KR101240691B1 - Waterproof Tape, Manufacturing Method thereof, and Waterproof Method using it - Google Patents

Waterproof Tape, Manufacturing Method thereof, and Waterproof Method using it Download PDF

Info

Publication number
KR101240691B1
KR101240691B1 KR1020110007344A KR20110007344A KR101240691B1 KR 101240691 B1 KR101240691 B1 KR 101240691B1 KR 1020110007344 A KR1020110007344 A KR 1020110007344A KR 20110007344 A KR20110007344 A KR 20110007344A KR 101240691 B1 KR101240691 B1 KR 101240691B1
Authority
KR
South Korea
Prior art keywords
adhesive
waterproof
layer
film
waterproof tape
Prior art date
Application number
KR1020110007344A
Other languages
Korean (ko)
Other versions
KR20110109816A (en
Inventor
김원준
Original Assignee
김원준
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김원준 filed Critical 김원준
Publication of KR20110109816A publication Critical patent/KR20110109816A/en
Application granted granted Critical
Publication of KR101240691B1 publication Critical patent/KR101240691B1/en

Abstract

본 발명에 따른 다용도 방수테이프는 점착가능한 비가황 부틸고무를 포함하는 방수층, 상기 방수층의 상부면에 결합되며 상기 방수층의 표면을 보호하고, 알루미늄 박막의 상하부면에 각각 필름이 합지된 표면보호층, 및 고분자계 접착제에 의하여 상기 표면보호층의 상부면에 결합되는 도막층을 포함하되, 상기 필름은 PEN(Polyethylene Naphthalate), PET, PE, PVC, TPO 또는 TPU 중 적어도 어느 하나의 재질로 이루어진 것을 특징으로 한다.
따라서, 본 발명의 다용도 방수테이프에 의하면 기재상에 자착식으로 접착가능하고 두께가 얇기 때문에 기재면과의 단차 및 이음부의 단차를 최소화할 수 있으며, 연결 이음부에 매우 우수한 방수성을 제공할 수 있고, 주변환경의 색상에 따라 다양한 색상을 제공할 수 있으며, 내열성 및 내자외선성이 우수하기 때문에 각종 구조물의 지하 또는 내부 뿐만 아니라 옥외에 노출시켜 다양한 용도로 사용할 수 있다.The multi-purpose waterproof tape according to the present invention is a waterproof layer comprising a tackifiable non-vulcanized butyl rubber, is coupled to the upper surface of the waterproof layer to protect the surface of the waterproof layer, the surface protective layer each laminated on the upper and lower surfaces of the aluminum thin film, And a coating layer bonded to the upper surface of the surface protection layer by a polymer adhesive, wherein the film is made of at least one of polyethylene naphthalate (PEN), PET, PE, PVC, TPO, or TPU. It is done.
Therefore, according to the multipurpose waterproof tape of the present invention, since the adhesive layer is self-adhesive on the substrate and the thickness is thin, the step difference with the substrate surface and the step portion of the joint can be minimized, and the connection joint can be provided with excellent waterproofness. It can provide various colors according to the color of the surrounding environment, and because of its excellent heat resistance and UV resistance, it can be used for various purposes by exposing it to the basement or interior of various structures as well as the outdoors.

Description

다용도 방수테이프, 그 제조방법 및 이를 이용한 방수시공방법{Waterproof Tape, Manufacturing Method thereof, and Waterproof Method using it}Multi-purpose waterproof tape, its manufacturing method and waterproof construction method using the same {Waterproof Tape, Manufacturing Method, and Waterproof Method using it}

본 발명은 다용도 방수테이프, 그 제조방법 및 이를 이용한 방수시공방법에 관한 것으로, 보다 상세하게는 기재상에 별도의 접착도구 없이 자착식으로 시공이 가능하고 이종 재질과의 접착이 용이하며, 두께가 얇아서 기재면 및 이음부의 단차를 최소화할 수 있고 표면에 각종 도막재의 마감이 가능할 뿐만 아니라, 내열도 및 내자외선성이 우수하여 옥외에 사용하는 경우에도 장시간의 수명을 유지할 수 있는 다용도 방수테이프, 그 제조방법 및 이를 이용한 방수시공방법에 관한 것이다.
The present invention relates to a multi-purpose waterproof tape, a method for manufacturing the same, and a waterproof construction method using the same. More specifically, it can be applied by a self-supporting method without a separate adhesive tool on a substrate, and easily adhered to different materials, and has a thickness. Multi-purpose waterproof tape that is thin, minimizes the level difference between the base surface and the joints, finishes various coating materials on the surface, and maintains long life even when used outdoors due to its excellent heat resistance and UV resistance. It relates to a manufacturing method and a waterproof construction method using the same.

일반적으로 토목 또는 건축 시공을 통해 이루어지는 콘크리트 구조물은 구조물 내의 수분 침투를 방지하고, 구조물 내의 금속 부식 등을 방지하기 위해서 방수 시공이 필수적으로 요구된다.In general, a concrete structure made through civil engineering or building construction is required to be waterproof construction to prevent moisture penetration into the structure, and to prevent metal corrosion in the structure.

뿐만 아니라, 목재주택이나 기타 건축물 등의 판넬 이음부, 캐노피, 이종 재질간의 접합 부위, 벽체 균열 부위 또는 창틀 틈새 등에 대해서도 마찬가지로 구조물 내부의 수분 침투를 방지하기 위한 방수 시공이 요구된다.In addition, waterproof construction is required to prevent moisture penetration inside the structure in the same way as panel joints, canopies, and dissimilar materials, wall cracks, or window frame gaps in wooden houses or other buildings.

이를 위하여 종래에는 고무 재질로 된 방수테이프를 방수 시공이 필요한 부분에 부착하거나 실리콘을 이용하여 이음부 또는 균열부의 틈새를 메우는 방식을 주로 사용하였다.To this end, conventionally, a method of attaching a waterproof tape made of a rubber material to a part requiring waterproof construction or using a silicon to fill a gap between a joint part or a crack part is mainly used.

그러나, 상기 종래 기술에 따른 방수 방식 중 이음부 등을 실리콘으로 메우는 방식은 실리콘이 이종 재질과의 접착력이 약하기 때문에 동절기에 박리 현상이 잦아서 거의 매년마다 보수 공사를 반복해야 하는 문제점이 있다.However, the method of filling the seams and the like in the waterproof method according to the prior art has a problem that the repair work is repeated almost every year because the peeling phenomenon frequently occurs in winter because the adhesive strength of the heterogeneous material is weak silicon.

또한, 상기 종래 기술에 따른 방식 중 고무 재질의 방수테이프를 이용하는 방식은 온도 변화에 대하여 방수성을 유지하기 위해서는 일정 두께 이상이 요구되기 때문에 기재면 및 이음부에서의 단차가 크게 형성되는 문제점과, 굴곡부위에서의 정밀시공이 곤란하다는 문제점이 있다.In addition, the method using the waterproof tape made of rubber material of the prior art according to the method is required to have a certain thickness or more in order to maintain the waterproofness against temperature changes, the problem that the step is greatly formed on the substrate surface and the joint, and the bent portion There is a problem that the precise construction from above is difficult.

또한, 상기 종래 기술에 따른 고무 재질의 방수테이프는 옥외에서 노출되어 시공될 경우에는 자외선이나 비, 바람 등에 의해 쉽게 부식 또는 수축이 되고, 고무 재질의 특성상 온도 변화에 취약하기 때문(즉, 내열성이 우수하지 못하기 때문)에 기재면에 부착된 접착제의 결합력이 약화되어 구조물로부터 쉽게 이탈됨으로써 방수 하자를 야기하는 문제점이 있었다.In addition, the waterproof tape of the rubber material according to the prior art is easily corroded or contracted by ultraviolet rays, rain, wind, etc., when exposed to the outdoors, and is vulnerable to temperature changes due to the characteristics of the rubber material (ie, heat resistance Because it is not excellent) the adhesive force of the adhesive attached to the surface of the substrate is weakened easily separated from the structure there was a problem causing a waterproof defect.

또한, 상기 종래 기술에 따른 고무 재질의 방수테이프는 보호필름 등이 결합된 외부 표면을 수용성 도료로 마감할 경우 상기 수용성 도료가 비바람과 자외선에 노출되어 방수테이프의 표면과 쉽게 분리되기 때문에 부득이 마감재를 유성 도료로 선택할 수 밖에 없어서 주변 페인트 색이나 질감에 따라 다양한 색상이나 질감을 표현하지 못하게 되는 문제점이 있었다
In addition, the waterproof tape of the rubber material according to the prior art is inevitable because the water-soluble paint is easily exposed to the surface of the waterproof tape is exposed to the wind and ultraviolet rays when the outer surface combined with a protective film, such as a water-soluble paint is inevitable There was a problem in that it was not possible to express various colors or textures according to the color or texture of the surrounding paint because it had to be selected as an oil paint.

본 발명은 이러한 종래 기술의 문제점을 해결하기 위한 것으로서, 본 발명의 목적은 내열성 및 내한성이 좋고 자외선에 강하여, 구조물의 지하 또는 내부뿐만 아니라 옥외에 노출시켜 사용하는 경우에도 수축이나 변형을 최소화하여 방수기능을 견고히 유지할 수 있는 다용도 방수테이프 및 그 제조방법을 제공하는 것이다.The present invention is to solve the problems of the prior art, the object of the present invention is heat resistance and cold resistance good and resistant to ultraviolet rays, waterproof even by minimizing shrinkage or deformation even when exposed to the basement or interior of the structure as well as outdoors It is to provide a multi-purpose waterproof tape and a method of manufacturing the same that can maintain the function firmly.

또한, 본 발명의 다른 목적은 두께를 얇게 구성할 수 있어서 연결 이음부 및 기재면과의 단차를 최소화할 수 있고, 측면이나 좁은 틈새 또는 굴곡진 부분에도 유연하게 부착이 가능한 다용도 방수테이프 및 그 제조방법을 제공하는 것이다. In addition, another object of the present invention can be configured to a thin thickness to minimize the step difference between the connecting seam and the substrate surface, and can be flexibly attached to the side or narrow gaps or curved parts, multi-purpose waterproof tape and its manufacture To provide a way.

또한, 본 발명의 또 다른 목적은 그 상부면에 도료를 도포할 수 있도록 방수테이프의 표면에 접착제에 의하여 견고하게 부착된 도막층을 형성함으로써, 주변 환경의 색에 따라 시공이 완료된 방수테이프의 외부 표면을 여러 가지 다양한 표면마감재(유성 및 수성도료)로 자유롭게 도포할 수 있는 다용도 방수테이프 및 그 제조방법을 제공하는 것이다.In addition, another object of the present invention is to form a coating layer firmly adhered by an adhesive on the surface of the waterproof tape to apply the paint on the upper surface, the exterior of the waterproof tape is completed according to the color of the surrounding environment It is to provide a multi-purpose waterproof tape and its manufacturing method which can freely apply the surface to a variety of surface finish (oil-based and water-based paint).

또한, 본 발명의 또 다른 목적은 내열성이 우수하여 판넬이나 철판, 유리 등에 시공하는 경우에도 하절기에 흘러내림 현상이 없는 다용도 방수테이프 및 그 제조방법을 제공하기 위한 것이다.
In addition, another object of the present invention is to provide a multi-purpose waterproof tape and a method of manufacturing the same, which is excellent in heat resistance and does not flow down in the summer, even when applied to a panel, iron plate, glass or the like.

상기 목적을 달성하기 위해 본 발명에 따른 다용도 방수테이프는 점착가능한 비가황 부틸고무를 포함하는 방수층, 상기 방수층의 상부면에 결합되며 상기 방수층의 표면을 보호하고, 알루미늄 박막의 상하부면에 각각 필름이 합지된 표면보호층, 및 고분자계 접착제에 의하여 상기 표면보호층의 상부면에 결합되는 도막층을 포함하되, 상기 필름은 PEN(Polyethylene Naphthalate), PET, PE, PVC, TPO 또는 TPU 중 적어도 어느 하나의 재질로 이루어진 것을 특징으로 한다.In order to achieve the above object, the multi-purpose waterproof tape according to the present invention is a waterproof layer comprising an adhesive non-vulcanized butyl rubber, is bonded to the upper surface of the waterproof layer, and protects the surface of the waterproof layer, the film on the upper and lower surfaces of the aluminum thin film, respectively It includes a laminated surface protective layer, and a coating layer bonded to the upper surface of the surface protective layer by a polymer-based adhesive, the film is at least one of polyethylene naphthalate (PEN), PET, PE, PVC, TPO or TPU Characterized in that made of a material.

또한, 상기 필름은 이축연신된 PEN 필름으로 구성되되, 상기 도막층과 결합되는 제1필름과 상기 방수층과 결합되는 제2필름 중 적어도 어느 하나는 결합력 강화를 위해 프라이머 또는 코로나 처리가 된 것을 특징으로 한다.In addition, the film is composed of a biaxially stretched PEN film, at least one of the first film and the second film to be bonded to the coating layer and the waterproof layer is characterized in that the primer or corona treatment to enhance the bonding strength do.

또한, 상기 방수층의 하부에 부착된 이형지층을 더 포함하되, 상기 도막층은 수용성 우레탄 도막재로 구성되고, 상기 방수테이프는 두께가 0.2 내지 2mm인 스트립 형상인 것을 특징으로 한다.In addition, further comprising a release paper layer attached to the lower portion of the waterproof layer, wherein the coating layer is composed of a water-soluble urethane coating material, the waterproof tape is characterized in that the strip shape of 0.2 to 2mm thickness.

또한, 본 발명에 따른 다용도 방수테이프의 제조방법은 알루미늄 박막의 상부면과 하부면에 각각 제1필름과 제2필름을 합지하는 표면보호층 형성단계, 상기 제1필름에 접착제와 도막재를 순차적으로 롤코팅하여 도막층을 형성하는 도막층 형성단계, 및 상기 제2필름에 점착가능한 비가황 부틸고무를 코팅하여 방수층을 형성하는 방수층 형성단계를 포함하되, 상기 제1,2필름은 각각 PEN(Polyethylene Naphthalate), PET, PE, PVC, TPO 또는 TPU 중 적어도 어느 하나의 재질로 이루어진 것을 특징으로 한다.In addition, the manufacturing method of the multi-purpose waterproof tape according to the present invention is a surface protective layer forming step of laminating the first film and the second film on the upper surface and the lower surface of the aluminum thin film, respectively, the adhesive and coating material on the first film sequentially A coating layer forming step of forming a coating layer by roll coating and forming a waterproof layer by coating a non-vulcanized butyl rubber adhesive to the second film, wherein the first and second films are each formed of PEN ( Polyethylene Naphthalate), PET, PE, PVC, TPO or TPU, characterized in that made of at least one material.

또한, 상기 표면보호층 형성단계는 상기 제1,2필름과 알루미늄 박막의 합지 이후 수 시간 내지 수 일 동안 숙성하는 숙성단계를 더 포함하는 것을 특징으로 한다.In addition, the forming of the surface protective layer may further include a aging step of ripening for several hours to several days after the lamination of the first and second films and the aluminum thin film.

또한, 상기 도막층 형성단계와 방수층 형성단계를 수행하기 이전에 결합력 강화를 위해 상기 제1,2필름 중 적어도 어느 하나에 코로나 또는 프라이머 처리를 하는 표면처리 단계를 더 포함하되, 상기 제1,2필름은 이축연신된 PEN 필름인 것을 특징으로 한다.In addition, before performing the coating layer forming step and the waterproof layer forming step further includes a surface treatment step of performing a corona or primer treatment on at least one of the first and second films to enhance the bonding force, the first, second The film is characterized in that it is a biaxially stretched PEN film.

또한, 본 발명에 따른 다용도 방수테이프를 이용한 방수시공방법은 방수를 위한 바탕기재면을 청소하는 제1단계, 상기 바탕기재면에 형성된 홈 또는 균열을 메우는 제2단계, 상기 바탕기재면에 프라이머를 도포하는 제3단계, 및 상기 프라이머가 도포된 바탕기재면에 제1항 내지 제3항 중 어느 하나의 항에 따른 방수테이프, 또는 제4항 내지 제6항 중 어느 하나의 항에 따라 제조된 방수테이프를 점착하는 제4단계를 포함하는 것을 특징으로 한다In addition, the waterproof construction method using a multi-purpose waterproof tape according to the present invention, the first step of cleaning the base substrate surface for waterproofing, the second step of filling the grooves or cracks formed on the base substrate surface, the primer on the base substrate surface A third step of applying, and the waterproof tape according to any one of claims 1 to 3 on the base substrate surface to which the primer is applied, or prepared according to any one of claims 4 to 6. And a fourth step of adhering the waterproof tape.

또한, 상기 제4단계에서 점착된 방수테이프의 표면에 표면마감재를 도포하는 제5단계를 더 포함하는 것을 특징으로 한다.
The method may further include a fifth step of applying a surface finish material to the surface of the waterproof tape adhered in the fourth step.

본 발명의 일 실시예에 따른 다용도 방수테이프 및 그 시공방법에 의하면 다음과 같은 효과가 있다.According to the multi-use waterproof tape and the construction method according to an embodiment of the present invention has the following effects.

첫째, 본 발명의 일 실시예에 따른 다용도 방수테이프는 내열성이 우수한 이축연신 타입의 PEN 필름과 기밀성 및 수밀성이 우수한 알루미늄 박막을 포함하기 때문에 방수성, 내열성, 내한성 및 내자외선성이 강하므로 구조물의 지하 또는 내부 뿐만 아니라 옥외에 노출시켜 다양한 용도로 사용할 수 있다.First, since the multi-purpose waterproof tape according to an embodiment of the present invention includes a biaxially-stretched PEN film having excellent heat resistance and an aluminum thin film having excellent airtightness and watertightness, the waterproof, heat resistance, cold resistance, and ultraviolet ray resistance are strong, so the basement of the structure Or it can be used for various purposes by being exposed to the outdoors as well as the inside.

둘째, 본 발명의 일 실시예에 따른 다용도 방수테이프는 접착제를 이용하여 견고하게 부착되는 도막층을 통해 유성 또는 수성 도막재 등 원하는 도료에 의해 외부 표면을 마감할 수 있고, 이로 인하여 기후변화 및 자외선에 노출되는 옥외에 설치되더라도 다양한 색상과 안정적인 외부 표면을 얻을 수 있다.Second, the multi-use waterproof tape according to an embodiment of the present invention can finish the outer surface by the desired paint, such as oil or water coating material through the coating layer firmly attached using an adhesive, thereby changing the climate and ultraviolet rays Even if they are installed outdoors, they can achieve a variety of colors and a stable exterior surface.

셋째, 본 발명의 일 실시예에 따른 다용도 방수테이프는 알루미늄 박막과 PEN 필름에 의하여 얇은 두께로도 종래 기술과 동일한 내구성을 구현할 수 있고 점착성이 강한 비가황 부틸고무를 포함하므로 어떠한 재질에도 잘 부착될 수 있기 때문에 이음부의 단차가 거의 없고 이종 재질과의 접착이 용이하여, 전체 방수공사는 물론 좁은 틈새나 굴곡진 부분의 부분 보수에도 이용될 수 있어서 시공부의 품질을 향상시키고 수명을 연장하는 효과를 얻을 수 있다.Third, the multi-purpose waterproof tape according to an embodiment of the present invention can realize the same durability as the prior art by a thin film and aluminum thin film and PEN film, and can be attached well to any material because it includes a strong adhesive vulcanized butyl rubber. Since there is little step difference between joints and easy adhesion with dissimilar materials, it can be used not only for the whole waterproofing work but also for repairing narrow gaps and bent parts, thereby improving the quality of the construction part and extending the service life. Can be.

넷째, 본 발명의 일 실시예에 따른 다용도 방수테이프는 투수성이 극히 낮은 알루미늄에 자외선과 열에 강한 이축연신타입의 PEN 필름을 합지시킨 후 그 상부에 자외선차단제가 포함된 도막재를 접착제를 이용하여 견고하게 결합시킨 구성이기 때문에 얇은 두께로도 충분한 방수성과 내구성을 구현할 수 있음은 물론, 하절기 등에 옥외에 노출시켜 사용하는 경우에도 흘러내림이나 수축팽창과 같은 변형을 최소화할 수 있다는 장점이 있다.
Fourth, the multi-purpose waterproof tape according to an embodiment of the present invention is laminated with a biaxially stretched type PEN film resistant to ultraviolet rays and heat to aluminum having extremely low water permeability and then using an adhesive with a coating material containing a sunscreen on the top thereof. Since it is a firmly combined configuration, it is possible to realize sufficient waterproofness and durability even in a thin thickness, and also to minimize deformations such as downflow and shrinkage expansion even when exposed to the outdoors in summer.

도1은 본 발명의 일실시예에 따른 다용도 방수테이프의 사시도,
도2a는 도1에 도시한 다용도 방수테이프의 단면을 확대한 도면,
도2b는 도1에 도시한 표면보호층의 단면을 확대한 도면,
도3은 도1에 따른 다용도 방수테이프의 제조방법에 대한 공정도, 및
도4는 도1에 따른 다용도 방수테이프를 이용한 방수시공방법에 대한 공정도이다.1 is a perspective view of a multipurpose waterproof tape according to an embodiment of the present invention,
Figure 2a is an enlarged view of the cross section of the multipurpose waterproof tape shown in Figure 1,
FIG. 2B is an enlarged view of the cross section of the surface protection layer shown in FIG. 1; FIG.
Figure 3 is a process chart for the manufacturing method of the multi-use waterproof tape according to Figure 1, and
Figure 4 is a process chart for a waterproof construction method using a multi-purpose waterproof tape according to FIG.

이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성요소들에 참조부호를 부가함에 있어서, 동일한 구성요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the drawings, the same reference numerals are used to designate the same or similar components throughout the drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear.

도1은 본 발명의 일실시예에 따른 다용도 방수테이프의 사시도이고, 도2a는 도1에 도시한 다용도 방수테이프의 단면을 확대한 도면이며, 도2b는 도1에 도시한 표면보호층의 단면을 확대한 도면이다.1 is a perspective view of a multi-use waterproof tape according to an embodiment of the present invention, Figure 2a is an enlarged view of the cross section of the multi-purpose waterproof tape shown in Figure 1, Figure 2b is a cross-sectional view of the surface protection layer shown in FIG. Is an enlarged view.

도1, 도2a, 및 도2b에 도시된 바와 같이 본 발명의 일실시예에 따른 다용도 방수테이프(1)는 이형지(5)가 부착된 방수층(10), 상기 방수층(10)의 상부면에 형성된 표면보호층(20), 및 상기 표면보호층(20)의 상부면에 형성된 도막층(30)을 포함하여 이루어진다.As shown in Figure 1, Figure 2a, and Figure 2b multi-purpose waterproof tape 1 according to an embodiment of the present invention is a waterproof layer 10 to which a release paper (5) is attached, the upper surface of the waterproof layer (10) It includes a surface protection layer 20 formed, and a coating layer 30 formed on the upper surface of the surface protection layer 20.

상기 방수층(10)은 부틸고무(IIR)를 주폴리머로 하여 보강재, 충진재, 노화방지재를 균일하게 혼합하여 이루어지는데, 본 실시예에서는 일예로서 부틸고무 15 중량%, 카본 보강제 10 중량%, 가소제 1중량%, 첨가제 25 중량%, 및 중탄 충전제 49 중량%으로 이루어지는 것으로 구성하였다.The waterproof layer 10 is made of butyl rubber (IIR) as a main polymer, a mixture of reinforcing materials, fillers and anti-aging materials is uniformly mixed. In this embodiment, 15% by weight of butyl rubber, 10% by weight carbon reinforcing agent, plasticizer 1 wt%, 25 wt% additives, and 49 wt% bicarbonate filler.

이때, 상기 충전제는 탈크, 카본블랙, 탄산칼슘, 및 이들의 혼합물로 이루어진 군으로부터 선택하여 사용할 수 있고, 상기 가소제는 디옥틸프탈레이트, 디부틸프탈레이트, 디이소노닐프탈레이트, 사이트릭애시드에스테르, 텍사놀/에스테르알콜 등이 사용될 수 있으며 이들은 단독 또는 1종 이상 혼합하여 사용할 수 있다.In this case, the filler may be selected from the group consisting of talc, carbon black, calcium carbonate, and mixtures thereof, and the plasticizer is dioctylphthalate, dibutyl phthalate, diisononyl phthalate, citric acid ester, texanol Ester alcohol, etc. may be used, and these may be used individually or in mixture of 1 or more types.

또한, 상기 첨가제는 로진(송진), 활제로서 스테아린산 등을 포함할 수 있으며 이들은 단독 또는 1종 이상 혼합하여 사용할 수 있다.In addition, the additive may include rosin (rosin), stearic acid as a lubricant and these may be used alone or in combination of one or more.

이와 같이 형성된 상기 방수층(10)은 비가황계 합성고무시트로서 방수성을 가질 뿐만 아니라 인체에 유해한 물질을 공중에 발생시키지 않고 신축성과 점착성이 우수하여 별도의 접착제 없이도 서로 일체화가 될 수 있는 자착 특성, 방음성, 방식성 및 방진성을 제공할 수 있다.The waterproof layer 10 formed as described above is a non-vulcanized synthetic rubber sheet having not only waterproofness but also excellent in elasticity and adhesiveness without generating harmful substances in the air, and can be integrated with each other without a separate adhesive, soundproofing It can provide corrosion resistance and dust resistance.

따라서, 본 발명의 일 실시예에 따른 방수테이프(1)는 기재에 대해서 리벳이나 못 등의 결합부재에 의해서 손상됨이 없이 자체의 점착성에 의하여 각종 이종 재질로 된 기재면에 쉽게 결합될 수 있다.Therefore, the waterproof tape 1 according to an embodiment of the present invention can be easily bonded to the substrate surface made of various heterogeneous materials by its own adhesiveness without being damaged by the coupling member such as rivets or nails with respect to the substrate.

또한, 고무재질로 된 상기 방수층(10)은 내구성 및 내열성이 비교적 우수하고 전술한 바와 같이 어떤 이종 재질과도 잘 부착이 되는 높은 점착성과 신축성을 가지고 있어서 기후에 따라 신축 팽창하는 콘크리트 등과 같은 기재의 열적 구동에 쉽게 순응할 수 있다.In addition, the waterproof layer 10 made of a rubber material is relatively excellent in durability and heat resistance, and has a high adhesiveness and elasticity that is well adhered to any heterogeneous material as described above, and thus is made of a base material such as concrete that expands and contracts according to the climate. It can be easily adapted to thermal drive.

또한, 상기 방수층(10)의 일면, 즉 설치면(또는 기재면)에 부착되는 부분에는 얇은 두께의 이형지(5)가 부착되어 방수테이프(1)를 시공할 경우 운반 및 이동을 용이하게 하는데, 상기 이형지(5)는 도1에 도시된 바와 같이 시공시 방수층(10)으로부터 쉽게 박리될 수 있다.In addition, one side of the waterproof layer 10, that is, a portion attached to the installation surface (or the substrate surface) is attached to the release paper 5 of a thin thickness to facilitate the transport and movement when constructing the waterproof tape (1), The release paper 5 may be easily peeled from the waterproof layer 10 during construction as shown in FIG. 1.

한편, 상기 방수층(10)의 타측 일면, 즉 상기 방수층(10)의 상부에는 표면보호층(20)이 결합되는데, 상기 표면보호층(20)은 상기 방수층(10)의 수축을 막고 방수성, 내열성, 내한성 및 내구성을 향상시켜 방수층(10)의 표면을 보호함으로써 방수테이프의 내구성을 제고하는 역할을 한다. On the other hand, the other surface of the waterproof layer 10, that is, the surface protective layer 20 is coupled to the upper portion of the waterproof layer 10, the surface protective layer 20 prevents the shrinkage of the waterproof layer 10 and waterproof, heat resistance By improving the cold resistance and durability to protect the surface of the waterproof layer 10 serves to enhance the durability of the waterproof tape.

본 발명의 일실시예에 있어서, 상기 표면보호층(20)은 투수성이 매우 낮은 알루미늄 박막(21)과, 상기 알루미늄 박막(21)의 양면에 각각 부착된 PEN(Polyethylene Naphthalate) 재질의 제1필름 및 제2필름(23, 25)을 포함한다.In one embodiment of the present invention, the surface protection layer 20 is a first thin film of aluminum (21) having a very low permeability and a polyethylene naphthalate (PEN) material attached to both surfaces of the aluminum thin film 21, respectively. Film and second films 23 and 25.

이때, 본 실시예에서는 상기 PEN 재질의 필름이 알루미늄 박막(21)의 상,하부면에 모두 합지되도록 구성하는데, 이는 PEN 재질의 필름이 알루미늄 박막(21)의 한쪽 면에만 합지될 경우 PEN 재질의 필름이 부착된 쪽으로 표면보호층(20)이 말리는 컬링 현상을 방지하기 위함이다. In this embodiment, the PEN material film is laminated on both the upper and lower surfaces of the aluminum thin film 21. When the PEN material is laminated on only one surface of the aluminum thin film 21, the PEN material is laminated. This is to prevent curling phenomenon in which the surface protection layer 20 is curled toward the film.

또한, 상기 알루미늄 박막(21)의 상하부면에 각각 제1필름 및 제2필름(23,25)을 합지시킬 때 후술하는 바와 같이 스트립 형상으로 구성되는 상기 방수테이프의 길이 방향으로 상기 표면보호층(20)의 양측 단부는 알루미늄 박막(21)의 개재없이 상기 필름(23,25)이 서로 직접 합지되도록 구성될 수 있다. In addition, when the first film and the second film (23, 25) is laminated on the upper and lower surfaces of the aluminum thin film 21, as described later, the surface protective layer in the longitudinal direction of the waterproof tape formed in a strip shape ( Both ends of the 20 may be configured such that the films 23 and 25 are directly laminated with each other without the aluminum thin film 21 interposed therebetween.

이 경우, 구체적으로는 도2b에 도시한 바와 같이 상기 필름(23,25)들은 알루미늄 박막(21)의 측면을 감싸도록 표면보호층(20)의 양 단부에서 상기 제1,2필름(23,25) 끼리 서로 합지된다.In this case, specifically, as shown in FIG. 2B, the films 23 and 25 may cover the sides of the aluminum thin film 21 at both ends of the surface protection layer 20. 25) Each other merges.

이는 이질적인 재료인 상기 알류미늄 박막(21)과 상기 필름 사이의 결합을 동질적인 재료인 상기 제1필름 및 제2필름(23, 25) 끼리의 결합으로 보강함으로써 표면보호층(20)의 결합을 보다 견고하게 하기 위한 것이며, 나아가 알루미늄 박막(21)이 외부에 노출된 측면을 따라 열화되는 현상과 이로 인하여 표면보호층(20)이 서로 박리되는 것을 방지할 수 있게 된다.This reinforces the bond between the aluminum thin film 21, which is a heterogeneous material, and the film, by bonding the first film and the second film 23, 25, which are homogeneous materials, to enhance the bonding of the surface protection layer 20. It is intended to be firm, and furthermore, a phenomenon in which the aluminum thin film 21 is deteriorated along a side exposed to the outside and thereby prevents the surface protection layer 20 from being peeled from each other.

상기 알루미늄 박막(21)는 투수성이 극히 낮고 치수안정성이 매우 우수하여 방수테이프의 방수기능을 제고시킬 뿐만 아니라, 자외선에 강하고 열적 구동에 의한 수축 또는 신장이 거의 없어서 상기 방수테이프를 옥외환경에 노출시켜 사용할 수 있도록 한다.The aluminum thin film 21 is extremely low in permeability and excellent in dimensional stability to enhance the waterproofing function of the waterproof tape, and is also resistant to ultraviolet rays and hardly shrinkage or elongation by thermal driving, thereby exposing the waterproof tape to the outdoor environment. To use it.

본 실시예에서는 상기 알루미늄 박막(21)은 박막으로 된 알루미늄 시트 또는 알루미늄의 미세분말을 균일한 두께로 제1,2필름(23,25) 사이에 도포하는 것에 의하여 바람직하게 구성될 수 있다.In the present embodiment, the aluminum thin film 21 may be preferably configured by applying a thin sheet of aluminum sheet or fine powder of aluminum between the first and second films 23 and 25 with a uniform thickness.

또한, 이와 달리 상기 알루미늄 박막(21)은 제1필름(23) 또는 제2필름(25) 중 어느 하나의 표면에 알루미늄 입자를 증착시켜 구성할 수도 있는데, 이 경우에는 필름을 합지시켜 표면보호층(20)을 형성하기 이전에 증착면을 고르게 연마하는 공정을 거치는 것이 바람직하다.Alternatively, the aluminum thin film 21 may be formed by depositing aluminum particles on the surface of either the first film 23 or the second film 25. In this case, the surface protective layer is laminated by laminating the film. It is preferable to go through the process of evenly polishing the deposition surface before forming (20).

한편, 상기 제1,2필름(23,25)은 전술한 알루미늄 박막(21)의 물리적 성능을 향상시키는 역할을 수행하는데, 구체적으로는 후술하는 바와 같이 상기 표면보호층(20)의 상하부면이 각각 방수층(10)과 도막층(30)과 용이하게 결합될 수 있도록 한다.Meanwhile, the first and second films 23 and 25 play a role of improving the physical performance of the aluminum thin film 21 described above. Specifically, upper and lower surfaces of the surface protection layer 20 may be formed as described below. Respectively, the waterproof layer 10 and the coating layer 30 may be easily combined with each other.

또한, PEN 재질로 된 상기 제1,2필름(23, 25)은 방수테이프의 내열성 및 내구성을 더욱 향상시키기 위하여 180℃ 이상의 고온을 견딜 수 있는 이축연신타입으로 구성되는데, 이와 같이 이축연신된 제1,2필름(23, 25)은 내열성이 우수함은 물론 강직한 분자사슬 구조로 인하여 PET 필름보다 얇은 두께에서도 우수한 인장강도, 충격강도, 파열강도 및 적정한 신도를 가지기 때문에 방수테이프의 두께를 더욱 최소화할 수 있다는 장점이 있다. In addition, the first and second films 23 and 25 made of PEN are made of a biaxial stretching type capable of withstanding high temperature of 180 ° C. or higher in order to further improve the heat resistance and durability of the waterproof tape. 1,2 film (23, 25) has excellent tensile strength, impact strength, burst strength and proper elongation even at thinner thickness than PET film due to its excellent heat resistance and rigid molecular chain structure, further minimizing the thickness of waterproof tape The advantage is that you can.

뿐만 아니라, 상기 PEN 재질은 일반적으로 알려진 바와 같이 융점이 266℃이고 유리전이온도가 123℃로서 PET 대비 약 50℃이상 높기 때문에 매우 우수한 열적 치수안정성을 가지며, PET 보다 우수한 전기 절연성, 유전율, 절연파괴전압을 가진다.In addition, since the PEN material has a melting point of 266 ° C. and a glass transition temperature of 123 ° C., which is about 50 ° C. or higher than PET, the PEN material has excellent thermal dimensional stability, and has excellent electrical insulation, dielectric constant, and dielectric breakdown than PET. Has a voltage.

따라서, 본 실시예에 따른 다용도 방수테이프는 상기 제1,2필름(23,25)을 PEN 재질을 이용하여 구성함으로써 고온에서도 수축팽창이 되지 않는 내열성과 전기적 안정성이 우수한 방수테이프를 제조할 수 있다는 장점이 있다.Therefore, the multi-purpose waterproof tape according to the present embodiment can be manufactured by using the PEN material of the first and second films 23 and 25 to produce a waterproof tape having excellent heat resistance and electrical stability that does not shrink and expand even at high temperatures. There is an advantage.

또한, 상기 PEN 재질의 제1,2필름(23, 25)은 필름에서 추출되는 올리고머(oligomer)가 작고, 매우 우수한 내유성, 내약품성, 내가수분해성, 가스차단성 및 내방사선성을 가지기 때문에 부틸 고무재질의 방수층(10)과 결합성이 우수함은 물론 옥외에 설치할 경우에도 외부 환경에 의한 영향을 최소화할 수 있기 때문에 장기간의 방수수명을 유지할 수 있다는 장점이 있다.In addition, the first and second films 23 and 25 made of PEN have a small amount of oligomers extracted from the film, and have very good oil resistance, chemical resistance, hydrolysis resistance, gas barrier properties, and radiation resistance. As well as excellent bondability with the waterproof layer 10 of the material, even when installed outdoors there is an advantage that it can maintain the long-term waterproof life because it can minimize the influence of the external environment.

이 경우, 상기 PEN 재질의 제1,2필름(23,25)은 친환경 소재로서 내열도가 높은 고분자계 미세접착제를 이용하여 알루미늄 박막(21)과 합지되면서 보다 견고한 구성을 가지게 됨은 물론 보다 친환경적인 표면보호층(20)을 이루게 된다.In this case, the first and second films 23 and 25 of the PEN material are environmentally friendly materials, and are laminated with the aluminum thin film 21 using a polymer-based microadhesive having high heat resistance, as well as having a more robust configuration. The surface protective layer 20 is formed.

본 실시예에서는 상기 제1,2필름(23,25)이 PEN 필름으로 이루어진 경우를 일예로서 설명하였으나 이에 한정되지 아니하며, 필요에 따라서는 동일한 기능을 수행하는 범위내에서 PET(Polyethylene Terephthalate), PE(Polyethylene), PVC(Polyvinyl Chloride),TPO(Thermoplastic Polyolefin), 또는 TPU(Thermoplastic Polyurethane) 중 적어도 어느 하나의 소재로 구성될 수도 있다.In the present exemplary embodiment, the first and second films 23 and 25 are made of a PEN film as an example, but the present invention is not limited thereto. If necessary, polyethylene terephthalate (PET) and PE may be used within the range of performing the same function. (Polyethylene), PVC (Polyvinyl Chloride), TPO (Thermoplastic Polyolefin), or TPU (Thermoplastic Polyurethane) may be composed of at least one material.

이와 같이 구성된 상기 표면보호층(20)은 알루미늄 박막(21)과 PEN 재질의 제1,2필름(23,25)을 포함함으로써 전술한 바와 같이 방수층(10)의 내자외선성, 방수성, 내열성, 내한성 및 내구성을 현저히 높일 수 있기 때문에, 본 발명에 따른 다용도 방수테이프(1)는 종래 기술에 따른 방수테이프와 동일한 수준의 내자외선성, 내열성 및 내한성을 제공하기 위해 요구되는 두께가 현저히 저감될 수 있다.The surface protection layer 20 configured as described above includes the aluminum thin film 21 and the first and second films 23 and 25 made of PEN, so that the ultraviolet ray resistance, the water resistance, the heat resistance, Since the cold resistance and durability can be significantly increased, the multipurpose waterproof tape 1 according to the present invention can significantly reduce the thickness required to provide the same level of UV resistance, heat resistance and cold resistance as the waterproof tape according to the prior art. have.

따라서, 본 발명에 따른 다용도 방수테이프는 두께가 얇고 어떠한 재질에도 잘 부착되므로 시공시 기재면과의 단차 또는 이음 부분의 단차를 최소화할 수 있음은 물론 측벽, 틈 사이, 굴곡진 곡면부분에 대해서도 용이하게 밀착되어 밀봉시킴으로써 수분이 쉽게 투과되지 못하게 할 수 있다.Therefore, the multi-purpose waterproof tape according to the present invention has a thin thickness and adheres well to any material, thereby minimizing the step difference between the base surface or the joint part during construction, as well as the side wall, the gap, and the curved curved part. It is possible to prevent moisture from permeating easily by being closely adhered and sealed.

또한, 상기와 같은 구성에 의하여 본 발명에 따른 방수테이프는 내열성 및 내자외선성이 더욱 향상되기 때문에 콘크리트 구조물의 지하 또는 내부 뿐만 아니라 하절기 또는 동절기에 자외선 또는 차가운 공기에 노출되는 옥외의 기재면, 철골구조물 또는 판넬외부 등에 시공되는 경우에도 방수테이프가 흘러내리는 현상이나 수축되는 현상을 최소화함으로써 방수성능을 견고하게 유지할 수 있다는 장점이 있다.In addition, the waterproof tape according to the present invention by the above configuration further improves the heat resistance and ultraviolet resistance, so as to be exposed to ultraviolet or cold air in the summer or winter as well as the basement or the interior of the concrete structure, steel frame Even when the structure or the outside of the panel is installed, there is an advantage that the waterproof tape can be maintained firmly by minimizing the phenomenon that the waterproof tape flows down or shrinks.

전술한 바와 같이 상기 알루미늄 박막(21)과 PEN 재질의 제1,2필름(23, 25)이 합지되어 표면보호층(20)을 형성하면, 상기 표면보호층(20)을 상기 방수층(10)에 결합하게 된다.As described above, when the aluminum thin film 21 and the first and second films 23 and 25 made of PEN are laminated to form the surface protection layer 20, the surface protection layer 20 is the waterproof layer 10. To be bound to

이때, 상기 방수층(10)과 결합되는 상기 표면보호층(20)의 일면, 즉 비가황 부틸고무가 코팅될 제2필름(25)에는 부착력 강화를 위해 프라이머 또는 코로나 처리를 하는 것이 바람직하다.In this case, it is preferable to apply a primer or corona treatment to one surface of the surface protective layer 20 that is combined with the waterproof layer 10, that is, the second film 25 to be coated with unvulcanized butyl rubber.

그리고, 후술할 도막층(30)과 결합될 표면보호층(20)의 다른면, 즉 제1필름(23)에도 마찬가지로 인쇄성 및 부착력 강화를 위하여 프라이머 또는 코로나 처리를 할 수 있는데, 이때 상기 프라이머는 일예로서 폴리우레탄 재질을 포함하는 이액형으로 구성될 수 있다.In addition, the other surface of the surface protection layer 20 to be combined with the coating layer 30 to be described later, that is, the first film 23 may be subjected to a primer or corona treatment to enhance printability and adhesion. As an example it may be configured as a two-component type containing a polyurethane material.

상기 표면보호층(20)에 결합되는 도막층(30)은 자외선 차단제가 첨가된 탄성도막재(31)를 접착제(33)를 이용하여 상기 표면보호층(20)에 일체화시키는 방식으로 형성되는데, 본 실시예에서는 일예로서 상기 도막재(31)를 수용성 우레탄 도막으로 구성하였다.The coating layer 30 bonded to the surface protection layer 20 is formed in such a way that the elastic coating material 31 to which the sunscreen is added is integrated with the surface protection layer 20 by using the adhesive 33. In this embodiment, the coating material 31 is formed of a water-soluble urethane coating film as an example.

이때, 상기 도막층(30)은 접착제(33)를 상기 표면보호층(20)의 제1필름(23) 위에 분사한 후, 접착제(33)가 굳기 전에 도막재(31)(본 실시예에서는 수용성 우레탄 도막재)를 2회 이상 도포하고 열풍으로 건조시켜 롤링하는 롤코팅 방식으로 제조한다.In this case, the coating layer 30 sprays the adhesive 33 on the first film 23 of the surface protection layer 20, and then the coating layer 31 (in this embodiment) before the adhesive 33 hardens. A water-soluble urethane coating material) is applied two or more times, and dried by hot air to prepare a roll coating method.

또한, 상기 접착제(33)는 시중에서 시판되는 것 중에서 다양하게 선택가능하나, 본 실시예에서는 접착성과 내열성이 우수한 고분자계 미세접착제를 이용하여 바람직하게 구현될 수 있다.In addition, the adhesive 33 may be variously selected from commercially available ones, but in the present embodiment, the adhesive 33 may be preferably implemented using a polymer-based microadhesive having excellent adhesion and heat resistance.

본 발명에서는 옥외 시공시 외부 환경에 의해 상기 도막층(30)이 표면보호층(20)과 박리되는 것을 방지하기 위하여 물성이 상이한 두 개의 재질을 접착시키는데 주로 사용되는 핫멜트, 수성화접착제 또는 UV경화형 접착제를 적용할 수 있다.In the present invention, in order to prevent the coating layer 30 from being peeled off from the surface protection layer 20 by the external environment during outdoor construction, hot melt, water-based adhesive or UV curing type used mainly to bond two materials having different physical properties. An adhesive can be applied.

또한, 요소수지, 우레탄수지, 폴리비닐알콜수지 또는 폴리비닐아세테이트수지를 포함하는 접착제, 스티렌계 열가소성 엘라스토머, 에틸렌 초산비닐계 접착제, 에틸렌 아크릴계 공중합체, 올레핀계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 폴리우레탄계 접착제, 또는 천연접착제 중 적어도 어느 하나를 적용할 수도 있다. In addition, adhesives including urea resins, urethane resins, polyvinyl alcohol resins or polyvinylacetate resins, styrene thermoplastic elastomers, ethylene vinyl acetate adhesives, ethylene acrylic copolymers, olefin adhesives, polyester adhesives, and polyamides At least any one of an adhesive, a polyurethane adhesive, or a natural adhesive may be applied.

종래 기술에 따를 경우 일반적으로 합성수지재로 구성된 필름면에는 수용성 도료의 부착력이 현저히 떨어져 비바람과 자외선에 오래 노출시킬 경우 열화에 의하여 상기 수용성 도료가 필름 표면으로부터 쉽게 분리되기 때문에 방수테이프의 외부 표면을 수용성 도료로 마감하지 못하는 문제점이 있었다.According to the prior art, the film surface composed of a synthetic resin material generally has a very low adhesion force of the water-soluble paint, so that the water-soluble paint is easily separated from the film surface by deterioration when exposed to rain and ultraviolet rays for a long time, so that the water-soluble surface of the waterproof tape is water-soluble. There was a problem that can not finish with paint.

이를 해결하기 위하여, 본 발명의 일실시예에 따른 방수테이프(1)는 접착제(33)를 이용하여 표면보호층(20)의 상부에 도막층(30)을 견고하게 결합시킴으로써, 방수시공이 완료된 이후에 주변 환경과의 조화를 고려하여 여러 가지 종류의 표면마감재(예를 들면, 유성 우레탄, 락카와 같은 유성도료 또는 수성 페인트와 같은 수성도료)에 의해 방수테이프(1)의 외부 표면을 마감할 수 있도록 하였다.In order to solve this problem, the waterproof tape 1 according to the embodiment of the present invention is firmly bonded to the coating layer 30 on the top of the surface protection layer 20 by using the adhesive 33, the waterproof construction is completed Afterwards, the outer surface of the waterproof tape 1 may be finished by various kinds of surface finishes (for example, oil-based urethanes, oil-based paints such as lacquers, or water-based paints such as water-based paints) in consideration of harmony with the surrounding environment. To make it possible.

뿐만 아니라, 상기 도막재(31)는 접착성과 내열성이 우수한 접착제(33)에 의하여 표면보호층(20)에 견고하게 부착되어 기후변화에 매우 안정적이기 때문에 본 발명에 따른 다용도 방수테이프(1) 건물 외부의 기후 및 자외선에 노출된 부분에 대한 방수부재로 사용될 수 있다.In addition, since the coating material 31 is firmly attached to the surface protection layer 20 by the adhesive 33 having excellent adhesiveness and heat resistance and is very stable to climate change, the multipurpose waterproof tape 1 building according to the present invention. It can be used as a waterproof member against external weather and UV exposed part.

따라서, 본 발명의 일실시예에 따른 다용도 방수테이프는 접착재에 의하여 제1필름에 결합된 도막층을 통하여 유성 또는 수성도료 등 원하는 표면마감재에 의해 외부 표면을 마감할 수 있음은 물론, 옥외 시공시 기후변화에도 매우 안정적인 외부 표면을 얻을 수 있게 된다.Therefore, the multi-purpose waterproof tape according to an embodiment of the present invention can finish the external surface by a desired surface finish material such as oil or water paint through the coating layer bonded to the first film by the adhesive material, as well as during outdoor construction A very stable outer surface can be obtained even with climate change.

한편, 상기와 같이 구성된 본 발명에 따른 다용도 방수테이프는 제품의 용도에 따라 적정한 폭(일예로서, 3cm, 5cm, 10cm 등)을 가진 스트립 형태로 재단된 후 통상의 테이프와 같이 롤 형태로 권취된다.On the other hand, the multi-purpose waterproof tape according to the present invention configured as described above is cut in the form of a strip having a suitable width (for example, 3cm, 5cm, 10cm, etc.) according to the use of the product is wound in a roll form like a conventional tape. .

이때, 상기 다용도 방수테이프의 두께는 제품이 롤 형태로 권취될 수 있고 통상의 테이프와 같이 곡면부나 틈새 등에 유연하게 접착될 수 있는 시트성질을 가짐과 동시에 상술한 바와 같이 방수성, 내열성, 내한성 및 내자외선성을 향상시킬 수 있는 두께로 결정되는 것이 바람직한데, 본 실시예에서는 상기 방수테이프의 두께를 약 2mm(구체적으로는 약 0.2 내지 0.6mm) 이하로 구성하였다.At this time, the thickness of the multi-purpose waterproof tape has a sheet property that the product can be wound in the form of a roll and can be flexibly bonded to a curved portion or a gap like a conventional tape, and at the same time as described above waterproof, heat resistance, cold resistance and resistance It is preferable to determine the thickness to improve the UV properties, in this embodiment, the thickness of the waterproof tape was configured to about 2mm (specifically about 0.2 to 0.6mm) or less.

이와 같이 본 발명의 방수테이프(1)는 점착성이 강한 비가황 부틸고무를 포함하기 때문에 어떠한 재질에도 잘 부착될 뿐만 아니라 알루미늄 박막과 PEN 재질의 제1,2필름이 포함된 표면보호층(20)과 도막층(30)에 의해 수분, 자외선, 온도변화와 같은 외부환경에도 강해 시공면의 품질을 향상시키고 수명을 연장하는 효과를 얻을 수 있다.
As described above, the waterproof tape 1 of the present invention includes a non-vulcanized butyl rubber with strong adhesiveness and thus is well adhered to any material, and the surface protective layer 20 including the aluminum thin film and the first and second films of PEN material. The coating layer 30 is also resistant to external environments such as moisture, ultraviolet rays, and temperature changes, thereby improving the quality of the construction surface and extending the service life.

도3은 본 발명의 일 실시예에 따른 다용도 방수테이프(1)의 제조방법에 대한 공정도이다.Figure 3 is a process chart for the manufacturing method of the multi-use waterproof tape 1 according to an embodiment of the present invention.

이하, 본 발명의 다용도 방수테이프의 제조방법에 대해 설명하기로 한다.Hereinafter, the manufacturing method of the multipurpose waterproof tape of the present invention will be described.

도3에 도시된 바와 같이 먼저 알루미늄 박막(21)의 상하부면에 PEN 재질의 제1,2필름(23,25)을 합지하여 표면보호층(20)을 형성한다(S10).As shown in FIG. 3, first, the first and second films 23 and 25 made of PEN are laminated on upper and lower surfaces of the aluminum thin film 21 to form a surface protection layer 20 (S10).

상기 S10 단계에서 제1,2필름(23,25)과 알루미늄 박막(21)의 합지가 완료되면, 상기 합지된 표면보호층(20)을 소정 시간동안 숙성(aging)하는 숙성단계를 수행하는데(S20), 상기 숙성단계는 합지 이후 수 시간 내지 수 일, 바람직하게는 24시간 내지 48시간의 범위를 가질 수 있다.When the lamination of the first and second films 23 and 25 and the aluminum thin film 21 is completed in step S10, a aging step of aging the laminated surface protective layer 20 for a predetermined time is performed ( S20), the aging step may have a range of several hours to several days, preferably 24 hours to 48 hours after lamination.

이와 같이 숙성단계를 거치는 이유는 제1,2필름(23, 25)과 알루미늄 박막(21)을 견고히 결합시켜 시공시에 서로 박리되지 않도록 하고, 합지면 사이에 개재될 수 있는 기포 등이 빠져나가도록 함으로써 제조가 완료된 방수테이프의 표면면이 주름지거나 울퉁불퉁해 지는 것을 방지하기 위한 것이다.The reason for the aging step as described above is that the first and second films 23 and 25 and the aluminum thin film 21 are firmly bonded so as not to be peeled off each other during construction, and bubbles, which may be interposed between the laminated surfaces, are released. This is to prevent wrinkles or bumps on the surface of the manufactured waterproof tape.

상기 S20 단계의 숙성단계가 완료되면 상기 제1,2필름(23,25)의 표면을 프라이머 처리 또는 코로나 처리를 수행하는 표면처리단계를 수행하는데(S30), 이는 후술하는 바와 같이 각각 도막층(30)과 방수층(10)이 부착될 제1,2필름(25)에 부착력을 강화시키기 위한 것이다.When the aging step of the step S20 is completed to perform a surface treatment step of performing a primer treatment or a corona treatment on the surface of the first, second film (23, 25) (S30), which will be described later each coating film layer ( 30) and to strengthen the adhesion to the first and second films 25 to which the waterproof layer 10 is to be attached.

본 실시예에서는 상기 S30 단계가 제1,2필름(23,25)에 모두 수행되는 경우를 일예로서 설명하였으나, 필요에 따라서는 이들 중 어느 하나에 대해서만 수행될 수도 있다.In the present exemplary embodiment, the case in which the step S30 is performed on both the first and second films 23 and 25 is described as an example, but may be performed only on any one of them as necessary.

상기 S30 단계가 완료되면 상부에 위치한 상기 제1필름(23)에 접착제와 도막재(본 실시예에서는 수용성 우레탄 도막재)를 순차적으로 롤코팅하여 도막층(30)을 형성하는 도막층 형성단계를 수행한다(S40).After the step S30 is completed, a coating layer forming step of forming a coating layer 30 by sequentially rolling an adhesive and a coating material (in this embodiment, a water-soluble urethane coating material) on the first film 23 located above Perform (S40).

상기 도막층(30)은 전술한 바와 같이 상기 접착제(33)를 상기 표면보호층(20)의 PEN 필름 위에 분사한 후, 접착제(33)가 굳기 전에 수성 우레탄 도막재를 2회 이상 도포하고 열풍으로 건조시켜 롤링하는 롤코팅 방식으로 제조될 수 있다.As described above, the coating layer 30 sprays the adhesive 33 onto the PEN film of the surface protection layer 20, and then applies an aqueous urethane coating material two or more times before the adhesive 33 is hardened and hot air. It may be prepared by a roll coating method of rolling to dry.

상기 S40 단계에 의해 도막층(30)이 형성되면, 하부에 위치한 상기 제2필름(25)에 점착가능한 비가황 부틸고무를 코팅하여 방수층(10)을 형성하는 방수층 형성단계를 수행한다(S50).When the coating layer 30 is formed by the step S40, a waterproof layer forming step of forming a waterproof layer 10 is performed by coating a non-vulcanizable butyl rubber on the second film 25 located below (S50). .

상기와 같은 공정에 의하여 기본 구성이 완료되면, 상기 방수층(10)을 이루는 비가황 부틸고무의 하부면에 이형지(5)를 부착하여 제조된 방수테이프(1)를 전술한 바와 같이 적당한 폭으로 재단하여 테이프와 같이 롤 형태로 권취한 후 다양한 용도로 사용할 수 있게 된다.
When the basic configuration is completed by the above process, the waterproof tape 1 manufactured by attaching the release paper 5 to the lower surface of the non-vulcanized butyl rubber forming the waterproof layer 10 is cut to an appropriate width as described above. After winding in the form of a roll like a tape can be used for various purposes.

도4는 본 발명의 일 실시예에 따른 다용도 방수테이프(1)를 이용한 방수시공방법에 대한 공정도이며, 이하에서는 본 발명의 다용도 방수테이프를 이용한 방수시공방법에 대해 설명하기로 한다.Figure 4 is a process chart for a waterproof construction method using a multi-use waterproof tape 1 according to an embodiment of the present invention, hereinafter will be described a waterproof construction method using a multi-purpose waterproof tape of the present invention.

먼저, 방수시공을 하고자 하는 바탕기재에 존재하는 이물질을 깨끗이 청소한 후 건조시키는데(S110), 이때 바탕기재면에 홈이나 균열 등이 있는 경우에는 퍼티 등을 이용하여 이를 메우는 작업을 동시에 수행한다(S120).First, clean and dry the foreign substances present in the base material to be waterproof construction (S110), at this time, if there is a groove or cracks on the base material surface, using a putty, etc. at the same time performs the work of filling them ( S120).

상기 S110 및 S120 단계가 완료되면 정리된 바탕기재면에 붓이나 롤러를 이용하여 프라이머를 도포하는데(S130), 상기 단계는 콘크리트나 조직이 단단하지 못한 재질에 대하여 방수테이프의 부착성을 강화하기 위한 것이기 때문에 바탕기재면의 재질에 따라서는 생략이 가능하다.When the steps S110 and S120 is completed to apply a primer using a brush or a roller on the surface of the base substrate is arranged (S130), the step is to enhance the adhesion of the waterproof tape to the material that is not hard or concrete Because of this, it can be omitted depending on the material of the base substrate surface.

상기 S130 단계가 완료되면 프라이머가 도포된 바탕기재면에 본 발명에 따른 다용도 방수테이프를 점착시키는 것에 의하여 방수시공을 완료한다(S140).When the step S130 is completed, the waterproof construction is completed by adhering the multi-use waterproof tape according to the present invention to the base substrate surface on which the primer is applied (S140).

이때, 필요에 따라서는 방수테이프가 부착된 부분의 주변 환경을 고려하여 전술한 바와 같이 유성도료나 수성도료 등의 여러 가지 다양한 표면마감재 중 어느 하나를 방수테이프의 표면에 도포할 수 있다.
In this case, if necessary, any one of various surface finishes such as an oil paint or an aqueous paint may be applied to the surface of the waterproof tape in consideration of the surrounding environment of the portion where the waterproof tape is attached.

이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. The foregoing description is merely illustrative of the technical idea of the present invention, and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention.

따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas falling within the scope of the same shall be construed as falling within the scope of the present invention.

5 : 이형지 10 : 방수층
20 : 표면보호층 21 : 알루미늄 박막
23, 25 : 제1,2필름 30 : 도막층
31 : 도막재 33 : 접착제5: release paper 10: waterproof layer
20: surface protective layer 21: aluminum thin film
23, 25: 1st, 2nd film 30: coating film layer
31: coating material 33: adhesive

Claims (9)

점착가능한 비가황 부틸고무를 포함하는 방수층;
상기 방수층의 상부면에 결합되어 상기 방수층의 표면을 보호하고, 알루미늄 박막의 상하부면에 각각 필름이 합지된 표면보호층; 및
고분자계 접착제에 의하여 상기 표면보호층의 상부면에 결합되는 도막층을 포함하되,
상기 필름은 PEN(Polyethylene Naphthalate), PET, PE, PVC, TPO 또는 TPU 중 적어도 어느 하나의 재질로 이루어지고,
상기 고분자계 접착제는 핫멜트, 수성화접착제, UV경화형 접착제, 요소수지, 우레탄수지, 폴리비닐알콜수지 또는 폴리비닐아세테이트수지를 포함하는 접착제, 스티렌계 열가소성 엘라스토머, 에틸렌 초산비닐계 접착제, 에틸렌 아크릴계 공중합체, 올레핀계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 폴리우레탄계 접착제, 또는 천연접착제 중 선택되는 적어도 어느 하나인 것을 특징으로 하는 다용도 방수테이프.A waterproof layer comprising a tackifiable non-vulcanized butyl rubber;
A surface protection layer bonded to an upper surface of the waterproof layer to protect the surface of the waterproof layer, and having a film laminated on upper and lower surfaces of the aluminum thin film; And
Including a coating layer bonded to the upper surface of the surface protection layer by a polymer adhesive,
The film is made of at least one of polyethylene naphthalate (PEN), PET, PE, PVC, TPO or TPU,
The polymer adhesive may include a hot melt, an aqueous curing adhesive, an UV curing adhesive, an urea resin, an urethane resin, an adhesive including a polyvinyl alcohol resin or a polyvinylacetate resin, a styrene thermoplastic elastomer, an ethylene vinyl acetate adhesive, an ethylene acrylic copolymer, and the like. , An olefin adhesive, a polyester adhesive, a polyamide adhesive, a polyurethane adhesive, or a natural adhesive. 제1항에 있어서,
상기 필름은 이축연신된 PEN 필름으로 구성되되,
상기 도막층과 결합되는 제1필름과 상기 방수층과 결합되는 제2필름 중 적어도 어느 하나는 결합력 강화를 위해 프라이머 또는 코로나 처리가 된 것을 특징으로 하는 다용도 방수테이프.The method of claim 1,
The film consists of biaxially stretched PEN film,
At least one of the first film is combined with the coating layer and the second film is combined with the waterproof layer is a multi-purpose waterproof tape, characterized in that the primer or corona treatment to enhance the bonding strength. 제2항에 있어서,
상기 방수층의 하부에 부착된 이형지층을 더 포함하되,
상기 도막층은 수용성 우레탄 도막재로 구성되고,
상기 방수테이프는 두께가 0.2 내지 2mm인 스트립 형상인 것을 특징으로 하는 다용도 방수테이프. The method of claim 2,
Further comprising a release paper layer attached to the lower portion of the waterproof layer,
The coating layer is composed of a water-soluble urethane coating material,
The waterproof tape is a multi-purpose waterproof tape, characterized in that the strip shape of 0.2 to 2mm thickness. 제3항에 있어서,
상기 방수테이프의 길이 방향으로 상기 표면보호층의 양측 단부는 알루미늄 박막의 개재없이 상기 필름이 서로 직접 합지된 것을 특징으로 하는 하는 다용도 방수테이프. The method of claim 3,
Both ends of the surface protection layer in the longitudinal direction of the waterproof tape is a multi-purpose waterproof tape, characterized in that the film is directly laminated with each other without intervening the aluminum thin film. 알루미늄 박막의 상부면과 하부면에 각각 제1필름과 제2필름을 합지하는 표면보호층 형성단계;
고분자계 접착제를 이용하여 상기 제1필름의 상부면에 도막재를 결합시켜 도막층을 형성하는 도막층 형성단계;
상기 제2필름에 점착가능한 비가황 부틸고무를 코팅하여 방수층을 형성하는 방수층 형성단계; 및
상기 방수층의 하부에 이형지를 부착한 후 스트립 형태로 재단하는 단계를 포함하되,
상기 제1,2필름은 각각 PEN(Polyethylene Naphthalate), PET, PE, PVC, TPO 또는 TPU 중 적어도 어느 하나의 재질로 이루어지고,
상기 고분자계 접착제는 핫멜트, 수성화접착제, UV경화형 접착제, 요소수지, 우레탄수지, 폴리비닐알콜수지 또는 폴리비닐아세테이트수지를 포함하는 접착제, 스티렌계 열가소성 엘라스토머, 에틸렌 초산비닐계 접착제, 에틸렌 아크릴계 공중합체, 올레핀계 접착제, 폴리에스테르계 접착제, 폴리아미드계 접착제, 폴리우레탄계 접착제, 또는 천연접착제 중 선택되는 적어도 어느 하나인 것을 특징으로 하는 다용도 방수테이프의 제조방법.Forming a surface protective layer for laminating the first film and the second film on the upper and lower surfaces of the aluminum thin film, respectively;
A coating layer forming step of forming a coating layer by bonding a coating material to an upper surface of the first film using a polymer adhesive;
Forming a waterproof layer by coating a non-vulcanized butyl rubber adhesive on the second film to form a waterproof layer; And
After the release paper is attached to the lower portion of the waterproof layer, including the step of cutting in the form of a strip,
The first and second films are each made of at least one of polyethylene naphthalate (PEN), PET, PE, PVC, TPO, or TPU,
The polymer adhesive may include a hot melt, an aqueous curing adhesive, an UV curing adhesive, an urea resin, an urethane resin, an adhesive including a polyvinyl alcohol resin or a polyvinylacetate resin, a styrene thermoplastic elastomer, an ethylene vinyl acetate adhesive, an ethylene acrylic copolymer, and the like. And an olefin adhesive, a polyester adhesive, a polyamide adhesive, a polyurethane adhesive, or a natural adhesive, at least one selected from the group. 제5항에 있어서,
상기 표면보호층 형성단계는 상기 제1,2필름과 알루미늄 박막의 합지 이후 수 시간 내지 수 일 동안 숙성하는 숙성단계를 더 포함하는 것을 특징으로 하는 다용도 방수테이프의 제조방법.The method of claim 5,
The forming of the surface protective layer may further include a aging step of ripening for several hours to several days after lamination of the first and second films and the aluminum thin film. 제6항에 있어서,
상기 도막층 형성단계와 방수층 형성단계를 수행하기 이전에 결합력 강화를 위해 상기 제1,2필름 중 적어도 어느 하나에 코로나 또는 프라이머 처리를 하는 표면처리 단계를 더 포함하되,
상기 제1,2필름은 이축연신된 PEN 필름인 것을 특징으로 하는 다용도 방수테이프의 제조방법.The method according to claim 6,
Before performing the coating layer forming step and the waterproof layer forming step further includes a surface treatment step of performing a corona or primer treatment on at least one of the first and second films to enhance the bonding force,
The first and second films are biaxially stretched PEN film, characterized in that the manufacturing method of the multi-purpose waterproof tape. 방수를 위한 바탕기재면을 청소하는 제1단계;
상기 바탕기재면에 형성된 홈 또는 균열을 메우는 제2단계;
상기 바탕기재면에 프라이머를 도포하는 제3단계; 및
상기 프라이머가 도포된 바탕기재면에 방수테이프를 점착하는 제4단계를 포함하되,
상기 방수테이프는 제1항 내지 제4항 중 어느 하나의 항에 따른 방수테이프이거나, 제5항 내지 제7항 중 어느 하나의 항에 따라 제조된 방수테이프인 것을 특징으로 하는 다용도 방수테이프를 이용한 방수시공방법.A first step of cleaning the base material surface for waterproofing;
A second step of filling a groove or a crack formed in the base substrate surface;
A third step of applying a primer on the base substrate surface; And
Including a fourth step of adhering the waterproof tape to the base substrate surface is coated with the primer,
The waterproof tape is a waterproof tape according to any one of claims 1 to 4, or a waterproof tape manufactured according to any one of claims 5 to 7 using a multi-purpose waterproof tape. Waterproof construction method. 제8항에 있어서,
상기 제4단계에서 점착된 방수테이프의 표면에 표면마감재를 도포하는 제5단계를 더 포함하는 것을 특징으로 하는 다용도 방수테이프를 이용한 방수시공방법.9. The method of claim 8,
And a fifth step of applying a surface finish material to the surface of the waterproof tape adhered in the fourth step.
KR1020110007344A 2010-03-28 2011-01-25 Waterproof Tape, Manufacturing Method thereof, and Waterproof Method using it KR101240691B1 (en)