KR101001536B1 - A method for preparing security thread - Google Patents

A method for preparing security thread Download PDF

Info

Publication number
KR101001536B1
KR101001536B1 KR1020080076436A KR20080076436A KR101001536B1 KR 101001536 B1 KR101001536 B1 KR 101001536B1 KR 1020080076436 A KR1020080076436 A KR 1020080076436A KR 20080076436 A KR20080076436 A KR 20080076436A KR 101001536 B1 KR101001536 B1 KR 101001536B1
Authority
KR
South Korea
Prior art keywords
metal
ink
silver wire
catalyst
film
Prior art date
Application number
KR1020080076436A
Other languages
Korean (ko)
Other versions
KR20100016809A (en
Inventor
서구원
이상근
주성현
김시석
Original Assignee
나노씨엠에스(주)
한국조폐공사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 나노씨엠에스(주), 한국조폐공사 filed Critical 나노씨엠에스(주)
Priority to KR1020080076436A priority Critical patent/KR101001536B1/en
Publication of KR20100016809A publication Critical patent/KR20100016809A/en
Application granted granted Critical
Publication of KR101001536B1 publication Critical patent/KR101001536B1/en

Abstract

본 발명은 은선의 제조방법과 이로부터 제조된 은선을 구비하는 보안용지 등의 위조방지 제품에 관한 것이다. 본 발명에 따른 은선의 제조방법은 기재 필름의 일면 또는 양면에 팔라듐 촉매를 함유하는 촉매형 잉크를 인쇄한 후 경화하여 촉매층을 형성하는 단계, 및 상기 촉매층 상에 금속나노 잉크를 인쇄한 후 경화하여 금속층을 형성하는 단계를 포함한다. The present invention relates to a method for manufacturing a silver wire and a counterfeit prevention product such as a security paper having the silver wire manufactured therefrom. The method for producing a silver wire according to the present invention comprises the steps of printing a catalyst ink containing a palladium catalyst on one or both sides of a base film and curing the catalyst layer to form a catalyst layer, and printing and curing the metal nano ink on the catalyst layer. Forming a metal layer.

상기 은선의 제조방법에 사용되는 촉매형 잉크 및 금속 나노 잉크는 저온 경화가 가능하여 기재 필름의 변형을 유발하지 않으며, 촉매형 잉크에 의해 형성된 촉매층은 금속층과 기재 필름과의 접착성을 향상시키고 금속층 패턴이 미세하고 정교하게 형성되도록 하는 효과가 있다.The catalyst type ink and the metal nano ink used in the method for producing the silver wire can be cured at low temperature and do not cause deformation of the base film. The catalyst layer formed by the catalyst type ink improves adhesion between the metal layer and the base film and There is an effect that the pattern is formed finely and finely.

은선, 촉매형 잉크, 나노잉크, 잉크젯, 보안제품 Hidden Line, Catalytic Ink, Nano Ink, Ink Jet, Security Products

Description

은선의 제조방법{A method for preparing security thread}A method for preparing security thread

본 발명은 은행권, 수표, 여권 및 기타 보안 문서에 사용되는 은선의 제조방법, 보다 상세하게는 기재 필름의 상부에 금속 나노입자가 함유된 금속 나노잉크를 인쇄하여 특정 패턴을 형성하는 은선의 제조방법, 및 이로부터 제조된 은선을 구비하는 위조방지제품에 관한 것이다.The present invention is a method for producing a silver wire used in banknotes, checks, passports and other security documents, more specifically a method for producing a silver wire to form a specific pattern by printing a metal nano ink containing metal nanoparticles on top of the base film And it relates to an anti-counterfeiting product having a silver wire produced therefrom.

은행권, 수표, 여권 및 기타 보안 문서에 사용되는 은선은 보안요소의 한 수단으로써, 은행권 등에 사용됨과 아울러, 기능의 개선이 이루어지고 있다.Hidden lines used in banknotes, checks, passports and other security documents are used as banknotes, as a means of security, and functions are being improved.

위키피디아(Wikipedia) 사전에서 은선(security thread)이라 함은 은행권 용지의 내부에 박막필름 형태의 띠를 넣어 위조방지를 강화하기 위한 보안요소를 말하며, 이러한 은선은 은행권 용지에 수직 방향으로 적용되며, 용지에 적용된 형태는 용지의 내부에 삽입(embedded)되는 것과 은선이 용지의 표면에 부분적으로 노출(windowed)되는 것이 있다. In the Wikipedia dictionary, the security thread refers to a security element for strengthening anti-counterfeiting by inserting a thin film-shaped strip inside the banknote paper. The hidden line is applied perpendicular to the banknote paper. Applied forms are embedded in the interior of the paper and hidden lines partially exposed on the surface of the paper.

일반적으로 은선은 플라스틱 필름 또는 금속박막이 코팅된 플라스틱 필름으로 만들어지며, 이러한 은선이 적용된 은행권을 빛에 비취어 보면 용지 내부에 숨 겨진 은선 또는 부분적으로 노출된 은선이 용지와 다른 명암차로 나타나며, 금속박막의 광택도 나타나는 것을 볼 수 있어 은행권의 위조 여부를 확인 할 수 있는 위조방지 요소기술이라고 설명하고 있다.Generally, silver wire is made of plastic film or plastic film coated with metal thin film, and when the banknote with silver wire is applied to the light, the hidden or partially exposed silver wire hidden inside the paper appears different from the paper. It can be seen that the glossiness of the thin film is also described, and it is explained that it is an anti-counterfeiting element technology that can check whether the banknote is counterfeit.

본 발명과 관련한 은선은 폴리에스터 필름 자체 또는 알루미늄을 진공 증착하여 만드는 것으로 널리 공지되어 있으며, 보안제품인 은행권, 수표, 여권 및 기타 보안 문서에 사용하여 왔다.The silver wire associated with the present invention is widely known by vacuum deposition of polyester film itself or aluminum and has been used in security products such as banknotes, checks, passports and other security documents.

일반적인 은선 기술로서 미국특허 210,089호, 964,014호, 1,929,828호(1933년)에는 불투명 재질을 두 장의 용지 사이에 넣어 보안이 강화된 용지를 만든 특허가 최초 기술되어 있다. As a general hidden line technology, U.S. patents 210,089, 964,014 and 1,929,828 (1933) describe the first patent for making a paper with enhanced security by putting an opaque material between two sheets of paper.

진보된 은선 이용 기술로서 미국특허 4,462,866호, 영국특허 1,552,853 A호, 1,604,463 A호에서는 초지과정에서 은선이 종이의 표면에 일정한 간격을 두고 부분적으로 노출되게 하는 "부분노출 은선(partially windowed security thread)" 제조 기술과 이용 기술을 기재하고 있다.As an advanced technique for using hidden lines, U.S. Patent Nos. 4,462,866, UK Patents 1,552,853 A, 1,604,463 A describe the "partially windowed security thread" which allows the hidden lines to be partially exposed at regular intervals on the surface of paper during the papermaking process. The manufacturing technique and the use technique are described.

이어서 미국특허 4,652,015호, 4,943,093호, 유럽특허 0,279,880호, 영국특허 2,338,680호에서는 금속이 코팅된 필름의 일부분을 탈금속(de-metalizing)하여 특정 문자나 패턴을 형성시킨 특허기술이 기재되어 있다.Subsequently, US Pat. Nos. 4,652,015, 4,943,093, European Patents 0,279,880, and British Patents 2,338,680 describe a patent technique in which a portion of a metal-coated film is de-metalized to form specific letters or patterns.

은선과 관련된 최근 기술과 위조방지 기술이 보강된 특허를 소개하면 다음과 같다.The recent technology related to hidden wires and patents fortified with anti-counterfeiting technology are as follows.

영국특허 1,095,286호(1967)에는 플라스틱 필름 또는 금속이 코팅된 필름에 형광잉크와 유색잉크를 인쇄한 은선을 기재하고 있으며, 미국특허 2005/0,174,644 A1호에는 플라스틱 박막 필름에 홀로그램과 자성특성을 부가하여 색상 다양화 효과와 기기감지 효과를 가지고 있는 은선을 기술하고 있다.British Patent No. 1,095,286 (1967) describes a silver wire printed with fluorescent ink and colored ink on a plastic film or a metal coated film, and US Patent 2005 / 0,174,644 A1 adds hologram and magnetic properties to a plastic thin film. It describes hidden lines with color diversification and device detection effects.

유럽특허 0,395,410 B1호, 0,341,002 B1호, 세계특허 01/03945 A1호, 미국특허 3,858,977호에는 박막 필름의 층 수 또는 층 구조를 조작하여 보는 각도에 따라 색상이 다르게 보이는 광가변 효과를 가지고 있는 은선을 기술하고 있으며, 미국특허 7,256,936호에는 편광필름을 이용한 광가변 효과의 은선을 기술하고 있다. European Patent Nos. 0,395,410 B1, 0,341,002 B1, World Patent 01/03945 A1, and US Patent 3,858,977 show a hidden line having a light variable effect that looks different depending on the viewing angle by manipulating the number of layers or the layer structure of a thin film. US Pat. No. 7,256,936 describes a hidden line of a light variable effect using a polarizing film.

영국특허 2,386,584 A호에는 금속-탈금속 은선 필름에 액정물질을 코팅하여 보는 각도에 따라 색상이 다양하게 보이는 광가변 효과를 가지고 있는 은선을 기술하고 있으며, 유럽특허 0,238,043에는 광가변 효과를 갖는 홀로그램에 열변색(thermochromic) 물질을 코팅을 하여 특정 온도에서 은선의 색상이 변하는 열변색 효과를 가지고 있는 은선을 기술하고 있다.British Patent No. 2,386,584 A describes a silver wire having a photovariable effect in which colors vary according to the viewing angle by coating a liquid crystal material on a metal-demetallic silver wire film, and European Patent 0,238,043 describes a hologram having a photovariable effect. It describes a hidden line that has a thermochromic effect by coating a thermochromic material and changing the color of the silver line at a specific temperature.

본 발명과 관련된 금속코팅 및 탈금속 방식을 적용한 은선에 대해는 미국특허 4,652,015, 4,943,093, 유럽특허 0,279,880, 영국특허 2,338,680 등이 있으며, 구체적인 기술은 다음과 같다. As for the silver wire to which the metal coating and the metal removal method related to the present invention are applied, there are US Patent 4,652,015, 4,943,093, European Patent 0,279,880, UK Patent 2,338,680, and the like.

위의 특허에서, 플라스틱 필름에 진공 증착된 알루미늄 층 부분을 선택적으로 탈금속화 하는 방법의 예를 들면, 플라스틱 필름에 알루미늄을 증착시키는 단계와 증착된 표면에 나타내고자 하는 문자나 특정패턴을 내부식성 수지로 인쇄를 하는 단계와 이러한 필름을 알루미늄을 녹이는 수산화나트륨 용액에 통과시켜서 수지가 인쇄되지 않은 부분을 제거하는 단계를 거쳐서 완성된다. In the above patent, for example, a method of selectively demetallizing a portion of a vacuum-deposited aluminum layer on a plastic film, for example, the step of depositing aluminum on a plastic film, and the character or specific pattern to be displayed on the deposited surface, It is completed by printing with a resin and passing the film through a sodium hydroxide solution for dissolving aluminum to remove the unprinted portion of the resin.

이렇게 제조된 은선의 광학적 효과를 살펴보면, 알루미늄 증착 층이 남아 있 는 표면은 특정패턴이 은빛 광택 효과를 나타내고 있으며, 이 은선이 종이 내부에 삽입되었을 경우에 종이를 밝은 곳에 비취어 보면 특정패턴이 빛을 통과시키지 않아서 나타나는 패턴의 명암 형상을 볼 수 있게 된다.Looking at the optical effect of the silver line produced in this way, the surface where the aluminum deposition layer remains, the specific pattern has a silvery gloss effect, and when the silver line is inserted into the paper, if the light is reflected in a bright place, the specific pattern is light. You can see the contrast of the pattern that does not pass through.

물론 상기 방법으로 특정패턴을 형성시키는 것 외에 금속분말로 만들어진 잉크 또는 비금속성 불투명 잉크로 인쇄를 하는 방법 등이 있지만 인쇄할 경우에는 미세하게 형성된 패턴의 경계면이 정교하게 형성되지 않는 단점이 있다.Of course, in addition to forming a specific pattern by the above method, there is a method of printing with ink made of metal powder or non-metallic opaque ink, etc., but when printing, there is a disadvantage in that the interface of the finely formed pattern is not formed precisely.

그리고 본 발명과 관련이 있는 특허 기술로서 나노기술을 이용한 인쇄회로 기판 제작 기술을 살펴보면 다음과 같다.And as a patented technology related to the present invention look at the printed circuit board manufacturing technology using nanotechnology as follows.

한국공개특허 10-2007-0025600, 10-2006-0028350, 10-2006-0017686, 10-2005-0101101 등에는 미세 인쇄회로 기판 제작에 관련한 것으로 구리나 은을 포함하는 금속염과 유기용제, 수지를 포함한 잉크를 제조하고, 이것을 잉크젯 프린터에 적용하여 도전배선을 형성하도록 인쇄를 한 다음, 고온(100 내지 300도 정도)으로 열처리하여 도전 배선의 패턴에서 금속박막이 석출하는 방법을 기술하고 있다. Korean Patent Publication No. 10-2007-0025600, 10-2006-0028350, 10-2006-0017686, 10-2005-0101101 and the like are related to the manufacture of fine printed circuit boards, including metal salts containing copper or silver, organic solvents and resins. An ink is prepared, which is applied to an inkjet printer, printed to form conductive wiring, and then heat-treated at a high temperature (about 100 to 300 degrees) to describe a method of depositing a metal thin film in a pattern of conductive wiring.

이러한 특허기술은 인쇄기판이 두껍기 때문에 고온으로 열처리하여도 무방하지만 은선에 이용할 경우에는 은선의 형태가 변형된다는 문제점이 있다.The patented technology may be heat-treated at a high temperature because the printed circuit board is thick, but there is a problem in that the shape of the hidden wire is deformed when used for the hidden wire.

본 발명은 상기의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 종래의 금속증착 및 탈금속 방식 또는 금속분말잉크을 이용한 인쇄기술과 차별화된 새로운 은선의 제조방법 및 이로부터 제조된 은선을 구비하는 위조방지제품을 제공함에 있다.The present invention has been made to solve the above problems, an object of the present invention is to provide a new method for producing a silver wire and a silver wire produced therefrom, which is different from the conventional metal deposition and demetallic printing method or printing using metal powder ink. To provide an anti-counterfeiting product.

보다 구체적으로 본원 발명은 은선을 제조함에 있어서 기재 필름 상에 패턴화된 금속층을 형성하되 기재 필름의 변형을 방지하기 위하여 저온 공정이 가능한 제조방법을 제공하고자 하는 것이며, 나아가 패턴화된 금속층과 기재 필름의 접착성을 향상시키고 금속층 패턴이 보다 미세하고 정교하게 형성될 수 있는 제조방법을 제공하고자 하는 것이다.More specifically, the present invention is to provide a manufacturing method capable of forming a patterned metal layer on the base film in the production of silver wire, but can be a low temperature process in order to prevent deformation of the base film, furthermore, the patterned metal layer and the base film To improve the adhesion of the metal layer pattern to provide a manufacturing method that can be formed more finely and finely.

본 발명은 기재 필름과 상기 기재 필름 상에 형성된 패턴화된 금속층을 포함하는 은선을 제조함에 있어서 패턴화된 금속층과 기재필름의 접착성을 향상시키고 금속층 패턴이 보다 미세하고 정교하게 형성도록 하기 위하여 상기 기재 필름과 패턴화된 금속층 사이에 패턴화된 촉매층을 개재하는 것을 특징으로 하는 은선의 제조방법을 제공한다.The present invention is to improve the adhesiveness of the patterned metal layer and the base film in the production of the silver line including the base film and the patterned metal layer formed on the base film and to form a finer and finer metal layer pattern Provided is a method for producing a silver wire, wherein the patterned catalyst layer is interposed between the base film and the patterned metal layer.

또한, 본 발명은 상기 은선의 제조방법으부터 제조된 은선을 구비하는 위조방지제품을 제공하며, 상기 위조방지제품으로는 대표적으로 보안용지를 들 수 있 고, 본 발명에 따라 제조된 은선을 보안용지 제조시 투입하여 종이 내 삽입하거나 부분 노출되도록 할 수 있다.In addition, the present invention provides an anti-counterfeiting product having a silver wire manufactured from the manufacturing method of the silver wire, the anti-counterfeiting product may include a security paper, and the security of the silver wire manufactured according to the present invention It can be inserted during paper manufacture and inserted into the paper or partially exposed.

본 발명에 따른 은선의 제조방법은 구체적으로 하기의 제조단계를 포함한다.The manufacturing method of the silver wire which concerns on this invention specifically includes the following manufacturing steps.

a) 기재 필름의 일면 또는 양면에 팔라듐 촉매를 함유하는 촉매형 잉크를 인쇄한 후 경화하여 촉매층을 형성하는 단계; 및a) printing a catalyst ink containing a palladium catalyst on one or both sides of the base film and curing the same to form a catalyst layer; And

b) 상기 촉매층 상에 금속나노 잉크를 인쇄한 후 경화하여 금속층을 형성하는 단계.b) printing the metal nano ink on the catalyst layer and curing the metal layer ink to form a metal layer.

상기 단계 후 금속층이 형성된 기재필름을 소정의 폭으로 재단하는 통상적인 제조 단계를 거쳐 목적하는 은선을 제조할 수 있다.After the above step, the target silver wire may be manufactured through a conventional manufacturing step of cutting the base film on which the metal layer is formed to a predetermined width.

상기 촉매형 잉크는 팔라듐 촉매 성분을 함유하고 있어 촉매형 잉크에 의해 형성된 촉매층 상에 금속나노잉크가 인쇄되고 경화되는 공정에서 금속나노 잉크에 함유된 금속 나노입자가 균일하게 촉매층 패턴을 따라 석출되도록 하며 기재 필름과 금속층을 보다 견고하게 접착하는 역할을 하게 된다.The catalytic ink contains a palladium catalyst component so that metal nanoparticles contained in the metal nano ink are uniformly deposited along the catalyst layer pattern in the process of printing and curing the metal nano ink on the catalyst layer formed by the catalytic ink. It serves to more firmly adhere the base film and the metal layer.

상기 제조단계에 사용하는 촉매형 잉크 및 금속 나노 잉크는 저온 경화가 가능한 조성물을 사용함으로써 저온에서 경화가 가능하도록 하는 것이 보다 바람직하고 바람직하게는 자외선 경화용 수지 조성물을 함유하여 자외선 경화에 의해 촉매층 및 금속층을 형성하는 것이 좋다.The catalyst type ink and the metal nano ink used in the manufacturing step are more preferably to be curable at low temperature by using a composition capable of low temperature curing, and preferably, the catalyst layer is formed by UV curing by containing a resin composition for ultraviolet curing. It is preferable to form a metal layer.

상기 기재 필름은 폴리아미드계 수지, 폴리에스테르계 수지, 폴리아크릴계 수지, 폴리비닐아세테이트계 수지, 폴리에틸렌계 수지, 폴리염화비닐계 수지 중에서 선택되는 어느 하나 또는 2 이상의 조합으로 이루어진 투명 필름을 사용하며, 바람직하게는 열적특성, 기계적 특성, 화학적 특성이 좋은 폴리에스테르계 수지를 사용한다. 상기 기재 필름은 아무 기능성도 부가되지 않은 투명 필름 그대로 사용하거나, 상기 투명 필름의 일면 또는 양면에 패턴화되거나 패턴화되지 않은 금속막이 형성되거나, 형광물질, 자성물질, 적외선물질, 상향전이물질 및 편광물질로부터 선택된 1종 이상이 코팅되거나, 홀로그램이 부가된 것을 사용할 수 있다.The base film uses a transparent film made of any one or a combination of two or more selected from polyamide resin, polyester resin, polyacrylic resin, polyvinylacetate resin, polyethylene resin, and polyvinyl chloride resin, Preferably, a polyester resin having good thermal, mechanical and chemical properties is used. The base film is used as it is a transparent film with no added functionality, or a patterned or unpatterned metal film is formed on one or both surfaces of the transparent film, or a fluorescent material, a magnetic material, an infrared material, an upward transition material, and a polarized light. At least one selected from materials may be coated or a hologram may be added.

상기 촉매형 잉크는 팔라듐 촉매, 환원제, 바인더, 아크릴레이트계 단량체, 광개시제 및 용제를 함유하는 자외선 경화형 잉크를 사용하는 것이 바람직하고, 예를 들면 팔라듐 촉매로서 팔라듐 아세테이트, 환원제로서 에틸락테이트, 바인더로서 폴리에스터 아크릴레이트 및 폴리에테르 개질 폴리디메틸실록산을 함유하는 자외선 경화형 잉크를 사용할 수 있다. The catalytic ink is preferably a UV curable ink containing a palladium catalyst, a reducing agent, a binder, an acrylate monomer, a photoinitiator and a solvent. For example, palladium acetate as a palladium catalyst, ethyl lactate as a reducing agent, and a binder UV curable inks containing polyester acrylates and polyether modified polydimethylsiloxanes can be used.

상기 금속나노 잉크는 금속 나노입자, 자외선 경화형 수지, 용제 및 광개시제를 함유하며, 산화합물, 금속촉매 등의 첨가제를 더 함유할 수 있다. 상기 금속 나노 잉크에 함유되는 금속 나노입자의 함량은 금속 나노 잉크 중량의 30 내지 50중량%인 것이 바람직한데, 이는 상기 함량이 30중량% 미만인 경우에는 균일한 금속층을 형성하기 어렵고, 상기 함량이 50중량%를 초과하여 너무 많은 경우에는 금속 잉크의 특성 상 비중차에 의한 안정성이 좋지 않아서 분리될 수 있다.The metal nano ink contains metal nanoparticles, an ultraviolet curable resin, a solvent and a photoinitiator, and may further contain additives such as an acid compound and a metal catalyst. The content of the metal nanoparticles contained in the metal nano ink is preferably 30 to 50% by weight of the metal nano ink, which is difficult to form a uniform metal layer when the content is less than 30% by weight, the content is 50 When the amount exceeds too much, the stability due to the specific gravity difference of the metal ink may not be good, and thus may be separated.

상기 금속 나노입자는 평균 입경이 1 내지 20nm인 금속 재료로 이루어진 것이 바람직하고, 상기 금속 재료로는 구리, 은, 알루미늄 또는 금으로부터 선택되는 1종 이상을 사용할 수 있다. 상기 금속 나노입자의 평균 입경이 1nm 미만인 경우는 제조하기가 용이하지 않고 제조비용이 상승하여 경제적이지 못하고 상기 입경이 20nm를 초과하는 경우에는 분산성이 저하되고 금속 잉크의 침강성이 발생할 수 있고 균일하고 미세한 인쇄 패턴을 형성하기에 용이하지 않게 된다.The metal nanoparticles are preferably made of a metal material having an average particle diameter of 1 to 20 nm, and the metal material may be one or more selected from copper, silver, aluminum or gold. If the average particle diameter of the metal nanoparticles is less than 1 nm, it is not easy to manufacture, the manufacturing cost is increased and economical. If the particle diameter is more than 20 nm, the dispersibility may be lowered, and the sedimentability of the metal ink may be generated. It is not easy to form a fine print pattern.

상기 금속 나노 잉크에 함유되는 자외선 경화형 수지는 일액형 우레탄 수지를 사용하는 것이 효과적이며, 아크릴레이트 말단을 갖는 에폭시 올리고머를 예로 들 수 있고, 잉크 내 함량은 20 내지 50 중량%인 것이 바람직하다. 상기 수지 성분의 함량이 20 중량% 미만인 경우에는 하층 막과의 접착성이 저하되어 바람직하지 못하고, 상기 성분이 50중량%를 초과하여 너무 많은 경우 점도 상승으로 인해 인쇄하기에 용이하지 않을 수 있으므로 상기 범위로 함량을 조절하는 것이 바람직하다. 상기 금속 나노잉크는 금속 나노입자 및 수지 성분 외에 광개시제, 용제 및 안정제 등의 첨가제를 더 함유한다. UV-curable resin contained in the metal nano ink is effective to use a one-component urethane resin, for example, an epoxy oligomer having an acrylate end, it is preferable that the content in the ink is 20 to 50% by weight. When the content of the resin component is less than 20% by weight, the adhesion with the lower layer film is lowered, which is not preferable, and if the component is more than 50% by weight, it may not be easy to print due to the viscosity increase. It is preferable to adjust the content to the range. The metal nanoink further contains additives such as photoinitiators, solvents, and stabilizers in addition to the metal nanoparticles and the resin component.

이하, 첨부한 도면들을 참조하여 본 발명의 바람직한 실시예들을 상세히 설명한다. 다음에 소개되는 실시예들은 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 예로서 제공되어지는 것이다. 따라서, 본 발명은 이하 설명되어지는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 그리고, 도면들에 있어서, 층 및 영역의 길이, 두께 등은 편의를 위하여 과장되어 표현될 수도 있다. 명세서 전체에 걸쳐서 동일한 참조번호들은 동일한 구성요소들을 나타낸다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. The following embodiments are provided by way of example so that those skilled in the art can fully understand the spirit of the present invention. Therefore, the present invention is not limited to the embodiments described below, but may be embodied in other forms. In the drawings, lengths, thicknesses, and the like of layers and regions may be exaggerated for convenience. Like numbers refer to like elements throughout.

도 1은 금속나노잉크가 특정인쇄 패턴으로 인쇄된 은선을 나타낸 전면도이고, 도 2는 금속나노 잉크가 특정인쇄 패턴으로 인쇄된 은선을 나타낸 측면도이며, 도 3은 금속나노 잉크가 네가티브 패턴으로 인쇄된 은선을 나타낸 전면도이고, 도 4는 금속나노 잉크가 네가티브 패턴으로 인쇄된 은선을 나타낸 측면도이며, 도 5는 알루미늄이 증착된 필름 층 위에 금속나노 잉크가 인쇄된 은선을 나타낸 측면도이고, 도 6은 은선이 보안용지 내부에 삽입된 상태를 나타낸 측면도이며, 도 7은 은선이 보안용지 내부에 부분적으로 삽입된 상태를 나타낸 측면도고, 도 8은 미세 인쇄패턴을 갖는 은선 시트를 나타낸 전면도이며, 도 9는 본 발명의 은선 제조방법을 나타낸 순서도이다.1 is a front view showing a silver line in which the metal nano ink is printed in a specific printing pattern, FIG. 2 is a side view showing a silver line in which the metal nano ink is printed in a specific printing pattern, and FIG. 3 is a metal nano ink printed in a negative pattern. 4 is a side view showing a silver line in which a metal nano ink is printed in a negative pattern, and FIG. 5 is a side view showing a silver line in which a metal nano ink is printed on a film layer on which aluminum is deposited, and FIG. Silver is a side view showing a state in which the hidden line is inserted into the security paper, Figure 7 is a side view showing a state in which the hidden line is partially inserted into the security paper, Figure 8 is a front view showing a hidden line sheet having a fine printing pattern, 9 is a flowchart illustrating a method for manufacturing a silver wire of the present invention.

본 발명에 따른 은선 제조방법에 대해 설명하면, 도 9에 참조되는 바와 같이 필름(11)의 표면에 증착된 이물질을 제거하는 필름세정단계(S5)와, 상기 필름(11)의 일면 또는 양면에 촉매용 잉크(12)를 인쇄하는 촉매형 잉크 인쇄단계(S10)과, 상기 필름(11)에 인쇄된 촉매형 잉크(12)를 경화하는 촉매층 형성단계(S20)와, 상기 촉매층(12)에 금속나노 잉크(13)를 인쇄하는 금속나노 잉크 인쇄단계(S30), 및 상기 금속나노 잉크(13)를 경화하는 금속층 형성단계(S40)로 이루어진다. Referring to the method for manufacturing the silver wire according to the present invention, as shown in Figure 9, the film cleaning step (S5) for removing the foreign matter deposited on the surface of the film 11, and on one or both sides of the film 11 In the catalyst type ink printing step S10 for printing the catalyst ink 12, the catalyst layer forming step S20 for curing the catalyst type ink 12 printed on the film 11, and the catalyst layer 12 A metal nano ink printing step (S30) for printing the metal nano ink 13, and a metal layer forming step (S40) for curing the metal nano ink 13.

금속층 형성 단계(S40) 후에 제조된 은선 시트의 일례를 도 8에 도시하였다. 도 8에 도시한 바와 같이 미세패턴이 연속적으로 형성된 은선 시트를 소정의 폭으로 재단하여 도 1 내지 도 5에 도시한 바와 같은 은선을 제조할 수 있다. 은선 시트를 재단하는 폭은 용도 및 패턴크기에 따라 다양하나 보안용지에 적용하는 은선의 경우에는 1 내지 5mm 폭으로 재단하는 것이 일반적이다.An example of the silver wire sheet manufactured after the metal layer forming step S40 is illustrated in FIG. 8. As shown in FIG. 8, the silver wire sheet having the fine patterns continuously formed may be cut to have a predetermined width to produce the silver wire as shown in FIGS. 1 to 5. The width of cutting the hidden wire sheet varies according to the use and the pattern size, but in the case of the hidden wire applied to the security paper, it is generally cut to a width of 1 to 5 mm.

도 1 내지 도 4는 본 발명의 은선을 나타낸 도면으로서, 은선(10)의 측면을 나타낸 도 2와 도 4에서 보는 바와 같이 본 발명의 은선(10)은 필름(11)과, 상기 필름(11)의 상면에 인쇄된 후 경화된 촉매층(12)과, 상기 촉매층(12)의 상면에 인 쇄된 후 경화된 금속층(13)으로 이루어진다.1 to 4 are diagrams showing the hidden line of the present invention. As shown in FIGS. 2 and 4 showing the side surfaces of the hidden line 10, the hidden line 10 of the present invention includes a film 11 and the film 11. And a hardened catalyst layer 12 printed on the upper surface of the c) and a hardened metal layer 13 printed on the upper surface of the catalyst layer 12.

상기 필름(11)은 촉매형 잉크(12)가 인쇄되는 것으로서, 상기 촉매형 잉크(12)의 인쇄가 용이하게 이루어짐과 동시에 인쇄된 촉매형 잉크(12)가 상기 필름(11)으로부터 이탈되지 않도록 상기 필름(11)은 열적특성, 기계적 특성, 화학적 특성이 좋은 폴리에스테르계 수지를 사용하는 것이 보다 바람직하다.The film 11 is a catalyst ink 12 is printed, so that the printing of the catalyst ink 12 is easy to be printed at the same time so that the printed catalyst ink 12 is not separated from the film (11). As for the film 11, it is more preferable to use a polyester resin having good thermal properties, mechanical properties, and chemical properties.

상기 필름(11)의 상면에 인쇄되는 촉매형 잉크는 이후 금속나노 잉크가 상기 필름(11)에 견고히 부착되도록 하는 역할을 하는 것으로서, 팔라듐 촉매를 함유하고 자외선 경화가 가능한 잉크를 사용하는 것이 바람직하고, 예를 들면 팔라듐(II) 아세테이트(Palladium(II) acetate) 1 내지 5 중량 %, 에틸락테이트(Ethyl Lactate) 1 내지 5 중량%, 폴리비닐피롤리돈(polyvinyl pyrollidone) 10 내지 15 중량 %, 아세트페논유도체(Acetophenone derivative) 1 내지 5 중량 %, 포스핀옥사이드페닐비스(2,4,6트리메틸벤조일)(Phosphine oxide phenylbis(2,4,6-Trimethylbenzoyl)) 1 내지 5 중량 %, 다기능성 아크릴레이트 혼합물(Mixture of multifunctional acrylates) 20 내지 25 중량 %, 디프로필렌글리콜디아크릴레이트(Dipropylene glycol diacrylate) 0.1 내지 10 중량 %; 폴리에스터 아크릴레이트(Polyester Acrylate) 0.1 내지 10 중량 %, 2-페녹시에틸 아크릴레이트(2-phenoxyethyl acrylate) 15 내지 25 중량 %; 폴리에테르 개질 폴리디메틸실로산(Polyether modified polydimethylsiloxane) 0.1 내지 1 중량%; 테트라키스(2-하이드록시프로필)에틸렌디아민(N,N,N',N'-Tetrakis (2-hydroxypropyl)ethylenediamine) 0.1 내지 5 중량 %, 및 에탄올(Ethanol) 0.1 내 지 2 중량 %로 이루어지는 자외선 경화형 잉크를 사용할 수 있다.The catalytic ink printed on the upper surface of the film 11 serves to firmly adhere the metal nano ink to the film 11, and it is preferable to use an ink containing a palladium catalyst and capable of ultraviolet curing. For example, 1 to 5% by weight of Palladium (II) acetate, 1 to 5% by weight of ethyl lactate, 10 to 15% by weight of polyvinyl pyrollidone, 1-5% by weight of acetphenone derivative, 1-5% by weight of phosphine oxide phenylbis (2,4,6-Trimethylbenzoyl), multifunctional acrylic 20 to 25% by weight of Mixture of multifunctional acrylates, 0.1 to 10% by weight of dipropylene glycol diacrylate; 0.1 to 10% by weight of polyester acrylate, 15 to 25% by weight of 2-phenoxyethyl acrylate; 0.1 to 1% by weight of polyether modified polydimethylsiloxane; UV light consisting of 0.1 to 5% by weight of tetrakis (2-hydroxypropyl) ethylenediamine (N, N, N ', N'-Tetrakis (2-hydroxypropyl) ethylenediamine) and 0.1 to 2% by weight of ethanol (Ethanol) Curable ink can be used.

상기 촉매용 잉크는 상기 필름(11)의 일면에만 인쇄될 수도 있으며, 양면에 모두 인쇄될 수도 있다. 상기 촉매용 잉크를 필름(11)에 인쇄하여 패턴을 형성하고 이를 자외선 경화하여 촉매층(12)을 형성한다. 촉매층은 도 1 및 도 2에 도시한 바와 같이 패턴이 양각으로 표현되도록 형성될 수도 있고, 도 3 및 도 4에 도시한 바와 같이 패턴이 음각으로 표현되도록 형성될 수도 있다.The catalyst ink may be printed on only one surface of the film 11 or both surfaces. The catalyst ink is printed on the film 11 to form a pattern, which is then UV cured to form the catalyst layer 12. The catalyst layer may be formed such that the pattern is embossed as shown in FIGS. 1 and 2, or may be formed such that the pattern is intaglio as shown in FIGS. 3 and 4.

상기 촉매층(12)의 상면에 인쇄된 후 경화되어 금속박막을 형성하는 금속층(13)은 금속 나노 입자와 자외선 경화형 수지 조성물을 함유한 금속나노잉크를 인쇄한 후 자외선 경화하여 형성된다. 상기 금속 나노잉크로는 구리, 은, 알루미늄, 및 금 중 어느 하나 또는 이들의 혼합으로 이루어진 평균 입경 1 내지 20nm의 금속 나노입자를 30 내지 50중량%로 함유하며, 분자량은 1000∼1500 범위이며, 아크릴레이트 말단을 갖는 에폭시올리고머 20~30 중량 %를 함유하고, 그 외에 용제, 광개시제 및 안정제를 함유하여 점도는 25 ℃에서 10∼20 센티포아즈(CPS), 표면장력은 20℃에서 40(dyne/cm), 비중은 1.02(g/㎤ ) 정도인 금속 나노잉크 조성물을 사용하였다. 상기 용제로는 아세트산에틸 등의 에스테르류, 아세토페논등의 케톤류, 에탄올, 부탄올, 에탄올 등의 알코올류, 톨루엔, 나프타 등 탄화수소류, N-메틸피롤리돈 등을 단독 또는 조합하여 사용할 수 있으며 시판되는 시너(thinner)를 사용할 수 있으나 이에 한정하는 것은 아니다. 상기 광개제로는 이소시아네이트계 광개시제를 사용할 수 있고, 안정제로서 디프로필렌글리콜 아크릴레이트를 사용할 수 있다.The metal layer 13, which is printed on the upper surface of the catalyst layer 12 and then cured to form a metal thin film, is formed by printing a metal nano ink containing metal nanoparticles and an ultraviolet curable resin composition, followed by ultraviolet curing. The metal nano ink contains 30 to 50% by weight of metal nanoparticles having an average particle diameter of 1 to 20 nm consisting of any one or a mixture of copper, silver, aluminum, and gold, the molecular weight is in the range of 1000 to 1500, 20 to 30% by weight of epoxy oligomer having an acrylate end, in addition to the solvent, photoinitiator and stabilizer, the viscosity is 10-20 centipoise (CPS) at 25 ℃, the surface tension is 40 (dyne at 20 ℃) / cm), specific gravity of the metal nanoink composition of about 1.02 (g / cm 3) was used. As the solvent, esters such as ethyl acetate, ketones such as acetophenone, alcohols such as ethanol, butanol and ethanol, hydrocarbons such as toluene and naphtha, N-methylpyrrolidone and the like can be used alone or in combination. Thinner may be used, but is not limited thereto. As the photoinitiator, an isocyanate-based photoinitiator may be used, and dipropylene glycol acrylate may be used as a stabilizer.

도 5에 참조되는 바와 같이 본 발명에 따른 제조방법으로 제조된 은선은 상기 필름(11)과 촉매층(12) 사이에 알루미늄층(14)이 증착되어 형성될 수도 있다.As shown in FIG. 5, the silver wire manufactured by the manufacturing method according to the present invention may be formed by depositing an aluminum layer 14 between the film 11 and the catalyst layer 12.

한편, 위와 같이 이루어진 상기 은선(10)의 일면 또는 양면에는 금속물질, 형광물질, 자성물질, 액정물질, 적외선물질, 및 홀로그램이 형성될 수 있다.On the other hand, a metal material, a fluorescent material, a magnetic material, a liquid crystal material, an infrared material, and a hologram may be formed on one or both surfaces of the silver wire 10 formed as described above.

상기 은선(10)의 일면 또는 양면에는 금속물질, 형광물질, 자성물질, 액정물질, 적외선물질, 및 홀로그램이 형성됨에 따라 은선(10)을 비롯한 상기 은선(10)이 적용된 보안용지의 보안성능이 향상된다는 장점이 있다.As the metal, fluorescent material, magnetic material, liquid crystal material, infrared material, and hologram are formed on one or both surfaces of the hidden line 10, the security performance of the security paper to which the hidden line 10 is applied, including the hidden line 10, is increased. It has the advantage of being improved.

도 6 및 도 7은 본 발명의 제조방법에 의해 제조된 은선을 적용한 보안 용지의 단면도를 나타낸 것으로 도 6은 보안 용지 내에 삽입된 경우를, 도 7은 보안용지에 부분 노출되는 경우를 나타낸 것이다.6 and 7 illustrate cross-sectional views of a security sheet to which a silver line manufactured by the manufacturing method of the present invention is applied. FIG. 6 illustrates a case where the security sheet is inserted into the security sheet, and FIG.

은선을 보안용지에 적용하는 것은 통상적인 제조공정으로 진행할 수 있으며, 보안용지를 제조하는 공정 중에서 일반적으로 환망 또는 장망에서 종이 지필이 생성되는 과정 중에 삽입하여 제조하거나 또는 지필이 생성된 후에 2개의 종이를 합지하는 과정 중에 종이의 사이에 투입하여 제조하게 되며 상기 제조 과정에서 종이 내에 완전히 삽입하거나 부분 노출되도록 제조할 수 있다.The application of the hidden wire to the security paper can be carried out in a conventional manufacturing process.In the process of manufacturing the security paper, two papers are inserted or manufactured after the paper paper is generated in the process of generating the paper paper in the network or the network. In the process of laminating to put between the paper to be manufactured and can be manufactured to be fully inserted or partially exposed in the paper during the manufacturing process.

본 발명에 따른 은선의 제조방법은 기재 필름과 패턴화된 금속층 사이에 패턴화된 촉매층을 개재함으로써 패턴화된 금속층과 기재필름의 접착성을 향상시키고 금속층 패턴이 보다 미세하고 정교하게 형성되는 장점이 있다.The production method of the silver wire according to the present invention has the advantage of improving the adhesion between the patterned metal layer and the base film by interposing a patterned catalyst layer between the base film and the patterned metal layer and forming a finer and finer metal layer pattern. have.

또한 본 발명에 따른 제조방법에 사용되는 촉매형 잉크 및 금속 나노잉크는 인쇄 방식으로 미세한 패턴을 형성할 수 있고 저온 경화가 가능하여 기재 필름의 변형을 방지하고 제조시간이 단축되는 잇점이 있다.In addition, the catalyst type ink and the metal nanoink used in the production method according to the present invention can form a fine pattern by a printing method and can be cured at low temperature, thereby preventing deformation of the base film and shortening the manufacturing time.

또한 인쇄 방식이고 저온 공정을 사용함으로써 기재 필름에 다양한 기능성을 부가하기 용이하여 은선의 보안 특성을 향상시킬 수 있고 얇은 박막으로 형성하기 용이하므로 다양한 위조방지용 제품에 적용가능한 장점이 있다.In addition, by using a printing method and a low temperature process, it is easy to add various functionalities to the base film to improve the security characteristics of the silver wire, and to form a thin thin film, which is applicable to various anti-counterfeiting products.

이하, 실시예를 통하여 본 발명을 보다 상세히 설명하고자 하나, 하기 실시예에 의하여 본 발명의 범위가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to Examples, but the scope of the present invention is not limited by the following Examples.

[실시예 1]Example 1

폴리에틸렌 테레프탈레이트(PET) 수지로 이루어진 롤 형태의 은선용 필름(11)의 표면을 이소프로필알콜을 이용하여 세정한다(S5).The surface of the roll-shaped silver wire film 11 made of polyethylene terephthalate (PET) resin is cleaned using isopropyl alcohol (S5).

이어서 하기 표 1의 조성을 갖는 촉매형 잉크로 필름 표면에 인쇄하는 단계(S10)로서 잉크젯 프린터[CMS, 씨엠에스테크놀로지(주), 메탈젯 5000형 피에조타입 프린터]를 이용하여 선폭과 간격을 각각 20~50㎛ 수준으로 연속된 글자 또는 형상을 인쇄한 후에 프린터에 장착 된 자외선램프(240W/㎠)로 조사하여 상기 촉매층(12)을 형성한다(S20).Subsequently, as a step (S10) of printing on the surface of the film with the catalytic ink having the composition shown in Table 1, an inkjet printer [CMS, CMS Technology Co., Ltd., MetalJet 5000 type piezo type printer] was used to set the line width and spacing, respectively. After printing the continuous letters or shapes at a level of ˜50 μm, the catalyst layer 12 is formed by irradiating with an ultraviolet lamp (240 W / cm 2) mounted to the printer (S20).

[표 1] TABLE 1

Figure 112008056213188-pat00001
Figure 112008056213188-pat00001

상기 촉매형 잉크로 인쇄한 후 경화하여 형성된 촉매층(12) 위에 구리 나노입자를 함유한 하기 표 2의 조성을 갖는 금속 나노 잉크를 잉크젯 프린터로 인쇄(S30)한 다음에 메탈젯 프린터에 장착된 자외선램프로 자외선을 조사하여 박막의 금속층(13)이 형성되도록 한다(S40).After printing with the catalyst ink and curing the metal nano ink having a composition of Table 2 containing copper nanoparticles on the catalyst layer 12 formed by curing (S30) and then mounted on the metal jet printer UV lamp Ultraviolet rays are irradiated to form the metal layer 13 of the thin film (S40).

[표 2]TABLE 2

Figure 112008056213188-pat00002
Figure 112008056213188-pat00002

이와 같이 제조된 롤을 1.2mm의 폭으로 연속적으로 슬리팅(slitting)하여 은선(10)을 제조하였다.The roll thus prepared was continuously slitting to a width of 1.2 mm to prepare a hidden wire 10.

제조된 은선을 적용하여 보안용지를 제조하였으며, 보안용지를 제조할 때 환망 초지기에서 통상의 방법으로 투입하여 도 7에 도시한 바와 같이 종이(21) 내에 은선(10)이 부분적으로 삽입(110)되고 부분적으로 노출(120)된 위조방지용 보안용지(20)를 제조하였다.The security paper was manufactured by applying the manufactured silver wire, and when the security paper was manufactured, the wire was inserted in a conventional manner in a paper machine, and as shown in FIG. 7, the hidden wire 10 was partially inserted into the paper 21 as shown in FIG. 7. And partially exposed 120 for the anti-counterfeit security paper 20 was prepared.

상기 위조방지용 보안용지(20)는 도 7에서 참조되는 바와 같이 은선(10)이 부분적으로 노출된 곳(120)에서는 인쇄된 글자의 미세한 패턴이 금색의 광택을 가지는 시각적 효과가 있으며, 용지를 밝은 곳에 비취어 보면 삽입된 은선(110)에는 인쇄된 패턴이 흑백의 명암으로 나타나 글자를 판독할 수 있다.The anti-counterfeiting security paper 20 has a visual effect that the fine pattern of the printed letters have a golden luster in the place 120 where the hidden line 10 is partially exposed, as shown in FIG. In light of this, the printed pattern appears in black and white contrast on the inserted hidden line 110 to read the letters.

[실시예 2][Example 2]

은색 광택이 있는 은선(10)을 제조하기 위하여 금 나노입자 대신에 은 나노 입자를 함유한 금속나노 잉크를 바코드 패턴으로 인쇄한 것을 제외하고는 실시예 1과 동일한 방법으로 은선을 제조하였다.Silver wire was manufactured in the same manner as in Example 1, except that metal nano ink containing silver nanoparticles instead of gold nanoparticles was printed in a barcode pattern in order to manufacture silver glossy silver wire 10.

이로써 도 7에 참조되는 바와 같이 보안용지 상에 은선(10)이 부분적으로 노출된 곳(120)에서는 인쇄된 바코드 패턴이 은색의 광택을 가지는 시각적 효과가 있으며, 상기 보안용지를 밝은 곳에 비취어 보면 삽입된 부분(110)에는 바코드 패턴이 흑백의 명암으로 나타나며, 이 패턴은 기기감지 요소로 이용할 수 있다.As a result, as shown in FIG. 7, where the hidden line 10 is partially exposed on the security paper 120, the printed barcode pattern has a visual effect of silver shine, and the security paper is reflected in a bright place. In the inserted portion 110, a barcode pattern is displayed in black and white contrast, which can be used as a device sensing element.

[실시예 3]Example 3

도 5에 참조되는 바와 같이 폴리에틸렌 테레프탈레이트 수지 필름의 일면에 알루미늄이 전체적으로 증착된 알루미늄층(14)을 가진 롤 PET 필름(11)을 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 은선 및 보안용지를 제조하였다.As shown in FIG. 5, the silver wire and the security in the same manner as in Example 1 except for using the roll PET film 11 having the aluminum layer 14 having aluminum deposited entirely on one surface of the polyethylene terephthalate resin film. Paper was prepared.

제조된 보안용지의 부분적으로 노출된 은선(120)에서는 알루미늄 증착에 의한 은색 바탕 위에 금색의 글자가 보이며, 용지를 밝은 곳에 비취어 보면 삽입된 은선(110)은 흑색의 띠로 보인다.In the partially exposed silver line 120 of the manufactured security paper, gold letters are seen on the silver background by aluminum deposition, and the silver line 110 inserted is visible as a black strip when the paper is reflected in a bright place.

[실시예 4]Example 4

촉매층 및 금속층이 형성될 표면에 비가시성 적색 형광 물질인 CdMoO4:Eu3+이 전체적으로 코팅된 롤 PET 필름(11)을 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 은선 및 보안용지를 제조하였다.The silver wire and the security paper were prepared in the same manner as in Example 1, except that the roll PET film 11 coated with CdMoO 4 : Eu 3+ , which is an invisible red fluorescent substance, was used on the surface of the catalyst layer and the metal layer. It was.

이와 같이 제조된 보안용지는 실시예 1과 같은 동일한 효과를 가지고 있으며, 자외선 램프를 비취면 은선(10)이 적색 형광을 나타낸다.The security paper thus produced has the same effect as in Example 1, and the silver line 10 shows red fluorescence when the ultraviolet lamp is reflected.

[실시예 5]Example 5

촉매층이 형성되지 않는 면에 코발트계 자성물질을 고루 도포한 후, 그 표면에 멜라민계 투명수지를 코팅처리한 롤 PET 필름(11)을 사용하는 것을 제외하고는 실시예 1과 동일한 방법으로 은선 및 보안용지를 제조하였다.After applying the cobalt-based magnetic material evenly to the surface where the catalyst layer is not formed, using the roll PET film 11 coated with melamine-based transparent resin on the surface of the silver line and Security paper was prepared.

이와 같이 제조된 보안용지는 실시예 1과 같은 동일한 효과와 자성감지 특성을 가지는 복합적 은선(10)이 만들어진다.The security paper thus produced is made of a composite hidden line 10 having the same effect and magnetic sensing characteristics as in the first embodiment.

본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 만족하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.The terms or words used in this specification and claims are not to be construed as limiting in their usual or dictionary meanings, and the inventors may appropriately define the concept of terms in order to best explain their invention in the best way possible. It should be interpreted as meaning and concept corresponding to the technical idea of the present invention based on the principle that the present invention. Therefore, the embodiments described in the specification and the drawings shown in the drawings are only the most preferred embodiments of the present invention and do not satisfy all of the technical idea of the present invention, various equivalents that may be substituted for them at the time of the present application It should be understood that there may be variations and variations.

도 1은 금속나노 잉크가 특정인쇄 패턴으로 인쇄된 은선을 나타낸 전면도.1 is a front view showing a silver line in which the metal nano ink is printed in a specific printing pattern.

도 2는 금속나노 잉크가 특정인쇄 패턴으로 인쇄된 은선을 나타낸 측면도.Figure 2 is a side view showing a silver line in which the metal nano ink is printed in a specific printing pattern.

도 3은 금속나노 잉크가 네가티브 패턴으로 인쇄된 은선을 나타낸 전면도.Figure 3 is a front view showing a silver line in which the metal nano ink is printed in a negative pattern.

도 4는 금속나노 잉크가 네가티브 패턴으로 인쇄된 은선을 나타낸 측면도.Figure 4 is a side view showing a silver line in which the metal nano ink is printed in a negative pattern.

도 5는 알루미늄이 증착된 필름 층 위에 금속나노 잉크가 인쇄된 은선을 나타낸 측면도.5 is a side view showing a silver line on which a metal nano ink is printed on a film layer on which aluminum is deposited.

도 6은 은선이 보안용지 내부에 삽입된 상태를 나타낸 측면도.Figure 6 is a side view showing a state in which the hidden line is inserted inside the security paper.

도 7은 은선이 보안용지 내부에 부분적으로 삽입된 상태를 나타낸 측면도.7 is a side view showing a state in which the hidden line is partially inserted into the security paper.

도 8은 미세 인쇄패턴을 갖는 은선 시트를 나타낸 전면도.8 is a front view showing a hidden line sheet having a fine printed pattern.

도 9는 본 발명의 은선 제조방법을 나타낸 순서도.9 is a flow chart showing a method for producing a silver wire of the present invention.

**도면의 주요부분에 대한 부호의 설명**DESCRIPTION OF REFERENCE NUMERALS

10: 은선 11: 기재 필름10: hidden line 11: base film

12: 촉매층 13: 금속층12: catalyst layer 13: metal layer

14: 알루미늄 증착층 20: 보안용지14: aluminum deposition layer 20: security paper

21 : 종이21: paper

110: 삽입된 부분 120: 노출된 부분110: inserted portion 120: exposed portion

Claims (10)

a) 기재 필름(11)의 일면 또는 양면에 팔라듐 촉매로서 팔라듐 아세테이트를 함유하고, 에틸락테이트, 폴리에스터 아크릴레이트, 폴리에테르 개질 폴리디메틸실록산, 아크릴레이트계 단량체, 광개시제 및 용제를 함유하는 촉매형 잉크를 인쇄한 후 경화하여 촉매층(12)을 형성하는 단계; 및a) Catalyst type containing palladium acetate as a palladium catalyst on one or both surfaces of the base film 11, containing ethyl lactate, polyester acrylate, polyether-modified polydimethylsiloxane, acrylate monomer, photoinitiator and solvent Curing the ink after printing to form the catalyst layer 12; And b) 상기 촉매층(12) 상에 금속나노 잉크를 인쇄한 후 경화하여 금속층(13)을 형성하는 단계;b) printing the metal nano ink on the catalyst layer 12 and then curing to form a metal layer 13; 를 포함하는 위조방지용 은선의 제조방법.Method of producing a forgery preventing silver wire comprising a. 삭제delete 삭제delete 제 1 항에 있어서,The method of claim 1, 상기 금속 나노 잉크는 금속 나노입자, 자외선 경화형 수지, 용제 및 광개시제를 함유하는 위조방지용 은선의 제조방법.The metal nano ink is a method for producing an anti-counterfeiting silver wire containing a metal nanoparticle, an ultraviolet curable resin, a solvent and a photoinitiator. 제 4 항에 있어서,The method of claim 4, wherein 상기 금속 나노입자는 금속 나노 잉크 중량의 30 내지 50중량%인 위조방지 용 은선의 제조방법.The metal nanoparticles are 30 to 50% by weight of the metal nano ink weight of the anti-counterfeiting silver wire manufacturing method. 제 4 항에 있어서,The method of claim 4, wherein 상기 금속 나노입자는 구리, 은, 알루미늄 또는 금으로부터 선택되는 1종 이상이고 평균 입경이 1 내지 20nm인 위조방지용 은선의 제조방법.The metal nanoparticles are at least one selected from copper, silver, aluminum or gold and the method for producing a counterfeit silver wire having an average particle diameter of 1 to 20nm. 제 1 항에 있어서,The method of claim 1, 상기 기재 필름(11)은 폴리아미드계 수지, 폴리에스테르계 수지, 폴리아크릴계 수지, 폴리비닐아세테이트계 수지, 폴리에틸렌계 수지 및 폴리염화비닐계 수지로부터 선택되는 1종 이상의 투명 필름; 또는 상기 투명 필름의 일면 또는 양면에 패턴화되거나 패턴화되지 않은 금속막이 형성되거나, 형광물질, 자성물질, 적외선물질, 상향전이물질 및 편광물질로부터 선택된 1종 이상이 코팅되거나, 홀로그램이 부가된 필름;인 것을 특징으로 하는 위조방지용 은선의 제조방법.The base film 11 may include at least one transparent film selected from polyamide resin, polyester resin, polyacrylic resin, polyvinylacetate resin, polyethylene resin, and polyvinyl chloride resin; Or a film having a patterned or unpatterned metal film formed on one or both surfaces of the transparent film, coated with one or more selected from fluorescent materials, magnetic materials, infrared materials, upward transition materials, and polarizing materials, or added with a hologram Method for producing a forged silver wire, characterized in that; 삭제delete 삭제delete 삭제delete
KR1020080076436A 2008-08-05 2008-08-05 A method for preparing security thread KR101001536B1 (en)