KR101143639B1 - Sealing method of aluminum by using soybean substance - Google Patents
Sealing method of aluminum by using soybean substance Download PDFInfo
- Publication number
- KR101143639B1 KR101143639B1 KR1020090083579A KR20090083579A KR101143639B1 KR 101143639 B1 KR101143639 B1 KR 101143639B1 KR 1020090083579 A KR1020090083579 A KR 1020090083579A KR 20090083579 A KR20090083579 A KR 20090083579A KR 101143639 B1 KR101143639 B1 KR 101143639B1
- Authority
- KR
- South Korea
- Prior art keywords
- aluminum
- sealing
- soybean
- extract
- water
- Prior art date
Abstract
본 발명은 콩의 추출물을 이용하여 봉공처리하므로, 인체에 무해한 친환경 알루미늄 제품을 생산할 수 있도록 한 콩을 이용한 알루미늄 양극산화 봉공 처리방법에 관한 것이다.The present invention relates to a method for processing aluminum anodized sealing using soybean so that it can be sealed using the extract of soybean, so that it can produce environmentally friendly aluminum products harmless to the human body.
이를 위해, 알루미늄 제품의 표면을 양극 산화처리한 후, 착색 과정을 거쳐 봉공처리하는 방법에 있어서, 착색된 알루미늄 또는 알루미늄합금을 콩 추출물을 유효성분으로 하는 건욕액에 침적하여 봉공처리하는 것을 특징으로 한다.To this end, in the method of anodizing the surface of the aluminum product, and then sealing through a coloring process, the colored aluminum or aluminum alloy is sealed by dipping in a dry bath containing soybean extract as an active ingredient. do.
상기한 구성에 따라, 산화피막과 착색공정을 거친 알루미늄 제품을 콩의 추출물을 유효성분으로 한 건욕액에 침적하여 봉공처리함으로써, 봉공처리된 알루미늄 제품의 내구성, 내식성 및 내광성을 확보할 수 있고, 인체에 무해한 친환경 알루미늄 제품의 생산이 가능한 효과도 있다.According to the above configuration, by sealing the aluminum product subjected to the anodizing and coloring process in a dry bath containing the extract of soybean as an active ingredient, it can ensure the durability, corrosion resistance and light resistance of the sealed aluminum product, It is also possible to produce eco-friendly aluminum products that are harmless to humans.
콩, 알루미늄, 피막, 착색, 봉공.Beans, aluminum, film, tinted, sealed.
Description
본 발명은 봉공 처리방법에 관한 것으로, 더욱 상세하게는 피막 및 착색된 알루미늄 제품 표면에 콩의 추출물을 이용하여 봉공처리하므로, 인체에 무해한 친환경 알루미늄 제품을 생산할 수 있도록 한 콩을 이용한 알루미늄 양극산화 봉공 처리방법에 관한 것이다.The present invention relates to a sealing method, more specifically, the sealing process using an extract of soybean on the surface of the coating and the colored aluminum product, aluminum anodized sealing using soybeans to produce environmentally friendly aluminum products harmless to the human body It relates to a treatment method.
일반적으로, 알루미늄을 양극으로 하여 일정한 전해액에서 적정조건으로 분극을 시킬 경우, 자연피막보다 두꺼운 양극 산화피막이 생성되는데, 이를 양극산화 피막처리라 한다.In general, when aluminum is used as the anode and polarized under appropriate conditions in a constant electrolyte solution, an anodized film thicker than a natural film is produced, which is called anodizing.
이와 같은, 알루미늄 표면처리 과정에서 어느 공정도 소홀히 할 수 없으나, 특히 산화피막 형성공정에서 부주의나 편차가 생기면 제품에 직접적인 영향을 받을 뿐만 아니라, 그 다음 공정인 착색공정이나 봉공처리에도 큰 영향을 주게 되므로, 이 산화피막 형성공정은 대단히 중요한 공정에 해당된다.In this case, any process cannot be neglected in the aluminum surface treatment process, but if carelessness or deviation occurs in the oxide film forming process, it is not only directly affected by the product, but also greatly influences the subsequent coloration process or sealing process. Therefore, this oxide film forming process is a very important process.
한편, 알루미늄 표면에 산화피막을 형성하는 양극산화처리방법에는 여러 가지 방법이 있는데, 주로 사용되는 방법은 방식성이 우수하고 치밀한 산화피막을 얻 을 수 있는 수산법, 황산법, 크롬산법 등을 들 수 있다.On the other hand, there are various methods of anodizing to form an oxide film on the surface of aluminum, and the most commonly used methods are the fishery method, sulfuric acid method, and chromic acid method, which are excellent in corrosion resistance and obtain a dense oxide film. have.
여기서, 수산법은 산화피막을 형성하고자 하는 알루미늄 제품을 H2C2O4 수산용액에 넣고, 직류, 교류 또는 직류에 교류를 동시에 보내면서 산화피막을 형성하는 방법으로, 전류 효율이 좋고 통전량에 비례하여 산화피막의 두께가 증가하게 된다.Here, the fishery method is to put an aluminum product to form an oxide film in H 2 C 2 O 4 oxalic acid solution, and to form an oxide film while sending alternating current to direct current, alternating current or direct current at the same time. In proportion to the thickness of the oxide film is increased.
그리고, 황산법은 알루미늄 제품을 황산액에 넣고 교류를 보내면서 산화피막을 형성하는 것으로, 황산의 농도가 낮을수록 피막이 단단하게 형성되며, 가격이 싸므로 널리 이용되고 있다.In addition, the sulfuric acid method forms an oxide film by sending aluminum product into a sulfuric acid solution and sending alternating current. As the sulfuric acid concentration is lower, the film is harder and the film is cheap.
또한, 크롬산법은 산화크롬수용액에 알루미늄 제품을 넣고 교류를 보내면서 산화피막을 형성하는 것으로, 내마모성은 작으나 내식성이 대단히 크다.In addition, the chromic acid method is to form an oxide film while the aluminum product is put in the chromium oxide aqueous solution to send alternating current, abrasion resistance is small but corrosion resistance is very large.
상기한 방법들로 알루미늄의 표면에 양극산화처리를 실시하여 산화피막을 형성하는 과정에서 시간의 변화를 주면 색조를 조절할 수 있게 되지만, 시간의 조절을 통해 얻어지는 산화피막의 색조는 엷은 색조에서 짙은 색조로, 예를 들면 엷은 브론즈색에서 흑색으로 변화하는 단일계통의 색상만이 얻어지는 단점이 있다.Although the color tone can be adjusted by changing the time in the process of forming an oxide film by performing anodization on the surface of aluminum by the above-described methods, the color tone of the oxide film obtained by controlling the time is light to dark tones. For example, there is a disadvantage in that only a single system color changing from light bronze to black is obtained.
위의 공정에 따라 형성된 아노다이징은 내광성과 내식성을 목적으로 기공을 막아주는 봉공처리를 해야 하는데, 봉공처리의 방법은 수화봉공처리, 금속염 봉공처리, 유기물 봉공처리, 도장에 의한 봉공처리 등의 방법 등 여러 가지 방법이 적용된다.Anodizing formed according to the above process should be sealed to prevent pores for the purpose of light resistance and corrosion resistance, the method of sealing is a method such as hydration sealing, metal salt sealing, organic sealing, sealing by coating, etc. Several methods apply.
이 중, 수화봉공처리는 양극산화처리에 의해 형성된 AL2O3가 베마이트로 변 화하는 경우 결정수를 포함하는 것에 의해 체적이 팽창해서 미세공이 막히는 것으로, 탕 침적방식과, 증기 봉공방식으로 나뉘어진다.Among these, the hydration sealing treatment is a process in which when the AL 2 O 3 formed by anodizing changes to boehmite, the volume is expanded and the fine pores are clogged by containing crystallized water. Divided.
탕 침적방식은 순수 물이 80℃ 이상이 되어야 하며, PH는 4.0 이상이 적당한데, 근래에는 순수물에 촉진제를 넣기 때문에 온도는 65~70℃ 에서도 잘 이루어진다. 그리고, 촉진제로는 주로 니켈 성분이 사용되는데, 시중에서 판매되는 상품으로는 아루마이드 실과와 H-298이라는 제품들이 있다.In the water immersion method, pure water should be more than 80 ℃, and the pH should be more than 4.0. In recent years, since the accelerator is added to pure water, the temperature is well at 65 ~ 70 ℃. Nickel is mainly used as a promoter, and commercially available products include aramid fruit and H-298.
이러한, 촉진제의 투입량은 실라가 5g/L 정도이고, H-298은 40ml/L 정도가 적당하며, 침적시간은 두 가지 모두 300초 이상이면 피막 15㎛까지는 충분하다.The amount of the accelerator is about 5 g / L in Sila, about 40 ml / L in H-298, and the deposition time is sufficient up to 15 µm if the deposition time is both 300 seconds or more.
그리고, 증기 봉공방식은 양극산화 후 수세하여 3~5㎏/㎤의 수증기에 20분 정도 유치해 봉공하는 방식으로, 이 방법의 장점은 반응이 빠르고, 물의 PH 등의 영향을 받지 않으며, 안정된 막을 얻을 수 있고, 내식성이 우수하며, 착색된 색이 침적방식보다 변색이 적다.In addition, the steam sealing method is an anodized, washed with water to attract 3 to 5 kg / cm 3 of water vapor for 20 minutes to seal, the advantage of this method is that the reaction is fast, and is not affected by the pH of the water, and the stable membrane Obtainable, excellent in corrosion resistance, and less colored in color than the deposition method.
반면, 이 방법의 단점은 설비비용이 많이 들고, 연속작업을 하는 경우 봉공에서 끊어질 수 있으며, 피막이 두꺼우면 크랙이 생길 수 있고, 리벳트 가공한 곳에 잔류한 전해액이 유출해 얼룩이 발생하기 쉬운 문제가 있다.On the other hand, the disadvantage of this method is that the cost of equipment is high, and continuous work may cause breakage in sealing, and if the film is thick, cracks may occur, and electrolytes remaining in the riveted areas may leak out and cause stains. There is.
따라서, 봉공처리 방법으로 주로 사용되는 방식은 열탕에 촉진제를 넣어 침적하는 방식이며, 이같은 탕 침적방식이 모든 면에서 부작용이 적다.Therefore, the method mainly used as the sealing method is a method of depositing the accelerator in the boiling water, this type of bath deposition method has less side effects in all respects.
그러나, 상기한 탕 침적방식에 촉진제로 사용되는 니켈 및 그 화합물은 인체에 치명적인 금속이기 때문에 작업자의 건강을 심각하게 해칠 수 있는 문제가 있고, 이로 인해 상기한 니켈 및 그 화합물을 유해물질로 규정하는 논의가 활발히 진 행되고 있는 실정에 있다.However, since the nickel and the compound used as an accelerator in the above-described hot water deposition method are fatal metals to the human body, there is a problem that may seriously damage the health of the worker, and thus, the nickel and the compound are defined as hazardous substances. There is a lot of discussion going on.
즉, 동물 실험결과등을 통해서 니켈 화합물은 사람의 코와 폐에 암을 유발한다는 확실한 증거가 있어 인체 발암성 물질로 분류되고 있고, 또한 니켈 화합물에 의한 급성 반응으로 점막자극, 접촉성 피부염, 알러지성 피부염이 발생할 수 있으며, 또 니켈 화합물에 노출되면 천식이 일어날 수 있는 것이다.In other words, the animal test results show that the nickel compound is classified as a human carcinogen because there is certain evidence that it causes cancer in human nose and lungs. Also, acute reaction by nickel compound causes mucosal irritation, contact dermatitis and allergy. Sexual dermatitis can occur, and asthma can occur when exposed to nickel compounds.
본 발명은 전술한 바와 같은 종래의 문제점을 해결하기 위하여 안출한 것으로, 피막 및 착색된 알루미늄 제품 표면에 콩의 추출물을 이용하여 봉공처리하므로, 인체에 무해한 친환경 알루미늄 제품을 생산할 수 있도록 한 콩을 이용한 알루미늄 양극산화 봉공 처리방법을 제공하는 데 있다.The present invention has been made in order to solve the conventional problems as described above, because the sealing process using the extract of the bean on the surface of the coating and the colored aluminum product, using a soybean to produce an environmentally friendly aluminum product harmless to the human body It is to provide a method for processing aluminum anodized sealing.
상기와 같은 목적을 달성하기 위한 본 발명의 구성은, 알루미늄 제품의 표면을 양극 산화처리한 후, 착색 과정을 거쳐 봉공처리하는 방법에 있어서, 착색된 알루미늄 또는 알루미늄합금을 콩 추출물을 유효성분으로 하는 건욕액에 침적하여 봉공처리하는 것을 특징으로 한다.The composition of the present invention for achieving the above object, in the method of sealing the surface of the aluminum product after anodizing, and then subjected to a coloring process, the colored aluminum or aluminum alloy soybean extract as an active ingredient It is characterized in that the sealing treatment by immersion in the dry bath.
상기한 과제 해결수단을 통해 본 발명은, 산화피막과 착색공정을 거친 알루미늄 제품을 콩의 추출물을 유효성분으로 한 건욕액에 침적하여 봉공처리함으로써, 봉공처리된 알루미늄 제품의 내구성, 내식성 및 내광성을 확보할 수 있고, 인체에 무해한 친환경 알루미늄 제품의 생산이 가능하여 유아용기구 및 내외장 건축자재, 주방기기, 가전제품, 그리고 피부 접촉이 많은 휴대폰 케이스 등에 다양하게 적용 가능한 효과가 있다.The present invention through the above-mentioned means for solving the problem, by immersing the aluminum product subjected to the anodizing and coloring process in a dry bath containing the extract of the soybean as an active ingredient, sealing, thereby durability, corrosion resistance and light resistance of the sealed aluminum product It can be secured, and it is possible to produce eco-friendly aluminum products that are harmless to the human body, so that it can be applied to various applications such as baby appliances, interior and exterior construction materials, kitchen appliances, home appliances, and cell phone cases with high skin contact.
본 발명의 바람직한 실시예를 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.When described in detail with reference to the accompanying drawings a preferred embodiment of the present invention.
도 1은 본 발명에 의한 봉공처리 이전에 피막 형성된 알루미늄 표면에 착색이 이루어진 형태의 개략적으로 나타낸 단면도이고, 도 2는 도 1을 통해 착색된 알루미늄 표면에 콩을 이용하여 봉공처리된 형태를 개략적으로 나타낸 단면도이다.1 is a cross-sectional view schematically showing a form in which the color is formed on the coated aluminum surface before the sealing process according to the present invention, Figure 2 is a schematic view of the form sealed using a bean on the colored aluminum surface through Figure 1 It is sectional drawing shown.
본 발명의 콩을 이용한 알루미늄 양극산화 봉공 처리방법은, 알루미늄 또는 알루미늄합금을 양극 산화처리하여 다공질형 산화 피막층을 형성하는 단계와, 상기 다공질형 산화 피막층이 형성된 알루미늄 또는 알루미늄합금을 천연염료에 착색하여 염색 및 착색처리하는 단계와, 착색된 알루미늄 또는 알루미늄합금을 콩 추출물을 유효성분으로 하는 건욕액에 침적하여 봉공처리하는 단계로 이루어진다.Aluminum anodized sealing processing method using soybean of the present invention, anodizing the aluminum or aluminum alloy to form a porous oxide film layer, and coloring the aluminum or aluminum alloy formed with the porous oxide film layer on a natural dye The dyeing and coloring process, and the step of encapsulating the colored aluminum or aluminum alloy in a dry bath containing the soybean extract as an active ingredient.
여기서, 상기 봉공처리하는 단계는, 다시 콩 추출물을 추출하는 단계와, 건욕액을 확보하는 단계와, 침적단계로 이루어진다.Here, the sealing step, the extract of the soybean extract again, the step of securing a bath solution, and the deposition step.
구체적으로 살펴보면, 물과 콩을 1:1의 중량비율로 혼합하고, 이를 대략 13~17시간 정도 불린다. 그리고, 물에 불려진 콩에 상당량의 물을 더 혼합한 후, 중불에서 가열하고, 거품이 생겨 넘칠 때 약불로 1시간 더 가열한다. 이 후, 콩의 건더기를 걸러내어 콩 추출물을 추출한다.Specifically, water and beans are mixed at a weight ratio of 1: 1, which is called about 13 to 17 hours. Then, a considerable amount of water is further mixed with the soybeans soaked in water, and then heated on medium heat, and further heated on low heat for 1 hour when foaming occurs. Thereafter, the beans are filtered to extract bean extract.
그리고, 물에 대해 콩 추출물 10~15중량%를 혼합한 후, 60~85℃의 온도로 가열하여 건욕액을 확보한다.Then, after mixing 10-15% by weight of the soybean extract with respect to water, and heated to a temperature of 60 ~ 85 ℃ to secure a dry bath solution.
또한, 착색된 알루미늄 또는 알루미늄합금을 착색된 색상에 따라 침적시간을 달리 하여 건욕액에 침적한다. 여기서, 침적시간은 6~10분을 진행하는 것이 바람직하다.In addition, the colored aluminum or aluminum alloy is deposited in the bath solution by varying the deposition time according to the colored color. Here, the deposition time is preferably carried out for 6 to 10 minutes.
또한, 상기 콩 추출물은 인체에 무해한 콩이 사용 가능한 것으로, 청대콩, 껍질콩, 강낭콩, 서리태, 서목태, 완두콩, 작두콩, 백태 등의 모든 콩의 종류가 사용될 수 있으며, 특히 이와 같은 콩 중에서도 그 열매 내부에 들어 있는 콩 종자의 추출물을 유효성분으로 사용하게 된다.In addition, the soybean extract can be used soybeans harmless to the human body, all kinds of beans such as blue beans, haricot beans, kidney beans, seotae, seomoktae, peas, small beans, white baek, etc. can be used, especially among such beans inside the fruit Soybean seed extract contained in will be used as an active ingredient.
상기 본 발명의 콩을 이용한 알루미늄의 양극산화 봉공 처리방법을 자세하게 설명하면 다음과 같다.Referring to the anodized sealing method of aluminum using the bean of the present invention in detail.
[다공질형 산화 피막층 형성단계][Formation of Porous Oxide Layer]
염료의 흡착량과 흡착력을 증대시키기 위해 알루미늄 또는 알루미늄합금을 황산, 수산, 크롬산, 인산 등의 산성수용액 속에서 양극산화처리하면 다수의 미세공을 갖는 다공질형 산화피막층을 형성한다.In order to increase the adsorption amount and adsorption capacity of the dye, anodizing the aluminum or aluminum alloy in an acidic solution such as sulfuric acid, hydroxyl, chromic acid, and phosphoric acid forms a porous oxide layer having a plurality of fine pores.
한편, 연질 아노다이징 피막은 1A/dm2 에서 1분에 약 0.28미르론 오르며, 구리함유 재질(2000 계열)은 피막속도가 느리다.On the other hand, the soft anodizing film rises about 0.28 microns per minute at 1 A / dm 2 , and the copper-containing material (2000 series) has a slow film rate.
알루미늄 산화 피막층을 염색 처리시 미세공을 갖지 않은 베리어형 보다는 다수의 미세공을 갖는 다공질형 산화 피막층이 염료 흡착량 및 흡착령이 증가하여 염색 염료의 흡착 내구성이 우수하다.When the aluminum oxide film layer is dyed, the porous oxide film layer having a plurality of micropores is more excellent than the barrier type having no micropores.
따라서, 본 발명에서는 알루미늄과 염색 염료간의 양호한 흡착 내구성을 얻기 위하여 알루미늄을 다공질형 산화 피막층으로 양극 산화 처리한다.Therefore, in the present invention, aluminum is anodized with a porous oxide layer in order to obtain good adsorption durability between aluminum and dyeing dye.
[천연염료 착색단계][Natural dye coloring step]
염료농도 0.1~30g/L, 60℃의 염색액에 침적하여 착색하고, 착색처리시간은 통상 10~30분을 처리한다.The dye concentration is dipped in a dye solution at 0.1 to 30 g / L and 60 ° C for coloring, and the coloring treatment time is usually 10 to 30 minutes.
염료로는 수용성 염료와 유용성 염료를 사용할 수 있는데, 본 출원인에 의해 선출원 발명된 특허 출원번호 제2008-56918호의 "천연식물을 이용한 알루미늄의 염색처리 방법"에 개시된 염료를 사용할 수도 있다.As the dye, water-soluble dyes and oil-soluble dyes can be used, and the dyes disclosed in the patent application No. 2008-56918, "Method for dyeing aluminum using natural plants", which have been previously filed by the present applicant, may be used.
그리고, 대부분 염료의 PH는 5.0~7.0 범위이고, 상기 PH를 낮출 때에는 아세트산을, 높일 때에는 희석한 수산화나트륨이나 아세트산나트륨을 사용한다.The pH of most dyes is in the range of 5.0 to 7.0, and when lowering the pH, acetic acid is used, and diluted sodium hydroxide or sodium acetate is used.
[봉공처리 단계][Sealing step]
염색 및 착색 처리된 알루미늄 제품의 내구성을 향상시키기 위해 콩에서 추출한 추출물을 유효성분으로 하는 건욕액에 상기 알루미늄 제품을 침적하여 봉공(실링)처리를 하는 것으로, 세부적인 내용은 다음과 같다.In order to improve durability of the dyed and colored aluminum product, the aluminum product is dipped in a dry bath using an extract extracted from soybean as an active ingredient, and sealing is performed (sealing). Details are as follows.
먼저, 콩의 종자 1㎏에 물 1ℓ를 넣고, 15시간 정도 불린다.First, 1 liter of water is put in 1 kg of soybean seeds, and it is called for about 15 hours.
그리고, 상기와 같이 불린 콩에 물 20ℓ를 넣고 중불에서 가열하고, 거품이 생겨 넘칠 때에 약불로 1시간 더 가열한다. 이 후, 채반을 통해 콩 건더기를 걸러내어 콩 추출물을 추출한다.Then, 20 liters of water is added to the soybeans called as above and heated on medium heat, and when foamed and overflowed, it is further heated on low heat for 1 hour. Thereafter, the beans are filtered through a rake to extract the bean extract.
이처럼, 추출된 추출물 100㎖ 당 물 1ℓ를 넣고, 이를 70℃까지 가열하여 건욕액을 확보한다.As such, 1 liter of water is added per 100 ml of extracted extract, which is heated to 70 ° C. to obtain a dry bath.
이때, 건욕액 제조에 사용되는 물은 Na+Cl- 성분이 검출되지 않는 순수한 물이나 증류수를 사용하는 것이 적절하다. 그리고, 건욕액의 추출물 농도가 10% 이하일 때에는 봉공처리 시간이 너무 길어져 생산성이 없고, 15%이상의 고농도에서는 알루미늄 제품 표면에 콩 성분의 추출물이 묻어 나와 제품 건조 후 일일이 표면을 닦아 주어야 하는 문제가 있어, 건용액의 콩 추출물 농도는 10~15% 가 되도록 제조하는 것이 바람직하다.At this time, it is appropriate to use pure water or distilled water in which the Na + Cl − component is not used for the water used to prepare the bath solution. In addition, when the extract concentration of the bath solution is 10% or less, the sealing time is too long and there is no productivity. At high concentrations of 15% or more, the extract of soybean ingredient is buried on the surface of the aluminum product. , Soybean extract concentration of the dry solution is preferably prepared to be 10 to 15%.
또한, 건욕액 제조시 가열온도는 60℃ 이하인 경우 봉공작업 초기에 착색된 염료가 탈색되어 구현하고자 하는 색상과 달리 생산되며, 85℃ 이상의 고온에서는 제품의 표면에 얼룩이 생기게 되므로, 건욕액 제조시 가열온도는 60~85℃가 바람직하다.In addition, when the heating temperature is 60 ℃ or less in the manufacturing of the bath solution is produced different from the color to be realized by the color dye at the beginning of the sealing work, and at a high temperature of more than 85 ℃ will cause stains on the surface of the product, heating when manufacturing the bath solution As for temperature, 60-85 degreeC is preferable.
아울러, 이처럼 착색된 알루미늄 제품은 깨끗하게 세척한 후 건욕액에 침적하여, 알루미늄 제품 표면에 봉공처리를 하게 된다.In addition, the colored aluminum product is washed cleanly and then immersed in a dry bath to seal the aluminum product surface.
여기서, 상기 알루미늄 제품에 착색된 색상이 백색계열이나 연한 파스톤텔계열인 경우에는 대략 6분의 착색시간을 적용하고, 적색, 청색, 보라색계열의 색상인 경우에는 대략 8분의 착색시간을 적용하며, 흑색계열의 색상인 경우에는 대략 10분의 착색시간을 적용하는 것이 적절하다.In this case, when the color of the aluminum product is white or light pasteltel, the coloring time of about 6 minutes is applied, and when the colors of red, blue, and purple color are applied, the coloring time of about 8 minutes is applied. In the case of black color, it is appropriate to apply a coloring time of approximately 10 minutes.
상기 본 발명의 콩을 이용한 알루미늄 양극산화 봉공처리방법은 기존의 봉공처리 방법과 피막을 형성하고 착색하는 단계까지는 유사하나, 콩을 이용한 봉공처리시 콩 추출물의 농도, 건욕액 제조시 가열온도, 봉공처리시간 등의 조정을 통해 이상적인 봉공처리를 수행할 수 있고, 이로 인해 알루미늄 제품 표면에 내식성 및 내구성, 내광성이 향상된 봉공 처리작업의 공정 표준화를 이룬 것이다.The aluminum anodized sealing processing method using the beans of the present invention is similar to the conventional sealing method and the step of forming the film and coloring, but the concentration of the soybean extract during the sealing process using soybean, the heating temperature in the preparation of the bath solution, sealing By adjusting the processing time, it is possible to perform the ideal sealing treatment, thereby achieving a process standardization of the sealing processing work improved corrosion resistance, durability, light resistance on the surface of aluminum products.
즉, 본 발명은 알루미늄 피막에 봉공 처리하여 피막 내구성 강화를 증대시키는 기술적 과제와, 천연 봉공처리를 통해 인체의 무해한 친환경 알루미늄 제품의 봉공 처리방법을 개발한 것이다.That is, the present invention is to develop a sealing method of the environmentally friendly aluminum products harmless to the human body through the technical problem of sealing the aluminum film to increase the durability of the film and natural sealing.
이하, 실시예를 통하여 좀 더 상세히 설명한다.Hereinafter, the embodiment will be described in more detail.
실시예 1Example 1
IT 및 가전 부품(휴대폰, PMP, PDA, 디지털카메라, 오디오 부품 등)용 알루미늄 제품을 20% 황산 수용액에서 액온도 25℃, 15V 교류전류로 40분동안 아노다이징 처리하여 피막두께 12㎛로 다공질의 산화막을 형성한 후, 골드착색을 하여 시편을 준비하고, 건욕된 10% 콩 추출물에 70℃에서 6분간 침적 봉공처리한 결과, 염수분무시험 1000시간 이상의 내식성과 120일 이상의 자연방치 상태에서도 우수한 내구성을 보였다.Aluminum oxide for IT and home appliance parts (mobile phones, PMPs, PDAs, digital cameras, audio parts, etc.) is anodized for 40 minutes at 20 ° C sulfuric acid solution at a liquid temperature of 25 ° C and 15V AC current for a film thickness of 12㎛. After forming, the specimens were prepared by gold coloring, and the resultant was sealed for 6 minutes at 70 ° C. in a dry 10% soybean extract. Seemed.
실시예 2Example 2
상기 실시예1과 동일한 알루미늄 제품에 20% 황산 수용액에서 액온도 25℃, 15V 교류전류로 60분동안 아노다이징 처리하여 피막두께 15㎛로 다공질의 산화막을 형성한 후, 본 출원인에 의해 선출원 발명된 특허 출원번호 제2008-56918호의 천연염료 락을 이용하여 적색 염료로 착색하고, 10% 콩 추출물에 70℃에서 8분간 침적 봉공처리한 결과, 염수분무시험에서 1000시간 이상의 내식성과 120일 이상의 자연방치 상태에서도 우수한 내구성을 보였다.In the same aluminum product as in Example 1 in an aqueous solution of 20% sulfuric acid in an aqueous solution of 25 ℃, 15V AC current anodizing for 60 minutes to form a porous oxide film with a film thickness of 15㎛, the patent filed by the applicant Using the natural dye lock of Application No. 2008-56918, colored with red dye, and 10% soybean extract was subjected to immersion sealing at 70 ° C. for 8 minutes. Also showed excellent durability.
실시예 3Example 3
상기 실시예1과 동일한 알루미늄 제품에 20% 황산 수용액에서 액온도 25℃, 15V 교류전류로 1시간 10분동안 아노다이징 처리하여 피막두께 17㎛로 다공질의 산화막을 형성한 후, 흑색염료로 착색하고 10% 콩 추출물에 70℃에서 10분간 침적 봉공처리한 결과, 실시예1과 실시예2의 제품과 동일한 내구성과 내식성을 나타내었다.The same aluminum product as in Example 1 was anodized for 1 hour and 10 minutes in a 20% sulfuric acid aqueous solution at a liquid temperature of 25 ° C. and 15V AC current to form a porous oxide film having a film thickness of 17 μm, and then colored with black dye. After soaking for 10 minutes in 70% soybean extract, it showed the same durability and corrosion resistance as the product of Example 1 and Example 2.
한편, 본 발명은 상기한 구체적인 예에 대해서만 상세히 설명되었지만 본 발명의 기술사상 범위 내에서 다양한 변형 및 수정이 가능함은 당업자에게 있어서 명백한 것이며, 이러한 변형 및 수정이 첨부된 특허청구범위에 속함은 당연한 것이다.On the other hand, the present invention has been described in detail only with respect to the specific examples described above it will be apparent to those skilled in the art that various modifications and variations are possible within the technical scope of the present invention, it is natural that such variations and modifications belong to the appended claims. .
도 1은 본 발명에 의한 봉공처리 이전에 피막 형성된 알루미늄 표면에 착색이 이루어진 형태의 개략 단면도,Figure 1 is a schematic cross-sectional view of the color is formed on the surface of the aluminum formed before the sealing process according to the present invention,
도 2는 본 발명에 의한 착색된 알루미늄 표면에 콩을 이용하여 봉공처리된 형태의 개략 단면도.Figure 2 is a schematic cross-sectional view of a sealed form using a bean on the colored aluminum surface according to the present invention.
Claims (5)