KR101033875B1 - Fabrication method of spectacle frame - Google Patents
Fabrication method of spectacle frame Download PDFInfo
- Publication number
- KR101033875B1 KR101033875B1 KR1020080133101A KR20080133101A KR101033875B1 KR 101033875 B1 KR101033875 B1 KR 101033875B1 KR 1020080133101 A KR1020080133101 A KR 1020080133101A KR 20080133101 A KR20080133101 A KR 20080133101A KR 101033875 B1 KR101033875 B1 KR 101033875B1
- Authority
- KR
- South Korea
- Prior art keywords
- sheet
- spectacle frame
- heterogeneous
- dimensional
- acetate
- Prior art date
Abstract
본 발명의 목적은 형상 복원능력이 우수한 열가소성 엔지니어링 플라스틱 계열의 폴리아미드 사출물과 아세테이트계의 입체문양시트를 결합시켜 박리현상이 없는 화려한 고품질의 안경테를 제작할 수 있는 이종소재 안경테의 제조방법과 그 방법에 의해 제조된 안경테를 제공하는데 있다.An object of the present invention is to provide a method of manufacturing a heterogeneous spectacle frame which can produce a gorgeous high quality spectacle frame without peeling phenomenon by combining a thermoplastic engineering plastic-based polyamide injection molded product having excellent shape restoring ability with an acetate-based stereoscopic sheet. It is to provide a spectacle frame manufactured by.
본 발명의 이종소재 안경테의 제조방법은 아세테이트계 입체문양시트를 사전에 결정된 디자인 패턴으로 컷팅하는 공정과, 디자인 패턴에 따라 컷팅된 입체문양시트를 연화제에 침지하여 연화시키는 공정과, 사전에 제작한 폴리아미드 안경테 사출물의 정해진 위치에 연화된 입체문양시트를 접착제를 이용하여 접착시킨 후 가열 가압을 실시하여 이종소재를 접합시킴과 동시에 연화된 입체문양시트를 복원시키거나 또는 핫멜트융착공정, 가열융착공정, 고주파융착공정, 초음파융착공정 중 어느 하나의 공정을 실시하여 이종소재를 접합시킴과 동시에 연화된 입체문양시트를 복원시키는 공정과, 상기 공정에서 제작된 아세테이트 입체문양시트와 폴리아미드 사출물의 결합에 의한 이종소재 안경테를 건조한 후 바렐에서 표면연마를 실시하는 공정과, 표면이 연마된 이종소재 안경테의 표면층에 탑코팅을 실시하는 공정을 포함하는 것을 특징으로 한다.The manufacturing method of the heterogeneous spectacle frame of the present invention is a process of cutting the acetate-based three-dimensional pattern sheet in a predetermined design pattern, and a step of softening the three-dimensional pattern sheet cut according to the design pattern by softening agent, and prepared in advance The softened three-dimensional pattern sheet is bonded to a predetermined position of the polyamide spectacle frame by using an adhesive, and then heated and pressed to bond dissimilar materials, and at the same time, the softened three-dimensional pattern sheet is restored, or a hot melt fusion process or a heat fusion process. , Bonding the heterogeneous materials and restoring the softened three-dimensional pattern sheet at the same time by performing any one of a high frequency fusion process and an ultrasonic fusion process, and the bonding of the acetate three-dimensional sheet and the polyamide injection molded product produced in the process. A process of surface polishing in barrel after drying the heterogeneous material frames It characterized in that it comprises a step of performing a top coating on the surface layer of the heterogeneous spectacle frame polished surface.
아세테이트, 입체문양시트, 폴리아미드, 안경테, 이종소재, 사출물 Acetate, solid pattern sheet, polyamide, spectacle frame, dissimilar materials, injection molding
Description
본 발명은 아세테이트계 수지에 색소나 펄(pearl), 금속 페이스트 등을 브렌딩하여 자개문양을 띄는 입체문양의 아세테이트 필름을 제작하고 이렇게 제작된 아세테이트 필름을 가공성과 형상복원성이 우수한 열가소성 엔지니어링 플라스틱 계열의 폴리아미드 사출물에 접착 결합시켜 박리현상이 없는 화려한 고품질의 안경테를 제작할 수 있도록 한 이종소재 안경테의 제조방법과 그 방법에 의해 제조된 안경테에 관한 것이다.The present invention is to produce a three-dimensional acetate film having a mother-of-pearl pattern by blending pigments, pearls, metal pastes, etc. in acetate-based resin, and the acetate film of the thermoplastic engineering plastic series The present invention relates to a method of manufacturing a heterogeneous spectacle frame and to a spectacle frame manufactured by the method, wherein the spectacle frame is manufactured by adhesive bonding to a polyamide injection molding to produce a gorgeous high quality spectacle frame without peeling phenomenon.
현대사회에 있어서 안경은 시력교정의 기능을 넘어 사용자 자신을 세련되고 아름답게 장식하는 하나의 장신구와 같은 기능을 가지게 되었다. 따라서 기능성에 촛점이 맞추어지는 안경렌즈와는 달리 그 안경렌즈가 장착될 안경테는 디자인과 형상이 세련되고 아름다워야만 소비자들이 선택하게 된다.In modern society, eyeglasses have more than a function of correcting vision, and have the function of a trinket that decorates the user beautifully and beautifully. Therefore, unlike the spectacle lens that focuses on functionality, the spectacle frame on which the spectacle lens will be mounted is selected by consumers only when the design and shape are stylish and beautiful.
안경테는 보통 금속제 또는 합성수지재 또는 금속과 합성수지를 적절히 결합시킨 콤비타입으로 대별할 수 있는데, 최근에는 다양한 변형과 디자인에 유리하고 가벼운 합성수지재의 안경테가 주류를 이룬다고 할 수 있다.The spectacle frame can be roughly classified into a metal or synthetic resin material or a combination type of a metal and a synthetic resin suitably. Recently, the spectacle frame made of light and synthetic resin material is advantageous in various modifications and designs.
합성수지재의 안경테 표면에 다양한 문양을 부여하는 방법으로 폴리아미드계와 같이 내열성 및 탄성 복원력이 우수한 수지를 이용하여 안경테 형상을 사출한 다음 그 표면에 특정 문양을 부여하기 위해 염색이나 인쇄 또는 음,양각을 형성할 수 있다.As a method of imparting various patterns to the spectacle frame surface of synthetic resin material, the shape of the spectacle frame is injected using a resin having excellent heat resistance and elastic restoring power, such as polyamide, and then dyed or printed or yin and embossed to impart a specific pattern to the surface. Can be formed.
이 경우 수지를 이용한 안경테의 형상 추출은 용이하나 그 표면을 장식하기 위한 염색, 입체문양 인쇄, 음각/양각 등의 후속 공정이 매우 복잡하고 정밀한 조건을 요구하기 때문에 제품 생산성을 높이는데 한계가 있다.In this case, it is easy to extract the shape of the spectacle frame using a resin, but there are limitations in increasing product productivity because subsequent processes such as dyeing, three-dimensional pattern printing, and engraving / embossing to decorate the surface require very complicated and precise conditions.
합성수지재의 안경테 표면에 다양한 문양을 부여하기 위한 다른 방법으로 합성수지물로 성형사출된 안경테 표면에 별도의 공정을 통하여 사전에 제작된 특정 문양의 필름을 부착하는 방법이 있다.Another method for imparting various patterns to the spectacle frame surface of the synthetic resin material is a method of attaching a film of a specific pattern prepared in advance through a separate process on the spectacle frame molded and molded with the synthetic resin.
이 방법은 안경테의 제작공수를 향상시켜 대량생산을 가능하게 하지만 안경테 표면장식용 문양이 평면적이어서 안경테를 화려하고 입체적인 디자인으로 장식하는데 한계점을 가지고 있다. 더욱이 문양이 형성된 필름의 경도가 높은 경우 그 표면에의 디자인 문양 인쇄공정이 까다롭고 인쇄상태의 안정적인 유지가 어려울 뿐만 아니라 그 필름이 안경테 사출물에서 박리되기 쉽다. 이를 고려하여 문양이 형성될 필름의 경도를 낮출 경우 안경테 사출물과의 안정된 접착상태를 유지하지만 그 표면이 쉽게 손상되는 문제를 초래한다.This method improves the manufacturing process of the spectacle frame and enables mass production, but has a limitation in decorating the spectacle frame with a colorful and three-dimensional design because the pattern of the decorative surface of the spectacle frame is flat. Moreover, when the hardness of the patterned film is high, the design pattern printing process on the surface is difficult, and it is difficult to maintain stable printing state, and the film is easily peeled off from the spectacle frame. In consideration of this, when the hardness of the film to be patterned is lowered, it maintains a stable adhesive state with the spectacle frame, but causes a problem that the surface is easily damaged.
한편, 입체문양 패턴을 갖는 고 내구성 및 고품위의 안경테를 제작하는 방법 으로 내부전체에 입체문양을 갖는 일정한 두께(일예로 T~15T 정도)의 입체문양 평판시트를 제작한 다음 이 후판의 평판시트를 직접 안경 형상으로 절삭가공하여 제 작하는 방법이 있다. 이 방법은 매우 화려하고 세련된 고품격의 안경테를 제작하는 것을 가능하게 하지만 수율이 낮아 고가격의 입체문양 후판시트 원자재 비용이 크게 증가되는 문제를 가져온다. On the other hand, by producing a high-durability and high-quality eyeglass frame having a three-dimensional pattern pattern to produce a three-dimensional pattern flat sheet having a certain thickness (for example, T ~ 15T) having a three-dimensional pattern throughout the inside and then the flat sheet of this thick plate There is a method of manufacturing by cutting directly into glasses shape. This method makes it possible to manufacture high-quality eyeglass frames that are very colorful and refined, but the low yield brings about a problem that the cost of raw materials for high-cost three-dimensional thick plate sheet is greatly increased.
본 발명은 상기한 바와 같은 종래기술의 문제점을 해결하기 위한 것으로, 본 발명의 목적은 형상 복원능력이 우수한 열가소성 엔지니어링 플라스틱 계열의 폴리아미드 사출물과 아세테이트계의 입체문양시트를 결합시켜 박리현상이 없는 화려한 고품질의 안경테를 제작할 수 있는 이종소재 안경테의 제조방법과 그 방법에 의해 제조된 안경테를 제공하는데 있다.The present invention is to solve the problems of the prior art as described above, an object of the present invention is to combine the polyamide injection molding of the thermoplastic engineering plastics series having excellent shape resilience and the three-dimensional pattern sheet of the acetate-based brilliant peeling phenomenon Disclosed is a method of manufacturing a heterogeneous spectacle frame and a spectacle frame manufactured by the method.
상기 목적을 달성하기 위한 본 발명의 이종소재 안경테의 제조방법은 수지에 특정색소, 펄, 금속 페이스트를 브렌딩하여 자개문양을 갖는 아세테이트계의 입체문양시트를 제작하는 공정과, 아세테이트계 입체문양시트를 사전에 결정된 디자인 패턴으로 컷팅하는 공정과, 디자인 패턴에 따라 컷팅된 입체문양시트를 연화제에 침지하여 연화시키는 공정과, 사전에 제작한 폴리아미드 안경테 사출물의 정해진 위치에 연화된 입체문양시트를 접착제를 이용하여 접착시킨 후 가열 가압을 실시하여 이종소재를 접합시킴과 동시에 연화된 입체문양시트를 복원시키거나 또는 핫멜트융착공정, 가열융착공정, 고주파융착공정, 초음파융착공정 중 어느 하나의 공정을 실시하여 이종소재를 접합시킴과 동시에 연화된 입체문양시트를 복원시키는 공정과, 상기 공정에서 제작된 아세테이트 입체문양시트와 폴리아미드 사출물의 결합에 의한 이종소재 안경테를 건조한 후 바렐에서 표면연마를 실시하는 공정과, 표면이 연마된 이종소재 안경테의 표면층에 탑코팅을 실시하는 공정을 포함하는 것을 특징으로 한다.Method for producing a heterogeneous spectacle frame of the present invention for achieving the above object is a step of producing a three-dimensional sheet of acetate-based pattern having a mother-pearl pattern by blending a specific pigment, pearl, metal paste on the resin, and acetate-based three-dimensional sheet The process of cutting to a predetermined design pattern, the process of dipping and softening the three-dimensional pattern sheet cut according to the design pattern with a softener, and the three-dimensional pattern sheet softened at a predetermined position of the polyamide eyeglass frame injection molded in advance. After bonding by using heat press to bond the heterogeneous material to restore the softened three-dimensional pattern sheet or perform any one of the hot melt fusion process, heat fusion process, high frequency fusion process, ultrasonic fusion process Bonding the dissimilar materials and restoring the softened three-dimensional pattern sheet; And drying the heterogeneous spectacle frame by combining the acetate solid pattern sheet and polyamide injection molded product produced in the above, and performing surface polishing in a barrel, and performing a top coating on the surface layer of the heterogeneous spectacle frame polished surface. It is characterized by.
또한 상기 목적을 달성하기 위한 본 발명의 이종소재 안경테는 폴리아미드계 안경테 사출물의 표면에 3D 자개문양의 아세테이트계 입체문양시트가 서로 접착제에 의한 접합 또는 융착공정에 의해 융착되고, 상기 아세테이트계 입체문양시트상에는 보호용 탑코팅을 형성한 것을 특징으로 한다.In addition, the heterogeneous spectacle frame of the present invention for achieving the above object is a 3D mother-shaped acetate pattern sheet on the surface of the polyamide-based spectacle frame injection molding is fused by bonding or fusion process with an adhesive, the acetate-based stereo pattern A protective top coating is formed on the sheet.
본 발명의 이종소재 안경테의 제조방법은 간단하고 낮은 비용으로 표면이 입체문양으로 장식되면서 탄성복원력이 우수한 고내열성, 고내화학성 및 고품격을 갖는 안경테를 제작할 수 있는 특유의 효과를 가져온다.The manufacturing method of the heterogeneous spectacle frame of the present invention is simple and low cost, the surface is decorated with a three-dimensional pattern, bringing a unique effect of producing a spectacle frame having high heat resistance, high chemical resistance and high quality with excellent elastic resilience.
또한 본 발명은 이종소재간 접착시 입체문양시트의 연화 및 복원(경화)을 통하여 이종소재의 접착력을 획기적으로 증대시켜 제품의 내구성과 안정성을 향상시킨다.In addition, the present invention significantly increases the adhesive strength of heterogeneous materials through softening and restoring (hardening) of the three-dimensional pattern sheet when bonding between dissimilar materials to improve the durability and stability of the product.
첨부한 도면을 참고로 하여 본 발명을 설명하면 다음과 같다.Hereinafter, the present invention will be described with reference to the accompanying drawings.
먼저 본 발명에 적용되는 입체문양시트는 도 1의 제조공정도에 따라 제작된다.First, the three-dimensional pattern sheet applied to the present invention is manufactured according to the manufacturing process diagram of FIG.
여기에서 참고되는 바와 같이, 입체문양시트의 제조공정의 제1단계는 수지에 색소, 펄 및 금속 페이스트 등을 브렌딩하여 다양한 컬러의 프리수지시트를 제조하는 공정이다.As referred to herein, the first step of the manufacturing process of the three-dimensional pattern sheet is a process of manufacturing a pre-resin sheet of various colors by blending a pigment, pearl, metal paste, and the like in the resin.
상기 수지는 투명의 아세테이트 수지를 말하며, 여기에 다양한 색소를 첨가 하여 수mm 내지 수십mm 두께의 단색컬러(블랙컬러, 레드컬러, 블루컬러 등)시트 또는 복합컬러시트로 제작될 수 있다.The resin refers to a transparent acetate resin, by adding a variety of pigments it can be produced in a monochromatic sheet (black color, red color, blue color, etc.) sheet or a composite color sheet of several mm to several tens of millimeters thick.
제2단계에서는 제1단계에서 제조된 다양한 단색 또는 복합 컬러의 프리수지시트를 필요한 모양과 크기로 절단하고 절단된 프리수지시트 조각들을 규칙적 또는 불규칙적으로 적층 배치한 다음 가열가압하여 적층된 프리수지시트들의 겔화 융착에 따른 후판입체문양시트를 제조한다.In the second step, various pre- and multi-colored pre-resin sheets prepared in the first step are cut into the required shape and size, and the cut pieces of the pre-resin sheets are regularly or irregularly stacked, and then heated and pressed to be laminated. To prepare a thick-stereoscopic sheet according to the gelation fusion of these.
이때, 적절한 크기와 모양으로 절단된 프리수지시트 조각들을 규칙적 또는 불규칙적으로 적층 배치함에 있어 서로 컬러를 달리하여 격자배치 또는 사선배치함으로서 프리수지시트 조각배열이 들어간 곳과 그렇치 못한 곳에 의해 공간부가 생기게 되며, 이러한 상태에서 특정형태(예를 들면 4각 형태)의 금속틀내에서 동시 가열 및 가압하면 상, 하층간의 수지시트가 불규칙적 또는 규칙적으로 교류하여 압착되므로 최종적으로 후판 상태의 입체문양시트가 만들어지게 된다.At this time, in the regular or irregular stacking arrangement of the pieces of pre-resin sheet cut to the appropriate size and shape, the space is created by the lattice arrangement or the diagonal arrangement of the pre-resin sheet fragments and the places where the pre-resin sheet array is not. In this state, when heating and pressing simultaneously in a metal frame of a specific shape (for example, a quadrangular shape), the resin sheet between the upper and lower layers is compressed by irregular or regular alternating pressure, and thus a solid plate sheet in the form of a thick plate is finally made. .
구체적으로, 상기 후판입체문양시트를 얻기 위한 가열가압 이전의 프리수지시트의 적층방식은 먼저 절단하지 않은 투명 또는 특정컬러의 프리수지시트 상에 앞서 절단된 투명 또는 특정컬러의 프리수지시트 조각들을 규칙적 또는 불규칙적으로 배치한 후 절단하지 않은 또 다른 프리수지시트를 덮고 그 위에 다시 절단된 프리수지시트 조각들을 규칙적 또는 불규칙적으로 배치하는 방식으로 적층하게 되며, 이러한 프리수지시트 조각들의 배치조건에서의 가열 가압을 통해 현란하고 아름다운 입체문양시트를 얻을 수 있는 후판입체문양시트가 만들어지게 된다.Specifically, the lamination method of the pre-resin sheet prior to heating and pressing to obtain the thick plate-shaped pattern sheet is a regular or pre-cut sheet of the transparent or specific color pre-cut sheet cut on the transparent or specific color pre-resin sheet not cut first Or by arranging the irregularly placed precut sheet which is not cut after being placed irregularly, and then placing the cut pieces of the cut resin sheet on a regular basis or at irregular intervals. Through the thick plate three-dimensional pattern sheet to obtain a brilliant and beautiful three-dimensional pattern sheet is made.
제3단계에서는 후판입체문양시트를 시어링머신에 장착하여 후판입체문양시트 의 표면을 얇게 켜내는 것으로 박막입체문양시트를 얻는다.In the third step, the thin plate three-dimensional glyph sheet is obtained by mounting the thick three-dimensional glyph sheet on the shearing machine and turning the surface of the thick three-dimensional glyph sheet thinly.
여기에서 얻어진 박막입체문양시트는 투명을 포함한 다양한 컬러의 프리수지시트 조각들의 상,하,좌,우 불규칙 배열상태에서의 용융압착 성형에 따른 다양한 컬러(빛)의 산란과 펄의 반사에 의해 3D(입체)시트의 특성을 가지게 된다.The thin-film three-dimensional pattern sheet obtained here is 3D due to scattering of various colors (light) and reflection of pearls according to melt compression molding in irregularly arranged states of pieces of pre-resin sheets of various colors including transparent. It will have the characteristics of the (stereo) sheet.
제4단계에서는 후판입체문양시트에서 시어링된 박막입체문양시트의 표면을 연마하여 최종 입체문양시트를 완성한다.In the fourth step, the surface of the thin-film three-dimensional glyph sheet sheared from the thick plate glyph sheet is polished to complete the final three-dimensional glyph sheet.
이렇게 제조된 입체문양시트는 다양한 컬러와 빛의 산란에 의해 3D(입체) 현상을 나타내는 자개특성을 그대로 나타내게 된다.The three-dimensional pattern sheet thus produced exhibits the mother-of-pearl characteristic of 3D (stereoscopic) phenomenon by various colors and light scattering.
도 2a 내지 도 2e는 도 1의 공정에 의해 제작된 박막 입체문양시트의 다양한 예의 사진이다.2A to 2E are photographs of various examples of the thin-film three-dimensional pattern sheet produced by the process of FIG.
여기에서 보는 바와 같이 입체문양시트는 자개와 같은 현란하고 고급스러운3D문양을 표출하게 된다.As seen here, the three-dimensional glyph sheet expresses the brilliant and luxurious 3D patterns such as mother-of-pearl.
도 3은 본 발명에 따른 이종소재 안경테의 제조방법 설명도이다.3 is an explanatory diagram of a method for manufacturing a heterogeneous spectacle frame according to the present invention.
본 발명의 제1공정에서는 수지에 특정색소, 펄, 금속 페이스트 등을 브렌딩하여 압축 성형하는 것으로 제작된 후판을 시어링하여 얻어진 자개문양의 아세테이트계 입체문양시트를 사전에 결정된 디자인 패턴으로 컷팅한다. 이에 앞서 박막 가공된 입체문양시트의 한쪽 면은 시트의 전체 컬러에 변화를 주기 위한 다른 색의 착색이 선행될 수 있다. 즉, 박막 입체문양시트의 연마되지 않은 한쪽 면에 선택적으로 원하는 컬러의 착색을 실시할 경우 해당 입체문양시트의 바탕컬러를 간단히 변경시킬 수 있어 동일한 패턴에서 다양한 컬러의 구현이 가능하게 된다.In the first step of the present invention, the mother-of-pearl patterned three-dimensional pattern sheet obtained by shearing a thick plate produced by blending a specific pigment, pearl, metal paste or the like into a resin is cut into a predetermined design pattern. Prior to this, one side of the thin-film processed three-dimensional pattern sheet may be preceded by coloring of another color to change the overall color of the sheet. That is, when the desired color is selectively colored on one of the unpolished surfaces of the thin-film three-dimensional pattern sheet, the background color of the three-dimensional pattern sheet can be simply changed to implement various colors in the same pattern.
여기서 사전에 결정된 디자인은 입체문양시트를 장식할 안경테 사출물의 외형을 따라 컷팅하는 것을 포함하여, 입체문양시트를 조각단위로 모자이크 방식으로 안경테 사출물에 부착하기 위한 조각단위 컷팅 형태 등 모든 수공 및 NC가공 컷팅을 포함한다.Here, the predetermined design includes cutting along the outline of the spectacle frame injection molding to decorate the three-dimensional pattern sheet, and all manual and NC processing, such as a cutting unit cut form for attaching the three-dimensional sheet to the spectacle frame in a mosaic manner in pieces. It includes cutting.
제2공정에서는 컷팅된 입체문양시트를 연화제에 침지시켜 연화시킨다. 이 연화공정은 강도가 매우 높은 아세테이트 입체문양시트를 연질화시켜 그 입체문양시트가 접착될 대상의 형상에 쉽게 순응하게 한다. 연화제는 일예로 아세톤 수용액을 사용할 수 있으며, 연화정도는 침지시간, 연화제의 농도, 입체문양시트의 두께 등에 따라 달라지므로 실시예에 따라 적당히 조절할 필요가 있다.In the second step, the cut three-dimensional pattern sheet is softened by immersing it in a softener. This softening process softens the acetate rigid glyph sheet, which has a very high strength, so that the rigid glyph sheet easily conforms to the shape of the object to be bonded. As an example, a softening agent may be used in an acetone aqueous solution, and the softening degree may be appropriately adjusted according to the embodiment since the softening degree depends on the immersion time, the concentration of the softener, and the thickness of the three-dimensional pattern sheet.
제3공정에서는 사전에 제작한 폴리아미드 안경테 사출물의 정해진 위치에 연화된 입체문양시트를 접착시킨다.In the third step, the softened three-dimensional pattern sheet is bonded to a predetermined position of the polyamide eyeglass frame injection molded in advance.
안경테 사출물과 입체문양시트의 접착에 있어 정확한 위치결정을 위해 지그가 사용될 수 있다. 대부분의 경우, 안경테를 이루는 렌즈프레임과 안경다리가 입체형상으로 성형 사출되므로 단순 수작업에 의해 그 사출물의 특정위치에 언제나 정확히 일치시켜 입체문양시트를 부착하는 것이 쉽지않다. 이러한 문제는 지그를 이용하여 쉽게 해결할 수 있다.A jig can be used for accurate positioning of the spectacle frame and the three-dimensional glyph sheet. In most cases, since the lens frame constituting the spectacle frame and the leg of the glasses are molded in three-dimensional shape, it is not easy to attach the three-dimensional pattern sheet at all times to exactly match the specific position of the injection by simple manual labor. This problem can be easily solved using a jig.
예를 들면 몰드형태의 지그내에 정해진 형상으로 컷팅된 아세테이트 입체문양시트, 엄밀하게는 연화된 아세테이트 입체문양시트를 위치시킨 다음 그 위에서 몰드형태의 전용 지그를 따라 폴리아미드 안경테 사출물을 위치시키면 사출물과 입체문양시트를 언제나 정확하게 얼라인된 상태로 접착시킬 수 있다.For example, an acetate solid pattern sheet, rigidly softened acetate solid sheet, cut into a predetermined shape in a mold-shaped jig, and then a polyamide spectacle frame injection molded along a dedicated jig in a mold, may be injected and Glyph sheets can always be glued together in a precisely aligned state.
이때 접착제가 사용되는데 수지계열 접착제와 무수지계열 접착제 모두를 사용할 수 있다. 그러나 고내구성 및 고품위의 품질을 유지하고자하는 경우 무수지 계열의 접착제를 이용하여 아세테이트 입체문양시트와 폴리아미드 안경테 사출물을 접합시키는 것이 바람직하다.At this time, an adhesive is used, and both a resin adhesive and an anhydride adhesive may be used. However, in order to maintain high durability and high quality, it is preferable to use an anhydride-based adhesive to bond the acetate solid pattern sheet and the polyamide eyeglass frame injection molding.
무수지 접착제를 사용하는 경우 안경테 사출물과 입체문양시트 사이의 접착면에 층이 생기지 않아 안경테에서 입체문양시트가 박리될 가능성이 없고 외관도 미려함이 유지된다.In the case of using an anhydrous adhesive, there is no layer on the adhesive surface between the spectacle frame injection and the three-dimensional pattern sheet, so that the three-dimensional pattern sheet may not be peeled off from the spectacle frame and the appearance is kept beautiful.
폴리아미드 안경테 사출물과 아세테이트 입체문양시트의 접합은 위에서 설명한 접착제 방식 외에도 여러 종류의 융착기술을 이용하여 접합시킬 수 있다. 예를 들면, 잘 알려져 있는 초음파융착공정 기술, 고주파융착공정 기술, 가열융착공정 기술 및 핫멜트융착공정 기술 등을 이용하여 안경테 사출물에 입체문양시트를 융착 접합시켜 안경테 전체를 원하는 패턴이나 형상으로 디자인할 수 있다.Bonding the polyamide spectacle frame insert and the acetate conformal sheet may be performed using a variety of fusion techniques in addition to the adhesive method described above. For example, by using a well-known ultrasonic welding process technology, high frequency welding process technology, heat welding process technology and hot melt welding process technology, the three-dimensional pattern sheet is fused and bonded to the frame of the spectacle frame to design the entire spectacle frame in the desired pattern or shape. Can be.
이때에도 안경테 사출물과 입체문양시트가 사전에 정해진 정확한 위치에서 접합이 이루어지도록 앞서 설명한 안경테와 입체문양시트 접합용 전용 지그가 사용될 수 있다. In this case, the jig for joining the spectacle frame and the three-dimensional pattern sheet described above may be used so that the injection of the spectacle frame and the three-dimensional pattern sheet are bonded at a predetermined precise position.
제4공정에서는 안경테 사출물과 입체문양시트 사이에 접착제를 개재시킨 상태에서 통상의 접착조건에 따라 가열가압을 실시한다.In the fourth step, heating and pressing are carried out in accordance with ordinary bonding conditions with an adhesive interposed between the injection frame and the three-dimensional pattern sheet.
이때 연화된 입체문양시트는 안경테 사출물의 표면에 순응하여 긴밀히 접착한 초기상태에서 그대로 복원되어 원래의 단단한 성질로 되돌아간다.At this time, the softened three-dimensional pattern sheet is restored as it is in the initial state closely adhered to the surface of the frame of the frame, and returns to its original rigid properties.
또한 접착제로서 무수지접착제를 사용한 경우 안경테 사출물과 입체문양시트 는 그들 사이의 층간 갭 없이 서로 융착되는 형태로 접착된다.In addition, when an anhydrous adhesive is used as the adhesive, the spectacle frame injection molding and the three-dimensional pattern sheet are bonded in such a manner that they are fused to each other without an interlayer gap therebetween.
한편, 접착제를 이용한 안경테 사출물과 입체문양시트의 가열 가압 조건하에서의 접합 공정과는 달리, 초음파융착공정, 고주파융착공정, 가열융착공정 및 핫멜트융착공정 등을 이용한 안경테 사출물과 입체문양시트의 융착 접합시, 별도의 건조과정과 가열 가압을 생략할 수 있어 공정의 간략화를 기대할 수 있다.On the other hand, unlike the bonding process under the heating and pressurization conditions of the eyeglass frame injection molding and the three-dimensional pattern sheet using an adhesive, when the fusion bonding of the eyeglass frame injection molding and the three-dimensional pattern sheet using an ultrasonic welding process, a high frequency welding process, a hot melting process and a hot melt fusion process As a result, a separate drying process and heating and pressurization can be omitted, and the process can be simplified.
제5공정에서는 아세테이트 입체문양시트와 폴리아미드 안경테 사출물의 이종소재 접합에 의해 제작된 안경테를 표면 연마를 위한 바렐에 장입하여 바렐링을 실시하는 것으로 안경테와 입체문양시트 사이의 접합면 등에 형성될 수 있는 버어 등을 제거시켜 안경테 외관을 정리한다.In the fifth step, the frame made by joining the heterogeneous materials of the acetate three-dimensional pattern sheet and the polyamide spectacle frame is loaded into a barrel for surface polishing to perform barreling, and thus the joint surface between the three-dimensional sheet and the three-dimensional sheet may be formed. Clean the exterior of the frame by removing any burrs.
다음 제6단계에서는 투명층 또는 기타 컬러층을 만들 수 있는 안경테의 최종표면 탑코팅을 실시한다.In the sixth step, the final surface top coating of the spectacle frame, which can make a transparent layer or other color layers, is performed.
도 4는 본 발명의 이종소재 안경테의 공정별 단면구조도이다.Figure 4 is a cross-sectional structure diagram for each process of the heterogeneous spectacle frame of the present invention.
여기에서 참고되는 바와 같이 (연화된)폴리아미드 안경테 사출물(10)에 무수지 접착제(11)를 도포하고 그 위에 아세테이트 입체문양시트(12)를 위치시킨 다음 가압 가열하면 무수지 접착제층은 사라지고 폴리아미드 안경테 사출물(10)과 아세테이트 입체문양시트(12)이 직접 면 접합되어 실질적으로 이들은 서로 융착된 상태가 된다.As referred to herein, an
이후 아세테이트 입체문양시트상에 탑코팅(13)을 실시하는 것으로 제종 안경테 제품을 완성한다.After the
도 5a 내지 도 5e는 본 발명 안경테의 실시예의 참고사진으로서, 안경테의 렌즈프레임과 안경다리에 전체적으로 또는 선택적으로 입체문양을 갖는 아세테이트 시트가 부착된 것을 보이고 있다.5A to 5E are reference photographs of embodiments of the spectacle frame according to the present invention, and show that an acetate sheet having a stereoscopic pattern is attached to the lens frame and the leg of the spectacle frame as a whole or selectively.
여기에서 보는 바와 같이 본 발명의 이종소재 안경테는 폴리아미드계 안경테 사출물의 표면에 3D 자개문양의 아세테이트계 입체문양시트가 접착 또는 융착되고 이 아세테이트계 입체문양시트상에 탑코팅이 형성된 형태의 구조를 갖는다.As seen here, the heterogeneous spectacle frame according to the present invention has a structure in which a 3D mother-of-pearl pattern-like acetate-like sheet is adhered or fused to the surface of the polyamide-based spectacle frame, and a top coating is formed on the acetate-based sheet. Have
도 1은 본 발명에 적용될 입체문양시트의 제조공정 순서도이다.1 is a flow chart of the manufacturing process of the three-dimensional pattern sheet to be applied to the present invention.
도 2a 내지 도 2e는 도 2의 공정에 의해 제조된 박막 입체문양시트 실시예의 참고사진이다.2A to 2E are reference photographs of the embodiment of the thin-film solid pattern sheet manufactured by the process of FIG. 2.
도 3은 본 발명의 이종소재 안경테의 제조공정 순서도이다.Figure 3 is a flow chart of the manufacturing process of the heterogeneous spectacle frame of the present invention.
도 4는 본 발명의 이종소재 안경테의 공정별 단면구조도이다.Figure 4 is a cross-sectional structure diagram for each process of the heterogeneous spectacle frame of the present invention.
도 5a 내지 도 5e는 본 발명 안경테의 실시예의 참고사진이다.5A to 5E are reference photographs of embodiments of the spectacle frame according to the present invention.
*도면의 주요부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *
10 : 폴리아미드 안경테 사출물10: polyamide eyeglass frame injection molding
11 : 무수지 접착제11: anhydrous adhesive
12 : 아세테이트 입체문양시트12: acetate solid sheet
13 : 탑코팅13: Top Coating
Claims (5)