KR101059787B1 - A decorative board containing aromatic ingredients, floorboards and finishing boards using the same - Google Patents
A decorative board containing aromatic ingredients, floorboards and finishing boards using the same Download PDFInfo
- Publication number
- KR101059787B1 KR101059787B1 KR1020090051038A KR20090051038A KR101059787B1 KR 101059787 B1 KR101059787 B1 KR 101059787B1 KR 1020090051038 A KR1020090051038 A KR 1020090051038A KR 20090051038 A KR20090051038 A KR 20090051038A KR 101059787 B1 KR101059787 B1 KR 101059787B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- paper
- layer
- impregnated
- printed pattern
- Prior art date
Abstract
본 발명은 아로마 성분이 함유된 화장판과 이를 이용한 마루판 및 마감판에 관한 것으로서, 좀더 상세하게는 크라프트지층(10-1) 상부에 인쇄무늬지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%를 혼합한 혼합액에 함침하여 건조한 인쇄무늬지층(20-1)을 2층 구조로 적층하여 가열 압착 형성한 화장판; 크라프트지(Kraft paper)와 인쇄무늬지를 페놀수지에 함침 건조한 크라프트지층(10-2)과 인쇄무늬지층(20-2) 상부에 보호지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%을 혼합한 혼합액에 함침하여 건조한 보호지층(30-2)을 3층 구조로 적층하여 가열 압착 형성한 화장판; 상기 화장판을 합판, MDF와 같은 판재나 상부에 접착한 마루판; 및 상기 화장판을 파티클 보드 상부에 접착한 마감판을 제공하여 다양하게 사용하되, 상기 화장판, 마루판, 마감판에 함유된 천연 아로마 성분에 의해 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등 인체 유익을 제공하는데 그 특징이 있다.The present invention relates to a make-up plate containing an aromatic component and a floorboard and a finishing plate using the same, and more specifically, the printed pattern paper on the top of the kraft paper layer 10-1 to melamine resin 99.7 to 99.9% by weight of the aroma stock solution 0.3 to 0.1. A makeup plate formed by impregnating the mixed solution mixed with the weight% by drying the printed pattern paper layer 20-1 in a two-layered structure and heat-compressing; Kraft paper and printed pattern paper impregnated with phenolic resin Kraft paper layer (10-2) and printed patterned layer (20-2) on top of the protective paper melamine resin 99.7 ~ 99.9% by weight of aroma stock solution 0.3 ~ 0.1% by weight Impregnated in the mixed solution mixed with a dried protective paper layer (30-2) laminated in a three-layer structure formed by heating compression bonding; A floorboard having the decorative plate bonded to a board or upper part such as plywood and MDF; And using a variety of boards to provide a finishing plate bonded to the top of the particle board, using a variety of natural aroma components contained in the makeup plate, floorboards, finishing boards concentrated learning, dry skin care or when you can not sleep, anxiety, It is characterized by providing benefits to the human body, such as relieving stress.
아로마, 화장판, 마루판, 마감판, 접착, 인체 유익 Aroma, makeup board, floorboard, finish board, adhesion, human benefit
Description
본 발명은 아로마 성분과 멜라민수지 혼합액에 함침된 시트를 이용하여 화장판, 마루판, 마감판을 제조하므로 아로마 성분에 의한 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등의 인체 유익을 제공하는 아로마 성분이 함유된 화장판과 이를 이용한 마루판 및 마감판에 관한 것이다.The present invention uses a sheet impregnated with a mixture of aromatic components and melamine resins to prepare a makeup plate, floorboards, finishing plates, so that the benefits of learning by aroma components, dry skin care or when you do not sleep, anxiety, stress relief, etc. The present invention relates to a decorative plate containing an aromatic component and a floorboard and a finishing board using the same.
일반적으로 빌딩, 사무실, 호텔, 점포, 주택, 아파트 등의 내장재나 기타 가구 제작 등에 사용되는 판재는 상품성을 높이기 위해 화장판을 접합 사용하는 방식을 이용하고 있다.In general, the plate used in the interior materials of buildings, offices, hotels, stores, houses, apartments, and other furniture, and the like used a joining plate to enhance the merchandise.
상기 화장판은 크라프트지(Kraft paper)를 페놀수지에 함침 건조한 크라프트지층과, 인쇄무늬가 인쇄된 인쇄무늬지를 멜라민수지에 함침 건조한 인쇄무늬층을 2층 구조로 적층하여 가열 압착 형성하거나, 상기 인쇄무늬층 상부에 보호지를 메라민 함침 건조한 보호층을 더 추가한 3층 구조로 적층하여 가열 압착 형성하고 있다.The decorative plate is formed by laminating a kraft paper layer impregnated with kraft paper in a phenolic resin and a printed pattern layer impregnated with melamine resin with a printed pattern printed with a printed pattern in a two-layered structure, followed by thermal compression molding. The protective paper is laminated on the patterned layer in a three-layered structure in which a dry protective layer further impregnated with melamine is laminated to form a hot press.
그리고 상기한 화장판은 합판이나 MDF, 파티클보드 등의 표면에 접합하여 마루판이나 마감판 등으로 다양하게 사용하게 되는 것이다.And the decorative plate is bonded to the surface of plywood, MDF, particleboard, etc. will be used in various ways such as floorboards and finish plates.
그런데 상기한 종래의 화장판은 단순히 외관미에 대한 상품성만을 고려하였다.By the way, the above-mentioned conventional decorative plate simply considered the commerciality for the appearance beauty.
이에 본 출원인은 상기 화장판의 외관미는 물론 인체에 유익을 제공하는 제품의 개발에 노력하였다.The present applicant has tried to develop a product that provides benefits to the human body as well as the appearance of the decorative plate.
본 발명은 상기한 종래 기술이 갖는 제반 문제점을 해결하고자 발명된 것으로서, 아로마 성분과 멜라민수지 혼합액에 함침된 시트를 이용하여 화장판, 마루판, 마감판을 제조하므로 아로마 성분에 의한 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등 인체의 유익을 제공하는데 그 목적이 있다.The present invention has been invented to solve the problems of the prior art as described above, because it manufactures a decorative plate, floorboard, finish plate using the sheet impregnated with the aromatic component and melamine resin mixture, concentrated learning by the aromatic component, dry skin Management or when you can not sleep, anxiety, stress relief and provide the human benefits.
이러한 본 발명은,This invention,
크라프트지(Kraft paper)를 페놀수지에 함침 건조한 크라프트지층 상부에 인쇄무늬가 인쇄된 인쇄무늬지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%를 혼합한 혼합액에 함침하되, 상기 혼합액이 인쇄무늬지의 무게 대비 45~60% 도포되도록 함침처리하여 건조한 인쇄무늬지층을 2층 구조로 적층하여 가열 압착 형성한 화장판을 제공함에 그 특징이 있다.Impregnating kraft paper with phenolic resin Immerse the printed pattern on which the printed pattern is printed on the top of the dry kraft paper layer in a mixture of 99.7 to 99.9% by weight of melamine resin and 0.3 to 0.1% by weight of an aroma stock solution. It is characterized by providing a decorative plate formed by heat-pressing by stacking the dried printed patterned paper layer in a two-layer structure by impregnating the coating to be 45 to 60% of the weight of the printed patterned paper.
본 발명은 크라프트지(Kraft paper)와 인쇄무늬지를 페놀수지에 함침 건조한 크라프트지층과 인쇄무늬지층 상부에 보호지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%을 혼합한 혼합액에 함침하되, 상기 혼합액이 보호지의 무게 대비 65~80% 도포되도록 함침처리하여 건조한 보호지층을 3층 구조로 적층하여 가열 압착 형성한 화장판을 제공함에 그 특징이 있다.The present invention impregnated kraft paper and printed pattern paper with a phenolic resin and impregnated a dry kraft paper layer and a protective paper on top of the printed patterned paper layer in a mixed solution of 99.7 to 99.9% by weight of melamine resin and 0.3 to 0.1% by weight of an aromatic stock solution. In addition, the mixed solution is impregnated so as to apply 65 to 80% of the weight of the protective paper by drying the protective paper layer in a three-layer structure to provide a decorative plate formed by heating compression bonding.
본 발명은 상기한 본 발명의 화장판을 합판, MDF와 같은 판재나 상부에 접착한 마루판이나 파티클 보드 상부에 접착한 마감판을 제공하는데 그 특징이 있다.The present invention is characterized in that the decorative plate of the present invention described above is provided with a laminate such as plywood, MDF, or a floorboard bonded to the top, or a finishing board bonded to the top of the particle board.
이러한 본 발명은, 아로마 성분과 멜라민수지 혼합액에 함침된 시트를 이용한 화장판을 제공함은 물론 상기 화장판이 적용된 마루판, 마감판을 제공하므로 실내에서 다양한 미감을 갖는 상품성과 함께 천연 아로마 성분에 의해 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등의 인체 유익을 제공하는 효과를 갖는 것이다.The present invention, as well as providing a decorative plate using a sheet impregnated with the aromatic component and melamine resin mixture solution, as well as providing a floorboard, a finishing plate to which the decorative plate is applied, focusing on learning by natural aroma components with a variety of aesthetics indoors , Dry skin care or when you can not sleep, has the effect of providing the human benefits, such as anxiety, relieve stress.
이하, 상기한 본 발명의 실시 예에 대해 살펴보기로 한다.Hereinafter, an embodiment of the present invention described above will be described.
본 발명은 인체의 유익을 제공하는 로즈, 페퍼민트, 자스민, 유칼투스, 아벤더, 마조람, 레몬, 소나무, 제라늄,티트리, 타임, 오렌지, 주니퍼, 카모마일, 바질 등의 천연 아로마 성분을 이용하는 것이다.The present invention utilizes natural aroma components such as rose, peppermint, jasmine, eucalyptus, avenger, marjoram, lemon, pine, geranium, tea tree, thyme, orange, juniper, chamomile, basil, etc., which provide human benefits.
본 발명의 화장판(100)은 도 1에 도시된 바와 같이, 크라프트지(Kraft paper)를 페놀수지에 함침 건조한 크라프트지층(10-1) 상부에 인쇄무늬가 인쇄된 인쇄무늬지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%를 혼합한 혼합액에 함침하되, 상기 혼합액이 인쇄무늬지의 무게 대비 45~60% 도포되도록 함침처리하여 건조한 인쇄무늬지층(20-1)을 2층 구조로 적층하여 가열 압착 형성한 것이다.As shown in FIG. 1, the
또한, 도 2에 도시된 바와 같이, 크라프트지(Kraft paper)와 인쇄무늬지를 페놀수지에 함침 건조한 크라프트지층(10-2)과 인쇄무늬지층(20-2) 상부에 보호지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%을 혼합한 혼합액에 함침하되, 상기 혼합액이 보호지의 무게 대비 65~80% 도포되도록 함침처리하여 건조한 보호지층(30-2)을 3층 구조로 적층하여 가열 압착 형성한 것이다.In addition, as shown in Figure 2, kraft paper (kraft paper) and printed pattern paper impregnated with phenolic resin, kraft paper layer (10-2) and the protective paper on the printed pattern paper layer 20-2, the protective paper melamine resin 99.7 ~ 99.9 Impregnated into a mixed solution of 0.3% to 0.1% by weight of the aroma stock solution, but impregnated so that the mixed solution is applied to 65 to 80% of the weight of the protective paper, and dried by drying the protective paper layer 30-2 in a three-layer structure. It is formed by crimping.
즉, 도 1은 2층 구조이고 도 2는 3층 구조로 시트를 적층한 화장판을 제공하는 것이다.That is, Figure 1 is a two-layer structure and Figure 2 is to provide a decorative plate laminated the sheet in a three-layer structure.
이때 상기 혼합액의 멜라민수지를 99.7 중량% 미만으로 혼합하는 경우에 함침처리가 용이하지 못하게 되는 단점이 있고, 99.9 중량% 초과로 혼합하는 경우에 아로마 원액의 함유량이 너무 작게되어 아로마 효과를 충분히 얻기 곤란한 단점 때문에 99.7 ~99.9 중량%으로 혼합함이 바람직하고, 아로마 원액을 0.1 중량% 미만으로 혼합하는 경우에 인체의 유익을 주는 효과가 현저히 저하되고, 0.3 중량% 초과로 혼합하는 경우에 멜라민수지 성분의 부족에 따른 함침처리가 용이하지 못하게 되는 단점 때문에 0.3~0.1 중량%으로 혼합함이 바람직하다.In this case, when the melamine resin of the mixed solution is mixed at less than 99.7% by weight, there is a disadvantage in that the impregnation process is not easy. Due to the disadvantage, it is preferable to mix at 99.7 to 99.9% by weight, and when the aroma stock solution is mixed at less than 0.1% by weight, the beneficial effect of the human body is remarkably lowered, and when mixed to more than 0.3% by weight of the melamine resin component It is preferable to mix 0.3 to 0.1% by weight because of the disadvantage that the impregnation treatment is not easy due to lack.
또한, 상기 크라프트지층과 인쇄무늬지층이 적층된 경우에는 멜라민수지와 아로마 원액의 혼합액이 인쇄무늬지의 무게 대비 45%미만으로 도포되는 경우에 도포층이 너무 얇게 형성되어 인쇄무늬지의 보호가 쉽지 않고, 60%초과로 도포되는 경우에 도포층이 너무 불필요하게 두껍게 형성되기때문에 45~60%로 형성함이 바람직하다.In addition, in the case where the kraft paper layer and the printed pattern paper layer are laminated, when the mixed solution of melamine resin and the aroma stock solution is applied at less than 45% of the weight of the printed pattern paper, the coating layer is formed so thin that it is not easy to protect the printed paper. In the case where the coating layer is applied in excess of 60%, the coating layer is formed to be unnecessarily thick, so it is preferably formed at 45 to 60%.
또한, 상기 크라프트지층과 인쇄무늬지층 및 보호지층이 적층된 경우에는 상기 보호지층이 인쇄무늬지층 보다 얇기 때문에 멜라민수지와 아로마 원액의 혼합액을 크라프트지층과 인쇄무늬지층이 적층된 경우보다 더 두껍게 형성하되, 상기 멜라민수지와 아로마 원액의 혼합액이 인쇄무늬지의 무게 대비 65%미만으로 도포되는 경우에 도포층이 너무 얇게 형성되어 인쇄무늬지의 보호가 쉽지 않고, 80%초과로 도포되는 경우에 도포층이 너무 불필요하게 두껍게 형성되기때문에 65~80%로 형성함이 바람직하다.In addition, when the kraft paper layer, the printed pattern layer and the protective layer are stacked, the protective layer is thinner than the printed pattern layer, so that the mixture of melamine resin and the aroma stock solution is formed thicker than when the kraft paper layer and the printed pattern layer are laminated. When the mixed solution of the melamine resin and the aroma stock solution is applied at less than 65% of the weight of the printed pattern paper, the coating layer is formed so thin that the protection of the printed pattern paper is not easy, and when the coating layer is applied at an amount exceeding 80%, It is preferable to form 65 to 80% because it is formed unnecessarily thick.
또한, 상기 크라프트지층과 인쇄무늬지층이 적층된 경우나 상기 크라프트지층과 인쇄무늬지층 및 보호지층이 적층된 경우에 가열 압착 조건은 125~130℃, 45~65kg/㎠으로 가열 압착하되, 유지시간 20~25분, 냉각시간20~30분을 행하여 제조함이 바람직하다.In addition, in the case where the kraft paper layer and the printed patterned paper layer are laminated or when the kraft paper layer, the printed patterned paper layer and the protective paper layer are laminated, the heat compression conditions are heat-compressed at 125 to 130 ° C. and 45 to 65 kg / cm 2. It is preferable to carry out 20-25 minutes and 20-30 minutes of cooling time, and to manufacture.
이와 같은 본 발명의 화장판을 빌딩, 사무실, 호텔, 점포, 주택, 아파트 등의 내장재나 기타 가구 제작 등에 사용하는 경우에 화장판의 상부층(도 1의 인쇄무늬지층, 도 2의 보호지층)에 포함되어 있는 천연 아로마 성분에 의해 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등의 인체 유익을 제공하게 되는 것이다.In the case of using the decorative plate of the present invention such as building materials, offices, hotels, stores, houses, apartments, or other furniture production, the upper layer of the decorative plate (printed pattern layer of FIG. 1, protective layer of FIG. 2) The natural aroma components included will provide benefits to the human body, such as learning concentration, dry skin care or when you can't sleep, relieving anxiety and stress.
또한, 본 발명은 상기한 본 발명의 화장판(100)을 도 3 및 도 4에 도시된 바와 같이 합판이나 MDF와 같은 판재(40) 상부에 접착하여 마루판(200)을 제공하는 것이다.In addition, the present invention is to provide a
즉, 도 3에서와 같이 크라프트지(Kraft paper)를 페놀수지에 함침 건조한 크라프트지층(10-1) 상부에 인쇄무늬가 인쇄된 인쇄무늬지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%를 혼합한 혼합액에 함침하되, 상기 혼합액이 인쇄무늬지의 무게 대비 45~60% 도포되도록 함침처리하여 건조한 인쇄무늬지층(20-1)을 2층 구조로 적층하여 가열 압착 형성한 화장판을 합판이나 MDF와 같은 판재(40) 상부에 접착 형성하는 것이다.That is, as shown in Figure 3 kraft paper (impregnated) kraft paper (phenol paper) impregnated with a phenolic resin, the printed patterned paper on which the printed pattern is printed on the dried kraft paper layer (10-1) 99.7 ~ 99.9% by weight of the aromatic stock solution 0.3 ~ 0.1 weight Impregnated in the mixed solution mixed with%, impregnated so that the mixture is applied to 45 ~ 60% of the weight of the printed pattern paper, laminated dry printed pattern paper layer (20-1) in a two-layer structure laminated plywood formed by heat compression Or to form an adhesive on the
또한, 도 4에서와 같이 크라프트지(Kraft paper)와 인쇄무늬지를 페놀수지에 함침 건조한 크라프트지층(10-2)과 인쇄무늬지층(20-2) 상부에 보호지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%을 혼합한 혼합액에 함침하되, 상기 혼합액이 보호지의 무게 대비 65~80% 도포되도록 함침처리하여 건조한 보호지층(30-2)을 3층 구조로 적층하여 가열 압착 형성한 화장판을 합판이나 MDF와 같은 판재(40) 상부에 접착 형성하는 것이다.In addition, as shown in Figure 4 kraft paper and printed pattern paper impregnated with phenolic resin in the kraft paper layer (10-2) and the printed patterned layer (20-2), the protective paper on the melamine resin 99.7 ~ 99.9 weight% It was impregnated into the mixed solution mixed 0.3 ~ 0.1% by weight of the aroma stock solution, the impregnating treatment so that the mixed solution is applied to 65 ~ 80% of the weight of the protective paper by laminating a dry protective paper layer (30-2) in a three-layer structure formed by heat compression The decorative plate is to form an adhesive on the
이때, 상기 크라프트지층과 인쇄무늬지층을 적층한 화장판을 합판이나 MDF와 같은 판재(40) 상부에 접착하는 경우에 접착 조건은 160~180℃, 14~22kg/㎠으로 가 열 압착하되, 유지시간 30~50초로 행하여 제조하고, 상기 크라프트지층과 인쇄무늬지층 및 보호지층을 적층한 화장판을 합판이나 MDF와 같은 판재(40) 상부에 접착하는 경우에 접착 조건은 상온에서 4~7kg/㎠으로 압착하되, 유지시간 2시간으로 행하여 제조함이 바람직하다.At this time, in the case of adhering the kraft paper layer and the printed pattern paper layer laminated on the
이와 같이 본 발명의 화장판을 이용한 마루판(200)을 제조하여 상기 마루판을 이용하여 실내 마루를 제조 사용하는 경우에 상기 화장판의 상부층에 포함되어 있는 천연 아로마 성분에 의해 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등의 인체 유익 등을 제공하게 되는 것이다.As such, when manufacturing the
또한, 본 발명은 상기한 본 발명의 화장판(100)을 도 5에 도시된 바와 같이 파티클 보드(50) 상부에 접착하여 마감판(300)을 제공하는 것이다.In addition, the present invention is to provide a
즉, 크라프트지(Kraft paper)를 페놀수지에 함침 건조한 크라프트지층(10-1) 상부에 인쇄무늬가 인쇄된 인쇄무늬지를 멜라민수지 99.7 ~99.9 중량%에 아로마 원액 0.3~0.1 중량%를 혼합한 혼합액에 함침하되, 상기 혼합액이 인쇄무늬지의 무게 대비 45~60% 도포되도록 함침처리하여 건조한 인쇄무늬지층(20-1)을 2층 구조로 적층하여 가열 압착 형성한 화장판을 파티클 보드(50) 상부에 접착 형성하는 것이다.That is, a mixed solution in which 99.7 to 99.9% by weight of aroma stock solution was mixed with 99.7 to 99.9% by weight of a melamine resin with a printed pattern on which kraft paper was impregnated with phenolic resin and dried on the kraft paper layer 10-1. Impregnated in, but the impregnated treatment so that the mixed solution is applied to 45 ~ 60% of the weight of the printed pattern paper by drying the printed pattern paper layer (20-1) in a two-layer structure to form a heating plate compression plate formed on the top of the particle board (50) To form a bond to.
이때, 상기 크라프트지층과 인쇄무늬지층을 적층한 화장판을 파티클 보드(50) 상부에 접착하는 경우에 접착 조건은 160~180℃, 14~22kg/㎠으로 가열 압착하되, 유지시간 30~50초로 행하여 제조함이 바람직하다.At this time, in the case of adhering the kraft paper layer and the printed plate laminated layer laminated on the
이와 같이 본 발명의 화장판을 이용한 마감판(300)을 제조하여 상기 실내 벽 면이나 천정 등의 마감재로 사용하는 경우에 상기 화장판의 상부층에 포함되어 있는 천연 아로마 성분에 의해 학습 집중, 건조 피부관리나 잠이 안올때, 불안, 스트레스 해소 등의 인체 유익 등을 제공하게 되는 것이다.As described above, when the
도 1 및 도 2는 본 발명 화장판의 실시 예를 보여주는 단면도.1 and 2 is a cross-sectional view showing an embodiment of the present invention decorative plate.
도 3 및 도 4는 본 발명 화장판을 이용한 마루판의 실시 예를 보여주는 단면도.3 and 4 is a cross-sectional view showing an embodiment of the floorboard using the present invention decorative plate.
도 5는 본 발명 화장판을 이용한 마감판의 실시 예를 보여주는 단면도.Figure 5 is a cross-sectional view showing an embodiment of the finish plate using the present invention decorative plate.
**도면의 주요 부분에 대한 부호의 설명**** Description of the symbols for the main parts of the drawings **
10-1,10-2: 크라프트지층10-1,10-2: Kraft Strata
20-1,20-2: 인쇄무늬지층20-1,20-2: Printed patterned layer
30-2: 보호지층30-2: protective layer
40: 판재40: plate
50: 파티클 보드50: Particle Board
100: 화장판100: makeup plate
200: 마루판200: floorboard
300: 마감판300: finish plate
Claims (5)