Prior art keywords
weight
solid fuel
waste paper
paper sludge
waste
Prior art date
Application number
KR1020090026129A
Other languages
Korean (ko)
Other versions
KR20090045161A (en
Inventor
손민일
Original Assignee
손민일
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 손민일 filed Critical 손민일
Priority to KR1020090026129A priority Critical patent/KR101033860B1/en
Publication of KR20090045161A publication Critical patent/KR20090045161A/en
Application granted granted Critical
Publication of KR101033860B1 publication Critical patent/KR101033860B1/en

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10L—FUELS NOT OTHERWISE PROVIDED FOR; NATURAL GAS; SYNTHETIC NATURAL GAS OBTAINED BY PROCESSES NOT COVERED BY SUBCLASSES C10G, C10K; LIQUEFIED PETROLEUM GAS; ADDING MATERIALS TO FUELS OR FIRES TO REDUCE SMOKE OR UNDESIRABLE DEPOSITS OR TO FACILITATE SOOT REMOVAL; FIRELIGHTERS
    • C10L5/00—Solid fuels
    • C10L5/40—Solid fuels essentially based on materials of non-mineral origin
    • C10L5/46—Solid fuels essentially based on materials of non-mineral origin on sewage, house, or town refuse
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B09—DISPOSAL OF SOLID WASTE; RECLAMATION OF CONTAMINATED SOIL
    • B09B—DISPOSAL OF SOLID WASTE
    • B09B3/00—Destroying solid waste or transforming solid waste into something useful or harmless
    • B09B3/20—Agglomeration, binding or encapsulation of solid waste
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10L—FUELS NOT OTHERWISE PROVIDED FOR; NATURAL GAS; SYNTHETIC NATURAL GAS OBTAINED BY PROCESSES NOT COVERED BY SUBCLASSES C10G, C10K; LIQUEFIED PETROLEUM GAS; ADDING MATERIALS TO FUELS OR FIRES TO REDUCE SMOKE OR UNDESIRABLE DEPOSITS OR TO FACILITATE SOOT REMOVAL; FIRELIGHTERS
    • C10L5/00—Solid fuels
    • C10L5/02—Solid fuels such as briquettes consisting mainly of carbonaceous materials of mineral or non-mineral origin
    • C10L5/34—Other details of the shaped fuels, e.g. briquettes
    • C10L5/36—Shape
    • C10L5/363—Pellets or granulates
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10L—FUELS NOT OTHERWISE PROVIDED FOR; NATURAL GAS; SYNTHETIC NATURAL GAS OBTAINED BY PROCESSES NOT COVERED BY SUBCLASSES C10G, C10K; LIQUEFIED PETROLEUM GAS; ADDING MATERIALS TO FUELS OR FIRES TO REDUCE SMOKE OR UNDESIRABLE DEPOSITS OR TO FACILITATE SOOT REMOVAL; FIRELIGHTERS
    • C10L2290/00—Fuel preparation or upgrading, processes or apparatus therefore, comprising specific process steps or apparatus units
    • C10L2290/08—Drying or removing water
    • C—CHEMISTRY; METALLURGY
    • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
    • C10L—FUELS NOT OTHERWISE PROVIDED FOR; NATURAL GAS; SYNTHETIC NATURAL GAS OBTAINED BY PROCESSES NOT COVERED BY SUBCLASSES C10G, C10K; LIQUEFIED PETROLEUM GAS; ADDING MATERIALS TO FUELS OR FIRES TO REDUCE SMOKE OR UNDESIRABLE DEPOSITS OR TO FACILITATE SOOT REMOVAL; FIRELIGHTERS
    • C10L2290/00—Fuel preparation or upgrading, processes or apparatus therefore, comprising specific process steps or apparatus units
    • C10L2290/24—Mixing, stirring of fuel components
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E50/00—Technologies for the production of fuel of non-fossil origin
    • Y02E50/10—Biofuels, e.g. bio-diesel
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E50/00—Technologies for the production of fuel of non-fossil origin
    • Y02E50/30—Fuel from waste, e.g. synthetic alcohol or diesel
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
    • Y02W10/00—Technologies for wastewater treatment
    • Y02W10/20—Sludge processing

Abstract

본 발명은 폐제지슬러지와 폐유를 이용한 고체연료 및 그 제조방법에 관한 것이다. 본 발명은 제지공장에서 배출된 폐제지슬러지에 폐유, 바인더, 유화제 및 0.01 ~ 20중량%의 수분함량을 갖는 폐제지슬러지 분말 또는 폐지 분말을 일정한 비율로 혼합한 후, 상기 혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛으로 제조한 다음, 수분함량이 0.01 ~ 10중량%가 되도록 건조함으로써, 저위발열량 3,500 kcal/kg 이상의 높은 발열량을 가지면서 친환경적인 고체연료를 제조하는 방법 및 이에 따라 제조된 고체연료를 제공한다.

Figure R1020090026129

폐제지슬러지, 폐유, 고체연료, 펠렛(pellet), 수분함량

The present invention relates to a solid fuel using waste paper sludge and waste oil and a method for producing the same. The present invention mixes the waste paper sludge powder or waste paper powder having a water content of 0.01 to 20% by weight to waste paper sludge discharged from the paper mill at a constant ratio, and then pellets the mixture. It is manufactured into pellets in a semi-solid state by extrusion into a molding machine, and dried to a moisture content of 0.01 to 10% by weight, thereby producing an environmentally friendly solid fuel having a high calorific value of more than 3,500 kcal / kg of low calorific value and accordingly It provides a produced solid fuel.

Figure R1020090026129

Waste Paper Sludge, Waste Oil, Solid Fuel, Pellets, Water Content

Description

펠렛 형태의 고체연료 및 그의 제조방법{Solid fuel of pellet form and method for preparing the same}Solid fuel of pellet form and method for preparing the same

본 발명은 현재 환경공해를 발생시키는 제지슬러지와 폐유를 이용한 고체 연료 및 그 제조방법에 관한 것이다.The present invention relates to a solid fuel and a method for producing the same using papermaking sludge and waste oil generating environmental pollution.

고체연료를 제조하기 위하여 출발물질로 사용되는 제지슬러지는 제지공장의 최종공정에서 함수율 70 ~ 85중량％인 탈수케익 형태로 발생되며, 수분을 제외한 고형물을 기준으로 유기물이 적게는 30중량％에서 많게는 70중량％ 이상까지도 함유되어 있고, 이로 인한 고형분의 발열량이 적게는 2,000kcal/kg ~ 5,000kcal/kg 정도의 비교적 높은 열량을 갖고 있다. 따라서 이와 같은 유기성 제지슬러지는 학문상으로도 저급탄소계 연료로 분류되고 있으며, 우리나라에서는 2004년 기준으로 650 만톤씩 발생하고 있으나 현재는 이들 제지슬러지에 대한 처리방법이 환경문제를 비롯한 여러 가지 사회문제를 일으키는 것으로 인식되자 정부에서는 2011년 2월 까지 제지슬러지의 해양투기를 금지하고, 재활용 등을 통한 육상처리 원칙을 발표 한 바 있어 이 분야에서 적절한 재활용 기술의 개발 보급이 매우 시급한 실정이다.Paper sludge, which is used as a starting material for the manufacture of solid fuel, is produced in the form of dehydrated cakes with a water content of 70 to 85% by weight in the final process of the paper mill. It contains up to 70% by weight or more, and thus has a relatively high calorific value of about 2,000 kcal / kg to 5,000 kcal / kg. Therefore, such organic paper sludge is classified as a low carbon fuel in the academic field. In Korea, it generated 6.5 million tons as of 2004. Currently, the treatment method for these paper sludges is various social problems including environmental issues. The government has banned the dumping of paper sludge by sea until February 2011, and announced the principle of land treatment through recycling, so it is very urgent to develop and distribute appropriate recycling technology in this field.

또한 폐유의 경우 년 간 약 4억L 이상이 발생하고 있으며, 발생량 대비 약 30중량％가 매립에 의하여 처리되고 있다. 폐유의 재활용율은 67중량％로 높은 편이나 정제에 따른 방법에 있어 많은 에너지 비용이 소모되므로, 이 또한 공정 개선이 시급한 실정이다.In the case of waste oil, more than about 400 million liters per year are generated, and about 30% by weight of the generated oil is treated by landfilling. Although the recycling rate of the waste oil is high at 67% by weight, a lot of energy costs are consumed in the refining method, which is also urgently needed to improve the process.

지금까지 제지슬러지를 재활용 처리하는 방법 중에서 대체연료로 활용하고자 하는 노력이 계속되고 있기는 하나 제지슬러지의 수분함량이 약 70중량％ 이상을 차지하고 있어 연료화에 큰 장애가 되고 있고, 건조를 통해 얻은 제지슬러지 고형분의 경우도 연료로서의 물성을 결정하는 데 가장 중요한 휘발분의 함량과 고정탄소의 함량이 기존의 석탄계 화석연료와는 정반대의 비율로 구성되어 있어 기존의 연소 시스템에서는 연료로 활용하는 것에는 많은 제약이 따르고 있는 실정이어서 이를 극복하는데 많은 어려움이 있는 상황이다.Although efforts to recycle paper sludge have been made as an alternative fuel, the water content of paper sludge accounts for more than 70% by weight, which is a major obstacle to fueling, and paper sludge obtained through drying In the case of solids, the volatile content and the fixed carbon content, which are most important for determining the physical properties of the fuel, are composed in the opposite ratio of the existing coal-based fossil fuels. There is a lot of difficulty in overcoming this situation.

최근에는 우리나라에서도 다양한 슬러지를 연료로 재활용하기 위하여 슬러지에 도시에서 배출되는 가연성 생활 폐기물 및 기름을 보조연료로 혼합하고, 성형성을 높이기 위하여 점토나 모래를 섞어 기존의 연탄이나 조개탄 모형의 연료탄을 제조하거나, 슬러지에 다량의 코크스 및 석탄류를 혼합하여 고형 연료화하는 사례들이 발표되었다.Recently, in Korea, in order to recycle various sludge as fuel, combustible domestic waste and oil discharged from the city are mixed with auxiliary fuel, and clay or sand is mixed to improve formability and manufactured fuel coal of conventional briquettes or briquettes. In other cases, a large amount of coke and coal is mixed into sludge to solidify fuel.

예를 들면, 한국 공개특허공보 1994-0014200에는 제지슬러지를 탈수한 후 이를 기름에 튀겨내어 연료로 사용하는 가열된 기름을 이용한 제지슬러지의 수분 추출방법 및 장치가 공개되었으며, 한국 공개특허공보 1991-0001084에는 펄프제지슬 러지를 파라핀왁스에 혼합한 후 헥사민 과망간산칼륨을 가하여 가압 성형하여 제조된 고형연료가 공개 되었고, 한국공개특허공보 1994-0024040에는 나무류 폐지류 제지슬러지 등의 폐기물에 탄산칼슘, 제오라이트 및 결합제로 혼합한 다음압축성형기로 가압하여 제조된 가연성 각종폐기물을 이용하여 숯을 만드는 제조방법이 공개 되었다. 이밖에도 한국공개특허공보 1999-0074336호, 한국등록특허공보 제10-0319803호, 한국등록특허공보 제 10-0419189호에서는 하수슬러지에 석탄가루 혹은 석유 코크스를 첨가하여 폐기물을 연료화 하는 방법 등이 공개 되어 있다. 그러나 상기 기술들은 서로 상이한 물성의 재료가 섞여있어 연소의 최적 조건을 맞추기가 힘들뿐 아니라 불완전연소 등으로 인한 각종 대기오염물질이 배출되며, 불연성 재료가 첨가되어 있어 연소시키기 힘들므로 실용화 되지 않고 있는 실정이다. 또한 석탄분말이나 석유 코크스 분말을 열량보강재로 첨가하는 방법에 있어서도 단순히 제지슬러지의 열량을 높이기 위하여 첨가제를 제지슬러지 고형분에 대하여 적게는 1.25배에서 많게는 45배 가까이 첨가하므로 이것은 열량보강재에 제지슬러지를 첨가하는 형태가 되므로 폐기물의 활용도가 상대적으로 크게 저하됨을 의미한다. 이와 같이 기존의 특허에 기재된 연료들은 과량의 첨가제 사용에 따른 원가부담 및 제도적인 밑받침을 받지 못하는 연료로서 그 활용도 측면에서 현실적으로 현장 보급이 어려운 기술이라고 할 수 있다.For example, Korean Patent Laid-Open Publication No. 1994-0014200 discloses a method and apparatus for extracting water from paper sludge using heated oil that dehydrates paper sludge and then fry it in oil to use as fuel. In 0001084, a solid fuel prepared by mixing pulp paper sludge with paraffin wax and then pressurizing with hexamine potassium permanganate was disclosed. Korean Patent Publication No. 1994-0024040 discloses calcium carbonate in wastes such as paper waste paper sludge, etc. , A method of making charcoal using various combustible wastes prepared by mixing zeolite and binder and then pressing with a compression molding machine has been disclosed. In addition, Korean Laid-Open Patent Publication No. 1999-0074336, Korean Registered Patent Publication No. 10-0319803, and Korean Registered Patent Publication No. 10-0419189 disclose methods for fueling waste by adding coal powder or petroleum coke to sewage sludge. have. However, the above technologies are mixed with materials of different physical properties, and it is difficult to meet the optimum conditions of combustion, and various air pollutants are emitted due to incomplete combustion, and non-combustible materials are added to make it difficult to burn, and thus are not practical. to be. In addition, in the method of adding coal powder or petroleum coke powder as a calorific reinforcing material, additives are added at least 1.25 to 45 times the amount of paper sludge solids to increase the calorific value of paper sludge. This means that the utilization of waste is significantly reduced. As described above, the fuels described in the existing patents are fuels that do not receive the cost burden and institutional underpinning due to the use of an excessive amount of additives and can be said to be a technology that is practically difficult to spread in the field of use.

폐유의 자원화 기술로는 이온정제법, 감압증류법 그리고 고온 열분해법 등이 있다. 이온정제법은 폐유중 수분과 침전물을 제거하고 약품처리를 통하여 중금속 등을 제거하여 제품을 생산하는 방법이며, 감압증류방법은 박막증류 또는 탑증류 방법의 감압증류 방식은 폐유중의 수분과 침전물 등을 제거하는 전처리 과정을 거친후 진공하에서 열매체를 가열원으로 하여 증류하는 방법이다. 그리고 고온열분해법은 폐유를 450-500℃로 가열하여 라디칼반응에 의하여 고분자를 저분자화 하여 경질유를 얻는 방법이다.Waste oil recycling techniques include ion purification, distillation under reduced pressure, and high temperature pyrolysis. Ion purification method removes water and sediment from waste oil and removes heavy metals through chemical treatment to produce products. Decompression distillation method uses thin film distillation or tower distillation method under reduced pressure distillation method. After the pretreatment process to remove the distillation under vacuum the heating medium as a heating source. The high temperature pyrolysis method is a method of obtaining light oil by heating the waste oil at 450-500 ° C. to lower the polymer by radical reaction.

이와 같이 폐유의 재자원화를 위해서는 몇 개의 공정을 거쳐야만 자원할 수 있다. 그러나 폐유중 폐윤활유의 경우에는 연소시의 악취발생실태를 조사한 결과 배출허용기준 이내로 나타나, 고형화시켜 재생에너지로 활용할 경우에는 상기와 같은 전처리가 필요 없이 직접 소각 처리할 수 있다.As such, in order to recycle waste oil, only a few processes can be used for resources. However, in the case of the waste lubricating oil in the waste oil, the result of the investigation of the occurrence of odor during combustion appears within the emission allowance standard, and when solidified and used as renewable energy, it can be incinerated directly without the need for the above pretreatment.

현재 폐제지슬러지는 땅에 매립하거나 해양투기를 하므로 환경공해를 야기시키고 있으며, 폐유의 경우 이온정제법, 열분해 정제법, 감압증류법 등의 고비용으로 재자원화를 시행하고 있으므로 그 실효성에 의문이 제기되고 있다. 또한 2005년 부터는 상기 제지슬러지의 경우 땅에 매립하는 것을 점차적으로 줄여나가는 방법이 제기되고 있으며, 해양투기 또한 금지하고 있는 실정이다.At present, waste paper sludge is landfilled or dumped at sea, causing environmental pollution, and waste oil is recycled at high cost such as ion purification, pyrolysis and distillation, which raises the question of its effectiveness. have. In addition, since 2005, a method of gradually reducing landfilling of papermaking sludge has been proposed, and marine dumping is also prohibited.

따라서 본 발명은 이러한 폐자원을 자원화하는 방법의 일환으로 폐제지슬러지와 폐유 및 첨가제를 혼합하여 3,500 kcal/kg(저위발열량) 이상의 열량을 얻을 수 있으며, 이와 동시에 연소에 따른 염소나 황의 배출량 그리고 중금속 등을 조절하여 고체연료로서 갖춰야 할 조건(자원절약과 재활용 촉진에 관한 법률 제20조의3 제2항 관련)을 갖는 양질의 고체연료를 제조하는 방법 및 이에 따라 제조된 고체연료를 제공하는 데에 그 목적이 있다. Therefore, the present invention can obtain more than 3,500 kcal / kg (low calorific value) calories by mixing waste paper sludge, waste oil and additives as part of the method of recycling such waste resources, and at the same time emissions of chlorine or sulfur due to combustion and heavy metals To provide high quality solid fuel having the conditions to be equipped as solid fuel (refer to Article 20-3 (2) of the Law on Resource Conservation and Recycling Promotion) and to provide solid fuel produced accordingly. The purpose is.

상기 목적을 달성하기 위하여 본 발명은, The present invention to achieve the above object,

바인더, 유화제 및 폐유를 포함하는 혼합용액을 제조하는 제1단계;A first step of preparing a mixed solution containing a binder, an emulsifier and waste oil;

상기 제1단계에서 제조된 혼합용액에 제지공장에서 배출된 폐제지슬러지를 혼합하여 제1혼합물을 제조하는 제2단계;A second step of preparing a first mixture by mixing the waste paper sludge discharged from the paper mill with the mixed solution prepared in the first step;

상기 제2단계에서 제조된 제1혼합물에 폐제지슬러지 건조 분말 또는 폐지 건 조 분말을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 제2혼합물을 제조하는 제3단계; A third step of preparing a semi-solid state second mixture having a moisture content of 0.01 to 30 wt% by mixing waste paper sludge dry powder or waste paper dry powder with the first mixture prepared in the second step;

상기 제3단계에서 제조된 제2혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4단계; 및 A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the second mixture prepared in the third step into a pellet molding machine; And

상기 제4단계에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5단계를 포함하는 고체연료의 제조방법을 제공한다. It provides a method for producing a solid fuel comprising a fifth step of drying the pellet fuel prepared in the fourth step to a water content of 0.01 to 10% by weight.

또한, 본 발명은, In addition, the present invention,

제지공장에서 배출된 폐제지슬러지를 탈수, 건조 및 분쇄하여 폐제지슬러지 분말을 제조하는 제1공정;A first step of manufacturing waste paper sludge powder by dewatering, drying and grinding waste paper sludge discharged from the paper mill;

바인더, 유화제 및 폐유를 포함하는 혼합용액을 제조하는 제2공정;A second step of preparing a mixed solution containing a binder, an emulsifier, and waste oil;

상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3공정; A third step of preparing a semi-solid mixture having a water content of 0.01 to 30 wt% by mixing the waste paper sludge powder prepared in the first step with the mixed solution prepared in the second step;

상기 제3공정에서 제조된 혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4공정; 및A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the mixture prepared in the third step into a pellet molding machine; And

상기 제4공정에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5공정을 포함하는 고체연료의 제조방법을 제공한다. It provides a method for producing a solid fuel comprising a fifth step of drying the pellet fuel prepared in the fourth step to a moisture content of 0.01 to 10% by weight.

이에 더하여, 본 발명은, In addition, the present invention,

제지공장에서 배출된 폐제지슬러지를 탈수공정 및 건조공정을 통하여 수분함량 0.01 ~ 20중량%가 되도록 한 후, 분쇄기를 통해 30 ~ 100메쉬(mesh) 크기로 분쇄한 폐제지슬러지 분말을 제조하는 제1공정;After the waste paper sludge discharged from the paper mill is dehydrated and dried to have a water content of 0.01 to 20% by weight, and then to produce waste paper sludge powder pulverized to a size of 30 ~ 100 mesh (mesh) through a grinder 1 step;

바인더, 유화제 및 폐유를 혼합하되, 고체연료 총 중량에 대하여 바인더 3 ~ 20중량%, 유화제 0.1 ~ 5중량% 및 폐유 5 ~ 31중량%가 되도록 혼합한 혼합용액을 제조하는 제2공정;A second step of preparing a mixed solution in which a binder, an emulsifier, and waste oil are mixed, such that the binder is 3 to 20% by weight, an emulsifier 0.1 to 5% by weight, and 5 to 31% by weight of waste oil, based on the total weight of the solid fuel;

상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말을 고체연료 총 중량에 대하여 60 ~ 70중량％가 되도록 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3공정;The waste paper sludge powder prepared in the first step was mixed to 60 to 70% by weight based on the total weight of the solid fuel, and the water content was 0.01 to 30% by weight in the mixed solution prepared in the second step. A third step of preparing a mixture;

상기 제3공정에서 제조된 혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4공정; 및A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the mixture prepared in the third step into a pellet molding machine; And

상기 제4공정에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5공정을 포함하는 고체연료의 제조방법을 제공한다. It provides a method for producing a solid fuel comprising a fifth step of drying the pellet fuel prepared in the fourth step to a moisture content of 0.01 to 10% by weight.

또한, 상기 바인더는 친유성 계면활성제, 친수성 유화안정제 및 친유성 유화안정제 중에서 선택된 하나 또는 둘 이상으로 이루어질 수 있다. In addition, the binder may be made of one or two or more selected from lipophilic surfactants, hydrophilic emulsion stabilizers and lipophilic emulsion stabilizers.

아울러, 상기 유화제는 친유성 계면활성제, 친수성 유화안정제 및 친유성 유화안정제 중에서 선택된 하나 또는 둘 이상으로 이루어질 수 있다. In addition, the emulsifier may be made of one or two or more selected from lipophilic surfactants, hydrophilic emulsion stabilizers and lipophilic emulsion stabilizers.

또한, 본 발명은 상기 본 발명에 따른 제조방법에 의해 제조된 펠렛 형태의 고체연료를 제공한다. In addition, the present invention provides a pellet fuel produced by the production method according to the present invention.

본 발명은 3,500 kcal/kg(저위발열량) 이상의 발열량을 가지는 고체연료를 제조할 수 있으며, 이와 동시에 연소에 따른 염소나 황의 배출량 그리고 중금속 등을 조절하여 고체연료로서 갖춰야 할 조건(자원절약과 재활용 촉진에 관한 법률 제20조의3 제2항 관련)을 갖는 양질의 고체연료를 제조할 수 있는 효과를 갖는다. The present invention can produce a solid fuel having a calorific value of more than 3,500 kcal / kg (low calorific value), and at the same time to control the emissions of chlorine or sulfur and heavy metals due to combustion (resource saving and promoting recycling) Has the effect of producing high quality solid fuels with respect to Article 20-3 (2) of the Act.

이하, 본 발명의 실시예를 도시한 첨부된 도면을 참조하여 본 발명을 보다 상세히 설명한다. Hereinafter, with reference to the accompanying drawings showing an embodiment of the present invention will be described in more detail the present invention.

도 1은 본 발명의 제1형태에 따른 고체연료를 제조하기 위한 제조 공정도이고, 도 2는 본 발명의 제2형태에 따른 고체연료를 제조하기 위한 제조 공정도이다. 첨부된 도면에서, (1) 폐유 (2) 바인더 (3) 유화제 (4) 믹스기 (5) 폐제지슬러지 (6) 탈수기 (7) 분쇄기 (8) 폐제지슬러지 분말 (9) 펠렛(pellet)성형기 (10) 반고체상태의 펠렛(pellet) (11) 건조기 (12) 고체연료이다.1 is a manufacturing flow chart for producing a solid fuel according to the first aspect of the present invention, Figure 2 is a manufacturing flow chart for producing a solid fuel according to the second aspect of the present invention. In the accompanying drawings, (1) waste oil (2) binder (3) emulsifier (4) mixer (5) waste paper sludge (6) dehydrator (7) grinder (8) waste paper sludge powder (9) pellets Molding machine (10) Pellets (11) Semi-solid state (12) Dryer (12) Solid fuel.

먼저, 도 1을 참조하여 본 발명의 제1형태를 설명하면 다음과 같다. First, the first embodiment of the present invention will be described with reference to FIG. 1.

도 1은 본 발명의 제1형태에 따라서, 제지공장에서 배출된 상태의 폐제지슬러지(5), 예를 들어 수분함량이 30 ~ 80중량％인 폐제지슬러지(5)를 초기에 사용하여 고체연료(12)를 제조하는 방법을 설명하기 위한 평면 공정 구성도이다. Fig. 1 shows solid waste by first using waste paper sludge 5 in a state discharged from a paper mill, for example, waste paper sludge 5 having a water content of 30 to 80% by weight according to the first aspect of the present invention. It is a planar process block diagram for demonstrating the method of manufacturing the fuel 12.

도 1을 참조하여 설명하면, 본 발명의 제1형태에 따라서 고체연료(12)는, 바인더(2), 유화제(3) 및 폐유(1)를 혼합하는 제1단계(혼합용액 제조단계); 상기 제1단계에서 제조된 혼합용액에 제지공장에서 배출된 폐제지슬러지(5)를 혼합하는 제2단계(제1혼합물 제조단계): 상기 제2단계에서 제조된 혼합물에 수분함량이 0.01 ~ 20중량%인 폐제지슬러지 분말(8) 또는 폐지 분말을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3단계(제2혼합물 제조단계); 및 상기 제3단계에서 제조된 혼합물을 압출하여, 반고체 상태의 펠렛(10) 형태로 고체연료를 제조하는 제4단계(펠렛 형태의 고체연료 제조단계); 및 상기 제4단계에서 제조된 펠렛(10) 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5단계(고체연료의 건조단계)를 통하여 제조된다. Referring to FIG. 1, the solid fuel 12 according to the first aspect of the present invention includes a first step (mixing solution preparation step) of mixing the binder 2, the emulsifier 3, and the waste oil 1; The second step of mixing the waste paper sludge (5) discharged from the paper mill to the mixed solution prepared in the first step (first mixture production step): the water content of 0.01 to 20 in the mixture prepared in the second step A third step (second mixture production step) of mixing the waste paper sludge powder 8 or the waste paper powder by weight to prepare a semi-solid mixture having a water content of 0.01 to 30% by weight; And a fourth step of manufacturing the solid fuel in the form of pellets 10 in a semi-solid state by extruding the mixture prepared in the third step (pellet form solid fuel production step); And a fifth step (drying of the solid fuel) to dry the solid fuel in the form of pellets 10 prepared in the fourth step to have a moisture content of 0.01 to 10 wt%.

이때, 상기 제1단계(혼합용액의 제조단계)에서는, 고체연료 총 중량에 대하여 상기 바인더(2)는 3 ~ 20중량%, 상기 유화제(3)는 0.1 ~ 5중량%, 그리고 상기 폐유(1)는 5 ~ 31중량%가 되도록 믹스기(4)를 이용하여 혼합한다. At this time, in the first step (manufacturing step of the mixed solution), the binder (2) is 3 to 20% by weight, the emulsifier (3) is 0.1 to 5% by weight relative to the total weight of the solid fuel, and the waste oil (1 ) Is mixed using the mixer (4) to be 5 to 31% by weight.

또한, 상기 제2단계(제1혼합물 제조단계)에서는, 상기 제1단계의 혼합용액에 제지공장에서 배출된 폐제지슬러지(5)를 혼합하되, 수분을 제외한 순수 슬러지 중 량이 고체연료 총 중량에 대하여 60 ~ 70중량％가 되도록 혼합한다. 이때, 상기 제지공장에서 배출된 폐제지슬러지(5)는 수분함량이 30 ~ 80중량％인 폐제지슬러지가 사용될 수 있다. In addition, in the second step (first mixture production step), the waste paper sludge 5 discharged from the paper mill is mixed with the mixed solution of the first step, the weight of pure sludge excluding the water to the total weight of the solid fuel It mixes so that it may become 60 to 70 weight% with respect to. At this time, the waste paper sludge 5 discharged from the paper mill may be used waste paper sludge having a water content of 30 to 80% by weight.

그리고 상기 제3단계(제2혼합물 제조단계)에서는, 상기 제2단계에서 제조된 혼합물에 수분함량이 0.01 ~ 20중량%인 폐제지슬러지 분말(8) 또는 폐지 분말을 혼합하는데, 이때 상기 폐제지슬러지 분말(8)은 또는 폐지 분말은 고체연료 총 중량에 대하여 5 ~ 20중량％가 되도록 믹스기(4)에 넣어 혼합한다. 이러한 제3단계를 통하여 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조한다. 상기 제3단계에서, 상기 폐제지슬러지 분말(8)과 폐지 분말은 수분함량 0.01 ~ 20중량%인 것이 사용되는데, 이때 상기 폐제지슬러지 분말(8)은 제지공장에서 배출된 폐제지슬러지(5), 예를 들어 수분함량이 30 ~ 80중량％인 폐제지슬러지(5)를 탈수기(6)를 이용한 탈수공정 및 건조기(11)를 이용한 건조공정을 통하여 수분함량 0.01 ~ 20중량％가 되도록 건조한 후, 분쇄기(7)를 이용하여 분쇄한 것을 사용한다. 아울러, 상기 폐제지슬러지 분말(8)은 분쇄기(7)에서 30 ~ 100메쉬(mesh) 크기로 분쇄될 수 있다. 보다 구체적인 구현예에 따라서, 상기 폐제지슬러지 분말(8)은 수분함량 50 ~ 80 중량％의 폐제지슬러지(5)를 탈수 공정으로 수분함량이 40 중량％ 이하가 되도록 낮춘 후, 진공건조 또는 80℃ ~ 150℃에서 열풍 건조를 통하여 수분함량이 0.01 ~ 20중량％가 되도록 유지시킨 다음, 분쇄기(7)를 통하여 30 ~ 100메쉬(mesh) 크기의 분말 형태로 제조한 것을 사용할 수 있다. 이러한 폐제지슬러지 분말(8)은 고체연료 중의 수분을 흡수하고 기름성분을 흡착시킬 수 있다. In the third step (second mixture production step), the waste paper sludge powder (8) or waste paper powder having a water content of 0.01 to 20% by weight is mixed with the mixture prepared in the second step, wherein the waste paper The sludge powder 8 or waste paper powder is mixed in the mixer 4 so as to be 5 to 20% by weight based on the total weight of the solid fuel. Through this third step, a semi-solid mixture having a moisture content of 0.01 to 30 wt% is prepared. In the third step, the waste paper sludge powder (8) and waste paper powder is used that the water content of 0.01 to 20% by weight, wherein the waste paper sludge powder (8) is waste paper sludge (5) discharged from the paper mill For example, the waste paper sludge (5) having a water content of 30 to 80% by weight is dried to a water content of 0.01 to 20% by weight through a dehydration process using a dehydrator (6) and a drying process using a dryer (11). After that, the crushed using the grinder 7 is used. In addition, the waste paper sludge powder 8 may be ground to a size of 30 ~ 100 mesh (mesh) in the grinder (7). According to a more specific embodiment, the waste paper sludge powder (8) is 50 to 80% by weight of the waste paper sludge (5) by lowering the water content to 40% by weight or less by a dehydration process, vacuum drying or 80 After maintaining the water content to 0.01 to 20% by weight through hot air drying at ℃ ~ 150 ℃, it can be used to prepare a powder form of 30 to 100 mesh (mesh) size through the grinder (7). Such waste paper sludge powder 8 can absorb moisture in solid fuel and adsorb oil components.

상기 제4단계(펠렛 형태의 고체연료 제조단계)에서는, 상기 제3단계에서 제조된 혼합물을 펠렛(pellet) 성형기(9)에 넣고 압출하여, 반고체 상태의 펠렛(10) 형태로 고체연료를 제조한다. 이때, 펠렛(10) 형태의 고체연료는 펠렛 성형기(9)를 통해 직경 30 mm 이하, 길이 100 mm 이하의 크기를 가질 수 있다. In the fourth step (pellet-shaped solid fuel manufacturing step), the mixture prepared in the third step is put into a pellet molding machine (9) and extruded, to produce a solid fuel in the form of a pellet (10) in a semi-solid state do. At this time, the solid fuel in the form of pellet 10 may have a size of less than 30 mm in diameter, less than 100 mm in length through the pellet forming machine (9).

또한, 상기 제5단계(고체연료의 건조단계)에서는, 상기 제4단계에서 제조된 펠렛(10) 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는데, 이때 고체연료(12)의 수분함량이 0.01 ~ 10중량％가 되도록 내부 온도가 80℃ ~ 150℃인 건조기(11)에 넣어 건조할 수 있다. In addition, in the fifth step (drying of the solid fuel), the solid fuel in the form of pellets 10 prepared in the fourth step is dried to a water content of 0.01 to 10% by weight, wherein the solid fuel 12 It may be dried in the dryer 11 having an internal temperature of 80 ° C to 150 ° C so that the moisture content is 0.01 to 10% by weight.

상기 제1형태에 따라 제조된 본 발명에 따른 고체연료(12)는 저위발열량 3,500 kcal/kg 이상을 갖는다. 또한, 상기와 같이 제조된 고체연료(12)는 연소 후 수분을 제외한 중량 기준(건기준)으로 고체연료(12)로서 갖춰야할 조건인 회분 함유량 20 중량％ 이하, 염소 함유량 2.0 중량％ 이하, 황 함유량 0.6중량％ 이하를 만족한다. 아울러, 상기와 같이 제조된 고체연료(12)는, 금속성분이 연소 후 수분을 제외한 중량 기준(건기준)으로 고체연료(12)로서 갖춰야할 조건인 수은 1.20mg/kg 이하, 카드뮴 9.0 mg/kg 이하, 납 200 mg/kg 이하, 비소 13 mg/kg 이하를 만족한다. The solid fuel 12 according to the present invention prepared according to the first aspect has a low calorific value of 3,500 kcal / kg or more. In addition, the solid fuel 12 prepared as described above has a ash content of 20% by weight or less, chlorine content of 2.0% by weight or less, which is a condition to be provided as a solid fuel 12 on a weight basis (dry basis) excluding moisture after combustion. Content 0.6 weight% or less is satisfied. In addition, the solid fuel 12 prepared as described above is a mercury of 1.20mg / kg or less, cadmium 9.0mg /, which is a condition that a metal component should have as a solid fuel 12 on a weight basis (dry basis) excluding moisture after combustion. It satisfies kg or less, lead 200 mg / kg or less, and arsenic 13 mg / kg or less.

다음으로, 도 2를 참조하여 본 발명의 제2형태를 설명하면 다음과 같다. Next, a second embodiment of the present invention will be described with reference to FIG. 2.

도 2는 본 발명의 제2형태에 따라서, 제지공장에서 배출된 상태의 폐제지슬러지(5), 예를 들어 수분함량이 50 ~ 80중량％인 폐제지슬러지(5)를 탈수기(6) 및 건조기(11)를 이용하여 수분함량이 0.01 ~ 20중량%인 폐제지슬러지 분말(8)로 만든 후, 이를 사용하여 고체연료(12)를 제조하는 방법을 설명하기 위한 평면 공정 구성도이다. 2 shows a dehydrator 6 for waste paper sludge 5 in a state discharged from a paper mill, for example, waste paper sludge 5 having a water content of 50 to 80% by weight according to a second aspect of the present invention. After the waste paper sludge powder (8) having a moisture content of 0.01 to 20% by weight using the dryer (11), a planar process configuration diagram for explaining a method for producing a solid fuel (12) using the same.

도 2를 참조하여 설명하면, 본 발명의 제2형태에 따라서 고체연료(12)는, 제지공장에서 배출된 폐제지슬러지(5)를 이용하여 폐제지슬러지 분말(8)을 제조하는 제1공정(분말 제조공정); 바인더(2), 유화제(3) 및 폐유(1)를 혼합하는 제2공정(혼합용액 제조공정); 상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말(5)을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3공정(혼합물 제조공정); 상기 제3공정에서 제조된 혼합물을 압출하여, 반고체 상태의 펠렛(10) 형태로 고체연료를 제조하는 제4공정(펠렛 형태의 고체연료 제조공정); 및 상기 제4공정에서 제조된 펠렛(10) 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5공정(고체연료의 건조공정)을 통하여 제조된다. Referring to Figure 2, according to the second aspect of the present invention, the solid fuel 12 is a first step of producing waste paper sludge powder 8 using the waste paper sludge 5 discharged from the paper mill. (Powder manufacturing process); A second step of mixing the binder 2, the emulsifier 3, and the waste oil 1 (mixed solution production step); A third step of preparing a semi-solid mixture having a water content of 0.01 to 30 wt% by mixing the waste paper sludge powder 5 prepared in the first step with the mixed solution prepared in the second step (mixture preparation) fair); Extruding the mixture prepared in the third process to produce a solid fuel in the form of a pellet (10) in a semi-solid state (solid fuel production process of the pellet form); And a fifth process (drying of solid fuel) for drying the solid fuel in the form of pellets 10 prepared in the fourth process to have a moisture content of 0.01 to 10% by weight.

상기 제1공정에서는, 제지공장에서 배출된 폐제지슬러지(5), 예를 들어 수분함량이 30 ~ 80중량％인 폐제지슬러지(5)를 탈수기(6)를 이용한 탈수공정 및 건조기(11)를 이용한 건조공정을 통하여 수분함량 0.01 ~ 20중량％가 되도록 건조한 후, 분쇄하여 폐제지슬러지 분말(8)을 제조한다. 이때, 상기 폐제지슬러지 분말(8)은 분쇄기(7)를 통해 30 ~ 100메쉬(mesh) 크기를 갖도록 분쇄된다. 보다 구체적인 구현예에 따라서, 상기 폐제지슬러지 분말(8)은 수분함량 50 ~ 80 중량％의 폐제지슬러지(5)를 탈수공정으로 수분함량이 40 중량％ 이하가 되도록 낮춘 후, 진 공건조 또는 80℃ ~ 150℃에서 열풍 건조를 통하여 수분함량이 0.01 ~ 20중량％가 되도록 유지시킨 다음, 분쇄기(7)를 통하여 30 ~ 100메쉬(mesh) 크기의 분말 형태로 제조된다. In the first step, the waste paper sludge 5 discharged from the paper mill, for example, the waste paper sludge 5 having a water content of 30 to 80% by weight using the dehydrator 6 and the dryer 11 Through a drying step using a dried to a water content of 0.01 to 20% by weight, and then pulverized to produce a waste paper sludge powder (8). At this time, the waste paper sludge powder 8 is crushed to have a size of 30 ~ 100 mesh (mesh) through the grinder (7). According to a more specific embodiment, the waste paper sludge powder (8) is a water content of 50 to 80% by weight of the waste paper sludge (5) by a dehydration process to lower the water content to 40% by weight or less, vacuum drying or The water content is maintained at 0.01 to 20% by weight through hot air drying at 80 ° C. to 150 ° C., and then, a powder of a size of 30 to 100 mesh is manufactured through a grinder 7.

이때, 상기 제2공정(혼합용액의 제조공정)에서는, 고체연료 총 중량에 대하여 상기 바인더(2)는 3 ~ 20중량%, 상기 유화제(3)는 0.1 ~ 5중량%, 그리고 상기 폐유(1)는 5 ~ 31중량%가 되도록 믹스기(22)를 이용하여 혼합한다. At this time, in the second step (manufacturing process of the mixed solution), the binder (2) is 3 to 20% by weight, the emulsifier (3) is 0.1 to 5% by weight, and the waste oil (1) ) Is mixed using the mixer 22 to 5 to 31% by weight.

상기 제3공정(혼합물 제조공정)에서는, 상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말(5)을 혼합하는데, 이때 고체연료 총 중량에 대하여 폐제지슬러지 분말(5)이 60 ~ 70중량％가 되도록 믹스기(22)에 넣어 혼합한다. 이러한 제3공정을 통하여 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조한다. In the third step (mixture manufacturing step), the waste paper sludge powder (5) prepared in the first step is mixed with the mixed solution prepared in the second step, wherein the waste paper sludge powder with respect to the total weight of the solid fuel It puts into the mixer 22 so that (5) may be 60 to 70 weight%, and mixes. Through this third process, a semi-solid mixture having a water content of 0.01 to 30% by weight is prepared.

또한, 상기 제4공정(펠렛 형태의 고체연료 제조공정)에서는, 상기 제3공정에서 제조된 혼합물을 펠렛(pellet) 성형기(9)에 넣고 압출하여, 반고체 상태의 펠렛(10) 형태로 고체연료를 제조한다. 이때, 펠렛(10) 형태의 고체연료는 펠렛 성형기(9)를 통해 직경 30 mm 이하, 길이 100 mm 이하의 크기를 가질 수 있다. In addition, in the fourth step (pellet-shaped solid fuel manufacturing step), the mixture prepared in the third step is put into a pellet molding machine (9) and extruded, the solid fuel in the form of a semi-solid pellet (10) To prepare. At this time, the solid fuel in the form of pellet 10 may have a size of less than 30 mm in diameter, less than 100 mm in length through the pellet forming machine (9).

아울러, 상기 제5공정(고체연료의 건조공정)에서는, 상기 제4공정에서 제조된 펠렛(10) 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는데, 이때 고체연료(12)의 수분함량이 0.01 ~ 10중량％가 되도록 내부 온도가 70℃ ~ 150℃인 진공 건조기(11)에 넣어 건조할 수 있다. In addition, in the fifth step (drying of the solid fuel), the solid fuel in the form of pellets 10 prepared in the fourth step is dried to have a water content of 0.01 to 10% by weight, wherein the solid fuel 12 It may be dried in a vacuum dryer 11 having an internal temperature of 70 ° C to 150 ° C so that the moisture content is 0.01 to 10% by weight.

상기 제2형태에 따라 제조된 본 발명에 따른 고체연료(12)는 저위발열량 3,500 kcal/kg 이상을 갖는다. 또한, 상기와 같이 제조된 고체연료(12)는 연소 후 수분을 제외한 중량 기준(건기준)으로 고체연료(12)로서 갖춰야할 조건인 회분 함유량 20 중량％ 이하, 염소 함유량 2.0 중량％ 이하, 황 함유량 0.6중량％ 이하를 만족한다. 아울러, 상기와 같이 제조된 고체연료(12)는, 금속성분이 연소 후 수분을 제외한 중량 기준(건기준)으로 고체연료(12)로서 갖춰야할 조건인 수은 1.20mg/kg 이하, 카드뮴 9.0 mg/kg 이하, 납 200 mg/kg 이하, 비소 13 mg/kg 이하를 만족한다. The solid fuel 12 according to the present invention manufactured according to the second aspect has a low calorific value of 3,500 kcal / kg or more. In addition, the solid fuel 12 prepared as described above has a ash content of 20% by weight or less, chlorine content of 2.0% by weight or less, which is a condition to be provided as a solid fuel 12 on a weight basis (dry basis) excluding moisture after combustion. Content 0.6 weight% or less is satisfied. In addition, the solid fuel 12 prepared as described above is a mercury of 1.20mg / kg or less, cadmium 9.0mg /, which is a condition that a metal component should have as a solid fuel 12 on a weight basis (dry basis) excluding moisture after combustion. It satisfies kg or less, lead 200 mg / kg or less, and arsenic 13 mg / kg or less.

본 발명(상기 제1형태 및 제2형태)에서, 상기 바인더와 유화제는 각각 친유성 계면활성제, 친수성 유화안정제 및 친유성 유화안정제 중에서 선택된 하나 또는 둘 이상으로 이루어질 수 있다. 이때, 상기 바인더와 유화제는, 구체적인 예를 들어 폴리비닐아세테이트(Poly Vinyl Acetate)를 사용할 수 있다. In the present invention (the first and second forms), the binder and the emulsifier may be composed of one or two or more selected from lipophilic surfactants, hydrophilic emulsion stabilizers and lipophilic emulsion stabilizers, respectively. At this time, the binder and the emulsifier may be used, for example, poly vinyl acetate (Poly Vinyl Acetate).

한편, 본 발명의 고체연료를 제조하기 위해서는 먼저 폐유의 종류에 따른 성분조사와 각 제지회사별로 배출되는 제지슬러지의 특성 연구가 선행되어야 하므로 다음과 같이 [표 1]에 폐유의 종류에 따른 성분조사와 [표 2]에 전국의 200여개 공장중 38개 공장(총생산량의 약 56중량％)에서 하루 발생되는 폐제지슬러지의 양과 물성에 관하여 조사하였다.On the other hand, in order to manufacture the solid fuel of the present invention, first, the component investigation according to the type of waste oil and the characteristics of the paper sludge discharged by each paper company must be preceded. In Table 2, the amount and physical properties of waste paper sludge produced in 38 plants (about 56% by weight of total output) out of 200 plants nationwide were investigated.

[표 1] 폐유의 종류에 따른 성분조사[Table 1] Component investigation according to the type of waste oil

Figure 112009018402097-pat00001
Figure 112009018402097-pat00001

폐유의 경우 종류에 따른 황의 함량이 상이하므로 고체연료 제조 시에 0.6 중량％ 이하가 되도록 고려하여 혼합하여야 할 것이다. 그러나 폐제지슬러지 중에는 탄산칼슘 성분이 포함되어 있으며, 이러한 탄산칼슘은 황의 흡착 능력이 우수하다는 연구 결과가 있으므로, 이로 인한 대기 중의 황의 배출은 어느정도 차단되는 효과를 갖게 될 것이다.Since the amount of sulfur varies depending on the type of waste oil, the waste oil should be mixed in consideration of 0.6 wt% or less. However, waste paper sludge contains calcium carbonate, and these studies show that calcium carbonate has excellent sulfur adsorption capacity. Thus, the discharge of sulfur into the air will be somewhat blocked.

[표 2] 제지 생산 품목별 배출 슬러지의 특성[Table 2] Characteristics of discharged sludge by paper production item

제지종류
(Papers)Paper Type
(Papers) 슬러지 생산
(sludge production, 중량%)Sludge production
(sludge production, weight percent) 고체
(solid, 중량%)solid
(solid, weight percent) 재
(ash, 중량%)ashes
(ash, weight percent) 셀룰로오스
(cellulose, 중량%)cellulose
(cellulose, wt%) 종이
(Paper)paper
(Paper) 21.8721.87 32.3432.34 30.0830.08 46.1946.19 신문용지
(News print paper)Newspaper
(News print paper) 28.6028.60 28.9228.92 31.9231.92 40.6240.62 크래프트지
(Kraft paper)Kraft paper
(Kraft paper) 14.8614.86 28.4528.45 15.4515.45 61.2061.20 우드프리페이퍼
(Woodfree paper)Wood Free Paper
(Woodfree paper) 5.795.79 35.2035.20 59.6359.63 28.9528.95 화장지
(Tissues)paper towel
(Tissues) 31.7031.70 34.9334.93 36.5836.58 39.3739.37 기타
(Others)Etc
(Others) 8.148.14 30.0830.08 34.7434.74 35.0735.07 평균
(Average)Average
(Average) 20.7520.75 31.0431.04 32.1132.11 43.4443.44

폐제지슬러지의 고형분함량은 탈수 정도를 나타내는바 탈수가 많이 진행된 것일수록, 즉 고형분 함량이 낮은 것일수록 유동성이 적어 다루기 쉽고 전체 물량이 적어져 운반 및 기타 후속처리가 용이하다.The solid content of the waste paper sludge indicates the degree of dehydration. The more the dehydration proceeds, that is, the lower the solid content, the lower the fluidity, the easier it is to handle, and the smaller the total quantity, the easier the transport and other subsequent treatment.

폐제지슬러지의 탈수 정도는 첫째, 폐제지슬러지 고유의 물빠짐 성질과 둘째, 탈수장비의 성능에 의해 결정된다. 최근 환경오염에 관한 관심이 높아지고 그에 대한 규제가 심해져서 공해방지를 위한 투자가 증대하고 폐수처리도 활성 오니법을 적용한 생물학적 처리가 보편화 경향을 보인다. 따라서 탈수가 매우 어려운 활성오니 제지슬러지의 발생이 증가하고 있다. 탈수장비는 공장에 따라 다양하지만 성능면에서 우수한 벨트 프레스(Belt Press)를 대부분의 공장에서 사용하고 있다.The degree of dewatering of waste paper sludge is determined firstly by the inherent water drainage characteristics of waste paper sludge and secondly by the performance of dewatering equipment. Recently, with increasing interest in environmental pollution and severe regulation, investment for pollution prevention is increasing, and biological treatment using activated sludge treatment is also becoming more common. Therefore, the generation of activated sludge paper sludge is very difficult to dehydrate. Dewatering equipment varies from factory to factory, but belt presses that are superior in performance are used in most plants.

또한 제지 공장에서의 폐제지슬러지의 회분은 종이의 용재에 따라 활석, 고령토, 탄산칼슘 등의 각종 광물질 충진제를 첨가하고 있으며, 이들 충진제는 많은 양이 폐수중에 섞여서 방출되어 이들이 폐수처리과정에서 폐제지슬러지의 요인이 된다. 따라서 저렴한 펄프와 다량의 충진제를 사용하는 백상지 공장의 폐제지슬러지 회분함량은 매우 높아서 성능이 좋은 백상지 공장의 폐제지슬러지에서는 유기성분이 별로 없고 70중량％ 이상의 회분을 함유한 것도 있다. 본 발명의 고체연료 제조를 위한 회분실험에서는 800℃에서 1g의 분쇄 폐제지슬러지를 사용하여 회분실험을 수행한 결과 페제지슬러지에 함유된 회분의 함량은 평균 0.08중량％였다.Also, the ash of waste paper sludge in the paper mill is added with various mineral fillers such as talc, kaolin and calcium carbonate, depending on the paper material, and these fillers are released in a large amount by mixing them in the wastewater. It is a factor of sludge. Therefore, the waste paper sludge ash content of the woody paper mill using low-cost pulp and a large amount of filler is very high, and the waste paper sludge of the woody paper mill, which has good performance, contains little organic component and contains more than 70% by weight of ash. In the ash test for the preparation of the solid fuel of the present invention, the ash content in the waste paper sludge was 1 g at 800 ° C., and the content of ash contained in the waste paper sludge was 0.08% by weight.

또한 수분함량이 70중량％ 정도인 폐제지슬러지를 연료화하기 위해서는 폐제지슬러지의 수분에 대한 증발속도와 최대 함수율 등에 대한 기초 자료가 필요하므로 다음의 실험을 수행하였다.In addition, in order to fuel waste paper sludge having a water content of about 70% by weight, basic data on the evaporation rate and the maximum water content of waste paper sludge were needed.

첫 번째로 폐지슬러지의 수분에 관한 특성을 알아보기 위하여 수분의 함수율을 실험한 결과 제지공장에서 배출된 폐제지슬러지에는 평균 27중량％의 순수 제지슬러지와 73중량％의 수분이 함유되어 있음을 알 수 있었다. 또한 수분의 증발속도를 측정한 결과는 도 3과 같으며 결과식은 다음과 같다. 이와 같은 실험의 결과로 수분의 증발속도는 시간에 정비례함을 알 수 있다.First, the moisture content test of waste paper sludge was carried out to find out the moisture content of waste paper sludge discharged from the paper mill and found that 27% by weight of pure paper sludge and 73% by weight of water are contained. Could. In addition, the result of measuring the evaporation rate of water is shown in Figure 3 and the resulting equation is as follows. As a result of this experiment, it can be seen that the evaporation rate of water is directly proportional to time.

V(증발속도, g/sec) = 0.99948×Time(sec) - 4.87372×10-5 V (evaporation rate, g / sec) = 0.99948 × Time (sec)-4.87372 × 10 -5

두번째로 분쇄 폐제지슬러지의 최대 수분 함수율에 대한 실험을 실시하였다.Secondly, an experiment on the maximum water content of the ground waste paper sludge was carried out.

즉, 폐제지슬러지가 단위 질량당 최대로 함유할 수 있는 수분의 함량을 측정하기 위하여 80℃에서 분쇄 폐제지슬러지를 티백에 1.00 g씩 담아 티백이 흡수하는 물의 양을 측정한 결과 약 4분만에 평형상태에 도달하였으며, 그 결과는 도 4와 같으며 분쇄제지슬러지의 최대 함수율은 약 320％였다. That is, in order to measure the maximum amount of water that the waste paper sludge can contain per unit mass, 1.00 g of the ground waste paper sludge was put into the tea bag at 80 ° C. and the amount of water absorbed by the tea bag was measured in about 4 minutes. Equilibrium was reached, and the result was as shown in FIG. 4, and the maximum water content of the pulverized paper sludge was about 320%.

세번째로 분쇄한 폐제지슬러지에 대한 첨가제의 흡착 효율을 고려하기 위하여 비표면적(BET법)에 대한 실험을 실시하였다.Third, experiments on specific surface area (BET method) were carried out to consider the adsorption efficiency of additives on the ground paper sludge.

80℃에서 72시간 동안 건조시킨 분쇄 폐제지슬러지의 BET법에 따른 비표면적 측정 결과는 [표 3]과 같으며, 평균 비표면적은 5.903 m2/g이었다.Specific surface area measurement results according to the BET method of the pulverized waste paper sludge dried at 80 ℃ for 72 hours are shown in Table 3, the average specific surface area was 5.903 m 2 / g.

[표 3] BET 측정 결과[Table 3] BET measurement results

번호(No.)No. 시료
(Sample, g)sample
(Sample, g) 흡착물질
(Absorbate)Adsorption material
(Absorbate) 분석시간
(Analysis Time, min)Analysis time
(Analysis Time, min) BET 비표면적
(m2/g)BET specific surface area
(m 2 / g) 1One 0.32250.3225 질소
(Nitrozen)nitrogen
(Nitrozen) 238238 5.2095.209 22 0.26690.2669 질소
(Nitrozen)nitrogen
(Nitrozen) 187187 6.6666.666 33 0.52340.5234 질소
(Nitrozen)nitrogen
(Nitrozen) 3232 5.8335.833

네 번째로는 폐제지슬러지와 폐유와의 최적혼합비를 선택하기 위하여 여러 비율에 따른 실험을 수행하였다.Fourthly, experiments were conducted at various ratios to select the optimal mixing ratio between waste paper sludge and waste oil.

분쇄한 폐제지슬러지를 용도에 따라 재 성형할 때 폐유 등의 액상 첨가제와의 혼합 후 재 성형에 적당한 최적의 농도를 선택하기 위하여 80℃에 72시간 동안 건조된 폐제지슬러지를 분쇄한 후, 총량이 1200 g이 되도록 폐제지슬러지와 폐유와의 혼합비를 1:1, 1:2, 1:3, 3:1, 2:1의 중량비로 각각 혼합한 다음, 분쇄기를 이용하여 재 분쇄한 후 각각의 성상을 비교한 결과 중량비가 3:1(폐제지슬러지:폐유) 인 경우가 가장 적당한 성상을 형성하였다. 이때의 판별 기준은 액상 성분 중 수분이 너무 많으면 건조에 막대한 지장을 초래하며, 액상이 적으면 재성형시에 원하는 모양을 만들 수 없기 때문에 육안과 재성형시의 편리성 그리고 증발속도 등 고려하여 적당한 중량비를 선택하였다.When remolding the waste paper sludge according to the application, after mixing with liquid additives such as waste oil, the waste paper sludge dried at 80 ° C. for 72 hours is selected in order to select an optimal concentration suitable for the reforming. The mixing ratio between the waste paper sludge and the waste oil was mixed at a weight ratio of 1: 1, 1: 2, 1: 3, 3: 1, and 2: 1 so as to be 1200 g, and then crushed again using a grinder. The weight ratio of 3: 1 (waste paper sludge: waste oil) produced the most suitable properties. At this time, the criterion for determination is that too much moisture in the liquid component causes enormous obstacles to drying, and if the liquid content is small, the desired shape can not be formed during re-forming, so it is appropriate considering the convenience of visual and re-forming and evaporation rate. The weight ratio was selected.

다섯 번째로는 고체연료의 내부의 응집력 및 표면강도를 향상시키기 위해서 바인더의 함량에 따른 실험을 수행하였다. 특히 바인더의 양은 상기의 폐제지슬러지와 폐유와의 최적혼합비에 따라 고체상의 총량에 대한 바인더의 비를 100 : 3, 100 : 6, 100 : 9, 100 : 12, 100 : 15의 중량비로 하여 측정한 경우 100 : 7.3정도가 최적 조건임을 알 수 있었다.Fifth, experiments were conducted according to the binder content to improve the cohesion and surface strength of the solid fuel. In particular, the amount of binder is measured by the ratio of the binder to the total amount of the solid phase in the weight ratio of 100: 3, 100: 6, 100: 9, 100: 12, 100: 15 according to the optimum mixing ratio between the waste paper sludge and the waste oil. In one case, the optimum condition was 100: 7.3.

＜ 실시 예 1 ＞<Example 1>

우드프리페이퍼(Woodfree paper)를 주로 생산하는 공장의 폐제지슬러지를 주원료로 하여 고체연료를 제조하였다. 이때 61중량％의 폐제지슬러지와 31중량％의 폐유와 7중량％의 바인더, 그리고 폴리비닐아세테이트(Poly Vinyl Acetate) 0.5중량％와 프로필 알코올(propyl alcohol 0.5중량％로 구성되는 혼합물을 이용하여 직경 6 mm 이하, 길이 20 mm 이하인 펠렛(pellet) 형태로 만들고, 이후 150℃열로 건조하여 고체연료를 제조하였다. 하기 표 4에 보인 바와 같이, 제조된 고체연료는, 저위발열량이 3,500 kcal/kg 이상이며, 수분함량이 10 중량％ 이하이고, 연소 후 수분을 제외한 중량 기준(건기준)으로 고체연료로서 갖춰야할 조건인 회분 함유량 20 중량％ 이하, 염소 함유량 2.0 중량％ 이하, 황 함유량 0.6 중량％ 이하, 그리 고 금속성분은 수은 1.20mg/kg 이하, 카드뮴 9.0 mg/kg 이하, 납 200 mg/kg 이하, 비소 13 mg/kg 이하의 조건을 만족함을 알 수 있었다. Solid fuel was manufactured using waste paper sludge as a main raw material of a factory that mainly produces woodfree paper. In this case, the diameter was determined using a mixture comprising 61% by weight of waste paper sludge, 31% by weight of waste oil, 7% by weight of binder, and 0.5% by weight of polyvinyl acetate and 0.5% by weight of propyl alcohol. It was made into a pellet (pellet) of 6 mm or less, 20 mm or less in length, and then dried by heat at 150 ° C. As shown in Table 4, the produced solid fuel had a low calorific value of 3,500 kcal / kg or more. Moisture content of 10% by weight or less, ash content of 20% by weight or less, chlorine content of 2.0% by weight or less, sulfur content of 0.6% by weight or less, which is a condition to be provided as a solid fuel on a weight basis (dry basis) excluding moisture after combustion. In addition, it was found that the metal component satisfies the following conditions: mercury 1.20 mg / kg or less, cadmium 9.0 mg / kg or less, lead 200 mg / kg or less, and arsenic 13 mg / kg or less.

[표 4] 우드프리페이퍼(Woodfree paper) 공장의 제지슬러지를 이용한 고체연료 시험 결과[Table 4] Solid fuel test results using paper sludge from Woodfree paper factory

Figure 112009018402097-pat00002
Figure 112009018402097-pat00002

＜ 실시 예 2 ＞<Example 2>

뉴스프린트페이퍼(News print paper)를 주로 생산하는 공장의 폐제지슬러지를 주원료로 하여 고체연료를 제조하였다. 이때 61중량％의 폐제지슬러지와 31중량％의 폐유와 7중량％의 바인더 그리고 폴리비닐아세테이트(Poly Vinyl Acetate) 0.5중량％와 프로필 알코올(propyl alcohol) 0.5중량％로 구성되는 혼합물을 이용하여 고체연료를 제조하였다. 이에 따라 제조된 고체연료의 분석결과를 하기 표 5에 나타내었다. Solid fuel was prepared using waste paper sludge as a main raw material of a factory that mainly produces news print paper. At this time, solid by using a mixture consisting of 61% by weight waste paper sludge, 31% by weight waste oil, 7% by weight binder, 0.5% by weight of poly vinyl acetate and 0.5% by weight of propyl alcohol Fuel was prepared. The analysis results of the solid fuel thus prepared are shown in Table 5 below.

[표 5] 뉴스프린트페이퍼(News print paper) 공장의 폐제지슬러지를 이용한 고체연료 시험 결과[Table 5] Solid fuel test results using waste paper sludge from News print paper factory

Figure 112009018402097-pat00003
Figure 112009018402097-pat00003

지난 2004년 기준 폐기물처리방식의 기준으로 볼 때, 아직도 자원회수가 가능한 가연성 폐기물의 60중량％ 이상이 매립되고 있다. 그러나 매립처리에 대한 규제강화로 인하여 폐제지슬러지의 경우 발생량 대비 40중량％ 정도가 해양투기 등의 방법으로 처리를 해오고 있으며, 폐유의 경우 발생량 대비 약 30중량％가 매립에 의하여 처리되고 있다. In 2004, more than 60% by weight of combustible waste, which is still recoverable, is landfilled. However, about 40% by weight of waste paper sludge has been treated by ocean dumping, etc. due to the strengthening of regulations on landfill treatment, and about 30% by weight of waste oil is processed by landfilling.

따라서 본 발명에 따라서 폐제지슬러지 및 폐유의 재생 에너지로의 활용은 근래에 환경부에서 주장하는 "자원순환"과 "지속가능한 발전"에 크게 부합된다 할 수 있다.Therefore, according to the present invention, the utilization of waste paper sludge and waste oil as renewable energy can be said to be largely in line with "resource circulation" and "sustainable power generation" insisted by the Ministry of Environment.

또한 2002년 기준으로 폐제지슬러지의 경우 약 60만 톤/년이 위탁 처리되고 있으며, 위탁처리비용은 32,000 원/톤이므로 약 200억원/년의 처리비용 절감효과를 가지며, 약 4억L/년 이상의 폐유 발생에 대한 처리비용이 25원/L로서, 재생업체의 경우 약 100억원의 수익 효과가 발생한다. 하기 표 6은 연도별 슬러지 처리내역 및 처리비용을 나타낸 것이다. As of 2002, about 600,000 tons / year of consigned paper sludge is consigned, and the consignment treatment cost is 32,000 won / ton, which reduces the processing cost of about 20 billion KRW / year, and about 400 million L / year. The disposal cost for waste oil generation is W25 / L, which will generate profits of W10bn for recycling companies. Table 6 shows the sludge treatment history and treatment costs for each year.

[표 6] 슬러지 처리내역 및 처리비용[Table 6] Sludge Treatment Details and Treatment Costs

Figure 112009018402097-pat00004
Figure 112009018402097-pat00004

도 1은 본 발명의 제1형태에 따른 고체연료(12)를 제조하는 공정도이다.1 is a process chart for producing a solid fuel 12 according to the first aspect of the present invention.

도 2는 본 발명의 제2형태에 따른 고체연료(12)를 제조하는 공정도이다.2 is a process chart for producing the solid fuel 12 according to the second aspect of the present invention.

＜도면의 주요부분에 대한 부호의 설명＞Description of the Related Art

(1) 폐유 (2) 바인더 (3) 유화제 (4) 믹스기 (5) 젖은폐제지슬러지 (6) 탈수기 (7)분쇄기 (8) 폐제지슬러지 분말 (9) 펠렛성형기 (10) 반고체상태 펠렛 (11) 건조기 (12)고체연료(1) Waste oil (2) Binders (3) Emulsifiers (4) Mixers (5) Wet waste paper sludge (6) Dehydrator (7) Grinder (8) Waste paper sludge powder (9) Pellet forming machine (10) Semi-solid pellets (11) Dryers (12) Solid fuels

Claims (10)

바인더, 유화제 및 폐유를 포함하는 혼합용액을 제조하는 제1단계;A first step of preparing a mixed solution containing a binder, an emulsifier and waste oil; 상기 제1단계에서 제조된 혼합용액에 제지공장에서 배출된 폐제지슬러지를 혼합하여 제1혼합물을 제조하는 제2단계;A second step of preparing a first mixture by mixing the waste paper sludge discharged from the paper mill with the mixed solution prepared in the first step; 상기 제2단계에서 제조된 제1혼합물에 폐제지슬러지 건조 분말 또는 폐지 건조 분말을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 제2혼합물을 제조하는 제3단계; A third step of preparing a semi-solid state second mixture having a moisture content of 0.01 to 30 wt% by mixing waste paper sludge dry powder or waste paper dry powder with the first mixture prepared in the second step; 상기 제3단계에서 제조된 제2혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4단계; 및 A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the second mixture prepared in the third step into a pellet molding machine; And 상기 제4단계에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5단계를 포함하는 것을 특징으로 하는 특징으로 하는 고체연료의 제조방법.Method for producing a solid fuel, characterized in that it comprises a fifth step of drying the pellet fuel prepared in the fourth step to the water content of 0.01 to 10% by weight. 제지공장에서 배출된 폐제지슬러지를 탈수, 건조 및 분쇄하여 폐제지슬러지 분말을 제조하는 제1공정;A first step of manufacturing waste paper sludge powder by dewatering, drying and grinding waste paper sludge discharged from the paper mill; 바인더, 유화제 및 폐유를 포함하는 혼합용액을 제조하는 제2공정;A second step of preparing a mixed solution containing a binder, an emulsifier, and waste oil; 상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말을 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3공정; A third step of preparing a semi-solid mixture having a water content of 0.01 to 30 wt% by mixing the waste paper sludge powder prepared in the first step with the mixed solution prepared in the second step; 상기 제3공정에서 제조된 혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4공정; 및A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the mixture prepared in the third step into a pellet molding machine; And 상기 제4공정에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5공정을 포함하는 것을 특징으로 하는 고체연료의 제조방법. And a fifth step of drying the pellet-shaped solid fuel prepared in the fourth step so as to have a moisture content of 0.01 to 10% by weight. 제지공장에서 배출된 폐제지슬러지를 탈수공정 및 건조공정을 통하여 수분함량 0.01 ~ 20중량%가 되도록 한 후, 분쇄기를 통해 30 ~ 100메쉬(mesh) 크기로 분쇄한 폐제지슬러지 분말을 제조하는 제1공정;After the waste paper sludge discharged from the paper mill is dehydrated and dried to have a water content of 0.01 to 20% by weight, and then to produce waste paper sludge powder pulverized to a size of 30 ~ 100 mesh (mesh) through a grinder 1 step; 바인더, 유화제 및 폐유를 혼합하되, 고체연료 총 중량에 대하여 바인더 3 ~ 20중량%, 유화제 0.1 ~ 5중량% 및 폐유 5 ~ 31중량%가 되도록 혼합한 혼합용액을 제조하는 제2공정;A second step of preparing a mixed solution in which a binder, an emulsifier, and waste oil are mixed, such that the binder is 3 to 20% by weight, an emulsifier 0.1 to 5% by weight, and 5 to 31% by weight of waste oil, based on the total weight of the solid fuel; 상기 제2공정에서 제조된 혼합용액에 상기 제1공정에서 제조된 폐제지슬러지 분말을 고체연료 총 중량에 대하여 60 ~ 70중량％가 되도록 혼합하여, 수분함량이 0.01 ~ 30중량%인 반고체 상태의 혼합물을 제조하는 제3공정;The waste paper sludge powder prepared in the first step was mixed to 60 to 70% by weight based on the total weight of the solid fuel, and the water content was 0.01 to 30% by weight in the mixed solution prepared in the second step. A third step of preparing a mixture; 상기 제3공정에서 제조된 혼합물을 펠렛(pellet) 성형기에 넣고 압출하여 반고체 상태의 펠렛 형태의 고체연료를 제조하는 제4공정; 및A fourth step of preparing a solid fuel in a pellet form in a semi-solid state by inserting the mixture prepared in the third step into a pellet molding machine; And 상기 제4공정에서 제조된 펠렛 형태의 고체연료를 수분함량 0.01 ~ 10중량％가 되도록 건조하는 제5공정을 포함하는 고체연료의 제조방법. And a fifth step of drying the pellet-shaped solid fuel prepared in the fourth step so as to have a moisture content of 0.01 to 10% by weight. 삭제delete 제1항 내지 제3항 중 어느 한 항에 있어서,The method according to any one of claims 1 to 3, 상기 폐유는 자동차유, 선박유, 절연유, 기어유 및 터빈유 중에서 선택된 하나 또는 둘 이상의 혼합폐유인 것을 특징으로 하는 고체연료의 제조방법. The waste oil is a method of producing a solid fuel, characterized in that one or two or more mixed waste oil selected from automobile oil, ship oil, insulating oil, gear oil and turbine oil. 삭제delete 삭제delete 삭제delete 제1항 내지 제3항 중 어느 한 항에 따른 제조방법에 의해 제조된 것을 특징으로 하는 펠렛 형태의 고체연료. A solid fuel in the form of pellets, which is prepared by the process according to any one of claims 1 to 3. 삭제delete
KR1020090026129A 2009-03-26 2009-03-26 Solid fuel of pellet form and method for preparing the same KR101033860B1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
KR1020090026129A KR101033860B1 (en) 2009-03-26 2009-03-26 Solid fuel of pellet form and method for preparing the same

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
KR1020090026129A KR101033860B1 (en) 2009-03-26 2009-03-26 Solid fuel of pellet form and method for preparing the same

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
KR1020070083404A Division KR20090019168A (en) 2007-08-20 2007-08-20 Solid fuel of pellet form and method for preparation there of

Publications (2)

Publication Number Publication Date
KR20090045161A KR20090045161A (en) 2009-05-07
KR101033860B1 true KR101033860B1 (en) 2011-05-16

Family

ID=40855491

Family Applications (1)

Application Number Title Priority Date Filing Date
KR1020090026129A KR101033860B1 (en) 2009-03-26 2009-03-26 Solid fuel of pellet form and method for preparing the same

Country Status (1)

Country Link
KR (1) KR101033860B1 (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101539224B1 (en) * 2014-08-29 2015-07-27 동하정보기술 주식회사 Method for preparing biomass solid refuse fuel
KR102212866B1 (en) * 2020-09-08 2021-02-05 한양대학교 산학협력단 Manure of livestock resourceization device and method

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101310121B1 (en) * 2012-06-19 2013-09-17 남혜정 Solid fuel and manufacturing method thereof
KR101722114B1 (en) 2015-08-11 2017-04-04 주식회사 뷰티라인 Manufacturing method of solid fuel using laver waste

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS568493A (en) * 1979-07-03 1981-01-28 Masayuki Yokozawa Reclaimed waste powder fuel
JPS5662891A (en) * 1979-10-26 1981-05-29 Murooka Yoichi Preparation of solid fuel from waste
JPS60112892A (en) * 1983-11-22 1985-06-19 Kansai Sangyo Kk Process for producing solid fuel from industrial waste
KR100443472B1 (en) * 1995-11-08 2004-10-15

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS568493A (en) * 1979-07-03 1981-01-28 Masayuki Yokozawa Reclaimed waste powder fuel
JPS5662891A (en) * 1979-10-26 1981-05-29 Murooka Yoichi Preparation of solid fuel from waste
JPS60112892A (en) * 1983-11-22 1985-06-19 Kansai Sangyo Kk Process for producing solid fuel from industrial waste
KR100443472B1 (en) * 1995-11-08 2004-10-15

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101539224B1 (en) * 2014-08-29 2015-07-27 동하정보기술 주식회사 Method for preparing biomass solid refuse fuel
KR102212866B1 (en) * 2020-09-08 2021-02-05 한양대학교 산학협력단 Manure of livestock resourceization device and method

Also Published As

Publication number Publication date
KR20090045161A (en) 2009-05-07

Similar Documents

Publication Publication Date Title
KR101539224B1 (en) Method for preparing biomass solid refuse fuel
KR101293642B1 (en) Manufacturing method of solid fuel from sludge and solid fuel from sludge
KR100908450B1 (en) Method to manufacture porous solid fuel using sludge and solid fuel thereof
JP4603620B2 (en) Method for producing molded solid fuel using porous coal as raw material
KR101098785B1 (en) Method for manufacturing solid fuel
KR101876555B1 (en) Solid fuel using paper sludge and coffee sludge and manufacturing method thereof
KR101182642B1 (en) Carbonized solid fuel and method for manufacturing the same
KR102014980B1 (en) A manufacturing method for solid refuse fuel comprising wastewater sludge
RU2007121675A (en) METHOD FOR CONVERTING SOLID BIO-WASTE TO RENEWABLE FUEL
KR20070076557A (en) A solid fuel manufacturing method use of the sewage sludge and food wastes and inflammable wastes
KR100918945B1 (en) Accelerant composition for producing fuel from sluge and method for preparing thereof, and sludge solid fuel produced by using the same
KR101033860B1 (en) Solid fuel of pellet form and method for preparing the same
KR20150106563A (en) Fuel from sewage sludge
Teoh et al. Chemical investigation and process optimization of glycerine pitch in the green production of roofing tiles
KR101999650B1 (en) Hybrid Sludge Fuel, Manufacturing Method and System of Fuel Production thereof
KR100768591B1 (en) A new solid fuel like bituminous coal from organic sludge and preparation method thereof
KR100991483B1 (en) Biomass drying method using microwave drying device &amp; oil
KR20090019168A (en) Solid fuel of pellet form and method for preparation there of
KR100908680B1 (en) Solid fuel using waste paper sludge and waste oil, method for manufacturing the same
KR100793850B1 (en) Method for treating sewage sludge and dehydrated cake produced thereby
KR100754440B1 (en) Regeneration fuel manufacturing apparatus using waste oil and organic sludge
KR100417983B1 (en) Manufacturing method of solid fuel using food waste
KR100319803B1 (en) New Formed Fuels and preparation Method from Sewage Waste Sludge
CN109097147B (en) Sludge granular fuel and preparation method thereof
RU2160304C1 (en) Method of production of solid fuel

Legal Events

Date Code Title Description
A107 Divisional application of patent
A201 Request for examination
E902 Notification of reason for refusal
E902 Notification of reason for refusal
E701 Decision to grant or registration of patent right