질을 사용하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 1,
The double hardenable first hard coating layer is
A method for producing an insert mold transfer film, comprising using a material having 90% by weight or more of a fluorine-containing acrylic polymer based on 100% by weight of a photocurable solid.
제1항에 있어서,
상기 이중경화성 제2하드코팅층은
광경화성 고형물 100중량%를 기준으로 아크릴계 중합체가 90 중량% 이상인 물질을 사용하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 1,
The double hardenable second hard coating layer
A method for producing an insert mold transfer film, comprising using a material having an acrylic polymer of 90% by weight or more based on 100% by weight of a photocurable solid.
제7항에 있어서,
상기 불소 함유 아크릴계 중합체는
폴리(트리플루오로메틸메타크릴레이트), 폴리(2,2,2-트리플루오로에틸아크릴레이트), 폴리(2,2,2-트리플루오로에틸메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(2-(트리플루오로메틸)에틸아크릴레이트), 폴리(2-(트리플루오로메틸)에틸메타크릴레이트) 중 하나 이상을 포함하는 물질을 사용하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 7, wherein
The fluorine-containing acrylic polymer
Poly (trifluoromethylmethacrylate), poly (2,2,2-trifluoroethylacrylate), poly (2,2,2-trifluoroethylmethacrylate), poly (1,1, 1,3,3,3-hexafluoro-2-propylmethacrylate), poly (1,1,1,3,3,3-hexafluoro-2-propylmethacrylate), poly (2- (Trifluoromethyl) ethyl acrylate) and poly (2- (trifluoromethyl) ethyl methacrylate). A method for producing an insert mold transfer film, comprising using a material containing at least one of (trifluoromethyl) ethyl methacrylate).
제8항에 있어서,
상기 아크릴계 중합체는
우레탄 아크릴레이트, 우레탄 메타아크릴레이트, 에폭시 아크릴레이트, 에폭시 메타아크릴레이트, 에스터 아크릴레이트, 에스터 메타아크릴레이트, 아크릴릭 아크릴레이트, 폴리에스텔 아크릴 레이트, 아민변성 아크릴레이트 중 하나 이상을 사용하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
9. The method of claim 8,
The acrylic polymer
At least one of urethane acrylate, urethane methacrylate, epoxy acrylate, epoxy methacrylate, ester acrylate, ester methacrylate, acrylic acrylate, polyester acrylate, and amine-modified acrylate. Insert mold transfer film manufacturing method.
제1항에 있어서,
상기 인쇄층은
금속효과층, 펄잉크층 및 미러잉크층 중 하나 이상을 포함하는 것을 특징으로 하는 인서트 몰드 전사 필름 제조 방법.
The method of claim 1,
The print layer is
An insert mold transfer film manufacturing method comprising at least one of a metal effect layer, a pearl ink layer and a mirror ink layer.
제1항의 방법으로 제조되고,
위로부터, 기재필름;, 이형층;, 불소 함유 아크릴계 중합체가 포함된 제1하드코팅층;, 제2하드코팅층;, 인쇄층;, 프라이머층; 및 접착층;이 순차적으로 적층된 구조를 포함하는 인서트 몰드 전사 필름.
Prepared by the method of claim 1,
From above, a base film ;, a release layer; a first hard coating layer containing a fluorine-containing acrylic polymer; a second hard coating layer; a printing layer; a primer layer; And an adhesive layer; the insert mold transfer film comprising a structure in which the layers are sequentially stacked.
제12항에 있어서,
상기 기재필름은
PET(Poly Ethylene Terephthalate) 또는 PETG(Poly Ethylene Terephthalate Glycol) 수지를 포함하는 것을 특징으로 하는 인서트 몰드 전사 필름.
The method of claim 12,
The base film is
An insert mold transfer film comprising PET (Poly Ethylene Terephthalate) or PETG (Poly Ethylene Terephthalate Glycol) resin.
제12항에 있어서,
상기 이형층은
멜라민계 고분자 수지 또는 실리콘계 고분자 수지를 포함하는 것을 특징으로 하는 인서트 몰드 전사 필름.
The method of claim 12,
The release layer is
An insert mold transfer film comprising a melamine polymer resin or a silicone polymer resin.
제12항에 있어서,
상기 제1하드코팅층은
광경화성 고형물 100중량%를 기준으로 불소 함유 아크릴계 중합체가 90중량% 이상인 것을 특징으로 하는 인서트 몰드 전사 필름.
The method of claim 12,
The first hard coating layer is
Insert mold transfer film, characterized in that 90% by weight or more of the fluorine-containing acrylic polymer based on 100% by weight of the photocurable solids.
제12항에 있어서,
상기 불소 함유 아크릴계 중합체는
폴리(트리플루오로메틸메타크릴레이트), 폴리(2,2,2-트리플루오로에틸아크릴레이트), 폴리(2,2,2-트리플루오로에틸메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(1,1,1,3,3,3-헥사플루오로-2-프로필메타크릴레이트), 폴리(2-(트리플루오로메틸)에틸아크릴레이트), 폴리(2-(트리플루오로메틸)에틸메타크릴레이트) 중 하나 이상을 포함하는 것을 특징으로 하는 인서트 몰드 전사 필름.


The method of claim 12,
The fluorine-containing acrylic polymer
Poly (trifluoromethylmethacrylate), poly (2,2,2-trifluoroethylacrylate), poly (2,2,2-trifluoroethylmethacrylate), poly (1,1, 1,3,3,3-hexafluoro-2-propylmethacrylate), poly (1,1,1,3,3,3-hexafluoro-2-propylmethacrylate), poly (2- (Trifluoromethyl) ethyl acrylate) and poly (2- (trifluoromethyl) ethyl methacrylate).


KR1020110033335A 2011-04-11 2011-04-11 Insert mold transcription film having improved contamination resistance and method for fabricating the same KR101276497B1 (en)