KR101265992B1 - Method of manufacturing crystal glass ornament for showed Nacre-pattern - Google Patents

Method of manufacturing crystal glass ornament for showed Nacre-pattern Download PDF

Info

Publication number
KR101265992B1
KR101265992B1 KR1020080110843A KR20080110843A KR101265992B1 KR 101265992 B1 KR101265992 B1 KR 101265992B1 KR 1020080110843 A KR1020080110843 A KR 1020080110843A KR 20080110843 A KR20080110843 A KR 20080110843A KR 101265992 B1 KR101265992 B1 KR 101265992B1
Authority
KR
South Korea
Prior art keywords
mother
pearl
pattern
crystal
plate
Prior art date
Application number
KR1020080110843A
Other languages
Korean (ko)
Other versions
KR20100052003A (en
Inventor
김기홍
김민진
Original Assignee
김민진
김기홍
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김민진, 김기홍 filed Critical 김민진
Priority to KR1020080110843A priority Critical patent/KR101265992B1/en
Publication of KR20100052003A publication Critical patent/KR20100052003A/en
Application granted granted Critical
Publication of KR101265992B1 publication Critical patent/KR101265992B1/en

Abstract

본 발명은 자개무늬가 표출되는 크리스탈 장식물의 제조방법에 관한 것으로, 특수코팅된 자개판(10)을 요구되는 형상으로 절단하는 재단단계(S100)와; 상기 재단단계에 의해 가공된 자개판(10)의 배면에 자개장식물의 용도에 따라 그에 알맞은 명도 및 색깔의 도료를 채색인쇄하여 배색층(20)을 형성하는 배면인쇄단계(S200)와; 상기 배면인쇄단계에 의해 자개판(10)의 배색층(20) 배면에 접착제나 양면처리 된 접착 이형지(30)를 부착하는 이형지부착단계(S300)와; 상기 이형지부착단계에 의해 배면에 이형지(30)가 부착된 자개판(10)의 전면에 디지털인쇄방법에 의해 자개 패턴의 무늬를 인쇄하여 배경색층(40)을 형성하는 제1전면인쇄단계(S400)와; 상기 제1전면인쇄단계의 배경색층(40)에 실크스크린 인쇄방법에 의해 무늬층(50)을 형성하는 제2전면인쇄단계(S500)와; 상기 제2전면인쇄단계에 의해 자개판(10)의 표면에 형성된 배경색층(40)과 무늬층(50)에 투명의 무항변 도료를 이용하여 상기 자개판(10)의 표면에 투명코팅층(60)을 형성하여 경화하는 코팅단계(S600)와; 상기 코팅단계에 의해 형성된 자개판(10)의 투명코팅층(60) 표면에 접착부재(70)를 도포하고, 자개판(10)의 형상에 대응하는 투명한 크리스탈(80)을 구비하여 그 배면에 자개판(10)을 대응시켜 경화기(H)에서 경화하는 증착단계(S700)와; 상기 증착단계에 의해 자개판(10)과 크리스탈(80)을 완전 증착한 후, 자개판(10) 배면의 이형지(30)를 제거하고, 우단 또는 미러 금속판 등으로 형성된 상패, 상장, 액자 등의 물품 표면에 접착하여 마감처리하는 마감단계(S800);로 이루어지는 것을 특징으로 하는 자개무늬가 표출되는 크리스탈 장식물의 제조방법.The present invention relates to a method of manufacturing a crystal ornament, the mother-of-pearl pattern is expressed, cutting step (S100) for cutting the specially coated mother-of-pearl plate 10 to the required shape; A back printing step (S200) of forming a color layer 20 by coloring and printing paints of appropriate brightness and color according to the purpose of the mother-of-pearl plants on the back of the mother-of-pearl plate 10 processed by the cutting step; A release paper attaching step (S300) for attaching adhesive or double-sided adhesive release paper 30 to the rear surface of the color layer 20 of the mother-of-pearl plate 10 by the back printing step; First front printing step of forming a background color layer 40 by printing a pattern of the mother-of-pearl pattern by a digital printing method on the front of the mother-of-pearl plate 10 having the release paper 30 attached to the back by the step of attaching the release paper (S400). )Wow; A second front printing step (S500) of forming a pattern layer 50 on the background color layer 40 of the first front printing step by a silk screen printing method; The transparent coating layer 60 is formed on the surface of the mother pad 10 using a transparent anhydrous paint on the background color layer 40 and the pattern layer 50 formed on the surface of the mother pad 10 by the second front printing step. Coating step (S600) to form and harden; The adhesive member 70 is coated on the surface of the transparent coating layer 60 of the mother plate 10 formed by the coating step, and is provided with a transparent crystal 80 corresponding to the shape of the mother plate 10. Deposition step (S700) to correspond to the plate 10 to cure in the curing machine (H); After completely depositing the mother-of-pearl 10 and the crystal 80 by the deposition step, the release paper 30 on the back of the mother-of-pearl 10 is removed, and a plaque, certificate, picture frame, etc. formed of a right end or a mirror metal plate, etc. A finishing step (S800) by adhering to the surface of the article to finish the treatment; Method of producing a crystal ornament, characterized in that the mother-of-pearl pattern.

자개판, 크리스탈, 증착. Mother board, crystal, vapor deposition.

Description

자개무늬가 표출되는 크리스탈 장식물의 제조방법{Method of manufacturing crystal glass ornament for showed Nacre-pattern}Method of manufacturing crystal glass ornament for showed Nacre-pattern}

본 발명은 자개무늬가 표출되는 크리스탈 장식물의 제조방법에 관한 것으로, 더욱 상세하게는 투명한 크리스탈 장식물의 배면에 자개무늬를 액상의 UV 접착제 또는 에폭시 수지의 접착부재를 이용하여 접착함으로써, 크리스탈과 자개판의 접착부위의 불량없이 자개판에 형성된 자개무늬가 투명한 크리스탈 전면으로 깨끗하고 미려하게 표출되고, 자개무늬를 가진 크리스탈 장식물의 제조가 용이하여 대량생산이 가능하며, 높은 품질과 품격을 가진 제품의 생산이 가능하여 고부가가치를 실현할 수 있는 자개무늬가 표출되는 크리스탈 장식물의 제조방법에 관한 것이다. The present invention relates to a method for producing a crystal ornament in which the mother-of-pearl pattern is expressed, and more particularly, by adhering the mother-of-pearl pattern on the back of the transparent crystal ornament using a liquid UV adhesive or an adhesive member of an epoxy resin, the crystal and mother-of-pearl plate The mother-of-pearl pattern formed on the mother-of-pearl plate is clean and beautifully expressed on the transparent crystal surface without defects of the adhesive part of the mother-of-pearl. The present invention relates to a method for producing a crystal ornament in which mother-of-pearl pattern is expressed, which can realize high added value.

일반적으로 상장 또는 상패, 다양한 기념패, 액자, 거울, 가구 등의 물품에는 물품의 품질 및 품격을 높이기 위한 수단의 하나로 다양한 무늬를 형성하게 된다. 이러한 물품에 형성되는 무늬는 물품의 제작시, 물품 표면에 다양한 무늬를 직접 인쇄하는 방법과 별도로 제작된 장식물을 부착하여 무늬를 형성하는 방법 등을 들 수 있다. Generally, items such as certificate or plaque, various commemorative plaques, picture frames, mirrors, furniture, etc. form various patterns as one of means for enhancing the quality and dignity of the goods. Patterns formed on such articles include a method of directly printing a variety of patterns on the surface of the article, and a method of forming a pattern by attaching a decorative material produced separately.

상기의 방법중 후자에 속하는 별도로 제작된 장식물을 부착하여 물품의 품질이나 품격을 높일 수 있도록 된 장식물이 현재 다양하게 개발되어 있다. 이러한 장식물 중의 하나로 자개를 이용한 것을 들 수 있다. 현재 다양하게 사용되고 있는 자개를 이용한 장식물은 상장 또는 상패, 다양한 기념패, 액자, 거울, 가구 등의 물품 표면에 다양한 무늬를 장식하고, 품질 및 품격을 높여 상품가치를 증대시키고, 높은 부가가치를 창출하고 있다.Among the above methods, a variety of decorations have been developed that are capable of improving the quality and quality of articles by attaching separately made decorations belonging to the latter. One of such decorations is the one using mother-of-pearl. Decorations using mother-of-pearl that are currently being used in various ways are decorated with various patterns on the surface of items such as certificate or plaque, various memorial plaques, frames, mirrors, furniture, etc., increasing the value and quality of goods and creating high added value. .

따라서, 상술한 바와 같이 물품의 품질 및 품격을 높이고, 이로 인해 상품가치의 상승과 높은 부가가치의 창출이 가능한 자개를 이용한 물품이 다수 개시되고 있다. 그러나, 이러한 자개을 이용한 장식물은 그 제작방법이 상당히 어렵고, 높은 비용이 발생된다는 단점을 가진다. Therefore, as described above, a number of articles using mother-of-pearl which can improve the quality and class of the article and thereby increase the product value and create high added value are disclosed. However, the decoration using the mother-of-pearl has the disadvantage that the manufacturing method is quite difficult and high cost is generated.

여기서, 자개를 이용한 장식물의 종래 제작방법을 살펴보면 자개를 절삭하여 자개무늬를 얻은 후 자개판의 공간에 끼워넣는 방식의 상감기법을 통하여 자개문양을 형성하는 방법이 있다.Here, a method of forming a mother-of-pearl pattern through the inlay technique of cutting the mother-of-pearl and obtaining the mother-of-pearl pattern and inserting the mother-of-pearl into the space of the mother board is described.

이와 같이 절삭에 의해 자개무늬를 형성하는 방법을 구체적으로 살펴보면 여러 조각의 얇은 자개를 에폭시 접착제등로 연결 부착하여 0.5 mm 두께의 판자개를 만든 후, 이를 10장 또는 50 장씩 적층하여 그 사이에 묽은 아교를 칠해서 부판하 여 이것을 건조시키고 최종적으로 정교한 톱날을 이용하여 색상별로 판자개를 절삭하여 문양을 얻어내는 방법이다.In detail, how to form a mother-of-pearl pattern by cutting, attaching several pieces of thin mother-of-pearl and attaching them with an epoxy adhesive, etc. to make a 0.5 mm thick plank, then laminating them by 10 or 50 sheets Glue the plate to dry it, and finally use a sophisticated saw blade to cut the plank by color to get a pattern.

이러한, 상기와 같이 색상별의 자개무늬가 얻어지면 상감기법에 의해 다양한 색상의 자개무늬를 형성하는 바, 이는 예를 들어 흰색 자개판에 청색 자개문양을 상감하여 넣기 위해서는 백색 자개판에 도안이 들어갈 수 있는 공간을 정밀하게 절삭으로 오려서 공간을 형성한 후 역시 동일한 모양으로 청색 자개를 오려서 상기 백색 자개판에 형성된 공간에 끼워 넣어 상감기법에 의한 자개문양을 형성하게 된다.When the mother-of-pearl pattern of each color is obtained as described above, the mother-of-pearl pattern of various colors is formed by the inlay technique. For example, in order to put the blue mother-of-pearl pattern inlaid on the mother-of-pearl, the pattern goes into the white mother-of-pearl. After cutting the space that can be cut precisely to form a space, cut the blue mother-of-pearl in the same shape and insert it into the space formed on the white mother-of-pearl to form a mother-of-pearl pattern by the inlay technique.

그러나 상기와 같이 상감기법에 의한 자개무늬 형성방법은 자개절삭에 상당한 기능을 보유한 사람이라 하더라도 이는 자개무늬를 정교하게 절삭하기 위해서는 적어도 10년 이상의 고도로 숙련된 기술이 필요하게 되며 특히, 자개가 매우 얇기 때문에 한장 한장 낱장으로 자개문양을 끼워 넣는 상감공법은 요구되는 숙련도와 제조시간이 지나치게 많이 소요되어 이러한 방식으로 제조되는 칠기 제품은 매우 고가일 뿐만 아니라, 생산성이 비 상감기법에 비해 크게 저하되어 비능률적이며 자개의 두께가 얇기 때문에 쉽게 부셔져서 불량이 쉽게 발생하게 된다는 문제가 있다.However, the method of forming the mother-of-pearl pattern by the inlaid method as described above requires a highly skilled technique of at least 10 years in order to precisely cut the mother-of-pearl pattern, even if the person has a significant function in the mother-of-pearl cutting Therefore, the inlay method of inserting mother-of-pearl patterns into pieces one by one requires too much skill and manufacturing time, and lacquer products produced in this way are not only very expensive, but also the productivity is greatly reduced compared to the inlaid method, which is inefficient. Since the mother-of-pearl's thickness is thin, there is a problem that defects occur easily.

따라서 근래에는 상기와 같은 문제점에 따라 자개판의 전면에 구현하고자 하 는 다양한 색상의 자개문양을 일일이 하나씩 오려붙이는 공법에 의하지 않고서도 인쇄기법을 통하여 다양한 색상의 자개문양을 구현하고자 하는 방법이 일부 시도되고 있다.Therefore, in recent years, some attempts have been made to implement a mother-of-pearl pattern of various colors through a printing technique without the method of cut-and-paste the mother-of-pearl pattern of various colors one by one according to the above problems. It is becoming.

한편, 후자에 간략이 언급한 인쇄기법을 통한 자개무늬의 구현으로 자개무늬는 다양한 물품에 장식되고 적용되고 있다. 그러나, 대부분의 물품에 장식되는 자개무늬는 물품의 표면에 부착되는 방식으로 외부로부터의 오염 및 손상이 쉽고, 이로 인해 물품의 상품가치가 떨어져 손해를 판매자는 손해를 보는 경우가 빈번하다. On the other hand, mother-of-pearl pattern is decorated and applied to various articles by the implementation of the mother-of-pearl pattern through the printing method mentioned briefly in the latter. However, the mother-of-pearl pattern that is decorated on most articles is easily attached to the surface of the article, so that it is easy to be contaminated and damaged from the outside, and thus the seller loses the product value of the article.

이중, 대표적 물품을 예를 들어 설명하면 상장, 상패, 기념패, 액자 등의 물품을 들 수 있다. 이와 같은 물품은 다양한 장식을 위해 자개를 많이 이용하고 있는 실정이지만 대부분이 불투명한 재질의 표면에 자개무늬를 부착하여 제작되고 있어 앞서 말한 바와 같이, 외부요인으로 인한 오염과 충격에 따른 손상이 쉽고, 보관시에도 상당한 주의를 요하게 된다. 또한, 자개를 일일이 붙여 제작하여야 함으로써, 대량생산이 사실상 불가능하고, 외부 오염등으로 인한 상품성의 가치하락과 직결된다. Among these, if the typical article is explained with an example, articles, such as a certificate, a plaque, a memorial plaque, and a picture frame, are mentioned. Such items are used a lot of mother-of-pearl for various decorations, but most of them are made by attaching mother-of-pearl pattern on the surface of opaque material. As mentioned above, damages due to contamination and impact due to external factors are easy, Great care is required when storing. In addition, the mother-of-pearl must be produced one by one, which is practically impossible to mass-produce, and is directly connected to the deterioration of the merchandise value due to external contamination.

또한, 크리스탈과 같은 표면에 문양이 형성된 물품의 경우에는 자개무늬를 적용하기는 불가능하다. 일반적으로 자개무늬를 물품에 적용하기 위해서는 물품의 표면이 편평해야 하야 하고, 그렇지 못하면 자개무늬를 부착할 부분이 없어 자개무 늬를 형성이 곤란하다. 즉, 자개무늬를 접목하는 대상 물품의 형상의 제약이 많이 따르는 문제점이 있다.In addition, it is impossible to apply mother-of-pearl pattern in the case of an article having a pattern formed on a surface such as a crystal. Generally, in order to apply mother-of-pearl pattern to the article, the surface of the article must be flat, otherwise it is difficult to form mother-of-pearl because there is no part to attach mother-of-pearl pattern. That is, there is a problem that a lot of constraints on the shape of the object to be grafted mother-of-pearl pattern.

이러한 문제점을 해결하기 우해 크리스탈의 배면을 가공하여 자개무늬를 형성하는 방법이 일부 시도되고 있으나, 이러한, 배면에 자개무늬를 형성시, 단순히 접착제를 크리스탈의 배면에 도포하여 자개판을 증착함으로써, 접착제의 도포 불량과 접착제의 도포시 이물질에 의한 크리스탈의 투과율 저하 등으로 인해 배면에 형성된 자개무늬가 크리스탈 전면으로 표출불량이 발생되어 상품가치의 하락을 가져오는 결과만을 초래하고 있다. In order to solve this problem, a method of forming a mother-of-pearl pattern by processing the back side of the crystal has been attempted. However, when the mother-of-pearl pattern is formed on the back side, by simply applying an adhesive to the back side of the crystal and depositing a mother-of-pearl, Due to the poor coating of the adhesive and the decrease in the transmittance of the crystal due to the foreign matter during the application of the adhesive, the mother-of-pearl pattern formed on the back surface is poorly expressed to the front of the crystal, resulting in a decrease in the value of the product.

따라서, 본 발명은 상술한 바와 같은 문제점을 해결하기 위해 창출한 것으로, 투명한 크리스탈과 자개판이 결합된 장식물의 제조시, 투명크리스탈과 자개판의 접착부위에 이물질이나 접착불량으로 인한 자개무늬가 투명한 크리스탈 배면으로부터 전면으로의 표출불량이 방지되도록 접착부재에 의해 투명한 크리스탈의 배면에 투시되는 자개무늬가 깨끗하고 미려하게 표출되도록 증착되는 자개무늬가 표출되는 크리스탈 장식물의 제조방법을 제공하는 데 그 목적이 있다.Therefore, the present invention was created to solve the problems described above, when the decoration of the transparent crystal and the mother board, the mother-of-pearl pattern is transparent due to foreign matter or poor adhesion to the adhesive portion of the transparent crystal and mother board The object of the present invention is to provide a method for producing a crystal ornament in which mother-of-pearl pattern is deposited to be displayed cleanly and beautifully by the adhesive member so that the mother-of-pearl pattern projected on the back of the transparent crystal by the adhesive member is prevented. have.

또한, 본 발명은 투명한 크리스탈의 배면에 자개판이 깨끗하고 미려하게 증착됨으로써, 품질이 우수한 제품의 생산이 가능하여 고부가가치를 실현할 수 있을 뿐만 아니라, 투명크리스탈과 자개판을 접착부재에 의해 간편하게 증착가능하여 제품의 생산성이 향상되고, 이를 통해 대량생산이 가능한 자개무늬가 표출되는 크리스탈 장식물의 제조방법에 관한 것이다. In addition, the present invention is a clean and beautiful vapor deposition on the back of the transparent crystal, it is possible to produce a product of high quality, high value-added, as well as to easily deposit the transparent crystal and magnetic shield by the adhesive member It is possible to improve the productivity of the product, through which the mother-of-pearl pattern that can be mass-produced relates to a method of manufacturing a crystal ornament.

상술한 바와 같은 목적을 해결하기 위한 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법은 특수코팅된 자개판(10)을 요구되는 형상으로 절단하는 재단단계(S100)와; 상기 재단단계에 의해 가공된 자개판(10)의 배면에 자개장식물의 용도에 따라 그에 알맞은 명도 및 색깔의 도료를 채색인쇄하여 배색층(20)을 형성하는 배면인쇄단계(S200)와; 상기 배면인쇄단계에 의해 자개판(10)의 배색층(20) 배면에 접착제나 양면처리 된 접착 이형지(30)를 부착하는 이형지부착단계(S300)와; 상기 이형지부착단계에 의해 배면에 이형지(30)가 부착된 자개판(10)의 전면에 디지털인쇄방법에 의해 자개 패턴의 무늬를 인쇄하여 배경색층(40)을 형성하는 제1전면인쇄단계(S400)와; 상기 제1전면인쇄단계의 배경색층(40)에 실크스크린 인쇄방법에 의해 무늬층(50)을 형성하는 제2전면인쇄단계(S500)와; 상기 제2전면인쇄단계에 의해 자개판(10)의 표면에 형성된 배경색층(40)과 무늬층(50)에 투명의 무항변 도료를 이용하여 상기 자개판(10)의 표면에 투명코팅층(60)을 형성하여 경화하는 코팅단계(S600)와; 상기 코팅단계에 의해 형성된 자개판(10)의 투명코팅층(60) 표면에 접착부재(70)를 도포하고, 자개판(10)의 형상에 대응하는 투명한 크리스탈(80)을 구비하여 그 배면에 자개판(10)을 대응시켜 경화기(H)에서 경화하는 증착단계(S700)와; 상기 증착단계에 의해 자개판(10)과 크리스탈(80)을 완전 증착한 후, 자개판(10) 배면의 이형지(30)를 제거하고, 우단 또는 미러 금속판 등으로 형성된 상패, 상장, 액자 등의 물품 표면에 접착하여 마감처리하는 마감단계(S800);로 이루어지는 것을 특징으로 한다. Method for producing a crystal ornament with mother-of-pearl pattern according to the present invention for solving the above object is a cutting step (S100) for cutting the specially coated mother-of-pearl plate 10 to the required shape; A back printing step (S200) of forming a color layer 20 by coloring and printing paints of appropriate brightness and color according to the purpose of the mother-of-pearl plants on the back of the mother-of-pearl plate 10 processed by the cutting step; A release paper attaching step (S300) for attaching adhesive or double-sided adhesive release paper 30 to the rear surface of the color layer 20 of the mother-of-pearl plate 10 by the back printing step; First front printing step of forming a background color layer 40 by printing a pattern of the mother-of-pearl pattern by a digital printing method on the front of the mother-of-pearl plate 10 having the release paper 30 attached to the back by the step of attaching the release paper (S400). )Wow; A second front printing step (S500) of forming a pattern layer 50 on the background color layer 40 of the first front printing step by a silk screen printing method; The transparent coating layer 60 is formed on the surface of the mother pad 10 using a transparent anhydrous paint on the background color layer 40 and the pattern layer 50 formed on the surface of the mother pad 10 by the second front printing step. Coating step (S600) to form and harden; The adhesive member 70 is coated on the surface of the transparent coating layer 60 of the mother plate 10 formed by the coating step, and is provided with a transparent crystal 80 corresponding to the shape of the mother plate 10. Deposition step (S700) to correspond to the plate 10 to cure in the curing machine (H); After completely depositing the mother-of-pearl 10 and the crystal 80 by the deposition step, the release paper 30 on the back of the mother-of-pearl 10 is removed, and a plaque, certificate, picture frame, etc. formed of a right end or a mirror metal plate, etc. It is characterized by consisting of; finishing step (S800) by adhering to the surface of the article.

여기서, 상기 투명코팅층(60)을 형성하는 무항변 도료는 에폭시 또는 우레탄 중 어느 하나인 것이 바람직하다. Here, the uncoated paint forming the transparent coating layer 60 is preferably any one of epoxy or urethane.

한편, 상기 증착단계의 접착부재(70)는 온도40℃~60℃의 경화기 내부에서 빠 르게 경화건조되어 크리스탈(80)과 자개판(10)이 빠르고 깨끗하게 증착되도록 자외선 경화 접착제인 액상의 UV 접착제 또는 기포제거제가 혼합된 액상의 에폭시 수지인 것을 특징으로 한다. On the other hand, the adhesive member 70 of the deposition step is a quick curing curing in the curing machine of the temperature 40 ℃ ~ 60 ℃ to quickly and clean the crystal 80 and mother-of-pearl plate 10 of the liquid UV adhesive which is an ultraviolet curing adhesive Or a liquid epoxy resin in which a bubble removing agent is mixed.

본 발명은 투명한 크리스탈과 자개판이 결합된 장식물의 제조시, 투명크리스탈과 자개판의 접착부위에 이물질이나 접착불량으로 인한 자개무늬가 투명한 크리스탈 배면으로부터 전면으로의 표출불량이 방지되도록, UV 접착제 또는 에폭시 수지의 접착부재에 의해 투명한 크리스탈의 배면에 투시되는 자개무늬가 깨끗하고 미려하게 표출되도록 증착되는 효과가 있다. The present invention is a UV adhesive or so that when the decoration of the transparent crystal and mother-of-pearl combination, the mother-of-pearl pattern caused by the foreign matter or poor adhesion on the adhesive portion of the transparent crystal and the mother-of-pearl prevents the display defect from the transparent crystal back to the front surface. The mother-of-pearl pattern projected on the back of the transparent crystal by the adhesive member of the epoxy resin is deposited to be clean and beautifully expressed.

또한, 본 발명은 투명한 크리스탈의 배면에 자개판이 깨끗하고 미려하게 UV 접착제 또는 에폭시 수지의 접착부재에 의해 증착됨으로써, 품질이 우수한 제품의 생산이 가능하여 고부가가치를 실현할 수 있을 뿐만 아니라, 투명크리스탈과 자개판을 UV 접착제 또는 에폭시 수지의 접착부재에 의해 간편하게 증착가능하여 제품의 생산성이 향상되고, 이를 통해 대량생산이 가능한 장점이 있다.In addition, the present invention is a mother-of-pearl is clean and beautifully deposited on the back of the transparent crystal by a UV adhesive or an epoxy resin adhesive member, it is possible to produce a product of high quality and realize high added value, transparent crystal And the mother board can be easily deposited by the adhesive member of the UV adhesive or epoxy resin to improve the productivity of the product, there is an advantage that can be mass-produced.

이하, 첨부된 도면을 참조로 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 구성 및 작용에 대하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail the configuration and operation of the method of manufacturing a crystal ornament with mother-of-pearl pattern according to the present invention.

도 1은 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 제조공정 순서도이고, 도 2는 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 단면예시도이며, 도 3은 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 적용물품의 사시도이다.1 is a manufacturing process flow chart of a method of manufacturing a crystal ornament with a mother-of-pearl pattern according to the present invention, Figure 2 is a cross-sectional view of a method of manufacturing a crystal ornament with a mother-of-pearl pattern according to the present invention, Figure 3 is a present It is a perspective view of the article of application of the manufacturing method of the crystal ornament which the mother-of-pearl pattern which concerns on this invention is expressed.

도 1에 나타난 제조공정 순서도에 나타난 바와 같이, 본 발명의 자개무늬가 표출되는 크리스탈 장식물의 제조방법은 재단단계(S100), 배면인쇄단계(S200), 이형지부착단계(S300), 제1전면인쇄단계(S400), 제2전면인쇄단계(S500), 코팅단계(S600), 증착단계(S700), 마감단계(S800)를 포함한다.As shown in the manufacturing process flow chart shown in Figure 1, the method of manufacturing a crystal ornament with the mother-of-pearl pattern of the present invention is a cutting step (S100), back printing step (S200), release paper attaching step (S300), the first front printing It includes a step (S400), the second front printing step (S500), coating step (S600), deposition step (S700), finishing step (S800).

상기 재단단계(S100)는 코팅된 자개판(10)을 요구되는 형상으로 절단하는 것으로, 후술되는 투명크리스탈(80)의 배면형상에 대응되도록 절단한다. 여기서, 요구되는 형상은 구체적으로 사각, 원형, 링형 등 다양한 형상으로 형성된 투명재질의 유리, 플라스틱 등의 물품에도 가능하다. 여기서, 자개판(10)의 절단은 소형 톰슨기를 이용하여 후술되는 크리스탈의 배면에 대응되도록 절단하는 것이 바람직하다.The cutting step (S100) is to cut the coated mother board 10 to the required shape, and cut to correspond to the back shape of the transparent crystal 80 to be described later. Here, the required shape is specifically also possible for articles such as glass, plastic, and the like formed in various shapes such as square, circle, and ring. Here, the cutting of the mother plate 10 is preferably cut so as to correspond to the back of the crystal to be described later using a small Thompson.

상기 배면인쇄단계(S200)는 앞서 말한 상기 재단단계에 의해 후술되는 투명한 크리스탈(80)의 배면 형상에 대응되도록 가공된 자개판(10)의 배면에 다양한 색상의 자개색상을 표출하도록 자개장식물의 용도에 따라 그에 알맞은 명도 및 색깔 의 도료를 채색인쇄하여 배색층(20)을 형성한다. 여기서, 상기 배색층(20)은 자개판(10)의 배면에 단일색으로 형성하게 되는 것으로, 자개는 그 자체가 반투명체의 물질로서 자개판(10)의 배면에 소정의 색채로 단일색의 배색층(20)을 형성하게 되면 그 배색층(20)의 색깔이 자개판(10)을 투과하면서 자개고유의 색채와 어우러져 고유한 빛을 나타내기 때문에 뛰어난 미감과 장식성을 표출하는 것이다.The back printing step (S200) is the use of mother-of-pearl plants to express the mother-of-pearl color of various colors on the back of the mother-of-pearl plate 10 processed to correspond to the back shape of the transparent crystal 80 to be described later by the cutting step According to the coloring and printing the paint of the appropriate brightness and color to form a color layer (20). Here, the color layer 20 is to be formed in a single color on the back of the mother-of-pearl plate 10, the mother-of-pearl is a semi-transparent material as a single color in a predetermined color on the back of the mother-of-pearl plate 10 ( 20), the color of the color layer 20 penetrates the mother-of-pearl plate 10, and is combined with the colors of the mother-of-pearl to show a unique light, thereby expressing an excellent aesthetic and decorative property.

상기 이형지부착단계(S300)는 후술되는 투명한 크리스탈(80)과 자개판(10)이 최종 증착된 후, 상장, 상패, 액자 등의 물품에 크리스탈과 자개판이 증착된 장식물이 용이하게 접착되도록 상기 배면인쇄단계에 의해 자개판(10)의 배색층(20) 배면에 접착제나 양면처리 된 접착 이형지(30)를 부착한다. The release paper attaching step (S300) is a transparent crystal 80 to be described later and the mother board 10 after the final deposition, the decoration such that the crystals and mother-of-pearl deposited on the items such as award, plaque, picture frame is easily adhered to the An adhesive or double-sided adhesive release paper 30 is attached to the rear surface of the color layer 20 of the mother-of-pearl plate 10 by the back printing step.

상기 제1전면인쇄단계(S400)는 상기 이형지부착단계에 의해 배면에 이형지(30)가 부착된 자개판(10)의 전면에 디지털인쇄방법 즉, 컴퓨터에 입력된 문양을 일러스트 파일이나 이미지파일로 디지털 평판프린트 8색기에 출력 인쇄하는 방법에 의해 자개 패턴의 무늬를 인쇄하여 배경색층(40)을 형성한다. The first front printing step (S400) is a digital printing method on the front of the mother-of-pearl plate 10 on which the release paper 30 is attached to the back by the release paper attaching step, that is, a pattern input to a computer as an illustration file or an image file. The background color layer 40 is formed by printing a mother-of-pearl pattern by a method of output printing to eight digital flatbed printers.

상기 제2전면인쇄단계(S500)는 전술한 상기 제1전면인쇄단계의 배경색층(40)에 자개 무늬의 최종 문양을 형성하는 무늬층(50)을 형성한다. 여기서, 무늬층(50)의 형성은 실크스트린 인쇄방법을 통해 형성하는 것이 바람직하다.The second front printing step S500 forms a pattern layer 50 that forms a final pattern of mother-of-pearl pattern on the background color layer 40 of the first front printing step. Here, the formation of the pattern layer 50 is preferably formed through the silk screen printing method.

상기 코팅단계(S600)는 전술한 제2전면인쇄단계에 의해 자개판(10)의 표면에 형성된 배경색층(40)과 무늬층(50)에 의해 형성된 자개무늬를 투명의 무항변 도료를 이용하여 상기 자개판(10)의 표면에 투명코팅층(60)을 형성하여 경화한다. 여기서, 투명코팅층(60)은 배경색층(40)과 무늬층(50)이 변색되는 것을 방지하고, 자개본연의 색감을 나타내도록 한다. The coating step (S600) is a mother-of-pearl pattern formed by the background color layer 40 and the pattern layer 50 formed on the surface of the mother plate 10 by the above-described second front printing step by using a transparent anus-free paint The transparent coating layer 60 is formed on the surface of the mother plate 10 to cure. Here, the transparent coating layer 60 prevents the background color layer 40 and the pattern layer 50 from being discolored, and displays the natural color of the mother of pearl.

한편, 코팅단계를 통해 투명코팅층(60)을 형성하는 상기 무항변 도료는 에폭시 또는 우레탄 중 어느 하나를 사용하는 것이 바람직하다. 일반적으로 에폭시 및 우레탄은 경화에 있어 반응수축이 매우 작고 또한 휘발물을 발생하지 않으며, 전기적, 기계적 성질이 매우 우수하고, 치수 안정성이 매우 좋으며, 내수성, 내 약품성, 내 마모성이 우수하여 자개무늬를 형성하는 배경색층(40)과 무늬층(50)의 색상의 변질을 방지할 수 있다. On the other hand, the unprotected paint to form the transparent coating layer 60 through the coating step, it is preferable to use any one of epoxy or urethane. In general, epoxy and urethane have very small reaction shrinkage in curing, do not generate volatiles, have excellent electrical and mechanical properties, very good dimensional stability, and have excellent water resistance, chemical resistance, and abrasion resistance. The alteration of the color of the background color layer 40 and the pattern layer 50 to be formed can be prevented.

상기 증착단계(S700)는 후술되는 크리스탈과 전술한 자개판을 증착하여 증착부분의 오염없이 깨끗하게 증착되어 자개판에 형성된 자개무늬가 크리스탈의 전면을 통해 아름답게 표출되도록 하는 단계로서, 전술한 상기 코팅단계에 의해 형성된 자개판(10)의 투명코팅층(60) 표면에 접착부재(70)를 도포하고, 자개판(10)의 형상에 대응하는 투명한 크리스탈(80)을 구비하여 그 배면에 자개판(10)을 대응시켜 경화기(H)에서 경화하는 단계이다. The deposition step (S700) is a step of depositing the crystal described later and the mother-of-pearl plate described above so that the mother-of-pearl pattern formed on the mother-of-pearl plate is beautifully expressed through the front surface of the crystal by depositing cleanly without contamination of the deposition portion. The adhesive member 70 is applied to the transparent coating layer 60 surface of the mother plate 10 formed by the above, and is provided with a transparent crystal 80 corresponding to the shape of the mother plate 10. ) To harden in the curing machine (H).

여기서, 투명한 크리스탈(80)은 주로 상패, 상장, 액자, 거울 등에 주로 사용되는 것으로, 배면이 편평한 면을 가지고 있어 배면에 다양한 무늬의 형성이 가능한 것이다. 즉, 종래의 단순한 크리스탈 상패, 상장, 액자, 거울 등의 물품의 무늬의 단조로움을 본 발명에 따른 자개판과 크리스탈의 증착방법을 통해 보다 다양한 무늬를 가진 크리스탈 장식물의 제공이 가능한 것은 자명한 것이며, 자개판의 크리스탈과의 증착을 통해 보다 품질이 우수한 제품의 생산이 가능한 것이다.Here, the transparent crystal 80 is mainly used in plaques, awards, picture frames, mirrors, etc., the back surface has a flat surface is capable of forming various patterns on the back surface. In other words, it is obvious that the conventional monolithic pattern of items such as a simple plaque, certificate, picture frame, mirror, etc. can be provided with a crystal decoration having more various patterns through the motherplate and crystal deposition method according to the present invention. In addition, it is possible to produce products of higher quality through deposition with crystals of mother board.

한편, 상기 크리스탈(80)과 자개판(10)을 오염없이 깨끗하게 증착하기 위한 접착부재(70)는 UV 접착제 또는 에폭시 수지 중 어느 하나를 이용한다. 여기서, 상기 UV 접착제는 자개판(10)의 투명코팅층(60)에 넓게 도포한다. On the other hand, the adhesive member 70 for cleanly depositing the crystal 80 and the mother plate 10 without contamination uses any one of a UV adhesive or an epoxy resin. Here, the UV adhesive is widely applied to the transparent coating layer 60 of the mother plate (10).

다음으로, 투명한 크리스탈(80)의 배면에 UV 접착제가 도포된 자개판(10)을 대응하여 밀착시킨다. 이후, 투명한 크리스탈(80)과 자개판(10)의 증착을 위해 온도40℃~60℃의 경화기 내부에 투입하여 투명한 크리스탈(80)과 자개판(10)이 UV 접착제에 의해 빠르게 경화건조되어 증착되도록 한다. 이와 같이, UV접착제에 의해 크리스탈(80)과 자개판(10)이 경화기 내에서 빠르게 증착됨으로써, 크리스탈(80)의 배면에 증착되는 자개판(10)이 접착불량이나 이물질의 오염없이 깨끗하게 증착되어 크리스탈(80) 표면으로부터 자개판(10)에 형성된 자개무늬가 선명한 색감을 가지며 표출되는 것이다. Next, the mother board 10 to which the UV adhesive is applied is brought into close contact with the back of the transparent crystal 80. Subsequently, the transparent crystal 80 and the mother board 10 are placed in a curing machine at a temperature of 40 ° C. to 60 ° C. to rapidly deposit and dry the transparent crystal 80 and the mother board 10 by UV adhesive. Be sure to As such, the crystal 80 and the mother plate 10 are rapidly deposited in the curing machine by the UV adhesive, so that the mother plate 10 deposited on the back of the crystal 80 is cleanly deposited without a poor adhesion or contamination of foreign matter. The mother-of-pearl pattern formed on the mother-of-pearl plate 10 from the surface of the crystal 80 is expressed with a vivid color.

한편, 투명한 크리스탈(80)과 자개판(10)의 증착은 UV 접착제 이외에 에폭시 수지로도 가능하다. 에폭시 수지는 경질 에폭시와 기포제거제를 혼합하여 자개판(10)의 투명코팅층(60)에 넓게 도포한다. On the other hand, the deposition of the transparent crystal 80 and mother plate 10 can be made of an epoxy resin in addition to the UV adhesive. The epoxy resin is applied to the transparent coating layer 60 of the mother board 10 by mixing a hard epoxy and a bubble removing agent.

다음으로, UV 접착제에 의한 증착과 동일한 방법으로 투명한 크리스탈(80)의 배면에 경질의 에폭시 수지가 도포된 자개판(10)을 대응하여 밀착시킨다. 이후, 투명한 크리스탈(80)과 자개판(10)의 증착을 위해 온도40℃~60℃의 경화기 내부에서 빠르게 경화건조되어 증착되도록 한다. 따라서, 상술한 UV 접착제와 동일하게 크리스탈(80)과 자개판(10)이 빠르게 증착되고, 크리스탈(80)의 배면에 증착되는 자개판(10)이 접착불량이나 이물질의 오염없이 깨끗하게 증착이 가능하다. Next, the mother board 10 to which the hard epoxy resin is applied is brought into close contact with the back of the transparent crystal 80 in the same manner as the vapor deposition by the UV adhesive. Thereafter, in order to deposit the transparent crystal 80 and the mother plate 10, the curing is rapidly dried in a curing machine at a temperature of 40 ° C ~ 60 ° C to be deposited. Accordingly, the crystal 80 and the mother plate 10 are quickly deposited in the same manner as the above-described UV adhesive, and the mother plate 10 deposited on the back of the crystal 80 can be cleanly deposited without poor adhesion or contamination of foreign matter. Do.

상기 마감단계(S800)는 앞서 상술한 상기 증착단계에 의해 자개판(10)과 크리스탈(80)이 완전 증착한 후, 자개판(10) 배면의 전술한 이형지(30)를 제거하고,우단 또는 미러금속판 등으로 형성된 상패, 상장, 액자 등의 물품의 표면에 접착하여 마감처리함으로써, 자개무늬가 선명하게 표출되고 미려함을 뽑낼 수 있는 크리스탈 장식물의 제작이 가능하다. The finishing step (S800) after the mother plate 10 and the crystal 80 is completely deposited by the above-described deposition step, remove the above-described release paper 30 on the back of the mother plate 10, right or By adhering to the surface of articles such as plaques, awards, frames, etc. formed by mirror metal plates and the like, the mother-of-pearl pattern can be clearly expressed and the crystal ornaments can be extracted.

상술한 바와 같이 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법는 아래의 설명과 같으며, 이하 사용상태에 따른 실시예를 설명하기로 한다. As described above, a method of manufacturing a crystal ornament in which mother-of-pearl pattern is expressed according to the present invention is as described below, and an embodiment according to a use state will be described.

도 2의 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법에 따른 실시예에 따른 단면 예시도에 나타난 바와 같이, 배면에 배색층(20)과 이형지(30)가 형성된 자개판(10)의 상부 표면에 배경색층(40)과 무늬층(50)이 형성되고, 그 표면에 에폭시를 도포하여 경화된 투명코팅층(60)을 형성한다. As shown in the cross-sectional view of the embodiment according to the method of manufacturing a crystal ornament in which the mother-of-pearl pattern according to the present invention of FIG. 2 is expressed, the mother-of-pearl plate 10 having the color layer 20 and the release paper 30 formed on the rear surface thereof is shown. Background color layer 40 and the pattern layer 50 is formed on the upper surface of, and the epoxy is applied to the surface to form a cured transparent coating layer 60.

다음으로, 도 3에 도시된 바와 같이, 상패, 상장, 액자 등의 물품을 선정하여 그 표면에 부착하는 투명한 크리스탈(80)을 구비하고, 도 2에 도시된 바와 같이, 투명한 크리스탈(80)의 배면에 자개판(10)을 대응한다. 이때, 자개판(10)의 투명코팅층(60)에는 UV 접착제 또는 에폭시 수지를 넓게 도포하여 대응한다.Next, as illustrated in FIG. 3, the transparent crystal 80 may be provided to select and attach an article such as a plaque, award, picture frame, etc. to the surface thereof, and as illustrated in FIG. The mother board 10 corresponds to the back side. At this time, the transparent coating layer 60 of the mother board 10 by applying a UV adhesive or epoxy resin widely.

다음으로, 투명한 크리스탈(80)과 UV 접착제 또는 에폭시 수지가 도포된 자개판(10)이 포개어진 상태로 경화기에 수용하여 온도40℃~60℃를 유지한 상태로 UV 접착제 또는 에폭시 수지를 빠르게 경화한다. 이때, UV 접착제 또는 에폭시 수지가 투명한 크리스탈(80)과 자개판(10) 사이에서 경화됨에 따라 투명한 크리스탈(80)과 자개판(10)의 접착부위의 불량없이 깨끗히 증착되고, 이에 따라, 자개판에 형성된 자개무늬의 배경색층(40)과 무늬층(50)이 투명한 크리스탈의 전면으로 요구되는 색상을 그대로 유지한 상태로 표출이 가능하다.Next, the transparent crystal 80 and the mother board 10 coated with the UV adhesive or epoxy resin are accommodated in a state in which the UV adhesive or the epoxy resin is rapidly cured while being kept in a temperature of 40 ° C. to 60 ° C. do. At this time, as the UV adhesive or the epoxy resin is cured between the transparent crystal 80 and the mother plate 10, the transparent crystal 80 and the mother plate 10 is deposited cleanly without a defect of the adhesive portion of the mother plate, accordingly, the mother plate The background color layer 40 and the pattern layer 50 of the mother-of-pearl pattern formed in the state can be expressed while maintaining the color required as the front of the transparent crystal.

다음으로, 투명한 크리스탈(80)과 자개판(10)이 UV 접착제 또는 에폭시 수지 중 어느 하나에 의해 증착된 후, 자개판(10) 배면의 이형지(30)를 제거한다. 이후, 상패, 상장, 액자 등의 물품의 우단 또는 미러금속판으로 형성된 표면에 크리스탈과 자개판을 증착하여 접착함으로써, 자개무늬를 표출하는 크리스탈 장식품의 제작이 가능하여 물품의 제작시간이 단축되고, 이로 인해 생산성이 향상되어 대량생산이 가능함은 물론이며, 자개무늬의 표출이 뛰어난 우수한 크리스탈 장식품의 제작이 가능하여 높은 품질의 제품을 통해 고부가가치의 제품생산이 가능한 것은 자명한 것이다. Next, after the transparent crystal 80 and the mother board 10 are deposited by either UV adhesive or epoxy resin, the release paper 30 on the back of the mother board 10 is removed. Then, by depositing and adhering the crystal and mother-of-pearl plate on the right end or the surface of the mirror metal plate, such as plaques, awards, picture frames, etc., it is possible to manufacture a crystal ornament to express the mother-of-pearl pattern, thereby shortening the production time of the article, As a result, productivity is improved and mass production is possible, as well as the production of excellent crystal ornaments with excellent expression of mother-of-pearl.

한편, 본 발명의 상세한 설명에서는 구체적인 실시예에 관해서 설명하였으나, 본 발명의 범위에서 벗어나지 않는 한도 내에서 여러가지 변형이 가능함을 당해 분야에서 통상의 지식을 가진자에게 있어서, 그와 같은 변형은 청구 범위 기재의 범위 내에 있는 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those skilled in the art that various changes and modifications may be made without departing from the scope of the invention as defined in the appended claims. Is within the scope of the description.

도 1은 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 제조공정 순서도이다.1 is a manufacturing process flow chart of a method of manufacturing a crystal ornament with mother-of-pearl pattern according to the present invention.

도 2는 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 단면예시도이다.Figure 2 is an exemplary cross-sectional view of a method of manufacturing a crystal ornament with mother-of-pearl pattern according to the present invention.

도 3은 본 발명에 따른 자개무늬가 표출되는 크리스탈 장식물의 제조방법의 적용물품의 사시도이다.Figure 3 is a perspective view of the article of application of the method of manufacturing a crystal ornament with mother-of-pearl pattern according to the present invention.

<도면의 주요부분의 부호에 대한 설명><Description of Signs of Major Parts of Drawings>

10 : 자개판 20 : 배색층10: mother-of-pearl 20: color layer

30 : 이형지 40 : 배경색층30: release paper 40: background color layer

50 : 무늬층 60 : 투명코팅층50: pattern layer 60: transparent coating layer

70 : 접착부재 80 : 크리스탈70: adhesive member 80: crystal

S100 : 재단단계 S200 : 배면인쇄단계S100: Cutting step S200: Back printing step

S300 : 이형지부착단계 S400 : 제1전면인쇄단계S300: release paper attaching step S400: first front printing step

S500 : 제2전면인쇄단계 S600 : 코팅단계S500: second front printing step S600: coating step

S700 : 증착단계 S800 : 마감단계S700: Deposition Step S800: Finishing Step

Claims (4)

코팅된 자개판(10)을 요구되는 형상으로 절단하는 재단단계(S100)와;Cutting step (S100) for cutting the coated mother board 10 into the required shape; 상기 재단단계에 의해 가공된 자개판(10)의 배면에 자개장식물의 용도에 따라 그에 알맞은 명도 및 색깔의 도료를 채색인쇄하여 배색층(20)을 형성하는 배면인쇄단계(S200)와;A back printing step (S200) of forming a color layer 20 by coloring and printing paints of appropriate brightness and color according to the purpose of the mother-of-pearl plants on the back of the mother-of-pearl plate 10 processed by the cutting step; 상기 배면인쇄단계에 의해 자개판(10)의 배색층(20) 배면에 접착제나 양면처리 된 접착 이형지(30)를 부착하는 이형지부착단계(S300)와;A release paper attaching step (S300) for attaching adhesive or double-sided adhesive release paper 30 to the rear surface of the color layer 20 of the mother-of-pearl plate 10 by the back printing step; 상기 이형지부착단계에 의해 배면에 이형지(30)가 부착된 자개판(10)의 전면에 디지털인쇄방법에 의해 자개 패턴의 무늬를 인쇄하여 배경색층(40)을 형성하는 제1전면인쇄단계(S400)와;First front printing step of forming a background color layer 40 by printing a pattern of the mother-of-pearl pattern by a digital printing method on the front of the mother-of-pearl plate 10 having the release paper 30 attached to the back by the step of attaching the release paper (S400). )Wow; 상기 제1전면인쇄단계의 배경색층(40)에 실크스크린 인쇄방법에 의해 무늬층(50)을 형성하는 제2전면인쇄단계(S500)와;A second front printing step (S500) of forming a pattern layer 50 on the background color layer 40 of the first front printing step by a silk screen printing method; 상기 제2전면인쇄단계에 의해 자개판(10)의 표면에 형성된 배경색층(40)과 무늬층(50)에 투명의 무항변 도료를 이용하여 상기 자개판(10)의 표면에 투명코팅층(60)을 형성하여 경화하는 코팅단계(S600)와;The transparent coating layer 60 is formed on the surface of the mother pad 10 using a transparent anhydrous paint on the background color layer 40 and the pattern layer 50 formed on the surface of the mother pad 10 by the second front printing step. Coating step (S600) to form and harden; 상기 코팅단계에 의해 형성된 자개판(10)의 투명코팅층(60) 표면에 접착부재(70)를 도포하고, 자개판(10)의 형상에 대응하는 투명한 크리스탈(80)을 구비하여 그 배면에 자개판(10)을 대응시켜 경화기(H)에서 경화하는 증착단계(S700)와;The adhesive member 70 is coated on the surface of the transparent coating layer 60 of the mother plate 10 formed by the coating step, and is provided with a transparent crystal 80 corresponding to the shape of the mother plate 10. Deposition step (S700) to correspond to the plate 10 to cure in the curing machine (H); 상기 증착단계에 의해 자개판(10)과 크리스탈(80)을 완전 증착한 후, 자개판(10) 배면의 이형지(30)를 제거하고, 우단 또는 미러 금속판 등으로 형성된 상패, 상장, 액자 등의 물품 표면에 접착하여 마감처리하는 마감단계(S800);로 이루어지는 것을 특징으로 하는 자개무늬가 표출되는 크리스탈 장식물의 제조방법.After completely depositing the mother-of-pearl 10 and the crystal 80 by the deposition step, the release paper 30 on the back of the mother-of-pearl 10 is removed, and a plaque, certificate, picture frame, etc. formed of a right end or a mirror metal plate, etc. A finishing step (S800) by adhering to the surface of the article to finish the treatment; Method of producing a crystal ornament, characterized in that the mother-of-pearl pattern. 제 1항에 있어서, The method of claim 1, 상기 투명코팅층(60)을 형성하는 무항변 도료는 에폭시 또는 우레탄 중 어느 하나인 것을 특징으로 하는 자개무늬가 표출되는 크리스탈 장식물의 제조방법.The uncoated paint to form the transparent coating layer 60 is a method of producing a crystal ornament, the mother-of-pearl pattern is characterized in that either epoxy or urethane. 제 1항에 있어서,The method of claim 1, 상기 증착단계의 접착부재(70)는 온도40℃~60℃의 경화기 내부에서 6시간 경화건조되어 크리스탈(80)과 자개판(10)이 깨끗하게 증착되도록 자외선 경화 접착제인 액상의 UV 접착제인 것을 특징으로 하는 자개무늬가 표출되는 크리스탈 장식물의 제조방법.The adhesive member 70 of the deposition step is a hard UV adhesive that is a UV curing adhesive so that the crystal 80 and the mother-of-pearl 10 is cleanly dried by curing within 6 hours at a temperature of 40 ° C. to 60 ° C. The method of manufacturing a crystal ornament which mother-of-pearl pattern is expressed. 제 1항에 있어서,The method of claim 1, 상기 증착단계의 접착부재(70)는 온도40℃~60℃의 경화기 내부에서 6시간 경화건조되어 크리스탈(80)과 자개판(10)이 깨끗하게 증착되도록 기포제거제가 혼합 된 액상의 에폭시 수지인 것을 특징으로 하는 자개무늬가 표출되는 크리스탈 장식물의 제조방법.The adhesive member 70 of the deposition step is a liquid epoxy resin in which a bubble removing agent is mixed so that the crystal 80 and the mother-of-pearl 10 are cleanly dried by drying for 6 hours in a curing machine having a temperature of 40 ° C. to 60 ° C. Method of producing a crystal ornament, characterized in that the mother-of-pearl pattern is characterized.
KR1020080110843A 2008-11-10 2008-11-10 Method of manufacturing crystal glass ornament for showed Nacre-pattern KR101265992B1 (en)