KR101156953B1 - Method making pottery contain the mica - Google Patents
Method making pottery contain the mica Download PDFInfo
- Publication number
- KR101156953B1 KR101156953B1 KR1020080111828A KR20080111828A KR101156953B1 KR 101156953 B1 KR101156953 B1 KR 101156953B1 KR 1020080111828 A KR1020080111828 A KR 1020080111828A KR 20080111828 A KR20080111828 A KR 20080111828A KR 101156953 B1 KR101156953 B1 KR 101156953B1
- Authority
- KR
- South Korea
- Prior art keywords
- mica
- heating
- undergone
- molding
- loess
- Prior art date
Abstract
본 발명은 운모가 함유된 옹기 제조방법에 관한 것으로, 좀더 상세히는 운모분말과 황토분말을 사용하여 옹기 형틀을 제작한 후 건조시켜 1차열처리하고 내부표면과 외부표면을 유약 처리하여 다시 2차열처리하여 옹기사용시 운모와 황토의 효능을 체험할 수 있도록 함과 동시에 옹기에서 훈증 및 원적외선의 발산을 증가시키위해, 옹기 원료인 황토와 결합하여 황토의 음이온 발생을 한층 더 발생을 증대시키고 아토피와 향균, 탈취 등의 효능이 높은 운모를 혼합하여 황토의 특성상 수분에 손상되는 문제점을 해결함과 동시에 황토와 운모를 결합하여 견고성을 증대시켜 물속에서도 사용하는 반신욕 좌욕기에도 사용이 가능하게 함과 동시에 일반생활에서 사용되는 조미료와 주식과 부식물의 저장용구, 주류 발효 도구, 음료수 저장 용구 등을 형성하여 옹기 사용시 황토의 효능과 운모의 효능인 신진대사 촉진과 노화방지 생리작용 활성화, 여드름, 주근깨 등 피부 트러블에 많은 효과, 혈액순환을 촉진, 향균작용에 탁월한 효과가 있는 것이다.More particularly, the present invention relates to a method for producing a mica-containing pottery, and more particularly, to a method for producing pottery using mica powder and ocher powder, In order to increase the emission of fumigation and far infrared rays in Onggi, it is combined with the loess material of Onggi to increase the generation of anions of loess, and to increase the incidence of atopy, It combines loess and mica to increase durability. It also makes it possible to use it in semi-bathing baths that are used in water, and at the same time, To form seasonings, stocks and storage of corrosive substances, liquor fermentation tools, beverage storage equipment, etc. Protection efficacy and promoting the metabolic efficacy of the use of mica and earthenware Ocher aging promote physiological function activated, pimples, freckles, and many other effects, blood circulation to the skin problems, there is a great effect on the antibacterial action.
옹기, 운모, 흑운모, 백운모, 견운모, 백운모, 금운모, 황토, 유약, 좌욕기 Onggi, mica, biotite, muscovite, sericite, muscovite, gold mica, loess, glaze,
Description
본 발명은 운모가 함유된 옹기 제조방법에 관한 것으로, 좀더 상세히는 운모분말과 황토분말을 사용하여 옹기 형틀을 제작한 후 건조시켜 1차열처리하고 내부표면과 외부표면을 유약 처리하여 다시 2차열처리하여 옹기사용시 운모와 황토의 효능을 체험할 수 있도록 함과 동시에 옹기에서 훈증 및 원적외선의 발산을 증가시키도록 하는 제조방법에 관한 것이다.More particularly, the present invention relates to a method for producing a mica-containing pottery, and more particularly, to a method for producing pottery using mica powder and ocher powder, Thereby enabling the user to experience the effect of mica and loess upon use of the onggi, and at the same time to increase the emission of fumigant and far-infrared rays from the pot.
일반적으로 옹기의 제조방법으로는 먼저 점토 흙을 반죽해서 응달에 약간 말린 뒤 떡매로 쳐서 벽돌 모양으로 만들고, 바닥에 쳐서 판자 모양의 타래미로 만든 뒤 타래미를 물레 위에 올려놓고 방망이로 다듬는 일을 하여 제작하고, 이를 그늘에 말리고 유약을 발라 가마에 넣고 구워 제작하는 것이다.Generally, Onggi is made by clay clay, dried in the shade a little, dried in the shade and made into a brick shape, and hit the floor to make a plank-like tarayama, then put the tarayaki on the spinning wheel and trim it with a bat It is dried in the shade, glazed, put into a kiln and baked.
이때 물레의 속도, 손놀림에 따라 갖가지 옹기가 만들어지며, 이와 같이 해서 손으로 빚은 항아리를 그늘에 차곡차곡 쌓아 보통 15일 동안 은근하게 말리고, 이 항아리들이 30%정도 말랐을 때 유약을 바르고 음지에서 20여 일 이상 건조시킨 후 다음 가마에 넣고 4일 주야로 1,300℃의 온도를 유지시켜 가면서 불을 때워 옹기를 제조하는 것이다.At this time, various kinds of pottery are made according to the speed of the spinning wheel and the hand movements. In this way, the pots made by hand are piled up in the shade and dried for 15 days in the dark. When these pots are dried by 30%, they are glazed, After drying, it is put into the next kiln and the temperature is maintained at 1,300 ° C for four days and nights, and fire is made to produce a pot.
그리고, 이러한 옹기의 사용처는 일반생활에서 사용되는 것으로, 주로 조미료와 주식과 부식물의 저장용구, 주류 발효 도구, 음료수 저장 용구 등으로 거의 사용되고 있으나, 최근에는 옹기를 이용하여 훈증을 이용한 좌욕기에도 그 사용범위가 넓어지고 있는 실정이다.The use of this Onggi is generally used in general life. It is mainly used for seasoning, stock and storage of corrosive materials, alcoholic fermentation tools, beverage storage equipment, etc. Recently, however, The range is becoming wider.
이러한 옹기의 사용처 중 좌욕기는 훈증을 이용하여 하부에 약탕기가 들어갈 수 있는 공간을 마련하고 상부에는 사람이 앉을 수 있도록 하여 훈증을 이용하여 좌욕할 수 있도록 하는 것이나, 최근에는 훈증을 이용한 좌욕기를 일반좌욕과 물이나 광천에 몸을 배꼽까지 잠그고 좌욕하는 반신욕좌욕을 주로 사용하고 있으나, 이러한 반신욕좌욕기의 옹기는 그 재료가 황토 등이 주성분으로 되어 있어 반신욕에는 황토의 성분특성상 물에 풀어지게 되므로 견고하지 못하는 이유로 옹기의 재질로 구성된 반신욕좌욕기는 주로 사용되지 않고 합성수지 등의 프라스틱류로 성형하여 사용하고 있었다.Among the uses of Onggi, there is a space where a bathtub can be inserted into the lower part by using fumigation, and a person can sit on the upper part so as to be able to take a bath with fumigation. In recent years, And water and mineral springs. However, the Onggi of this semi-conscious bathing machine is mainly composed of loess, etc., and because of the nature of the loess, For the reason, the semi-bathing bath consisting of Onggi's materials was mainly used and molded into plastic such as synthetic resin.
따라서, 이러한 프라스틱의 재질로 사용한 반신욕 좌욕기에는 몸에 유익한 황토 등의 성분을 찾기 어려워 훈증을 이용한 좌욕에 크게 이롭지 못하는 효과로 사용횟수가 낮아지게 되므로 황토 등을 주성분으로 하는 옹기를 이용하여 황토의 특성상 물에 풀리지 않도록 하여 황토의 음이온발생의 효능과 훈증을 이용한 좌욕기의 효능을 발휘할 수 있는 옹기를 제조하는 것을 선호하게 되었다.Therefore, it is difficult to find ingredients such as yellow loess which is useful for the body in the half-bath bath which is made of such a plastic material, and the number of times of use is lowered due to the effect of not being very beneficial to the left-side bath using fumigation. Therefore, by using Onggi, It has been preferred to produce Onggi which can exhibit the efficacy of the generation of negative ions of loess and the efficacy of using a fumigating so as not to be dissolved in water.
따라서, 이러한 통상의 옹기 제작용 원료인 고령토, 점토, 황토 또는 규조토중에서 선택한 것을 주재료로 하여 성형, 제작한 것으로, 상기 주재료의 재질 특성상 물에 풀리는 현상으로 인해 물에 잠수시켜 반신욕하는 좌욕기에는 오랜 사용시 적합하지 못하는 실정이었다.Therefore, it is molded and manufactured with the main ingredient selected from kaolin, clay, loess, or diatomaceous earth which is the raw material for making such ordinary pottery. Due to the material property of the main material, the water is submerged in water, It was not appropriate.
본 발명은 상술한 종래의 문제점을 해결하기 위한 것으로서, 위와 같이 일반적으로 사용되는 옹기에 음이온 발생을 증가시킬 수 있도록 기존에 사용되고 있던 음이온 발생시키기 위한 옹기 원료인 황토와 결합하여 황토의 음이온 발생을 한층 더 발생을 증대시키고 아토피와 향균, 탈취 등의 효능이 높은 운모를 혼합하여 황토의 특성상 수분에 손상되는 문제점을 해결함과 동시에 황토와 운모를 결합하여 견고성을 증대시켜 물속에서도 사용하는 반신욕 좌욕기에도 사용이 가능하게 함과 동시에 일반생활에서 사용되는 조미료와 주식과 부식물의 저장용구, 주류 발효 도구, 음료수 저장 용구 등을 형성하여 옹기 사용시 음이온의 체험을 증가시킬 수 있는 것이다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide an onion- It improves the growth and solves the problem of damaging to moisture due to the nature of loess by mixing mica with high efficacy such as atopy, antibacterial and deodorization. It also increases firmness by combining loess and mica and is also used for half bath bath It is possible to increase the experience of negative ions when using pottery by forming condiments used in ordinary living, storing stocks and corrosive materials, liquor fermenting tools, beverage storage devices, and the like.
황토를 지하 1m 이하에서 채광시 10℃ 이하에서 채광하여 20 ~ 30일 대기온도에서 1차숙성공정과; 상기 1차숙성공정을 거친 황토와 운모를 혼합하여 50 ~ 100메쉬의 분말로 가공하는 가공공정과; 상기 가공공정을 거친 황토와 운모분혼합을 23℃에서 15일간 숙성하는 2차숙성공정과; 상기 2차숙성공정을 거친 황토분말 65중량부와 운모분말 30중량부를 물 15중량부와 혼합하여 반죽물을 생성하는 반죽공정과; 상기 반죽공정을 거친 반죽물을 옹기의 성형틀을 형성하는 1차성형공정과; 상기 성형공정을 거친 성형틀을 그늘에서 2일간 건조시키는 건조공정과; 상기 건조공정을 거친 성형틀을 완전한 옹기의 모형으로 성형하는 2차성형공정과; 상기 2차성형공정을 거친 성형틀을 그늘에서 30일간 건조시켜 성형틀의 내부 수분을 700ppm 이하로 낮추는 2차건조공정과; 상기 2차건조공정을 거친 성형틀의 표면에 유약을 도포하는 유약공정과; 상기 유약공정을 거친 성형틀을 가마에 투입하여 24시간동안 100℃에서 가열하여 수분을 제거하는 1차가열공정과; 상기 1차가열공정을 거친 성형틀을 48시간동안 400℃ 이하에서 가열하는 2차가열공정과; 상기 2차가열공정을 거친 성형틀을 24시간동안 900℃ 에서 가열하는 3차가열공정과; 상기 3차가열공정을 거친 성형틀을 48시간동안 1100℃ 에서 가열하는 4차가열공정과; 상기 4차가열공정을 거친 가마에서 불을 끄고 성형틀을 96시간동안 대기중에 식히는 식힘공정을 거쳐 완성하는 것이다.The first stage is the first aging process at 20 ~ 30 days at min. A processing step of mixing yellow loess and mica that have undergone the primary aging step and processing the resultant into a powder of 50 to 100 mesh; A second aging step of aging the mixture of the yellow loess and the mica having undergone the above-mentioned processing step at 23 DEG C for 15 days; A kneading step of mixing 65 parts by weight of the loess powder and 30 parts by weight of the mica powder which have undergone the second aging step with 15 parts by weight of water to produce a kneaded product; A primary molding step of forming kneading molds by kneading the kneaded product; A drying step of drying the molding frame having undergone the molding step in a shade for 2 days; A secondary molding step of molding the molding frame having undergone the drying step into a complete mold of a pottery; A secondary drying step of drying the molding frame having undergone the secondary molding process for 30 days in a shade to reduce the internal moisture of the molding frame to 700 ppm or less; A glaze step of applying a glaze to the surface of a molding die having undergone the secondary drying step; A first heating step of putting a molding frame having passed through the glaze step into a kiln and heating it at 100 DEG C for 24 hours to remove moisture; A secondary heating step of heating the molding frame having undergone the primary heating process at 400 DEG C or lower for 48 hours; A third heating step of heating the forming mold after the second heating step at 900 DEG C for 24 hours; A fourth heating step of heating the forming mold after the third heating step at 1100 캜 for 48 hours; And the mold is closed in the atmosphere for 96 hours by turning off the fire in the kiln after the fourth heating process.
따라서, 본 발명은 상기한 바와 같이 옹기에 음이온과 원적외선 발생을 증가시킬 수 있도록 기존에 사용되고 있던 음이온 발생시키기 위한 옹기 원료인 황토와 결합하여 황토의 효능인 인체에 흡수되면 신진대사를 촉진시켜 노화를 방지하고 원적외선이 세포의 생리작용을 활성화하여 피부의 자정활동을 향상시킴으로써 여드름, 주근깨 등등 피부 트러블에 많은 효과를 발휘하고 음이온을 방출하여 산성화된 피부를 알카리성으로 바꾸고 혈액순환을 촉진시키며 노화의 원인인 활성산소, 피부의 노폐물 제거, 정화작용, 향균작용에 탁월한 효과를 주며 과산화 지질을 환원 시키고 분해하며 체내 유해물질을 분해하며 피부를 윤택하고 탄력있게 변화시키는 효 능과 원적외선 방사율이 높으며 열을 받으면 방사되는 발암물질도 제거시키는 운모를 혼합하여 옹기 성형시 수분에 강하게 하여 반신욕 좌욕기에도 사용을 가능하게 하는 이점이 있는 것이다.Accordingly, the present invention relates to a method for enhancing the generation of anion and far-infrared rays in Onggi as described above, which is combined with yellow clay, which is a raw material for generating negative ions, By activating the physiological action of the cells, the far-infrared rays enhance the skin's self-cleaning activity, thereby exerting a lot of effects on skin troubles such as acne and freckles, releasing negative ions, converting acidified skin into alkaline, promoting blood circulation, It has excellent effect on active oxygen, elimination of waste of skin, purification effect, antibacterial effect, reducing and decomposing lipid peroxidation, decomposing harmful substances in the body, changing skin elasticity and elasticity, and emitting far infrared rays. Mica that removes the carcinogens It will have advantages at the time of strongly water-molding pottery, which enables the use of even half-bath jwayokgi.
본 발명의 또 다른 효과로는 일반생활에서 사용되는 조미료와 주식과 부식물의 저장용구, 주류 발효 도구, 음료수 저장 용구 등을 형성하여 옹기 사용시 음이온과 원적외선의 체험을 증가시킬 수 있는 것이다.Another effect of the present invention is to increase the experience of anions and far-infrared rays when using pottery by forming condiments used in general life, stocks of stocks, storage of corrosive materials, liquor fermentation tools, and beverage storage devices.
본 발명의 운모가 함유된 옹기의 제조방법을 설명하기 전에 먼저 본 발명에 사용되는 원석에서 발생하는 원적외선은 체내 깊숙히 침투하여 세포고유의 파장과 공진 공명하고, 인체의 지방질, 단백질, 탄수화물의 영양소를 분해하여 영양균형을 유지시키고, 세포의 분자와 원자를 진동시켜 신체의 신진대사를 촉진시키고, 특히, 인체에 다양한 치료효과 등을 제공하는 것으로 여러 연구문서에서 증명하고 있는바, 상기 원적외선이 많이 발생될수록 바람직한 것이다.Before describing the production method of the mango containing mica of the present invention, the far infrared ray generated from the raw stones used in the present invention penetrates deeply into the body, resonates with the intrinsic wavelength of the cell and resonates with the nutrients of the human body fat, protein and carbohydrate It has been proved in several research documents that it is necessary to decompose to maintain nutritional balance and to vibrate the molecules and atoms of the cells to promote the metabolism of the body and in particular to provide various therapeutic effects to the human body. The more desirable it becomes.
그리고, 본 발명의 옹기에 함유하여 원적외선을 발산가능케 하는 운모에 대해 먼저 설명하자면, 화강암 가운데 많이 들어 있는 규산염 광물의 하나로 단사 정계에 속하는 결정으로, 흔히 육각의 판(板) 모양을 띠며 얇은 조각으로 잘 갈라지는 성질이 있으며, 운모의 종류에는 백운모, 흑운모, 견운모, 금운모로 나누어져 있는 것이다.The mica which is contained in the Onggi of the present invention and capable of emitting far-infrared rays will be described first. It is one of the silicate minerals contained in granite, and belongs to monoclinic system. It is a hexagonal plate, There is a good cracking nature, and the kinds of mica are divided into muscovite, biotite, sericite, and gold mica.
상기 백운모는 운모와 같은 결정구조를 가지는 단사정계에 속하는 광물로 철과 마그네슘을 소량 함유하기도 하고 굳기는 2 ~ 2.4, 비중은 2.7 ~ 3, 무색, 백색, 황색, 회색, 녹색, 갈색을 띠며 크롬 함유시, 선록색을 띠며 내화성이 강하고 전기 부도체라서 전기 절연체로 사용되며, 철이나 마그네슘을 소량 함유한 것도 있으며, 판상, 편상, 인상 결정을 이루어, 흔히 육각형의 외곽을 나타내며, 밑면에 완전한 쪼개짐이 있고, 벽개조각은 탄력성이 높으며, 굳기 2 ~ 2.5, 비중 2.7 ~ 3이고 무색 또는 백색으로 투명한데, 때로는 황색, 회색, 녹색, 갈색 등을 띠며, 내화성이 강하며, 전기 부도체이어서 전기 절연체로서 사용되며 분포는 매우 넓어서, 화산암을 제외한 각종 암석 중에서 산출되며, 다른 광물의 분해로 인하여 생성되기도 하며 캐나다, 인도, 러시아 연방 등지에서는 질이 좋은 것이 산출된다The muscovite is a monoclinic mineral having a crystal structure such as mica. It contains a small amount of iron and magnesium and has a hardness of 2 to 2.4, a specific gravity of 2.7 to 3, a colorless, white, yellow, gray, green, It is used for electrical insulators because it is light green and has excellent fire resistance. It contains iron or magnesium in small amount. It is made of plate, flake, and impression crystals. It shows a hexagonal outline. The cleavage pieces are highly elastic and have a hardness of 2 to 2.5 and a specific gravity of 2.7 to 3. They are colorless or white and transparent and sometimes yellow, gray, green and brown. They are resistant to fire and are used as electric insulators It is produced in various rocks except volcanic rocks. It is produced by decomposition of other minerals. It is produced in Canada, India, Russian Federation In the back, good quality is calculated
상기 흑운모는 운모와 같은 결정구조를 가지는 단사정계에 속하는 광물로 색깔은 흑색, 갈흑색, 녹흑색을 띠고, 화성암, 변성암에서 산출되며 퇴적암에도 드물지 않게 산출되고 판상 또는 인상을 이루며 흔히 육각형 또는 능면체를 나타내고 밑면에 쪼개짐이 완전하고 박편은 탄성을 가지는데 금운모에 비하여 작고, 흑색, 갈흑색, 녹흑색 등을 띠며, 쪼개짐면은 진주광택이 있고, 때로는 금속광택을 가지며, 굳기 2.5 ~ 3.0, 비중 2.7 ~ 3.1이며 분포는 매우 넓고 많은 화성암, 변성암에서 산출되며, 퇴적암에도 드물지 않으며, 임의적으로 마그네슘과 철의 비가 2 : 1 이하인 것으로 정의하며, 흑운모는 황토와 맥반석 보다 약3배이상 원적외선 방사율(94%)이 높으며 게르마늄 함유량이 36ppm에 이르는 생명의 돌로서 특히 중국산 천연옥과 시멘트가 열을 받으면 방사되는 발암물질도 제거시키는 기적의 돌이며 옛부터 흑운모석을 약돌이라 부릅니다.The biotite is a monoclinic mineral having a crystal structure such as mica. The color of the biotite is black, dark black, and rust black. It is produced in igneous and metamorphic rocks. It is rare in sedimentary rocks. , And the flakes are completely resilient and have elasticity. They are smaller in size than gold mica and have black, dark brown, and greenish black color. The cleaved surface has pearly luster, sometimes metallic luster, hardness of 2.5-3.0, It has a specific gravity of 2.7 ~ 3.1 and its distribution is very broad and is calculated from many igneous and metamorphic rocks. It is not uncommon in sedimentary rocks. It is arbitrarily defined as the ratio of magnesium to iron is less than 2: 1. The biotite is more than 3 times far infrared ray emissivity 94%) and germanium content is 36ppm. It is a stone of life. Especially, It is a miracle stone that removes the carcinogenic material that is lost.
상기 견운모는 질이 치밀하거나 미세한 비늘 모양 백운모의 총칭으로 세리사이트라고도 하며 비단이라는 뜻의 그리스어에서 연유하고 단사정계에 속하며, 백색 또는 회백색에 진주광택이 있으며, 원래는 결정편암, 특히 견운모편암의 주성분 광물을 말하였으나, 오늘날에는 열수작용으로 생긴 점토 모양의 미세한 백운모를 가리킨다. 화학성분은 백운모와 거의 같으나, 일반적으로 칼륨 K는 백운모보다 적고 수분 H2O가 다소 많으며, 장석, 근청석, 홍주석 등의 2차적 변질물로서 생성되고, 가벼운 동력변성작용을 받은 천매암질 점판암 또는 천매암의 가장 흔한 구성광물이며, 도석은 화산암의 변질로 인해 생기는데, 석영(70 %)과 견운모(30 %)로 이루어지며 견운모는 옹기나 내화벽돌의 혼입재로 쓰이며, 그 밖에 도료, 전기절연체, 활마재, 화장품용 등 용도가 다양하다.The sericite is a generic term of fine or fine scaly muscovite. It is also called sericite. It belongs to the monoclinic system which is derived from Greek meaning silk. It has a white or grayish white pearl luster. It is originally a main component of crystalline schist, Minerals, but today refers to microscopic muscovite in the form of clay formed by hydrothermal action. The chemical composition is almost the same as that of muscovite, but potassium K is generally less than muscovite and has a slightly higher H2O content. It is produced as a secondary alteration of feldspar, cordierite, and red sandstone and has a light kinetic metamorphism. It is composed of quartz (70%) and sericite (30%). The sericite is used as a mixture of pottery and refractory bricks, and other materials such as paints, electrical insulators, , And cosmetics.
상기 금운모는 흑운모에 가까운 것으로 단사정계에 속하는 운모이며 굳기는 2.5 ~ 3, 비중은 2.78 ~ 2.85이며 내화재와 전기 절연체로 사용되며 플루오르가 많고 철은 거의 없으며 판상결정 이지만 때로는 주상결정을 이루며, 밑면에 완전한 쪼개짐이 있고, 탄성이 강하고 갈색, 황갈색, 적갈색 등을 띠고, 밑면은 진주광택 또는 아금속 광택이 나며, 때로는 구리 비슷한 반사를 보이며 또 금홍석을 함유하는 일이 있어서, 비추어 보면 별 모양의 6사광채를 내며, 내화재, 전기 절연체로 사용되며, 석회암 또는 고회암과 화성암과의 접촉부에 투휘석, 회철휘석, 투각섬석 등과 함께 산출되며 캐나다, 미국, 핀란드, 노르웨이 등에서는 대량으로 산출되고 한국에서는 함북, 황해 등에서 산출된다.The gold mica is close to biotite and is a monoclinic mica. It has a hardness of 2.5 to 3 and a specific gravity of 2.78 to 2.85. It is used as an electrical insulator with refractory material. It has a large amount of fluorine and almost no iron. It is a plate-like crystal but occasionally a columnar crystal. It has a complete cleavage, is highly elastic and has brownish, yellowish brown, reddish brown color, and the bottom has pearly luster or metallic luster. Sometimes it shows copper-like reflection and also contains rutile. It is used as refractory material and electric insulator. It is produced in conjunction with limestone or high hysteresis and igneous rock in conjunction with tourmaline, gray iron, and hornblende. It is produced in large quantities in Canada, USA, Finland, , And Yellow Sea.
상기와 같은 목적을 달성하기 위한 본 발명에 따른 운모가 함유된 옹기 제조방법으로는In order to accomplish the above object, the present invention provides a method for producing mica-containing Onggi
황토를 지하 1m 이하에서 채광시 10℃ 이하에서 채광하여 20 ~ 30일 대기온도에서 1차숙성공정과;The first stage is the first aging process at 20 ~ 30 days at min.
상기 1차숙성공정을 거친 황토와 운모를 혼합하여 50 ~ 100메쉬의 분말로 가공하는 가공공정과;A processing step of mixing yellow loess and mica that have undergone the primary aging step and processing the resultant into a powder of 50 to 100 mesh;
상기 가공공정을 거친 황토와 운모분혼합을 23℃에서 15일간 숙성하는 2차숙성공정과;A second aging step of aging the mixture of the yellow loess and the mica having undergone the above-mentioned processing step at 23 DEG C for 15 days;
상기 2차숙성공정을 거친 황토분말 65중량부와 운모분말 30중량부를 물 15중량부와 혼합하여 반죽물을 생성하는 반죽공정과;A kneading step of mixing 65 parts by weight of the loess powder and 30 parts by weight of the mica powder which have undergone the second aging step with 15 parts by weight of water to produce a kneaded product;
상기 반죽공정을 거친 반죽물을 옹기의 성형틀을 형성하는 1차성형공정과;A primary molding step of forming kneading molds by kneading the kneaded product;
상기 성형공정을 거친 성형틀을 그늘에서 2일간 건조시키는 건조공정과;A drying step of drying the molding frame having undergone the molding step in a shade for 2 days;
상기 건조공정을 거친 성형틀을 완전한 옹기의 모형으로 성형하는 2차성형공정과;A secondary molding step of molding the molding frame having undergone the drying step into a complete mold of a pottery;
상기 2차성형공정을 거친 성형틀을 그늘에서 30일간 건조시켜 성형틀의 내부 수분을 700ppm 이하로 낮추는 2차건조공정과;A secondary drying step of drying the molding frame having undergone the secondary molding process for 30 days in a shade to reduce the internal moisture of the molding frame to 700 ppm or less;
상기 2차건조공정을 거친 성형틀의 표면에 유약을 도포하는 유약공정과;A glaze step of applying a glaze to the surface of a molding die having undergone the secondary drying step;
상기 유약공정을 거친 성형틀을 가마에 투입하여 24시간동안 100℃에서 가열하여 수분을 제거하는 1차가열공정과;A first heating step of putting a molding frame having passed through the glaze step into a kiln and heating it at 100 DEG C for 24 hours to remove moisture;
상기 1차가열공정을 거친 성형틀을 48시간동안 400℃ 이하에서 가열하는 2차가열공정과;A secondary heating step of heating the molding frame having undergone the primary heating process at 400 DEG C or lower for 48 hours;
상기 2차가열공정을 거친 성형틀을 24시간동안 900℃ 에서 가열하는 3차가열공정과;A third heating step of heating the forming mold after the second heating step at 900 DEG C for 24 hours;
상기 3차가열공정을 거친 성형틀을 48시간동안 1100℃ 에서 가열하는 4차가열공정과;A fourth heating step of heating the forming mold after the third heating step at 1100 캜 for 48 hours;
상기 4차가열공정을 거친 가마에서 불을 끄고 성형틀을 96시간동안 대기중에 식히는 식힘공정을 거쳐 완성하는 것이다.And the mold is closed in the atmosphere for 96 hours by turning off the fire in the kiln after the fourth heating process.
상기 2차숙성공정을 거친 황토분말 65중량부와 운모분말 30중량부를 물 15중량부와 혼합하여 반죽물을 생성하는 반죽공정에서 상기 운모분말 30중량부의 바람직한 실시예로는 백운모, 흑운모, 견운모, 금운모분말을 각각 30중량부로 사용하거나 상기 백운모, 흑운모, 견운모, 금운모분말을 혼합하여 30중량부로 사용하는 것이 바람직하다.In a kneading process in which 65 weight parts of the loess powder and 30 weight parts of the mica powder that have undergone the second aging step are mixed with 15 weight parts of water to produce a kneaded product, preferred examples of the mica powder include 30 weight parts of muscovite, And 30 parts by weight of the gold mica powder or 30 parts by weight of the mixture of muscovite, biotite, sericite and gold mica powder are preferably used.
상기와 같이 본 발명의 목적을 달성하기 위한 운모를 함유한 옹기 제조방법으로는 황토를 채광하여 20 ~ 30일 대기온도에서 숙성시켜 운모와 5 : 5의 비율로 혼합하여 50 ~ 100메쉬의 분말로 가공하여 황토분말와 운모분말을 형성하여 23℃에서 15일간 한번더 숙성시킨 후 황토분말과 운모분말을 물과 함께 혼합하여 반죽물을 생성시켜 통상의 믹서기에 투입하여 압출하여 가느다란 형태로 압출하여 상기 가느다란 형태의 반죽물을 물래의 상부에 옹기 형태로 반죽하고 물래작업으로 인하여 완전한 옹기 외형을 완성하고 그늘에서 2일간 건조시킨 후 홈이나 구멍을 형성하여 완전한 옹기의 모형으로 성형하여 다시 그늘에서 30일간 건조시켜 성형틀의 내부 수분을 700ppm 이하로 낮추고 난 후 표면에 옹기의 외부에 액체나 기체가 스며들지 못하게 하며 겉면에 광택이 나게 하는 유약을 도포하고 가마에 투입하여 24시간동안 100℃에서 가열하여 상기 옹기의 내부에 수분을 제거한 후 48시간동안 400℃ 이하에서 서서히 열을 올려 가열하여 상기 옹기가 가열하면서 옹기의 터짐을 방지하도록 하고 다시 24시간동안 900℃ 에서 가열하고 다시 48시간동안 1100℃로 가열하여 완전하게 가열공정을 거친 가마에서 불을 끄고 96시간동안 대기중에 식혀 옹기를 완성하는 것이다.As described above, in order to achieve the object of the present invention, the method of producing mica containing inorganics includes mining yellow loess and aging at an atmospheric temperature for 20 to 30 days, mixing the mica at a ratio of 5: 5, The mixture was mixed with water to produce a kneaded product. The kneaded product was added to a conventional blender to be extruded and extruded into a slender form to prepare a kneaded product. The kneading of the slender form is kneaded on the top of the woven fabric in the form of pottery, and the complete outline of the pottery is completed due to the sewing work. After drying for 2 days in the shade, a groove or hole is formed and molded into a complete pottery model. After drying for a day, the internal moisture of the molding frame is lowered to 700ppm or less, so that the liquid or gas does not permeate the surface of the pot, and the surface The glaze was applied to the kiln and heated at 100 ° C. for 24 hours to remove moisture from the inside of the pot. The pot was heated at 400 ° C. or lower for 48 hours to heat the pot. And then heated again at 900 ° C for 24 hours and then heated to 1100 ° C for another 48 hours to turn off the fire in a completely heated kiln and to cool in air for 96 hours to complete the pot.
상기와 같은 제조방법을 통해 제조되는 옹기의 반죽물 형성시 황토분말과 운모분말을 혼합하여 옹기의 주재료로 형성하는 것으로, 황토분말과 혼합하는 운모분말의 특성상 음이온이 발생하도록 함과 동시에 운모분말과 혼합하여 물에 잘 풀어지지 않도록 하는 것이다.When forming the kneaded product of the Onggi produced through the above-described manufacturing method, the ocher powder and the mica powder are mixed to form the main ingredient of the Onggi, so that the mica powder mixed with the ocher powder causes the anion to be generated, So as not to be dissolved in water.
Claims (1)