KR100986908B1 - 오스테나이트계 스테인레스강 연주주편의 제조방법 - Google Patents
오스테나이트계 스테인레스강 연주주편의 제조방법 Download PDFInfo
- Publication number
- KR100986908B1 KR100986908B1 KR1020030092917A KR20030092917A KR100986908B1 KR 100986908 B1 KR100986908 B1 KR 100986908B1 KR 1020030092917 A KR1020030092917 A KR 1020030092917A KR 20030092917 A KR20030092917 A KR 20030092917A KR 100986908 B1 KR100986908 B1 KR 100986908B1
- Authority
- KR
- South Korea
- Prior art keywords
- stainless steel
- cast
- austenitic stainless
- steel
- scale
- Prior art date
Abstract
Description
유량(l/min) | 노즐의 각도(°) | 노즐과 주편의 거리(mm) | 평균스케일두께(㎛) |
4.09 | 95 | 250 | 24 |
4.09 | 110 | 250 | 26 |
5.08 | 95 | 250 | 19 |
5.08 | 110 | 250 | 20 |
6.05 | 95 | 250 | 14 |
6.05 | 110 | 250 | 16 |
노즐의 각도(°) | 유량(l/min) | 노즐과 주편간의 거리(mm) | 평균스케일 두께(㎛) |
냉각효율 적합성 |
95° | 4.09 | 50 | 10 | x |
95° | 4.09 | 100 | 16 | o |
95° | 4.09 | 140 | 19 | o |
95° | 4.09 | 250 | 24 | o |
95° | 4.09 | 300 | 32 | x |
비수량(l/kg) | 델타페라이트 평균함량(%) |
스케일두께(㎛) | 결함지수 | |
1000∼1200℃구간 | 전체영역평균 | |||
0.45 | 0.44 | 4.4 | 83 | 발생 |
0.50 | 0.44 | 4.9 | 58 | 미발생 |
0.60 | 0.50 | 5.8 | 42 | 미발생 |
0.65 | 0.60 | 6.1 | 40 | 미발생 |
0.70 | 0.44 | 6.3 | 39 | 발생(국부크랙) |
Claims (1)
- 중량%로, Cr:16.6∼17.1%, Ni: 7.6∼8%, Cu: 2.1∼2.4%, C:0.03∼0.05%, N:0.025%이하, Si:0.5∼0.7%, Mn:1.3∼1.6%, P: 0.035%이하, S:0.05%이하, 잔부는 Fe 및 기타 불가피한 성분을 함유하는 오스테나이트계 스테인레스강의 연주주편의 제조방법에 있어서,상기 연주주편의 이차냉각시 이차냉각대에서 노즐과 주편간의 거리를 100∼250mm로 하고, 주편의 표면온도가 1200∼1000℃인 구간에서 비수량을 0.50∼0.65l/kg으로 하여 냉각하는 것을 특징으로 하는 304J1L 오스테나이트계 스테인레스강 연주주편의 제조방법.