KR101041415B1 - Fabric with improved flexibility of chemical protecting cloth - Google Patents

Fabric with improved flexibility of chemical protecting cloth Download PDF

Info

Publication number
KR101041415B1
KR101041415B1 KR1020110001251A KR20110001251A KR101041415B1 KR 101041415 B1 KR101041415 B1 KR 101041415B1 KR 1020110001251 A KR1020110001251 A KR 1020110001251A KR 20110001251 A KR20110001251 A KR 20110001251A KR 101041415 B1 KR101041415 B1 KR 101041415B1
Authority
KR
South Korea
Prior art keywords
fabric
adhesive
protective clothing
activated carbon
chemical
Prior art date
Application number
KR1020110001251A
Other languages
Korean (ko)
Inventor
강재성
서현관
Original Assignee
삼양화학공업주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼양화학공업주식회사 filed Critical 삼양화학공업주식회사
Priority to KR1020110001251A priority Critical patent/KR101041415B1/en
Application granted granted Critical
Publication of KR101041415B1 publication Critical patent/KR101041415B1/en

Abstract

PURPOSE: Fabric for chemical protective clothing with improved flexibility is provided to prevent coating phenomenon and to enable a user to feel a comfort. CONSTITUTION: Fabric for chemical protective clothing comprises: support cloth(11) which is made of woven fabric in order to protect the human body from external chemical toxic material and in which adhesive is spread on the surface thereof; an adsorption layer which is adhered to the support cloth and consists of bead type activated charcoal capable of adsorbing chemical toxic material; and cover cloth(17) on which polyamide adhesive is spread in an amount of 5-15g/m^2 in order to fix bead type activated charcoal.

Description

유연성이 개선된 화학방호복용 원단{fabric with improved flexibility of chemical protecting cloth} Fabric with improved flexibility of chemical protecting cloth

본 발명은 화학방호복용 원단에 관한 것으로서, 보다 상세하게는 활동성이 향상되고 활성탄의 이탈을 방지하여 독성 화학물질에 대한 방호성능이 향상되는 유연성이 개선된 화학방호복용 원단에 관한 것이다. The present invention relates to a fabric for chemical protective clothing, and more particularly, to a chemical protective clothing fabric having improved flexibility, which improves the activity and prevents the release of activated carbon to improve the protection performance against toxic chemicals.

현대전에서 대량 살상무기의 개발과 보유국가가 증가함에 따라 인체나 장비를 보호할 수 있는 제품들이 요구되고 있다. 상기 대량 살상무기 중 화학무기는 생산비용이 저가이며, 소형화된 제조설비로 빠른 시간 내에 대량 생산이 가능하고 상대적으로 관리 취급이 용이함과 동시에 위협도가 매우 크다. With the development and possession of weapons of mass destruction (WMD) in modern warfare, products that can protect the human body or equipment are required. Among the weapons of mass destruction, chemical weapons are low in production cost, and can be mass-produced in a short time with a miniaturized manufacturing facility, and are relatively easy to manage and handle, and have a great threat.

이에 따라, 인체를 보호할 수 있는 각종 보호 장비들, 예컨대 화학 보호복 및 방독면 등이 요구되고 있으며, 일반적으로 화학 보호복의 종류에는 공기의 통기성으로 구분하여 크게 통기성 보호복 및 불통기성 보호복으로 나뉠 수 있다. Accordingly, various protective equipments for protecting the human body are required, such as chemical protective clothing and gas masks. In general, chemical protective clothing is classified into breathable protective clothing and non-breathable protective clothing. Can be divided.

그리고, 상기 화학 보호복은 유독성 화학물질의 오염 지역을 회피하거나 작전을 수행할 때 인체에서 발산된 열이 보호복 내부에 축적되어 활동성을 둔화시키는 열적 스트레스를 고려하여 현재 세계 각국에서는 통기성 보호복을 위주로 개발하고 적용되고 있다. In addition, the chemical protective clothing is a breathable protective clothing currently in various countries in the world in consideration of the thermal stress that the heat emitted from the human body accumulates inside the protective clothing when the operation is avoided or the operation of the contaminated area of toxic chemicals is performed. It is mainly developed and applied.

또한, 통상적으로 유독성 화학물질에 지역이 오염되면 증기상의 유독물질이 인체에 직접적인 영향을 준다고 여겼기 때문에 상기 통기성 보호복에서는 증기상 작용제를 흡착하여 걸러낼 수 있는 활성탄이 포함된 원단과 그 위에 위장성능을 부여한 원단을 적용한 이중 구조를 채택하고 있다. In addition, in general, when the area is contaminated with toxic chemicals, it is considered that vapor toxic substances have a direct effect on the human body, so the breathable protective clothing has a fabric containing activated carbon that can adsorb and filter out vapor phase agents and gastrointestinal performance thereon It adopts the double structure that applied the cloth which I gave.

여기서, 상기 활성탄이 포함된 원단, 즉 증기상 가스 필터 여과 직물은 대부분 활성탄이 침적되거나 코팅된 직물을 이용하고 있다. 이것을 상기 화학 보호복에서는 내피(inner fabric)라고 통칭하고 있다. Here, the fabric containing the activated carbon, that is, the vapor gas filter filtration fabric is mostly using a fabric in which activated carbon is deposited or coated. This chemical protective clothing is commonly referred to as inner fabric.

그리고, 상기 내피는 통상 지지원단, 활성탄 및 커버원단이 적층된 구조로 되어 있다. 또한, 상기 내피의 일반적인 제작 공정은 다음과 같다. 먼저, 상기 지지원단에 접착제를 전사한 후 활성탄 층을 부착하고, 상기 부착된 활성탄 층에 접착제가 도포되어 있는 상기 커버원단을 결합한다. In addition, the endothelial has a structure in which a support fabric, an activated carbon, and a cover fabric are usually laminated. In addition, the general manufacturing process of the endothelium is as follows. First, the adhesive is transferred to the support fabric, and then an activated carbon layer is attached, and the cover fabric having an adhesive applied to the attached activated carbon layer is combined.

이에 따라, 상기 지지원단, 상기 활성탄, 상기 커버원단 및 상기 접착제 등 서로 다른 물질들이 적층됨에 따라 최종 제품의 강연도(stiffness)는 현격하게 상승하게 된다. 그러므로, 상기 화학 보호복의 착용 시 불편함을 느끼게 되고, 일반적인 전투 활동 시에도 상기 지지원단에 부착되어 있는 상기 활성탄의 이탈이 발생하게 된다. 특히, 기온이 저온으로 내려갈 경우 상기 내피를 가공할 때 적용되는 접착제가 급속히 경화되어 섬유의 강직도가 증가됨에 따라 상기 활성탄의 이탈 및 활동의 부자연스러움은 더욱 증가된다. Accordingly, as the support material, the activated carbon, the cover fabric, and the adhesive are stacked with different materials, the stiffness of the final product is significantly increased. Therefore, discomfort is felt when the chemical protective clothing is worn, and detachment of the activated carbon, which is attached to the support fabric, occurs during general combat activities. In particular, when the temperature decreases to a low temperature, as the adhesive applied when processing the endothelial is rapidly cured and the rigidity of the fiber is increased, the release of the activated carbon and the unnaturalness of the activity are further increased.

즉, 상기 화학 보호복은 활동 시에 방호성능을 유지하는 것도 중요 인자 중의 하나이지만 활동성이 보장되어야만 효과적인 작전을 수행할 수 있다. 특히, 착용 후 활동 시 방호성능을 유지하기 위해서는 사기 내피에 부착된 흡착 소재가 이탈되지 않아야 하며, 제품의 유연성이 낮아짐으로 인하여 인체의 체열 상승율을 높여 착용 후 활동성이 저하되지 않아야 한다. In other words, the chemical protective clothing is one of the important factors to maintain the protective performance at the time of activity can be effective operation only if the activity is guaranteed. In particular, in order to maintain the protective performance during the activity after wearing, the adsorbent material attached to the fraudulent endothelium should not be released, and due to the low flexibility of the product, the body's heat rise rate should not be increased and the activity after wearing should not be reduced.

그러나, 종래의 제품에서는 상기 화학 보호복의 내피의 유연성을 간과하여 상기 활성탄이 이탈되거나 제품의 유연성이 저하되어 결국 방호성능의 저하 및 체열을 증가시킴으로써 착용 후의 활동성이 저하되는 문제점이 있었다. However, in the conventional products, the flexibility of the endothelial of the chemical protective clothing is overlooked, and the activated carbon is released or the flexibility of the product is lowered, resulting in deterioration of protection performance and increased body heat, thereby deteriorating activity after wearing.

상기와 같은 문제점을 해결하기 위하여, 본 발명은 활동성이 향상되고 활성탄의 이탈을 방지하여 독성 화학물질에 대한 방호성능이 향상되는 유연성이 개선된 화학방호복용 원단을 제공하는 것을 해결과제로 한다. In order to solve the above problems, the present invention is to provide a chemical protective clothing fabric improved in the activity of improving activity and preventing the escape of activated carbon to improve the protective performance against toxic chemicals.

상기의 과제를 해결하기 위해서, 본 발명은 외부의 화학성 독성물질로부터 인체가 보호되도록 직조된 직물로 이루어지되, 유리전이온도가 -45~-5 ℃이며 점도가 3,000~11,000 mPas인 습기경화형 폴리우레탄 일액형 접착제로 이루어진 부착용 접착제가 일측 표면에 30~80 g/㎡의 점착량으로서 도트형으로 도포된 지지원단; 상기 부착용 접착제에 의해 상기 지지원단에 접착되며, 상기 화학성 독성물질이 흡착되는 구슬형 활성탄으로 이루어진 흡착층; 및 상기 흡착층에 적층되어 상기 구슬형 활성탄이 고착되도록 폴리아미드 일액형 접착제로 이루어진 고착용 접착제가 5~15 g/㎡의 점착량으로 도포된 커버원단을 포함하여 이루어지는 유연성이 개선된 화학방호복용 원단을 제공한다. In order to solve the above problems, the present invention consists of a woven fabric to protect the human body from external chemical toxic substances, the glass transition temperature is -45 ~-5 ℃ moisture viscosity polyurethane of 3,000 ~ 11,000 mPas A support fabric in which the adhesive for attachment consisting of a one-component adhesive is applied in a dot shape as an adhesive amount of 30 to 80 g / m 2 on one surface; An adsorption layer adhered to the support fabric by the attachment adhesive and made of bead-type activated carbon to which the chemical toxic substances are adsorbed; And a cover fabric laminated on the adsorption layer, and a cover fabric coated with a polyamide one-component adhesive such that the bead activated carbon is fixed at an adhesive amount of 5 to 15 g / m 2. Provide fabric.

여기서, 상기 부착용 접착제는 0.6~1 mm 직경의 도트가 0.02~0.4 mm의 간격을 이루도록 도트형으로 도포되며, 상기 구슬형 활성탄의 직경은 0.2~0.7 mm로 이루어짐이 바람직하다. Here, the adhesive for adhesive is applied in a dot shape so that the dot of 0.6 ~ 1 mm diameter forms a 0.02 ~ 0.4 mm, the diameter of the bead-shaped activated carbon is preferably made of 0.2 ~ 0.7 mm.

그리고, 상기 지지원단은 굵기 10~90 denier인 복합원사로 이루어지며, 상기 지지원단의 밀도는 경사 80~150 올/5cm 및 위사 70~130 올/5cm로 이루어짐이 바람직하다. In addition, the support fabric is made of a composite yarn having a thickness of 10 ~ 90 denier, the density of the support fabric is preferably made of inclined 80 ~ 150 ol / 5 cm and weft 70 ~ 130 ol / 5 cm.

또한, 상기 커버원단은 경위사의 방향성이 없는 부직물 및 50~100 수로 이루어진 면직물을 포함하는 그룹 중 선택된 직물로 이루어짐이 바람직하다. In addition, the cover fabric is preferably made of a fabric selected from the group comprising a non-woven fabric and a cotton fabric consisting of 50 to 100 non-directional weft yarns.

삭제delete

상기의 해결 수단을 통해서, 본 발명의 유연성이 개선된 화학방호복용 원단은 다음과 같은 효과를 제공한다. Through the above solution, the chemical protective clothing fabric improved flexibility of the present invention provides the following effects.

첫째, 본 발명에 따른 유연성이 개선된 화학방호복용 원단은 부착용 접착제를 일정한 간격을 가진 도트형으로 도포함으로써 원단에 접착제가 부착된 후에도 코팅현상이 일어나지 않아 유연성이 증가되어 완성된 화학방호복의 착용감이 향상되며 인체의 활동성이 현저히 증대될 수 있다. First, the chemical protective clothing fabric with improved flexibility according to the present invention by applying the adhesive adhesive in a dot shape with a predetermined interval does not occur even after the adhesive is attached to the fabric coating does not increase the flexibility to wear the finished chemical protective clothing It can be improved and the activity of the human body can be significantly increased.

둘째, 부착용 접착제의 유리전이온도를 급격히 낮춤에 따라 저온에서도 원단의 유연성이 확보되어 상기 원단의 굽힘으로 인해 활성탄이 이탈되는 것을 방지하여 방호성능이 현저히 향상될 수 있다. Secondly, as the glass transition temperature of the adhesive is sharply lowered, the flexibility of the fabric is ensured even at low temperatures, thereby preventing the activated carbon from being released due to the bending of the fabric, thereby significantly improving the protection performance.

셋째, 지지원단의 직조 시에 복합원사를 경사 및 위사에 걸쳐 고밀도로 직조함으로써 원단이 조밀하게 형성됨에 따라 접착제가 섬유 사이에 스며들어 숙성 시 굳어짐을 방지하므로 상기 원단의 유연성을 더욱 향상될 수 있다. Third, as the fabric is densely formed by weaving the composite yarn at high density across the warp and weft yarns during the weaving of the support fabric, the adhesive penetrates between the fibers to prevent hardening during aging, thereby further improving the flexibility of the fabric. .

도 1은 본 발명의 바람직한 실시예에 따른 유연성이 개선된 화학방호복용 원단을 나타낸 단면도.
도 2는 본 발명의 바람직한 실시예에 따른 지지원단에 도포된 부착용 접착제를 나타낸 평면도.
도 3은 본 발명의 바람직한 실시예에 따른 유연성이 개선된 화학방호복용 원단의 제작 과정을 나타낸 흐름도. 1 is a cross-sectional view showing a fabric for improved chemical protective clothing according to a preferred embodiment of the present invention.
Figure 2 is a plan view showing the adhesive adhesive applied to the support fabric according to a preferred embodiment of the present invention.
Figure 3 is a flow chart showing the manufacturing process of improved chemical protective clothing fabric in accordance with a preferred embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 따른 유연성이 개선된 화학방호복용 원단을 상세히 설명한다. Hereinafter, with reference to the accompanying drawings will be described in detail the fabric for improved chemical protective clothing according to a preferred embodiment of the present invention.

여기서, 상기 화학방호복은 외부의 화학성 독성물질을 흡착하여 걸러낼 수 있는 흡착층이 형성된 원단 및 그 위에 위장성능을 부여한 원단을 적용한 이중 구조로 이루어지며, 본 발명에 따른 유연성이 개선된 화학방호복용 원단은 상기 흡착층이 형성된 원단으로 이해함이 바람직하다. Here, the chemical protective suit is made of a double structure applying a fabric having an adsorption layer formed to adsorb the external chemical toxic substances, and the fabric imparted camouflage performance thereon, for improved chemical protective clothing according to the present invention The fabric is preferably understood to be the fabric on which the adsorption layer is formed.

즉, 본 발명에 따른 유연성이 개선된 화학방보복용 원단에 상기 위장성능을 부여한 원단을 결합하여 적용함으로써 상기 화학방호복이 완성되어 이루어질 수 있다. That is, the chemical protective clothing can be completed by applying a combination of the fabric imparting the camouflage performance to the chemical protective clothing for improved flexibility according to the present invention.

도 1은 본 발명의 바람직한 실시예에 따른 유연성이 개선된 화학방호복용 원단(10)을 나타낸 단면도이다. 1 is a cross-sectional view showing a fabric 10 for improved chemical protective clothing according to a preferred embodiment of the present invention.

도 1에서 보는 바와 같이, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)은 지지원단(11), 흡착층 및 커버원단(17)을 포함하여 이루어진다. 여기서, 상기 지지원단(11)은 직조 혹은 편직된 직물로 이루어지되, 일측 표면에 30~80 g/㎡의 접착량의 저온형 유리전이온도를 가진 부착용 접착제(13)가 도트형으로 도포되어 이루어진다. As shown in FIG. 1, the fabric 10 for improved chemical protective clothing according to the present invention includes a support fabric 11, an adsorption layer, and a cover fabric 17. Here, the support fabric 11 is made of a woven or knitted fabric, the adhesive is attached to the surface of the adhesive 13 having a low-temperature glass transition temperature of 30 ~ 80 g / ㎡ of adhesion amount on one surface .

상세히, 상기 지지원단(11)의 직조형태는 니트형, 평직형 및 능직형 등으로 이루어질 수 있으나, 본 발명에서는 기본적인 유연성을 고려하여 니트형이 바람직하다. 또한, 상기 지지원단(11)은 상기 부착용 접착제(13)가 도포되는 일측 표면은 평활한 구조로 직조됨이 바람직하다. In detail, the woven form of the support fabric 11 may be made of a knit type, a plain weave type and a twill type, but in the present invention, a knit type is preferable in consideration of basic flexibility. In addition, the support fabric 11 is preferably one side surface to which the attachment adhesive 13 is applied is woven into a smooth structure.

그리고, 접착제 도포 장비에 거치 시 경사 방향으로 신축성이 부과될 경우 상기 직물의 섬유 간격이 벌어지게 되므로 신축성이 없는 형태로 직조되어야 한다. 왜냐하면, 직물의 섬유간격이 벌어진 상태로 상기 부착용 접착제(13)가 도포되면 섬유 사이로 상기 부착용 접착제(13)가 스며들어가 강연도를 높이는 결과를 초래하기 때문이다. In addition, when the elasticity is applied in the inclined direction when mounted on the adhesive coating equipment, since the fiber spacing of the fabric is opened, it must be woven in a form without elasticity. This is because, when the adhesive adhesive 13 is applied in a state in which the fiber spacing of the fabric is opened, the adhesive adhesive 13 penetrates between the fibers, resulting in an increase in the ductility.

또한, 상기 저온형 유리전이온도를 가진 부착용 접착제(13)는 30~80 g/㎡으로 도포됨이 바람직한데, 그의 점착량이 30 g/㎡ 미만이 되면 후술하는 상기 흡착층의 구슬형 활성탄(15)의 접착성이 떨어지게 되며, 80 g/㎡을 초과하여 도포되면 비연속적으로 도포된 접착제들이 서로 연결고리를 형성하여 막이 만들어짐으로써 상기 지지원단(11)의 유연성이 현격히 떨어지게 된다. In addition, the low temperature-type glass transition temperature of the adhesive adhesive 13 is preferably applied at 30 ~ 80 g / ㎡, when the adhesion amount is less than 30 g / ㎡ bead-type activated carbon (15) of the adsorption layer to be described later ), The adhesiveness is reduced, and when applied in excess of 80 g / ㎡ is applied to the discontinuously applied adhesives to form a connection to each other film is made, the flexibility of the support fabric 11 is significantly reduced.

여기서, 상기 저온형 유리전이온도를 가진 부착용 접착제(13)란, 상기 화학방호복을 착용하고 영하의 온도에서 활동 시에 상기 온도에 의해 접착제가 굳어짐에 따라 상기 화학방호복이 뻣뻣해지는 것을 방지하기 위한 것으로 상기 유리전이온도를 낮춘 부착용 접착제(13)로 이해함이 바람직하다. Here, the adhesive for attaching the low temperature type glass transition temperature 13 is to prevent the chemical protective clothing from becoming stiff as the adhesive hardens by the temperature when the chemical protective clothing is worn and the activity is performed at sub-zero temperatures. It is preferable to understand the adhesive 13 for lowering the glass transition temperature.

한편, 상기 흡착층은 상기 부착용 접착제(13)에 의해 상기 지지원단(11)에 접착되며 상기 화학성 독성물질이 흡착되는 구슬형 활성탄(15)으로 이루어진다. 상세히, 상기 구슬형 활성탄(15)은 상기 화학방호복의 방호성능에 영향을 주는 주요 핵심 소재로서, 상기 부착용 접착제(13)의 도포 및 접착은 상기 구슬형 활성탄(15)의 표면 부분이 접착제에 의해 피복되지 않아야 하며 화학성 독성물질의 효과적인 흡착을 위해 주변 공기와 접촉 가능하도록 실행되어야 한다. On the other hand, the adsorption layer is made of bead-type activated carbon 15 is adhered to the support fabric 11 by the attachment adhesive 13 and the chemical toxic substances are adsorbed. In detail, the bead activated carbon 15 is a main material that affects the protective performance of the chemical protective suit, and the application and adhesion of the adhesive 13 is performed by the surface portion of the bead activated carbon 15 by an adhesive. It must be uncovered and implemented to allow contact with ambient air for effective adsorption of chemical toxicants.

그리고, 상기 커버원단(17)은 상기 흡착층에 적층되어 상기 구슬형 활성탄(15)이 고착되도록 고착용 접착제가 도트형으로 도포되어 이루어진다. 즉, 상기 커버원단(17)이 상기 흡착층에 적층됨으로써 본 발명에 따른 상기 화학방호복용 원단(10)을 이루고 상기 커버원단(17)에 상기 위장성능을 부여한 원단이 결합되어 상기 화학방호복이 완성될 수 있다. In addition, the cover fabric 17 is laminated on the adsorption layer is made of a fixing adhesive is applied in a dot shape so that the bead-shaped activated carbon 15 is fixed. That is, the cover fabric 17 is laminated on the adsorption layer to form the chemical protective clothing fabric 10 according to the present invention and the fabric fabric imparting the camouflage performance to the cover fabric 17 is combined to complete the chemical protective clothing Can be.

또한, 상기 고착용 접착제는 상기 부착용 접착제(13)와 같이 상기 구슬형 활성탄(15)의 표면 부분이 접착제에 의해 피복되지 않아야 하며 화학성 독성물질의 효과적인 흡착을 위해 주변 공기와 접촉 가능하도록 도포 및 접착됨이 바람직하다. In addition, the fixing adhesive may be coated and adhered such that the surface portion of the bead-shaped activated carbon 15, such as the adhesive adhesive 13, is not covered by the adhesive and is in contact with the surrounding air for effective adsorption of chemical toxic substances. Is preferred.

한편, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)의 지지원단(11)에는 상기 부착용 접착제(13)가 도트형으로 도포됨이 바람직한데, 그에 대하여 도 2를 참조하여 설명하면 다음과 같다. On the other hand, the support fabric 11 of the improved chemical protective clothing fabric 10 according to the present invention is preferably the adhesive adhesive 13 is applied in a dot shape, it will be described with reference to FIG. Is the same as

도 2는 본 발명의 바람직한 실시예에 따른 지지원단(11)에 도포된 부착용 접착제(13)를 나타낸 평면도이다. 2 is a plan view showing the adhesive adhesive 13 applied to the support fabric 11 according to a preferred embodiment of the present invention.

도 1 및 도 2에서 보는 바와 같이, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)의 상기 부착용 접착제(13)는 0.6~1 mm 직경의 도트가 0.02~0.4 mm의 간격을 이루는 도트형으로 상기 지지원단(11)에 도포됨이 바람직하다. As shown in Figures 1 and 2, the adhesive for the adhesive 13 of the improved chemical protective clothing fabric 10 according to the present invention is a dot of 0.6 ~ 1 mm diameter dot 0.02 ~ 0.4 mm intervals It is preferable to apply to the support fabric 11 in the form.

여기서, 상기 지지원단(11)에 상기 부착용 접착제(13)를 도포하는 형태는 도트형, 줄무늬형 및 격자형 등이 있는데, 이들 중에서 도트형으로 도포함이 바람직하다. 또한, 상기 지지원단(11)에 상기 부착용 접착제(13)를 도포 시 상기 도트의 간격을 0.02~0.4 mm로 하여 상기 부착용 접착제(13) 도트의 간격과 상기 구슬형 활성탄(15)의 접점이 교차하도록 조절하여 상기 구슬형 활성탄(15)이 치밀하게 부착되도록 하는 것이 바람직하다. Here, the form of applying the adhesive 13 for the attachment to the support fabric 11, there is a dot, stripe, lattice, etc., of which the dot is preferably included. In addition, when applying the adhesive adhesive 13 to the support fabric 11, the interval of the dot is 0.02 ~ 0.4 mm, the interval of the adhesive adhesive 13 dot and the contact point of the bead-shaped activated carbon 15 intersect. It is preferable that the bead activated carbon 15 is tightly attached so as to be adjusted.

예컨대, 상기 부착용 접착제(13) 도트의 간격이 0.02 mm 미만이 되면 상기 부착용 접착제(13) 간의 연결고리가 생겨 접착제 막층이 형성될 가능성이 높고, 상기 지지원단(11) 내에 상기 부착용 접착제(13)가 스며들어 강연도가 상승할 수 있다. 그리고, 상기 부착용 접착제(13) 도트의 간격이 0.4 mm를 초과하면 상기 구슬형 활성탄(15)이 부착되지 않은 빈 공간이 생겨 상기 화학방호복의 방호성능이 저하될 수 있다. For example, when the interval of the adhesive adhesive 13 dot is less than 0.02 mm, there is a high possibility that a connection ring between the adhesive adhesive 13 is formed, thereby forming an adhesive film layer, and the adhesive adhesive 13 in the support fabric 11 is formed. The saturation may rise as it permeates. In addition, when the interval of the dot of the adhesive adhesive 13 exceeds 0.4 mm, an empty space in which the bead-shaped activated carbon 15 is not attached may be formed, and the protective performance of the chemical protective suit may be reduced.

즉, 상기 부착용 접착제(13) 도포 간격을 0.02~0.4 mm로 유지하면 상기 지지원단(11)에 상기 부착용 접착제(13)를 도포한 후에도 코팅현상이 일어나지 않아 상기 지지원단(11)의 유연성이 유지될 수 있다. That is, if the application interval of the adhesive adhesive 13 is maintained at 0.02 to 0.4 mm, coating does not occur even after the adhesive 13 is applied to the support fabric 11, thereby maintaining the flexibility of the support fabric 11. Can be.

또한, 상기 구슬형 활성탄(15)은 가장 효과적인 흡착성능을 나타내기 위해서 직경이 0.2~0.7 mm로 이루어짐이 바람직한데, 상기 부착용 접착제(13)의 간격이 넓게 형성되면 상기 구슬형 활성탄(15)이 부착되지 않는 부분이 나올 수 있으며, 상기 간격이 좁게 형성되면 상기 지지원단(11) 자체에 접착제 막이 형성되어 상기 화학방호복용 원단(10)의 유연성이 현격히 저하될 수 있다. In addition, the bead activated carbon 15 is preferably made of 0.2 ~ 0.7 mm in diameter in order to exhibit the most effective adsorption performance, the bead activated carbon 15 is formed when the interval of the adhesive for attachment 13 is formed wide The non-attached portion may come out, and when the gap is narrow, an adhesive film is formed on the support fabric 11 itself, and thus the flexibility of the chemical protective clothing fabric 10 may be significantly reduced.

한편, 상기 지지원단(11)은 굵기 10~90 denier인 복합원사로 이루어지며, 상기 경사는 80~150 올/5cm의 밀도이고 상기 위사는 70~130 올/5cm의 밀도로 이루어짐이 바람직하다. On the other hand, the support fabric 11 is made of a composite yarn having a thickness of 10 ~ 90 denier, the inclination is preferably made of a density of 80 ~ 150 ool / 5cm and the weft yarn is a density of 70 ~ 130 ool / 5cm.

여기서, 상기 복합원사란 일반적으로 섬유의 제직 시에 단사 즉, 한 가닥이 한 올을 이루는 상태로 제직하면 기본 섬유의 유연성이 저하될 뿐만 아니라 원단으로 제직된 후에도 인열 및 인장강도가 떨어지게 되어 물리적 물성 저하를 초래하게 되므로 아주 가는 단원사를 꼬아서 만든 것이 복합원사이다. Here, the composite yarn is generally a single yarn, ie, one strand when weaving a fiber when weaving the fiber, not only the flexibility of the basic fiber is lowered but also the tear and tensile strength after weaving into the fabric physical properties Since it causes degradation, it is a composite yarn made by twisting very thin single yarn.

그리고, 상기 복합원사를 10~90 denier의 굵기로 형성하는 이유는 상기 복합원사의 굵기가 10 denier 미만으로 되면 상기 화학방호복용 원단(10)의 제조 시 상기 부착용 접착제(13)가 스며들게 되고, 90 denier를 초과하게 되면 상기 화학방호복용 원단(10) 자체의 유연성이 현격히 떨어지게 된다. The reason for forming the composite yarn with a thickness of 10 to 90 denier is that when the thickness of the composite yarn is less than 10 denier, the adhesive adhesive 13 is impregnated when the chemical protective clothing fabric 10 is manufactured. When the denier is exceeded, the flexibility of the chemical protective clothing fabric 10 itself is significantly reduced.

또한, 상기 경사는 직물을 짤 때 세로방향으로 놓인 실이며, 상기 위사는 가로방향으로 놓인 실로 상기 경사 및 상기 위사의 밀도에 따라 상기 화학방호복용 원단(10)의 신축성이 좌우될 수 있다. In addition, the inclination is a yarn placed in the longitudinal direction when weaving the fabric, the weft yarn is a yarn laid in the transverse direction can be stretched depending on the inclination and the density of the weft weft fabric 10 for the chemical protective clothing.

여기서, 상기 경사 및 상기 위사의 밀도가 낮을 경우에는 상기 부착용 접착제(13)를 상기 지지원단(11)에 도포 시에 상기 부착용 접착제(13)가 섬유 사이를 침투하여 숙성 시 굳어지게 됨으로써 상기 화학방호복용 원단(10)의 유연성이 저하될 수 있으며, 밀도가 높아져도 상기 화학방호복용 원단(10)의 유연성이 떨어질 수 있다. Here, when the warp and the weft density is low, when the adhesive adhesive 13 is applied to the support fabric 11, the adhesive 13 penetrates between the fibers and hardens during aging, thereby protecting the chemical. The flexibility of the taking fabric 10 may be lowered, and even if the density is increased, the flexibility of the chemical protective garment 10 may be reduced.

한편, 상기 커버원단(17)은 경위사의 방향성이 없는 부직물 및 50~100 수로 이루어진 면직물을 포함하는 그룹 중 선택된 직물로 이루어짐이 바람직하다. On the other hand, the cover fabric 17 is preferably made of a fabric selected from the group comprising a nonwoven fabric and a cotton fabric consisting of 50 to 100 non-directional weft yarns.

상세히, 상기 커버원단(17)은 상기 고착용 접착제가 도포되어 최종적으로 상기 구슬형 활성탄(15)을 고착시키는 역할을 하며 상기 커버원단(17) 위에 상기 위장성능을 부여한 원단을 덮어 상기 화학방호복이 제작되는데, 이를 착용하여 활동할 경우 움직임에 의한 마찰로 인해 상기 구슬형 활성탄(15)의 손상을 최소로 줄일 수 있다. In detail, the cover fabric 17 serves to secure the bead-type activated carbon 15 by applying the fixing adhesive and to cover the fabric to which the camouflage performance is imparted on the cover fabric 17. It is manufactured, when it is worn and active to reduce the damage of the bead-shaped activated carbon (15) due to the friction caused by the movement.

또한, 상기 커버원단(17)도 상기 화학방호복용 원단(10)의 유연성에 지대한 미치게 됨에 따라 경사 및 위사의 방향성이 없는 부직물 및 가는 면직물로 제직된 직물을 덮어주게 된다. In addition, the cover fabric 17 also covers the fabric woven with a non-woven fabric and a thin cotton fabric with no direction of warp and weft as it extends to the flexibility of the chemical protective clothing fabric (10).

여기서, 상기 면직물은 50~100 수로 이루어짐이 바람직한데, 상기 면직물의 수란 1 inch의 넓이에 교차되어 있는 경사 및 위사의 수로서 가로 및 세로 2.54 cm의 넓이에 얼마나 많은 수의 실이 교차되어 있는지를 표시하는 단위로 이해함이 바람직하다. Here, the cotton fabric is preferably made of 50 to 100, the number of the cotton fabric is the number of warp and weft that intersect the width of 1 inch how many threads are crossed in the width and width of 2.54 cm width. It is preferable to understand by the unit to display.

그리고, 상기 면직물의 수가 50 수 미만이 되면 상기 커버원단(17)의 굵기가 굵어져 상기 화학방호복용 원단(10)의 중량이 상승하게 되고, 상기 화학방호복용 원단(10)의 유연성 또한 급격히 저하될 수 있다. 또한, 상기 면직물의 수가 100 수를 초과하게 되면 경제적인 측면에서 비용이 많이 소요되게 되고 제직 또한 어려운 문제점이 있다. When the number of cotton fabrics is less than 50, the thickness of the cover fabric 17 is increased, and the weight of the chemical protective clothing fabric 10 is increased, and the flexibility of the chemical protective clothing fabric 10 is also sharply reduced. Can be. In addition, if the number of the cotton fabric exceeds 100, it takes a lot of cost in terms of economics, weaving also has a difficult problem.

한편, 상기 부착용 접착제(13)는 습기경화형 폴리우레탄 일액형 접착제가 바람직하며, 상기 고착용 접착제는 폴리아미드 일액형 접착제가 바람직하다. 여기서, 일액형 접착제는 유기용제를 사용하지 않고 열을 가하여 용융하여 접착함으로써 상기 구슬형 활성탄(15)의 성능 저하를 가져오지 않는 동시에 피부에 2차 자극이 없기 위한 목적으로 사용될 수 있다. On the other hand, the attachment adhesive 13 is preferably a moisture-curable polyurethane one-component adhesive, the fixing adhesive is preferably a polyamide one-component adhesive. Here, the one-component adhesive may be used for the purpose of not causing a decrease in the performance of the bead-shaped activated carbon 15 by applying heat and melting without applying an organic solvent and at the same time without secondary stimulation to the skin.

그리고, 상기 습기경화형 폴리우레탄 일액형 접착제는 3,000~11,000 mPas의 점도로 이루어짐이 바람직하며, 상온과 저온의 유연성을 동시에 고려하여 유리전이온도가 -45~-5 ℃로 인 것이 바람직하다. In addition, the moisture-curable polyurethane one-component adhesive is preferably made of a viscosity of 3,000 ~ 11,000 mPas, it is preferable that the glass transition temperature is -45 ~-5 ℃ in consideration of flexibility at room temperature and low temperature.

상세히, 상기 유리전이온도가 -45~-5 ℃인 습기경화형 폴리우레탄 일액형 접착제로 상기 지지원단(11)에 도포하였을 경우에는 상온에서는 상기 화학방호복의 유연성이 크게 차이가 나지 않는다. 그러나, 상기 유리전이온도가 -5 ℃를 초과하는 습기경화형 폴리우레탄 일액형 접착제일 경우 즉, 상기 유리전이온도가 0 ℃ 정도가 되면 저온 환경에서 상기 화학방호복을 착용 시 상기 화학방호복용 원단(10)의 유연성이 떨어져 섬유가 뻣뻣해지고 이에 따라 착용감이 떨어지게 된다. In detail, when the glass transition temperature is applied to the support fabric 11 with a moisture-curable polyurethane one-component adhesive having a temperature of −45 to −5 ° C., the flexibility of the chemical protective clothing is not significantly different at room temperature. However, when the glass transition temperature is a moisture-curable polyurethane one-component adhesive that exceeds -5 ℃, that is, the glass transition temperature is about 0 ℃ when the chemical protective clothing when wearing the chemical protective clothing fabric (10 ), The flexibility is reduced and the fibers are stiff, resulting in poor fit.

또한, 상기 화학방호복의 착용 후 활동 시에 인체에 움직임에 따른 섬유의 굽힘이 지속적으로 발생함에 따라 방호성능에 가장 중요한 소재인 상기 구슬형 활성탄(15)이 상기 화학방호복용 원단(10)으로부터 이탈될 수 있으며, 이에 따라, 상기 화학방호복용 원단(10)에 상기 구슬형 활성탄(15)의 기능이 떨어지는 부분이 생기게 되어 결국 방호성능이 저하될 수 있다. In addition, the bend activated carbon (15), which is the most important material for protection performance, is separated from the chemical protective clothing fabric (10) as the bending of the fiber according to the movement in the human body occurs continuously during the activity after wearing the chemical protective clothing. As a result, the chemical protective clothing fabric 10 may be a portion of the function of the bead-shaped activated carbon 15 is degraded, the protective performance may be reduced.

그리고, 상기 커버원단(17)에 도포되는 상기 고착용 접착제는 폴리아미드 일액형 접착제가 바람직한데, 그의 점착량은 5~15 g/㎡으로 도포됨이 바람직하다. In addition, the fixing adhesive applied to the cover fabric 17 is preferably a polyamide one-component adhesive, the amount of the adhesive is preferably applied at 5 ~ 15 g / ㎡.

아울러, 상기 폴리아미드 일액형 접착제의 유리전이온도는 상기 습기경화형 폴리우레탄 일액형 접착제보다 다소 높게 이루어질 수도 있다. 그 이유는, 상기 지지원단(11)의 상기 습기경화형 폴리우레탄 일액형 접착제는 30~80 g/㎡으로 많은 양이 도포되기 때문에 상기 습기경화형 폴리우레탄 일액형 접착제 간의 연결고리가 많이 형성되나, 상기 커버원단(17)의 상기 폴리아미드 일액형 접착제는 5~15 g/㎡으로서 큰 영향을 미치지 않기 때문이다. In addition, the glass transition temperature of the polyamide one-component adhesive may be made somewhat higher than the moisture-curable polyurethane one-component adhesive. The reason is that the moisture-curable polyurethane one-component adhesive of the support fabric 11 is 30 to 80 g / ㎡ because a large amount is applied, the connection between the moisture-curable polyurethane one-component adhesive is formed a lot, This is because the polyamide one-component adhesive of the cover fabric 17 is 5 to 15 g / m 2 and does not have a large influence.

여기서, 상기 폴리아미드 일액형 접착제의 점착량이 15 g/㎡를 초과하여 도포되면 상기 화학방호복용 원단(10)의 자체 중량이 상승하게 되고, 5 g/㎡ 미만으로 도포되면 접착되지 않는 부분이 발생함에 따라 상기 구슬형 활성탄(15)의 이탈이 발생할 수 있다. Here, when the adhesive amount of the polyamide one-component adhesive is applied in excess of 15 g / ㎡ the self-weight of the chemical protective clothing fabric 10 is increased, and when applied below 5 g / ㎡ occurs a non-adhesive part As the separation of the bead-shaped activated carbon 15 may occur.

한편, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)의 강연도와 착용 후 상기 구슬형 활성탄(15)의 이탈량을 각각 측정하는 실험을 실시하였고 그 결과가 표 1 내지 표 3과 같이 나타났다. 여기서, 상기 실험은 실험실 표준 조건에서 각각의 시편을 채취하여 약 24 시간 동안 방치한 후 섬유의 강연도 시험방법(KS K 0539, 켄딜레버 법)으로 실시하였으며, 시험 환경은 각각 상온(20 ℃) 및 저온(-25 ℃)에서 실시하였다. 상기 강연도란 뻣뻣함과 부드러움의 정도를 나타내는 것으로, 직물의 움직임에 대한 저항성 즉 유연한 정도를 평가하는 것으로 이해함이 바람직하다. On the other hand, the experiment was performed to measure the stiffness of the flexible protective chemical fabric 10 according to the present invention and the amount of departure of the bead-type activated carbon 15 after wearing and the results are shown in Table 1 to Table 3 appear. Here, the test was carried out by the method of testing the ductility of the fiber (KS K 0539, Kendilber method) after each specimen was taken under laboratory standard conditions and left for about 24 hours, and the test environment was at room temperature (20 ° C.). And low temperature (-25 ° C). The stiffness represents the degree of stiffness and softness, and it is preferable to understand the evaluation of resistance to fabric movement, that is, the degree of flexibility.

그리고, 상기 강연도 시험의 장비는 플렉소 미터를 사용하고, 상기 시험의 원리는 직사각형의 직물 시험편을 한쪽 끝이 경사진 플랫폼에 수평으로 된 부분에 받쳐 놓는다. 또한, 상기 시험편을 길이방향으로 움직여 들어가는 부분이 걸리도록 하고 자중에 따라 아래로 구부러지도록 한다. 상기 시험편의 끝이 플래폼을 지나 평평한 면에 닿았을 때 그리고 평면으로 각이 41.5 °보다 아래로 기울었을 때 상기 시험편의 구부러진 길이를 측정한다. 이때, 굴곡성은 상기 시험편의 구부러진 길이와 직물의 단위 면적당 중량으로부터 계산될 수 있다. And, the equipment of the ductility test uses a flexometer, and the principle of the test is to support a rectangular fabric test piece in a portion horizontal to one end inclined platform. In addition, the test piece is to be moved in the longitudinal direction to take the part and bend down according to its own weight. The bent length of the specimen is measured when the tip of the specimen passes the platform and touches a flat surface and when the angle is inclined below 41.5 ° in a plane. In this case, the flexibility may be calculated from the bent length of the test piece and the weight per unit area of the fabric.

표 1은 유리전이온도가 서로 다른 상기 부착용 접착제(13)를 사용하여 플렉스 강연도 및 상기 구슬형 활성탄(15)의 이탈량을 측정한 결과이다. Table 1 shows the results of measuring the flex stiffness and the amount of detachment of the bead-type activated carbon 15 using the adhesive 13 having different glass transition temperatures.

부착용 접착제
유리전이온도Adhesive
Glass transition temperature 시험 원단면
Trial fabric cotton
원단 방향
Fabric direction
플렉스 강연도 (cm-mg)Flex Lecture (cm-mg) 활성탄 이탈량
(g/벌)Activated Carbon Release
(g / bee) 상온 20 ℃Room temperature 20 ℃ 영하 25 ℃Minus 25 ℃
-5 ℃
-5 ℃

지지원단
Support
경사slope 36703670 1072410724
10.37
10.37 위사Weft 36723672 1385813858 커버원단
Cover fabric
경사slope 26232623 1056210562 위사Weft 90179017 1584415844
-32 ℃
-32 ℃
지지원단
Support
경사slope 21782178 39793979
4.59
4.59 위사Weft 32853285 51135113 커버원단
Cover fabric
경사slope 22092209 38063806 위사Weft 57325732 59775977
-45 ℃
-45 ℃

지지원단
Support
경사slope 18571857 26672667
2.17
2.17 위사Weft 19471947 25342534 커버원단
Cover fabric
경사slope 16551655 32403240 위사Weft 21642164 23462346

여기서, 상기 실험의 부착용 접착제(13)는 습기경화형 폴리우레탄 일액형 접착제를 사용하였으며, 상기 지지원단(11)은 니트형으로 직조되었다. 또한, 상기 부착용 접착제(13)는 유리전이온도가 -5 ℃, -32 ℃, -45℃인 3종류를 적용하고 도트형으로 도포하였으며, 상기 도트의 간격은 0.15 mm로 조정하였다. 그리고, 상기 부착용 접착제(13)의 점착량은 55 g/㎡으로 조정하였다. Here, the adhesive for attachment 13 of the experiment was used a moisture-curable polyurethane one-component adhesive, the support fabric 11 was woven into a knit type. In addition, the adhesion adhesive 13 was applied in three types of glass transition temperature of -5 ℃, -32 ℃, -45 ℃ was applied in a dot shape, the interval of the dot was adjusted to 0.15 mm. And the adhesion amount of the said adhesive agent 13 for attachment was adjusted to 55 g / m <2>.

표 1에서 보는 바와 같이, 상기 부착용 접착제(13)의 유리전이온도가 -45℃일 때, 상온 및 저온에서 상기 화학방호복용 원단(10)의 유연도가 증가되며 상기 구슬형 활성탄(15)의 이탈량이 줄어드는 것을 알 수 있다. As shown in Table 1, when the glass transition temperature of the adhesive adhesive 13 is -45 ℃, the flexibility of the chemical protective clothing fabric 10 at room temperature and low temperature is increased and the bead-type activated carbon 15 of It can be seen that the amount of departure is reduced.

또한, 표 2는 상기 표 1에서 유연성이 가장 우수하다고 판단되는 유리전이온도의 상기 부착용 접착제(13)를 각각 간격을 다르게 도포하여 플렉스 강연도 및 상기 구슬형 활성탄(15)의 이탈량을 측정한 결과이다. In addition, Table 2 is to measure the flex stiffness and the amount of detachment of the bead-type activated carbon (15) by applying different intervals to each of the adhesive for attachment 13 of the glass transition temperature which is determined to have the highest flexibility in Table 1 The result is.

부착용 접착제
도포 간격Adhesive
Application thickness 시험 원단면
Trial fabric cotton
원단 방향
Fabric direction
플렉스 강연도 (cm-mg)Flex Lecture (cm-mg) 활성탄 이탈량
(g/벌)Activated Carbon Release
(g / bee) 상온 20 ℃Room temperature 20 ℃ 영하 25 ℃Minus 25 ℃
0.01 mm
0.01 mm

지지원단
Support
경사slope 56715671 96219621
5.21
5.21 위사Weft 56965696 1123111231 커버원단
Cover fabric
경사slope 52215221 98029802 위사Weft 82148214 1324713247
0.15 mm
0.15 mm

지지원단
Support
경사slope 18571857 26672667
2.17
2.17 위사Weft 19471947 25342534 커버원단
Cover fabric
경사slope 16551655 32403240 위사Weft 21642164 23462346
0.5 mm
0.5 mm

지지원단
Support
경사slope 16351635 23152315
3.26
3.26 위사Weft 18161816 21322132 커버원단
Cover fabric
경사slope 16421642 28602860 위사Weft 22342234 22372237

여기서, 상기 실험의 부착용 접착제(13)는 유리전이온도가 -45℃인 습기경화형 폴리우레탄 일액형 접착제를 사용하였으며, 상기 지지원단(11)은 니트형으로 직조되었다. 또한, 상기 부착용 접착제(13)는 도트형으로 하여 55 g/㎡의 점착량으로 도포하였다. Here, the adhesive for the adhesive 13 of the experiment used a moisture-curable polyurethane one-component adhesive with a glass transition temperature of -45 ℃, the support fabric 11 was woven into a knit type. In addition, the said adhesive agent 13 for adhesion was made into the dot form, and was apply | coated with the adhesive amount of 55 g / m <2>.

표 2에서 보는 바와 같이, 상기 부착용 접착제(13)의 도포 간격이 0.15 mm일 때, 상온 및 저온에서 상기 화학방호복용 원단(10)의 유연도가 증가되며 상기 구슬형 활성탄(15)의 이탈량이 줄어드는 것을 알 수 있다. As shown in Table 2, when the application interval of the adhesive adhesive 13 is 0.15 mm, the flexibility of the chemical protective clothing fabric 10 is increased at room temperature and low temperature, and the amount of leaving of the bead-type activated carbon 15 is increased. You can see it shrinks.

한편, 표 3은 상기 표 1 및 상기 표 2에서 유연성이 가장 우수하며, 상기 구슬형 활성탄(15)의 이탈량이 적은 유리전이온도의 상기 부착용 접착제(13)를 각각 점착량을 다르게 도포하여 플렉스 강연도 및 상기 구슬형 활성탄(15)의 이탈량을 측정한 결과이다. On the other hand, Table 3 is the most excellent flexibility in Table 1 and Table 2, flex lecture by applying different amounts of adhesion to the adhesive 13 for the glass transition temperature of the less amount of detachment of the bead-type activated carbon 15, respectively Figure 2 shows the result of measuring the amount of separation of the bead activated carbon (15).

부착용 접착제
점착량Adhesive
Adhesive amount 시험 원단면
Trial fabric cotton
원단 방향
Fabric direction
플렉스 강연도 (cm-mg)Flex Lecture (cm-mg) 활성탄 이탈량
(g/벌)Activated Carbon Release
(g / bee) 상온 20 ℃Room temperature 20 ℃ 영하 25 ℃Minus 25 ℃
15 g/㎡
15 g / ㎡

지지원단
Support
경사slope 14251425 16841684
6.29
6.29 위사Weft 16271627 19531953 커버원단
Cover fabric
경사slope 14161416 18961896 위사Weft 13981398 19801980
55 g/㎡
55 g / ㎡

지지원단
Support
경사slope 18571857 26672667
2.17
2.17 위사Weft 19471947 25342534 커버원단
Cover fabric
경사slope 16551655 32403240 위사Weft 21642164 23462346
95 g/㎡
95 g / ㎡

지지원단
Support
경사slope 43264326 52695269
4.01
4.01 위사Weft 52145214 49854985 커버원단
Cover fabric
경사slope 36253625 47694769 위사Weft 38263826 50475047

여기서, 상기 실험의 부착용 접착제(13)는 유리전이온도가 -45℃인 습기경화형 폴리우레탄 일액형 접착제를 사용하였으며, 상기 지지원단(11)은 니트형으로 직조되었다. 또한, 상기 부착용 접착제(13)는 도트형으로 하여 상기 도트의 간격은 0.15 mm로 조정하였다. Here, the adhesive for the adhesive 13 of the experiment used a moisture-curable polyurethane one-component adhesive with a glass transition temperature of -45 ℃, the support fabric 11 was woven into a knit type. In addition, the said adhesive agent for attachment 13 was made into the dot form, and the space | interval of the said dot was adjusted to 0.15 mm.

표 3에서 보는 바와 같이, 상기 부착용 접착제(13)의 점착량이 55 g/㎡일 때, 상온 및 저온에서 상기 화학방호복용 원단(10)의 유연도가 증가되며 상기 구슬형 활성탄(15)의 이탈량이 줄어드는 것을 알 수 있다. As shown in Table 3, when the adhesion amount of the adhesive adhesive 13 is 55 g / ㎡, the flexibility of the chemical protective clothing fabric 10 is increased at room temperature and low temperature and the detachment of the bead-type activated carbon 15 It can be seen that the amount is reduced.

이에 따라, 표 1 내지 표 3의 결과로부터 유추하여 상기 부착용 접착제(13)의 유리전이온도가 -45 ℃, 도포된 상기 부착용 접착제(13)의 도트 간격이 0.15 mm, 상기 부착용 접착제(13)의 점착량이 55 g/㎡일 경우, 상온과 저온에서 상기 화학방호복용 원단(10)의 유연성이 현저히 증가되는 것을 확인할 수 있다. Accordingly, inferred from the results of Tables 1 to 3, the glass transition temperature of the adhesive agent 13 is -45 deg. C, the dot spacing of the adhesive agent 13 applied is 0.15 mm, and the adhesive agent 13 of the adhesive agent 13 When the adhesive amount is 55 g / ㎡, it can be seen that the flexibility of the chemical protective clothing fabric 10 is significantly increased at room temperature and low temperature.

결론적으로, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)은 상기 부착용 접착제(13)를 일정한 간격으로 도트형으로 도포함으로써 상기 지지원단(11)에 접착제가 부착된 후에도 코팅현상이 일어나지 않아 유연성이 증가되어 완성된 상기 화학방호복의 착용감이 향상되며 인체의 활동성이 현저히 증대될 수 있다. In conclusion, the chemical protective clothing fabric 10 having improved flexibility according to the present invention does not occur even after the adhesive is attached to the support fabric 11 by applying the attachment adhesive 13 in a dot shape at regular intervals. Do not increase the flexibility is improved wearing comfort of the completed chemical protective clothing and the activity of the human body can be significantly increased.

또한, 상기 부착용 접착제(13)의 유리전이온도를 급격히 낮춤에 따라 저온에서도 상기 지지원단(11)의 유연성이 확보되어 상기 지지원단(11)의 굽힘으로 인해 상기 구슬형 활성탄(15)이 이탈되는 것을 방지하여 상기 화학방호복의 방호성능이 현저히 향상될 수 있다.In addition, as the glass transition temperature of the adhesive 13 is rapidly lowered, the flexibility of the support fabric 11 is ensured even at low temperatures, and the bead-shaped activated carbon 15 is separated due to the bending of the support fabric 11. By preventing the protection performance of the chemical protective clothing can be significantly improved.

그리고, 상기 지지원단(11)의 직조 시에 복합원사를 경사 및 위사에 걸쳐 고밀도로 직조함으로써 상기 지지원단(11)이 조밀하게 형성됨에 따라 상기 부착용 접착제(13)가 섬유 사이에 스며들어 숙성 시 굳어짐을 방지하므로 상기 지지원단(11)의 유연성을 더욱 확보할 수 있다. In addition, when the support fabric 11 is densely formed by weaving the composite yarn at high density across the warp and the weft yarn during the weaving of the support fabric 11, the adhesive adhesive 13 penetrates between fibers and matures. Since it prevents the hardening, it is possible to further secure the flexibility of the support fabric (11).

한편, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)의 제작 과정을 도 3을 참조하여 설명하면 다음과 같다. On the other hand, the manufacturing process of the improved chemical protective clothing fabric 10 according to the present invention with reference to Figure 3 as follows.

도 3은 본 발명의 바람직한 실시예에 따른 유연성이 개선된 화학방호복용 원단(10)의 제작 과정을 나타낸 흐름도이다. 3 is a flow chart showing the manufacturing process of the improved chemical protective clothing fabric 10 in accordance with a preferred embodiment of the present invention.

도 1 내지 도 3에서 보는 바와 같이, 본 발명에 따른 상기 화학방호복용 원단(10)은 먼저, 상기 지지원단(11)에 상기 부착용 접착제(13)를 도포하여 이루어진다(s101). 여기서, 상기 지지원단(11)은 기본적인 유연성을 고려하여 니트형으로 직조됨이 바람직하며, 직물의 섬유간격이 벌어지지 않도록 신축성이 없는 형태로 직조됨이 바람직하다. As shown in Figures 1 to 3, the chemical protective clothing fabric 10 according to the present invention is first made by applying the adhesive adhesive 13 for the support fabric 11 (s101). Here, the support fabric 11 is preferably woven in the form of knit in consideration of basic flexibility, it is preferable to be woven in a form without elasticity so that the fiber spacing of the fabric does not open.

또한, 상기 부착용 접착제(13)는 상기 지지원단(11)에 도트형으로 도포되되, 상기 도트의 직경은 0.6~1 mm를 이루며, 상기 도트 사이의 간격은 0.02~0.4 mm를 이루도록 도포됨이 바람직하다. 즉, 상기 도트의 간격을 0.02~0.4 mm로 하여 상기 부착용 접착제(13) 도트의 간격과 상기 구슬형 활성탄(15)의 접점이 교차하도록 조절하여 상기 구슬형 활성탄(15)이 치밀하게 부착되도록 하는 것이 바람직하다. In addition, the attachment adhesive 13 is applied to the support fabric 11 in the form of a dot, the diameter of the dot is 0.6 ~ 1 mm, the interval between the dots is preferably applied to form a 0.02 ~ 0.4 mm. Do. That is, the interval of the dot is 0.02 ~ 0.4 mm to adjust the interval of the adhesive adhesive 13 dot and the contact point of the bead activated carbon 15 to cross the bead activated carbon (15) to be closely attached It is preferable.

여기서, 상기 부착용 접착제(13)는 30~80 g/㎡으로 도포됨이 바람직한데, 그의 점착량이 30 g/㎡ 미만이 되면 후술하는 상기 흡착층의 구슬형 활성탄(15)의 접착성이 떨어지게 되며, 80 g/㎡을 초과하여 도포되면 비연속적으로 도포된 접착제들이 서로 연결고리를 형성하여 막이 만들어짐으로써 상기 지지원단(11)의 유연성이 현격히 떨어지게 된다. In this case, the adhesive 13 is preferably applied at 30 to 80 g / m 2, but when the amount of adhesion thereof is less than 30 g / m 2, adhesiveness of the bead-type activated carbon 15 of the adsorption layer to be described later is deteriorated. When applied in excess of 80 g / m 2, discontinuously applied adhesives form a connection to each other to form a film, thereby greatly reducing the flexibility of the support fabric 11.

그리고, 상기 부착용 접착제(13)가 도포된 상기 지지원단(11)에 상기 구슬형 활성탄(15)을 부착하여(s102) 외부의 화학성 독성물질을 흡착하여 걸러낼 수 있는 상기 흡착층을 형성한다. In addition, the bead-shaped activated carbon 15 is attached to the support fabric 11 to which the adhesive agent 13 is applied (s102) to form the adsorption layer capable of absorbing and filtering out chemical toxic substances from the outside.

여기서, 상기 구슬형 활성탄(15)은 0.2~0.7 mm의 직경으로 이루어진 것이 가장 효과적인 흡착성능을 나타낼 수 있는데, 상기 구슬형 활성탄(15)의 부착과 상기 지지원단(11)에 접착제 막이 형성되는 것을 방지하기 위하여 상기 부착용 접착제(13)의 간격이 상기와 같이 조절될 수 있다. Here, the bead activated carbon 15 may be formed of a diameter of 0.2 ~ 0.7 mm to show the most effective adsorption performance, the adhesion of the bead activated carbon 15 and the adhesive film is formed on the support fabric 11 In order to prevent the interval of the adhesive adhesive 13 can be adjusted as described above.

또한, 상기 구슬형 활성탄(15)이 부착된 상기 부착용 접착제(13)를 고착시키기 위하여 소정의 시간 동안 숙성시키며(s103), 상기 구슬형 활성탄(15)이 부착된 상기 지지원단(11)에 결합되는 상기 커버원단(17)에 상기 고착용 접착제를 도포한다(s104). In addition, to be aged for a predetermined time to secure the attachment adhesive 13 to which the bead activated carbon 15 is attached (s103), and bonded to the support fabric 11 to which the bead activated carbon 15 is attached. Applying the fixing adhesive to the cover fabric 17 is to be (s104).

아울러, 상기 고착용 접착제는 상기 커버원단(17)에 도트형으로 도포되며, 5~15 g/㎡의 점착량으로 도포됨이 바람직하다. 즉, 상기 커버원단(17)은 상기 구슬형 활성탄(15)을 고착시킴과 동시에 이탈을 방지하도록 상기 고착용 접착제가 도포되어 상기 구슬형 활성탄(15)이 부착된 상기 지지원단(11)에 결합된다(s105). In addition, the fixing adhesive is applied to the cover fabric 17 in a dot shape, it is preferably applied in an adhesive amount of 5 ~ 15 g / ㎡. That is, the cover fabric 17 is fixed to the bead activated carbon 15 and at the same time the fixing adhesive is applied to prevent the separation is coupled to the support fabric 11 attached to the bead activated carbon 15 (S105).

이를 통해, 본 발명에 따른 유연성이 개선된 화학방호복용 원단(10)이 완성되고, 상기 화학방호복용 원단(10)의 커버원단(17)에 위장성능을 부여한 원단을 결합함으로써 상기 화학방호복이 완성될 수 있다. Through this, the chemical protective clothing fabric 10 with improved flexibility according to the present invention is completed, the chemical protective clothing is completed by combining the fabric imparting camouflage performance to the cover fabric 17 of the chemical protective clothing fabric 10 Can be.

이상 설명한 바와 같이, 본 발명은 상술한 각 실시예에 한정되는 것은 아니며, 본 발명의 청구항에서 청구한 범위를 벗어남 없이 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 변형실시되는 것은 가능하며, 이러한 변형실시는 본 발명의 범위에 속한다. As described above, the present invention is not limited to the above-described embodiments, but may be modified by those skilled in the art without departing from the scope of the claims of the present invention. Such modifications are within the scope of the present invention.

10: 화학방호복용 원단 11: 지지원단
13: 부착용 접착제 15: 구슬형 활성탄
17: 커버원단 10: fabric for chemical protective clothing 11: support fabric
13: Adhesive for Attachment 15: Beaded Activated Carbon
17: cover fabric

Claims (5)

외부의 화학성 독성물질로부터 인체가 보호되도록 직조된 직물로 이루어지되, 유리전이온도가 -45~-5 ℃이며 점도가 3,000~11,000 mPas인 습기경화형 폴리우레탄 일액형 접착제로 이루어진 부착용 접착제가 일측 표면에 30~80 g/㎡의 점착량으로서 도트형으로 도포된 지지원단;
상기 부착용 접착제에 의해 상기 지지원단에 접착되며, 상기 화학성 독성물질이 흡착되는 구슬형 활성탄으로 이루어진 흡착층; 및
상기 흡착층에 적층되어 상기 구슬형 활성탄이 고착되도록 폴리아미드 일액형 접착제로 이루어진 고착용 접착제가 5~15 g/㎡의 점착량으로 도포된 커버원단을 포함하여 이루어지는 유연성이 개선된 화학방호복용 원단. It consists of a woven fabric that protects the human body from external chemical toxic substances. The adhesive for adhesion consists of moisture-curable polyurethane one-component adhesive with a glass transition temperature of -45 ~ -5 ℃ and viscosity of 3,000 ~ 11,000 mPas. A support fabric coated in a dot shape with an adhesive amount of 30 to 80 g / m 2;
An adsorption layer adhered to the support fabric by the attachment adhesive and made of bead-type activated carbon to which the chemical toxic substances are adsorbed; And
Bonding adhesive made of a polyamide one-component adhesive is laminated on the adsorption layer to secure the flexible protective chemical fabric comprising a cover fabric coated with an adhesive amount of 5 ~ 15 g / ㎡ . 제 1 항에 있어서,
상기 부착용 접착제는 0.6~1 mm 직경의 도트가 0.02~0.4 mm의 간격을 이루도록 도트형으로 도포되며,
상기 구슬형 활성탄의 직경은 0.2~0.7 mm로 이루어짐을 특징으로 하는 유연성이 개선된 화학방호복용 원단. The method of claim 1,
The adhesive for adhesive is applied in the form of dots so that the 0.6 ~ 1 mm diameter dot makes an interval of 0.02 ~ 0.4 mm,
The diameter of the bead-shaped activated carbon fabric for improved chemical protective clothing, characterized in that consisting of 0.2 ~ 0.7 mm. 제 1 항에 있어서,
상기 지지원단은 굵기 10~90 denier인 복합원사로 이루어지며,
상기 지지원단의 밀도는 경사 80~150 올/5cm 및 위사 70~130 올/5cm로 이루어짐을 특징으로 하는 화학방호복용 원단. The method of claim 1,
The support fabric is made of a composite yarn having a thickness of 10 ~ 90 denier,
Density of the support fabric is a chemical protective clothing fabric, characterized in that made of inclined 80-150 ol / 5cm and weft 70-130 ol / 5cm. 제 1 항에 있어서,
상기 커버원단은 경위사의 방향성이 없는 부직물 및 50~100 수로 이루어진 면직물을 포함하는 그룹 중 선택된 직물로 이루어짐을 특징으로 하는 유연성이 개선된 화학방호복용 원단. The method of claim 1,
The cover fabric is improved chemical protective clothing fabric, characterized in that made of a fabric selected from the group comprising a nonwoven fabric and a cotton fabric consisting of 50 to 100 non-weft warp yarn. 삭제delete
KR1020110001251A 2011-01-06 2011-01-06 Fabric with improved flexibility of chemical protecting cloth KR101041415B1 (en)