KR101141504B1 - The waterproof construction method for concrete structure using the membrane agent - Google Patents
The waterproof construction method for concrete structure using the membrane agent Download PDFInfo
- Publication number
- KR101141504B1 KR101141504B1 KR1020110115368A KR20110115368A KR101141504B1 KR 101141504 B1 KR101141504 B1 KR 101141504B1 KR 1020110115368 A KR1020110115368 A KR 1020110115368A KR 20110115368 A KR20110115368 A KR 20110115368A KR 101141504 B1 KR101141504 B1 KR 101141504B1
- Authority
- KR
- South Korea
- Prior art keywords
- agent
- coating
- resin
- weight
- concrete structure
- Prior art date
Abstract
Description
본 발명은 바탕조정의 도막제와 이를 이용한 콘크리트 구조물의 방수공법에 관한 것으로, 더욱 상세하게는 표면의 요철 또는 공극을 보강할 수 있는 도막제와, 이를 이용하여 방수도막의 부풀음, 도막의 불균일성, 내균열성 저하 등의 문제점을 해결할 수 있는 콘크리트 구조물의 방수공법에 관한 것이다.
The present invention relates to a coating agent for ground adjustment and a waterproofing method of a concrete structure using the same, and more particularly, a coating agent capable of reinforcing irregularities or voids on the surface, and swelling of the waterproof coating layer, nonuniformity of the coating layer, It relates to a waterproof method of a concrete structure that can solve problems such as degradation of crack resistance.
건축물과 같은 건설구조물은 콘크리트와 철근 등으로 구성되는데, 이러한 콘크리트 구조물의 옥상이나 슬라브에는 그 표면에 직접 방수재를 소정 두께로 도포하여 누수가 발생하지 않도록 방수층을 형성하는 것이 일반적이다. 그러나 이와 같은 방수층은 기온변화에 따른 구조물의 수축, 팽창의 반복에 의해 구조체는 물론, 상기 방수층까지 균열이 생겨 누수가 발생하였고, 방수층의 균열된 부위를 통해 우수가 구조물 내부로 침투하여 구조물 전체의 수명을 단축시키는 문제점이 있어, 이러한 문제점을 해결하기 위하여 현재까지 아스팔트 방수공법, 시트 방수공법, 도막 방수공법 등이 사용되고 있다. Construction structures such as buildings are composed of concrete and reinforcing bars, etc., it is common to form a waterproof layer on the roof or slab of such a concrete structure by applying a waterproof material directly to the surface to a certain thickness to prevent leakage. However, such a waterproof layer was leaked due to cracks in the structure as well as the waterproof layer due to repeated contraction and expansion of the structure according to the temperature change, and rainwater penetrated into the structure through the cracked portion of the waterproof layer, Since there is a problem of shortening the life, in order to solve this problem, asphalt waterproofing method, sheet waterproofing method, coating film waterproofing method and the like have been used to date.
이중에서 특히 아스팔트 방수공법은 사용역사가 가장 오래되고 사용실적이 많은 공법에 해당한다. 그러나 아스팔트 방수공법은 시공현장에서 가열ㅇ용융하여 사용해야 하므로 역한 취기가 발생되고, 화기를 취급함으로써 화재의 위험이 있으며, 사계절이 뚜렷한 우리나라와 같은 기후에서는 온도차이로 인해 방수재 도막의 자체 균열이 발생하여 방수성능을 상실할 수 있다는 문제점이 있다. Among them, the asphalt waterproofing method is one of the oldest and the most used. However, the asphalt waterproofing method must be heated and melted at the construction site, resulting in adverse odor, and there is a risk of fire by handling fire, and in Korea, where the four seasons are clear, due to temperature differences, the crack of the waterproofing film itself occurs. There is a problem that can lose the waterproof performance.
또한 시트 방수공법은 온도에 크게 영향을 받지 않으며, 재료의 물성이 균질한 우수한 방수효과를 발휘한다는 장점은 있으나, 비용이 많이 들고 시공과정에서 시트간의 연결 작업이 어려워 표면이 균일하지 못하고, 연결부위 누수로 인하여 방수기능을 상실할 수 있는 단점이 있다.In addition, the sheet waterproofing method is not significantly influenced by temperature, and has the advantage of exhibiting excellent waterproofing effect with homogeneous physical properties, but the surface is not uniform due to high cost and difficult connection work between sheets during construction. There is a disadvantage that can lose the waterproof function due to leakage.
반면에 도막 방수공법은 작업현장에서 액상상태로 도포되기 때문에 연결부위가 없는 연속 시공이 가능하고, 흐름성이 좋고 기계적 강도가 우수하다는 장점이 있으나, 바닥면의 굴곡에 의한 도포된 도막의 두께가 불균일해지며, 콘크리트의 온도상승으로 인한 수분증발이나 수증기압발생 등에 의한 도막의 부풀음이 발생되어 방수성능을 상실하게 되는 현상이 발생된다는 문제점이 있다.
On the other hand, the coating film waterproofing method is applied in the liquid state at the work site, so it is possible to perform continuous construction without connecting parts, and it has the advantage of excellent flow and mechanical strength, but the thickness of the coated film due to the bending of the bottom surface There is a problem that the non-uniform, the swelling of the coating film due to the water vaporization or the generation of water vapor pressure due to the rise of the temperature of the concrete is generated to lose the waterproof performance.
이에 본 발명에서는 상기와 같은 방수도막의 부풀음 발생문제, 도막의 불균일성, 내균열성 저하 등의 문제점을 해결하고자, 표면의 요철 또는 공극을 보강할 수 있는 바탕조정의 도막제를 제공하는 것을 목적으로 한다.Accordingly, in the present invention, to solve the problems such as swelling problem of the waterproof coating film, non-uniformity of the coating film, lowering the crack resistance, etc., an object of the present invention is to provide a coating agent of the base adjustment that can reinforce the surface irregularities or voids do.
또한 콘크리트 구조물의 방수공법에 있어서 기존의 방수 공법들의 장점은 유지하면서 상기와 같은 문제점을 해결하고자, 표면의 요철 또는 공극을 보강할 수 있는 바탕조정의 도막제를 도포하여 도막을 형성하는 단계와 도막방수제를 도포하여 방수도막을 형성하는 단계가 포함되는, 친환경적인 콘크리트 구조물의 방수공법을 제공하고자 한다.
In addition, in order to solve the above problems while maintaining the advantages of the existing waterproof method in the waterproof method of concrete structures, the step of forming a coating film by applying a coating agent of the background adjustment that can reinforce the surface irregularities or voids It is to provide a waterproof method of eco-friendly concrete structure, including the step of forming a waterproof coating by applying a waterproofing agent.
상기와 같은 목적을 달성하기 위하여, In order to achieve the above object,
본 발명은, 시멘트 30~50중량%, 분산제0.5~2중량% , 광물계 무기질 49~66중량%및 단섬유 0.5~2중량%로 이루어지는 무기질 분말 55~75중량%; 수용성 고분자 20~35중량%; 및 수성 비닐아세테이트 에멀젼 5~10중량%로 이루어지는 것을 특징으로 하는 바탕조정의 도막제에 관한 것이다.The present invention, 55 to 75% by weight of the inorganic powder consisting of 30 to 50% by weight of cement, 0.5 to 2% by weight of dispersant, 49 to 66% by weight of mineral type minerals and 0.5 to 2% by weight of short fibers; 20 to 35% by weight of a water-soluble polymer; And 5 to 10% by weight of an aqueous vinyl acetate emulsion.
바람직하게는 상기 단섬유는 0.01~2mm 길이의 미세한 섬유상인 셀룰로스계 단섬유 또는 폴리에틸렌계 단섬유인 것을 특징으로 한다.Preferably, the short fibers are characterized in that the cellulose-based short fibers or polyethylene-based short fibers which is a fine fiber of 0.01 ~ 2mm length.
또한 바람직하게는 상기 수용성 고분자는 수계 에폭시 수지, 수계 우레탄 수지, 수계 폴리우레아 수지, 수계 폴리우레탄-폴리우레아 수지 중에서 선택된 1종 이상의 수지인 것을 특징으로 한다.
Also preferably, the water-soluble polymer is at least one resin selected from an aqueous epoxy resin, an aqueous urethane resin, an aqueous polyurea resin, and an aqueous polyurethane-polyurea resin.
또한 본 발명은, 콘크리트 구조물 표면의 이물질을 제거하는 전처리 단계; 상기 전처리한 표면에 프라이머를 도포하는 단계; 상기 프라이머를 도포한 표면에 바탕조정의 도막제를 도포하여 표면의 요철 또는 공극이 메꿈 또는 보강된 바탕조정 도막을 형성하는 단계; 상기 형성된 바탕조정 도막에 도막방수제를 도포하여 방수 도막을 형성하는 단계; 및 상기 방수 도막에 탑코팅제를 도포하여 코팅층을 형성하는 단계를 포함하여 이루어지는 것을 특징으로 하는 콘크리트 구조물의 방수공법에 관한 것이다. In another aspect, the present invention, the pre-treatment step of removing foreign matter on the surface of the concrete structure; Applying a primer to the pretreated surface; Applying a coating agent of a background adjustment to the surface on which the primer is applied to form a background adjustment coating film having unevenness or voids on the surface; Forming a waterproof coating film by applying a film waterproofing agent to the formed base adjustment film; And applying a top coating agent to the waterproof coating film to form a coating layer.
바람직하게는 상기 프라이머는 에폭시 수지, 폴리우레탄 수지, 아크릴수지, 폴리 우레아 수지, 폴리우레탄-폴리우레아 수지 및 무기질 탄성도막제 중에서 선택된 1종 이상의 수지인 것을 특징으로 한다.Preferably, the primer is at least one resin selected from an epoxy resin, a polyurethane resin, an acrylic resin, a polyurea resin, a polyurethane-polyurea resin, and an inorganic elastic coating agent.
또한 본 발명에 있어서, 바탕조정의 도막제는 상기에서 제조한 도막제인 것이 바람직하다.Moreover, in this invention, it is preferable that the coating agent of background adjustment is the coating agent manufactured above.
또한 본 발명에 있어서 상기 도막방수제는, In the present invention, the coating film waterproofing agent,
경화제로서 이소시아네이트프리폴리머와, 주제로서 폴리올화합물의 중량비가 1:1~1:5이고, 경도가 Shore A 30~100인 2액형 폴리우레탄 수지; 경화제로서 분말경화촉진제와, 주제로서 MMA(methyl methacrylate) 수지의 중량비가 5:100 인 MMA계 도막 방수제; 에폭시 수지; 아크릴 도막 방수제; 경화제로서 이소시아네이트 프리폴리머와, 주제로서 아민 화합물의 부피비가 1:1~1:2인 경도(Shore A 30~100, Shore D 10~80)를 갖는 폴리우레아 수지; 및 경화제로서 이소시아네이트 프리폴리머와, 주제인 아민-폴리올 화합물의 부피비가 1:1~1:2인 경도 (Shore A 30~100, Shore D 10~80)를 갖는 폴리우레탄-폴리우레아 수지 중에서 선택되는 어느 하나의 방수제인 것이 바람직하다.
2-component polyurethane resins having a weight ratio of isocyanate prepolymer as a curing agent and a polyol compound as a main material of 1: 1 to 1: 5, and a hardness of Shore A 30 to 100; An MMA coating film waterproofing agent having a weight ratio of a powder curing accelerator as a curing agent and a MMA (methyl methacrylate) resin as a curing agent at 5: 100; Epoxy resins; Acrylic coating waterproofing agent; Polyurea resin which has hardness (Shore A 30-100, Shore D 10-80) whose volume ratio of an isocyanate prepolymer as a hardening | curing agent and an amine compound as a main ingredient is 1: 1-1: 2; And a polyurethane-polyurea resin having a hardness (Shore A 30-100, Shore D 10-80) in which the volume ratio of the isocyanate prepolymer and the main amine-polyol compound is 1: 1 to 1: 2 as a curing agent. It is preferable that it is one waterproofing agent.
또한 바람직하게는 상기 탑코팅제는 폴리 우레탄계 화합물, 아크릴계 화합물 및 MMA계 화합물 중에서 선택된 1종 이상의 화합물인 것을 특징으로 한다.
Also preferably, the top coating agent is at least one compound selected from a polyurethane compound, an acrylic compound and an MMA compound.
상술한 바와 같이 본 발명의 바탕조정의 도막제는 도막 방수제를 도포하기 전에 도포하여 콘크리트 표면 위에 요철 또는 공극이 있는 콘크리트 구조물의 표면을 메꾸고 표면을 평활하게 함으로써 도막방수제가 평탄하고 균일하게 도포할 수 있게 하고, 콘크리트의 온도상승으로 인한 수분증발이나 수증기압발생 등에 의한 도막의 부풀음 발생을 억제하여 도막의 방수성능을 현저하게 향상시키는 효과가 있다. As described above, the coating agent of the background adjustment of the present invention is applied before applying the coating waterproofing agent to fill the surface of the concrete structure with irregularities or voids on the concrete surface and smooth the surface so that the coating waterproofing agent can be applied evenly and uniformly. It is possible to suppress the swelling of the coating film due to the water vaporization or the generation of water vapor pressure due to the temperature rise of the concrete, thereby improving the waterproof performance of the coating film significantly.
또한 본 발명에 의한 콘크리트 구조물의 방수공법은 콘크리트 구조물 표면의 요철 또는 공극을 보강할 수 있는 바탕조정의 도막제를 도포하여 바탕조정 도막을 형성한 후, 방수도막 및 코팅층을 형성함으로써 방수 도막의 부풀음이 발생하지 않고, 도막의 두께가 균일하며, 도막의 내균열성이 저하를 방지하여 방수성능을 향상시키면서도 연속시공이 가능하고, 흐름성이 좋아 시공효율을 높일 수 있게 되는 효과가 있다.
In addition, the waterproofing method of the concrete structure according to the present invention by applying a coating agent of the base adjustment that can reinforce the unevenness or voids on the surface of the concrete structure to form the base adjustment coating film, then forming a waterproof coating and coating layer to swell the waterproof coating film This does not occur, the thickness of the coating film is uniform, and the crack resistance of the coating film is prevented from deterioration, thereby improving the waterproofing performance, and the continuous construction is possible, and the flowability is improved, thereby improving the construction efficiency.
이하, 본 발명을 더욱 상세히 설명한다.Hereinafter, the present invention will be described in more detail.
일 양태로서, 본 발명은 도막 방수제의 도포 전에 도포하여 표면 위에 요철 또는 공극이 있는 콘크리트 구조물의 표면을 메꾸고 표면을 평활하게 함으로써 도막방수제가 평탄하고 균일하게 도포할 수 있게 하고, 콘크리트의 온도상승으로 인한 수분증발이나 수증기압발생 등에 의한 도막의 부풀음 발생을 억제하는 도막제에 관한 것으로, 무기질 분말 55~75중량%; 수용성 고분자 20~35중량%; 및 수성 비닐아세테이트 에멀젼 5~10중량%로 이루어진다. In one aspect, the present invention is applied before the coating film waterproofing agent to fill the surface of the concrete structure with irregularities or voids on the surface and smooth the surface to allow the coating waterproofing agent to be applied flat and uniform, the temperature rise of the concrete It relates to a coating agent for suppressing the swelling of the coating film due to water vaporization or the development of water vapor pressure, etc., 55 to 75% by weight of the inorganic powder; 20 to 35% by weight of a water-soluble polymer; And 5 to 10% by weight of an aqueous vinyl acetate emulsion.
보다 구체적으로, 본 발명에 있어서 상기 무기질 분말은 55중량% 미만이면 내후성 및 내구성이 저하되고, 75중량%를 초과할 경우 신축성에 문제가 있으므로, 55~75중량% 범위에서 포함되도록 한다. 이러한 상기 무기질 분말은 시멘트 30~50중량%, 분산제0.5~2중량% , 광물계 무기질 49~66중량%및 단섬유 0.5~2중량%로 구성되는데, 시멘트의 배합비가 30중량% 미만이면 수밀성이 좋지 못해 방수성능에 문제점이 있고 50중량%를 초과하면 신축성이 좋지 못해 인장력과 복원력에 문제점이 있으며, 분산제가 0.5중량% 미만이면 분산제로서의 역할이 미미하게 되고 2중량%를 초과하면 과량이 되므로, 광물계 무기질은 49~66중량%로 구성한다. 또한 상기 광물계 무기질로는 석분과 실리카 등을 사용할 수 있다. 단섬유는 길이가 0.01 내지 2mm 의 미세한 섬유상으로 초기 경화과정에서 발생될수 있는 소성 변형에 의한 수축균열을 방지해 주는 역할을 하며, 본 발명에서는 셀룰로스계 단섬유 또는 폴리에틸렌계 단섬유를 사용하는 것이 바람직하다.More specifically, in the present invention, when the inorganic powder is less than 55% by weight, weather resistance and durability are lowered, and when it exceeds 75% by weight, there is a problem in elasticity, so that it is included in the range of 55 to 75% by weight. The inorganic powder is composed of 30 to 50% by weight of cement, 0.5 to 2% by weight of dispersant, 49 to 66% by weight of mineral-based minerals and 0.5 to 2% by weight of short fibers. If the blending ratio of cement is less than 30% by weight, water tightness is good. There is a problem in waterproof performance, and if it exceeds 50% by weight, there is a problem in tensile strength and restoring force due to poor elasticity.If the dispersant is less than 0.5% by weight, the role as a dispersant becomes insignificant, and when it exceeds 2% by weight, the mineral system Minerals comprise 49 to 66% by weight. In addition, stone minerals, silica, and the like may be used as the mineral-based inorganic material. Short fibers serve to prevent shrinkage cracking caused by plastic deformation, which may occur during the initial curing process, in the form of a fine fiber having a length of 0.01 to 2 mm, and in the present invention, it is preferable to use cellulose short fibers or polyethylene short fibers. Do.
또한, 본 발명에 있어서 상기 수용성 고분자는 수계 에폭시 수지, 수계 우레탄 수지, 수계 폴리우레아 수지, 수계 폴리우레탄-폴리우레아 수지 중에서 선택된 1종 이상의 수지를 이용하고, 20중량% 미만이면 점도 상승으로 인하여 작업성이 저하되고, 35중량%를 초과할 경우, 바탕면의 조정을 위한 다른 성분의 함량이 감소되어 바탕면을 조정하는 성능이 저하되는 문제점이 있다. In addition, in the present invention, the water-soluble polymer uses at least one resin selected from water-based epoxy resins, water-based urethane resins, water-based polyurea resins, and water-based polyurethane-polyurea resins. If the property is lowered and exceeds 35% by weight, there is a problem in that the content of other components for the adjustment of the base surface is reduced to decrease the performance of adjusting the base surface.
또한, 본 발명에 있어서 상기 수성 비닐 아세테이트 에멀젼은 접착력 강화 및 유연성을 부여하기 위해 사용하는 것으로써, 5중량% 미만이 되면 원하는 효과를 얻을 수가 없고 10중량%를 초과할 경우, 내수성의 저하의 문제가 있다.
In addition, in the present invention, the aqueous vinyl acetate emulsion is used to enhance adhesion and flexibility, and when the amount is less than 5% by weight, a desired effect cannot be obtained. There is.
다른 양태로서 본 발명은 상기한 바탕조정의 도막제를 도포하여 도막을 형성하는 단계와, 도막방수제를 도포하여 방수도막을 형성하는 단계가 포함되는 콘크리트 구조물의 방수공법에 관한 것으로, 콘크리트 구조물 표면의 이물질을 제거하는 전처리 단계; 상기 전처리한 표면에 프라이머를 도포하는 단계; 상기 프라이머를 도포한 표면에 바탕조정의 도막제를 도포하여 표면의 요철 또는 공극이 메꿈 또는 보강된 바탕조정 도막을 형성하는 단계; 상기 형성된 바탕조정 도막에 도막방수제를 도포하여 방수 도막을 형성하는 단계; 및 상기 방수 도막에 탑코팅제를 도포하여 코팅층을 형성하는 단계를 포함하여 이루어진다.In another aspect, the present invention relates to a waterproofing method of a concrete structure comprising the step of forming a coating film by coating the coating agent of the above-described background adjustment, and forming a waterproof coating film by applying a coating film waterproofing agent, A pretreatment step of removing foreign matters; Applying a primer to the pretreated surface; Applying a coating agent of a background adjustment to the surface on which the primer is applied to form a background adjustment coating film having unevenness or voids on the surface; Forming a waterproof coating film by applying a film waterproofing agent to the formed base adjustment film; And forming a coating layer by applying a top coating agent to the waterproof coating film.
보다 구체적으로 본 발명에 있어서 상기 전처리 단계는 콘크리트 구조물 표면에 이물질 및 레이턴스 층을 제거하는 단계이다. More specifically, in the present invention, the pretreatment step is a step of removing the foreign matter and the latency layer on the surface of the concrete structure.
본 발명에 있어서 상기 프라이머의 도포 단계는 전처리를 한 콘크리트 표면과 표면 보강용 도막제와의 접착력을 증가시키고, 콘크리트 표면내부로 침투성이 우수하고 구체를 강화하기 위하여, 상기 전처리된 표면을 에폭시 수지, 폴리우레탄 수지, 아크릴수지, 폴리 우레아 수지, 폴리우레탄-폴리우레아 수지 및 무기질 탄성도막제 중에서 선택된 1종 이상의 수지로 형성된 프라이머를 도포한다. 이 때, 프라이머는 붓, 롤러 또는 에어리스 스프레이 등의 방법에 의해 간편하게 도장할 수 있다. In the present invention, the step of applying the primer is to increase the adhesion between the pre-treated concrete surface and the coating material for surface reinforcement, and excellent penetration into the concrete surface and to strengthen the sphere, the pre-treated surface is epoxy resin, A primer formed of at least one resin selected from a polyurethane resin, an acrylic resin, a polyurea resin, a polyurethane-polyurea resin, and an inorganic elastic coating agent is applied. At this time, the primer can be easily coated by a method such as a brush, a roller, or an airless spray.
또한 본 발명에 있어서 상기 바탕조정의 도막의 형성단계는 상기 프라이머를 도포한 표면에서 상술한 도막제를 도포하여 표면의 요철 또는 공극이 메꿈 또는 보강된 바탕조정 도막을 형성하는 단계로, 상기 형성된 바탕조정 도막에 의하여 도막방수제가 평탄하고 균일하게 도포할 수 있게 되고, 콘크리트의 온도상승으로 인한 수분증발이나 수증기압발생 등에 의한 방수 도막의 부풀음 발생을 억제하게 된다. In the present invention, the step of forming the coating film of the base adjustment is a step of forming the base adjustment coating film having the unevenness or voids formed on the surface by applying the coating agent described above on the surface on which the primer is applied. By the adjusting coating film, the coating film waterproofing agent can be applied flatly and uniformly, and the occurrence of swelling of the waterproof coating film due to moisture evaporation or water vapor pressure caused by the temperature rise of the concrete is suppressed.
또한 본 발명에 있어서 상기 방수 도막의 형성단계는 상기에서 형성된 도막에 도막 방수제를 도포하여, 인장강도와 신장률 등 기계적 물성이 우수하고 탄성력이 좋은 방수 도막을 형성하는 단계이다. In the present invention, the forming step of the waterproof coating film is a step of forming a waterproof coating film having excellent elasticity and mechanical properties such as tensile strength and elongation rate by applying a coating film waterproofing agent to the coating film formed above.
이 때, 상기 도막 방수제로는 경화제로서 이소시아네이트프리폴리머와, 주제로서 폴리올화합물의 중량비가 1:1~1:5이고, 경도가 Shore A 30~100인 2액형 폴리우레탄 수지; 경화제로서 분말경화촉진제와, 주제로서 MMA(methyl methacrylate) 수지의 중량비가 5:100 인 MMA계 도막 방수제; 에폭시 수지; 및 아크릴 도막 방수제 중에서 1종 이상을 선택하여 레기 또는 롤러 등으로 도포할 수 있다. 또한, 상기 도막 방수제로는 경화제인 이소시아네이트 프리폴리머와, 주제로서 아민 화합물의 부피비가 1:1~1:2인 경도(Shore A 30~100, Shore D 10~80)를 갖는 폴리우레아 수지를 들수 있고, 경화제인 이소시아네이트 프리폴리머와 , 주제인 아민-폴리올 화합물의 부피비가 1:1~1:2인 경도 (Shore A 30~100, Shore D 10~80)를 갖는 폴리우레탄-폴리우레아 수지를 들 수 있으며, 붓 또는 롤러로 작업할 수 있고, 필요시 전용 2액형 고압 스프레이 장비를 사용하여 도포할 수 있다.At this time, the coating film waterproofing agent is a two-component polyurethane resin having a weight ratio of isocyanate prepolymer as a curing agent and a polyol compound as a main material of 1: 1 to 1: 5, and hardness of Shore A 30 to 100; An MMA coating film waterproofing agent having a weight ratio of a powder curing accelerator as a curing agent and a MMA (methyl methacrylate) resin as a curing agent at 5: 100; Epoxy resins; And at least 1 type of acrylic coating film waterproofing agent can be selected, and can be apply | coated with a paper or roller. In addition, the coating film waterproofing agent may include a polyurea resin having an isocyanate prepolymer as a curing agent and a hardness (Shore A 30 to 100, Shore D 10 to 80) having a volume ratio of 1: 1 to 1: 2 as the main amine compound. And polyurethane-polyurea resins having a hardness (Shore A 30-100, Shore D 10-80) in which the volume ratio of the isocyanate prepolymer as a curing agent and the main amine-polyol compound is 1: 1 to 1: 2. It can be worked with a brush or roller and can be applied using a dedicated two-part high pressure spray equipment if necessary.
또한 본 발명에 있어서 상기 코팅층의 형성단계는 상기에서 형성된 방수도막에 탑코팅제를 도포하여 코팅층을 형성하는 단계로, 코팅층을 형성함으로써 옥상과 같은 노출형 구조물의 자외선, 오존 및 산성비 등에 대한 내후성과, 내마모성 등의 내구성을 부여할 수 있게 되는 바, 상기 탑코팅제로는 폴리 우레탄계 화합물, 아크릴계 화합물 및 MMA계 화합물 중에서 1종 이상을 선택하도록 한다.
In the present invention, the step of forming the coating layer is a step of forming a coating layer by applying a top coating agent to the waterproofing coating formed in the above, by forming a coating layer, such as weather resistance against ultraviolet rays, ozone and acid rain of an exposed structure such as a rooftop, Since the durability such as wear resistance can be imparted, the top coating agent may be selected from at least one of a polyurethane compound, an acrylic compound, and an MMA compound.
이하 실시예 및 비교예를 통하여 본 발명을 더욱 상세히 설명하나, 본 발명의 보호범위가 이에 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples, but the protection scope of the present invention is not limited thereto.
<실시예 1~3><Examples 1-3>
먼저, 하기 표 1에 나타낸 배합비(중량%)로 각각의 원료를 배합하고 교반하여 바탕조정의 도막제를 제조하였다. 이 때, 무기질 분말은 시멘트 40중량%, 분산제와 단섬유를 각각 1중량%, 광물계 무기질을 58중량%로 구성된 것을 사용하였다.
First, each raw material was mix | blended and stirred in the compounding ratio (weight%) shown in following Table 1, and the coating film of background adjustment was prepared. At this time, the inorganic powder was composed of 40% by weight cement, 1% by weight of the dispersant and short fibers, respectively, 58% by weight of mineral-based minerals.
30Water based epoxy resin
30
27Waterborne Polyurea Resin
27
25Water-based Polyurethane Resin
25
다음으로, 50*150*5mm 크기의 시험용 콘크리트 밑판을 전처리한 표면에, 프라이머, 바탕조정의 도막제, 도막방수제 및 탑 코팅제를 순서대로 도포하여 시편을 제조하였다. Next, a specimen was prepared by applying a primer, a backing coating agent, a film waterproofing agent, and a top coating agent in order to the surface of the test concrete base plate having a size of 50 * 150 * 5 mm.
도막제Paint
30Water based epoxy resin
30
27Waterborne Polyurea Resin
27
25Water-based Polyurethane Resin
25
화합물Polyurethane
compound
이 때, 상기 실시예 1, 3에 사용된 에폭시 수지 프라이머는 국내에서 범용으로 사용되고 있는 수용성 에폭시 프라이머(㈜삼화페인트공업으로부터 구입)를 사용하였고, 실시예 2의 폴리우레탄 수지 프라이머는 국내에서 범용으로 사용되고 있는 방수용 우레탄 프라이머(㈜삼화페인트공업으로부터 구입)를 사용하였다.At this time, the epoxy resin primers used in Examples 1 and 3 used water-soluble epoxy primers (commercially available from Samwha Paint Co., Ltd.) that are used in Korea, and the polyurethane resin primers of Example 2 were used in Korea. Waterproof urethane primer (purchased from Samwha Paint Co., Ltd.) was used.
또한, 도막방수제로 실시예 1, 2는 노출 도막 방수제(㈜강남화성으로부터 구입, 경도가 Shore A로 60인 2액형 폴리우레탄 수지)를 사용하였고, 실시예 3은 직접 제조(특허 등록 10-0978451)한 MMA(Methyl MethAcrylate)계 도막방수제를 사용하였다.In addition, Examples 1 and 2 used an exposure coating waterproofing agent (purchased from Gangnam Hwasung Co., Ltd., two-component polyurethane resin having a hardness of 60 Shore A), and Example 3 was manufactured directly (Patent Registration 10-0978451). ) MMA (Methyl Meth Acrylate) based film waterproofing agent was used.
또한, 탑코팅제로 실시예 1, 2의 폴리우레탄계 화합물은 국내에서 범용으로 사용되고 있는 노출방수제 제품(㈜강남화성으로부터 구입)를 사용하였고, 실시예 3은 직접 제조(특허 등록 10-0978451)한 MMA계 화합물을 사용하였다.
In addition, the polyurethane compound of Examples 1 and 2 was used as a top coating agent, and an exposure waterproofing product (purchased from Gangnam Hwaseong Co., Ltd.), which is commonly used in Korea, and Example 3 was directly manufactured (Patent Registration 10-0978451). System compounds were used.
<비교예 1>Comparative Example 1
50*150*5mm 크기의 시험용 콘크리트 밑판을 전처리한 표면에, 노출 방수제 프라이머(폴리우레탄 수지, ㈜강남화성으로부터 구입)를 도포하고, 노출 도막 방수제(경도가 Shore A로 60인 2액형 폴리우레탄 수지, 강남화성으로부터 구입)를 도포한 다음, 폴리우레탄 탑코팅제(㈜강남화성으로부터 구입)를 도포하였다.
A surface waterproofing primer (polyurethane resin, purchased from Gangnam Hwaseong Co., Ltd.) was applied to the surface of the test concrete base plate having a size of 50 * 150 * 5mm, and a two-component polyurethane resin having a hardness of 60 with Shore A. And a polyurethane top coating agent (purchased from Gangnam Hwaseong Co., Ltd.) were applied.
<비교예 2> Comparative Example 2
50*150*5mm 크기의 시험용 콘크리트 밑판을 전처리한 표면에 수용성 에폭시 프라이머(㈜삼화페인트공업으로부터 구입)를 도포하고, 노출 도막 방수제(강남화성으로부터 구입, 경도가 Shore A로 60인 2액형 폴리우레탄 수지)를 도포한 다음, 아크릴계 탑코팅제로서 노출 방수용 상도(㈜조광페인트로부터 구입)를 이용하여 도포하였다.
A water-soluble epoxy primer (purchased from Samwha Paint Co., Ltd.) was applied to the surface of the test concrete base plate of 50 * 150 * 5mm size, and an exposed coating waterproofing agent (purchased from Gangnam Chemical, hardness of 60 with Shore A, 2-component polyurethane) Resin) was applied and then coated using an acrylic waterproof coating (available from Dye Paint).
<평가 및 결과><Evaluation and result>
상기 실시예 1 내지 3, 비교예 1 내지 2에 따라 제작한 시험용 시편을 KS L 1001의 방법(0.12MPa 의 증기압을 168시간동안 시편에 가한 후 외관 변화(부풀음 발생유무 등)를 확인)으로 그 성능을 평가하고 그 평가결과를 하기 표 3에 나타내었다.
The test specimens prepared according to Examples 1 to 3 and Comparative Examples 1 to 2 were subjected to the method of KS L 1001 (a change in appearance after confirming the appearance of swelling after adding a vapor pressure of 0.12 MPa for 168 hours). The performance was evaluated and the evaluation results are shown in Table 3 below.
도막제Paint
30Water based epoxy resin
30
27Waterborne Polyurea Resin
27
25Water-based Polyurethane Resin
25
화합물Polyurethane
compound
상기 표 3에서 나타낸 바와 같이, 도막제를 도포하지 않은 비교예 1, 2의 경우에는 도막의 부풀음이 발생하여 방수성능을 상실하게 됨을 확인할 수 있었고, 실시예 1 내지 3의 경우, 외관상태가 양호하고, 도막의 부풀음이나 균열이 나타나지 않아 뛰어난 방수성능을 가지는 것으로 평가되었다.
As shown in Table 3, in Comparative Examples 1 and 2, which did not apply the coating agent, it was confirmed that swelling of the coating film caused the loss of waterproofing performance. In Examples 1 to 3, the appearance state was good. It was evaluated that the coating film had no swelling or cracking and had excellent waterproofing performance.
이와 같이 본 발명은 기재된 실시예에 한정되는 것이 아니고, 본 발명의 사상 및 범위를 벗어나지 않고 다양하게 수정 및 변형할 수 있음은 이 기술의 분야에서 통상의 지식을 가진 자에게 자명하다. 따라서 그러한 수정예 또는 변형예들은 본 발명의 특허청구범위에 속한다 하여야 할 것이다.It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the invention. Therefore, such modifications or variations will have to be belong to the claims of the present invention.
Claims (10)
상기 전처리한 표면에 프라이머를 도포하는 단계;
상기 프라이머를 도포한 표면에 바탕조정의 도막제를 도포하여 표면의 요철 또는 공극이 메꿈 또는 보강된 바탕조정 도막을 형성하는 단계;
상기 형성된 바탕조정 도막에 도막방수제를 도포하여 방수 도막을 형성하는 단계; 및
상기 방수도막에 탑코팅제를 도포하여 코팅층을 형성하는 단계를 포함하여 이루어지고,
상기 바탕조정의 도막제는,
시멘트 30~50중량%, 분산제0.5~2중량%, 광물계 무기질 49~66중량%및 단섬유 0.5~2중량%로 이루어지는 무기질 분말 55~75중량%; 수용성 고분자 20~35중량%; 및 수성 비닐아세테이트 에멀젼 5~10중량%로 이루어지는 것을 특징으로 하고,
상기 도막방수제는,
경화제로서 이소시아네이트프리폴리머와, 주제로서 폴리올화합물의 중량비가 1:1~1:5이고, 경도가 Shore A 30~100인 2액형 폴리우레탄 수지; 경화제로서 분말경화촉진제와, 주제로서 MMA(methyl methacrylate) 수지의 중량비가 5:100 인 MMA계 도막 방수제; 에폭시 수지; 아크릴 도막 방수제; 경화제로서 이소시아네이트 프리폴리머와, 주제로서 아민 화합물의 부피비가 1:1~1:2인 경도(Shore A 30~100, Shore D 10~80)를 갖는 폴리우레아 수지; 및 경화제로서 이소시아네이트 프리폴리머와, 주제인 아민-폴리올 화합물의 부피비가 1:1~1:2인 경도 (Shore A 30~100, Shore D 10~80)를 갖는 폴리우레탄-폴리우레아 수지 중에서 선택되는 1종 이상의 방수제인 것을 특징으로 하는,
콘크리트 구조물의 방수공법.A pretreatment step of removing foreign matter from the surface of the concrete structure;
Applying a primer to the pretreated surface;
Applying a coating agent of a background adjustment to the surface on which the primer is applied to form a background adjustment coating film having unevenness or voids on the surface;
Forming a waterproof coating film by applying a film waterproofing agent to the formed base adjustment film; And
It comprises a step of forming a coating layer by applying a top coating agent to the waterproof coating,
The coating agent of the background adjustment,
55 to 75% by weight of the inorganic powder consisting of 30 to 50% by weight of cement, 0.5 to 2% by weight of dispersant, 49 to 66% by weight of mineral based minerals and 0.5 to 2% by weight of short fibers; 20 to 35% by weight of a water-soluble polymer; And 5 to 10% by weight of an aqueous vinyl acetate emulsion, characterized in that
The coating film waterproofing agent,
2-component polyurethane resins having a weight ratio of isocyanate prepolymer as a curing agent and a polyol compound as a main material of 1: 1 to 1: 5, and a hardness of Shore A 30 to 100; An MMA coating film waterproofing agent having a weight ratio of a powder curing accelerator as a curing agent and a MMA (methyl methacrylate) resin as a curing agent at 5: 100; Epoxy resins; Acrylic coating waterproofing agent; Polyurea resin which has hardness (Shore A 30-100, Shore D 10-80) whose volume ratio of an isocyanate prepolymer as a hardening | curing agent and an amine compound as a main ingredient is 1: 1-1: 2; And a polyurethane-polyurea resin having a hardness (Shore A 30-100, Shore D 10-80) in which the volume ratio of the isocyanate prepolymer and the main amine-polyol compound is 1: 1 to 1: 2 as a curing agent. It is a waterproofing agent more than a kind,
Waterproofing method of concrete structure.
상기 프라이머는 에폭시 수지, 폴리우레탄 수지, 아크릴수지, 폴리 우레아 수지, 폴리우레탄-폴리우레아 수지 및 무기질 탄성도막제 중에서 선택된 1종 이상의 수지인 것을 특징으로 하는 콘크리트 구조물의 방수공법.The method of claim 4, wherein
The primer is waterproofing method of concrete structure, characterized in that at least one resin selected from epoxy resin, polyurethane resin, acrylic resin, polyurea resin, polyurethane-polyurea resin and inorganic elastic coating agent.
상기 탑코팅제는 폴리 우레탄계 화합물, 아크릴계 화합물 및 MMA계 화합물 중에서 선택된 1종 이상의 화합물인 것을 특징으로 하는 콘크리트 구조물의 방수공법.The method of claim 4, wherein
The top coating agent is a waterproof method of a concrete structure, characterized in that at least one compound selected from polyurethane compounds, acrylic compounds and MMA compounds.
상기 단섬유는 0.01~2mm 길이의 미세한 섬유상인 셀룰로스계 단섬유 또는 폴리에틸렌계 단섬유인 것을 특징으로 하는 콘크리트 구조물의 방수공법.The method of claim 4, wherein
The short fiber is a waterproof construction method of a concrete structure, characterized in that the cellulose-based short fibers or polyethylene-based short fibers of a fine fiber of 0.01 ~ 2mm length.
상기 수용성 고분자는 수계 에폭시 수지, 수계 우레탄 수지, 수계 폴리우레아 수지, 수계 폴리우레탄-폴리우레아 수지 중에서 선택된 1종 이상의 수지인 것을 특징으로 하는 콘크리트 구조물의 방수공법.The method of claim 4, wherein
The water-soluble polymer is a waterproof construction method of a concrete structure, characterized in that at least one resin selected from water-based epoxy resin, water-based urethane resin, water-based polyurea resin, water-based polyurethane-polyurea resin.