KR101245350B1 - Concrete water tank for panels - Google Patents

Concrete water tank for panels Download PDF

Info

Publication number
KR101245350B1
KR101245350B1 KR1020130019302A KR20130019302A KR101245350B1 KR 101245350 B1 KR101245350 B1 KR 101245350B1 KR 1020130019302 A KR1020130019302 A KR 1020130019302A KR 20130019302 A KR20130019302 A KR 20130019302A KR 101245350 B1 KR101245350 B1 KR 101245350B1
Authority
KR
South Korea
Prior art keywords
panel
water tank
concrete
adhesive layer
elastic adhesive
Prior art date
Application number
KR1020130019302A
Other languages
Korean (ko)
Inventor
문성호
Original Assignee
주식회사 문창
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 문창 filed Critical 주식회사 문창
Priority to KR1020130019302A priority Critical patent/KR101245350B1/en
Application granted granted Critical
Publication of KR101245350B1 publication Critical patent/KR101245350B1/en

Abstract

PURPOSE: A panel for a concrete water tank is provided to improve the resistibility of the inner wall surface of the water tank against load stress or bending stress, and to provide excellent adhesive properties and waterproofing properties among a sheet panel, a high elastic adhesive layer, and a stainless panel. CONSTITUTION: A panel for a concrete water tank includes a concrete wall(110), a primer layer(120), a high elastic adhesive layer(130), a stainless panel(140), a PE(polyethylene) film(160), and a PE resin layer(150). The inner wall surface of the water tank is formed by concrete walls assembled into a box shape. The primer layer is formed in between the concrete wall and the high elastic adhesive layer. The high elastic adhesive layer is formed in between the stainless panel and the concrete wall. The stainless panel is formed on the upper side of the high elastic adhesive layer. The PE film is formed in between the stainless panel and the PE resin layer. The PE film adheres to the stainless panel and the PE resin layer by thermal fusion. The PE resin layer adheres to the upper side of the stainless panel at a prescribed thickness.

Description

콘크리트 물탱크용 패널{Concrete water tank for panels}Concrete water tank for panels

본 발명은 콘크리트 물탱크용 패널에 관한 것이다. 더욱 상세하게는 콘크리트 물탱크의 내부 벽면에 하중이나 휨응력에 대한 저항성을 향상시키고, PE 수지층, 고탄성 접착층 및 스테인레스 패널 간의 우수한 접착성 및 방수성을 제공하며, 장기간 저장된 물에 의해 패널의 부식이나 녹방지, 물이끼에 의한 미생물 서식 방지를 개선할 수 있음은 물론, 물탱크 패널의 수밀성이 우수하면서도 보다 위생적인 상태로 물을 장기간 보관 가능한 콘크리트 물탱크용 패널에 관한 것이다.
The present invention relates to a panel for a concrete water tank. More specifically, it improves resistance to load or bending stress on the inner wall of the concrete water tank, provides excellent adhesion and waterproofness between PE resin layer, high elastic adhesive layer and stainless steel panel, and prevents corrosion or rust of panels by long-term stored water. The present invention relates to a concrete water tank panel capable of storing water for a long time in a more hygienic state with excellent watertightness of the water tank panel as well as preventing and improving microbial habitat by water moss.

일반적으로 사무용 건물, 아파트 및 공공건물 등 대부분의 주거용 및 상업용 건물에는 음용수를 공급하기 위한 물탱크가 옥상 또는 지하에 설치되고, 공장 등에서는 산업용 용수를 공급하기 위한 용도로 물탱크가 설치되고 있으며 그 재질에 따라 스테인리스(Stainless)수조, SMC(Sheet Molding Compound)수조, FRP(Fiber Reinforced Plastic)수조 및 콘크리트(Concrete)수조 등으로 구분된다.In general, most residential and commercial buildings, such as office buildings, apartments, and public buildings, have water tanks for supplying drinking water on the roof or basement, and water tanks are installed for the purpose of supplying industrial water in factories. Depending on the material, it is divided into stainless steel tank, SMC (Sheet Molding Compound) tank, FRP (Fiber Reinforced Plastic) tank and concrete tank.

스테인리스 수조는 대부분 사각형태의 단위패널을 시공현장에서 조립하여 제작되며, 위생적이고 유지보수가 편리한 반면 저수조내 기층부에 체류하는 염소가스에 의한 부식에 매우 취약하므로 별도의 코팅 처리를 해야 할뿐만 아니라 가격이 높아 일반적으로 사용되기 어려운 문제점이 있다.Most stainless steel tanks are manufactured by assembling a rectangular unit panel at a construction site, and are not only hygienic and easy to maintain, but also very vulnerable to corrosion caused by chlorine gas remaining in the base of the reservoir. There is a problem that the price is difficult to use in general.

또한, SMC수조에서 사용되는 소재는 액상 매트릭스수지에 저수축제, 충진제, 경화제, 증점제, 안료 등의 첨가제에서 가압 프레스 성형하여 물탱크 제작에 적합한 형태로 성형하고 이를 조립하여 SMC수조를 제작한다. 이는 SMC수조의 면이 깨끗하고 착색이 가능하여 소규모 저수조에 적합하고 내식성이 있고 위생성이 뛰어난 장점이 있는 반면, 일반FRP에 비해 유리섬유 함유량이 적어 인장강도가 상대적으로 약하고 수밀성을 확보하기 위해서는 추가적인 실링처리를 해야 하는 문제점이 있다.In addition, the material used in the SMC tank is press-molded with additives such as low shrinkage agent, filler, hardener, thickener, pigment, etc. in the liquid matrix resin to form into a shape suitable for the water tank manufacturing and assembling it to produce the SMC tank. It has the advantage of being suitable for small water tank, corrosion resistance and hygiene, because the surface of SMC tank is clean and can be colored, whereas the glass fiber content is lower than that of general FRP, so the tensile strength is relatively weak and additional sealing is needed to secure water tightness. There is a problem that must be handled.

또한, FRP재질의 수조는 가볍고, 내구성, 내충격성 및 내마모성이 우수한 장점과 함께 가공성이 우수하여 주로 소용량의 물탱크 용도로 사용되고 있으나, 고온에서는 사용할 수 없다는 문제점을 지니고 있다.In addition, the water tank of the FRP material is light, durable, impact resistance and wear resistance with the advantages of excellent workability and mainly used for small capacity water tank, but has a problem that can not be used at high temperatures.

그리고, 콘크리트 수조는 저렴한 가격과 우수한 내구성으로 인하여 일반적으로 대형 수조의 용도로 가장 많이 사용되고 있으며 내부에는 위생성 확보를 위한 다양한 방법의 내부처리가 이루어지고 있다. 보편적으로 콘크리트 수조 내부의 위생성과 방수처리를 위하여 에폭시(Epoxy)수지가 사용되고 있으나, 시간의 경과에 따라 에폭시수지에서 유해물질이 용출될 뿐만 아니라 방수층의 균열과 박리로 인하여 물이 콘크리트와 직접 접촉하게 됨으로써 수질오염이 발생하는 문제점이 있다.In addition, concrete tanks are generally used most commonly for large tanks due to low price and excellent durability, and internal treatment of various methods is performed inside to secure hygiene. In general, epoxy resins are used for hygiene and waterproof treatment inside concrete tanks.However, over time, not only harmful substances are eluted from the epoxy resins, but water also comes into direct contact with concrete due to cracking and peeling of the waterproof layer. As a result, water pollution occurs.

전술한 여러 종류의 물탱크에서 나타나는 문제점들은 근본적으로 사용되는 소재 자체의 고유한 특성에 의해 나타나는 문제점들이며, 이와 같은 문제점들을 극복하기 위하여 최근에는 폴리에틸렌을 물탱크의 소재로 사용하고자 하는 연구가 진행중이다.The problems in the various types of water tanks described above are fundamentally caused by the inherent characteristics of the materials used. In order to overcome these problems, researches on using polyethylene as a material for water tanks are underway. .

즉, 공개특허 제2003-0035916호에 개재된 "폴리에틸렌 시트를 사용한 콘크리트 수조의 방수구조"에서는 기존 콘크리트 수조 내부에 부직포와 붙임용 시트를 사용하여 폴리에틸렌 시트를 부착하는 기술을 제시하고 있고, 공개특허 제2001-0109505호에 개재된 패널수조 제조방법 및 패널수조"에서는 아연도금강판을 주재료로 하는 물탱크용 단위패널의 내측면에 위생방수시트를 부착하고, 외측면에 보온재를 일체로 성형하여 제조되는 물탱크용 단위패널의 제조방법 및 이를 이용한 물탱크의 제작방법에 대하여 제시하고 있다.That is, the "waterproof structure of a concrete water tank using a polyethylene sheet" disclosed in Patent Publication No. 2003-0035916 proposes a technique for attaching a polyethylene sheet using a nonwoven fabric and a sheet for attaching to the existing concrete water tank, Panel water tank manufacturing method and panel water tank disclosed in No. 2001-0109505 are manufactured by attaching a sanitary waterproof sheet to the inner surface of the unit panel for water tank mainly composed of galvanized steel sheet, and integrally molding the insulating material on the outer surface. A method of manufacturing a unit panel for a water tank and a method of manufacturing a water tank using the same are provided.

그러나, 전술한 종래 기술에는 다음과 같은 문제점이 있다.However, the above-described prior art has the following problems.

첫째, 기존의 콘크리트 수조내부에 부직포와 붙임용 시트를 이용하여 폴리에틸렌 시트를 부착하는 방법은 콘크리트면과 폴리에틸렌 시트의 전체면이 콘크리트 면과 직접 부착되지 않고 부자재를 이용하여 폴리에틸렌 시트의 일부분만 부착되어 부착면이 쉽게 떨어지거나 폴리에틸렌 시트의 굴곡현상이 발생하는 문제점이 있다.First, the method of attaching the polyethylene sheet using the nonwoven fabric and the sheet for attaching the concrete to the existing concrete tank is that the entire surface of the concrete surface and the polyethylene sheet is not directly attached to the concrete surface, and only a part of the polyethylene sheet is attached using the subsidiary materials. There is a problem that the adhesion surface is easily falling or the phenomenon of bending the polyethylene sheet occurs.

둘째, 금속패널 등에 고주파 가열기를 이용하여 가열한 후 폴리에틸렌 분말을 분사하여 부착하거나 일정한 두께의 폴리에틸렌 시트를 부착하는 방법은 폴리에틸렌과 금속패널사이에 강한 접착을 유지할 수 있는 접착성분없이 단순히 폴리에틸렌이 용융되면서 금속패널 등에 부착됨으로써, 냉각 후에는 폴리에틸렌이 금속패널과 쉽게 분리될 뿐만 아니라 고주파 가열기를 통한 금속패널의 간접적인 가열만으로 폴리에틸렌을 용융시키기 때문에 부착시킬 수 있는 폴리에틸렌의 두께에 한계가 있는 문제점이 있다.
Second, after heating by using a high frequency heater in a metal panel or the like, by spraying polyethylene powder or attaching a polyethylene sheet having a predetermined thickness, the polyethylene is simply melted without an adhesive component that can maintain strong adhesion between the polyethylene and the metal panel. By being attached to a metal panel, there is a problem in that the polyethylene is easily separated from the metal panel after cooling and the polyethylene can be attached because the polyethylene is melted only by indirect heating of the metal panel through a high frequency heater.

대한민국 공개특허 제2003-0035916호 (2003.05.09.)Republic of Korea Patent Publication No. 2003-0035916 (2003.05.09.)

대한민국 공개특허 제2001-0109505호 (2001.12.10.)
Republic of Korea Patent Publication No. 2001-0109505 (2001.12.10.)

이와 같은 문제점을 해결하기 위하여 본 발명은 콘크리트 물탱크의 내부 벽면에 하중이나 휨응력에 대한 저항성을 향상시키고, 시트 패널, 고탄성 접착층 및 스테인레스 패널 간의 우수한 접착성 및 방수성을 제공하는데 그 목적이 있다.In order to solve this problem, the present invention has an object to improve the resistance to load or bending stress on the inner wall surface of the concrete water tank, and to provide excellent adhesion and waterproofness between the sheet panel, the high elastic adhesive layer and the stainless panel.

또한, 본 발명은 장기간 저장된 물에 의해 패널의 부식이나 녹방지, 물이끼에 의한 미생물 서식 방지를 개선할 수 있음은 물론, 물탱크 패널의 수밀성이 우수하면서도 보다 위생적인 상태로 물을 장기간 보관할 수 있도록 하는데 그 목적이 있다.In addition, the present invention can improve the prevention of corrosion or rust of the panel by the stored water for a long time, the prevention of microbial habitat by water moss, as well as excellent water-tightness of the water tank panel, so that the water can be stored in a more hygienic state for a long time Its purpose is to.

또한, 본 발명은 접착 기능을 가지는 고탄성 접착층을 무용제 에폭시 수지와 발포폴리스타이렌, 또는 무용제 에폭시 수지와 우레탄을 혼합 구성함으로써, 접착제의 사용량을 현저하게 절감할 수 있으며, 발포폴리스타이렌 또는 우레탄의 요철 형상으로 인해 접착력을 극대화시키는데 그 목적이 있다.
In addition, the present invention by mixing a high elastic adhesive layer having an adhesive function with a solvent-free epoxy resin and a foamed polystyrene, or a solvent-free epoxy resin and a urethane, it is possible to significantly reduce the amount of the adhesive, due to the uneven shape of the foamed polystyrene or urethane The purpose is to maximize adhesion.

이와 같은 과제를 달성하기 위한 본 발명은 콘크리트 물탱크용 패널에 있어서, 박스형태로 조립되며, 물탱크의 내부 벽면을 구성하는 콘크리트 벽체; 상기 콘크리트 벽체의 내측 벽면에 소정의 두께로 도포되어 일체로 구성되며, 무용제 에폭시 수지와 함께 소정의 탄성력을 구비한 발포폴리스타이렌(expanded polystyrene)이 일정 비율로 혼합 구성된 고탄성 접착층; 상기 콘크리트 벽체와 고탄성 접착층 사이에 구성되며, 콘크리트 벽체의 내측 벽면을 평탄화하여 고탄성 접착층과의 접착력을 극대화하는 프라이머층; 상기 고탄성 접착층에 소정의 두께로 접착되는 스테인레스 패널; 상기 스테인레스 패널과 열융착에 의해 접착되며, 소정의 두께를 가진 PE수지로 이루어진 PE 수지층; 상기 PE 수지층과 스테인레스 부재 사이에 구성되어 열융착에 의해 접착되도록 구성되는 PE 필름; 으로 이루어진 물탱크용 패널을 포함하고, 상기 콘크리트 벽체와 상기 고탄성 접착층, 스테인레스 패널 및 PE 수지층을 체결하는 체결수단; 및 상기 물탱크용 패널이 다수 접착된 물탱크의 수밀력을 극대화할 수 있도록 PE 재질로 이루어지며, 물탱크용 패널들 간의 경계선을 밀봉하는 마감부를 포함하는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In order to achieve the above object, the present invention provides a panel for a concrete water tank, which is assembled in a box shape and comprises a concrete wall constituting an inner wall of the water tank; A highly elastic adhesive layer formed integrally by being applied to the inner wall of the concrete wall in a predetermined thickness and integrally formed with a predetermined ratio of expanded polystyrene having a predetermined elasticity together with a solvent-free epoxy resin; A primer layer formed between the concrete wall and the high elastic adhesive layer and maximizing adhesion to the high elastic adhesive layer by planarizing the inner wall of the concrete wall; A stainless panel bonded to the high elastic adhesive layer to a predetermined thickness; PE resin layer is bonded to the stainless panel by heat fusion, PE resin layer having a predetermined thickness; A PE film configured between the PE resin layer and the stainless member to be bonded by heat fusion; Comprising a water tank panel consisting of, the fastening means for fastening the concrete wall and the high elastic adhesive layer, a stainless panel and a PE resin layer; And the water tank panel is made of a PE material to maximize the watertight force of the water tank is bonded to a plurality of concrete water tank panel, characterized in that it comprises a finish sealing the boundary between the panel for the water tank to provide.

또한, 본 발명에 있어서, 상기 고탄성 접착층은 무용제 에폭시 수지와, 발포폴리스타이렌 또는 우레탄 중 어느 하나를 선택하여 혼합하되, 1:1의 비율로 혼합하여 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the high-elastic adhesive layer is selected from any one of the solvent-free epoxy resin, foamed polystyrene or urethane and mixed, it provides a panel for concrete water tank, characterized in that the mixture is configured in a ratio of 1: 1. do.

또한, 본 발명에 있어서, 상기 고탄성 접착층은 무용제 에폭시 수지와, 발포폴리스타이렌 및 우레탄을 혼합한 혼합물과 1:1의 비율로 혼합 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the high elastic adhesive layer provides a concrete water tank panel, characterized in that the mixture is composed of a mixture of a solvent-free epoxy resin, a foamed polystyrene and urethane in a ratio of 1: 1.

또한, 본 발명에 있어서, 상기 발포폴리스타이렌 및 우레탄은 원형, 타원형으로 구성되거나, 삼각형 및 사각형과 같은 다각형의 형태로 구성되어 혼합이 이루어지며, 3mm~5mm 의 크기를 가지도록 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the expanded polystyrene and urethane is composed of a circular, elliptical, or in the form of a polygon such as a triangle and a square is made of a mixture, characterized in that configured to have a size of 3mm ~ 5mm Provide panels for concrete water tanks.

또한, 본 발명에 있어서, 상기 고탄성 접착층은 발포폴리스타이렌 및 우레탄은 총 충량에 있어서 발포폴리스타이렌 50중량%, 우레탄 50중량%로 혼합한 다음, 무용제 에폭시 수지와 1:1의 비율로 혼합하는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the high elastic adhesive layer is foamed polystyrene and urethane is mixed in 50% by weight of expanded polystyrene, 50% by weight of urethane in the total charge, and then mixed with a solvent-free epoxy resin in a ratio of 1: 1. It provides a panel for concrete water tank.

또한, 본 발명에 있어서, 상기 스테인레스 패널은 GI 아연도강판의 재질로도 사용이 가능하며, 이때 바람직한 두께로는 0.2mm~1.5mm의 두께로 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the stainless panel may be used as a material of the GI galvanized steel sheet, in which the preferred thickness provides a panel for a concrete water tank, characterized in that composed of a thickness of 0.2mm ~ 1.5mm. do.

또한, 본 발명에 있어서, 상기 PE 수지층은 1.0 ~ 2.5mm의 두께로 구성되어 스테인레스 패널의 일면에 적층 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the PE resin layer is provided with a concrete water tank panel, characterized in that composed of a thickness of 1.0 ~ 2.5mm laminated on one surface of a stainless panel.

또한, 본 발명에 있어서, 상기 PE 수지층과 스테인레스 패널은 크린 에포씰과 고무(RUBBER)변성 에폭시(NBR변성 EPOXY RESIN) 수지와 폴리아미드(POLYAMIDE) 경화제를 포함한 혼합물로 이루어진 접착제에 의해 접착되는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.In addition, in the present invention, the PE resin layer and the stainless panel is bonded by an adhesive made of a mixture comprising a clean epoch seal, rubber (RUBBER) modified epoxy (NBR modified EPOXY RESIN) resin and a polyamide (POLYAMIDE) curing agent Provided is a panel for a concrete water tank.

또한, 본 발명에 있어서, 상기 마감부는 양측 단부가 각각 물탱크 패널들의 PE 수지층과 융착기를 통해 융착이 이루어져 물탱크 패널과 일체로 구성되도록 하는 융착부와, 이 융착부와 일체로 형성되며, 체결수단의 머리부가 내장되도록 소정의 두께로 이루어진 밀봉부를 포함하는 것을 특징으로 하는 콘크리트 물탱크용 패널을 제공한다.
In addition, in the present invention, the finishing portion is fused to both ends are formed by fusion through the PE resin layer and the fusion machine of the water tank panels, respectively, and integrally formed with the water tank panel, and is formed integrally with the fusion portion, It provides a panel for a concrete water tank, characterized in that it comprises a sealing portion of a predetermined thickness so that the head of the fastening means is built.

이와 같은 본 발명에 따르면, 콘크리트 물탱크의 내부 벽면에 하중이나 휨응력에 대한 저항성을 향상시키고, 시트 패널, 고탄성 접착층 및 스테인레스 패널 간의 우수한 접착성 및 방수성을 제공하는데 그 목적이 있다.According to the present invention, the purpose is to improve the resistance to the load or bending stress on the inner wall surface of the concrete water tank, and to provide excellent adhesion and waterproofness between the sheet panel, the high elastic adhesive layer and the stainless panel.

또한, 본 발명은 장기간 저장된 물에 의해 패널의 부식이나 녹방지, 물이끼에 의한 미생물 서식 방지를 개선할 수 있음은 물론, 물탱크 패널의 수밀성이 우수하면서도 보다 위생적인 상태로 물을 장기간 보관할 수 있도록 하는데 그 목적이 있다.In addition, the present invention can improve the prevention of corrosion or rust of the panel by the stored water for a long time, the prevention of microbial habitat by water moss, as well as excellent water-tightness of the water tank panel, so that the water can be stored in a more hygienic state for a long time Its purpose is to.

또한, 본 발명에 따르면, 접착 기능을 가지는 고탄성 접착층을 무용제 에폭시 수지와 발포폴리스타이렌, 또는 무용제 에폭시 수지와 우레탄을 혼합 구성함으로써, 접착제의 사용량을 현저하게 절감할 수 있으며, 발포폴리스타이렌 또는 우레탄의 요철 형상으로 인해 접착력을 극대화할 수 있는 효과가 있다.In addition, according to the present invention, by forming a high elastic adhesive layer having an adhesive function by mixing a solvent-free epoxy resin and a foamed polystyrene, or a solvent-free epoxy resin and a urethane, the amount of the adhesive can be significantly reduced, the uneven shape of the foamed polystyrene or urethane Due to the effect that can maximize the adhesive force.

도 1은 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 사시도,
도 2는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 단면도,
도 3은 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널이 설치된 상태를 개략적으로 나타낸 도면,
도 4는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 요부 확대도,
도 5는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널의 융착부를 나타낸 도면이다.1 is a perspective view showing a panel for a concrete water tank according to a preferred embodiment of the present invention,
Figure 2 is a cross-sectional view showing a panel for a concrete water tank according to a preferred embodiment of the present invention,
3 is a view schematically showing a state in which a panel for concrete water tanks according to a preferred embodiment of the present invention is installed;
Figure 4 is an enlarged view of the main portion showing a panel for a concrete water tank according to a preferred embodiment of the present invention,
5 is a view showing a fusion of the panel for a concrete water tank according to a preferred embodiment of the present invention.

이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성요소들에 참조 부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the drawings, the same reference numerals are used to designate the same or similar components throughout the drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

도 1은 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 사시도, 도 2는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 단면도, 도 3은 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널이 설치된 상태를 개략적으로 나타낸 도면, 도 4는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널을 나타낸 요부 확대도, 도 5는 본 발명의 바람직한 실시예에 따른 콘크리트 물탱크용 패널의 융착부를 나타낸 도면이다.1 is a perspective view showing a panel for a concrete water tank according to a preferred embodiment of the present invention, Figure 2 is a cross-sectional view showing a panel for a concrete water tank according to a preferred embodiment of the present invention, Figure 3 is a preferred embodiment of the present invention 4 is a view schematically illustrating a state in which a panel for concrete water tanks is installed, FIG. 4 is an enlarged view illustrating main panels for concrete water tanks according to a preferred embodiment of the present invention, and FIG. 5 is concrete water according to a preferred embodiment of the present invention. It is a figure which shows the fusion | melting part of the tank panel.

도시된 바와 같이, 본 발명의 콘크리트 물탱크용 패널은 박스형태로 조립된 물탱크의 내부 벽면에 하중이나 휨응력에 대한 저항성을 강하게 하여 높은 수압에 견딜 수 있도록 콘크리트로 이루어진 벽체(110)를 구성하고, 이 콘크리트 벽체(110)의 내면에 우수한 접착성과 방수성 향상, 부식 및 녹방지, 수밀성이 우수하면서도 보다 위생적인 상태로 물을 보관할 수 있도록 콘크리트 벽체(110)의 종, 횡방향으로 전체면에 박스형태로 고탄성 접착층(130), 스테인레스 패널(140) 및 PE수지로 이루어진 시트패널(150)이 순차적으로 적층 구성되되 접착 및 체결 구성된다.As shown, the concrete water tank panel of the present invention constitutes a wall 110 made of concrete to withstand high water pressure by strengthening the resistance to load or bending stress on the inner wall surface of the water tank assembled in the form of a box and Box on the entire surface in the longitudinal and transverse directions of the concrete wall 110 to store water in a more hygienic state with excellent adhesion and waterproofness, corrosion and rust prevention, watertightness on the inner surface of the concrete wall 110, In the form, the high elastic adhesive layer 130, the stainless panel 140 and the sheet panel 150 made of a PE resin are sequentially laminated, but is bonded and fastened.

고탄성 접착층(130)은 스테인레스 패널(140)과 콘크리트 벽체(110) 사이에 구성되어 이 스테인레스 패널(140)과 콘크리트 벽체(110)을 일체로 접착하기 위한 접착용 구성요소이다. The high elastic adhesive layer 130 is formed between the stainless panel 140 and the concrete wall 110 is an adhesive component for integrally bonding the stainless panel 140 and the concrete wall 110.

이러한 고탄성 접착층(130)은 무용제 에폭시 수지를 주성분으로 사용되며, 이 무용제 에폭시 수지와 함께 소정의 탄성력을 구비한 발포폴리스타이렌(expanded polystyrene)이 혼합 구성되는 것이다. The high elastic adhesive layer 130 is a solvent-free epoxy resin is used as a main component, and the expanded polystyrene having a predetermined elastic force together with the solvent-free epoxy resin (expanded polystyrene) is mixed.

여기서, 발포폴리스타이렌은 폴리스타이렌을 발포제(發泡劑)의 작용으로 팽창시킨 것으로 거품폴리스타이렌·스타이로폼(styrofoam)·발포스타이렌·스타이로폴 등 여러 이름으로 불리며, 영문 머리글자를 따서 EPS로 약칭하기도 한다. 희고 가벼우며, 내수성·단열성·방음성·완충성 등이 우수하여 널리 사용된다.Here, expanded polystyrene is a polystyrene expanded by the action of a blowing agent (foam) and is called by various names such as foam polystyrene, styrofoam, foamed styrene, styropol, abbreviated as EPS after the English initials. Sometimes. It is white and light, and is widely used because of its excellent water resistance, insulation, soundproofing, and buffering properties.

아울러, 본 발명의 고탄성 접착층(130)은 무용제 에폭시 수지와 발포폴리스타이렌을 혼합하는 것을 한정하는 것은 아니며, 무용제 에폭시 수지와 우레탄을 혼합하여 사용할 수 있으며, 무용제 에폭시 수지와 발포폴리스타이렌 및 우레탄을 일정 비율로 혼합하여 사용하여도 무방할 것이다.In addition, the high elastic adhesive layer 130 of the present invention is not limited to mixing the solvent-free epoxy resin and the foamed polystyrene, it can be used by mixing a solvent-free epoxy resin and urethane, a solvent-free epoxy resin, foamed polystyrene and urethane in a certain ratio It may be used in combination.

이와 같은 고탄성 접착층(130)은 무용제 에폭시 수지와 발포폴리스타이렌, 또는 무용제 에폭시 수지와 우레탄이 혼합될 때, 혼합 비율을 1:1의 비율로 혼합이 이루어지도록 한다. Such a high elastic adhesive layer 130, when the solvent-free epoxy resin and the foamed polystyrene, or the solvent-free epoxy resin and the urethane is mixed, the mixing ratio is to be made in a ratio of 1: 1.

그리고, 무용제 에폭시 수지와 발포폴리스타이렌 및 우레탄이 혼합되는 경우에도 1:1의 비율로 혼합이 이루어지되, 발포폴리스타이렌 및 우레탄은 총 충량에 있어서 발포폴리스타이렌 50중량%, 우레탄 50중량%로 혼합한 다음, 무용제 에폭시 수지와 1:1의 비율로 혼합하도록 한다.In addition, even when the solvent-free epoxy resin and the expanded polystyrene and urethane are mixed, the mixing is performed in a ratio of 1: 1, and the expanded polystyrene and the urethane are mixed in 50% by weight of expanded polystyrene and 50% by weight of urethane in the total filling amount. Mix with a solvent-free epoxy resin in a ratio of 1: 1.

아울러, 본 발명의 혼합물인 발포폴리스타이렌 및 우레탄은 원형, 타원형으로 구성되거나, 삼각형 및 사각형과 같은 다각형의 형태로 구성되어 혼합이 이루어지며, 입자의 크기는 3mm~5mm 의 크기를 가지도록 구성됨이 바람직하나, 이에 한정하는 것은 아니다.In addition, the expanded polystyrene and urethane mixture of the present invention is composed of a circular, elliptical, or in the form of a polygon, such as a triangle and a square, the mixing is made, the size of the particles is preferably configured to have a size of 3mm ~ 5mm. However, it is not limited thereto.

한편, 본 발명은 콘크리트 벽체(110)와 고탄성 접착층(130) 사이에 구성되며, 콘크리트 벽체의 내측 벽면을 평탄화하는 프라이머층(120)을 구성하여 콘크리트 벽체(110)와 고탄성 접착층(130) 간의 접착력을 극대화하고, 내식성 및 부착성을 향상시키도록 한다.On the other hand, the present invention is configured between the concrete wall 110 and the high elastic adhesive layer 130, constitutes a primer layer 120 to planarize the inner wall surface of the concrete wall, the adhesive force between the concrete wall 110 and the high elastic adhesive layer 130 To maximize corrosion resistance and adhesion.

아울러, 콘크리트 벽체(110)의 내벽면에 고탄성 접착층(130)의 도포가 완료되면, 소정의 두께를 가지는 스테인레스 패널(140)이 고탄성 접착층(130)의 상부로 적층 구성되게 접착한다.In addition, when the application of the high elastic adhesive layer 130 is completed on the inner wall surface of the concrete wall 110, the stainless panel 140 having a predetermined thickness is bonded to be laminated on the high elastic adhesive layer 130.

스테인레스 패널(140)은 그 재질을 스테인레스 재질로 한정하지 아니하고, GI 아연도강판의 재질로도 사용이 가능하며, 이때 바람직한 두께로는 0.2mm~1.5mm의 두께로 사용되도록 한다. The stainless panel 140 is not limited to the material of the stainless material, it can be used as a material of the GI galvanized steel sheet, the preferred thickness is to be used in a thickness of 0.2mm ~ 1.5mm.

또한, 스테인레스 패널(140)의 상부에는 소정의 두께로 이루어진 PE 수지층(150)이 적층되게 접착 구성된다.In addition, the upper portion of the stainless panel 140, the PE resin layer 150 made of a predetermined thickness is bonded to be laminated.

PE 수지층(150)은 PE수지로 이루어지며, 1.0 ~ 2.5mm의 두께로 구성되어 스테인레스 패널(140)의 일면에 적층 구성된다. PE resin layer 150 is made of a PE resin, is composed of a thickness of 1.0 ~ 2.5mm is laminated on one surface of the stainless panel 140.

이러한 PE 수지층(150)은 스테인레스 패널(140)과 PE 필름(160)에 의해 접착이 이루어지며, 열융착에 의해 스테인레스 패널(140)과 적층되게 접착 구성됨이 바람직하나, 이에 한정하는 것은 아니다.The PE resin layer 150 is bonded by the stainless panel 140 and the PE film 160, and is preferably configured to be laminated with the stainless panel 140 by thermal fusion, but is not limited thereto.

즉, 본 발명의 스테인레스 패널(140)과 PE 수지층(150) 사이에는 열융착이 가능한 PE 필름(160) 뿐만 아니라, 크린 에포씰과 고무(RUBBER)변성 에폭시(NBR변성 EPOXY RESIN) 수지와 폴리아미드(POLYAMIDE) 경화제를 포함한 혼합물로 이루어진 접착제를 사용할 수도 있을 것이다. That is, between the stainless panel 140 and the PE resin layer 150 of the present invention, as well as the PE film 160 capable of heat sealing, as well as a clean epoch seal and rubber (RUBBER) modified epoxy (NBR modified EPOXY RESIN) resin and poly It is also possible to use adhesives consisting of a mixture comprising a POLYAMIDE curing agent.

이와 같이 구성된 본 발명의 콘크리트 물탱크용 패널은 도 3에 도시된 바와 같이, 박스 형태로 이루어진 콘크리트 벽체(110)의 내부 벽면에 프라이머층(120), 고탄성 접착층(130), 스테인레스 패널(140), PE 필름(160) 및 PE 수지층(150)을 순차적으로 적층되게 구성하여 접착하여 일체로 구성되도록 한다.As illustrated in FIG. 3, the panel for concrete water tank according to the present invention has a primer layer 120, a high elastic adhesive layer 130, and a stainless panel 140 on an inner wall surface of the concrete wall 110 having a box shape. The PE film 160 and the PE resin layer 150 are sequentially laminated and bonded to be integrally formed.

그리고, 전술한 물탱크용 패널의 접착이 완료되면, 앙카볼트와 같은 체결수단(202)을 통해 접착된 물탱크용 패널과 콘크리트 벽체(110) 간의 체결이 이루어지도록 구성한다. When the adhesion of the water tank panel is completed, the water tank panel and the concrete wall 110 bonded through the fastening means 202 such as an anchor bolt are configured to be fastened.

여기서, 스테인레스 패널(140) 및 PE 수지층(150)에는 콘크리트 벽체(110)와 체결수단(202)을 통해 체결이 이루어질 수 있도록 체결공(220)을 형성하여 콘크리트 벽체(110)와 견고한 결합력을 가질 수 있도록 구성된다. Here, the fastening hole 220 is formed in the stainless panel 140 and the PE resin layer 150 through the concrete wall 110 and the fastening means 202 to form a firm coupling force with the concrete wall 110. It is configured to have.

아울러, 물탱크용 패널들 간의 경계선(패널과 패널의 단부가 접하면서 발생하는 미세한 틈)과, 체결수단(202)의 체결로 인해 발생하는 체결공(220)과의 틈을 밀폐하여 물탱크의 수밀력을 더욱 극대화할 수 있도록 PE 재질로 이루어진 마감부(210)가 구비된다.In addition, the boundary between the panel for the water tank (fine gap generated when the panel and the end of the panel is in contact with) and the gap between the fastening hole 220 generated by the fastening means 202 is sealed to close the water tank Finish 210 is made of a PE material to further maximize the watertight force.

마감부(210)는 물탱크 패널이 접하는 경계선이 중앙에 위치하도록 하여 체결수단(202)이 외부로 노출되는 것을 방지함과 동시에, 물탱크 패널이 접하는 경계선으로 저장된 물이 유입되거나, 부식물이 물탱크의 내부로 유출되는 것을 차단함으로써, 장기간 물탱크를 위생적으로 사용할 수 있도록 구성된다.The closing portion 210 prevents the fastening means 202 from being exposed to the outside by placing the boundary line where the water tank panel is in contact with the center, and at the same time, the stored water flows into the boundary line where the water tank panel is in contact with, or the corrosive water By preventing the outflow into the tank, the water tank can be sanitarily used for a long time.

이러한 마감부(210)는 양측 단부가 각각 물탱크 패널들의 PE 수지층(150)과 융착기를 통해 융착이 이루어져 물탱크 패널과 마감부(210)가 일체로 구성되도록 하는 융착부(214)와, 이 융착부(214)의 중앙측에 일체로 형성되며, 체결수단(202)의 머리부가 내장되도록 소정의 두께로 이루어진 밀봉부(212)로 이루어진다. The finish portion 210 is a fusion portion 214 for both ends are fused through the PE resin layer 150 and the fusion machine of the water tank panels, respectively, so that the water tank panel and the finish portion 210 are integrally formed; It is formed integrally with the center side of the fusion portion 214, and consists of a sealing portion 212 made of a predetermined thickness so that the head of the fastening means 202 is embedded.

이와 같이 구성된 본 발명의 콘크리트 물탱크용 패널은 콘크리트 물탱크의 내부 벽면에 하중이나 휨응력에 대한 저항성을 향상시키고, 시트 패널, 고탄성 접착층 및 스테인레스 패널 간의 우수한 접착성 및 방수성을 제공하고, 장기간 저장된 물에 의해 패널의 부식이나 녹방지, 물이끼에 의한 미생물 서식 방지를 개선할 수 있음은 물론, 물탱크 패널의 수밀성이 우수하면서도 보다 위생적인 상태로 물을 장기간 보관할 수 있도록 하며, 접착 기능을 가지는 고탄성 접착층을 무용제 에폭시 수지와 발포폴리스타이렌, 또는 무용제 에폭시 수지와 우레탄을 혼합 구성함으로써, 접착제의 사용량을 현저하게 절감할 수 있으며, 발포폴리스타이렌 또는 우레탄의 요철 형상으로 인해 접착력을 극대화할 수 있는 매우 유용한 발명이다.The concrete water tank panel of the present invention configured as described above improves the resistance to load or bending stress on the inner wall surface of the concrete water tank, provides excellent adhesion and waterproofness between the sheet panel, the high elastic adhesive layer and the stainless panel, and the water stored for a long time This prevents corrosion and rust of the panel, and prevents microbial habitat by water moss, as well as excellent water-tightness of the water tank panel, which allows for long-term storage of water in a more hygienic state, and has a high elastic adhesive layer having an adhesive function. By using a solvent-free epoxy resin and expanded polystyrene, or by mixing a solvent-free epoxy resin and urethane, it is possible to significantly reduce the amount of the adhesive, it is a very useful invention that can maximize the adhesive strength due to the uneven shape of the expanded polystyrene or urethane.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
The above description is merely illustrative of the technical idea of the present invention, and those skilled in the art to which the present invention pertains may make various modifications and changes without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas falling within the scope of the same shall be construed as falling within the scope of the present invention.

110: 콘크리트 벽체 120: 프라이머층
130: 고탄성 접착층 140: 스테인레스 패널
150: PE 수지층 160: PE 필름
202: 체결수단 210: 마감부
212: 밀봉부 214: 융착부110: concrete wall 120: primer layer
130: high elastic adhesive layer 140: stainless panel
150: PE resin layer 160: PE film
202: fastening means 210: finish
212 sealing part 214: welding part

Claims (9)

콘크리트 물탱크용 패널에 있어서,
박스형태로 조립되며, 물탱크의 내부 벽면을 구성하는 콘크리트 벽체;
상기 콘크리트 벽체의 내측 벽면에 소정의 두께로 도포되어 일체로 구성되며, 무용제 에폭시 수지와 함께 소정의 탄성력을 구비한 발포폴리스타이렌(expanded polystyrene)이 일정 비율로 혼합 구성된 고탄성 접착층;
상기 콘크리트 벽체와 고탄성 접착층 사이에 구성되며, 콘크리트 벽체의 내측 벽면을 평탄화하여 고탄성 접착층과의 접착력을 극대화하는 프라이머층;
상기 고탄성 접착층에 소정의 두께로 접착되는 스테인레스 패널;
상기 스테인레스 패널과 열융착에 의해 접착되며, 소정의 두께를 가진 PE 수지층;
상기 PE 수지층과 스테인레스 부재 사이에 구성되어 열융착에 의해 접착되도록 구성되는 PE 필름; 으로 이루어진 물탱크용 패널을 포함하고,
상기 콘크리트 벽체와 상기 고탄성 접착층, 스테인레스 패널 및 PE 수지층을 체결하는 체결수단; 및
상기 물탱크용 패널이 다수 접착된 물탱크의 수밀력을 극대화할 수 있도록 PE 재질로 이루어지며, 물탱크용 패널들 간의 경계선을 밀봉하는 마감부
를 포함하는 것을 특징으로 하는 콘크리트 물탱크용 패널.
In the panel for concrete water tank,
A concrete wall assembled in a box shape and constituting an inner wall of the water tank;
A highly elastic adhesive layer formed integrally by being applied to the inner wall of the concrete wall in a predetermined thickness and integrally formed with a predetermined ratio of expanded polystyrene having a predetermined elasticity together with a solvent-free epoxy resin;
A primer layer formed between the concrete wall and the high elastic adhesive layer and maximizing adhesion to the high elastic adhesive layer by planarizing the inner wall of the concrete wall;
A stainless panel bonded to the high elastic adhesive layer to a predetermined thickness;
PE resin layer is bonded to the stainless panel by heat fusion, and has a predetermined thickness;
A PE film configured between the PE resin layer and the stainless member to be bonded by heat fusion; Including a panel for the water tank consisting of,
Fastening means for fastening the concrete wall with the high elastic adhesive layer, a stainless panel, and a PE resin layer; And
The water tank panel is made of a PE material to maximize the watertightness of the water tank bonded to the plurality, the finishing portion for sealing the boundary line between the water tank panels
Panel for concrete water tank comprising a.
제 1 항에 있어서,
상기 고탄성 접착층은 무용제 에폭시 수지와, 발포폴리스타이렌 또는 우레탄 중 어느 하나를 선택하여 혼합하되, 1:1의 비율로 혼합하여 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 1,
Wherein the high elastic adhesive layer is a solvent-free epoxy resin, foamed polystyrene or urethane selected by mixing any one of the panels, the concrete water tank panel, characterized in that the mixture is configured in a ratio of 1: 1.
제 2 항에 있어서,
상기 고탄성 접착층은 무용제 에폭시 수지와, 발포폴리스타이렌 및 우레탄을 혼합한 혼합물과 1:1의 비율로 혼합 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 2,
The high elastic adhesive layer is a concrete water tank panel, characterized in that the mixture is composed of a solvent-free epoxy resin, a mixture of expanded polystyrene and urethane in a ratio of 1: 1.
제 2 항에 있어서,
상기 발포폴리스타이렌 및 우레탄은 원형, 타원형으로 구성되거나, 삼각형 및 사각형과 같은 다각형의 형태로 구성되어 혼합이 이루어지며, 입자의 크기가 3mm~5mm 의 크기를 가지도록 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 2,
The polystyrene foam and urethane is composed of a circular, oval, or a polygonal shape, such as a triangle and a square, the mixing is made, the concrete water tank, characterized in that the size of the particle is configured to have a size of 3mm ~ 5mm Panel.
제 3 항에 있어서,
상기 고탄성 접착층은 발포폴리스타이렌 및 우레탄은 총 충량에 있어서 발포폴리스타이렌 50중량%, 우레탄 50중량%로 혼합한 다음, 무용제 에폭시 수지와 1:1의 비율로 혼합하는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 3, wherein
The high elastic adhesive layer is foamed polystyrene and urethane in the total amount of foam polystyrene 50% by weight, urethane 50% by weight, and then mixed with a solvent-free epoxy resin in a ratio of 1: 1, characterized in that the panel for concrete water tank.
제 1 항에 있어서,
상기 스테인레스 패널은 GI 아연도강판의 재질로도 사용이 가능하며, 이때 바람직한 두께로는 0.2mm~1.5mm의 두께로 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 1,
The stainless panel is also available as a material of the GI galvanized steel sheet, wherein the preferred thickness panel for concrete water tank, characterized in that consisting of a thickness of 0.2mm ~ 1.5mm.
제 1 항에 있어서,
상기 PE 수지층은 1.0 ~ 2.5mm의 두께로 구성되어 스테인레스 패널의 일면에 적층 구성되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 1,
The PE resin layer is composed of a thickness of 1.0 ~ 2.5mm panel for a concrete water tank, characterized in that the laminated structure on one side of the stainless panel.
제 1 항에 있어서,
상기 PE 수지층과 스테인레스 패널은 크린 에포씰과 고무(RUBBER)변성 에폭시(NBR변성 EPOXY RESIN) 수지와 폴리아미드(POLYAMIDE) 경화제를 포함한 혼합물로 이루어진 접착제에 의해 접착되는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 1,
The PE resin layer and the stainless panel are for concrete water tanks, characterized in that the adhesive is made of a mixture comprising a clean epoch seal and rubber (RUBBER) modified epoxy (NBR modified EPOXY RESIN) resin and a polyamide (POLYAMIDE) curing agent. panel.
제 1 항에 있어서,
상기 마감부는 양측 단부가 각각 물탱크 패널들의 PE 수지층과 융착기를 통해 융착이 이루어져 물탱크 패널과 일체로 구성되도록 하는 융착부와, 이 융착부와 일체로 형성되며, 체결수단의 머리부가 내장되도록 소정의 두께로 이루어진 밀봉부를 포함하는 것을 특징으로 하는 콘크리트 물탱크용 패널.
The method of claim 1,
The finishing part is a fusion unit formed at both ends of the water tank panel by fusion through the PE resin layer and the fusion machine to be integrally formed with the water tank panel, and formed integrally with the fusion unit, so that the head of the fastening means is built-in. Panel for concrete water tank, characterized in that it comprises a sealing made of a predetermined thickness.
KR1020130019302A 2013-02-22 2013-02-22 Concrete water tank for panels KR101245350B1 (en)