KR101268041B1 - the composite of sulfur concrete with decomposed granite soil - Google Patents
the composite of sulfur concrete with decomposed granite soil Download PDFInfo
- Publication number
- KR101268041B1 KR101268041B1 KR1020100109568A KR20100109568A KR101268041B1 KR 101268041 B1 KR101268041 B1 KR 101268041B1 KR 1020100109568 A KR1020100109568 A KR 1020100109568A KR 20100109568 A KR20100109568 A KR 20100109568A KR 101268041 B1 KR101268041 B1 KR 101268041B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- sulfur
- concrete composition
- masato
- Prior art date
Abstract
본 발명은 마사토와 황토가 포함된 유황 콘크리트 조성물 및 그 유황 콘크리트 조성물로 만들어지는 바다투입물 및 호안블록에 관한 것으로, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 20∼50 중량부, 황토 분말 1∼5 중량부, 쇄석 30∼50 중량부로 구성하는 유황 콘크리트 조성물을 구비하고, 그 유황 콘크리트 조성물을 120℃ 내지 130℃의 온도로 가열하면서 교반한 모르타르를 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제조·제공되어, 유황 콘크리트 조성물에 포함되는 배합물에 의해 자연친화적이며, 강도가 우수하고, 수질을 개선할 수 있는 것이다.The present invention relates to a sulfur concrete composition containing masato and ocher, and a sea input and a lake block made from the sulfur concrete composition, and 20 to 50 parts by weight of masato, and ocher powder 1 with respect to 30 to 55 parts by weight of sulfur polymer cement. Artificial reefs, tetrapots and artificial seaweeds were prepared by using a mortar that had a sulfur concrete composition composed of ˜5 parts by weight and 30 to 50 parts by weight of crushed stone and stirred while heating the sulfur concrete composition to a temperature of 120 ° C to 130 ° C. It is manufactured and provided with sea inputs such as seaweeds and lake block, etc., and it is nature-friendly, excellent strength, and water quality can be improved by the compound contained in sulfur concrete composition.
Description
본 발명은 마사토와 황토가 포함된 유황 콘크리트 조성물 및 그 유황 콘크리트 조성물로 만들어지는 바다투입물 및 호안블록에 관한 것으로, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 20∼50 중량부, 황토 분말 1∼5 중량부, 쇄석 30∼50 중량부로 구성하는 유황 콘크리트 조성물을 구비하고, 그 유황 콘크리트 조성물을 120℃ 내지 130℃의 온도로 가열하면서 교반한 모르타르를 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제조·제공되어, 유황 콘크리트 조성물에 포함되는 배합물에 의해 자연친화적이며, 강도가 우수하고, 수질을 개선할 수 있는 것이다.
The present invention relates to a sulfur concrete composition containing masato and ocher, and a sea input and a lake block made from the sulfur concrete composition, and 20 to 50 parts by weight of masato, and ocher powder 1 with respect to 30 to 55 parts by weight of sulfur polymer cement. Artificial reefs, tetrapots and artificial seaweeds were prepared by using a mortar that had a sulfur concrete composition composed of ˜5 parts by weight and 30 to 50 parts by weight of crushed stone and stirred while heating the sulfur concrete composition to a temperature of 120 ° C to 130 ° C. It is manufactured and provided with sea inputs such as seaweeds and lake block, etc., and it is nature-friendly, excellent strength, and water quality can be improved by the compound contained in sulfur concrete composition.
일반적으로 콘크리트는 시멘트가 물과 반응하여 굳어지는 수화반응을 이용하여 시멘트에 모래와 자갈, 골재 따위를 적당히 섞고 물에 반죽한 혼합물을 말하는 것으로, 만드는 방법이 간단하고 내구성이 커서 토목 공사나 건축의 주요 재료로 사용되며, 순수한 콘크리트는 인장력에 약하기 때문에, 주로 철근을 이용하여 보강하며, 이러한 콘크리트를 이용하여, 주택, 건물 등의 건축 구조물은 물론, 댐이나 도로포장·교량 등의 토목 공사는 물론, 개·관수로관이나 호안블록에 이용하거나, 또는, 인공어초, 인공해림초, 테트라포트 등과 같은 일정 강도를 가진 바다투입물에 사용되고 있다.
In general, concrete refers to a mixture of cement, sand, gravel, aggregate, etc. mixed with water and kneaded in water by using a hydration reaction in which cement reacts with water, and the method of making concrete is simple and durable. It is used as a main material, and pure concrete is weak in tensile strength, so it is mainly reinforced with reinforcing bars. Using this concrete, as well as civil works such as dams, road pavements and bridges, as well as building structures such as houses and buildings In addition, it is used for open-water irrigation pipes and shore banks, or for sea input having a certain strength such as artificial reefs, artificial seaweeds, and tetraports.
그러나 종래 콘크리트의 경우 주재료가 시멘트를 사용하는데, 이들을 시공한 후에는 이들로부터 발생하는 시멘트의 독성(예를 라돈과 같은 기타 중금속)들이 배출되어, 강가의 호안블록이나 바다투입물에 사용하면서, 식물, 어류, 동물 등에 유해한 문제점이 있었다.
However, in the case of conventional concrete, the main material is cement, and after construction, the toxins of cement (e.g., other heavy metals such as radon) generated from them are discharged, and used in river banks and sea inputs, plants, There was a problem that is harmful to fish, animals and the like.
아울러, 일반 콘크리트로 토목 구조물로 사용하면 시간이 지나면서 레이턴스의 발생으로 표면이 깨끗하지 못한 문제점이 있었으며, 종래 콘크리트를 폐기할 때에는, 환경에 대한 유해성으로 별로로 수집하여 폐기처분하여야 하므로, 처리 비용이 높고, 매립시에는 각종 환경 오염을 유발하는 문제점이 있으므로, 친환경적인 콘크리트 조성물의 개발이 요구되고 있다.
In addition, when used as a civil engineering structure as a general concrete, there was a problem that the surface is not clean due to the generation of latencies over time, and when the conventional concrete is disposed, it must be collected and disposed of separately as hazardous to the environment, Since the cost is high and there is a problem of causing various environmental pollution during landfill, the development of environmentally friendly concrete composition is required.
따라서 본 발명은 상기의 문제점을 해결하고자, 쇄석, 바텀 애쉬, 순환 골재 중에서 적어도 하나 선택한 골재류, 유황 폴리머 시멘트, 마사토, 황토 분말로 구성하는 유황 콘크리트 조성물을 구비하고, 그 유황 콘크리트 조성물을 120℃ 내지 130℃의 온도로 가열하면서 교반한 모르타르를 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제조·제공되어, 유황 콘크리트 조성물의 배합물에 의해 자연친화적이며, 강도가 우수하고, 수질을 개선하도록 한다. Therefore, the present invention is to solve the above problems, is provided with a sulfur concrete composition composed of aggregates, sulfur polymer cement, masato, ocher powder at least one selected from crushed stone, bottom ash, recycled aggregate, the sulfur concrete composition 120 ℃ It is manufactured and provided with sea inputs such as artificial reefs, tetrapots, artificial seaweeds, and raft blocks using a heated mortar while heating to a temperature of from 130 ° C to 130 ° C. To improve the water quality.
또한, 상기 유황 콘크리트 조성물에는 제오라이트나 패각류 껍데기 분쇄물 중에 선택한 기능성 물질이 더 추가되어, 이 유황 콘크리트 조성물로 제조한 물건을 바다에 투입함에 따라, 제오라이트에 의해 수질을 개선하거나, 또는, 패각류 껍데기 분쇄물에 의해 수중에 칼슘을 공급하도록 한다.
In addition, the sulfur concrete composition is further added to the functional material selected in the zeolite or shell shell shell crushed, by improving the water quality by the zeolite as the article made by the sulfur concrete composition into the sea, or shellfish Calcium is supplied to the water by shell grinding.
이와 같이 본 발명은, 쇄석, 바텀 애쉬, 순환 골재 중에서 적어도 하나 선택한 골재류, 유황 폴리머 시멘트, 마사토, 황토 분말로 구성하는 유황 콘크리트 조성물을 구비하고, 그 유황 콘크리트 조성물을 120℃ 내지 130℃의 온도로 가열하면서 교반한 모르타르를 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제조·제공되어, 유황 콘크리트 조성물의 배합물에 의해 자연친화적이며, 강도가 우수하고, 수질을 개선하는 효과가 있다.As described above, the present invention includes a sulfur concrete composition composed of at least one aggregate selected from crushed stone, bottom ash, and recycled aggregate, sulfur polymer cement, masato, and ocher powder, and the sulfur concrete composition has a temperature of 120 ° C to 130 ° C. It is manufactured and provided with sea inputs such as artificial reefs, tetrapots, artificial seaweeds, and raft blocks using a mortar stirred while heating, and is naturally friendly with the sulfur concrete composition. Has the effect of improving.
또한, 상기 유황 콘크리트 조성물에는 제오라이트나 패각류 껍데기 분쇄물 중에 선택한 기능성 물질이 더 추가되어, 이 유황 콘크리트 조성물로 제조한 물건을 바다에 투입함에 따라, 제오라이트에 의해 수질을 개선하거나, 또는, 패각류 껍데기 분쇄물에 의해 수중에 칼슘을 공급하는 효과가 있다.
In addition, the sulfur concrete composition is further added to the functional material selected in the zeolite or shell shell shell crushed, by improving the water quality by the zeolite as the article made by the sulfur concrete composition into the sea, or shellfish There is an effect of supplying calcium into the water by the shell mill.
본 발명은 마사토와 황토가 포함된 유황 콘크리트 조성물 및 그 유황 콘크리트 조성물로 만들어지는 바다투입물 및 호안블록에 관한 것으로, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 20∼50 중량부, 황토 분말 1∼5 중량부, 쇄석 30∼50 중량부로 구성하는 유황 콘크리트 조성물을 구비하고, 그 유황 콘크리트 조성물을 120℃ 내지 130℃의 온도로 가열하면서 교반한 모르타르를 이용하여, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물 및 호안블록 등으로 제조·제공되어, 유황 콘크리트 조성물에 포함되는 배합물에 의해 자연친화적이며, 강도가 우수하고, 수질을 개선할 수 있는 것이다.
The present invention relates to a sulfur concrete composition containing masato and ocher, and a sea input and a lake block made from the sulfur concrete composition, and 20 to 50 parts by weight of masato, and ocher powder 1 with respect to 30 to 55 parts by weight of sulfur polymer cement. Artificial reefs, tetrapots and artificial seaweeds were prepared by using a mortar that had a sulfur concrete composition composed of ˜5 parts by weight and 30 to 50 parts by weight of crushed stone and stirred while heating the sulfur concrete composition to a temperature of 120 ° C to 130 ° C. It is manufactured and provided with sea inputs such as seaweeds and lake block, etc., and it is nature-friendly, excellent strength, and water quality can be improved by the compound contained in sulfur concrete composition.
본 발명에 따른 유황 콘크리트 조성물과 그 유황 콘크리트 조성물로 제조된 바다투입물 및 호안블럭을 순차로 설명하면 다음과 같다.
The sulfur concrete composition according to the present invention and the sea inputs and the rake block made of the sulfur concrete composition are described in sequence.
먼저, 본 발명에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트, 마사토, 황토 분말, 골재류, 또는, 기능성물질로 구성하고, 골재류는 쇄석, 바텀 애쉬, 순환 골재 중에서 적어도 하나 선택하여 사용하며, 기능성물질은 제오라이트나 패각류 껍데기 분쇄물 중에서 선택하여 사용하는데, 이러한 유황 콘크리트 조성물은 골재류의 종류나 분쇄물의 포함에 따라 7개의 실시예를 가지며, 각 실시예에 따른 배합비와 배합예를 상세히 설명하면 다음과 같다.
First, the sulfur concrete composition according to the present invention is composed of sulfur polymer cement, masato, ocher powder, aggregates, or a functional material, and the aggregates are used by selecting at least one of crushed stone, bottom ash, and circulating aggregate. The material is selected from zeolite or shell shell crushed, and the sulfur concrete composition has seven embodiments according to the type of aggregate or the inclusion of crushed, and the mixing ratio and the blending example according to each embodiment will be described in detail. As follows.
첫 번째로, 제 1실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 20∼50 중량부, 황토 분말 1∼5 중량부, 쇄석 30∼50 중량부로 구성한다.First, the sulfur concrete composition according to the first embodiment is composed of 20 to 50 parts by weight of masato, 1 to 5 parts by weight of ocher powder, and 30 to 50 parts by weight of crushed stone based on 30 to 55 parts by weight of sulfur polymer cement.
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 쇄석은 250㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder is used in the size of 200 mesh or more, it is preferable to use a size of 250 mm or less. .
그리고 이러한 제 1실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 800㎏, 마사토 480㎏, 황토 분말 24㎏, 쇄석 696㎏으로 구성한다.And when looking at the mixing example of the sulfur concrete composition according to the first embodiment, sulfur polymer cement 800kg, Masato 480kg, ocher powder 24kg, crushed stone 696kg.
아울러, 앞서 설명한 제 1실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 1]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the first embodiment described above are shown in the following [Table 1].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
두 번째로, 제 2실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼50 중량부에 대해서, 마사토 10∼30 중량부, 황토 분말 0.5∼3 중량부, 바텀 애쉬 40∼60 중량부로 구성한다.Secondly, the sulfur concrete composition according to the second embodiment is composed of 10 to 30 parts by weight of masato, 0.5 to 3 parts by weight of ocher powder, and 40 to 60 parts by weight of bottom ash, based on 30 to 50 parts by weight of sulfur polymer cement. .
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 바텀 애쉬는 150㎜㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the ocher powder particle size of 200 mesh or more, bottom ash is 150 mm mm or less to use the size desirable.
또, 이러한 제 2실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 750㎏, 마사토 290㎏, 황토 분말 10㎏, 바텀 애쉬 950㎏으로 구성한다.In addition, when looking at the mixing example of the sulfur concrete composition according to the second embodiment, it is composed of 750 kg of sulfur polymer cement, 290 kg of Masato, 10 kg of ocher powder, 950 kg of bottom ash.
아울러, 앞서 설명한 제 2실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 2]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the second embodiment described above are shown in the following [Table 2].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
세 번째로, 제 3실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 50∼65 중량부에 대해서, 마사토 20∼40 중량부, 황토 분말 1∼3 중량부, 순환 골재 15∼45 중량부로 구성한다.Thirdly, the sulfur concrete composition according to the third embodiment is composed of 20 to 40 parts by weight of masato, 1 to 3 parts by weight of ocher powder, and 15 to 45 parts by weight of recycled aggregate, based on 50 to 65 parts by weight of sulfur polymer cement. .
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 순환 골재는 40㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder is used in the size of 200 mesh or more, it is preferable to use a size of 40 mm or less circulating aggregate. Do.
또, 이러한 제 3실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 1100㎏, 마사토 500㎏, 황토 분말 25㎏, 순환 골재 375㎏으로 구성한다.In addition, when looking at the blending example of the sulfur concrete composition according to the third embodiment, 1100kg of sulfur polymer cement, 500kg of masato, 25kg of ocher powder, 375kg of circulating aggregate.
아울러, 앞서 설명한 제 3실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 3]에 나타내었다.
In addition, the mixing ratio and the mixing example for the sulfur concrete composition according to the third embodiment described above are shown in the following [Table 3].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
네 번째로, 제 4실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼50 중량부에 대해서, 마사토 20∼40 중량부, 황토 분말 1∼3 중량부, 쇄석 20∼50 중량부, 바텀 애쉬 20∼45 중량부로 구성한다.Fourthly, the sulfur concrete composition according to the fourth embodiment includes 20 to 40 parts by weight of masato, 1 to 3 parts by weight of ocher powder, 20 to 50 parts by weight of crushed stone, and bottom ash based on 30 to 50 parts by weight of sulfur polymer cement. It consists of 20-45 weight part.
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 쇄석은 250㎜㎜ 이하 크기, 바텀 애쉬 150㎜㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder is 200 mesh or more, crushed stone is 250 mm mm or less, bottom ash 150 mm Preference is given to using sizes of mm or less.
또, 이러한 제 4실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 700㎏, 마사토 330㎏, 황토 분말 20㎏, 쇄석 530㎏, 바텀 애쉬 420㎏으로 구성한다.In addition, when looking at the mixing example of the sulfur concrete composition according to the fourth embodiment, the sulfur polymer cement 700kg, Masato 330kg, ocher powder 20kg, crushed stone 530kg, bottom ash 420kg.
아울러, 앞서 설명한 제 4실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 4]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the fourth embodiment described above are shown in the following [Table 4].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
다섯 번째, 제 5실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 20∼35 중량부, 황토 분말 0.5∼3 중량부, 제오라이트 25∼65 중량부로 구성한다.Fifth, the sulfur concrete composition according to the fifth embodiment is composed of 20 to 35 parts by weight of masato, 0.5 to 3 parts by weight of ocher powder, and 25 to 65 parts by weight of zeolite with respect to 30 to 55 parts by weight of sulfur polymer cement.
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 제오라이트는 250㎜㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder is 200 mesh or more in size, zeolite is preferably 250 mm mm or less in size Do.
또, 이러한 제 5실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 900㎏, 마사토 500㎏, 황토 분말 10㎏, 제오라이트는 590㎏으로 구성한다.In addition, in the blending example of the sulfur concrete composition according to the fifth embodiment, 900 kg of sulfur polymer cement, 500 kg of masato, 10 kg of ocher powder, and zeolite consist of 590 kg.
아울러, 앞서 설명한 제 5실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 5]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the fifth embodiment described above are shown in the following [Table 5].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
여섯 번째, 제 6실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 10∼30 중량부, 황토 분말 0.5∼3 중량부, 쇄석 10∼25 중량부, 제오라이트 20∼40 중량부로 구성한다.Sixth, the sulfur concrete composition according to the sixth embodiment, 10 to 30 parts by weight of masato, 0.5 to 3 parts by weight of ocher powder, 10 to 25 parts by weight of crushed stone, and 20 to Zeolite to 30 to 55 parts by weight of sulfur polymer cement It consists of 40 weight part.
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 쇄석은 250㎜㎜ 이하 크기, 제오라이트는 250㎜㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder uses a size of 200 mesh or more, crushed stone is 250 mm mm or less, zeolite 250 mm Preference is given to using sizes of mm or less.
또, 이러한 제 6실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 950㎏, 마사토 350㎏, 황토 분말 10㎏, 쇄석 240㎏, 제오라이트 450㎏으로 구성한다.In addition, in the blending example of the sulfur concrete composition according to the sixth embodiment, sulfur polymer cement 950 kg, Masato 350 kg, ocher powder 10 kg, crushed stone 240 kg, zeolite 450 kg.
아울러, 앞서 설명한 제 6실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 6]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the sixth embodiment described above are shown in the following [Table 6].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
마지막으로, 제 7실시예에 따른 유황 콘크리트 조성물은, 유황 폴리머 시멘트 30∼55 중량부에 대해서, 마사토 10∼30 중량부, 황토 분말 0.5∼3 중량부, 쇄석 15∼45 중량부, 바텀 애쉬 10∼20 중량부, 순환 골재 5∼40 중량부, 패각류 껍데기 분쇄물 1∼10 중량부로 구성한다.Finally, the sulfur concrete composition according to the seventh embodiment is 10 to 30 parts by weight of Masato, 0.5 to 3 parts by weight of ocher powder, 15 to 45 parts by weight of crushed stone, and bottom ash 10 to 30 to 55 parts by weight of sulfur polymer cement. It consists of -20 weight part, circulating aggregate 5-40 weight part, and shellfish shell grinding 1-10 weight part.
한편, 유황 콘크리트 조성물에 포함되는 배합물의 입자 크기를 살펴보면, 마사토는 10㎜ 이하 크기를 사용하고, 황토 분말의 입자 크기는 200mesh 이상 크기를 사용하며, 쇄석은 250㎜㎜ 이하 크기, 바텀 애쉬는 150㎜㎜ 이하 크기, 순환 골재는는 40㎜㎜ 이하 크기, 패각류 껍데기 분쇄물은 10㎜㎜ 이하 크기를 사용하는 것이 바람직하다.On the other hand, when looking at the particle size of the formulation contained in the sulfur concrete composition, Masato is 10 mm or less in size, the particle size of the ocher powder is 200 mesh or more, crushed stone is 250 mm mm or less, bottom ash 150 It is preferable to use a size of mm or less, the size of the circulating aggregate is 40 mm or less, and the shellfish shell crushed product is 10 mm or less.
또, 이러한 제 7실시예에 따른 유황 콘크리트 조성물의 배합예를 보면, 유황 폴리머 시멘트 980㎏, 마사토 320㎏, 황토 분말 10㎏, 쇄석 400㎏, 바텀 애쉬 150㎏, 순환 골재 100㎏, 패각류 껍데기 분쇄물 40㎏으로 구성한다.In addition, in the combination example of the sulfur concrete composition according to the seventh embodiment, sulfur polymer cement 980 kg, Masato 320 kg, ocher powder 10 kg, crushed stone 400 kg, bottom ash 150 kg, circulating aggregate 100 kg, shell shells It consists of 40 kg of comminutes.
아울러, 앞서 설명한 제 7실시예에 따른, 유황 콘크리트 조성물에 대한 배합비와 배합예를 다음 [표 7]에 나타내었다.
In addition, the blending ratio and blending example for the sulfur concrete composition according to the seventh embodiment described above are shown in the following [Table 7].
(중량부)Mixing ratio
(Parts by weight)
(㎏)Formulation example
(Kg)
이렇게 구성하는 유황 콘크리트 조성물은, 단순한 모양, 인공어초, 테트라포트, 인공해림초와 같은 바다투입물, 또는, 호안블록 등의 물건으로 제조되는데, 간단히 제조 방법을 설명하면, 앞서 설명한 배합비로 혼합되어, 120 내지 150℃의 온도로 교반한 모르타르를 구성하고, 만들려고 하는 형상의 몰드 내부(필요에 따라, 몰드 내부에 철근을 배근할 수도 있다)에 교반된 모르타르를 거푸집에 타설하면서 진동으로 다진 다음, 상온에서 냉각 완료한 후에 바로 탈형하면, 바다투입물, 호안블록의 제조가 완료된다.
The sulfur concrete composition constituted as described above is manufactured in a simple shape, sea inputs such as artificial reefs, tetrapots, artificial seaweeds, or articles such as rafting blocks. The mortar was stirred at a temperature of 120 to 150 ° C., and the mortar was stirred in a mold while vibrating the mortar stirred in the mold (if necessary, the reinforcing bar may be placed inside the mold). If the mold is demoulded immediately after the cooling is completed at room temperature, the preparation of sea inputs and raft blocks is completed.
참고로, 앞서 유황 콘크리트 조성물을 교반하기 위해서는, 가열기가 내장된 교반기, 또는, 통상의 교반기와 상기 교반기를 가열할 수 있는 가열 수단이 구비되어, 온도 유지와 교반이 용이하도록 하는 것이 바람직하다.
For reference, in order to stir the sulfur concrete composition, it is preferable that a stirrer with a heater or a heating device capable of heating the stirrer with a conventional stirrer is provided to facilitate temperature maintenance and agitation.
이렇게 본 발명에 따른 유황 콘크리트 조성물로 제조하는 바다투입물은, 구형, 원통형, 삼각뿔형 형상과 같은 간단한 모양으로 제조하거나, 테트라포트(tetrapod), 인공해림초 등으로 제조되어 바다에 투입하여 사용하는데, 친환경적이며, 다양한 바다 생물의 서식처가 되도록 하며, 마사토, 황토 분말, 제오라이트 등에 의해 항균 작용, 오염 방지 및 수질 정화 효과를 가지며, 패각류 껍데기 분쇄물에 의해서 수중에 칼슘을 공급하며, 쇄석, 순환 골재, 바텀 애쉬와 같은 골재류 및 유황 폴리머 시멘트가 포함되어, 밀도가 높고, 내구성과 강도가 우수한 특징이 있다.
Thus, the sea input prepared by the sulfur concrete composition according to the present invention is prepared in a simple shape, such as spherical, cylindrical, triangular pyramid shape, or manufactured by using tetrapod, artificial seaweed, etc. It is eco-friendly and provides habitat for various sea creatures. It has antibacterial effect, anti-pollution and water purification effect by masato, ocher powder, zeolite, etc., and supplies calcium in water by shell shell crushing. Aggregates, such as bottom ash, and sulfur polymer cement are included, and are characterized by high density, excellent durability and strength.
또한, 본 발명에 따른 유황 콘크리트 조성물로 제조하는 호안블록은, 해안가, 강가 및 부둣가 등에 설치되어 사용되는데, 친환경적이고, 주변의 오염물을 흡착하면서 수질을 정화하는 효과가 있다.
In addition, the revetment block produced by the sulfur concrete composition according to the present invention is used to be installed on the shore, riverside and dockside, etc., is environmentally friendly, and has the effect of purifying the water quality while adsorbing the surrounding contaminants.
이외에도, 상기 유황 콘크리트 조성물은, 직육면체, 원기둥 모양 등 다양한 모양으로 제작되어, 수족관 및 어항에 투입하여 사용하거나, 또는, 바다, 저수지 또는 호수 등에 그대로 투입하거나, 또는, 수면 근처에서 떠 있는 상태를 유지하도록, 공과 같이 속이 빈 구, 또는 발포 폴리스티렌과 같이 물에 뜨는 부체(浮體, floating body)에 연결하여 수심이 깊은 호수, 저수지 등에 투입하면, 수중의 오염물을 흡착하여 수질을 정화할 수 있는 것이다.
In addition, the sulfur concrete composition is manufactured in various shapes such as a rectangular parallelepiped and a cylindrical shape, and used in an aquarium and a fish tank, or used as it is in an ocean, a reservoir or a lake, or kept floating near the surface of the water. If you connect it to a hollow sphere like a ball or a floating body such as expanded polystyrene and put it in a deep lake or reservoir, you can absorb the pollutants in the water and purify the water quality. .
또한, 상기 포함되는 유황 콘크리트 조성물을 구성하는 배합물 대해서 각각 간단히 설명하면 다음과 같다.In addition, briefly explaining each of the formulations constituting the sulfur concrete composition included as follows.
먼저, 유황 폴리머 시멘트(S.P.C, Sulfur Polymer Cement)는, 산업 부산물로서의 유황을 화학 기질재 특성인 폴리머 반응을 이용하는 것으로서, 열을 통하여 황이 용융되고 이에 따른 황의 점성을 이용한 재료이고, 종래의 석회 콘크리트처럼 시멘트와 물이 반응하여 경화되는 것이 아니라 가열을 통한 용융과 자연 냉각을 통한 경화로 이루어지는 원리이며, 고강도, 속경성 및 화학저항성을 재료로, 친환경적이고, 내구성이 우수하며, 노후화되어 폐기처분을 할 경우 재활용이 쉬어 환경 친화적인 특징이 있다.
First, Sulfur Polymer Cement (SPC) is a material that uses sulfur as an industrial by-product and uses a polymer reaction, which is a characteristic of a chemical substrate, and is a material that melts sulfur through heat and thereby uses the viscosity of sulfur. Cement and water do not react and harden, but they are melted by heating and hardened by natural cooling.It is made of high strength, fast-hardening and chemical resistance material, which is environmentally friendly, durable and obsolete. Recycling is easy and environmentally friendly.
그리고 마사토(진사토-眞砂土, 화강토)는, 화강암이 풍화하여 모래로 변한 흙(풍화 화강토)을 말하며, 친환경적인 특징이 있다.And Masato (jinsato- 眞 砂土, granite soil) refers to the soil (weather granite soil) turned into sand by weathering granite, and has an environmentally friendly feature.
그리고 황토 분말은, 일반적인 황토를 200 메시(mesh) 이상으로 분말화 한 것으로, 상기 황토는, 실리카(SiO2), 알루미나(Al2O3), 철분, 마그네슘(Mg), 나트륨(Na), 카리 등 수많은 무기질이 함유된 미세입자로, 다량의 미네랄을 포함하고, 원적외선을 다량 방사하며, 축적된 토양 미생물과 효소작용에 의한 항균, 방충, 탈취 효과, 오염 물질 제거 등의 효과가 있다.
The ocher powder is a powder of general ocher at 200 mesh or more, and the ocher is composed of silica (SiO 2 ), alumina (Al 2 O 3 ), iron, magnesium (Mg), sodium (Na), It is a fine particle containing a lot of minerals such as Kari, contains a large amount of minerals, emits a large amount of far infrared rays, and has the effect of antibacterial, insect repellent, deodorizing effect, pollutant removal by accumulated soil microorganism and enzyme action.
또한, 쇄석은 돌을 잘게 부숴서 깨뜨린 것으로, 밀도를 높이고 강도를 높이는 특징이 있다.
In addition, the crushed stone is crushed stone is broken, it is characterized by increasing the density and strength.
이어서, 바텀 애쉬(bottom ash)는 석탄이 연소할 때 노안에서 직접 보일러 바닥으로 떨어지는 재를 말하는 것(산업자원부 고시 제 2004 - 32호)으로, 규산질이 60％ 이상 함유된 다공질로 형성되어 가벼운(경량) 특성이 있다.
Subsequently, bottom ash refers to ash falling directly from the presbyopia to the boiler floor when coal is burned (Ministry of Commerce, Industry and Energy Notice No. 2004-32), which is formed into a porous material containing 60% or more siliceous and light ( Light weight) characteristics.
또, 순환 골재는, 건설폐기물의 재활용촉진에 관한 법률 제2조 제7호의 규정(건설폐기물을 물리적 또는 화학적 처리과정 등을 거쳐 제35조의 규정에 의한 품질기준에 적합하게 한 것)에 적합한 골재를 말하는 것으로, 케이에스(KS) 규격으로 규정되어 있으며, 그 중에서도 콘크리트용 순환 골재(KSF2573), 도로보조기층용 순환 골재(KSF2574)를 사용하며, 그 중, 콘크리트용 순환 골재(recycled aggregate for concrete)는, 폐콘크리트의 파쇄·처리를 거쳐 생산되어, 품질 기준(KS 규격)을 만족하는 골재를 말한다.In addition, recycled aggregates are aggregates that comply with the provisions of Article 2 (7) of the Act on the Promotion of Recycling of Construction Waste (which makes construction wastes meet the quality standards under Article 35 through physical or chemical treatment, etc.). That is, it is prescribed in KS (KS) standard, and among them, concrete aggregate aggregates (KSF2573), road aggregate layer recycled aggregates (KSF2574) are used, and among them, recycled aggregate for concrete , Aggregate which is produced through crushing and processing of waste concrete and satisfies the quality standard (KS standard).
그리고 제오라이트(Zeolite)는, 물 분자가 결정수 형태로 구조 중에 존재하는 함수(含水) 알루미늄의 규산염 광물이며, 상기 구조 중에 존재하는 결정수는, 일반 구조수와는 달리 분자로 존재하기 때문에 제오라이트를 비석수라 불리기도 하는데, 이는 가열에 따라 탈수하여도 그 구조는 파괴되지 않고, 물 분자가 있던 곳은 그대로 세공으로 남아 마치 스펀지와 같은 구조가 되었다가, 다시 그 세공에 수분이나 가스를 흡착하여 원상으로 복귀하는데, 이러한 물리적 흡착성과 화학적인 양이온 치환작용 인해서, 해양 오염 방지와 수질 정화 등에 효과가 있다.Zeolite is a silicate mineral of hydrous aluminum in which water molecules are present in the form of crystal water, and since the crystal water in the structure is present as a molecule unlike general structure water, It is also called non-stone, and it does not destroy the structure even if it is dehydrated by heating, and the water molecules were left as pores as if it were a sponge-like structure. This physical adsorption and chemical cation substitution effect is effective in preventing marine pollution and water purification.
마지막으로, 패각류 껍데기 분쇄물은 굴이나 조개 등과 같은 패각류의 껍데기를 9㎜ 이하의 크기로 분쇄한 것으로 패각류 껍데기 분쇄물은 바다투입물이 물속에 투입되어, 바다투입물이 물속에서 수중으로 칼슘을 공급하여, 황산 이온의 발생을 억제하는 효과가 있다.
Finally, shell shell crushed shell is a crushed shell of shellfish such as oysters or shells with a size of 9 mm or less. Shell shell crushed shell is made by sea inputs into the water, and sea inputs into the water It is effective to suppress the generation of sulfate ions by supplying the
Claims (9)
A sulfur concrete composition containing masato and ocher, comprising 30 to 50 parts by weight of sulfur polymer cement, 10 to 30 parts by weight of masato, 0.5 to 3 parts by weight of ocher powder, and 40 to 60 parts by weight of bottom ash.
Masato and loess are characterized by comprising 30 to 50 parts by weight of sulfur polymer cement, 20 to 40 parts by weight of masato, 1 to 3 parts by weight of ocher powder, 20 to 50 parts by weight of crushed stone, and 20 to 45 parts by weight of bottom ash. Sulfur concrete composition included.
To 30 to 55 parts by weight of sulfur polymer cement, Masato 10 to 30 parts by weight, loess powder 0.5 to 3 parts by weight, crushed stone 15 to 45 parts by weight, bottom ash 10 to 20 parts by weight, circulating aggregate 5 to 40 parts by weight, shell Sulfur concrete composition containing masato and ocher, characterized by consisting of 1 to 10 parts by weight of crushed shells.